JP2005268026A - Coating composite for active material layer, electrode plate for non-aqueous electrolytic liquid secondary battery, and non-aqueous electrolytic liquid secondary battery - Google Patents
Coating composite for active material layer, electrode plate for non-aqueous electrolytic liquid secondary battery, and non-aqueous electrolytic liquid secondary battery Download PDFInfo
- Publication number
- JP2005268026A JP2005268026A JP2004078322A JP2004078322A JP2005268026A JP 2005268026 A JP2005268026 A JP 2005268026A JP 2004078322 A JP2004078322 A JP 2004078322A JP 2004078322 A JP2004078322 A JP 2004078322A JP 2005268026 A JP2005268026 A JP 2005268026A
- Authority
- JP
- Japan
- Prior art keywords
- active material
- material layer
- secondary battery
- electrode plate
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、リチウムイオン二次電池に代表される非水電解液二次電池用の活物質層用塗工組成物、電極材、及び当該電極材を用いた非水電解液二次電池に関する。 The present invention relates to a coating composition for an active material layer for a non-aqueous electrolyte secondary battery represented by a lithium ion secondary battery, an electrode material, and a non-aqueous electrolyte secondary battery using the electrode material.
近年、電子機器や通信機器の小型化および軽量化が急速に進んでおり、これらの駆動用電源として用いられる二次電池に対しても小型化および軽量化が要求されている。このため、従来のアルカリ蓄電池に代わり、高エネルギー密度で高電圧を有する非水電解液二次電池、代表的にはリチウムイオン二次電池が提案されている。 In recent years, electronic devices and communication devices are rapidly becoming smaller and lighter, and secondary batteries used as power sources for driving these devices are also required to be smaller and lighter. For this reason, in place of the conventional alkaline storage battery, a non-aqueous electrolyte secondary battery having a high energy density and a high voltage, typically a lithium ion secondary battery has been proposed.
非水電解液二次電池の正極用電極板(正極板)は、マンガン酸リチウムやコバルト酸リチウム等の複合酸化物を正極活物質として用い、そのような正極活物質と結着材(バインダー)とを適当な湿潤剤(溶剤)に分散または溶解させてスラリー状の塗工組成物を調製し、当該塗工組成物を金属箔からなる集電体上に塗工して正極活物質層を形成することにより作製される。 A positive electrode plate (positive electrode plate) of a non-aqueous electrolyte secondary battery uses a composite oxide such as lithium manganate or lithium cobaltate as a positive electrode active material, and such a positive electrode active material and a binder (binder). Is dispersed or dissolved in a suitable wetting agent (solvent) to prepare a slurry-like coating composition, and the coating composition is applied onto a current collector made of a metal foil to form a positive electrode active material layer. It is produced by forming.
一方、非水電解液二次電池の負極用電極板(負極板)は、充電時に正極活物質層から放出されるリチウムイオン等の陽イオンを吸蔵できるカーボン等の炭素質材料を負極活物質として用い、そのような負極活物質と結着材(バインダー)とを適当な湿潤剤(溶剤)に分散または溶解させてスラリー状の塗工組成物を調製し、当該塗工組成物を金属箔からなる集電体上に塗工して負極活物質層を形成することにより作製される。 On the other hand, the negative electrode plate (negative electrode plate) of the non-aqueous electrolyte secondary battery uses a carbonaceous material such as carbon that can occlude cations such as lithium ions released from the positive electrode active material layer during charging as the negative electrode active material. A slurry-like coating composition is prepared by dispersing or dissolving such a negative electrode active material and a binder (binder) in an appropriate wetting agent (solvent), and the coating composition is removed from the metal foil. The negative electrode active material layer is formed by coating on the current collector.
そして、正極電極板と負極電極板それぞれに電流を取り出すための端子を取り付け、両電極板の間に短絡を防止するためのセパレータを挟んで巻き取り、非水電解質溶液を満たした容器に密封することにより二次電池が組み立てられる。 Then, by attaching terminals for taking out current to each of the positive electrode plate and the negative electrode plate, sandwiching a separator for preventing a short circuit between the two electrode plates, winding it, and sealing it in a container filled with the nonaqueous electrolyte solution A secondary battery is assembled.
近年さらに、より高容量の非水電解液二次電池が要求されてきており、活物質層中における直接電池容量に起因する活物質の配合量を増加するため、活物質を集電体上に固定するための結着材や導電性を確保するための導電材等、直接電池容量に関わらない材料を、活物質層用塗工組成物からできるだけ減らすことがなされている。また、使用する導電材を工夫して、サイクル特性や放電特性の向上を図る試みがなされている(例えば、特許文献1、特許文献2、特許文献3)。 In recent years, a higher capacity non-aqueous electrolyte secondary battery has been required, and in order to increase the amount of the active material due to the direct battery capacity in the active material layer, the active material is placed on the current collector. Materials that are not directly related to battery capacity, such as a binder for fixing and a conductive material for ensuring conductivity, are reduced as much as possible from the coating composition for the active material layer. In addition, attempts have been made to improve cycle characteristics and discharge characteristics by devising a conductive material to be used (for example, Patent Document 1, Patent Document 2, and Patent Document 3).
高容量化のため塗膜の中に存在する導電材を極端に減らすと、導電パスの形成が不十分となり、塗膜の抵抗が上がり、サイクル特性の悪化及び内部抵抗の上昇といった電池性能が悪化する問題が、特に正極において生じており、導電材を極端に減らすことにより活物質の配合割合を増加して電池容量を上げることに限界が生じていた。一方、導電材の配合割合が少ない活物質層用塗工組成物は、保存安定性が悪く、数日放置しておくと体積抵抗率が上昇するという問題もあった。 If the conductive material present in the coating film is extremely reduced for higher capacity, the formation of the conductive path becomes insufficient, the resistance of the coating film increases, and the battery performance deteriorates such as deterioration of cycle characteristics and increase of internal resistance. This problem has occurred particularly in the positive electrode, and there has been a limit in increasing the battery capacity by increasing the blending ratio of the active material by extremely reducing the conductive material. On the other hand, the coating composition for an active material layer having a small proportion of the conductive material has poor storage stability, and has a problem that the volume resistivity increases when it is left for several days.
本発明は上記の実状に鑑みて成し遂げられたものであり、その第一の目的は、保存安定性が良く、高い電池容量の非水電解液二次電池用電極板を安定して製造し得る活物質層用塗工組成物を提供することにある。 The present invention has been accomplished in view of the above-mentioned circumstances, and the first object thereof is to provide a storage battery with a good storage stability and to stably produce an electrode plate for a non-aqueous electrolyte secondary battery having a high battery capacity. It is providing the coating composition for active material layers.
本発明は上記の実状に鑑みて成し遂げられたものであり、その第二の目的は、高い電池容量を実現し、サイクル特性の悪化及び内部抵抗の上昇といった問題が生じ難い非水電解液二次電池用電極板を提供することにある。 The present invention has been accomplished in view of the above-mentioned circumstances, and its second object is to achieve a high battery capacity, and to produce a secondary battery that is unlikely to cause problems such as deterioration in cycle characteristics and increase in internal resistance. The object is to provide an electrode plate for a battery.
また、本発明の第三の目的は、上記電極板を用いて、高い電池容量でありながら、サイクル特性の悪化及び内部抵抗の上昇といった電池性能が悪化する問題が生じ難い非水電解液二次電池を提供することにある。 The third object of the present invention is to provide a non-aqueous electrolyte secondary solution that uses the electrode plate and has a high battery capacity, but hardly causes problems such as deterioration of cycle characteristics and increase of internal resistance. To provide a battery.
本発明に係る活物質層用塗工組成物は、活物質100重量部に対して導電材を2重量部以下含有し、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有する。 The coating composition for an active material layer according to the present invention contains 2 parts by weight or less of a conductive material with respect to 100 parts by weight of the active material, the oil absorption amount of dibutyl phthalate is 250 ml / 100 g or more, and the BET specific surface area is 50. Carbon black of ˜150 m 2 / g is contained in the total conductive material by 50% by weight or more.
本発明においては、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有するため、カーボンブラック等の導電材が均一に分散した状態が安定に保持される。このため、活物質100重量部に対して導電材を2重量部以下と少量含有する活物質層用塗工組成物でありながら、導電性が確保されて体積抵抗率が低い値を有し、その上保存安定性が良い。活物質100重量部に対して導電材を2重量部以下と少量しか含有しないため、高い電池容量の非水電解液二次電池用電極板を安定して製造し得る。 In the present invention, carbon black having an oil absorption of dibutyl phthalate of 250 ml / 100 g or more and a BET specific surface area of 50 to 150 m 2 / g is contained in the entire conductive material by 50 wt% or more. A state where the conductive material is uniformly dispersed is stably maintained. For this reason, while it is a coating composition for an active material layer containing a conductive material in a small amount of 2 parts by weight or less with respect to 100 parts by weight of the active material, conductivity is ensured and the volume resistivity has a low value, In addition, storage stability is good. Since the conductive material is contained in a small amount of 2 parts by weight or less with respect to 100 parts by weight of the active material, an electrode plate for a non-aqueous electrolyte secondary battery having a high battery capacity can be stably produced.
本発明に係る活物質層用塗工組成物は、調製後25℃で7日静置した後の体積抵抗率が150Ω・cm以下であることが好ましい。 The active material layer coating composition according to the present invention preferably has a volume resistivity of 150 Ω · cm or less after being allowed to stand at 25 ° C. for 7 days after preparation.
本発明に係る非水電解液二次電池用電極板は、集電体の一面側又は両面に、活物質100重量部に対して導電材を2重量部以下含有し、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有する活物質層を設けてなることを特徴とする。 The electrode plate for a non-aqueous electrolyte secondary battery according to the present invention contains 2 parts by weight or less of a conductive material with respect to 100 parts by weight of the active material on one side or both sides of the current collector, and the oil absorption of dibutyl phthalate Is characterized in that an active material layer containing 50% by weight or more of carbon black having a BET specific surface area of 50 to 150 m 2 / g in a total conductive material is provided.
本発明に係る非水電解液二次電池用電極板は、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有する活物質層を設けてなるため、活物質100重量部に対して導電材を2重量部以下と少量含有する活物質層でありながら、カーボンブラック等の導電材が均一に分散した状態が安定に保持され、導電性が確保されて体積抵抗率が低い値を有する活物質層が得られる。活物質100重量部に対して導電材を2重量部以下と少量しか含有しないため活物質層中に存在する活物質の割合が高くなり、高い電池容量を実現し、また、導電材が均一に分散した状態が安定に保持されるため、サイクル特性の悪化及び内部抵抗の上昇といった問題が生じ難い。 In the electrode plate for a non-aqueous electrolyte secondary battery according to the present invention, carbon black having an oil absorption of dibutyl phthalate of 250 ml / 100 g or more and a BET specific surface area of 50 to 150 m 2 / g is contained in all conductive materials. Since an active material layer containing at least wt% is provided, the conductive material such as carbon black is uniformly dispersed while the active material layer contains a small amount of conductive material of 2 parts by weight or less with respect to 100 parts by weight of the active material. As a result, an active material layer having a low volume resistivity can be obtained. Since the conductive material is contained in a small amount of 2 parts by weight or less with respect to 100 parts by weight of the active material, the ratio of the active material present in the active material layer is increased, a high battery capacity is realized, and the conductive material is uniform. Since the dispersed state is stably maintained, problems such as deterioration in cycle characteristics and increase in internal resistance are unlikely to occur.
前記活物質層の体積抵抗率は、サイクル特性の悪化及び内部抵抗の上昇といった問題が生じ難い点から、150Ω・cm以下であることが好ましい。また、前記活物質層は、調製後25℃で7日静置した後の体積抵抗率が150Ω・cm以下である活物質層用塗工組成物を用いて形成されたものであることが、低い体積抵抗率の実現の点から好ましい。 The volume resistivity of the active material layer is preferably 150 Ω · cm or less from the viewpoint that problems such as deterioration in cycle characteristics and increase in internal resistance are unlikely to occur. In addition, the active material layer is formed using an active material layer coating composition having a volume resistivity of 150 Ω · cm or less after standing at 25 ° C. for 7 days after preparation. This is preferable from the viewpoint of realizing a low volume resistivity.
次に、本発明に係る非水電解液二次電池は、上記本発明に係る非水電解液二次電池用電極板を備えることを特徴とする。この二次電池は、内部に装填された電極板が、導電材を少量含有する活物質層でありながら、該活物質層の体積抵抗率が低い値を有するため、高い電池容量でありながら、サイクル特性が良く、内部抵抗が低い。 Next, the non-aqueous electrolyte secondary battery according to the present invention includes the electrode plate for a non-aqueous electrolyte secondary battery according to the present invention. In this secondary battery, while the electrode plate loaded therein is an active material layer containing a small amount of a conductive material, the volume resistivity of the active material layer has a low value, so that the battery capacity is high, Good cycle characteristics and low internal resistance.
本発明の活物質層用塗工組成物は、カーボンブラック等の導電材が均一に分散した状態が安定に保持され、活物質100重量部に対して導電材を2重量部以下と少量含有する活物質層用塗工組成物でありながら、導電性が確保されて体積抵抗率が低い値を有し、その上保存安定性が良い。活物質100重量部に対して導電材を2重量部以下と少量しか含有せず、活物質の配合割合が多いため、高い電池容量の非水電解液二次電池用電極板を安定して製造し得る。 The active material layer coating composition of the present invention stably maintains a state in which a conductive material such as carbon black is uniformly dispersed, and contains a small amount of the conductive material of 2 parts by weight or less with respect to 100 parts by weight of the active material. Although it is a coating composition for an active material layer, conductivity is ensured and the volume resistivity has a low value, and in addition, storage stability is good. Containing less than 2 parts by weight or less of conductive material with respect to 100 parts by weight of active material, and high proportion of active material, stable production of non-aqueous electrolyte secondary battery electrode plates with high battery capacity Can do.
本発明に係る非水電解液二次電池用電極板は、活物質100重量部に対して導電材を2重量部以下と少量しか含有せず、活物質の配合割合が多いため、高い電池容量を実現し、また、導電材が均一に分散した状態が安定に保持されるため、サイクル特性の悪化及び内部抵抗の上昇といった問題が生じ難い。 The electrode plate for a non-aqueous electrolyte secondary battery according to the present invention contains only a small amount of a conductive material of 2 parts by weight or less with respect to 100 parts by weight of the active material and has a high blending ratio of the active material. In addition, since the state in which the conductive material is uniformly dispersed is stably maintained, problems such as deterioration in cycle characteristics and increase in internal resistance are unlikely to occur.
また、本発明に係る非水電解液二次電池は、内部に装填された電極板が、導電材を少量含有する活物質層でありながら、該活物質層の体積抵抗率が低い値を有するため、高い電池容量でありながら、サイクル特性が良く、内部抵抗が低い。 Moreover, the nonaqueous electrolyte secondary battery according to the present invention has a low volume resistivity of the active material layer while the electrode plate loaded therein is an active material layer containing a small amount of a conductive material. Therefore, while having a high battery capacity, the cycle characteristics are good and the internal resistance is low.
<活物質層用塗工組成物>
本発明に係る活物質層用塗工組成物は、活物質100重量部に対して導電材を2重量部以下含有し、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有することを特徴とする。
ここで、フタル酸ジブチルの吸油量(以下、DBP吸油量と略記する場合がある)は、JIS−K6221「ゴム用カーボンブラックの試験方法」6.1.1項により求めることができる。また、BET比表面積は、窒素吸着法によるBET比表面積をいう。
<Coating composition for active material layer>
The coating composition for an active material layer according to the present invention contains 2 parts by weight or less of a conductive material with respect to 100 parts by weight of the active material, the oil absorption amount of dibutyl phthalate is 250 ml / 100 g or more, and the BET specific surface area is 50. Carbon black of ˜150 m 2 / g is contained in the total conductive material in an amount of 50% by weight or more.
Here, the oil absorption amount of dibutyl phthalate (hereinafter sometimes abbreviated as DBP oil absorption amount) can be obtained according to JIS-K6221 “Testing Method of Carbon Black for Rubber”, Section 6.1.1. Moreover, a BET specific surface area says the BET specific surface area by a nitrogen adsorption method.
本発明に係る活物質層用塗工組成物は、正極用であっても負極用であってもいずれでも良い。正極用活物質層塗工組成物は、少なくとも正極活物質、導電材及び通常は結着材を含有する。一方、負極用活物質層塗工組成物は、少なくとも負極活物質、導電材及び通常は結着材を含有する。 The active material layer coating composition according to the present invention may be used for either the positive electrode or the negative electrode. The positive electrode active material layer coating composition contains at least a positive electrode active material, a conductive material, and usually a binder. On the other hand, the negative electrode active material layer coating composition contains at least a negative electrode active material, a conductive material, and usually a binder.
正極活物質としては、従来から非水電解液二次電池の正極活物質として用いられている材料を用いることができ、例えば、LiMn2O4(マンガン酸リチウム)、LiCoO2(コバルト酸リチウム)若しくはLiNiO2(ニッケル酸リチウム)等のリチウム酸化物、または
TiS2、MnO2、MoO3もしくはV2O5等のカルコゲン化合物を例示することができる。特に、LiCoO2を正極用活物質として用い、炭素質材料を負極用活物質として用いることにより、4ボルト程度の高い放電電圧を有するリチウム系2次電池が得られる。
As the positive electrode active material, it is possible to use a material used as a positive electrode active material of nonaqueous electrolyte secondary batteries conventionally, for example, LiMn 2 O 4 (lithium manganate), LiCoO 2 (lithium cobaltate) Alternatively, a lithium oxide such as LiNiO 2 (lithium nickelate) or a chalcogen compound such as TiS 2 , MnO 2 , MoO 3, or V 2 O 5 can be exemplified. In particular, by using LiCoO 2 as a positive electrode active material and a carbonaceous material as a negative electrode active material, a lithium secondary battery having a high discharge voltage of about 4 volts can be obtained.
正極活物質は、塗工層中に均一に分散させるために、1〜100μmの範囲の粒径を有し、且つ平均粒径が3〜30μmの粉体であることが好ましい。これらの正極用活物質は単独で用いてもよいし、2種以上を組み合わせて用いてもよい。 The positive electrode active material is preferably a powder having a particle diameter in the range of 1 to 100 μm and an average particle diameter of 3 to 30 μm in order to uniformly disperse it in the coating layer. These positive electrode active materials may be used alone or in combination of two or more.
一方、負極活物質としては、従来から非水電解液二次電池の負極活物質として用いられている材料を用いることができ、例えば、天然グラファイト、人造グラファイト、アモルファス炭素、カーボンブラック、または、これらの成分に異種元素を添加したもののような炭素質材料が好んで用いられる。溶媒が有機系の場合には金属リチウムまたはリチウム合金のようなリチウム含有金属が好適に用いられる。 On the other hand, as the negative electrode active material, materials conventionally used as the negative electrode active material of non-aqueous electrolyte secondary batteries can be used. For example, natural graphite, artificial graphite, amorphous carbon, carbon black, or these Carbonaceous materials such as those obtained by adding different elements to these components are preferably used. When the solvent is organic, a lithium-containing metal such as lithium metal or a lithium alloy is preferably used.
負極活物質の粒子形状は特に限定されないが、例えば、鱗片状、塊状、繊維状、球状のものが使用可能である。負極活物質は、塗工層中に均一に分散させるために、1〜100μmの範囲の粒径を有し、且つ平均粒径が3〜30μmの粉体であることが好ましい。これらの負極用活物質は単独で用いてもよいし、2種以上を組み合わせて用いてもよい。 Although the particle shape of a negative electrode active material is not specifically limited, For example, a flaky shape, a lump shape, a fiber shape, and a spherical shape can be used. The negative electrode active material is preferably a powder having a particle size in the range of 1 to 100 μm and an average particle size of 3 to 30 μm in order to be uniformly dispersed in the coating layer. These negative electrode active materials may be used alone or in combination of two or more.
塗工組成物中の正極又は負極活物質の配合割合は、溶剤を除く配合成分を基準(固形分基準)とした時に、高い電池容量を実現とサイクル特性とのバランスの点から90〜98.5重量%とすることが好ましく、更に96〜98.5重量%とすることが好ましい。 The blending ratio of the positive electrode or negative electrode active material in the coating composition is 90 to 98.degree. From the viewpoint of achieving a high battery capacity and a balance between cycle characteristics when the blending component excluding the solvent is used as a standard (solid content standard). It is preferably 5% by weight, more preferably 96 to 98.5% by weight.
本発明において正極又は負極用活物質層塗工組成物には、活物質100重量部に対して導電材を2重量部以下含有し、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有するように導電材を添加する。フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有するようにすると、導電材が均一に分散した状態が安定に保持される。このため、活物質100重量部に対して導電材を2重量部以下と少量含有する活物質層用塗工組成物でありながら、導電性が確保されて体積抵抗率が低い値を有し、その上保存安定性が良い。活物質100重量部に対して導電材を2重量部以下と少量しか含有しないため、高い電池容量の非水電解液二次電池用電極板を安定して製造し得る。 In the present invention, the active material layer coating composition for positive electrode or negative electrode contains 2 parts by weight or less of a conductive material with respect to 100 parts by weight of the active material, the oil absorption of dibutyl phthalate is 250 ml / 100 g or more, and the BET ratio The conductive material is added so that carbon black having a surface area of 50 to 150 m 2 / g is contained in the total conductive material by 50% by weight or more. When carbon black having an oil absorption of dibutyl phthalate of 250 ml / 100 g or more and a BET specific surface area of 50 to 150 m 2 / g is contained in all conductive materials by 50% by weight or more, the conductive material is uniformly dispersed. The state is kept stable. For this reason, while it is a coating composition for an active material layer containing a conductive material in a small amount of 2 parts by weight or less with respect to 100 parts by weight of the active material, conductivity is ensured and the volume resistivity has a low value, In addition, storage stability is good. Since the conductive material is contained in a small amount of 2 parts by weight or less with respect to 100 parts by weight of the active material, an electrode plate for a non-aqueous electrolyte secondary battery having a high battery capacity can be stably produced.
フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックは、分散安定性の点から、さらに好ましくはフタル酸ジブチルの吸油量が250〜320ml/100gで且つBET比表面積が50〜100m2/gであるカーボンブラックを用いることが好ましい。上記性状を示すカーボンブラックとしては、例えば、MMMCarbon製SuperP(フタル酸ジブチルの吸油量が290ml/100g、BET比表面積が62m2/g)が挙げられる。フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有するようにすると、導電性が確保されて体積抵抗率が低い値を有し、その上保存安定性が良くなるが、更に体積抵抗率が低くなる点から、上記性状を示すカーボンブラックは多く含まれるほど好ましく、全導電材中に60重量%以上、更に70重量%以上配合されることが好ましい。 Carbon black having an oil absorption of dibutyl phthalate of 250 ml / 100 g or more and a BET specific surface area of 50 to 150 m 2 / g is more preferably 250 to 320 ml / g from the viewpoint of dispersion stability. It is preferable to use carbon black having 100 g and a BET specific surface area of 50 to 100 m 2 / g. Examples of the carbon black exhibiting the above properties include SuperP (manufactured by MMMCarbon having an oil absorption of 290 ml / 100 g of dibutyl phthalate and a BET specific surface area of 62 m 2 / g). When carbon black having an oil absorption of dibutyl phthalate of 250 ml / 100 g or more and a BET specific surface area of 50 to 150 m 2 / g is contained in all conductive materials by 50 wt% or more, conductivity is ensured and volume is increased. The resistivity has a low value and the storage stability is improved, but the volume resistivity is further lowered. From the viewpoint of lowering the volume resistivity, it is preferable that a larger amount of carbon black having the above properties is contained. As mentioned above, it is preferable that 70 weight% or more is further blended.
フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックと共に用いられる他の導電材としては、特に制限されず、例えば、グラファイト、フタル酸ジブチルの吸油量とBET比表面積が上記範囲外のカーボンブラックまたはアセチレンブラック等の炭素質材料が用いられる。 Other conductive materials used together with carbon black having an oil absorption of dibutyl phthalate of 250 ml / 100 g or more and a BET specific surface area of 50 to 150 m 2 / g are not particularly limited. For example, graphite, dibutyl phthalate A carbonaceous material such as carbon black or acetylene black whose oil absorption and BET specific surface area are outside the above ranges is used.
また、正極又は負極用活物質層塗工組成物には、通常、結着材が添加される。結着材としては従来から用いられているもの、例えば、熱可塑性樹脂、より具体的にはポリエステル樹脂、ポリアミド樹脂、ポリアクリル酸エステル樹脂、ポリカーボネート樹脂、ポリウレタン樹脂、セルロース樹脂、ポリオレフィン樹脂、ポリビニル樹脂、PTFEやポリフッ化ビニリデン等のフッ素系樹脂、または、ポリイミド樹脂あるいはスチレンブタジエンゴム等のゴム系樹脂等を使用することができる。この際、反応性官能基を導入したアクリレートモノマーまたはオリゴマーを結着材中に混入させることも可能である。そのほかにも、ゴム系の樹脂や、アクリル樹脂、ウレタン樹脂等の熱硬化性樹脂、アクリレートモノマー、アクリレートオリゴマー或いはそれらの混合物からなる電離放射線硬化性樹脂、上記各種の樹脂の混合物を使用することもできる。 Moreover, a binder is normally added to the active material layer coating composition for positive electrodes or negative electrodes. Conventionally used binders such as thermoplastic resins, more specifically polyester resins, polyamide resins, polyacrylate resins, polycarbonate resins, polyurethane resins, cellulose resins, polyolefin resins, polyvinyl resins Fluorine resin such as PTFE and polyvinylidene fluoride, or rubber resin such as polyimide resin or styrene butadiene rubber can be used. At this time, an acrylate monomer or oligomer into which a reactive functional group has been introduced can be mixed in the binder. In addition, rubber resins, thermosetting resins such as acrylic resins and urethane resins, ionizing radiation curable resins made of acrylate monomers, acrylate oligomers or mixtures thereof, and mixtures of the above various resins may be used. it can.
塗工組成物中の結着材の配合割合は、固形分基準で通常は0.5〜10重量%、好ましくは0.9〜4重量%とする。 The blending ratio of the binder in the coating composition is usually 0.5 to 10% by weight, preferably 0.9 to 4% by weight, based on the solid content.
正極又は負極用活物質層塗工組成物を調製する溶剤としては、トルエン、メチルエチルケトン、N−メチル−2−ピロリドン或いはこれらの混合物のような有機溶剤を用いることができる。塗工組成物中の溶剤は、通常は固形分が組成物全体に対して40〜85重量%、好ましくは50〜80、さらに好ましくは60〜80重量%となるように配合し、塗工液をスラリー状に調製する。 As a solvent for preparing the positive electrode or negative electrode active material layer coating composition, an organic solvent such as toluene, methyl ethyl ketone, N-methyl-2-pyrrolidone, or a mixture thereof can be used. The solvent in the coating composition is usually blended so that the solid content is 40 to 85% by weight, preferably 50 to 80, more preferably 60 to 80% by weight, based on the entire composition, Is prepared in a slurry state.
正極又は負極活物質層用塗工組成物は、適宜選択した正極又は負極活物質、導電材、通常結着材、及び他の配合成分を適切な溶剤中にいれ、ホモジナイザー、ボールミル、サンドミル、ロールミルまたはプラネタリーミキサ等の分散機により混合分散して、スラリー状に調製できる。 The coating composition for the positive electrode or negative electrode active material layer is prepared by placing an appropriately selected positive electrode or negative electrode active material, conductive material, normal binder, and other compounding components in an appropriate solvent, and homogenizer, ball mill, sand mill, roll mill. Or it can mix and disperse | distribute with dispersers, such as a planetary mixer, and can prepare in a slurry form.
本発明に係る活物質層用塗工組成物は、調製後25℃で7日静置した後の体積抵抗率が150Ω・cm以下であることが、保存安定性、及び低い体積抵抗率の活物質層を実現し、電池のサイクル特性を良好にする点から好ましい。なお、体積抵抗率は、100μmのPETフィルム上の一面側に活物質層塗工組成物を乾燥後の塗膜が100μmとなるように塗布、乾燥し、得られた塗膜について、抵抗率計(例えば、三菱化学製、ロレスタ−EP)を用いて四端子四探針法にて測定したものをいう。 The coating composition for an active material layer according to the present invention has a volume resistivity of 150 Ω · cm or less after standing at 25 ° C. for 7 days after preparation, so that the storage stability and the activity of low volume resistivity are reduced. This is preferable from the viewpoint of realizing a material layer and improving the cycle characteristics of the battery. In addition, volume resistivity is a resistivity meter about the obtained coating film which applied and dried so that the coating film after drying the active material layer coating composition may be 100 μm on one side of a 100 μm PET film. (For example, manufactured by Mitsubishi Chemical, Loresta-EP) and measured by a four-terminal four-probe method.
<非水電解液二次電池用電極板>
本発明に係る非水電解液二次電池用電極板は、集電体の一面側又は両面に、活物質100重量部に対して導電材を2重量部以下含有し、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有する活物質層を設けてなることを特徴とする。
<Electrode plate for non-aqueous electrolyte secondary battery>
The electrode plate for a non-aqueous electrolyte secondary battery according to the present invention contains 2 parts by weight or less of a conductive material with respect to 100 parts by weight of the active material on one side or both sides of the current collector, and the oil absorption of dibutyl phthalate Is characterized in that an active material layer containing 50% by weight or more of carbon black having a BET specific surface area of 50 to 150 m 2 / g in a total conductive material is provided.
本発明に係る非水電解液二次電池用電極板は、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有する活物質層を設けてなるため、活物質100重量部に対して導電材を2重量部以下と少量含有する活物質層でありながら、カーボンブラック等の導電材が均一に分散した状態が安定に保持され、導電性が確保されて体積抵抗率が低い値を有する活物質層が得られる。活物質100重量部に対して導電材を2重量部以下と少量しか含有しないため活物質層中に存在する活物質の割合が高くなり、高い電池容量を実現し、また、導電材が均一に分散した状態が安定に保持されるため、サイクル特性の悪化及び内部抵抗の上昇といった問題が生じ難い。 In the electrode plate for a non-aqueous electrolyte secondary battery according to the present invention, carbon black having an oil absorption of dibutyl phthalate of 250 ml / 100 g or more and a BET specific surface area of 50 to 150 m 2 / g is contained in all conductive materials. Since an active material layer containing at least wt% is provided, the conductive material such as carbon black is uniformly dispersed while the active material layer contains a small amount of conductive material of 2 parts by weight or less with respect to 100 parts by weight of the active material. As a result, an active material layer having a low volume resistivity can be obtained. Since the conductive material is contained in a small amount of 2 parts by weight or less with respect to 100 parts by weight of the active material, the ratio of the active material present in the active material layer is increased, a high battery capacity is realized, and the conductive material is uniform. Since the dispersed state is stably maintained, problems such as deterioration in cycle characteristics and increase in internal resistance are unlikely to occur.
本発明に係る非水電解液二次電池用電極板は、正極板であっても負極板であってもいずれでも良い。正極板は、少なくとも正極活物質、導電材及び通常は結着材を含有する正極用活物質層塗工組成物を集電体の一面側又は両面に塗布して、正極活物質層を形成することによって作製される。一方、負極板は、少なくとも負極活物質、導電材及び通常は結着材を含有する負極用活物質層塗工組成物を集電体の一面側又は両面に塗布して、負極活物質層を形成することによって作製される。 The electrode plate for a non-aqueous electrolyte secondary battery according to the present invention may be a positive electrode plate or a negative electrode plate. The positive electrode plate is formed by applying a positive electrode active material layer coating composition containing at least a positive electrode active material, a conductive material, and usually a binder to one or both sides of a current collector to form a positive electrode active material layer It is produced by. On the other hand, the negative electrode plate is coated with a negative electrode active material layer coating composition containing at least a negative electrode active material, a conductive material, and usually a binder, on one side or both sides of the current collector, It is produced by forming.
電極板の活物質層は、少なくとも正極又は負極活物質、導電材、及び通常結着材を含有し、さらに必要に応じてその他の成分を含有してなるものであり、乾燥後の活物質層に含有される各成分の配合割合は、活物質層用塗工組成物の固形分基準での配合割合と同じである。従って、本発明に係る非水電解液二次電池用電極板は、活物質100重量部に対して導電材を2重量部以下含有し、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有する、上記本発明に係る活物質層用塗工組成物を用いて、集電体の一面側又は両面に塗布して、活物質層を形成することによって作製することができる。 The active material layer of the electrode plate contains at least a positive electrode or negative electrode active material, a conductive material, and a normal binder, and further contains other components as necessary. The active material layer after drying The blending ratio of each component contained in is the same as the blending ratio on the basis of the solid content of the coating composition for active material layer. Therefore, the electrode plate for a non-aqueous electrolyte secondary battery according to the present invention contains 2 parts by weight or less of a conductive material with respect to 100 parts by weight of the active material, the oil absorption of dibutyl phthalate is 250 ml / 100 g or more, and BET Using the coating composition for an active material layer according to the present invention, which contains 50% by weight or more of carbon black having a specific surface area of 50 to 150 m 2 / g, It can produce by apply | coating to both surfaces and forming an active material layer.
正極板の集電体としては通常、アルミニウム箔が好ましく用いられる。一方、負極板の集電体としては、電解銅箔や圧延銅箔等の銅箔が好ましく用いられる。集電体の厚さは通常、5〜50μm程度とする。 In general, an aluminum foil is preferably used as the current collector of the positive electrode plate. On the other hand, as the current collector of the negative electrode plate, a copper foil such as an electrolytic copper foil or a rolled copper foil is preferably used. The thickness of the current collector is usually about 5 to 50 μm.
正極又は負極活物質層用塗工組成物の塗布方法は、特に限定されないが、例えばスライドダイコート、コンマダイレクトコート、コンマリバースコート等のように、厚い塗工層を形成できる方法が適している。ただし、活物質層に求められる厚さが比較的薄い場合には、グラビアコートやグラビアリバースコート等により塗布してもよい。活物質層は、複数回塗布、乾燥を繰り返すことにより形成してもよい。 A method for applying the coating composition for the positive electrode or the negative electrode active material layer is not particularly limited, but a method capable of forming a thick coating layer such as a slide die coat, a comma direct coat, a comma reverse coat, and the like is suitable. However, when the thickness required for the active material layer is relatively thin, it may be applied by gravure coating or gravure reverse coating. The active material layer may be formed by repeating application and drying a plurality of times.
乾燥工程における熱源としては、熱風、赤外線、遠赤外線、マイクロ波、高周波、或いはそれらを組み合わせて利用できる。乾燥工程において集電体をサポート又はプレスする金属ローラーや金属シートを加熱して放出させた熱によって乾燥してもよい。また、乾燥後、電子線または放射線を照射することにより、結着材を架橋反応させて活物質層を得ることもできる。塗布と乾燥は、複数回繰り返してもよい。 As a heat source in the drying process, hot air, infrared rays, far infrared rays, microwaves, high frequencies, or a combination thereof can be used. You may dry with the heat which discharge | released the metal roller and metal sheet which support or press a collector in a drying process. In addition, after drying, the active material layer can also be obtained by irradiating an electron beam or radiation to cause a crosslinking reaction of the binder. Application and drying may be repeated a plurality of times.
更に、得られた正極又は負極活物質層をプレス加工することにより、活物質層の密度、集電体に対する密着性、均質性を向上させることができる。 Furthermore, by pressing the obtained positive electrode or negative electrode active material layer, the density of the active material layer, the adhesion to the current collector, and the homogeneity can be improved.
プレス加工は、例えば、金属ロール、弾性ロール、加熱ロールまたはシートプレス機等を用いて行う。本発明においてプレス温度は、活物質層の塗工膜を乾燥させる温度よりも低い温度とする限り、室温で行っても良いし又は加温して行っても良いが、通常は室温(室温の目安としては15〜35℃である。)で行う。 The press working is performed using, for example, a metal roll, an elastic roll, a heating roll, a sheet press machine, or the like. In the present invention, the pressing temperature may be performed at room temperature or may be performed as long as the temperature is lower than the temperature for drying the coating film of the active material layer. As a guide, it is 15 to 35 ° C.).
ロールプレスは、ロングシート状の負極板を連続的にプレス加工できるので好ましい。ロールプレスを行う場合には定位プレス、定圧プレスいずれを行っても良い。プレスのライン速度は通常、5〜50m/min.とする。ロールプレスの圧力を線圧で管理する場合、加圧ロールの直径に応じて調節するが、通常は線圧を0.5kgf/cm〜1tf/cmとする。 The roll press is preferable because a long sheet-like negative electrode plate can be continuously pressed. When performing the roll press, either a stereotaxic press or a constant pressure press may be performed. The line speed of the press is usually 5 to 50 m / min. And When the pressure of the roll press is managed by linear pressure, the pressure is adjusted according to the diameter of the pressure roll, but the linear pressure is usually 0.5 kgf / cm to 1 tf / cm.
また、シートプレスを行う場合には通常、4903〜73550N/cm2(500〜7500kgf/cm2)、好ましくは29420〜49033N/cm2(3000〜5000kgf/cm2)の範囲に圧力を調節する。プレス圧力が小さすぎると活物質層の均質性が得られにくく、プレス圧力が大きすぎると集電体を含めて電極板自体が破損してしまう場合がある。活物質層は、一回のプレスで所定の厚さにしてもよく、均質性を向上させる目的で数回に分けてプレスしてもよい。 Also, normally when performing sheet pressing, 4903~73550N / cm 2 (500~7500kgf / cm 2), preferably to adjust the pressure in the range of 29420~49033N / cm 2 (3000~5000kgf / cm 2). If the pressing pressure is too low, it is difficult to obtain the homogeneity of the active material layer. If the pressing pressure is too high, the electrode plate itself including the current collector may be damaged. The active material layer may have a predetermined thickness by a single press, or may be pressed several times for the purpose of improving homogeneity.
正極又は負極活物質層の塗工量は通常、20〜350g/m2とし、その厚さは、乾燥、プレス後に通常10〜200μm、好ましくは50〜190μmの範囲にする。負極活物質層の密度は、塗工後は1.0g/cc程度であるが、プレス後は1.5g/cc以上(通常は1.5〜1.75g/cc程度)まで増大する。従って、プレス加工を支障なく行って体積エネルギー密度を向上させることにより、電池の高容量化を図ることが出来る。 The coating amount of the positive electrode or negative electrode active material layer is usually 20 to 350 g / m 2 , and the thickness thereof is usually 10 to 200 μm, preferably 50 to 190 μm after drying and pressing. The density of the negative electrode active material layer is about 1.0 g / cc after coating, but increases to 1.5 g / cc or more (usually about 1.5 to 1.75 g / cc) after pressing. Therefore, the capacity of the battery can be increased by improving the volume energy density by performing the pressing without hindrance.
前記活物質層の体積抵抗率は、導電性が確保されてサイクル特性の悪化及び内部抵抗の上昇といった問題が生じ難い点から、150Ω・cm以下であることが好ましい。活物質層の体積抵抗率は、集電体とは絶縁させて測定する必要があるため、導電性のない基材上に活物質層を作製して測定する。活物質層の体積抵抗率は、具体的には、上記活物質層塗工組成物の体積抵抗率と同様に、100μmのPETフィルム上の一面側に活物質層塗工組成物を乾燥後の塗膜が100μmとなるように塗布、乾燥し、得られた塗膜について、抵抗率計(例えば、三菱化学製、ロレスタ−EP)を用いて四端子四探針法にて測定したものをいう。 The volume resistivity of the active material layer is preferably 150 Ω · cm or less from the viewpoint that conductivity is ensured and problems such as deterioration in cycle characteristics and increase in internal resistance are unlikely to occur. Since the volume resistivity of the active material layer needs to be measured while being insulated from the current collector, the active material layer is formed on a non-conductive base material and measured. Specifically, the volume resistivity of the active material layer is the same as the volume resistivity of the active material layer coating composition described above, after drying the active material layer coating composition on one side of a 100 μm PET film. It is applied and dried so that the coating film becomes 100 μm, and the coating film obtained is measured by a four-terminal four-probe method using a resistivity meter (for example, Loresta EP, manufactured by Mitsubishi Chemical Corporation). .
前記活物質層の体積抵抗率が150Ω・cm以下であるようにするためには、活物質層は、調製後25℃で7日静置した後の体積抵抗率が150Ω・cm以下である活物質層用塗工組成物を用いて形成されることが好ましい。 In order for the volume resistivity of the active material layer to be 150 Ω · cm or less, the active material layer is an active material having a volume resistivity of 150 Ω · cm or less after standing at 25 ° C. for 7 days. It is preferably formed using the material layer coating composition.
以上のようにして本発明に係る非水電解液二次電池用電極板が得られ、この電極板を用いて非水電解液二次電池を作製することができる。 As described above, the electrode plate for a non-aqueous electrolyte secondary battery according to the present invention is obtained, and a non-aqueous electrolyte secondary battery can be produced using this electrode plate.
本発明に係る電極板を用いて二次電池を作製する際には、電池の組立工程に移る前に活物質層中の水分及び/又は溶剤を除去するために、真空オーブン等で加熱処理や減圧処理等のエージングをあらかじめ行うことが好ましい。 When producing a secondary battery using the electrode plate according to the present invention, in order to remove moisture and / or solvent in the active material layer before moving to the battery assembly process, heat treatment or It is preferable to perform aging such as decompression in advance.
上記したような方法により作製された正極板及び負極板を、ポリエチレン製多孔質フィルムのようなセパレータを介して渦巻状に巻き回し、外装容器に挿入する。挿入後、正極板の端子接続部(集電体の露出面)と外装容器の上面に設けた正極端子をリードで接続し、一方、負極板の端子接続部(集電体の露出面)と外装容器の底面に設けた負極端子をリードで接続し、外装容器に非水電解液を充填し、密封することによって、本発明に係る電極板を備えた非水電解液二次電池が完成する。 The positive electrode plate and the negative electrode plate produced by the method as described above are spirally wound through a separator such as a polyethylene porous film and inserted into an outer container. After insertion, the terminal connection part of the positive electrode plate (exposed surface of the current collector) and the positive electrode terminal provided on the upper surface of the outer container are connected by leads, while the terminal connection part of the negative electrode plate (exposed surface of the current collector) The negative electrode terminal provided on the bottom surface of the outer container is connected with a lead, and the outer container is filled with a nonaqueous electrolyte and sealed, thereby completing a nonaqueous electrolyte secondary battery including the electrode plate according to the present invention. .
リチウム系二次電池を作製する場合には、溶質であるリチウム塩を有機溶媒に溶かした非水電解液が用いられる。リチウム塩としては、例えば、LiClO4、LiBF4、LiPF6、LiAsF6、LiCl、LiBr等の無機リチウム塩、または、LiB(C6H5)4、LiN(SO2CF3)2、LiC(SO2CF3)3、LiOSO2CF3、LiOSO2C2F5、LiOSO2C3F7、LiOSO2C4F9、LiOSO2C5F11、LiOSO2C6F13、LiOSO2C7F15等の有機リチウム塩等が用いられる。 When producing a lithium secondary battery, a nonaqueous electrolytic solution in which a lithium salt as a solute is dissolved in an organic solvent is used. Examples of the lithium salt include inorganic lithium salts such as LiClO 4 , LiBF 4 , LiPF 6 , LiAsF 6 , LiCl, and LiBr, or LiB (C 6 H 5 ) 4 , LiN (SO 2 CF 3 ) 2 , LiC ( SO 2 CF 3 ) 3 , LiOSO 2 CF 3 , LiOSO 2 C 2 F 5 , LiOSO 2 C 3 F 7 , LiOSO 2 C 4 F 9 , LiOSO 2 C 5 F 11 , LiOSO 2 C 6 F 13 , LiOSO 2 C An organic lithium salt such as 7 F 15 is used.
リチウム塩を溶解するための有機溶媒としては、環状エステル類、鎖状エステル類、環状エーテル類、鎖状エーテル類等を例示できる。より具体的には、環状エステル類としては、プロピレンカーボネート、ブチレンカーボネート、γ−ブチロラクトン、ビニレンカーボネート、2−メチル−γ−ブチロラクトン、アセチル−γ−ブチロラクトン、γ−バレロラクトン等を例示できる。 Examples of the organic solvent for dissolving the lithium salt include cyclic esters, chain esters, cyclic ethers, chain ethers and the like. More specifically, examples of cyclic esters include propylene carbonate, butylene carbonate, γ-butyrolactone, vinylene carbonate, 2-methyl-γ-butyrolactone, acetyl-γ-butyrolactone, γ-valerolactone, and the like.
鎖状エステル類としては、ジメチルカーボネート、ジエチルカーボネート、ジブチルカーボネート、ジプロピルカーボネート、メチルエチルカーボネート、メチルブチルカーボネート、メチルプロピルカーボネート、エチルブチルカーボネート、エチルプロピルカーボネート、ブチルプロピルカーボネート、プロピオン酸アルキルエステル、マロン酸ジアルキルエステル、酢酸アルキルエステル等を例示できる。 Chain esters include dimethyl carbonate, diethyl carbonate, dibutyl carbonate, dipropyl carbonate, methyl ethyl carbonate, methyl butyl carbonate, methyl propyl carbonate, ethyl butyl carbonate, ethyl propyl carbonate, butyl propyl carbonate, propionic acid alkyl ester, malon Examples thereof include acid dialkyl esters and acetic acid alkyl esters.
環状エーテル類としては、テトラヒドロフラン、アルキルテトラヒドロフラン、ジアルキルテトラヒドロフラン、アルコキシテトラヒドロフラン、ジアルコキシテトラヒドロフラン、1,3−ジオキソラン、アルキル−1,3−ジオキソラン、1,4−ジオキソラン等を例示できる。 Examples of cyclic ethers include tetrahydrofuran, alkyltetrahydrofuran, dialkyltetrahydrofuran, alkoxytetrahydrofuran, dialkoxytetrahydrofuran, 1,3-dioxolane, alkyl-1,3-dioxolane, 1,4-dioxolane and the like.
鎖状エーテル類としては、1,2−ジメトキシエタン、1,2−ジエトキシエタン、ジエチルエーテル、エチレングリコールジアルキルエーテル、ジエチレングリコールジアルキルエーテル、トリエチレングリコールジアルキルエーテル、テトラエチレングリコールジアルキルエーテル等を例示することができる。 Examples of chain ethers include 1,2-dimethoxyethane, 1,2-diethoxyethane, diethyl ether, ethylene glycol dialkyl ether, diethylene glycol dialkyl ether, triethylene glycol dialkyl ether, and tetraethylene glycol dialkyl ether. Can do.
(実施例1;非水電解液二次電池用電極板の作製)
正極用活物質としてLiCoO2粉末を100重量部と、導電材としてMMMCarbon製SuperPを2重量部と、結着材としてポリフッ化ビニリデンを2重量部と、溶剤としてN−メチル−ピロリドン44重量部とを、プラネタリディスパで混合分散することにより、活物質層用塗工組成物の調製を行った。一面あたりの塗工量は約250g/m2とし、厚さ15μmのアルミ箔の一面側にダイコートを用いて活物質層用塗工組成物を塗工した。その後、乾燥し、ロールプレスにより圧延し、電極板を得た。評価結果を表1に示す。
Example 1 Production of Electrode Plate for Nonaqueous Electrolyte Secondary Battery
100 parts by weight of LiCoO 2 powder as the positive electrode active material, 2 parts by weight of SuperP made by MMMCarbon as the conductive material, 2 parts by weight of polyvinylidene fluoride as the binder, and 44 parts by weight of N-methyl-pyrrolidone as the solvent Was mixed and dispersed in a planetary dispa to prepare a coating composition for an active material layer. The coating amount per side was about 250 g / m 2, and the active material layer coating composition was applied to one side of an aluminum foil having a thickness of 15 μm using a die coat. Then, it dried and rolled with the roll press, and the electrode plate was obtained. The evaluation results are shown in Table 1.
(実施例2〜4、比較例1〜3)
表1に示した配合により、実施例1と同様に活物質層用塗工組成物の調製を行い、実施例1と同様に塗工し、乾燥し、圧延して電極板を得た。評価結果を表1に示す。
(Examples 2-4, Comparative Examples 1-3)
With the formulation shown in Table 1, a coating composition for active material layer was prepared in the same manner as in Example 1, and coated in the same manner as in Example 1, dried and rolled to obtain an electrode plate. The evaluation results are shown in Table 1.
(評価)
(1)活物質層用塗工組成物の保存後体積抵抗率
活物質層用塗工組成物を調製後25℃で7日静置した後、100μmのPETフィルム上の一面側に活物質層塗工組成物を乾燥後の塗膜が100μmとなるように塗布、乾燥し、得られた塗膜について、抵抗率計(例えば、三菱化学製、ロレスタ−EP)を用いて四端子四探針法にて測定し、調製後25℃で7日静置した後の活物質層用塗工組成物の体積抵抗率により保存安定性を評価した。調製後25℃で7日静置した後の体積抵抗率が150Ω・cm以下であったものは○、150Ω・cmより大きいものは×とした。
(Evaluation)
(1) Volume resistivity after storage of coating composition for active material layer After preparing the coating composition for active material layer and leaving it at 25 ° C. for 7 days, the active material layer is formed on one side of a 100 μm PET film. The coating composition was applied and dried so that the coating film after drying was 100 μm, and the obtained coating film was subjected to a four-terminal four-probe using a resistivity meter (for example, Loresta-EP, manufactured by Mitsubishi Chemical Corporation). The storage stability was evaluated based on the volume resistivity of the coating composition for active material layer after measurement and after standing at 25 ° C. for 7 days after preparation. A sample having a volume resistivity of 150 Ω · cm or less after standing at 25 ° C. for 7 days after the preparation was indicated as “◯”, and a sample having a volume resistivity greater than 150 Ω · cm as “X”.
(2)活物質層の体積抵抗率の測定
100μmのPETフィルム上の一面側に活物質層塗工組成物を乾燥後の塗膜が100μmとなるように塗布、乾燥し、得られた塗膜について、抵抗率計(例えば、三菱化学製、ロレスタ−EP)を用いて四端子四探針法にて測定した。
(2) Measurement of volume resistivity of active material layer The coated film obtained by applying and drying the active material layer coating composition on one side of a 100 μm PET film so that the coated film after drying becomes 100 μm. Was measured by a four-terminal four-probe method using a resistivity meter (for example, Loresta-EP, manufactured by Mitsubishi Chemical Corporation).
本発明に係る活物質層用塗工組成物が調製された実施例1〜4では、調製後25℃で7日静置した後の体積抵抗率が150Ω・cm以下であり、保存安定性が良かった。また、本発明に係る活物質層用塗工組成物を用いて作製された本発明に係る電極板である実施例1〜4は、フタル酸ジブチルの吸油量が250ml/100g以上で且つBET比表面積が50〜150m2/gであるカーボンブラックを全導電材中に50重量%以上含有する活物質層を設けてなるため、活物質100重量部に対して導電材を2重量部以下と少量含有する活物質層でありながら、活物質層の体積抵抗率が150Ω・cmより低く、且つ、高い電池容量を実現した。一方、比較例では、活物質層用塗工組成物は、調製後25℃で7日静置した後の体積抵抗率が150Ω・cm以下より大きくなり、保存安定性が悪かった。また、比較例の電極板は、活物質100重量部に対して導電材を2重量部以下含有するため高い電池容量は実現するものの、活物質層の体積抵抗率が150Ω・cmより大きく、サイクル特性の悪化や内部抵抗の上昇といった電池性能を悪化させるものであった。
In Examples 1 to 4 in which the coating composition for active material layer according to the present invention was prepared, the volume resistivity after standing at 25 ° C. for 7 days after preparation was 150 Ω · cm or less, and the storage stability was high. Was good. Moreover, Examples 1-4 which are the electrode plates which concern on this invention produced using the coating composition for active material layers which concerns on this invention are oil absorption amount of dibutyl phthalate 250 ml / 100g or more, and BET ratio Since an active material layer containing 50% by weight or more of carbon black having a surface area of 50 to 150 m 2 / g is provided in the entire conductive material, the conductive material is less than 2 parts by weight with respect to 100 parts by weight of the active material. Although the active material layer was contained, the volume resistivity of the active material layer was lower than 150 Ω · cm, and a high battery capacity was realized. On the other hand, in the comparative example, the coating composition for an active material layer had a volume resistivity of less than 150 Ω · cm after standing for 7 days at 25 ° C. after preparation and poor storage stability. Further, the electrode plate of the comparative example contains 2 parts by weight or less of a conductive material with respect to 100 parts by weight of the active material, so that a high battery capacity is realized, but the volume resistivity of the active material layer is larger than 150 Ω · cm, Battery performance such as deterioration of characteristics and increase of internal resistance was deteriorated.
Claims (6)
A nonaqueous electrolyte secondary battery comprising the electrode plate for a nonaqueous electrolyte secondary battery according to claim 3.