JP2005239575A - Cosmetic composition containing polyamide porous particle and used for skin and hair - Google Patents
Cosmetic composition containing polyamide porous particle and used for skin and hair Download PDFInfo
- Publication number
- JP2005239575A JP2005239575A JP2004048108A JP2004048108A JP2005239575A JP 2005239575 A JP2005239575 A JP 2005239575A JP 2004048108 A JP2004048108 A JP 2004048108A JP 2004048108 A JP2004048108 A JP 2004048108A JP 2005239575 A JP2005239575 A JP 2005239575A
- Authority
- JP
- Japan
- Prior art keywords
- cosmetic composition
- polyamide
- particles
- porous particles
- hair
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
本発明は、狭い粒子径分布あるいは粒子長分布をもち、さらに特定の比表面積を有し、球状、筒状又はダンベル状のポリアミド多孔質粒子を含有する皮膚用及び毛髪用の化粧料組成物に関するものである。 The present invention relates to a cosmetic composition for skin and hair, which has a narrow particle size distribution or particle length distribution, further has a specific surface area, and contains spherical, cylindrical or dumbbell-shaped polyamide porous particles. Is.
特許文献１には、数平均粒子径１〜３０μｍ、粒子径分布が１〜１．５であり、ＢＥＴ比表面積０．１〜８０ｍ２／ｇであるポリアミド多孔質粒子及びその製造方法が開示されている。
特許文献２は、ポリアミド多孔質粒子を含有するスキンクレンジングマスク化粧品組成物が開示されている。
Patent Document 2 discloses a skin cleansing mask cosmetic composition containing polyamide porous particles.
皮膚表面、又は毛髪に塗ると非常に伸ばしやすく、てからない化粧品組成物を提供することを目的とする。 An object of the present invention is to provide an unprecedented cosmetic composition that is very easy to stretch when applied to the skin surface or hair.
本発明は、化粧品組成物に添加するポリアミド多孔質粒子として、粒径あるいは粒子長分布の狭い多孔質であって比表面積の大きい、さらに吸油性の大きい、球状、または筒状もしくはダンベル状のポリアミド多孔質粒子を化粧品組成物の中でも、特にクレンジング剤、ローション、化粧水、乳液、眼の周縁用（着色、非着色ケア−）クリーム、洗顔料、入浴剤、石鹸などスキンケア用途に含有させることで、皮膚表面での優れた吸油特性を有すること及びスクラブ剤としてのスキンクレンジング効果、及びあらかじめ脂質や水分、保湿性剤および栄養分などを包括させておいた粒子細孔から成分を除包させることによる保湿効果や栄養分補給効果、及び皮膚の滑らかさや化粧伸びの良さが増す効果を有することを見出した。 The present invention relates to a polyamide porous particle to be added to a cosmetic composition, a porous material having a narrow particle size or particle length distribution, a large specific surface area, a large oil absorption, a spherical shape, or a cylindrical or dumbbell-shaped polyamide. By including porous particles in cosmetic compositions, especially for skin care applications such as cleansing agents, lotions, lotions, milky lotions, creams for the edges of the eyes (colored and non-colored care), face wash, bath additives, soaps, etc. By having excellent oil-absorbing properties on the skin surface and skin cleansing effect as a scrub agent, and by decapsulating components from particle pores that have been pre-packaged with lipids, moisture, moisturizing agents, nutrients, etc. It has been found that it has a moisturizing effect, a nutrient replenishing effect, and an effect of increasing the smoothness of the skin and the goodness of makeup elongation.
また、本発明のポリアミド多孔質粒子を毛髪用化粧品組成物（シャンプー、ヘアコンディショナー、パーマ剤、ヘアクリーム、ヘアワックス、ヘアジェル）に含有させることにより、スクラブ機能による洗髪時の汚れの除去（クレンジング効果）及び、あらかじめ栄養分や水分、保湿性剤を包括させておいた粒子から成分を除包させることによって洗い流した後や乾燥後に毛髪のすべり感、しなやかさ、つやの向上及びその効果の持続が保たれることを見出した。 In addition, by incorporating the porous polyamide particles of the present invention into a cosmetic composition for hair (shampoo, hair conditioner, permanent agent, hair cream, hair wax, hair gel), removal of dirt during hair washing by the scrub function (cleansing effect) ) And after removing the ingredients from the particles that have been pre-packaged with nutrients, moisture and moisturizer, the hair feels slippery, supple, glossy and continues to be effective after drying. I found out.
本発明は、ポリアミド多孔質粒子を含む皮膚用及び毛髪用の化粧品組成物であり、該ポリアミド多孔質粒子が、下記に示す特性（Ａ）［Ａ１からＡ６］及び／又は（Ｂ）［Ｂ１からＢ６］を有する多孔質粒子であることを特徴とする化粧品組成物を提供することである。
・ポリアミド多孔質粒子の特性（Ａ）：
（Ａ１）ＢＥＴ比表面積が、５ｍ２／ｇ以上、
（Ａ２）煮あまに油吸油量が、２００ｍＬ／１００ｇ以上、
（Ａ３）ＤＳＣによる結晶化度が、４０％以上、
（Ａ４）数平均粒子径が、１〜３０μｍの範囲、
（Ａ５）粒度分布指数（ＰＤＩ）が、１．０〜１．５の範囲、
（Ａ６）形状が、球状の粒子。
・ポリアミド多孔質粒子の特性（Ｂ）：
（Ｂ１）ＢＥＴ比表面積が、５ｍ２／ｇ以上、
（Ｂ２）煮あまに油吸油量が、２００ｍＬ／１００ｇ以上、
（Ｂ３）ＤＳＣによる結晶化度が、４０％以上、
（Ｂ４）数平均粒子長が、０．５〜２５μｍの範囲、
（Ｂ５）粒子径に対する粒子長の比が、３〜５０の範囲、
（Ｂ６）形状が、筒状及びダンベル状から選ばれる粒子。
The present invention is a cosmetic composition for skin and hair containing polyamide porous particles, wherein the polyamide porous particles have the following characteristics (A) [A1 to A6] and / or (B) [B1 B6] is a porous particle, and a cosmetic composition is provided.
-Characteristics of polyamide porous particles (A):
(A1) BET specific surface area is 5 m 2 / g or more,
(A2) Oil absorption in boiled sea bream is 200 mL / 100 g or more,
(A3) Crystallinity by DSC is 40% or more,
(A4) Number average particle diameter is in the range of 1 to 30 μm,
(A5) Particle size distribution index (PDI) is in the range of 1.0 to 1.5,
(A6) Particles having a spherical shape.
-Properties of polyamide porous particles (B):
(B1) BET specific surface area is 5 m 2 / g or more,
(B2) Oil absorption in boiled sea bream is 200 mL / 100 g or more,
(B3) Crystallinity by DSC is 40% or more,
(B4) Number average particle length is in the range of 0.5 to 25 μm,
(B5) The ratio of the particle length to the particle diameter is in the range of 3-50,
(B6) Particles whose shape is selected from a cylindrical shape and a dumbbell shape.
本発明の化粧品組成物の好ましい態様を示す。
ポリアミド多孔質粒子の特性（Ａ１）及び／又は（Ｂ１）のＢＥＴ比表面積が、８ｍ２／ｇ以上であることが好ましい。
ポリアミド多孔質粒子の特性（Ａ２）及び／又は（Ｂ２）の煮あまに油吸油量が、２４０ｍＬ／１００ｇ以上、特に２５０ｍＬ／１００ｇ以上であることが好ましい。
ポリアミド多孔質粒子の特性（Ａ３）及び／又は（Ｂ３）の結晶化度が、４５％以上、さらに５０％以上であることが好ましい。
ポリアミド多孔質粒子の特性（Ａ５）の粒度分布指数（ＰＤＩ）が、１．０〜１．３の範囲であることが好ましい。
本発明の化粧品組成物は、水溶性媒体、さらに必要に応じて無機充填材、ゲル化剤、脂肪酸、エマルジョン、シリコーンオイル、有機添加物などを含むことが好ましい。
本発明の化粧品組成物は、油性媒体を含むことが好ましい。
本発明の化粧品組成物は、クレンジング剤、ローション、化粧水、乳液、眼の周縁用（着色、非着色ケア−）クリーム、洗顔料、入浴剤、石鹸などの皮膚用と、シャンプー、ヘアコンディショナー、パーマ剤、ヘアクリーム、ヘアワックス、ヘアジェルなどの毛髪用の化粧品組成物であることが好ましい。
The preferable aspect of the cosmetic composition of this invention is shown.
It is preferable that the BET specific surface area of the characteristic (A1) and / or (B1) of the polyamide porous particles is 8 m 2 / g or more.
It is preferable that the oil absorption amount is 240 mL / 100 g or more, particularly 250 mL / 100 g or more in the boiled sesame of the characteristics (A2) and / or (B2) of the polyamide porous particles.
The crystallinity of the characteristics (A3) and / or (B3) of the polyamide porous particles is preferably 45% or more, and more preferably 50% or more.
It is preferable that the particle size distribution index (PDI) of the characteristic (A5) of the polyamide porous particles is in the range of 1.0 to 1.3.
The cosmetic composition of the present invention preferably contains a water-soluble medium and, if necessary, an inorganic filler, a gelling agent, a fatty acid, an emulsion, a silicone oil, an organic additive, and the like.
The cosmetic composition of the present invention preferably contains an oily medium.
The cosmetic composition of the present invention is a cleansing agent, lotion, lotion, milky lotion, skin for eyes (colored and non-colored care), face wash, bath preparation, soap, shampoo, hair conditioner, It is preferably a cosmetic composition for hair such as a permanent agent, a hair cream, a hair wax, or a hair gel.
本発明のポリアミド多孔質粒子を含む化粧品組成物を人間の皮膚に適用すると、皮膚表面での優れた吸油特性を有すること及びスクラブ剤としてのスキンクレンジング効果、及びあらかじめ脂質や水分、保湿性剤、栄養分などを包括させておいた粒子細孔から成分を除包させることによる保湿効果や栄養分補給効果、及び皮膚の滑らかさや化粧伸びの良さが増す効果を同時に満たすことができる。
また本発明のポリアミド多孔質粒子を含む化粧品組成物を毛髪に適用すると、スクラブ機能による洗髪時の汚れの除去（クレンジング効果）及び、あらかじめ栄養分や水分、保湿性剤を包括させておいた粒子から成分を除包させることによって洗い流した後や乾燥後に毛髪のすべり感、しなやかさ、つやの向上及びその効果の持続が保たれる。
When the cosmetic composition containing the polyamide porous particles of the present invention is applied to human skin, it has excellent oil absorption properties on the skin surface, a skin cleansing effect as a scrub agent, and a lipid, moisture, moisturizing agent in advance. It is possible to simultaneously satisfy the moisturizing effect and nutrient replenishment effect by decapsulating the components from the particle pores containing the nutrients and the like, and the effect of increasing the smoothness of the skin and the goodness of the makeup.
In addition, when the cosmetic composition containing the porous polyamide particles of the present invention is applied to hair, it removes dirt (cleansing effect) at the time of washing with the scrub function, and from the particles preliminarily containing nutrients, moisture and moisturizing agents. By removing the ingredients, the hair slipperiness, suppleness and glossiness are improved and the effect is maintained after washing or drying.
本発明は、ポリアミド多孔質粒子の多孔質構造及び凸凹構造を用いて皮膚から分泌する皮脂や汗成分をすばやく吸収し、同時に粒子のスクラブ機能により皮膚表面から取り除くクレンジング効果の高い化粧品組成物、及びあらかじめ粒子細孔部に脂質や水分、栄養分などを包括させておいた状態から成分を除包させることによる保湿効果などのスキンケア効果の高い化粧品組成物の改良を提供する。 The present invention is a cosmetic composition having a high cleansing effect that quickly absorbs sebum and sweat components secreted from the skin using the porous structure and uneven structure of the polyamide porous particles, and simultaneously removes it from the skin surface by the scrubbing function of the particles, and Provided is an improvement in a cosmetic composition having a high skin care effect such as a moisturizing effect by decapsulating ingredients from a state in which lipids, moisture, nutrients and the like are preliminarily included in the pores of the particles.
さらに、毛髪についてコンディショナーや栄養分や水分を除包させることで、スクラブ機能と共に洗髪時の効果的な汚れの除去や洗髪後及び乾燥後の毛髪のすべり感、しなやかさ、つやの向上及びその効果の持続が保たれる化粧品組成物の改良を提供する。 Furthermore, by removing the conditioner, nutrients and moisture from the hair, the scrubbing function effectively removes dirt during washing, improves the slipperiness, suppleness and gloss of the hair after washing and drying, and sustains the effect. An improvement in a cosmetic composition is provided.
本発明の化粧品組成物は、一成分としてポリアミド多孔質粒子を含み、その構成成分や目的により、皮膚、唇、頭皮、礎毛、眼、爪又は髪などに適用することができる。代表的な化粧品組成物としては、ペースト状あるいは粉状のもの、またエマルジョン液体として肌に塗布しやすいものなどの形態のものを挙げることができる。 The cosmetic composition of the present invention contains polyamide porous particles as one component, and can be applied to the skin, lips, scalp, foundation hair, eyes, nails, hair, and the like depending on the component and purpose. Typical cosmetic compositions include those in the form of a paste or powder and those that are easily applied to the skin as an emulsion liquid.
本発明の化粧品組成物は、ポリアミド多孔質粒子１〜６０重量％及び油溶性媒体０．１〜５０重量％を含有していることが好ましく、特にポリアミド多孔質粒子３〜４０重量％及び油溶性媒体１〜３０重量％を含有していることが好ましい。
本発明の化粧品組成物は、クレンジング用途に用いる場合、ポリアミド多孔質粒子１〜３５重量％を含有し、特にポリアミド多孔質粒子１０〜２０重量％を含有することが好ましい。
The cosmetic composition of the present invention preferably contains 1 to 60% by weight of porous polyamide particles and 0.1 to 50% by weight of an oil-soluble medium, particularly 3 to 40% by weight of porous polyamide particles and oil-soluble. It is preferable to contain 1 to 30% by weight of the medium.
When used in cleansing applications, the cosmetic composition of the present invention contains 1 to 35% by weight of polyamide porous particles, and preferably 10 to 20% by weight of polyamide porous particles.
本発明の化粧品組成物は、ポリアミド多孔質粒子１〜６０重量％及び液体媒体を１〜９９％重量部含むものであることが好ましく、特にポリアミド多孔質粒子３〜４０重量％及び１０〜９７重量％を含有していることが好ましい。
液体媒体としては、水溶成分、油性あるいはラッテックスのものが望ましく、油性成分であれば揮発性あるいは不揮発性シリコーンオイル、流動パラフィン、植物性油、ワックス、グリセリン、エチレングリコールなどを挙げることが出来る。
The cosmetic composition of the present invention preferably contains 1 to 60% by weight of polyamide porous particles and 1 to 99% by weight of a liquid medium, particularly 3 to 40% by weight and 10 to 97% by weight of porous polyamide particles. It is preferable to contain.
The liquid medium is preferably a water-soluble component, oily or latex, and examples of the oily component include volatile or nonvolatile silicone oil, liquid paraffin, vegetable oil, wax, glycerin, and ethylene glycol.
クレンジング用の化粧品組成物は、特に皮膚表層の角質層の死んだ細胞を除去し、過剰に存在する脂肪成分（皮脂）を除去することによって皮膚の深層まで清潔にし、皮膚を引き締め、皮膚を柔軟にする効果を示す。
また、特に毛髪用としても、毛髪表面の汚れを除去することで毛髪を清潔に保つ効果を有する。
また粒子のスクラブ機能により角質を取り除く作用も同時に有する。スクラブ機能を有する粒子サイズは一次粒子のサイズのみならず、顆粒などの二次凝集体により１０μｍ〜２００μｍまで効果を示す。
The cleansing cosmetic composition removes dead cells from the stratum corneum, especially the skin surface layer, cleans the skin deeper by removing excess fat components (sebum), tightens the skin and softens the skin Shows the effect.
Moreover, especially for hair, it has the effect of keeping the hair clean by removing dirt on the hair surface.
It also has the effect of removing the keratin by the particle scrubbing function. The particle size having the scrub function is effective not only from the size of the primary particles but also from 10 μm to 200 μm due to secondary aggregates such as granules.
皮膚や毛髪に対する保湿効果や栄養補給効果及びすべり感、しなやかさ、つやの向上などの効果の高い化粧品組成物は、皮膚及び毛髪に対して、多孔質粒子細孔部にあらかじめ包括させておいた脂質や水分、保湿性剤、栄養分などを徐包させることにより、効果の持続が保たれる。 Cosmetic compositions with high effects such as moisturizing effect, nutritional supplementation effect, slipperiness, suppleness, and gloss improvement for skin and hair are the lipids previously incorporated in the pores of porous particles for skin and hair. Sustained effects can be maintained by gradually wrapping water, moisture, moisturizing agents and nutrients.
保湿性剤としてはグリセロール、プロピレングリコール、ジプロピレングリコール、１，３ジブチレングリコール、ポリグリセロール、ソルビトール、グルコース、スクコース、ポリエチレングリコール、メチルグルセス、マルチトール、マンニトール、マグネシウムグルコナート、ヘキシレングリコールあるいは水溶性のシリコーンを含有する酸を用いることができる。 As humectants, glycerol, propylene glycol, dipropylene glycol, 1,3 dibutylene glycol, polyglycerol, sorbitol, glucose, sucrose, polyethylene glycol, methylgluces, maltitol, mannitol, magnesium gluconate, hexylene glycol or water-soluble An acid containing a functional silicone can be used.
脂質及び栄養分としては、セラミド、コラーゲン、ビタミンＡ類、ビタミンＣ類、ビタミンＥ類及びビタミン誘導体、各種アミノ酸があげられる。
本化粧品組成物は、クリーム状、水溶液、エマルジョン、ジェルなどの形態からなる。
Examples of lipids and nutrients include ceramide, collagen, vitamins A, vitamins C, vitamins E, vitamin derivatives, and various amino acids.
The cosmetic composition is in the form of cream, aqueous solution, emulsion, gel or the like.
化粧品組成物は、ポリアミド多孔質粒子及び水溶性媒体、さらに必要に応じて無機充填材、ゲル化剤、脂肪酸、エマルジョン、シリコーンオイル、有機添加物などを含むことが出来る。 The cosmetic composition can contain polyamide porous particles and a water-soluble medium, and further, if necessary, an inorganic filler, a gelling agent, a fatty acid, an emulsion, a silicone oil, an organic additive, and the like.
水溶性媒体には、上記保湿性剤成分のほかに香料、ＢＡＳＦ社のＣＲＥＭＯＰＨＯＲ Ｒ４６０のような香料可溶剤または素練り促進剤、着色剤および、水、エタノールなどの各種アルコールなどを含むことが出来る。 In addition to the moisturizing agent component, the water-soluble medium can contain a fragrance, a fragrance solubilizing agent such as CREMOPHOR R460 manufactured by BASF or a peptizer, a coloring agent, and various alcohols such as water and ethanol. .
無機充填材には、チタン、シリカ、タルク、カオリン、マイカ、珪、藻土などがある。 Inorganic fillers include titanium, silica, talc, kaolin, mica, silica, algae and the like.
ゲル化剤として、不飽和カルボン酸ポリマーまたはコポリマー、不飽和エステルのポリマーまたはコポリマー、多糖類の誘導体、ゴム、コロイド性のケイ酸塩、ポリエチレングリコール及びその誘導体、ポリビニルピロリドン及びその誘導体、親水性のシリカゲルが用いられる。 As gelling agents, unsaturated carboxylic acid polymers or copolymers, unsaturated ester polymers or copolymers, polysaccharide derivatives, rubber, colloidal silicates, polyethylene glycol and its derivatives, polyvinylpyrrolidone and its derivatives, hydrophilic Silica gel is used.
脂肪酸としては、飽和脂肪酸と不飽和脂肪酸及びそれらの誘導体とを用いることが出来、例えば、カプリル酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸など、及びそれらの混合物などを挙げることが出来る。
不飽和脂肪酸としては、パルミトール酸、ミリストオレイン酸、オレイン酸など及びそれらの混合物、リノール酸・リノレイン酸、エルカ酸などのポリ不飽和脂肪酸などを挙げることが出来る。脂肪酸の誘導体は、ヒドロキシ化、エステル化されたものを用いることができる。
As the fatty acid, saturated fatty acid, unsaturated fatty acid and derivatives thereof can be used, and examples thereof include caprylic acid, lauric acid, myristic acid, palmitic acid, stearic acid, and a mixture thereof.
Examples of the unsaturated fatty acid include palmitolic acid, myristoleic acid, oleic acid, and mixtures thereof, and polyunsaturated fatty acids such as linoleic acid / linolenic acid and erucic acid. As the fatty acid derivative, a hydroxylated or esterified derivative can be used.
エマルジョンとしては、油中水型が好ましい。油相はシリコーンオイル、鉱物油、植物油、蜜蝋、油脂、ワックスなどの非シリコーン有機油またはそれらの混合物を用いることができる。 The emulsion is preferably a water-in-oil type. As the oil phase, non-silicone organic oils such as silicone oil, mineral oil, vegetable oil, beeswax, fats and oils, and waxes, or mixtures thereof can be used.
シリコーンオイルには、揮発性シリコーンオイル、不揮発性シリコーンオイルなどがある。 Silicone oil includes volatile silicone oil and non-volatile silicone oil.
有機添加物は、アミノ酸、尿素などの湿潤剤、香料、色素、防腐剤、界面活性剤などがある。 Organic additives include wetting agents such as amino acids and urea, fragrances, pigments, preservatives, surfactants and the like.
油溶性媒体としては、パラフィン、ポリエチレンワヅクス、流動パラフィン、カルナバワックス、植物油、蜜蝋、シリコーンオイル、脂肪族アルコールなどがある。 Examples of the oil-soluble medium include paraffin, polyethylene wax, liquid paraffin, carnauba wax, vegetable oil, beeswax, silicone oil, and aliphatic alcohol.
界面活性剤は、陰イオン性界面活性剤、陽イオン性界面活性剤、非イオン性界面活性剤などがある。
陰イオン性界面活性剤としては、ラウリン酸ナトリウム、パルミチン酸ナトリウムなどの脂肪酸石鹸のほか、高級アルキル硝酸エステル塩、アルキルエーテル硫酸エステル塩、高級脂肪酸アミドスルホン酸塩、リン酸エステル塩などが上げられる。
陽イオン性界面活性剤としては、塩化アルキルトリメチルアンモニウム、塩化ジアルキルジメチルアンモニウムなどが用いられる。
非イオン性界面活性剤としては、（ポリ）グリセリン脂肪酸エステル、ソルビタン脂肪酸エステル、蔗糖脂肪酸エステル、ポリオキシアルキレン（炭素数２又は３）アルキルエーテル、ポリオキシエチレン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、ポリオキシエチレングリセリン脂肪酸エステル、ポリオキシエチレン硬化ひまし油、ポリオキシエチレン硬化ひまし油脂肪酸エステル、ポリオキシエチレン・ポリオキシプロピレンブロック共重合体などが挙げられる。
Examples of the surfactant include an anionic surfactant, a cationic surfactant, and a nonionic surfactant.
Examples of anionic surfactants include fatty acid soaps such as sodium laurate and sodium palmitate, as well as higher alkyl nitrates, alkyl ether sulfates, higher fatty acid amide sulfonates, and phosphate esters. .
As the cationic surfactant, alkyltrimethylammonium chloride, dialkyldimethylammonium chloride and the like are used.
Nonionic surfactants include (poly) glycerin fatty acid ester, sorbitan fatty acid ester, sucrose fatty acid ester, polyoxyalkylene (carbon number 2 or 3) alkyl ether, polyoxyethylene fatty acid ester, polyoxyethylene sorbitan fatty acid ester, Examples include polyoxyethylene glycerin fatty acid ester, polyoxyethylene hydrogenated castor oil, polyoxyethylene hydrogenated castor oil fatty acid ester, and polyoxyethylene / polyoxypropylene block copolymer.
本発明の化粧品組成物は、必要に応じて無機顔料、分散剤、防腐剤、酸化防止剤、コンディショナーなどを適当量添加することができる。 The cosmetic composition of the present invention may contain an appropriate amount of an inorganic pigment, a dispersant, a preservative, an antioxidant, a conditioner or the like, if necessary.
分散剤としては、ヘキサメタリン酸ナトリウム、ピロリン酸ナトリウム、有機酸、ポリビニルピロリドン、ポリビニルアルコール、メチルビニルエーテル／無水マレイン酸架橋コポリマーなどが挙げられる。 Examples of the dispersant include sodium hexametaphosphate, sodium pyrophosphate, organic acid, polyvinyl pyrrolidone, polyvinyl alcohol, and methyl vinyl ether / maleic anhydride crosslinked copolymer.
コンディショナーとしては、ジメチコーン、ジメチコーンコポリオール、アミノジメチコーン及びそれらの混合物、またポリクアテルニウム−１０、ポリクアテルニウム−７、グアヒドロキシプロピルトリアンモニウムクロリドなどの重合体コンディショナー及びこれらの混合物から選択することができる。 Conditioners include dimethicone, dimethicone copolyol, aminodimethicone and mixtures thereof, and polymer conditioners such as polyquaternium-10, polyquaternium-7, guahydroxypropyltriammonium chloride and mixtures thereof. You can choose.
本発明の化粧品組成物は、ポリアミド多孔質粒子の他の成分しては、水溶性媒体、各種脂肪酸、脂肪族アルコール、蜜蝋などのワックスとそれらの誘導体などの合成油及び油脂、各種の植物油たとえば椿油などの天然油及び油脂などといった油性媒体、水性媒体、各種のエマルジョン媒体などを添加することができる。 The cosmetic composition of the present invention includes, as other components of the polyamide porous particles, synthetic oils and fats such as water-soluble media, waxes such as various fatty acids, fatty alcohols and beeswax and their derivatives, and various vegetable oils such as An oily medium such as natural oil such as camellia oil and fat, an aqueous medium, various emulsion media, and the like can be added.
化粧品組成物には、つや消し効果や艶出し効果、汗取り効果、その他剥離防止効果などとして、タルク、粘土などの無機物粉体、塩化ナトリウムなどの無機塩、有機粉末、繊維状粉末などが配合されていてもよい。 Cosmetic compositions are formulated with frost, gloss, sweat removal and other anti-peeling effects such as inorganic powders such as talc and clay, inorganic salts such as sodium chloride, organic powders and fibrous powders. May be.
化粧品組成物は、脂肪性肌を処理するための活性剤を含んでもよい。
活性剤としては、例えば、β−ラクタム誘導体、シプロフロキサシン、ノルマルフロキサシン、テトラサイクリン及びその塩、エリスロマイシン及びその塩など、及び植物からの抽出物などを含んでいてもよい。
The cosmetic composition may include an active agent for treating fatty skin.
Examples of the active agent may include a β-lactam derivative, ciprofloxacin, normalfloxacin, tetracycline and a salt thereof, erythromycin and a salt thereof, and an extract from a plant.
ポリアミド多孔質粒子は、下記に示す特性（Ａ）［Ａ１からＡ６］及び／又は（Ｂ）［Ｂ１からＢ６］を有する多孔質粒子を用いることが出来る。
・ポリアミド多孔質粒子の特性（Ａ）：
（Ａ１）ＢＥＴ比表面積が、５ｍ２／ｇ以上、
（Ａ２）煮あまに油吸油量が、２００ｍＬ／１００ｇ以上、
（Ａ３）ＤＳＣによる結晶化度が、４０％以上、
（Ａ４）数平均粒子径が、１〜３０μｍの範囲、
（Ａ５）粒度分布指数（ＰＤＩ）が、１．０〜１．５の範囲、
（Ａ６）形状が、球状の粒子。
・ポリアミド多孔質粒子の特性（Ｂ）：
（Ｂ１）ＢＥＴ比表面積が、５ｍ２／ｇ以上、
（Ｂ２）煮あまに油吸油量が、２００ｍＬ／１００ｇ以上、
（Ｂ３）ＤＳＣによる結晶化度が、４０％以上、
（Ｂ４）数平均粒子長が、０．５〜２５μｍの範囲、
（Ｂ５）粒子径に対する粒子長の比が、３〜５０の範囲、
（Ｂ６）形状が、筒状及びダンベル状から選ばれる粒子。
As the polyamide porous particles, porous particles having the following characteristics (A) [A1 to A6] and / or (B) [B1 to B6] can be used.
-Characteristics of polyamide porous particles (A):
(A1) BET specific surface area is 5 m 2 / g or more,
(A2) Oil absorption in boiled sea bream is 200 mL / 100 g or more,
(A3) Crystallinity by DSC is 40% or more,
(A4) Number average particle diameter is in the range of 1 to 30 μm,
(A5) Particle size distribution index (PDI) is in the range of 1.0 to 1.5,
(A6) Particles having a spherical shape.
-Properties of polyamide porous particles (B):
(B1) BET specific surface area is 5 m 2 / g or more,
(B2) Oil absorption in boiled sea bream is 200 mL / 100 g or more,
(B3) Crystallinity by DSC is 40% or more,
(B4) Number average particle length is in the range of 0.5 to 25 μm,
(B5) The ratio of the particle length to the particle diameter is in the range of 3-50,
(B6) Particles whose shape is selected from a cylindrical shape and a dumbbell shape.
ポリアミド多孔質粒子は、上記に示す特性（Ａ）［Ａ１からＡ６］及び／又は（Ｂ）［Ｂ１からＢ６］を有する多孔質粒子を、ポリアミド多孔質粒子中、好ましくは７０〜１００質量％、さらに好ましくは８０〜１００質量％、より好ましくは９０〜１００質量％、特に好ましくは９５〜１００質量％含むことが好ましい。
ポリアミド多孔質粒子は、上記に示す特性（Ａ）［Ａ１からＡ６］を有する多孔質粒子及び（Ｂ）［Ｂ１からＢ６］を有する多孔質粒子を、単独で用いてもよく、またこれらを混合して用いてもよい。ポリアミド多孔質粒子において、上記に示す特性（Ａ）［Ａ１からＡ６］を有する多孔質粒子及び（Ｂ）［Ｂ１からＢ６］を有する多孔質粒子を混合して用いる場合、特性Ａの多孔質粒子と特性Ｂの多孔質粒子の混合割合は、目的に応じて適宜選択して用いることが出来る。
The polyamide porous particles include the porous particles having the characteristics (A) [A1 to A6] and / or (B) [B1 to B6] shown above, preferably 70 to 100% by mass in the polyamide porous particles, More preferably, it is 80-80 mass%, More preferably, it is 90-100 mass%, Most preferably, it is preferable to contain 95-100 mass%.
As the polyamide porous particles, the porous particles having the characteristics (A) [A1 to A6] and the porous particles (B) [B1 to B6] shown above may be used alone or in combination. May be used. When the porous particles having the characteristics (A) [A1 to A6] and the porous particles having (B) [B1 to B6] shown above are mixed and used in the polyamide porous particles, the porous particles having the characteristics A The mixing ratio of the porous particles having the characteristic B can be appropriately selected depending on the purpose.
ポリアミド多孔質粒子は、脂肪族、脂環族及び芳香族のポリアミド、又はこれらの共重合体から製造されるものを用いることができ、特に脂肪族及び／又は脂環族ポリアミドが好ましい。
たとえば、脂肪族ポリアミドとしては、ポリアミド６、ポリアミド６６、ポリアミド８〜１２の単独重合体及びそれらの共重合体である。好ましくは、ポリアミド６、ポリアミド１１、ポリアミド１２の単独重合体及びそれらの共重合体などをあげることができる。
ポリアミド多孔質粒子は、特開２００２−８０６２９号公報に記載の方法またはその他の公知の方法に基づき、製造条件を適宜選択して製造することができる。
As the polyamide porous particles, aliphatic, alicyclic and aromatic polyamides or those produced from copolymers thereof can be used, and aliphatic and / or alicyclic polyamides are particularly preferable.
For example, the aliphatic polyamide is a homopolymer of polyamide 6, polyamide 66, polyamide 8-12, or a copolymer thereof. Preferable examples include homopolymers of polyamide 6, polyamide 11, and polyamide 12, and copolymers thereof.
Polyamide porous particles can be produced by appropriately selecting production conditions based on the method described in JP-A-2002-80629 or other known methods.
ポリアミド多孔質粒子の特性（Ａ１）及び／又は（Ｂ１）のＢＥＴ比表面積は、５ｍ２／ｇ以上、好ましくは８ｍ２／ｇ以上、さらに好ましくは９ｍ２／ｇ以上、特に好ましくは１０ｍ２／ｇ以上であることが好ましい。比表面積が上記範囲より小さいと、あらかじめ包括させた脂質や水分、保湿性剤、栄養分などを速やかに除包させる効果が弱くなる。 BET specific surface area properties of the polyamide porous particles (A1) and / or (B1) is, 5 m 2 / g or more, preferably 8m 2 / g or more, more preferably 9m 2 / g or more, particularly preferably 10 m 2 / It is preferable that it is more than g. When the specific surface area is smaller than the above range, the effect of quickly decapsulating lipids, moisture, moisturizing agents, nutrients and the like included in advance is weakened.
ポリアミド多孔質粒子の特性（Ａ２）及び／又は（Ｂ２）の煮あまに油吸油量は、２００ｍＬ／１００ｇ以上、好ましくは２４０ｍＬ／１００ｇ以上、特に好ましくは２５０ｍＬ／１００ｇ以上であることが好ましい。煮あまに油吸油量が２００ｍＬ／１００ｇ以上あると、余分な皮脂の吸収が速やかで大きく、肌を長時間清潔の保ち、化粧もちがよくなる。さらに、脂質や水分、保湿性剤、栄養分の包括にも非常に有効である。 It is preferable that the oil absorption amount of the polyamide porous particles (A2) and / or (B2) is 200 mL / 100 g or more, preferably 240 mL / 100 g or more, particularly preferably 250 mL / 100 g or more. When the amount of oil absorption is 200 mL / 100 g or more in boiled sesame, the absorption of excess sebum is quick and large, keeping the skin clean for a long time and improving makeup. Furthermore, it is very effective for inclusion of lipids, moisture, moisturizers and nutrients.
ポリアミド多孔質粒子の特性（Ａ３）及び／又は（Ｂ３）の結晶化度は、４０％以上、好ましくは４５％以上、さらに好ましくは５０％以上、特に好ましくは５５％以上であることが好ましい。結晶化度が上記範囲内では、充分な硬度を示し、このため化粧品の製造時や使用時に粒子の変形や崩壊が発生しにくくなり、粒子表面のピラーの強度が強く、クレンジング効果も増す。 The crystallinity of the characteristics (A3) and / or (B3) of the polyamide porous particles is preferably 40% or more, preferably 45% or more, more preferably 50% or more, and particularly preferably 55% or more. When the crystallinity is within the above range, sufficient hardness is exhibited. Therefore, deformation and collapse of the particles are less likely to occur during the production and use of cosmetics, the strength of the pillars on the particle surface is strong, and the cleansing effect is increased.
ポリアミドの結晶化度は、Ｒ．Ｖｉｅｗｅｇら、ｋｕｎｓｔｓｔｏｆｆｅ ＩＶ ｐｏｌｙａｍｉｄｅ、２１８頁、Ｃａｒｌ Ｈａｎｇｅｒ Ｖｅｒｌａｇ、１９６６年の記載を引用し、数式（１）より算出され、ポリアミド６及びポリアミド６６の結晶相の融解熱は、各々４５ｃａｌ／ｇとする。 The crystallinity of the polyamide is Reference is made to the description of Vieweg et al., Kunststoff IV polyamide, page 218, Carl Hanger Verlag, 1966, calculated from Equation (1), and the heat of fusion of the crystalline phases of polyamide 6 and polyamide 66 is 45 cal / g, respectively.
ΔＨobs：ポリアミド多孔質粒子の融解熱（ｃａｌ／ｇ）、
ΔＨｍ：ポリアミドの結晶相の融解熱（ｃａｌ／ｇ）とする。
ΔH obs : heat of fusion of porous polyamide particles (cal / g),
ΔH m : Heat of fusion (cal / g) of the crystal phase of polyamide.
ポリアミド多孔質粒子の数平均粒子径（Ａ４）は、１〜３０μｍの範囲、さらに好ましくは１〜２５μｍ、特に好ましくは２〜２０μｍの範囲である。ポリアミド多孔質粒子の数平均粒子径（Ａ４）が、上記範囲より小さいと、肌の起伏を隠すのに十分ではなく、また、分散性が劣り、肌理にむらがでることがある。
また、ポリアミド多孔質粒子の数平均粒子径の範囲より大きいと、肌理が不均一となり、化粧品組成物として感触が劣るからから好ましくない。
The number average particle diameter (A4) of the polyamide porous particles is in the range of 1 to 30 μm, more preferably 1 to 25 μm, and particularly preferably 2 to 20 μm. When the number average particle diameter (A4) of the polyamide porous particles is smaller than the above range, it is not sufficient to hide the undulations of the skin, and the dispersibility is inferior and the texture may be uneven.
On the other hand, if it is larger than the range of the number average particle diameter of the polyamide porous particles, it is not preferred because the texture becomes non-uniform and the touch is inferior as a cosmetic composition.
ポリアミド球形粒子の粒度分布指数（ＰＤＩ）（Ａ５）は、１．０〜１．５の範囲にあり、好ましくは１．０〜１．３の範囲である。このＰＤＩは、１に近いほど粒子の分散が均一になるため、化粧品組成物に加えた場合に、その製造や使用に際して優れた効果を示す。 The particle size distribution index (PDI) (A5) of the polyamide spherical particles is in the range of 1.0 to 1.5, preferably in the range of 1.0 to 1.3. The closer this PDI is to 1, the more uniform the dispersion of the particles. Therefore, when added to a cosmetic composition, this PDI shows an excellent effect in its production and use.
筒状及びダンベル状から選ばれる多孔質粒子の数平均粒子長（Ｂ４）は、０．５〜２５μｍの範囲、好ましくは２〜２０μｍの範囲、更に好ましくは５〜１５μｍの範囲にある。ポリアミド多孔質粒子の平均粒子長が、上記範囲より小さいと、肌の起伏を隠すのに十分ではなく、また、分散性が劣り、肌理にむらがでることがある。 The number average particle length (B4) of the porous particles selected from a cylindrical shape and a dumbbell shape is in the range of 0.5 to 25 μm, preferably in the range of 2 to 20 μm, and more preferably in the range of 5 to 15 μm. If the average particle length of the polyamide porous particles is smaller than the above range, it is not sufficient to hide the undulations of the skin, and the dispersibility is inferior and the texture may be uneven.
筒状及びダンベル状から選ばれる多孔質粒子の粒子径に対する粒子長の比（Ｂ５）は、３〜１００の範囲、好ましくは４〜５０、さらに好ましくは４〜２０、特に好ましくは４〜１０にある。粒子径に対する粒子長の比が３より小さいと、肌の決めを隠蔽する効果が低くなる。また、１００以上では、ポリアミド多孔質粒子の分散性が悪くなる。 The ratio (B5) of the particle length to the particle diameter of the porous particles selected from a cylindrical shape and a dumbbell shape is in the range of 3 to 100, preferably 4 to 50, more preferably 4 to 20, and particularly preferably 4 to 10. is there. When the ratio of the particle length to the particle diameter is smaller than 3, the effect of concealing the skin decision is reduced. Moreover, when it is 100 or more, the dispersibility of the polyamide porous particles becomes poor.
ポリアミドの筒状及びダンベル状の多孔質粒子において、粒子長は筒状及びダンベル状粒子の両端間の最も直線距離の長い部分の長さであり、粒子径は粒子中央部の径である。だたしダンベル状粒子の場合の粒子径は、最も細い部分の径を意味する。 In the cylindrical and dumbbell-shaped porous particles of polyamide, the particle length is the length of the longest linear distance between both ends of the cylindrical and dumbbell-shaped particles, and the particle diameter is the diameter of the particle center. However, the particle diameter in the case of dumbbell-shaped particles means the diameter of the thinnest part.
ポリアミド多孔質粒子の平均細孔径は、好ましくは０．０１〜０．２μｍであり、さらに好ましくは０．０２〜０．１５μｍである。細孔径が上記範囲内では、成分を包括させる効果又は除包させる効果に優れるために好ましい。 The average pore diameter of the polyamide porous particles is preferably 0.01 to 0.2 μm, more preferably 0.02 to 0.15 μm. When the pore diameter is within the above range, it is preferable because the effect of encapsulating the components or the effect of decapsulating is excellent.
ポリアミド多孔質粒子に残留するポリアミドの溶媒量は、小さいほど安全性に優れると考えられ、溶媒含有量が、好ましくは５０ｐｐｍ以下、さらに好ましくは２０ｐｐｍ以下、特に好ましくは１０ｐｐｍ以下であることが好ましい。 It is considered that the smaller the amount of polyamide solvent remaining in the polyamide porous particles, the better the safety, and the solvent content is preferably 50 ppm or less, more preferably 20 ppm or less, and particularly preferably 10 ppm or less.
ポリアミド多孔質粒子は、上記の特開２００２−８０６２９号公報に記載の方法により、ポリアミド溶液と、ポリアミドの非溶媒及び適度の水を混合し、一時的に透明な均一溶液を作成し、その後ポリマーを析出させることにより製造することができる。ポリアミド溶液は、ポリアミド０．１〜３０重量％と溶媒９９．８〜７０重量％の合計１００重量％、さらに好ましくはポリアミドが０．２〜２５重量％と溶媒９９．８〜７５重量％の合計１００重量％である。 Polyamide porous particles are prepared by mixing a polyamide solution, a non-solvent of polyamide and moderate water by the method described in JP-A-2002-80629, and then temporarily preparing a transparent uniform solution. Can be produced by precipitating. The polyamide solution is a total of 100% by weight of 0.1-30% by weight of polyamide and 99.8-70% by weight of solvent, more preferably a total of 0.2-25% by weight of polyamide and 99.8-75% by weight of solvent. 100% by weight.
ポリアミドの溶媒としては、芳香族アルコール及びギ酸などを挙げることができる。ポリアミド溶液に用いられる芳香族アルコールとしては、ｏ−クレゾール、ｍ−クレゾール、ｐ−クレゾール、クロロフェノール、フェノールなど及びそれらの混合物を用いることができる。 Examples of the polyamide solvent include aromatic alcohol and formic acid. As the aromatic alcohol used in the polyamide solution, o-cresol, m-cresol, p-cresol, chlorophenol, phenol and the like and mixtures thereof can be used.
ポリアミドの非溶媒は、芳香族アルコール及び水が部分的に相容するもの（少量溶解するもの）を用いることができ、一例として脂肪族アルコール、脂肪族ケトンなど及びこれらの混合溶液などを用いることができる。また、ポリアミドの非溶媒は、水と相溶することが重要であり、一例としてメタノール、エタノール、プロパノール、イソプロパノール、アセトン、メチルエチルケトンなどの炭素数１〜４の脂肪族アルコール、炭素数１〜５の脂肪族ケトンなど及びこれらの混合溶液などを用いることができる。 As the non-solvent for polyamide, one that is partially compatible with aromatic alcohol and water (one that dissolves in a small amount) can be used. For example, aliphatic alcohol, aliphatic ketone, and a mixed solution thereof can be used. Can do. In addition, it is important that the non-solvent of the polyamide is compatible with water. As an example, an aliphatic alcohol having 1 to 4 carbon atoms such as methanol, ethanol, propanol, isopropanol, acetone, methyl ethyl ketone, or the like having 1 to 5 carbon atoms. Aliphatic ketones and mixed solutions thereof can be used.
ポリアミド多孔質粒子を製造するにあたり、非溶媒と水とは、非溶媒９８〜１０重量％及び水２〜９０重量％が好ましい。 In producing polyamide porous particles, the non-solvent and water are preferably 98 to 10% by weight of non-solvent and 2 to 90% by weight of water.
ポリアミド多孔質粒子の製造に際して、ポリアミド溶液、非溶媒及び水の添加順序については、ポリアミド溶液、非溶媒及び水を混合し、一時的に溶液が透明で均一に保たれれば良く、特に添加順序などに制限がなく、いかなる順序、方法でも良い。
すなわち、ポリアミド多孔質粒子は、
（１）ポリアミド溶液に、非溶媒を添加し、次に水を加える、
（２）非溶媒と水とを混合し、ポリアミド溶液を加える、
（３）ポリアミド溶液に水を添加し、非溶媒を加えるなどの方法を利用することができる。
具体的に云えば、ポリアミド多孔質粒子は、ポリアミド溶液、非溶媒及び水とを混合し、一時的に溶液が透明で均一な溶液を形成させて、時間的な経過を経て、例えば０．１秒〜１２０分程度の時間経過後、ポリマー粒子を析出させる方法により製造することができる。ポリアミド多孔質粒子の製造に際して、一時的にであっても、均一な溶液を形成することが重要である。
In the production of the polyamide porous particles, the addition order of the polyamide solution, the non-solvent and the water is only required to mix the polyamide solution, the non-solvent and the water so that the solution is temporarily kept transparent and uniform. There are no restrictions on the above, and any order and method may be used.
That is, polyamide porous particles are
(1) Add a non-solvent to the polyamide solution and then add water.
(2) Mix non-solvent and water and add polyamide solution;
(3) A method of adding water to the polyamide solution and adding a non-solvent can be used.
Specifically, the polyamide porous particles are mixed with a polyamide solution, a non-solvent, and water to temporarily form a transparent and uniform solution. It can be produced by a method in which polymer particles are precipitated after a lapse of time of about 2 to 120 minutes. In producing the polyamide porous particles, it is important to form a uniform solution even temporarily.
ポリアミド多孔質粒子の製造において、一時的に溶液が透明で均一な溶液を、早く形成させるために、溶液に適当な攪拌を与えてもよい。
ポリアミド多孔質粒子の製造において、ポリアミド溶液、非溶媒及び水を混合し、一時的に透明で均一な溶液からポリマー粒子を析出させる温度は、５〜７０℃が好ましい。
In the production of the polyamide porous particles, the solution may be appropriately agitated in order to quickly form a transparent and uniform solution.
In the production of the polyamide porous particles, the temperature at which the polyamide solution, the non-solvent and water are mixed and the polymer particles are precipitated from the temporarily transparent and uniform solution is preferably 5 to 70 ° C.
ポリアミド多孔質粒子の製造において、析出したポリアミド多孔質粒子は、溶液からデカンテーション、遠心分離、濾過などの通常の方法で溶液から分離することができ、例えば、ポリアミド多孔質粒子の析出した溶液に、さらにメタノールを加え、デカンテーションや遠心分離などの方法で、ポリアミド多孔質粒子を分離することができる。また、析出したポリアミド多孔質粒子はさらに数回メタノールやアセトンなどで洗浄し、デカンテーションや遠心分離などの方法で分離してもよく、さらに熱風乾燥、真空乾燥にしてもよい。また、超臨界ＣＯ２を用いて分離しても良い。 In the production of the polyamide porous particles, the precipitated polyamide porous particles can be separated from the solution by a usual method such as decantation, centrifugation, and filtration. Further, the polyamide porous particles can be separated by a method such as addition of methanol and decantation or centrifugation. The precipitated polyamide porous particles may be further washed several times with methanol, acetone, or the like, and separated by a method such as decantation or centrifugation, and may be further dried with hot air or vacuum. It may also be separated using supercritical CO 2.
本発明の化粧品組成物は、クレンジング剤、ローション、化粧水、乳液、眼の周縁用（着色、非着色ケア−）クリーム、洗顔料、入浴剤、石鹸などの皮膚用、シャンプー、ヘアコンディショナー、パーマ剤、ヘアクリーム、ヘアワックス、ヘアジェルなどの毛髪用に用いることが出来る。 The cosmetic composition of the present invention is a cleansing agent, lotion, lotion, milky lotion, skin for eyes (colored and non-colored care), facial wash, bath preparation, soap, shampoo, hair conditioner, permanent. It can be used for hair such as agents, hair creams, hair waxes and hair gels.
以下において実施例および比較例を掲げて本発明をさらに詳しく説明するが、本発明の要旨を越えない限り以下の例に限定されるものではない。 In the following, the present invention will be described in more detail with reference to examples and comparative examples. However, the present invention is not limited to the following examples as long as the gist of the present invention is not exceeded.
（粒子の観察）
走査型電子顕微鏡写真（拡大倍率５０００倍）を用いて、写真より粒子２０個を任意で選び、その粒子形状を観察し、粒子長及び粒子径を測定する。粒子長及び粒子径は、２０個の平均値とする。
(Particle observation)
Using a scanning electron micrograph (magnification of 5000 times), 20 particles are arbitrarily selected from the photograph, the particle shape is observed, and the particle length and particle diameter are measured. The particle length and particle diameter are 20 average values.
（数平均粒子径の測定、粒度分布指数（ＰＤＩ）の算出）
ポリアミド多孔質粒子の粒子形状と大きさは、走査型電子顕微鏡（ＳＥＭ）を用いて観察する。球形粒子の粒径は、ＳＥＭ写真より測定し、球形と異なる粒子の粒径は、投影面積から相当円の直径を測定する。
数平均粒子径（Ｄｎ）及び体積平均粒子径（Ｄｖ）は、１００個の粒子径より数式（２）及び数式（３）に従い、算出する。粒度分布指数（ＰＤＩ）は、数式（４）に従い算出する。
(Measurement of number average particle diameter, calculation of particle size distribution index (PDI))
The particle shape and size of the polyamide porous particles are observed using a scanning electron microscope (SEM). The particle size of the spherical particles is measured from the SEM photograph, and the particle size of the particles different from the spherical shape is a diameter of an equivalent circle from the projected area.
The number average particle diameter (Dn) and the volume average particle diameter (Dv) are calculated from 100 particle diameters according to Equation (2) and Equation (3). The particle size distribution index (PDI) is calculated according to Equation (4).
（比表面積の測定）
ポリアミド多孔質粒子の比表面積は、窒素吸着によるＢＥＴ法３点測定で行う。
(Measurement of specific surface area)
The specific surface area of the polyamide porous particles is measured by BET method three-point measurement by nitrogen adsorption.
（細孔径分布）
水銀ポロシメーターを用いて、測定範囲０．００３４〜４００μｍで測定し、平均細孔径を求める。
(Pore size distribution)
Using a mercury porosimeter, the average pore diameter is determined by measuring in a measurement range of 0.0034 to 400 μm.
（熱示差分析：ＤＳＣ）
熱示差分析装置を用いて、流速４０ｍｌ／分の窒素の気流下、室温から昇温速度１０℃／分で昇温させ、温度範囲１８０〜２３５℃における吸熱ピーク面積求め、融解熱を算出する。
(Thermal differential analysis: DSC)
Using a thermal differential analyzer, the temperature is raised from room temperature at a heating rate of 10 ° C./min under a nitrogen stream at a flow rate of 40 ml / min, the endothermic peak area in the temperature range of 180 to 235 ° C. is determined, and the heat of fusion is calculated.
（煮あまに油吸油量）
ＪＩＳ・Ｋ５１０１に記載してある吸油量の測定方法に従って測定した吸油量である。
(Oil oil absorption in boiled sweet potato)
This is the oil absorption measured according to the method for measuring the oil absorption described in JIS / K5101.
（ポリアミド多孔質粒子の含有溶媒量の測定）
熱抽出−クライオフォーカス−ガスクロマトグラフ−質量分析装置を用いて、抽出温度２３０℃、１０分、ガスクロマトグラフ−質量分析測定温度５０℃から２０℃／分で２６０℃まで行い、測定イオンのピーク面積強度から求めた。
(Measurement of solvent content of polyamide porous particles)
Using a heat extraction-cryofocus-gas chromatograph-mass spectrometer, the extraction temperature is 230.degree. C. for 10 minutes, and the gas chromatograph-mass spectrometry measurement temperature is 50.degree. I asked for it.
[実施例１]
（ポリアミド多孔質粒子の調整）
ポリアミド６（分子量１３０００）１０ｇとｍ−クレゾール２００ｇからなるナイロン溶液を作製した。ナイロン溶液１００ｇ、メタノール５０００ｇ及び水１００ｇとをマグネチックスターラーで攪拌混合して１分攪拌後、溶液は均一になった。攪拌２分後にポリマー粒子が析出してきた。混合溶液を２４時間静置して、ポリマー粒子の析出を終了させた。得られた析出ポリマー粒子は、加温したメタノール、アセトンで洗浄し、その後遠心分離によりポリアミド粒子を単離した。
得られたポリアミド粒子は、数平均粒子径７．８１μｍであり、比較的均一なで球状のポリアミド多孔質粒子で、粒度分布指数（ＰＤＩ）は１．０８であった。得られたポリアミド粒子は、ＢＥＴ比表面積１０．８ｍ２／ｇ、平均細孔径は０．０４μｍであり、煮あまに油吸油量は２８０ｍＬ／１００ｇ、結晶化度は５８％、ｍ−クレゾール含有量は５ｐｐｍであった。
[Example 1]
(Polyamide porous particle adjustment)
A nylon solution consisting of 10 g of polyamide 6 (molecular weight 13000) and 200 g of m-cresol was prepared. 100 g of nylon solution, 5000 g of methanol and 100 g of water were stirred and mixed with a magnetic stirrer and stirred for 1 minute, and then the solution became uniform. After 2 minutes of stirring, polymer particles were precipitated. The mixed solution was allowed to stand for 24 hours to complete the precipitation of polymer particles. The obtained precipitated polymer particles were washed with warm methanol and acetone, and then the polyamide particles were isolated by centrifugation.
The obtained polyamide particles had a number average particle diameter of 7.81 μm, were relatively uniform and spherical polyamide porous particles, and the particle size distribution index (PDI) was 1.08. The obtained polyamide particles have a BET specific surface area of 10.8 m 2 / g, an average pore size of 0.04 μm, an oil absorption amount of 280 mL / 100 g, boiled sesame, a crystallinity of 58%, and an m-cresol content. Was 5 ppm.
（クレンジング用化粧品組成物の調整）
下記の成分組成Ａ〜Ｇを準備した。
Ａ相：水酸化ナトリウム（０．５５重量％）。
Ｂ相：１,３−ブチレングリコール（２５重量％）。
Ｃ相：防腐剤（０．３重量％）。
Ｄ相：香料（０．２重量％）。
Ｅ相：素練り促進剤（０．２重量％）。
Ｆ相：ゲル化剤（０．５重量％）。
Ｇ相：上記で得られたポリアミド粒子（１５重量％）。
水を加えて１００重量％とした。
上記Ａ−Ｅ相を９０℃の水に溶かし、ついでＧ相を投入し激しく攪拌して均一溶解後、５０℃にてＦ相を投入し攪拌した。これを室温に冷却することで、クリーム状ゲルを得た。これを皮膚表面に塗ると非常に伸ばしやすく、滑らかであり、水により容易に除去可能で、皮膚を柔らかく清潔で、てからないものとした。
(Adjustment of cleansing cosmetic composition)
The following component compositions A to G were prepared.
Phase A: Sodium hydroxide (0.55% by weight).
Phase B: 1,3-butylene glycol (25% by weight).
Phase C: preservative (0.3% by weight).
Phase D: Perfume (0.2% by weight).
Phase E: Peptizer (0.2% by weight).
Phase F: Gelling agent (0.5% by weight).
G phase: The polyamide particles obtained above (15% by weight).
Water was added to make up 100% by weight.
The above A-E phase was dissolved in 90 ° C. water, then the G phase was added and stirred vigorously to dissolve uniformly, and then the F phase was added at 50 ° C. and stirred. By cooling this to room temperature, a creamy gel was obtained. When applied to the skin surface, it was very easy to stretch, smooth and easily removable with water, making the skin soft and clean and unpretentious.
[実施例２]
ポリアミド６（分子量１３,０００）の１．０重量％のｍ−クレゾール溶液２２．０重量％に、メタノール５５．６重量％と水２２．２重量％とからなる混合物を、攪拌しながら、１２０秒間かけて添加した。攪拌を停止したのち静置したところ、ポリマー粒子が析出した。析出したポリマー粒子を遠心分離器で単離したのち、熱アルコールで洗浄し、２４時間真空乾燥してポリアミド６の粒子を得た。
得られたポリアミド６の粒子は、平均粒子長１０．５μｍ、粒子径に対する粒子長の比５．０、平均細孔径０．１３５μｍで、ダンベル状の多孔質粒子であった。
得られたポリアミド６の粒子は、煮あまに油吸油量３７０ｍＬ／１００ｇ、ＢＥＴ比表面積は１０．７ｍ２／ｇ、結晶化度は６２％、ｍ−クレゾール含有量は６ｐｐｍであった。
Ｇ相として得られたポリアミド６の粒子を用いた以外は、実施例１と同様にして、クレンジング用クリームゲルを得た。これを皮膚表面に塗ると非常に伸ばしやすく、滑らかであり、水により容易に除去可能で、皮膚を柔らかく清潔で、てからないものとした。
[Example 2]
A mixture of 55.6 wt% methanol and 22.2 wt% water was added to 22.0 wt% of a 1.0 wt% m-cresol solution of polyamide 6 (molecular weight 13,000) while stirring. Added over a second. When the stirring was stopped and the mixture was allowed to stand, polymer particles were precipitated. The precipitated polymer particles were isolated with a centrifugal separator, washed with hot alcohol, and vacuum-dried for 24 hours to obtain polyamide 6 particles.
The obtained polyamide 6 particles were dumbbell-shaped porous particles having an average particle length of 10.5 μm, a ratio of the particle length to the particle size of 5.0, and an average pore size of 0.135 μm.
The obtained polyamide 6 particles had an oil absorption of 370 mL / 100 g, a BET specific surface area of 10.7 m 2 / g, a crystallinity of 62%, and an m-cresol content of 6 ppm.
A cleansing cream gel was obtained in the same manner as in Example 1 except that the polyamide 6 particles obtained as the G phase were used. When applied to the skin surface, it was very easy to stretch, smooth and easily removable with water, making the skin soft and clean and unpretentious.
[比較例１]
ラウロラクタム５０９を流動パラフィン１３０ｍＬ、さらに分散助剤として、ステアリン酸ソーダ１ｇを添加し、温度１６０℃まで加熱し、ナトリウム２３０ｍｇ、アセチルカプロラクタムを０．９８ｍＬ添加し、２時間重合した。濾過後沸騰キシレンで洗浄し、その後真空乾燥し、ポリアミド粒子を得た。
得られたポリアミド粒子は、数平均粒子径５．９μｍ、粒度分布指数（ＰＤＩ）１．３２で、粒子表面に細孔は観察されなかった。
得られたポリアミド粒子は、煮あまに油吸油量６５ｍｌ／１００ｇであった。
Ｇ相として得られたポリアミド６の粒子を用いた以外は、実施例１と同様にして、クレンジング用クリームゲルを得た。皮膚表面に塗ったが伸びは悪く、滑らかさに欠けていた。水により容易に除去可能であったが、化粧や皮脂成分の除去が良くなかった。
[Comparative Example 1]
Laurolactam 509 was added with 130 mL of liquid paraffin and 1 g of sodium stearate as a dispersion aid, heated to 160 ° C., 230 mg of sodium and 0.98 mL of acetylcaprolactam were added, and polymerized for 2 hours. After filtration, it was washed with boiling xylene and then vacuum dried to obtain polyamide particles.
The obtained polyamide particles had a number average particle size of 5.9 μm and a particle size distribution index (PDI) of 1.32, and no pores were observed on the particle surface.
The obtained polyamide particles had an oil absorption of 65 ml / 100 g when boiled.
A cleansing cream gel was obtained in the same manner as in Example 1 except that the polyamide 6 particles obtained as the G phase were used. Although it was applied to the skin surface, it stretched poorly and lacked smoothness. Although it could be easily removed with water, makeup and sebum components were not well removed.
[実施例３]
（化粧水の調整）
実施例１で得たポリアミド粒子を用い、下記の成分組成Ａ〜Ｈを均一に混ぜ合わして、化粧水を調製した。
Ａ相：ＰＯＥソルビタンモノステアリン酸エステル（４０重量％）
Ｂ相：エタノール（２５重量％）
Ｃ相：実施例１で得たポリアミド粒子（５重量％）
Ｄ相：１,３−ブチレングリコール（５重量％）
Ｅ相：セラミド（５重量％）
Ｆ相：コラーゲン（５重量％）
Ｇ相：ビタミン（５重量％）
Ｈ相：精製水（１０重量％）
[Example 3]
(Toner lotion adjustment)
Using the polyamide particles obtained in Example 1, the following component compositions A to H were uniformly mixed to prepare a lotion.
Phase A: POE sorbitan monostearate (40% by weight)
Phase B: Ethanol (25% by weight)
Phase C: polyamide particles obtained in Example 1 (5% by weight)
Phase D: 1,3-butylene glycol (5% by weight)
Phase E: Ceramide (5% by weight)
Phase F: Collagen (5% by weight)
Phase G: Vitamin (5% by weight)
Phase H: purified water (10% by weight)
[実施例４]
（コンディショニングシャンプー）
実施例１で得たポリアミド粒子を用い、下記の成分組成Ａ〜Ｆを均一に混ぜ合わして、コンディショナー効果のあるシャンプーを調製した。
Ａ相：メチルビニルエーテル／無水マレイン酸架橋ポリマー（５％）（２０重量％）
Ｂ相：ポリクアテルテニウム−１０（０．２重量％）
Ｃ相：アルキルトリメチルアンモニウムクロリド（０．５重量％）、セチルアルコール（０．５重量％）
Ｄ相：へキシレングリコール（１重量％）
Ｅ相：トリウムラウリルエーテルスルフェート（２５重量％）、リエタノールアミンラウリルスルフェート（２０重量％）
Ｆ相：実施例１で得たポリアミド粒子（１０重量％）
水を加えて１００重量％とした。
ただし、Ａ相は、米国のＩＳＰ社のＳｔａｂｉｌｉｚｅ−０６（商品名）である。
[Example 4]
(Conditioning shampoo)
Using the polyamide particles obtained in Example 1, the following component compositions A to F were uniformly mixed to prepare a shampoo having a conditioner effect.
Phase A: methyl vinyl ether / maleic anhydride crosslinked polymer (5%) (20% by weight)
Phase B: Polyquaternium-10 (0.2% by weight)
Phase C: alkyltrimethylammonium chloride (0.5% by weight), cetyl alcohol (0.5% by weight)
Phase D: Hexylene glycol (1% by weight)
Phase E: thorium lauryl ether sulfate (25% by weight), reethanolamine lauryl sulfate (20% by weight)
Phase F: Polyamide particles obtained in Example 1 (10% by weight)
Water was added to make up 100% by weight.
However, A phase is Stabilize-06 (trade name) of ISP in the United States.
Claims (5)
該ポリアミド多孔質粒子が、下記に示す特性（Ａ）［Ａ１からＡ６］及び／又は（Ｂ）［Ｂ１からＢ６］を有する多孔質粒子であることを特徴とする化粧品組成物。
・ポリアミド多孔質粒子の特性（Ａ）：
（Ａ１）ＢＥＴ比表面積が、５ｍ２／ｇ以上、
（Ａ２）煮あまに油吸油量が、２００ｍＬ／１００ｇ以上、
（Ａ３）ＤＳＣによる結晶化度が、４０％以上、
（Ａ４）数平均粒子径が、１〜３０μｍの範囲、
（Ａ５）粒度分布指数（ＰＤＩ）が、１．０〜１．５の範囲、
（Ａ６）形状が、球状の粒子。
・ポリアミド多孔質粒子の特性（Ｂ）：
（Ｂ１）ＢＥＴ比表面積が、５ｍ２／ｇ以上、
（Ｂ２）煮あまに油吸油量が、２００ｍＬ／１００ｇ以上、
（Ｂ３）ＤＳＣによる結晶化度が、４０％以上、
（Ｂ４）数平均粒子長が、０．５〜２５μｍの範囲、
（Ｂ５）粒子径に対する粒子長の比が、３〜５０の範囲、
（Ｂ６）形状が、筒状及びダンベル状から選ばれる粒子。 A cosmetic composition for skin and hair comprising polyamide porous particles;
A cosmetic composition, wherein the polyamide porous particles are porous particles having the following characteristics (A) [A1 to A6] and / or (B) [B1 to B6].
-Characteristics of polyamide porous particles (A):
(A1) BET specific surface area is 5 m 2 / g or more,
(A2) Oil absorption in boiled sea bream is 200 mL / 100 g or more,
(A3) Crystallinity by DSC is 40% or more,
(A4) Number average particle diameter is in the range of 1 to 30 μm,
(A5) Particle size distribution index (PDI) is in the range of 1.0 to 1.5,
(A6) Particles having a spherical shape.
-Properties of polyamide porous particles (B):
(B1) BET specific surface area is 5 m 2 / g or more,
(B2) Oil absorption in boiled sea bream is 200 mL / 100 g or more,
(B3) Crystallinity by DSC is 40% or more,
(B4) Number average particle length is in the range of 0.5 to 25 μm,
(B5) The ratio of the particle length to the particle diameter is in the range of 3-50,
(B6) Particles whose shape is selected from a cylindrical shape and a dumbbell shape.
（１）クレンジング剤、ローション、化粧水、乳液、眼の周縁用（着色、非着色ケア−）クリーム、洗顔料、入浴剤及び石鹸の皮膚用、及び、
（２）シャンプー、ヘアコンディショナー、パーマ剤、ヘアクリーム、ヘアワックス及びヘアジェルの毛髪用の化粧品組成物であることを特徴とする請求項１〜４のいずれか１項に記載の化粧品組成物。
Cosmetic composition
(1) Cleansing agents, lotions, lotions, emulsions, peripheral eye (colored, non-colored care) creams, facial cleansers, bath salts and soap skins, and
(2) The cosmetic composition according to any one of claims 1 to 4, which is a cosmetic composition for shampoo, hair conditioner, permanent agent, hair cream, hair wax and hair gel hair.