JP2005203116A - Method of double-side coating and coated electrode - Google Patents
Method of double-side coating and coated electrode Download PDFInfo
- Publication number
- JP2005203116A JP2005203116A JP2004005087A JP2004005087A JP2005203116A JP 2005203116 A JP2005203116 A JP 2005203116A JP 2004005087 A JP2004005087 A JP 2004005087A JP 2004005087 A JP2004005087 A JP 2004005087A JP 2005203116 A JP2005203116 A JP 2005203116A
- Authority
- JP
- Japan
- Prior art keywords
- electrode
- coating
- paint
- double
- current collector
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、塗料の塗工に際して、ラス、エキスパンドメタル、エッチング、パンチング箔などの表裏貫通孔を備えた多孔質基材にたいする塗料の両面塗工方法に関する。 The present invention relates to a double-side coating method for coating a porous substrate having front and back through-holes such as lath, expanded metal, etching, punching foil and the like.
近年、環境問題がクローズアップされる中、太陽光発電や風力発電によるクリーンエネルギーの貯蔵システムや、電力の負荷平準化を目的とした分散型電源、あるいはガソリン車にかわる電気自動車用あるいはハイブリッド電気自動車用の電源(メイン電源と補助電源)の開発が盛んに行われている。 In recent years, as environmental problems have been raised, clean energy storage systems using solar power generation and wind power generation, distributed power sources for the purpose of electric power load leveling, or electric vehicles or hybrid electric vehicles that replace gasoline vehicles Power supplies (main power supply and auxiliary power supply) have been actively developed.
また、自動車の電装設備の電源としては、これまで鉛電池が用いられていたが、最近ではパワーウインドーやIT関連機器の搭載などが充実してきたこともあり、これらの用途においてもエネルギー密度、出力密度の高い新しい電源が求められるようになってきている。 In addition, lead batteries have been used as power sources for automotive electrical equipment, but recently there have been many improvements in the installation of power windows and IT-related equipment. In these applications as well, energy density and output density A new high-power supply has been demanded.
こうした駆動電源等を含めた蓄電装置としては、リチウムイオン二次電池や電気二重層キャパシタが注目されている。しかしながら、リチウムイオン電池はエネルギー密度は高いものの出力特性、安全性やサイクル寿命には問題を残している。一方、電気二重層キャパシタは、ICやLSIのメモリーバックアップ用電源として広く利用されている電子部品であり、一充電当たりの放電容量は電池に比べて小さいものの、瞬時の充放電特性に優れ、数万サイクル以上の充放電にも耐えるという、リチウムイオン電池やニッケル水素電池にはない高い出力特性とメンテナンスフリー性を備えている。 Lithium ion secondary batteries and electric double layer capacitors have attracted attention as power storage devices including such drive power sources. However, although the lithium ion battery has a high energy density, there are still problems in output characteristics, safety and cycle life. On the other hand, an electric double layer capacitor is an electronic component that is widely used as a memory backup power source for ICs and LSIs. Although its discharge capacity per charge is smaller than that of a battery, it has excellent instantaneous charge / discharge characteristics. It has high output characteristics and maintenance-free characteristics that are not found in lithium-ion batteries and nickel-metal hydride batteries.
電気二重層キャパシタはこうした利点を有してはいるが、一般的な電気二重層キャパシタのエネルギー密度は3〜4Wh/l程度で、リチウムイオン電池に比べて二桁程度小さいため、電気自動車用途などの高エネルギー密度が要求される駆動電源としては、未だ実用化レベルに到達していないのが現状である。電気自動車用途を考えた場合、実用化には6〜10Wh/l、普及させるには20Wh/lのエネルギー密度が必要であるといわれている。 Although the electric double layer capacitor has such advantages, the energy density of a general electric double layer capacitor is about 3 to 4 Wh / l, which is about two orders of magnitude smaller than that of a lithium ion battery. As a drive power source that requires a high energy density, it has not yet reached a practical level. When considering the use of electric vehicles, it is said that an energy density of 6 to 10 Wh / l is required for practical use and 20 Wh / l is required for widespread use.
こうした高エネルギー密度、高出力特性を要する用途に対応する蓄電装置としては、近年、ハイブリットキャパシタと呼ばれる蓄電装置が注目されている。電極には、電極−電解液界面において電荷の移動を伴う(ファラデー反応)非分極性電極と、電荷の移動を伴わない(非ファラデー反応)分極性電極がある。一般に電池は両極に非分極性電極を用いた構成であり、電気二重層キャパシタは両極に分極性電極を用いた構成であるが、ハイブリットキャパシタと呼ばれるものは、片極に分極性電極を、もう片極に非分極性電極を用いた構成である。電池の高いエネルギー密度と電気二重層キャパシタの高い出力特性を兼ね備えた蓄電装置として開発が活発化している。
高エネルギータイプのキャパシタ関連としては、リチウムイオンを吸蔵、脱離しうる材料に、予め化学的方法又は電気化学的方法でリチウムイオンを吸蔵させた材料を負極に用いるキャパシタが提案されている(例えば、特許文献1、2参照)。
In recent years, a power storage device called a hybrid capacitor has attracted attention as a power storage device corresponding to such applications requiring high energy density and high output characteristics. There are two types of electrodes: a non-polarizable electrode with charge transfer at the electrode-electrolyte interface (Faraday reaction) and a polarizable electrode with no charge transfer (non-Faraday reaction). In general, a battery has a configuration using non-polarizable electrodes on both sides, and an electric double layer capacitor has a configuration using polarizable electrodes on both sides, but what is called a hybrid capacitor has a polarizable electrode on one side. In this configuration, a nonpolarizable electrode is used for one electrode. The development of a power storage device that combines the high energy density of a battery and the high output characteristics of an electric double layer capacitor has become active.
As a high-energy type capacitor-related, a capacitor has been proposed in which a material in which lithium ions are occluded and desorbed in advance by a chemical method or an electrochemical method is used for a negative electrode. (See
また、自動車用電源など大型セルを対象とした場合において、予めリチウムを負極に担持させる方法としては、正極集電体および負極集電体がそれぞれ表裏に貫通する孔を備え、負極活物質がリチウムを可逆的に担持可能であり、負極由来のリチウムが負極あるいは正極と対向して配置されたリチウムと電気化学的接触により担持される有機電解質電池が提案されている(例えば、特許文献3参照)。該発明においては、電極集電体に表裏面を
貫通する孔を設けることにより、リチウムイオンが電極集電体に遮断されることなく電極の表裏間を移動できるため、積層枚数の多いセル構成の蓄電装置においても、当該貫通孔を通じて、リチウム近傍に配置された負極だけでなくリチウムから離れて配置された負極にもリチウムを電気化学的に担持させることが可能となる。また、当該貫通孔を通じてリチウムイオンが自由に各極間を移動できるため、充放電がスムーズに進行する。
In addition, when a large cell such as an automobile power source is targeted, as a method of supporting lithium on the negative electrode in advance, the positive electrode current collector and the negative electrode current collector are provided with holes penetrating the front and back, respectively, and the negative electrode active material is lithium. An organic electrolyte battery has been proposed in which lithium derived from the negative electrode is supported by electrochemical contact with lithium disposed opposite to the negative electrode or the positive electrode (see, for example, Patent Document 3). . In the invention, by providing a hole penetrating the front and back surfaces of the electrode current collector, lithium ions can move between the front and back surfaces of the electrode without being blocked by the electrode current collector. Also in the power storage device, lithium can be electrochemically supported not only on the negative electrode arranged in the vicinity of lithium but also on the negative electrode arranged away from lithium through the through hole. Further, since lithium ions can freely move between the electrodes through the through-hole, charging and discharging proceed smoothly.
また、正極、負極、並びに、リチウムイオンを移送可能な電解質を備えた有機電解質キャパシタであって、正極がリチウムイオンおよびアニオンを可逆的に担持可能であるとともに、負極がリチウムイオンを可逆的に担持可能であり、負極活物質の単位重量当たりの静電容量が、正極活物質の単位重量当たりの静電容量の3倍以上であり、かつ、正極活物質重量が負極活物質重量よりも大きく、負極には予めリチウムが担持されている有機電解質キャパシタが提案されている。該発明においては、静電容量の異なる正極と負極の活物質量比を適切に制御することにより、大型セルにおいて高エネルギー密度を達成している(例えば、特許文献4参照)。 An organic electrolyte capacitor having a positive electrode, a negative electrode, and an electrolyte capable of transporting lithium ions, wherein the positive electrode can reversibly carry lithium ions and anions, and the negative electrode reversibly carries lithium ions. The capacitance per unit weight of the negative electrode active material is more than three times the capacitance per unit weight of the positive electrode active material, and the positive electrode active material weight is greater than the negative electrode active material weight, An organic electrolyte capacitor in which lithium is previously supported on the negative electrode has been proposed. In the invention, a high energy density is achieved in a large cell by appropriately controlling the active material amount ratio between the positive electrode and the negative electrode having different capacitances (see, for example, Patent Document 4).
該発明において重要となるのは、例えばエキスパンドメタルのような表裏面を貫通する孔を有した集電体上に電極層を形成することである。従来の電極の塗工方法は、ダイコーターやロールコーター、コンマコーター、グラビアコーター等を用いて、例えばアルミニウム箔のように表裏面を貫通した孔を有しない集電体に対し、片面に塗工した後乾燥工程を経て、もう片面に同様に塗工を施していた。 What is important in the present invention is to form an electrode layer on a current collector having holes penetrating the front and back surfaces, such as expanded metal. The conventional electrode coating method uses a die coater, roll coater, comma coater, gravure coater, etc., for example, coating on one side of a current collector that does not have holes penetrating the front and back surfaces, such as aluminum foil. Then, after passing through a drying process, the other side was similarly coated.
また、両面塗工の方法も提案されており、垂直方向に走行する基材の搬送路の両側に一対のダイを配し、この一対のダイの上方に一対のブレードを設けて、ダイから吐出された塗料をブレードで掻き落として塗工厚みを制御するツインブレード法(例えば、特許文献5参照)やダイの塗料噴出し圧力により塗工厚みを制御する両面塗工方法(例えば、特許文献6参照)などがある。 Also, a double-sided coating method has been proposed. A pair of dies are arranged on both sides of a conveying path of a substrate traveling in a vertical direction, and a pair of blades are provided above the pair of dies to discharge from the die. The twin-blade method (for example, refer to Patent Document 5) in which the applied paint is scraped off with a blade to control the coating thickness, and the double-sided coating method in which the coating thickness is controlled by the paint spraying pressure of the die (for example, Patent Document 6) See).
また、両面塗工精度の改善を図った例がいくつかあるが(例えば、特許文献7〜10参照)、いずれの方法も基材の両側に2台のダイを宛がい両面塗工を行っている(本願、図1参照)。
ラスやエキスパンドメタルなどの表裏面を貫通する孔を有した集電体(多孔質基材)上に電極層を形成するために、活物質を含む塗料のロールコーターやコンマコーターを用いた片面毎の塗工では、集電体の裏側へ塗料が抜け、コーターのヘッドと押さえローラーとの間に塗料が付着し、厚みむらを生じたり、摩擦を生じて集電体が切れる等の不具合が生じていた。 Each side using a roll coater or comma coater of a paint containing an active material to form an electrode layer on a current collector (porous substrate) having holes penetrating the front and back surfaces such as lath and expanded metal In this coating, the paint comes off to the back side of the current collector, and the paint adheres between the coater head and the pressing roller, resulting in unevenness in thickness and friction, causing the current collector to break. It was.
また、上述のごとく提案されているように、基材の両側に対向する一対のダイを宛がい、基材の両面から塗料を塗工する両面塗工の場合、必ず2台のダイを必要とし、そのため各ダイに対して必要となる塗料タンクや供給ポンプ、フィルター、配管などがそれぞれ2セット必要となっていた。 In addition, as suggested above, in the case of double-sided coating in which a pair of dies facing both sides of the base material are applied and the paint is applied from both sides of the base material, two dies are required. Therefore, two sets of paint tanks, supply pumps, filters, pipes and the like necessary for each die are required.
また、塗工厚さや表面状態を制御するためには、2台のダイのクリアランスや塗料の吐出量、ダイリップ部のクリアランスなど厳密に調整する必要があった。 Further, in order to control the coating thickness and the surface state, it is necessary to strictly adjust the clearance between the two dies, the discharge amount of the paint, the clearance of the die lip portion, and the like.
また、該集電体は強度が無孔箔に比べ弱い上に孔を有しているため、100μm以下という薄い電極を製造するのが困難であった。 Further, since the current collector is weaker than the non-porous foil and has holes, it is difficult to produce a thin electrode of 100 μm or less.
また、コンマコーターなどの一般的な横型の塗工機に、ラスやエキスパンドメタルなどの表裏面を貫通する孔を有した集電体を搬送すると、回転しているローラーに塗料が転写してしまい、すぐに薄切れを起こしてしまうという問題があった。 Also, if a current collector with holes that penetrate the front and back surfaces, such as lath and expanded metal, is transported to a common horizontal coating machine such as a comma coater, the paint will be transferred to the rotating roller. There was a problem that it would cause slices immediately.
したがって、本発明の目的は、ラスやエキスパンドメタルなどの表裏面を貫通する孔を有した集電体上に、簡便に塗料の両面塗工を行う方法および電極を提供することにある。 Accordingly, an object of the present invention is to provide a method and an electrode for simply applying a double-sided coating on a current collector having holes penetrating front and back surfaces such as lath and expanded metal.
本発明者等は前記課題を解決すべく鋭意検討した結果、表裏貫通孔を備えた基材に塗料の両面塗工を行う際に、基材の搬送部に固定ロールを設けて、搬送する多孔質基材が固定ロールから離れる部分に液溜まりを作製することにより、多孔質基材に対し塗料の両面塗工が可能であることを見出し、本発明を完成させたものである。 As a result of intensive studies to solve the above-mentioned problems, the present inventors have provided a fixed roll in the transporting portion of the base material and transported it when performing double-side coating of the paint on the base material provided with front and back through holes. The present invention has been completed by finding that a double-sided coating of a porous substrate can be applied to a porous substrate by producing a liquid pool in a portion where the porous substrate is separated from the fixed roll.
すなわち、本発明は、
[1] 蓄電装置の電極において、表裏貫通孔を備えたアルミ、銅などの多孔質基材に対する塗工に際し、乾燥炉より前搬送部に固定バーを設けて、塗料が多孔質基材の片面に塗工された電極を未乾燥状態のまま搬送され、この固定バーで基材が固定バーから離れる内角側の接触部分に液溜まりを作製することにより、塗料を多孔質基材の表裏両面に塗工しうる両面塗工方法。
[2] 固定バーが固定ロールであり、コンマコーターのコンマヘッドに対向してローラーを設けたものであることを特徴とする[1]記載の両面塗工方法。
[3]表裏貫通孔を備えたアルミ、銅などの多孔質基材に対し、[1]および[2]記載の方法にて塗工して得られた電極。
である。
That is, the present invention
[1] In the electrode of the electricity storage device, when coating a porous base material such as aluminum or copper with front and back through holes, a fixing bar is provided in the front conveyance section from the drying furnace, and the coating is applied to one side of the porous base material. The electrode coated on is transported in an undried state, and by creating a liquid pool in the contact portion on the inner corner side where the substrate separates from the fixed bar with this fixed bar, the paint is applied to both the front and back surfaces of the porous substrate. Double-sided coating method that can be applied.
[2] The double-sided coating method according to [1], wherein the fixed bar is a fixed roll, and a roller is provided facing the comma head of the comma coater.
[3] An electrode obtained by coating the porous substrate such as aluminum and copper having front and back through holes by the method described in [1] and [2].
It is.
従来の一般的な両面塗工は、図1に示すように、基材の両側に対向する一対のダイ2を
宛がい、各ダイ2の塗料噴出し部であるダイリップ3から吐出される塗料を未塗工基材1の両面に同時塗工する、いわゆる垂直方向の縦型塗工がほとんどであった。垂直方向で塗工された電極の乾燥は、ある程度乾燥が進まないと接触するローラーに塗料が転写され箔切れをおこしてしまうために未乾燥状態のままでは横方向に搬送方向を換えることが出来ず、そのために縦型乾燥炉を垂直方向に高く設置する必要があった。しかし、塗工設備建屋の天井高さなどの制限があるために横型乾燥炉ほど炉長を確保しにくく、そのためある程度限られた乾燥炉長内で塗工された電極を乾燥する必要があるために、どうしても塗工速度が制限を受けていた。また、多孔質基材は、同じ厚みの箔に比べ強度が劣るので、垂直方向に高く上げると自重で基材切れを起こす恐れがあった。
As shown in FIG. 1, the conventional general double-side coating applies a pair of
それに対し本発明では、図2および図3に示すように、基材の搬送経路に固定ロールを設けることにより液溜まりを作製し、そこを通過した多孔質基材は両面塗工が施され、簡易的に横型乾燥炉へ搬送できる特長を有する。 On the other hand, in the present invention, as shown in FIG. 2 and FIG. 3, a liquid pool is prepared by providing a fixed roll in the transport path of the base material, and the porous base material that has passed there is subjected to double-sided coating, It has the feature that it can be easily transported to a horizontal drying oven.
本発明の両面塗工方法は、表裏貫通孔を備えたアルミ、銅などの多孔質基材に対する塗工に際し、乾燥炉より前搬送部に固定ロールを設けて、この固定ロールに対し、接触面と反対側となる面に片面塗工された電極を未乾燥状態のまま搬送し、基材が固定ロールから離れる内角側の接触部分に液溜まりを作製することにより、多孔質基材に対して塗料を表裏両面に同時に塗工することを特徴とした両面塗工方法である。
本発明において、表裏貫通孔を備えた多孔質基材としては一般に電池やキャパシタなどの用途で提案されている種々の材質を用いることができ、正極用基材にはアルミニウム、ステンレス等、負極用基材にはステンレス、銅、ニッケル等をそれぞれ好適に用いることができる。また、形状としては例えばエキスパンドメタル、パンチングメタル、金属網、発泡体、あるいはエッチングにより貫通孔を付与した多孔質箔等を挙げることができる。
The double-sided coating method of the present invention is provided with a fixed roll in the front conveyance section from the drying furnace when coating a porous substrate such as aluminum and copper having front and back through holes, and the contact surface with respect to the fixed roll By transporting the electrode coated on one side on the surface opposite to the surface in an undried state, and creating a liquid pool in the contact portion on the inner angle side where the substrate is separated from the fixed roll, the porous substrate It is a double-sided coating method characterized in that a paint is applied to both front and back surfaces simultaneously.
In the present invention, various materials generally proposed for applications such as batteries and capacitors can be used as the porous substrate having front and back through holes, and the positive electrode substrate is made of aluminum, stainless steel, or the like. Stainless steel, copper, nickel and the like can be suitably used for the base material. Examples of the shape include an expanded metal, a punching metal, a metal net, a foam, or a porous foil provided with through holes by etching.
基材の厚さは、正極用、負極用が同じ厚さでもよいが、材質が異なる場合、比重の重い方を薄くする方がセル容積当たりの重量を低減する上での効果が大きい。本発明において、正極用としてアルミニウム、負極用として銅を用いた場合、負極用を正極用より薄くすることが、より好ましい。 The thickness of the base material may be the same for the positive electrode and the negative electrode, but when the materials are different, reducing the weight with a higher specific gravity is more effective in reducing the weight per cell volume. In the present invention, when aluminum is used for the positive electrode and copper is used for the negative electrode, it is more preferable to make the negative electrode thinner than the positive electrode.
電極基材の貫通孔の形態、数等は、電解液が電極基材に遮断されることなく電極の表裏間を移動できるように、適宜設定することができる。 The form, number, and the like of the through holes of the electrode base material can be appropriately set so that the electrolyte can move between the front and back surfaces of the electrode without being blocked by the electrode base material.
この電極基材の気孔率は、{1−(基材重量/基材真比重)/(基材見かけ体積)}の比を百分率に換算して得られるものと定義する。本発明用いる電極基材の気孔率は、通常、10〜79%、好ましくは20〜60%、さらに好ましくは30〜50%、最も好ましくは、35〜45%である。また、本発明に用いる基材の厚みは特に限定するものでは無いが、好ましくは5〜50μm、より好ましくは10〜40μmである。
本発明において両面塗工される電極の厚みは、特に限定されるものではないが、通常30〜300μm、好ましくは40〜200μm、より好ましくは50〜100μmである。
The porosity of this electrode base material is defined as that obtained by converting the ratio of {1- (base material weight / base material true specific gravity) / (base material apparent volume)} into percentage. The porosity of the electrode substrate used in the present invention is usually 10 to 79%, preferably 20 to 60%, more preferably 30 to 50%, and most preferably 35 to 45%. The thickness of the substrate used in the present invention is not particularly limited, but is preferably 5 to 50 μm, more preferably 10 to 40 μm.
Although the thickness of the electrode coated on both sides in the present invention is not particularly limited, it is usually 30 to 300 μm, preferably 40 to 200 μm, more preferably 50 to 100 μm.
例えば負極にリチウムを担持させるのに、電極基材(集電体)の気孔率が高い場合には、担持させるのに要する時間が短く、リチウムの担持むらも生じにくいが、基材の強度は低下し、皺や切れが発生しやすい。また、貫通孔に導電性材料を保持させることが困難となり、導電性材料の脱落、電極の切れ等により、電極製造歩留まりが低下する等の問題が生じる。 For example, when the electrode substrate (current collector) has a high porosity to support lithium on the negative electrode, the time required for the support is short, and uneven lithium support does not occur. It tends to drop and become wrinkled and cut. In addition, it is difficult to hold the conductive material in the through hole, and problems such as a decrease in electrode manufacturing yield occur due to dropping of the conductive material, cutting of the electrode, and the like.
一方、気孔率が低い場合には、負極にリチウムを担持させるのに要する時間が長くなり生産効率の低下およびセル特性のバラツキ増大などの問題が発生するが、基材(集電体)
の強度は高くなり、活物質の脱落も起こりにくいため電極歩留まりは高くなる。電極基材(集電体)の気孔率や孔径は、電池の構造(積層タイプや捲回タイプなど)や生産性を考慮し、上述の範囲で適宜選定することが望ましい。
On the other hand, when the porosity is low, the time required to support lithium on the negative electrode becomes long, causing problems such as a decrease in production efficiency and an increase in variation in cell characteristics, but the substrate (current collector)
The strength of the electrode increases, and the active material does not easily fall off, so that the electrode yield increases. The porosity and pore diameter of the electrode substrate (current collector) are preferably selected as appropriate within the above-mentioned range in consideration of the battery structure (lamination type, winding type, etc.) and productivity.
多孔質基材は帯状であり、厚さは特に限定されないが厚さ5〜50μmが好適であり、さらには厚さ10〜40μmが好適である。また、幅も特に限定されないが約100〜1000mm、さらには約200〜500mmが好適である。図4に、電極集電体の一例を示す。図4(a)は、気孔率38%のエキスパンドメタル、図4(b)は気孔率37%の金属網、図4(c)は気孔率34%パンチングメタルの例である。図4(c)の例では、電極集電体の貫通孔は丸状であるが、貫通孔の形状はこれに限定されるものではなく、例えば、図4(d)に示す四角状(気孔率45%)、図4(e)に示す十文字状(気孔率35%)等、適宜設定できる。 The porous substrate is strip-shaped, and the thickness is not particularly limited, but is preferably 5 to 50 μm, and more preferably 10 to 40 μm. The width is not particularly limited, but is preferably about 100 to 1000 mm, more preferably about 200 to 500 mm. FIG. 4 shows an example of the electrode current collector. 4A shows an example of an expanded metal with a porosity of 38%, FIG. 4B shows an example of a metal net with a porosity of 37%, and FIG. 4C shows an example of a punching metal with a porosity of 34%. In the example of FIG. 4C, the through-hole of the electrode current collector is round, but the shape of the through-hole is not limited to this. For example, the square-shaped (pores) shown in FIG. Rate 45%), a cross shape (porosity 35%) shown in FIG.
本発明における用いる塗料は、、活物質とバインダ樹脂等からなり、多孔質基材に塗布されるものである。
活物質は特に限定されないが、電池またはキャパシタ用の電極の場合、粉末状、粒状、短繊維状等の成形しやすい形状にある炭素材料や酸化物等の活物質が含まれる。該活物質としては、正極活物質として例えばコークス、ピッチ、樹脂やヤシ殻、おがくずなどの植物などを出発原料とし、水蒸気、二酸化炭素や水酸化カリウムなどを用いて賦活した各種活性炭や導電性高分子、ポリアセン系物質、細孔直径2.0〜50nmのメソポアが顕著に発達したメソポアカーボン等の炭素材料や、LiCoO2、LiNiO2やMnO2等の金属酸化物、負極活物質としては、例えば天然黒鉛、人造黒鉛などのグラファイト、コークス、ピッチ、熱硬化性樹脂、ヤシ殻や樹木などを出発原料とする種々の炭素材料、炭素繊維、ポリアセン系物質、錫酸化物、珪素酸化物等を用いることができる。なかでもポリアセン系有機半導体(PAS)は、アモルファス構造を有することから、リチウムイオンの挿入・脱離に対して膨潤・収縮といった構造変化がないためサイクル特性に優れ、またリチウムイオンの挿入・脱離に対して等方的な分子構造(高次構造)であるため急速充電、急速放電にも優れた特性を有することから負極活物質として特に好適である。
塗料は該活物質をバインダー樹脂と混合して作製される。電池またはキャパシタ用電極のバインダー樹脂としては、用いる電解液に不溶のものであればよく、水を分散媒もしくは溶剤として用いる水系樹脂、あるいは、アルコールやN−メチルピロリドン等の有機溶剤を分散媒もしくは溶剤として用いる非水系樹脂を用いることができる。例えば共重合ポリマーのポリ(スチレンーブタジエン)(以下、SBRと省略する)等のゴム系バインダー樹脂、カルボキシメチルセルロース系樹脂は水系樹脂であり、フェノール樹脂やメラミン樹脂は組成により水系樹脂としても非水系樹脂としても用いることができる。
The paint used in the present invention comprises an active material and a binder resin, and is applied to a porous substrate.
The active material is not particularly limited, but in the case of an electrode for a battery or a capacitor, an active material such as a carbon material or an oxide having a shape that is easy to mold, such as powder, granule, or short fiber, is included. Examples of the active material include positive electrode active materials such as coke, pitch, resins, coconut shells, sawdust, and other activated carbons activated with water vapor, carbon dioxide, potassium hydroxide, and the like. Examples of molecules, polyacene-based materials, carbon materials such as mesopore carbon in which mesopores having a pore diameter of 2.0 to 50 nm are remarkably developed, metal oxides such as LiCoO 2 , LiNiO 2 and MnO 2 , and negative electrode active materials include Uses various carbon materials, carbon fibers, polyacene materials, tin oxide, silicon oxide, etc. starting from graphite such as natural graphite and artificial graphite, coke, pitch, thermosetting resin, coconut shells and trees be able to. In particular, polyacenic organic semiconductors (PAS) have an amorphous structure, so there is no structural change such as swelling / shrinkage with respect to lithium ion insertion / desorption, and cycle characteristics are excellent, and lithium ion insertion / desorption is also possible. Since it has an isotropic molecular structure (higher order structure), it has excellent characteristics in rapid charge and rapid discharge, and is therefore particularly suitable as a negative electrode active material.
The paint is prepared by mixing the active material with a binder resin. The binder resin for the battery or capacitor electrode may be any resin that is insoluble in the electrolyte used, an aqueous resin using water as a dispersion medium or solvent, or an organic solvent such as alcohol or N-methylpyrrolidone as a dispersion medium or A non-aqueous resin used as a solvent can be used. For example, rubber binder resins such as copolymer poly (styrene-butadiene) (hereinafter abbreviated as SBR), carboxymethyl cellulose resins are aqueous resins, and phenol resins and melamine resins are non-aqueous resins depending on the composition. It can also be used as a resin.
また、アクリル樹脂、ポリアミド樹脂、ポリエチレン樹脂などは、エマルジョン化することにより、水系樹脂として用いることができる。一方、ポリ四フッ化エチレン、ポリフッ化ビニリデン等の含フッ素系樹脂、ポリイミド樹脂、ポリアミド・イミド共重合樹脂は非水系樹脂の代表的な例である。
これらの中でもフッ素系、水系のSBR系樹脂、アクリル系樹脂、非水系のフッ素系樹脂が好ましい。
An acrylic resin, a polyamide resin, a polyethylene resin, or the like can be used as a water-based resin by emulsification. On the other hand, fluorine-containing resins such as polytetrafluoroethylene and polyvinylidene fluoride, polyimide resins, and polyamide / imide copolymer resins are typical examples of non-aqueous resins.
Of these, fluorine-based and water-based SBR resins, acrylic resins, and non-aqueous fluorine-based resins are preferable.
バインダー樹脂の混合比は、上記活物質に対して重量基準で1〜20%、好ましくは2〜10%、特に好ましくは2〜5%である。 The mixing ratio of the binder resin is 1 to 20%, preferably 2 to 10%, particularly preferably 2 to 5%, based on the weight of the active material.
塗料の活物質等の固形分濃度については特に限定するものでは無いが、通常10〜70%、好ましくは12%〜60%程度であり、凝集物が無く、均一な液状を有する塗料が好適に用いられる。 The solid content concentration of the active material of the paint is not particularly limited, but it is usually 10 to 70%, preferably about 12% to 60%, and a paint having no uniform aggregate and a uniform liquid is suitable. Used.
塗料の粘度についても特に限定するものでは無いが、20℃で通常50〜5000[mPa・s]、好ましくは100〜2000[mPa・s]程度の塗料を好適に用いることができる。 The viscosity of the coating is not particularly limited, but a coating of about 50 to 5000 [mPa · s], preferably about 100 to 2000 [mPa · s] at 20 ° C. can be suitably used.
本発明における固定バーの材質はステンレスや樹脂等、塗料との相性に応じて適宜設定できる。また径も塗料の粘度、性状あるいは塗工される膜厚等に応じて適宜設定するのが望ましい。また、塗料の粘度、性状によっては液溜まりが生じない場合があるので注意が必要である。固定バーの断面の形状は、真円(固定ロール)、半円、カマボコ状、楕円等でも良い。この場合固定とは、回転などの動作をすることなく固定状態であり、塗料の液溜りを形成する。回転すると、液溜りが生じにくくなり、塗料が必要以外の部分に塗工されることがある。 The material of the fixing bar in the present invention can be appropriately set according to the compatibility with the paint, such as stainless steel and resin. Further, it is desirable that the diameter is appropriately set in accordance with the viscosity, properties, film thickness to be applied, and the like. Also, care should be taken because the liquid pool may not be formed depending on the viscosity and properties of the paint. The shape of the cross section of the fixed bar may be a perfect circle (fixed roll), a semicircle, a kamaboko shape, an ellipse, or the like. In this case, the term “fixed” refers to a fixed state without any operation such as rotation, and forms a liquid pool of paint. When it rotates, it becomes difficult for liquid accumulation to occur, and the paint may be applied to parts other than necessary.
また、塗料の供給は多孔質基材の幅にまんべんなく行き渡るノズルやトレーなど供給できる手段であればどのような方式でも良く、その供給速度は特に限定されるものではないが、例えば100mm幅の多孔質基材では1〜100ml/minが好適であり、更には2〜30ml/minが好適である。この事によって前述の厚みの電極が得られるのである。
本発明の請求項1にある片面塗工は、リバースコーター、グラビアコーター、グラビアリバースコーター、ブレードコーターなど一般的な塗工機によって行うことが出来、特にその片面塗工方法を限定するものでは無い。
以下具体的な実施例により詳細を説明する。
In addition, the coating material may be supplied by any method as long as it can supply nozzles, trays and the like that are evenly distributed over the width of the porous substrate, and the supply speed is not particularly limited. In the case of a base material, 1 to 100 ml / min is preferable, and 2 to 30 ml / min is more preferable. As a result, the electrode having the above-described thickness can be obtained.
The single-side coating according to
Details will be described below with reference to specific examples.
(実施例1)
(負極PAS塗料の製造法)
厚さ0.5mmのフェノール樹脂成形板をシリコニット電気炉中に入れ、窒素雰囲気下で500℃まで50℃/時間の速度で、更に10℃/時間の速度で650℃まで昇温し、熱処理し、PASを合成した。かくして得られたPAS板をボールミルで粉砕することにより、平均粒子径が7μmのPAS粉体を得た。このPAS粉体のH/C比は0.22であった。
(Example 1)
(Production method of negative electrode PAS paint)
A 0.5 mm thick phenolic resin molded plate is placed in a siliconite electric furnace, heated to 500 ° C. at a rate of 50 ° C./hour, and further at a rate of 10 ° C./hour to 650 ° C. in a nitrogen atmosphere, followed by heat treatment. PAS was synthesized. The PAS plate thus obtained was pulverized with a ball mill to obtain a PAS powder having an average particle size of 7 μm. The H / C ratio of this PAS powder was 0.22.
次に、上記PAS粉体92重量部、アセチレンブラック粉体4重量部、SBR4重量部、カルボキシメチルセルロース3.2重量部に対しイオン交換水を添加して固形分が50〜60%となる組成にて充分混合することにより塗料を得た。 Next, ion-exchanged water is added to 92 parts by weight of the PAS powder, 4 parts by weight of acetylene black powder, 4 parts by weight of SBR, and 3.2 parts by weight of carboxymethylcellulose, so that the solid content becomes 50 to 60%. And thoroughly mixed to obtain a paint.
(負極1の製造方法)
厚さ32μm(気孔率50%)の銅製エキスパンドメタル(日本金属工業株式会社製)に対し、リバースコーターを用いて塗工速度1.0m/minで上述の負極PAS塗料の片面塗工行い、乾燥炉に基材が入る前に図2に示すような固定ロールを通過させ、その接触部に液溜まりを作製することにより両面塗工電極負極1を作製した。なお、この電極は、プレス後負極全体の厚さ(両面の負極電極層厚さと負極集電体厚さの合計)が81μmであった。
(実施例2)
リバースコーターでの塗工量を調整して、実施例1と同様に両面塗工を行うことにより、全体の厚さが104μmの負極2を得た。すなはち、片面塗工電極の厚みを変えることにより厚みの異なる両面同時電極を得ることが出来た。
(実施例3)
図3に示すようなコンマコーターで、コンマヘッドに相当するロール11に対向する、通常回転しているロール(固定ロール7)の回転を止め、これに厚さ32μm(気孔率50%)の銅製エキスパンドメタル(日本金属工業株式会社製)を取り付け、上述の負極P
AS塗料を塗工した。その際、基材が固定ロールから離れる内角側の接触部分に液溜まりを作製することにより両面塗工電極にし、横型乾燥炉へ搬送した。こうして、プレス後負極全体の厚さ(両面の負極電極層厚さと負極集電体厚さの合計)が81μmの負極3を得た。
(実施例4)
(正極活性炭塗料の製造法)
ヤシ殻を原料とし、電気炉中に入れ窒素気流下で50℃/時間の速度950℃まで昇温した後、窒素/水蒸気1:1の混合ガスにより2時間賦活することにより、比表面積1860m2/gの活性炭を製造した。該活性炭をボールミル粉砕機で粉砕して平均粒子径が5μmの活性炭粉末を得た。
上記活性炭粉末92重量部、アセチレンブラック粉体4重量部、SBR4重量部、カルボキシメチルセルロース1重量部に対し、イオン交換水を加えて固形分が30〜35%となる組成にて充分混合することにより塗料を得た。
(Method for producing negative electrode 1)
The above-described negative electrode PAS coating is applied to a copper expanded metal (made by Nippon Metal Industry Co., Ltd.) having a thickness of 32 μm (porosity 50%) using a reverse coater at a coating speed of 1.0 m / min and dried. Before the base material enters the furnace, a fixed roll as shown in FIG. 2 is passed, and a liquid reservoir is produced at the contact portion, thereby producing a double-side coated electrode
(Example 2)
By adjusting the coating amount with a reverse coater and performing double-sided coating in the same manner as in Example 1, a
(Example 3)
In the comma coater as shown in FIG. 3, the rotation of the normally rotating roll (fixed roll 7) facing the roll 11 corresponding to the comma head is stopped, and this is made of copper having a thickness of 32 μm (porosity 50%). Attached to expanded metal (manufactured by Nippon Metal Industry Co., Ltd.), the negative electrode P described above
AS paint was applied. At that time, a liquid pool was prepared at a contact portion on the inner angle side where the base material was separated from the fixed roll to form a double-sided coated electrode and conveyed to a horizontal drying furnace. Thus, negative electrode 3 having a total negative electrode thickness of 81 μm after pressing (total thickness of negative electrode layers on both sides and negative electrode current collector thickness) was obtained.
Example 4
(Production method of positive electrode activated carbon paint)
Coconut shell is used as a raw material, put into an electric furnace, heated to a rate of 950 ° C. at a rate of 50 ° C./hour in a nitrogen stream, and then activated with a mixed gas of nitrogen / water vapor 1: 1 for 2 hours to obtain a specific surface area of 1860 m 2. / G of activated carbon was produced. The activated carbon was pulverized by a ball mill pulverizer to obtain activated carbon powder having an average particle size of 5 μm.
By adding ion exchange water to the above-mentioned 92 parts by weight of activated carbon powder, 4 parts by weight of acetylene black powder, 4 parts by weight of SBR, and 1 part by weight of carboxymethyl cellulose, and sufficiently mixing the composition to a solid content of 30 to 35%. A paint was obtained.
(正極1の製造法)
基材として厚さ35μm(気孔率50%)のアルミニウム製エキスパンドメタル(日本金属工業株式会社製)、塗料として固形分15%のカーボン系の導電性塗料(日本黒鉛工業株式会社製、バニーハイトT−702A)を用いる以外は実施例2と同様に両面塗工を実施した。ただし、塗工された基材が乾燥炉に入る手前で基材に対し垂直方向からエアを吹き付けることにより、エキスパンドメタルの貫通孔内に保持された塗料を吹き飛ばしたため、エキスパンドメタルの金属部に導電性塗料がコーティングされた下塗り基材が得られた。
該下塗り基材と該正極塗料を用いて、実施例1と同様に両面塗工を行い、プレス後正極全体の厚さ(両面の正極電極層厚さと両面の導電層厚さと正極集電体厚さの合計)が122μmの正極1を得た。
(Method for producing positive electrode 1)
Aluminum expanded metal (made by Nippon Metal Industry Co., Ltd.) with a thickness of 35 μm (porosity 50%) as a base material, and carbon-based conductive paint with a solid content of 15% (Nihon Graphite Industry Co., Ltd., Bunny Height T-) Double-sided coating was performed in the same manner as in Example 2 except that 702A) was used. However, the coating material held in the through hole of the expanded metal was blown away by blowing air from the vertical direction to the substrate before the coated substrate entered the drying furnace, so that the metal part of the expanded metal was electrically conductive. An undercoating substrate coated with a functional paint was obtained.
Using the undercoat substrate and the positive electrode paint, double-side coating was performed in the same manner as in Example 1, and the thickness of the entire positive electrode after pressing (the thickness of the positive electrode layer on both sides, the thickness of the conductive layer on both sides, and the thickness of the positive electrode current collector) A
(セルの作成)
厚さ122μmの正極1と実施例1で製造した厚さ82μmの負極1を図11に示すような形状で電極面積がそれぞれ、5.0×8.0cm2になるようにカットし、セパレータとして厚さ30μmのセルロース/レーヨン混合不織布を用いて、図11に示したように正極集電体、負極集電体の接続端子との溶接部(以下「接続端子溶接部」という)がそれぞれ反対側になるよう配置し、正極、負極各8枚積層した。最上部と最下部はセパレータを配置させて4辺をテープ止めして電極積層ユニットを得た。負極活物質重量に対して400mAh/g分のリチウム金属としては、厚さ90μmのリチウム金属箔を厚さ80μmのステンレス網に圧着したものを用い、負極と対向するように電極積層ユニットの最外部に1枚配置した。負極(8枚)とリチウムを圧着したステンレス網はそれぞれ溶接し、接触させ電極積層ユニットを得た。
(Create cell)
The
上記電極積層ユニットの正極集電体の端子溶接部(8枚)に、予めシール部分にシーラントフィルムを熱融着した巾10mm、長さ30mm、厚さ0.2mmのアルミニウム製正極端子を重ねて超音波溶接した。同様に負極集電体の端子溶接部(8枚)に、予めシール部分にシーラントフィルムを熱融着した巾10mm、長さ30mm、厚さ0.2mmのニッケル製負極端子を重ねて超音波溶接し、縦102mm、横52mm、深さ1.2mmに深絞りした外装フィルム2枚(トータル2.4mmのスペース)の内部へ設置した。外装ラミネートフィルムの端子部2辺と他の1辺を熱融着した後、電解液としてエチレンカーボネート、ジエチルカーボネートおよびプロピレンカーボネートを重量比で3:4:1とした混合溶媒に、1モル/lの濃度にLiPF6を溶解した溶液を真空含浸させた後、残り1辺を減圧下にて熱融着し、真空封止を行うことによりフィルム型キャパシタを2セル組立てた。 An aluminum positive electrode terminal having a width of 10 mm, a length of 30 mm, and a thickness of 0.2 mm, in which a sealant film is heat-sealed in advance to the seal portion, is stacked on the terminal welded portion (eight sheets) of the positive electrode current collector of the electrode laminate unit. Ultrasonic welding. Similarly, a nickel negative electrode terminal having a width of 10 mm, a length of 30 mm and a thickness of 0.2 mm, which is preliminarily heat-sealed with a sealant film, is superposed on the terminal welded portion (8 sheets) of the negative electrode current collector, and ultrasonic welding is performed. And it installed in the inside of two exterior films (space of a total of 2.4 mm) deep-drawn to length 102mm, width 52mm, and depth 1.2mm. After heat-sealing the two sides of the terminal portion of the exterior laminate film and the other side, 1 mol / l in a mixed solvent of ethylene carbonate, diethyl carbonate and propylene carbonate in a weight ratio of 3: 4: 1 as an electrolytic solution. A solution in which LiPF 6 was dissolved at a concentration of 2 was vacuum-impregnated, and the remaining one side was heat-sealed under reduced pressure and vacuum-sealed to assemble two cells of film type capacitors.
(セルの特性評価)
14日間室温にて放置後、1セル分解したところ、リチウム金属は完全に無くなっていたことから、リチウムは正極および負極の表裏間を移動して全ての負極に予備充電されたと判断した。
(Characteristic evaluation of cells)
One cell was disassembled after standing at room temperature for 14 days, and lithium metal was completely lost. Therefore, it was judged that lithium was precharged to all negative electrodes by moving between the front and back surfaces of the positive electrode and the negative electrode.
また、残った1セルを600mAの定電流でセル電圧が3.6Vになるまで充電し、その後3.6Vの定電圧を印加する定電流−定電圧充電を1時間行った。次いで、60mAの定電流でセル電圧が1.8Vになるまで放電した。この3.6V−1.8Vのサイクルを繰り返し、3回目の放電容量は65mAhであった。また、セルの縦長さを100mm、横長さを50mmとした時のエネルギー密度は14.6Wh/lであった。
上述の通り、本発明による両面塗工電極を用いることにより、高エネルギー密度を有するキャパシタが得られることを確認した。
Further, the remaining 1 cell was charged with a constant current of 600 mA until the cell voltage reached 3.6 V, and then a constant current-constant voltage charge in which a constant voltage of 3.6 V was applied was performed for 1 hour. Next, the battery was discharged at a constant current of 60 mA until the cell voltage became 1.8V. This 3.6V-1.8V cycle was repeated, and the discharge capacity for the third time was 65 mAh. The energy density when the vertical length of the cell was 100 mm and the horizontal length was 50 mm was 14.6 Wh / l.
As described above, it was confirmed that a capacitor having a high energy density was obtained by using the double-sided coated electrode according to the present invention.
1 基材
1' 片面塗工領域
1''両面塗工領域
2、2' ダイ
3 ダイリップ
4 塗料
5 片面塗工電極
6 液溜まり
7、7' 固定バー
8 乾燥炉
9 両面塗工電極
18 正極
18a 正極集電体
19 負極
19a 負極集電体
20 セパレータ
DESCRIPTION OF
Claims (3)