JP2005161959A - Recycled solid tire for snowy road, and method for manufacturing the same - Google Patents
Recycled solid tire for snowy road, and method for manufacturing the same Download PDFInfo
- Publication number
- JP2005161959A JP2005161959A JP2003402647A JP2003402647A JP2005161959A JP 2005161959 A JP2005161959 A JP 2005161959A JP 2003402647 A JP2003402647 A JP 2003402647A JP 2003402647 A JP2003402647 A JP 2003402647A JP 2005161959 A JP2005161959 A JP 2005161959A
- Authority
- JP
- Japan
- Prior art keywords
- tire
- layer
- polyurethane elastomer
- rubber
- solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明は、雪道用再生ソリッドタイヤ及びその製造方法に係り、特に、摩耗したソリッドラバータイヤの有効な再生技術に関するものである。 The present invention relates to a recycled solid tire for a snow road and a method for manufacturing the same, and more particularly to an effective regeneration technique for a worn solid rubber tire.
従来から、自動車等の車両には、その荷重を負担し、車両と路面との間で円滑な力の伝達の機能を持つタイヤとして、中空部内に空気が封入されてなる構造の空気入りタイヤの他、中実構造のゴム円環体からなるソリッドタイヤが、よく知られている。そして、このソリッドタイヤは、タイヤの機能としての負荷能力、緩衝能力及びゴムの弾性を利用したものであって、主として低速、重荷重車両、例えばフォークリフトトラック、産業用トラクタ、蓄電池運搬車、トレーラ等に広く用いられてきており、その構成には、多くの場合、単一のトレッドゴムをホイールに直接に焼付けしたもの、ベースバンドにゴム材料を加硫接着し、ホイールに圧入するもの、円環状のトレッドゴムをホイールの外周部に嵌め込むもの等が知られている。 Conventionally, a pneumatic tire having a structure in which air is enclosed in a hollow portion as a tire that bears the load on a vehicle such as an automobile and has a function of transmitting a smooth force between the vehicle and a road surface. In addition, a solid tire made of a solid rubber ring is well known. The solid tire uses load capacity, shock absorbing capacity, and rubber elasticity as tire functions, and is mainly used for low speed, heavy load vehicles such as forklift trucks, industrial tractors, battery storage vehicles, trailers, etc. In many cases, a single tread rubber is baked directly on the wheel, a rubber material is vulcanized and bonded to the base band, and the ring is pressed into the wheel. Such a tread rubber is fitted into the outer periphery of the wheel.
ところで、かかるソリッドタイヤは、一般に、NR等のゴム材料にてトレッドゴムが構成されてなるソリッドラバータイヤとして用いられているが、そのようなタイヤは、路面と接触して、その摩擦力によって車両の移動を許容するものであるところから、長期間の使用により、路面との接触面の摩耗が進み、耐用寿命となれば、廃棄されることとなるが、近年、その廃タイヤの処理が大きな社会問題となってきている。特に、ソリッドラバータイヤは、乗用車等に用いられている空気入りタイヤに比較して重いために、その取扱いが困難であり、また、焼却し難く、更に他の用途への利用が難しい等の問題があるために、その処分に大きな困難を伴なっているのである。 By the way, such a solid tire is generally used as a solid rubber tire in which a tread rubber is constituted by a rubber material such as NR. However, such a tire comes into contact with a road surface and the vehicle is driven by its frictional force. Since the wear of the contact surface with the road surface is advanced due to long-term use and the service life is reached, it will be discarded. It has become a social problem. In particular, solid rubber tires are heavier than pneumatic tires used in passenger cars, etc., making them difficult to handle, difficult to incinerate, and difficult to use for other purposes. Therefore, the disposal is accompanied with great difficulty.
このため、特許文献1においては、摩耗タイヤの表面をバフ研磨し、そのトレッド部に、再生用トレッドゴムを接着してなる構造のニューマチック型ソリッドタイヤが提案され、それによって、従来、処理に困っていた摩耗タイヤを有効に利用すると共に、タイヤ材料の節約やタイヤの作製時間の短縮を実現し得ることが、明らかにされている。 For this reason, Patent Document 1 proposes a pneumatic solid tire having a structure in which the surface of a worn tire is buffed and a tread rubber is adhered to the tread portion. It has been clarified that it is possible to effectively use a worn tire that has been in trouble, and to save tire materials and shorten the production time of the tire.
しかしながら、そのような摩耗タイヤのトレッド部に、再び、再生用トレッドゴムを接着しても、そのようにして得られた再生タイヤの使用により、トレッドゴム部の摩耗は再び発生することとなるのであり、従ってトレッドゴム部の耐久性の向上は充分でないことに加えて、かかるトレッドゴム部を構成するゴム材料には、一般に、補強剤としてカーボンブラックが配合されて、黒色とされているところから、そのようなトレッドゴム部と路面との摩擦により、路面には、黒色のタイヤ跡がつく問題がある。そして、この路面についた黒色のタイヤ跡は、美観を損ない、フォークリフトトラック等の作業現場においては、黒色のゴム摩耗粉と共に、作業環境を悪化せしめるものとなっているのである。 However, even if the reclaimed tread rubber is again adhered to the tread portion of such a worn tire, wear of the tread rubber portion will occur again due to the use of the regenerated tire thus obtained. Therefore, in addition to the fact that the durability of the tread rubber part is not sufficiently improved, the rubber material constituting the tread rubber part is generally blackened with carbon black as a reinforcing agent. There is a problem that a black tire mark is formed on the road surface due to friction between the tread rubber portion and the road surface. The black tire marks on the road surface are detrimental to the aesthetics, and at the work site such as a forklift truck, the work environment is deteriorated together with the black rubber wear powder.
また、特許文献2においては、ウレタンゴムタイヤを用いた転輪の再生方法として、使用済タイヤを用い、そのベースバンドからゴムタイヤを除去した後、そのゴムタイヤが除去されたベースバンド外周面に、エーテル系ウレタンゴム層を形成して、再生転輪を得る技術が、明らかにされている。
In
而して、そのような再生転輪においては、路面にはウレタンゴムが接することとなるところから、通常のNR等のゴム材料からなるトレッドゴムに比較して、耐摩耗性に優れている特徴があり、そのため、再生転輪の耐久性乃至は寿命が効果的に向上せしめられ得るという利点を有しているものの、そのような通常のトレッドゴムに比べて、クッション性乃至は緩衝性において劣り、かかる再生転輪を装着したフォークリフトトラック等の車両を運転する際に、運転者に対して不快な衝撃が伝達される等という問題を内在している。尤も、そのような再生転輪のクッション性を高めるには、そのウレタンゴムタイヤ部分を発泡体構造としたり、また、その硬度を著しく低くして、その柔軟性を高めたりする等の対策が考えられるのであるが、そうすると、ウレタンエラストマー本来の耐摩耗性が損なわれ、その耐久性に問題を生じるようになるのである。 Thus, in such a regenerative wheel, since the urethane rubber is in contact with the road surface, it is superior in wear resistance as compared with a tread rubber made of a rubber material such as a normal NR. Therefore, although it has an advantage that the durability or life of the recycle wheel can be effectively improved, it is inferior in cushioning or cushioning properties compared to such a normal tread rubber. When driving a vehicle such as a forklift truck equipped with such a regenerative wheel, an unpleasant impact is transmitted to the driver. However, in order to improve the cushioning properties of such regenerative wheels, it is conceivable to take measures such as making the urethane rubber tire part into a foam structure, or significantly reducing its hardness and increasing its flexibility. However, in this case, the inherent wear resistance of the urethane elastomer is impaired, and a problem arises in its durability.
また一方、工場等の敷地内で資材等の運搬に用いられているフォークリフトトラック等においては、雪道や凍結した路面上を走行する際に、ソリッドタイヤが滑り易いことが問題となっている。このため、スリップし難い雪道用のソリッドタイヤも要求されているのである。 On the other hand, in forklift trucks and the like used for transporting materials on the site of factories and the like, there is a problem that solid tires are slippery when traveling on snowy roads or frozen road surfaces. For this reason, there is a demand for solid tires for snow roads that do not slip easily.
ここにおいて、本発明は、かかる事情を背景にして為されたものであって、その大きな解決課題とするところは、摩耗が進み、耐用寿命となった廃棄ソリッドラバータイヤの有効な再生技術を提供することにあり、中でも、特に、耐摩耗性や、衝撃の吸収・緩和特性に優れると共に、雪道においても滑り難い雪道用再生ソリッドタイヤと、かかる雪道用再生ソリッドタイヤの有利な製造手法を提供することにある。 Here, the present invention has been made in the background of such circumstances, and the major solution is to provide an effective regeneration technology for a discarded solid rubber tire that has been worn out and has reached the end of its useful life. Among them, in particular, it is excellent in wear resistance, shock absorption / relaxation characteristics, and it is hard to slip even on snowy roads, and an advantageous manufacturing method for such solid road tires for snowy roads. Is to provide.
そして、本発明は、上記せる課題の解決のために、その第一の態様とするところは、摩耗したソリッドラバータイヤにおける摩耗残にて与えられる所定厚さのラバー層と、該ラバー層の外周面上に一体的に形成された常温硬化型のポリウレタンエラストマー層とを有する再生ソリッドタイヤであって、前記ポリウレタンエラストマー層の構成材料よりも耐摩耗性に優れた材料からなる複数のピンが、その少なくとも端部を該ポリウレタンエラストマー層の外周面に露呈するように、タイヤ周方向及び幅方向の所定の位置に、固定的に埋設されていることを特徴とする雪道用再生ソリッドタイヤにある。 In order to solve the above-described problems, the present invention has a first aspect in which a rubber layer having a predetermined thickness given by wear remaining in a worn solid rubber tire, and an outer periphery of the rubber layer Recycled solid tire having a room temperature curing type polyurethane elastomer layer integrally formed on the surface, and a plurality of pins made of a material having higher wear resistance than the constituent material of the polyurethane elastomer layer, A regenerated solid tire for snowy roads is fixedly embedded at predetermined positions in the tire circumferential direction and width direction so that at least an end portion is exposed on the outer peripheral surface of the polyurethane elastomer layer.
また、本発明に従う雪道用再生ソリッドタイヤにおける第二の態様にあっては、前記ピンが、その一部において、タイヤ外周面から外方に突出せしめられる構成が採用される。 Further, in the second aspect of the solid road tire for snow road according to the present invention, a configuration is adopted in which a part of the pin protrudes outward from the outer peripheral surface of the tire.
さらに、本発明に従う雪道用再生ソリッドタイヤの第三の態様おいては、前記ピンが、その一部において、前記ラバー層に突入せしめられる構成が、採用されることとなる。 Furthermore, in the third aspect of the solid road tire for snow road according to the present invention, a configuration is adopted in which the pin is partly plunged into the rubber layer.
加えて、本発明に従う雪道用再生ソリッドタイヤの第四の態様においては、前記ポリウレタンエラストマー層が、空気を微細に分散、含有せしめてなるポリウレタン原料を常温硬化させることによって、形成される。 In addition, in the fourth aspect of the solid road tire for snow road according to the present invention, the polyurethane elastomer layer is formed by curing a polyurethane raw material in which air is finely dispersed and contained at room temperature.
また、本発明に従う雪道用再生ソリッドタイヤの第五の態様では、前記ポリウレタンエラストマー層が、前記ラバー層の外周面上に一体的に形成された第一の層と、該第一の層の外周面上に形成されて、該第一の層の構成材料よりも耐摩耗性に優れたポリウレタンエラストマーからなる第二の層とから、構成されることとなる。 In the fifth aspect of the solid road tire for snow road according to the present invention, the polyurethane elastomer layer is integrally formed on the outer peripheral surface of the rubber layer, and the first layer comprises: A second layer made of a polyurethane elastomer formed on the outer peripheral surface and having higher wear resistance than the constituent material of the first layer.
さらに、本発明の好ましい第六の態様においては、前記第二の層が、前記第一の層よりも高い硬度を有している。 Furthermore, in a preferred sixth aspect of the present invention, the second layer has a higher hardness than the first layer.
ところで、本発明は、上述せる如き雪道用再生ソリッドタイヤの製造方法も、また、その対象とするものであって、摩耗したソリッドラバータイヤを準備し、該タイヤにおける摩耗残となる所定厚さのラバー層がホイール全周に残るようにした状態において、かかるラバー層の外周面上の所定の位置に、複数の凹窩を穿設し、次いで、該複数の凹窩の各々に、耐摩耗性に優れた材料からなるピンをその外周面に接着剤を適用して嵌入せしめ、固定した後、常温硬化型のポリウレタン原料を、反応硬化せしめることによって、前記タイヤの摩耗した外周面上に、所定厚さのポリウレタンエラストマー層を一体的に形成する一方、該複数のピンの少なくとも端部を該ポリウレタンエラストマー層外周面に露呈させたことを特徴とする雪道用再生ソリッドタイヤの製造方法を、その第一の態様としている。 By the way, the present invention is also directed to a method for producing a solid tire for reclaimed snow road as described above, and a worn solid rubber tire is prepared, and a predetermined thickness is left as a residual wear in the tire. With the rubber layer remaining on the entire circumference of the wheel, a plurality of recesses are drilled at predetermined positions on the outer peripheral surface of the rubber layer, and then each of the plurality of recesses is subjected to wear resistance. A pin made of a material having excellent properties is applied to the outer peripheral surface by applying an adhesive and fixed, and then a room temperature curing type polyurethane raw material is reacted and cured on the worn outer peripheral surface of the tire. A snowy road regenerative software characterized in that a polyurethane elastomer layer having a predetermined thickness is integrally formed, and at least ends of the plurality of pins are exposed on the outer peripheral surface of the polyurethane elastomer layer. The manufacturing method of Ddotaiya, and its first aspect.
また、本発明に従う雪道用再生ソリッドタイヤの製造方法の好ましい第二の態様においては、前記ポリウレタン原料中に空気が導入されて、微細に分散せしめられた後、反応硬化せしめられることにより、硬度の調整されたポリウレタンエラストマー層が形成されることとなる。 Further, in a second preferred embodiment of the method for producing a regenerated solid tire for snowy road according to the present invention, air is introduced into the polyurethane raw material, finely dispersed, and then hardened by reaction and hardening. Thus, the adjusted polyurethane elastomer layer is formed.
そして、このような本発明に従う雪道用再生ソリッドタイヤにおける、先述した第一の態様によれば、ホイールの外周部に取り付けられる円環状のトレッド部が、ソリッドラバータイヤの摩耗残にて与えられる所定厚さのラバー層(内側層)と、かかるラバー層上に一体的に形成された常温硬化型のポリウレタンエラストマー層(外側層)とからなる複層構造とされているところから、そのようなトレッド部の接地面から受ける衝撃は、内側のラバー層にて効果的に吸収・緩和され得ることとなると共に、そのようなトレッド部の接地面を与える外側の常温硬化型のポリウレタンエラストマー層は、ポリウレタンエラストマー材料の本来有する良好な耐摩耗特性によって、耐久性が著しく高められ、以て、得られる雪道用再生ソリッドタイヤの耐用寿命が格段に向上せしめられ得ることとなるのである。 And according to the 1st aspect mentioned above in such a reproduction solid tire for snowy roads according to this invention, the annular tread part attached to the perimeter part of a wheel is given by the wear residue of a solid rubber tire. Such a structure is a multilayer structure composed of a rubber layer (inner layer) having a predetermined thickness and a room temperature curing type polyurethane elastomer layer (outer layer) integrally formed on the rubber layer. The impact received from the contact surface of the tread part can be effectively absorbed and relaxed by the inner rubber layer, and the outside room temperature curing type polyurethane elastomer layer that provides such a contact surface of the tread part is Recycled solid tires for snowy roads, which have significantly improved durability due to the good wear resistance inherent in polyurethane elastomer materials. Is the so that the service life can be brought remarkably improved.
また、かかる雪道用再生ソリッドタイヤにおける、トレッド部の外側層を構成するポリウレタンエラストマー層には、通常のラバー層とは異なり、カーボンブラックが、何等、配合されてはいないことから、そのような雪道用再生ソリッドタイヤ(トレッドゴム)の接地路面には、従来のソリッドラバータイヤの如き、黒色のタイヤ跡が付くようなことはなく、そのために、美観の悪化、更には黒色の摩耗ゴム粉の飛散等による作業環境の悪化の如き問題が惹起されることはないのである。更に、かかる雪道用再生ソリッドタイヤは、摩耗したソリッドラバータイヤの摩耗残となるラバー層を実質的に残して、それをトレッド部の内側層として利用するものであるところから、ソリッドタイヤのトレッド部全体をポリウレタンエラストマー層にて構成する場合よりも、遥かに、ポリウレタンエラストマー材料の使用量を低減せしめることが出来、以て、ソリッドタイヤの再生の為に必要とされるトレッド部の材料の大幅な節約が可能となる。 Further, in such a solid road tire for snow road, the polyurethane elastomer layer constituting the outer layer of the tread portion is different from the normal rubber layer, and carbon black is not blended at all. The ground road surface of recycled solid tires (tread rubber) for snowy roads does not have black tire marks like conventional solid rubber tires. Thus, problems such as deterioration of the working environment due to the scattering of the dust are not caused. Further, such a recycled solid tire for snowy roads has a rubber layer that remains a worn portion of the worn solid rubber tire and uses it as an inner layer of the tread portion. It is possible to reduce the amount of polyurethane elastomer material used compared to the case where the entire part is made of a polyurethane elastomer layer, which means that the tread material required for solid tire regeneration can be greatly reduced. Savings.
しかも、そのような雪道用再生ソリッドタイヤには、耐摩耗性に優れた材料からなるピンが、少なくとも端部をポリウレタンエラストマー層の外周面に露呈するように、タイヤ周方向及び幅方向の所定の位置に、固定的に埋設されているところから、かかる雪道用再生ソリッドタイヤを装着した車両等を、雪道や凍結した道において運転した際にも、タイヤ表面に露呈したピンが、路面上の雪や氷に突き刺さったり、かかる雪や氷を引っ掻き、これによって、タイヤと路面と間の摩擦が効果的に高められ得て、滑り乃至はスリップの発生が有利に防止され得ることとなる。 In addition, in such a solid road tire for snowy roads, predetermined pins in the tire circumferential direction and the width direction are provided so that the pins made of a material having excellent wear resistance are exposed at least at the ends on the outer circumferential surface of the polyurethane elastomer layer. When a vehicle equipped with such a solid road tire for snowy roads is driven on a snowy road or a frozen road, the pin exposed on the tire surface is exposed to the road surface. The above-mentioned snow or ice can be stabbed or scratched, so that the friction between the tire and the road surface can be effectively increased, and the occurrence of slipping or slipping can be advantageously prevented. .
従って、かくの如き本発明に従う雪道用再生ソリッドタイヤにあっては、耐摩耗性や衝撃の吸収・緩和特性に優れるばかりでなく、使用耐久性にも優れ、しかも路面へのタイヤ跡の付着による弊害等の発生が有利に防止され得ると共に、雪道や凍結した路面においてもスリップの発生が効果的に防止され得るのである。また、摩耗が進み、耐用寿命となったソリッドラバータイヤの廃棄処分も不要となり、かかるソリッドラバータイヤの再生が極めて有効的に実現され得ることとなり、以て、廃タイヤの処理による社会問題を効果的に解消し得るといった利点も享受され得ることとなるのである。 Therefore, in the solid road tire for snow road according to the present invention as described above, it not only has excellent wear resistance and shock absorption / relaxation properties, but also has excellent durability and adhesion of tire marks to the road surface. It is possible to advantageously prevent the occurrence of adverse effects due to the occurrence of slips and to effectively prevent the occurrence of slips even on snowy roads and frozen road surfaces. In addition, it is no longer necessary to dispose of solid rubber tires that have become worn out and have reached the end of their useful lives, and the regeneration of such solid rubber tires can be realized extremely effectively, thereby effectively addressing social problems due to the disposal of waste tires. Therefore, the advantage that it can be eliminated can be enjoyed.
また、本発明に従う雪道用再生ソリッドタイヤの第二の態様によれば、ピンによる滑り止め効果乃至はスリップ防止効果が、より一層高度に発揮され得る。 Further, according to the second aspect of the solid road tire for snow road according to the present invention, the anti-slip effect or the anti-slip effect by the pin can be exhibited to a higher degree.
さらに、本発明に従う雪道用再生ソリッドタイヤの第三の態様によれば、ピンがタイヤの厚さ方向の奥深くまで埋設されることとなる。これにより、ピンが、タイヤから、具体的にはポリウレタンエラストマー層から抜け出るようなことが、有利に防止され得るようになる。 Furthermore, according to the 3rd aspect of the reproduction solid tire for snowy roads according to this invention, a pin will be embed | buried deeply in the thickness direction of a tire. As a result, it is possible to advantageously prevent the pins from slipping out of the tire, in particular from the polyurethane elastomer layer.
加えて、本発明に従う雪道用再生ソリッドタイヤの上記した第四の態様によれば、前記ポリウレタンエラストマー層は、空気を微細に分散、含有せしめてなるポリウレタン原料を常温硬化させることにより、形成されているところから、かかるポリウレタンエラストマー層中には、空気の微細気泡が存在せしめられることとなり、以て、そのようなポリウレタンエラストマー層が効果的に柔軟化され得て、その硬度乃至はクッション性が調整され得ることにより、かかるポリウレタンエラストマー層による衝撃の吸収・緩和特性が、有利に改善され得ることとなる。 In addition, according to the fourth aspect of the above-described solid road tire for snowy road according to the present invention, the polyurethane elastomer layer is formed by room temperature curing of a polyurethane raw material in which air is finely dispersed and contained. Therefore, in the polyurethane elastomer layer, fine air bubbles are allowed to exist, so that the polyurethane elastomer layer can be effectively softened, and the hardness or cushioning property thereof can be improved. By being able to be adjusted, the impact absorption / relaxation characteristics of the polyurethane elastomer layer can be advantageously improved.
また、本発明に従う雪道用再生ソリッドタイヤの第五及び第六の態様によれば、前記ラバー層の外周面上に一体的に形成されたポリウレタンエラストマー層(第一の層)上に、更に、該第一の層の構成材料(ポリウレタンエラストマー)よりも耐摩耗性に優れたポリウレタンエラストマーからなるポリウレタンエラストマー層(第二の層)が、一体的に形成されているところから、雪道用再生ソリッドタイヤのトレッド部全体としての耐久性が更に向上され、その耐用寿命が、より一層高められ得るのであり、また、このような耐摩耗性に優れた第二の層の形成によって、該第二の層とラバー層との間の常温硬化型の第一の層を、微細気泡によって、より一層柔軟化せしめることが出来るところから、かかる雪道用再生ソリッドタイヤの衝撃の吸収・緩和作用の増大を有利に図ることが出来るのである。 According to the fifth and sixth aspects of the solid road tire for snow road according to the present invention, on the polyurethane elastomer layer (first layer) integrally formed on the outer peripheral surface of the rubber layer, Since the polyurethane elastomer layer (second layer) made of the polyurethane elastomer having higher wear resistance than the constituent material of the first layer (polyurethane elastomer) is integrally formed, the regeneration for the snow road The durability of the entire tread portion of the solid tire is further improved, and the service life of the solid tire can be further enhanced. By forming the second layer having excellent wear resistance, the second tire The impact of the recycled solid tire for snowy roads can be increased by making the first layer of the room temperature curing type between the rubber layer and the rubber layer more flexible with fine bubbles. Achieving advantageously increased the absorption and mitigation action is that possible.
また、本発明に従う雪道用再生ソリッドタイヤの製造方法における、前記した第一の態様によれば、上述せる如き各種の特徴を有する雪道用再生ソリッドタイヤが、有利に製造され得る。また、ラバー層上に一体形成されるポリウレタンエラストマー層の形成材料として、常温硬化型のポリウレタン原料が用いられているところから、ポリウレタンエラストマー層の形成時にラバー層を高温下に晒す必要がなく、このため、熱によるラバー層の特性変化の発生が効果的に回避され得ると共に、摩耗したソリッドラバータイヤの再生が、迅速に行われ得ることとなる。 Also, according to the first aspect of the method for producing a solid road tire for snow road according to the present invention, the solid road tire for snow road having various characteristics as described above can be advantageously produced. In addition, since a room temperature curing type polyurethane raw material is used as a material for forming the polyurethane elastomer layer integrally formed on the rubber layer, it is not necessary to expose the rubber layer to a high temperature when forming the polyurethane elastomer layer. Therefore, the occurrence of a change in the rubber layer characteristics due to heat can be effectively avoided, and the worn solid rubber tire can be quickly regenerated.
さらに、ピンが、ソリッドラバータイヤの摩耗残にて与えられるラバー層(内側層)と、かかるラバー層上に一体的に形成されたポリウレタンエラストマー層(外側層)とからなるトレッド部内に強固に固着せしめられることとなり、これによって、使用時における、ポリウレタンエラストマー層からのピンの離脱も、効果的に防止され得る。その結果、ピンによる滑り止め効果乃至はスリップ防止効果も、長期に亘って有利に発揮せしめられることとなる。 In addition, the pin is firmly fixed in the tread portion composed of a rubber layer (inner layer) given by the remaining wear of the solid rubber tire and a polyurethane elastomer layer (outer layer) integrally formed on the rubber layer. As a result, the pin can be effectively prevented from being detached from the polyurethane elastomer layer during use. As a result, the anti-slip effect or the anti-slip effect by the pin can be exhibited advantageously over a long period of time.
また、かかる本発明に従う雪道用再生ソリッドタイヤの製造方法の第二の態様によれば、ポリウレタンエラストマー層の高度を小さく為して、ポリウレタンエラストマー層を柔軟化せしめることが出来、タイヤの全体的なクッション性の調整が容易となる。 In addition, according to the second aspect of the method for producing a regenerated solid tire for snowy road according to the present invention, the polyurethane elastomer layer can be made soft by reducing the height of the polyurethane elastomer layer. Easy cushioning adjustment.
以下、本発明を更に具体的に明らかにするために、本発明の実施の形態について、図面を参照しつつ、詳細に説明することとする。 Hereinafter, in order to clarify the present invention more specifically, embodiments of the present invention will be described in detail with reference to the drawings.
先ず、図1には、ソリッドラバータイヤ10が車両に装着されて使用され、そのトレッド部16が摩耗した状態が、部分側面図の形態において示されている。即ち、ソリッドラバータイヤ10は、従来と同様に、NR、IR、SBR、BR、EPM、EPDM,IIR等のゴム材料の一種又は二種以上をブレンドして、成形され、一般的には、NRやIRを主体としたブレンドゴムを用いて、加硫成形されたものであって、従来からソリッドタイヤとして市販されているものである。なお、そのようなソリッドラバータイヤ10は、全体として円環形状を呈し、その円環形状の内周部に対して、車両の車軸に取り付けられるホイール12の外周面が、よく知られているように、焼付式、圧入式、嵌め込み式等の方式において取り付けられるようになっている。
First, FIG. 1 shows a state in which the
そして、このようなソリッドラバータイヤ10にあっては、その側面に、その使用限界を示すトレッドウェアインジケータ(タイヤウェアインジケータ)14が、矢印等の形態において、刻設乃至は浮き出し形成されており、路面との接触によるトレッド部16の摩耗により、路面に接地するタイヤ外周面がトレッドウェアインジケータ14に至ると、ソリッドラバータイヤ10は、その耐用寿命に達したと判断されて、新品のソリッドラバータイヤに取り替えられることとなるのである。
And in such a
ところで、本発明にあっては、この耐用寿命に達した、摩耗したソリッドラバータイヤ18を用い、その摩耗残となる所定厚さのラバー層20が、ホイール12の全周に残るようにした状態において、図2に示される如く、その摩耗した外周面22上に、常温硬化型のポリウレタンエラストマー層24を所定厚さにおいて一体的に形成して、新たなトレッド部(16)を再生する一方、かかるトレッド部内の所定の位置に、耐摩耗性に優れた材料からなる複数のピン26が、その少なくとも端部を、ポリウレタンエラストマー層24の外周面28に露呈するように、固定的に埋設され、以て、雪道用再生ソリッドタイヤ30として、再び車両に適用され得るようにしたのである。
By the way, in the present invention, the worn
ここで、かかる摩耗残のラバー層20上に一体的に形成されるポリウレタンエラストマー層24は、従来からよく知られている常温硬化型のポリウレタン原料を用いて、それをラバー層20の外周面22上において注型成形することにより、所望の厚さにおいて形成されることとなる。具体的には、ここで採用される常温硬化型のポリウレタン原料とは、一般に、ポリイソシアネート成分として、変性ジフェニルメタン−4,4′−ジイソシアネート等のNDI系イソシアネートを用い、またポリオール成分として、ポリエーテルポリオール等を用い、そして、それらポリイソシアネート成分とポリオール成分とを低温下において迅速に反応硬化せしめる触媒として、芳香族1級アミン等の芳香族アミンを用いてなるものであって、各種の市販品の中から適宜に選択され、例えば、独国:バイエル社から「デスモジュール」、「バイテック」等の名称にて市販されているものを用い、10〜50℃の温度下において、反応硬化せしめることにより、目的とするポリウレタンエラストマーが形成される。なお、その反応は、各成分の混合後、約1分程度経過すれば、ある程度の固化状態が実現され、そして、室温にて3日程度経過すれば、実質的な反応は終了し、最終物性が実現されるようになるものである。
Here, the
このように、ポリウレタンエラストマー層24の形成に、常温硬化型のポリウレタン原料が用いられていることにより、その反応硬化(キュアリング)のために、摩耗したソリッドラバータイヤ18におけるラバー層20を高温下に晒す必要がなく、そのために、ラバー層20の熱等に基づくところの特性変化を効果的に回避し得ることとなるのであって、これにより、所定のポリウレタンエラストマー層24がラバー層20上に一体的に形成されてなる雪道用再生ソリッドタイヤ30において、かかるラバー層20に基づくところの衝撃に対するクッション性乃至は緩衝性を有利に発現せしめ、また、そのようなラバー層20の耐久性、ひいては雪道用再生ソリッドタイヤ30全体としての耐用寿命の向上を、有利に図り得るのである。
Thus, the room temperature curing type polyurethane raw material is used for forming the
また、このような構成の雪道用再生ソリッドタイヤ30にあっては、ポリウレタンエラストマー層24の外周面28が、路面に対する接地面となるところから、ポリウレタンエラストマー本来の耐摩耗特性が発揮され得て、以て、雪道用再生ソリッドタイヤ30の耐用寿命が著しく延長せしめられ得るのであり、しかも、そのような耐摩耗性に優れたポリウレタンエラストマー層24の内側には、ラバー層20が存在しているところから、かかるポリウレタンエラストマー層24の硬度が、例えばショアA硬度で、80A〜90Aとなっても、接地面から車両側に伝達される衝撃は、ラバー層20によって、効果的に吸収乃至は緩和され得ることとなり、その結果、かかる雪道用再生ソリッドタイヤ30の装着された車両の乗り心地等の改善に、大きく寄与せしめられ得るのである。
Further, in the
しかも、そのようなポリウレタンエラストマー層24は、ラバー層20とは異なり、補強剤としてのカーボンブラックは、何等、配合されてはいないために、路面上を雪道用再生ソリッドタイヤ30が転動されても、黒色のタイヤ跡が付くようなことは全くないのである。
Moreover, since the
なお、このポリウレタンエラストマー層24は、その優れた耐摩耗特性を維持し得る限度において、多数の微細な気泡を内在して構成される発泡体構造とすれば、それらの気泡によって、ポリウレタンエラストマー層24自体による衝撃の吸収乃至は緩和特性も発揮させることが可能となる。そして、そのような発泡体構造は、特に、空気を微細に分散、含有せしめてなるポリウレタン原料を常温硬化させることによって、有利に形成され、また、そのような微細な空気粒にて形成される気泡の存在量を調整することによって、ポリウレタンエラストマー層24の硬度が、適宜に調整され得ることとなる。
If the
また一方、本実施形態の雪道用再生ソリッドタイヤ30のトレッド部内に固定的に埋設されているピン26は、トレッド部に比して遥かに小さな円柱形状を呈する棒状体であって、滑り止め効果やスリップ防止効果を得るべく、上述せる如きポリウレタンエラストマー層24の構成材料よりも耐摩耗性に優れた材料から構成されている。具体的には、そのようなピン26の構成材料としては、上記のように耐摩耗性に優れたものであれば、何等限定されるものではなく、例えば、ポリウレタンエラストマー、ポリカーボネート、「ジュラコン」等の名称にて市販されているポリアセタール等の樹脂材料や、従来からスパイクタイヤにおけるスパイクピン(鋲)の構成材料として用いられている公知の金属材料、また、セラミック材料等を挙げることが出来る。これらの中でも、ラバー層20やポリウレタンエラストマー層24、特に、後者のポリウレタンエラストマー層24との接着性が良好な樹脂材料が好ましく、また、かかる樹脂材料の中でも、特に、氷雪道路上の氷や雪よりも硬く、アスファルトやコンクリート等の路面よりも柔軟である樹脂材料が、好適に採用され得るのであり、このような材料を採用することによって、路面の損傷等が極めて効果的に防止され得るのである。
On the other hand, the
このように、本実施形態の雪道用再生ソリッドタイヤ30にあっては、タイヤ周方向及び幅方向の所定の位置に、耐摩耗性に優れた材料からなるピン26が固設されているところから、かかる雪道用再生ソリッドタイヤを装着した車両等を、雪道や凍結した道において運転した際にあっても、タイヤ表面(28)のピン26が、路面上の雪や氷に突き刺さったり、かかる雪や氷を引っ掻くこととなり、これにより、タイヤと路面と間の摩擦が増大せしめられ得て、タイヤの滑り乃至はスリップの発生が効果的に防止され得るようになっている。
Thus, in the snow road recycled
しかも、本実施形態においては、かかるピン26の軸方向の一方の端部32が、タイヤ外周面であるポリウレタンエラストマー層24の外周面28から外方に突出せしめられているところから、上述せる如きピン26による滑り止め効果やスリップ防止効果が、極めて効果的に発現され得るようになっているのである。なお、そのようなピン26のタイヤ表面(28)からの突出量は、特に制限されるものではなく、フォークリフトトラック等の車両の乗り心地や、路面に対する影響、ピン26による滑り止め性能等を勘案して、一般に、従来のスパイクタイヤにおけるスパイクピンの突出量と同様な突出量が、設定されることとなる。
Moreover, in the present embodiment, one
さらに、本実施形態のピン26は、その軸方向の他方の端部34、即ちトレッド部の内側に位置する端部34が、内側層である、ソリッドラバータイヤの摩耗残にて与えられるラバー層20内に突入せしめられ、タイヤの厚さ方向の奥深くにまで埋設されている。このため、ピン26のトレッド部への接着面積が有利に増大せしめられて、ピン26がトレッド部内に強固に固着されるようになっている。このため、トレッド部からのピン26の落脱が有利に防止され、ピン26による滑り止め効果乃至はスリップ防止効果が、長期に亘って有利に発揮せしめられる。
Further, the
また、本発明にあっては、ポリウレタンエラストマー層が、複層構造とされる構成も有利に採用され、その一実施形態が、図3に示されている。かかる図3においては、ポリウレタンエラストマー層が二層構造とされており、そこでは、ラバー層20上に形成された、上述せる如きポリウレタン原料から形成されるポリウレタンエラストマー層24が第一の層(内側ポリウレタンエラストマー層)とされ、かかる第一の層(24)の外周面28上に、更に、別のポリウレタンエラストマーからなる第二の層36(外側ポリウレタンエラストマー層)が形成されている。そこにおいて、第一の層(24)上に一体的に形成された第二の層36は、第一の層(24)を構成するポリウレタンエラストマーよりも耐摩耗性に優れたポリウレタンエラストマーにて、所定厚さにおいて形成されており、かかる図3に示される雪道用再生ソリッドタイヤ38は、一体的な三層構造のトレッド部を有して、構成されている。また、この場合においても、ピン26による滑り止め効果乃至はスリップ防止効果を得るべく、ピン26は、複層構造のポリウレタンエラストマー層よりも、つまり外側に形成される第二の層36よりも、耐摩耗性に優れた材料から形成されることは、勿論言うまでもないところである。
Moreover, in this invention, the structure by which a polyurethane elastomer layer is made into a multilayer structure is also employ | adopted advantageously, One embodiment is shown by FIG. In FIG. 3, the polyurethane elastomer layer has a two-layer structure, in which a
なお、ここにおいて、上述せる如き第二の層36を構成するポリウレタンエラストマーは、耐摩耗性に優れたポリウレタンエラストマーを与える公知のポリウレタン原料を用いて、形成されることとなるが、それは、一般に、NDIエラストマーとして得られるものであって、具体的には、ポリイソシアネート成分としてナフタリン−1,5−ジイソシアネート(NDI)を用い、ポリオール成分としては、ポリエステルポリオール等を用い、それらの成分を予め反応させて、NDI/エステルプレポリマーを形成した後、それにグリコール架橋剤や水を配合して、目的とするソリッドNDIエラストマーやマイクロセルラーNDIエラストマーを形成させることにより、目的とする第二の層36が注型成形手法等により形成されることとなる。なお、そのような耐摩耗性に優れたポリウレタンエラストマーを与えるポリウレタン原料も市場において入手可能であり、例えば、独国:バイエル社から「ブルコラン」の名称にて提供されるポリウレタン原料を有利に用いることが出来る。
Here, the polyurethane elastomer constituting the
そして、このような耐摩耗性に優れた第二の層36が形成されてなる雪道用再生ソリッドタイヤ38にあっては、その耐用寿命が更に一段と改善せしめられ得るのであり、また、そのような第二の層36が、その内側の第一の層(24)よりも高い硬度を有しているように構成することによって、更に、優れた耐摩耗特性が実現され得るのである。
In the snow road recycled
加えて、そのような第二の層36の存在は、また、その内側に位置する第一の層(24)の発泡体構造を高めて、その硬度を低下せしめることが出来、それによって、ラバー層20に加えて、第一の層(24)も、衝撃の吸収乃至は抑制に寄与せしめることが出来ることとなる。
In addition, the presence of such a
ところで、かくの如き構成の本発明に従う雪道用再生ソリッドタイヤ30,38は、例えば、以下の如き注型成形法等の公知の成形手法を用いた手法によって製造されるととなる。即ち、先ず、摩耗したソリッドラバータイヤ18が準備される。そして、常温硬化型のポリウレタンエラストマー層(第一の層)24の形成に先立って、摩耗したソリッドラバータイヤ18におけるラバー層20の外周面22には、その表面の清浄化の後、サンドブラストが実施され、外周面22の粗面化が実施される。このサンドブラストには、破砕されて角が付けられた砂粒子が用いられ、この砂粒子の吹き付けによって、摩耗残であるラバー層20の外周面22の表面が粗面化される。また、フライス盤を用いた切削加工を行なって、ラバー層20の外周面22の粗面化を実施しても良く、この場合にも、ラバー層20の外周面22がホイール12に対して同心的に位置する円筒面となるように、切削加工が施されることとなる。
By the way, the regenerated
そして、上述せる如きサンドブラストや切削加工によって、摩耗したソリッドラバータイヤ18が、例えば、外周面22における幅方向の偏減りが著しいものであっても、或いはそうでなくとも、ラバー層20が、ホイール12の全周に均一な厚さをもって残るような形態とされ、これによって、ラバー層20における、衝撃に対する吸収・緩和特性が、その全周において均等に発揮され得るようになる。
And even if the
そして、かかる粗面化加工が終了したら、ドリル等の公知の穿孔機を用いて、ラバー層20の外周面22上の所定の位置に、図4に示される如き、複数の凹窩40(ここでは、周方向24個×幅方向3個、計72個の凹窩)が、所定の深さにて、穿設される。
When the roughening process is completed, a plurality of concave cavities 40 (here, as shown in FIG. 4) are formed at predetermined positions on the outer
次いで、かかる複数の凹窩40の各々に、上記した耐摩耗性に優れた材料からなる円柱状のピン26が、一本ずつ、嵌入せしめられる。この際、ピン26の外周面の少なくとも凹窩40に嵌入する部位には、ゴム用や樹脂用等の公知の接着剤が適用されるのであり、このように接着剤の塗布されたピン26を用いることによって、かかるピン26が、ラバー層20に強固に固定されることとなり、以て、後の注型成形時等において、ラバー層20に固定したピン26が凹窩40から抜け出たり、傾いたりするようなことが、有利に防止され得るのである。なお、接着剤は、ピン26の、少なくとも凹窩に挿入する部位に適用されておれば良いが、ピン26の外表面の略全面に塗布されていても良い。
Next, one
なお、ピン26をラバー層20に固定した後、或いはピン26を凹窩40に挿入するに先立って、かかるラバー層20の粗面化された外周面22上に、ポリウレタン用やゴム用の公知の接着剤が、例えば、刷毛やスプレー装置等の塗布装置を用いて塗布せしめられることが望ましく、これによって、ラバー層20の外周面22上に、ポリウレタンエラストマー層24が強固に固着されるようになる。
In addition, after fixing the
そして、複数のピン26が固定されたソリッドラバータイヤ18(ラバー層20)は、図5〜図7に示されるように、所定の注型装置にセットされる。具体的には、本実施形態において用いられる注型装置42は、略円筒形状を呈し、四分割される外型44(44a〜44d)と、この外型44の内側空間内に同心的に配置される、円板部46と円柱部48とからなる中子状の内型50とから構成されており、かかる外型44の内面52には、ピン26の外方に突出する端部32を収容するために、所定深さの収容孔54が、ラバー層20に固定されたピン26のそれぞれに対応するように、設けられている。そして、図5に示されるように、内型50に対して、複数のピン26が固定されたソリッドラバータイヤ18が、ホイール12を取り外した状態で、その内孔内に内型50の円柱部48を嵌入し、次いで、図6に示されるように、4つの外型44a〜44dが、その内面52に設けられた各々の収容孔54内にピン26がそれぞれ収容されるように、組み付け、型合せされることによって、かかる注型装置42内にセットされるのである。
And the solid rubber tire 18 (rubber layer 20) to which the
その後、図8に示されるように、注型装置42内にセットされた摩耗ソリッドラバータイヤ18のラバー層20の外周面22と外型44の内面52との間の隙間56内に、公知の注入装置58から、所定の常温硬化型のポリウレタン原料60が注入され、充填せしめられる。この注入装置58としては、例えば、ミキシングヘッドやガンタイプの注入器等、公知の構造を有するものが適宜に選択されて用いられ、このような注入装置58に対して、ポリイソシアネート成分(A)と硬化剤(触媒)を配合したポリオール成分(B)とが供給されて、それらの成分が、適当な動的攪拌機(ダイナミックミキサー)や静的攪拌機(スタティックミキサー)を用いて、均一に混合せしめられた後、注型装置42内に注入されるようになっている。なお、注入装置58には、圧縮空気(C)も、必要に応じて導入せしめられ得るようになっており、この圧縮空気の導入によって、ポリウレタン原料60内には、空気が微細に分散、含有せしめられることとなる。
Thereafter, as shown in FIG. 8, a known gap is formed in the
そして、そのようなポリウレタン原料60が注型装置42内に注入されて、常温下において反応硬化せしめられることにより、ラバー層20の外周には、ポリウレタンエラストマー層(第一の層)24が、必要に応じて微細な気泡が分散されてなる形態において、一体的に形成されると共に、複数のピン26は、ポリウレタンエラストマー層(第一の層)24の所定の部位において、それぞれ、固定的に埋設される。その後、注型装置42からの脱型により取り出された、ラバー層20とポリウレタンエラストマー層(第一の層)24との一体成形品62には、その外周面28に、所定の高さにおいて、複数のピン26がその軸方向の一方の端部32において突出する。
Then, such a polyurethane
その後、図10に示されるように、このような一体成形品62に対して、必要な仕上げ加工が施される一方、ポリウレタンエラストマー層の外周角部がR加工されて、湾曲部64とされて、タイヤとしての使用中における欠け等の問題が惹起されないようにして、目的とする雪道用再生ソリッドタイヤ66が、完成されるのである。
Thereafter, as shown in FIG. 10, the necessary finish processing is performed on such an integrally molded
このような雪道用再生ソリッドタイヤ66の製造方法によれば、タイヤ全体をポリウレタンエラストマーにて形成するものではなく、摩耗残となる所定厚さのラバー層20がホイール全周に残るようにした状態において、その外周面にポリウレタンエラストマー層(第一の層)24を一体的に形成するものであるところから、ポリウレタン原料60の使用量も少なくて済むという経済効果も享受し得ることとなるのである。そして、この図8〜図10に示した実施形態では、圧縮空気(C)の吹き込みによって、ポリウレタン原料60中には、微細な空気泡が導入されて、微細に分散せしめられた状態において反応硬化せしめられ、以て、微細な空気粒子の存在するポリウレタンエラストマー層(第一の層)24として形成されているが、そのような微細な空気粒子の存在の程度によって、ポリウレタンエラストマー層(第一の層)24の硬度が変化せしめられるところから、圧縮空気(C)の吹き込み量によって得られるポリウレタンエラストマー層(第一の層)24の硬度を有利に調整し得るのである。
According to such a manufacturing method of a snow road recycled
なお、図3に示される如き耐摩耗性に優れた第二の層36を、第一の層(24)上に形成する場合にあっては、図5に示される如き一体成形品62を用い、それを一回り大きな別の注型装置にセットして、第一の層(24)の形成の場合と同様にして、かかる第一の層(24)の外周部に、所定のポリウレタン原料を用いて注型成形すればよい。この場合にあっても、図3に示されるように複数のピン26が、ポリウレタンエラストマー層(第二の層36)の外周面から外方に突出するように、第一の層(24)及び第二の層36を形成するための外型として、それぞれ、所定の深さの収容孔を有するものが、適宜に用いられることとなる。
In the case where the
そして、上述の如くして得られた、雪道用再生ソリッドタイヤ66には、その内孔内に、従来と同様な焼付式、圧入式、或いは嵌め込み式等の方式にて、ホイール12が固定的に取りけられて、車両に装着され、使用されることとなるのであり、これにより、前述せる如きポリウレタンエラストマー層をラバー層20上に設けたことに基づくところの格別の作用・効果が、奏されることとなるのである。
Then, in the
以上、本発明の好ましい実施形態について詳述してきたが、それは文字通りの例示であって、本発明は、そのような実施形態の記載によって、何等、限定的に解釈されるものでないことが、理解されるべきである。 Although preferred embodiments of the present invention have been described in detail above, they are literal examples, and it is understood that the present invention is not construed as being limited in any way by the description of such embodiments. It should be.
例えば、本発明において用いられる摩耗したソリッドラバータイヤ18としては、フォークリフトトラック、産業用トラクタ、蓄電池運搬車、トレーラ等に従来から用いられている、通常のゴム材質のソリッドタイヤ、所謂ソリッドラバータイヤの回収物等が対象とされる他、荷車等の車輪やキャスタに用いられている通常のソリッドゴムからなるタイヤ等も、その対象とされ得るものであり、また、そのようなソリッドタイヤには、ニューマチック型ソリッドタイヤやシリンドリカルベース式ソリッドタイヤが含まれており、そのようなソリッドタイヤのゴム材質のものに対して、本発明が適用されることとなる。
For example, the worn
また、上例の雪道用再生ソリッドタイヤの製造工程においては、摩耗したソリッドラバータイヤ18が、ホイール12から取り外された形態において、注型装置42内にセットされて、そのラバー層20の外周面に、目的とするポリウレタンエラストマー層24が、一体的に形成されているが、そのような摩耗したソリッドラバータイヤ18からホイール12を取り外すことなく、それらが一体に組み合わされた形態において、注型装置42内にセットして、目的とするポリウレタンエラストマー層24をラバー層20の外周面22上に形成せしめるようにすることも可能である。
Further, in the manufacturing process of the above-described recycled solid tire for snowy road, the worn
さらに、ポリウレタンエラストマー層24を与えるポリウレタン原料60中には、補強剤としてのカーボンブラックの配合は回避されるが、そのようなポリウレタンエラストマー層24を所望の色に着色するための着色剤や、抗菌作用を付与するための抗菌剤、更には光触媒、紫外線吸収剤等の、公知の添加剤を配合せしめることも可能である。
Furthermore, in the polyurethane
加えて、上記の実施形態においては、ピン26が、タイヤ表面を与えるポリウレタンエラストマー層24,36の外周面よりも外方に、所定の高さだけ突出せしめられた構造とされているが、ピンは、少なくともその端部が、タイヤ表面に露呈しておれば、上述せる如きピンによる滑り止め効果やスリップ防止効果を得ることが可能であり、例えば、図11に示されるように、ピン26の一方の端面が、ピン26の周囲のタイヤ表面と面一とされた構造も、本発明において採用され得ることとなる。なお、このような構造の雪道用再生ソリッドタイヤ68を製造するに際しては、注型装置の外型として、上例の如き収容孔54が何等設けられていない内面を有するものが採用されることは、勿論、言うまでもないところである。
In addition, in the above embodiment, the
また、ピン26の形状にあっても、上述せる如き形状に何等限定されるものではなく、従来よりスパイクタイヤに採用されているスパイクピンの公知の各種の形状が、何れも採用され得るのである。例えば、図12に示される如き、ポリウレタンエラストマー層24の厚さに比して長さの短いリベット状のピン70を用いることも可能である。
Moreover, even if it exists in the shape of the
なお、このような長さの短いピンを採用する場合には、上述せるようにラバー層20の外周面22に複数の凹窩40を形成する必要はなく、例えば、図13に示されるように、先ず、複数のピン70を、注型装置42の外型44a〜dの内面52に着脱可能に固定した後、かかる複数のピン70が固定された注型装置42に、摩耗したソリッドラバータイヤ18がセットされる。そして、このようにセットされた状態において、摩耗ソリッドラバータイヤ18のラバー層20の外周面22と外型44の内面52との間の隙間72内に、上例と同様に、所定の常温硬化型のポリウレタン原料60が注入されて、常温下において反応硬化せしめられることにより、ラバー層20の外周に、ポリウレタンエラストマー層24が一体的に形成され、以て、図12に示される如き雪道用再生ソリッドタイヤ74が製造されることとなる。
When such a short pin is employed, it is not necessary to form a plurality of
また、上例の雪道用再生ソリッドタイヤ66にあっては、周方向及び幅方向に所定の間隔をあけて、24本(周方向)×3本(幅方向)、計72本のピン26が埋設されていたが、ピン26の本数や配設位置は、タイヤの用途等に応じて、適宜に設定され得るものであり、上例の本数や配設位置に何等限定されるものではない。
In the above-described recycled
さらに、タイヤ外周面には、必要に応じて、各種のトレッドパターンが形成され得る。なお、かかるトレッドパターンは、例えば、タイヤ外周面を与えるポリウレタンエラストマー層の注型成形時に、所望とするトレッドパターンに対応する内面を有する外型が用いられたり、或いは、注型成形後、タイヤ外周面に対して、所定の切削加工が施される等して、形成されることとなる。 Furthermore, various tread patterns may be formed on the tire outer peripheral surface as necessary. As the tread pattern, for example, an outer mold having an inner surface corresponding to a desired tread pattern is used at the time of cast molding of a polyurethane elastomer layer that gives a tire outer peripheral surface, or after cast molding, The surface is formed by performing a predetermined cutting process or the like.
その他、一々列挙はしないが、本発明は、当業者の知識に基づいて種々なる変形、修正、改良等を加えた態様において、実施され得るものであり、また、そのような実施の態様が、本発明の趣旨を逸脱しない限りにおいて、何れも、本発明の範疇に属するものであることが、理解されるべきである。 In addition, although not enumerated one by one, the present invention can be carried out in a mode to which various variations, modifications, improvements, and the like are added based on the knowledge of those skilled in the art. It should be understood that all belong to the scope of the present invention without departing from the spirit of the present invention.
10 ソリッドラバータイヤ 12 ホイール
14 トレッドウェアインジケータ 16 トレッド部
18 ソリッドラバータイヤ 20 ラバー層
22 外周面 24 ポリウレタンエラストマー層
26,70 ピン 28 外周面
30,38,66,68,74 雪道用再生ソリッドタイヤ
32,34 端部 36 第二の層
40 凹窩 42 注型装置
44 外型 50 内型
52 内面 54 収容孔
56,72 隙間 58 注入装置
60 ポリウレタン原料 62 一体成形品
64 湾曲部
DESCRIPTION OF
Claims (8)
The regenerated solid tire for snowy road according to claim 7, wherein a polyurethane elastomer layer with adjusted hardness is formed by introducing air into the polyurethane raw material, finely dispersing it, and then reacting and curing it. Manufacturing method.