JP2005075912A - Coating agent, building material, paper, film, food-packaging material, food-packaging container, and tableware - Google Patents

Coating agent, building material, paper, film, food-packaging material, food-packaging container, and tableware Download PDF

Info

Publication number
JP2005075912A
JP2005075912A JP2003307301A JP2003307301A JP2005075912A JP 2005075912 A JP2005075912 A JP 2005075912A JP 2003307301 A JP2003307301 A JP 2003307301A JP 2003307301 A JP2003307301 A JP 2003307301A JP 2005075912 A JP2005075912 A JP 2005075912A
Authority
JP
Japan
Prior art keywords
coating agent
coating
oxide
film
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2003307301A
Other languages
Japanese (ja)
Inventor
Takashi Ogi
喬 尾木
Kyohei Ueda
恭平 上田
Masaki Shibata
正樹 芝田
Hitoshi Mizutani
均 水谷
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GIFU SERATSUKU SEIZOSHO KK
Original Assignee
GIFU SERATSUKU SEIZOSHO KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GIFU SERATSUKU SEIZOSHO KK filed Critical GIFU SERATSUKU SEIZOSHO KK
Priority to JP2003307301A priority Critical patent/JP2005075912A/en
Publication of JP2005075912A publication Critical patent/JP2005075912A/en
Pending legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a coating agent, a building material, paper, a film, a food-packaging material, a food-packaging container and a tableware, having effects for inhibiting the diffusion of a sick building syndrome material, a harmful chemical material or an odor-generating material, and adsorbing and decomposing the material, and facilitating the disposal treatment because of having biodegradability. <P>SOLUTION: The coating agent is produced by mixing 24.5 pts. wt. shellac, 75 pts. wt. ethanol, 0.25 pts. wt. additive containing silver oxide and 0.25 pts. wt. carnauba, and dissolving and dispersing the mixture. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

本発明は、例えば、建材等の表面に塗布するコーティング剤、建材、紙、フィルム、食品包装材、食品包装容器、及び食器に関する。   The present invention relates to a coating agent, a building material, paper, a film, a food packaging material, a food packaging container, and tableware applied to the surface of a building material, for example.

従来より、建材からホルムアルデヒド等のシックハウス物質や、臭気発生物質が放散されることが知られている。それらシックハウス物質や臭気発生物質の放散を抑制するために、建材の表面に合成樹脂を主成分とする塗料を塗布する技術が用いられてきた（特許文献１参照）。   Conventionally, it is known that thick house substances such as formaldehyde and odor generating substances are diffused from building materials. In order to suppress the diffusion of these sick house substances and odor generating substances, a technique of applying a paint mainly composed of a synthetic resin to the surface of building materials has been used (see Patent Document 1).

また、建材に、シックハウス物質や、臭気発生物質を分解、低減、抑制する効果のある添加物を含浸、混入、塗布する方法が知られている。
特開平１０−２５１５６５号公報 In addition, there is known a method of impregnating, mixing, and applying an additive having an effect of decomposing, reducing, or suppressing a sick house substance or an odor generating substance on a building material.
Japanese Patent Laid-Open No. 10-251565

しかし、建材などの表面に、上記の塗料を塗布する方法では、十分にシックハウス物質や臭気発生物質の放散を抑制することができないという問題があった。   However, the above-described method of applying the paint to the surface of a building material has a problem that it is not possible to sufficiently suppress the dissipation of sick house materials and odor generating materials.

また、建材の表面に塗布する塗料は、生分解性がないことから、塗料を塗布した建材の廃棄処分が困難であるという環境面での問題があった。   In addition, since the paint applied to the surface of the building material is not biodegradable, there is an environmental problem that it is difficult to dispose of the building material to which the paint is applied.

更に、建材に、シックハウス物質や臭気発生物質を分解、低減、抑制する効果のある添加物を含浸、混入、塗布する方法では、効果が局部的、一次的であるという問題があった。   Furthermore, the method of impregnating, mixing, and applying an additive having the effect of decomposing, reducing, and suppressing the sick house substance and the odor generating substance on the building material has a problem that the effect is local and primary.

本発明は以上の点に鑑みなされたものであり、シックハウス物質や臭気発生物質の放散を抑制、及び吸着・分解する効果があり、生分解性を有することにより廃棄処分が容易であるコーティング剤、建材、紙、フィルム、食品包装材、食品包装容器、及び食器を提供することを目的とする。   The present invention has been made in view of the above points, and has the effect of suppressing the emission of sick house materials and odor generating materials, and the effect of adsorbing and decomposing, and the coating agent that is easy to dispose by having biodegradability, The object is to provide building materials, paper, films, food packaging materials, food packaging containers, and tableware.

（１）請求項１の発明は、
セラック（脱色セラックや白色セラックを含む）、ロジン、サンダラック、ゴマラカリマオ、アカロイド、カルナバロウ、ミツロウ、キャンデリラロウ、イボタロウ、セラックワックス、ライスワックス、ラノリンの中から選ばれる一種以上から成る天然樹脂成分と、銀、銀イオン、酸化銀、ヨウ素、ヨウ素包接デキストリン誘導体、マグネシウム、酸化マグネシウム、亜鉛、酸化亜鉛、酸化チタン、酸化アルミニウム、酸化チタン系光触媒の中から選ばれる一種以上から成る添加物成分と、を含むことを特徴とするコーティング剤を要旨とする。 (1) The invention of claim 1
Natural resin component consisting of at least one selected from shellac (including decolorized shellac and white shellac), rosin, sandalak, sesame kalimao, acaloid, carnauba wax, beeswax, candelilla wax, ibotarou, shellac wax, rice wax, lanolin An additive component comprising at least one selected from silver, silver ions, silver oxide, iodine, iodine inclusion clathrin dextrin derivative, magnesium, magnesium oxide, zinc, zinc oxide, titanium oxide, aluminum oxide, and titanium oxide photocatalyst The gist of the present invention is a coating agent comprising:

本発明のコーティング剤を、例えば、木材などの建材、紙、フィルム、食品包装材、食品包装容器、又は食器の表面に塗布すると、建材等の表面に塗膜が形成される。建材等に含まれるホルムアルデヒド等のシックハウス物質や臭気物質は、この塗膜を透過する際に、塗膜中に含まれる添加物成分と接触し、化学的に分解される。従って、本発明のコーティング剤を用いれば、建材等からのシックハウス物質や臭気物質の放散を抑制、及び吸着・分解することができる。さらに、空気中に含まれるシックハウス物質や臭気物質も、塗膜中に含まれる添加物成分と接触し、化学的に分解される。   When the coating agent of the present invention is applied to the surface of a building material such as wood, paper, film, food packaging material, food packaging container, or tableware, for example, a coating film is formed on the surface of the building material or the like. Sick house substances such as formaldehyde and odorous substances contained in building materials and the like are chemically decomposed when they pass through the coating film and come into contact with additive components contained in the coating film. Therefore, if the coating agent of the present invention is used, it is possible to suppress, adsorb and decompose the emission of sick house substances and odorous substances from building materials and the like. Furthermore, the sick house substance and odor substance contained in the air also come into contact with the additive components contained in the coating film and are chemically decomposed.

また、塗膜中の添加物成分は抗菌抗カビ効果も奏するので、本発明のコーティング剤を用いれば、建材等に、抗菌抗カビ性を付与することができる。   Moreover, since the additive component in the coating film also exhibits antibacterial and antifungal effects, the antibacterial and antifungal properties can be imparted to building materials and the like by using the coating agent of the present invention.

また、本発明のコーティング剤は、天然樹脂成分を主成分としており、この天然樹脂成分は生分解性が高い。そのため、本実施例のコーティング剤自体も生分解性が高く、環境に影響を与えることなく廃棄することが可能である。また、本発明のコーティング剤は、焼却処分も可能である。   Moreover, the coating agent of this invention has a natural resin component as a main component, and this natural resin component has high biodegradability. Therefore, the coating agent itself of this example is also highly biodegradable and can be discarded without affecting the environment. The coating agent of the present invention can be incinerated.

更に、このコーティング剤を使用した建材、紙、フィルム、食品包装材、食品包装容器、及び食器もまた、環境に影響を与えることなく廃棄することができる。   Furthermore, building materials, papers, films, food packaging materials, food packaging containers, and tableware using this coating agent can also be discarded without affecting the environment.

・添加物成分として酸化チタン又は酸化チタン系光触媒を含む場合、それらの配合量は、全固形分に対して、０．００５〜１０．０重量％の割合が好ましい。   -When titanium oxide or a titanium oxide photocatalyst is included as an additive component, the blending amount thereof is preferably 0.005 to 10.0% by weight with respect to the total solid content.

・本発明のコーティング剤には、その他の成分として、例えば、ポリエチレン、ポリプロピレン等のポリオレフィン、マイクロクリスタリンワックスパラフィンワックス等のワックスを配合することができる。
（２）請求項２の発明は、
合成樹脂を含むことを特徴とする請求項１に記載のコーティング剤を要旨とする。 -In the coating agent of this invention, waxes, such as polyolefin, such as polyethylene and a polypropylene, a microcrystalline wax paraffin wax, can be mix | blended as another component, for example.
(2) The invention of claim 2
The gist of the coating agent according to claim 1, comprising a synthetic resin.

本発明のコーティング剤は、合成樹脂を含むことにより、造膜性の向上、耐水性、耐熱性、耐溶剤性付与、経時安定性向上、分散性向上、着色等の効果を奏する。   By including the synthetic resin, the coating agent of the present invention has the effects of improving the film forming property, imparting water resistance, heat resistance, solvent resistance, improving temporal stability, improving dispersibility, coloring, and the like.

・前記合成樹脂としては、例えば、アクリル樹脂等が挙げられる。
（３）請求項３の発明は、
合成樹脂成分と、銀、銀イオン、酸化銀、ヨウ素、ヨウ素包接デキストリン誘導体、マグネシウム、酸化マグネシウム、亜鉛、酸化亜鉛、酸化チタン、酸化アルミニウム、酸化チタン系光触媒の中から選ばれる一種以上から成る添加物成分と、を含むことを特徴とするコーティング剤を要旨とする。 -As said synthetic resin, an acrylic resin etc. are mentioned, for example.
(3) The invention of claim 3
Composed of synthetic resin component and one or more selected from silver, silver ion, silver oxide, iodine, iodine clathrate dextrin derivative, magnesium, magnesium oxide, zinc, zinc oxide, titanium oxide, aluminum oxide, titanium oxide photocatalyst The gist of the coating agent is characterized by containing an additive component.

本発明のコーティング剤を、例えば、木材などの建材、紙、フィルム、食品包装材、食品包装容器、及び食器の表面に塗布すると、建材等の表面に塗膜が形成される。建材等に含まれるホルムアルデヒド等のシックハウス物質や臭気物質は、この塗膜を透過する際に、塗膜中に含まれる添加物成分と接触し、化学的に分解される。従って、本発明のコーティング剤を用いれば、建材等からのシックハウス物質や臭気物質の放散を抑制、及び吸着・分解することができる。さらに、空気中に含まれるシックハウス物質や臭気物質も、塗膜中に含まれる添加物成分と接触し、化学的に分解される。   When the coating agent of the present invention is applied to the surface of, for example, building materials such as wood, paper, film, food packaging materials, food packaging containers, and tableware, a coating film is formed on the surfaces of the building materials and the like. Sick house substances such as formaldehyde and odorous substances contained in building materials and the like are chemically decomposed when they pass through the coating film and come into contact with additive components contained in the coating film. Therefore, if the coating agent of the present invention is used, it is possible to suppress, adsorb and decompose the emission of sick house substances and odorous substances from building materials and the like. Furthermore, the sick house substance and odor substance contained in the air also come into contact with the additive components contained in the coating film and are chemically decomposed.

また、塗膜中の添加物成分は抗菌抗カビ効果も奏するので、本発明のコーティング剤を用いれば、建材等に、抗菌抗カビ性を付与することができる。   Moreover, since the additive component in the coating film also exhibits antibacterial and antifungal effects, the antibacterial and antifungal properties can be imparted to building materials and the like by using the coating agent of the present invention.

・前記合成樹脂としては、例えば、アクリル樹脂等が挙げられる。
（４）請求項４の発明は、
全固形分に対する前記添加物成分の割合が０．００２〜１０重量％の範囲内であることを特徴とする請求項１〜３のいずれかに記載のコーティング剤を要旨とする。 -As said synthetic resin, an acrylic resin etc. are mentioned, for example.
(4) The invention of claim 4
The gist of the coating agent according to any one of claims 1 to 3, wherein the ratio of the additive component to the total solid content is in the range of 0.002 to 10% by weight.

本発明のコーティング剤は、コーティング剤全量に対する添加物成分の割合が０．００２重量％以上であるので、シックハウス物質や臭気物質の放散を抑制、及び吸着・分解する効果や、抗菌抗カビ効果が十分高い。また、コーティング剤全量に対する添加物成分の割合が１０重量％以下であるので、経済性において優れている。尚、コーティング剤全量に対する添加物成分の割合が１０重量％を超えても、シックハウス物質や臭気物質の放散を防止する効果や抗菌抗カビ効果は大きく変わらない。   The coating agent of the present invention has an additive component ratio of 0.002% by weight or more based on the total amount of the coating agent. High enough. Moreover, since the ratio of the additive component with respect to the total amount of the coating agent is 10% by weight or less, it is excellent in economic efficiency. In addition, even if the ratio of the additive component with respect to the total amount of the coating agent exceeds 10% by weight, the effect of preventing the release of the sick house substance and the odorous substance and the antibacterial and antifungal effect are not greatly changed.

特に、添加物成分に銀または酸化銀が含まれる場合は、その配合量は、全固形分に対して、０．００２〜４．０重量％（特に好ましくは、０．００４〜１重量％）の割合が好ましい。   In particular, when silver or silver oxide is contained in the additive component, the blending amount is 0.002 to 4.0% by weight (particularly preferably 0.004 to 1% by weight) based on the total solid content. Is preferred.

また、添加物成分に亜鉛が含まれる場合は、その配合量は、全固形分に対して、０．００２〜１．０重量％の割合が好ましい。   Moreover, when zinc is contained in an additive component, the compounding quantity has a preferable ratio of 0.002-1.0 weight% with respect to the total solid.

また、添加物成分に酸化亜鉛が含まれる場合は、その配合量は、全固形分に対して、０．００２〜１．０重量％の割合が好ましい。   Moreover, when zinc oxide is contained in an additive component, the compounding quantity has the preferable ratio of 0.002-1.0 weight% with respect to the total solid.

また、添加物成分に酸化アルミニウムが含まれる場合は、その配合量は、全固形分に対して、０．００２〜１．０重量％の割合が好ましい。   Moreover, when an aluminum oxide is contained in an additive component, the compounding quantity has the preferable ratio of 0.002-1.0 weight% with respect to the total solid.

また、添加物成分にヨウ素、またはヨウ素包接デキストリン誘導体（例えばシクロデキストリンヨウ素包接体）が含まれる場合は、その配合量は、全固形分に対して、０．００５〜１０．０重量％の割合が好ましい。
（５）請求項５の発明は、
アルコール系溶剤又は水から成る溶媒を含むことを特徴とする請求項１〜４のいずれかに記載のコーティング剤を要旨とする。 When the additive component contains iodine or an iodine inclusion dextrin derivative (for example, a cyclodextrin iodine inclusion complex), the blending amount is 0.005 to 10.0% by weight based on the total solid content. Is preferred.
(5) The invention of claim 5
The gist of the coating agent according to any one of claims 1 to 4, which comprises an alcohol solvent or a solvent comprising water.

本発明のコーティング剤は、アルコール系溶剤又は水から成る溶媒を含むことにより、例えば、液状の剤形を有している。そのため、建材等の基材に塗布することが容易である。   The coating agent of this invention has a liquid dosage form by including the solvent which consists of alcohol solvent or water, for example. Therefore, it is easy to apply to a base material such as a building material.

・前記アルコール系溶剤としては、例えば、エタノール、メタノール、プロピルアルコール、ブタノール等が挙げられる。
（６）請求項６の発明は、
請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする建材を要旨とする。 -Examples of the alcohol solvent include ethanol, methanol, propyl alcohol, butanol and the like.
(6) The invention of claim 6
A gist is a building material comprising a coating layer made of the coating agent according to claim 1.

本発明の建材は、例えば、その表面の全部又は一部を覆うように、請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えている。そのため、建材の中にシックハウス物質や臭気物質を含む場合でも、それらの物質はコーティング層を透過する際に添加物成分により分解されるので、外部へのシックハウス物質や臭気物質の放散を低減することができる。   The building material of this invention is provided with the coating layer which consists of a coating agent in any one of Claims 1-5 so that the whole or a part of the surface may be covered, for example. Therefore, even if building materials contain sick house substances and odorous substances, these substances are decomposed by additive components when permeating the coating layer, so the emission of sick house substances and odorous substances to the outside should be reduced. Can do.

また、本発明の建材は、コーティング層に含まれる添加物成分により抗菌抗カビ効果を奏する。   Moreover, the building material of this invention has an antibacterial and antifungal effect by the additive component contained in a coating layer.

更に、本発明の建材は、天然樹脂を主成分とする、生分解性の高いコーティング剤からなるコーティング層を備えている場合は、環境に影響を与えることなく廃棄することが可能である。更に、本発明の建材は、焼却処分をすることが可能である。   Furthermore, when the building material of the present invention is provided with a coating layer made of a natural resin as a main component and made of a highly biodegradable coating agent, it can be discarded without affecting the environment. Furthermore, the building material of the present invention can be incinerated.

・前記建材としては、例えば、巾木、ドアパネル、天井板、パネル、壁材、クロス等の内装材が挙げられる。
（７）請求項７の発明は、
請求項１〜７の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする紙を要旨とする。 -As said building material, interior materials, such as a baseboard, a door panel, a ceiling board, a panel, a wall material, a cloth, are mentioned, for example.
(7) The invention of claim 7
A gist is a paper comprising a coating layer comprising the coating agent according to claim 1.

本発明の紙は、例えば、その表面の全部又は一部を覆うように、請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えている。そのため、紙の中にシックハウス物質、有害化学物質、または臭気物質を含む場合でも、それらの物質はコーティング層を透過する際に分解されるので、外部へのシックハウス物質、有害化学物質、及び臭気物質の放散を低減することができる。   The paper of this invention is provided with the coating layer which consists of a coating agent in any one of Claims 1-5 so that the whole or a part of the surface may be covered, for example. For this reason, even if sick paper, toxic chemicals, or odorous substances are included in the paper, these substances are decomposed when passing through the coating layer. Can be reduced.

また、本発明の紙は、コーティング層に含まれる添加物成分により抗菌抗カビ効果を奏する。   Moreover, the paper of the present invention exhibits an antibacterial and antifungal effect due to the additive component contained in the coating layer.

更に、本発明の紙は、天然樹脂を主成分とする、生分解性の高いコーティング剤からなるコーティング層を備えている場合は、環境に影響を与えることなく廃棄することが可能である。更に、本発明の紙は、焼却処分をすることが可能である。   Furthermore, when the paper of the present invention is provided with a coating layer made of a natural resin as a main component and made of a highly biodegradable coating agent, it can be discarded without affecting the environment. Furthermore, the paper of the present invention can be incinerated.

・前記紙としては、例えば、各種包装紙、壁紙、敷き紙の用途に用いられる紙がある。
（８）請求項８の発明は、
請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とするフィルムを要旨とする。 -As said paper, there exist paper used for the use of various wrapping papers, wallpaper, and laying paper, for example.
(8) The invention of claim 8
A gist comprising a coating layer comprising the coating agent according to claim 1.

本発明のフィルムは、例えば、その表面の全部又は一部を覆うように、請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えている。そのため、フィルムの中にシックハウス物質、有害化学物質、または臭気物質を含む場合でも、それらの物質はコーティング層を透過する際に分解されるので、外部へのシックハウス物質、有害化学物質、及び臭気物質の放散を低減することができる。   The film of this invention is provided with the coating layer which consists of a coating agent in any one of Claims 1-5 so that the whole or a part of the surface may be covered, for example. Therefore, even if the film contains sick house substances, hazardous chemical substances, or odorous substances, those substances are decomposed when passing through the coating layer, so the sick house substances, harmful chemical substances, and odorous substances to the outside Can be reduced.

また、本発明のフィルムは、コーティング層に含まれる添加物成分により抗菌抗カビ効果を奏する。   Moreover, the film of this invention has an antibacterial and antifungal effect by the additive component contained in a coating layer.

更に、本発明のフィルムは、天然樹脂を主成分とする、生分解性の高いコーティング剤からなるコーティング層を備えている場合は、環境に影響を与えることなく廃棄することが可能である。更に、本発明のフィルムは、焼却処分をすることが可能である。   Furthermore, the film of the present invention can be discarded without affecting the environment when it is provided with a coating layer composed of a natural resin as a main component and made of a coating agent having high biodegradability. Furthermore, the film of the present invention can be incinerated.

・前記フィルムの素材としては、例えば、ポリエチレン、ポリプロピレン、ポリエステル、ポリカーボネート、ポリビニールアルコール、エチレンビニールアルコール共重合体、サラン樹脂、ナイロン、塩化ビニリデン、塩化ビニール、ポリ乳酸、複合フィルム、アルミ蒸着フィルム等があり、フィルムの用途としては、各種包装フィルム、ビニールクロス、テーブルクロス、保護フィルムがある。
（９）請求項９の発明は、
請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする食品包装材（食品包装容器も含む）を要旨とする。 As the material of the film, for example, polyethylene, polypropylene, polyester, polycarbonate, polyvinyl alcohol, ethylene vinyl alcohol copolymer, saran resin, nylon, vinylidene chloride, vinyl chloride, polylactic acid, composite film, aluminum vapor deposition film, etc. As film applications, there are various packaging films, vinyl cloths, table cloths, and protective films.
(9) The invention of claim 9
A gist is a food packaging material (including a food packaging container) comprising a coating layer comprising the coating agent according to any one of claims 1 to 5.

本発明の食品包装材は、例えば、その表面の全部又は一部を覆うように、請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えている。そのため、食品包装材の中に有害化学物質や臭気物質を含む場合でも、それらの物質はコーティング層を透過する際に分解されるので、外部への有害化学物質や臭気物質の放散を低減することができる。   The food packaging material of this invention is provided with the coating layer which consists of a coating agent in any one of Claims 1-5 so that the whole or a part of the surface may be covered, for example. Therefore, even if harmful chemical substances or odorous substances are included in the food packaging material, these substances are decomposed when permeating the coating layer, thus reducing the emission of harmful chemical substances and odorous substances to the outside. Can do.

また、本発明の食品包装材は、コーティング層に含まれる添加物成分により抗菌抗カビ効果を奏する。   In addition, the food packaging material of the present invention exhibits an antibacterial and antifungal effect due to the additive component contained in the coating layer.

更に、本発明の食品包装材は、天然樹脂を主成分とする、生分解性の高いコーティング剤からなるコーティング層を備えている場合は、環境に影響を与えることなく廃棄することが可能である。更に、本発明の食品包装材は、焼却処分をすることが可能である。   Furthermore, the food packaging material of the present invention can be disposed of without affecting the environment when it has a coating layer made of a natural resin as a main component and made of a highly biodegradable coating agent. . Furthermore, the food packaging material of the present invention can be incinerated.

・前記食品包装材または食品包装容器の素材としては、例えば、ポリエチレン、ポリプロピレン、ポリエステル、ポリカーボネート、ポリビニールアルコール、エチレンビニールアルコール共重合体、サラン樹脂、ナイロン、塩化ビニリデン、塩化ビニール、ポリ乳酸、複合フィルム、アルミ蒸着フィルム、アルミ等の金属、ウレタン樹脂、紙、複合紙、セルロース、プラスチック、セラミック、木、樹脂等が挙げられる。
（１０）請求項１０の発明は、
請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする食器を要旨とする。 -Examples of the food packaging material or food packaging container include polyethylene, polypropylene, polyester, polycarbonate, polyvinyl alcohol, ethylene vinyl alcohol copolymer, Saran resin, nylon, vinylidene chloride, vinyl chloride, polylactic acid, and composite Examples thereof include films, aluminum vapor deposition films, metals such as aluminum, urethane resins, paper, composite paper, cellulose, plastics, ceramics, wood, and resins.
(10) The invention of claim 10
A gist is provided with a coating layer comprising the coating agent according to any one of claims 1 to 5.

本発明の食器は、例えば、その表面の全部又は一部を覆うように、請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えている。そのため、食器の中に有害化学物質や臭気物質を含む場合でも、それらの物質はコーティング層を透過する際に分解されるので、外部への有害化学物質や臭気物質の放散を低減することができる。   The tableware of this invention is provided with the coating layer which consists of a coating agent in any one of Claims 1-5 so that all or a part of the surface may be covered, for example. Therefore, even if the tableware contains harmful chemical substances or odorous substances, these substances are decomposed when passing through the coating layer, so the emission of harmful chemical substances and odorous substances to the outside can be reduced. .

また、本発明の食器は、コーティング層に含まれる添加物成分により抗菌抗カビ効果を奏する。   Moreover, the tableware of this invention has an antibacterial and antifungal effect by the additive component contained in a coating layer.

更に、本発明の食器は、天然樹脂を主成分とする、生分解性の高いコーティング剤からなるコーティング層を備えている場合は、環境に影響を与えることなく廃棄することが可能である。更に、本発明の食器は、焼却処分をすることが可能である。   Furthermore, when the tableware of the present invention is provided with a coating layer made of a natural resin as a main component and made of a coating agent having high biodegradability, it can be discarded without affecting the environment. Furthermore, the tableware of the present invention can be incinerated.

以下に本発明のコーティング剤、建材、紙、フィルム、食品包装材、食品包装容器、及び食器の形態の例（実施例）を説明する。   Examples (Examples) of forms of the coating agent, building material, paper, film, food packaging material, food packaging container, and tableware of the present invention will be described below.

ａ）表１に示す組成(単位は重量部）に従い、各成分を混合・溶解及び分散することにより、実施例１−１〜１−５のコーティング剤及び比較例のコーティング剤を製造した。   a) According to the composition shown in Table 1 (units are parts by weight), the respective components were mixed, dissolved, and dispersed to prepare the coating agents of Examples 1-1 to 1-5 and the comparative example.

Figure 2005075912
表１において、ＰＥＡＲＬ−Ｎ８１１（商品名、（株）岐阜セラツク製造所製）は、脱色セラック（天然樹脂成分）である。
Figure 2005075912
 In Table 1, PEARL-N811 (trade name, manufactured by Gifu Serask Manufacturing Co., Ltd.) is decolorizing shellac (natural resin component).

また、ゼオミック（商品名、（株）シナネンゼオミック製）は、添加物成分である酸化銀を約２重量％の割合で含む抗菌性ゼオライトである。   Zeomic (trade name, manufactured by Sinanen Zeomic Co., Ltd.) is an antibacterial zeolite containing silver oxide as an additive component at a ratio of about 2% by weight.

実施例１−１では、上記のゼオミックを全固形分（溶媒であるエタノール以外の成分）に対して１重量％の割合で含む。従って、実施例１−１のコーティング剤は、全固形分に対する添加物成分（酸化銀）の割合が０．０２重量％であり、請求項４の発明の範囲内である。   In Example 1-1, the above-mentioned zeomic is included at a ratio of 1% by weight with respect to the total solid content (components other than ethanol as a solvent). Therefore, in the coating agent of Example 1-1, the ratio of the additive component (silver oxide) to the total solid content is 0.02% by weight, and is within the scope of the invention of claim 4.

実施例１−２では、全固形分に対する添加物成分（酸化銀）の割合が０．００２重量％であり、請求項４の発明の範囲内である。   In Example 1-2, the ratio of the additive component (silver oxide) to the total solid content is 0.002% by weight, which is within the scope of the invention of claim 4.

実施例１−３では、全固形分に対する添加物成分（酸化銀）の割合が１．０重量％であり、請求項４の発明の範囲内である。   In Example 1-3, the ratio of the additive component (silver oxide) to the total solid content is 1.0% by weight, which is within the scope of the invention of claim 4.

実施例１−４では、全固形分に対する添加物成分（酸化銀）の割合が０．００１重量％であり、請求項１の発明の範囲内ではあるが、請求項４の発明の範囲外である。   In Example 1-4, the ratio of the additive component (silver oxide) to the total solid content is 0.001% by weight, which is within the scope of the invention of claim 1, but outside the scope of the invention of claim 4. is there.

実施例１−５では、全固形分に対する添加物成分（酸化銀）の割合が１．１重量％であり、請求項１の発明の範囲内であるが、請求項４の発明の範囲外である。   In Example 1-5, the ratio of the additive component (silver oxide) to the total solid content is 1.1 wt%, which is within the scope of the invention of claim 1, but outside the scope of the invention of claim 4. is there.

ｂ）次に、前記ａ）で製造した実施例１−１〜１−５のコーティング剤及び比較例のコーティング剤を、建材、紙、フィルム、食品包装材、食品包装容器、及び食器の表面に塗布し、コーティング層を備えた建材、紙、フィルム、食品包装材、食品包装容器、及び食器を製造した。   b) Next, the coating agents of Examples 1-1 to 1-5 manufactured in a) and the coating agent of the comparative example are applied to the surfaces of building materials, paper, films, food packaging materials, food packaging containers, and tableware. The building material, paper, film, food packaging material, food packaging container, and tableware provided with the coating layer were applied.

塗布量は、２０ｇ／ｍ2とした。塗布方法は、刷毛塗り、スプレー塗布、ディップ法等を用いることができる。 The coating amount was 20 g / m 2 . As the coating method, brush coating, spray coating, dipping method, or the like can be used.

ここで、フィルムとは、ポリエチレン、ポリプロピレン、ポリエステル、ポリカーボネート、ポリビニールアルコール、エチレンビニールアルコール共重合体、サラン樹脂、ナイロン、塩化ビニリデン、塩化ビニール、ポリ乳酸、複合フィルム、アルミ蒸着フィルム等から成るフィルムであり、食品包装材及び食品包装容器とは、ポリエチレン、ポリプロピレン、ポリエステル、ポリカーボネート、ポリビニールアルコール、エチレンビニールアルコール共重合体、サラン樹脂、ナイロン、塩化ビニリデン、塩化ビニール、ポリ乳酸、複合フィルム、アルミ蒸着フィルム、アルミ等の金属、ウレタン樹脂、紙、複合紙、セルロース、プラスチック、セラミック、木、樹脂等からなるものである。   Here, the film is a film made of polyethylene, polypropylene, polyester, polycarbonate, polyvinyl alcohol, ethylene vinyl alcohol copolymer, saran resin, nylon, vinylidene chloride, vinyl chloride, polylactic acid, composite film, aluminum vapor deposition film, etc. Food packaging materials and food packaging containers are polyethylene, polypropylene, polyester, polycarbonate, polyvinyl alcohol, ethylene vinyl alcohol copolymer, Saran resin, nylon, vinylidene chloride, vinyl chloride, polylactic acid, composite film, aluminum It is made of a vapor-deposited film, a metal such as aluminum, urethane resin, paper, composite paper, cellulose, plastic, ceramic, wood, resin or the like.

ｃ）次に、本実施例のコーティング剤、建材、紙、フィルム、食品包装材、食品包装容器、及び食器の奏する効果を説明する。   c) Next, the effects of the coating agent, building material, paper, film, food packaging material, food packaging container, and tableware of this example will be described.

(i)本実施例のコーティング剤を木材などの建材、紙、フィルム、食品包装材、食品包装容器、及び食器の表面に塗布すると、建材等の表面に塗膜（コーティング層）が形成される。建材等に含まれるホルムアルデヒド等のシックハウス物質や臭気物質は、この塗膜を透過する際に、塗膜中に含まれる添加物成分と接触し、化学的に分解される。従って、本発明のコーティング剤を用いれば、建材等からのシックハウス物質や臭気物質の放散を抑制、及び吸着・分解することができる。   (i) When the coating agent of this embodiment is applied to the surface of building materials such as wood, paper, film, food packaging materials, food packaging containers, and tableware, a coating film (coating layer) is formed on the surface of the building materials. . Sick house substances such as formaldehyde and odorous substances contained in building materials and the like are chemically decomposed when they pass through the coating film and come into contact with additive components contained in the coating film. Therefore, if the coating agent of the present invention is used, it is possible to suppress, adsorb and decompose the emission of sick house substances and odorous substances from building materials and the like.

(ii)本実施例のコーティング剤は、天然樹脂成分を主成分としており、この天然樹脂成分は生分解性が高い。そのため、本実施例のコーティング剤自体も生分解性が高く、環境に影響を与えることなく廃棄することが可能である。また、本実施例のコーティング剤は、焼却処分も可能である。   (ii) The coating agent of this example has a natural resin component as a main component, and this natural resin component has high biodegradability. Therefore, the coating agent itself of this example is also highly biodegradable and can be discarded without affecting the environment. Moreover, the coating agent of a present Example can also be incinerated.

更に、このコーティング剤を使用した建材、紙、フィルム、食品包装材、食品包装容器、及び食器もまた、環境に影響を与えることなく廃棄することができる。   Furthermore, building materials, papers, films, food packaging materials, food packaging containers, and tableware using this coating agent can also be discarded without affecting the environment.

(iii)本実施例のコーティング剤を木材などの建材、紙、フィルム、食品包装材、食品包装容器、及び食器の表面に塗布すると、建材等の表面に塗膜（コーティング層）が形成される。この塗膜は、その中に添加物成分を含むことにより、抗菌抗カビ効果を奏する。従って、本発明のコーティング剤を用いれば、建材等に抗菌抗カビ効果を奏することができる。   (iii) When the coating agent of this embodiment is applied to the surface of building materials such as wood, paper, film, food packaging material, food packaging container, and tableware, a coating film (coating layer) is formed on the surface of the building material. . This coating film has an antibacterial and antifungal effect by including an additive component therein. Therefore, if the coating agent of the present invention is used, an antibacterial and antifungal effect can be exerted on building materials and the like.

表２に示す組成(単位は重量部）に従い、各成分を混合・溶解及び分散することにより、各種の天然樹脂を含む実施例２−１〜２−７のコーティング剤を製造した。   According to the composition shown in Table 2 (units are parts by weight), the components of Examples 2-1 to 2-7 containing various natural resins were produced by mixing, dissolving, and dispersing each component.

Figure 2005075912
表２において、ＧＳＮ（商品名、（株）岐阜セラツク製造所製）は、セラック（天然樹脂成分）である。また、ＧＢＮ−Ｄ（商品名、（株）岐阜セラツク製造所製）は、白色セラック（天然樹脂成分）である。
Figure 2005075912
 In Table 2, GSN (trade name, manufactured by Gifu Serask Manufacturing Co., Ltd.) is shellac (natural resin component). GBN-D (trade name, manufactured by Gifu Serask Manufacturing Co., Ltd.) is white shellac (natural resin component).

実施例２−１〜２−７のコーティング剤では、全固形分に対する割合が１重量％となるように、ゼオミックを含んでいる、そして、ゼオミックは、２重量％の割合で酸化銀（添加物成分）を含んでいる。従って、実施例２−１〜２−７のコーティング剤では、全固形分に対する割合が０．０２重量％となるように酸化銀を含んでおり、請求項４の発明の範囲内である。   In the coating agents of Examples 2-1 to 2-7, zeomic was included so that the ratio to the total solid content was 1 wt%, and zeomic was silver oxide (additive) at a ratio of 2 wt%. Component). Therefore, the coating agents of Examples 2-1 to 2-7 contain silver oxide so that the ratio to the total solid content is 0.02% by weight, and are within the scope of the invention of claim 4.

本実施例２−１〜２−７のコーティング剤は、前記実施例１と同様の効果を奏する。   The coating agents of Examples 2-1 to 2-7 have the same effects as those of Example 1.

表３に示す組成(単位は重量部）に従い、各成分を混合・溶解及び分散することにより、各種の天然樹脂を含む実施例３−１〜３−５のコーティング剤を製造した。   According to the composition shown in Table 3 (unit is parts by weight), the components were mixed, dissolved, and dispersed to produce the coating agents of Examples 3-1 to 3-5 containing various natural resins.

Figure 2005075912
実施例３−１〜３−５のコーティング剤では、全固形分に対する割合が１重量％となるように、ゼオミックを含んでいる、そして、ゼオミックは、２重量％の割合で酸化銀（添加物成分）を含んでいる。従って、実施例２−１〜２−７のコーティング剤では、全固形分に対する割合が０．０２重量％となるように酸化銀を含んでおり、請求項４の発明の範囲内である。
Figure 2005075912
 In the coating agents of Examples 3-1 to 3-5, zeomic was included so that the ratio to the total solid content was 1% by weight, and zeomic was silver oxide (additive) at a ratio of 2% by weight. Component). Therefore, the coating agents of Examples 2-1 to 2-7 contain silver oxide so that the ratio to the total solid content is 0.02% by weight, and are within the scope of the invention of claim 4.

本実施例３−１〜３−５のコーティング剤は、前記実施例１と同様の効果を奏する。   The coating agents of Examples 3-1 to 3-5 have the same effects as those of Example 1.

表４に示す組成(単位は重量部）に従い、各成分を混合・溶解及び分散することにより、各種の添加剤成分を含む実施例４−１〜４−５のコーティング剤を製造した。   According to the composition shown in Table 4 (unit is part by weight), the coating agents of Examples 4-1 to 4-5 containing various additive components were produced by mixing, dissolving, and dispersing each component.

Figure 2005075912
表４において、ノバロン（商品名、東亜合成（株））は、銀（添加物成分）を約４重量％の割合で含む。また、バクテキラー（商品名、カネボウ化成（株）製）は、銀（添加物成分）を約２〜３重量％の割合で含み、亜鉛（添加物成分）を約５重量％の割合で含む。また、シーバイオ（商品名、（株）海水化学研究所製）は、酸化亜鉛（添加物成分）を数重量％の割合で含む。また、ＣＤＩ（商品名、日宝化学（株）製）は、シクロデキストリンヨウ素包接体（添加物成分）を５〜２０重量％の割合で含む。また、アパタイト被覆酸化チタン（（株）ノナミサイエンス製）は、酸化チタン（添加物成分）を約６０重量％の割合で含む。
Figure 2005075912
 In Table 4, Novalon (trade name, Toa Gosei Co., Ltd.) contains silver (additive component) at a ratio of about 4% by weight. Bactekiller (trade name, manufactured by Kanebo Kasei Co., Ltd.) contains silver (additive component) in a proportion of about 2 to 3% by weight and zinc (additive component) in a proportion of about 5% by weight. Sea Bio (trade name, manufactured by Seawater Chemical Research Co., Ltd.) contains zinc oxide (additive component) at a ratio of several weight percent. Moreover, CDI (trade name, manufactured by Niho Chemical Co., Ltd.) contains cyclodextrin iodine inclusion bodies (additive components) at a ratio of 5 to 20% by weight. Apatite-coated titanium oxide (manufactured by Nonami Science Co., Ltd.) contains titanium oxide (additive component) at a ratio of about 60% by weight.

本実施例４−１〜４−５のコーティング剤は、前記実施例１と同様の効果を奏する。   The coating agents of Examples 4-1 to 4-5 have the same effects as those of Example 1.

表５に示す組成(単位は重量部）に従い、各成分を混合・溶解及び分散することにより、各種の添加剤成分を２種類以上含む実施例５−１〜５−６のコーティング剤、及び比較例のコーティング剤を製造した。   According to the composition shown in Table 5 (unit is parts by weight), the coating agents of Examples 5-1 to 5-6 containing two or more kinds of various additive components by mixing, dissolving and dispersing each component, and comparison An example coating agent was prepared.

Figure 2005075912
本実施例５−１〜５−６のコーティング剤は、前記実施例１と同様の効果を奏する。
Figure 2005075912
 The coating agents of Examples 5-1 to 5-6 have the same effects as those of Example 1.

表６に示す組成(単位は重量部）に従い、各成分を混合・溶解及び分散することにより、実施例６−１〜６−３のコーティング剤を製造した。   The coating agents of Examples 6-1 to 6-3 were produced by mixing, dissolving, and dispersing each component in accordance with the composition shown in Table 6 (unit: parts by weight).

Figure 2005075912
実施例６−１〜６−２のコーティング剤は、合成樹脂（アクリル樹脂）を含み、請求項２の発明の範囲内である。また、実施例６−３のコーティング樹脂は、天然樹脂を含まずに合成樹脂を含み、請求項３の発明の範囲内である。
Figure 2005075912
 The coating agents of Examples 6-1 to 6-2 include a synthetic resin (acrylic resin) and are within the scope of the invention of claim 2. Further, the coating resin of Example 6-3 does not include a natural resin but includes a synthetic resin, and is within the scope of the invention of claim 3.

本実施例６−１〜６−３のコーティング剤は、生分解性を除き、前記実施例１と同様の効果を奏する。   The coating agents of Examples 6-1 to 6-3 have the same effects as those of Example 1 except for biodegradability.

次に、実施例１−１及び実施例４−３のコーティング剤による、抗菌抗カビ効果を確かめるために行った実験について説明する。   Next, the experiment conducted in order to confirm the antibacterial and antifungal effect by the coating agent of Example 1-1 and Example 4-3 is demonstrated.

実験方法は、抗菌試験については、ＪＩＳ Ｚ ２８０１の方法に準拠した。試験結果を表７に示す。この表７において対照とは、菌液のみによる試験である。また、「セラックのみ」とは、コーティング剤を添加するのではなく、セラックのみを添加した試験である。また、「＞１０」は、菌を検出しなかったことを示す。   The experiment method conformed to the method of JIS Z 2801 for the antibacterial test. The test results are shown in Table 7. In Table 7, the control is a test using only the bacterial solution. In addition, “only shellac” is a test in which only a shellac is added, not a coating agent. Further, “> 10” indicates that no bacteria were detected.

Figure 2005075912
表７に示すように、実施例１−１のコーティング剤を用いた場合は、黄色ブドウ球菌及び大腸菌が顕著に減少しており、抗菌効果が高いことが確かめられた。これに対し、セラックのみを添加した場合及び対照の場合では、黄色ブドウ球菌の数は殆ど同等であり、大腸菌は増加していた。
Figure 2005075912
 As shown in Table 7, when the coating agent of Example 1-1 was used, Staphylococcus aureus and Escherichia coli were significantly reduced, and it was confirmed that the antibacterial effect was high. In contrast, when only shellac was added and in the case of the control, the number of Staphylococcus aureus was almost the same, and Escherichia coli increased.

尚、本発明は前記実施例になんら限定されるものではなく、本発明を逸脱しない範囲において種々の態様で実施しうることはいうまでもない。   Needless to say, the present invention is not limited to the above-described embodiments, and can be implemented in various modes without departing from the scope of the present invention.

Claims (10)

セラック、ロジン、サンダラック、ゴマラカリマオ、アカロイド、カルナバロウ、ミツロウ、キャンデリラロウ、イボタロウ、セラックワックス、ライスワックス、ラノリンの中から選ばれる一種以上から成る天然樹脂成分と、
銀、銀イオン、酸化銀、ヨウ素、ヨウ素包接デキストリン誘導体、マグネシウム、酸化マグネシウム、亜鉛、酸化亜鉛、酸化チタン、酸化アルミニウム、酸化チタン系光触媒の中から選ばれる一種以上から成る添加物成分と、を含むことを特徴とするコーティング剤。 Natural resin component consisting of at least one selected from shellac, rosin, sandalak, sesame kalimao, acaloid, carnauba wax, beeswax, candelilla wax, ibotarou, shellac wax, rice wax, lanolin;
An additive component consisting of one or more selected from silver, silver ions, silver oxide, iodine, iodine clathrate dextrin derivative, magnesium, magnesium oxide, zinc, zinc oxide, titanium oxide, aluminum oxide, and titanium oxide photocatalyst; The coating agent characterized by including. 合成樹脂を含むことを特徴とする請求項１に記載のコーティング剤。   The coating agent according to claim 1, comprising a synthetic resin. 合成樹脂成分と、
銀、銀イオン、酸化銀、ヨウ素、ヨウ素包接デキストリン誘導体、マグネシウム、酸化マグネシウム、亜鉛、酸化亜鉛、酸化チタン、酸化アルミニウム、酸化チタン系光触媒の中から選ばれる一種以上から成る添加物成分と、を含むことを特徴とするコーティング剤。 A synthetic resin component;
An additive component consisting of one or more selected from silver, silver ions, silver oxide, iodine, iodine clathrate dextrin derivative, magnesium, magnesium oxide, zinc, zinc oxide, titanium oxide, aluminum oxide, titanium oxide photocatalyst, The coating agent characterized by including. 全固形分に対する前記添加物成分の割合が０．００２〜１０重量％の範囲内であることを特徴とする請求項１〜３のいずれかに記載のコーティング剤。   The ratio of the said additive component with respect to total solid content exists in the range of 0.002 to 10 weight%, The coating agent in any one of Claims 1-3 characterized by the above-mentioned. アルコール系溶剤又は水から成る溶媒を含むことを特徴とする請求項１〜４のいずれかに記載のコーティング剤。   The coating agent according to claim 1, comprising an alcohol solvent or a solvent comprising water. 請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする建材。   A building material comprising a coating layer comprising the coating agent according to claim 1. 請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする紙。   A paper comprising a coating layer comprising the coating agent according to any one of claims 1 to 5. 請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とするフィルム。   A film comprising a coating layer comprising the coating agent according to claim 1. 請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする食品包装材。   A food packaging material comprising a coating layer comprising the coating agent according to claim 1. 請求項１〜５の何れかに記載のコーティング剤からなるコーティング層を備えることを特徴とする食器。   Tableware provided with the coating layer which consists of a coating agent in any one of Claims 1-5.
JP2003307301A 2003-08-29 2003-08-29 Coating agent, building material, paper, film, food-packaging material, food-packaging container, and tableware Pending JP2005075912A (en)