JP2005003878A

JP2005003878A - Conductive belt

Info

Publication number: JP2005003878A
Application number: JP2003166514A
Authority: JP
Inventors: Katsumi Terakawa; 克美寺川; Toshio Kamata; 敏生鎌田
Original assignee: Sumitomo Rubber Industries Ltd
Current assignee: Sumitomo Rubber Industries Ltd
Priority date: 2003-06-11
Filing date: 2003-06-11
Publication date: 2005-01-06
Anticipated expiration: 2023-06-11
Also published as: JP3884726B2

Abstract

<P>PROBLEM TO BE SOLVED: To provide a conductive belt showing properties excellent in elasticity modulus, electric resistance and hardness, etc., as a belt for a wet-developing system electrophotographic device. <P>SOLUTION: The conductive belt has a two-layer structure constituted of a resin base layer 1A and a fluororubber elastic layer 1B arranged on the outer peripheral side of the base layer 1A, conductive agent material is applied on both the base layer and the elastic layer, the base layer is constituted so that the tensile modulus of elasticity is ≥2000MPa, the surface electric resistance of the inner peripheral surface is ≥10<SP>6</SP>Ω/sq. and ≤10<SP>12</SP>Ω/sq. , and the elastic layer is constituted so that the hardness A according to JIS is ≥30 and ≤70, and the volume resistivity is ≥10<SP>6</SP>Ωcm and ≤10<SP>12</SP>Ωcm. <P>COPYRIGHT: (C)2005,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、導電性ベルトに関し、詳しくは、湿式現像方式の電子写真装置用の中間転写ベルトとして好適に用いられるものである。
【０００２】
【従来の技術】
複写機、プリンター、ファクシミリ等の電子写真方式の画像形成装置の中間転写ベルト等に用いられる導電性ベルトは、カーボンブラック等の導電性フィラーにより導電性が付与される場合と、ウレタンゴム、アクリロニトリルブタジエンゴム（ＮＢＲ）、エピクロルヒドリンゴム等のイオン導電性ゴムやイオン導電剤により導電性が付与される場合とがある。
【０００３】
例えば、特開平８−１１０７１１号公報（特許文献１）では、電子導電性フィラーの配合によって体積抵抗率が調整された電子導電系半導電性合成樹脂材料を用いて形成した電子導電系半導電層と、イオン導電剤の配合によって体積抵抗率が調整されたイオン導電系半導電性材料を用いて形成したイオン導電系半導電層とを積層せしめて構成した導電性プラスチックベルトが提案されている。
【０００４】
また、最近のプリンター等の高速化に対処してベルトスピードの変化を少なくするために、ベルトの高弾性率化が要求されている。そこで、本出願人は、特開２００２−２２９３４５号公報（特許文献２）では、引張弾性率が５００ＭＰａ以上で電子導電性を有し、且つ体積抵抗率を１０^６〜１０^１１Ω・ｃｍとした樹脂製のベース層と、ＪＩＳＡ硬度が７０以下でイオン導電性を有し体積抵抗率を１０^８〜１０^１４Ω・ｃｍとしたエラストマー製の中間層と、非電子導電性であり樹脂製の表面コーティング層とを備えた３層構造の導電性ベルトを提案している。
【０００５】
【特許文献１】
特開平８−１１０７１１号公報
【０００６】
【特許文献２】
特開２００２−２２９３４５号公報
【０００７】
【発明が解決しようとする課題】
しかしながら、特許文献１では、電気的特性の経時変化が低減されているものの、ベルトが、トナーと溶媒とを含む液体現像剤を使用する湿式画像形成装置の中間転写ベルトに用いられると、液体現像剤の溶媒によりベルトの各層が膨潤し、著しく耐久性が悪くなるという問題がある。
【０００８】
一方、特許文献２の導電性ベルトは、高弾性率のベース層を備えておりベルトスピードの変化を少なくしているものの、ブレードによる表面クリーニングや転写時の圧力等により、表面コーティング層が摩耗したり剥離したりすることも考えられ、ベルト表面の耐久性において未だ改善の余地がある。
【０００９】
以上のように、導電性ベルトには、液体現像剤の溶媒による膨潤が生じず、かつ、中間転写ベルト等として用いた場合に、良好な転写性を実現する電気特性が要求されている。
【００１０】
本発明は上記した問題に鑑みてなされたものであり、湿式現像方式の電子写真装置用のベルトとして用いた場合に、その外周面からベルト内部への溶媒の進入が低減され、長期に渡って優れた耐久性が得られる導電性ベルトを提供することを課題としている。
【００１１】
【課題を解決するための手段】
上記課題を解決するため、本発明は、樹脂製のベース層と、該ベース層の外周側に配置されるゴム製の弾性層とからなる２層構造とし、
上記ベース層は、ポリイミド樹脂又はポリアミドイミド樹脂を用いて形成され、導電性フィラーにより導電性が付与された電子導電性とし、
上記弾性層は、フッ素ゴムを用いて形成され、導電性フィラーにより導電性が付与された電子導電性とし、
上記ベース層は、引張弾性率を２０００ＭＰａ以上５０００ＭＰａ以下とし、内周面の表面電気抵抗率を１０^６Ω／□以上１０^１２Ω／□以下とし、かつ、
上記弾性層は、ＪＩＳＡ硬度を３０以上７０以下とし、体積抵抗率を１０^６Ω・ｃｍ以上１０^１２Ω・ｃｍ以下としていることを特徴とする導電性ベルトを提供している。
【００１２】
上記本発明の導電性ベルトでは、表面にコーテイング層を設けずに、弾性層を表面層としているため厚み方向に柔軟性を有し、かつ、表面コーテイング層を設けた場合に発生するブレードによる表面クリーニング、転写時の圧力により表面コーテイング層が摩耗したり剥離したりする従来の問題を解決することができる。特に、表面の弾性層をフッ素ゴムを用いて形成されているため、湿式現像方式の電子写真装置の中間転写ベルトとして用いた場合、パラフィン溶媒等の液体現像剤の溶媒に対して安定し、溶媒に対する膨潤率を低減することができる。
【００１３】
さらに、ベース層は、ポリイミド樹脂又はポリアミドイミド樹脂を用いて形成されているため、適度な剛性を有しておりベルト使用時にベルトに伸びが生じることもない。
このため、フッ素ゴムを用いて形成される弾性層をベース層の外周面上に配置した２層構造とすると、厚み方向に対する柔軟性とベルト強度を維持しながら、接触による表面の摩耗が極力抑えられ、長期に渡って良好な耐久性を実現することができる。
【００１４】
また、ベース層及び弾性層は、導電性フィラーにより導電性が付与された電子導電性であるため、フッ素ゴムやポリイミド樹脂又はポリアミドイミド樹脂の上記性能を低下させることなく、所望の表面電気抵抗率や体積抵抗率に調整することを可能としている。
以上より、上記弾性層と、上記ベース層とからなる２層構造の本発明の導電性ベルトは、電気特性を維持しながら、優れた耐久性を実現することができる。
【００１５】
上記弾性層は、液体現像剤の溶媒に対する膨潤率を３％以下としていることが好ましい。
上記範囲とすると、ベルトの外周面からベルト内部への溶媒の進入が低減され、溶媒による膨潤及び外周面の機械的な劣化を防止でき、優れた耐久性を得ることができる。また、ベース層の該溶媒に対する膨潤率は３％以下が好ましい。なお、従来公知の液体現像剤の溶媒の中でも、パラフィン溶媒は、比較的低コストで、安全性、臭気性にも優れているため好適である。
【００１６】
ベース層の引張弾性率を２０００ＭＰａ以上５０００ＭＰａ以下とすることにより、ベルトの伸びが押さえられ、ベルトスピードの変化を少なくすることができると共に、画像の色ずれを防止することができ良好な画像を得ることができる。また、ベース層の内周面の表面電気抵抗率を１０^６Ω／□以上１０^１２Ω／□以下とすることにより、転写後にベルトに残存する電荷を効率良く除却する作用が働き、残存電荷が画像形成に及ぼす悪影響を防止することができる。
【００１７】
上記弾性層のＪＩＳＡ硬度を３０以上７０以下とすることにより、転写ニップ幅が大きく、かつ良好な体積抵抗率を実現でき、表面が粗いラフ紙に対しても良好な転写特性を得ることができ、良好な画像を得ることができる。
また、弾性層の体積抵抗率を１０^６Ω・ｃｍ以上１０^１２Ω・ｃｍ以下とすることにより、画像形成装置の中間転写ベルト等の導電性ベルトとして好適な電気特性を有することとなり、良好な画像を得ることができる。
【００１８】
ベース層及び弾性層に配合される導電性フィラーとしては、ケッチェンブラック、ファーネスブラック、アセチレンブラック等のカーボンブラック、酸化亜鉛、酸化鉄、酸化チタン、チタン酸カリウム、アンチモンドープ酸化チタン、酸化スズ、グラファイト等の導電性金属酸化物、カーボン繊維等が挙げられる。
上記範囲の表面電気抵抗率や体積抵抗率を付与するために配合する導電性フィラーの量は、導電性フィラーの種類やベース層として用いられる樹脂にもよるが、樹脂又はゴムの固形分１００重量部に対して１重量部〜５０重量部、さらには３重量部〜４０重量部が好ましい。なお、液状の樹脂又はゴム中に配合する場合には、分散剤を配合し導電性フィラーを均一に分散していることが好ましい。
【００１９】
弾性層は、液状フッ素ゴムをベース層の外周面に塗工し加熱硬化して形成されていることが好ましい。これにより、均一な厚みで強度も良好な弾性層とすることができる。特に、ディスペンサーにより、塗布する原料をノズルの先端から連続的に供給して均一な厚みに塗布することが好ましい。その他、弾性層の塗工方法としては、ロールコータ、バーコート、スプレーコート、静電塗装、ディップコート等による方法も挙げられる。
【００２０】
また、ベース層は、ポリイミド樹脂又はポリアミドイミド樹脂の前駆体溶液を上記同様に金型の外周面に塗工し加熱硬化して形成していることが好ましい。ベース層は、その他、遠心成形や押出成形等により形成することもできる。
【００２１】
ベース層と弾性層とは、プライマーを介して接着しても良く、これにより、良好な密着性を得ることができる。具体的には、弾性層を塗布形成する前に、ベース層の表面にプライマーを塗布しておくことが好ましい。
【００２２】
ベース層の厚みは５０μｍ〜１５０μｍ、さらには７０μｍ〜１１０μｍであるのが好ましい。弾性層の厚みは２５μｍ〜４００μｍ、さらには５０μｍ〜３００μｍであるのが好ましい。これにより、ベルト全体として良好な柔軟性と強度が得られる上に、ベース層と弾性層との接着性も良好なものとなる。なお、弾性層の厚みは、ベース層の厚みよりも大きい方が好ましい。
【００２３】
弾性層の外周面の表面粗さはＲｚは２μｍ以下が好ましい。これにより、残留トナーのクリーニング性をより良好なものとすることができる。表面粗さＲｚとは、ＪＩＳＢ０６０１に定義された材料の表面粗さを表すパラメータである。
【００２４】
上記のように本発明の導電性ベルトは、液体現像剤の溶媒に対する膨潤率が小さく耐久性に優れ、長期に渡り高画質を得ることができるため、湿式画像形成装置の中間転写ベルトとして好適に用いることができる。その他、画像形成装置の転写ベルト、定着ベルト、現像ベルト、搬送ベルト等として用いることもできる。
【００２５】
【発明の実施の形態】
以下、本発明の実施形態を図面を参照して説明する。
図１は、本発明の第１実施形態の導電性ベルト１を示す。
導電性ベルト１の全体形状は略円筒状であるが、可撓性に富んでおり自重等で自在に変形し得るので、種々の形状となり得る。図１では、２つの軸間に張設された場合が想定された全体形状、即ち、進行方向における断面が略長円形状を示している。導電性ベルト１を中間転写ベルトとして用いた場合、外周面１ａにトナーが付着し、内周面１ｂはベルトの回転中に駆動軸や従動軸等と直接接触する。
【００２６】
導電性ベルト１は、図１（Ｂ）に示すように、樹脂製のベース層１Ａと、ベース層１Ａの外周側に配置されるゴム製の弾性層１Ｂとからなる２層構造としている。
【００２７】
ベース層１Ａは、ポリアミドイミド樹脂を用いて形成され、引張弾性率を２７００ＭＰａとし、適度な剛性を有し、導電性フィラーであるカーボンブラックにより導電性が付与された電子導電性であり、内周面の表面電気抵抗率を１．５８×１０^１０Ω／□としている。また、ベース層１Ａは、パラフィン溶媒に対する膨潤率が０．２％であり、厚みは８０μｍとしている。ベース層１Ａは、ポリアミドイミドワニスにカーボンブラックを均一に分散させたものを円筒状金型の外周面に塗工し加熱硬化して形成されている。
【００２８】
弾性層１Ｂは、フッ素ゴムを用いて形成され、ＪＩＳＡ硬度を６５とし、導電性フィラーであるカーボンブラックにより導電性が付与された電子導電性であり、体積抵抗率を３．１６×１０^１１Ω・ｃｍとしている。弾性層１Ｂは、パラフィン溶媒に対する膨潤率が２．２％であり、厚みは２００μｍとしている。弾性層１Ｂは、溶媒に溶解させた液状フッ素ゴムにカーボンブラックを均一に分散させたものをベース層の外周面に塗工し加熱硬化して形成されている。
【００２９】
以下、本発明の導電性ベルトの製造方法について詳述する。
まず、導電性を付与するためにカーボンブラックと分散剤を添加したポリアミドイミド樹脂の前駆体溶液からなる原料Ａを予め調整しておく。
この原料Ａを原料供給手段であるディスペンサーのノズルの先端から、円筒状の金型の外周面に連続的に供給し、金型を回転させながら、ノズルを金型の軸線方向に移動させて、原料Ａを金型の外周面の所要範囲に均一な厚みで塗布する。該方法により金型の外周面上に塗布された原料Ａを２５０℃で２時間、金型を回転させながら加熱して硬化させてベース層を得る。
【００３０】
次に、導電性を付与するためにカーボンブラックと分散剤を添加したフッ素ゴム溶液からなる原料Ｂを、上記ベース層の外周面に、上記同様の方法により均一な厚みで塗布する。ベース層の外周面上に塗布された原料Ｂを１５０℃で１時間、金型を回転させながら加熱して硬化させて弾性層を得る。
このようにベース層と弾性層とからなる２層構造のベルトを金型上に形成した後、常温まで冷却後、金型から脱型して導電性ベルトを作製している。
【００３１】
図２は、電子写真方式の湿式画像形成装置１０の模式図であり、本発明の導電性ベルトを中間転写ベルト１１として用いている。
湿式画像形成装置１０は、中間転写ベルト１１、感光体１２、感光体１２を帯電させる帯電器１３、画像を画像形成媒体１７に定着させる定着ローラ１４、４色の液体現像剤１５（１５ａ、１５ｂ、１５ｃ、１５ｄ）、画像形成媒体供給トレー１６、感光体１２上を洗浄するクリーニングブレード１８、転写ローラ１９を備えている。本実施形態では、液体現像剤１５の溶媒をパラフィン系オイルとしている。
【００３２】
湿式画像形成装置１０によって画像が形成される場合、まず、感光体１２が図中の矢印の方向に回転し、感光体１２が帯電器１３により帯電された後に、レーザーＬが感光体１２の非画像部を露光して除電され、画線部に相当する部分が帯電した状態になる。
次に、液体現像剤１５ａが感光体１２上に供給されて、帯電画線部に液体現像剤１５ａが付着し１色目の画像が形成される。この液体現像剤１５ａの画像は中間転写ベルト１１上へ転写する。同様にして、感光体１２上に形成された液体現像剤１５ｂ〜１５ｄの各色の画像が中間転写ベルト１１上に転写され、中間転写ベルト１１上に４色の液体現像剤１５（１５ａ〜１５ｄ）からなるフルカラー画像が一旦形成される。
その後、画像形成媒体供給トレー１６から画像形成媒体１７が送られ、このフルカラー画像は、転写ローラ１９により中間転写ベルト１１から、画像形成媒体１７上へ転写される。その後、所定の温度に加熱されている定着ローラ１４を通過することで画像が画像形成媒体１７の表面へ定着される。
【００３３】
本発明の導電性ベルトである中間転写ベルト１１は、ベース層の引張弾性率が高い上に、弾性層は優れた柔軟性を有しており、表面粗さが大きいラフ紙等への転写性能も良好であり、良好な画像を得ることができる。また、液体現像剤の溶媒に対する膨潤率も小さいため、長期に渡って使用を繰り返しても溶媒によりベルトが膨潤することがなく、良好な耐久性を実現することができる。
【００３４】
以下、本発明の導電性ベルトの実施例、比較例について詳述する。
【００３５】
（実施例１）
表１に記載のベース層▲１▼と弾性層▲１▼とからなる２層構造の導電性ベルトとした。ベース層▲１▼は、トリメリット酸とジフェニルメタンジイソシアネートから合成したポリアミドイミドワニスにカーボンブラック及び分散剤を配合しビーズミルで均一に分散させたものを円筒状金型に塗工し加熱硬化して形成した。カーボンブラックは樹脂固形分１００重量部に対して２０重量部配合した。
弾性層▲１▼は、溶媒に溶解させたフッ素ゴム（ダイキン工業（株）製、ＤＰＳ−２３１ＲＤ）にカーボンブラック及び分散剤を配合しビーズミルで均一に分散させたものをベース層１の外周面に塗工し加熱硬化して形成した。カーボンブラックはゴム固形分１００重量部に対して１８重量部配合した。
上記実施形態と同様の方法で導電性ベルトを作製した。なお、後述する方法により各層の物性値を評価した。
【００３６】
【表１】

【００３７】
（比較例１）
表２に記載のベース層▲１▼と弾性層▲２▼と表層▲１▼とからなる３層構造の導電性ベルトとした。
ベース層▲１▼は、実施例１と同様とした。
弾性層▲２▼は、ポリプロピレングリコールとトリレンジイソシアネートより得られるＮＣＯ含有量６．９％の末端イソシアネートプレポリマーとを主剤とし、芳香族ジアミン及びポリプロピレングリコールを硬化剤とする２液硬化型のウレタンゴムをベース層▲１▼の外周面に塗工し加熱硬化して形成した。
表層▲１▼は、ポリテトラメチレンエーテルグリコールとジイソシアネートを主成分とするポリウレタンディスパージョンにフッ素ポリマーディスパージョンを配合した水系塗料を弾性層２の外周面に静電塗装で形成した。
ベース層と弾性層は実施例１と同様の方法で形成した。なお、後述する方法により各層の物性値を評価した。
【００３８】
【表２】

【００３９】
（各層のパラフィン溶媒に対する膨潤性）
各層をパラフィン溶媒の一種であるｎ−デカンに２３℃、２４時間浸漬したときの体積膨潤率を、「パラフィン溶媒に対する膨潤率（％）」として評価した。結果を表３に示す。
【００４０】
【表３】

【００４１】
（ベルト耐久試験結果）
実施例１と比較例１の各導電性ベルトの外周面の一部をパラフィン溶媒に接液した状態でウレタン製のブレードを接触させながらベルトを回転させて、各ベルトの表層となる弾性層▲１▼及び表層▲１▼の変化を観察した。結果を表４に示す。
【００４２】
【表４】

【００４３】
（引張弾性率の測定）
ＡＳＴＭＤ−８８２に準拠した方法で測定した。
【００４４】
（表面電気抵抗率の測定）
ＪＩＳＫ６９１１に準拠した方法で測定した。
【００４５】
（体積抵抗率の測定）
三菱化学（株）製、高抵抗率計ハイレスターＵＰを用いて、２３℃相対湿度５５％の恒温恒湿条件下で測定した。測定方法は、ＪＩＳＫ６９１１に記載の体積抵抗率の測定方法に従い、測定時の印加電圧は５００Ｖとした。
【００４６】
（硬度）
ＪＩＳＡ硬度は、ＪＩＳＫ６２５３「加硫ゴム及び熱可塑性ゴムの硬さ試験方法」の規定に従い、デュロメータ硬さ試験、タイプＡで試験した。
【００４７】
上記各表の結果に示すように、実施例１は、弾性層がフッ素ゴムを用いて形成され、パラフィン溶媒に対する膨潤率が小さいため、ベルトの外周面からベルト内部への溶媒の進入を低減することができ、長期に渡って優れた耐久性を得ることができる。
【００４８】
一方、比較例１は、表層の膨潤率が大きいため、ベルトの外周面からベルト内部への溶媒の進入を抑制できず表層が溶媒により膨潤して強度が低下し、耐久性試験において１００回の回転で表層に剥離が生じた。
【００４９】
【発明の効果】
以上の説明より明らかなように、本発明によれば、ベルトは剛性を有するベース層と、その外周面上に配置する弾性層との２層構造とし、弾性層の表面にコーテイング層を設けていないため、該コーテイング層の摩耗、剥離による耐久性の低下は生じない。
また、外層とされる弾性層をフッ素ゴムを用いて形成しているため、パラフィン溶媒等の液体現像剤の溶媒に対して安定しており、該溶媒によるベルトの膨潤を低減することができ、長期に渡って良好な耐久性を実現することができる。かつ、フッ素ゴムは、耐摩耗性にも優れる上に、摩擦係数も低減することができ、トナーの離型性にも優れている。
さらに、ベース層は、ポリイミド樹脂又はポリアミドイミド樹脂を用いて形成されているため、高弾性率であり適度な剛性を有し、ベルトスピードの変化にも対応することができ、ベルト使用時にベルトに伸びが生じることもない。
【００５０】
このため、ゴム弾性を有する弾性層と、剛性を有するベース層からなる２層構造の本発明の導電性ベルトは、電気特性を維持しながら、優れた耐久性を実現することができ、ラフ紙等に対しても良好な転写特性を実現することができる。また、２層構造としているため、３層や４層以上の構造とした導電性ベルトに比べ生産性にも優れている。
【００５１】
従って、本発明の導電性ベルトは、複写機、ファクシミリ、プリンター等の画像形成装置の各種ベルトに有用であり、特に液体現像剤を使用する湿式画像形成装置の中間転写ベルトとして好適に用いることができる。
【図面の簡単な説明】
【図１】（Ａ）は本発明の導電性ベルトの概略斜視図であり、（Ｂ）は図１（Ａ）のＩＩ−ＩＩ線に沿った断面図である。
【図２】湿式画像形成装置の概略構成図である。
【符号の説明】
１導電性ベルト
１Ａベース層
１Ｂ弾性層
１０湿式画像形成装置
１１中間転写ベルト
１２感光体
１９転写ローラ[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a conductive belt, and more specifically, is suitably used as an intermediate transfer belt for a wet developing type electrophotographic apparatus.
[0002]
[Prior art]
Conductive belts used for intermediate transfer belts in electrophotographic image forming apparatuses such as copiers, printers, facsimiles, etc. include cases where conductivity is imparted by conductive fillers such as carbon black, urethane rubber, acrylonitrile butadiene Conductivity may be imparted by an ion conductive rubber such as rubber (NBR) or epichlorohydrin rubber or an ion conductive agent.
[0003]
For example, in JP-A-8-110711 (Patent Document 1), an electronic conductive semiconductive layer formed using an electronic conductive semiconductive synthetic resin material whose volume resistivity is adjusted by blending an electronic conductive filler. There has been proposed a conductive plastic belt formed by laminating an ion conductive semiconductive layer formed using an ion conductive semiconductive material whose volume resistivity is adjusted by blending an ion conductive agent.
[0004]
Also, in order to cope with recent increases in the speed of printers and the like and to reduce changes in belt speed, a higher elastic modulus of the belt is required. In view of this, the present applicant has disclosed in Japanese Patent Application Laid-Open No. 2002-229345 (Patent Document 2) that the tensile elastic modulus is 500 MPa or more and has electronic conductivity, and the volume resistivity is 10 ⁶ to 10 ¹¹ Ω · cm. A base layer made of resin, an intermediate layer made of elastomer having a JIS A hardness of 70 or less and ionic conductivity and a volume resistivity of 10 ⁸ to 10 ¹⁴ Ω · cm, and non-electroconductive and resin-made A three-layered conductive belt with a surface coating layer is proposed.
[0005]
[Patent Document 1]
JP-A-8-110711 [0006]
[Patent Document 2]
Japanese Patent Laid-Open No. 2002-229345
[Problems to be solved by the invention]
However, in Japanese Patent Application Laid-Open No. H10-228707, although the change in electrical characteristics with time is reduced, when the belt is used as an intermediate transfer belt of a wet image forming apparatus using a liquid developer containing a toner and a solvent, liquid development is performed. There is a problem that each layer of the belt swells due to the solvent of the agent and the durability is remarkably deteriorated.
[0008]
On the other hand, although the conductive belt of Patent Document 2 has a base layer with a high elastic modulus and reduces changes in belt speed, the surface coating layer is worn by surface cleaning with a blade or pressure during transfer. There is still room for improvement in the durability of the belt surface.
[0009]
As described above, the conductive belt is required to have electrical characteristics that do not swell due to the solvent of the liquid developer and that realize good transferability when used as an intermediate transfer belt or the like.
[0010]
The present invention has been made in view of the above-described problems, and when used as a belt for an electrophotographic apparatus of a wet development type, the invasion of a solvent from the outer peripheral surface into the belt is reduced, and for a long time. An object of the present invention is to provide a conductive belt capable of obtaining excellent durability.
[0011]
[Means for Solving the Problems]
In order to solve the above problems, the present invention has a two-layer structure comprising a resin base layer and a rubber elastic layer disposed on the outer peripheral side of the base layer,
The base layer is formed using a polyimide resin or a polyamide-imide resin, and has an electronic conductivity imparted with conductivity by a conductive filler,
The elastic layer is made of fluororubber, and has electronic conductivity imparted with conductivity by a conductive filler,
The base layer has a tensile elastic modulus of 2000 MPa to 5000 MPa, a surface electrical resistivity of the inner peripheral surface of 10 ⁶ Ω / □ to 10 ¹² Ω / □, and
The elastic layer provides a conductive belt having a JIS A hardness of 30 to 70 and a volume resistivity of 10 ⁶ Ω · cm to 10 ¹² Ω · cm.
[0012]
In the conductive belt of the present invention, the surface by the blade generated when the surface coating layer is provided because the elastic layer is used as the surface layer without providing a coating layer on the surface, and the surface layer is provided with flexibility in the thickness direction. The conventional problem that the surface coating layer is worn or peeled off by the pressure during cleaning and transfer can be solved. In particular, since the elastic layer on the surface is formed using fluororubber, when used as an intermediate transfer belt of an electrophotographic apparatus of a wet development type, it is stable against a solvent of a liquid developer such as a paraffin solvent. The swelling ratio with respect to can be reduced.
[0013]
Furthermore, since the base layer is formed using a polyimide resin or a polyamideimide resin, the base layer has an appropriate rigidity and does not cause elongation when the belt is used.
For this reason, if a two-layer structure in which an elastic layer formed of fluororubber is arranged on the outer peripheral surface of the base layer, surface wear due to contact is suppressed as much as possible while maintaining flexibility and belt strength in the thickness direction. Therefore, good durability can be realized over a long period of time.
[0014]
Moreover, since the base layer and the elastic layer are electronically conductive with conductivity imparted by a conductive filler, the desired surface electrical resistivity can be obtained without deteriorating the performance of fluororubber, polyimide resin or polyamideimide resin. And volume resistivity can be adjusted.
As described above, the conductive belt of the present invention having a two-layer structure composed of the elastic layer and the base layer can achieve excellent durability while maintaining electric characteristics.
[0015]
The elastic layer preferably has a swelling ratio of the liquid developer with respect to the solvent of 3% or less.
If it is the said range, the approach of the solvent from the outer peripheral surface of a belt to the inside of a belt will be reduced, the swelling by a solvent and the mechanical deterioration of an outer peripheral surface can be prevented, and the outstanding durability can be acquired. The swelling ratio of the base layer with respect to the solvent is preferably 3% or less. Of the conventionally known liquid developer solvents, paraffin solvents are preferable because they are relatively low cost and are excellent in safety and odor.
[0016]
By setting the tensile elastic modulus of the base layer to 2000 MPa or more and 5000 MPa or less, the elongation of the belt can be suppressed, the change in the belt speed can be reduced, and the color shift of the image can be prevented to obtain a good image. be able to. In addition, by setting the surface electrical resistivity of the inner peripheral surface of the base layer to 10 ⁶ Ω / □ or more and 10 ¹² Ω / □ or less, the function of efficiently removing the charge remaining on the belt after transfer works, and the residual charge is reduced. An adverse effect on image formation can be prevented.
[0017]
By setting the JIS A hardness of the elastic layer to 30 or more and 70 or less, a transfer nip width is large and a good volume resistivity can be realized, and good transfer characteristics can be obtained even on rough paper having a rough surface. And a good image can be obtained.
Further, by setting the volume resistivity of the elastic layer to 10 ⁶ Ω · cm or more and 10 ¹² Ω · cm or less, the elastic layer has suitable electrical characteristics as a conductive belt such as an intermediate transfer belt of an image forming apparatus, and is favorable. An image can be obtained.
[0018]
As the conductive filler blended in the base layer and the elastic layer, carbon black such as ketjen black, furnace black, acetylene black, zinc oxide, iron oxide, titanium oxide, potassium titanate, antimony-doped titanium oxide, tin oxide, Examples thereof include conductive metal oxides such as graphite, carbon fibers, and the like.
The amount of the conductive filler blended to give the surface electrical resistivity and volume resistivity in the above range depends on the kind of the conductive filler and the resin used as the base layer, but the solid content of the resin or rubber is 100 weight. The amount is preferably 1 to 50 parts by weight, more preferably 3 to 40 parts by weight with respect to parts. In addition, when mix | blending in liquid resin or rubber | gum, it is preferable to mix | blend a dispersing agent and to disperse | distribute the electroconductive filler uniformly.
[0019]
The elastic layer is preferably formed by applying liquid fluororubber to the outer peripheral surface of the base layer and heating and curing. Thereby, an elastic layer having a uniform thickness and good strength can be obtained. In particular, it is preferable to apply a uniform thickness by continuously supplying the material to be applied from the tip of the nozzle with a dispenser. In addition, examples of the elastic layer coating method include a roll coater, bar coating, spray coating, electrostatic coating, dip coating, and the like.
[0020]
The base layer is preferably formed by applying a precursor solution of polyimide resin or polyamideimide resin to the outer peripheral surface of the mold in the same manner as described above, followed by heat curing. The base layer can also be formed by centrifugal molding, extrusion molding, or the like.
[0021]
The base layer and the elastic layer may be bonded via a primer, whereby good adhesion can be obtained. Specifically, it is preferable to apply a primer to the surface of the base layer before applying and forming the elastic layer.
[0022]
The thickness of the base layer is preferably 50 μm to 150 μm, more preferably 70 μm to 110 μm. The thickness of the elastic layer is preferably 25 μm to 400 μm, more preferably 50 μm to 300 μm. As a result, good flexibility and strength can be obtained as a whole belt, and adhesion between the base layer and the elastic layer is also good. Note that the thickness of the elastic layer is preferably larger than the thickness of the base layer.
[0023]
As for the surface roughness of the outer peripheral surface of the elastic layer, Rz is preferably 2 μm or less. Thereby, the cleaning property of the residual toner can be improved. The surface roughness Rz is a parameter representing the surface roughness of the material defined in JIS B0601.
[0024]
As described above, the conductive belt of the present invention is suitable as an intermediate transfer belt of a wet image forming apparatus because it has a low swelling ratio with respect to the solvent of the liquid developer and is excellent in durability and high image quality can be obtained over a long period of time. Can be used. In addition, it can also be used as a transfer belt, a fixing belt, a developing belt, a conveying belt, or the like of an image forming apparatus.
[0025]
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
FIG. 1 shows a conductive belt 1 according to a first embodiment of the present invention.
Although the overall shape of the conductive belt 1 is substantially cylindrical, it is rich in flexibility and can be freely deformed by its own weight or the like, and thus can have various shapes. In FIG. 1, the overall shape assumed to be stretched between two axes, that is, the cross section in the traveling direction shows a substantially oval shape. When the conductive belt 1 is used as an intermediate transfer belt, toner adheres to the outer peripheral surface 1a, and the inner peripheral surface 1b is in direct contact with a drive shaft, a driven shaft, or the like while the belt is rotating.
[0026]
As shown in FIG. 1B, the conductive belt 1 has a two-layer structure including a resin base layer 1A and a rubber elastic layer 1B disposed on the outer peripheral side of the base layer 1A.
[0027]
The base layer 1A is formed using a polyamide-imide resin, has a tensile elastic modulus of 2700 MPa, has an appropriate rigidity, and is electronically conductive with conductivity imparted by carbon black as a conductive filler. The surface electrical resistivity of the surface is 1.58 × 10 ¹⁰ Ω / □. The base layer 1A has a swelling ratio of 0.2% with respect to the paraffin solvent and a thickness of 80 μm. The base layer 1A is formed by coating a polyamide die varnish with carbon black uniformly dispersed on the outer peripheral surface of a cylindrical mold and heating and curing.
[0028]
The elastic layer 1B is made of fluororubber, has a JIS A hardness of 65, is electroconductive with conductivity imparted by carbon black as a conductive filler, and has a volume resistivity of 3.16 × 10 ^11. Ω · cm. The elastic layer 1B has a swelling rate of 2.2% with respect to the paraffin solvent and a thickness of 200 μm. The elastic layer 1 </ b> B is formed by coating a liquid fluororubber dissolved in a solvent with carbon black uniformly dispersed on the outer peripheral surface of the base layer and heating and curing.
[0029]
Hereinafter, the manufacturing method of the electroconductive belt of this invention is explained in full detail.
First, a raw material A composed of a precursor solution of a polyamideimide resin to which carbon black and a dispersant are added in order to impart conductivity is prepared in advance.
This raw material A is continuously supplied from the tip of the nozzle of the dispenser as the raw material supply means to the outer peripheral surface of the cylindrical mold, and while rotating the mold, the nozzle is moved in the axial direction of the mold, The raw material A is applied to the required range of the outer peripheral surface of the mold with a uniform thickness. The base material is obtained by heating and curing the raw material A applied on the outer peripheral surface of the mold by the method at 250 ° C. for 2 hours while rotating the mold.
[0030]
Next, a raw material B made of a fluororubber solution to which carbon black and a dispersant are added to impart conductivity is applied to the outer peripheral surface of the base layer with a uniform thickness by the same method as described above. The elastic layer is obtained by heating and curing the raw material B applied on the outer peripheral surface of the base layer at 150 ° C. for 1 hour while rotating the mold.
Thus, after forming the belt of the two-layer structure which consists of a base layer and an elastic layer on a metal mold | die, after cooling to normal temperature, it removes from a metal mold | die and the electroconductive belt is produced.
[0031]
FIG. 2 is a schematic diagram of the electrophotographic wet image forming apparatus 10, and the conductive belt of the present invention is used as the intermediate transfer belt 11.
The wet image forming apparatus 10 includes an intermediate transfer belt 11, a photoconductor 12, a charger 13 for charging the photoconductor 12, a fixing roller 14 for fixing an image on an image forming medium 17, and four color liquid developers 15 (15a and 15b). 15c, 15d), an image forming medium supply tray 16, a cleaning blade 18 for cleaning the photosensitive member 12, and a transfer roller 19. In this embodiment, the solvent of the liquid developer 15 is paraffinic oil.
[0032]
When an image is formed by the wet image forming apparatus 10, first, the photoconductor 12 rotates in the direction of the arrow in the figure, and the photoconductor 12 is charged by the charger 13, and then the laser L is not applied to the photoconductor 12. The image portion is exposed to charge and is neutralized, and the portion corresponding to the image portion is charged.
Next, the liquid developer 15a is supplied onto the photoreceptor 12, and the liquid developer 15a adheres to the charged image line portion to form a first color image. The image of the liquid developer 15a is transferred onto the intermediate transfer belt 11. Similarly, each color image of the liquid developers 15b to 15d formed on the photosensitive member 12 is transferred onto the intermediate transfer belt 11, and four color liquid developers 15 (15a to 15d) are transferred onto the intermediate transfer belt 11. A full-color image consisting of is once formed.
Thereafter, the image forming medium 17 is sent from the image forming medium supply tray 16, and the full color image is transferred from the intermediate transfer belt 11 onto the image forming medium 17 by the transfer roller 19. Thereafter, the image is fixed on the surface of the image forming medium 17 by passing through the fixing roller 14 heated to a predetermined temperature.
[0033]
The intermediate transfer belt 11 which is the conductive belt of the present invention has a high tensile elastic modulus of the base layer, and the elastic layer has excellent flexibility, and transfer performance to rough paper or the like having a large surface roughness. And a good image can be obtained. Further, since the swelling ratio of the liquid developer with respect to the solvent is small, the belt does not swell due to the solvent even when the liquid developer is used for a long time, and good durability can be realized.
[0034]
Examples of the conductive belt of the present invention and comparative examples will be described in detail below.
[0035]
(Example 1)
A conductive belt having a two-layer structure comprising a base layer (1) and an elastic layer (1) shown in Table 1 was obtained. Base layer (1) is formed by blending a polyamide imide varnish synthesized from trimellitic acid and diphenylmethane diisocyanate with carbon black and a dispersant, and uniformly dispersing them in a bead mill, and applying them to a cylindrical mold, followed by heat curing. did. Carbon black was blended in an amount of 20 parts by weight based on 100 parts by weight of resin solids.
The elastic layer {circle around (1)} is an outer peripheral surface of the base layer 1 obtained by mixing carbon black and a dispersant in fluororubber (Daikin Kogyo Co., Ltd., DPS-231RD) dissolved in a solvent and uniformly dispersing it with a bead mill. It was formed by coating and heat curing. Carbon black was blended in an amount of 18 parts by weight with respect to 100 parts by weight of rubber solid content.
A conductive belt was produced in the same manner as in the above embodiment. In addition, the physical-property value of each layer was evaluated by the method mentioned later.
[0036]
[Table 1]

[0037]
(Comparative Example 1)
A conductive belt having a three-layer structure comprising a base layer (1), an elastic layer (2), and a surface layer (1) described in Table 2 was obtained.
The base layer (1) was the same as in Example 1.
The elastic layer {circle around (2)} is a two-component curable urethane mainly composed of polypropylene glycol and a terminal isocyanate prepolymer having an NCO content of 6.9% obtained from tolylene diisocyanate, and an aromatic diamine and polypropylene glycol as a curing agent. Rubber was applied to the outer peripheral surface of the base layer (1) and heat-cured to form.
Surface layer (1) was formed by electrostatic coating on the outer peripheral surface of elastic layer 2 with a water-based paint in which a fluoropolymer dispersion was blended with a polyurethane dispersion mainly composed of polytetramethylene ether glycol and diisocyanate.
The base layer and the elastic layer were formed by the same method as in Example 1. In addition, the physical-property value of each layer was evaluated by the method mentioned later.
[0038]
[Table 2]

[0039]
(Swellability of each layer to paraffin solvent)
The volume swelling rate when each layer was immersed in n-decane, which is a kind of paraffin solvent, at 23 ° C. for 24 hours was evaluated as “swelling rate (%) with respect to paraffin solvent”. The results are shown in Table 3.
[0040]
[Table 3]

[0041]
(Result of belt durability test)
An elastic layer serving as a surface layer of each belt by rotating the belt while contacting a urethane blade with a part of the outer peripheral surface of each conductive belt of Example 1 and Comparative Example 1 in contact with a paraffin solvent. Changes in 1 and surface layer (1) were observed. The results are shown in Table 4.
[0042]
[Table 4]

[0043]
(Measurement of tensile modulus)
It measured by the method based on ASTM D-882.
[0044]
(Measurement of surface electrical resistivity)
It measured by the method based on JISK6911.
[0045]
(Measurement of volume resistivity)
Using a high resistivity meter Hi-Lester UP manufactured by Mitsubishi Chemical Corporation, measurement was performed under constant temperature and humidity conditions of 23 ° C. and 55% relative humidity. The measurement method was in accordance with the volume resistivity measurement method described in JIS K6911, and the applied voltage during measurement was 500V.
[0046]
(hardness)
The JIS A hardness was tested with a durometer hardness test, type A, in accordance with the provisions of JIS K6253 “Method for testing hardness of vulcanized rubber and thermoplastic rubber”.
[0047]
As shown in the results of the above tables, in Example 1, the elastic layer is formed using fluororubber, and the swelling rate with respect to the paraffin solvent is small, so that the solvent enters the belt from the outer peripheral surface of the belt. It is possible to obtain excellent durability over a long period of time.
[0048]
On the other hand, in Comparative Example 1, since the swelling rate of the surface layer is large, the penetration of the solvent from the outer peripheral surface of the belt to the inside of the belt cannot be suppressed, and the surface layer is swollen by the solvent and the strength is lowered. The surface layer was peeled off by rotation.
[0049]
【The invention's effect】
As is clear from the above description, according to the present invention, the belt has a two-layer structure of a base layer having rigidity and an elastic layer disposed on the outer peripheral surface thereof, and a coating layer is provided on the surface of the elastic layer. Therefore, the durability of the coating layer is not deteriorated due to wear or peeling.
In addition, since the elastic layer to be the outer layer is formed using fluororubber, it is stable against the solvent of a liquid developer such as a paraffin solvent, and the swelling of the belt by the solvent can be reduced. Good durability can be realized over a long period of time. In addition, the fluororubber is excellent in wear resistance, can reduce a friction coefficient, and is excellent in toner releasability.
Furthermore, since the base layer is formed using a polyimide resin or a polyamide-imide resin, it has a high elastic modulus and appropriate rigidity, and can respond to changes in belt speed. There is no elongation.
[0050]
For this reason, the conductive belt of the present invention having a two-layer structure comprising an elastic layer having rubber elasticity and a base layer having rigidity can achieve excellent durability while maintaining electrical characteristics, Therefore, good transfer characteristics can be realized. Moreover, since it has a two-layer structure, it is excellent in productivity as compared with a conductive belt having a structure of three layers or four layers or more.
[0051]
Therefore, the conductive belt of the present invention is useful for various belts of image forming apparatuses such as copying machines, facsimiles, and printers, and is particularly preferably used as an intermediate transfer belt of a wet image forming apparatus using a liquid developer. it can.
[Brief description of the drawings]
FIG. 1A is a schematic perspective view of a conductive belt of the present invention, and FIG. 1B is a cross-sectional view taken along line II-II in FIG.
FIG. 2 is a schematic configuration diagram of a wet image forming apparatus.
[Explanation of symbols]
DESCRIPTION OF SYMBOLS 1 Conductive belt

1A Base layer

1B Elastic layer 10 Wet image forming apparatus 11 Intermediate transfer belt 12 Photoconductor 19 Transfer roller

Claims

樹脂製のベース層と、該ベース層の外周側に配置されるゴム製の弾性層とからなる２層構造とし、
上記ベース層は、ポリイミド樹脂又はポリアミドイミド樹脂を用いて形成され、導電性フィラーにより導電性が付与された電子導電性とし、
上記弾性層は、フッ素ゴムを用いて形成され、導電性フィラーにより導電性が付与された電子導電性とし、
上記ベース層は、引張弾性率を２０００ＭＰａ以上５０００ＭＰａ以下とし、内周面の表面電気抵抗率を１０^６Ω／□以上１０^１２Ω／□以下とし、かつ、
上記弾性層は、ＪＩＳＡ硬度を３０以上７０以下とし、体積抵抗率を１０^６Ω・ｃｍ以上１０^１２Ω・ｃｍ以下としていることを特徴とする導電性ベルト。A two-layer structure comprising a resin base layer and a rubber elastic layer disposed on the outer peripheral side of the base layer,
The base layer is formed using a polyimide resin or a polyamide-imide resin, and has an electronic conductivity imparted with conductivity by a conductive filler,
The elastic layer is made of fluororubber, and has electronic conductivity imparted with conductivity by a conductive filler,
The base layer has a tensile elastic modulus of 2000 MPa to 5000 MPa, an inner surface electrical resistivity of 10 ⁶ Ω / □ to 10 ¹² Ω / □, and
The conductive belt is characterized in that the elastic layer has a JIS A hardness of 30 to 70 and a volume resistivity of 10 ⁶ Ω · cm to 10 ¹² Ω · cm.

湿式現像方式の電子写真装置の中間転写ベルトとして用いられ、液体現像剤の溶媒に対する上記弾性槽の膨潤率を３％以下としている請求項１に記載の導電製ベルト。2. The conductive belt according to claim 1, which is used as an intermediate transfer belt of an electrophotographic apparatus of a wet development type, and the swelling ratio of the elastic tank with respect to the solvent of the liquid developer is 3% or less.

上記弾性層は、液状フッ素ゴムを上記ベース層の外周面に塗工し加熱硬化して形成されている請求項１または請求項２に記載の導電性ベルト。3. The conductive belt according to claim 1, wherein the elastic layer is formed by applying liquid fluororubber to the outer peripheral surface of the base layer and then heat-curing the elastic layer.