JP2004216217A - Method for manufacturing moisture absorbing/desorbing material - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a method for manufacturing a moisture absorbing/desorbing material having stable quality with good productivity by dispersing a moisture absorbing/desorbing substance in an aqueous resin coating solution to apply the same to a base material without issuing a problem such as the thickening, gelling or the like of the coating solution, requiring excessive quantity of heat or a long drying time for the purpose of drying a coating film after coating or causing the blistering of the coating film after drying. <P>SOLUTION: After the base material is coated with an aqueous resin coating agent having microcapsules, each of which is formed by microencapsulating a moisture absorbing/desorbing medium with a water inpermeable shell, are dispersed therein and the coated base material is dried, at least a part of the shells of the microcapsules is destructed by heating and/or pressurization to expose the encapsulated moisture absorbing/desorbing medium to the outside to develop a moisture absorbing/desorbing capacity. <P>COPYRIGHT: (C)2004,JPO&NCIPI

Description

【０００１】
【発明の属する技術分野】
本発明は、高湿時には環境空気中の水分を吸収する一方、低湿時には吸収していた水分を環境空気中に放散することにより、環境空気中の湿度の変動を緩和する機能を有する吸放湿性材料に関するものであり、特に建築物の内装材などとして有用である。
【０００２】
【従来の技術】
現代の建築物は、鉄筋コンクリート構造やプレハブ工法の普及、樹脂加工合板等の合成材料からなる新建材や扉及び窓における金属サッシの発達等によって、かつての純日本建築と比較すれば著しく気密性の高いものとなっている。係る建築物の高気密性は、冷暖房効果の向上によるエネルギー資源の節約や、防音性の向上による近隣騒音公害の防止などの観点からは、大変に望ましいものであると言うことができる。
【０００３】
しかしその反面、室内における居住者の生活活動（人間の呼気、炊事、風呂・シャワー等）が発生する湿気が、室外に逃げられずに室内に籠もり易く、行き場を失った湿気が壁面や窓ガラス、窓枠サッシ等の表面に結露して、美観上及び触感上望ましくないのみならず、建築材料の汚損や腐蝕の原因となって、建築物の寿命を縮める要因ともなり兼ねないという問題がある。
【０００４】
この問題の解決策としては、建築物に強制換気装置又は空気調和装置等を設置して、室内の湿度を常に一定範囲内に保つ方法なども、一部で研究されてはいるが、廊下や収納空間等も含めた建築物内部全体を対象に強制換気又は空気調和させる為には、初期の設備投資負担が著しく重くなることに加えて、夜間や外出時も含めて設備を２４時間稼働させると電気代の負担も重く、設備の保守点検の手間や費用もかかることから、一般家庭用としてはあまり現実的な方法であるとは考えられていない。
【０００５】
そこで、上記の様な特殊な設備によらずに室内の湿度を調節する方法として、高湿時には環境空気中の水分を吸収する一方、低湿時には吸収していた水分を環境空気中に放散する機能を有する、吸放湿性材料を室内に設置することで、室内の湿度変動を緩和する方法が考案されている。この吸放湿性材料の設置の態様としては種々考えられるが、吸放湿機能を迅速且つ十分に発揮するためには、環境空気と接触する表面積が大きいほど有利であると考えられることから、建築物の室内において大きな表面積を占める壁面や天井面等を、吸放湿性材料を使用した壁紙等の内装材で仕上げる方法が、最も有望視されている。
【０００６】
上記の吸放湿性材料を使用した壁紙として具体的には例えば、難燃紙等の裏打紙の上にポリ塩化ビニル樹脂等の発泡樹脂層を設けた通常の壁紙において、発泡樹脂層に例えばシリカゲル又はゼオライト等の吸湿性無機粉体や、アクリル系樹脂又はポリビニルアルコール系樹脂等の高吸水性ポリマー等の吸放湿性物質を配合することによって、樹脂層に吸放湿性を具備させたものなどが考案されている（特許文献１、２）。
【０００７】
【特許文献１】
特開昭６０−８１３７８号公報
【特許文献２】
特開平１−２２９８９８号公報
【０００８】
しかし、吸放湿性物質を配合する樹脂層を構成する樹脂として、ポリ塩化ビニル樹脂の様な疎水性の強い樹脂を使用すると、樹脂層の内部に存在する吸放湿性物質は、疎水性の樹脂に妨げられて外部との間での水分のやり取りが出来ないため、実質的に樹脂層の表面に存在する吸放湿性物質だけしか吸放湿性能を有効に発現することが出来ず、極めて効率が悪いという問題がある。
【０００９】
そこで、吸放湿性物質を配合する樹脂として、ポリ塩化ビニル樹脂の様な疎水性の強い樹脂に代えて、水溶液又は水分散液の形で塗工可能な水性樹脂を用いた吸放湿性壁紙の提案も、既にある（特許文献３、４参照）。特に、微細樹脂粒子の水分散液である水性エマルジョン系樹脂を用いたものは、乾燥塗膜の微多孔質構造に起因して、透湿度の高い樹脂層が形成されるため、樹脂層の表面のみならず内部に存在する吸放湿性物質にも、効果的に吸放湿性能を発揮させ易いという利点がある。
【００１０】
【特許文献３】
特開平９−１２３３３９号公報
【特許文献４】
特開平１０−１２８８９２号公報
【００１１】
しかし、水を溶媒又は分散媒とする水性樹脂塗工剤に、高吸水性ポリマーや吸湿性無機粉体等の吸放湿性物質を配合して塗工しようとすると、これら吸放湿性物質が塗工剤中の水分を吸収するために、塗工剤が溶媒又は分散媒としての水分の一部を失って増粘ないしゲル化して、塗工状態が不安定になったり、極端な場合には塗工不能となってしまったりするという問題がある。
【００１２】
この問題の回避策として、吸放湿性物質に予め飽和するまで水を吸収させてから塗工剤中に配合する方法の提案もある（特許文献４）。しかし、特に高吸水性ポリマーは、水で飽和させると数十倍ないし数百倍にまで膨潤してゲル状体となるため、これを塗工剤中に分散して塗工することは必ずしも容易ではない。
【００１３】
さらに、吸湿性無機粉体にしても高吸水性ポリマーにしても、塗工後の塗膜の乾燥工程において、塗工液の溶媒又は分散媒としての水分に加えて、これらの吸放湿性物質が吸収していた水分を乾燥させるために、多くの熱量や乾燥時間を必要とし、生産効率が悪いことや、溶媒又は分散媒としての水分が蒸発して除去された後になっても、それよりも蒸発速度の遅い、吸放湿性物質が吸収していた水分が、徐々に放出されることにより、塗膜に膨れを発生し易いことなどの問題もある。
【００１４】
【発明が解決しようとする課題】
本発明は、従来の技術における上記のような問題点に着目してなされたもので、その課題とするところは、吸放湿性物質を水性樹脂塗工液中に分散して塗工する吸放湿性材料の製造方法において、該塗工液の増粘やゲル化等の問題を発生することなく良好に塗工可能であり、しかも塗工後の塗膜の乾燥のために過大な熱量や乾燥時間を要したり乾燥後の塗膜に膨れを発生したりすることなく、安定した品質で生産性よく製造可能な吸放湿性材料の製造方法を提供することにある。
【００１５】
【課題を解決するための手段】
本発明の吸放湿性材料の製造方法は、非透水性の殻の内部に、吸水性物質及び／又は吸湿性物質を少なくとも含む吸放湿媒体を内包したマイクロカプセルを、水性樹脂の溶液又は水分散液中に分散してなる水性樹脂塗工剤を、基材上に塗布し乾燥させて塗膜を形成した後、前記塗膜中のマイクロカプセルの少なくとも一部の殻を破壊して、該マイクロカプセルに内包された吸放湿媒体を殻の外に露出させて、吸放湿性樹脂層を形成することを特徴とするものである。
【００１６】
特に、前記マイクロカプセルの殻の破壊を、加熱により、又は加圧により、若しくはそれらの併用により行うことを特徴とするものであり、さらには、前記マイクロカプセルの殻は熱可塑性樹脂からなり、前記加熱は該熱可塑性樹脂の融点以上の温度にまで加熱することを特徴とするものである。
【００１７】
また特に、前記水性樹脂塗工剤にさらに発泡剤を配合し、塗膜の形成後に発泡させることを特徴とするものであり、さらに、前記発泡は加熱により行い、該加熱により該発泡と同時に前記マイクロカプセルの殻の破壊を行うことを特徴とするものであり、またさらには、前記マイクロカプセルの殻は熱可塑性樹脂からなり、前記発泡の際の加熱は該熱可塑性樹脂の融点以上の温度にまで加熱することを特徴とするものである。
【００１８】
また特に、前記塗膜の表面にエンボス加工を施すことを特徴とするものであり、さらに、前記エンボス加工の際の加圧により、前記マイクロカプセルの殻の破壊を行うことを特徴とするものであり、またさらに、前記エンボス加工は加熱エンボス加工であり、該加熱エンボス加工の際の加熱及び加圧により、前記マイクロカプセルの殻の破壊を行うことを特徴とするものであり、またさらに、前記マイクロカプセルの殻は熱可塑性樹脂からなり、前記加熱エンボス加工の際の加熱は該熱可塑性樹脂の融点以上の温度にまで加熱することを特徴とするものである。
【００１９】
また特に、前記マイクロカプセルは、前記吸放湿性樹脂層の表面近傍に濃集していることを特徴とするものである。また特に、前記吸放湿性樹脂層の表面に、透湿性の保護層を設けることを特徴とするものである。
【００２０】
【発明の実施の形態】
本発明に従って吸放湿材料を製造するには、まず、吸放湿媒体を非透水性の殻内に内包したマイクロカプセルを用意する。吸放湿媒体は、吸水性物質及び吸湿性物質から選ばれる一方又は両方を少なくとも含むことが必要であり、その他に例えばバインダー樹脂や安定剤等の添加剤を含んでいてもよい。
【００２１】
吸水性物質は、水酸基やカルボキシル基等の親水性の官能基を多く含む比較的疎な構造の物質であって、自身の体積を越える多量の水分を内部に吸収貯蔵可能な物質であればよく、具体的には公知の一般的な高吸水性ポリマー等が用いられる。
【００２２】
この高吸水性ポリマーとしては、例えば、澱粉−アクリル酸グラフト重合体、澱粉−アクリロニトリルグラフト重合体、セルロース−アクリロニトリルグラフト重合体、ポリビニルアルコール架橋重合体、ポリアクリル酸ナトリウム架橋体、アクリル酸メチル−酢酸ビニル共重合体鹸化物等が用いられる。
【００２３】
また、馬鈴薯澱粉やデキストリン類、コラーゲン（膠質）、ゼラチン、カゼイン、キトサン等の天然物を用いることもでき、これらの吸水性物質はそれぞれを単独で、または２種以上を任意に混合して使用することができる。
【００２４】
吸湿性物質は、例えばシリカゲル、ゼオライト、ラジオライト、珪藻土、焼成タルク等の様に、大きな比表面積を有する多孔質の親水性無機物質の粒子からなる物質であって、これらの吸湿性物質はそれぞれを単独で、または２種以上を任意に混合して使用することができる。
【００２５】
上記の吸水性物質と吸湿性物質とは、そのいずれかのみを使用してもよいが、前者は飽和吸水量は非常に多いが湿度（水蒸気）に対する吸放湿速度は遅く、後者は吸放湿速度は速いが飽和吸湿（水）量はあまり多くないので、いずれか単独では十分な性能が得られにくい場合が多い。
【００２６】
これに対し、吸水性物質と吸湿性物質とを併用すると、高湿時には、環境空気中の水蒸気を吸湿性物質が積極的に吸収して液体状に凝結させ、これを吸水性物質に受け渡して貯蔵させる作用をなし、一方低湿時には逆に、吸水性物質が貯蔵していた水分を吸湿性物質が受け取って環境空気中に気化蒸散させる作用をなすことにより、飽和吸湿量及び吸放湿速度の両面に優れた吸放湿性材料を用意に得ることができる利点がある。
【００２７】
これら吸水性物質及び／又は吸湿性物質を含む吸放湿媒体を被覆する殻の材質は、例えばポリアクリル系樹脂、ポリメタクリル系樹脂、ポリスチレン系樹脂、ポリオレフィン系樹脂、ポリアミド系樹脂、ポリエステル系樹脂、ポリブタジエン系樹脂、ポリエーテル系樹脂等、又はそれらの共重合体、ブレンド物等の熱可塑性樹脂が用いられるのが一般的である。
【００２８】
これらの熱可塑性樹脂によって吸放湿媒体を被覆する殻を形成する方法としては、例えば界面重合法、ｉｎ ｓｉｔｕ重合法、コアセルベーション法、液中乾燥法、気中懸濁法、噴霧乾燥法等が知られているが、粒子を確実に形成するには、界面重合法若しくはｉｎ ｓｉｔｕ重合法が好ましい。
【００２９】
上記各種の方法の中でも、マイクロカプセルの製造に最も一般的に用いられているのは界面重合法であり、この製法において使用される殻の構成材料としては、ポリアクリル系樹脂、ポリメタクリル系樹脂、スチレン系樹脂、ポリアミド系樹脂、又はそれらの共重合体若しくはブレンド物が好ましい。
【００３０】
いずれの製法や材料による場合であっても、殻の構成材料である樹脂自体が水溶性である場合には、架橋等の手段を用いて水不溶化させる必要がある。水溶性樹脂の水不溶化の手段としては公知の技術を用い、例えばイソシアネート化合物又はエポキシ化合物等の架橋剤を共存させ、各架橋剤の架橋条件にあわせて架橋構造をとらせることができる。
【００３１】
殻の構成材料の選択は、内包物質である吸放湿媒体の構成材料との相性を考慮しつつ適宜に選択すればよい。両者の重量比率としては、殻が１０〜９０重量％、より好ましくは１０〜６０重量％、吸放湿媒体が１０〜９０重量％、より好ましくは４０〜９０重量％の範囲内とすることが好ましい。
【００３２】
マイクロカプセルの粒径については、本発明において特に制限はないが、あまり小さすぎると、マイクロカプセル自体の製造が困難であるほか、加熱や圧力等による殻の破壊も困難となって、本発明の目的が達成できなくなる場合があり、逆にあまり大きすぎると、水性樹脂塗工剤中への分散が困難となったり、塗工適性が悪化したり、塗膜の表面が極端に粗面化したりする原因となるので、一般的には、平均粒径０．１〜１００μｍ程度とすることが望ましい。
【００３３】
なお、上記の様に高吸水性ポリマー等を非透水性の熱可塑性樹脂からなる殻の内部に内包したマイクロカプセル自体は、例えば特開昭６２−２２０６３１号や特開平１０−２７９９０９号等に見られる様に、既に公知である。
【００３４】
また、これに類似したものに、特開平１１−７６８１５号公報に示される如く、多数の微細孔を設けた殻の内部に吸放湿媒体を内包したマイクロカプセルも知られているが、この様に殻が多孔質のものは一般的には、本発明の目的にはそぐわない。殻の微細孔から侵入した水分を吸放湿媒体が吸収することにより、水性樹脂塗工剤の増粘やゲル化の原因となったり、水分を吸収して膨潤した吸放湿媒体が殻の微細孔から殻外へ滲み出したり、あるいは該膨潤による内圧に耐えられずに殻が破壊されてしまったりするおそれがあるからである。
【００３５】
以上の様にしてマイクロカプセルを用意したら、次に、それを水性樹脂の水溶液又は水分散液中に分散して、水性樹脂塗工剤を調製する。
【００３６】
上記水性樹脂として具体的には、例えば水溶塩型アクリル系樹脂、ポリアクリルアミド、ポリビニルアルコール、ポリビニルピロリドン、カゼイン、セルロース誘導体、デキストリン類等の水溶性樹脂や、例えばアクリル系樹脂、ポリウレタン系樹脂、スチレン−ブタジエン共重合体系樹脂、酢酸ビニル系樹脂、エチレン−酢酸ビニル共重合体樹脂、シリコーン系樹脂、ポリブテン系樹脂等の非水溶性樹脂粒子を水中に分散してなる水性エマルジョン系樹脂等、或いはそれらの２種以上の混合物等を使用することができる。
【００３７】
なお、上記水性樹脂が水溶性樹脂を少なくとも含む場合には、製造される吸放湿性材料が水に濡れることがあっても塗膜が溶解することがない様に、例えばメラミン化合物、ブロックイソシアネート化合物、エポキシ化合物、ヒドラジン誘導体、アジリジン、有機過酸化物等の架橋剤を添加したり、或いは電子線等の電離放射線を照射する等の手段により、塗工後に塗膜中の樹脂を架橋させて水不溶化させることが望ましい。
【００３８】
上記水溶性樹脂と水性エマルジョン系樹脂とを比較すると、塗工液の安定性や塗工乾燥後の表面物性、微多孔質状となることによる高透湿性などの面で、水性エマルジョン系樹脂の採用が望ましい。また、係る水性エマルジョン系樹脂を、架橋剤の配合又は電離放射線照射等により、塗工後に架橋させてもよいことも勿論である。
【００３９】
上記水性樹脂塗工剤中への前記マイクロカプセルの添加量は、本発明において特に制限されるものではないが、あまり少なすぎると十分な吸放湿効果が得られず、逆にあまり多すぎても、相対的にバインダー樹脂分が少なくなるために塗膜が脆くなり、表面強度が低下する原因となるので、一般的には水性樹脂の固形分１００重量部に対して１０〜２００重量部程度、さらに好ましくは３０〜１５０重量部程度の範囲内とすることが好ましい。
【００４０】
この水性樹脂塗工剤には、前記マイクロカプセルの他、必要に応じて例えば着色剤、充填剤、分散剤、消泡剤、湿潤剤、増粘剤、難燃剤、防炎剤、紫外線吸収剤、光安定剤、酸化防止剤、帯電防止剤、滑剤、減摩剤、艶調整剤、抗菌剤、防黴剤等の種々の添加剤を適宜添加することもできる。
【００４１】
また、機械発泡法又は発泡剤を添加する方法等の従来公知の手段により、塗膜を多孔質の細胞状に発泡させてもよく、そうすることによって、塗膜の透湿性を更に向上させて、吸放湿機能を更に存分に発揮させることもできる。また、本発明の吸放湿性材料を住宅等の建築物における壁紙等の内装材に使用する場合には、水性樹脂塗工剤の塗膜を発泡させることでエンボスによる凹凸模様の形成を容易にし、意匠性にも優れた内装材を容易に得ることができる利点もある。
【００４２】
上記発泡剤としては、例えばアゾジカルボンアミド（ＡＤＣＡ）等のアゾ系化合物、ｐ，ｐ’−オキシビスベンゼンスルホニルヒドラジド（ＯＢＳＨ）等のニトロソ化合物等の有機発泡剤や、例えば炭酸水素ナトリウム、炭酸アンモニウム等の無機発泡剤等の熱分解型化学発泡剤や、例えばポリアクリロニトリル系樹脂、フェノール系樹脂、エポキシ系樹脂等の熱軟化性柔軟性殻体の内部にイソブタン等の低沸点液体を内包してなる熱膨張型マイクロカプセル発泡剤等を使用することができる。
【００４３】
上記発泡剤の添加量は、本発明において特に制限されるものではないが、一般的には水性樹脂の固形分１００重量部に対して１〜２０重量部程度を添加することが好ましく、更に好ましくは３〜１０重量部である。１重量部に満たない場合には、発泡倍率が低く、吸放湿機能の向上効果もあまり期待できず、またエンボスの凹凸模様による意匠性の向上も困難である。一方、２０重量部を越えると、発泡セルが著しく粗雑な状態となり、発泡後の塗膜の表面強度が弱くなってしまうからである。
【００４４】
以上の様にして水性樹脂塗工剤を調製したら、それを適宜の基材の表面に塗工して塗膜を形成する。塗工対象物である基材の材質や形状については、本発明において何ら制限されるものではなく、製造する吸放湿性材料の用途に応じて適宜選定すればよい。
【００４５】
基材として使用可能な材料の例を挙げれば、例えば紙、織布又は不織布等の繊維質シートや、ポリオレフィン系樹脂シートやポリエステル系樹脂シート、アクリル系樹脂シート等の合成樹脂シート、合成ゴムシート、アクリル樹脂板やポリカーボネート樹脂板、ＡＢＳ樹脂板、ＦＲＰ等の合成樹脂系基材、合板や集成材、木質繊維板、パーティクルボード等の木質系基材、鋼板や真鍮板、ステンレス板、アルミニウム板等の金属系基材、石膏ボードや珪酸カルシウム板、セメント板、コンクリート板等の無機質系基材等、或いはそれらの複数種の積層体等である。
【００４６】
また、基材の表面には必要に応じて、例えば目止め処理、ベースコート処理、研磨処理、プライマー処理、コロナ放電処理、オゾン処理、プラズマ処理、火炎処理、電離放射線処理、酸処理、アルカリ処理等の適宜の表面処理が施されていてもよい。
【００４７】
特に、本発明の吸放湿性材料を壁紙として使用する場合には、従来より合成樹脂系壁紙（いわゆるビニル壁紙）用の基材として使用されていた任意のシート状の材料が使用可能である。
【００４８】
具体的には例えば、木質パルプ等のセルロース系繊維からなる抄造紙にスルファニル酸グアナジン又はリン酸グアナジン等の水溶性難燃剤を含浸させたパルプ紙系難燃紙や、セルロース系繊維の抄紙時に炭酸カルシウム、水酸化アルミニウム又は水酸化マグネシウム等の無機質剤を混抄した無機混抄紙、ガラス繊維、アルミナ繊維、チタン酸カリウム繊維等の無機繊維を単独で又はセルロース系繊維と混合して抄造した無機繊維紙等の難燃紙乃至不燃紙や、同じく難燃剤や無機質剤を添加し又は無機繊維を用いて製造した難燃性乃至不燃性の織布又は不織布等、何れも使用可能である。
【００４９】
水性樹脂塗工剤を基材上に塗工する方法としては、例えばナイフコート法、エアーナイフコート法、ノズルコート法、グラビアコート法、マイクログラビアコート法、ロータリースクリーンコート法、リバースロールコート法、コンマコート法、リップコート法、ダイコート法、スプレーコート法、ディップコート法、フローコート法等、従来公知の任意の塗工方法が採用可能であり、塗工後の乾燥方法としては、例えば熱風または赤外線ヒーター等の熱源をそれぞれ単独若しくはこれらの複数種を組み合わせて用いることもできる。
【００５０】
水性樹脂塗工剤の塗布量は、本発明において特に限定されるものではないが、あまり薄すぎると含まれる吸放湿媒体の絶対量が少ないために十分な吸放湿効果が得られず、一方逆にあまり厚すぎても底層部に含まれる吸放湿媒体が実質的に機能せずに材料の無駄となってしまうので、これらを考慮して適宜設計する必要がある。
【００５１】
一般的には、十分な吸放湿効果を得るためには、少なくとも厚さが１０μｍ以上の塗膜を形成する必要があり、さらに好ましくは３０μｍ以上である。一方、厚みの上限については、塗膜の透湿度にも依存するが、透湿度を向上させにくい非発泡層とする場合には概ね３００μｍ程度、高い透湿度を容易に得やすい発泡層とする場合には概ね２０００μｍ程度を、それぞれ上限とするのがよい。
【００５２】
こうして水性樹脂塗工剤を塗工し、十分に乾燥させて塗膜を形成したら、該塗膜中に含まれる吸放湿媒体を内包したマイクロカプセルのうち、少なくとも一部のマイクロカプセルの殻を破壊して、該マイクロカプセルに内包された吸放湿媒体を殻の外に露出させる処理を施す。この処理を施すことによって、吸放湿媒体が外気中の水蒸気を吸収したり、又は吸収していた水分を水蒸気として外気中へ放散したりすることが可能となり、塗膜は吸放湿機能を獲得して吸放湿性樹脂層となる。
【００５３】
マイクロカプセルの殻の破壊は、塗膜に含まれる全てのマイクロカプセルに対して実施できれば最も理想的であるが、実際には全てのマイクロカプセルの殻を破壊し尽くすことはあまり現実的ではないから、実用上十分な吸放湿性機能が発現する様に、出来るだけ多くのマイクロカプセルの殻を破壊すればよい。
【００５４】
マイクロカプセルの殻の破壊方法については、本発明において特に制限されることなく任意の方法を適用して構わないが、最も一般的なのは加熱による方法と加圧による方法である。勿論その両者を併用することも可能である。
【００５５】
前者の加熱による方法の原理には主として次の２通りがある。その第１は、殻を構成する熱可塑性樹脂が溶融して流動し、殻の厚みが不均一となって最終的には孔があく現象を利用するものである。この場合には、少なくとも殻を構成する熱可塑性樹脂の融点以上の温度に加熱する必要がある。また、殻を構成する熱可塑性樹脂を架橋させ過ぎると、溶融粘度が高くなって流動しにくくなるので、架橋はさせないか又は控え目にしておくことが有利である。
【００５６】
また第２は、殻と内包物との熱膨張差を利用するもので、内包物である吸放湿媒体の熱膨張率が殻の熱膨張率より大きく、しかも殻の伸びが小さい場合には、加熱による吸放湿媒体の膨張に殻が追従できずに割れる現象を利用するものである。この場合には、殻が熱膨張しにくく且つ伸びにくくなる様に十分に架橋させてやる必要があるが、架橋させすぎたり又は殻が厚すぎたりすると、殻の強度が増して加熱しても割れにくくなるので、殻の架橋密度と厚さの設計に十分な配慮が必要である。
【００５７】
後者の加圧による方法は、要するに、マイクロカプセルに圧力を掛けて圧し潰す方法である。この方法による場合は、殻は伸びが少なく脆く割れ易いことが有利であり、このためには、分子鎖の絡み合いの少ない低分子量の樹脂や、分子内架橋等により団子状になった分子からなる樹脂を使用するか、若しくは分子間を十分に架橋させて伸びにくくすることが有利である。但し、架橋させすぎたり殻が厚すぎたりすると、殻の強度が増して加圧しても割れにくくなるので、注意が必要である。
【００５８】
また、より効率良くマイクロカプセルの殻を破壊するためには、加熱と加圧とを併用する方法が有効である。上記した殻の溶融流動を利用するタイプの場合には、加圧が溶融した殻の流動を促進し、孔があきやすくなる。また、後者の熱膨張差を利用するタイプの場合にあっても、熱膨張差による応力に加圧による応力が加わって、殻が割れ易くなるからである。
【００５９】
塗膜の加圧は、平圧方式で行っても構わないが、特に基材がシート状である場合には、連続生産性を考慮して、円圧（ロールプレス）方式が採用される場合が多い。この場合、シートがロール間を通過する際に、塗膜の表面とロールの表面との間には、かなり大きな摩擦力が発生し、この摩擦力は、少なくとも塗膜の表面近傍に存在するマイクロカプセルの殻の破壊を促進する作用をなす。
【００６０】
この作用は、前述した殻の溶融流動を利用するタイプのマイクロカプセルを使用し、加熱を併用する場合に、特に顕著である。従って、殻を構成する熱可塑性樹脂の融点以上の温度に加熱しつつ加圧する方法によることが、殻の破壊方法としては最も効率が高い。
【００６１】
但し、上記の作用は、塗膜の底層部に存在するマイクロカプセルには殆ど及ばないので、あまりこの作用に頼ると、結果的に吸放湿機能に寄与せずに無駄になるマイクロカプセルが増えることになる。この無駄を低減するためには、吸放湿媒体を内包するマイクロカプセルを、塗膜中においてその表面近傍に濃集させてやるとよい。
【００６２】
その方法としては、水性樹脂塗工剤の主成分である水性樹脂の水溶液又は水分散液よりも比重の小さいマイクロカプセルを使用して、塗工後の塗膜中で重力の作用によりマイクロカプセルを表面に浮揚させる方法や、マイクロカプセルの表面にシリコーン化合物や脂肪酸誘導体等の疎水性物質を付着させる等して疎水性を付与しておき、水との反撥作用を利用してマイクロカプセルを塗膜表面に浮揚させる方法などを用いることができる。
【００６３】
なお、殻の破壊方法の種類を問わず、吸放湿媒体を内包したマイクロカプセルが塗膜の表面近傍に濃集していれば、外気との間での吸放湿に対するバインダー樹脂の阻害が少ないため、同一の量のマイクロカプセルを使用しても、吸放湿速度や飽和吸湿量をより向上させることができるので有利である。
【００６４】
水性樹脂塗工剤に発泡剤を配合し、塗工後に加熱により発泡させる場合には、該発泡時の加熱により、塗膜の発泡と同時にマイクロカプセルの殻の破壊を行うこともできる。例えば、殻が熱可塑性樹脂からなるマイクロカプセルを使用して、その融点以上の温度で加熱発泡を行うことにより、発泡と同時にマイクロカプセルの殻を破壊して、吸放湿機能を発現させることができる。
【００６５】
水性樹脂塗工剤の塗工後、その塗膜の表面には、凹凸模様による立体的な意匠感を付与するために、金属製等のエンボス版又はエンボスロール等を使用して加圧することによるエンボス加工を施すことができる。そしてその際には、該エンボス加工時の加圧を利用して、マイクロカプセルの殻の破壊を行うことにより、凹凸模様の付与と同時に吸放湿機能を発現させることもできる。
【００６６】
上記エンボス加工は、常温で行われる場合もあるが、一般的には、塗膜を熱により軟化させて容易に凹凸模様を成形可能とするために、加熱下で行われる場合（加熱エンボス加工）が多い。そして、該加熱エンボス加工時の加熱及び加圧により、マイクロカプセルの殻の破壊を行うことにより、加熱の効果と加圧の効果との相乗効果により、極めて効率的に殻を破壊させることができる。
【００６７】
例えば、殻が熱可塑性樹脂からなるマイクロカプセルを使用して、その融点以上の温度で加熱エンボス加工を行うことにより、加熱エンボス加工と同時にマイクロカプセルの殻を破壊して、吸放湿機能を発現させることができる。
【００６８】
水性樹脂塗工剤の塗膜に、上記加熱発泡及び加熱エンボス加工の双方の処理を施す場合には、まず加熱発泡させ、しかる後に加熱エンボス加工を行うのが一般的である。そして、後者の加熱エンボス加工は、前者の加熱発泡よりも高温且つ短時間で行われるのが一般的である。
【００６９】
この場合、マイクロカプセルの殻の破壊は、先の工程である加熱発泡工程において既に行われる様にすることも出来るし、或いは、加熱発泡の際には殻を破壊させない温度範囲で行うことにより、殻が未破壊の発泡層を形成し、しかる後に、加熱エンボス加工の工程において、加熱及び加圧により殻を破壊させるようにしてもよい。
【００７０】
しかし、上記両者を比較すると、前者の方法によると、加熱発泡工程において殻が破壊され、殻から露出して発泡層のバインダー樹脂中に分散した吸放湿媒体が、後の加熱エンボス工程において、溶融したバインダー樹脂によって周囲を包囲された形で圧密される結果、得られる吸放湿効果が減殺される場合がある。
【００７１】
これに対し、後者の方法によれば、加熱発泡の際には殻が未破壊の状態を保持したマイクロカプセルが、塗膜の発泡の作用により発泡層の表面近傍に押し上げられ、その後の加熱エンボス工程において、短時間の加熱及び加圧により、周囲の発泡層との関係を大きく変更しないまま、マイクロカプセルの殻が破壊されて吸放湿媒体が露出する結果、優れた吸放湿効果を発現し易い利点がある。
【００７２】
本発明の製造方法によって得られる吸放湿性材料は、マイクロカプセルに内包された吸放湿媒体が、該マイクロカプセルの殻の破壊により露出しているとは言っても、該マイクロカプセル自体が吸放湿性樹脂層中に分散状態で存在していることに加え、吸放湿媒体の表面のうちの多くの部分が殻の残骸で被覆されていることから、単に高吸水性ポリマーの分散液を表面に塗布した場合等に比較すれば、高湿時や水濡れ時の表面のべとつきは遥かに少ない。
【００７３】
しかし、それでも高湿時や水濡れ時の表面のべとつき等の問題が気になる場合には、上記の様にして得た吸放湿媒体を内包するマイクロカプセルを含む吸放湿性樹脂層の表面に、透湿性の保護層を設けることもできる。この透湿性の保護層は、着色した水分を吸放湿媒体が吸収することによる変色を防止し、耐汚染性を向上させる効果をも有する。
【００７４】
上記透湿性の保護層は、それ自体は水に溶けたり吸水により膨潤したりすることのない程度の耐水性を有しつつ、吸放湿媒体を内包したマイクロカプセルを含む下地の塗膜と外気との間での水蒸気の流通を妨げない程度の透湿性を有する材質であればよく、例えばアクリル系樹脂、ウレタン系樹脂、スチレン−ブタジエン共重合体系樹脂、酢酸ビニル系樹脂、エチレン−酢酸ビニル共重合体系樹脂、エチレン−ビニルアルコール共重合体系樹脂、シリコーン系樹脂、ポリアミド系樹脂、ポリブテン系樹脂等を使用することができ、これらの２種以上の混合物や積層被膜等であってもよい。
【００７５】
透湿性の保護層の厚さは、薄過ぎると防水性が不十分となってべとつき防止や汚染防止等の効果を十分に得ることができず、一方厚過ぎても透湿度が低下して吸放湿性能を減殺する原因となるので、両者を勘案して適宜設計する必要があり、一般的には０．５〜２０μｍ程度の範囲内で設計することが好ましい。
【００７６】
上記透湿性の保護層を形成する時期には一切制限はなく、水性樹脂塗工剤の塗工後、マイクロカプセルの殻の破壊前であっても破壊後であっても良いし、発泡させる場合は発泡前であっても発泡後であってもよく、また、エンボス加工を施す場合はその前であっても後であってもよい。さらに、多層塗工法により水性樹脂塗工剤の塗工と同時に塗工形成してもよい。このほか必要に応じて、吸放湿性樹脂層の表面及び／又は透湿性の保護層の表面に、適宜の絵柄の印刷を施したりしてもよい。
【００７７】
【実施例】
以下に本発明の具体的な実施例及び比較例を挙げて更に詳細に説明する。
【００７８】
実施例１
＜マイクロカプセルの調製＞
水１００重量部に平均粒径０．７μｍのシリカゲル粉末を３０重量部分散したものをセパラブルフラスコに仕込み、窒素を吹き込み空気を置換した。これを８０℃に昇温し、ジアミノエチルメタクリレート８０重量部を添加し、８０℃で１時間懸濁させた。その後、８％の過硫酸アンモニウム水溶液を１時間かけて滴下し、その後２時間８０℃を保ち、シリカゲル粉末を内包し平均粒径約１μｍ、殻の融点約１８０℃、固形分５０重量％のマイクロカプセルの水分散液を得た。
【００７９】
＜水性樹脂塗工剤の調製＞
上記のマイクロカプセルの水分散液１００重量部を、固形分５０重量％、固形分樹脂の融点約１７０℃のアクリル系樹脂水性エマルジョン１００重量部と混合したところ、増粘したりゲル化したりすることなく、良好な塗工適性を有する水性樹脂塗工剤が得られた。
【００８０】
＜吸放湿性材料の作製＞
上記水性樹脂塗工剤を、通常の壁紙用裏打紙の表面に、乾燥後の塗布厚１００μｍに塗布し、１００℃で３分間乾燥させた。その際の乾燥条件は、マイクロカプセルを配合していない塗工剤を同厚で塗工した場合と同等の条件で、迅速且つ十分に乾燥可能であり、乾燥後の表面状態も良好であった。しかる後、２５０℃３０秒間の条件で加熱エンボス加工を施して、凹凸模様を賦形すると同時にマイクロカプセルの殻を破壊して、本発明の吸放湿性材料を作製した。
【００８１】
比較例１
上記マイクロカプセルに代えて、その作製に使用したものと同一のシリカゲル粉末１００重量部を、上記アクリル系樹脂水性エマルジョン１００重量部と混合したところ、液がゲル化して塗工不可能となった。そこで、シリカゲル粉末の配合量を減らしながら塗工可能な水性樹脂塗工剤が得られる条件を探したところ、アクリル系樹脂水性エマルジョン１００重量部当たりシリカゲル粉末１０重量部が限度であることが分かった。そこで、この配合比率で水性樹脂塗工剤を調製し、以下上記実施例１と同一の条件で吸放湿性材料を作製した。
【００８２】
実施例２
上記比較例１との対照のため、上記実施例１において、アクリル系樹脂水性エマルジョン１００重量部に対するマイクロカプセルの配合量を１０重量部に減じ、その他は上記実施例１と同一の条件で本発明の吸放湿性材料を作製した。
【００８３】
吸放湿試験
上記実施例１、２及び比較例１の吸放湿性材料について、まず２５℃５０％ＲＨの環境下で２４時間養生した後、２５℃９０％ＲＨの環境下に入れて、経時による重量変化を求め、十分に飽和したと認められた１２０時間後に、２５℃５０％ＲＨの環境下に戻し、さらに経時による重量変化を求めた。その結果を図１のグラフに示す。但し、吸湿量は、最初の養生の完了時の重量を基準にした、その後の吸湿後の重量増加量である。
【００８４】
このグラフに示されるとおり、配合量が同じであれば、マイクロカプセル化したもの（実施例２）としていないもの（比較例１）とでは、吸放湿効果の差は殆ど無いことが確認できた。そして、前者は後者よりも大量に配合可能であり（実施例１）、それにより後者よりも遥かに大きな吸放湿機能の付与が可能であるという優位性が実証された。
【００８５】
実施例３
＜水性樹脂塗工剤の調製＞
上記実施例１において調製したマイクロカプセルの水分散液１００重量部と、固形分５０重量％、固形分樹脂の融点約１７０℃のアクリル系樹脂水性エマルジョン１００重量部と、ポリアクリロニトリル系樹脂製の殻の内部にイソブタンを内包したマイクロカプセル発泡剤５重量部とを混合して、水性樹脂塗工剤を調製した。
【００８６】
＜吸放湿性材料の作製＞
上記水性樹脂塗工剤を、通常の壁紙用裏打紙の表面に、乾燥後の塗布厚１００μｍに塗布し、１００℃で３分間乾燥させた後、２２０℃に加熱して発泡させると同時に、シリカゲル粉末を内包するマイクロカプセルの殻を破壊して、本発明の吸放湿性材料を作製した。
【００８７】
実施例４
上記実施例３において、水性樹脂塗工剤の乾燥後の発泡を、シリカゲル粉末を内包するマイクロカプセルの殻が破壊されない１６０℃で行い、しかる後、２５０℃３０秒間の条件で加熱エンボス加工を施して、凹凸模様を賦形すると同時にマイクロカプセルの殻を破壊して、本発明の吸放湿性材料を作製した。
【００８８】
実施例５
上記実施例４において、加熱エンボス加工後の塗膜の表面に、透湿性ポリウレタン系樹脂をスプレーコート法にて乾燥後の厚み３μｍに塗布して、透湿性の保護層を形成して、本発明の吸放湿性材料を作製した。
【００８９】
上記実施例３〜５の吸放湿性材料について、前記と同一の条件で吸放湿試験を実施したところ、これらはいずれも上記実施例１とほぼ同等の吸放湿効果を示すことが確認された。
【００９０】
【発明の効果】
以上詳細に説明したとおり、本発明の吸放湿材料の製造方法によれば、吸放湿媒体を非透水性の殻で被覆したマイクロカプセルとすることにより、増粘やゲル化等により塗工を困難にすることなく、水性樹脂塗工剤中への配合量を従来より格段に増すことが可能となる。
【００９１】
しかも、該マイクロカプセルに内包される吸放湿媒体は、水性樹脂塗工剤の配合中や塗工中に水分を吸収したり、乾燥中にその水分を放出したりすることがないから、乾燥に要する熱量や乾燥時間等の負荷を増すことがなく、乾燥中の水分放出により塗膜の表面が粗れたりすることもない。
【００９２】
そして、該塗工剤の塗工後に、該マイクロカプセルの少なくとも一部の殻を加熱及び／又は加圧により破壊することにより、該マイクロカプセルに内包される吸放湿媒体を殻の外に露出させることができることから、従来よりも格段に優れた吸放湿効果を発現させることができるという顕著な効果を奏するものである。
【図面の簡単な説明】
【図１】本発明の実施例及び比較例の吸放湿性能試験結果を示すグラフ。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention has a function of absorbing moisture in environmental air at high humidity and dissipating the absorbed moisture at low humidity to environmental air, thereby reducing moisture fluctuation in environmental air. It is related to materials, and is particularly useful as an interior material for buildings.
[0002]
[Prior art]
Due to the spread of reinforced concrete structures and prefabricated construction methods, new construction materials made of synthetic materials such as resin-processed plywood, and the development of metal sashes for doors and windows, modern buildings are extremely airtight compared to the former pure Japanese architecture. It is expensive. The high airtightness of such a building can be said to be very desirable from the viewpoint of saving energy resources by improving the cooling and heating effects, and preventing noise pollution in the vicinity by improving soundproofing.
[0003]
However, on the other hand, the moisture generated by the living activities of the resident (human breathing, cooking, bath / shower, etc.) in the room is not easily escaped to the outside and is easily trapped in the room. Condensation on the surface of glass, window frame sash, etc. is not only undesirable from the viewpoint of aesthetics and tactile feeling, but also causes stains and corrosion of building materials and may shorten the life of the building. is there.
[0004]
As a solution to this problem, a method of installing a forced-ventilation device or an air-conditioning device in a building to keep the indoor humidity within a certain range has been studied in some cases, but it has been studied in some places such as corridors. In order to apply forced ventilation or air conditioning to the entire interior of the building including the storage space, etc., the initial capital investment burden will be remarkably heavy, and the equipment will be operated for 24 hours, including at night and when going out. It is not considered to be a very practical method for ordinary households because the burden of electricity costs is heavy and the maintenance and inspection of the equipment is troublesome and costly.
[0005]
Therefore, as a method of adjusting the indoor humidity without using the special equipment as described above, the function of absorbing the moisture in the environmental air at high humidity and dissipating the absorbed moisture into environmental air at low humidity A method has been devised in which a moisture-absorbing and desorbing material having the following characteristics is installed in a room to reduce indoor humidity fluctuation. Although various modes of installation of the moisture absorbing / releasing material can be considered, it is considered that a larger surface area in contact with the environmental air is more advantageous in order to quickly and sufficiently exhibit the moisture absorbing / releasing function. A method of finishing a wall surface, a ceiling surface, or the like occupying a large surface area in a room of an object with an interior material such as a wallpaper using a moisture-absorbing / desorbing material is most promising.
[0006]
Specifically, as a wallpaper using the above-described moisture absorbing and releasing material, for example, in a normal wallpaper provided with a foamed resin layer such as polyvinyl chloride resin on a backing paper such as flame retardant paper, for example, silica gel in the foamed resin layer Or, by blending a hygroscopic substance such as a hygroscopic inorganic powder such as zeolite or a highly water-absorbing polymer such as an acrylic resin or a polyvinyl alcohol-based resin, a resin layer having a hygroscopic property is provided. It has been devised (Patent Documents 1 and 2).
[0007]
[Patent Document 1]
JP-A-60-81378
[Patent Document 2]
JP-A-1-229898
[0008]
However, if a highly hydrophobic resin such as a polyvinyl chloride resin is used as the resin constituting the resin layer containing the moisture absorbing / releasing substance, the moisture absorbing / releasing substance present inside the resin layer becomes a hydrophobic resin. Since moisture cannot be exchanged with the outside due to being hindered by moisture, only moisture-absorbing and desorbing substances existing on the surface of the resin layer can effectively exhibit moisture-absorbing and desorbing performance, which is extremely efficient. There is a problem that is bad.
[0009]
Therefore, instead of a resin having a strong hydrophobicity such as polyvinyl chloride resin as a resin containing a moisture-absorbing and releasing substance, a moisture-absorbing and desorbing wallpaper using an aqueous resin that can be applied in the form of an aqueous solution or an aqueous dispersion is used. There have already been proposals (see Patent Documents 3 and 4). In particular, in the case of using an aqueous emulsion resin which is an aqueous dispersion of fine resin particles, a resin layer having high moisture permeability is formed due to the microporous structure of the dried coating film. Not only the moisture-absorbing / desorbing substance present inside, but also there is an advantage that the moisture-absorbing / desorbing performance is easily exhibited effectively.
[0010]
[Patent Document 3]
JP-A-9-123339
[Patent Document 4]
JP-A-10-128892
[0011]
However, when an attempt is made to apply a water-absorbing and desorbing substance such as a super-absorbent polymer or a hygroscopic inorganic powder to an aqueous resin coating agent using water as a solvent or a dispersion medium, the water-absorbing and desorbing substance is applied. In order to absorb the water in the coating agent, the coating agent loses a part of the water as a solvent or a dispersion medium, thickens or gels, and the coating state becomes unstable or in extreme cases There is a problem that coating becomes impossible.
[0012]
As a workaround for this problem, there has been proposed a method of absorbing water until the moisture-absorbing / desorbing substance is saturated beforehand and then blending it into a coating agent (Patent Document 4). However, especially when the superabsorbent polymer is saturated with water, it swells to tens to hundreds of times to form a gel, and it is not always easy to disperse this in a coating agent and apply it. is not.
[0013]
Furthermore, in the drying step of the coated film after coating, in addition to moisture as a solvent or a dispersion medium of the coating liquid, these moisture absorbing and releasing substances Requires a large amount of heat and drying time in order to dry the water that has been absorbed, resulting in poor production efficiency, and even after the water as a solvent or dispersion medium has been removed by evaporation. In addition, there is also a problem that the evaporation rate is low, and the moisture absorbed by the moisture absorbing / releasing substance is gradually released, so that the coating film easily swells.
[0014]
[Problems to be solved by the invention]
The present invention has been made in view of the above-mentioned problems in the prior art, and an object thereof is to absorb and release a moisture-absorbing and desorbing substance by dispersing it in an aqueous resin coating solution. In the method for producing a wet material, it is possible to apply well without causing problems such as thickening and gelling of the coating liquid, and excessive heat and drying for drying the coating film after coating. An object of the present invention is to provide a method for producing a moisture-absorbing and desorbing material that can be produced with stable quality and high productivity without requiring time and without causing swelling of a dried coating film.
[0015]
[Means for Solving the Problems]
The method for producing a moisture-absorbing and desorbing material according to the present invention comprises the steps of: forming a microcapsule containing a water-absorbing substance and / or a moisture-absorbing medium containing at least a moisture-absorbing substance inside a water-impermeable shell; An aqueous resin coating agent dispersed in a dispersion is applied on a substrate and dried to form a coating film, and then at least a part of the shell of the microcapsules in the coating film is broken, The moisture-absorbing / desorbing medium contained in the microcapsules is exposed outside the shell to form a moisture-absorbing / releasing resin layer.
[0016]
In particular, the breaking of the shell of the microcapsule is characterized by being performed by heating, or by pressurization, or by a combination thereof, and further, the shell of the microcapsule is made of a thermoplastic resin, The heating is characterized by heating to a temperature higher than the melting point of the thermoplastic resin.
[0017]
Further, particularly, a foaming agent is further added to the aqueous resin coating composition, and foaming is performed after forming the coating film.Furthermore, the foaming is performed by heating, and the heating is performed simultaneously with the foaming. The shell of the microcapsule is characterized in that it is broken, and the shell of the microcapsule is made of a thermoplastic resin, and the heating during the foaming is performed at a temperature equal to or higher than the melting point of the thermoplastic resin. It is characterized by heating to
[0018]
In particular, the method is characterized in that embossing is performed on the surface of the coating film, and further, the shell of the microcapsule is broken by applying pressure during the embossing. Yes, furthermore, the embossing is a heating embossing, characterized in that the shell of the microcapsule is broken by heating and pressing during the heating embossing, and further, The shell of the microcapsule is made of a thermoplastic resin, and the heating at the time of the heating embossing is performed by heating to a temperature equal to or higher than the melting point of the thermoplastic resin.
[0019]
In particular, the microcapsules are concentrated near the surface of the moisture absorbing / releasing resin layer. In particular, a moisture-permeable protective layer is provided on the surface of the moisture-absorbing and releasing resin layer.
[0020]
BEST MODE FOR CARRYING OUT THE INVENTION
In order to produce a moisture absorbing / releasing material according to the present invention, first, a microcapsule in which a moisture absorbing / releasing medium is contained in a water-impermeable shell is prepared. The moisture absorbing / releasing medium needs to contain at least one or both selected from a water absorbing substance and a moisture absorbing substance, and may further contain additives such as a binder resin and a stabilizer.
[0021]
The water-absorbing substance is a substance having a relatively sparse structure containing many hydrophilic functional groups such as a hydroxyl group and a carboxyl group, and any substance capable of absorbing and storing a large amount of water exceeding its own volume. Specifically, a known general superabsorbent polymer or the like is used.
[0022]
Examples of the superabsorbent polymer include starch-acrylic acid graft polymer, starch-acrylonitrile graft polymer, cellulose-acrylonitrile graft polymer, polyvinyl alcohol crosslinked polymer, sodium polyacrylate crosslinked product, methyl acrylate-acetic acid. Saponified vinyl copolymer is used.
[0023]
Natural substances such as potato starch, dextrins, collagen (collagen), gelatin, casein and chitosan can also be used. These water-absorbing substances can be used alone or in any combination of two or more. can do.
[0024]
The hygroscopic substance is a substance composed of particles of a porous hydrophilic inorganic substance having a large specific surface area, such as silica gel, zeolite, radiolite, diatomaceous earth, calcined talc, and the like. Can be used alone or in admixture of two or more.
[0025]
Either one of the above-mentioned water-absorbing substance and hygroscopic substance may be used, but the former has a very large saturated water absorption but has a low moisture absorption / desorption rate for humidity (water vapor), and the latter has a water absorption / desorption rate. Although the moisture rate is high, the amount of saturated moisture absorption (water) is not so large, and it is often difficult to obtain sufficient performance by using either alone.
[0026]
On the other hand, when a water-absorbing substance and a hygroscopic substance are used in combination, at high humidity, the water-absorbing substance actively absorbs water vapor in the environmental air and condenses into a liquid state, which is transferred to the water-absorbing substance. On the other hand, when the humidity is low, on the other hand, when the moisture is absorbed by the water-absorbing substance, the moisture-absorbing substance receives the moisture and vaporizes and evaporates it into the environment air, thereby reducing the saturated moisture absorption and the moisture absorption / desorption rate. There is an advantage that an excellent moisture absorbing / releasing material can be easily obtained on both sides.
[0027]
The shell material for covering the moisture absorbing / releasing medium containing these water absorbing substances and / or hygroscopic substances is, for example, polyacrylic resin, polymethacrylic resin, polystyrene resin, polyolefin resin, polyamide resin, polyester resin. In general, thermoplastic resins such as polybutadiene-based resins, polyether-based resins, and copolymers and blends thereof are used.
[0028]
As a method of forming a shell covering the moisture absorbing / releasing medium with these thermoplastic resins, for example, an interfacial polymerization method, an in situ polymerization method, a coacervation method, a submerged drying method, an air suspension method, a spray drying method Although an interfacial polymerization method or an in-situ polymerization method is preferable for surely forming particles.
[0029]
Among the above various methods, the one most commonly used for the production of microcapsules is the interfacial polymerization method, and the shell material used in this production method is a polyacrylic resin, a polymethacrylic resin. , A styrene-based resin, a polyamide-based resin, or a copolymer or blend thereof.
[0030]
Regardless of the method or material used, if the resin constituting the shell is itself water-soluble, it is necessary to make it water-insoluble by means such as crosslinking. As a means for insolubilizing the water-soluble resin with water, a known technique may be used, for example, a crosslinking agent such as an isocyanate compound or an epoxy compound may coexist, and a crosslinked structure may be formed in accordance with the crosslinking conditions of each crosslinking agent.
[0031]
The constituent material of the shell may be appropriately selected in consideration of the compatibility with the constituent material of the moisture absorbing / releasing medium which is an included substance. The weight ratio of the two is preferably in the range of 10 to 90% by weight, more preferably 10 to 60% by weight, and the moisture absorbing and releasing medium in the range of 10 to 90% by weight, more preferably 40 to 90% by weight. preferable.
[0032]
The particle size of the microcapsules is not particularly limited in the present invention, but if it is too small, it is difficult to manufacture the microcapsules themselves, and it is also difficult to break the shell by heating, pressure, or the like. The purpose may not be achieved.On the contrary, if it is too large, it may be difficult to disperse in the aqueous resin coating agent, or the coating aptitude may deteriorate, or the surface of the coating film may be extremely roughened. In general, the average particle size is desirably about 0.1 to 100 μm.
[0033]
As described above, the microcapsule itself in which a superabsorbent polymer or the like is encapsulated in a shell made of a non-permeable thermoplastic resin is disclosed in, for example, JP-A-62-220631 and JP-A-10-279909. As already mentioned, it is already known.
[0034]
Similar to this, as shown in Japanese Patent Application Laid-Open No. H11-76815, a microcapsule in which a moisture absorbing / releasing medium is enclosed inside a shell having a large number of micropores is also known. Porous shells generally do not meet the purpose of the present invention. The moisture absorbing / desorbing medium absorbs the moisture that has penetrated through the fine pores of the shell, causing the water-based resin coating agent to increase the viscosity or gelling. This is because the shell may ooze out of the micropores to the outside of the shell, or the shell may be broken without being able to withstand the internal pressure due to the swelling.
[0035]
After preparing the microcapsules as described above, the microcapsules are then dispersed in an aqueous resin solution or dispersion to prepare an aqueous resin coating composition.
[0036]
Specific examples of the water-based resin include water-soluble salt-type acrylic resins, water-soluble resins such as polyacrylamide, polyvinyl alcohol, polyvinylpyrrolidone, casein, cellulose derivatives, dextrins, and acrylic resins, polyurethane resins, and styrene. -An aqueous emulsion resin or the like obtained by dispersing water-insoluble resin particles such as butadiene copolymer resin, vinyl acetate resin, ethylene-vinyl acetate copolymer resin, silicone resin, and polybutene resin in water, or the like; Or a mixture of two or more of the above.
[0037]
In the case where the aqueous resin contains at least a water-soluble resin, for example, a melamine compound, a blocked isocyanate compound, and the like, so that the coating film is not dissolved even if the produced moisture-absorbing / desorbing material is wet with water. After coating, the resin in the coating film is cross-linked by adding a cross-linking agent such as an epoxy compound, a hydrazine derivative, an aziridine, an organic peroxide, or irradiating ionizing radiation such as an electron beam. It is desirable to make it insoluble.
[0038]
When comparing the water-soluble resin and the aqueous emulsion resin, the stability of the coating liquid and the surface properties after coating and drying, in terms of high moisture permeability by becoming a microporous, the aqueous emulsion resin Adoption is desirable. In addition, it is a matter of course that the aqueous emulsion-based resin may be crosslinked after coating by blending a crosslinking agent or irradiating with ionizing radiation.
[0039]
The amount of the microcapsules to be added to the aqueous resin coating agent is not particularly limited in the present invention, but if it is too small, a sufficient moisture absorbing / releasing effect cannot be obtained, and conversely, it is too large. Also, since the binder resin content is relatively small, the coating film becomes brittle and causes a decrease in surface strength. Therefore, generally, about 10 to 200 parts by weight based on 100 parts by weight of the solid content of the aqueous resin More preferably, it is preferably in the range of about 30 to 150 parts by weight.
[0040]
In addition to the microcapsules, the water-based resin coating agent may optionally contain, for example, a coloring agent, a filler, a dispersant, an antifoaming agent, a wetting agent, a thickener, a flame retardant, a flame retardant, and an ultraviolet absorber. Various additives such as a light stabilizer, an antioxidant, an antistatic agent, a lubricant, a lubricant, a gloss adjusting agent, an antibacterial agent, and a fungicide can be appropriately added.
[0041]
Further, the coating film may be foamed into a porous cell by a conventionally known means such as a mechanical foaming method or a method of adding a foaming agent, thereby further improving the moisture permeability of the coating film. In addition, the function of absorbing and releasing moisture can be fully exhibited. Further, when the moisture-absorbing and desorbing material of the present invention is used for interior materials such as wallpaper in buildings such as houses, it is easy to form an embossed pattern by embossing by foaming a coating film of an aqueous resin coating agent. There is also an advantage that an interior material excellent in design can be easily obtained.
[0042]
Examples of the foaming agent include organic foaming agents such as azo compounds such as azodicarbonamide (ADCA), nitroso compounds such as p, p'-oxybisbenzenesulfonylhydrazide (OBSH), and sodium hydrogen carbonate and ammonium carbonate. Thermally decomposable chemical foaming agents such as inorganic foaming agents, etc., and low boiling point liquids such as isobutane are contained inside a thermosoftening flexible shell such as polyacrylonitrile resin, phenolic resin, epoxy resin, etc. Thermal expansion type microcapsule foaming agent or the like can be used.
[0043]
The addition amount of the foaming agent is not particularly limited in the present invention, but it is generally preferable to add about 1 to 20 parts by weight, more preferably 100 parts by weight of the solid content of the aqueous resin. Is 3 to 10 parts by weight. When the amount is less than 1 part by weight, the expansion ratio is low, the effect of improving the moisture absorption / release function cannot be expected much, and the improvement of the design by the embossed uneven pattern is difficult. On the other hand, if it exceeds 20 parts by weight, the foamed cells will be extremely coarse and the surface strength of the coating film after foaming will be weakened.
[0044]
After preparing the aqueous resin coating agent as described above, it is applied to the surface of an appropriate substrate to form a coating film. The material and shape of the substrate to be coated are not particularly limited in the present invention, and may be appropriately selected according to the use of the hygroscopic material to be manufactured.
[0045]
Examples of materials that can be used as the base material include, for example, paper, fibrous sheets such as woven or nonwoven fabrics, synthetic resin sheets such as polyolefin resin sheets and polyester resin sheets, acrylic resin sheets, and synthetic rubber sheets. , Acrylic resin plate, polycarbonate resin plate, ABS resin plate, synthetic resin base material such as FRP, plywood, laminated wood, wood fiber board, wood base material such as particle board, steel plate, brass plate, stainless steel plate, aluminum plate And inorganic base materials such as a gypsum board, a calcium silicate plate, a cement plate, and a concrete plate, or a laminate of a plurality of types thereof.
[0046]
If necessary, the surface of the base material may be, for example, a filler treatment, a base coat treatment, a polishing treatment, a primer treatment, a corona discharge treatment, an ozone treatment, a plasma treatment, a flame treatment, an ionizing radiation treatment, an acid treatment, an alkali treatment, or the like. May be subjected to an appropriate surface treatment.
[0047]
In particular, when the moisture-absorbing and desorbing material of the present invention is used as wallpaper, any sheet-like material conventionally used as a base material for synthetic resin-based wallpaper (so-called vinyl wallpaper) can be used.
[0048]
Specifically, for example, pulp paper-based flame-retardant paper obtained by impregnating a water-soluble flame retardant such as guanazine sulfanilate or guanazine phosphate into paper-made paper made of cellulosic fibers such as wood pulp, or carbonic acid during papermaking of cellulosic fibers Inorganic fiber paper made by mixing inorganic fibers such as calcium, aluminum hydroxide or magnesium hydroxide, and inorganic fibers such as glass fiber, alumina fiber, potassium titanate fiber alone or mixed with cellulosic fiber. Any of flame-retardant paper or non-combustible paper, or a flame-retardant or non-flammable woven or non-woven fabric produced by adding a flame retardant or an inorganic agent or using an inorganic fiber can be used.
[0049]
As a method of applying the aqueous resin coating agent on the substrate, for example, knife coating method, air knife coating method, nozzle coating method, gravure coating method, micro gravure coating method, rotary screen coating method, reverse roll coating method, Conventionally known arbitrary coating methods such as a comma coating method, a lip coating method, a die coating method, a spray coating method, a dip coating method, and a flow coating method can be adopted.As a drying method after the coating, for example, hot air or A heat source such as an infrared heater can be used alone or in combination of two or more of them.
[0050]
The coating amount of the aqueous resin coating agent is not particularly limited in the present invention, but a sufficient moisture absorbing / releasing effect cannot be obtained because the absolute amount of the moisture absorbing / releasing medium contained is too small if the thickness is too small. On the other hand, if the thickness is too large, the moisture absorbing / releasing medium contained in the bottom layer portion does not substantially function and the material is wasted. Therefore, it is necessary to appropriately design in consideration of these.
[0051]
Generally, in order to obtain a sufficient moisture absorption / release effect, it is necessary to form a coating film having a thickness of at least 10 μm, more preferably at least 30 μm. On the other hand, the upper limit of the thickness depends on the moisture permeability of the coating film, but when it is a non-foamed layer in which it is difficult to improve the moisture permeability, it is approximately 300 μm. The upper limit is preferably about 2000 μm.
[0052]
After applying the aqueous resin coating agent in this manner and sufficiently drying to form a coating film, at least a part of the microcapsule shells among the microcapsules containing the moisture absorbing / releasing medium contained in the coating film is removed. Breaking is performed to expose the moisture absorbing / releasing medium contained in the microcapsules to the outside of the shell. By performing this treatment, the moisture absorbing / releasing medium can absorb water vapor in the outside air, or can dissipate the absorbed water into the outside air as water vapor, and the coating film has a moisture absorbing / releasing function. Acquires it and becomes a moisture absorbing / releasing resin layer.
[0053]
Most ideally, microcapsule shell destruction can be performed on all microcapsules contained in the coating film, but it is not practical to destroy all microcapsule shells in practice. It is sufficient to break as many microcapsule shells as possible so as to exhibit a practically sufficient moisture absorbing / releasing function.
[0054]
Regarding the method of breaking the shell of the microcapsule, any method may be applied without particular limitation in the present invention, but the most common methods are a method by heating and a method by pressurization. Of course, both can be used together.
[0055]
The principle of the former method by heating mainly includes the following two types. The first is to use a phenomenon in which the thermoplastic resin constituting the shell melts and flows, the thickness of the shell becomes uneven, and finally a hole is formed. In this case, it is necessary to heat to at least the melting point of the thermoplastic resin constituting the shell. Further, if the thermoplastic resin constituting the shell is excessively crosslinked, the melt viscosity becomes high and it becomes difficult to flow. Therefore, it is advantageous that the crosslinking is not performed or the crosslinkage is reduced.
[0056]
The second is to utilize the difference in thermal expansion between the shell and the inclusion. When the moisture expansion / desorption medium, which is the inclusion, has a higher thermal expansion coefficient than the shell and the shell has a small elongation, It utilizes a phenomenon in which the shell cannot follow the expansion of the moisture-absorbing / desorbing medium due to heating and breaks. In this case, it is necessary to cross-link sufficiently so that the shell is hardly thermally expanded and hardly stretched, but if the cross-linking is too thick or the shell is too thick, the strength of the shell increases and even if heated, Careful attention must be paid to the design of the shell crosslink density and thickness as it is less likely to break.
[0057]
In short, the latter method of applying pressure is a method of applying pressure to the microcapsules and crushing them. In the case of this method, it is advantageous that the shell has a low elongation and is brittle and easily cracked. It is advantageous to use a resin or to sufficiently crosslink between the molecules to make it difficult to elongate. However, care must be taken because excessive cross-linking or too thick shell increases the strength of the shell and makes it difficult to break even when pressed.
[0058]
In order to more efficiently break the shell of the microcapsule, it is effective to use both heating and pressurization. In the case of the above-described type utilizing the melt flow of the shell, the pressurization promotes the flow of the melted shell, and holes are easily formed. Further, even in the latter case of the type utilizing the difference in thermal expansion, stress due to pressure is applied to the stress due to the difference in thermal expansion, so that the shell is easily broken.
[0059]
Pressurization of the coating film may be performed by a flat pressure method, but in particular, when the base material is in a sheet shape, a circular pressure (roll press) method is adopted in consideration of continuous productivity. There are many. In this case, when the sheet passes between the rolls, a considerably large frictional force is generated between the surface of the coating film and the surface of the roll, and this frictional force is at least the microscopic force existing near the surface of the coating film. Acts to promote the destruction of the capsule shell.
[0060]
This effect is particularly remarkable when microcapsules of the above-mentioned type utilizing the shell melt flow are used in combination with heating. Therefore, the most efficient method for breaking the shell is to apply pressure while heating to a temperature equal to or higher than the melting point of the thermoplastic resin constituting the shell.
[0061]
However, since the above-mentioned action hardly reaches the microcapsules existing in the bottom layer portion of the coating film, if this action is relied on too much, microcapsules that do not contribute to the moisture absorbing / releasing function will eventually be wasted. Will be. In order to reduce this waste, microcapsules containing a moisture absorbing / releasing medium may be concentrated near the surface of the coating film.
[0062]
As the method, using a microcapsule having a smaller specific gravity than an aqueous solution or aqueous dispersion of an aqueous resin which is a main component of an aqueous resin coating agent, the microcapsules are formed by the action of gravity in a coated film after application. Hydrophobicity is imparted to the surface of the microcapsules by attaching a hydrophobic substance such as a silicone compound or a fatty acid derivative to the surface of the microcapsules, and the microcapsules are coated using water repulsion. A method of floating on the surface can be used.
[0063]
Regardless of the type of shell breaking method, if the microcapsules enclosing the moisture absorbing / releasing medium are concentrated near the surface of the coating film, the inhibition of the binder resin with respect to moisture absorbing / releasing with the outside air is prevented. Since the number of microcapsules is small, the use of the same amount of microcapsules is advantageous because the moisture absorption / release rate and the saturated moisture absorption can be further improved.
[0064]
When a foaming agent is added to the aqueous resin coating composition and foaming is performed by heating after the coating, the shell of the microcapsule can be broken simultaneously with the foaming of the coating film by heating during the foaming. For example, by using a microcapsule whose shell is made of a thermoplastic resin and performing heating and foaming at a temperature equal to or higher than its melting point, the shell of the microcapsule can be broken at the same time as the foaming, and the moisture absorption / release function can be exhibited. it can.
[0065]
After the application of the aqueous resin coating agent, the surface of the coating film is pressed by using an embossing plate or embossing roll made of metal or the like in order to impart a three-dimensional design feeling due to the uneven pattern. Embossing can be applied. At that time, the shell of the microcapsule is broken by utilizing the pressure at the time of the embossing, so that the function of absorbing and releasing moisture can be exhibited simultaneously with the provision of the uneven pattern.
[0066]
The embossing may be performed at room temperature, but is generally performed under heating (heating embossing) in order to soften the coating by heat and easily form an uneven pattern. There are many. The shell of the microcapsule is broken by the heating and pressurization during the heating embossing, and the shell can be broken very efficiently by the synergistic effect of the heating effect and the pressurizing effect. .
[0067]
For example, by using a microcapsule whose shell is made of thermoplastic resin and performing heating embossing at a temperature equal to or higher than its melting point, the shell of the microcapsule is destroyed simultaneously with the heating embossing, and a moisture absorption / release function is exhibited. Can be done.
[0068]
When performing both of the above-mentioned heat foaming and heat embossing treatment on the coating film of the aqueous resin coating agent, it is common to heat foam first and then perform heat embossing. The latter heating embossing is generally performed at a higher temperature and in a shorter time than the former heating foaming.
[0069]
In this case, the destruction of the shell of the microcapsule can be performed already in the heating foaming step, which is the previous step, or by performing the heating in a temperature range that does not break the shell during foaming. The shell may form an unbroken foam layer, and thereafter, in a heating embossing step, the shell may be broken by heating and pressing.
[0070]
However, when comparing the above, according to the former method, the shell is broken in the heating and foaming step, and the moisture absorbing / releasing medium which is exposed from the shell and dispersed in the binder resin of the foamed layer is heated in the subsequent heating embossing step. As a result of being compacted in a form surrounded by the molten binder resin, the obtained moisture absorbing / releasing effect may be reduced.
[0071]
On the other hand, according to the latter method, the microcapsules, whose shells remain intact during heating and foaming, are pushed up to the vicinity of the surface of the foamed layer by the action of foaming of the coating film, and then heated and embossed. In the process, by heating and pressing for a short time, the shell of the microcapsule is broken and the moisture absorbing / releasing medium is exposed without greatly changing the relationship with the surrounding foam layer, resulting in excellent moisture absorbing / releasing effect. There is an advantage that it is easy to do.
[0072]
In the moisture-absorbing and desorbing material obtained by the production method of the present invention, although the moisture-absorbing and desorbing medium contained in the microcapsules is exposed due to the destruction of the shell of the microcapsules, the microcapsules themselves absorb and release. In addition to being present in a dispersed state in the moisture-absorbing resin layer, since a large part of the surface of the moisture-absorbing / desorbing medium is covered with shell debris, the dispersion of the superabsorbent polymer is simply used. Compared to the case where the composition is applied to the surface or the like, the stickiness of the surface at the time of high humidity or wet with water is far less.
[0073]
However, if the problem of stickiness of the surface at the time of high humidity or wetness is still worrisome, the surface of the hygroscopic resin layer containing the microcapsules enclosing the hygroscopic medium obtained as described above may be used. May be provided with a moisture-permeable protective layer. This moisture-permeable protective layer also has an effect of preventing discoloration due to absorption of colored moisture by the moisture absorbing / releasing medium, and improving stain resistance.
[0074]
The moisture-permeable protective layer itself has water resistance to the extent that it does not dissolve in water or swell due to water absorption, and the base coat containing microcapsules containing a moisture absorbing / releasing medium and the outside air Any material can be used as long as it has a moisture permeability that does not impede the flow of water vapor between it and acrylic resin, urethane resin, styrene-butadiene copolymer resin, vinyl acetate resin, ethylene-vinyl acetate copolymer. A polymer-based resin, an ethylene-vinyl alcohol copolymer-based resin, a silicone-based resin, a polyamide-based resin, a polybutene-based resin, or the like can be used, and a mixture of two or more of these, a laminated film, or the like may be used.
[0075]
If the thickness of the moisture-permeable protective layer is too small, the waterproofness becomes insufficient, so that it is not possible to obtain sufficient effects such as stickiness prevention and contamination prevention. It is necessary to appropriately design in consideration of both of them, since it may cause the moisture release performance to be reduced. In general, it is preferable to design in the range of about 0.5 to 20 μm.
[0076]
There is no restriction on the timing of forming the moisture-permeable protective layer, and after application of the aqueous resin coating agent, it may be before or after breaking the shell of the microcapsule, or when foaming. May be before or after foaming, and may be before or after embossing. Furthermore, you may apply | coat and form simultaneously with application | coating of an aqueous resin coating agent by a multilayer coating method. In addition, if necessary, an appropriate pattern may be printed on the surface of the moisture-absorbing and releasing resin layer and / or the surface of the moisture-permeable protective layer.
[0077]
【Example】
Hereinafter, the present invention will be described in more detail with reference to specific examples and comparative examples.
[0078]
Example 1
<Preparation of microcapsules>
A separable flask was charged with 30 parts by weight of silica gel powder having an average particle size of 0.7 μm dispersed in 100 parts by weight of water, and nitrogen was blown in to replace the air. This was heated to 80 ° C, 80 parts by weight of diaminoethyl methacrylate was added, and the mixture was suspended at 80 ° C for 1 hour. Thereafter, an 8% aqueous solution of ammonium persulfate was added dropwise over 1 hour, and then kept at 80 ° C. for 2 hours. Microcapsules containing silica gel powder and having an average particle size of about 1 μm, a shell melting point of about 180 ° C., and a solid content of 50% by weight were added. Was obtained.
[0079]
<Preparation of aqueous resin coating agent>
When 100 parts by weight of the aqueous dispersion of the above microcapsules is mixed with 100 parts by weight of an aqueous acrylic resin emulsion having a solid content of 50% by weight and a melting point of the solid content resin of about 170 ° C., the viscosity increases or gels. No water-based resin coating agent having good coating suitability was obtained.
[0080]
<Preparation of hygroscopic material>
The aqueous resin coating composition was applied to a surface of a normal backing paper for wallpaper to a coating thickness of 100 μm after drying, and dried at 100 ° C. for 3 minutes. The drying conditions at that time were the same as those in the case where a coating agent containing no microcapsules was applied with the same thickness, and the drying was quick and sufficient, and the surface condition after drying was also good. . Thereafter, heat embossing was performed at 250 ° C. for 30 seconds to form a concavo-convex pattern and simultaneously break the shell of the microcapsule to produce the moisture-absorbing and releasing material of the present invention.
[0081]
Comparative Example 1
When 100 parts by weight of the same silica gel powder as used in the preparation was mixed with 100 parts by weight of the acrylic resin aqueous emulsion in place of the microcapsules, the solution gelled and became impossible to apply. Then, when conditions for obtaining an aqueous resin coating agent that can be applied while reducing the amount of the silica gel powder were searched, it was found that the limit was 10 parts by weight of the silica gel powder per 100 parts by weight of the acrylic resin aqueous emulsion. . Therefore, a water-based resin coating agent was prepared at this mixing ratio, and a moisture-absorbing and desorbing material was produced under the same conditions as in Example 1 above.
[0082]
Example 2
For comparison with Comparative Example 1, in Example 1, the amount of the microcapsules was reduced to 10 parts by weight with respect to 100 parts by weight of the aqueous acrylic resin emulsion, and the other conditions were the same as in Example 1 above. Was prepared.
[0083]
Moisture absorption / release test
The moisture absorbing and releasing materials of Examples 1 and 2 and Comparative Example 1 were first cured for 24 hours in an environment of 25 ° C. and 50% RH, and then placed in an environment of 25 ° C. and 90% RH. 120 hours after it was determined that the sample was sufficiently saturated, the sample was returned to an environment of 25 ° C. and 50% RH, and the change in weight with time was determined. The results are shown in the graph of FIG. However, the amount of moisture absorption is the amount of weight increase after moisture absorption based on the weight at the completion of the first curing.
[0084]
As shown in this graph, it was confirmed that there was almost no difference in the moisture absorption / release effect between the microcapsulated product (Example 2) and the non-encapsulated product (Comparative Example 1) when the blending amount was the same. . The former can be blended in a larger amount than the latter (Example 1), thereby demonstrating the advantage that a much larger moisture absorbing / releasing function can be imparted than the latter.
[0085]
Example 3
<Preparation of aqueous resin coating agent>
100 parts by weight of the aqueous dispersion of microcapsules prepared in Example 1 above, 100 parts by weight of an acrylic resin aqueous emulsion having a solid content of 50% by weight and a melting point of the solid content resin of about 170 ° C., and a shell made of polyacrylonitrile resin Was mixed with 5 parts by weight of a microcapsule foaming agent containing isobutane inside to prepare an aqueous resin coating agent.
[0086]
<Preparation of hygroscopic material>
The above aqueous resin coating agent is applied to the surface of a normal backing paper for wallpaper to a coating thickness of 100 μm after drying, dried at 100 ° C. for 3 minutes, and then heated to 220 ° C. for foaming, and at the same time, silica gel The shell of the microcapsule containing the powder was broken to produce the moisture-absorbing and releasing material of the present invention.
[0087]
Example 4
In the above Example 3, foaming of the aqueous resin coating composition after drying was performed at 160 ° C. at which the shell of the microcapsule containing the silica gel powder was not broken, and thereafter, heat embossing was performed at 250 ° C. for 30 seconds. Then, the shell of the microcapsule was broken at the same time as forming the concavo-convex pattern, thereby producing the moisture-absorbing and releasing material of the present invention.
[0088]
Example 5
In the above Example 4, a moisture-permeable polyurethane-based resin was applied to a thickness of 3 μm after drying by a spray coating method on the surface of the coating film after the heat embossing to form a moisture-permeable protective layer. Was prepared.
[0089]
When a moisture absorption / desorption test was performed on the moisture absorption / desorption materials of Examples 3 to 5 under the same conditions as described above, it was confirmed that each of them exhibited a moisture absorption / desorption effect almost equivalent to that of Example 1 above. Was.
[0090]
【The invention's effect】
As described in detail above, according to the method for producing a moisture-absorbing / desorbing material of the present invention, the moisture-absorbing / desorbing medium is formed into a microcapsule coated with a water-impermeable shell, so that the coating is performed by thickening or gelling. Without making it difficult, it is possible to significantly increase the compounding amount in the aqueous resin coating composition as compared with the conventional case.
[0091]
In addition, the moisture absorbing / releasing medium contained in the microcapsules does not absorb water during compounding or coating of the aqueous resin coating agent and does not release the water during drying. The amount of heat required for drying and the load such as drying time are not increased, and the surface of the coating film is not roughened due to the release of moisture during drying.
[0092]
Then, after the application of the coating agent, at least a part of the shell of the microcapsule is broken by heating and / or pressurizing, thereby exposing the moisture absorbing / releasing medium contained in the microcapsule to the outside of the shell. Therefore, a remarkable effect of exhibiting a much better moisture absorption / release effect than before can be achieved.
[Brief description of the drawings]
FIG. 1 is a graph showing the results of a moisture absorption / release performance test of Examples and Comparative Examples of the present invention.

Claims (14)

非透水性の殻の内部に、吸水性物質及び／又は吸湿性物質を少なくとも含む吸放湿媒体を内包したマイクロカプセルを、水性樹脂の溶液又は水分散液中に分散してなる水性樹脂塗工剤を、基材上に塗布し乾燥させて塗膜を形成した後、前記塗膜中のマイクロカプセルの少なくとも一部の殻を破壊して、該マイクロカプセルに内包された吸放湿媒体を殻の外に露出させて、吸放湿性樹脂層を形成することを特徴とする吸放湿性材料の製造方法。Aqueous resin coating in which microcapsules containing a moisture absorbing / releasing medium containing at least a water absorbing material and / or a moisture absorbing material inside a water impermeable shell are dispersed in an aqueous resin solution or aqueous dispersion. After the agent is applied on a substrate and dried to form a coating film, at least a part of the shell of the microcapsule in the coating film is broken, and the moisture absorbing / releasing medium contained in the microcapsule is coated with the shell. Forming a moisture-absorbing / desorbing resin layer by exposing the material to the outside. 前記マイクロカプセルの殻の破壊を、加熱により行うことを特徴とする請求項１に記載の吸放湿性材料の製造方法。The method for producing a moisture-absorbing and releasing material according to claim 1, wherein the breaking of the shell of the microcapsule is performed by heating. 前記マイクロカプセルの殻の破壊を、加圧により行うことを特徴とする請求項１に記載の吸放湿性材料の製造方法。The method for producing a moisture-absorbing and releasing material according to claim 1, wherein the shell of the microcapsule is broken by pressurization. 前記マイクロカプセルの殻の破壊を、加熱及び加圧の併用により行うことを特徴とする請求項１に記載の吸放湿性材料の製造方法。The method for producing a moisture-absorbing / desorbing material according to claim 1, wherein the shell of the microcapsule is broken by a combination of heating and pressure. 前記マイクロカプセルの殻は熱可塑性樹脂からなり、前記加熱は該熱可塑性樹脂の融点以上の温度にまで加熱することを特徴とする請求項２又は４に記載の吸放湿性材料の製造方法。5. The method according to claim 2, wherein the shell of the microcapsule is made of a thermoplastic resin, and the heating is performed to a temperature equal to or higher than the melting point of the thermoplastic resin. 前記水性樹脂塗工剤にさらに発泡剤を配合し、塗膜の形成後に発泡させることを特徴とする請求項１〜５のいずれかに記載の吸放湿性材料の製造方法。The method for producing a moisture-absorbing and desorbing material according to any one of claims 1 to 5, wherein a foaming agent is further added to the aqueous resin coating agent, and foaming is performed after forming a coating film. 前記発泡は加熱により行い、該加熱により該発泡と同時に前記マイクロカプセルの殻の破壊を行うことを特徴とする請求項６に記載の吸放湿性材料の製造方法。The method according to claim 6, wherein the foaming is performed by heating, and the shell of the microcapsule is broken at the same time as the foaming is performed by the heating. 前記マイクロカプセルの殻は熱可塑性樹脂からなり、前記発泡の際の加熱は該熱可塑性樹脂の融点以上の温度にまで加熱することを特徴とする請求項７に記載の吸放湿性材料の製造方法。The method according to claim 7, wherein the shell of the microcapsule is made of a thermoplastic resin, and the heating during the foaming is performed to a temperature equal to or higher than the melting point of the thermoplastic resin. . 前記塗膜の表面にエンボス加工を施すことを特徴とする請求項１〜８のいずれかに記載の吸放湿性材料の製造方法。The method according to any one of claims 1 to 8, wherein the surface of the coating film is embossed. 前記エンボス加工の際の加圧により、前記マイクロカプセルの殻の破壊を行うことを特徴とする請求項９に記載の吸放湿性材料の製造方法。The method for producing a moisture-absorbing and desorbing material according to claim 9, wherein the shell of the microcapsule is broken by applying pressure during the embossing. 前記エンボス加工は加熱エンボス加工であり、該加熱エンボス加工の際の加熱及び加圧により、前記マイクロカプセルの殻の破壊を行うことを特徴とする請求項１０に記載の吸放湿性材料の製造方法。The method according to claim 10, wherein the embossing is heating embossing, and the shell of the microcapsule is destroyed by heating and pressing during the heating embossing. . 前記マイクロカプセルの殻は熱可塑性樹脂からなり、前記加熱エンボス加工の際の加熱は該熱可塑性樹脂の融点以上の温度にまで加熱することを特徴とする請求項１１に記載の吸放湿性材料の製造方法。The moisture absorbing and releasing material according to claim 11, wherein the shell of the microcapsule is made of a thermoplastic resin, and heating during the heating embossing is performed to a temperature equal to or higher than the melting point of the thermoplastic resin. Production method. 前記マイクロカプセルは、前記吸放湿性樹脂層の表面近傍に濃集していることを特徴とする請求項１〜１２のいずれかに記載の吸放湿性材料の製造方法。The method according to any one of claims 1 to 12, wherein the microcapsules are concentrated near the surface of the moisture-absorbing and releasing resin layer. 前記吸放湿性樹脂層の表面に、透湿性の保護層を設けることを特徴とする請求項１〜１３のいずれかに記載の吸放湿性材料の製造方法。The method for producing a moisture-absorbing / desorbing material according to any one of claims 1 to 13, wherein a moisture-permeable protective layer is provided on a surface of the moisture-absorbing / desorbing resin layer.