JP2004091302A - Method of manufacturing optical fiber preform - Google Patents
Method of manufacturing optical fiber preform Download PDFInfo
- Publication number
- JP2004091302A JP2004091302A JP2002258920A JP2002258920A JP2004091302A JP 2004091302 A JP2004091302 A JP 2004091302A JP 2002258920 A JP2002258920 A JP 2002258920A JP 2002258920 A JP2002258920 A JP 2002258920A JP 2004091302 A JP2004091302 A JP 2004091302A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- glass pipe
- pressure
- optical fiber
- pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】
【発明の属する技術分野】
本発明は、クラッド用ガラスパイプ内に、コア用ガラスロッド、又はコア及びクラッド用ガラスロッドを挿入し、上記ガラスパイプ内を減圧しながら両者を加熱することで、上記ガラスパイプとガラスロッドとの一体化及び延伸を行う光ファイバ母材の製造方法に関する。
【0002】
【従来の技術】
従来より、光ファイバにおいてクラッドとなるガラスパイプ内に、光ファイバにおいてコアとなるガラスロッド、又はコア及びクラッドとなるガラスロッドを挿入し、このガラスパイプとガラスロッドとを一体化させて光ファイバ母材を製造する、いわゆるロッドインチューブ法が知られている(例えば、特許文献1参照)。このロッドインチューブ法では、例えばガラスロッドが内挿されたガラスパイプ内を減圧しつつ、このガラスパイプとガラスロッドとの双方を、その軸方向に略リング状のヒータ内に通過させる。こうすることで、ガラスパイプとガラスロッドとがその一端から他端に向かって順次加熱され、溶融したガラスパイプがこのガラスパイプ内外の圧力差によって縮径する。このことによって、ガラスパイプとガラスロッドとが順次一体化して、光ファイバ母材が製造される。
【0003】
こうして製造された光ファイバ母材は線引き工程によって光ファイバとなるわけであるが、この線引き工程を上記ロッドインチューブ法による光ファイバ母材の製造と同時に行う方法も知られている(例えば、特許文献2参照)。
【0004】
ところで、近年、生産コストの低減化等の観点から、光ファイバ母材を大型化することが求められており、このため、上記光ファイバ母材を大径にすることが行われている。
【0005】
ところが、このような大径の光ファイバ母材をそのまま線引きすると、目標径の光ファイバに安定させるまでに長時間を要することとなってしまい、大量の母材を初期安定化に消費してしまうようになってしまう。その結果、上記光ファイバ母材から光ファイバへの歩留まりが悪化してしまい、本来低コスト化の目的で行った光ファイバ母材の大型化が、逆にその目的を達成できないものとなってしまうという不都合がある。
【0006】
そこで、このような不都合を解消するために、通常は製造された大径の光ファイバ母材を、線引き工程の前に歩留まりが最大となる最適の径まで縮径させるようにしている。そして、この光ファイバ母材の縮径工程を、上記ガラスパイプ及びガラスロッドの一体化による光ファイバ母材の製造と同時に行うことにより、生産性を向上させる方法が知られている(例えば、特許文献3参照)。
【0007】
【特許文献1】
特公昭56−45867号公報
【特許文献2】
特開昭50−85345号公報
【特許文献3】
特開平7−10580号公報
【0008】
【発明が解決しようとする課題】
ところで、ロッドインチューブ法による光ファイバ母材の製造においては、ガラスパイプとガラスロッドとの間に生じている隙間をガラスパイプを縮径変形させることによって潰して、このガラスパイプとガラスロッドとを一体化させるようにしている。このため、その製造条件によっては、ガラスパイプとガラスロッドとが偏心した状態で一体化してしまう場合がある。こうしてガラスパイプとガラスロッドとが偏心してしまうと、光ファイバ母材において、光ファイバのコアとなる部分(以下、この部分をコア部という)が偏心してしまうこととなり、それに伴い、この光ファイバ母材を線引きした光ファイバにおいてはコアが偏心してしまうようになる。
【0009】
また、ロッドインチューブ法による光ファイバ母材の製造においては、ガラスパイプを縮径変形させるため、その製造条件によっては、ガラスパイプが周方向に不均一に変形してしまい、その結果、光ファイバ母材の横断面形状が、真円形状でなく例えば楕円形状等になってしまう場合がある。
【0010】
本発明は、このような事情に鑑みてなされたものであり、その目的とするところは、ガラスパイプとガラスロッドとの一体化及び延伸によって光ファイバ母材を製造するときに、光ファイバ母材におけるコア部の偏心を防止すると共に、光ファイバ母材の横断面形状のゆがみを防止することにある。
【0011】
【課題を解決するための手段】
上記目的を達成するために、本発明者は、先ず、ガラスパイプとガラスロッドとを一体化させるときのガラスパイプ内の圧力に着目した。すなわち、従来のロッドインチューブ法による光ファイバの製造方法では、ガラスパイプとガラスロッドとの一体化を確実に行うため、ガラスパイプ内の圧力を極力低くして(ガラスパイプ内の真空度を高めて)、ガラスパイプとガラスロッドとの一体化を行うようにしていた。
【0012】
このように、ガラスパイプ内の圧力を低く設定することにより、ガラスパイプ内外の圧力差が大きくなってガラスパイプを縮径させる力が高まり、ガラスパイプとガラスロッドとを確実に一体化させることが可能になるものの、ガラスパイプ内の圧力が低いときには、コアの偏心を招いてしまうことが、本発明者が行った実験により確認された。これは、ガラスパイプ内の圧力を低く設定することによりガラスパイプを縮径させる力が高まることで、ガラスロッドが溶融する前の固体状態のガラスロッドがガラスパイプに対して偏心している状態で、ガラスパイプの縮径変形によってガラスパイプとガラスロッドとが一体化してしまい、その結果、光ファイバ母材におけるコア部の偏心を招き、ひいては光ファイバにおけるコアの偏心を招いているものと考えられる。
【0013】
そこで、本発明者が、ガラスパイプ内の圧力を比較的高く設定して、光ファイバ母材を製造したところ、ガラスパイプとガラスロッドとの偏心が抑制された。これは、ガラスパイプ内の圧力が高いことでガラスパイプを縮径させる力が小さくなるが、こうすることで、ガラスパイプの縮径変形は緩やかになって、十分に溶融したガラスロッドが、ガラスパイプの縮径変形によってその中心に向かって移動するようになり、ガラスパイプとガラスロッドとが略同軸となった状態で、このガラスパイプとガラスロッドとが一体化するためと考えられる。
【0014】
しかしながら、ガラスパイプ内の圧力を比較的高く設定したときには、今度は、光ファイバ母材の横断面形状にゆがみが生じ、横断面形状が楕円形状等になってしまう不都合が生じた。
【0015】
これは、ガラスパイプとガラスロッドとは、一体化される際に、略リング状に形成されたヒータ内を通過することによって、全周にわたって加熱されるが、このとき、上記ガラスパイプに加えられる熱の周方向分布が不均一であることに起因していると考えられる。
【0016】
つまり、ガラスパイプ内の圧力が比較的低いときには、ガラスパイプを縮径させる力が強いため、熱分布が不均一であっても、ガラスパイプは周方向に略均等に縮径変形してガラスロッドと一体化する。このため、光ファイバ母材の横断面形状は略真円形状となる。
【0017】
ところが、ガラスパイプ内の圧力が比較的高く、このガラスパイプを縮径させる力が弱いときには、周方向に対する熱分布の不均一性によって、ガラスパイプにおいて、十分に加熱されて十分溶融した部分は縮径変形しやすくなり、十分に加熱されずに溶融が不十分な部分は縮径変形し難くなる。こうして、ガラスパイプは均等に縮径変形しなくなり、その結果、ガラスパイプ内の圧力が比較的高いときには、光ファイバ母材の横断面形状のゆがみが発生してしまうものと考えられる。
【0018】
このように、光ファイバ母材の横断面形状のゆがみを防止するには、ガラスパイプ内の圧力を低く設定することが好ましいが、こうして、ガラスパイプ内の圧力を低く設定すると、上述したように、コア部の偏心を招くこととなるため、光ファイバ母材におけるコア部の偏心の防止と、光ファイバ母材のゆがみの防止とは、相反する要求となる。
【0019】
そこで、この問題を解消させるべく、本発明者は、ロッドインチューブ法におけるガラスパイプの縮径変形のメカニズムに着目した。
【0020】
すなわち、ロッドインチューブ法による光ファイバの製造方法では、ガラスパイプを、一端から他端に向かって軸方向に順次溶融させると共に、ガラスパイプ内外の圧力差で順次、縮径変形させることによって、このガラスパイプとガラスロッドとを軸方向に順次一体化させるようにしている。このため、ガラスパイプにおいて、溶融して変形途中にある部分は、既に縮径変形してガラスロッドと一体化している部分と連なっている。
【0021】
こうして、上記溶融して変形途中にある部分が、ガラスロッドと一体化している部分に連なっていることで、上記変形途中にある部分が縮径変形するときは、上記ガラスロッドと一体化している部分に引き寄せられるように変形する。そのため、上記溶融して変形途中にある部分がガラスロッドと一体化したときには、その横断面形状は、それよりも以前の時点でガラスロッドと一体化した部分における横断面形状と略同じになる。
【0022】
従って、ガラスパイプが周方向に均等に変形せずに、ゆがんだ形状でガラスロッドと一体化してしまうと、その後もガラスパイプは、そのゆがんだ形状に沿うように縮径変形して、ガラスロッドと一体化するようになる。一方、ガラスパイプが周方向に均等に変形して、横断面が真円形状でガラスロッドと一体化すると、その後は、ガラスパイプ内外の圧力差が小さくても、ガラスパイプは、その真円形状に沿うように縮径変形して、ガラスロッドと一体化するようになる。つまり、光ファイバ母材の横断面形状が真円形状となるのである。
【0023】
以上のメカニズムを考慮して、本発明では、ガラスパイプとガラスロッドとを一体化させる開始時には、ガラスパイプ内の圧力を、比較的低圧の第1圧力とする一方、ガラスパイプとガラスロッドとを一体化させている最中に、ガラスパイプ内の圧力を、上記第1圧力から、比較的高圧の第2圧力に切り替えることとした。
【0024】
具体的に、本発明は、ガラスロッドが内挿されたガラスパイプ内を減圧しながら、該ガラスパイプ及びガラスロッドの双方を、その一端から他端に向かって軸方向に順次加熱することで上記ガラスパイプとガラスロッドとを順次一体化しつつ、所定の外径に延伸して光ファイバ母材を製造する光ファイバ母材の製造方法に係る。
【0025】
そして、本発明に係る光ファイバの製造方法では、上記ガラスパイプとガラスロッドとの一体化の開始時には、上記ガラスパイプ内の圧力を、大気圧よりも低い第1圧力に設定すると共に、上記ガラスパイプとガラスロッドとの一体化の最中に、上記ガラスパイプ内の圧力を、上記第1圧力から、該第1圧力よりも高くかつ大気圧よりも低い第2圧力に切り換えることとする。
【0026】
こうすることで、ガラスパイプとガラスロッドとの一体化を開始する時点では、ガラスパイプ内の圧力が、比較的低圧の第1圧力(但し、第1圧力は大気圧よりも低い)に設定される。これにより、ガラスパイプ内外の圧力差が大きくなってガラスパイプを縮径させる力が強くなるため、このガラスパイプは、熱分布が周方向に不均一であっても、周方向に均等に縮径変形してガラスロッドと一体化する。従って、ガラスパイプとガラスロッドとが一体化した部分においては、その横断面形状が真円形状となる。
【0027】
こうして、ガラスパイプとガラスロッドとが、その一端側(一体化開始の端部側)において、真円形状の横断面形状で一体化するようになれば、上記ガラスパイプ内の圧力を、上記第1圧力から、この第1圧力よりも高圧かつ大気圧よりも低圧の第2圧力に切り換える。こうして、ガラスパイプ内の圧力を比較的高圧にした状態で、ガラスパイプとガラスロッドとの一体化を継続する。
【0028】
こうすることで、ガラスパイプを縮径させる力が弱くなるものの、上述したように、上記ガラスパイプは、上記ガラスパイプとガラスロッドとが一体化している部分に引き寄せられるように変形する。一方で、既にガラスパイプとガラスロッドとが一体化している部分においては、その横断面形状が真円形状となっていることから、上記ガラスパイプは、上記真円形状に沿うように縮径変形して、ガラスロッドと一体化するようになる。このため、製造された光ファイバ母材は、その横断面形状が真円形状になる。
【0029】
また、ガラスパイプを縮径させる力が弱くなることで、ガラスパイプの急激な縮径変形が抑制される。これにより、十分に溶融したガラスロッドが、ガラスパイプの縮径変形によってその中心に向かって移動するようになり、ガラスパイプとガラスロッドとが略同軸となった状態で、このガラスパイプとガラスロッドとが一体化する。これにより、ガラスパイプとガラスロッドとの偏心が抑制され、光ファイバ母材において、そのコア部の偏心が抑制される。その結果、上記光ファイバ母材を線引きした光ファイバにおけるコアの偏心が抑制される。
【0030】
こうして、本発明に係る光ファイバ母材の製造方法によると、光ファイバ母材のコア部の偏心が防止されると共に、光ファイバ母材の断面形状のゆがみが防止される。
【0031】
尚、ガラスパイプ内の圧力を、比較的高圧の第2圧力に設定した場合においても、単位時間当たりに一体化するガラスパイプ及びガラスロッドの総ガラス量であるガラス処理量、及び上記ガラスパイプ及びガラスロッドを加熱する加熱温度等の製造条件を適宜設定することによって、ガラスパイプとガラスロッドとを確実に一体化させて、例えばガラスパイプとガラスロッドとを一体化させたときの、パイプ及びロッドの界面における気泡や剥離(以下、界面におけるこうした気泡や剥離を輝点ともいう)の発生を防止することが可能である。
【0032】
ここで、ガラスパイプ内の圧力は、光ファイバ母材の外径が目標外径となったタイミングで、第1圧力から第2圧力に切り換えるようにすればよい。
【0033】
つまり、上述したように、光ファイバ母材は、ガラスパイプとガラスロッドとが軸方向に順次一体化されて製造されるが、この光ファイバ母材の外径が目標外径となるまでの部分は、製品にはなり得ず、光ファイバ母材の外径が目標外径となった後の部分が製品となる。
【0034】
そこで、ガラスパイプとガラスロッドとの一体化を開始してから、光ファイバ母材の外径が目標外径となるまでは、ガラスパイプ内の圧力を比較的低圧の第1圧力とすることによって、ガラスパイプとガラスロッドとの一体化を促進しつつ、横断面形状が真円形状となるように、ガラスパイプとガラスロッドとを一体化させる。
【0035】
一方、光ファイバ母材の外径が目標外径となった後には、それ以降にガラスパイプとガラスロッドとが一体化する部分は製品取りの部分であるから、ガラスパイプ内の圧力を比較的高圧の第2圧力とすることによって、ガラスパイプとガラスロッドとの偏心を抑制する。その結果、歩留まりの向上が図られる。
【0036】
尚、上記第1圧力は、熱分布が不均一であっても、横断面が真円形状となるように、ガラスパイプを縮径変形させることが可能な程度の圧力とすればよく、具体的には、−10kPa(ゲージ圧)よりも低圧とすればよく、−11kPa〜−16kPa程度が好ましい。
【0037】
一方、上記第2圧力は、ガラスパイプとガラスロッドとの偏心を防止し得る程度の圧力とすればよく、具体的には、−10kPa(ゲージ圧)以上とすればよく(但し、大気圧よりも低圧)、好ましくは−5kPa以上、より好ましくは−3kPa以上である。
【0038】
【発明の効果】
以上説明したように、本発明における光ファイバ母材の製造方法によれば、ガラスパイプとガラスロッドとの一体化の最中において、光ファイバ母材の外径が目標外径となったタイミングで、ガラスパイプ内の圧力を、比較的低圧の第1圧力から、比較的高圧の第2圧力に切り換えることにより、光ファイバ母材におけるコア部の偏心と、横断面形状のゆがみとを共に防止することができる。
【0039】
【発明の実施の形態】
以下、本発明の実施形態を図面に基いて説明する。
【0040】
図1は、本発明の実施形態に係る光ファイバ母材の製造装置1を示している。この製造装置1は、ロッドインチューブ法により光ファイバ母材7を製造するものであって、具体的には、光ファイバにおいてクラッドとなるガラスパイプ2と、光ファイバにおいてコアとなる、又はコア及びクラッドとなるガラスロッド3とを一体化させて光ファイバ母材7を製造するように構成されている。
【0041】
ここで、上記ガラスパイプ2としては、例えば、OVD(Outside Vapor−phase Deposition)法等によって製造されたものを用いるようにすればよい。また、ガラスパイプ2としては、その外径がφ180mm程度、内径がφ50mm程度、長さが2000mm程度のものが例示される。
【0042】
また、上記ガラスロッド3としては、VAD(Vapor−phase Axial Deposition)法によってガラス微粒子を堆積させたガラス微粒子堆積体を焼結して延伸したものや、MCVD(Modified Chemical Vapor Deposition)法でクラッドパイプ内面にコアガラスを形成し中実化したものを用いるようにすればよい。また、ガラスロッド3としては、その径がφ45〜50mm程度、長さが2500mm程度のものが例示される。
【0043】
上記製造装置1には、Z方向(同図における上下方向)に延びて配設された上記ガラスパイプ2の上端部分を把持することで、このガラスパイプ2を吊り下げ状態にする第1把持部41と、同じくZ方向に延びて配設された上記ガラスロッド3の上端部分を把持することで、このガラスロッド3を吊り下げ状態にする第2把持部42とが設けられている。この第1及び第2把持部41,42はそれぞれ、ガラスパイプ2及びガラスロッド3の位置を、X方向(同図における紙面横方向)及びY方向(紙面に直行する方向)に移動可能に構成されていると共に、上記ガラスパイプ2及びガラスロッド3のZ方向に対する傾きを調整可能に構成されている。この構成により、上記ガラスパイプ2及びガラスロッド3は、それぞれ鉛直にかつ、互いに同軸に位置付けられるようになる。
【0044】
また、上記各把持部41,42はそれぞれ、Z方向に移動可能に構成されており、この各把持部41,42の下方への移動に伴い、上記ガラスパイプ2及びガラスロッド3がそれぞれ下方に移動するようにしている。尚、上記第1及び第2把持部41,42の移動速度は、それぞれ変更可能であると共に、第1把持部41と第2把持部42とで互いに異なる速度に設定することも可能である。このため、上記ガラスパイプ2及びガラスロッド3の移動速度(後述するヒータ5への送り速度)が調整可能にされており、さらに、上記ガラスパイプ2の送り速度とガラスロッド3の送り速度とを互いに異ならせることも可能にされている。
【0045】
上記第1把持部41の下方位置には、上記ガラスパイプ2及びガラスロッド3を加熱する略リング状のヒータ5が配設されている。このヒータ5は、図示省略の加熱炉内に配設されたものであって、上記ガラスパイプ2の外径よりも大きい内径を有していると共に、上記ガラスパイプ2及びガラスロッド3と略同軸となる位置に配設されている。これにより、上記ガラスパイプ2及びガラスロッド3はその軸方向に上記ヒータ5内を通過可能にされている。
【0046】
この構成によって、上記第1及び第2把持部41,42によってガラスパイプ2及びガラスロッド3が下方に移動されると、このガラスパイプ2及びガラスロッド3は上記ヒータ5内をその一端(下端)から順次通過するようになる。これにより、ガラスパイプ2及びガラスロッド3が、その一端から他端に向かって順次加熱されることになる。
【0047】
尚、このヒータ5を備える加熱炉としては、具体的には、カーボン抵抗加熱炉や高周波誘導加熱炉が例示される。
【0048】
上記ヒータ5の下方位置には、このヒータ5の中心軸を挟んだX方向の両側位置に、それぞれ2つのローラ6,6、…が配設されている。この各ローラ6は、Y軸回りに回転可能に構成されており、上記ヒータ5を通過することによって一体化したガラスパイプ2とガラスロッド3との一体化物(光ファイバ母材7)を、X方向に相対向した二対のローラ6,6,…で挟み込んで、この一体化物を下方に引き取るように構成されている。この各ローラ6,6の回転速度は変更可能に構成されており、これにより、一体化物のヒータ5からの引き取り速度を調整することが可能にされている。こうして一体化物のヒータ5からの引き取り速度を調整することにより、上記一体化物の外径を所定の径(目標外径)の光ファイバ母材7にさせるようにしている。
【0049】
また、上記第1把持部41に把持されたガラスパイプ2の上端面には、その上端開口を閉止する閉止キャップ8が取り付けられる。この閉止キャップ8には、図示省略の真空ポンプが接続されており、この真空ポンプを駆動させることによって、上記ガラスパイプ2内を減圧にすることができるようになっている。
【0050】
次に、この製造装置1による光ファイバ母材7の製造方法について説明すると、先ず、ガラスパイプ2の上端部分を第1把持部41によって把持し、この第1把持部41によって、上記ガラスパイプ2がヒータ5に対して同軸となるように上記ガラスパイプ2のX,Y方向位置をそれぞれ調整すると共に、上記ガラスパイプ2が鉛直に配設されるように上記ガラスパイプ2の傾きを調整する。
【0051】
次に、ガラスロッド3の上端部分を第2把持部42によって把持し、この第2把持部42によって、上記ガラスロッド3がガラスパイプ3に対して同軸となるように上記ガラスロッド3のX,Y方向位置をそれぞれ調整すると共に、上記ガラスロッド3が鉛直に配設されるように上記ガラスロッド3の傾きを調整する。そして、ガラスロッド3をガラスパイプ2内に内挿する。
【0052】
尚、図示は省略するが、ガラスパイプ2の上端に、このガラスパイプ2と同軸となるように補助パイプを取り付け、この補助パイプの上端部分を上記第1把持部41によって把持するようにしてもよい。また、ガラスロッド3の上端に、このガラスロッド3と同軸となるように補助ロッドを取り付け、この補助ロッドの上端部分を上記第2把持部42によって把持するようにしてもよい。さらに、ガラスパイプ2の下端に、このガラスパイプ2と同軸となるように補助パイプを取り付け、同じくガラスロッド3の下端に、このガラスロッド3と同軸となるように補助パイプを取り付けるようにしてもよい。
【0053】
そして、上記ガラスパイプ2の上端開口を閉止キャップ8により閉止し、真空ポンプを駆動させて上記ガラスパイプ2内を減圧する。こうしてガラスパイプ2内を減圧しながら、上記第1及び第2把持部41,42をそれぞれ所定の速度で下方に移動させることにより、上記ガラスパイプ2とガラスロッド3とをヒータ5内に送る。
【0054】
これにより、上記ガラスパイプ2とガラスロッド3とが、その軸方向に上記ヒータ5内を通過するようになって、上記ガラスパイプ2とガラスロッド3とが、その下端から上端に向かって上記ヒータ5により順次加熱される。このため、上記ガラスパイプ2とガラスロッド3とは、その下端から上端に向かって順次溶融するが、このとき、ガラスパイプ2内が減圧されているため、このガラスパイプ2内外の圧力差によって溶融したガラスパイプ2が縮径する。その結果、ガラスパイプ2とガラスロッド3とが、その長手方向に順次一体化する。
【0055】
こうして一体化したガラスパイプ2とガラスロッド3との一体化物は、ローラ6,6,…によって引き取られることで、所定の外径になるまで延伸され、光ファイバ母材7が製造されることになる。
【0056】
そして、本実施形態では、上記ガラスパイプ2とガラスロッド3とを一体化させるときの上記ガラスパイプ2内の圧力を、一体化の開始時には比較的低圧の第1圧力に設定するのに対し、上記ガラスパイプ2とガラスロッド3とを一体化させている最中に、所定のタイミングで、上記ガラスパイプ2内の圧力を、上記第1圧力から、比較的高圧の第2圧力に切り換えるようにする。
【0057】
ここで、第1及び第2圧力はそれぞれ、大気圧よりも低圧であって、具体的に、第1圧力は−10kPa(ゲージ圧)よりも低く設定する。好ましくは、−11kPa〜−16kPa程度である。一方、第2圧力は−10kPa(ゲージ圧)以上に設定する。好ましくは、−5kPa以上、より好ましくは−3kPa以上である。
【0058】
このガラスパイプ2内の圧力の切り替えは、真空ポンプの作動を制御することにより行うようにすればよい。また、例えばガラスパイプ2内に連通する真空ポンプを2つ備えるようにし、この2つの真空ポンプの双方を作動させることによって、ガラスパイプ2内の圧力を第1圧力に設定する一方、所定のタイミングで、2つの真空ポンプの内のいずれか一方の作動を停止させることによって、ガラスパイプ2内の圧力を第2圧力に設定するようにしてもよい。
【0059】
このようにガラスパイプ2とガラスロッド3との一体化を開始する時点では、ガラスパイプ2内の圧力を、比較的低圧の第1圧力(但し、第1圧力は大気圧よりも低い)に設定することにより、ガラスパイプ2内外の圧力差が大きくなってガラスパイプ2を縮径させる力が強くなる。このため、上記ヒータ5によってガラスパイプ2及びガラスロッド3に加えられる熱の周方向分布が不均一であっても、このガラスパイプ2は、周方向に均等に縮径変形してガラスロッド3と一体化する。従って、ガラスパイプ2とガラスロッド3とが一体化した部分においては、その横断面形状が真円形状となる。
【0060】
こうして、ガラスパイプ2とガラスロッド3とが、その一体化開始の端部側において真円形状の横断面形状で一体化するようになると共に、光ファイバ母材7の外径が目標外径となれば、上記ガラスパイプ2内の圧力を、第1圧力から、比較的高圧の第2圧力に切り換え、ガラスパイプ2内の圧力を比較的高圧にした状態で、ガラスパイプ2とガラスロッド3との一体化を継続する。
【0061】
こうすることで、ガラスパイプ2を縮径させる力は弱くなるものの、このガラスパイプ2において現在溶融して変形途中にある部分は、既に縮径変形してガラスロッド3と一体化している部分と連なっていることで、この変形途中にある部分は、上記ガラスロッド3と一体化している部分に引き寄せられるように変形する。そのため、上記溶融して変形途中にある部分がガラスロッドと一体化したときには、その横断面形状は、ガラスロッドと一体化した部分における横断面形状と略同じになる。
【0062】
一方で、上述したように、既にガラスパイプ2とガラスロッド3とが一体化している部分においては、その横断面形状が真円形状となっていることから、上記ガラスパイプ2は、ガラスパイプ2内外の圧力差が小さくても、上記真円形状に沿うように縮径変形して、ガラスロッド3と一体化するようになる。こうして製造された光ファイバ母材7は、その横断面形状が真円形状になる。
【0063】
また、ガラスパイプ2を縮径させる力が弱くなることで、ガラスパイプ2の急激な縮径変形が抑制される。これにより、ガラスパイプ2の緩やかな縮径変形によって、十分に溶融したガラスロッド3がその中心に向かって移動するようになり、ガラスパイプ2とガラスロッド3とが略同軸となった状態で、このガラスパイプ2とガラスロッド3とが一体化するようになる。こうして、光ファイバ母材7において、そのコア部の偏心が抑制されるため、上記光ファイバ母材7を線引きした光ファイバにおけるコアの偏心が抑制される。
【0064】
従って、本発明に係る光ファイバ母材7の製造方法によると、光ファイバ母材7のコア部の偏心が防止されると共に、光ファイバ母材7の横断面形状のゆがみが防止される。
【0065】
尚、ガラスパイプ2内の圧力を、比較的高圧の第2圧力に設定したときにおいても、単位時間当たりに一体化するガラスパイプ2及びガラスロッド3の総ガラス量であるガラス処理量、及び上記ガラスパイプ2及びガラスロッド3を加熱する加熱温度等の製造条件を適宜設定することによって、ガラスパイプ2とガラスロッド3とを確実に一体化させて、例えばガラスパイプ2とガラスロッド3とを一体化させたときの輝点の発生を防止することが可能である。ここで、ガラス処理量の調整は、主にガラスパイプ2の送り速度とガラスロッド3の送り速度との調整によって行い、加熱温度の調整は、ヒータ5の作動条件の調整によって行う。
【0066】
また特に、ガラスパイプ2として、その外径Dがφ100mm≦D≦φ200mmを満たすものを用いた場合には、ガラスパイプ2内の圧力を比較的高い圧力に設定しても、ガラス処理量の調整及び加熱温度の調整等によって、輝点の発生が防止された光ファイバ母材7を製造することが可能になる。つまり、ガラスパイプ2がφ100mm以上の外径を有するものであるときには、ガラスパイプ2内の圧力を比較的高圧に設定しても、適切な製造条件が得られる。
【0067】
尚、上記ガラスパイプ2の最大外径として規定したφ200mmの値は、主に製造装置1の大きさによって規定される値である。従って、例えば製造装置1がより大型のものであって、φ200mm以上の外径を有するガラスパイプ2であっても光ファイバ母材7を製造可能なものであれば、φ200mm以上のガラスパイプ2を用いて光ファイバ母材7を製造してもよい。
【0068】
さらに、ガラスパイプ2内の圧力の切り替えタイミングは、ガラスパイプ2とガラスロッド3とを一体化させた光ファイバ母材7が、目標外径になったタイミングとするのがよい。こうすることで、歩留まりを向上させることができる。
【0069】
すなわち、光ファイバ母材7の外径が目標外径となる前の部分は製品取りの部分ではないため、ガラスパイプ2とガラスロッド3との偏心を考慮する必要はない。そこで、横断面形状が真円形状となるように、ガラスパイプとガラスロッドとを一体化させるべく、ガラスパイプ2内の圧力を比較的低圧の第1圧力とする。
【0070】
一方、光ファイバ母材7の外径が目標外径となった後の部分は製品取りの部分であるから、ガラスパイプ2内の圧力を比較的高圧の第2圧力とすることによって、ガラスパイプ2とガラスロッド3との偏心を抑制する。こうすることで、歩留まりの向上が図られる。
【0071】
【実施例】
次に、本発明に関して具体的に実施した実施例について説明する。
【0072】
先ず、表1に示す製造条件で、ガラスパイプ2とガラスロッド3とを一体化させた光ファイバ母材を3つ製造した(実施例及び比較例1,2)。尚、このとき使用したガラスパイプ2は、外径がφ180mm、内径がφ54mmのものである。また、ガラスロッド3は、外径がφ50mmのものである。
【0073】
【表1】
【0074】
表中、「ガラス処理量」とは、単位時間当たりに一体化するガラスパイプ2及びガラスロッド3の総ガラス量であって、このガラス処理量は、製造装置1における第1及び第2把持部41,42の移動速度を調整することにより、ガラスパイプ2及びガラスロッド3のヒータ5への送り速度を調整することによって、調整する。また、「速度比」とは、ガラスパイプ2の送り速度とガラスロッド3の送り速度との比であって、この速度比も、第1及び第2把持部41,42の移動速度の調整によって、調整する。
【0075】
また、ガラスパイプ2及びガラスロッド3の加熱温度(定温度)は、ヒータ出力の調整によって、調整する。
【0076】
さらに、製造装置1には、ガラスパイプ2内の圧力を低下させるための真空ポンプとして、第1及び第2の2つの真空ポンプが設けられており、この内、第1の真空ポンプは、その作動条件を制御可能に、つまり目標圧力を設定可能に構成されているのに対し、第2の真空ポンプは、その作動条件を制御不可に、つまり作動のON・OFFのみが可能に構成されている。そして、第1の真空ポンプ(真空1)の目標圧力を−5kPaとし、第2の真空ポンプ(真空2)をOFFとしたときには、ガラスパイプ2内の圧力は−3kPaとなる(比較例1)。一方、第1の真空ポンプの目標圧力を−5kPaとし、第2の真空ポンプをONとしたときには、ガラスパイプ2内の圧力は−11kPaとなる(比較例2)。
【0077】
また、実施例では、第1の真空ポンプの目標圧力を−5kPaとする一方、第2の真空ポンプは、一体化を開始する時点ではONとし、一体化の最中における所定のタイミングでOFFとした。従って、実施例では、ガラスパイプ2内の圧力は、ガラスパイプ2とガラスロッド3との一体化を開始する時点では、比較的低圧の−11kPaとなり、その後、比較的高圧の−3kPaとなる。
【0078】
そして、以上の製造条件で、上述したように、ガラスパイプ2とガラスロッド3とを一体化させて、実施例に係る光ファイバ母材7と、比較例1,2に係る光ファイバ母材7とをそれぞれ製造したところ、表1に示すように、実施例に係る光ファイバ母材7においては、コア部の偏心量の最小値が0.08mm、その最大値が0.32mmであった。一方、比較例1に係る光ファイバ母材7においては、コア部の偏心量の最小値が0.03mm、その最大値が0.27mmであり、比較例2に係る光ファイバ母材7においては、コア部の偏心量の最小値が0.06mm、その最大値が0.39mmであった。従って、ガラスパイプ2内の圧力が比較的低圧の比較例2に係る光ファイバ母材7は、コア部の偏心量(最大値)が、実施例及び比較例1に比べて大きくなった。
【0079】
また、上記実施例及び比較例1,2に係る光ファイバ母材7の横断面形状のゆがみを測定した。これは、光ファイバ母材7の所定の横断面において、互いに異なる2箇所で測定した外径の差(偏径差)の最大値によって評価した。表1に示すように、ガラスパイプ2内の圧力が比較的高い比較例1は、最大偏径差が0.51mmと大きくなった。これに対し、ガラスパイプ2内の圧力が比較的低い比較例2は、最大偏径差が0.17mmと小さくなり、また、ガラスパイプ2内の圧力を、一体化の最中に低圧から高圧に切り換えた実施例も、最大偏径差が0.15mmと小さくなった。
【0080】
尚、実施例及び比較例1,2のいずれの光ファイバ母材7においても、ガラスパイプ2とガラスロッド3との界面に輝点は発生しなかった(表中、○で示す)。
【0081】
次に、上記実施例及び比較例1,2の光ファイバ母材7を、それぞれ線引きして光ファイバとした。実施例に係る光ファイバの、長手方向の各位置におけるコアの偏心量を図2に示す。一方、比較例1に係る光ファイバの、長手方向の各位置におけるコアの偏心量を図3に示すと共に、比較例2に係る光ファイバの、長手方向の各位置におけるコアの偏心量を図4に示す
図2〜図4によると、比較例1に係る光ファイバにおいては、コアの偏心量が0.1〜0.2μm程度であり、実施例に係る光ファイバにおいては、コアの偏心量が0.3μm程度であるのに対し、比較例2に係る光ファイバにおいては、コアの偏心量が0.5μm程度であった。
【0082】
以上の結果から、ガラスパイプ2とガラスロッド3とを一体化させるときに、比較例1のように、ガラスパイプ2内の圧力を比較的高く設定したときには、光ファイバ母材7におけるコア部の偏心は抑制されるものの、光ファイバ母材7の横断面形状のゆがみが生じてしまう。一方、比較例2のように、ガラスパイプ2内の圧力を比較的低く設定したときには、光ファイバ母材7の横断面形状のゆがみが防止されるものの、光ファイバ母材7におけるコア部の偏心が生じてしまう。
【0083】
これに対し、実施例のように、ガラスパイプ2とガラスロッド3とを一体化させている最中に、ガラスパイプ2内の圧力を低圧から、高圧に切り換えたときには、光ファイバ母材7におけるコア部の偏心が防止されると共に、光ファイバ母材7の横断面形状のゆがみも防止されることが判る。
【図面の簡単な説明】
【図1】光ファイバ母材の製造装置を示す概略図である。
【図2】実施例に係る光ファイバのコアの偏心量を示す図である。
【図3】比較例1に係る光ファイバのコアの偏心量を示す図である。
【図4】比較例2に係る光ファイバのコアの偏心量を示す図である。
【符号の説明】
2 ガラスパイプ
3 ガラスロッド
7 光ファイバ母材[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention, in a glass pipe for cladding, by inserting a glass rod for core, or a glass rod for core and cladding, and heating both while decompressing the inside of the glass pipe, the glass pipe and the glass rod The present invention relates to a method of manufacturing an optical fiber preform for performing integration and stretching.
[0002]
[Prior art]
Conventionally, a glass rod serving as a core in an optical fiber, or a glass rod serving as a core and a cladding, is inserted into a glass pipe serving as a cladding in an optical fiber, and the glass pipe and the glass rod are integrated into an optical fiber motherboard. A so-called rod-in-tube method for manufacturing a material is known (for example, see Patent Document 1). In this rod-in-tube method, for example, both the glass pipe and the glass rod are passed through a substantially ring-shaped heater in the axial direction while reducing the pressure inside the glass pipe into which the glass rod is inserted. By doing so, the glass pipe and the glass rod are sequentially heated from one end to the other end, and the diameter of the molten glass pipe is reduced by the pressure difference between the inside and outside of the glass pipe. As a result, the glass pipe and the glass rod are sequentially integrated, and the optical fiber preform is manufactured.
[0003]
The optical fiber preform manufactured in this manner is converted into an optical fiber by a drawing step. A method is also known in which this drawing step is performed simultaneously with the production of the optical fiber preform by the rod-in-tube method (for example, see Patent Reference 2).
[0004]
By the way, in recent years, from the viewpoint of reduction in production cost and the like, it has been required to increase the size of the optical fiber preform. For this reason, the diameter of the optical fiber preform has been increased.
[0005]
However, if such a large-diameter optical fiber preform is drawn as it is, it takes a long time to stabilize the optical fiber of the target diameter, and a large amount of the preform is consumed for initial stabilization. It becomes like this. As a result, the yield from the optical fiber preform to the optical fiber deteriorates, and the enlargement of the optical fiber preform originally performed for the purpose of cost reduction cannot achieve the purpose. There is an inconvenience.
[0006]
Therefore, in order to eliminate such inconveniences, the diameter of the normally manufactured large diameter optical fiber preform is reduced to an optimum diameter that maximizes the yield before the drawing step. A method of improving the productivity by performing the diameter reducing step of the optical fiber preform simultaneously with the production of the optical fiber preform by integrating the glass pipe and the glass rod is known (for example, Patent Reference 3).
[0007]
[Patent Document 1]
JP-B-56-45867
[Patent Document 2]
JP-A-50-85345
[Patent Document 3]
JP-A-7-10580
[0008]
[Problems to be solved by the invention]
By the way, in the production of an optical fiber preform by the rod-in-tube method, a gap formed between the glass pipe and the glass rod is crushed by reducing the diameter of the glass pipe, and the glass pipe and the glass rod are separated. They are integrated. Therefore, depending on the manufacturing conditions, the glass pipe and the glass rod may be integrated in an eccentric state. If the glass pipe and the glass rod are eccentric in this way, the core portion of the optical fiber (hereinafter, this portion is referred to as a core portion) in the optical fiber preform is eccentric. In an optical fiber obtained by drawing a material, the core becomes eccentric.
[0009]
Also, in the production of an optical fiber preform by the rod-in-tube method, the glass pipe is deformed in a circumferential direction depending on the production conditions in order to reduce the diameter of the glass pipe, and as a result, the optical fiber is deformed. The cross-sectional shape of the base material may be an elliptical shape instead of a perfect circular shape.
[0010]
The present invention has been made in view of such circumstances, and an object thereof is to produce an optical fiber preform by integrating and stretching a glass pipe and a glass rod. And to prevent the optical fiber preform from being distorted in the cross-sectional shape.
[0011]
[Means for Solving the Problems]
In order to achieve the above object, the present inventor first focused on the pressure in the glass pipe when the glass pipe and the glass rod were integrated. That is, in the conventional optical fiber manufacturing method by the rod-in-tube method, in order to surely integrate the glass pipe and the glass rod, the pressure in the glass pipe is reduced as much as possible (to increase the degree of vacuum in the glass pipe). T), the glass pipe and the glass rod are integrated.
[0012]
Thus, by setting the pressure in the glass pipe low, the pressure difference between the inside and outside of the glass pipe increases, the force for reducing the diameter of the glass pipe increases, and the glass pipe and the glass rod can be surely integrated. Although it became possible, it was confirmed by experiments conducted by the present inventor that when the pressure in the glass pipe was low, the core was eccentric. This is because the solid state glass rod before the glass rod melts is eccentric to the glass pipe by increasing the force to reduce the diameter of the glass pipe by setting the pressure inside the glass pipe low, It is considered that the glass pipe and the glass rod are integrated by the diameter reduction deformation of the glass pipe, and as a result, the eccentricity of the core portion of the optical fiber preform is caused, and the eccentricity of the core of the optical fiber is caused.
[0013]
Then, when the present inventor manufactured the optical fiber preform by setting the pressure in the glass pipe relatively high, the eccentricity between the glass pipe and the glass rod was suppressed. This is because the pressure inside the glass pipe is high and the force to reduce the diameter of the glass pipe is small, but by doing so, the diameter reduction deformation of the glass pipe is moderate and the sufficiently molten glass rod It is considered that the glass pipe and the glass rod are integrated in a state where the pipe moves toward the center due to the diameter reduction deformation of the pipe and the glass pipe and the glass rod are substantially coaxial.
[0014]
However, when the pressure in the glass pipe is set to a relatively high value, the cross section of the optical fiber preform is distorted, and the cross section becomes in an elliptical shape.
[0015]
When the glass pipe and the glass rod are integrated, the glass pipe and the glass rod are heated over the entire circumference by passing through a heater formed in a substantially ring shape. At this time, the glass pipe and the glass rod are added to the glass pipe. This is considered to be due to the non-uniform heat distribution in the circumferential direction.
[0016]
In other words, when the pressure in the glass pipe is relatively low, the glass pipe has a strong force to reduce the diameter of the glass pipe. Integrate with For this reason, the cross-sectional shape of the optical fiber preform is substantially circular.
[0017]
However, when the pressure inside the glass pipe is relatively high and the force for reducing the diameter of the glass pipe is weak, the portion of the glass pipe that has been sufficiently heated and melted is reduced due to the uneven heat distribution in the circumferential direction. Diameter deformation is apt to occur, and a portion that is not sufficiently heated and is insufficiently melted is hardly reduced in diameter. Thus, it is considered that the glass pipe is not uniformly reduced in diameter, and as a result, when the pressure in the glass pipe is relatively high, the cross section of the optical fiber preform is distorted.
[0018]
As described above, in order to prevent distortion of the cross-sectional shape of the optical fiber preform, it is preferable to set the pressure in the glass pipe low. Thus, when the pressure in the glass pipe is set low, as described above, Since the eccentricity of the core portion is caused, prevention of eccentricity of the core portion in the optical fiber preform and prevention of distortion of the optical fiber preform are contradictory requirements.
[0019]
Then, in order to solve this problem, the present inventor paid attention to the mechanism of diameter reduction deformation of the glass pipe in the rod-in-tube method.
[0020]
That is, in the method of manufacturing an optical fiber by the rod-in-tube method, the glass pipe is melted in the axial direction from one end to the other end, and the diameter is sequentially reduced by the pressure difference between the inside and outside of the glass pipe. The glass pipe and the glass rod are sequentially integrated in the axial direction. For this reason, in the glass pipe, the part which is being melted and being deformed is connected to the part which has already been reduced in diameter and integrated with the glass rod.
[0021]
In this way, the portion that is being melted and being deformed is connected to the portion that is integrated with the glass rod, so that when the portion that is being deformed is reduced in diameter, it is integrated with the glass rod. Deform to be drawn to the part. Therefore, when the portion that is being melted and being deformed is integrated with the glass rod, its cross-sectional shape becomes substantially the same as the cross-sectional shape of the portion integrated with the glass rod earlier than that.
[0022]
Therefore, if the glass pipe is not uniformly deformed in the circumferential direction and is integrated with the glass rod in a distorted shape, the glass pipe is further reduced in diameter to conform to the distorted shape, and the glass rod is thereafter deformed. Will be integrated. On the other hand, when the glass pipe is uniformly deformed in the circumferential direction, and the cross section is integrated with the glass rod in a perfect circular shape, the glass pipe will then maintain its perfect circular shape even if the pressure difference between the inside and outside of the glass pipe is small. , And is integrated with the glass rod. That is, the cross-sectional shape of the optical fiber preform becomes a perfect circle.
[0023]
In consideration of the above mechanism, in the present invention, at the start of integrating the glass pipe and the glass rod, the pressure in the glass pipe is set to a relatively low first pressure, and the glass pipe and the glass rod are combined. During the integration, the pressure in the glass pipe was switched from the first pressure to the relatively high second pressure.
[0024]
Specifically, the present invention is to heat both the glass pipe and the glass rod in the axial direction sequentially from one end to the other end while reducing the pressure in the glass pipe in which the glass rod is inserted. The present invention relates to a method for manufacturing an optical fiber preform, in which a glass pipe and a glass rod are sequentially integrated and stretched to a predetermined outer diameter to manufacture an optical fiber preform.
[0025]
In the method for manufacturing an optical fiber according to the present invention, at the time of starting the integration of the glass pipe and the glass rod, the pressure in the glass pipe is set to a first pressure lower than the atmospheric pressure, and During the integration of the pipe and the glass rod, the pressure in the glass pipe is switched from the first pressure to a second pressure higher than the first pressure and lower than the atmospheric pressure.
[0026]
By doing so, at the time when the integration of the glass pipe and the glass rod is started, the pressure in the glass pipe is set to a relatively low first pressure (however, the first pressure is lower than the atmospheric pressure). You. As a result, the pressure difference between the inside and outside of the glass pipe is increased, and the force for reducing the diameter of the glass pipe is increased. Therefore, even if the heat distribution is uneven in the circumferential direction, the diameter of the glass pipe is reduced uniformly in the circumferential direction. Deforms and integrates with the glass rod. Therefore, in a portion where the glass pipe and the glass rod are integrated, the cross-sectional shape is a perfect circle.
[0027]
In this way, when the glass pipe and the glass rod are integrated at one end side (end end side of the integration start) with a perfect circular cross section, the pressure in the glass pipe is reduced to The first pressure is switched to a second pressure higher than the first pressure and lower than the atmospheric pressure. Thus, the integration of the glass pipe and the glass rod is continued while the pressure in the glass pipe is relatively high.
[0028]
By doing so, although the force for reducing the diameter of the glass pipe is reduced, as described above, the glass pipe is deformed so as to be drawn to a portion where the glass pipe and the glass rod are integrated. On the other hand, in the part where the glass pipe and the glass rod are already integrated, the cross-sectional shape is a perfect circle, so that the glass pipe is reduced in diameter so as to follow the perfect circle. Then, it comes to be integrated with the glass rod. Therefore, the manufactured optical fiber preform has a perfect circular cross-sectional shape.
[0029]
In addition, since the force for reducing the diameter of the glass pipe is reduced, rapid reduction in the diameter of the glass pipe is suppressed. As a result, the sufficiently melted glass rod moves toward the center due to the diameter reduction deformation of the glass pipe, and the glass pipe and the glass rod are substantially coaxial with each other. And are integrated. Thereby, the eccentricity of the glass pipe and the glass rod is suppressed, and the eccentricity of the core portion of the optical fiber preform is suppressed. As a result, the eccentricity of the core in the optical fiber drawn from the optical fiber preform is suppressed.
[0030]
Thus, according to the method of manufacturing an optical fiber preform according to the present invention, the eccentricity of the core portion of the optical fiber preform is prevented, and the cross-sectional shape of the optical fiber preform is prevented from being distorted.
[0031]
In addition, even when the pressure in the glass pipe is set to a relatively high second pressure, the glass processing amount, which is the total amount of glass pipe and glass rod integrated per unit time, By appropriately setting the manufacturing conditions such as the heating temperature for heating the glass rod, the glass pipe and the glass rod are surely integrated, for example, when the glass pipe and the glass rod are integrated, the pipe and the rod At the interface (hereinafter, such bubbles or separation at the interface may also be referred to as bright spots).
[0032]
Here, the pressure in the glass pipe may be switched from the first pressure to the second pressure at the timing when the outer diameter of the optical fiber preform reaches the target outer diameter.
[0033]
That is, as described above, the optical fiber preform is manufactured by sequentially integrating the glass pipe and the glass rod in the axial direction, but the portion until the outer diameter of the optical fiber preform reaches the target outer diameter is obtained. Cannot be a product, and the part after the outer diameter of the optical fiber preform reaches the target outer diameter becomes a product.
[0034]
Therefore, the pressure in the glass pipe is set to a relatively low first pressure until the outer diameter of the optical fiber preform reaches the target outer diameter after the integration of the glass pipe and the glass rod is started. The glass pipe and the glass rod are integrated so that the cross-sectional shape becomes a perfect circle while promoting the integration of the glass pipe and the glass rod.
[0035]
On the other hand, after the outer diameter of the optical fiber preform reaches the target outer diameter, since the portion where the glass pipe and the glass rod are integrated after that is the product taking part, the pressure in the glass pipe is relatively reduced. The eccentricity between the glass pipe and the glass rod is suppressed by setting the high second pressure. As a result, the yield is improved.
[0036]
Note that the first pressure may be a pressure capable of reducing the diameter of the glass pipe so that the cross section becomes a perfect circle even if the heat distribution is not uniform. In this case, the pressure may be lower than -10 kPa (gauge pressure), and is preferably about -11 kPa to -16 kPa.
[0037]
On the other hand, the second pressure may be a pressure at which eccentricity between the glass pipe and the glass rod can be prevented, and specifically, may be -10 kPa (gauge pressure) or more (however, from the atmospheric pressure. Pressure), preferably -5 kPa or more, more preferably -3 kPa or more.
[0038]
【The invention's effect】
As described above, according to the optical fiber preform manufacturing method of the present invention, during the integration of the glass pipe and the glass rod, at the timing when the outer diameter of the optical fiber preform reaches the target outer diameter. By switching the pressure in the glass pipe from the first pressure at a relatively low pressure to the second pressure at a relatively high pressure, both the eccentricity of the core portion of the optical fiber preform and the distortion of the cross-sectional shape are prevented. be able to.
[0039]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, embodiments of the present invention will be described with reference to the drawings.
[0040]
FIG. 1 shows an optical fiber
[0041]
Here, as the
[0042]
The
[0043]
The
[0044]
Each of the
[0045]
A substantially ring-shaped
[0046]
With this configuration, when the first and
[0047]
The heating furnace including the
[0048]
Below the
[0049]
A closing cap 8 for closing the upper end opening is attached to the upper end surface of the
[0050]
Next, a method of manufacturing the optical fiber preform 7 by the
[0051]
Next, the upper end portion of the
[0052]
Although not shown, an auxiliary pipe is attached to the upper end of the
[0053]
Then, the upper end opening of the
[0054]
As a result, the
[0055]
The integrated product of the
[0056]
In the present embodiment, the pressure in the
[0057]
Here, the first and second pressures are each lower than the atmospheric pressure, and specifically, the first pressure is set lower than -10 kPa (gauge pressure). Preferably, it is about -11 kPa to -16 kPa. On the other hand, the second pressure is set to -10 kPa (gauge pressure) or more. Preferably, it is -5 kPa or more, more preferably -3 kPa or more.
[0058]
The switching of the pressure in the
[0059]
When the integration of the
[0060]
In this way, the
[0061]
By doing so, although the force for reducing the diameter of the
[0062]
On the other hand, as described above, in a portion where the
[0063]
In addition, since the force for reducing the diameter of the
[0064]
Therefore, according to the method for manufacturing the optical fiber preform 7 according to the present invention, the eccentricity of the core portion of the optical fiber preform 7 is prevented, and the distortion of the cross-sectional shape of the optical fiber preform 7 is also prevented.
[0065]
Even when the pressure in the
[0066]
In particular, when a
[0067]
The value of φ200 mm defined as the maximum outer diameter of the
[0068]
Further, the switching timing of the pressure in the
[0069]
That is, since the part before the outer diameter of the optical fiber preform 7 reaches the target outer diameter is not a part for obtaining products, it is not necessary to consider the eccentricity between the
[0070]
On the other hand, since the portion after the outer diameter of the optical fiber preform 7 has reached the target outer diameter is a product picking-up portion, the pressure inside the
[0071]
【Example】
Next, examples of the present invention will be described.
[0072]
First, three optical fiber preforms in which the
[0073]
[Table 1]
[0074]
In the table, “glass processing amount” is the total glass amount of the
[0075]
The heating temperature (constant temperature) of the
[0076]
Further, the
[0077]
In the embodiment, while the target pressure of the first vacuum pump is set to -5 kPa, the second vacuum pump is turned on at the time of starting the integration and turned off at a predetermined timing during the integration. did. Therefore, in the embodiment, the pressure in the
[0078]
Then, under the above manufacturing conditions, as described above, the
[0079]
Further, the distortion of the cross-sectional shape of the optical fiber preform 7 according to the example and the comparative examples 1 and 2 was measured. This was evaluated based on the maximum value of the difference between the outer diameters (diameter difference) measured at two different positions in a predetermined cross section of the optical fiber preform 7. As shown in Table 1, in Comparative Example 1 in which the pressure in the
[0080]
In each of the optical fiber preforms 7 of Examples and Comparative Examples 1 and 2, no luminescent spot was generated at the interface between the
[0081]
Next, the optical fiber preforms 7 of the above example and comparative examples 1 and 2 were each drawn to obtain an optical fiber. FIG. 2 shows the amount of eccentricity of the core at each position in the longitudinal direction of the optical fiber according to the example. On the other hand, FIG. 3 shows the eccentricity of the core at each position in the longitudinal direction of the optical fiber according to Comparative Example 1, and FIG. 4 shows the eccentricity of the core at each position in the longitudinal direction of the optical fiber according to Comparative Example 2. Shown in
2 to 4, the eccentricity of the core is about 0.1 to 0.2 μm in the optical fiber according to Comparative Example 1, and the eccentricity of the core is 0.1 μm in the optical fiber according to the example. While the optical fiber according to Comparative Example 2 had a core eccentricity of about 0.5 μm, whereas the optical fiber according to Comparative Example 2 had a diameter of about 3 μm.
[0082]
From the above results, when the
[0083]
On the other hand, when the pressure in the
[Brief description of the drawings]
FIG. 1 is a schematic view showing an apparatus for manufacturing an optical fiber preform.
FIG. 2 is a diagram illustrating an eccentricity of a core of an optical fiber according to an example.
FIG. 3 is a diagram showing the amount of eccentricity of the core of the optical fiber according to Comparative Example 1.
FIG. 4 is a diagram showing the amount of eccentricity of the core of the optical fiber according to Comparative Example 2.
[Explanation of symbols]
2 Glass pipe
3 Glass rod
7 Optical fiber preform
Claims (2)
上記ガラスパイプとガラスロッドとの一体化の開始時には、上記ガラスパイプ内の圧力を、大気圧よりも低い第1圧力に設定すると共に、
上記ガラスパイプとガラスロッドとの一体化の最中に、上記ガラスパイプ内の圧力を、上記第1圧力から、該第1圧力よりも高くかつ大気圧よりも低い第2圧力に切り換える
ことを特徴とする光ファイバ母材の製造方法。While depressurizing the inside of the glass pipe in which the glass rod is inserted, both the glass pipe and the glass rod are sequentially heated in the axial direction from one end to the other end, so that the glass pipe and the glass rod are sequentially heated. A method of manufacturing an optical fiber preform, which is integrated and stretched to a predetermined outer diameter to produce an optical fiber preform,
At the start of the integration of the glass pipe and the glass rod, the pressure in the glass pipe is set to a first pressure lower than the atmospheric pressure,
During the integration of the glass pipe and the glass rod, the pressure in the glass pipe is switched from the first pressure to a second pressure higher than the first pressure and lower than the atmospheric pressure. A method of manufacturing an optical fiber preform.
ガラスパイプ内の圧力を、光ファイバ母材の外径が目標外径となったタイミングで、第1圧力から第2圧力に切り換える
ことを特徴とする光ファイバ母材の製造方法。In claim 1,
A method for manufacturing an optical fiber preform, wherein the pressure in the glass pipe is switched from the first pressure to the second pressure at a timing when the outer diameter of the optical fiber preform reaches a target outer diameter.