JP2004085651A - Easy peeling heat-sensitive label - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an easy peeling heat-sensitive label of which the heat-sensitive adhesive layer does not remain on a body to be stuck, and which does not tear when being peeled off for recycling a vessel, but which facilitates peeling by hand. <P>SOLUTION: In the easy peeling heat-sensitive label 1 of which the base material 10 is provided with a printed layer 12 on one side and a heat-sensitive adhesive layer 14 on the other side, the heat-sensitive adhesive layer 14 is formed of a heat-sensitive resin such as EVA added with an adherence agent to provide the easy peeling heat-sensitive label 1 with a coating film in the range of 10-60μm thickness, and this heat-sensitive adhesive layer 14 can be obtained by melt extrusion. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、常温では粘着性がなく、加熱により活性化して粘着性がでる感熱性粘着剤層を備えた感熱ラベルに関するものであり、特にガラス瓶やプラスチック容器などに加熱貼着され、使用後に剥離を容易にし、容器のリサイクルに貢献する易剥離性感熱ラベルに関する。
【０００２】
【従来の技術】
従来、紙等の表面に印刷が施され、裏面には感熱性粘着剤層が施され、この感熱性粘着剤層は、常温では粘着性がないが、加熱によって活性化して粘着性を帯び、ガラス瓶やプラスチック容器等に貼着する感熱ラベルが知られ、特にこのラベルのメーカー側にとっては、通常の粘着ラベルと異なり貼着前の粘着剤面を覆う剥離台紙を必要とせず、加熱によってガラス瓶やプラスチック容器などに貼着されるので、製造に対し粘着、固着に取扱い易い感熱ラベルとして広く普及している。
【０００３】
上記でいう感熱性粘着剤とは、例えば「接着便覧」第１２版第１３１頁（高分子刊行会発行昭和５５年刊）に記載されているように、その基本的組成は、非水溶性高分子材料、粘着付与剤、固体可塑剤からなり、常温では粘着性がないが、加熱によって活性化して粘着性が生じ、その粘着性が冷却後もかなりの期間持続するような接着剤（粘着剤）をいい、通常、この粘着剤の乾燥塗膜はタックがないので、この粘着剤を覆うための剥離台紙が不要である。
【０００４】
上記組成のうちの非水溶性高分子材料は、接着力を与える成分であり、例えば、ポリ酢酸ビニル、エチレン−酢酸ビニル共重合体、ポリアクリル酸エステル系、ポリ塩化ビニル系、天然ゴム、合成ゴム、酢酸ビニル−アクリル酸エステル共重合体、ポリエステル系、ポリウレタン系の非水溶性高分子化合物類が使用される。
【０００５】
また、上記粘着付与剤は、加熱により活性化された際に粘着性を増強させるための成分であり、例えば、ロジン誘導体、テルペン樹脂系、石油樹脂系、フェーノール樹脂系、キシレン樹脂系等の樹脂類が使用される。
【０００６】
また、上記固体可塑剤は、常温では固体であって、その融点以上に加熱されると溶融し、前記非水溶性高分子材料や粘着付与剤を膨潤・溶解して、粘着・接着性を発現させる。そして、一旦溶解した後はなかなか結晶化しないので、活性化後の粘着保持時間を長くとることができるもので、例えば、フタル酸ジフェニル、フタル酸ジヘキシル、フタル酸ジシクロヘキシル、フタル酸ジヒドロアビエチル、イソフタル酸ジメチル、安息香酸スクロース、ジ安息香酸エチレングリコール、トリ安息香酸トリメチロールエタン、トリ安息香酸グリセリド、テトラ安息香酸ペンタエリエット、オクタ酢酸スクロース、クエン酸トリシクロヘキシルＮ−シクロヘキシル−Ｐ−トルエンスルホンアミド等の常温で固体の有機化合物が使用される。
【０００７】
上記のような、非水溶性高分子材料と、粘着付与剤と、固体可塑剤とを水性溶媒に分散してなる感熱性粘着剤を、紙や合成樹脂フィルム等の基材の少なくとも片面に塗布、乾燥することによってディレードタック（遅延粘着）型の感熱ラベルとするものである。
【０００８】
上記のようにして得られた感熱ラベルは、熱活性後、各種被貼着体、例えば、ガラス瓶、プラスチックボトル等、あるいはガラス板、ステンレス板、ポリエチレンやポリエステル板等に貼着されて使用される。
【０００９】
また、上記ディレードタック（遅延粘着）型の感熱ラベルに対し、常温では接着（粘着）性はないが、加熱によって活性化して接着（粘着）性が生じ、加熱後即座に被着体（ガラス瓶等）に貼着し、冷却で固化し接着されるホットメルト型の感熱ラベルがあり、このホットメルト接着剤としては、例えばベースポリマーとしてのエチレン−酢酸ビニル共重合体、スチレン−ブタジエンまたはスチレン−イソプレンなどのブロック共重合体、ポリアミド、アクリルエステル共重合体などに、ホットタック性の付与とともに溶融粘度を下げて塗布し易くする粘着付与剤としてのウッドロジン等ロジンおよびその誘導体など、さらに溶融粘度やブロッキング性等を調整するパラフィンワックスなどで代表されるワックス類が添加されたものがあった。
【００１０】
【発明が解決しようとする課題】
しかしながら、上記ディレードタック（遅延粘着）型の感熱ラベルあるいはホットメルト型の感熱ラベルは、被貼着体であるガラス瓶等の使用後、例えばリユースあるいはリサイクルのため、被貼着体から剥離する場合、その被貼着体によって接着（貼着）強度に差はあるものの、感熱性粘着剤あるいはホットメルト接着剤が被貼着体に転着して残ったり、基材が紙の場合は紙の層間破壊等を起こし破れたりして、被貼着体に残った感熱粘着剤あるいはホットメルト接着剤等の除去に多大の労力を要するという問題があった。
【００１１】
さらにまた上記ディレードタック（遅延粘着）型の感熱ラベルにおいては、被貼着体へのラベリングに際し、粉吹き（感熱性粘着剤層のエマルジョン粉末が飛散する）現象が発生し、ラベリング機械回りの頻繁の清掃を不可欠にするという問題点があった。
【００１２】
本発明は、かかる従来技術の問題点を解決するものであり、その課題とするところは、常温では粘着性がなく、加熱により粘着性が発現する感熱性粘着剤層を備えた感熱ラベルにおいて、使用後の剥離に際し、感熱性粘着剤層が被貼着体に残ったり、ラベルが破れたりせず、手による剥離を容易にし、かつラベリング時での粉吹き現象のない易剥離性感熱ラベルを提供することにある。
【００１３】
【課題を解決するための手段】
本発明に於いて上記課題を達成するために、まず請求項１の発明では、基材の片面に表示層が施され、他の面に感熱性粘着剤層が施されている感熱ラベルにおいて、前記感熱性粘着剤層は、粘着付与剤が添加された感熱樹脂でなり、厚さ１０〜６０μｍの範囲の塗布膜でなることを特徴とする易剥離性感熱ラベルとしたものである。
【００１４】
上記請求項１の発明によれば、上記感熱性粘着剤層は、粘着付与剤が添加された感熱樹脂で形成されているので、常温では粘着性がなく、被貼着体への貼着（ラベリング）に際し、加熱によりこの感熱性粘着剤層に粘着性が発現し、粘着付与剤によりある程度のディレードタック性を有するので貼着し易く、さらに厚さ１０〜６０μｍの範囲の塗布膜とすることによって、使用後の剥離に際し、この厚さのある塗布膜が破壊等に強くなる（破れ難くなる）ので、感熱性粘着剤層の層間剥離による残りや基材を含めた破れ等がなくなり、手による被貼着体からの剥離を容易にし、また従来のディレードタック型の感熱ラベルのようなエマルジョンタイプの感熱性粘着剤ではないので、ラベリング時での粉吹き現象のない易剥離性感熱ラベルを提供できる。
上記感熱性粘着剤層の塗布膜の厚さが１０μｍに満たないと耐破れ性等に乏しくなるので、使用後の剥離に際し、塗布膜が破れたりして被着体に残ったりし、逆に６０μｍを越えると基材との接着性に乏しくなったり、さらに材料コストが嵩むなどの問題が発生するので好ましくない。
【００１５】
また、請求項２の発明では、上記感熱性粘着剤層の塗布膜は、溶融押出機により形成されていることを特徴とする請求項１記載の易剥離性感熱ラベルとしたものである。
【００１６】
上記請求項２の発明によれば、厚さ１０〜６０μｍという厚い塗布膜を溶融押出機によって形成するので、上記感熱性粘着剤層の形成がより高効率で、製造コストが嵩まない易剥離性感熱ラベルとすることができる。
【００１７】
【発明の実施の形態】
以下本発明の実施の形態を説明する。
本発明の易剥離性感熱ラベルの構成は、図１の側断面図に示すように、例えば基材（１０）の表面に印刷層（１２）が施され、裏面には感熱性粘着剤層（１４）が施されている感熱ラベル（１）である。
【００１８】
また、上記易剥離性感熱ラベルの構成として、例えば図２の側断面図に示すように、基材（１０）と感熱性粘着剤層（１４）の間にアンカーコート層（１６）を施したものや印刷層（１２）上に保護層（１８）を設けて耐磨耗性のあるものとすることもできる。また図示しないが、基材が透明なプラスチックフィルムの場合は、基材の裏面に印刷層を施して、表面の保護層を省略し、耐磨耗性のある易剥離性感熱ラベルとすることもできる。
【００１９】
そこで、上記請求項１に係る発明では、図１または図２に示す感熱性粘着剤層（１４）は、粘着付与剤が添加された感熱樹脂でなり、その厚さが１０〜６０μｍの範囲の塗布膜で形成されている易剥離性感熱ラベル（１）とするものである。
【００２０】
上記感熱樹脂としては、例えば酢酸ビニル（ＶＡ）含有量５〜３０％のエチレン／酢酸ビニル共重合体（ＥＶＡ）、エチレン／メタアクリル酸共重合体（ＥＭＡＡ）、エチレン／アクリル共重合体（ＥＡＡ）、あるいは直鎖状低密度ポリエチレン（ＬＬＤＰＥ）等が挙げられ、溶融押出機でフィルム化が可能な樹脂が使用できる。
【００２１】
また、上記感熱樹脂に添加される粘着付与剤としては、加熱により活性化された際に粘着性を増強させるための成分であり、例えば、ロジン誘導体、テルペン樹脂系、石油樹脂系、フェーノール樹脂系、キシレン樹脂系等の樹脂類が挙げられ、上記感熱樹脂に対し０．５％程度添加されて使用される。
【００２２】
また、上記基材（１０）としては、例えば坪量３０〜１００ｇ／ｍ２　程度の片アート紙、両アート紙、アルミニウム蒸着紙、さらに厚さ１５〜２５μｍ程度のポリエチレンテレフタレートフィルム、延伸ポリプロピレンフィルム、延伸ナイロンフィルムなどが使用される。
【００２３】
また、上記請求項２に係る発明では、図１または図２に示す感熱性粘着剤層（１４）を、溶融押出機によって基材（１０）の片面（裏面）に押し出し、上記請求項１に係る発明の、その厚さを１０〜６０μｍの塗布膜として易剥離性感熱ラベル（１）とするものである。
【００２４】
上記のようにして得られた易剥離性感熱ラベル（１）は、常温では粘着性がないので、例えば粘着ラベルのように粘着層を覆うための剥離台紙が不要で、ガラス瓶等被貼着体への貼着に際し、例えば感熱ラベラーで感熱性粘着剤層（１４）を加熱すると粘着性が発現し、この粘着性が保持されている間に被貼着体に加圧固着せしめられるもので、一定時間経過後（実際は使用後）、手でこの易剥離性感熱ラベル（１）を剥離すると、ラベルが破れたり、感熱性粘着剤層（１４）が被貼着体に残ったりすることがなく、スムースに剥離することのできる易剥離性感熱ラベル（１）である。
【００２５】
【実施例】
次に実施例により、本発明を具体的に説明する。
〈実施例１〉
基材として坪量７９．１ｇ／ｍ２　の片アート紙を用い、その表面であるアートコート面にオフセット印刷法により印刷して表示層とし、その上にアクリル樹脂でなるオーバーコートニスをグラビアコーティング法にて保護層を形成した。
【００２６】
次に基材の他の面（裏面）に、感熱樹脂として酢酸ビニル含有量（ＶＡ％）２０％のエチレン／酢酸ビニル共重合体（ＥＶＡ）に粘着付与剤としてロジン誘導体を０．５％添加し、これを溶融押出機で押し出し、厚さ３０μｍの感熱性粘着剤層を形成し、幅７６ｍｍにスリットしてロール状の易剥離性感熱ラベルを得た。
【００２７】
〈比較例１〉
感熱性粘着剤層として、樹脂がアクリル系のディレードタック型感熱ニスを用いて１０ｇ／ｍ２　に塗布した以外は、実施例１と同様にしてロール状の感熱ラベルを得た。
【００２８】
上記実施例１および比較例１で得られたロール状の感熱ラベルを、感熱ラベラーに装填し、ＰＥＴボトル表面にラベリングし、一週間後に手で剥離して、その状態を目視で観察した結果、
実施例１で得られた易剥離性感熱ラベルでは、紙の材破がなく、かつＰＥＴボトルに感熱性粘着剤層の残りも見られなかった。
これに対し比較例１で得られた感熱ラベルでは、紙の材破が発生し、その一部がＰＥＴボトルに残り、そけを取るのが容易ではなかった。
【００２９】
【発明の効果】
本発明は以上の構成であるから、下記に示す如き効果がある。
即ち、上記請求項１に係る発明においては、基材の片面に表示層が施され、他の面に感熱性粘着剤層が施されている感熱ラベルにおいて、上記感熱性粘着剤層は、粘着付与剤が添加された感熱樹脂で形成されているので、常温では粘着性がなく、被貼着体への貼着（ラベリング）に際し、加熱によりこの感熱性粘着剤層に粘着性が発現し、粘着付与剤によりある程度のディレードタック性を有するので貼着し易く、さらに厚さ１０〜６０μｍの範囲の塗布膜とすることによって、使用後の剥離に際し、この厚さのある塗布膜が破壊等に強くなる（破れ難くなる）ので、感熱性粘着剤層の層間剥離による残りや基材を含めた破れ等がなくなり、手による被貼着体からの剥離を容易にし、貼着される容器等のリサイクルやリユースに貢献し、また従来のディレードタック型の感熱ラベルのようなエマルジョンタイプの感熱性粘着剤ではないので、ラベリング時での粉吹き現象のない易剥離性感熱ラベルを提供できる。
【００３０】
また、上記請求項２に係る発明においては、厚さ１０〜６０μｍという厚い塗布膜を溶融押出機によって形成するので、上記感熱性粘着剤層の形成がより高効率で、製造コストが嵩まない易剥離性感熱ラベルとすることができる。
【００３１】
従って本発明は、常温では粘着性がなく、加熱により活性化して粘着性が発現する感熱性粘着剤層を備えた感熱ラベルで、特にガラス瓶やプラスチック容器などに加熱貼着され、使用後に剥離を容易にし、その容器のリサイクルやリユースに貢献する易剥離性感熱ラベルとして、優れた実用上の効果を発揮する。
【図面の簡単な説明】
【図１】本発明の易剥離性感熱ラベルの一実施の形態を積層側断面で表した説明図である。
【図２】本発明の易剥離性感熱ラベルの他の一実施の形態を積層側断面で表した説明図である。
【符号の説明】
１‥‥易剥離性感熱ラベル
１０‥‥基材
１２‥‥印刷層
１４‥‥感熱性粘着剤層
１６‥‥アンカーコート層
１８‥‥保護層[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a heat-sensitive label having a heat-sensitive pressure-sensitive adhesive layer which is not tacky at room temperature and is activated by heating to become tacky, and is particularly applied to a glass bottle or a plastic container by heating and peeling after use. The present invention relates to an easily peelable heat-sensitive label that facilitates recycling and contributes to recycling of containers.
[0002]
[Prior art]
Conventionally, printing is performed on the surface of paper or the like, and a heat-sensitive adhesive layer is applied on the back surface.This heat-sensitive adhesive layer has no tackiness at room temperature, but is activated by heating and becomes tacky, Thermal labels are known to be attached to glass bottles, plastic containers, etc.In particular, unlike label manufacturers, this label manufacturer does not require a release liner to cover the adhesive before it is applied. Since it is affixed to a plastic container or the like, it is widely used as a heat-sensitive label that is easy to handle for sticking and sticking to production.
[0003]
The heat-sensitive adhesive referred to above is, for example, as described in “Adhesion Handbook”, 12th edition, p. 131 (published by the Society of Polymer Publishing, 1980), and its basic composition is a water-insoluble polymer. Adhesive (adhesive) consisting of materials, tackifiers, and solid plasticizers, is non-tacky at room temperature, but is activated by heating to produce tack, and the tack persists for a considerable period of time after cooling Usually, since the dried coating film of the pressure-sensitive adhesive has no tack, a release liner for covering the pressure-sensitive adhesive is not required.
[0004]
The water-insoluble polymer material in the above composition is a component that gives an adhesive force, for example, polyvinyl acetate, ethylene-vinyl acetate copolymer, polyacrylate, polyvinyl chloride, natural rubber, synthetic rubber Rubber, vinyl acetate-acrylate copolymers, polyester-based and polyurethane-based water-insoluble polymer compounds are used.
[0005]
Further, the tackifier is a component for enhancing the tackiness when activated by heating, for example, a resin such as a rosin derivative, a terpene resin, a petroleum resin, a phenol resin, and a xylene resin. Kind is used.
[0006]
Further, the solid plasticizer is a solid at room temperature, melts when heated above its melting point, swells and dissolves the water-insoluble polymer material and tackifier, and develops adhesion and adhesion. Let it. Since it does not readily crystallize once dissolved, it is possible to increase the adhesive retention time after activation.For example, diphenyl phthalate, dihexyl phthalate, dicyclohexyl phthalate, dihydroabiethyl phthalate, isophthalate Dimethyl succinate, sucrose benzoate, ethylene glycol dibenzoate, trimethylolethane tribenzoate, glyceride tribenzoate, pentaerythrate tetrabenzoate, sucrose octaacetate, tricyclohexyl citrate N-cyclohexyl-P-toluenesulfonamide, etc. Organic compounds that are solid at room temperature are used.
[0007]
As described above, a heat-sensitive adhesive obtained by dispersing a water-insoluble polymer material, a tackifier, and a solid plasticizer in an aqueous solvent is applied to at least one surface of a substrate such as paper or a synthetic resin film. And dried to form a delayed tack (delayed adhesive) type heat-sensitive label.
[0008]
The heat-sensitive label obtained as described above is used after being thermally activated and attached to various adherends, for example, a glass bottle, a plastic bottle, or the like, or a glass plate, a stainless plate, a polyethylene or polyester plate, or the like. .
[0009]
In addition, the above-mentioned delayed tack (delayed adhesion) type thermal label does not have adhesiveness (adhesiveness) at room temperature, but is activated by heating to generate adhesiveness (adhesiveness). ) Is a hot-melt type heat-sensitive label which is adhered to the substrate and solidified and bonded by cooling. Examples of the hot-melt adhesive include an ethylene-vinyl acetate copolymer as a base polymer, styrene-butadiene or styrene-isoprene. Such as block copolymers, polyamides, acrylic ester copolymers, etc., rosin such as wood rosin and its derivatives as tackifiers to reduce the melt viscosity with hot tack and to facilitate application, further melt viscosity and blocking There was a wax to which waxes represented by paraffin wax etc. for adjusting properties etc. were added
[0010]
[Problems to be solved by the invention]
However, when the delayed tack (delayed adhesive) -type heat-sensitive label or hot-melt-type heat-sensitive label is peeled off from the adherend after use of the adherend, such as a glass bottle, for example, for reuse or recycling, Although there is a difference in adhesion (adhesion) strength depending on the adherend, the heat-sensitive adhesive or hot melt adhesive is transferred to the adherend and remains on the adherend. There has been a problem that a great deal of labor is required to remove the heat-sensitive adhesive or the hot-melt adhesive remaining on the adherend due to breakage or the like.
[0011]
Further, in the delayed tack (delayed adhesive) type thermal label, a phenomenon of powder blowing (dispersion of the emulsion powder of the thermosensitive adhesive layer) occurs when labeling an adherend, and frequent labeling around the labeling machine. There was a problem that cleaning was indispensable.
[0012]
The present invention is to solve the problems of the prior art, the subject of the present invention is that there is no adhesive at room temperature, a heat-sensitive label provided with a heat-sensitive adhesive layer that exhibits adhesiveness by heating, When peeling after use, the heat-sensitive adhesive layer does not remain on the adherend, the label is not broken, the peeling by hand is easy, and the easily peelable heat-sensitive label without powder blowing phenomenon at the time of labeling is used. To provide.
[0013]
[Means for Solving the Problems]
In order to achieve the above object in the present invention, first, in the invention of claim 1, in a heat-sensitive label in which a display layer is provided on one surface of a substrate and a heat-sensitive adhesive layer is provided on the other surface, The heat-sensitive adhesive layer is made of a heat-sensitive resin to which a tackifier is added, and is a coating film having a thickness of 10 to 60 μm.
[0014]
According to the first aspect of the present invention, since the heat-sensitive adhesive layer is formed of a heat-sensitive resin to which a tackifier is added, the heat-sensitive adhesive layer has no tackiness at normal temperature and is attached to an adherend ( At the time of labeling), the heat-sensitive pressure-sensitive adhesive layer develops adhesiveness by heating and has a certain degree of delayed tackiness due to the tackifier, so that it is easy to stick, and a coating film having a thickness in the range of 10 to 60 μm. As a result, when peeling after use, the thick coated film becomes strong against destruction or the like (it becomes difficult to be torn), so that the residue due to delamination of the heat-sensitive adhesive layer and the tear including the base material are eliminated, and the hand is removed. It is easy to peel off from the adherend by the above, and because it is not an emulsion-type heat-sensitive adhesive like the conventional delayed tack-type heat-sensitive label, an easy-to-peel heat-sensitive label that does not have a powder blowing phenomenon during labeling Offer It can be.
If the thickness of the coating film of the heat-sensitive adhesive layer is less than 10 μm, the film will have poor tear resistance, etc., and upon peeling after use, the coating film is broken or remains on the adherend, and conversely, If it exceeds 60 μm, problems such as poor adhesion to the substrate and further increase in material cost occur, which is not preferable.
[0015]
In the invention according to claim 2, the coating film of the heat-sensitive adhesive layer is formed by a melt extruder to provide the easily peelable heat-sensitive label according to claim 1.
[0016]
According to the second aspect of the invention, since a thick coating film having a thickness of 10 to 60 μm is formed by a melt extruder, the formation of the heat-sensitive adhesive layer is more efficient, and the production cost is not increased. It can be a thermosensitive label.
[0017]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, embodiments of the present invention will be described.
As shown in the side sectional view of FIG. 1, the configuration of the easily peelable thermosensitive label of the present invention is such that, for example, a printing layer (12) is provided on the surface of a substrate (10), and a heat-sensitive adhesive layer ( 14) is a heat-sensitive label (1) provided with the same.
[0018]
In addition, as a configuration of the easily peelable heat-sensitive label, an anchor coat layer (16) is provided between the base material (10) and the heat-sensitive adhesive layer (14), for example, as shown in a side sectional view of FIG. A protective layer (18) may be provided on the object or the printed layer (12) to make it wear-resistant. Although not shown, when the base material is a transparent plastic film, a printing layer may be applied to the back surface of the base material, the protective layer on the surface may be omitted, and an easily peelable heat-sensitive label having abrasion resistance may be formed. it can.
[0019]
Therefore, in the invention according to claim 1, the heat-sensitive adhesive layer (14) shown in FIG. 1 or 2 is made of a heat-sensitive resin to which a tackifier is added, and has a thickness of 10 to 60 μm. This is an easily peelable thermosensitive label (1) formed of a coating film.
[0020]
Examples of the heat-sensitive resin include ethylene / vinyl acetate copolymer (EVA), ethylene / methacrylic acid copolymer (EMAA), and ethylene / acrylic copolymer (EAA) having a vinyl acetate (VA) content of 5 to 30%. ) Or linear low-density polyethylene (LLDPE). A resin that can be formed into a film by a melt extruder can be used.
[0021]
Further, as a tackifier added to the heat-sensitive resin, a component for enhancing the tackiness when activated by heating, for example, rosin derivative, terpene resin, petroleum resin, phenol resin resin And xylene resin-based resins, which are used by being added to the above-mentioned heat-sensitive resin at about 0.5%.
[0022]
Examples of the base material (10) include single art paper, double art paper, and aluminum-evaporated paper having a basis weight of about 30 to 100 g / m2, a polyethylene terephthalate film having a thickness of about 15 to 25 μm, a stretched polypropylene film, and a stretched polypropylene film. A nylon film or the like is used.
[0023]
Further, in the invention according to claim 2, the heat-sensitive adhesive layer (14) shown in FIG. 1 or FIG. 2 is extruded onto one surface (back surface) of the substrate (10) by a melt extruder. The invention provides an easily peelable thermosensitive label (1) as a coating film having a thickness of 10 to 60 μm.
[0024]
Since the easily peelable heat-sensitive label (1) obtained as described above has no tackiness at room temperature, a peeling backing for covering the adhesive layer, such as an adhesive label, is unnecessary, and an adherend such as a glass bottle is not required. When the heat-sensitive adhesive layer (14) is heated by, for example, a heat-sensitive labeler at the time of sticking to the heat-sensitive adhesive, the stickiness is developed, and the pressure-sensitive adhesive is fixed to the adherend while the tackiness is maintained. After a certain period of time (actually after use), when the easily peelable heat-sensitive label (1) is peeled by hand, the label is not broken and the heat-sensitive adhesive layer (14) does not remain on the adherend. And an easily peelable heat-sensitive label (1) that can be peeled smoothly.
[0025]
【Example】
Next, the present invention will be specifically described with reference to examples.
<Example 1>
A piece of art paper having a basis weight of 79.1 g / m2 is used as a base material, and an art coat surface, which is a surface thereof, is printed by an offset printing method to form a display layer, and an overcoat varnish made of an acrylic resin is gravure coated thereon. To form a protective layer.
[0026]
Next, to the other surface (back surface) of the base material, 0.5% of a rosin derivative is added as a tackifier to an ethylene / vinyl acetate copolymer (EVA) having a vinyl acetate content (VA%) of 20% as a heat-sensitive resin. This was extruded with a melt extruder to form a heat-sensitive adhesive layer having a thickness of 30 μm, and slit into a width of 76 mm to obtain a roll-shaped easily peelable heat-sensitive label.
[0027]
<Comparative Example 1>
A roll-shaped heat-sensitive label was obtained in the same manner as in Example 1 except that the resin was applied to the heat-sensitive adhesive layer at 10 g / m2 using a delayed tack-type heat-sensitive varnish made of an acrylic resin.
[0028]
The roll-shaped heat-sensitive label obtained in Example 1 and Comparative Example 1 was loaded on a heat-sensitive labeler, labeled on the surface of a PET bottle, peeled by hand one week later, and the state was visually observed.
In the easily peelable heat-sensitive label obtained in Example 1, no paper material was broken, and no residue of the heat-sensitive adhesive layer was observed on the PET bottle.
On the other hand, in the heat-sensitive label obtained in Comparative Example 1, breakage of the paper occurred, and a part thereof remained in the PET bottle, and it was not easy to remove the shading.
[0029]
【The invention's effect】
The present invention having the above configuration has the following effects.
That is, in the invention according to claim 1, in a heat-sensitive label in which a display layer is provided on one surface of a base material and a heat-sensitive adhesive layer is provided on the other surface, the heat-sensitive adhesive layer has an adhesive layer. Since it is formed of a heat-sensitive resin to which an imparting agent has been added, there is no tackiness at room temperature, and upon application (labeling) to an adherend, the heat-sensitive pressure-sensitive adhesive layer develops tackiness by heating, It has a certain degree of delayed tackiness due to the tackifier, so it is easy to stick, and by forming a coating film having a thickness in the range of 10 to 60 μm, when peeling after use, this thick coating film may break. Since it becomes strong (it becomes difficult to tear), the residue due to delamination of the heat-sensitive adhesive layer and tearing including the base material are eliminated, and the peeling from the adherend by hand is facilitated. Contribute to recycling and reuse, Is not a emulsion-type heat-sensitive adhesive, such as delayed tack type thermal label of years, it can provide easy peelability thermal label without powdering phenomenon at the time of labeling.
[0030]
Further, in the invention according to claim 2, since a thick coating film having a thickness of 10 to 60 μm is formed by a melt extruder, the formation of the heat-sensitive adhesive layer is more efficient, and the production cost is not increased. An easily peelable thermosensitive label can be obtained.
[0031]
Accordingly, the present invention is a heat-sensitive label having a heat-sensitive adhesive layer that is not tacky at room temperature and is activated by heating to exhibit tackiness, and is particularly heat-adhered to a glass bottle, a plastic container, or the like, and peels off after use. It has excellent practical effects as an easily peelable thermal label that facilitates and contributes to the recycling and reuse of the container.
[Brief description of the drawings]
FIG. 1 is an explanatory view showing an embodiment of the easily peelable heat-sensitive label of the present invention in a lamination side cross section.
FIG. 2 is an explanatory view showing another embodiment of the easily peelable heat-sensitive label of the present invention in a lamination side cross section.
[Explanation of symbols]
1 {easy peeling heat-sensitive label 10} substrate 12} printing layer 14 {heat-sensitive adhesive layer 16} anchor coating layer 18} protective layer

Claims (2)

基材の片面に表示層が施され、他の面に感熱性粘着剤層が施されている感熱ラベルにおいて、前記感熱性粘着剤層は、粘着付与剤が添加された感熱樹脂でなり、厚さ１０〜６０μｍの範囲の塗布膜でなることを特徴とする易剥離性感熱ラベル。In a heat-sensitive label in which a display layer is provided on one surface of a base material and a heat-sensitive adhesive layer is provided on the other surface, the heat-sensitive adhesive layer is made of a heat-sensitive resin to which a tackifier is added, and An easily peelable heat-sensitive label comprising a coating film having a thickness of 10 to 60 μm. 上記感熱性粘着剤層の塗布膜は、溶融押出機により形成されていることを特徴とする請求項１記載の易剥離性感熱ラベル。The easily peelable heat-sensitive label according to claim 1, wherein the coating film of the heat-sensitive adhesive layer is formed by a melt extruder.

Images