JP2004012591A - Sidelight type backlight device and liquid crystal display device - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a sidelight type backlight device with high luminance and excellent durability and without uneven brightness, and a liquid crystal display device. <P>SOLUTION: The sidelight type backlight device has a reflection body mounted under a light transmission plate 2. The light transmission plate 2 has a prism shape on the light-emitting surface side. The ratio of diffuse reflectance to reflectance as a whole (diffusibility) of the reflection body with respect to a light ray of 550 nm wavelength is set to be 1-50%. <P>COPYRIGHT: (C)2004,JPO

Description

【０００１】
【発明の属する技術分野】
本発明は、輝度が高く輝度ムラの少ない液晶表示装置などに適用されるサイドライト型のバックライト装置および液晶表示装置に関する。
【０００２】
【従来技術】
液晶ディスプレイはこれまでのＣＲＴ（Ｃａｔｈｏｄｅ　Ｒａｙ　Ｔｕｂｅ）ディスプレイに比べ、薄型であり省スペース化できること、また、低電圧で作動すること、消費電力が少なく省エネルギー化できるなどの特徴から、中小型機器のディスプレイを中心に広く用いられている。
【０００３】
現在広く使用されている液晶ディスプレイは、光源にバックライトを用いる透過型液晶ディスプレイである。この液晶ディスプレイにおける表示の見やすさは、液晶自身の性能もさることながら、バックライトの性能によるところも大きくなっている。バックライトの方式は近年の液晶ディスプレイのさらなる軽量、薄型化が必須事項となっていることや、輝度の均一性や、光源からの熱が液晶パネルに伝達しにくいなどの理由より、光源の前方に反射板を置く直下型ではなく、導光板を用い、その一端に配置された光源からの光を多重反射させることで面光源化するサイドライト式バックライトが多く用いられている。
【０００４】
導光板の下には、白色ＰＥＴ（ポリエチレンテレフタレート）フィルム等からなる乱反射部材が配設されている場合が多く、この乱反射部材で光を拡散させることにより、均一な輝度を得ることが出来る。しかしながら、この乱反射部材では、正反射成分が殆どないため、全体としては均一ではあるが十分な輝度は得ることができないという問題がある。また、透明性または透光性を有するＰＥＴフィルム上にアルミニウムを蒸着したシートを用いると、白色ＰＥＴに比べ輝度は向上するものの、拡散反射成分が無いため、シートの僅かな歪みが輝度ムラに大きく影響してしまい、美しい画像を得ることができない。この問題を解決するため、表面を粗面化したフィルムに金属を蒸着したシートが開発されたが、用いる金属にアルミニウムを使うと、耐久性は優れるが輝度の改善は少ない。また、可視光域で最も反射率の高い銀を使うと、十分な輝度が得られるものの、銀は耐久性が乏しい為、劣化が早く、輝度が経時的に低下してしまうという問題があった。またこれらの反射シートを用いたバックライトは経時的に輝度ムラが増大するという問題があった。
【０００５】
【発明が解決しようとする課題】
本発明は、高輝度で耐久性に優れ、さらに輝度ムラの無いサイドライト型バックライト装置および液晶表示装置を提供することを目的とする。
【０００６】
【課題を解決するための手段】
本発明者らは、上記の課題を解決するため鋭意検討した結果、特定の形状を有する導光板を用い適度な拡散反射率を有する反射体を導光板の下に配置することにより、輝度ムラを解消もしくは著しく低減出来ること、高い輝度および耐久性を同時に実現出来ることを見出した。
【０００７】
本発明は一つには導光板の下に反射体が装備されたサイドライト型バックライト装置であって、導光板の出光面側がプリズム形状を有し、反射体の波長５５０ｎｍの光線における全反射率に対する拡散反射率の割合（拡散率）が１％〜５０％であることを特徴とするサイドライト型バックライト装置であり、
一つには前記反射体が基板と反射層とからなり、反射層側に最大幅０．１μｍ〜５０μｍ、高さ０．１μｍ〜４５μｍの突起物を１ｍｍ^２当たり２個以上１００個以下有することを特徴とするサイドライト型バックライト装置であり、
一つには前記反射体の波長５５０ｎｍにおける全反射率が９０％以上、かつ、拡散反射率が１０％以下であることを特徴とするサイドライト型バックライト装置であり、
一つには前記導光板がプリズム形状を有する面の反対側の面に凹凸形状を有することを特徴とするサイドライト型バックライト装置であり、
一つには前記導光板のプリズム形状面と反対側の面の凹凸形状が俵型であることを特徴とするサイドライト型バックライト装置である。
【０００８】
本発明に従えば、特定の形状を有する導光板と適度な拡散率を有する反射体を用いたバックライトは、輝度ムラを解消もしくは著しく低減すると共に、高い輝度、耐久性、広い視野角を同時に実現することが可能である。
【０００９】
一つには前記サイドライト型バックライト装置を備えることを特徴とする液晶表示装置である。
【００１０】
本発明に従えば、輝度、耐久性が高く、輝度ムラが著しく低減され、視野角の広い視認性に優れた液晶ディスプレイを提供することができる。従って、長期にわたり均一で高輝度な光を得られる為、液晶の表示能力を向上させることができる本発明の工業的意義は大きい。
【００１１】
【発明の実施の形態】
以下図面を参考にして本発明の好適な実施例を詳細に説明する。
【００１２】
本明細書においては、後述する反射体の反射層を形成する側の面をＡ面、反対側をＢ面と呼ぶことがある。また、導光板の出光面をＣ面、出光面と反対側の面を反射入光面またはＤ面と呼ぶことがある。
【００１３】
図１は、本発明の実施の一形態である反射体１の例を示す断面図である。
本発明の反射体は基板１０と反射層２０とからなり、Ａ面側に粒子３０を塗布して突起物を形成し、Ｂ面側に易滑面４０を形成する。
【００１４】
図２は、本発明の実施の一形態である導光板２の断面図である。出光面がプリズム形状に成形されている。
【００１５】
図３は、本発明の実施の一形態である導光板２の反射入光面の平面図である。俵型の凹形状が規則的な配列で形成されている。
【００１６】
図４は、反射体１を備えたサイドライト型バックライト装置３の斜視図である。サイドライト型バックライト装置３は、導光板２の反射入光面に、反射層２０が接するように反射体１が配置され、出光面側に下向きプリズムシート７０、拡散シート８０が順次設置され、側面に光源５０とランプリフレクター６０とが備えられている。光源５０からの光は、反射体１によって反射され、液晶表示パネルの背面に取り付けることで面光源装置として機能する。
【００１７】
使用される導光板２は、例えば、ポリメチルメタクリレートなどのアクリル系樹脂、ポリカーボネートやポリカーボネート・ポリスチレン組成物などのポリカーボネート系樹脂、エポキシ系樹脂などの透明性または透光性樹脂やガラスなどの約４００ｎｍ〜７００ｎｍの波長域において透明性を有するものが好ましく用いられるが、光源の波長領域に応じて透明性を示す材料であれば必ずしもこれらに限定される訳ではない。
【００１８】
導光板２の厚さは、使用目的の導光板のサイズや、光源の大きさなどにより適宜に決定することができるが、好ましくは５ｍｍ以下、より好ましくは１〜４ｍｍである。また、厚みは一様である必要はなく、光源５０付近が厚く、光源５０から離れるに連れ、薄くなる形状が好ましい場合がある。
【００１９】
導光板２の出光面側はプリズム形状が形成されている。このプリズム形状は、台形型、山型等があるが、山型であることが好ましい。また上記プリズム形状は連続していても不連続でも良いが、連続した形状であることが成形、集光効率等の点で好ましい。更に、上記プリズム形状は光源側の面と垂直に並ぶように形成されることが好ましい。この際のピッチは１０〜３００μｍ、好ましくは１５〜２００μｍ、更に好ましくは２０〜１５０μｍである。
【００２０】
導光板２の反射入光面は、ドット形状の凹凸を有するのが好ましい。該凹凸形状は、ドーム型、俵型、台形、くさび形、箱形、円筒型、角錐型、円錐型等が例示できるが、ドーム型、箱形、俵型であることが好ましく、更に好ましくは俵型である。この凹凸高さ（深さ）は１００μｍ以下、好ましくは１〜５０μｍであり、最大幅は、３００μｍ以下、好ましくは１０〜２００μｍであり、アスペクト比は１〜１０、好ましくは１〜６である。またピッチは１〜７００μｍ、好ましくは１０〜５００μｍ、更に好ましくは５０μｍ〜４００μｍである。突起の密度は一様である必要はなく光源付近が密であったり、周辺部が密であることが好ましい場合がある。また上記の凹凸はランダムに配置されていても規則的に整列していても良いが、上記のプリズム形状と直行する方向に整列していること、更には光源側の面と平行方向に整列していることが好ましい。
【００２１】
導光板２のプリズム形状および凹凸形状の形成は、予め目的とする表面形状の金型を用意し、射出成形法により成型する方法や、金型が比較的安価な平滑な表面の射出成形体を得た後に、熱変形、切削加工、印刷により所定の表面形状を形成する方法、所定の表面形状を有するシートを貼合する方法等を例示することが出来る。
【００２２】
本発明において、反射体１の少なくともＡ面側、Ｂ面側のいずれかから測定した反射率の波長５５０ｎｍにおける拡散反射率と全反射率の比（拡散反射率／全反射率：拡散率）は１〜５０％であり、好ましくは１〜２０％、特に好ましくは１〜１７％、更に好ましくは１〜１５％である。また、全反射率は通常８５％以上、好ましくは９０％以上、特に好ましくは９０〜９９％であり、拡散反射率は５０％以下、好ましくは２０％以下、より好ましくは１７％以下、特に好ましくは１〜１０％である。なお、５５０ｎｍは、人間の眼の受光感度が最も高くなる波長であり、実際の視認性を評価するに適している。
【００２３】
基板１０は、引っ張り弾性率は２０００ＭＰａ以上、好ましくは２５００ＭＰａ以上、更に好ましくは３０００ＭＰａ以上、特に好ましくは３５００ＭＰａ以上であることを特徴とする。引っ張り弾性率は、ＡＳＴＭ Ｄ−８８２規格にて主に測定される。
【００２４】
具体的には物理的、化学的に安定なガラス板、セラミック板等の板状、シート状の無機材料、高分子シート、高分子フィルム等の有機材料等が適宜用いられる。これらの中でも、形状の自由度が高く、例えば反射層２０を作成する際にロールツーロールプロセスが適用できる高分子フィルムが望ましい。
【００２５】
本発明の反射体１において、使用するに好ましい高分子フィルムは、例えばポリエチレンテレフタレート（ＰＥＴ）、ポリエチレンナフタレートなどのポリエステル類、ビスフェノールＡ系ポリカーボネートなどのポリカーボネート類、環状オレフィン共重合体、ポリイミド類、ナイロン等のポリアミド類、ポリエーテルスルホン類、ポリスルホン系樹脂、ポリアリレート系樹脂、フッ素系樹脂、ポリエーテルーテルケトン類、ポバール等のポリアセタール類等各種プラスチックからなるフィルムが挙げられるが、必ずしもこれらに限定されるものではなく、結晶化温度やガラス転移点が高く、平滑な表面を持つものであれば使用できる。なかでもポリエチレンテレフタレート等のポリエステル類、ポリカーボネート類、ポリアミド類が好ましい。
【００２６】
使用される高分子フィルムの厚みは、通常は１〜２５０μｍであり、好ましくは５〜２００μｍ、特に好ましくは１０〜２００μｍである。
【００２７】
本発明の反射体１は、基板１０上の後述する反射層２０を有する面側に好ましくは突起物を有している。上記の突起物は基板１０に直接形成させることも出来るし、別途作製した突起物層フィルムやシートを基板１０に貼り合わせることも出来る。また、後述する反射層２０の上に形成することも可能である。
【００２８】
上記の突起物の最大幅は０．１〜５０μｍであり、好ましくは１〜５０μｍ、より好ましくは１０〜５０μｍ、更に好ましくは１５〜４５μｍ、特に好ましくは２０〜４０μｍである。また上記突起物の高さは、０．１〜４５μｍであり、好ましくは１〜４５μｍ、より好ましくは５〜４５μｍ、更に好ましくは１０〜４０μｍ、特に好ましくは１５〜３５μｍである。また、突起物の形状は特に制限はなく、粒子型、ドーム型、山型、ピラミッド型、円柱型、角柱型、台形、プリズム型、不定形等を例示することが出来る。また単段形状であっても多段形状であっても良くこれらの形状が混在していたり、多段に組み合わさっていても良い。突起物は、１ｍｍ^２当たり２個以上、１００個以下有することが好ましく、更に好ましくは５個以上９０個以下である。
【００２９】
これらの突起物の作成方法に関しても特に制限はないが、（１）粒子等の固形物を塗布させる方法、（２）粒子などの固形物を樹脂と混練してフィルム、シート状に成形する方法、（３）粒子などの固形物を半溶融状態のフィルム、シートに散布後冷却して定着させる方法、（４）スクリーン印刷の様な印刷技術を利用して突起物を形成する方法、（５）熱可塑性樹脂をシート、フィルムに成型する際に凹凸形状を有する冷却ロールを使用し、ロールの凹凸形状を突起物として転写する方法、（６）マイクロ金型を利用して形成する方法（７）サンドブラスト法などの研磨、摩擦行程を有する方法（８）フォトリソグラフィーを利用して形成する方法（９）エッチング法を利用して形成する方法等を適用させることが出来る。また上記等の方法で得られる突起物を熱処理等で変形させることも可能である。
【００３０】
上記の突起物を形成する方法の中でも特に表面状態の調整が比較的容易な、粒子３０を塗布することにより形成する方法が好ましい。塗布する粒子としては、例えば、アクリル、ポリスチレン、ビニルベンゼン、スチレンメタクリレート、スチレンアクリレート、スチレンブタジエン等の高分子（有機）粒子をはじめ、シリカ、アルミナ、チタニア、ジルコニア、酸化鉛（鉛白）、酸化亜鉛（亜鉛華）、炭酸カルシウム、炭酸バリウム、硫酸バリウム、チタン酸カリウム、ケイ酸ソーダなどからなる無機微粒子や、酸化錫、酸化インジウム、酸化カドミウム、酸化アンチモンなどの導電性透明微粒子なども用いることができるが、必ずしもこれらに限定されるものではない。特にアクリル樹脂またはシリカを用いることが好ましい。
【００３１】
本発明において塗布される粒子３０は、平均粒子径が０．１〜５０μｍ、好ましくは１〜５０μｍ、より好ましくは１０〜５０μｍ、更に好ましくは１５〜４５μｍ、特に好ましくは２０〜４０μｍの粒子を使用することが好ましい。
【００３２】
上記粒子３０の粒径分布は小さい方が好ましく、平均粒子径に対する粒子径の標準偏差の割合は５０％以下であることが好ましい。さらに好ましくは４０％以下である。　但し、必要に応じて２種以上の粒子を用いることも出来る。この場合、主成分の粒子の割合は５０％以上、好ましくは７０％以上、より好ましくは７５％以上、特に好ましくは８０％以上である。
【００３３】
平均粒子径の分布は、少量の粒子を分散させた溶液を動的光散乱法により測定することで求めることができる。また、粒子を撮影したＳＥＭ（Ｓｃａｎｎｉｎｇ　Ｅｌｅｃｔｒｏｎ　Ｍｉｃｒｏｓｃｏｐｅ）写真から無作為に選んだ１００個の粒子径より求めることもできる。また、粒子径は、ＳＥＭ写真以外に光学顕微鏡を用いても読みとることができる。また、得られた写真または像を、画像処理することからも粒径分布を求めることができる。
【００３４】
前記粒子３０は、通常、バインダーとして用いられる樹脂中に分散させた状態で塗布される。バインダー樹脂としては、例えばポリメタクリル酸メチルなどのアクリル樹脂、ポリアクリロニトリル樹脂、ポリメタアクリルニトリル樹脂、エチルシリケートより得られる重合体などの珪素樹脂、フッ素系樹脂、ポリエステル系樹脂、ポリスチレン樹脂、アセテート系樹脂、ポリエーテルサルホン系樹脂、ポリカーボネート系樹脂、ポリアミド系樹脂、ポリイミド系樹脂、ポリオレフィン系樹脂、ポリウレタン系樹脂、尿素樹脂、メラミン樹脂、エポキシ樹脂や、これらの混合物などが挙げられるが、必ずしもこれらに限定される物ではない。これらは基板１０及び粒子３０との密着性を考慮して選択される。なかでも、ポリエステル系樹脂、アクリル樹脂が好ましい。
【００３５】
通常これらの粒子３０をバインダー樹脂に分散させるためには溶媒を用いる。溶媒としては、トルエン、メチルエチルケトン、酢酸エチル、イソプロピルアルコールなどが好ましく用いられる。これらは塗布作業に一般的に用いられる溶媒であり、これら以外でも基板１０や粒子３０に影響を与えない溶媒であれば、問題なく使用できる。また、必要に応じてイソシアネート類やメラミン類などの架橋剤、ぬれ剤や増粘剤、分散剤、消泡剤、などの添加剤を加えてもよい。
【００３６】
粒子３０のバインダー樹脂に対する配合率は、粒子３０がバインダー樹脂に対して０．１ｗｔ％以上１０ｗｔ％以下であることが好ましい。配合率が、０．１ｗｔ％より小さい場合、必要な反射光の拡散特性が得られないため好ましくない場合がある。また、１０ｗｔ％より大きい場合は、光の拡散性が強くなり過ぎるため好ましくない場合がある。
【００３７】
粒子３０を含む塗工液は、基板１０上にｗｅｔ状態で塗工量１０ｇ／ｍ^２以上、４０ｇ／ｍ^２で塗布することが好ましい。粒子の配合率は、反射体１表面の粒子密度に反映され、反射体１の拡散率に影響を及ぼす。また塗布量は、基板１０上のバインダー層の厚みに反映され、粒子３０の頂上と反射層２０との高さの差つまり、導光板２と反射体１との接触時の間隔に影響を及ぼす。塗布液量を１０ｇ／ｍ^２より小さくすると、塗布液中に含まれる粒子３０の量が不足し、必要な反射光の拡散特性が得られない場合があり好ましくない。また、塗布液量を４０ｇ／ｍ^２より大きくすると、粒子３０がバインダー樹脂に埋もれてしまい、必要な突起高さが得られない場合があり好ましくない。つまり、上述範囲で粒子配合量と塗布液の塗布量とを調整することで、基板１０上に１ｍｍ^２当たり、２個以上１００個以下の突起物を得ることができる。また、バインダー樹脂表面から粒子頂部までの突起物高さは、触診粗さ計や表面形状測定装置などにより容易に測定することができる。
【００３８】
上記の粒子３０とバインダー樹脂を含む混合液を基板１０に塗布する方法としては、広い粘度範囲にわたって塗布が可能であり、塗工中にも塗膜厚さを調整でき、また塗膜厚さを大幅に変えることが出来るなどの特徴をもつ、ロールコータ法、リバースロールコータ法があり、比較的運転技術を要さず、幅広でも塗工厚さが均一で、薄膜コーティング出来るなどの特徴をもつクラビアコータ法、高速塗工、高生産性や、塗工厚さの均一性、広範囲に塗装が出来るなどの特徴をもつダイコート（押出）法、などが挙げられるが、いずれの方法においても上記の突起物密度および突起物高さを実現できる。
【００３９】
他に好ましい突起物の作成方法として、基板１０である高分子フィルム中に粒子を添加する方法を用いてもよい。
粒子を添加する方法で使用される粒子としては、上述した塗工法に記載の粒子と同様の材料を用いることが出来る。
これらの粒子を溶融状態の樹脂と混練してフィルム、シート状に成形したり、半溶融状態のフィルムやシートに上記の粒子を散布し、必要に応じてプレス、冷却処理を行うことで粒子を定着し、突起物層を形成させることが出来る。
【００４０】
本発明の反射体１は、例えば上記の様な方法により作製した突起物上に反射層２０を形成する事によって得られる。また、基板１０上に反射層２０を形成した後、突起物を形成することも出来る、反射層上に更に突起物を形成することも可能である。
【００４１】
反射層２０は、基板１０側から順に、（ａ）下地層、（ｂ）銀を主体とする金属層、（ｃ）保護層を積層したものであることが好ましい。
【００４２】
（ａ）下地層の好ましい例としては、銀とは異なる金属層や金属酸化物層を挙げることが出来る。具体的には、金、銅、ニッケル、鉄、コバルト、タングステン、モリブデン、タンタル、クロム、インジウム、マンガン、チタン、パラジウム、ジルコニウム、ビスマス、スズ、亜鉛、アンチモン、セリウム、ネオジウム、ランタン、トリウム、マグネシウム、ガリウムなどの金属単体、もしくは２種以上からなる合金、インジウム、チタン、ジルコニウム、ビスマス、スズ、亜鉛、アンチモン、タンタル、セリウム、ネオジウム、ランタン、トリウム、マグネシウム、ガリウム等の酸化物、これら酸化物の混合物や硫化亜鉛等の金属化合物が例示できる。これらの中でも金、銅、ニッケル、鉄、コバルト、タングステン、モリブデン、タンタル、クロム、インジウム、マンガン、チタン、パラジウム単体、またはこれらの２種類以上からなる合金、酸化亜鉛、酸化インジウム、酸化スズ、酸化珪素が好ましく、特に好ましくは酸化アルミニウムが５重量％以下でドープされた酸化亜鉛、ガリウムが１０重量％以下でドープされた酸化亜鉛、インジウムとスズとの酸化物（ＩＴＯ）または二酸化珪素などの透明性および透光性を有する酸化物を挙げることが出来る。またこれらの２種類以上を組み合わせたり、多層化して用いることも出来る。
【００４３】
（ｂ）銀を主体とする金属層には、銀単体或いは、不純物として金、銅、ニッケル、鉄、コバルト、タングステン、モリブデン、タンタル、クロム、インジウム、マンガン、チタン、パラジウムなどを少量含有しているものや銀を主体とした合金が好ましく用いられる。これらの不純物の含有量は、金属の種類によって異なるが、０．００２〜８重量％であり、好ましくは０．００４〜５重量％、特に好ましくは０．００５〜４重量％である。
【００４４】
（ｃ）保護層には上記（ａ）下地層と同様の金属や酸化物の他、これらと銀を主体とした合金から選ばれる２種類以上を組み合わせたり、多層化して用いることが出来る。
【００４５】
これらの中でも金属酸化物、好ましくは、インジウム、チタン、ジルコニウム、ビスマス、スズ、亜鉛、アンチモン、タンタル、セリウム、ネオジウム、ランタン、トリウム、マグネシウム、ガリウム等の酸化物、これら酸化物の混合物、特に好ましくは酸化アルミニウムが５重量％以下でドープされた酸化亜鉛、ガリウムが１０重量％以下でドープされた酸化亜鉛、インジウムとスズとの酸化物（ＩＴＯ）、二酸化珪素などの透明酸化物が用いられる。
【００４６】
上記の下地層、銀を主体とする金属層および保護層である金属薄膜層の形成法としては、湿式法及び乾式法がある。湿式法とはメッキ法の総称であり、溶液から金属を析出させて膜を形成する方法である。具体例をあげるとすれば、銀鏡反応などがある。一方、乾式法とは、真空成膜法の総称であり、具体的に例示するとすれば、抵抗加熱式真空蒸着法、電子ビーム加熱式真空蒸着法、イオンプレーティング法、イオンビームアシスト真空蒸着法、スパッタ法などがある。とりわけ、本発明には連続的に成膜するロール・ツー・ロール方式が可能な真空成膜法が好ましく用いられる。
【００４７】
真空蒸着法では、金属の原材料を電子ビーム、抵抗加熱、誘導加熱などで溶融させ、蒸気圧を上昇させ、好ましくは１３．３ｍＰａ（０．１ｍＴｏｒｒ）以下で基材表面に蒸発させる。この際に、アルゴンなどのガスを１３．３ｍＰａ以上で導入し、高周波もしくは直流のグロー放電を起こしても良い。
【００４８】
スパッタ法には、ＤＣマグネトロンスパッタ法、ＲＦマグネトロンスパッタ法、イオンビームスパッタ法、ＥＣＲスパッタ法、コンベンショナルＲＦスパッタ法、コンベンショナルＤＣスパッタ法などを用いる。
スパッタ法においては、原材料として金属の板状のターゲットを用いればよく、スパッタガスにはヘリウム、ネオン、アルゴン、クリプトン、キセノンなどを使用するが、好ましくはアルゴンを用いる。ガスの純度は９９％以上が好ましいが、より好ましくは９９．５％以上である。また、透明酸化膜の形成には、真空成膜法が好ましく用いられる。主に、スパッタ法が使用され、スパッタガスには、ヘリウム、ネオン、アルゴン、クリプトン、キセノンなどを使用し、条件によっては酸素ガスを用いて行うこともある。
【００４９】
上記の（ａ）下地層、（ｂ）銀を主体とする層、（ｃ）保護層は（ａ）（ｂ）（ｃ）の順に積層されるが３層に限定されるものではなく（ａ）（ｂ）（ｃ）（ｂ）（ｃ）（ａ）（ｂ）（ｃ）（ｂ）（ａ）（ｂ）（ｃ）の様な最外層が保護層であれば多層構造であっても良いが、層数が増えると生産効率が低下する傾向にあるので、好ましくは３〜２０層より好ましくは３〜１５層である。
【００５０】
突起物上や基板上などに成形する薄膜の厚さは、反射体１を構成した際に光線透過率が１％未満になるように考慮して決められる。
【００５１】
本発明の反射層における各層の厚みは、以下のようにすることが好ましい。
【００５２】
（ａ）下地層の厚みは、金属層を用いた場合、５ｎｍ以上５０ｎｍ以下が好ましく、より好ましくは５ｎｍ以上３０ｎｍ以下である。該層の厚みが５ｎｍより薄い場合は、所望のバリヤー効果が得られず、（ｂ）銀を主体とする金属層に凝集を発生させる場合がある。また、５０ｎｍより厚くしてもその効果に変化が無い。また、透明酸化物を用いた場合、透明酸化物層の厚みは、１ｎｍ以上２０ｎｍ以下が好ましく、さらに好ましくは、２ｎｍ以上１０ｎｍ以下である。透明酸化物層の厚みが１ｎｍより薄い場合は、所望のバリヤー効果が得られず、（ｂ）銀を主体とする金属層に凝集を発生させる。また、１０ｎｍより厚くしてもその効果に変化が無い。
【００５３】
（ｂ）銀を主体とする金属層の厚みは、７０ｎｍ以上４００ｎｍ以下が好ましく、より好ましくは１００ｎｍ以上３００ｎｍ以下、さらに好ましくは１２０ｎｍ以上２５０ｎｍ以下である。銀を主体とする層の厚みが７０ｎｍより薄い場合は、十分な金属層の形成が出来ていないため、所望の反射率を得ることが出来ない場合がある。また、４００ｎｍより厚くしてもその効果に変化はない。
【００５４】
（ｃ）保護層の厚みは、金属層を用いた場合、５ｎｍ以上５０ｎｍ以下が好ましく、より好ましくは５ｎｍ以上３０ｎｍ以下である。該層の厚みが５ｎｍより薄い場合は、所望のバリヤー効果が得られず、（ｂ）銀を主体とする金属層に凝集を発生させる場合がある。また、５０ｎｍより厚くしてもその効果に変化が無い。また、透明酸化物を用いた場合、該層の厚みは、１ｎｍ以上２０ｎｍ以下が好ましく、さらに好ましくは、２ｎｍ以上１０ｎｍ以下である。透明酸化物層の厚みが１ｎｍより薄い場合は、所望のバリヤー効果が得られず、（ｂ）銀を主体とする金属層に凝集を発生させる。また、１０ｎｍより厚くしてもその効果に変化が無い。
【００５５】
前記各層の膜厚の測定方法としては、触針粗さ計、繰り返し反射干渉計、マイクロバランス、水晶振動子法などの方法があり、特に水晶振動子法では成膜中に膜厚が測定可能であるため所望の膜厚を得るのに適している。また、前もって成膜の条件を定めておき、試料基材上に成膜を行い、成膜時間と膜厚の関係を調べた上で、成膜時間により膜厚を制御する方法もある。
【００５６】
本発明の反射体は、引っ張り弾性率が高い基板を用いているので、後述するサイドライト型バックライト装置に用いた場合でも凹凸層樹脂のひずみに対する影響も受けにくいことが、経時的に輝度ムラの増大を押さえていると考えられる。
【００５７】
本発明のサイドライト型バックライト装置３では、上記のように作製した反射体１を導光板２の下面に配置し、金属薄膜層側もしくは基板１０側を上面として設置することを特徴とする。バックライト装置としては、サイドライト型として一般的に用いられているものであればよい。
【００５８】
使用する光源５０としては、例えば、白熱電球、発光ダイオード（ＬＥＤ）、エレクトロルミネセンス（ＥＬ）、蛍光ランプ、メタルハイドライドランプなどが挙げられ、中でも蛍光ランプが好ましく用いられる。蛍光ランプにはその電極構造、点灯方式により熱陰極型と、冷陰極型に大別され、電極、インバーターとも熱陰極型の方が大きくなる傾向にある。熱陰極型は、発光に寄与しない電極近傍の電飾損失が小さく効率がよく、冷陰極型に比べ数倍優れた発光効率を示し、発光も強いが、寿命は冷陰極型の方が優れており、低消費電力性、耐久性などの点から冷陰極型がより好ましく用いられる。
【００５９】
通常、サイドライト型バックライト装置には、集光のためランプ面と垂直方向にプリズム形状が形成されたプリズムシートとランプ面と平行方向にプリズム形状が形成されたプリズムシート各１枚が使用される。
【００６０】
本発明のサイドライト型バックライト装置３には、導光板にプリズム形状が形成されているので、プリズムシート７０は１枚で良い場合が多く、この際には導光板のプリズムとは垂直方向にプリズム形状が形成されたプリズムシート７０が用いられることが好ましい。プリズムシート７０は通常導光板の上側に配置される。
【００６１】
本発明のバックライト装置３には、拡散シート８０が配置される事が好ましい。上記拡散シートには、導光板やプリズムシートの形状が表示画面に像として現れることや、僅かに残る可能性のある輝度ムラ等の発生を防ぐ等の効果がある。このため、上記拡散シート８０は導光板２、プリズムシート７０の上側に配置される事が好ましい。
【００６２】
本発明のサイドライト型バックライト装置３では、驚くべきことに導光板２と反射層２０との間に特定の間隔をおいて反射体１を設置することで輝度ムラを抑制することが出来る。この間隔は、具体的には導光板２から見た反射層２０の凹部と導光板２との間隔である。通常、導光板２と本発明の反射体１とは直接接しているので、この間隔はＡ面を導光板２側に配置した場合、突起物の高さで制御でき、Ｂ面を導光板側に配置した場合、基板１０の厚みと突起物の高さで制御することが出来る。またスペーサーなどをこれらの間に挿入してこの間隔を調整することも出来る。この間隔は、５μｍ以上、好ましくは１０μｍ以上、より好ましくは１０〜１００μｍ、特に好ましくは１０〜９０μｍ、更に好ましくは１５〜８５μｍである。
これらの配置の内、Ａ面を導光板２側に配置する方法がより好ましい。
【００６３】
本発明の反射体１および反射体基板１０は基板側の面（Ｂ面）に易滑処理がなされていても良い。易滑処理を施すことで、液晶表示装置を組み付ける際の作業性が向上する。
易滑処理の方法について特に制限はないが、具体的には微粒子を含む塗工液を塗布する方法、エンボス加工に寄り凹凸を形成する方法。シリカなどの粒子を基板１０表面に高圧空気と共に吹き付けるサンドブラスト法、エッチング等の化学的方法などを用いることできる。この中でも塗工液を塗布する方法が好ましく用いられる。
本発明のサイドライト型バックライト装置では、上述したような方法で作成された反射体１を使用することで、反射面に歪みが生じた場合でも、輝度ムラが発生し難く、また、従来の装置に比べ格段の輝度向上を実現することができる。
【００６４】
【実施例】
実施例１
突起物となる粒子として平均粒子径が３０μｍであるアクリル粒子を６部、バインダー樹脂としてポリエステル樹脂（Ｔｇ：２０℃、分子量：５００００）１００部、硬化剤として脂肪族イソシアネートを２０部、バインダー樹脂に対し粒子の配合量を６．０ｗｔ％とし、固形分比が２４ｗｔ％になるようにトルエンとエチルメチルケトンからなる溶剤を用いて溶液を調合した後、厚さ１８８μｍのＰＥＴフィルム（引っ張り弾性率：４５００ＭＰａ）上に塗布を行いＡ面側の突起物を得た。次に、平均粒子径が１．５μｍのアクリル粒子、バインダー樹脂としてアクリル／メラミン樹脂を用い、バインダー樹脂に対し、粒子の配合量を、２．０ｗｔ％とし、固形分比が１５ｗｔ％になるようにトルエンとエチルメチルケトンからなる溶剤を用いて溶液を調合した後、ＰＥＴフィルムのＢ面側に塗布を行い、易滑面を得た。
次にＡ面側に、ＤＣマグネトロンスパッタ法で、２％のＡｌ_２Ｏ_３がドープされた酸化亜鉛（純度９９．９％）をターゲットとし、純度９９．５％のアルゴンをスパッタガスとして、酸化亜鉛を膜厚５ｎｍになるように下地層を形成した。続いて、このフィルムをスパッタ装置から取り出すことなく、同様にＤＣマグネトロンスパッタ法で、純度９９．９％の銀をターゲットととし、純度９９．５％のアルゴンをスパッタガスとして銀を膜厚２００ｎｍになるように成形した。続いて、このフィルムをスパッタ装置から取り出すことなく、ＤＣマグネトロンスパッタ法で、２％のＡｌ_２Ｏ_３がドープされた酸化亜鉛（純度９９．９％）をターゲットとし、純度９９．５％のアルゴンをスパッタガスとして、酸化亜鉛を膜厚５ｎｍになるように保護層を形成し、図１に示すような所望の反射体１を得た。この反射体１を日立自記分光光度計（型式Ｕ―３４００）に１５０φの積分球を設置し、波長５５０ｎｍにおける各反射率を金属層側から測定したところ、全反射率、拡散反射率はそれぞれ９６．４％、５．０％であり、拡散率は５．２％であった。次にＡ面側の突起物の高さを表面形状測定装置（ＤＥＫＴＡＫ３：Ｖｅｅｃｏ社製）で１０点測定したところ、その平均値は、２５．８μｍ、光学顕微鏡で最大幅を１０点測定したところ、その平均値は３１．２μｍであった。また、１ｍｍ^２当たり最大幅２０〜４０μｍ、高さ１５〜３５μｍの粒子数は２５個存在した。測定後の反射体１を、恒温恒湿槽に入れ、６０℃、９０％ＲＨの湿熱条件で５００時間放置した。５００時間経過後、反射体１を取り出して表面を観察したところ、金属の凝集は見られなかった。また、再度分光光度計により、全反射率、拡散反射率を測定した結果、反射率が９６．０％、拡散反射率が５．４％と湿熱前とほとんどかわらなかった。また、この反射体１を導光板２の下面に金属層側が上になるようにセットし、導光板２の上にはランプ側の面と平行にプリズム形状が形成されたプリズムシート、拡散シートを配置し、図４のようなサイドライト型バックライト装置３を得た。導光板はランプリフレクター側が厚さ３ｍｍ、反対側が厚さ１ｍｍとなる形状であり、反射体側に俵型の突起が形成されている。この突起の平均長さは１００μｍ、平均アスペクト比が３．５、平均ピッチは１００μｍであり、該突起はランプ側の面と平行の向きに整列している。また出光面側は山型プリズム形状で、ランプ側の面と垂直の方向に整列している。平均ピッチは１００μｍである。この状態で、光源５０を点灯し、面中央での正面方向に得られる輝度を測定するとともに、セットした反射体１に故意に歪みを与えた場合および６０℃９０％の湿熱層に５００時間放置した後の面光源の輝度ムラについて観察した結果を表１に示す。
【００６５】
実施例２
突起物となる粒子として平均粒子径３５μｍのアクリル粒子を用いた以外は実施例１と同様にして反射体を得、評価を行った。結果を表１に示した。
【００６６】
実施例３
厚さ１８８μｍのＰＥＴフィルム（引っ張り弾性率：４５００ＭＰａ）上のＡ面側に、ＤＣマグネトロンスパッタ法で、２％のＡｌ_２Ｏ_３がドープされた酸化亜鉛（純度９９．９％）をターゲットとし、純度９９．５％のアルゴンをスパッタガスとして、上記酸化亜鉛を膜厚５ｎｍになるように下地層を形成した。続いて、このフィルムをスパッタ装置から取り出すことなく、同様にＤＣマグネトロンスパッタ法で、純度９９．９％の銀をターゲットととし、純度９９．５％のアルゴンをスパッタガスとして銀を膜厚１５０ｎｍになるように成形した。続いて、このフィルムをスパッタ装置から取り出すことなく、ＤＣマグネトロンスパッタ法で、２％のＡｌ_２Ｏ_３がドープされた酸化亜鉛（純度９９．９％）をターゲットとし、純度９９．５％のアルゴンをスパッタガスとして、酸化亜鉛を膜厚５ｎｍになるように保護層を形成し反射層２０とした。
【００６７】
続いてこのスパッタ面上に実施例１と同様の方法でアクリル粒子とバインダー樹脂を含む塗工液を用いて塗工し、突起を得た。突起物を顕微鏡で観察したところ、１ｍｍ^２当たり２０個の粒子が確認された。
【００６８】
次に、実施例１と同様にして、ＰＥＴフィルム上のＢ面側に塗布を行い反射体を得た。結果を表１に示した。
【表１】

比較例１
反射入光面側、出光面側のいずれもが平滑な導光板を用い、ランプと平行方向にプリズム形状が形成されたプリズムシートとランプと垂直方向にプリズム形状が形成されたプリズムシートを各１枚用いた以外は実施例１と同様にしてバックライトの作製および評価を行った。結果を表１に示した。
【図面の簡単な説明】
【図１】は、本発明における反射体１の一例を示す断面図である。
【図２】は、本発明における導光板２の一例を示す断面図である。
【図３】は、本発明における導光板２の一例を示す平面図である。
【図４】は、本発明のサイドライト型バックライト装置３の一例を示す斜視図である。
（符号の説明）
１：反射体
２：導光板
３：バックライト
１０：基板
２０：反射層
３０：粒子
４０：易滑層
５０：光源
６０：ランプリフレクター
７０：プリズムシート
８０：拡散シート[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a sidelight-type backlight device and a liquid crystal display device applied to a liquid crystal display device having high luminance and less luminance unevenness.
[0002]
[Prior art]
Liquid crystal displays are small and small-sized displays compared to conventional CRT (Cathode Ray Tube) displays because they are thinner and can save space, operate at low voltage, consume less power and can save energy. It is widely used, mainly.
[0003]
A liquid crystal display widely used at present is a transmission type liquid crystal display using a backlight as a light source. The visibility of the display on this liquid crystal display depends not only on the performance of the liquid crystal itself but also on the performance of the backlight. As for the backlight system, it is necessary to further reduce the weight and thickness of the liquid crystal display in recent years, and it is difficult to transfer the heat from the light source to the liquid crystal panel because of the uniformity of the brightness and the difficulty in transmitting heat from the light source to the liquid crystal panel. Instead of a direct light type with a reflecting plate, a side light type backlight, which uses a light guide plate and multiple-reflects light from a light source disposed at one end thereof to form a surface light source, is often used.
[0004]
In many cases, a diffuse reflection member made of a white PET (polyethylene terephthalate) film or the like is provided below the light guide plate. By diffusing light with the diffuse reflection member, uniform brightness can be obtained. However, since the irregular reflection member has almost no specular reflection component, there is a problem that although it is uniform as a whole, sufficient luminance cannot be obtained. In addition, when a sheet in which aluminum is deposited on a transparent or translucent PET film is used, luminance is improved as compared with white PET, but since there is no diffuse reflection component, slight distortion of the sheet causes large luminance unevenness. The effect is so that a beautiful image cannot be obtained. In order to solve this problem, a sheet in which a metal is deposited on a film having a roughened surface has been developed. However, when aluminum is used as the metal to be used, the durability is excellent but the brightness is not improved much. Further, when silver having the highest reflectance in the visible light region is used, sufficient luminance can be obtained, but silver has poor durability, so that silver deteriorates quickly, and there is a problem that luminance decreases with time. . In addition, backlights using these reflection sheets have a problem that luminance unevenness increases with time.
[0005]
[Problems to be solved by the invention]
An object of the present invention is to provide a sidelight-type backlight device and a liquid crystal display device which are high in luminance and excellent in durability and free from luminance unevenness.
[0006]
[Means for Solving the Problems]
The present inventors have conducted intensive studies to solve the above problems, and as a result, by using a light guide plate having a specific shape and disposing a reflector having an appropriate diffuse reflectance under the light guide plate, luminance unevenness is reduced. It has been found that it can be eliminated or significantly reduced, and high luminance and durability can be simultaneously realized.
[0007]
The present invention is, in part, a sidelight type backlight device in which a reflector is provided below a light guide plate, wherein the light exit surface side of the light guide plate has a prism shape, and the reflector has a total reflection of 550 nm light. A ratio of the diffuse reflectance to the reflectance (diffusivity) is from 1% to 50%.
For one, the reflector comprises a substrate and a reflective layer, and a protrusion having a maximum width of 0.1 μm to 50 μm and a height of 0.1 μm to 45 μm is formed on the reflective layer side by 1 mm. ² It is a sidelight type backlight device characterized by having 2 or more and 100 or less per unit,
One is a sidelight type backlight device characterized in that the total reflectance of the reflector at a wavelength of 550 nm is 90% or more and the diffuse reflectance is 10% or less,
One is a sidelight type backlight device, characterized in that the light guide plate has an uneven shape on a surface opposite to a surface having a prism shape,
One is a sidelight type backlight device, wherein the uneven shape of the surface of the light guide plate opposite to the prism-shaped surface is a bale shape.
[0008]
According to the present invention, a backlight using a light guide plate having a specific shape and a reflector having an appropriate diffusion rate eliminates or significantly reduces luminance unevenness, and simultaneously achieves high luminance, durability, and a wide viewing angle. It is possible to realize.
[0009]
One is a liquid crystal display device comprising the sidelight type backlight device.
[0010]
According to the present invention, it is possible to provide a liquid crystal display having high luminance, high durability, significantly reduced luminance unevenness, and excellent visibility with a wide viewing angle. Accordingly, since uniform and high-luminance light can be obtained over a long period of time, the present invention, which can improve the display capability of liquid crystal, has great industrial significance.
[0011]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the drawings.
[0012]
In the present specification, the surface on the side where the reflective layer of the reflector described later is formed may be referred to as surface A, and the opposite surface may be referred to as surface B. The light exit surface of the light guide plate may be referred to as a C surface, and the surface opposite to the light exit surface may be referred to as a reflection light entrance surface or a D surface.
[0013]
FIG. 1 is a sectional view showing an example of a reflector 1 according to one embodiment of the present invention.
The reflector of the present invention comprises the substrate 10 and the reflection layer 20, and forms the projections by applying the particles 30 on the A surface side, and forms the smooth surface 40 on the B surface side.
[0014]
FIG. 2 is a sectional view of the light guide plate 2 according to one embodiment of the present invention. The light exit surface is formed in a prism shape.
[0015]
FIG. 3 is a plan view of a reflected light incident surface of the light guide plate 2 according to one embodiment of the present invention. A bale-shaped concave shape is formed in a regular arrangement.
[0016]
FIG. 4 is a perspective view of the sidelight type backlight device 3 including the reflector 1. In the sidelight type backlight device 3, the reflector 1 is arranged so that the reflection layer 20 is in contact with the reflection light entrance surface of the light guide plate 2, and the downward prism sheet 70 and the diffusion sheet 80 are sequentially installed on the light exit surface side, A light source 50 and a lamp reflector 60 are provided on a side surface. Light from the light source 50 is reflected by the reflector 1 and functions as a surface light source device when attached to the back of the liquid crystal display panel.
[0017]
The light guide plate 2 to be used is, for example, an acrylic resin such as polymethyl methacrylate, a polycarbonate resin such as a polycarbonate or a polycarbonate / polystyrene composition, or a transparent or translucent resin such as an epoxy resin or glass having a thickness of about 400 nm. A material having transparency in a wavelength range of from 700 nm to 700 nm is preferably used, but is not necessarily limited to these materials as long as the material shows transparency according to the wavelength range of the light source.
[0018]
The thickness of the light guide plate 2 can be appropriately determined depending on the size of the light guide plate to be used, the size of the light source, and the like, but is preferably 5 mm or less, more preferably 1 to 4 mm. In addition, the thickness does not need to be uniform, and it may be preferable that the thickness is near the light source 50 and becomes thinner as the distance from the light source 50 increases.
[0019]
The light guide surface of the light guide plate 2 has a prism shape. The prism shape includes a trapezoidal shape and a mountain shape, but is preferably a mountain shape. The prism shape may be continuous or discontinuous, but a continuous shape is preferable in terms of molding, light-collecting efficiency, and the like. Further, it is preferable that the prism shape is formed so as to be aligned perpendicular to the surface on the light source side. The pitch at this time is 10 to 300 μm, preferably 15 to 200 μm, and more preferably 20 to 150 μm.
[0020]
It is preferable that the reflection light incident surface of the light guide plate 2 has dot-shaped irregularities. The concavo-convex shape can be exemplified by a dome shape, a bale shape, a trapezoid, a wedge shape, a box shape, a cylindrical shape, a pyramid shape, a conical shape, and the like. It is a bale type. The unevenness height (depth) is 100 μm or less, preferably 1 to 50 μm, the maximum width is 300 μm or less, preferably 10 to 200 μm, and the aspect ratio is 1 to 10, preferably 1 to 6. The pitch is 1 to 700 µm, preferably 10 to 500 µm, and more preferably 50 µm to 400 µm. The density of the protrusions does not need to be uniform, and it may be preferable that the vicinity of the light source is dense or the periphery is dense. The irregularities may be arranged randomly or regularly arranged, but they must be arranged in a direction perpendicular to the prism shape, and furthermore, be arranged in a direction parallel to the light source side surface. Is preferred.
[0021]
The prism shape and the concavo-convex shape of the light guide plate 2 can be formed by preparing a mold having a desired surface shape in advance and molding by an injection molding method, or by using a relatively inexpensive mold having a relatively inexpensive smooth surface. After it is obtained, a method of forming a predetermined surface shape by thermal deformation, cutting, and printing, a method of bonding a sheet having a predetermined surface shape, and the like can be exemplified.
[0022]
In the present invention, the ratio of the diffuse reflectance at a wavelength of 550 nm of the reflectance measured from at least one of the side A and the side B of the reflector 1 (diffuse reflectance / total reflectance: diffusion rate) is: It is 1 to 50%, preferably 1 to 20%, particularly preferably 1 to 17%, and more preferably 1 to 15%. Further, the total reflectance is usually 85% or more, preferably 90% or more, particularly preferably 90 to 99%, and the diffuse reflectance is 50% or less, preferably 20% or less, more preferably 17% or less, and particularly preferably. Is 1 to 10%. Note that 550 nm is a wavelength at which the light receiving sensitivity of the human eye is highest, and is suitable for evaluating actual visibility.
[0023]
The substrate 10 has a tensile modulus of 2000 MPa or more, preferably 2500 MPa or more, more preferably 3000 MPa or more, and particularly preferably 3500 MPa or more. The tensile modulus is measured mainly according to ASTM D-882 standard.
[0024]
Specifically, a plate-like or sheet-like inorganic material, such as a physically and chemically stable glass plate or a ceramic plate, or an organic material such as a polymer sheet or a polymer film is appropriately used. Among these, a polymer film which has a high degree of freedom in shape and which can be applied to a roll-to-roll process when forming the reflective layer 20, for example, is desirable.
[0025]
In the reflector 1 of the present invention, preferred polymer films to be used include, for example, polyesters such as polyethylene terephthalate (PET) and polyethylene naphthalate, polycarbonates such as bisphenol A-based polycarbonate, cyclic olefin copolymers, polyimides, and the like. Films made of various plastics such as polyamides such as nylon, polyethersulfones, polysulfone resins, polyarylate resins, fluorine resins, polyether-terketones, polyacetals such as poval, but not necessarily limited to these However, any material having a high crystallization temperature or glass transition point and a smooth surface can be used. Among them, polyesters such as polyethylene terephthalate, polycarbonates and polyamides are preferred.
[0026]
The thickness of the polymer film used is usually from 1 to 250 μm, preferably from 5 to 200 μm, particularly preferably from 10 to 200 μm.
[0027]
The reflector 1 of the present invention preferably has a protrusion on the surface of the substrate 10 having the later-described reflective layer 20. The above-mentioned protrusions can be directly formed on the substrate 10, or a separately prepared protrusion layer film or sheet can be bonded to the substrate 10. Further, it can be formed on a reflective layer 20 described later.
[0028]
The maximum width of the protrusion is 0.1 to 50 μm, preferably 1 to 50 μm, more preferably 10 to 50 μm, still more preferably 15 to 45 μm, and particularly preferably 20 to 40 μm. The height of the projection is 0.1 to 45 μm, preferably 1 to 45 μm, more preferably 5 to 45 μm, further preferably 10 to 40 μm, and particularly preferably 15 to 35 μm. The shape of the projection is not particularly limited, and examples thereof include a particle type, a dome type, a mountain type, a pyramid type, a cylindrical type, a prism type, a trapezoidal shape, a prism type, and an irregular shape. The shape may be a single-stage shape or a multi-stage shape, and these shapes may be mixed or may be combined in multiple stages. The protrusion is 1mm ² The number is preferably 2 or more and 100 or less, more preferably 5 or more and 90 or less.
[0029]
There are no particular restrictions on the method of forming these protrusions, but (1) a method of applying solids such as particles, and (2) a method of kneading the solids such as particles with a resin to form a film or sheet. (3) a method of spraying solid matter such as particles onto a semi-molten film or sheet and then cooling and fixing the solid matter; (4) a method of forming projections using a printing technique such as screen printing; A) a method of using a cooling roll having an uneven shape when molding a thermoplastic resin into a sheet or a film, and transferring the uneven shape of the roll as a protrusion; (6) a method of forming using a micro mold (7) A) a method having a polishing and friction process such as a sand blast method; (8) a method using photolithography; and (9) a method using an etching method. Further, the protrusion obtained by the above method can be deformed by heat treatment or the like.
[0030]
Among the methods of forming the above-mentioned protrusions, a method of forming the protrusions by applying the particles 30 is particularly preferable because the adjustment of the surface state is relatively easy. Examples of the particles to be applied include polymer (organic) particles such as acrylic, polystyrene, vinylbenzene, styrene methacrylate, styrene acrylate, and styrene butadiene, silica, alumina, titania, zirconia, lead oxide (lead white), and oxide. Use of inorganic fine particles made of zinc (zinc white), calcium carbonate, barium carbonate, barium sulfate, potassium titanate, sodium silicate, and conductive transparent fine particles of tin oxide, indium oxide, cadmium oxide, antimony oxide, and the like. However, the present invention is not necessarily limited to these. In particular, it is preferable to use an acrylic resin or silica.
[0031]
As the particles 30 applied in the present invention, particles having an average particle diameter of 0.1 to 50 μm, preferably 1 to 50 μm, more preferably 10 to 50 μm, still more preferably 15 to 45 μm, and particularly preferably 20 to 40 μm are used. Is preferred.
[0032]
The particle size distribution of the particles 30 is preferably small, and the ratio of the standard deviation of the particle size to the average particle size is preferably 50% or less. More preferably, it is 40% or less. However, if necessary, two or more kinds of particles can be used. In this case, the proportion of the main component particles is at least 50%, preferably at least 70%, more preferably at least 75%, particularly preferably at least 80%.
[0033]
The average particle size distribution can be determined by measuring a solution in which a small amount of particles are dispersed by a dynamic light scattering method. It can also be determined from 100 particle diameters randomly selected from SEM (Scanning Electron Microscope) photographs of the particles. Further, the particle diameter can be read by using an optical microscope in addition to the SEM photograph. The particle size distribution can also be determined by subjecting the obtained photograph or image to image processing.
[0034]
The particles 30 are usually applied in a state of being dispersed in a resin used as a binder. As the binder resin, for example, an acrylic resin such as polymethyl methacrylate, a polyacrylonitrile resin, a polymethacrylonitrile resin, a silicon resin such as a polymer obtained from ethyl silicate, a fluorine resin, a polyester resin, a polystyrene resin, and an acetate resin Resins, polyether sulfone resins, polycarbonate resins, polyamide resins, polyimide resins, polyolefin resins, polyurethane resins, urea resins, melamine resins, epoxy resins, and mixtures thereof, but not necessarily It is not limited to. These are selected in consideration of the adhesion between the substrate 10 and the particles 30. Among them, polyester resins and acrylic resins are preferred.
[0035]
Usually, a solvent is used to disperse these particles 30 in the binder resin. As the solvent, toluene, methyl ethyl ketone, ethyl acetate, isopropyl alcohol and the like are preferably used. These are solvents generally used in the coating operation, and any other solvent that does not affect the substrate 10 or the particles 30 can be used without any problem. If necessary, additives such as a crosslinking agent such as isocyanates and melamines, a wetting agent, a thickener, a dispersant, and an antifoaming agent may be added.
[0036]
It is preferable that the compounding ratio of the particles 30 to the binder resin is 0.1 wt% to 10 wt% of the particles 30 to the binder resin. If the blending ratio is less than 0.1 wt%, the required diffusion characteristics of reflected light cannot be obtained, which may be undesirable. On the other hand, if the content is more than 10 wt%, the light diffusivity becomes too strong, which may not be preferable.
[0037]
The coating liquid containing the particles 30 is coated on the substrate 10 in a wet state at a coating amount of 10 g / m 2. ² Above, 40 g / m ² It is preferred to apply with. The mixing ratio of the particles is reflected in the particle density on the surface of the reflector 1 and affects the diffusivity of the reflector 1. The amount of coating is reflected in the thickness of the binder layer on the substrate 10 and affects the difference in height between the top of the particles 30 and the reflective layer 20, that is, the distance at the time of contact between the light guide plate 2 and the reflector 1. . 10 g / m coating liquid ² If it is smaller, the amount of the particles 30 contained in the coating liquid will be insufficient, and the required diffusion characteristic of reflected light may not be obtained, which is not preferable. In addition, the amount of the coating solution is 40 g / m ² If the size is larger, the particles 30 are buried in the binder resin, and a required projection height may not be obtained, which is not preferable. In other words, by adjusting the amount of the particles and the amount of the coating solution applied within the above range, 1 mm ² As a result, 2 to 100 protrusions can be obtained. Further, the height of the protrusion from the surface of the binder resin to the top of the particle can be easily measured by a palpation roughness meter or a surface shape measuring device.
[0038]
As a method of applying the mixed liquid containing the particles 30 and the binder resin to the substrate 10, coating can be performed over a wide viscosity range, the coating thickness can be adjusted even during coating, and the coating thickness can be reduced. There are roll coater method and reverse roll coater method, which have the characteristics that they can be changed drastically.It has relatively little operation skills, has a uniform coating thickness even when it is wide, and has the characteristics of being capable of thin film coating. Die coating (extrusion), which has features such as the gravure coater method, high-speed coating, high productivity, uniformity of coating thickness, and the ability to apply over a wide range, and the like. The projection density and the projection height can be realized.
[0039]
As another preferable method of forming the protrusions, a method of adding particles to the polymer film as the substrate 10 may be used.
As the particles used in the method of adding particles, the same materials as the particles described in the above-described coating method can be used.
These particles are kneaded with a resin in a molten state to form a film or a sheet, or the above particles are sprayed on a film or a sheet in a semi-molten state, and if necessary, pressed and cooled to perform the particles. By fixing, a projection layer can be formed.
[0040]
The reflector 1 of the present invention can be obtained, for example, by forming the reflective layer 20 on a projection produced by the above method. Further, after the reflection layer 20 is formed on the substrate 10, a projection can be formed. Further, a projection can be further formed on the reflection layer.
[0041]
The reflective layer 20 is preferably formed by sequentially laminating (a) an underlayer, (b) a metal layer mainly composed of silver, and (c) a protective layer from the substrate 10 side.
[0042]
(A) Preferable examples of the underlayer include a metal layer and a metal oxide layer different from silver. Specifically, gold, copper, nickel, iron, cobalt, tungsten, molybdenum, tantalum, chromium, indium, manganese, titanium, palladium, zirconium, bismuth, tin, zinc, antimony, cerium, neodymium, lanthanum, thorium, magnesium , Gallium and other simple metals, or alloys of two or more, indium, titanium, zirconium, bismuth, tin, zinc, antimony, tantalum, cerium, neodymium, lanthanum, thorium, magnesium, gallium, and other oxides, and these oxides And metal compounds such as zinc sulfide. Among them, gold, copper, nickel, iron, cobalt, tungsten, molybdenum, tantalum, chromium, indium, manganese, titanium, palladium alone, or an alloy composed of two or more thereof, zinc oxide, indium oxide, tin oxide, oxide Silicon is preferred, particularly preferably zinc oxide doped with aluminum oxide at 5% by weight or less, zinc oxide doped with gallium at 10% by weight or less, oxide of indium and tin (ITO) or transparent such as silicon dioxide. Oxide having a light transmitting property. Further, two or more of these may be combined or used in multiple layers.
[0043]
(B) The metal layer mainly composed of silver contains silver alone or a small amount of impurities such as gold, copper, nickel, iron, cobalt, tungsten, molybdenum, tantalum, chromium, indium, manganese, titanium, and palladium. And alloys mainly composed of silver are preferably used. The content of these impurities varies depending on the type of metal, but is 0.002 to 8% by weight, preferably 0.004 to 5% by weight, and particularly preferably 0.005 to 4% by weight.
[0044]
As the protective layer (c), in addition to the same metals and oxides as the base layer (a), two or more selected from alloys mainly composed of these metals and silver can be used in combination or as a multilayer.
[0045]
Among these, metal oxides, preferably indium, titanium, zirconium, bismuth, tin, zinc, antimony, tantalum, cerium, neodymium, lanthanum, thorium, magnesium, oxides such as gallium, and mixtures of these oxides, particularly preferred Examples of the transparent oxide include zinc oxide doped with aluminum oxide at 5% by weight or less, zinc oxide doped with gallium at 10% by weight or less, oxide of indium and tin (ITO), and silicon dioxide.
[0046]
As a method for forming the underlayer, the metal layer mainly composed of silver, and the metal thin film layer serving as a protective layer, there are a wet method and a dry method. The wet method is a general term for the plating method, and is a method of depositing a metal from a solution to form a film. A specific example is a silver mirror reaction. On the other hand, the dry method is a general term for a vacuum film forming method, and specific examples thereof include a resistance heating vacuum evaporation method, an electron beam heating vacuum evaporation method, an ion plating method, and an ion beam assisted vacuum evaporation method. And a sputtering method. In particular, a vacuum film forming method capable of a roll-to-roll method for continuously forming a film is preferably used in the present invention.
[0047]
In the vacuum evaporation method, a raw material of a metal is melted by an electron beam, resistance heating, induction heating, or the like, the vapor pressure is increased, and the metal is evaporated on the surface of the base material at preferably 13.3 mPa (0.1 mTorr) or less. At this time, a gas such as argon may be introduced at 13.3 mPa or more to cause high frequency or direct current glow discharge.
[0048]
As the sputtering method, a DC magnetron sputtering method, an RF magnetron sputtering method, an ion beam sputtering method, an ECR sputtering method, a conventional RF sputtering method, a conventional DC sputtering method, or the like is used.
In the sputtering method, a metal plate-shaped target may be used as a raw material, and helium, neon, argon, krypton, xenon, or the like is used as a sputtering gas, but argon is preferably used. The purity of the gas is preferably 99% or more, more preferably 99.5% or more. For forming the transparent oxide film, a vacuum film forming method is preferably used. A sputtering method is mainly used, and helium, neon, argon, krypton, xenon, or the like is used as a sputtering gas, and oxygen gas may be used depending on conditions.
[0049]
The above-mentioned (a) underlayer, (b) layer mainly composed of silver, and (c) protective layer are laminated in the order of (a), (b) and (c), but are not limited to three layers. If the outermost layer such as (b) (c) (b) (c) (a) (b) (c) (b) (a) (b) (c) is a protective layer, it has a multilayer structure. However, since the production efficiency tends to decrease as the number of layers increases, it is preferably 3 to 20 layers, more preferably 3 to 15 layers.
[0050]
The thickness of the thin film formed on the protrusion or the substrate is determined in consideration of the light transmittance of less than 1% when the reflector 1 is formed.
[0051]
The thickness of each layer in the reflection layer of the present invention is preferably as follows.
[0052]
(A) When a metal layer is used, the thickness of the underlayer is preferably 5 nm or more and 50 nm or less, more preferably 5 nm or more and 30 nm or less. If the thickness of the layer is smaller than 5 nm, the desired barrier effect cannot be obtained, and (b) aggregation may occur in the silver-based metal layer. Even if the thickness is more than 50 nm, there is no change in the effect. When a transparent oxide is used, the thickness of the transparent oxide layer is preferably from 1 nm to 20 nm, more preferably from 2 nm to 10 nm. When the thickness of the transparent oxide layer is less than 1 nm, the desired barrier effect cannot be obtained, and (b) aggregation occurs in the silver-based metal layer. Even if the thickness is more than 10 nm, there is no change in the effect.
[0053]
(B) The thickness of the silver-based metal layer is preferably from 70 nm to 400 nm, more preferably from 100 nm to 300 nm, even more preferably from 120 nm to 250 nm. If the thickness of the layer mainly composed of silver is smaller than 70 nm, a desired reflectance may not be obtained in some cases because a sufficient metal layer is not formed. Even if the thickness is more than 400 nm, the effect is not changed.
[0054]
(C) When a metal layer is used, the thickness of the protective layer is preferably from 5 nm to 50 nm, more preferably from 5 nm to 30 nm. If the thickness of the layer is smaller than 5 nm, the desired barrier effect cannot be obtained, and (b) aggregation may occur in the silver-based metal layer. Even if the thickness is more than 50 nm, there is no change in the effect. In the case where a transparent oxide is used, the thickness of the layer is preferably from 1 nm to 20 nm, more preferably from 2 nm to 10 nm. When the thickness of the transparent oxide layer is less than 1 nm, the desired barrier effect cannot be obtained, and (b) aggregation occurs in the silver-based metal layer. Even if the thickness is more than 10 nm, there is no change in the effect.
[0055]
As a method of measuring the film thickness of each layer, there are methods such as a stylus roughness meter, a repetitive reflection interferometer, a microbalance, and a crystal oscillator method. In particular, the film thickness can be measured during film formation in the crystal oscillator method. Therefore, it is suitable for obtaining a desired film thickness. There is also a method in which the conditions for film formation are determined in advance, a film is formed on a sample substrate, the relationship between the film formation time and the film thickness is examined, and the film thickness is controlled by the film formation time.
[0056]
Since the reflector of the present invention uses a substrate having a high tensile modulus, even when used in a sidelight-type backlight device described later, it is hardly affected by the distortion of the resin of the uneven layer. It is considered that the increase in
[0057]
The sidelight type backlight device 3 of the present invention is characterized in that the reflector 1 produced as described above is arranged on the lower surface of the light guide plate 2 and the metal thin film layer side or the substrate 10 side is set as the upper surface. The backlight device may be any device that is generally used as a sidelight type.
[0058]
The light source 50 to be used includes, for example, an incandescent light bulb, a light emitting diode (LED), an electroluminescence (EL), a fluorescent lamp, a metal hydride lamp, and the like, and among them, a fluorescent lamp is preferably used. Fluorescent lamps are roughly classified into a hot cathode type and a cold cathode type depending on their electrode structure and lighting method, and the hot cathode type tends to be larger for both electrodes and inverters. The hot-cathode type has a small illumination loss near the electrode that does not contribute to light emission, has good efficiency, exhibits luminous efficiency several times better than the cold-cathode type, emits light more strongly, but has a longer life than the cold-cathode type. Therefore, the cold cathode type is more preferably used from the viewpoint of low power consumption and durability.
[0059]
Normally, a sidelight type backlight device uses a prism sheet having a prism shape perpendicular to the lamp surface and a prism sheet having a prism shape parallel to the lamp surface to collect light. You.
[0060]
In the sidelight type backlight device 3 of the present invention, since the prism shape is formed on the light guide plate, only one prism sheet 70 may be sufficient in many cases. In this case, the prism is perpendicular to the prism of the light guide plate. It is preferable to use a prism sheet 70 having a prism shape. The prism sheet 70 is usually arranged above the light guide plate.
[0061]
It is preferable that the diffusion sheet 80 be disposed in the backlight device 3 of the present invention. The diffusion sheet has effects such as preventing the shape of the light guide plate and the prism sheet from appearing as an image on the display screen and preventing the occurrence of luminance unevenness that may possibly remain slightly. For this reason, it is preferable that the diffusion sheet 80 is disposed above the light guide plate 2 and the prism sheet 70.
[0062]
Surprisingly, in the sidelight type backlight device 3 of the present invention, luminance unevenness can be suppressed by disposing the reflector 1 at a specific distance between the light guide plate 2 and the reflective layer 20. This interval is specifically the interval between the concave portion of the reflection layer 20 and the light guide plate 2 as viewed from the light guide plate 2. Normally, since the light guide plate 2 and the reflector 1 of the present invention are in direct contact with each other, when the surface A is disposed on the light guide plate 2 side, this distance can be controlled by the height of the protrusion, and the surface B is connected to the light guide plate side. In this case, it can be controlled by the thickness of the substrate 10 and the height of the protrusion. In addition, a spacer or the like can be inserted between them to adjust the distance. This interval is 5 μm or more, preferably 10 μm or more, more preferably 10 to 100 μm, particularly preferably 10 to 90 μm, and still more preferably 15 to 85 μm.
Of these arrangements, a method of arranging the A surface on the light guide plate 2 side is more preferable.
[0063]
In the reflector 1 and the reflector substrate 10 of the present invention, a surface (B surface) on the substrate side may be subjected to a slippery treatment. By performing the slippery process, workability when assembling the liquid crystal display device is improved.
There is no particular limitation on the method of the lubricating treatment, and specifically, a method of applying a coating liquid containing fine particles, and a method of forming irregularities by embossing. A chemical method such as a sand blast method in which particles such as silica are blown onto the surface of the substrate 10 together with high-pressure air, an etching method, or the like can be used. Among them, a method of applying a coating liquid is preferably used.
In the sidelight type backlight device of the present invention, by using the reflector 1 formed by the above-described method, even when the reflection surface is distorted, luminance unevenness hardly occurs. A remarkable improvement in luminance can be realized as compared with the device.
[0064]
【Example】
Example 1
6 parts of acrylic particles having an average particle diameter of 30 μm as particles to become protrusions, 100 parts of polyester resin (Tg: 20 ° C., molecular weight: 50,000) as binder resin, 20 parts of aliphatic isocyanate as curing agent, and binder resin On the other hand, the solution was prepared using a solvent composed of toluene and ethyl methyl ketone so that the blending amount of the particles was 6.0 wt% and the solid content ratio was 24 wt%, and then a PET film having a thickness of 188 μm (tensile elastic modulus: 4500 MPa) to obtain a projection on the A side. Next, acrylic particles having an average particle size of 1.5 μm, an acryl / melamine resin is used as a binder resin, and the compounding amount of the particles is set to 2.0 wt% with respect to the binder resin so that the solid content ratio becomes 15 wt%. Was prepared using a solvent consisting of toluene and ethyl methyl ketone, and then applied to the B side of the PET film to obtain a smooth surface.
Next, on the A side, 2% of Al was deposited by DC magnetron sputtering. ₂ O ₃ The underlayer was formed using zinc oxide (purity: 99.9%) as a target, argon having a purity of 99.5% as a sputtering gas, and zinc oxide having a thickness of 5 nm. Subsequently, without removing this film from the sputtering apparatus, similarly, by DC magnetron sputtering, silver having a purity of 99.9% was used as a target, silver having a purity of 99.5% was used as a sputtering gas, and silver was formed to a film thickness of 200 nm. It was molded so as to become. Subsequently, without removing this film from the sputtering apparatus, 2% Al was obtained by DC magnetron sputtering. ₂ O ₃ A protective layer was formed using zinc oxide (purity: 99.9%) as a target, argon having a purity of 99.5% as a sputtering gas, and zinc oxide having a thickness of 5 nm, as shown in FIG. A desired reflector 1 was obtained. When this reflector 1 was installed on a Hitachi self-recording spectrophotometer (model U-3400) with an integrating sphere of 150φ, and each reflectance at a wavelength of 550 nm was measured from the metal layer side, the total reflectance and the diffuse reflectance were 96 respectively. 0.4% and 5.0%, and the diffusivity was 5.2%. Next, the height of the protrusion on the side A was measured at 10 points by a surface shape measuring device (DEKTAK3: manufactured by Veeco). The average value was 25.8 μm, and the maximum width was measured at 10 points by an optical microscope. The average value was 31.2 μm. Also, 1mm ² There were 25 particles having a maximum width of 20 to 40 μm and a height of 15 to 35 μm. The reflector 1 after the measurement was placed in a thermo-hygrostat, and left for 500 hours under the condition of 60 ° C. and 90% RH. After 500 hours, the reflector 1 was taken out and the surface was observed. As a result, no metal aggregation was observed. Further, the total reflectance and the diffuse reflectance were measured again by the spectrophotometer. As a result, the reflectance was 96.0%, and the diffuse reflectance was 5.4%, which was almost the same as before the wet heat. Further, the reflector 1 is set on the lower surface of the light guide plate 2 so that the metal layer side faces upward. On the light guide plate 2, a prism sheet or a diffusion sheet having a prism shape formed in parallel with the lamp side surface is provided. Then, a sidelight type backlight device 3 as shown in FIG. 4 was obtained. The light guide plate has a thickness of 3 mm on the lamp reflector side and a thickness of 1 mm on the opposite side, and has a bale-shaped projection formed on the reflector side. The average length of the projections is 100 μm, the average aspect ratio is 3.5, and the average pitch is 100 μm. The projections are aligned in a direction parallel to the surface on the lamp side. The light-emitting surface has a mountain-shaped prism shape and is aligned in a direction perpendicular to the lamp-side surface. The average pitch is 100 μm. In this state, the light source 50 is turned on, the luminance obtained in the front direction at the center of the surface is measured, and when the set reflector 1 is intentionally distorted and left in a wet heat layer at 60 ° C. and 90% for 500 hours. Table 1 shows the results of observation of luminance unevenness of the surface light source after the above.
[0065]
Example 2
A reflector was obtained and evaluated in the same manner as in Example 1 except that acrylic particles having an average particle diameter of 35 μm were used as the particles to be projected. The results are shown in Table 1.
[0066]
Example 3
A 2% Al film was formed on the A surface side of a 188 μm-thick PET film (tensile elastic modulus: 4500 MPa) by DC magnetron sputtering. ₂ O ₃ The underlayer was formed using zinc oxide (purity 99.9%) doped with as a target and argon having a purity of 99.5% as a sputtering gas so that the zinc oxide had a thickness of 5 nm. Subsequently, without removing the film from the sputtering apparatus, similarly, by DC magnetron sputtering, silver having a purity of 99.9% was used as a target, argon having a purity of 99.5% was used as a sputtering gas, and silver was formed to a film thickness of 150 nm. It was molded so as to become. Subsequently, without removing this film from the sputtering apparatus, 2% Al was obtained by DC magnetron sputtering. ₂ O ₃ A protective layer was formed to a thickness of 5 nm using zinc oxide (purity 99.9%) as a target, argon having a purity of 99.5% as a sputtering gas, and a reflective layer 20 was formed.
[0067]
Subsequently, a coating solution containing acrylic particles and a binder resin was applied on the sputtered surface in the same manner as in Example 1 to obtain projections. When the protrusions were observed with a microscope, 1 mm ² Twenty particles per particle were confirmed.
[0068]
Next, in the same manner as in Example 1, coating was performed on the side B of the PET film to obtain a reflector. The results are shown in Table 1.
[Table 1]

Comparative Example 1
Each of the prism sheet having a prism shape formed in a direction parallel to the lamp and a prism sheet having a prism shape formed in a direction perpendicular to the lamp is formed by using a light guide plate having a smooth surface on both the reflection light incidence surface side and the light emission surface side. A backlight was produced and evaluated in the same manner as in Example 1 except that the number of the backlights was used. The results are shown in Table 1.
[Brief description of the drawings]
FIG. 1 is a sectional view showing an example of a reflector 1 according to the present invention.
FIG. 2 is a sectional view showing an example of the light guide plate 2 according to the present invention.
FIG. 3 is a plan view showing an example of the light guide plate 2 according to the present invention.
FIG. 4 is a perspective view showing an example of the sidelight type backlight device 3 of the present invention.
(Explanation of reference numerals)
1: Reflector
2: Light guide plate
3: Backlight
10: Substrate
20: reflective layer
30: Particle
40: Easy sliding layer
50: Light source
60: Lamp reflector
70: Prism sheet
80: Diffusion sheet

Claims (6)

導光板の下に反射体が装備されたサイドライト型バックライト装置であって、導光板の出光面側がプリズム形状を有し、反射体の波長５５０ｎｍの光線における全反射率に対する拡散反射率の割合（拡散率）が１％〜５０％の範囲であることを特徴とするサイドライト型バックライト装置。What is claimed is: 1. A side-light type backlight device having a reflector provided below a light guide plate, wherein a light exit surface side of the light guide plate has a prism shape, and a ratio of a diffuse reflectance to a total reflectance of light having a wavelength of 550 nm of the reflector. (Diffusivity) in the range of 1% to 50%. 前記反射体が基板と反射層とからなり、反射層側に最大幅０．１μｍ〜５０μｍ、高さ０．１μｍ〜４５μｍの突起物を１ｍｍ^２当たり２個以上１００個以下有することを特徴とする請求項１に記載のサイドライト型バックライト装置。The reflector comprises a substrate and a reflective layer, and has, on the reflective layer side, two or more protrusions having a maximum width of 0.1 μm to 50 μm and a height of 0.1 μm to 45 μm per mm ^{2 of not} less than 100. The backlight device according to claim 1. 前記反射体の波長５５０ｎｍにおける全反射率が９０％以上であり、かつ、拡散反射率が１０％以下であることを特徴とする請求項１または２に記載のサイドライト型バックライト装置。3. The sidelight type backlight device according to claim 1, wherein the total reflectance of the reflector at a wavelength of 550 nm is 90% or more, and the diffuse reflectance is 10% or less. 前記導光板がプリズム形状を有する面の反対側の面に凹凸形状を有することを特徴とする請求項１〜３いずれかに記載のサイドライト型バックライト装置。The side light type backlight device according to any one of claims 1 to 3, wherein the light guide plate has an uneven shape on a surface opposite to a surface having a prism shape. 前記導光板のプリズム形状面と反対側の面の凹凸形状が俵型であることを特徴とする請求項４に記載のサイドライト型バックライト装置。5. The sidelight type backlight device according to claim 4, wherein the uneven shape of the surface of the light guide plate opposite to the prism-shaped surface is a bale shape. 請求項１〜５いずれかに記載のサイドライト型バックライト装置を備えることを特徴とする液晶表示装置。A liquid crystal display device comprising the sidelight type backlight device according to claim 1.

Images