JP2003508570A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2003508570A5 JP2003508570A5 JP2001520779A JP2001520779A JP2003508570A5 JP 2003508570 A5 JP2003508570 A5 JP 2003508570A5 JP 2001520779 A JP2001520779 A JP 2001520779A JP 2001520779 A JP2001520779 A JP 2001520779A JP 2003508570 A5 JP2003508570 A5 JP 2003508570A5
- Authority
- JP
- Japan
- Prior art keywords
- film
- component
- copolymer
- astm
- measured
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Description
【特許請求の範囲】
【請求項1】
a)25℃より高い融点及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する主要割合のオレフィン系モノマーと小割合のオレフィン系モノマーとの半結晶性コポリマー成分であって、前記主要割合のオレフィン系モノマーはエチレン又はプロピレンであり、そして前記小割合のオレフィン系モノマーは前記主要割合のオレフィン系モノマーとは異なり、そして挿入重合可能な、線状、分岐した、又は環含有のC2乃至C30オレフィン、及びそれら組み合わせから成る群から選択される、半結晶性コポリマー成分、及び
b)200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレン成分のブレンドを含む冷延伸フィルムであって、
前記コポリマーが前記フィルム中に連続相として存在し、そして前記フィルムが160MPa未満の(ASTM D−1708で測定される)引張弾性率を有する、冷延伸フィルム。
【請求項2】
前記主要割合のオレフィン系モノマーがエチレンであり、そして前記コポリマー中に84モル%以上かつ98モル%以下の量で存在する、請求項1のフィルム。
【請求項3】
前記コポリマーが1.5乃至4.0のMWD及び狭い組成分布を有する、請求項2のフィルム。
【請求項4】
前記主要割合のオレフィン系モノマーがプロピレンであり、そして前記コポリマー中に49モル%以上かつ90モル%以下の量で存在する、請求項1のフィルム。
【請求項5】
前記コポリマーが5乃至40重量%の結晶度を含む、請求項4のフィルム。
【請求項6】
前記小割合のオレフィン系モノマーが、エチレン及びα−オレフィンから選択される1種以上である、請求項1のフィルム。
【請求項7】
前記小割合のα−オレフィンが、エチレン、プロピレン、1−ブテン、1−ヘキセン、4−メチル−1−ペンテン、3−メチル−1−ペンテン、3,5,5−トリメチル−1−ヘキセン、及び1−オクテンから成る群から選択される、請求項6のフィルム。
【請求項8】
ブレンド成分の総重量に基づいて30乃至90重量%の前記コポリマー成分及び70乃至10重量%の前記ポリスチレン成分を含む、請求項1のフィルム。
【請求項9】
染料、顔料、充填剤、ワックス、可塑剤、酸化防止剤、熱安定剤、光安定剤、粘着防止剤、加工助剤、及びそれらの組み合わせから成る群から選択される1種以上の添加剤をさらに含む、請求項1のフィルム。
【請求項10】
前記フィルムが実質的に充填剤を含まず、そしてどちらか一方の成分単独よりも大きい透湿度を有する、請求項1のフィルム。
【請求項11】
a) i)各々が49乃至90モル%のプロピレン及び少なくとも1種のエチレン又はC4乃至C20α−オレフィンを含む1種以上の熱可塑性コポリマーであって、前記熱可塑性コポリマーが、25℃以上の融点、1.5乃至4.0のMWD、5乃至40重量%の結晶度、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、 ii) 各々が84乃至98モル%のエチレン及び少なくとも1種のC3乃至C20α−オレフィンを含む1種以上の熱可塑性コポリマーであって、前記熱可塑性コポリマーが、25℃以上の融点、1.5乃至4.0のMWD、狭い組成分布、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、及び iii) i)とii)のブレンド、から選択される第1のポリマー成分、及びb)200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレン成分のブレンドを含む冷延伸フィルムであって、前記フィルムが、160MPa未満の(ASTM D−1708で測定される)引張弾性率及び少なくとも100g−ミル/m2−日の透湿度を有する、フィルム。
【請求項12】
前記フィルムが実質的に充填剤を含まない、請求項11のフィルム。
【請求項13】
2種の非相溶性ポリマー成分のブレンドから形成されたフィルムを製造する方法であって、前記フィルムは前記ポリマー成分のどちらか一方から形成されたフィルムよりも高いWVTRを有し、前記方法は、a)半結晶性の第1のポリマー成分と第2のポリマー成分とのブレンドから、前記第1のポリマー成分が連続相であるブレンドを製造するのに十分な量と条件において、フィルムを形成する工程、及び
b)前記フィルムを、前記軟質ポリマー成分の結晶度の100%未満の溶融を生じさせるのに十分な温度において、前記第1のポリマーと第2のポリマーの間の界面の少なくとも一部の分離を生じさせるのに十分な延伸された寸法まで、延伸する工程、を含み、
前記第1のポリマー成分が、
i)各々が49乃至90モル%のプロピレン及び挿入重合可能なプロピレン以外の少なくとも1種のC2至C30オレフィン系モノマーを含む1種以上の熱可塑性コポリマーであって、25℃以上の融点、1.5乃至4.0のMWD、5乃至40重量%の結晶度、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、
ii)各々が84乃至98モル%のエチレン及び挿入重合可能な少なくとも1種のC3乃至C30オレフィン系モノマーを含む1種以上の熱可塑性コポリマーであって、25℃以上の融点、1.5乃至4.0のMWD、狭い組成分布、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、及び
iii)i)とii)のブレンド、から選択され、
そして前記第2のポリマー成分が、200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレンポリマーである、方法。
【請求項14】
前記オレフィン系モノマーがエチレン及びα−オレフィンから選択される1種以上である、請求項13の方法。
【請求項15】
a)25℃より高い融点及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、主要割合のオレフィン系モノマーと小割合のオレフィン系モノマーとの半結晶性コポリマー成分であって、前記主要割合のオレフィン系モノマーはプロピレンであり、そして前記小割合のオレフィン系モノマーはエチレン及び挿入重合可能なC4乃至C20α−オレフィン、及びそれらの組み合わせから選択される1種以上である、半結晶性コポリマー成分、及び
b)0.93以上の密度及び200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリエチレンホモポリマー成分又はポリエチレンコポリマー成分、のブレンドを含む冷延伸フィルムであって、
前記半結晶性コポリマーは前記フィルム中に連続相として存在し、そして前記フィルムは160MPa未満の(ASTM D−1708で測定される)引張弾性率を有する、冷延伸フィルム。
【請求項16】
前記半結晶性コポリマーが1.5乃至4.0のMWD及び狭い組成分布を有する、請求項15のフィルム。
【請求項17】
前記主要割合のオレフィン系モノマーは、前記半結晶性コポリマー中に49モル%以上かつ90モル%以下の量で存在する、請求項15のフィルム。
【請求項18】
前記半結晶性コポリマーは、5乃至40重量%の結晶度を含む、請求項15のフィルム。
【請求項19】
前記小割合のオレフィン系モノマーがエチレンである。請求項15のフィルム。
【請求項20】
ブレンド成分の総重量に基づいて30乃至90重量%の前記コポリマー成分及び70乃至10重量%の前記ポリエチレン成分を含む、請求項15のフィルム。
【請求項21】
染料、顔料、充填剤、ワックス、可塑剤、酸化防止剤、熱安定剤、光安定剤、粘着防止剤、加工助剤、及びそれらの組み合わせから成る群から選択される1種以上の添加剤をさらに含む、請求項15のフィルム。
【請求項22】
前記フィルムが実質的に充填剤を含まず、そしてどちらか一方の成分単独からのフィルムよりも大きい透湿度を有する、請求項15のフィルム。
【請求項23】
a)25℃より高い融点及び350MPa未満の(ASTM D−790で測定される)割線モジュラスを有する、主要割合のオレフィン系モノマーと小割合のオレフィン系モノマーとの半結晶性コポリマー成分であって、前記主要割合のオレフィン系モノマーはエチレン又はプロピレンであり、そして前記小割合のオレフィン系モノマーは前記主要割合のオレフィン系モノマーとは異なり、そして挿入重合可能な、線状、分岐した、又は環含有のC2乃至C30オレフィン、及びそれらの組み合わせから成る群から選択される、半結晶性コポリマー成分、及び
b)400MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレン成分、のブレンドを含む冷延伸フィルムであって、
前記コポリマーは前記フィルム中に連続相として存在し、そして前記フィルムが375MPa未満の(ASTM D−1708で測定される)引張弾性率を有する、冷延伸フィルム。
【請求項24】
前記主要割合のオレフィン系モノマーはエチレンであり、そして前記コポリマー中に84モル%以上かつ98モル%以下の量で存在する、請求項23のフィルム。
【請求項25】
前記コポリマーが1.5乃至4.0のMWD及び狭い組成分布を有する、請求項23のフィルム。
【請求項26】
ブレンド成分の総重量に基づいて30乃至90重量%の前記コポリマー成分及び70乃至10重量%の前記ポリスチレン成分を含む、請求項22のフィルム。
【請求項27】
染料、顔料、充填剤、ワックス、可塑剤、酸化防止剤、熱安定剤、光安定剤、粘着防止剤、加工助剤、及びそれらの組み合わせから成る群から選択される添加剤をさらに含む、請求項23のフィルム。
【請求項28】
前記フィルムが実質的に充填剤を含まず、そしてどちらか一方の成分単独からのフィルムよりも大きい透湿度を有する、請求項23のフィルム。
【請求項1】
a)25℃より高い融点及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する主要割合のオレフィン系モノマーと小割合のオレフィン系モノマーとの半結晶性コポリマー成分であって、前記主要割合のオレフィン系モノマーはエチレン又はプロピレンであり、そして前記小割合のオレフィン系モノマーは前記主要割合のオレフィン系モノマーとは異なり、そして挿入重合可能な、線状、分岐した、又は環含有のC2乃至C30オレフィン、及びそれら組み合わせから成る群から選択される、半結晶性コポリマー成分、及び
b)200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレン成分のブレンドを含む冷延伸フィルムであって、
前記コポリマーが前記フィルム中に連続相として存在し、そして前記フィルムが160MPa未満の(ASTM D−1708で測定される)引張弾性率を有する、冷延伸フィルム。
【請求項2】
前記主要割合のオレフィン系モノマーがエチレンであり、そして前記コポリマー中に84モル%以上かつ98モル%以下の量で存在する、請求項1のフィルム。
【請求項3】
前記コポリマーが1.5乃至4.0のMWD及び狭い組成分布を有する、請求項2のフィルム。
【請求項4】
前記主要割合のオレフィン系モノマーがプロピレンであり、そして前記コポリマー中に49モル%以上かつ90モル%以下の量で存在する、請求項1のフィルム。
【請求項5】
前記コポリマーが5乃至40重量%の結晶度を含む、請求項4のフィルム。
【請求項6】
前記小割合のオレフィン系モノマーが、エチレン及びα−オレフィンから選択される1種以上である、請求項1のフィルム。
【請求項7】
前記小割合のα−オレフィンが、エチレン、プロピレン、1−ブテン、1−ヘキセン、4−メチル−1−ペンテン、3−メチル−1−ペンテン、3,5,5−トリメチル−1−ヘキセン、及び1−オクテンから成る群から選択される、請求項6のフィルム。
【請求項8】
ブレンド成分の総重量に基づいて30乃至90重量%の前記コポリマー成分及び70乃至10重量%の前記ポリスチレン成分を含む、請求項1のフィルム。
【請求項9】
染料、顔料、充填剤、ワックス、可塑剤、酸化防止剤、熱安定剤、光安定剤、粘着防止剤、加工助剤、及びそれらの組み合わせから成る群から選択される1種以上の添加剤をさらに含む、請求項1のフィルム。
【請求項10】
前記フィルムが実質的に充填剤を含まず、そしてどちらか一方の成分単独よりも大きい透湿度を有する、請求項1のフィルム。
【請求項11】
a) i)各々が49乃至90モル%のプロピレン及び少なくとも1種のエチレン又はC4乃至C20α−オレフィンを含む1種以上の熱可塑性コポリマーであって、前記熱可塑性コポリマーが、25℃以上の融点、1.5乃至4.0のMWD、5乃至40重量%の結晶度、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、 ii) 各々が84乃至98モル%のエチレン及び少なくとも1種のC3乃至C20α−オレフィンを含む1種以上の熱可塑性コポリマーであって、前記熱可塑性コポリマーが、25℃以上の融点、1.5乃至4.0のMWD、狭い組成分布、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、及び iii) i)とii)のブレンド、から選択される第1のポリマー成分、及びb)200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレン成分のブレンドを含む冷延伸フィルムであって、前記フィルムが、160MPa未満の(ASTM D−1708で測定される)引張弾性率及び少なくとも100g−ミル/m2−日の透湿度を有する、フィルム。
【請求項12】
前記フィルムが実質的に充填剤を含まない、請求項11のフィルム。
【請求項13】
2種の非相溶性ポリマー成分のブレンドから形成されたフィルムを製造する方法であって、前記フィルムは前記ポリマー成分のどちらか一方から形成されたフィルムよりも高いWVTRを有し、前記方法は、a)半結晶性の第1のポリマー成分と第2のポリマー成分とのブレンドから、前記第1のポリマー成分が連続相であるブレンドを製造するのに十分な量と条件において、フィルムを形成する工程、及び
b)前記フィルムを、前記軟質ポリマー成分の結晶度の100%未満の溶融を生じさせるのに十分な温度において、前記第1のポリマーと第2のポリマーの間の界面の少なくとも一部の分離を生じさせるのに十分な延伸された寸法まで、延伸する工程、を含み、
前記第1のポリマー成分が、
i)各々が49乃至90モル%のプロピレン及び挿入重合可能なプロピレン以外の少なくとも1種のC2至C30オレフィン系モノマーを含む1種以上の熱可塑性コポリマーであって、25℃以上の融点、1.5乃至4.0のMWD、5乃至40重量%の結晶度、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、
ii)各々が84乃至98モル%のエチレン及び挿入重合可能な少なくとも1種のC3乃至C30オレフィン系モノマーを含む1種以上の熱可塑性コポリマーであって、25℃以上の融点、1.5乃至4.0のMWD、狭い組成分布、及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、1種以上の熱可塑性コポリマー、及び
iii)i)とii)のブレンド、から選択され、
そして前記第2のポリマー成分が、200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレンポリマーである、方法。
【請求項14】
前記オレフィン系モノマーがエチレン及びα−オレフィンから選択される1種以上である、請求項13の方法。
【請求項15】
a)25℃より高い融点及び100MPa未満の(ASTM D−790で測定される)曲げ弾性率を有する、主要割合のオレフィン系モノマーと小割合のオレフィン系モノマーとの半結晶性コポリマー成分であって、前記主要割合のオレフィン系モノマーはプロピレンであり、そして前記小割合のオレフィン系モノマーはエチレン及び挿入重合可能なC4乃至C20α−オレフィン、及びそれらの組み合わせから選択される1種以上である、半結晶性コポリマー成分、及び
b)0.93以上の密度及び200MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリエチレンホモポリマー成分又はポリエチレンコポリマー成分、のブレンドを含む冷延伸フィルムであって、
前記半結晶性コポリマーは前記フィルム中に連続相として存在し、そして前記フィルムは160MPa未満の(ASTM D−1708で測定される)引張弾性率を有する、冷延伸フィルム。
【請求項16】
前記半結晶性コポリマーが1.5乃至4.0のMWD及び狭い組成分布を有する、請求項15のフィルム。
【請求項17】
前記主要割合のオレフィン系モノマーは、前記半結晶性コポリマー中に49モル%以上かつ90モル%以下の量で存在する、請求項15のフィルム。
【請求項18】
前記半結晶性コポリマーは、5乃至40重量%の結晶度を含む、請求項15のフィルム。
【請求項19】
前記小割合のオレフィン系モノマーがエチレンである。請求項15のフィルム。
【請求項20】
ブレンド成分の総重量に基づいて30乃至90重量%の前記コポリマー成分及び70乃至10重量%の前記ポリエチレン成分を含む、請求項15のフィルム。
【請求項21】
染料、顔料、充填剤、ワックス、可塑剤、酸化防止剤、熱安定剤、光安定剤、粘着防止剤、加工助剤、及びそれらの組み合わせから成る群から選択される1種以上の添加剤をさらに含む、請求項15のフィルム。
【請求項22】
前記フィルムが実質的に充填剤を含まず、そしてどちらか一方の成分単独からのフィルムよりも大きい透湿度を有する、請求項15のフィルム。
【請求項23】
a)25℃より高い融点及び350MPa未満の(ASTM D−790で測定される)割線モジュラスを有する、主要割合のオレフィン系モノマーと小割合のオレフィン系モノマーとの半結晶性コポリマー成分であって、前記主要割合のオレフィン系モノマーはエチレン又はプロピレンであり、そして前記小割合のオレフィン系モノマーは前記主要割合のオレフィン系モノマーとは異なり、そして挿入重合可能な、線状、分岐した、又は環含有のC2乃至C30オレフィン、及びそれらの組み合わせから成る群から選択される、半結晶性コポリマー成分、及び
b)400MPaより大きい(ASTM D−790で測定される)曲げ弾性率を有するポリスチレン成分、のブレンドを含む冷延伸フィルムであって、
前記コポリマーは前記フィルム中に連続相として存在し、そして前記フィルムが375MPa未満の(ASTM D−1708で測定される)引張弾性率を有する、冷延伸フィルム。
【請求項24】
前記主要割合のオレフィン系モノマーはエチレンであり、そして前記コポリマー中に84モル%以上かつ98モル%以下の量で存在する、請求項23のフィルム。
【請求項25】
前記コポリマーが1.5乃至4.0のMWD及び狭い組成分布を有する、請求項23のフィルム。
【請求項26】
ブレンド成分の総重量に基づいて30乃至90重量%の前記コポリマー成分及び70乃至10重量%の前記ポリスチレン成分を含む、請求項22のフィルム。
【請求項27】
染料、顔料、充填剤、ワックス、可塑剤、酸化防止剤、熱安定剤、光安定剤、粘着防止剤、加工助剤、及びそれらの組み合わせから成る群から選択される添加剤をさらに含む、請求項23のフィルム。
【請求項28】
前記フィルムが実質的に充填剤を含まず、そしてどちらか一方の成分単独からのフィルムよりも大きい透湿度を有する、請求項23のフィルム。