JP2003306859A - Layered fiber assembly for forming three-dimensional sheet and method for producing three-dimensional sheet - Google Patents
Layered fiber assembly for forming three-dimensional sheet and method for producing three-dimensional sheetInfo
- Publication number
- JP2003306859A JP2003306859A JP2002107928A JP2002107928A JP2003306859A JP 2003306859 A JP2003306859 A JP 2003306859A JP 2002107928 A JP2002107928 A JP 2002107928A JP 2002107928 A JP2002107928 A JP 2002107928A JP 2003306859 A JP2003306859 A JP 2003306859A
- Authority
- JP
- Japan
- Prior art keywords
- heat
- shrinkable
- fiber
- dimensional sheet
- fiber layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、熱収縮性繊維層と
非熱収縮性繊維層とを積層して部分接合してなり、熱収
縮性繊維層を熱収縮させることによって、非熱収縮性繊
維層側に凹凸が形成された立体シートとなる立体シート
形成用の積層繊維集合体、及び該積層繊維集合体を用い
た立体シートの製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention comprises a heat-shrinkable fiber layer and a non-heat-shrinkable fiber layer which are laminated and partially bonded to each other. The present invention relates to a laminated fiber assembly for forming a three-dimensional sheet, which is a three-dimensional sheet having irregularities formed on the fiber layer side, and a method for producing a three-dimensional sheet using the laminated fiber assembly.
【０００２】[0002]
【従来の技術及び発明が解決しようとする課題】従来、
熱収縮性繊維層と非熱収縮性繊維層とを積層して部分的
に接合し、熱処理により、非熱収縮性繊維層側に凹凸を
形成した立体シートが知られている。特開平９−１１１
６３１公報には、熱収縮性繊維を５０重量％以上含む第
１繊維層の片面もしくは両面に、前記熱収縮性繊維が収
縮する温度において実質的に収縮しない繊維からなる熱
収縮性繊維層が積層されてなる不織布であって、且つ第
１繊維層及び熱収縮性繊維層の少なくとも一方の繊維層
に熱融着性繊維が該不織布中３０重量％以上含まれてお
り、両繊維層は規則的な線状熱融着により厚さ方向に一
体化され、線状熱融着部が凹部、線状熱融着部同士の間
が凸部になっており、該熱収縮性繊維層が表面に連続も
しくは不連続の筋状に規則的な多数の皺を形成している
多皺性不織布が提案されている。しかし、この多皺性不
織布においては、第１繊維層の熱収縮力が十分コントロ
ールされていないことから、多数の皺を形成するのに十
分な熱収縮性を発現させることができないことがあり、
結果として、十分に***した凸部形状を表面に安定して
形成させることが困難であった。また同様の理由で、製
造工程において十分な収縮速度を得られないため、収縮
処理時間が長くなり、製造コストが高いという欠点があ
る。2. Description of the Related Art Conventionally, the problems to be solved by the invention
There is known a three-dimensional sheet in which a heat-shrinkable fiber layer and a non-heat-shrinkable fiber layer are laminated and partially bonded to each other, and unevenness is formed on the non-heat-shrinkable fiber layer side by heat treatment. Japanese Patent Laid-Open No. 9-111
631 discloses a heat-shrinkable fiber layer made of fibers that do not substantially shrink at the temperature at which the heat-shrinkable fiber shrinks is laminated on one or both sides of the first fiber layer containing 50 wt% or more of the heat-shrinkable fiber. And a heat-fusible fiber is contained in at least one of the first fiber layer and the heat-shrinkable fiber layer in an amount of 30% by weight or more in the non-woven fabric. Are integrated in the thickness direction by linear thermal fusion bonding, the linear thermal fusion bonding portion is a concave portion, and the linear thermal fusion bonding portion is a convex portion, and the heat shrinkable fiber layer is formed on the surface. A wrinkled non-woven fabric has been proposed in which a large number of wrinkles that are regular or continuous in a continuous or discontinuous manner are formed. However, in this multi-wrinkle nonwoven fabric, since the heat shrinkage force of the first fiber layer is not sufficiently controlled, it may not be possible to develop sufficient heat shrinkability to form a large number of wrinkles,
As a result, it has been difficult to stably form a sufficiently raised convex shape on the surface. Further, for the same reason, there is a drawback that the shrinking treatment time becomes long and the manufacturing cost is high because a sufficient shrinking speed cannot be obtained in the manufacturing process.
【０００３】従って、本発明の目的は、熱処理により表
面に十分な凸状形状を形成させることができ、しかも前
記熱処理の工程において十分な収縮速度が得られ、熱処
理時間を短縮して立体シートの製造コストを削減するこ
とのできる、立体シート形成用の積層繊維集合体及び該
積層繊維集合体を用いた立体シートの製造方法を提供す
ることにある。また、本発明の目的は、熱処理より熱収
縮性繊維層を収縮させることにより、非熱収縮層の変形
を可能とした積層体を提供することにある。Therefore, it is an object of the present invention to form a sufficient convex shape on the surface by heat treatment, obtain a sufficient shrinkage rate in the heat treatment step, and shorten the heat treatment time to obtain a three-dimensional sheet. It is an object of the present invention to provide a laminated fiber aggregate for forming a three-dimensional sheet and a method for producing a three-dimensional sheet using the laminated fiber aggregate, which can reduce the production cost. Another object of the present invention is to provide a laminate capable of deforming a non-heat-shrinkable layer by shrinking the heat-shrinkable fiber layer by heat treatment.
【０００４】[0004]
【課題を解決するための手段】本発明は、熱収縮性繊維
を含む熱収縮性繊維層と非熱収縮性繊維層とを積層し、
両繊維層を部分的に接合してなる、立体シート形成用の
積層繊維集合体であって、前記熱収縮性繊維は、最大熱
収縮応力が０．７０〜３．００ｍＮ／ｄｔｅｘである立
体シート形成用の積層繊維集合体を提供することによ
り、上記の目的を達成したものである。According to the present invention, a heat-shrinkable fiber layer containing heat-shrinkable fibers and a non-heat-shrinkable fiber layer are laminated,
A laminated fiber assembly for forming a three-dimensional sheet, which is obtained by partially joining both fiber layers, wherein the heat-shrinkable fiber has a maximum heat-shrinkage stress of 0.70 to 3.00 mN / dtex. The above object is achieved by providing a laminated fiber assembly for forming.
【０００５】また、本発明は、前記立体シート形成用の
積層繊維集合体に、前記熱収縮性繊維の収縮開始温度以
上の温度の熱処理を施し前記熱収縮性繊維層を熱収縮さ
せることによって、前記非熱収縮性繊維層における前記
熱収縮性繊維層との接合部以外の部分が凸状に***した
立体シートを得る立体シートの製造方法を提供すること
により、上記の目的を達成したものである。Further, according to the present invention, the laminated fiber assembly for forming a three-dimensional sheet is subjected to heat treatment at a temperature equal to or higher than the contraction start temperature of the heat-shrinkable fiber to heat-shrink the heat-shrinkable fiber layer. By providing a method for producing a three-dimensional sheet in which a portion other than a joint portion with the heat-shrinkable fiber layer in the non-heat-shrinkable fiber layer is raised in a convex shape, the above object is achieved. is there.
【０００６】また、本発明は、熱収縮性繊維を含む熱収
縮性繊維層と非熱収縮層とを積層し、両層を接合してな
る積層体であって、前記熱収縮性繊維は、最大熱収縮応
力が０．７０〜３．００ｍＮ／ｄｔｅｘである積層体を
提供することにより、上記目的を達成したものである。Further, the present invention is a laminate comprising a heat-shrinkable fiber layer containing heat-shrinkable fibers and a non-heat-shrinkable layer, both layers being joined together, wherein the heat-shrinkable fiber comprises: The above object was achieved by providing a laminate having a maximum heat shrinkage stress of 0.70 to 3.00 mN / dtex.
【０００７】[0007]
【発明の実施の形態】以下本発明を、その好ましい実施
形態に基づき図面を参照しながら説明する。図１には、
本発明の立体シート形成用の積層繊維集合体の一実施形
態が、該積層繊維集合体に熱処理を施して得られる立体
シートと共に示されている。本実施形態の立体シート形
成用の積層繊維集合体１０は、図１（ａ）に示すよう
に、熱収縮性繊維を含む熱収縮性繊維層１と非熱収縮性
繊維層２とを積層し、両繊維層１，２を部分的に接合し
てなる。両繊維層１，２は、それぞれ、繊維の集合体か
ら構成されており、互いに、異なる種類及び／又は配合
の繊維の集合体から構成されている。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will now be described based on its preferred embodiments with reference to the drawings. In Figure 1,
One embodiment of the laminated fiber assembly for forming a three-dimensional sheet of the present invention is shown together with a three-dimensional sheet obtained by subjecting the laminated fiber assembly to a heat treatment. As shown in FIG. 1A, the laminated fiber assembly 10 for forming a three-dimensional sheet of the present embodiment is obtained by laminating a heat-shrinkable fiber layer 1 containing heat-shrinkable fibers and a non-heat-shrinkable fiber layer 2. The two fiber layers 1 and 2 are partially joined. Each of the two fiber layers 1 and 2 is formed of an aggregate of fibers, and is formed of an aggregate of fibers of different types and / or blends.
【０００８】熱収縮性繊維層１には、熱収縮性繊維が含
まれている。この熱収縮性繊維は、積層繊維集合体１０
中に、熱収縮可能な状態で含まれている。The heat-shrinkable fiber layer 1 contains heat-shrinkable fibers. This heat-shrinkable fiber is a laminated fiber assembly 10
It is contained in a state capable of heat shrinkage.
【０００９】本発明の立体シート形成用の積層繊維集合
体においては、熱収縮性繊維層に含ませる熱収縮性繊維
として、最大熱収縮応力が０．７０〜３．００ｍＮ／ｄ
ｔｅｘ、好ましくは０．７５〜１．５０ｍＮ／ｄｔｅｘ
のものを用いる。熱収縮性繊維の最大熱収縮応力が０．
７０ｍＮ／dｔｅｘ未満であると、立体シート製造時の
熱収縮処理（熱処理により収縮を発現させる工程）にお
いて、十分な熱収縮速度が得られず、表面に十分な高低
差を有する凹凸形状を形成させることができない。この
場合、熱収縮処理の時間を長くすることも考えられる
が、その場合には、非熱収縮性繊維層の温度が上昇
し、非熱収縮性繊維の樹脂の少なくとも一部が融解温度
以上にまで昇温され、立体シートの柔軟性、弾力性が損
なわれたり、立体シートの製造速度、特に熱収縮処理
工程の製造速度が他の工程（例えば、繊維ウェブのカー
ディング工程、熱収縮性繊維層と非熱収縮性繊維層を接
合させる工程）に比べ著しく遅くなって生産性に劣り、
安価で実用的な立体シートを供給することが困難とな
る。他方、前記最大熱収縮応力が３．００ｍＮ／ｄｔｅ
ｘ超であると、繊維開繊時に発生する開繊装置と繊維
間の摩擦熱、および繊維同士の摩擦熱によって、熱収縮
繊維が熱収縮するため、熱収縮性繊維層を形成すること
が難しくなる。特に、熱収縮繊維層として、カード法に
よって形成されたウェブ、又は該ウエブにヒートエンボ
スによって部分的に熱融着部を形成したヒートロール不
織布を用いる場合、そのウエブの形成の際に、地合いの
乱れが顕著になり、実質的にウエブを製造することが不
可能となる。また、熱収縮処理工程において、公知の
シート材料の乾燥やヒートセット等の熱処理を行う装置
（例えば、特開平３−２７９４６０に記載の上下ノズル
から熱風を噴出し熱処理を行う装置や、特開平５−１１
７９６１に記載のテンターチェーンを用いた熱処理装置
を熱収縮処理を目的に改良した装置）などを用いた場合
には、熱収縮速度が速く、基材の収縮が急激であるた
め、シートの収縮率を一定に保つことが非常に困難であ
る。In the laminated fiber assembly for forming a three-dimensional sheet of the present invention, the maximum heat shrinkage stress of the heat shrinkable fibers contained in the heat shrinkable fiber layer is 0.70 to 3.00 mN / d.
tex, preferably 0.75 to 1.50 mN / dtex
Use the one. The maximum heat shrinkage stress of the heat shrinkable fiber is 0.
When it is less than 70 mN / dtex, a sufficient heat shrinkage rate cannot be obtained in the heat shrinkage treatment (step of causing shrinkage by heat treatment) during production of a three-dimensional sheet, and an uneven shape having a sufficient height difference is formed on the surface. I can't. In this case, it is conceivable to lengthen the time of the heat-shrinking treatment, but in that case, the temperature of the non-heat-shrinkable fiber layer rises, and at least a part of the resin of the non-heat-shrinkable fiber reaches the melting temperature or higher. The flexibility and elasticity of the three-dimensional sheet are impaired, and the production speed of the three-dimensional sheet, particularly the heat-shrinking treatment step, is different from other processes (for example, carding process of fiber web, heat-shrinkable fiber). Layer) and the non-heat-shrinkable fiber layer are joined together)
It becomes difficult to supply an inexpensive and practical three-dimensional sheet. On the other hand, the maximum heat shrinkage stress is 3.00 mN / dte
When it is more than x, the heat-shrinkable fibers are thermally shrunk due to the frictional heat between the fiber-spreading device and the fibers generated during fiber-spreading, and the frictional heat between the fibers, making it difficult to form the heat-shrinkable fiber layer. Become. In particular, as the heat-shrinkable fiber layer, when using a web formed by a card method, or a heat roll non-woven fabric in which a heat-sealed portion is partially formed by heat embossing on the web, when the web is formed, The turbulence becomes noticeable, making it virtually impossible to produce a web. Further, in the heat shrinking treatment step, an apparatus for performing heat treatment such as drying and heat setting of a known sheet material (for example, an apparatus for ejecting hot air from upper and lower nozzles for heat treatment described in JP-A-3-279460; -11
When a heat treatment apparatus using a tenter chain described in 7961 is improved for the purpose of heat shrinkage treatment), the heat shrinkage rate is high and the shrinkage of the substrate is rapid, so that the shrinkage rate of the sheet Is very difficult to keep constant.
【００１０】本発明において、熱収縮性繊維層に含ませ
る熱収縮性繊維は、その破断伸度がその目標値の±３０
％以内にするのが好ましく、±２０％以内にするのが更
に好ましい。本実施形態の積層繊維集合体においては、
熱収縮性繊維として偏心芯鞘型複合繊維（非収縮成分：
ポリプロピレン、収縮成分：エチレン・プロピレンコポ
リマー）を用いており、この場合の破断伸度は８０％±
３０％以内であることが好ましい。熱収縮性繊維の破断
伸度が５０％未満であると、熱収縮性繊維の最大熱収縮
応力が３．００ｍＮ／ｄｔｅｘ超の場合と同様の問題を
生じる。他方、熱収縮性繊維の破断伸度が１１０％超、
特に１２０％超であると熱収縮性繊維の最大熱収縮応力
を０．７ｍＮ／ｄｔｅｘ以上とすることが困難となり、
上述したように、立体シートの表面に十分な高低差を有
する凹凸形状を形成させることができない。In the present invention, the heat-shrinkable fiber contained in the heat-shrinkable fiber layer has a breaking elongation of ± 30 of the target value.
%, Preferably within ± 20%, and more preferably within ± 20%. In the laminated fiber assembly of the present embodiment,
Eccentric core-sheath type composite fiber (non-shrinkable component:
Polypropylene, shrinkage component: ethylene-propylene copolymer) is used, and the breaking elongation in this case is 80% ±
It is preferably within 30%. If the breaking elongation of the heat-shrinkable fiber is less than 50%, the same problem as in the case where the maximum heat-shrinkable stress of the heat-shrinkable fiber exceeds 3.00 mN / dtex occurs. On the other hand, the breaking elongation of the heat-shrinkable fiber exceeds 110%,
Especially when it exceeds 120%, it becomes difficult to set the maximum heat shrinkage stress of the heat shrinkable fiber to 0.7 mN / dtex or more,
As described above, it is not possible to form the uneven shape having a sufficient height difference on the surface of the three-dimensional sheet.
【００１１】ここで、熱収縮性繊維の最大熱収縮応力
は、以下のようにして測定される。熱応力測定装置（カ
ネボウエンジニアリング株式会社製、ＫＥ−２ＬＳ）を
用いて測定を行った。試料長５０ｍｍ、試料重量１１０
ｄｔｅｘの試料を取付用フックにセットする。初荷重
３．３ｇｆ／１１０ｄｔｅｘを試料に加え、試料長を５
０ｍｍに保った状態で、４０℃から１７０℃まで昇温速
度１．２５℃／ｓｅｃ（２４０秒で３００℃まで昇温す
るように昇温する）で装置を加熱し、その過程において
荷重計が示した最大荷重を、１ｄｔｅｘあたりに換算し
て最大熱収縮応力（ｍＮ／ｄｔｅｘ）とする。後述する
実施例で用いた潜在捲縮性繊維の場合には、１３０〜１
７０℃の範囲で最大熱収縮応力を発現した。The maximum heat shrinkage stress of the heat shrinkable fiber is measured as follows. The measurement was performed using a thermal stress measuring device (KE-2LS, manufactured by Kanebo Engineering Co., Ltd.). Sample length 50 mm, sample weight 110
Set the dtex sample on the mounting hook. An initial load of 3.3 gf / 110 dtex was added to the sample, and the sample length was 5
With the temperature kept at 0 mm, the device was heated from 40 ° C. to 170 ° C. at a temperature rising rate of 1.25 ° C./sec (increases the temperature to 300 ° C. in 240 seconds). The maximum load shown is converted per 1 dtex to be the maximum heat shrinkage stress (mN / dtex). In the case of latently crimpable fibers used in the examples described below, 130 to 1
The maximum heat shrinkage stress was developed in the range of 70 ° C.
【００１２】また、熱収縮性繊維の破断伸度は、以下の
ようにして測定される。ＪＩＳ Ｌ１０１５ ７．７引
張強さ及び伸び率に示されている、標準時試験方法にて
評価した。
（１）試料
表面が滑らかな紙片に、固定間距離２０ｍｍで繊維を１
本ずつ緩く張った状態で、両端を接着剤などで固定した
ものを試料とする。
（２）測定方法
試料を単繊維引張試験機の試料取り付け用のチャックに
取り付け、下記の条件で試験を行う。なお、このときチ
ャック間の紙片は切断されている。
チャック間距離：２０ｍｍ 引張速度：２０±１
ｍｍ／分
両端を固定し、初荷重をかけたときの伸びを緩み（ｍ
ｍ）として読み、更に試料を引張、試料が切断した時の
初荷重からの伸び（ｍｍ）を測定する。下記の式（１）
により乾伸度を算出する。試験回数は３０回とし、その
平均値を乾伸度とする。初荷重は、繊維の種類によって
適宜選ばれるが、本実施形態の場合は、１／２０ｇｆ×
デニール数とした。
乾伸度（％）＝[（Ｅ２−Ｅ１）／（Ｌ＋Ｅ１）]×１００ （１）
Ｅ１：緩み（ｍｍ）、Ｅ２：切断時の伸び（ｍｍ）、
Ｌ：つかみ間隔（ｍｍ）The breaking elongation of the heat-shrinkable fiber is measured as follows. It was evaluated by the standard time test method shown in JIS L1015 7.7 Tensile strength and elongation. (1) 1 piece of fiber with a fixed distance of 20 mm on a piece of paper with a smooth sample surface
The sample is made by loosely stretching each book and fixing both ends with an adhesive. (2) Measurement method A sample is attached to a sample attachment chuck of a single fiber tensile tester, and a test is performed under the following conditions. At this time, the paper piece between the chucks is cut. Distance between chucks: 20mm Peeling speed: 20 ± 1
mm / min Fix both ends and loosen the elongation when the initial load is applied (m
Read as m), further pull the sample, and measure the elongation (mm) from the initial load when the sample is cut. The following formula (1)
The dry elongation is calculated by. The number of tests is 30 and the average value is the dry elongation. The initial load is appropriately selected depending on the type of fiber, but in the case of this embodiment, 1/20 gf ×
The number of denier was set. Dry elongation (%) = [(E2-E1) / (L + E1)] × 100 (1) E1: Looseness (mm), E2: Elongation at cutting (mm),
L: Grip interval (mm)
【００１３】上述した最大熱収縮応力の要件を満足する
熱収縮性繊維は、例えば、後述する実施例におけるよう
に熱収縮性繊維として潜在捲縮性繊維を用いる場合に
は、熱収縮性に優れたポリマーの選定、および該潜在捲
縮性繊維を製造する工程（繊維の製造工程：紡糸工程→
延伸工程→捲縮工程→カット工程）のうちの延伸工程に
おいて、繊維の破断伸度が８０±３０％となるように、
延伸倍率をコントロールすることによって得られる。具
体的な一例として、前記潜在捲縮性繊維を、収縮率の異
なる２種類の成分からなる偏心芯鞘型もしくはサイド・
バイ・サイド型の複合繊維とし、その両成分をエチレン
−プロピレンランダム共重合体（高収縮成分）及びポリ
プロピレン（低収縮成分）とした場合、ポリプロピレン
のＱ値が５未満、好ましくは３．５以下であるポリマー
を選定し、エチレン−プロピレンランダム共重合体の融
点が１４５℃以下、好ましくは１４０℃以下であるポリ
マーを選定して、溶融紡糸し、得られた紡糸フィラメン
トを延伸倍率２〜６倍の範囲で延伸処理を施すことによ
り所望の最大熱収縮応力が得られる。The heat-shrinkable fiber satisfying the above-mentioned maximum heat-shrinkage stress has excellent heat-shrinkability when, for example, a latently crimpable fiber is used as the heat-shrinkable fiber as in Examples described later. Selected polymer, and the step of producing the latently crimpable fiber (fiber production step: spinning step →
In the drawing process of (drawing process → crimping process → cutting process), the breaking elongation of the fiber is 80 ± 30%,
It is obtained by controlling the draw ratio. As a specific example, the latently crimpable fiber is formed of an eccentric sheath-core type or a side-core type composed of two kinds of components having different shrinkage rates.
When the bi-side type composite fiber is used and both components thereof are ethylene-propylene random copolymer (high shrinkage component) and polypropylene (low shrinkage component), the Q value of polypropylene is less than 5, preferably 3.5 or less. Is selected, the melting point of the ethylene-propylene random copolymer is 145 ° C. or lower, preferably 140 ° C. or lower, melt spinning is performed, and the obtained spinning filament is drawn at a draw ratio of 2 to 6 times. A desired maximum heat shrinkage stress can be obtained by subjecting the film to a stretching treatment within the range.
【００１４】本発明の立体シート形成用の積層繊維集合
体に用いる熱収縮性繊維は、上述した最大熱収縮応力の
要件を満足するものである限り、各種公知のもの等を特
に制限なく用いることができるが、熱収縮時にコイル状
の３次元捲縮を発現し繊維の配向方向（一般に製造時の
原反流れ方向）とそれに直行する方向の両方に均等に収
縮するという点から、熱収縮性繊維として潜在捲縮性繊
維を用いることが好ましい。また、潜在捲縮性繊維を用
いると、得られる立体シートが全体としてエラストマー
的な性質を発現し、その立体シートを例えば後述する使
い捨て吸収性物品の構成部材として用いた場合に、着用
者の動作に対する追従性が良好となり、該吸収性物品の
フィット性が向上し、液漏れが効果的に防止される。潜
在捲縮性繊維は、加熱される前は、従来の不織布用の繊
維と同様に取り扱うことができ、且つ所定温度での加熱
によって螺旋状の捲縮が発現して収縮する性質を有する
繊維である。As the heat-shrinkable fibers used in the laminated fiber assembly for forming a three-dimensional sheet of the present invention, various known ones may be used without particular limitation as long as they satisfy the above-mentioned requirements for the maximum heat-shrinkage stress. However, the heat-shrinkability is due to the fact that the coil-like three-dimensional crimp is developed during heat shrinkage, and the fiber is uniformly shrunk in both the fiber orientation direction (generally, the original fabric flow direction during manufacturing) and the direction orthogonal thereto. It is preferable to use latently crimpable fibers as the fibers. In addition, when the latent crimpable fiber is used, the obtained three-dimensional sheet exhibits elastomeric properties as a whole, and the action of the wearer when the three-dimensional sheet is used as a constituent member of a disposable absorbent article described later, for example. The following property is improved, the fit of the absorbent article is improved, and liquid leakage is effectively prevented. The latently crimpable fiber is a fiber which can be handled in the same manner as a conventional nonwoven fabric fiber before being heated, and has a property that a helical crimp is developed and contracted by heating at a predetermined temperature. is there.
【００１５】潜在捲縮性繊維は、例えば、収縮率の異な
る２種類の成分からなる偏心芯鞘型若しくは同心芯鞘型
の複合繊維又はサイド・バイ・サイド型の複合繊維から
なる。その例としては、特開平９−２９６３２５号公報
や特許２７５９３３１号明細書に記載のものが挙げられ
る。収縮率の異なる２種類の成分（熱可塑性ポリマー
等）としては、（１）エチレン−プロピレンランダム共
重合体（高収縮率成分）とポリプロピレン（低収縮率成
分）との組み合わせ、（２）ポリエチレンテレフタレー
ト（ＰＥＴ，低収縮率成分）とポリエチレンテレフタレ
ートとイソフタル酸の共重合体（ＣｏＰＥＴ，高収縮率
成分）との組み合わせが挙げられる。その太さは１．０
〜１１．０ｄｔｅｘ程度が好適である。熱捲縮性繊維
は、ステープルファイバでも長繊維のフィラメントでも
よい。尚、熱収縮性繊維の収縮開始温度は例えば８０〜
１５０℃とすることができる。熱収縮開始温度とは、昇
温可能な炉にその繊維を置き、一定速度で昇温したと
き、その繊維が実質的に収縮開始した時の実測温度を言
う。The latently crimpable fibers are, for example, eccentric core-sheath type or concentric core-sheath type composite fibers or side-by-side type composite fibers composed of two kinds of components having different shrinkage rates. Examples thereof include those described in Japanese Patent Application Laid-Open No. 9-296325 and Japanese Patent No. 2759331. The two types of components having different shrinkage ratios (thermoplastic polymers, etc.) include (1) a combination of an ethylene-propylene random copolymer (high shrinkage ratio component) and polypropylene (low shrinkage ratio component), (2) polyethylene terephthalate (PET, low shrinkage component) and a combination of polyethylene terephthalate and isophthalic acid copolymer (CoPET, high shrinkage component). Its thickness is 1.0
Approximately 11.0 dtex is preferable. The heat-crimpable fibers may be staple fibers or filaments of long fibers. The shrinkage start temperature of the heat shrinkable fiber is, for example, 80 to
It can be 150 ° C. The heat shrinkage start temperature means an actually measured temperature when the fiber is placed in a furnace capable of heating and is heated at a constant rate and the fiber substantially starts shrinking.
【００１６】熱収縮性繊維層１は、熱収縮性繊維１００
％からなるものでも、或いは他の繊維を含んでいるもの
でも良い。熱収縮性繊維層１に含ませる他の繊維として
は、例えば後述する非熱収縮性繊維層２に含まれる熱融
着性繊維が挙げられる。熱収縮性繊維層１に他の繊維が
含まれる場合であっても、立体シートの製造時に、熱収
縮性繊維の収縮が阻害されないようにする観点から、熱
収縮性繊維の量は、熱収縮性繊維層１の重量に対して５
０重量％以上、特に７０〜９０重量％であることが好ま
しい。ここでいう熱融着繊維とは、芯鞘型熱融着性複合
繊維であり、該芯鞘型熱融着性複合繊維の主に鞘部の樹
脂の熱融着により、繊維交点が熱融着される繊維のこと
である。非熱収縮性繊維層２と共に熱収縮性繊維層１に
も熱融着性繊維を含ませても良いが、その場合には、熱
収縮性繊維の熱収縮性を阻害させない観点から、熱収縮
性繊維層１の重量に対して５０重量％以下、特に２０重
量％以下であることが好ましい。The heat-shrinkable fiber layer 1 is composed of heat-shrinkable fibers 100.
%, Or may contain other fibers. Examples of other fibers contained in the heat-shrinkable fiber layer 1 include heat-fusible fibers contained in the non-heat-shrinkable fiber layer 2 described later. Even when the heat-shrinkable fiber layer 1 contains other fibers, the amount of the heat-shrinkable fibers is set so that the shrinkage of the heat-shrinkable fibers is not obstructed during the production of the three-dimensional sheet. 5 based on the weight of the elastic fiber layer 1
It is preferably 0% by weight or more, and particularly preferably 70 to 90% by weight. The heat-sealing fiber as used herein is a core-sheath heat-fusible composite fiber, and the fiber intersection is heat-melted mainly by heat-sealing the resin of the sheath of the core-sheath heat-fusible composite fiber. The fibers that are worn. The heat-shrinkable fiber layer 1 and the heat-shrinkable fiber layer 1 may contain the heat-fusible fiber, but in that case, the heat-shrinkable fiber does not impair the heat-shrinkability of the heat-shrinkable fiber. It is preferably 50% by weight or less, and particularly preferably 20% by weight or less with respect to the weight of the functional fiber layer 1.
【００１７】本発明で用いる熱収縮性繊維は、特に、複
合繊維からなる潜在捲縮性繊維であって、該潜在捲縮性
繊維中の成分として、エチレン−プロピレンランダム共
重合体を含むものが好ましい。斯かる繊維を用いると、
熱収縮開始温度が８０〜１２０℃程度と比較的低温から
収縮するため、非熱収縮層として熱融着性繊維からなる
不織布を用いた場合も、非熱収縮層を融解させ風合いを
悪化させることなく収縮できるという点で優れている。
また非熱収縮層として、芯成分がポリエステル系または
ポリプロピレン系樹脂であり、鞘成分がポリエチレン系
またはポリプロピレンを主成分とするエチレン−プロピ
レンランダム共重合体からなる熱融着性複合繊維を用い
た場合には、非熱収縮性繊維層と熱収縮性繊維層の接合
の観点から、本発明で用いる熱収縮性繊維は、特に、複
合繊維からなる潜在捲縮性繊維であって、該潜在捲縮性
繊維中の成分として、エチレン−プロピレンランダム共
重合体を含むものが好ましい。The heat-shrinkable fiber used in the present invention is, in particular, a latent crimpable fiber composed of a composite fiber, which contains an ethylene-propylene random copolymer as a component in the latent crimpable fiber. preferable. With such fibers,
Since the heat shrinkage start temperature shrinks from a relatively low temperature of about 80 to 120 ° C., even when a non-woven fabric made of heat-fusible fibers is used as the non-heat shrinkable layer, the non-heat shrinkable layer is melted to deteriorate the texture. It is excellent in that it can shrink without shrinkage.
Further, as the non-heat-shrinkable layer, when the core component is a polyester-based or polypropylene-based resin, and the sheath component is a polyethylene-based or a heat-fusible conjugate fiber made of an ethylene-propylene random copolymer containing polypropylene as a main component is used. From the viewpoint of joining the non-heat-shrinkable fiber layer and the heat-shrinkable fiber layer, the heat-shrinkable fiber used in the present invention is, in particular, a latent crimpable fiber composed of a composite fiber, Those containing an ethylene-propylene random copolymer as a component in the functional fiber are preferable.
【００１８】熱収縮性繊維層１を構成する繊維集合体の
形態としては、構成繊維が未接合状態にあるウエブ、又
は不織布が挙げられる。ウエブの形態である熱収縮性繊
維層１としては、熱収縮性繊維を含み且つカード法によ
って形成されたウエブが挙げられる。不織布の形態であ
る熱収縮性繊維層１としては、熱収縮性繊維を含む、各
種不織布製造法で製造された不織布が挙げられる。不織
布製造法としては、熱融着法、水流交絡法、ニードルパ
ンチ法、溶剤接着法、スパンボンド法、メルトブローン
法が挙げられる。熱収縮性繊維層１を構成させる繊維集
合体としてウェブを用いると、得られる立体シートが全
体としてエラストマー的な性質を顕著に発現し、その立
体シートを例えば後述する使い捨て吸収性物品の構成部
材として用いた場合に、着用者の動作に対する追従性が
良好となり、該吸収性物品のフィット性が向上し、液漏
れが効果的に防止される。また、一方で不織布を用いる
と、ハンドリング性や巻回してロール状にした場合の繰
出し性に関して、顕著に改善される。したがって、本発
明では、熱収縮繊維層１として、ウェブを使うか不織布
を使うかは、その立体シートの使用場面と製造方法によ
って適宜選択される。Examples of the form of the fiber assembly constituting the heat-shrinkable fiber layer 1 include a web in which the constituent fibers are not joined, or a nonwoven fabric. Examples of the heat-shrinkable fiber layer 1 in the form of a web include a web containing heat-shrinkable fibers and formed by the card method. Examples of the heat-shrinkable fiber layer 1 in the form of a non-woven fabric include non-woven fabrics containing heat-shrinkable fibers and manufactured by various non-woven fabric manufacturing methods. Examples of the non-woven fabric manufacturing method include a heat fusion method, a hydroentangling method, a needle punch method, a solvent bonding method, a spun bond method, and a melt blown method. When a web is used as the fiber assembly constituting the heat-shrinkable fiber layer 1, the obtained three-dimensional sheet remarkably exhibits elastomeric properties, and the three-dimensional sheet is used as a constituent member of a disposable absorbent article described later, for example. When used, the followability to the motion of the wearer is improved, the fit of the absorbent article is improved, and liquid leakage is effectively prevented. On the other hand, when a non-woven fabric is used, the handling property and the feeding property when rolled into a roll form are significantly improved. Therefore, in the present invention, whether to use a web or a nonwoven fabric as the heat-shrinkable fiber layer 1 is appropriately selected depending on the use situation of the three-dimensional sheet and the manufacturing method.
【００１９】非熱収縮性繊維層２は、熱収縮性を示さな
いか又は熱収縮性を示すが熱収縮性繊維層１よりもその
程度が小さい。本実施形態における非熱収縮性繊維層２
は、非熱収縮性繊維を主体として構成されている。非熱
収縮性繊維とは、熱収縮性を示さない繊維、及び熱収縮
性は示すが熱収縮性繊維層に含まれる熱収縮性繊維の熱
収縮開始温度以下で実質的に熱収縮しない繊維の双方を
含む。The non-heat-shrinkable fiber layer 2 does not show heat-shrinkability or shows heat-shrinkability, but its degree is smaller than that of the heat-shrinkable fiber layer 1. Non-heat-shrinkable fiber layer 2 in this embodiment
Is mainly composed of non-heat-shrinkable fibers. The non-heat-shrinkable fiber means a fiber that does not exhibit heat-shrinkability, and a fiber that exhibits heat-shrinkability but does not substantially heat-shrink below the heat-shrinking onset temperature of the heat-shrinkable fiber contained in the heat-shrinkable fiber layer. Including both.
【００２０】非熱収縮性繊維層２を構成する繊維集合体
の形態としては、構成繊維が未接合状態にあるウエブ又
は不織布が挙げられる。ウェブの例としては、カード法
によって形成されたウェブ、エアレイド法によって形成
されたウェブなどが挙げられる。不織布の例としては、
熱融着法によって形成された不織布、水流交絡法によっ
て形成された不織布、ニードルパンチ法によって形成さ
れた不織布、溶剤接着法によって形成された不織布、ス
パンボンド法によって形成された不織布、メルトブロー
ン法によって形成された不織布などが挙げられる。非熱
収縮性繊維層２の形態が、特にウエブの形態または５〜
２０ｇ／ｍ2の低目付不織布であると、熱収縮性繊維層
１の熱収縮によって非熱収縮性繊維層２の面積ないし形
状を変化させることが容易となり、非熱収縮性繊維層２
を厚み方向に凸状に盛り上げることが容易になるので好
ましい。特にウエブの形態の場合は、盛り上がった凸部
の中が繊維で満たされるので、クッション性に富み柔ら
かな風合いを有する立体シートが得られるので好まし
い。ウエブは例えばカード法によって形成することがで
きる。非熱収縮性繊維層２が、斯かるウエブから形成さ
れた立体シートには、嵩高で且つ該ウェブを構成する繊
維で満たされた凸部４が形成され、また繊維が凸部４に
沿うように配向する。特に、非熱収縮性繊維層２が、カ
ード法によって形成されたウエブの形態であると、非熱
収縮性繊維層２が極めて疎な構造となり、得られる立体
シートは、粘度の高い液の透過や保持が可能となる。ま
た立体シートを厚み方向へ圧縮させたときの圧縮変形性
も高くなる。粘度の高い液としては、軟便若しくは経
血、対人用の清浄剤若しくは保湿剤、又は対物用の清浄
剤が挙げられる。Examples of the form of the fiber assembly forming the non-heat-shrinkable fiber layer 2 include a web or a nonwoven fabric in which the constituent fibers are in an unbonded state. Examples of the web include a web formed by the card method and a web formed by the air laid method. Examples of non-woven fabrics include
Non-woven fabric formed by heat fusion method, non-woven fabric formed by hydroentanglement method, non-woven fabric formed by needle punch method, non-woven fabric formed by solvent bonding method, non-woven fabric formed by spunbond method, formed by melt blown method And the like. The form of the non-heat-shrinkable fiber layer 2 is particularly the form of a web or 5
A low basis weight nonwoven fabric of 20 g / m 2 makes it easy to change the area or shape of the non-heat-shrinkable fiber layer 2 by the heat shrinkage of the heat-shrinkable fiber layer 1, and the non-heat-shrinkable fiber layer 2
Is preferable because it becomes easy to build up in a convex shape in the thickness direction. Particularly in the case of the form of a web, the raised protrusions are filled with fibers, so that a three-dimensional sheet having a rich cushioning property and a soft texture can be obtained, which is preferable. The web can be formed, for example, by the card method. On the three-dimensional sheet in which the non-heat-shrinkable fiber layer 2 is formed from such a web, convex portions 4 which are bulky and filled with the fibers constituting the web are formed, and the fibers are arranged along the convex portions 4. Orient to. In particular, when the non-heat-shrinkable fiber layer 2 is in the form of a web formed by the card method, the non-heat-shrinkable fiber layer 2 has an extremely sparse structure, and the obtained three-dimensional sheet has a high viscosity permeation liquid. And can be held. Further, the compressive deformability when the three-dimensional sheet is compressed in the thickness direction also becomes high. Examples of the highly viscous liquid include loose stools or menstrual blood, detergents or moisturizers for humans, or detergents for objectives.
【００２１】特に非熱収縮性繊維層２が、熱融着性複合
繊維を５０％以上より好ましくは７０％以上含む場合
は、生理用ナプキンやオムツなどの吸収性物品や対人用
ワイパー、清掃用ワイパーに用いた場合にも、肌もしく
は清掃対象物表面との摩擦においても、非熱収縮繊維層
２からの繊維の脱落が抑制され、脱落繊維の肌への貼り
つきや、清掃対象物表面への脱落繊維の付着が抑制さ
れ、好適である。さらにこの場合に用いられる熱融着性
複合繊維がエアスルー法を用いて製造された不織布であ
る場合、前記効果が顕著に発現する。また、本実施形態
においては、非熱収縮性繊維層２中に熱融着性繊維を含
ませることで、上述した熱収縮性繊維層１と非熱収縮性
繊維層２とを、部分的接合させる際に、層間のはく離強
度を増加させる観点から好適である。Particularly when the non-heat-shrinkable fiber layer 2 contains 50% or more, more preferably 70% or more, of the heat-fusible composite fiber, absorbent articles such as sanitary napkins and diapers, wipers for humans, and cleaning. Even when used as a wiper, the fibers are prevented from falling off from the non-heat-shrinkable fiber layer 2 even when they are rubbed against the skin or the surface of the object to be cleaned, and the falling fibers stick to the skin or to the surface of the object to be cleaned. Adhesion of the fallen fibers is suppressed, which is preferable. Furthermore, when the heat-fusible conjugate fiber used in this case is a nonwoven fabric manufactured by the air-through method, the above-mentioned effect is remarkably exhibited. In addition, in the present embodiment, the non-heat-shrinkable fiber layer 2 contains a heat-fusible fiber to partially bond the heat-shrinkable fiber layer 1 and the non-heat-shrinkable fiber layer 2 described above. In doing so, it is preferable from the viewpoint of increasing the peel strength between the layers.
【００２２】前記熱融着性繊維の例としては、熱可塑性
ポリマー材料からなる繊維が好適に用いられる。熱可塑
性ポリマー材料としては、ポリエチレンやポリプロピレ
ン等のポリオレフィン、ポリエチレンテレフタレート等
のポリエステル類、ポリアミドなどが挙げられる。ま
た、これらの熱可塑性ポリマー材料の組合せからなる芯
鞘型複合繊維も用いることができる。前記繊維の繊度は
用途にもよるが、０．５〜２０ｄｔｅｘ、特に１〜１０
ｄｔｅｘであることが、立体シート材料を吸収性物品の
構成部材に用いた場合や、対人用ワイパーなどに用いる
場合には良好な感触を発現させる点から好ましい。As an example of the heat-fusible fiber, a fiber made of a thermoplastic polymer material is preferably used. Examples of the thermoplastic polymer material include polyolefin such as polyethylene and polypropylene, polyesters such as polyethylene terephthalate, and polyamide. Further, a core-sheath type conjugate fiber made of a combination of these thermoplastic polymer materials can also be used. The fineness of the fiber depends on the application, but is 0.5 to 20 dtex, particularly 1 to 10
The dtex is preferable from the viewpoint of exhibiting a good feel when the three-dimensional sheet material is used as a constituent member of an absorbent article or when it is used as a wiper for personal use.
【００２３】本実施形態の立体シート形成用の積層繊維
集合体１０においては、上述したように、熱収縮性繊維
層１と非熱収縮性繊維層２とは熱融着により部分的に接
合されている。そして、積層繊維集合体１０を平面視し
た場合、該積層繊維集合体１０には、図２（ａ）に示す
菱形格子状パターンの接合部３が形成されている。本実
施形態における個々の接合部は、円形のものであるが、
個々の接合部の形状は、楕円形、三角形若しくは矩形又
はこれらの組み合わせ等であってもよい。また接合部を
連続した形状、例えば直線や曲線などの線状に形成して
もよい。接合部３の形成パターンは、図２（ｂ）及び図
２（ｃ）に示すようなパターンとすることもできる。In the laminated fiber assembly 10 for forming a three-dimensional sheet of this embodiment, as described above, the heat-shrinkable fiber layer 1 and the non-heat-shrinkable fiber layer 2 are partially joined by heat fusion. ing. When the laminated fiber assembly 10 is viewed in a plan view, the laminated fiber assembly 10 is provided with the bonding portions 3 in the rhombic lattice pattern shown in FIG. 2A. Although the individual joints in this embodiment are circular,
The shape of each joint may be elliptical, triangular or rectangular, or a combination thereof. Further, the joint portion may be formed in a continuous shape, for example, a linear shape such as a straight line or a curved line. The formation pattern of the joint portion 3 may be a pattern as shown in FIGS. 2B and 2C.
【００２４】積層繊維集合体１０の面積に対する接合部
３の面積率（積層繊維集合体１０の単位面積当りの接合
部３の面積）は、両繊維層の接合強度を十分に高くする
点、及び熱収縮性繊維層の変形により凸状の立体的な形
状を十分に形成して嵩高な立体シートを得る観点から、
接合部３の形成後且つ熱収縮性繊維層１の熱収縮前にお
いては３〜５０％、特に５〜３５％であり、熱収縮させ
て立体シートをした状態においては６〜９０％、特に１
０〜７０％であることが好ましい。接合部３の形成方法
としては、ヒートエンボス、超音波エンボス、接着剤に
よる接着などの各種接合手段を用いることができる。The area ratio of the joint portion 3 to the area of the laminated fiber assembly 10 (area of the joint portion 3 per unit area of the laminated fiber assembly 10) is such that the joint strength of both fiber layers is sufficiently high, and From the viewpoint of obtaining a bulky three-dimensional sheet by sufficiently forming a convex three-dimensional shape by the deformation of the heat-shrinkable fiber layer,
It is 3 to 50%, especially 5 to 35% after the formation of the joint portion 3 and before the heat shrinkage of the heat shrinkable fiber layer 1, and 6 to 90%, especially 1 in the state of being heat-shrinked to form a three-dimensional sheet.
It is preferably 0 to 70%. As a method of forming the joining portion 3, various joining means such as heat embossing, ultrasonic embossing, and bonding with an adhesive can be used.
【００２５】図３は、本実施形態の立体シート形成用の
積層繊維集合体１０の製造工程、及び該積層繊維集合体
１０に熱処理を施して立体シート２０を得る立体シート
の製造工程を連続的に行う場合を示す図である。図３に
示す製造方法においては、上述した最大熱収縮応力の要
件を満足する熱収縮性繊維をカード機に導入してカード
ウエブからなる熱収縮性繊維層１を得、該熱収縮性繊維
層１に、別に製造したエアースルー不織布からなる非熱
収縮性繊維層２を重ね合わせた後、これらを、少なくと
も一方を加熱可能な凹凸ロール同士又は凹凸ロールと平
滑ロールとの組み合わせからなる熱エンボスロール装置
６に導入して、上述した構成の立体シート形成用の積層
繊維集合体１０を製造する。この積層繊維集合体１０
は、この段階において回収し、例えばロール状の巻回物
として保管したり、別のラインに移して用いることもで
きるが、図３に示す方法においては、得られた積層繊維
集合体１０をそのまま搬送して、その搬送経路に配置さ
れた熱処理装置７により熱処理する。この熱処理は、熱
収縮性繊維層１に含まれる熱収縮性繊維の熱収縮開始温
度以上で行う。この熱処理により、熱収縮性繊維層１が
熱収縮し、それに伴って、非熱収縮性繊維層２における
接合部３以外の部分が大きく凸状に変形して***し、表
面に多数の凸部が形成される。尚、熱処理装置における
熱処理は、熱風を透過させたり、吹き付けたりする方法
の他、マイクロウェーブ、蒸気、赤外線、ヒートロール
の接触等の方法を用いることもできる。FIG. 3 shows a continuous process of manufacturing the laminated fiber assembly 10 for forming a three-dimensional sheet of the present embodiment, and a three-dimensional sheet manufacturing process in which the laminated fiber assembly 10 is heat-treated to obtain a three-dimensional sheet 20. It is a figure which shows the case where it performs to. In the manufacturing method shown in FIG. 3, heat-shrinkable fibers satisfying the above-mentioned maximum heat-shrinkage stress requirement are introduced into a card machine to obtain a heat-shrinkable fiber layer 1 made of a card web, and the heat-shrinkable fiber layer is obtained. 1 is overlaid with a non-heat-shrinkable fiber layer 2 made of an air-through nonwoven fabric, which is separately manufactured, and then these are heat-embossing rolls composed of concavo-convex rolls capable of heating at least one of them or a combination of a concavo-convex roll and a smooth roll. Introduced into the apparatus 6, the laminated fiber assembly 10 for forming a three-dimensional sheet having the above-described configuration is manufactured. This laminated fiber assembly 10
Can be collected at this stage and stored, for example, as a roll-shaped wound product or transferred to another line and used, but in the method shown in FIG. 3, the obtained laminated fiber assembly 10 is used as it is. It is conveyed and heat-treated by the heat treatment device 7 arranged on the conveyance path. This heat treatment is performed at the heat shrinkage start temperature of the heat shrinkable fibers contained in the heat shrinkable fiber layer 1 or higher. By this heat treatment, the heat-shrinkable fiber layer 1 is heat-shrunk, and along with it, the portions other than the joint portion 3 in the non-heat-shrinkable fiber layer 2 are largely convexly deformed and raised, and a large number of convex portions are formed on the surface. Is formed. The heat treatment in the heat treatment apparatus may be performed by a method of transmitting or blowing hot air, or a method of contacting with microwave, steam, infrared ray, heat roll, or the like.
【００２６】本実施形態の立体シート形成用の積層繊維
集合体１０によれば、例えば、このようにして、図１
（ｂ）に示すように、表面に十分に***した凸状形状が
形成された立体シート２０を製造することができる。ま
た、上記の熱処理においては、積層繊維集合体１０中の
熱収縮性繊維層１を、収縮前後の面積収縮率で、好まし
くは５０％以上、特に好ましくは６０％以上熱収縮させ
ることができ、しかも面積収縮率が５０％に達するまで
の熱処理時間を２０秒以下、好ましくは１〜１０秒、更
に好ましくは２〜６秒で行うことができる。斯かる条件
での熱処理が可能であると、表面に十分に***した凸状
形状が形成された立体シート２０を、低い製造コストに
て効率的に製造可能である。熱収縮性繊維層２の熱収縮
前後の面積収縮率は、収縮前の基準面積Ｓ0、基準面積
の収縮後の面積Ｓ1から下記の式（２）にて求められ
る。
面積収縮率（％）＝（Ｓ0 −Ｓ1 ）／Ｓ0 ×１００ （２）According to the laminated fiber assembly 10 for forming a three-dimensional sheet of the present embodiment, for example, as shown in FIG.
As shown in (b), it is possible to manufacture a three-dimensional sheet 20 having a sufficiently raised convex shape formed on its surface. In the above heat treatment, the heat-shrinkable fiber layer 1 in the laminated fiber assembly 10 can be heat-shrinked by the area shrinkage ratio before and after shrinkage of preferably 50% or more, particularly preferably 60% or more, Moreover, the heat treatment time until the area shrinkage ratio reaches 50% can be performed in 20 seconds or less, preferably 1 to 10 seconds, and more preferably 2 to 6 seconds. When the heat treatment under such conditions is possible, the three-dimensional sheet 20 having a sufficiently raised convex shape formed on the surface can be efficiently manufactured at a low manufacturing cost. The area shrinkage ratio of the heat-shrinkable fiber layer 2 before and after heat shrinkage is calculated from the reference area S 0 before shrinkage and the area S 1 after shrinkage of the reference area by the following formula (2). Area shrinkage ratio (%) = (S 0 −S 1 ) / S 0 × 100 (2)
【００２７】本発明に係る立体シート２０は、非熱収縮
性繊維層２によって形成される凸部４の形状がどのよう
なものであっても、凸部４の最頂部における立体シート
２０の厚みＴ〔図１（ｂ）参照〕と、接合部３における
立体シートの厚みＴ’〔図１（ｂ）参照〕との比Ｔ／
Ｔ’が２以上、特に３以上であるものが好ましい。この
比が２以上であると、立体シート２０に十分に高い嵩高
感が付与される。Ｔ／Ｔ’の上限値は、凸部４の保形性
や、立体シート２０の坪量の観点から決定され、具体的
には１０程度、特に６程度である。In the three-dimensional sheet 20 according to the present invention, the thickness of the three-dimensional sheet 20 at the top of the convex portion 4 is whatever the shape of the convex portion 4 formed by the non-heat-shrinkable fiber layer 2 is. Ratio T / of T [see FIG. 1 (b)] and thickness T ′ of the three-dimensional sheet at the joint 3 [see FIG. 1 (b)]
It is preferable that T ′ is 2 or more, and particularly 3 or more. When this ratio is 2 or more, the three-dimensional sheet 20 has a sufficiently high sense of bulk. The upper limit of T / T ′ is determined from the viewpoint of the shape retention of the convex portion 4 and the basis weight of the three-dimensional sheet 20, and is specifically about 10 and particularly about 6.
【００２８】厚みＴ及びＴ’は以下の方法で測定され
る。先ず、厚みＴについては、立体シート２０を５０ｍ
ｍ×５０ｍｍの大きさに裁断し、これを測定片とする。
測定片上に、この測定片よりも大きなサイズの１０ｇの
プレートを載置し、この状態下に測定片の厚さを測定す
る。測定機器には例えばダイヤルゲージ式の厚み計やレ
ーザー変位計が用いられる。このようにして測定された
値を凸状部分の厚みＴとする。The thicknesses T and T'are measured by the following method. First, regarding the thickness T, the three-dimensional sheet 20 is 50 m
It is cut into a size of m × 50 mm and used as a measurement piece.
A 10 g plate having a size larger than the measurement piece is placed on the measurement piece, and the thickness of the measurement piece is measured under this state. A dial gauge type thickness gauge or a laser displacement gauge is used as the measuring device. The value thus measured is defined as the thickness T of the convex portion.
【００２９】一方、厚みＴ’については、接合部３の大
きさと同等またはそれよりも小さいサイズの接触子を接
合部３に接触させ、１０〜４０Ｎ／ｃｍ2 の圧力を加え
た状態での厚みを測定する。このようして測定された値
を接合部３の厚みＴ’とする。測定機器には、厚みＴの
測定に用いられるものと同様のものを用いることができ
る。On the other hand, with respect to the thickness T ', the thickness in a state where a contact having a size equal to or smaller than the size of the joint 3 is brought into contact with the joint 3 and a pressure of 10 to 40 N / cm 2 is applied. To measure. The value thus measured is taken as the thickness T ′ of the joint 3. As the measuring device, the same device as that used for measuring the thickness T can be used.
【００３０】本発明で製造する立体シートは、例えば１
回あるいは数回の使用で廃棄される使い捨て物品の構成
部材として好適に使用される。特に、生理用ナプキンや
使い捨ておむつなどの使い捨て吸収性物品、掃除用ワイ
パーや対人ワイパーなどの使い捨てワイパーの構成部材
として好適である。使い捨て吸収性物品、例えば液透過
性の表面材と、液不透過性の裏面材と、両シート間に介
在された吸収体とを有する吸収性物品の構成部材として
用いる場合には、その構成部材の一部、例えば表面材、
裏面材又はサイド立体ガードの何れかの部材の一部とし
て使用される。The three-dimensional sheet produced by the present invention is, for example, 1
It is preferably used as a component of a disposable article that is discarded after being used once or several times. In particular, it is suitable as a constituent member of disposable absorbent articles such as sanitary napkins and disposable diapers, and disposable wipers such as cleaning wipers and personal wipers. When used as a constituent member of a disposable absorbent article, for example, an absorbent article having a liquid-permeable front surface material, a liquid-impermeable back surface material, and an absorber interposed between both sheets, the constituent member thereof Part of, for example surface material,
Used as part of either the backing material or side solid guard.
【００３１】また、本発明である積層体は、熱収縮性繊
維を含む熱収縮性繊維層と非熱収縮層とを積層し、両層
を接合してなる積層体であって、前記熱収縮性繊維は、
最大熱収縮応力が０．７０〜３．００ｍＮ／ｄｔｅｘで
ある積層体である。熱収縮性繊維および熱収縮性繊維層
は、前述の積層繊維集合体におけるものと同様のものが
用いられる。非熱収縮層は、前述の非熱収縮性繊維層が
用いられる他、前述の熱融着性複合繊維を有する繊維積
層体、熱融着性樹脂を含むフィルム層が挙げられる。具
体的には、吸収体や防漏シート、外層材等の吸収性物品
の構成材料が挙げられる。前記積層体は、前記熱収縮性
繊維層と前記非熱収縮層とがヒートシールや接着剤等に
より、部分的または全体的に接合されて形成される。そ
して、接合された後、前記積層体に熱収縮性繊維層に含
まれる熱収縮性繊維の熱収縮開始温度以上での熱処理が
行われる。尚、この熱処理は、前述の立体シートで用い
られた装置および方法が適宜用いられる。この熱処理に
より、熱収縮性繊維層が熱収縮し、それに伴って、非熱
収縮層が変形される。例えば、非熱収縮層は、熱収縮性
繊維層との非熱収縮層の接合部以外の部分が凸状に変形
して***したり、皺が形成されたり、また全体的に湾曲
される。本発明で製造する積層体は、使い捨て物品の構
成部材として好適に使用される。特に、生理用ナプキン
や使い捨ておむつなどの使い捨て吸収性物品、掃除用ワ
イパーや対人ワイパーなどの使い捨てワイパーの構成部
材として好適である。使い捨て吸収性物品、例えば液透
過性の表面材と、液不透過性の裏面材と、両シート間に
介在された吸収体とを有する吸収性物品の構成部材とし
て用いる場合には、身体にフィットさせるため吸収性物
品に変形を与える構成材料として用いられたり、特に熱
収縮後の熱収縮性繊維層が伸縮可能であれば、ウェスト
ギャザーや脚周りギャザーや防漏ギャザー等に好適であ
る。The laminate of the present invention is a laminate obtained by laminating a heat-shrinkable fiber layer containing heat-shrinkable fibers and a non-heat-shrinkable layer, and joining the two layers together. Sex fiber
It is a laminate having a maximum heat shrinkage stress of 0.70 to 3.00 mN / dtex. As the heat-shrinkable fiber and the heat-shrinkable fiber layer, the same ones as those in the above-mentioned laminated fiber assembly are used. As the non-heat-shrinkable layer, the above-mentioned non-heat-shrinkable fiber layer is used, as well as a fiber laminate having the above-mentioned heat-fusible composite fiber, a film layer containing a heat-fusible resin. Specific examples include constituent materials of absorbent articles such as an absorber, a leak-proof sheet, and an outer layer material. The laminate is formed by partially or wholly joining the heat-shrinkable fiber layer and the non-heat-shrinkable layer with a heat seal, an adhesive, or the like. Then, after being joined, the laminate is subjected to a heat treatment at a heat shrinkage start temperature or higher of the heat shrinkable fibers contained in the heat shrinkable fiber layer. The apparatus and method used for the above-mentioned three-dimensional sheet are appropriately used for this heat treatment. By this heat treatment, the heat-shrinkable fiber layer is heat-shrinked, and the non-heat-shrinkable layer is deformed accordingly. For example, in the non-heat-shrinkable layer, a portion other than the joint portion of the non-heat-shrinkable layer with the heat-shrinkable fiber layer is deformed into a convex shape and bulges, wrinkles are formed, or entirely curved. The laminated body manufactured by the present invention is suitably used as a constituent member of a disposable article. In particular, it is suitable as a constituent member of disposable absorbent articles such as sanitary napkins and disposable diapers, and disposable wipers such as cleaning wipers and personal wipers. When used as a constituent member of a disposable absorbent article, for example, a liquid-permeable front material, a liquid-impermeable back material, and an absorbent body interposed between both sheets, it fits to the body Therefore, it is suitable for waist gathers, gathers around legs, leak preventive gathers, etc., if it is used as a constituent material that deforms the absorbent article or if the heat-shrinkable fiber layer after heat shrinking is expandable.
【００３２】以下実施例により本発明を更に詳細に説明
する。しかし、本発明の範囲は斯かる実施例に制限され
ない。The present invention will be described in more detail with reference to the following examples. However, the scope of the invention is not limited to such embodiments.
【００３３】〔実施例１〕
（１）熱収縮性繊維層の製造。
熱収縮性繊維として潜在捲縮性の偏心芯鞘型複合繊維
（芯；ポリプロピレン（融点１５５〜１７０℃）、鞘；
エチレン・プロピレンコポリマー（融点１４０〜１５０
℃）、芯／鞘重量比＝５／５、繊度２．２ｄｔｅｘ、繊
維長５１ｍｍ、熱収縮開始温度９０℃）を用いた。この
繊維の最大熱収縮応力及び破断伸度を、それぞれ表１に
示した。この繊維を原料として、前記潜在捲縮性繊維を
繊維開繊用のカード機を用いて、繊維ウェブを製造し
た。ウェブの目付は２０ｇ／ｍ2であった。凹凸ロール
と平滑ロールからなるヒートエンボス装置を用い、加工
速度８０ｍ／ｍｉｎ、凹凸ロール温度１４５℃、平滑ロ
ール温度１４０℃、エンボス面積率２８％でヒートエン
ボス加工した。このようにして熱収縮性繊維層を得た。Example 1 (1) Production of heat-shrinkable fiber layer. Latent crimpable eccentric core-sheath type composite fiber (core; polypropylene (melting point 155 to 170 ° C.), sheath;
Ethylene / propylene copolymer (melting point 140-150
C.), core / sheath weight ratio = 5/5, fineness 2.2 dtex, fiber length 51 mm, heat shrinkage start temperature 90 ° C.). The maximum heat shrinkage stress and the breaking elongation of this fiber are shown in Table 1, respectively. Using this fiber as a raw material, the latent crimpable fiber was manufactured using a card machine for fiber opening. The fabric weight of the web was 20 g / m 2 . Heat embossing was performed at a processing speed of 80 m / min, an uneven roll temperature of 145 ° C., a smooth roll temperature of 140 ° C., and an embossed area ratio of 28% using a heat embossing device including an uneven roll and a smooth roll. In this way, a heat-shrinkable fiber layer was obtained.
【００３４】（２）非熱収縮性繊維層の製造
非熱収縮性繊維としての熱融着性繊維として大和紡績株
式会社製の芯鞘型複合繊維（商品名ＳＨ、芯；ポリエチ
レンテレフタレート（融点２５０〜２５５℃）、鞘；ポ
リエチレン（融点１２８〜１３０℃）、芯／鞘重量比＝
５／５、繊度２．２ｄｔｅｘ、繊維長５１ｍｍ）を用い
た。この繊維を原料として、繊維開繊用のカード機を用
いて、繊維ウェブを製造した。ウェブの目付は１２ｇ／
ｍ2であった。エアスルー熱処理機を用いて、１３０℃
〜１４０℃の熱風条件下で５〜２０秒間熱処理し、非熱
収縮性繊維層のエアスルー不織布を形成した。(2) Production of non-heat-shrinkable fiber layer As a heat-fusible fiber as a non-heat-shrinkable fiber, a core-sheath type composite fiber (trade name SH, core; polyethylene terephthalate (melting point 250) manufactured by Daiwa Spinning Co., Ltd. ~ 255 ° C), sheath; polyethylene (melting point 128-130 ° C), core / sheath weight ratio =
5/5, fineness 2.2 dtex, fiber length 51 mm) were used. Using this fiber as a raw material, a card machine for fiber opening was used to produce a fiber web. Web weight is 12g /
It was m 2 . Using air through heat treatment machine, 130 ℃
Heat treatment was performed for 5 to 20 seconds under hot air conditions of ~ 140 ° C to form an air-through nonwoven fabric of a non-heat-shrinkable fiber layer.
【００３５】（３）立体シート形成用の積層繊維集合体
の製造
得られた熱収縮性繊維層と非熱収縮性繊維層とを積層
し、下記条件で熱融着して一体化させた。熱収縮性繊維
層と非熱収縮性繊維層とを重ね合わせ、超音波エンボス
装置によって部分的に接合した。接合部は直径１．５ｍ
ｍの円形であり、前後左右に隣り合う各円形の中心間距
離が７ｍｍの千鳥状に配置されたドットパターンを形成
していた。得られた立体シート形成用の積層繊維集合体
における接合部の面積率は７．２％であった。(3) Manufacture of laminated fiber assembly for forming three-dimensional sheet The obtained heat-shrinkable fiber layer and non-heat-shrinkable fiber layer were laminated and heat-sealed under the following conditions to be integrated. The heat-shrinkable fiber layer and the non-heat-shrinkable fiber layer were superposed and partially bonded by an ultrasonic embossing device. Diameter of joint is 1.5m
The circles were m-shaped, and the dot patterns were arranged in a zigzag pattern in which the center-to-center distance between adjacent circles in the front, rear, left, and right was 7 mm. The area ratio of the bonded portion in the obtained laminated fiber assembly for forming a three-dimensional sheet was 7.2%.
【００３６】（４）立体シートの製造
立体シート形成用の積層繊維集合体に対して、１３０℃
±１０℃の熱風を通過させる熱処理を行い、立体シート
を得た。ここで１３０℃±１０℃の熱風とは、積層繊維
集合体に当たる前の熱風の初期温度のことであり、具体
的にはシートよりも熱風の吹き出し部に近い側に設置さ
れた温度センサーが検知する初期温度のことである。初
期温度とは、該熱処理を行った熱処理装置に、シートを
入れる直前の熱風温度のことである。(4) Manufacture of three-dimensional sheet 130 ° C. with respect to a laminated fiber assembly for forming a three-dimensional sheet
Heat treatment was performed by passing hot air of ± 10 ° C to obtain a three-dimensional sheet. Here, the hot air of 130 ° C. ± 10 ° C. refers to the initial temperature of the hot air before hitting the laminated fiber assembly, and specifically, the temperature sensor installed on the side closer to the hot air blowing section than the sheet detects. It is the initial temperature at which The initial temperature is the hot air temperature immediately before the sheet is put into the heat treatment apparatus that has performed the heat treatment.
【００３７】本実施例の複合繊維の融点は、ＪＩＳ Ｋ
７１２１に記載のプラスチックの転移温度測定方法に準
じる方法で測定した。具体的には下記の条件で測定を行
った。
・測定装置 ：セイコーインスツルメンツ株式会社製ＤＳＣ６２００
・サンプル重量 ：１．００ｍｇ±０．２０ｍｇ
・加熱速度 ：１０℃／ｍｉｎ
・窒素ガス流量 ：３０〜５０ｍｌ／ｍｉｎ
・熱収縮性偏心芯鞘型複合繊維（芯；ポリプロピレン、
鞘；エチレン・プロピレンコポリマー）の芯鞘各成分の
融点
（ポリプロピレン融点）：１５０〜１８０℃の範囲に現
れる吸熱ピークの内もっと も大きな吸熱ピークの頂点
の温度とする。
（エチレン・プロピレン・コポリマー融点）：１１０〜
１５０℃の範囲に現れる吸 熱ピークの内もっとも大き
な吸熱ピークの頂点の温度とする。
・非熱収縮性熱融着性繊維（芯；ポリエチレンテレフタ
レート、鞘；ポリエチレン）の芯鞘各成分の融点
（ポリエチレンテレフタレート融点）：２３０〜２７０
℃の範囲に現れる吸熱ピー クの内もっとも大きな吸熱
ピークの頂点の温度とする。
（ポリエチレン融点）：１１０〜１４０℃の範囲に現れ
る吸熱ピークの内もっとも 大きな吸熱ピークの頂点の
温度とする。The melting point of the composite fiber of this example is JIS K
It was measured by a method according to the method for measuring the transition temperature of plastics described in 7121. Specifically, the measurement was performed under the following conditions. -Measuring device: DSC6200 manufactured by Seiko Instruments Inc.-Sample weight: 1.00 mg ± 0.20 mg-Heating rate: 10 ° C / min-Nitrogen gas flow rate: 30-50 ml / min-Heat-shrinkable eccentric core-sheath composite fiber ( Core: polypropylene,
Melting point (polypropylene melting point) of each core-sheath component of the sheath; ethylene / propylene copolymer: The temperature at the top of the endothermic peak that is larger than the endothermic peaks appearing in the range of 150 to 180 ° C. (Ethylene propylene copolymer melting point): 110
The temperature at the top of the largest endothermic peak among the endothermic peaks appearing in the range of 150 ° C. -Meat of non-heat-shrinkable heat-fusible fiber (core; polyethylene terephthalate, sheath; polyethylene), melting point of each component (polyethylene terephthalate melting point): 230 to 270
The temperature at the top of the largest endothermic peak of the endothermic peak that appears in the range of ° C. (Polyethylene melting point): The temperature at the top of the largest endothermic peak among the endothermic peaks in the range of 110 to 140 ° C.
【００３８】〔実施例２及び比較例１，２〕非熱収縮性
繊維層の製造に用いる熱収縮性繊維を、それぞれ、表１
に示す繊度、最大収縮応力及び破断伸度のものに代えた
以外は、実施例１と同様にして、立体シート形成用の積
層繊維集合体及び立体シートの製造を行った。尚、最大
収縮応力は、主として繊維製造における延伸工程におい
て、繊維の破断伸度８０±３０％の範囲になるように、
十分コントロールがなされたかにより実施例１のものと
異なっている。[Example 2 and Comparative Examples 1 and 2] The heat-shrinkable fibers used for producing the non-heat-shrinkable fiber layer are shown in Table 1 respectively.
A laminated fiber assembly for forming a three-dimensional sheet and a three-dimensional sheet were produced in the same manner as in Example 1 except that the fineness, the maximum shrinkage stress, and the elongation at break shown in (4) were used. Incidentally, the maximum shrinkage stress is set so that the breaking elongation of the fiber is in the range of 80 ± 30% mainly in the drawing step in the fiber production.
It differs from that of Example 1 depending on whether sufficient control was performed.
【００３９】〔評価〕上記の熱処理における最大面積収
縮率及び収縮速度をそれぞれ以下のようにして算出し
て、表１に示した。また、得られた立体シートにおける
前記比Ｔ／Ｔ’を測定して表１に合わせて示した。
（１）最大面積収縮率
上述した積層繊維集合体に対する熱収縮処理において
は、次項（２）の「収縮速度」に記載の通り、熱処理前
の積層繊維集合体に対してマーキングしておくと共に、
積層集合体に対する熱処理を６０秒以上行い、熱処理を
６０秒行った時点のマーキング間距離を測定し、その測
定値（収縮後寸法）及び収縮前のマーキング間距離（収
縮前寸法）から、次式により面積収縮率を算出し、それ
を最大面積収縮率とした。
面積収縮率＝[（ＭＤ収縮前寸法×ＣＤ収縮前寸法）−
（ＭＤ収縮後寸法×ＣＤ収縮後寸法）]／（ＭＤ収縮前
寸法×ＣＤ収縮前寸法）
（２）収縮速度（面積収縮率が５０％に達するまでの熱
処理時間）
前記熱収縮処理と同時に前記立体シート形成用の積層繊
維集合体の収縮速度を測定した。収縮速度の測定方法
は、熱処理前の立体シート形成用の積層繊維集合体のＭ
Ｄ、ＣＤ方向それぞれに、一定間隔で点状のマーキング
を一対施し、これらのマーキング間距離の変化を、カメ
ラで観察、撮影し測定した。ここで収縮速度は、面積収
縮率が５０％に達するまでの熱処理の時間を求めた。な
お、ある時刻の面積収縮率は、上記ＭＤ、ＣＤのマーキ
ング間隔から下記の式によって求めた。
面積収縮率＝[（ＭＤ収縮前マーキング間隔×ＣＤ収縮
前マーキング間隔）−（ＭＤある時刻のマーキング間隔
×ＣＤある時刻のマーキング間隔）]／（ＭＤ収縮前マ
ーキング間隔×ＣＤ収縮前マーキング間隔）[Evaluation] The maximum areal shrinkage rate and shrinkage rate in the above heat treatment were calculated as follows and shown in Table 1. The ratio T / T 'of the obtained three-dimensional sheet was measured and shown in Table 1. (1) Maximum Area Shrinkage Rate In the heat shrinkage treatment for the above-mentioned laminated fiber aggregate, as described in “Shrinkage speed” in the next item (2), the laminated fiber aggregate before heat treatment is marked, and
The heat treatment for the laminated assembly is performed for 60 seconds or more, and the distance between markings at the time when the heat treatment is performed for 60 seconds is measured. From the measured value (dimension after shrinkage) and the distance between markings before shrinkage (dimension before shrinkage), Then, the area shrinkage rate was calculated by using the calculated value as the maximum area shrinkage rate. Area shrinkage rate = [(MD shrinkage dimension x CD shrinkage dimension)-
(Dimension after MD shrinkage × Dimension after CD shrinkage) / (Dimension before MD shrinkage × Dimension before CD shrinkage) (2) Shrinkage speed (heat treatment time until the area shrinkage ratio reaches 50%) Simultaneously with the heat shrinkage treatment The shrinkage rate of the laminated fiber assembly for forming a three-dimensional sheet was measured. The method of measuring the shrinkage rate is M of the laminated fiber assembly for forming a three-dimensional sheet before heat treatment.
A pair of dot-like markings were made at regular intervals in each of the D and CD directions, and changes in the distance between these markings were observed and photographed by a camera and measured. Here, as the shrinkage rate, the time of heat treatment until the area shrinkage rate reached 50% was obtained. The area shrinkage ratio at a certain time was calculated from the above MD and CD marking intervals by the following formula. Area shrinkage rate = [(MD shrinkage marking interval x CD shrinkage marking spacing)-(MD certain time marking spacing x CD certain time marking spacing)] / (MD shrinkage marking spacing x CD shrinkage marking spacing)
【００４０】[0040]
【表１】 [Table 1]
【００４１】表１に示す結果から明らかなように、実施
例の積層繊維集合体（本発明品）によれば、表面に十分
な凸状形状が形成された立体シートを、極めて短時間の
熱処理により製造することができ、安価で実用的な立体
シートが得られる。これに対して、比較例の立体シート
は、収縮速度が１０ｓｅｃ以上要するため、短時間の熱
処理により製造することが困難である。また、最大面積
収縮率も実施例に比べ小さく、６０％以下となってお
り、結果として凸部の最頂部における厚みと、接合部の
厚みの比であるＴ／Ｔ’が実施例に比べ、小さくなって
おり十分な凸状形状を形成したとは言えない。As is clear from the results shown in Table 1, according to the laminated fiber assembly of the present invention (product of the present invention), a three-dimensional sheet having a surface having a sufficient convex shape was heat treated for an extremely short time. Can be produced, and an inexpensive and practical three-dimensional sheet can be obtained. On the other hand, the three-dimensional sheet of the comparative example requires a shrinking speed of 10 seconds or more, and thus is difficult to manufacture by heat treatment for a short time. Further, the maximum area shrinkage rate is smaller than that of the example, that is, 60% or less, and as a result, T / T ', which is the ratio of the thickness at the top of the convex portion to the thickness of the joint portion, is It cannot be said that it has become small enough to form a sufficient convex shape.
【００４２】[0042]
【発明の効果】本発明によれば、熱処理により表面に十
分な凸状形状を形成させることができ、しかも前記熱処
理の工程において十分な収縮速度が得られ、熱処理時間
を短縮して立体シートの製造コストを削減することので
きる、立体シート形成用の積層繊維集合体及び該積層繊
維集合体を用いた立体シートの製造方法を提供すること
ができる。According to the present invention, a sufficient convex shape can be formed on the surface by heat treatment, a sufficient shrinkage rate can be obtained in the heat treatment step, and the heat treatment time can be shortened. It is possible to provide a laminated fiber aggregate for forming a three-dimensional sheet and a method for producing a three-dimensional sheet using the laminated fiber aggregate that can reduce the manufacturing cost.
【図１】本発明の立体シート形成用の積層繊維集合体の
一実施形態を、該積層繊維集合体を熱収縮して得られる
立体シートと共に示す模式断面図である。FIG. 1 is a schematic cross-sectional view showing an embodiment of a laminated fiber assembly for forming a three-dimensional sheet of the present invention, together with a three-dimensional sheet obtained by heat-shrinking the laminated fiber assembly.
【図２】積層繊維集合体に形成された接合部の形成パタ
ーンの例を示す平面図である。FIG. 2 is a plan view showing an example of a formation pattern of a joint portion formed in a laminated fiber assembly.
【図３】図１に示す立体シート形成用の積層繊維集合体
１０の製造工程、及び該積層繊維集合体１０に熱処理を
施して立体シート２０を得る立体シートの製造工程を連
続的に行う場合を示す概略工程図である。FIG. 3 is a case where the manufacturing process of the laminated fiber assembly 10 for forming a three-dimensional sheet shown in FIG. 1 and the manufacturing process of the three-dimensional sheet in which the three-dimensional sheet 20 is obtained by subjecting the laminated fiber assembly 10 to heat treatment are continuously performed. It is a schematic process drawing which shows.
１０ 立体シート形成用の積層繊維集合体 １ 非熱収縮性繊維層 ２ 熱収縮性繊維層 ３ 熱融着部（接合部） ４ 凸部 ２０ 立体シート 10 Laminated fiber aggregate for forming three-dimensional sheet 1 Non-heat-shrinkable fiber layer 2 Heat shrinkable fiber layer 3 Thermal fusion part (joint part) 4 convex 20 three-dimensional sheet
───────────────────────────────────────────────────── フロントページの続き (72)発明者 宮本 孝信 栃木県芳賀郡市貝町赤羽2606 花王株式会 社研究所内 (72)発明者 金田 学 栃木県芳賀郡市貝町赤羽2606 花王株式会 社研究所内 Ｆターム(参考） 4F100 AK64A AL03A BA02 BA32 DG01A DG01B DG06A DG06B DG14A DG20A EJ42 EJ422 JA03 JA03A JA03B JK08A YY00A 4L047 AA14 AA27 AB09 BA05 BA08 BA24 CA05 CA12 CA15 CA19 CC16 DA00 ─────────────────────────────────────────────────── ─── Continued front page (72) Inventor Takanobu Miyamoto Kao Stock Exchange 2606, Akabane, Kai-cho, Haga-gun, Tochigi Prefecture Company research institute (72) Inventor Manabu Kaneda Kao Stock Exchange 2606, Akabane, Kai-cho, Haga-gun, Tochigi Prefecture Company research institute F-term (reference) 4F100 AK64A AL03A BA02 BA32 DG01A DG01B DG06A DG06B DG14A DG20A EJ42 EJ422 JA03 JA03A JA03B JK08A YY00A 4L047 AA14 AA27 AB09 BA05 BA08 BA24 CA05 CA12 CA15 CA19 CC16 DA00
Claims (5)
熱収縮性繊維層とを積層し、両繊維層を部分的に接合し
てなる、立体シート形成用の積層繊維集合体であって、 前記熱収縮性繊維は、最大熱収縮応力が０．７０〜３．
００ｍＮ／ｄｔｅｘである立体シート形成用の積層繊維
集合体。1. A laminated fiber assembly for forming a three-dimensional sheet, comprising a heat-shrinkable fiber layer containing heat-shrinkable fibers and a non-heat-shrinkable fiber layer, and both fiber layers being partially joined. The heat shrinkable fiber has a maximum heat shrinkage stress of 0.70 to 3.
A laminated fiber assembly for forming a three-dimensional sheet having a density of 00 mN / dtex.
潜在捲縮性繊維であり、該潜在捲縮性繊維はエチレン−
プロピレンランダム共重合体を含む請求項１記載の立体
シート形成用の積層繊維集合体。2. The heat-shrinkable fiber is a latent crimpable fiber composed of a conjugate fiber, and the latent crimpable fiber is ethylene-
The laminated fiber assembly for forming a three-dimensional sheet according to claim 1, comprising a propylene random copolymer.
熱収縮性繊維層とを積層し、両繊維層を部分的に接合し
てなる、立体シート形成用の積層繊維集合体であり、前
記熱収縮性繊維は、最大熱収縮応力が０．７０〜３．０
０ｍＮ／ｄｔｅｘである立体シート形成用の積層繊維集
合体に、 前記熱収縮性繊維の収縮開始温度以上の温度の熱処理を
施し前記熱収縮性繊維層を熱収縮させることによって、
前記非熱収縮性繊維層における前記熱収縮性繊維層との
接合部以外の部分が凸状に***した立体シートを得る立
体シートの製造方法。3. A laminated fiber assembly for forming a three-dimensional sheet, comprising a heat-shrinkable fiber layer containing heat-shrinkable fibers and a non-heat-shrinkable fiber layer, and the two fiber layers are partially joined. And the heat shrinkable fiber has a maximum heat shrinkage stress of 0.70 to 3.0.
A laminated fiber assembly for forming a three-dimensional sheet having a density of 0 mN / dtex is subjected to heat treatment at a temperature equal to or higher than the shrinkage start temperature of the heat-shrinkable fiber to heat-shrink the heat-shrinkable fiber layer,
A method for producing a three-dimensional sheet, wherein a three-dimensional sheet is obtained in which a portion of the non-heat-shrinkable fiber layer other than a joint with the heat-shrinkable fiber layer is raised in a convex shape.
縮前後の面積収縮率が５０％以上であり、且つ面積収縮
率５０％に達するまでの熱処理時間が２〜１０秒である
請求項３記載の立体シートの製造方法。4. The heat treatment has an area shrinkage ratio of 50% or more before and after shrinkage of the heat shrinkable fiber layer, and a heat treatment time of 2 to 10 seconds until the area shrinkage ratio reaches 50%. 3. The method for producing a three-dimensional sheet according to item 3.
熱収縮層とを積層し、両層を接合してなる積層体であっ
て、前記熱収縮性繊維は、最大熱収縮応力が０．７０〜
３．００ｍＮ／ｄｔｅｘである積層体。5. A laminate obtained by laminating a heat-shrinkable fiber layer containing heat-shrinkable fibers and a non-heat-shrinkable layer, and joining both layers, wherein the heat-shrinkable fiber has a maximum heat-shrinkable stress. Is 0.70
Laminate that is 3.00 mN / dtex.