JP2003276002A - Manufacturing method for artificial veneer - Google Patents
Manufacturing method for artificial veneerInfo
- Publication number
- JP2003276002A JP2003276002A JP2002084769A JP2002084769A JP2003276002A JP 2003276002 A JP2003276002 A JP 2003276002A JP 2002084769 A JP2002084769 A JP 2002084769A JP 2002084769 A JP2002084769 A JP 2002084769A JP 2003276002 A JP2003276002 A JP 2003276002A
- Authority
- JP
- Japan
- Prior art keywords
- veneer
- grain pattern
- artificial
- wood
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、人工単板の製造方
法に関するものである。TECHNICAL FIELD The present invention relates to a method for manufacturing an artificial veneer.
【０００２】[0002]
【従来の技術】従来より、広葉樹木材類似の柄を有する
人工単板の製造方法として、色調の異なる二種類の木質
単板とを交互に組み合わせて積層した後、金型中で湾
曲、一体成形して集成フリッチとし、この集成フリッチ
をスライスする人工単板の製造方法が知られている。2. Description of the Related Art Conventionally, as a method of manufacturing an artificial veneer having a pattern similar to that of hardwood, two types of veneer of different colors are alternately combined and laminated, and then curved and integrally molded in a mold. There is known a method of manufacturing an artificial veneer by slicing the flitch, which is obtained by slicing the flitch.
【０００３】しかし、かかる方法では、木目と木目の間
に所謂”あて目（木目と木目の間に存在する淡い木目模
様）”を有する樹種（例えば、ケヤキ、カバ等）の柄が
充分に表現できないという問題点があった。However, in such a method, the pattern of a tree species (for example, zelkova, hippopotamus, etc.) having a so-called "red eye (a pale wood grain pattern existing between the wood grain)" between the wood grains is sufficiently expressed. There was a problem that it could not be done.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、上記事由に
鑑みてなされたもので、その目的とするところは、上記
の”あて目”を有する樹種の柄をも表現可能な人工単板
の製造方法を提供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and an object of the present invention is to provide an artificial veneer capable of expressing a handle of a tree species having the above "eyes". It is to provide a manufacturing method.
【０００５】[0005]
【課題を解決するための手段】上記課題を解決するため
に、請求項１に係る発明の人工単板の製造方法にあって
は、非木目柄表現用単板と、木目柄表現用単板とを交互
に組み合わせて積層した後、金型中で湾曲、一体成形し
て集成フリッチとし、この集成フリッチをスライスする
人工単板の製造方法であって、前記非木目柄表現用単板
を、脱色後、染色した木質単板を複数枚積層した後、金
型中で湾曲、一体成形して形成した集成フリッチをスラ
イスすることによって形成することを特徴とするもので
ある。In order to solve the above problems, in a method for manufacturing an artificial veneer according to a first aspect of the present invention, a non-grain pattern expressing veneer and a grain pattern expressing veneer are provided. After alternately laminating and laminating, curved in a mold, integrally molded into a laminated flitch, which is a method of manufacturing an artificial veneer to slice the laminated flitch, the non-grain pattern expressing veneer, After bleaching, a plurality of dyed wood veneers are laminated, and then the flitch is formed by bending and integrally molding in a mold and slicing.
【０００６】請求項２に係る発明の人工単板の製造方法
にあっては、請求項１記載の人工単板の製造方法におい
て、前記非木目柄表現用単板を製造する金型と、前記人
工単板を製造する金型が同一であることを特徴とするも
のである。According to a second aspect of the present invention, there is provided a method for producing an artificial veneer according to the first aspect, wherein the die for producing the non-woodgrain pattern expressing veneer is the mold. It is characterized in that the molds for producing the artificial veneer are the same.
【０００７】請求項３に係る発明の人工単板の製造方法
にあっては、請求項１または請求項２記載の人工単板の
製造方法において、前記複数枚積層した木質単板が、総
て同一厚みであり、且つ、前記非木目柄表現用単板の厚
みが、前記木質単板の厚みと略同一であることを特徴と
するものである。In the method for manufacturing an artificial veneer of the invention according to claim 3, in the method for manufacturing an artificial veneer according to claim 1 or 2, all of the plurality of laminated wood veneers are The non-wood grain pattern expressing veneer has the same thickness and the thickness is substantially the same as that of the wood veneer.
【０００８】請求項４に係る発明の人工単板の製造方法
にあっては、請求項１乃至請求項３のいずれかに記載の
人工単板の製造方法において、前記木目柄表現用単板
が、着色木質単板を、複数枚積層した後、金型中で湾
曲、一体成形して集成フリッチとし、この集成フリッチ
をスライスすることによって形成することを特徴とする
ものである。According to a fourth aspect of the present invention, there is provided a method for producing an artificial veneer according to any one of the first to third aspects, wherein the veneer for expressing a wood grain pattern is The present invention is characterized in that a plurality of colored wood veneers are laminated, then curved and integrally molded in a mold to form an assembled flitch, and the assembled flitch is sliced to form.
【０００９】[0009]
【発明の実施の形態】以下、本発明の実施形態を図面に
基づき説明する。尚、本発明に係る人工単板の製造方法
は、下記の実施形態にのみ限定されるものではなく、本
発明の要旨を逸脱しない範囲内において種々変更を加え
得ることは勿論である。ここで、図１は、本発明の人工
単板の製造方法の典型的な実施形態における第１の段階
の概略を示す図である。さらに、図２は、本発明の人工
単板の製造方法の典型的な実施形態における第２の段階
の概略を示す図である。図３は、本発明の人工単板の製
造方法における第２の段階において第１の段階において
使用した金型２と異なる金型（金型２よりも内面の曲率
が小さいもの）を用いて製造した人工単板７ａにおいて
形成される不自然な”木目柄”模様を模式的に示す図で
ある。図４は、本発明の人工単板の製造方法において使
用できる木目柄表現用単板５の製造方法の一例を示す図
である。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below with reference to the drawings. The method for manufacturing an artificial veneer according to the present invention is not limited to the following embodiments, and it goes without saying that various modifications can be made without departing from the scope of the present invention. Here, FIG. 1 is a diagram showing an outline of a first stage in a typical embodiment of the method for manufacturing an artificial veneer of the present invention. Further, FIG. 2 is a diagram showing an outline of the second step in an exemplary embodiment of the method for manufacturing an artificial veneer of the present invention. FIG. 3 is manufactured by using a mold different from the mold 2 used in the first step in the second step of the method for manufacturing an artificial veneer of the present invention (one having a smaller inner surface curvature than the mold 2). It is a figure which shows typically the unnatural "wood pattern" pattern formed in the artificial veneer 7a. FIG. 4 is a diagram showing an example of a method for manufacturing the wood grain pattern expressing veneer 5 that can be used in the method for manufacturing an artificial veneer of the present invention.
【００１０】即ち、本実施形態の人工単板の製造方法に
おいては、まず、図１に示すように、例えば、広葉樹等
の木質素材よりなる木質単板（図示せず）を、脱色後、
染色して、染色単板１とし、これに接着剤を塗布して複
数枚積層した後、上型２ａ、下型２ｂよりなる金型２の
中で湾曲、一体成形して集成フリッチ３を形成する。さ
らに、この集成フリッチ３をスライスすることによって
非木目柄表現用単板４を形成する。この場合において、
染色単板１における染色の色調は、後述する目的の人工
単板７の色調に合わせることができる。また、染色単板
１の厚みは、木質単板の上記染色の均一性の確保とハン
ドリングの容易さを考慮すると０.７〜１.２ｍｍ程度
が、好適であると考えられるが、かかる範囲にのみ限定
されるものではなく、上記課題解決に寄与し得る限りに
おいて、何ら制限がないことはいうまでもない。That is, in the method for manufacturing an artificial veneer of the present embodiment, first, as shown in FIG. 1, a wood veneer (not shown) made of a wood material such as a hardwood is decolorized,
The dyed veneer 1 is dyed, an adhesive is applied to the dyed veneer 1 and a plurality of the dyed veneers 1 are laminated, and then curved and integrally molded in a mold 2 including an upper mold 2a and a lower mold 2b to form an assembled flitch 3. To do. Further, the laminated flitch 3 is sliced to form the non-grain pattern expressing veneer 4. In this case,
The color tone of the dyeing veneer 1 can be matched with the color tone of the artificial veneer 7 for the purpose described later. Further, the thickness of the dyed veneer 1 is considered to be preferably about 0.7 to 1.2 mm, considering the uniformity of the dyeing of the wood veneer and the ease of handling, but in such a range It is needless to say that there is no limitation as long as it can contribute to solving the above problems.
【００１１】次に、図２に示すように、この非木目柄表
現用単板４と、別途製造した木目柄表現用単板５とを、
両者の界面に接着剤を塗布して複数枚積層した後、非木
目柄表現用単板４の製造に使用したものと同一の金型、
即ち、上型２ａ、下型２ｂよりなる金型２の中で湾曲、
一体成形して集成フリッチ６を形成する。さらに、この
集成フリッチ６をスライスすることによって目的の人工
単板７を得るというものである。このようにして製造し
た人工単板７は、非木目柄表現用単板４と、木目柄表現
用単板５とによって構成される木目柄と併せて、非木目
柄表現用単板４よりなる相の中に、図１に示す工程で使
用した接着剤よりなる層が、上述の所謂”あて目”に該
当する淡い木目模様を形成し、このような”あて目”を
有する樹種等の多様な柄を有する人工単板が製造できる
こととなる。Next, as shown in FIG. 2, the non-wood grain pattern expressing veneer 4 and the separately produced wood grain pattern expressing veneer 5 are
The same mold as that used for manufacturing the non-wood grain pattern expressing veneer 4 after applying an adhesive agent on the interface between the two and laminating a plurality of sheets,
That is, in the mold 2 including the upper mold 2a and the lower mold 2b, a curve,
The integrated flitch 6 is formed by integrally molding. Further, the target artificial veneer 7 is obtained by slicing the assembled flitch 6. The artificial veneer 7 manufactured in this manner is composed of the non-wood grain pattern expressing veneer 4 together with the wood grain pattern constituted by the non-wood grain pattern expressing veneer 4 and the wood grain pattern expressing veneer 5. In the phase, the layer made of the adhesive used in the step shown in FIG. 1 forms a pale wood grain pattern corresponding to the so-called "address", and various kinds of tree species having such "address" An artificial veneer having a different handle can be manufactured.
【００１２】この場合、図１に示す工程において、複数
枚積層した染色単板１を、総て同一厚みとし、且つ、図
２に示す工程において、非木目柄表現用単板４の厚み
が、前記木質単板の厚みと略同一とすることにより、上
記の所謂”あて目”に該当する淡い木目模様をよりリア
ルな略等間隔に形成することができることとなる。In this case, in the process shown in FIG. 1, all of the dyed veneers 1 laminated are made to have the same thickness, and in the process shown in FIG. 2, the thickness of the non-grain pattern expressing veneer 4 is By making the thickness of the wood veneer substantially the same, it is possible to form lighter wood grain patterns corresponding to the so-called "eyes" at more realistic and substantially equal intervals.
【００１３】一方、図２に示す工程においては、非木目
柄表現用単板４と、木目柄表現用単板５とを、両者の界
面に接着剤を塗布して複数枚積層した後、湾曲、一体成
形して集成フリッチ６を形成する際に、非木目柄表現用
単板４の製造に使用したものと同一の金型２を使用する
ことが重要である。即ち、こうすることにより、上記の
所謂”あて目”に該当する淡い木目模様と前記木目柄表
現用単板５により形成される”木目柄”が略平行に並ん
で形成でき、より天然木材の木目模様に近似した模様が
形成できるからである。これに対して、この場合におい
て、異なる金型、例えば、金型２よりも内面の曲率が小
さいものを使用すると、図３に示す人工単板７ａのよう
に、上記の所謂”あて目”に該当する淡い木目模様と前
記木目柄表現用単板５により形成される”木目柄”が交
錯する不自然な木目となってしまう。On the other hand, in the process shown in FIG. 2, the non-wood grain pattern expressing veneer 4 and the wood grain pattern expressing veneer 5 are coated with an adhesive at the interface between the two and laminated, and then curved. When forming the integrated flitch 6 by integrally molding, it is important to use the same mold 2 as that used for manufacturing the non-grain pattern expressing veneer 4. That is, by doing so, the light grain pattern corresponding to the so-called "reverse eye" and the "grain pattern" formed by the veneer for expressing the grain pattern 5 can be formed substantially parallel to each other, and a more natural wood This is because a pattern similar to a wood grain pattern can be formed. On the other hand, in this case, if a different mold, for example, a mold whose inner surface has a curvature smaller than that of the mold 2, is used, the artificial veneer 7a shown in FIG. An unnatural wood grain is formed by the intersection of the corresponding light wood grain pattern and the "wood grain pattern" formed by the wood grain pattern expressing veneer 5.
【００１４】一方、上記の木目柄表現用単板５の製造方
法には、特に制限はなく、非木目柄表現用単板４に比較
して、より濃厚に染色されており、非木目柄表現用単板
４との色調の対比により、”木目柄”が表現できれば充
分であり、上記課題解決に寄与し得る限りにおいて、何
ら制限がないことはいうまでもないが、例えば、図１に
示した非木目柄表現用単板４を製造する方法と同様にし
て、着色単板８（染色単板１と同様に製造可能である
が、染色の程度がより濃厚である。）に接着剤を塗布し
て複数枚積層した後、上型９ａ、下型９ｂよりなる金型
９の中で湾曲、一体成形して集成フリッチ１０を形成し
た後、これをスライスすることによって木目柄表現用単
板５を形成する（図４）ことも可能であり、これによ
り、”木目柄”を形成する天然木の”集中導管部”の微
妙な外観を表現することが可能となり、製造した人工単
板７の木目柄全体が、より天然木に近似した外観を有す
ることとなる。この場合、スライスして形成する木目柄
表現用単板５の厚みについても、非木目柄表現用単板４
との色調の対比により、自然な”木目柄”が表現できれ
ば充分であり、特に限定はされないが、自然な”木目
柄”を表現するという観点に立てば、上記非木目柄表現
用単板４の厚みが、染色単板１の厚みと略同一の０.７
〜１.２ｍｍ程度の厚みである場合を想定すると０.０５
〜０.３ｍｍ程度が、好適であると考えられる。但し、
これについてもかかる範囲にのみ限定されるものではな
く、上記課題解決に寄与し得る限りにおいて、何ら制限
がないことはいうまでもない。On the other hand, the method for producing the veneer 5 for expressing the wood grain pattern is not particularly limited, and is dyed more densely than the veneer 4 for expressing the non-grain pattern, and the non-grain pattern expression is performed. It is sufficient if the "wood grain pattern" can be expressed by comparing the color tone with the veneer 4 for use, and it goes without saying that there is no limitation as long as it can contribute to the solution of the above problems. An adhesive is applied to the colored veneer 8 (which can be produced in the same manner as the dyed veneer 1 but the degree of dyeing is higher) in the same manner as the method for producing the non-wood grain pattern expressing veneer 4 described above. After coating and laminating a plurality of sheets, the laminated flitch 10 is formed by curving and integrally molding in a mold 9 composed of an upper mold 9a and a lower mold 9b, and then slicing this to produce a wood grain pattern expressing veneer. It is also possible to form 5 (Fig. 4), which forms a "wood pattern". That of natural wood it is possible to express subtle appearance of "centralized conduit portion", whole grain pattern of the artificial veneer 7 was manufactured, and have an appearance that approximates a more natural wood. In this case, the thickness of the wood veneer pattern expressing veneer 5 formed by slicing is also the same as that of the non-wood pattern expressing veneer 4.
It is sufficient if a natural "wood grain pattern" can be expressed by contrasting the color tone with, and it is not particularly limited, but from the viewpoint of expressing a natural "wood grain pattern", the above-mentioned non-wood grain pattern expressing veneer 4 The thickness of the dyed veneer 1 is about 0.7
Assuming a thickness of about 1.2 mm, 0.05
It is considered that about 0.3 mm is suitable. However,
It is needless to say that this is not limited to such a range and there is no limitation as long as it can contribute to the solution of the above problems.
【００１５】[0015]
【発明の効果】以上のように、請求項１に係る発明の人
工単板の製造方法にあっては、非木目柄表現用単板と、
木目柄表現用単板とを交互に組み合わせて積層した後、
金型中で湾曲、一体成形して集成フリッチとし、この集
成フリッチをスライスする人工単板の製造方法であっ
て、前記非木目柄表現用単板を、脱色後、染色した木質
単板を複数枚積層した後、金型中で湾曲、一体成形して
形成した集成フリッチをスライスすることによって形成
することを特徴とするので、所謂”あて目”を有する樹
種等の多様な柄を有する人工単板が製造できるという優
れた効果を奏する。As described above, in the method for manufacturing an artificial veneer according to the first aspect of the present invention, a veneer for expressing a non-grain pattern,
After alternately combining and laminating with wood grain pattern expressing veneer,
A method of manufacturing an artificial veneer that is curved in a mold and integrally molded to form a laminated flitch, and slices the laminated flitch, wherein the non-wood grain pattern expressing veneer is decolorized, and then a plurality of dyed wooden veneers are used. It is characterized in that it is formed by slicing laminated flitch formed by bending and integrally molding in a mold after laminating the sheets, so that an artificial monolith having various patterns such as tree species having so-called "eyes" It has an excellent effect that a plate can be manufactured.
【００１６】請求項２に係る発明の人工単板の製造方法
にあっては、請求項１記載の人工単板の製造方法におい
て、前記非木目柄表現用単板を製造する金型と、前記人
工単板を製造する金型が同一であることを特徴とするの
で、請求項１記載の人工単板の製造方法の発明の効果に
加えて、所謂”あて目”に該当する淡い木目模様と前記
木目柄表現用単板により形成される”木目柄”が略平行
に並んで形成でき、より天然木材の木目模様に近似した
模様が形成できるという優れた効果を奏する。According to a second aspect of the present invention, there is provided a method for producing an artificial veneer according to the first aspect, wherein the die for producing the non-woodgrain pattern expressing veneer is the mold. Since the molds for producing the artificial veneer are the same, in addition to the effect of the invention of the method for producing an artificial veneer according to claim 1, a light wood grain pattern corresponding to a so-called "heading" is obtained. The "wood grain pattern" formed by the wood grain pattern expressing single plate can be formed substantially parallel to each other, and an excellent effect that a pattern more similar to the wood grain pattern of natural wood can be formed.
【００１７】請求項３に係る発明の人工単板の製造方法
にあっては、請求項１または請求項２記載の人工単板の
製造方法において、前記複数枚積層した木質単板が、総
て同一厚みであり、且つ、前記非木目柄表現用単板の厚
みが、前記木質単板の厚みと略同一であることを特徴と
するので、請求項１または請求項２記載の人工単板の製
造方法の発明の効果に加えて、所謂”あて目”に該当す
る淡い木目模様をよりリアルな略等間隔に形成できると
いう優れた効果を奏する。In the method for manufacturing an artificial veneer according to the third aspect of the present invention, in the method for manufacturing an artificial veneer according to claim 1 or 2, all of the wood veneers laminated are laminated. The artificial veneer according to claim 1 or claim 2, which has the same thickness, and the thickness of the non-wood grain pattern expressing veneer is substantially the same as the thickness of the wood veneer. In addition to the effect of the invention of the manufacturing method, there is an excellent effect that light woodgrain patterns corresponding to so-called "eyes" can be formed at more realistic and substantially equal intervals.
【００１８】請求項４に係る発明の人工単板の製造方法
にあっては、請求項１乃至請求項３のいずれかに記載の
人工単板の製造方法において、前記木目柄表現用単板
が、着色木質単板を、複数枚積層した後、金型中で湾
曲、一体成形して集成フリッチとし、この集成フリッチ
をスライスすることによって形成することを特徴とする
ので、請求項１乃至請求項３のいずれかに記載の人工単
板の製造方法の発明の効果に加えて、製造した人工単板
の木目柄全体が、より天然木に近似した外観を有すると
いう優れた効果を奏する。According to a fourth aspect of the invention, there is provided a method for producing an artificial veneer according to any one of the first to third aspects, wherein the veneer for expressing a wood grain pattern is The laminated wood veneer is laminated by laminating a plurality of colored wood veneers, and then curved and integrally molded in a mold to form an assembled flitch, and the assembled flitch is sliced to be formed. In addition to the effect of the invention of the method for producing an artificial veneer according to any one of 3), the entire grain pattern of the produced artificial veneer has an excellent effect that the appearance is more similar to natural wood.
【図１】本発明の人工単板の製造方法の典型的な実施形
態における第１の段階の概略を示す図である。FIG. 1 is a diagram schematically showing a first step in an exemplary embodiment of the method for manufacturing an artificial veneer of the present invention.
【図２】本発明の人工単板の製造方法の典型的な実施形
態における第２の段階の概略を示す図である。FIG. 2 is a diagram schematically showing a second step in an exemplary embodiment of the method for manufacturing an artificial veneer of the present invention.
【図３】本発明の人工単板の製造方法における第２の段
階において第１の段階において使用した金型と異なる金
型を用いて製造した人工単板において形成される不自然
な”木目柄”模様を模式的に示す図である。FIG. 3 is an unnatural “wood grain pattern formed in an artificial veneer manufactured using a mold different from the mold used in the first step in the second step of the method for manufacturing an artificial veneer of the present invention. It is a figure which shows a pattern typically.
【図４】本発明の人工単板の製造方法において使用でき
る木目柄表現用単板の製造方法の一例を示す図である。FIG. 4 is a diagram showing an example of a method for producing a wood grain pattern expressing veneer that can be used in the method for producing an artificial veneer of the present invention.
【符号の説明】 １ 染色単板 ２ 金型 ２ａ 上型 ２ｂ 下型 ３ 集成フリッチ ４ 非木目柄表現用単板 ５ 木目柄表現用単板 ６ 集成フリッチ ７ 人工単板 ７ａ 人工単板 ８ 着色単板 ９ 金型 ９ａ 上型 ９ｂ 下型 １０ 集成フリッチ[Explanation of symbols] 1 dyed veneer 2 mold 2a Upper mold 2b Lower mold 3 integrated flitch 4 Non-grain pattern expression veneer 5 Veneer for wood grain pattern expression 6 integrated flitch 7 artificial veneer 7a artificial veneer 8 colored veneer 9 mold 9a Upper mold 9b Lower mold 10 assembled flitch
───────────────────────────────────────────────────── フロントページの続き (72)発明者 宮地 陽平 大阪府門真市大字門真1048番地松下電工株 式会社内 Ｆターム(参考） 2B002 AC02 AC07 AC11 AC12 BA01 BA06 BA08 BA10 BB02 BB06 2B200 AA07 BA01 BA04 DA04 EA06 EE13 EF11 FA24 FA31 2B230 AA23 BA03 BA04 BA17 BA18 EA07 EA15 EB03 EB05 EB13 EB28 EB29 EC24 2B242 BA11 BA13 BA19 BA25 ─────────────────────────────────────────────────── ─── Continued front page (72) Inventor Yohei Miyaji 1048, Kadoma, Kadoma-shi, Osaka Matsushita Electric Works Co., Ltd. Inside the company F term (reference) 2B002 AC02 AC07 AC11 AC12 BA01 BA06 BA08 BA10 BB02 BB06 2B200 AA07 BA01 BA04 DA04 EA06 EE13 EF11 FA24 FA31 2B230 AA23 BA03 BA04 BA17 BA18 EA07 EA15 EB03 EB05 EB13 EB28 EB29 EC24 2B242 BA11 BA13 BA19 BA25
Claims (4)
とを交互に組み合わせて積層した後、金型中で湾曲、一
体成形して集成フリッチとし、この集成フリッチをスラ
イスする人工単板の製造方法であって、前記非木目柄表
現用単板を、脱色後、染色した木質単板を複数枚積層し
た後、金型中で湾曲、一体成形して形成した集成フリッ
チをスライスすることによって形成することを特徴とす
る人工単板の製造方法。1. A non-wood grain pattern expressing veneer and a wood grain pattern expressing veneer are alternately combined and laminated, and then curved and integrally molded in a mold to form an integrated flitch, and the integrated flitch is sliced. A method for manufacturing an artificial veneer, wherein the non-wood grain pattern expressing veneer is decolorized, laminated with a plurality of dyed wood veneers, and then curved in a mold to form an integrated flitch. A method for manufacturing an artificial veneer characterized by being formed by slicing.
と、前記人工単板を製造する金型が同一であることを特
徴とする請求項１記載の人工単板の製造方法。2. The method for producing an artificial veneer according to claim 1, wherein the die for producing the veneer for expressing the non-grain pattern is the same as the die for producing the artificial veneer.
厚みであり、且つ、前記非木目柄表現用単板の厚みが、
前記木質単板の厚みと略同一であることを特徴とする請
求項１または請求項２記載の人工単板の製造方法。3. The laminated wood veneers have the same thickness, and the thickness of the non-grain pattern expressing veneer is:
The method for producing an artificial veneer according to claim 1 or 2, wherein the thickness is substantially the same as the thickness of the wood veneer.
を、複数枚積層した後、金型中で湾曲、一体成形して集
成フリッチとし、この集成フリッチをスライスすること
によって形成することを特徴とする請求項１乃至請求項
３のいずれかに記載の人工単板の製造方法。4. The wood grain pattern expressing veneer is formed by laminating a plurality of colored veneer veneers, bending them in a mold, and integrally molding the veneer to form an integrated flitch, and slicing the integrated flitch. The method for producing an artificial veneer according to any one of claims 1 to 3, characterized in that.