JP2003273575A - Electromagnetic wave shielding material and manufacturing method of the same - Google Patents
Electromagnetic wave shielding material and manufacturing method of the sameInfo
- Publication number
- JP2003273575A JP2003273575A JP2002071457A JP2002071457A JP2003273575A JP 2003273575 A JP2003273575 A JP 2003273575A JP 2002071457 A JP2002071457 A JP 2002071457A JP 2002071457 A JP2002071457 A JP 2002071457A JP 2003273575 A JP2003273575 A JP 2003273575A
- Authority
- JP
- Japan
- Prior art keywords
- electromagnetic wave
- wave shielding
- shielding material
- aluminum
- aluminum foil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、アルミニウム箔製
の電磁波シールド材に関する。TECHNICAL FIELD The present invention relates to an electromagnetic wave shielding material made of aluminum foil.
【０００２】[0002]
【従来の技術】近年、電磁波による電子機器の誤動作や
人体に対する影響等が大きな問題となってきており、電
磁波シールド技術が求められている。従来、電磁波シー
ルド材としては、アルミニウム箔等の金属箔がよく用い
られている。しかしながら、例えば電子レンジの窓やプ
ラズマディスプレーのフィルターのように、透視性が要
求される場合は、金属箔は用いることができない。2. Description of the Related Art In recent years, electromagnetic waves have become a serious problem such as malfunctions of electronic devices and effects on the human body, and electromagnetic wave shield technology is required. Conventionally, a metal foil such as an aluminum foil is often used as an electromagnetic wave shield material. However, when transparency is required, such as a window of a microwave oven or a filter of a plasma display, the metal foil cannot be used.
【０００３】電子レンジの場合は電磁波シールド材とし
てパンチングメタルが用いられることが多い。しかしな
がら、パンチングメタルはある程度の厚さと重量を有す
るという欠点がある。特開２０００−２８５９２６号に
は多数のメッシュ孔を備えた電解箔の電磁波シールド材
が開示されている。しかしながら、電解箔は大掛かりな
製造装置を必要とし、コスト的に高いものとなる上、比
重の大きな銅やニッケルに限られ、アルミニウム箔では
製造できない。In the case of a microwave oven, punching metal is often used as an electromagnetic wave shield material. However, punching metal has the disadvantage of having a certain thickness and weight. Japanese Patent Laid-Open No. 2000-285926 discloses an electromagnetic wave shield material for an electrolytic foil provided with a large number of mesh holes. However, the electrolytic foil requires a large-scale manufacturing apparatus, is costly, and is limited to copper or nickel having a large specific gravity, and cannot be manufactured using an aluminum foil.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的は、アル
ミニウム箔を用いた、軽量で透視性を有する電磁波シー
ルド材を提供することである。SUMMARY OF THE INVENTION An object of the present invention is to provide a light-weight and transparent electromagnetic wave shielding material using aluminum foil.
【０００５】[0005]
【課題を解決するための手段】本発明者は鋭意検討の結
果、アルミニウム箔にエッチングにより多数の開口を設
けることにより、上記の目的を達成できることを見出
し、本発明を完成した。即ち、本発明は以下のとおりで
ある。
１．エッチングにより得られた多数の開口を有するアル
ミニウム製電磁波シールド材、
２．アルミニウムの厚さが０．３ｍｍ以下である前記１
の電磁波シールド材、
３．片面に着色層を有してなる前記１又は２の電磁波シ
ールド材、
４．着色層がカーボンブラックまたはフェライトを含有
する前記３の電磁波シールド材、
５．少なくとも片面に樹脂層を有してなる前記１〜４の
いずれか１の電磁波シールド材、
６．粘着剤層を有する前記１〜５のいずれか１の電磁波
シールド材、
７．開口の径がシールド対象となる電磁波の波長の１／
５０以下である前記１〜６のいずれか１項の電磁波シー
ルド材、
８．開口率が２０〜８０％である前記１〜７のいずれか
１の電磁波シールド材。
９．アルミニウム箔と樹脂のラミネート材のアルミニウ
ム面をエッチングレジストにより開口部を残してマスキ
ングした後、エッチングすることを特徴とするアルミニ
ウム製電磁波シールド材の製造方法。As a result of intensive studies, the present inventor has found that the above object can be achieved by providing a large number of openings in an aluminum foil by etching, and completed the present invention. That is, the present invention is as follows. 1. 1. An aluminum electromagnetic wave shielding material having a large number of openings obtained by etching, 1 in which the thickness of aluminum is 0.3 mm or less
Electromagnetic wave shield material, 3. The electromagnetic wave shielding material according to 1 or 2 above, which has a colored layer on one surface thereof; 4. The electromagnetic wave shielding material as described in 3 above, wherein the colored layer contains carbon black or ferrite. 5. The electromagnetic wave shielding material according to any one of 1 to 4 above, which has a resin layer on at least one surface thereof; 6. The electromagnetic wave shielding material according to any one of 1 to 5 above, which has an adhesive layer. The diameter of the aperture is 1 / the wavelength of the electromagnetic wave to be shielded
7. The electromagnetic wave shielding material according to any one of 1 to 6 above, which is 50 or less. The electromagnetic wave shielding material according to any one of 1 to 7 above, which has an aperture ratio of 20 to 80%. 9. A method for producing an electromagnetic wave shielding material made of aluminum, which comprises masking the aluminum surface of a laminate material of aluminum foil and resin with an etching resist leaving an opening, and then etching.
【０００６】[0006]
【発明の実施の形態】本発明のアルミニウム製電磁波シ
ールド材における開口の形状は、円形、三角形、長方
形、その他の多角形が例示でき、円形、二等辺三角形、
正三角形、正方形、長方形、菱形、正六角形が好まし
く、円形が特に好ましい。アルミニウムの厚さは０．３
ｍｍ以下が好ましい。開口率は、２０〜８０％が好まし
い。ここで開口率とは、開口面積の開口部分を含む全電
磁波シールド材面積に対する割合である。開口径はシー
ルド対象となる電磁波の波長の１／５０以下が好まし
い。ただし、開口形状が円形以外の場合の開口径とは、
等面積の円形の径とする。BEST MODE FOR CARRYING OUT THE INVENTION The shape of the opening in the aluminum electromagnetic wave shielding material of the present invention can be exemplified by circle, triangle, rectangle and other polygons, such as circle, isosceles triangle,
A regular triangle, a square, a rectangle, a rhombus, and a regular hexagon are preferable, and a circle is particularly preferable. Aluminum has a thickness of 0.3
mm or less is preferable. The aperture ratio is preferably 20 to 80%. Here, the opening ratio is the ratio of the opening area to the total electromagnetic wave shielding material area including the opening portion. The opening diameter is preferably 1/50 or less of the wavelength of the electromagnetic wave to be shielded. However, the opening diameter when the opening shape is not circular is
The diameter should be a circle with the same area.
【０００７】図１は本発明の電磁波シールド材の一態様
を表した断面図である。１は開口２を有するアルミニウ
ム箔である。３はエッチングレジストを兼ねた着色層で
ある。例えば、プラズマディスプレーのフィルター場合
は着色層が濃色である方が見映えがよくて好ましい。着
色層がカーボンブラックまたはフェライト粒子を含む場
合は、該カーボンブラックまたはフェライト粒子が電磁
波シールド効果に寄与し、好ましい。４は片面に設けら
れた樹脂層、５は他の面に設けられた樹脂層である。通
常、開口部においては樹脂層４と５は接着している。６
は粘着剤層である。粘着剤層６は樹脂層４の側に設けて
もよい。通常、粘着剤層の表面は剥離シートで保護し、
使用時に剥離する。粘着剤層を設けることにより、一般
消費者が手軽に電磁波をシールドすることが可能であ
る。本発明の電磁波シールド材は、これらの要素を全て
具備する必要はなく、開口を有するアルミニウム箔を最
低限の要素とする。目的に応じて樹脂層４、５、着色層
３、粘着剤層６を適宜具備させればよい。FIG. 1 is a sectional view showing an embodiment of the electromagnetic wave shield material of the present invention. 1 is an aluminum foil having an opening 2. Reference numeral 3 is a colored layer that also serves as an etching resist. For example, in the case of a plasma display filter, it is preferable that the colored layer has a dark color because the appearance is good. When the colored layer contains carbon black or ferrite particles, the carbon black or ferrite particles contribute to the electromagnetic wave shielding effect, which is preferable. Reference numeral 4 is a resin layer provided on one surface, and 5 is a resin layer provided on the other surface. Usually, the resin layers 4 and 5 are bonded to each other in the opening. 6
Is an adhesive layer. The adhesive layer 6 may be provided on the resin layer 4 side. Usually, the surface of the adhesive layer is protected with a release sheet,
Peel off when using. By providing the adhesive layer, general consumers can easily shield electromagnetic waves. The electromagnetic wave shield material of the present invention does not need to include all of these elements, and the aluminum foil having openings is the minimum element. The resin layers 4, 5, the coloring layer 3, and the pressure-sensitive adhesive layer 6 may be appropriately provided according to the purpose.
【０００８】本発明の、多数の開口を有するアルミニウ
ム製電磁波シールド材は、例えば次のようにして製造で
きる。エッチングレジストで、アルミニウム箔の一方の
面を全面マスキングし、他方の面は所望の形状の開口部
を残してマスキングする。そしてエッチングレジストを
熱や紫外線、電子線等で硬化させた後、エッチング液で
処理し、マスキングされていない部分のアルミニウム箔
を溶解する。残ったエッチングレジストは剥離剤で剥離
してもよいが、剥離しなくても差し支えない。The aluminum electromagnetic wave shield material having a large number of openings of the present invention can be manufactured, for example, as follows. One surface of the aluminum foil is entirely masked with an etching resist, and the other surface is masked leaving an opening of a desired shape. Then, after the etching resist is cured by heat, ultraviolet rays, electron beams, etc., it is treated with an etching solution to dissolve the unmasked aluminum foil. The remaining etching resist may be stripped with a stripping agent, but it does not matter if it is not stripped.
【０００９】さらに他の方法としては、アルミニウム箔
の片面全面をエッチングレジストでマスキングする代わ
りに、アルミニウム箔とポリエステル、ポリエチレン、
ポリプロピレン等のエッチング液に対する耐性を有する
フィルムやシートとの積層材を用いる。フィルムやシー
トはエッチング後に剥離して除去してもよいが、剥離し
なくても差し支えなく、剥離しない方が電磁波シールド
材としての取扱いし易く好ましい。As another method, instead of masking one surface of the aluminum foil with an etching resist, the aluminum foil and polyester, polyethylene,
A laminated material with a film or sheet having resistance to an etching solution such as polypropylene is used. The film or sheet may be peeled off and removed after etching, but it does not matter if it is not peeled off, and it is preferable not to peel off because it is easy to handle as an electromagnetic wave shielding material.
【００１０】エッチングレジストとしては、所望のパタ
ーンにマスキングでき、かつエッチング液に耐性を有す
るものであればすべて使用できる。代表的にはプリント
基板の製造において使用される各種のエッチングレジス
トインキやドライフィルムを使用することができる。エ
ッチングレジストインキとしては熱硬化性のものや紫外
線硬化性のものがよく使用される。エッチングレジスト
インキでマスキングするには代表的にはスクリーン印刷
で行うことができる。例えばアルミニウム箔の片面全面
にスクリーン印刷し、乾燥後他面に所望の形状にパター
ンをスクリーン印刷し、これをインキの性質に応じて熱
または紫外線等で処理して硬化させる。アルミニウム箔
と樹脂フィルムまたはシートの積層材を使用する場合は
片面の印刷は不要である。エッチングレジストインキと
して着色したものを用い、そのまま剥離せずに着色層と
することもできる。着色層がカーボンブラックまたはフ
ェライト粒子を含む場合は、該カーボンブラックまたは
フェライト粒子が電磁波シールド効果に寄与し、好まし
い。Any etching resist can be used as long as it can mask a desired pattern and has resistance to an etching solution. Various etching resist inks and dry films typically used in the production of printed circuit boards can be used. As the etching resist ink, a thermosetting one or an ultraviolet curable one is often used. Masking with an etching resist ink can be typically performed by screen printing. For example, screen printing is performed on the entire surface of one side of the aluminum foil, and after drying, a pattern is printed on the other side in a desired shape, and this is cured by heat or ultraviolet rays depending on the properties of the ink. When a laminate of aluminum foil and resin film or sheet is used, printing on one side is not necessary. It is also possible to use a colored etching resist ink and form a colored layer without peeling it off. When the colored layer contains carbon black or ferrite particles, the carbon black or ferrite particles contribute to the electromagnetic wave shielding effect, which is preferable.
【００１１】ドライフイルムの場合は金属箔基材の両面
に密着して貼付し、さらにその片面には所望のパターン
を描いたマスキングフィルムを密着させ、紫外線等の光
を照射し、片面は全面を、他面はパターンを硬化させ
る。ついで弱アルカリ液等で潜像を現像し、片面は全
面、他面は所望のパターンにマスキングすることができ
る。上記はエッチングレジストの代表的な例であるが、
もちろんこれらに制限されるものではない。In the case of dry film, it is adhered to both sides of a metal foil base material, and a masking film having a desired pattern is adhered to one side thereof, and the whole surface is exposed to light such as ultraviolet rays. , The other side cures the pattern. Then, the latent image can be developed with a weak alkaline solution or the like to mask the entire surface on one side and the desired pattern on the other side. The above is a typical example of the etching resist,
Of course, it is not limited to these.
【００１２】エッチング液としては、アルミニウム箔を
溶解し、エッチングレジストを溶解しないものであれば
よく、例えば塩化第二鉄や塩化第二銅の溶液、塩酸等の
酸性溶液や、エッチングレジストがアルカリ耐性の場合
は苛性ソーダ溶液等のアルカリ溶液も使用することがで
きる。エッチング後、残ったレジストインキはそのまま
にしてもよいし、剥離してもよい。剥離する場合はエッ
チングレジストに適した剥離液を適宜用いればよく、苛
性ソーダ等のアルカリ溶液がよく用いられる。Any etching solution may be used as long as it dissolves the aluminum foil and does not dissolve the etching resist. For example, a solution of ferric chloride or cupric chloride, an acidic solution such as hydrochloric acid, or an etching resist having an alkali resistance. In this case, an alkaline solution such as a caustic soda solution can also be used. After etching, the remaining resist ink may be left as it is or may be peeled off. When stripping, a stripping solution suitable for the etching resist may be appropriately used, and an alkaline solution such as caustic soda is often used.
【００１３】本発明の電磁波シールド材は、アルミニウ
ム箔又は着色層がある場合はその上にさらに樹脂層を設
けてもよい。樹脂層は公知のコーティング法やラミネー
ト法等により設けることができる。本発明の電磁波シー
ルド材は、建造物、電子機器の筐体等あらゆるものの電
磁波シールドに利用できる。特に、ある程度の透視性を
要求されるもの、例えば電子レンジの前面ドア、病院等
の電磁波を遮蔽する必要のある建物の窓、プラズマディ
スプレー等に好適に使用できる。The electromagnetic wave shielding material of the present invention may be further provided with a resin layer on the aluminum foil or the colored layer, if any. The resin layer can be provided by a known coating method, laminating method, or the like. INDUSTRIAL APPLICABILITY The electromagnetic wave shield material of the present invention can be used as an electromagnetic wave shield for various things such as buildings and housings of electronic devices. In particular, it can be suitably used for objects that require a certain degree of transparency, such as front doors of microwave ovens, windows of buildings such as hospitals that need to shield electromagnetic waves, plasma displays, and the like.
【００１４】[0014]
【実施例】以下に、本発明を例で説明するが、本発明は
これらにより何ら限定されない。
実施例１
厚さ４０μｍのアルミニウム箔の片面に、有機溶媒可溶
形エッチングレジストをスクリーン印刷で長対角線が
０．６５ｍｍ、短対角線が０．４５ｍｍの多数の菱形形
状の開口を残すようにして印刷し、反対面は全面を同じ
エッチングレジストにて印刷し、１２０℃で２分乾燥し
た。開口率は５８％となるようにした。エッチング液
（塩化第二鉄）で処理し、エッチングレジストが印刷さ
れていない部分のアルミニウムを溶出し、図２に示すよ
うなアルミニウム製電磁波シールド材を得た。EXAMPLES The present invention is described below by way of examples, but the present invention is not limited to these. Example 1 An organic solvent-soluble etching resist was printed on one surface of an aluminum foil having a thickness of 40 μm by screen printing so as to leave a large number of diamond-shaped openings having a long diagonal of 0.65 mm and a short diagonal of 0.45 mm. Then, the entire opposite surface was printed with the same etching resist and dried at 120 ° C. for 2 minutes. The aperture ratio was set to 58%. It was treated with an etching solution (ferric chloride) to elute the aluminum in the area where the etching resist was not printed, to obtain an aluminum electromagnetic wave shielding material as shown in FIG.
【００１５】実施例２
厚さ４０μｍのアルミニウム箔の片面に、有機溶媒可溶
形エッチングレジストをスクリーン印刷で直径０．８ｍ
ｍの多数の円形の開口を残すようにして印刷し、反対面
は全面を同じエッチングレジストにて印刷し、１２０℃
で２分乾燥した。開口率は７０％となるようにした。エ
ッチング液（塩化第二鉄）で処理し、エッチングレジス
トが印刷されていない部分のアルミニウムを溶出し、ア
ルミニウム製電磁波シールド材を得た。Example 2 An organic solvent-soluble etching resist was screen-printed on one side of an aluminum foil having a thickness of 40 μm to a diameter of 0.8 m.
It is printed so as to leave a large number of circular openings of m, and the opposite surface is printed with the same etching resist on the entire surface,
And dried for 2 minutes. The aperture ratio was set to 70%. It was treated with an etching solution (ferric chloride) to elute the aluminum in the portion where the etching resist was not printed, to obtain an electromagnetic wave shielding material made of aluminum.
【００１６】評価例１
実施例１、２及び４０μｍ（参考例１）及び１０μｍ
（参考例２）のアルミニウム箔の電磁波シールド特性を
測定した。測定はアドバンテスト法（広世雅昭：ＥＭＣ
に関する測定技術解説，タケダ理研工業（株）、山口裕
顕，雫田治夫：Electronic Pack. Techn.,3-3(1987),6
0）によった。但し、試料と発信器、試料と受信器の間
隔はいずれも１０ｍｍとした。 結果を図３（実施例
１）、図４（実施例２）、図５（参考例１）、図６（参
考例２）に示した。図３〜６から、実施例１のシールド
性能は参考例１の４０μｍ厚のアルミニウム箔とほとん
ど差がなく、実施例２のシールド性能は参考例２の１０
μｍ厚のアルミニウム箔とほとんど差がないことが分か
る。Evaluation Example 1 Examples 1, 2 and 40 μm (Reference Example 1) and 10 μm
The electromagnetic wave shielding characteristics of the aluminum foil of (Reference Example 2) were measured. Advantest method (Masaaki Hiroyo: EMC
Measurement technology explanation, Takeda Riken Kogyo Co., Ltd., Hiroaki Yamaguchi, Haruo Shikada: Electronic Pack. Techn., 3-3 (1987), 6
0) However, the intervals between the sample and the transmitter and between the sample and the receiver were set to 10 mm. The results are shown in FIG. 3 (Example 1), FIG. 4 (Example 2), FIG. 5 (Reference Example 1), and FIG. 6 (Reference Example 2). 3 to 6, the shield performance of Example 1 is almost the same as that of the 40 μm thick aluminum foil of Reference Example 1, and the shield performance of Example 2 is 10 of Reference Example 2.
It can be seen that there is almost no difference from the aluminum foil having a thickness of μm.
【００１７】[0017]
【発明の効果】本発明の電磁波シールド材は、アルミニ
ウム箔により容易に製造することができ、電磁波シール
ド効果はアルミニウム箔と遜色ない。多数の開口を有
し、開口率が大きいので、透視性がある。また、樹脂と
ラミネートした場合は取り扱いやすく、さらに粘着材層
を有するものは、所望の箇所に容易に貼り付けることが
でき、簡単に電磁波を遮蔽することができる。また、素
材が比重が小さくて薄いアルミニウム箔である上に、開
口を有するので極めて軽量である。INDUSTRIAL APPLICABILITY The electromagnetic wave shielding material of the present invention can be easily manufactured with aluminum foil, and the electromagnetic wave shielding effect is comparable to that of aluminum foil. Since it has a large number of openings and a large aperture ratio, it is transparent. Further, when laminated with a resin, it is easy to handle, and those having an adhesive layer can be easily attached to a desired place and can easily shield electromagnetic waves. Further, since the material is a thin aluminum foil having a small specific gravity and has an opening, it is extremely lightweight.
【図１】本発明の電磁波シールド材の一態様を表した断
面図である。FIG. 1 is a cross-sectional view showing an aspect of an electromagnetic wave shield material of the present invention.
【図２】本発明の電磁波シールド材の一態様を表した平
面図である。FIG. 2 is a plan view showing an aspect of an electromagnetic wave shield material of the present invention.
【図３】実施例１のシールド性能を表した図である。FIG. 3 is a diagram showing the shield performance of Example 1.
【図４】実施例２のシールド性能を表した図である。FIG. 4 is a diagram showing the shield performance of Example 2;
【図５】参考例１のシールド性能を表した図である。5 is a diagram showing the shielding performance of Reference Example 1. FIG.
【図６】参考例２のシールド性能を表した図である。6 is a diagram showing the shield performance of Reference Example 2. FIG.
１ アルミニウム箔 ２ 開口 ３ エッチングレジストを兼ねた着色層 ４、５ 樹脂層 ６ 粘着剤層 1 aluminum foil 2 openings 3 Colored layer that doubles as an etching resist 4, 5 resin layer 6 Adhesive layer
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 4F100 AA23B AA37B AB10A AK01C AR00B AR00D BA01 BA02 BA03 BA04 BA07 BA10C BA10D CB05D DC11A EH012 EJ153 JA20A JD08 JL10B JL13D YY00A 5E321 AA03 AA04 AA05 AA23 AA45 AA46 BB23 BB25 BB32 CC16 GG05 GH01 ─────────────────────────────────────────────────── ─── Continued front page F term (reference) 4F100 AA23B AA37B AB10A AK01C AR00B AR00D BA01 BA02 BA03 BA04 BA07 BA10C BA10D CB05D DC11A EH012 EJ153 JA20A JD08 JL10B JL13D YY00A 5E321 AA03 AA04 AA05 AA23 AA45 AA46 BB23 BB25 BB32 CC16 GG05 GH01
Claims (9)
有するアルミニウム製電磁波シールド材。1. An electromagnetic wave shielding material made of aluminum having a large number of openings obtained by etching.
ある請求項１の電磁波シールド材。2. The electromagnetic wave shield material according to claim 1, wherein the thickness of aluminum is 0.3 mm or less.
２の電磁波シールド材。3. The electromagnetic wave shielding material according to claim 1, which has a colored layer on one surface.
イトを含有する請求項３の電磁波シールド材。4. The electromagnetic wave shield material according to claim 3, wherein the colored layer contains carbon black or ferrite.
求項１〜４のいずれか１項の電磁波シールド材。5. The electromagnetic wave shielding material according to claim 1, which has a resin layer on at least one surface.
か１項の電磁波シールド材。6. The electromagnetic wave shielding material according to claim 1, which has an adhesive layer.
波長の１／５０以下である請求項１〜６のいずれか１項
の電磁波シールド材。7. The electromagnetic wave shield material according to claim 1, wherein the diameter of the opening is 1/50 or less of the wavelength of the electromagnetic wave to be shielded.
７のいずれか１項の電磁波シールド材。8. The aperture ratio is 20 to 80%.
7. The electromagnetic wave shielding material according to any one of 7.
アルミニウム面をエッチングレジストにより開口部を残
してマスキングした後、エッチングすることを特徴とす
るアルミニウム製電磁波シールド材の製造方法。9. A method for producing an electromagnetic wave shielding material made of aluminum, which comprises etching an aluminum surface of a laminate material of aluminum foil and a resin with an etching resist while masking the aluminum surface leaving an opening.