JP2003227070A - Fiber structure - Google Patents
Fiber structureInfo
- Publication number
- JP2003227070A JP2003227070A JP2002347517A JP2002347517A JP2003227070A JP 2003227070 A JP2003227070 A JP 2003227070A JP 2002347517 A JP2002347517 A JP 2002347517A JP 2002347517 A JP2002347517 A JP 2002347517A JP 2003227070 A JP2003227070 A JP 2003227070A
- Authority
- JP
- Japan
- Prior art keywords
- cloth
- fiber structure
- pollen
- fiber
- structure according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、花粉症の原因であ
る花粉が付着しにくい花粉付着防止性に優れた繊維構造
物に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a fiber structure excellent in pollen adhesion preventive property in which pollen, which is a cause of pollinosis, is unlikely to adhere.
【０００２】[0002]
【従来の技術】花粉症は現代病であり、春先になると
鼻、目などに症状が起こり不快感を覚える人が多くなっ
ている。花粉症は発病するとなかなか完治しない病気
で、その治療も確立されておらず、予防策として皮膚、
目、鼻、口に花粉が触れないようさまざまな対策がとら
れている。2. Description of the Related Art Hay fever is a modern illness, and many people feel discomfort due to symptoms such as nose and eyes in early spring. Hay fever is a disease that does not completely cure when it develops, its treatment has not been established, and skin as a preventive measure,
Various measures have been taken to prevent pollen from touching the eyes, nose and mouth.
【０００３】鼻や口に花粉が触れない対策としては、防
塵マスクなどがあり静電気を発生させてマスク内に花粉
を吸着し、鼻や口で花粉を吸引しない方法が一般的であ
る。As a measure for preventing the pollen from touching the nose and mouth, there is generally a dust mask or the like, in which static electricity is generated to adsorb the pollen into the mask and not to suck the pollen through the nose or mouth.
【０００４】これらは、常にマスクをした状態でないと
効果はなく、日常生活的にマスクをすることは、息苦し
く負担になるものである。また、衣服に付着した花粉に
ついては付着したまま、家の中に持ち込まれマスクをは
ずせば、外の環境に近い状態となる。These are not effective unless they are always in a masked state, and wearing a mask in daily life is stuffy and burdensome. Also, if pollen that has adhered to your clothes remains attached, you can bring it into your house and remove the mask to get a closer look to the environment.
【０００５】花粉を防止するものとして、特開平６−１
５８４９４には、スルホン酸塩、カルボン酸塩、リン酸
塩、塩基性基またはホルミル基を有する化合物を含有し
平行水分率が１％以上である花粉補足用繊維構造物が提
案されている。これらは花粉のアレルゲン物質を化学的
に吸着するするものであり、これらを衣料として用いた
場合、花粉を付着させたまま家の中に入ることになる。
要するに家の中に花粉を持ち込むことになり花粉症の人
にとっては返って好ましくないものである。As a means for preventing pollen, Japanese Patent Laid-Open No. 6-1
58494 proposes a pollen supplementing fiber structure containing a sulfonate, a carboxylate, a phosphate, a compound having a basic group or a formyl group and having a parallel moisture content of 1% or more. These chemically adsorb allergen substances of pollen, and when these are used as clothing, they enter the house with pollen attached.
In short, pollen is brought into the house, which is not preferable for people with hay fever.
【０００６】また花粉を付着させないものとしては、特
開平６−１２６０９３には有孔フィルム／シートにより
形成された洗濯物用花粉防止カバーが提案されている。
これらは花粉が通過せず、水蒸気が通過する範囲の大き
さの孔を有するフィルムを用いるものであるが、フィル
ムでるため一般衣料として用いた場合、ファッション性
に欠け、またカーテンなどのインテリア用品としてもド
レープ性がないなど汎用性に欠けるものであった。また
フィルムは静電気が発生しやすく、花粉を呼び寄せやす
くまた一旦付着した花粉はなかなか取れないという問題
があった。[0006] For preventing the pollen from adhering, Japanese Patent Laid-Open No. 6-126093 proposes a pollen prevention cover for laundry formed of a perforated film / sheet.
These use a film that has pores that do not allow pollen to pass but have a size that allows water vapor to pass through.However, since it is a film, it lacks fashionability when used as general clothing, and as an interior product such as a curtain. However, it lacked versatility such as no drape. In addition, the film has a problem that static electricity is easily generated, pollen is easily attracted, and pollen once attached cannot be easily removed.
【０００７】[0007]
【特許文献１】特開平６−１５８４９４号公報[Patent Document 1] JP-A-6-158494
【０００８】[0008]
【発明が解決しようとする課題】本発明は、かかる従来
技術の背景に鑑み、浮遊する花粉が付着しにくく、且つ
落ちやすい花粉付着防止性に優れた繊維構造物を提供せ
んとするものである。SUMMARY OF THE INVENTION In view of such background of the prior art, the present invention is to provide a fiber structure excellent in pollen adhesion preventing property in which floating pollen is less likely to adhere and easily drops. .
【０００９】[0009]
【課題を解決するための手段】本発明は、かかる課題を
解決するために、次のような手段を採用するものであ
る。すなわち、本発明の繊維構造物は、ＫＥＳ法による
布帛表面の摩擦係数の平均偏差（ＭＭＤ）のタテ方向、
ヨコ方向の各々の値が０．０４以下で、かつ表面粗さの
平均偏差（ＳＭＤ）のタテ方向、ヨコ方向の各々の値が
４．０μｍ以下であって、かつ擬似花粉の繊維構造物表
面への付着数が、下記測定方法で２５０個以下である布
帛を用いてなることを特徴とする繊維構造物である。
（測定方法）７×７ｃｍの繊維布帛３０枚を２０℃×６
５％ＲＨで２４時間調湿後、１ｇの擬似花粉と共にポリ
エチレン袋の中に入れ、２０℃×６５％ＲＨの空気で、
約２０リットルに膨らませ口を縛る。The present invention employs the following means in order to solve the above problems. That is, the fiber structure of the present invention has a vertical direction of the mean deviation (MMD) of the coefficient of friction of the fabric surface by the KES method,
Each value in the horizontal direction is 0.04 or less, and the average deviation (SMD) of surface roughness in the vertical direction and each value in the horizontal direction is 4.0 μm or less, and the fiber structure surface of the pseudo pollen The fiber structure is characterized in that the number of adhered to the fabric is 250 or less by the following measuring method. (Measurement method) 30 pieces of 7 × 7 cm fiber cloth at 20 ° C. × 6
After conditioning the humidity at 5% RH for 24 hours, put it in a polyethylene bag together with 1 g of artificial pollen, and air at 20 ° C. × 65% RH.
Inflate to about 20 liters and tie the mouth.
【００１０】かかるポリエチレン袋を１回／１秒の速度
で縛り口を基準に上下に１００回振ったのち、繊維布帛
を取り出し、繊維布帛表面を５０倍に拡大し７．５×１
０ｃｍの範囲の擬似花粉の個数を数える。The polyethylene bag was shaken up and down 100 times at a speed of once / second based on the binding port, and then the fiber cloth was taken out, and the surface of the fiber cloth was magnified 50 times to 7.5 × 1.
Count the number of simulated pollens in the 0 cm range.
【００１１】[0011]
【発明の実施の形態】本発明は、前記課題、つまり花粉
が付着しにくという花粉付着防止性を向上させた花粉付
着防止繊維構造物について鋭意検討した結果、ＫＥＳ法
による布帛表面の摩擦係数の平均偏差（ＭＭＤ）のタテ
方向、ヨコ方向の各々の値が０．０４以下で、かつ表面
粗さの平均偏差（ＳＭＤ）のタテ方向、ヨコ方向の各々
の値が４．０μｍ以下である布帛、つまり布帛表面が平
滑である布帛が、擬似花粉の付着が少なく、つまり実際
の花粉付着も少なくなり、かかる課題を一挙に解決する
ことを究明したものである。BEST MODE FOR CARRYING OUT THE INVENTION The present invention has been made as a result of earnestly studying the above-mentioned problems, that is, a pollen adhesion-preventing fiber structure having an improved pollen adhesion preventing property that pollen is hard to adhere. The average deviation (MMD) of each of the vertical and horizontal values is 0.04 or less, and the average deviation (SMD) of the surface roughness is 4.0 μm or less in the vertical and horizontal directions. It was clarified that a cloth, that is, a cloth having a smooth cloth surface, has less pseudo-pollen adhesion, that is, less actual pollen adhesion, and solves the above problems all at once.
【００１２】本発明でいう摩擦係数の平均偏差は、ＫＥ
Ｓ法による布帛表面の摩擦係数の平均偏差（ＭＭＤ）で
あり、タテ方向、ヨコ方向の各々の値が０．０４以下で
あることが好ましい。本発明でいうタテ方向とは布帛の
長さ方向であり、ヨコ方向とは布帛の幅方向である。Ｍ
ＭＤが大きいということは摩擦係数の変動が大きく布帛
表面を摩擦した時、粘着性が高く引っかかりやすいこと
を意味する。ＭＭＤが０．０４より大きいと摩擦時のひ
っかかりが大きくなり、花粉が布帛表面に引っかかって
付着しやすく、落ちにくくなってしまうものである。The average deviation of the friction coefficient referred to in the present invention is KE
It is the average deviation (MMD) of the friction coefficient of the fabric surface by the S method, and it is preferable that each value in the vertical direction and the horizontal direction is 0.04 or less. In the present invention, the vertical direction is the length direction of the cloth, and the horizontal direction is the width direction of the cloth. M
When the MD is large, it means that the variation of the friction coefficient is large, and when the cloth surface is rubbed, it has high tackiness and is easily caught. If the MMD is larger than 0.04, the scratches during rubbing become large, and the pollen is easily caught by the surface of the fabric and adheres to it, which makes it difficult to remove it.
【００１３】本発明のＭＭＤは、カトーテック（株）Ｋ
ＥＳ−ＦＢ４を用い２０℃×６５％ＲＨの環境下で測定
する。２０ｇｆ／ｃｍの張力をかけた布帛に、０．５ｍ
ｍΦのピアノ線を１０本並べ５×５ｍｍに面上に巻いた
接触子を５０ｇｆの力で接触面を布帛に圧着させ、０．
１ｃｍ／秒の一定の速度で水平に２ｃｍ移動させた時の
摩擦係数の平均偏差である。The MMD of the present invention is K
It measures using ES-FB4 in the environment of 20 degreeC x 65% RH. 0.5m on the fabric with 20gf / cm tension
10 pieces of piano wire of mΦ are arranged and wound on the surface in a size of 5 × 5 mm, and the contact surface is pressure-bonded to the cloth with a force of 50 gf.
This is the average deviation of the coefficient of friction when horizontally moved by 2 cm at a constant speed of 1 cm / sec.
【００１４】本発明でいう表面粗さの平均偏差（ＳＭ
Ｄ）は、ＫＥＳ法による布帛の表面粗さであり、タテ方
向、ヨコ方向の各々の値が４．０μｍ以下であることが
好ましい。ＳＭＤが大きいということは布帛表面の凹凸
が大きいことを意味する。ＳＭＤが４．０μｍより大き
いと布帛表面の凹部に花粉は入り込み落ちにくくなって
しまうものである。The average deviation of the surface roughness (SM
D) is the surface roughness of the cloth measured by the KES method, and it is preferable that each value in the vertical direction and the horizontal direction is 4.0 μm or less. A large SMD means that there are large irregularities on the surface of the fabric. If the SMD is larger than 4.0 μm, the pollen will not easily get into the recesses on the surface of the fabric and fall off.
【００１５】本発明のＳＭＤは、カトーテック（株）Ｋ
ＥＳ−ＦＢ４を用い２０℃×６５％ＲＨの環境下で測定
する。２０ｇｆ／ｃｍの張力をかけた布帛に、０．５ｍ
ｍΦのピアノ線を５ｍｍ幅に１本折り曲げた接触子を１
０ｇｆで試料に圧着する。この接触子はバネで圧着され
るが、バネの定数は２５ｇｆとする。圧着させた摩擦子
を０．１ｃｍ／秒の一定の速度で水平に２ｃｍ移動させ
た時の布帛表面粗さの平均偏差である。The SMD of the present invention is manufactured by Kato Tech Co., Ltd. K
It measures using ES-FB4 in the environment of 20 degreeC x 65% RH. 0.5m on the fabric with 20gf / cm tension
1 contact piece of a piano wire of mΦ bent to a width of 5 mm
Crim the sample with 0 gf. This contactor is crimped by a spring, and the spring constant is 25 gf. It is the average deviation of the surface roughness of the fabric when the crimped friction element is moved horizontally 2 cm at a constant speed of 0.1 cm / sec.
【００１６】本発明でいう擬似花粉とは、石松子
（（有）津田商店 製）という花粉の粒径に近い天然物
であり、３０〜４０μｍのシダ科のヒカゲノカズラの胞
子である。大気中に浮遊している埃などの粒子は、１０
μｍ前後の非常に粒子の細かい無機物質が多く、また排
気ガスなどに含まれるカーボンブラックにおいては、
０．１μｍ前後とさらに細かい粒子であり、２０〜６０
μｍである花粉とは布帛への付着状態が異なるが、擬似
花粉は花粉に近い粒径および形状の擬似花粉が布帛表面
に付着しにくいということは、花粉も付着しにくいもの
である。The pseudo pollen referred to in the present invention is a natural product called Ishimatsuko (manufactured by Tsuda Shoten Co., Ltd.) having a particle size close to that of the pollen, and is a spore of a fernaceous lizard of the fern family of 30 to 40 μm. Particles such as dust floating in the atmosphere are 10
In the case of carbon black contained in exhaust gas, etc.
Finer particles around 0.1 μm, 20-60
Although the state of attachment to the cloth is different from the pollen having a particle size of μm, the fact that the pseudo pollen having a particle size and a shape close to that of the pollen does not easily adhere to the surface of the cloth means that the pollen does not easily adhere to the cloth.
【００１７】本発明は、かかる擬似花粉をポリエチレン
袋に１ｇ入れ、７ｃｍ×７ｃｍの繊維布帛３０枚と共に
１分間撹拌し、繊維表面に付着した擬似花粉の個数が、
繊維布帛表面を５０倍に拡大し、７．５×１０ｃｍの範
囲で２５０個以下であるものである。擬似花粉の付着個
数が２５０個を越えると、生地表面を肉眼で見た時に明
らかに花粉の付着が確認でき、花粉が付着しにくいとは
言い難いものである。According to the present invention, 1 g of the pseudo pollen is placed in a polyethylene bag and stirred for 30 minutes together with 30 pieces of 7 cm × 7 cm fiber cloth.
The surface of the fiber cloth is magnified 50 times, and the number is 250 or less in the range of 7.5 × 10 cm. When the number of the pseudo pollen adhered exceeds 250, it is difficult to say that the pollen is hard to adhere because the adherence of the pollen can be clearly confirmed when the surface of the cloth is visually observed.
【００１８】本発明の繊維構造物は、布帛表面にシリコ
ーン系化合物、ポリエステル系化合物、ワックス系化合
物、パラフィン系化合物、メラミン系化合物、グリオキ
ザール系化合物、ウレタン系化合物、アクリル系化合
物、エポキシ系化合物、ポリアミド系化合物、無機系化
合物等が固着していてもよく、全く何も固着していない
ものであっても良い。The fiber structure of the present invention comprises a silicone compound, a polyester compound, a wax compound, a paraffin compound, a melamine compound, a glyoxal compound, a urethane compound, an acrylic compound, an epoxy compound, A polyamide compound, an inorganic compound, or the like may be fixed, or nothing may be fixed at all.
【００１９】特に好ましくはフルオロアルキル基を有す
る（メタ）アクリル酸エステルを必須の重合単位とする
重合体が布帛表面に固着していることが好ましい。重合
体は、他の重合性モノマとの共重合体であっても良い。Particularly preferably, a polymer having a fluoroalkyl group-containing (meth) acrylic acid ester as an essential polymerization unit is fixed on the surface of the cloth. The polymer may be a copolymer with another polymerizable monomer.
【００２０】本発明でいうフルオロアルキル基を有する
（メタ）アクリル酸エステルとは、フルオロアルキル基
が（メタ）アクリル酸エステルのアルコール残基部分に
存在する化合物をいう。The (meth) acrylic acid ester having a fluoroalkyl group in the present invention means a compound in which a fluoroalkyl group is present in the alcohol residue portion of the (meth) acrylic acid ester.
【００２１】フルオロアルキル基とは、アルキル基の水
素原子の２個以上がフッ素原子に置換された基をいう。
フルオロアルキル基の炭素数は２〜２０が好ましく、特
に６〜１６が好ましい。また、フルオロアルキル基は、
直鎖状または分岐状の基が好ましい。分岐状の基である
場合には、分岐部分がフルオロアルキル基の末端部分に
存在し、かつ、炭素数１〜４程度の短鎖であるのが好ま
しい。 さらにフルオロアルキル基は、アルキル基の水
素原子の全てがフッ素原子に置換された基（すなわちパ
ーフルオロアルキル基）、またはパーフルオロアルキル
基を末端部分に有する基が好ましい。The fluoroalkyl group means a group in which two or more hydrogen atoms of the alkyl group are substituted with fluorine atoms.
The fluoroalkyl group preferably has 2 to 20 carbon atoms, and particularly preferably 6 to 16 carbon atoms. Further, the fluoroalkyl group is
A linear or branched group is preferred. In the case of a branched group, the branched portion is preferably present at the terminal portion of the fluoroalkyl group and is a short chain having about 1 to 4 carbon atoms. Further, the fluoroalkyl group is preferably a group in which all hydrogen atoms of the alkyl group are substituted with fluorine atoms (that is, a perfluoroalkyl group), or a group having a perfluoroalkyl group at the terminal portion.
【００２２】パーフルオロアルキル基の場合、炭素数
は、１〜２０が好ましく、４〜１６が特に好ましい。炭
素数が４未満の場合には、加工剤組成物の撥水性能が低
下する傾向にあり、１６より多い場合には、共重合体が
常温で固体となり、昇華性も大きく、取扱いが困難にな
る恐れがある。In the case of a perfluoroalkyl group, the carbon number is preferably 1-20, and particularly preferably 4-16. When the carbon number is less than 4, the water-repellent performance of the processing agent composition tends to decrease, and when the carbon number is more than 16, the copolymer becomes a solid at room temperature and has a large sublimation property, which makes the handling difficult. There is a risk of becoming.
【００２３】本発明の重合体は、かかる重合単位を１種
または２種以上含んでいてもよい。かかる重合単位を２
種以上含む場合には、炭素数の異なるフルオロアルキル
基を有する（メタ）アクリル酸エステルを用いることが
好ましい。The polymer of the present invention may contain one type or two or more types of such polymerized units. 2 such polymerized units
When it contains more than one species, it is preferable to use a (meth) acrylic acid ester having a fluoroalkyl group having a different carbon number.
【００２４】また、本発明の重合体は、ポリアルキレン
グリコール（メタ）アクリル酸エステルを重合単位とし
て含むことが好ましい。かかるポリアルキレングリコー
ルは、ポリエチレングリコールおよび／またはポリプロ
ピレングリコールであることが好ましい。特に好ましく
は疎水性のポリプロピレングリコールであり、これを含
むことによりＭＭＤ、ＳＭＤの数値が低くなり、平滑性
が向上し、花粉付着防止性がさらに大きく向上するもの
である。The polymer of the present invention preferably contains polyalkylene glycol (meth) acrylic acid ester as a polymerized unit. Such polyalkylene glycol is preferably polyethylene glycol and / or polypropylene glycol. Hydrophobic polypropylene glycol is particularly preferable, and by including it, the values of MMD and SMD are lowered, the smoothness is improved, and the pollen adhesion preventing property is further greatly improved.
【００２５】本発明の重合体は、アミノプラスト樹脂、
多官能性イソシアネート基含有ウレタン樹脂の少なくと
も１種とを含有してなる樹脂組成物を構成し、かかる樹
脂組成物の形で固着されているのが好ましい。かかる樹
脂組成物として用いることにより、該重合体の布帛表面
への固着の耐久性が向上するものである。The polymer of the present invention is an aminoplast resin,
It is preferable that a resin composition containing at least one kind of urethane resin containing a polyfunctional isocyanate group is constituted and fixed in the form of such a resin composition. By using it as such a resin composition, the durability of fixation of the polymer on the fabric surface is improved.
【００２６】アミノプラスト樹脂としては、トリメチロ
ールメラミン、ヘキサメチロールメラミンなどのメラミ
ン樹脂、ジメチロールプロピレン尿素、ジメチロールエ
チレン尿素、ジメチロールヒドロキシ尿素などの尿素系
樹脂、ジメチロールウロンなどのウロン樹脂などを用い
ることができる。中でもヘキサメチロールメラミン、ト
リメチロールメラミンが好適である。Examples of the aminoplast resin include melamine resins such as trimethylolmelamine and hexamethylolmelamine, urea resins such as dimethylolpropyleneurea, dimethylolethyleneurea and dimethylolhydroxyurea, and uron resins such as dimethyloluron. Can be used. Among them, hexamethylolmelamine and trimethylolmelamine are preferable.
【００２７】多官能性イソシアネート基含有ウレタン樹
脂としては、分子中に２個以上のイソシアネート官能基
を含む有機化合物であれば特に限定されるものではな
い。具体例としてはトリレンジイソシアネート、ヘキサ
メチレンジイソシアネート、ジフェニールメタンジイソ
シアネート、水素添加ジフェニールメタンジイソシアネ
ート、トリフェニールトリイソシアネート、キシレジン
イソシアネート、ジクロヘキシルメタンジイソシアネー
ト、トリメチロールプロパントリレンジイソシアネート
アダクト、フリセリントリレンジイソシアネートアダク
トなどに７０〜２００℃の加熱時に解離して活性なイソ
シアネート基が再生できるようなブロッキング化化合物
として、フェノール、マロン酸ジエチルエステル、メチ
ルエチルケトオキシム、重亜硫酸ソーダ、ε−カプロラ
クタムなどを反応させた多官能ブロックイソシアネート
ウレタン樹脂を挙げることができる。ブロックイソシア
ネートの熱分離速度の向上と熱解離温度の低下とを促進
するために用いる解離触媒としてはジブチルスズジオレ
ート、ジブチルスズステアレート、ステアリル亜鉛、有
機アミン化合物が好ましい。The polyfunctional isocyanate group-containing urethane resin is not particularly limited as long as it is an organic compound containing two or more isocyanate functional groups in the molecule. Specific examples include tolylene diisocyanate, hexamethylene diisocyanate, diphenyl methane diisocyanate, hydrogenated diphenyl methane diisocyanate, triphenyl triisocyanate, xylidine isocyanate, dichlorohexyl methane diisocyanate, trimethylol propane tolylene diisocyanate adduct, and friseline tolylene diisocyanate. Phenol, malonic acid diethyl ester, methyl ethyl ketoxime, sodium bisulfite, ε-caprolactam, etc. were reacted as a blocking compound capable of regenerating an active isocyanate group by dissociating into an isocyanate adduct upon heating at 70 to 200 ° C. Mention may be made of polyfunctional blocked isocyanate urethane resins. Dibutyltin dioleate, dibutyltin stearate, stearyl zinc, and organic amine compounds are preferable as the dissociation catalyst used to accelerate the thermal separation rate of the blocked isocyanate and reduce the thermal dissociation temperature.
【００２８】本発明の重合体におけるフルオロアルキル
基含有重合単位の含有割合は、布帛表面に付与された樹
脂成分中、３０〜７０ｗｔ％であることが好ましい。３
０ｗｔ％未満の場合は疎水性が低く粘着性が高くなり布
帛表面のＭＭＤが高くなり花粉付着が多くなる場合があ
る。また７０ｗｔ％を越えると撥水性が高くなるが布帛
表面のかさつき感が高くなり、布帛表面のＭＭＤ、ＳＭ
Ｄが高くなり花粉付着が多くなる傾向がある。The content of the fluoroalkyl group-containing polymerized units in the polymer of the present invention is preferably 30 to 70 wt% in the resin component applied to the surface of the cloth. Three
If it is less than 0 wt%, the hydrophobicity is low and the tackiness is high, the MMD on the fabric surface is high, and the pollen adhesion may increase. If it exceeds 70 wt%, the water repellency will be high, but the bulkiness of the fabric surface will be high, and the MMD and SM of the fabric surface will be increased.
D tends to increase and pollen adhesion tends to increase.
【００２９】布帛への樹脂組成物の付与方法としては、
フルオロアルキル基を有する（メタ）アクリル酸エステ
ルを必須の重合単位とする重合体に、アミノプラスト樹
脂および／または、多官能性イソシアネート基含有ウレ
タン樹脂を加えた処理液を布帛に付着した後熱処理され
ることが好ましい。処理液を付与する方法は、かかる処
理液に布帛を浸漬後パッディング法で付与する方法、ま
たはスプレー法で付与することが好ましい。熱処理は、
乾熱処理または湿熱処理のいずれかであり、好ましくは
１００〜２００℃の乾熱処理が好ましい。１００℃未満
であると洗濯耐久性が不十分であり、２００℃を越える
と繊維の黄変、脆化が生じる傾向にある。As a method for applying the resin composition to the cloth,
A treatment liquid obtained by adding a aminoplast resin and / or a urethane resin containing a polyfunctional isocyanate group to a polymer having a (meth) acrylic acid ester having a fluoroalkyl group as an essential polymerization unit is heat-treated after adhering to the cloth. Preferably. As a method of applying the treatment liquid, it is preferable to apply the treatment liquid by a padding method after dipping the cloth, or by a spray method. The heat treatment is
It is either a dry heat treatment or a wet heat treatment, preferably a dry heat treatment at 100 to 200 ° C. If it is less than 100 ° C, the washing durability is insufficient, and if it exceeds 200 ° C, the fibers tend to yellow and become brittle.
【００３０】また、花粉は、大気汚染物質と比較して粒
径が大きく、３０μｍ前後であるため、かかる重合体が
単繊維に均一に被膜として被覆されている必要はなく、
繊維束をかかる重合体が覆っていればよい。このことか
らかかる重合体が布帛にコーティングされ、布帛の片面
または両面にシート状に付着していても良い。Further, since the pollen has a particle size larger than that of the air pollutant and is around 30 μm, it is not necessary that the polymer is uniformly coated on the single fiber as a film.
The polymer may cover the fiber bundle. For this reason, such a polymer may be coated on a cloth and attached to one or both surfaces of the cloth in a sheet form.
【００３１】かかる繊維構造物を構成する布帛の繊維と
して、合成繊維、天然繊維、および再生繊維から選ばれ
た少なくとも１種を使用することができるが、かかる合
成繊維としてはポリエステル系繊維またはポリアミド系
繊維またはポリオレフィン系繊維等が好ましい。ポリエ
ステル系繊維としては、ポリエチレンテレフタレート、
ポリトリメチレンテレフタレート、ポリブチレンテレフ
タレートやこれらを主成分とした共重合ポリエステル系
繊維等が含まれ、また、ポリアミド系繊維としては、ナ
イロン６，ナイロン６６および第３成分を共重合したも
の等である。ポリオレフィン系繊維としては、ポリプロ
ピレン、ポリエチレン等が含まれる。また天然繊維とし
ては、絹等が好ましく、再生繊維としてはビスコースレ
ーヨン等が好ましい。At least one selected from synthetic fibers, natural fibers, and regenerated fibers can be used as the fibers of the cloth constituting such a fiber structure. The synthetic fibers are polyester fibers or polyamide fibers. Fibers or polyolefin fibers are preferred. As the polyester fiber, polyethylene terephthalate,
Polytrimethylene terephthalate, polybutylene terephthalate and copolymerized polyester fibers containing these as the main components are included, and polyamide fibers include those obtained by copolymerizing nylon 6, nylon 66 and a third component. . Polyolefin fibers include polypropylene and polyethylene. The natural fiber is preferably silk or the like, and the regenerated fiber is preferably viscose rayon or the like.
【００３２】本発明においては、布帛を構成する繊維ま
たは繊維束が交錯してできる隙間が、３０μｍ以下であ
ることが好ましい。花粉の粒径は３０μｍ前後であるた
め隙間が３０μｍを越えると、隙間から花粉が繊維構造
物の内部に入り込む可能性があるためである。In the present invention, it is preferable that the interstices formed by the fibers or fiber bundles constituting the cloth are 30 μm or less. This is because the particle diameter of pollen is around 30 μm, and if the gap exceeds 30 μm, the pollen may enter the inside of the fiber structure through the gap.
【００３３】また、布帛を構成する繊維としては、特に
好ましくは長繊維が用いられる。As the fibers constituting the fabric, long fibers are particularly preferably used.
【００３４】本発明の繊維構造物に用いられる布帛は、
織物、編物、または不織布であることが好ましいが、布
帛表面の平滑性を高めるためには、織物であることが好
ましい。The fabric used in the fiber structure of the present invention is
A woven fabric, a knitted fabric, or a non-woven fabric is preferable, but a woven fabric is preferable in order to enhance the smoothness of the fabric surface.
【００３５】本発明の繊維構造物は、花粉が付着しにく
いということから、コート、ウインドブレーカー、ブラ
ウス、ドレスシャツ、スカート、スラックス、手袋、帽
子または布団カバー、布団干しカバーなどの用途に好適
に使用されるものである。Since the fiber structure of the present invention does not easily adhere to pollen, it is suitable for applications such as coats, windbreakers, blouses, dress shirts, skirts, slacks, gloves, hats or duvet covers, and duvet covers. Is what is used.
【００３６】[0036]
【実施例】以下、実施例によって本発明をさらに詳細に
説明するが、本発明はこれら実施例に限定されるもので
はない。なお、実施例中の品質評価は次の方法に従っ
た。
（花粉付着防止性）７×７ｃｍの繊維布帛３０枚を２０
℃×６５％ＲＨで２４時間調湿後、１ｇの擬似花粉と共
にポリエチレン袋の中に入れ、２０℃×６５％ＲＨの空
気で、約２０リットルに膨らませ口を縛る。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples. The quality evaluation in the examples was performed according to the following method. (Prevention of pollen adhesion) 30 pieces of 7 × 7 cm fiber cloth 20
After conditioning the humidity at ℃ × 65% RH for 24 hours, put it in a polyethylene bag together with 1 g of artificial pollen, inflate it to about 20 liters with air at 20 ℃ × 65% RH, and tie the mouth.
【００３７】かかるポリエチレン袋を１回／１秒の速度
で縛り口を基準に上下に１００回振ったのち、繊維布帛
を取り出し、繊維布帛表面を５０倍に拡大し７．５×１
０ｃｍの範囲の擬似花粉の個数を数える。
（摩擦係数平均偏差／ＭＭＤ）
１．２０×２０ｃｍの試験片を準備する。
２．カトーテック（株）ＫＥＳ−ＦＢ４を用い２０℃×
６５％ＲＨの環境下で２０ｇｆの張力をかけ試験片を取
り付ける。
３．０．５ｍｍΦのピアノ線を５×５ｍｍに１０本面上
に巻いた接触子に５０ｇｆで試料に圧着させ、０．１ｃ
ｍ／秒の一定速度で水平に移動させ測定する。４．上記
方法で布帛のタテ、ヨコ方法を測定する。
（布帛表面粗さの平均偏差／ＳＭＤ）
１．２０×２０ｃｍの試験片を準備する。
２．カトーテック（株）ＫＥＳ−ＦＢ４を用い２０℃×
６５％ＲＨの環境下で２０ｇｆの張力をかけ試験片を取
り付ける。
３．０．５ｍｍΦのピアノ線を５ｍｍ幅に１本折り曲げ
た接触子に１０ｇｆで試料に圧着させ０．１ｃｍ／秒の
一定速度で水平に移動させ測定する。
４．上記方法で布帛のタテ、ヨコ方法を測定する。The polyethylene bag was shaken up and down 100 times at a speed of once per second based on the binding port, and then the fiber cloth was taken out, and the surface of the fiber cloth was enlarged 50 times to 7.5 × 1.
Count the number of simulated pollens in the 0 cm range. (Friction coefficient average deviation / MMD) 1. Prepare a 20 × 20 cm test piece. 2. 20 ° C. using KATO TECH KES-FB4
A test piece is attached by applying a tension of 20 gf under an environment of 65% RH. 3. Press the piano wire of 0.5mmΦ on a 10x5x5mm coil and press it onto the sample with 50gf, and then press 0.1c.
It is moved horizontally at a constant speed of m / sec for measurement. 4. The vertical and horizontal methods of the cloth are measured by the above method. (Average Deviation of Fabric Surface Roughness / SMD) A test piece of 1.20 × 20 cm is prepared. 2. 20 ° C. using KATO TECH KES-FB4
A test piece is attached by applying a tension of 20 gf under an environment of 65% RH. 3. A 0.5 mmΦ piano wire is bent to a width of 5 mm, and a contactor is pressed against the sample at 10 gf and moved horizontally at a constant speed of 0.1 cm / sec for measurement. 4. The vertical and horizontal methods of the cloth are measured by the above method.
【００３８】実施例１
タテ糸：ポリエステル ５６ｄｔｅｘ／７２ｆ 生糸
ヨコ糸：ポリエステル ８４ｄｔｅｘ／７２ｆ 生糸
密度 ：１７４×１０９本／インチ
上記織物を通常条件で精練、染色、乾燥し１６０℃で仕
上げセットを行った。Example 1 Warp yarn: Polyester 56dtex / 72f Raw yarn Weft yarn: Polyester 84dtex / 72f Raw yarn density: 174 × 109 yarns / inch The above woven fabric was scoured, dyed and dried at 160 ° C. for finishing setting. .
【００３９】得られた試験布について、花粉付着防止
性、ＭＭＤ、ＳＭＤの評価を行った。結果を表１に示
す。The test cloth thus obtained was evaluated for pollen adhesion preventive property, MMD and SMD. The results are shown in Table 1.
【００４０】得られた試験布は、ＭＭＤはタテが０．０
２３１、ヨコが０．０１０５であり、ＳＭＤはタテが
１．８３６、ヨコが１．４１６μｍであった。布帛表面
の粘着性が低く摩擦時の引っかかりが少なく、また布帛
表面の平滑であり、擬似花粉付着数は１４３個と優れた
花粉付着防止性を示した。The obtained test cloth has a MMD of 0.0
231, the width was 0.0105, and the SMD had a length of 1.836 and a width of 1.416 μm. The tackiness of the cloth surface was low, there was little catching at the time of rubbing, the cloth surface was smooth, and the number of pseudo-pollen particles adhered was 143, which was an excellent pollen adhesion preventing property.
【００４１】実施例２ タテ糸：ポリエステル ８４ｄｔｅｘ／７２ｆ 加工糸 ヨコ糸：ポリエステル 〃 加工糸 密度 ：１８８×９９本／インチ 上記織物を通常条件で精練、染色、乾燥した。Example 2 Vertical thread: Polyester 84dtex / 72f Processed thread Weft: Polyester 〃 Processed thread Density: 188 x 99 pieces / inch The above woven fabric was scoured, dyed and dried under normal conditions.
【００４２】次いで、パーフルオロアルキルエチルアク
リレートおよび、ポリオキシエチレングリコールモノメ
タクリレートおよびポリオキシプロピレングリコールモ
ノメタクリレートの共重合体ＴＫガード２０８（高松油
脂(株)製）、５０ｇ／ｌおよびアミノプラスト樹脂であ
るスミテックスレジンＭ−３（住友化学工業（株）製）
３ｇ／ｌおよび触媒として有機アミンからなる触媒ス
ミテックスレジンＡＣＸ（住友化学工業（株）製） ２
ｇ／ｌ、ブロックイソシアネートであるスーパーフレッ
シュＪＢ−７２００（(株)京絹化成 製）
３ｇ／ｌからなる処理液に試験布を浸漬したのち絞り率
８０％で絞り、１３０℃で乾燥後さらに１７５℃で４５
秒間乾熱処理を行った。Next, a perfluoroalkylethyl acrylate and a copolymer of polyoxyethylene glycol monomethacrylate and polyoxypropylene glycol monomethacrylate TK Guard 208 (manufactured by Takamatsu Yushi Co., Ltd.), 50 g / l and aminoplast resin. Sumitex Resin M-3 (Sumitomo Chemical Co., Ltd.)
Catalyst Sumitex Resin ACX (manufactured by Sumitomo Chemical Co., Ltd.) consisting of 3 g / l and an organic amine as a catalyst 2
The test cloth was dipped in a treatment liquid consisting of 3 g / l of super fresh JB-7200 (manufactured by Kyoshinkasei Co., Ltd.), which is a blocked isocyanate and super fresh JB-7200, and then squeezed at a squeezing ratio of 80% and dried at 130 ° C. for a further 175 45 at ℃
A dry heat treatment was performed for a second.
【００４３】得られた試験布について、花粉付着防止
性、ＭＭＤ、ＳＭＤの評価を行った。結果を表１に示
す。The test cloths thus obtained were evaluated for pollen adhesion preventive property, MMD and SMD. The results are shown in Table 1.
【００４４】得られた試験布は、ＭＭＤタテ０．０２３
７，ヨコ０．０１３５であり、ＳＭＤはタテ０．９９
６、ヨコ１．３１３μｍであった。布帛表面の粘着性が
低く摩擦時の引っかかりがが少なくまた布帛表面が平滑
であり、擬似花粉付着数は１７９個と優れた花粉付着防
止性を示した。The obtained test cloth has an MMD length of 0.023.
7, horizontal 0.0135, SMD vertical 0.99
6, the width was 1.313 μm. The tackiness of the cloth surface was low, there was little catching at the time of rubbing, the cloth surface was smooth, and the number of pseudo-pollen particles adhered was 179, indicating excellent pollen adhesion prevention properties.
【００４５】比較例１
タテ糸：ポリエステル １６７ｄｔｅｘ／４８ｆ
加工糸
ヨコ糸：ポリエステル６５％／綿３５％ ４５番手
密度 ：６８×６１本／インチ
上記織物を通常条件で精練、染色、乾燥し１６０℃で仕
上げセットを行った。Comparative Example 1 Warp yarn: Polyester 167 dtex / 48f
Processed yarn Weft yarn: Polyester 65% / Cotton 35% 45th count density: 68 × 61 yarns / inch The above fabric was scoured, dyed and dried under normal conditions, and finish set at 160 ° C.
【００４６】得られた試験布について、花粉付着防止
性、ＭＭＤ、ＳＭＤの評価を行った。結果を表１に示
す。The test cloths thus obtained were evaluated for pollen adhesion prevention property, MMD and SMD. The results are shown in Table 1.
【００４７】得られた試験布は、ＭＭＤがタテ０．０７
８５、ヨコ０．０５６４であり、ＳＭＤがタテ５．６０
８，ヨコ３．２１４であった。摩擦時の引っかかりが大
きく、布帛表面の平滑性に欠けるものであり、つまり花
粉の引っかかりが多く、擬似花粉付着数は６８４個と花
粉付着防止性が十分ではないものであった。The test cloth thus obtained had an MMD length of 0.07.
85, horizontal 0.0564, SMD vertical 5.60
It was 8, lateral 3.214. There was a large amount of catching during rubbing and lack of smoothness on the surface of the cloth. That is, there were many catches of pollen, and the number of pseudo pollen adhered was 684, indicating that the pollen adherence preventive property was not sufficient.
【００４８】比較例２
実施例１と同様の織物を通常条件で精練、染色、乾燥し
た。Comparative Example 2 The same fabric as in Example 1 was scoured, dyed and dried under normal conditions.
【００４９】次いで、リン酸エステル系帯電防止剤であ
るエレナスタットＥＡ−７（京浜化成（株）製）２０ｇ
／ｌからなる処理液に試験布を浸漬したのち絞り率８０
％で絞り、１６０℃で乾燥／乾熱処理を行った。Then, 20 g of Elenastat EA-7 (manufactured by Keihin Kasei Co., Ltd.) which is a phosphoric acid ester type antistatic agent.
After immersing the test cloth in the treatment liquid consisting of 1 / l, the drawing ratio is 80
%, And dried / heat-treated at 160 ° C.
【００５０】得られた試験布について、花粉付着防止
性、ＭＭＤ、ＳＭＤの評価を行った。結果を表１に示
す。The test cloths thus obtained were evaluated for pollen adhesion preventive property, MMD and SMD. The results are shown in Table 1.
【００５１】得られた試験布は、ＭＭＤがタテ０．０５
６４、ヨコ０．０３５５ＳＭＤがタテ４．４０４，ヨコ
２．１１２であった。帯電防止剤による布帛表面の粘着
性が高く、また布帛表面の平滑性に欠け、花粉が引っ付
きやすいものであった。擬似花粉付着数は７５６個と花
粉付着防止性が十分ではないものであった。The obtained test cloth has an MMD of 0.05 vertical.
64, horizontal 0.0355 SMD was vertical 4.404, horizontal 2.112. The antistatic agent had high tackiness on the cloth surface, lacked smoothness on the cloth surface, and pollen was easily stuck. The number of pseudo-pollens attached was 756, indicating that the pollen adhesion preventive property was not sufficient.
【００５２】[0052]
【表１】 [Table 1]
【００５３】表１から明らかなように、実施例１，２の
ものは、比較例のものに比して、５倍以上の花粉付着防
止性を有することがわかる。As is clear from Table 1, the examples 1 and 2 have 5 times or more the pollen adhesion preventive property as compared with the comparative example.
【００５４】[0054]
【発明の効果】本発明によれば、従来になかった優れた
花粉付着防止性防汚性を有する繊維構造物を提供するこ
とができ、特にコート、ウインドブレーカー、ブラウ
ス、帽子、布団干しカバーなど幅広い用途に好適な素材
を提供することができるものである。Industrial Applicability According to the present invention, it is possible to provide a fiber structure having excellent pollen antifouling and antifouling properties which have never been obtained, and particularly coats, windbreakers, blouses, hats, duvet covers and the like. It is possible to provide a material suitable for a wide range of uses.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ａ４１Ｄ 3/02 Ａ４１Ｄ 3/02 Ｚ 19/00 19/00 Ａ Ａ４２Ｂ 1/00 Ａ４２Ｂ 1/00 Ｚ Ｄ０６Ｍ 15/27 Ｄ０６Ｍ 15/27 15/423 15/423 15/564 15/564 Ｆターム(参考） 3B030 AA01 AA08 AA09 AB00 3B031 AA13 AB00 AE13 3B033 AA27 AB12 AC01 AC05 4L033 AA01 AA04 AB04 AC10 AC15─────────────────────────────────────────────────── ─── Continuation of the front page (51) Int.Cl. 7 Identification code FI theme code (reference) A41D 3/02 A41D 3/02 Z 19/00 19/00 A A42B 1/00 A42B 1/00 Z D06M 15 / 27 D06M 15/27 15/423 15/423 15/564 15/564 F-term (reference) 3B030 AA01 AA08 AA09 AB00 3B031 AA13 AB00 AE13 3B033 AA27 AB12 AC01 AC05 4L033 AA01 AA04 AB04 AC10 AC15
Claims (10)
偏差（ＭＭＤ）のタテ方向、ヨコ方向の各々の値が０．
０４以下で、かつ表面粗さの平均偏差（ＳＭＤ）のタテ
方向、ヨコ方向の各々の値が４．０μｍ以下であって、
かつ擬似花粉の繊維構造物表面への付着数が、下記測定
方法で２５０個以下である布帛を用いてなることを特徴
とする繊維構造物。 （測定方法）７×７ｃｍの繊維布帛３０枚を２０℃×６
５％ＲＨで２４時間調湿後、１ｇの擬似花粉と共にポリ
エチレン袋の中に入れ、２０℃×６５％ＲＨの空気で、
約２０リットルに膨らませ口を縛る。かかるポリエチレ
ン袋を１回／１秒の速度で縛り口を基準に上下に１００
回振ったのち、繊維布帛を取り出し、繊維布帛表面を５
０倍に拡大し７．５×１０ｃｍの範囲の擬似花粉の個数
を数える。1. The average deviation (MMD) of the coefficient of friction on the fabric surface measured by the KES method in each of the vertical and horizontal directions is 0.
04 or less, and the average value of the surface roughness (SMD) in the vertical direction and the horizontal direction is 4.0 μm or less,
A fiber structure characterized in that the number of adhered pseudo-pollens on the surface of the fiber structure is 250 or less by the following measuring method. (Measurement method) 30 pieces of 7 × 7 cm fiber cloth at 20 ° C. × 6
After conditioning the humidity at 5% RH for 24 hours, put it in a polyethylene bag together with 1 g of artificial pollen, and air at 20 ° C. × 65% RH.
Inflate to about 20 liters and tie the mouth. The polyethylene bag is moved up and down 100 times at a speed of once per second based on the binding port.
After shaking, take out the fiber cloth,
Expand to 0 times and count the number of pseudo pollens in the range of 7.5 × 10 cm.
る（メタ）アクリル酸エステルを必須の重合単位とする
重合体が付与されていることを特徴とする請求項１記載
の繊維構造物。2. The fiber structure according to claim 1, wherein a polymer having a fluoroalkyl group-containing (meth) acrylic acid ester as an essential polymerization unit is provided on the surface of the fabric.
ル酸エステルを重合単位として含む重合体が布帛表面に
付与されていることを特徴とする請求項１又は２に記載
の繊維構造物。3. The fiber structure according to claim 1 or 2, wherein a polymer containing a polyalkylene glycol (meth) acrylic acid ester as a polymerized unit is provided on the surface of the cloth.
レングリコールおよび／またはポリプロピレングリコー
ルであることを特徴とする請求項３に記載の繊維構造
物。4. The fiber structure according to claim 3, wherein the polyalkylene glycol is polyethylene glycol and / or polypropylene glycol.
重合単位の割合が、布帛に付与される樹脂成分中、３０
〜７０ｗｔ％であることを特徴とする請求項２〜４のい
ずれかに記載の繊維構造物。5. The proportion of fluoroalkyl group-containing polymerized units in the polymer is 30 in the resin component applied to the cloth.
It is-70 wt%, The fiber structure in any one of Claims 2-4 characterized by the above-mentioned.
または多官能性イソシアネート基含有ウレタン樹脂との
樹脂組成物として、布帛に付与されているものであるこ
とを特徴とする請求項２〜５のいずれかに記載の繊維構
造物。6. The polymer is an aminoplast resin and / or
Alternatively, the fiber structure according to any one of claims 2 to 5, wherein the fiber structure is a resin composition with a urethane resin containing a polyfunctional isocyanate group, which is applied to a cloth.
面または両面にコーティングされシート状に付着してい
るものであることを特徴とする請求項１〜６のいずれか
に記載の繊維構造物。7. The fiber according to claim 1, wherein the polymer or the resin composition is coated on one side or both sides of a cloth and attached in a sheet form. Structure.
してできる隙間が３０μｍ以下である請求項１〜７のい
ずれかに記載の繊維構造物。8. The fiber structure according to any one of claims 1 to 7, wherein a gap formed by intersecting fibers or fiber bundles constituting the cloth is 30 μm or less.
とを特徴とする請求項１〜８のいずれかに記載の防止繊
維構造物。9. The preventive fiber structure according to claim 1, wherein the fibers constituting the cloth are long fibers.
ーカー、ブラウス、ドレスシャツ、スカート、スラック
ス、手袋、帽子または布団カバーおよび布団干しカバー
である請求項１〜９のいずれかに記載の繊維構造物。10. The fiber structure according to claim 1, wherein the fiber structure is a coat, a windbreaker, a blouse, a dress shirt, a skirt, a slacks, gloves, a hat or a duvet cover and a duvet cover. object.