JP2003183438A - Thermoforming foamed sheet and container for fruit vegetable - Google Patents
Thermoforming foamed sheet and container for fruit vegetableInfo
- Publication number
- JP2003183438A JP2003183438A JP2001391604A JP2001391604A JP2003183438A JP 2003183438 A JP2003183438 A JP 2003183438A JP 2001391604 A JP2001391604 A JP 2001391604A JP 2001391604 A JP2001391604 A JP 2001391604A JP 2003183438 A JP2003183438 A JP 2003183438A
- Authority
- JP
- Japan
- Prior art keywords
- foamed sheet
- thermoforming
- fruit
- weight
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、ポリスチレン系樹
脂を主体とした発泡シート及び該発泡シートを熱成形し
てなる果菜容器に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a foamed sheet mainly composed of polystyrene resin and a fruit and vegetable container formed by thermoforming the foamed sheet.
【０００２】[0002]
【従来の技術】従来から、林檎、梨、桃、メロン、トマ
ト等を出荷する際等に使用される果菜容器として各種合
成樹脂発泡シートからなる容器、パルプからなる容器が
開発され使用されてきた。2. Description of the Related Art Conventionally, containers made of various synthetic resin foam sheets and containers made of pulp have been developed and used as fruit and vegetable containers used for shipping apples, pears, peaches, melons, tomatoes, etc. .
【０００３】上記パルプ製の容器（一般にパルプモール
ド品と言われている）は、低価格ではあるものの耐水性
が悪く、吸水すると緩衝性、強度等が低下するので、発
泡シート製の容器に比較すると物性的に好ましくない。The above-mentioned pulp container (generally referred to as a pulp-molded product) is low in price but poor in water resistance, and when it absorbs water, its buffering property and strength are lowered. Then, the physical properties are not preferable.
【０００４】前記合成樹脂発泡シートからなる果菜容器
としては、例えば架橋ポリエチレン樹脂発泡シートから
なる容器、無架橋ポリプロピレン樹脂発泡シートからな
る容器が知られている。As the fruit and vegetable container made of the synthetic resin foam sheet, for example, a container made of a crosslinked polyethylene resin foam sheet and a container made of a non-crosslinked polypropylene resin foam sheet are known.
【０００５】しかしながら、架橋ポリエチレン樹脂発泡
シートからなる容器は、緩衝性、成形性には優れている
が高価である。無架橋ポリプロピレン樹脂発泡シートか
らなる容器は、適度の緩衝性と剛性を合せ持ち、成形性
に優れるものの、特殊且つ高価なポリプロピレン系樹脂
を用いなければ良好な容器が得られないので、やはり高
価である。However, a container made of a crosslinked polyethylene resin foam sheet is excellent in cushioning property and moldability, but is expensive. A container made of a non-crosslinked polypropylene resin foam sheet has suitable cushioning properties and rigidity, and has excellent moldability, but a good container cannot be obtained unless a special and expensive polypropylene resin is used, so it is also expensive. is there.
【０００６】また、果菜容器用の発泡シートであって、
ポリスチレン系樹脂を主成分とする混合樹脂からなる発
泡シートが多数開示されており、例えば特許２９６９５
８６号公報がある。該特許２９６９５８６号公報には、
ポリスチレン系樹脂とスチレン・ブタジエンブロック共
重合体及びその水素添加物から選ばれる少なくとも１種
の樹脂との混合樹脂からなる発泡シートが開示されてい
る。該発泡シートから得られる容器は低価格で、従来の
ものと比較すると柔軟性は向上しているものの、その柔
軟性は未だ不十分である。A foamed sheet for a fruit and vegetable container,
A large number of foamed sheets made of a mixed resin containing a polystyrene-based resin as a main component are disclosed, for example, Japanese Patent No. 29695.
There is an 86 publication. In the Japanese Patent No. 2969586,
A foamed sheet made of a mixed resin of a polystyrene resin and at least one resin selected from styrene / butadiene block copolymers and hydrogenated products thereof is disclosed. A container obtained from the foamed sheet is low in price and has improved flexibility as compared with a conventional one, but the flexibility is still insufficient.
【０００７】[0007]
【発明が解決しようとする課題】本発明は上記課題を解
決するためになされたもので、柔軟性、適度な剛性、軽
量性、熱成形性、二次発泡性、耐水性等を備え、且つ、
製造コストが低く低価格で供給可能な熱成形用発泡シー
ト、及び該発泡シートを熱成形してなる果菜容器を提供
することを目的とするものである。SUMMARY OF THE INVENTION The present invention has been made to solve the above problems, and is provided with flexibility, appropriate rigidity, light weight, thermoformability, secondary foamability, water resistance, and the like. ,
It is an object of the present invention to provide a foam sheet for thermoforming which can be supplied at a low cost with a low manufacturing cost, and a fruit and vegetable container obtained by thermoforming the foam sheet.
【０００８】[0008]
【課題を解決するための手段】即ち本発明の熱成形用発
泡シートは、［１］（１）ポリスチレン系樹脂６０〜９
５重量％、（２）低密度ポリエチレン系樹脂２〜１５重
量％、（３）スチレン−ブタジエン−ブチレン−スチレ
ンブロック共重合体及び／又はスチレン−エチレン−ブ
チレン−スチレンブロック共重合体３〜２５重量％（但
し、（１）、（２）及び（３）の合計は１００重量％）
とからなる混合樹脂を主成分とし、密度が０．１ｇ／ｃ
ｍ3以下、厚みが１０ｍｍ以下であることを特徴とする
熱成形用発泡シート、［２］熱成形用発泡シートの密度
が０．０２〜０．１ｇ／ｃｍ3である前記（１）記載の
熱成形用発泡シート、［３］前記（１）又は（２）記載
の熱成形用発泡シートを熱成形することによって得られ
た、果菜収納凹部を有する果菜容器、を要旨とする。That is, the foam sheet for thermoforming of the present invention is [1] (1) polystyrene resin 60-9.
5% by weight, (2) low density polyethylene resin 2 to 15% by weight, (3) styrene-butadiene-butylene-styrene block copolymer and / or styrene-ethylene-butylene-styrene block copolymer 3 to 25% by weight % (However, the total of (1), (2) and (3) is 100% by weight)
The main component is a mixed resin consisting of and a density of 0.1 g / c
m 3 or less, the foam sheet for thermoforming, wherein the thickness is 10mm or less, [2] the density of the foam sheet for thermoforming is 0.02~0.1g / cm 3 (1) according The gist is a foamed sheet for thermoforming, and [3] a fruit and vegetable container having a fruit and vegetable storage recess obtained by thermoforming the foamed sheet for thermoforming according to (1) or (2).
【０００９】[0009]
【発明の実施の形態】本発明の熱成形用発泡シート（以
下、単に発泡シートという。）は、（１）ポリスチレン
系樹脂（以下、ＰＳ系樹脂という。）６０〜９５重量
％、（２）低密度ポリエチレン系樹脂（以下、ＬＤＰＥ
という。）２〜１５重量％、（３）スチレン−ブタジエ
ン−ブチレン−スチレンブロック共重合体（以下、ＳＢ
ＢＳという。）及び／又はスチレン−エチレン−ブチレ
ン−スチレンブロック共重合体（以下、ＳＥＢＳとい
う。）３〜２５重量％（但し、（１）、（２）及び
（３）の合計は１００重量％）とからなる混合樹脂を主
成分とする。かかる構成の発泡シートは熱成形と柔軟性
を兼ね備えているので、該発泡シートから熱成形によっ
て得られる成形品は、熱成形に用いる金型の形状通りの
形状になっている（以下、成形品が金型の形状通りの形
状になっていることを金型再現性という。）と共に柔軟
性に富むものである。BEST MODE FOR CARRYING OUT THE INVENTION The foam sheet for thermoforming of the present invention (hereinafter, simply referred to as a foam sheet) includes (1) 60 to 95% by weight of polystyrene resin (hereinafter referred to as PS resin), and (2). Low density polyethylene resin (hereinafter LDPE
Say. ) 2 to 15% by weight, (3) styrene-butadiene-butylene-styrene block copolymer (hereinafter referred to as SB
It is called BS. ) And / or styrene-ethylene-butylene-styrene block copolymer (hereinafter referred to as SEBS) 3 to 25% by weight (however, the total of (1), (2) and (3) is 100% by weight). The mixed resin is as a main component. Since the foamed sheet having such a structure has both thermoforming and flexibility, a molded article obtained by thermoforming from the foamed sheet has a shape that is the same as the shape of the mold used for thermoforming (hereinafter, the molded article). The mold has the same shape as that of the mold, which is called mold reproducibility.)
【００１０】前記ポリスチレン系樹脂とは、スチレンを
主体とする重合体をいい、スチレン単独重合体のみなら
ず、スチレンと共重合し得るビニル系単量体とスチレン
との共重合体、例えば、ポリスチレンとスチレンーブタ
ジエン共重合体との共重合物（一般に耐衝撃性ポリスチ
レン樹脂と呼ばれている。）、又は前記２種以上の混合
物も本発明のポリスチレン系樹脂の範囲に含まれるもの
である。尚、本発明におけるポリスチレン系樹脂は、ス
チレン成分が８０モル％以上のものであり、９０モル％
以上のものが好ましい。The polystyrene resin means a polymer mainly composed of styrene, and not only a styrene homopolymer but also a copolymer of styrene and a vinyl monomer copolymerizable with styrene, such as polystyrene. A copolymer of styrene with a styrene-butadiene copolymer (generally called an impact-resistant polystyrene resin) or a mixture of two or more of the above is also included in the scope of the polystyrene resin of the present invention. The polystyrene resin in the present invention has a styrene component of 80 mol% or more, and 90 mol%
The above is preferable.
【００１１】前記低密度ポリエチレン系樹脂とは、エチ
レンを主体とする重合体をいい、エチレンホモポリマー
のみならず、酢酸ビニル、メタクリレート、アクリレー
ト、プロピレン、α−オレフィン等、或いはその他エチ
レンと共重合可能なビニル系モノマーと、エチレンとの
共重合体も含まれる。尚、本発明における低密度ポリエ
チレン系樹脂は、密度が０．９１〜０．９３ｇ／ｃｍ３
であり、エチレン成分が５０モル％以上のものが好まし
く、６０モル％以上のものがより好ましい。The low density polyethylene resin means a polymer mainly composed of ethylene, and not only ethylene homopolymer but also vinyl acetate, methacrylate, acrylate, propylene, α-olefin, etc., or other copolymerizable with ethylene. A copolymer of a vinyl monomer and ethylene is also included. The low-density polyethylene resin used in the present invention has a density of 0.91 to 0.93 g / cm 3.
The ethylene component is preferably 50 mol% or more, and more preferably 60 mol% or more.
【００１２】前記ＳＢＢＳは、スチレン、ブタジエン、
ブチレンを構成単位とし、スチレン−ブタジエン−ブチ
レン−スチレン構造を有するエラストマーであり、スチ
レン成分単位が１０〜６５モル％であり、好ましくは２
０〜５５モル％のものである。ＳＢＢＳはＬＤＰＥ及び
ＰＳ系樹脂との相溶性に優れ、加工性能にも優れている
ので、ＰＳ系樹脂とＬＤＰＥとＳＢＢＳとからなる混合
樹脂を主成分とする発泡シートは、従来のＰＳ系樹脂を
主成分とする発泡シートでは得られなかったソフト感を
有しており、柔軟性に富むものとなる。ＳＢＢＳの具体
的な一例としては、旭化成株式会社製の商品名「タフテ
ックＰ」が挙げられる。The SBBS is styrene, butadiene,
An elastomer having butylene as a constitutional unit and having a styrene-butadiene-butylene-styrene structure, wherein the styrene component unit is 10 to 65 mol%, preferably 2
0 to 55 mol%. Since SBBS has excellent compatibility with LDPE and PS-based resins and excellent processing performance, a foamed sheet containing PS-based resin and a mixed resin of LDPE and SBBS as a main component is a conventional PS-based resin. It has a soft feeling that is not obtained with the foamed sheet as the main component, and is highly flexible. As a specific example of SBBS, the product name “Tuftec P” manufactured by Asahi Kasei Corporation can be mentioned.
【００１３】前記ＳＥＢＳは、スチレン、エチレン、ブ
チレンを構成単位とし、スチレン−エチレン−ブチレン
−スチレン構造を有するエラストマーであり、スチレン
成分単位が１０〜６５モル％であり、好ましくは２０〜
５５モル％のものである。ＳＥＢＳは、ＳＢＢＳと同様
に、ＬＤＰＥ及びＰＳ系樹脂との相溶性に優れ、加工性
能にも優れているので、ＰＳ系樹脂とＬＤＰＥとＳＥＢ
Ｓとからなる混合樹脂を主成分とする発泡シートは、従
来のＰＳ系樹脂を主成分とする発泡シートでは得られな
かったソフト感を有しており、柔軟性に富み、特に低温
脆性に優れている。ＳＥＢＳの具体的な一例としては、
旭化成株式会社製の商品名「タフテックＨ」が挙げられ
る。The SEBS is an elastomer having styrene-ethylene-butylene-styrene structure with styrene, ethylene and butylene as constitutional units, and the styrene component unit is 10 to 65 mol%, preferably 20 to
55 mol%. Like SBBS, SEBS has excellent compatibility with LDPE and PS-based resins and excellent processing performance, so PS-based resins, LDPE and SEB
The foamed sheet containing a mixed resin of S as a main component has a soft feeling that cannot be obtained with conventional foamed sheets containing a PS-based resin as a main component, is rich in flexibility, and is particularly excellent in low-temperature brittleness. ing. As a specific example of SEBS,
The product name "Tough Tech H" manufactured by Asahi Kasei Co., Ltd. may be mentioned.
【００１４】本発明における前記混合樹脂は、（１）Ｐ
Ｓ系樹脂６０〜９５重量％、（２）ＬＤＰＥ２〜１５重
量％、（３）ＳＢＢＳ及び／又はＳＥＢＳ３〜２５重量
％（但し、（１）、（２）及び（３）の合計は１００重
量％）からなり、（１）ＰＳ系樹脂６０〜８０重量％、
（２）ＬＤＰＥ５〜１５重量％、（３）ＳＢＢＳ及び／
又はＳＥＢＳ１５〜２５重量％（但し、（１）、（２）
及び（３）の合計は１００重量％）からなることが好ま
しい。The mixed resin in the present invention is (1) P
S-based resin 60 to 95% by weight, (2) LDPE 2 to 15% by weight, (3) SBBS and / or SEBS 3 to 25% by weight (however, the total of (1), (2) and (3) is 100% by weight. (1) PS resin 60 to 80% by weight,
(2) LDPE 5 to 15% by weight, (3) SBBS and /
Or 15 to 25% by weight of SEBS (however, (1), (2)
And (3) is preferably 100% by weight).
【００１５】前記混合樹脂におけるＰＳ系樹脂の配合量
が６０重量％未満の場合は、熱成形性が悪くなる上に加
熱時の発泡シートの収縮も大きくなりすぎる虞がある。
一方、９５重量％を超える場合は、得られる発泡シート
が脆くなり、果菜容器用発泡シートに要求される柔軟性
を発揮できない虞がある。If the amount of the PS-based resin in the mixed resin is less than 60% by weight, the thermoformability may deteriorate and the foamed sheet may shrink too much during heating.
On the other hand, when it exceeds 95% by weight, the obtained foamed sheet becomes brittle, and the flexibility required for the foamed sheet for fruit and vegetables containers may not be exhibited.
【００１６】混合樹脂におけるＬＤＰＥの配合量が２重
量％未満の場合は、得られる発泡シートが脆くなり、果
菜容器用発泡シートに要求される柔軟性を発揮できなく
なる虞があり、１５重量％を超える場合は、熱成形する
際に発泡シートの表面が溶けるような状態になると共
に、熱成形性が悪くなり、金型と同じ形状の容器を得る
ことができなくなる虞がある。If the blending amount of LDPE in the mixed resin is less than 2% by weight, the resulting foamed sheet may become brittle and the flexibility required for the foamed sheet for fruit and vegetable containers may not be exhibited. If it exceeds the above range, the surface of the foamed sheet may be melted during thermoforming, and the thermoformability may be deteriorated, so that a container having the same shape as the mold may not be obtained.
【００１７】混合樹脂におけるＳＢＢＳ及び／又はＳＥ
ＢＳの配合量が、３重量％未満の場合は、得られる発泡
シートが脆くなり、果菜容器用発泡シートに要求される
柔軟性を発揮できなくなる虞がある。一方、２５重量％
を超える場合は、熱成形する際に発泡シートの表面が溶
けたような状態になると共に、発泡シートのコストが高
くなる。SBBS and / or SE in mixed resin
If the blending amount of BS is less than 3% by weight, the resulting foamed sheet becomes brittle, and the flexibility required for the foamed sheet for fruit and vegetables containers may not be exhibited. On the other hand, 25% by weight
When it exceeds, the surface of the foamed sheet is melted during thermoforming, and the cost of the foamed sheet is increased.
【００１８】本発明の発泡シートは、以上説明したよう
に、ＰＳ系樹脂と、ＬＤＰＥと、ＳＢＢＳ及び／又はＳ
ＥＢＳとが特定の割合で配合された混合樹脂を主成分と
するので、果菜容器に要求される柔軟性及び適度な剛性
を有し、更に軽量で熱成形性に優れている。As described above, the foamed sheet of the present invention contains PS resin, LDPE, SBBS and / or S.
Since the main component is a mixed resin mixed with EBS in a specific ratio, it has the flexibility and appropriate rigidity required for a fruit and vegetable container, and is lightweight and excellent in thermoformability.
【００１９】本発明の発泡シートは、前記混合樹脂のみ
からなるものに限定されず、本発明の所期の目的を損な
わない範囲において、更に他の合成樹脂が混合されてい
ても良い。例えば、ポリプロピレン等のポリオレフィ
ン、ポリエチレンテレフタレート等のポリエステル、ポ
リカーボネート、ポリアミド、ＳＥＢＳ、ＳＢＢＳ以外
の熱可塑性エラストマー等が挙げられる。これらの他の
樹脂の配合量は３５重量％以下であることが好ましい。The foamed sheet of the present invention is not limited to the above-mentioned mixed resin alone, and may further contain other synthetic resin within the range not impairing the intended purpose of the present invention. Examples thereof include polyolefins such as polypropylene, polyesters such as polyethylene terephthalate, polycarbonates, polyamides, thermoplastic elastomers other than SEBS and SBBS. The blending amount of these other resins is preferably 35% by weight or less.
【００２０】さらに、本発明においては、発泡時の発泡
剤の透過を防ぎ、発泡シートの収縮を抑制するために、
前記混合樹脂中に収縮防止剤を添加することが好まし
い。収縮防止剤の具体例としては、例えば、ポリオキシ
エチレンモノミリステート、ポリオキシプロピレンモノ
ミリステート、ポリオキシエチレンモノパルミテート、
ポリオキシプロピレンモノパルミテート、ポリオキシエ
チレンモノステアレート、ポリオキシプロピレンモノス
テアレート、ポリオキシエチレンジステアレート、モノ
ラウリン酸グリセライド、モノミノスチン酸グリセライ
ド、モノパルミチン酸グリセライド、モノステアリン酸
グリセライド、モノアラキン酸グリセライド、ジラウリ
ン酸グリセライド、ジパルミチン酸グリセライド、ジス
テアリン酸グリセライド、1−パルミト−2−ステアリン
酸グリセライド、1−ステアロ−2−ミリスチン酸グリセ
ライド、トリステアリン酸グリセライド、モノべヘン酸
グリセライド等の各種脂肪族エステルが挙げられる。こ
れらの収縮防止剤の添加量は、０．５〜１０重量部であ
る。Further, in the present invention, in order to prevent the permeation of the foaming agent during foaming and to suppress the shrinkage of the foamed sheet,
It is preferable to add a shrinkage inhibitor to the mixed resin. Specific examples of the shrinkage inhibitor include, for example, polyoxyethylene monomyristate, polyoxypropylene monomyristate, polyoxyethylene monopalmitate,
Polyoxypropylene monopalmitate, polyoxyethylene monostearate, polyoxypropylene monostearate, polyoxyethylene distearate, monolauric acid glyceride, monominosuccinic acid glyceride, monopalmitic acid glyceride, monostearic acid glyceride, monoarachidic acid glyceride, Dilauric acid glyceride, dipalmitic acid glyceride, distearic acid glyceride, 1-palmito-2-stearic acid glyceride, 1-stearo-2-myristic acid glyceride, tristearic acid glyceride, various aliphatic esters such as monobehenic acid glyceride Can be mentioned. The addition amount of these shrinkage inhibitors is 0.5 to 10 parts by weight.
【００２１】その他、無機充填剤も収縮防止剤として用
いることができる。In addition, inorganic fillers can also be used as shrinkage inhibitors.
【００２２】本発明の発泡シートの密度は、０．１ｇ／
ｃｍ3以下である。発泡シートの密度が０．１ｇ／ｃｍ3
を超えると、緩衝性が失われ、熱成形性が悪くなる虞が
ある。発泡シートの密度が低くなると、熱成形時の伸び
が不十分なものとなる傾向があり、また、発泡シートを
製造すること自体も困難になる傾向があるので、発泡シ
ートの密度は、０．０２〜０．１ｇ／ｃｍ3であること
が好ましく、０．０４〜０．１ｇ／ｃｍ3であることが
より好ましい。The density of the foamed sheet of the present invention is 0.1 g /
It is not more than cm 3 . Foam sheet density is 0.1g / cm 3
If it exceeds, the buffering property may be lost and the thermoformability may be deteriorated. When the density of the foamed sheet is low, the elongation at the time of thermoforming tends to be insufficient, and it is difficult to manufacture the foamed sheet itself. Therefore, the density of the foamed sheet is 0. it is preferably 02~0.1g / cm 3, more preferably 0.04~0.1g / cm 3.
【００２３】本発明の発泡シートの厚みは１０ｍｍ以下
であり、緩衝性と熱成形時における発泡シートの破れ防
止という観点からは、好ましくは２〜８ｍｍであり、よ
り好ましくは２〜６ｍｍである。発泡シートの厚みが１
０ｍｍを超える場合は、発泡シートの平滑性、外観にお
いて良好なものを得ることが困難となり、熱成形におい
ても優れたものが得られない虞がある。The foamed sheet of the present invention has a thickness of 10 mm or less, preferably 2 to 8 mm, and more preferably 2 to 6 mm from the viewpoint of cushioning property and prevention of tearing of the foamed sheet during thermoforming. Foam sheet thickness is 1
When it exceeds 0 mm, it is difficult to obtain a foamed sheet having good smoothness and appearance, and it may not be possible to obtain an excellent one even in thermoforming.
【００２４】本発明の発泡シートにおいては、独立気泡
率が４０％以上であることが好ましく、５０％以上であ
ることがより好ましく、７０％以上であることが更に好
ましい。独立気泡率が４０％未満の場合は、熱成形時の
二次発泡性、緩衝性、反発弾性が失われる虞がある。In the foamed sheet of the present invention, the closed cell ratio is preferably 40% or more, more preferably 50% or more, and further preferably 70% or more. When the closed cell ratio is less than 40%, there is a possibility that secondary foamability, cushioning property and impact resilience during thermoforming may be lost.
【００２５】前記独立気泡率の測定は、ＡＳＴＭ Ｄ２
８５６手順Ｃにより、連続気泡率（％）を求め、下記式
（２）より求められる値である。但し、後述する積層発
泡シートの場合は、熱可塑性樹脂層の厚み分の体積を積
層発泡シートサンプル体積から差し引いて発泡シートの
みの独立気泡率を算出することとする。The closed cell ratio is measured by ASTM D2.
The open cell ratio (%) is determined by Procedure C 856, and is a value determined by the following equation (2). However, in the case of a laminated foam sheet described below, the volume of the thickness of the thermoplastic resin layer is subtracted from the laminated foam sheet sample volume to calculate the closed cell rate of only the foam sheet.
【００２６】[0026]
【数１】 独立気泡率（％）＝１００−連続気泡率（％） ・・・（２）[Equation 1] Closed cell rate (%) = 100-Open cell rate (%) (2)
【００２７】本発明の発泡シートは、その片面又は両面
にシートやフィルムを積層することにより、熱成形性、
剛性、引裂き強度等が改良された積層発泡シートとして
構成することができる。上記シート、フィルムを構成す
る熱可塑性樹脂としては、高密度ポリエチレン、低密度
ポリエチレン、直鎖状低密度ポリエチレン、エチレン−
酢酸ビニル共重合体等のポリエチレン系樹脂、ポリスチ
レン、耐衝撃性ポリスチレン等のポリスチレン系樹脂、
ポリプロピレン系樹脂、ポリエステル系樹脂等が挙げら
れる。これらの熱可塑性樹脂のうち、接着層を設けなく
ても積層可能なポリエチレン系樹脂やポリスチレン系樹
脂が好ましい。The foamed sheet of the present invention has a thermoformability obtained by laminating a sheet or film on one or both sides thereof.
It can be configured as a laminated foam sheet having improved rigidity, tear strength and the like. Examples of the thermoplastic resin forming the sheet or film include high-density polyethylene, low-density polyethylene, linear low-density polyethylene, and ethylene-
Polyethylene resin such as vinyl acetate copolymer, polystyrene, polystyrene resin such as high impact polystyrene,
Examples include polypropylene-based resins and polyester-based resins. Of these thermoplastic resins, polyethylene-based resins and polystyrene-based resins that can be laminated without providing an adhesive layer are preferable.
【００２８】本発明の発泡シートは、例えば押出機内で
上記混合樹脂を溶融し、これに発泡剤を添加混練した
後、押出機先端の環状ダイから押出して円筒状に発泡さ
せた後、この円筒状発泡体を押出方向に切り開いてシー
ト状とすることによって製造することができる。発泡シ
ートを得るために用いる発泡剤としては、例えば、ノル
マルブタン、イソブタン、ノルマルブタンとイソブタン
との混合物、ノルマルペンタン、イソペンタン、ヘキサ
ン等の脂肪族炭化水素、シクロブタン、シクロペンタン
等の環式脂肪族炭化水素、その他ハロゲン化炭化水素、
二酸化炭素、水、加熱分解型発泡剤等が挙げられる。こ
れらの発泡剤は単独又は２種以上を組み合わせて使用さ
れる。The foamed sheet of the present invention is obtained by, for example, melting the mixed resin in an extruder, adding and kneading the foaming agent, and extruding from an annular die at the tip of the extruder to foam into a cylindrical shape. It can be manufactured by cutting open the foam body in the extrusion direction to form a sheet. Examples of the foaming agent used to obtain the foamed sheet include, for example, normal butane, isobutane, a mixture of normal butane and isobutane, normal pentane, isopentane, aliphatic hydrocarbon such as hexane, cyclobutane, and cycloaliphatic cyclopentane. Hydrocarbons, other halogenated hydrocarbons,
Carbon dioxide, water, a heat decomposition type foaming agent, etc. are mentioned. These foaming agents are used alone or in combination of two or more kinds.
【００２９】発泡剤の配合量は、発泡剤の種類、目的と
する発泡シートの密度により適宜定められる。例えば発
泡剤としてノルマルブタンを主成分とするものを用いる
場合、密度０．０２〜０．１ｇ／ｃｍ3の発泡シートを
得るために必要な発泡剤の配合量は、樹脂物１００重量
部に対して１〜３０重量部程度である。The blending amount of the foaming agent is appropriately determined depending on the type of the foaming agent and the desired density of the foamed sheet. For example, when a foaming agent containing normal butane as a main component is used, the blending amount of the foaming agent required to obtain a foam sheet having a density of 0.02 to 0.1 g / cm 3 is 100 parts by weight of the resin material. 1 to 30 parts by weight.
【００３０】発泡シートを製造する際には、一般に気泡
核生成剤が添加される。この気泡核生成剤としては、た
とえば、タルクの如き無機物質の他、押出機内の温度で
分解してガスを発生する如き化学発泡剤も気泡核生成剤
として用いることができる。また押出機内の温度で反応
して炭酸ガスを発生する酸−アルカリの組み合わせ、た
とえば、クエン酸と重炭酸ナトリウム、クエン酸のアル
カリ塩と重炭酸ナトリウム等を組み合わせたものも気泡
核生成剤として用いることができる。これらの気泡核生
成剤を添加することにより、得られる発泡シートの気泡
の大きさを任意に調整することができると共に、発泡シ
ートの柔軟性、ソフト感等も向上させることができる。In producing the foamed sheet, a cell nucleating agent is generally added. As the cell nucleating agent, for example, in addition to an inorganic substance such as talc, a chemical foaming agent capable of decomposing at an internal temperature of the extruder to generate gas can be used. Also, an acid-alkali combination that reacts at the temperature in the extruder to generate carbon dioxide, for example, a combination of citric acid and sodium bicarbonate, an alkali salt of citric acid and sodium bicarbonate, and the like is also used as a bubble nucleating agent. be able to. By adding these cell nucleating agents, it is possible to arbitrarily adjust the cell size of the obtained foamed sheet and improve the flexibility and softness of the foamed sheet.
【００３１】前記積層発泡シートは、発泡シートのみを
製造した後、別工程で製造されたフィルムやシートを積
層する方法、押出発泡した発泡シートに他の押出機から
フィルムやシートを押出して積層するエクストルージョ
ンラミネート法、発泡性混合溶融樹脂と非発泡性熱可塑
性溶融樹脂とを共押出する共押出法により得ることがで
きる。Regarding the laminated foamed sheet, after the foamed sheet alone is manufactured, the film or sheet manufactured in a separate step is laminated, or the extruded foamed sheet is laminated by extruding the film or sheet from another extruder. It can be obtained by an extrusion laminating method or a co-extrusion method in which a foamable mixed molten resin and a non-foamable thermoplastic molten resin are co-extruded.
【００３２】本発明の果菜容器は、前記した本発明の発
泡シートを熱成形することによって得られたものであ
る。該果菜容器は、その一例を図１に示すように、果菜
収納凹部１を有する。果菜収納凹部１の数に制限はない
が、通常２〜３０形成される。果菜収納凹部１の形状
は、果菜を収納することさえできればいかなる形状でも
よいが、成形が容易であると共に果菜を効率良く収納で
きることから、図１に示すような、略半球形状が選択さ
れる。果菜容器２の外周の形状に制限はないが、通常は
取扱が容易であることから矩形が選択される。The fruit and vegetable container of the present invention is obtained by thermoforming the above-mentioned foamed sheet of the present invention. The fruit and vegetable container has a fruit and vegetable storage recess 1 as shown in FIG. The number of the fruit vegetable storage recesses 1 is not limited, but usually 2 to 30 are formed. The shape of the fruit and vegetable storage recess 1 may be any shape as long as it can store the fruit and vegetables, but since it is easy to mold and the fruit and vegetables can be efficiently stored, a substantially hemispherical shape as shown in FIG. 1 is selected. The shape of the outer periphery of the fruit and vegetable container 2 is not limited, but a rectangle is usually selected because it is easy to handle.
【００３３】果菜容器２は、果菜を保護するための緩衝
性に優れるとともに保形性に優れることが要求される。
このような点を考慮すると本発明の果菜容器２の平均密
度は、好ましくは０．１ｇ／ｃｍ3以下であり、より好
ましくは０．０２〜０．１ｇ／ｃｍ3であり、特に好ま
しくは０．０４〜０．１ｇ／ｃｍ3である。The fruit and vegetable container 2 is required to have excellent buffering properties for protecting the fruit and vegetables and excellent shape retention.
Considering such points, the average density of the fruit and vegetable container 2 of the present invention is preferably 0.1 g / cm 3 or less, more preferably 0.02 to 0.1 g / cm 3 , and particularly preferably 0. It is 0.04 to 0.1 g / cm 3 .
【００３４】平均密度が０．１ｇ／ｃｍ3未満の容器
は、発泡シートの密度、該発泡シートの二次発泡性を前
提として、成形金型の型合わせ時の隙間等を適宜調整す
ることにより得ることができる。For a container having an average density of less than 0.1 g / cm 3 , the density of the foamed sheet and the secondary foamability of the foamed sheet are premised, and the gap and the like at the time of matching the molding dies are appropriately adjusted. Obtainable.
【００３５】本明細書における果菜容器の平均密度は、
該容器を碁盤の目状に３ｃｍ間隔で分割し、各分割体か
ら任意に一辺２ｃｍ程度の略正方形の測定サンプルを切
り出し、各サンプルについて外形寸法から求められる体
積と、重量から各サンプルの密度（ｇ／ｃｍ3）を求
め、それらの値の算術平均値として算出される。The average density of the fruit and vegetable containers in this specification is
The container was divided into 3 square intervals in a grid pattern, and a substantially square measurement sample with a side of about 2 cm was arbitrarily cut out from each divided body, and the volume of each sample determined from the external dimensions and the density of each sample from the weight ( g / cm 3 ) is calculated and calculated as the arithmetic mean value of those values.
【００３６】本発明の果菜容器２における果菜収納凹部
１の肉厚は、収納される果菜の重さ及び果菜の表面の傷
つき易さに応じて選択される。具体的には、林檎、梨、
トマトを収納する場合には、果菜収納凹部１の厚みが１
〜３ｍｍ、桃、メロンを収納する場合には、果菜収納凹
部１の厚みが１〜４ｍｍとなるようにすることが好まし
い。本発明の発泡シートを使用すると、緩衝性に優れる
ため従来のものよりも厚みを薄くすることができる。The wall thickness of the fruit vegetable storage recess 1 in the fruit vegetable container 2 of the present invention is selected according to the weight of the fruit vegetable to be stored and the easiness of the surface of the fruit vegetable to be damaged. Specifically, apple, pear,
When storing tomatoes, the thickness of the fruit vegetable storage recess 1 is 1
When storing peaches and melons of ˜3 mm, it is preferable that the thickness of the fruit vegetable storage recess 1 is 1 to 4 mm. When the foamed sheet of the present invention is used, since it has excellent cushioning properties, it can be made thinner than conventional ones.
【００３７】尚、前記果菜収納凹部１の厚みは、一方の
収納凹部側面上端から反対側の収納凹部側面上端にかけ
て凹部１の中心を通る線を引き、該線上において等間隔
で７箇所以上の厚みを測定し、それらの算術平均値とし
て求められる値である。The thickness of the fruit and vegetable storage recessed portion 1 is determined by drawing a line passing through the center of the recessed portion 1 from the upper end of one side of the stored recessed portion to the upper end of the opposite side of the stored recessed portion, and at a thickness of 7 or more points at equal intervals. Is a value obtained by measuring and calculating the arithmetic mean value thereof.
【００３８】本発明の果菜容器２は、前記した発泡シー
トを熱成形することによって製造される。従って、熱成
形の際に発泡シートが引き延ばされて果菜収納凹部１の
シート厚みが薄くなる。このため、必要とする果菜収納
凹部１の平均シート厚みの０．８〜３倍の厚みの発泡シ
ートを用いることが好ましい。The fruit and vegetable container 2 of the present invention is manufactured by thermoforming the above-mentioned foamed sheet. Therefore, the foam sheet is stretched during thermoforming, and the sheet thickness of the fruit and vegetable storage recess 1 is reduced. For this reason, it is preferable to use a foamed sheet having a thickness of 0.8 to 3 times the average sheet thickness of the required fruit and vegetable storage concave portion 1.
【００３９】本発明の発泡シートを用いて果菜容器を熱
成形する方法について詳述する。まず発泡シートをヒー
ター等によって加熱して軟化させ、次に果菜容器に対応
した形状の金型で加熱軟化させた発泡シートを挟み、発
泡シートを容器形状の金型面に密着させることにより、
金型形状に沿った果菜容器が得られる。The method of thermoforming a fruit and vegetable container using the foamed sheet of the present invention will be described in detail. First, the foamed sheet is heated by a heater or the like to be softened, and then the foamed sheet softened by heating is sandwiched by a mold having a shape corresponding to the vegetable container, and the foamed sheet is brought into close contact with the mold surface of the container shape,
A vegetable container conforming to the mold shape can be obtained.
【００４０】本発明の発泡シートを、真空成形法により
熱成形する場合は、通常、シートの幅方向両端縁部を一
定幅でクランプするので、果菜収納凹部１として形成さ
れる発泡シートの部分、すなわち略金型凹部上に位置す
る部分のみが伸ばされて成形される。従って、発泡シー
ト両端縁部のクランプ間の幅を狭くしつつ真空成形を行
うことによって、シートの金型凹部上に位置する部分の
周囲部を、金型凹部へ引き込んで熱成形することが好ま
しい。このように熱成形することにより、容器厚みの比
較的均一な果菜容器が得られる。When the foamed sheet of the present invention is thermoformed by a vacuum forming method, usually, both widthwise end edges of the sheet are clamped with a constant width. That is, only the portion located above the recess of the mold is stretched and molded. Therefore, it is preferable to perform thermoforming by drawing the peripheral portion of the portion of the sheet located on the mold recess into the mold recess by vacuum forming while narrowing the width between the clamps at both edges of the foamed sheet. . By thermoforming in this way, a fruit and vegetable container having a relatively uniform container thickness can be obtained.
【００４１】また、成形に用いる雄型と雌型の形状、型
合わせ時の隙間、成形スピード等を調整したり、果菜収
納凹部１形状と、これらの配置等の調製を組み合わせて
おこなうことにより、果菜収納凹部１の平均シート厚
み、密度等を更に良好な範囲に調整することができる。Further, by adjusting the shapes of the male and female molds used for molding, the gaps at the time of mold matching, the molding speed, and the like, or by combining the shape of the fruit vegetable storage recess 1 and the arrangement thereof, and the like, The average sheet thickness, density and the like of the fruit and vegetable storage concave portion 1 can be adjusted to a more preferable range.
【００４２】また、前記積層発泡シートを用いて果菜容
器を熱成形すると、複雑なリブ形状を有するものや、果
菜収納凹部１の深さが深い果菜容器２であっても容易に
得ることができ、得られた果菜容器２は剛性に優れ、熱
成形時に表面が溶けた状態にならないので外観にも優れ
たものとなる。Further, by thermoforming a fruit and vegetable container using the above-mentioned laminated foamed sheet, it is possible to easily obtain a fruit and vegetable container having a complicated rib shape or a fruit and vegetable container 2 having a deep recess 1 for fruit and vegetables. The obtained fruit and vegetable container 2 has excellent rigidity and does not have a melted surface during thermoforming, and thus has an excellent appearance.
【００４３】[0043]
【実施例】以下、実施例、比較例を挙げて本発明を更に
詳細に説明する。EXAMPLES The present invention will be described in more detail with reference to Examples and Comparative Examples.
【００４４】尚、実施例、比較例において用いては、Ｐ
Ｓ樹脂として、エイ・アンド・エムスチレン株式会社製
スタイロン６８５（密度１．０５ｇ/ｃｍ３）を用い、
ＬＤＰＥとして住友化学株式会社製のＦ１０２（密度
０．９２ｇ／ｃｍ3）を用い、ＳＢＢＳの一として、旭
化成株式会社製の商品名「タフテックＰシリーズ ＪＴ
８３Ｐ」（ＳＢＢＳ１、密度０．８９ｇ/ｃｍ３）を用
い、他のＳＢＢＳとして、旭化成株式会社の商品名「タ
フテックＰシリーズ ＪＴ８４Ｐ」（ＳＢＢＳ２、密度
０．９７ｃｍ３）を用い、ＳＥＢＳとして、旭化成株式
会社製商品名「タフテックＨシリーズ Ｈ１０４１」
（密度０．９１ｇ/ｃｍ３）を用いた。When used in Examples and Comparative Examples, P
As S resin, Styron 685 (density 1.05 g / cm 3 ) manufactured by A & M Styrene Co., Ltd. is used,
As LDPE, Sumitomo Chemical Co., Ltd. F102 (density 0.92 g / cm 3 ) is used, and as one of SBBS, Asahi Kasei Corporation trade name “Tuftec P Series JT”.
83P ”(SBBS1, density 0.89 g / cm 3 ) is used as another SBBS, and the Asahi Kasei Corporation trade name“ Tuftec P Series JT84P ”(SBBS2, density 0.97 cm 3 ) is used as SEBS and Asahi Kasei stock. Company name "Tuftec H Series H1041"
(Density 0.91 g / cm 3 ) was used.
【００４５】実施例１
表１に示す割合で各種樹脂を配合した混合樹脂を準備し
た。Example 1 A mixed resin containing various resins in the proportions shown in Table 1 was prepared.
【００４６】上記混合樹脂１００重量部に収縮防止剤と
してモノステアリン酸グリセライドが1重量部、気泡核
生成剤としてタルク1重量部の割合で添加した。To 100 parts by weight of the above mixed resin, 1 part by weight of glyceride monostearate as a shrinkage inhibitor and 1 part by weight of talc as a cell nucleating agent were added.
【００４７】これらの混合樹脂を押出機に供給し、加熱
し溶融し混練してから、混合樹脂１００重量部に対し
て、発泡剤として混合ブタン（ノルマルブタン３５重量
％とイソブタン６５重量％との混合物）５．３重量部を
注入し、更に溶融混練した後、樹脂温度１５０℃に調整
してサーキュラーダイより円筒状に押出発泡させた。押
出された円筒状発泡体の内面及び外面をエアーにて冷却
しながらバルーンを形成させ、これを円柱状冷却装置の
表面上を通過させながら引き取り、その後、押出し方向
に沿って切り開いて発泡シートを得た。得られた発泡シ
ートの密度、厚さ、柔軟性を表１に示す。These mixed resins are supplied to an extruder, heated, melted and kneaded, and then mixed with 100 parts by weight of the mixed resin, butane (35% by weight of normal butane and 65% by weight of isobutane) as a foaming agent. After injecting 5.3 parts by weight of the mixture) and further melt-kneading, the resin temperature was adjusted to 150 ° C. and the mixture was extruded and foamed into a cylindrical shape from a circular die. A balloon is formed while cooling the inner and outer surfaces of the extruded cylindrical foam with air, and the balloon is drawn while passing over the surface of the columnar cooling device, and then cut along the extrusion direction to form a foam sheet. Obtained. Table 1 shows the density, thickness, and flexibility of the obtained foamed sheet.
【００４８】実施例２〜６
表１に示す割合で各種樹脂配合した混合樹脂を用いたこ
と以外は、実施例１と同様に発泡シートを得た。得られ
た発泡シートの密度、厚さ、柔軟性を表１に示す。尚、
実施例１〜６で得られた発泡シートの独立気泡率は、全
て８０％以上であった。Examples 2 to 6 Foamed sheets were obtained in the same manner as in Example 1 except that a mixed resin containing various resins in the proportions shown in Table 1 was used. Table 1 shows the density, thickness, and flexibility of the obtained foamed sheet. still,
The closed cell ratios of the foamed sheets obtained in Examples 1 to 6 were all 80% or more.
【００４９】比較例１〜５
表２に示す割合で各種樹脂配合した混合樹脂を用いたこ
と以外は、実施例１と同様に発泡シートを得た。得られ
た発泡シートの密度、厚さ、柔軟性を表２に示す。Comparative Examples 1 to 5 Foamed sheets were obtained in the same manner as in Example 1 except that a mixed resin containing various resins in the proportions shown in Table 2 was used. Table 2 shows the density, thickness, and flexibility of the obtained foamed sheet.
【００５０】実施例１〜６、比較例１〜５において得ら
れた発泡シートを用いて、真空加熱成形により、図１に
示すような果菜容器を成形した。発泡シートの二次発泡
性、金型再現性、熱成形後の表面状態を実施例１〜６に
ついては表１に、比較例１〜５については表２に示し
た。尚、上記果菜容器は外形が３００×４５０ｍｍ、凹
部の直径が１００ｍｍ、凹部の個数が８個である。Using the foamed sheets obtained in Examples 1 to 6 and Comparative Examples 1 to 5, a vegetable container as shown in FIG. 1 was molded by vacuum heat molding. The secondary foamability, mold reproducibility, and surface condition after thermoforming of the foamed sheet are shown in Table 1 for Examples 1 to 6 and Table 2 for Comparative Examples 1 to 5. The fruit container has an outer shape of 300 × 450 mm, a recess diameter of 100 mm, and eight recesses.
【００５１】[0051]
【表１】 [Table 1]
【００５２】[0052]
【表２】 [Table 2]
【００５３】尚、表２における発泡シートの密度、厚さ
等は、以下の通り測定して求めた値である。The density, thickness, etc. of the foamed sheet in Table 2 are values obtained by measurement as follows.
【００５４】発泡シートの厚さ
発泡シートの厚み方向垂直断面において、幅方向におい
て等間隔に２０箇所以上の測定点を選定し、発泡シート
厚みを測定し、各々の厚みの算術平均値として求めた。Thickness of Foamed Sheet In a cross section perpendicular to the thickness direction of the foamed sheet, 20 or more measurement points were selected at equal intervals in the width direction, the thickness of the foamed sheet was measured, and the arithmetic average value of each thickness was obtained. .
【００５５】発泡シートの密度
発泡シートのみの場合
厚み×縦１０ｃｍ×横１０cmの測定用サンプルを切り出
してサンプル重量（ｇ）を測定し、該重量（ｇ）を計算
により求められるサンプル体積（ｃｍ3）［１０（ｃ
ｍ）×１０（ｃｍ）×サンプルの厚み（ｃｍ）により求
める。］で割ることにより求めた。Density of Foamed Sheet In the case of foamed sheet alone, a measuring sample of thickness × length 10 cm × width 10 cm is cut out to measure the sample weight (g), and the weight (g) is calculated to obtain a sample volume (cm 3). ) [10 (c
m) × 10 (cm) × thickness of sample (cm). ] It was calculated by dividing by.
【００５６】発泡シートの密度
積層発泡シートの場合
厚み×縦１０ｃｍ×横１０cmの測定用サンプルを切り出
して重量（ｇ）を測定し、計算により求められる熱可塑
性樹脂層の重量（ｇ）［１０（ｃｍ）×１０（ｃｍ）×
熱可塑性樹脂層の厚み（ｃｍ）×熱可塑性樹脂層の密度
（ｇ／ｃｍ3）により求める。］を、積層発泡シートの
サンプル重量（ｇ）から差し引き、該差し引いて得られ
た値を、サンプル中の発泡シートのみの体積（ｃｍ3）
［１０（ｃｍ）×１０（ｃｍ）×サンプル中の発泡シー
トの厚み（ｃｍ）により求める。］で割ることにより求
めた。Density of Foamed Sheet In the case of laminated foamed sheet, a measurement sample of thickness × length 10 cm × width 10 cm is cut out and the weight (g) is measured, and the weight (g) [10 ( cm) x 10 (cm) x
It is determined by the thickness (cm) of the thermoplastic resin layer × the density (g / cm 3 ) of the thermoplastic resin layer. ] Is subtracted from the sample weight (g) of the laminated foam sheet, and the value obtained by the subtraction is the volume (cm 3 ) of only the foam sheet in the sample.
[10 (cm) × 10 (cm) × thickness (cm) of foamed sheet in sample) ] It was calculated by dividing by.
【００５７】上記実施例及び比較例にて得られた発泡シ
ートの柔軟性、熱成形後の表面状態、二次発泡性、熱成
形性の評価は以下のように評価した。The flexibility, the surface condition after thermoforming, the secondary foamability and the thermoformability of the foamed sheets obtained in the above Examples and Comparative Examples were evaluated as follows.
【００５８】発泡シートの柔軟性の評価
発泡シートを幅２０（ｍｍ）×長さ１２０（ｍｍ）の短
冊に切り出したものの長さ方向の端を手で持ってひねっ
た結果に基づいて、以下のようにて評価した。
◎：二回転ひねっても、短冊に裂けの発生がない。
○：二回転ひねると短冊に裂けが発生するが、一回転ひ
ねっただけでは短冊に裂けの発生がない。
×：一回転ひねっただけで、短冊に裂けが発生する。Evaluation of Flexibility of Foamed Sheet Based on the results obtained by cutting the foamed sheet into strips having a width of 20 (mm) × a length of 120 (mm) and twisting the ends in the lengthwise direction by hand, Was evaluated. ⊚: There is no tear in the strip even if it is twisted twice. ○: Twisting twice causes tears in the strip, but twisting only once does not cause tears in the strip. X: Tear occurs in the strip even if it is twisted once.
【００５９】熱成形後の表面状態の評価
上ヒーター２５０℃と下ヒーター２３０℃の間に発泡シ
ートを挿入して１２秒間加熱してから、発泡シートの表
面を目視にて観察し、以下の基準で評価した。
○：発泡シートの表面に変化がない場合
×：発泡シートの表面が溶けた場合Evaluation of Surface Condition after Thermoforming After inserting the foam sheet between the upper heater 250 ° C. and the lower heater 230 ° C. and heating for 12 seconds, the surface of the foam sheet was visually observed and the following criteria It was evaluated by. ◯: When the surface of the foamed sheet does not change ×: When the surface of the foamed sheet melts
【００６０】二次発泡性
押出発泡された発泡シートを３日間放置してから、上ヒ
ーター２５０℃と下ヒーター２３０℃の間に挿入し、１
２秒間加熱し、冷却した後の「厚さ１」を測定した。同
じ条件で押出発泡された発泡シートを１５日間放置して
から、同じ条件で加熱し、冷却した後の「厚さ２」を測
定した。
○：「厚さ１」と「厚さ２」が共に加熱する前の厚さの
１．３倍以上の場合
×：「厚さ１」が加熱する前の厚さの１．３倍以上、
「厚さ２」が加熱する前の厚さの１．３倍未満の場合Secondary Foamability The extruded foamed sheet was left for 3 days and then inserted between the upper heater 250 ° C. and the lower heater 230 ° C.
"Thickness 1" was measured after heating for 2 seconds and cooling. The foamed sheet extruded and foamed under the same conditions was left for 15 days, then heated under the same conditions and cooled to measure the "thickness 2". ◯: When “thickness 1” and “thickness 2” are both 1.3 times or more the thickness before heating ×: “thickness 1” is 1.3 times or more the thickness before heating,
When "thickness 2" is less than 1.3 times the thickness before heating
【００６１】熱成形性
得られた果菜容器を目視により観察し、以下の基準で評
価した。
○：金型再現性が良好である。
×：果菜容器の一部に亀裂が発生している。Thermoformability The obtained fruit and vegetable containers were visually observed and evaluated according to the following criteria. ◯: Mold reproducibility is good. X: A crack is generated in a part of the fruit vegetable container.
【００６２】[0062]
【発明の効果】以上説明したように本発明の熱成形用発
泡シートは、ポリスチレン系樹脂と、低密度ポリエチレ
ン系樹脂と、スチレン−ブタジエン−ブチレン−スチレ
ンブロック共重合体及び／又はスチレン−エチレン−ブ
チレン−スチレンブロック共重合体が特定の範囲内で配
合された混合樹脂を主成分とするので、柔軟性、適度な
剛性、軽量性、熱成形性、二次発泡性、耐水性等を有す
る。また、熱成形用発泡シートは汎用樹脂を主として用
いるので、製造コストが低く低価格で市場に供給可能で
ある。As described above, the foamed sheet for thermoforming of the present invention comprises a polystyrene resin, a low density polyethylene resin, a styrene-butadiene-butylene-styrene block copolymer and / or a styrene-ethylene-polymer. Since the butylene-styrene block copolymer is mainly composed of a mixed resin blended within a specific range, it has flexibility, appropriate rigidity, light weight, thermoformability, secondary foamability, water resistance and the like. Further, since the foam sheet for thermoforming mainly uses general-purpose resin, it can be supplied to the market at a low manufacturing cost and a low price.
【００６３】また、本発明の果菜容器は、上記熱成形用
発泡シートを熱成形して得られるので、発泡シートの特
性を引き継ぎ、柔軟性、適度な剛性、軽量性、耐水性等
に優れ、表面が美麗で、汎用性の高い安価な容器であ
る。Further, since the fruit and vegetable container of the present invention is obtained by thermoforming the above foam sheet for thermoforming, it inherits the characteristics of the foam sheet and is excellent in flexibility, appropriate rigidity, light weight, water resistance, etc. An inexpensive container with a beautiful surface and high versatility.
【図１】本発明の果菜容器の一例を示す斜視図である。FIG. 1 is a perspective view showing an example of a fruit and vegetable container of the present invention.
１ 果菜収納凹部 ２ 果菜容器 1 Fruit storage recess 2 Fruit and vegetable containers
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） //(Ｃ０８Ｌ 25/04 Ｂ６５Ｄ 1/00 Ａ 23:04 81/16 Ｄ 53:00） (72)発明者 有田 順一 神奈川県平塚市東八幡５−６−１ 株式会 社ジェイエスピー平塚工場内 (72)発明者 真宮 健太 神奈川県平塚市東八幡５−６−１ 株式会 社ジェイエスピー平塚工場内 (72)発明者 斉藤 良成 栃木県鹿沼市さつき町10−３ 株式会社ジ ェイエスピー鹿沼研究所内 Ｆターム(参考） 3E033 AA10 BA13 BA15 BA22 BB01 CA02 CA03 FA01 3E066 AA44 BA01 CA01 DA01 HA04 JA01 KA04 LA07 NA53 NA54 3E096 AA09 BA27 BB09 CA06 CB02 CC01 DA04 DB06 DC01 EA03X FA40 GA01 4F074 AA09B AA17 AA17B AA26B AA32 AA32B BA32 BA34 BA35 BA37 BA38 BA39 BA40 CA22 CC04Y CC22X DA02 DA23 DA34 4J002 BB032 BB052 BC031 BC041 BP013 EA016 EA026 FD326 GG01 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 7 Identification code FI theme code (reference) // (C08L 25/04 B65D 1/00 A 23:04 81/16 D 53:00) (72) Invention Organizer Junichi Arita 5-6-1 Higashi-Hachiman, Hiratsuka-shi, Kanagawa Stock company JSPY Hiratsuka factory (72) Inventor Kenta Shingu 5-6-1 Higashi-Hachiman, Hiratsuka city Kanagawa prefecture (72) Invention Person Saito Yoshinari 10-3 Satsuki-cho, Kanuma City, Tochigi Prefecture F-term in JSP Kanuma Research Institute (reference) 3E033 AA10 BA13 BA15 BA22 BB01 CA02 CA03 FA01 3E066 AA44 BA01 CA01 DA01 HA04 JA01 KA04 LA07 NA53 NA54 3E096 AA09 BA27 BB09 CA02 BB09 CA02 BB09 CA02 CC01 DA04 DB06 DC01 EA03X FA40 GA01 4F074 AA09B AA17 AA17B AA26B AA32 AA32B BA32 BA34 BA35 BA37 BA38 BA39 BA40 CA22 CC04Y CC22X DA02 DA23 DA34 4J002 BB032 BB052 BC031 BC041 BP013 EA016 EA026 FD326 GG01
Claims (3)
量％、（２）低密度ポリエチレン系樹脂２〜１５重量
％、（３）スチレン−ブタジエン−ブチレン−スチレン
ブロック共重合体及び／又はスチレン−エチレン−ブチ
レン−スチレンブロック共重合体３〜２５重量％（但
し、（１）、（２）及び（３）の合計は１００重量％）
とからなる混合樹脂を主成分とし、密度が０．１ｇ／ｃ
ｍ3以下、厚みが１０ｍｍ以下であることを特徴とする
熱成形用発泡シート。1. (1) 60 to 95% by weight of polystyrene resin, (2) 2 to 15% by weight of low density polyethylene resin, (3) styrene-butadiene-butylene-styrene block copolymer and / or styrene- Ethylene-butylene-styrene block copolymer 3 to 25% by weight (however, the total of (1), (2) and (3) is 100% by weight)
The main component is a mixed resin consisting of and a density of 0.1 g / c
A foam sheet for thermoforming, which has a thickness of m 3 or less and a thickness of 10 mm or less.
０．１ｇ／ｃｍ3である請求項１記載の熱成形用発泡シ
ート。2. The density of the thermoforming foam sheet is 0.02 to 0.02.
The foam sheet for thermoforming according to claim 1, which has a weight of 0.1 g / cm 3 .
ートを熱成形することによって得られた、果菜収納凹部
を有する果菜容器。3. A fruit and vegetable container having a fruit and vegetable storage concave portion, which is obtained by thermoforming the foam sheet for thermoforming according to claim 1 or 2.