JP2003147913A - Roof structure and manufacturing method therefor - Google Patents
Roof structure and manufacturing method thereforInfo
- Publication number
- JP2003147913A JP2003147913A JP2002257032A JP2002257032A JP2003147913A JP 2003147913 A JP2003147913 A JP 2003147913A JP 2002257032 A JP2002257032 A JP 2002257032A JP 2002257032 A JP2002257032 A JP 2002257032A JP 2003147913 A JP2003147913 A JP 2003147913A
- Authority
- JP
- Japan
- Prior art keywords
- roof
- modified silicone
- roof tile
- roof structure
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、耐熱性及び耐水性
に優れた屋根構造体及びその製造方法に関する。TECHNICAL FIELD The present invention relates to a roof structure excellent in heat resistance and water resistance and a method for manufacturing the same.
【０００２】[0002]
【従来の技術】屋根構造体は、住宅の屋根部分を構成す
るものであって、永年の風、雨、雪、霜等の気候変化や
落下物等から住宅を守り、住宅の耐久性を向上させる機
能を有するものである。和風住宅における屋根構造体
は、通常、複数の瓦を並べて構成された外側と、当該外
側を内側に接続させる瓦下地材とからなり、これらの複
数の瓦同士の間や、瓦と瓦下地材との間は、クギ、ビス
等の機械的方法により接合したり、又は、エポキシ樹脂
若しくは酢酸ビニル樹脂等の硬い樹脂で接着することが
行われている。2. Description of the Related Art A roof structure constitutes a roof part of a house and protects the house from climate change such as long-term wind, rain, snow, frost, and falling objects, and improves the durability of the house. It has a function to make it. A roof structure in a Japanese-style house is usually composed of an outer side formed by arranging a plurality of roof tiles and a roof tile base material connecting the outer side to the inside, and between the plurality of roof tiles or between the roof tile and the roof tile base material. Between the two, it is performed to bond them by a mechanical method such as nails or screws, or to bond them with a hard resin such as epoxy resin or vinyl acetate resin.
【０００３】しかしながら、従来の機械的な接合又は硬
い接着剤を用いて屋根構造体を構成した場合、屋根構造
体を構成する各構成部材の線膨張率の違いによる応力の
発生及び応力集中が起こり、永い間の使用により、瓦及
び硬化後の接着剤に亀裂、破壊が発生し、場合によって
は落下が起こる等の問題があった。However, when the roof structure is constructed by using a conventional mechanical joint or a hard adhesive, stress is generated and stress is concentrated due to the difference in linear expansion coefficient between the constituent members of the roof structure. However, there has been a problem that the roof tile and the adhesive after curing are cracked or broken and dropped in some cases due to long-term use.
【０００４】特開昭６２−２１５６５３号公報には、分
子中に少なくとも１個の官能性珪素基を有するポリエー
テル化合物、及び、特定の有機錫化合物を含有する硬化
性組成物が開示されているが、この硬化性組成物を接着
剤として用いた屋根構造体は、亀裂、破壊を防止するに
は不充分であった。Japanese Unexamined Patent Publication (Kokai) No. 62-215653 discloses a curable composition containing a polyether compound having at least one functional silicon group in the molecule and a specific organotin compound. However, the roof structure using this curable composition as an adhesive was insufficient to prevent cracking and breakage.
【０００５】[0005]
【発明が解決しようとする課題】本発明は、上記に鑑
み、剥離、亀裂及び構造部材のズレが発生せず、耐熱
性、耐水性に優れた屋根構造体及びその製造方法を提供
することを目的とする。SUMMARY OF THE INVENTION In view of the above, the present invention provides a roof structure which is free from peeling, cracking and displacement of structural members and which is excellent in heat resistance and water resistance, and a method for producing the same. To aim.
【０００６】[0006]
【課題を解決するための手段】本発明は、複数の瓦と瓦
下地材とからなり、上記複数の瓦同士の間、及び／又
は、上記瓦と上記瓦下地材との間を、変成シリコーン系
接着剤を用いて接着してなる屋根構造体であって、上記
接着剤は、硬化時のＪＩＳ Ｋ ６３０１に準拠する引
張試験における切断時の伸びが１００％以上であり、か
つ、永久伸びが５０％以下であるものであり、上記複数
の瓦同士の間、及び／又は、上記瓦と上記瓦下地材との
間が、ビード塗布量が０．１〜１０ｋｇ／ｍ2 であるビ
ード状に塗布された上記変成シリコーン系接着剤により
接着されてなることを特徴とするものである。以下本発
明を更に詳細に説明する。DISCLOSURE OF THE INVENTION The present invention comprises a plurality of roof tiles and a roof tile base material, and a modified silicone is provided between the plurality of roof tiles and / or between the roof tile and the roof tile base material. A roof structure that is adhered using a system adhesive, wherein the adhesive has an elongation at break of 100% or more in a tensile test according to JIS K 6301 at the time of curing, and a permanent elongation. It is 50% or less, and between the plurality of roof tiles and / or between the roof tile and the roof tile base material, a bead shape having a bead coating amount of 0.1 to 10 kg / m 2 is formed. It is characterized by being adhered by the above-mentioned modified silicone adhesive applied. The present invention will be described in more detail below.
【０００７】本発明の屋根構造体は、複数の瓦と瓦下地
材とからなり、上記複数の瓦同士の間、及び／又は、上
記瓦と上記瓦下地材との間を、変成シリコーン系接着剤
を用いて接着してなる。本発明で用いられる瓦として
は、例えば、和型セメント瓦、厚型スレート、石綿スレ
ート、アスファルトシングル、金属瓦、カラーベスト
（クボタ社製）、フルベストリード（松下電工社製）等
が挙げられる。本発明で用いられる瓦下地材としては、
例えば、合板、木根太、石膏ボード、スレート板、コン
クリート等が挙げられる。The roof structure of the present invention comprises a plurality of roof tiles and a roof tile base material, and a modified silicone adhesive is used between the plurality of roof tiles and / or between the roof tile and the roof tile base material. It is made to adhere by using an agent. Examples of the roof tile used in the present invention include Japanese cement roof tile, thick slate, asbestos slate, asphalt single, metal roof tile, color vest (made by Kubota), full vest lead (made by Matsushita Electric Works, Ltd.) and the like. . As the roof tile base material used in the present invention,
Examples thereof include plywood, wood joists, gypsum board, slate board, and concrete.
【０００８】本発明で用いられる変成シリコーン系接着
剤は、変成シリコーンポリマーに各種添加剤を加えたも
のである。上記変成シリコーンポリマーとしては、例え
ば、主鎖がポリオキシアルキレンであり、末端に架橋可
能な加水分解性シリル基を有するもの等が挙げられる。The modified silicone adhesive used in the present invention is a modified silicone polymer to which various additives are added. Examples of the modified silicone polymer include those having a main chain of polyoxyalkylene and having a crosslinkable hydrolyzable silyl group at the terminal.
【０００９】上記変成シリコーンポリマーとしては、例
えば、末端にアリル基を有するポリオキシアルキレン
を、ＶＩＩＩ族遷移金属の存在下で、下記一般式As the modified silicone polymer, for example, polyoxyalkylene having an allyl group at the terminal can be used in the presence of a transition metal of Group VIII with the following general formula:
【００１０】[0010]
【化１】 [Chemical 1]
【００１１】（式中、Ｒ1 、Ｒ2 、Ｒ3 は、同一又は異
なって、１価炭化水素基、ハロゲン化１価炭化水素基、
ハロゲン原子、アルコキシ基、アシルオキシ基、又は、
ケトキシメート基を表す。）で表される水素化ケイ素化
合物と反応させることにより得られるもの等が挙げられ
る。(Wherein R 1 , R 2 and R 3 are the same or different and are a monovalent hydrocarbon group, a halogenated monovalent hydrocarbon group,
A halogen atom, an alkoxy group, an acyloxy group, or
Represents a ketoximate group. The thing obtained by making it react with the silicon hydride compound represented by these are mentioned.
【００１２】上記変成シリコーンポリマーの主鎖である
ポリオキシアルキレンとしては、例えば、ポリオキシエ
チレン、ポリオキシプロピレン、ポリオキシブチレン等
が挙げられる。上記架橋可能な加水分解性シリル基とし
ては、メトキシシリル基が好ましい。Examples of the polyoxyalkylene which is the main chain of the modified silicone polymer include polyoxyethylene, polyoxypropylene, polyoxybutylene and the like. The crosslinkable hydrolyzable silyl group is preferably a methoxysilyl group.
【００１３】上記変成シリコーンポリマーの数平均分子
量は、４０００〜３００００が好ましい。４０００未満
であると、硬化時の弾性が不足し、３００００を超える
と、作業性に劣る。より好ましくは６０００〜３０００
０であり、さらに好ましくは１００００〜３００００で
ある。上記変成シリコーンポリマーの分子量分布（Ｍｗ
／Ｍｎ）は、１．６以下が好ましい。The modified silicone polymer preferably has a number average molecular weight of 4,000 to 30,000. If it is less than 4,000, the elasticity during curing will be insufficient, and if it exceeds 30,000, workability will be poor. More preferably 6000-3000
It is 0, and more preferably 10,000 to 30,000. Molecular weight distribution (Mw) of the modified silicone polymer
/ Mn) is preferably 1.6 or less.
【００１４】上記変成シリコーンポリマーとしては、例
えば、鐘淵化学工業社製、ＭＳポリマーＳ−２０３、Ｍ
ＳポリマーＳ−３０３、ＭＳポリマーＳ−９０３、サイ
リルポリマーＳＡＴ−２００、サイリルポリマーＭＡ４
３０、サイリルポリマーＭＡＸ４４７；旭硝子社製、エ
クセスターＥＳＳ−３６２０、エクセスターＥＳＳ−３
４３０、エクセスターＥＳＳ−２４２０、エクセスター
ＥＳＳ−２４１０等が挙げられる。これらは１種類でも
よいし、何種類かを混ぜて使用してもよい。Examples of the modified silicone polymer include MS polymers S-203 and M manufactured by Kanegafuchi Chemical Industry Co., Ltd.
S polymer S-303, MS polymer S-903, silyl polymer SAT-200, silyl polymer MA4
30, Cyryl polymer MAX447; manufactured by Asahi Glass Co., Ltd., Excester ESS-3620, Excester ESS-3
430, Excester ESS-2420, Excester ESS-2410 and the like. These may be used alone or in combination of several kinds.
【００１５】上記変成シリコーン系接着剤には、上記変
成シリコーンポリマーの他に、１分子中にアミノ基及び
アルコキシシリル基を有する化合物、シラノール縮合触
媒、脱水剤、充填剤、可塑剤、タレ防止剤等の各種の添
加剤が添加されている。The modified silicone adhesive includes, in addition to the modified silicone polymer, a compound having an amino group and an alkoxysilyl group in one molecule, a silanol condensation catalyst, a dehydrating agent, a filler, a plasticizer, an anti-sagging agent. Various kinds of additives such as are added.
【００１６】上記１分子中にアミノ基及びアルコキシシ
リル基を有する化合物は、接着付与剤として働くが、上
記の化合物としては、例えば、３−アミノプロピルトリ
メトキシシラン、３−アミノプロピルメチルジメトキシ
シラン、３−アミノプロピルトリエトキシシラン、Ｎ−
（２−アミノエチル）−３−アミノプロピルトリメトキ
シシラン、Ｎ−（２−アミノエチル）−３−アミノプロ
ピルメチルジメトキシシラン、Ｎ−（２−アミノエチ
ル）−３−アミノプロピルトリエトキシシラン、Ｎ，
Ｎ′−ビス−［３−（トリメトキシシリル）プロピル］
エチレンジアミン、Ｎ，Ｎ′−ビス−［３−（トリエト
キシシリル）プロピル］エチレンジアミン、Ｎ，Ｎ′−
ビス−［３−（メチルジメトキシシリル）プロピル］エ
チレンジアミン、Ｎ，Ｎ′−ビス−［３−（トリメトキ
シシリル）プロピル］ヘキサメチレンジアミン、Ｎ，
Ｎ′−ビス−［３−（トリエトキシシリル）プロピル］
ヘキサメチレンジアミン、Ｎ，Ｎ′−ビス−［３−（メ
チルジメトキシシリル）プロピル］ヘキサメチレンジア
ミン、Ｎ，Ｎ−ビス−［３−（トリメトキシシリル）プ
ロピル］エチレンジアミン、Ｎ，Ｎ−ビス−［３−（メ
チルジメトキシシリル）プロピル］エチレンジアミン、
Ｎ，Ｎ−ビス−［３−（トリエトキシシリル）プロピ
ル］エチレンジアミン、Ｎ，Ｎ−ビス−［３−（トリメ
トキシシリル）プロピル］ヘキサメチレンジアミン、
Ｎ，Ｎ−ビス−［３−（メチルジメトキシシリル）プロ
ピル］ヘキサメチレンジアミン、Ｎ，Ｎ−ビス−［３−
（トリエトキシシリル）プロピル］ヘキサメチレンジア
ミン、Ｎ，Ｎ−ビス−［３−（トリメトキシシリル）プ
ロピル］アミン、Ｎ，Ｎ−ビス−［３−（トリエトキシ
シリル）プロピル］アミン、Ｎ，Ｎ−ビス−［３−（メ
チルジメトキシシリル）プロピル］アミン等が挙げられ
る。これらは単独で又は２種以上を併用して使用するこ
とができる。The compound having an amino group and an alkoxysilyl group in one molecule functions as an adhesion promoter, and examples of the above compound include 3-aminopropyltrimethoxysilane, 3-aminopropylmethyldimethoxysilane, 3-aminopropyltriethoxysilane, N-
(2-Aminoethyl) -3-aminopropyltrimethoxysilane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, N- (2-aminoethyl) -3-aminopropyltriethoxysilane, N ，
N'-bis- [3- (trimethoxysilyl) propyl]
Ethylenediamine, N, N'-bis- [3- (triethoxysilyl) propyl] ethylenediamine, N, N'-
Bis- [3- (methyldimethoxysilyl) propyl] ethylenediamine, N, N'-bis- [3- (trimethoxysilyl) propyl] hexamethylenediamine, N,
N'-bis- [3- (triethoxysilyl) propyl]
Hexamethylenediamine, N, N'-bis- [3- (methyldimethoxysilyl) propyl] hexamethylenediamine, N, N-bis- [3- (trimethoxysilyl) propyl] ethylenediamine, N, N-bis- [ 3- (methyldimethoxysilyl) propyl] ethylenediamine,
N, N-bis- [3- (triethoxysilyl) propyl] ethylenediamine, N, N-bis- [3- (trimethoxysilyl) propyl] hexamethylenediamine,
N, N-bis- [3- (methyldimethoxysilyl) propyl] hexamethylenediamine, N, N-bis- [3-
(Triethoxysilyl) propyl] hexamethylenediamine, N, N-bis- [3- (trimethoxysilyl) propyl] amine, N, N-bis- [3- (triethoxysilyl) propyl] amine, N, N -Bis- [3- (methyldimethoxysilyl) propyl] amine and the like. These may be used alone or in combination of two or more.
【００１７】上記シラノール縮合触媒としては、例え
ば、ジブチル錫ジラウレート、ジブチル錫オキサイド、
ジブチル錫ジアセテート、ジブチル錫フタレート、ビス
（ジブチル錫ラウリン酸）オキサイド、ジブチル錫ビス
アセチルアセトナート、ジブチル錫ビス（モノエステル
マレート）、オクチル酸錫、ジブチル錫オクトエート、
ジオクチル錫オキサイド等の錫化合物；テトラ−ｎ−ブ
トキシチタネート、テトライソプロポキシチタネート等
のチタネート系化合物；ジブチルアミン−２−エチルヘ
キソエート等のアミン塩；その他の酸性触媒、その他の
塩基性触媒等が挙げられる。これらは単独で又は２種以
上を併用して使用することができる。Examples of the silanol condensation catalyst include dibutyltin dilaurate, dibutyltin oxide,
Dibutyltin diacetate, dibutyltin phthalate, bis (dibutyltin lauric acid) oxide, dibutyltin bisacetylacetonate, dibutyltin bis (monoester malate), tin octylate, dibutyltin octoate,
Tin compounds such as dioctyltin oxide; titanate compounds such as tetra-n-butoxy titanate and tetraisopropoxy titanate; amine salts such as dibutylamine-2-ethylhexoate; other acidic catalysts, other basic catalysts, etc. Is mentioned. These may be used alone or in combination of two or more.
【００１８】上記脱水剤としては、例えば、ビニルトリ
メトキシシラン、ジメチルジメトキシシラン、テトラエ
トキシシラン、メチルトリメトキシシラン、メチルトリ
エトキシシラン、テトラメトキシシラン、テトラエトキ
シシラン、フェニルトリメチルシラン、ジフェニルジメ
トキシシラン等のシラン化合物類；オルトギ酸メチル、
オルトギ酸エチル、オルト酢酸メチル、オルト酢酸エチ
ル等の加水分解性エステル化合物類等が挙げられる。こ
れらは単独で又は２種以上を併用して使用することがで
きる。Examples of the dehydrating agent include vinyltrimethoxysilane, dimethyldimethoxysilane, tetraethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, tetramethoxysilane, tetraethoxysilane, phenyltrimethylsilane and diphenyldimethoxysilane. Silane compounds; methyl orthoformate,
Examples thereof include hydrolyzable ester compounds such as ethyl orthoformate, methyl orthoacetate, and ethyl orthoacetate. These may be used alone or in combination of two or more.
【００１９】上記充填剤としては、例えば、炭酸カルシ
ウム、炭酸マグネシウム、含水ケイ酸、無水ケイ酸、ケ
イ酸カルシウム、シリカ、二酸化チタン、クレー、タル
ク、カーボンブラック、ガラスバルーン等が挙げられ
る。これらは単独で又は２種以上を併用して使用するこ
とができる。Examples of the above-mentioned fillers include calcium carbonate, magnesium carbonate, hydrous silicic acid, silicic acid anhydride, calcium silicate, silica, titanium dioxide, clay, talc, carbon black and glass balloons. These may be used alone or in combination of two or more.
【００２０】上記可塑剤としては、例えば、リン酸トリ
ブチル、リン酸トリクレジル等のリン酸エステル類；フ
タル酸ジオクチル等のフタル酸エステル類；グリセリン
モノオレイン酸エステル等の脂肪酸一塩基酸エステル
類；アジピン酸ジブチル、アジピン酸ジオクチル等の脂
肪酸二塩基酸エステル類；ポリプロピレングリコール類
等が挙げられる。これらは単独で又は２種以上を併用し
て使用することができる。Examples of the plasticizer include phosphoric acid esters such as tributyl phosphate and tricresyl phosphate; phthalic acid esters such as dioctyl phthalate; fatty acid monobasic acid esters such as glycerin monooleate; adipine. Fatty acid dibasic acid esters such as dibutyl acid and dioctyl adipate; polypropylene glycols and the like. These may be used alone or in combination of two or more.
【００２１】上記タレ防止剤としては、例えば、水添ひ
まし油、脂肪酸ビスアマイド、ヒュームドシリカ等が挙
げられる。上記変成シリコーン系接着剤には、更に必要
に応じて、老化防止剤、酸化防止剤、紫外線吸収剤、顔
料、溶剤、香料等を添加することができる。上記変成シ
リコーン系接着剤には、より強力な耐久接着性を発現さ
せるために、エポキシ樹脂を添加することもできる。Examples of the anti-sagging agent include hydrogenated castor oil, fatty acid bisamide, fumed silica and the like. If necessary, an antioxidant, an antioxidant, an ultraviolet absorber, a pigment, a solvent, a fragrance and the like can be added to the modified silicone adhesive. An epoxy resin may be added to the modified silicone adhesive in order to develop stronger and durable adhesiveness.
【００２２】上記変成シリコーン系接着剤として、特
に、好ましいものは、（Ａ）主鎖がポリオキシプロピレ
ンであり、末端に架橋可能な加水分解性シリル基を有
し、数平均分子量が６０００〜３００００の変成シリコ
ーンポリマー１００重量部、（Ｂ）１分子中にアミノ基
及びアルコキシシリル基を有する化合物０．２〜２０重
量部、及び（Ｃ）シラノール縮合触媒０．１〜１０重量
部を含有する室温硬化性組成物である。As the above-mentioned modified silicone-based adhesive, particularly preferable one is (A) a main chain of which is polyoxypropylene, which has a crosslinkable hydrolyzable silyl group at a terminal and has a number average molecular weight of 6,000 to 30,000. Room temperature containing 100 parts by weight of the modified silicone polymer, (B) 0.2 to 20 parts by weight of a compound having an amino group and an alkoxysilyl group in one molecule, and (C) 0.1 to 10 parts by weight of a silanol condensation catalyst. It is a curable composition.
【００２３】本発明で用いられる変成シリコーン系接着
剤の粘度は、ブルックフィールド粘度計で１０回転時に
１０万〜６０万ｃＰ（２３℃）が好ましい。１０万ｃＰ
未満であると、施工時に瓦がズレてしまい、６０万ｃＰ
を超えると、カートリッジからの押し出し性に問題が起
こる。The viscosity of the modified silicone adhesive used in the present invention is preferably 100,000 to 600,000 cP (23 ° C.) after 10 rotations with a Brookfield viscometer. 100,000 cP
If it is less than 600, the roof tile will be displaced during construction, resulting in 600,000 cP
If it exceeds, there is a problem in the extrudability from the cartridge.
【００２４】上記変成シリコーン系接着剤のチキソ性
は、ブルックフィールド粘度計での１回転時と１０回転
時との粘度の比で表され、（１回転での粘度）／（１０
回転での粘度）が３以上であることが好ましい。３未満
であると、施工時に瓦がズレたり、充分な接着面積が確
保できなくなる等の問題が生じる。The thixotropy of the modified silicone adhesive is expressed by the ratio of the viscosities of a Brookfield viscometer between one revolution and ten revolutions, and is (viscosity after one revolution) / (10).
It is preferable that the viscosity at rotation) is 3 or more. If it is less than 3, problems may occur such as the roof tile being displaced during construction, and a sufficient adhesive area cannot be secured.
【００２５】本発明において、上記瓦又は上記瓦下地材
の亀裂、破壊を防止するために、上記変成シリコーン系
接着剤は硬化時にゴム弾性体となることが必要である。
上記変成シリコーン系接着剤は、硬化時のＪＩＳ Ｋ
６３０１に準拠する引張試験における切断時の伸びが１
００％以上であり、かつ、永久伸びが５０％以下であ
る。伸びが１００％未満であると、又は、永久伸びが５
０％を超えると、寒暖等により構成部材に変形が起こっ
たときに亀裂、剥離、被着体のズレ等が発生する。In the present invention, in order to prevent the roof tile or the roof tile base material from cracking or breaking, it is necessary that the modified silicone adhesive becomes a rubber elastic body when cured.
The above modified silicone adhesive is JIS K when cured.
The elongation at break in the tensile test according to 6301 is 1
It is at least 00% and the permanent elongation is at most 50%. If the elongation is less than 100%, or the permanent elongation is 5
If it exceeds 0%, cracks, peeling, displacement of the adherend, etc. occur when the constituent members are deformed due to cold or warm weather.
【００２６】本発明２（請求項３記載の発明）は、複数
の瓦と瓦下地材とからなる屋根構造体を製造するにあた
り、上記複数の瓦同士の間、及び／又は、上記瓦と上記
瓦下地材との間を、変成シリコーン系接着剤を用いて接
着することによる屋根構造体の製造方法であって、上記
変成シリコーン系接着剤が、硬化時のＪＩＳ Ｋ ６３
０１に準拠する引張試験における切断時の伸びが１００
％以上であり、かつ、永久伸びが５０％以下であるもの
であり、上記複数の瓦同士の間、及び／又は、上記瓦と
上記瓦下地材との間を、ビード塗布量が０．１〜１０ｋ
ｇ／ｍ2 であるビード状に塗布した上記変成シリコーン
系接着剤により接着する屋根構造体の製造方法である。The present invention 2 (the invention according to claim 3) is for manufacturing a roof structure comprising a plurality of roof tiles and a roof tile base material, and / or between the plurality of roof tiles and / or the roof tile and the above roof tile. A method of manufacturing a roof structure by bonding a roof tile material with a modified silicone adhesive, wherein the modified silicone adhesive is JIS K 63 when cured.
The elongation at break in the tensile test according to 01 is 100.
% Or more and the permanent elongation is 50% or less, and the bead coating amount is 0.1 between the plurality of roof tiles and / or between the roof tile and the roof tile base material. ~ 10k
It is a method for producing a roof structure in which the modified silicone adhesive applied in a bead shape of g / m 2 is used for adhesion.
【００２７】本発明２の屋根構造体の製造方法にあた
り、上記変成シリコーン系接着剤として、特に、好まし
いものは、（Ａ）主鎖がポリオキシプロピレンであり、
末端に架橋可能な加水分解性シリル基を有し、数平均分
子量が６０００〜３００００の変成シリコーンポリマー
１００重量部、（Ｂ）１分子中にアミノ基及びアルコキ
シシリル基を有する化合物０．２〜２０重量部、及び
（Ｃ）シラノール縮合触媒０．１〜１０重量部を含有す
る室温硬化性組成物である。In the method for producing a roof structure of the present invention 2, as the above modified silicone adhesive, particularly preferable one is (A) whose main chain is polyoxypropylene,
100 parts by weight of a modified silicone polymer having a crosslinkable hydrolyzable silyl group and a number average molecular weight of 6000 to 30000, (B) a compound having an amino group and an alkoxysilyl group in one molecule 0.2 to 20 It is a room temperature curable composition containing 0.1 to 10 parts by weight of (C) silanol condensation catalyst.
【００２８】上記屋根構造体の製造にあたり、上記複数
の瓦同士の間、及び／又は、上記瓦と上記瓦下地材との
間を、変成シリコーン系接着剤を用いて接着する際の施
工方法としては、変成シリコーン系接着剤をカートリッ
ジ、フィルム等の包装容器に入れ、ビード塗布する方法
などがある。これらの場合の最適塗布量は０．１〜１０
ｋｇ／ｍ2 である。As a construction method for bonding the plurality of roof tiles and / or between the roof tile and the roof tile base material using a modified silicone adhesive in the manufacture of the roof structure. For example, there is a method in which a modified silicone adhesive is put in a packaging container such as a cartridge or a film and bead applied. The optimum coating amount in these cases is 0.1-10.
It is kg / m 2 .
【００２９】本発明の屋根構造体は、硬化時にゴム弾性
を有する変成シリコーン系接着剤を用いることにより、
線膨張率差による応力発生及び集中を防ぐことができ、
また、良好な接着性を有すると共に、耐熱性、耐水性等
の耐久性にも優れている。The roof structure of the present invention uses a modified silicone adhesive having rubber elasticity when cured,
It is possible to prevent stress generation and concentration due to the difference in linear expansion coefficient,
In addition to having good adhesiveness, it is also excellent in durability such as heat resistance and water resistance.
【００３０】[0030]
【実施例】以下に実施例を掲げて本発明を更に詳しく説
明するが、本発明はこれら実施例のみに限定されるもの
ではない。The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples.
【００３１】実施例１
変成シリコーンポリマーＡ（旭硝子社製、エクセスター
ＥＳＳ−３６２０、数平均分子量２００００）１００重
量部、硬化触媒としてジブチル錫ジラウレート２重量
部、可塑剤としてジオクチルフタレート（積水化学工業
社製）４０重量部、充填剤としてコロイダル炭酸カルシ
ウム（白石工業社製、ＣＣＲ）１３０重量部、脱水剤と
してビニルトリメトキシシラン（東芝シリコーン社製、
ＴＳＬ−８３１０）４重量部、及び、接着付与剤として
Ｎ−（２−アミノエチル）−３−アミノプロピルメチル
ジメトキシシラン（東芝シリコーン社製、ＴＳＬ−８３
４５）２重量部を配合し、プラネタリーミキサーで約６
０分間真空混練して変成シリコーン系接着剤Ａを得た。
この変成シリコーン系接着剤Ａについて、以下の試験方
法により硬化時の物性を評価した。Example 1 100 parts by weight of modified silicone polymer A (exastar ESS-3620, manufactured by Asahi Glass Co., Ltd., number average molecular weight 20000), 2 parts by weight of dibutyltin dilaurate as a curing catalyst, dioctyl phthalate as a plasticizer (Sekisui Chemical Co., Ltd.) 40 parts by weight, colloidal calcium carbonate (made by Shiraishi Industry Co., Ltd., CCR) 130 parts by weight as a filler, vinyltrimethoxysilane (made by Toshiba Silicone Co., Ltd. as a dehydrating agent,
TSL-8310) 4 parts by weight, and N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane (TSL-83 manufactured by Toshiba Silicone Co., Ltd.) as an adhesion promoter.
45) Mix 2 parts by weight and mix with a planetary mixer to about 6
Vacuum kneading was performed for 0 minutes to obtain a modified silicone adhesive A.
With respect to this modified silicone adhesive A, the physical properties at the time of curing were evaluated by the following test methods.
【００３２】（１）切断時の伸び
ＪＩＳ Ｋ ６３０１に準拠する引張試験（３号ダンベ
ル）を行い、切断時の伸びを測定した。
（２）永久伸び
ＪＩＳ Ｋ ６３０１に準拠する引張試験（３号ダンベ
ル）を行い、永久伸びを測定した。
（３）粘度
ＢＳ粘度計（ローターＮｏ．６）で１０回転、２０℃で
測定した。
（４）チキソ性
２０℃でＢＳ粘度計における（１回転粘度）／（１０回
転粘度）を測定した。物性の評価結果を表１に示した。(1) Elongation at Break A tensile test (No. 3 dumbbell) according to JIS K 6301 was carried out to measure the elongation at break. (2) Permanent elongation A tensile test (No. 3 dumbbell) based on JIS K 6301 was performed to measure the permanent elongation. (3) Viscosity The viscosity was measured with a BS viscometer (rotor No. 6) at 10 rotations and 20 ° C. (4) Thixotropic property (1 rotation viscosity) / (10 rotation viscosity) was measured by a BS viscometer at 20 ° C. The results of evaluation of physical properties are shown in Table 1.
【００３３】瓦としては、縦１００ｍｍ、横２５ｍｍの
カラーベスト（クボタ社製）を用い、図１に示したよう
に、上記の変成シリコーン系接着剤１を、接着剤層の厚
みが１ｍｍになるように瓦２に塗布し、接着幅が２５．
０ｍｍになるように更に瓦２を接着させ、２週間硬化養
生させて、せん断試験片を作製した。このせん断試験片
を用いて、図１に示したように、疲労試験を、変位量１
ｍｍ（４％）、変位速度１Ｈｚで行い、接着部又は構成
部材が破壊されるまでの疲労回数を測定した。その結
果、疲労回数は１００回以上であった。As the roof tile, a color vest having a length of 100 mm and a width of 25 mm (manufactured by Kubota Corporation) is used, and as shown in FIG. 1, the modified silicone adhesive 1 has an adhesive layer thickness of 1 mm. To the roof tile 2 and the adhesive width is 25.
The roof tile 2 was further adhered to 0 mm and cured and cured for 2 weeks to prepare a shear test piece. Using this shear test piece, as shown in FIG.
mm (4%) at a displacement rate of 1 Hz, and the number of times of fatigue until the bonded portion or the constituent member was broken was measured. As a result, the number of fatigues was 100 or more.
【００３４】実施例２
変成シリコーンポリマーＡの代わりに、変成シリコーン
ポリマーＢ（鐘淵化学工業社製、Ｓ−３０３）を用いた
こと以外は、実施例１と同様にして変成シリコーン系接
着剤Ｂを得た。この変成シリコーン系接着剤Ｂの硬化時
の物性を実施例１と同様にして評価し、評価結果を表１
に示した。瓦としてフルベストリード（松下電工社製）
を用い、接着剤として変成シリコーン系接着剤Ｂを用い
たこと以外は、実施例１と同様にしてせん断試験片を作
製し、疲労試験を行った結果、疲労回数は１００回以上
であった。Example 2 Modified silicone adhesive B was prepared in the same manner as in Example 1 except that modified silicone polymer B (S-303 manufactured by Kaneka Corporation) was used in place of modified silicone polymer A. Got The physical properties of the modified silicone adhesive B during curing were evaluated in the same manner as in Example 1, and the evaluation results are shown in Table 1.
It was shown to. Full best lead as roof tile (Matsushita Electric Works)
A shear test piece was prepared in the same manner as in Example 1 except that the modified silicone adhesive B was used as the adhesive, and the fatigue test was performed. As a result, the fatigue count was 100 times or more.
【００３５】実施例３
実施例１で得た変成シリコーン系接着剤Ａを３３３ｍｌ
カートリッジに充填し、図２に示した瓦３（松下電工社
製、フルベストリード、４５０ｍｍ×９０９ｍｍ）の図
２における上側の瓦面３ａに、上記変成シリコーン系接
着剤４を、約９０ｍｍ間隔で１０本の直線状（一本の直
線の長さは約２３０ｍｍ）となるように、ビード状（ビ
ード直径８ｍｍ）に塗布した。図３に示したように、塗
布された２枚の瓦３の、それぞれの変成シリコーン系接
着剤４塗布面上に、別の３枚の瓦３の裏面を載せるよう
にして貼り合わせる方法で、多数の瓦３同士を次々と接
着しながら、瓦３を瓦下地材上に施工し瓦屋根構造体と
した。なお、瓦３と瓦下地材との間の接合は通常の方法
によった。この施工に際して、上記の変成シリコーン系
接着剤４は中毒などを起こすこともなく良好に施工でき
た。得られた瓦屋根構造体が設けられた家屋を１年間実
用に供したが、施工後１年たっても瓦３が割れたり、ま
た屋根から落下したりすることは全く無かった。Example 3 333 ml of the modified silicone adhesive A obtained in Example 1
The modified silicone adhesive 4 was filled in a cartridge, and the above-mentioned modified silicone adhesive 4 was provided at an interval of about 90 mm on the roof tile surface 3a on the upper side in FIG. It was applied in a bead shape (bead diameter 8 mm) so as to form 10 straight lines (the length of one straight line is approximately 230 mm). As shown in FIG. 3, the two roof tiles 3 that have been applied are bonded to each other by placing the back surfaces of the other three roof tiles 3 on the modified silicone adhesive 4 coated surfaces, While adhering a large number of tiles 3 to each other one after another, the tiles 3 were constructed on a tile base material to obtain a tile roof structure. In addition, the joining between the roof tile 3 and the roof tile base material was performed by an ordinary method. During this construction, the modified silicone adhesive 4 was successfully constructed without causing poisoning. The house provided with the obtained tiled roof structure was put to practical use for one year, but the tile 3 was not cracked or dropped from the roof even one year after the construction.
【００３６】比較例１
酢酸ビニル溶剤系接着剤（積水化学工業社製、セキスイ
ボンド木レンガ用）を用いて、硬化時の物性を実施例１
と同様にして評価し、評価結果を表１に示した。接着剤
として、この酢酸ビニル溶剤系接着剤を用いた以外は、
実施例１と同様にしてせん断試験片を作製し、疲労試験
を行った結果、疲労回数は０回であった。Comparative Example 1 Using a vinyl acetate solvent-based adhesive (Sekisui Chemical Co., Ltd., for Sekisui bond wood bricks), the physical properties at the time of curing were evaluated.
Evaluation was carried out in the same manner as above, and the evaluation results are shown in Table 1. Except for using this vinyl acetate solvent-based adhesive as the adhesive,
A shear test piece was prepared in the same manner as in Example 1, and a fatigue test was performed. As a result, the number of fatigue cycles was 0.
【００３７】比較例２
エポキシ系接着剤（積水化学工業社製、エスロタイト）
を用いて、硬化時の物性を実施例１と同様にして評価
し、評価結果を表１に示した。接着剤として、このエポ
キシ系接着剤を用いた以外は、実施例２と同様にしてせ
ん断試験片を作製し、疲労試験を行った結果、疲労回数
は０回であった。Comparative Example 2 Epoxy adhesive (Eslotite manufactured by Sekisui Chemical Co., Ltd.)
Was used to evaluate the physical properties at the time of curing in the same manner as in Example 1, and the evaluation results are shown in Table 1. A shear test piece was prepared in the same manner as in Example 2 except that this epoxy adhesive was used as the adhesive, and the fatigue test was performed. As a result, the number of times of fatigue was 0.
【００３８】[0038]
【表１】 [Table 1]
【００３９】[0039]
【発明の効果】本発明の屋根構造体は、上述のとおりで
あるので、剥離、亀裂及び構造部材のズレが発生せず、
また、耐熱性、耐水性等の耐久性にも優れている。本発
明２の屋根構造体の製造方法は、上述のとおりであるの
で、剥離、亀裂及び構造部材のズレが発生せず、また、
耐熱性、耐水性等の耐久性にも優れた屋根構造体を製造
し得る。Since the roof structure of the present invention is as described above, peeling, cracking and displacement of structural members do not occur,
Also, it has excellent durability such as heat resistance and water resistance. Since the method for manufacturing the roof structure according to the second aspect of the present invention is as described above, peeling, cracking and displacement of the structural member do not occur, and
A roof structure excellent in durability such as heat resistance and water resistance can be manufactured.
【図１】実施例１及び２並びに比較例１及び２における
疲労試験を示す図である。FIG. 1 is a diagram showing a fatigue test in Examples 1 and 2 and Comparative Examples 1 and 2.
【図２】実施例３で用いた瓦を示す平面図である。2 is a plan view showing a roof tile used in Example 3. FIG.
【図３】実施例３で用いた施工方法を説明するための説
明図（平面図）である。FIG. 3 is an explanatory diagram (plan view) for explaining a construction method used in Example 3;
１ 変成シリコーン系接着剤 ２ 瓦 ３ 瓦 ４ 変成シリコーン系接着剤 1 Modified silicone adhesive 2 roof tiles 3 roof tiles 4 Modified silicone adhesive
Claims (4)
数の瓦同士の間、及び／又は、前記瓦と前記瓦下地材と
の間を、変成シリコーン系接着剤を用いて接着してなる
屋根構造体であって、前記変成シリコーン系接着剤が、
硬化時のＪＩＳ Ｋ ６３０１に準拠する引張試験にお
ける切断時の伸びが１００％以上であり、かつ、永久伸
びが５０％以下であるものであり、前記複数の瓦同士の
間、及び／又は、前記瓦と前記瓦下地材との間が、ビー
ド塗布量が０．１〜１０ｋｇ／ｍ2 であるビード状に塗
布された前記変成シリコーン系接着剤により接着されて
なることを特徴とする屋根構造体。1. A plurality of roof tiles and a roof tile base material, wherein the plurality of roof tiles are bonded to each other and / or the roof tile and the roof tile base material are bonded by using a modified silicone adhesive. The modified silicone adhesive is a roof structure comprising
The elongation at break in a tensile test according to JIS K 6301 at the time of curing is 100% or more, and the permanent elongation is 50% or less, between the plurality of roof tiles, and / or The roof structure is characterized in that the roof tile and the roof tile base material are adhered by the modified silicone adhesive applied in a bead shape having a bead coating amount of 0.1 to 10 kg / m 2. .
がポリオキシプロピレンであり、末端に架橋可能な加水
分解性シリル基を有し、数平均分子量が６０００〜３０
０００の変成シリコーンポリマー１００重量部、（Ｂ）
１分子中にアミノ基及びアルコキシシリル基を有する化
合物０．２〜２０重量部、及び（Ｃ）シラノール縮合触
媒０．１〜１０重量部を含有する室温硬化性組成物であ
ることを特徴とする請求項１記載の屋根構造体。2. The modified silicone-based adhesive has a main chain (A) of polyoxypropylene, a crosslinkable hydrolyzable silyl group at the terminal, and a number average molecular weight of 6000 to 30.
100 parts by weight of 000 modified silicone polymers, (B)
A room temperature curable composition containing 0.2 to 20 parts by weight of a compound having an amino group and an alkoxysilyl group in one molecule, and 0.1 to 10 parts by weight of a (C) silanol condensation catalyst. The roof structure according to claim 1.
体を製造するにあたり、前記複数の瓦同士の間、及び／
又は、前記瓦と前記瓦下地材との間を、変成シリコーン
系接着剤を用いて接着することによる屋根構造体の製造
方法であって、前記変成シリコーン系接着剤が、硬化時
のＪＩＳ Ｋ ６３０１に準拠する引張試験における切
断時の伸びが１００％以上であり、かつ、永久伸びが５
０％以下であるものであり、前記複数の瓦同士の間、及
び／又は、前記瓦と前記瓦下地材との間を、ビード塗布
量が０．１〜１０ｋｇ／ｍ2 であるビード状に塗布した
前記変成シリコーン系接着剤により接着することを特徴
とする屋根構造体の製造方法。3. When manufacturing a roof structure consisting of a plurality of roof tiles and a roof tile base material, between the plurality of roof tiles and / or
Alternatively, it is a method for manufacturing a roof structure by adhering the roof tile and the roof tile base material with a modified silicone adhesive, wherein the modified silicone adhesive is JIS K 6301 when cured. The elongation at break is 100% or more and the permanent elongation is 5 in the tensile test according to
0% or less, and between the plurality of roof tiles, and / or between the roof tile and the roof tile base material, a bead shape having a bead coating amount of 0.1 to 10 kg / m 2. A method for manufacturing a roof structure, which comprises bonding with the applied modified silicone adhesive.
がポリオキシプロピレンであり、末端に架橋可能な加水
分解性シリル基を有し、数平均分子量が６０００〜３０
０００の変成シリコーンポリマー１００重量部、（Ｂ）
１分子中にアミノ基及びアルコキシシリル基を有する化
合物０．２〜２０重量部、及び（Ｃ）シラノール縮合触
媒０．１〜１０重量部を含有する室温硬化性組成物であ
る請求項３記載の屋根構造体の製造方法。4. The modified silicone-based adhesive has (A) a main chain of polyoxypropylene, a crosslinkable hydrolyzable silyl group, and a number average molecular weight of 6000 to 30.
100 parts by weight of 000 modified silicone polymers, (B)
4. A room temperature curable composition containing 0.2 to 20 parts by weight of a compound having an amino group and an alkoxysilyl group in one molecule, and 0.1 to 10 parts by weight of a (C) silanol condensation catalyst. Roof structure manufacturing method.