JP2003076158A - Conductive endless belt and image forming device - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a conductive endless belt which is a resin film belt used for image forming devices of a tandem system, intermediate transfer system and tandem intermediate transfer system and has good strength, more particularly good bending durability, creep resistance and surface smoothness and an image forming device using the same. SOLUTION: The conductive endless belt which is a conductive endless belt for transfer and/or conveyance of the tandem system of transporting a recording medium held by electrostatic attraction to four kinds of image forming bodies cyclically driven by a driving member and successively transferring the respective toner images to the recording medium, in which a mixture composed of a thermoplastic resin and whiskers (fibrous inorganic compound of an aspect ration >=10 and/or metallic particles) is used as a base material and the image forming device using this conductive endless belt.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、複写機、プリンタ
ー等の電子写真装置や静電記録装置等における静電記録
プロセスにおいて、表面に静電潜像を保持した潜像保持
体等の画像形成体表面に現像剤を供給して形成されたト
ナー像を、紙等の記録媒体へと転写する際に用いられる
導電性エンドレスベルト（以下、単に「ベルト」とも称
する）及びこれを用いた画像形成装置に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to the formation of an image on a latent image carrier having an electrostatic latent image on its surface in an electrostatic recording process in an electrophotographic apparatus such as a copying machine or a printer, an electrostatic recording apparatus or the like. Conductive endless belt (hereinafter also simply referred to as "belt") used when transferring a toner image formed by supplying a developer to the body surface onto a recording medium such as paper, and image formation using the same Regarding the device.

【０００２】[0002]

【従来の技術】従来から、複写機、プリンター等におけ
る静電記録プロセスでは、まず、感光体（潜像保持体）
の表面を一様に帯電させ、この感光体に光学系から映像
を投射して光の当たった部分の帯電を消去することによ
って静電潜像を形成し、次いで、この静電潜像にトナー
を供給してトナーの静電的付着によりトナー像を形成
し、これを紙、ＯＨＰ、印画紙等の記録媒体へと転写す
ることにより、プリントする方法が採られている。この
場合、カラープリンターやカラー複写機においても、基
本的には前記プロセスに従ってプリントが行われるが、
カラー印刷の場合には、マゼンタ、イエロー、シアン、
ブラックの４色のトナーを用いて色調を再現するもの
で、これらのトナーを所定割合で重ね合わせて必要な色
調を得るための工程が必要であり、この工程を行うため
にいくつかの方式が提案されている。2. Description of the Related Art Conventionally, in an electrostatic recording process in a copying machine, a printer or the like, first of all, a photoconductor (latent image carrier)
Surface is uniformly charged, an image is projected from the optical system on this photoconductor to erase the electrostatic charge on the exposed part, and then an electrostatic latent image is formed. Is used to form a toner image by electrostatically adhering toner, and the toner image is transferred to a recording medium such as paper, OHP, photographic paper, etc. to perform printing. In this case, even in a color printer or a color copying machine, printing is basically performed according to the above process,
For color printing, magenta, yellow, cyan,
The color tone is reproduced by using black toner of four colors, and a step for superposing these toners at a predetermined ratio to obtain a necessary color tone is necessary. There are several methods for performing this step. Proposed.

【０００３】まず、第１には、モノクロ印刷を行う場合
と同様に、感光体上にトナーを供給して静電潜像を可視
化する際に、前記マゼンタ、イエロー、シアン、ブラッ
クの４色のトナーを順次重ねていくことにより現像を行
い、感光体上にカラーのトナー像を形成する多重現像方
式がある。この方式によれば比較的コンパクトに装置を
構成することが可能であるが、この方式では階調の制御
が非常に難しく、高画質が得られないという問題点があ
る。第２に、４つの感光ドラムを設け、各ドラムの潜像
を夫々マゼンタ、イエロー、シアン、ブラックのトナー
で現像することにより、マゼンタによるトナー像、イエ
ローによるトナー像、シアンによるトナー像及びブラッ
クによるトナー像の４つのトナー像を形成し、これらト
ナー像が形成された感光ドラムを１列に並べて各トナー
像を紙等の記録媒体に順次転写して記録媒体上に重ねる
ことにより、カラー画像を再現するタンデム方式があ
る。この方式は、良好な画像が得られるものの、４つの
感光ドラムと、各感光ドラムごとに設けられた帯電機構
及び現像機構が１列に並べられた状態となり、装置が大
型化するとともに高価なものとなる。First, when toner is supplied onto a photosensitive member to visualize an electrostatic latent image, as in the case of monochrome printing, first of all, four colors of magenta, yellow, cyan, and black are used. There is a multiple development system in which development is performed by sequentially stacking toner to form a color toner image on a photoconductor. According to this method, it is possible to configure the device relatively compactly, but this method has a problem that it is very difficult to control gradation and high image quality cannot be obtained. Secondly, four photosensitive drums are provided, and the latent images on the respective drums are developed with magenta, yellow, cyan, and black toners, respectively, so that a magenta toner image, a yellow toner image, a cyan toner image, and a black toner image are formed. By forming four toner images of toner images, arranging the photosensitive drums on which these toner images are formed in one row, and sequentially transferring each toner image to a recording medium such as paper and superimposing it on the recording medium, a color image is formed. There is a tandem method to reproduce. In this method, although a good image can be obtained, four photosensitive drums and a charging mechanism and a developing mechanism provided for each photosensitive drum are arranged in a line, which makes the apparatus large and expensive. Becomes

【０００４】図２にタンデム方式の画像形成装置の印字
部構成例を示す。感光体ドラム１、帯電ロール２、現像
ロール３、現像ブレード４、トナー供給ロール５及びク
リーニングブレード６で構成する印字ユニットをイエロ
ーＹ、マゼンタＭ、シアンＣ、ブラックＢの各トナーに
対応して４個並べており、駆動ローラ（駆動部材）９に
より循環駆動されて転写搬送ベルト１０で搬送した用紙
上に、トナーを順次転写しカラー画像を形成する。転写
搬送ベルトの帯電及び除電は夫々帯電ロール７及び除電
ロール８で行う。また、用紙をベルトへ吸着させるため
の用紙帯電には吸着ローラ（図示せず）が使用される。
これらの対応により、オゾンの発生を抑えることができ
る。吸着ローラでは、用紙を搬送路から転写搬送ベルト
に乗せるとともに、転写搬送ベルトへの静電吸着を行
う。また、転写後の用紙分離は、転写電圧を低くするこ
とにより用紙と転写搬送ベルトの吸着力を弱くして、曲
率分離のみで行うことができる。FIG. 2 shows an example of the configuration of a printing unit of a tandem type image forming apparatus. A printing unit composed of the photoconductor drum 1, the charging roll 2, the developing roll 3, the developing blade 4, the toner supply roll 5 and the cleaning blade 6 is provided for each of yellow Y, magenta M, cyan C and black B toners. The sheets are arranged side by side, and the toner is sequentially transferred onto the sheet conveyed by the transfer / conveying belt 10 by being circularly driven by the driving roller (driving member) 9 to form a color image. The transfer roller is charged and discharged by the charging roll 7 and the discharging roll 8, respectively. An attraction roller (not shown) is used for charging the sheet to attract the sheet to the belt.
With these measures, the generation of ozone can be suppressed. The suction roller puts the paper on the transfer / transport belt from the transport path and performs electrostatic attraction on the transfer / transport belt. Further, the sheet separation after the transfer can be performed only by the curvature separation by lowering the transfer voltage to weaken the adsorption force between the sheet and the transfer / transport belt.

【０００５】転写搬送ベルト１０の材料としては抵抗体
と誘電体があり、夫々に長所、短所を持っている。抵抗
体ベルトは電荷の保持が短時間であるため、タンデム型
の転写に用いた場合、転写での電荷注入が少なく４色の
連続する転写でも比較的電圧の上昇が少ない。また、次
の用紙の転写に繰り返して使用されるときも電荷が放出
されており、電気的なリセットは必要としない。しか
し、環境変動により抵抗値が変化するため、転写効率に
影響すること、用紙の厚さや幅の影響を受けやすいこと
などが短所となっている。一方、誘電体ベルトの場合は
注入された電荷の自然放出はなく、電荷の注入、放出と
も電気的にコントロールしなければならない。しかし、
安定に電荷が保持されるので、用紙の吸着が確実で高精
度な紙搬送が行える。誘電率は温湿度への依存性も低い
ため、環境に対しても比較的安定な転写プロセスとな
る。欠点は、転写が繰り返されるごとにベルトに電荷が
蓄積されるため、転写電圧が高くなることである。As materials for the transfer / conveyance belt 10, there are resistors and dielectrics, each of which has advantages and disadvantages. Since the resistor belt holds charges for a short time, when used for tandem type transfer, charge injection in transfer is small, and voltage rise is relatively small even in continuous transfer of four colors. Further, the electric charge is released even when it is repeatedly used for the transfer of the next sheet, and the electric reset is not necessary. However, since the resistance value changes due to environmental changes, there are disadvantages that it affects the transfer efficiency and is easily affected by the thickness and width of the paper. On the other hand, in the case of the dielectric belt, the injected charges are not spontaneously discharged, and the injection and discharge of the charges must be electrically controlled. But,
Since the electric charge is stably held, the paper can be attracted reliably and the paper can be conveyed with high accuracy. Since the permittivity also has low dependency on temperature and humidity, the transfer process is relatively stable even to the environment. The drawback is that the transfer voltage increases because the charge is accumulated on the belt each time the transfer is repeated.

【０００６】第３に、紙等の記録媒体を転写ドラムに巻
き付けてこれを４回転させ、周回ごとに感光体上のマゼ
ンタ、イエロー、シアン、ブラックを順次記録媒体に転
写してカラー画像を再現する転写ドラム方式もある。こ
の方式によれば比較的高画質が得られるが、記録媒体が
葉書等の厚紙である場合には、これを前記転写ドラムに
巻き付けることが困難であり、記録媒体種が制限される
という問題点がある。Thirdly, a recording medium such as paper is wound around a transfer drum and rotated four times, and magenta, yellow, cyan, and black on the photoconductor are sequentially transferred to the recording medium for each revolution to reproduce a color image. There is also a transfer drum system. According to this method, a relatively high image quality can be obtained, but when the recording medium is a thick paper such as a postcard, it is difficult to wind it around the transfer drum, and the recording medium type is limited. There is.

【０００７】前記多重現像方式、タンデム方式及び転写
ドラム方式に対して、良好な画質が得られ、かつ装置が
特に大型化するようなこともなく、しかも記録媒体種が
特に制限されるようなこともない方式として、中間転写
方式が提案されている。即ち、この中間転写方式は、感
光体上のトナー像を一旦転写保持するドラムやベルトか
らなる中間転写部材を設け、この中間転写部材の周囲に
マゼンタによるトナー像、イエローによるトナー像、シ
アンによるトナー像及びブラックによるトナー像を形成
した４つの感光体を配置して４色のトナー像を中間転写
部材上に順次転写することにより、この中間転写部材上
にカラー画像を形成し、このカラー画像を紙等の記録媒
体上に転写するものである。従って、４色のトナー像を
重ね合わせて階調を調整するものであるから、高画質を
得ることが可能であり、かつタンデム方式のように感光
体を１列に並べる必要がないので装置が特に大型化する
こともなく、しかも記録媒体をドラムに巻き付ける必要
もないので記録媒体種が制限されることもないものであ
る。また、タンデム方式と中間転写方式とを組み合わせ
たタンデム中間転写方式もある。中間転写方式によりカ
ラー画像の形成を行う装置として、中間転写部材として
無端ベルト状の中間転写部材を用いた画像形成装置を図
３に例示する。With respect to the above-mentioned multiple development system, tandem system and transfer drum system, good image quality can be obtained, the apparatus does not become particularly large, and the recording medium type is particularly limited. An intermediate transfer method has been proposed as a non-existent method. That is, in this intermediate transfer system, an intermediate transfer member including a drum and a belt for temporarily transferring and holding the toner image on the photosensitive member is provided, and a magenta toner image, a yellow toner image, and a cyan toner image are provided around the intermediate transfer member. Images are formed on the intermediate transfer member by sequentially transferring the four color toner images on the intermediate transfer member by disposing four photoconductors on which the image and the black toner image are formed. It is transferred onto a recording medium such as paper. Therefore, since the toner images of four colors are superposed to adjust the gradation, it is possible to obtain high image quality, and it is not necessary to arrange the photoconductors in one line as in the tandem system. The size of the recording medium is not particularly limited because the recording medium does not need to be wound around a drum and the size of the recording medium is not limited. There is also a tandem intermediate transfer method that combines the tandem method and the intermediate transfer method. As an apparatus for forming a color image by the intermediate transfer system, an image forming apparatus using an endless belt-shaped intermediate transfer member as an intermediate transfer member is illustrated in FIG.

【０００８】図３中、１１はドラム状の感光体であり、
図中矢印方向に回転するようになっている。この感光体
１１は、一次帯電器１２によって帯電され、次いで画像
露光１３により露光部分の帯電が消去され、第１の色成
分に対応した静電潜像がこの感光体１１上に形成され、
更に静電潜像が現像器４１により第１色のマゼンタトナ
ーＭで現像され、第１色のマゼンタトナー画像が感光体
１１上に形成される。次いで、このトナー画像が、駆動
ローラ（駆動部材）３０により循環駆動されて感光体１
１と接触しながら循環回転する中間転写部材２０に転写
される。この場合、感光体１１から中間転写部材２０へ
の転写は、感光体１１と中間転写部材２０とのニップ部
において、中間転写部材２０に電源６１から印加される
一次転写バイアスにより行われる。この中間転写部材２
０に第１色のマゼンタトナー画像が転写された後、前記
感光体１１はその表面がクリーニング装置１４により清
掃され、感光体１１の１回転目の現像転写操作が完了す
る。以降、感光体が３回転し、各周回ごとに現像器４２
〜４４を順次用いて第２色のシアントナー画像、第３色
のイエロートナー画像、第４色のブラックトナー画像が
順次感光体１１上に形成され、これが周回ごとに中間転
写部材２０に重畳転写され、目的のカラー画像に対応し
た合成カラートナー画像が中間転写部材２０上に形成さ
れる。なお、図３の装置にあっては、感光体１１の周回
ごとに現像器４１〜４４が順次入れ替わってマゼンタト
ナーＭ、シアントナーＣ、イエロートナーＹ、ブラック
トナーＢによる現像が順次行われるようになっている。In FIG. 3, 11 is a drum-shaped photosensitive member,
It is designed to rotate in the direction of the arrow in the figure. The photoconductor 11 is charged by the primary charger 12, then the exposed portion is erased by image exposure 13, and an electrostatic latent image corresponding to the first color component is formed on the photoconductor 11.
Further, the electrostatic latent image is developed by the developing device 41 with the magenta toner M of the first color, and the magenta toner image of the first color is formed on the photoconductor 11. Then, the toner image is circulated and driven by the driving roller (driving member) 30 to form the photosensitive member 1.
The image is transferred to the intermediate transfer member 20 that rotates while rotating in contact with 1. In this case, the transfer from the photoconductor 11 to the intermediate transfer member 20 is performed in the nip portion between the photoconductor 11 and the intermediate transfer member 20 by the primary transfer bias applied from the power supply 61 to the intermediate transfer member 20. This intermediate transfer member 2
After the first-color magenta toner image is transferred to 0, the surface of the photoconductor 11 is cleaned by the cleaning device 14, and the developing and transferring operation for the first rotation of the photoconductor 11 is completed. After that, the photoconductor rotates three times, and the developing unit 42 is rotated every revolution.
To 44 are sequentially used to sequentially form a cyan toner image of the second color, a yellow toner image of the third color, and a black toner image of the fourth color on the photoconductor 11, which are superposed and transferred to the intermediate transfer member 20 for each revolution. Then, a composite color toner image corresponding to the target color image is formed on the intermediate transfer member 20. In the apparatus shown in FIG. 3, the developing devices 41 to 44 are sequentially replaced for each revolution of the photoconductor 11 so that development with the magenta toner M, the cyan toner C, the yellow toner Y, and the black toner B is sequentially performed. Has become.

【０００９】次に、前記合成カラートナー画像が形成さ
れた中間転写部材２０に転写ローラ２５が当接し、その
ニップ部に給紙カセット１９から紙等の記録媒体２６が
給送される。これと同時に二次転写バイアスが電源２９
から転写ローラ２５に印加され、中間転写部材２０から
記録媒体２６上に合成カラートナー画像が転写されて加
熱定着され、最終画像となる。合成カラートナー画像を
記録媒体２６へと転写した後の中間転写部材２０は、表
面の転写残留トナーがクリーニング装置３５により除去
され、初期状態に戻り次の画像形成に備えるようになっ
ている。従来、かかる無端ベルト状の中間転写部材２０
として、半導電性の樹脂フィルムベルトと、繊維補強体
を有するゴムベルトとが主に用いられている。これらの
うち、半導電性の樹脂フィルムベルトとしては、従来、
ポリカーボネートにカーボンブラックを配合したものが
知られているが、最近では、折り曲げに対する耐久性面
での改良を図ったポリアルキレンテレフタレートを基材
とする樹脂フィルムベルト（特開平８−９９３７４号公
報）や、弾性面での改良を図った熱可塑性ポリイミドを
基材とする樹脂フィルムベルト（特開平１１−１７０３
８９号公報）などが提案されている。Next, the transfer roller 25 contacts the intermediate transfer member 20 on which the composite color toner image is formed, and the recording medium 26 such as paper is fed from the paper feed cassette 19 to the nip portion thereof. At the same time, the secondary transfer bias is the power source 29.
Is applied to the transfer roller 25 from the intermediate transfer member 20, and the composite color toner image is transferred from the intermediate transfer member 20 onto the recording medium 26 and heat-fixed to form a final image. After the transfer of the combined color toner image to the recording medium 26, the transfer residual toner on the surface of the intermediate transfer member 20 is removed by the cleaning device 35, and the initial state is restored to prepare for the next image formation. Conventionally, such an endless belt-shaped intermediate transfer member 20
For this purpose, a semiconductive resin film belt and a rubber belt having a fiber reinforcement are mainly used. Among these, as the semi-conductive resin film belt, conventionally,
Polycarbonate blended with carbon black is known, but recently, a resin film belt based on polyalkylene terephthalate (Japanese Patent Laid-Open No. 8-99374), which has been improved in terms of durability against bending, and , A resin film belt using thermoplastic polyimide as a base material, which has been improved in terms of elasticity (JP-A-11-1703).
No. 89) has been proposed.

【００１０】[0010]

【発明が解決しようとする課題】導電性エンドレスベル
トを使用するタンデム方式、中間転写方式及びタンデム
中間転写方式の画像形成装置においては、いずれも導電
性エンドレスベルトに対し、機構面で繰り返し連続使用
に耐える強度、特には屈曲耐久性、耐クリープ性及びベ
ルト表面の平滑性が要求される。In the image forming apparatus of the tandem system, the intermediate transfer system and the tandem intermediate transfer system using the electroconductive endless belt, the electrophotographic endless belt is repeatedly and continuously used in terms of its mechanism. It is required to have strength to endure, particularly bending durability, creep resistance and smoothness of the belt surface.

【００１１】そこで本発明の目的は、タンデム方式、中
間転写方式及びタンデム中間転写方式の画像形成装置に
使用する樹脂フィルムベルトにおいて、良好な強度、特
には良好な屈曲耐久性と耐クリープ性、更には表面の平
滑性を備える導電性エンドレスベルト及びこれを用いた
画像形成装置を提供することにある。Therefore, an object of the present invention is to provide a resin film belt for use in a tandem type, intermediate transfer type and tandem intermediate transfer type image forming apparatus, which has good strength, particularly good bending durability and creep resistance, and further Is to provide a conductive endless belt having a smooth surface and an image forming apparatus using the same.

【００１２】[0012]

【課題を解決するための手段】本発明者は、前記課題を
解決すべく各種合成樹脂について鋭意検討を行った結
果、導電性エンドレスベルトの基材として、熱可塑性樹
脂とウイスカとの混合物を用いることにより前記目的を
達成し得ることを見出し、本発明を完成するに至った。
すなわち本発明は下記に示す通りである。Means for Solving the Problems As a result of extensive studies on various synthetic resins to solve the above problems, the present inventor uses a mixture of a thermoplastic resin and whiskers as a base material of a conductive endless belt. As a result, they have found that the above object can be achieved, and completed the present invention.
That is, the present invention is as shown below.

【００１３】（１）．静電吸着により保持した記録媒体
を、駆動部材により循環駆動されて、４種の画像形成体
に運送し、各トナー像を該記録媒体に順次転写するタン
デム方式の転写及び／又は搬送用導電性エンドレスベル
トにおいて、熱可塑性樹脂とウイスカ（アスペクト比１
０以上の繊維状無機化合物及び／又は金属粒子）との混
合物を基材とすることを特徴とする導電性エンドレスベ
ルト。 （２）．画像形成体と記録媒体との間に配設され、駆動
部材により循環駆動されて、前記画像形成体表面に形成
されたトナー像を一旦自己の表面に転写保持し、これを
記録媒体へと転写する中間転写部材用導電性エンドレス
ベルトにおいて、熱可塑性樹脂とウイスカ（アスペクト
比１０以上の繊維状無機化合物及び／又は金属粒子）と
の混合物を基材とすることを特徴とする導電性エンドレ
スベルト。 （３）．前記混合物中のウイスカ成分の割合が、５〜５
０重量％であることを特徴とする前記（１）又は（２）
記載の導電性エンドレスベルト。 （４）．前記ウイスカの平均長軸繊維長が０．２〜４０
μｍであることを特徴とする前記（１）又は（２）記載
の導電性エンドレスベルト。 （５）．前記ウイスカが、ケイ酸カルシウム水和物（Ｃ
ａ₆ （Ｓｉ₆ ０₁₇）（ＯＨ）₂ ）を主成分として９０重
量％以上含有することを特徴とする前記（１）又は
（２）記載の導電性エンドレスベルト。 （６）．前記熱可塑性樹脂が、ポリアミド１２を含有す
ることを特徴とする前記（１）又は（２）記載の導電性
エンドレスベルト。 （７）．前記（１）又は（２）のいずれかに記載の導電
性エンドレスベルトを用いたことを特徴とする画像形成
装置。(1). A recording medium held by electrostatic attraction is cyclically driven by a driving member to be transported to four types of image forming bodies, and each toner image is sequentially transferred to the recording medium in a tandem system for transfer and / or transport conductivity. In the endless belt, thermoplastic resin and whisker (aspect ratio 1
A conductive endless belt comprising a mixture of 0 or more fibrous inorganic compounds and / or metal particles) as a base material. (2). The toner image formed on the surface of the image forming body is temporarily transferred and held on the surface of the image forming body, which is disposed between the image forming body and the recording medium and is circularly driven by a driving member, and then transferred to the recording medium. In the electroconductive endless belt for intermediate transfer member, the electroconductive endless belt is characterized by using a mixture of a thermoplastic resin and whiskers (fibrous inorganic compound and / or metal particles having an aspect ratio of 10 or more) as a base material. (3). The ratio of the whisker component in the mixture is 5 to 5
The above (1) or (2), which is 0% by weight
The conductive endless belt described. (4). The whisker has an average major axis fiber length of 0.2 to 40
The conductive endless belt according to (1) or (2) above, wherein the conductive endless belt has a thickness of μm. (5). The whiskers are calcium silicate hydrate (C
The electroconductive endless belt according to (1) or (2) above, which contains a ₆ (Si _{60 17} ) (OH) ₂ as a main component in an amount of 90% by weight or more. (6). The electrically conductive endless belt according to (1) or (2) above, wherein the thermoplastic resin contains polyamide 12. (7). An image forming apparatus using the conductive endless belt according to any one of (1) and (2).

【００１４】上述の本発明の導電性エンドレスベルト
は、良好な強度、特には良好な屈曲耐久性及び耐クリー
プ性を備え、かつ、ベルト表面の高い平滑性を有する。
また、前記駆動部材と導電性エンドレスベルトとに互い
に嵌合する嵌合部を設けた場合には、２以上の軸に張架
した導電性エンドレスベルトが回転とともに幅方向にず
れて行く現象を防止することができる。また、本発明の
画像形成装置によれば、長期間にわたる使用においても
不良を生ずることがなく、良好な画像を提供することが
できる。The above-mentioned conductive endless belt of the present invention has good strength, particularly good bending durability and creep resistance, and has a high smoothness of the belt surface.
Further, when the driving member and the conductive endless belt are provided with fitting portions for fitting each other, it is possible to prevent the conductive endless belt stretched around two or more shafts from shifting in the width direction with rotation. can do. Further, according to the image forming apparatus of the present invention, it is possible to provide a good image without causing a defect even after long-term use.

【００１５】[0015]

【発明の実施の形態】以下、本発明の実施の形態につき
詳細に説明する。導電性エンドレスベルトには、一般
に、ジョイントありのものとジョイントなしのもの（い
わゆるシームレスベルト）とがあるが、本発明において
はいずれのものであってもよい。本発明の導電性エンド
レスベルトは、前述したように、タンデム方式、中間転
写方式及びタンデム中間転写方式の転写部材等として用
いることができるものである。本発明の導電性エンドレ
スベルトが、例えば、図２に参照符号１０で示す転写搬
送ベルトである場合、駆動ローラ９等の駆動部材により
駆動され、これに伴い搬送される記録媒体上にトナーが
順次転写され、カラー画像が形成される。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described in detail below. The conductive endless belt is generally classified into a jointed type and a jointless type (so-called seamless belt), but any type may be used in the present invention. As described above, the conductive endless belt of the present invention can be used as a transfer member of a tandem system, an intermediate transfer system, and a tandem intermediate transfer system. When the conductive endless belt of the present invention is, for example, a transfer / conveyance belt shown by reference numeral 10 in FIG. 2, the toner is sequentially driven on the recording medium conveyed by being driven by the driving member such as the driving roller 9. Transferred to form a color image.

【００１６】また、本発明の導電性エンドレスベルト
が、例えば、図３に参照符号２０で示す中間転写部材で
ある場合、これを駆動ローラ３０等の駆動部材により循
環駆動させ、感光体ドラム（潜像保持体）１１と紙等の
記録媒体２６との間に配設することで、前記感光ドラム
１１の表面に形成されたトナー像を一旦転写保持し、次
いでこれを記録媒体２６へと転写する。なお、図３の装
置は、上述したように、中間転写方式によりカラー印刷
を行うものである。Further, when the conductive endless belt of the present invention is, for example, an intermediate transfer member indicated by reference numeral 20 in FIG. 3, it is circulated and driven by a driving member such as a driving roller 30 and the photosensitive drum (latent). The toner image formed on the surface of the photosensitive drum 11 is temporarily transferred and held by arranging it between the image carrier 11 and the recording medium 26 such as paper, and then transferred to the recording medium 26. . The apparatus of FIG. 3 performs color printing by the intermediate transfer method as described above.

【００１７】本発明の導電性エンドレスベルトの基材を
構成する熱可塑性樹脂とウイスカとの混合物において、
ウイスカ成分の割合が、５〜５０重量％であると好まし
く、１０〜３０重量％であるとさらに好ましい。ウイス
カ成分の割合が、５重量％未満であると、十分な耐屈曲
性及び耐クリープ性が得られないことがあり、５０重量
％を越えるとベルト表面の平滑性が損なわれることがあ
る。In the mixture of the thermoplastic resin and the whiskers, which constitutes the base material of the conductive endless belt of the present invention,
The proportion of the whisker component is preferably 5 to 50% by weight, more preferably 10 to 30% by weight. If the proportion of the whisker component is less than 5% by weight, sufficient flex resistance and creep resistance may not be obtained, and if it exceeds 50% by weight, the smoothness of the belt surface may be impaired.

【００１８】熱可塑性樹脂としては、特に限定されず市
販のものを使用すればよく、例えば、ポリアミド１２、
アクリロニトリル−ブタジエン−スチレン、アクリロニ
トリル−エチレンプロピレンースチレン、ポリアミド
６、ポリアミド６６、ポリアセタール、ポリメチルメタ
クリレート、ポリフッ化ビニリデン、ポリフッ化ビニ
ル、ポリ六フッ化エチレンプロピレン、ポリ三フッ化エ
チレン、ポリ（エチレン−テトラフルオロエチレン) 、
ポリアクリロニトリル、ポリアリレート、ポリブチレン
テレフタレート、ポリカーボネート、ポリエーテルエー
テルケトン、ポリエーテルイミド、ポリエーテルスルホ
ン、ポリエチレン、ポリエチレンテレフタレート、ポリ
スチレン、ポリフェニレンオキサイド、ポリスルホン及
びポリアリレート等が挙げられ、ポリアミド１２及びア
クリロニトリル−ブタジエン−スチレンが好ましく、ポ
リアミド１２がさらに好ましい。The thermoplastic resin is not particularly limited and may be a commercially available one, for example, polyamide 12,
Acrylonitrile-butadiene-styrene, acrylonitrile-ethylene propylene-styrene, polyamide 6, polyamide 66, polyacetal, polymethylmethacrylate, polyvinylidene fluoride, polyvinyl fluoride, polyhexafluoroethylene propylene, polytrifluoride ethylene, poly (ethylene- Tetrafluoroethylene),
Polyacrylonitrile, polyarylate, polybutylene terephthalate, polycarbonate, polyether ether ketone, polyetherimide, polyether sulfone, polyethylene, polyethylene terephthalate, polystyrene, polyphenylene oxide, polysulfone and polyarylate, and the like, polyamide 12, and acrylonitrile-butadiene. -Styrene is preferred and polyamide 12 is more preferred.

【００１９】また、ウイスカの主成分としては、特に限
定されず市販のものを使用すればよく、例えば、ケイ酸
カルシウム水和物ウイスカ（Ｃａ₆ ・Ｓｉ₆ Ｏ₁₇・（Ｏ
Ｈ） ₂ ）、塩基性水酸マグネシウム水和物ウイスカ（Ｍ
ｇＳＯ₄ ・５Ｍｇ（ＯＨ）₂・３Ｈ₂ Ｏ）、チタン酸カ
リウムウイスカ（Ｋ₂ Ｏ・６ＴｉＯ₂ 及びＫ₂ Ｏ・８Ｔ
ｉＯ₂ ）、ホウ酸アルミニウムウイスカ、チタン酸カリ
ウムウイスカ、カーボンウイスカ、黒鉛ウイスカ、炭化
チタンウイスカ、導電性チタン酸カリウムウイスカ、導
電性チタン酸バリウムウイスカ、導電性酸化チタンウイ
スカ、ウオラストナイトウイスカ、セピオライトウイス
カ、ホウ酸アルミニウムウイスカ、アルミナウイスカ、
クロムウイスカ、銅ウイスカ、鉄ウイスカ、ニッケルウ
イスカ、炭化ケイ素ウイスカ、窒化ケイ素ウイスカ、酸
化亜鉛ウイスカ及び炭酸カルシウムウイスカ等が挙げら
れ、ケイ酸カルシウム水和物ウイスカ、塩基性水酸マグ
ネシウム水和物ウイスカ及びチタン酸カリウムウイスカ
が好ましく、ケイ酸カルシウム水和物ウイスカがさらに
好ましい。ウイスカは、これらの成分を９０重量％以上
含有することが好ましく、７５重量％以上含有するとさ
らに好ましい。ウイスカは、平均長軸繊維長が０．２〜
４０μｍであると好ましく、０．４〜２０であるとさら
に好ましい。The main components of whiskers are not particularly limited.
A commercially available product may be used, such as silicic acid.
Calcium hydrate whisker (Ca₆・ Si₆O₁₇・ (O
H) ₂), Basic magnesium hydroxide hydrate whisker (M
gSO_Four・ 5Mg (OH)₂・ 3H₂O), titanium titanate
Rium whiskers (K₂O ・ 6TiO₂And K₂O / 8T
iO₂), Aluminum borate whiskers, potassium titanate
Um whiskers, carbon whiskers, graphite whiskers, carbonization
Titanium whiskers, conductive potassium titanate whiskers, conductive
Electroconductive barium titanate whisker, conductive titanium oxide whisker
Ska, wollastonite whisker, sepiolite whisker
Mosquito, aluminum borate whiskers, alumina whiskers,
Chrome whiskers, copper whiskers, iron whiskers, nickel whiskers
Isker, Silicon Carbide Whisker, Silicon Nitride Whisker, Acid
Examples include zinc oxide whiskers and calcium carbonate whiskers.
Calcium silicate hydrate whisker, basic hydroxide mug
Nesium hydrate whisker and potassium titanate whisker
Is preferred, and calcium silicate hydrate whiskers are
preferable. Whiskers contain 90% by weight or more of these ingredients
It is preferable to contain 75% by weight or more.
Preferred. Whiskers have an average major axis fiber length of 0.2 to
The thickness is preferably 40 μm, and more preferably 0.4 to 20.
Is preferred.

【００２０】さらに、熱可塑性樹脂とウイスカとの混合
物には、機能性成分として導電性材料を添加して導電性
を付与又は調整することができる。この場合、導電性材
料としては、特に限定されず、ラウリルトリメチルアン
モニウム、ステアリルトリメチルアンモニウム、オクタ
デシルトリメチルアンモニウム、ドデシルトリメチルア
ンモニウム、ヘキサデシルトリメチルアンモニウム、変
性脂肪酸・ジメチルエチルアンモニウムの過塩素酸塩、
塩素酸塩、ホウフッ化水素酸塩、硫酸塩、エトサルフェ
ート塩、ハロゲン化ベンジル塩（臭化ベンジル塩、塩化
ベンジル塩等）等の第４級アンモニウムなどの陽イオン
界面活性剤；脂肪族スルホン酸、高級アルコール硫酸エ
ステル塩、高級アルコールエチレンオキサイド付加硫酸
塩、高級アルコール燐酸エステル塩等の陰イオン界面活
性剤；各種ベタイン等の両性イオン界面活性剤；高級ア
ルコールエチレンオキサイド、ポリエチレングリコール
脂肪酸エステル、多価アルコール脂肪酸エステル等の非
イオン性帯電防止剤などの帯電防止剤、ＬｉＣＦ₂ ＳＯ
₂ 、ＮａＣｌＯ₄ 、ＬｉＢＦ₄ 、ＮａＣｌ等の周期律表
第１族の金属塩；Ｃａ（ＣｌＯ₄ ）₂ 等の周期律表第２
族の金属塩：及びこれらの帯電防止剤がイソシアネート
と反応する活性水素を有する基（水素基、カルボキシル
基、一級乃至二級アミン基等）を１個以上有するものな
どが挙げられる。更にまた、これらと多価アルコール
（１，４−ブタンジオール、エチレングリコール、ポリ
エチレングリコール、プロピレングリコール等）又はそ
の誘導体との錯体、或いはエチレングリコールモノメチ
ルエーテル、エチレングリコールモノエチルエーテル等
との錯体などのイオン導電剤；ケッチェンブラック、ア
セチレンブラック等の導電性カーボン；ＳＡＦ、ＩＳＡ
Ｆ、ＨＡＦ、ＦＥＦ、ＧＰＦ、ＳＲＦ、ＦＴ、ＭＴ等の
ゴム用カーボン；酸化処理を施したカラーインク用カー
ボン、熱分解カーボン、天然グラファイト、人造グラフ
ァイト等；酸化スズ、酸化チタン、酸化亜鉛、ニッケ
ル、銅等の金属及び金属酸化物；ポリアニリン、ポリピ
ロール、ポリアセチレン等の導電性ポリマーなどを例示
することができる。Furthermore, a conductive material can be added to the mixture of the thermoplastic resin and the whiskers as a functional component to impart or adjust the conductivity. In this case, the conductive material is not particularly limited, lauryl trimethyl ammonium, stearyl trimethyl ammonium, octadecyl trimethyl ammonium, dodecyl trimethyl ammonium, hexadecyl trimethyl ammonium, perchlorate of modified fatty acid dimethyl ethyl ammonium,
Cationic surfactants such as quaternary ammonium such as chlorates, borofluorides, sulphates, ethosulfates, benzyl halides (benzyl bromide, benzyl chloride etc.); aliphatic sulfonic acids , Higher alcohol sulfate ester salt, higher alcohol ethylene oxide addition sulfate salt, higher alcohol phosphate ester salt and other anionic surfactants; various betaine and other zwitterionic surfactants; higher alcohol ethylene oxide, polyethylene glycol fatty acid ester, polyvalent Antistatic agents such as nonionic antistatic agents such as alcohol fatty acid esters, LiCF ₂ SO
_2, NaClO _4, LiBF _4, periodic table Group 1 metal salts such as NaCl; Ca (ClO ₄₎ period of ₂ such as Table second
Group metal salts: and those in which these antistatic agents have one or more groups (hydrogen group, carboxyl group, primary or secondary amine group, etc.) having active hydrogen that reacts with isocyanate. Furthermore, a complex of these with a polyhydric alcohol (1,4-butanediol, ethylene glycol, polyethylene glycol, propylene glycol, etc.) or a derivative thereof, or a complex with ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, etc. Ion conductive agent; conductive carbon such as Ketjen black and acetylene black; SAF, ISA
Carbon for rubber such as F, HAF, FEF, GPF, SRF, FT, MT; carbon for color ink that has been subjected to oxidation treatment, pyrolytic carbon, natural graphite, artificial graphite, etc .; tin oxide, titanium oxide, zinc oxide, nickel Examples thereof include metals such as copper, and metal oxides; conductive polymers such as polyaniline, polypyrrole, and polyacetylene.

【００２１】これら導電性材料の基材への添加量は、導
電性材料がカーボンブラックの場合には樹脂成分１００
重量部に対して０．１〜１００重量部、好ましくは０．
５〜５０重量部とすることができ、これにより弾性材層
の体積抵抗値を１０⁶ 〜１０ ¹³Ω・ｃｍ、好ましくは１
０⁷〜１０¹²Ω・ｃｍに調整することができる。The amount of these conductive materials added to the substrate is
When the electrically conductive material is carbon black, the resin component 100
0.1 to 100 parts by weight, preferably 0.
5 to 50 parts by weight, whereby the elastic material layer
Volume resistance of 10⁶-10 ¹³Ω · cm, preferably 1
0⁷-10¹²It can be adjusted to Ω · cm.

【００２２】本発明においては、本発明の効果を損なわ
ない範囲内で上述の成分に加え他の機能性成分を添加す
ることができ、例えば、各種充填材、カップリング剤、
酸化防止剤、滑材、表面処理剤、顔料、紫外線吸収剤、
帯電防止剤、分散剤、中和剤、発泡剤、架橋剤、相溶化
材等を適宜配合することができる。本発明の導電性エン
ドレスベルトの厚さは、転写搬送ベルト又は中間転写部
材等の形態に応じて適宜選定されるものであるが、好ま
しくは５０〜２００μｍの範囲内である。In the present invention, other functional components may be added in addition to the above-mentioned components within the range that does not impair the effects of the present invention. For example, various fillers, coupling agents,
Antioxidant, lubricant, surface treatment agent, pigment, UV absorber,
An antistatic agent, a dispersant, a neutralizing agent, a foaming agent, a cross-linking agent, a compatibilizing agent and the like can be appropriately added. The thickness of the conductive endless belt of the present invention is appropriately selected according to the form of the transfer / transport belt or the intermediate transfer member, but is preferably in the range of 50 to 200 μm.

【００２３】本発明の導電性エンドレスベルトには、図
１に一点鎖線で示すように、図２の画像形成装置におけ
る駆動ローラ９又は図３の駆動ローラ３０などの駆動部
材と接触する側の面に、該駆動部材に形成した嵌合部
（図示せず）と嵌合する嵌合部を形成してもよく、本発
明の導電性エンドレスベルトは、このような嵌合部を設
け、これを駆動部材に設けた嵌合部（図示せず）と嵌合
させて走行させることにより、導電性エンドレスベルト
の幅方向のずれを防止することができる。この場合、前
記嵌合部は、特に制限されるものではないが、図１に示
すように、ベルトの周方向（回転方向）に沿って連続す
る凸条とし、これを駆動ローラ等の駆動部材の周面に周
方向に沿って形成した溝に嵌合させるようにすることが
好ましい。The conductive endless belt of the present invention has a surface on the side which comes into contact with a driving member such as the driving roller 9 in the image forming apparatus of FIG. 2 or the driving roller 30 of FIG. 3 as shown by the chain line in FIG. In addition, a fitting portion that fits with a fitting portion (not shown) formed on the drive member may be formed. The conductive endless belt of the present invention is provided with such a fitting portion, and It is possible to prevent the conductive endless belt from being displaced in the width direction by being fitted into a fitting portion (not shown) provided on the drive member and running. In this case, the fitting portion is not particularly limited, but as shown in FIG. 1, it is a ridge continuous along the circumferential direction (rotational direction) of the belt, which is a driving member such as a driving roller. It is preferable to fit into a groove formed along the circumferential direction on the circumferential surface.

【００２４】なお、図１（ａ）では、１本の連続する凸
条を嵌合部として設けた例を示したが、この嵌合部は多
数の凸部をベルトの周方向（回転方向）に沿って一列に
並べて突設してもよく、また嵌合部を２本以上設けたり
（図１（ｂ））、ベルトの幅方向中央部に設けてもよ
い。更に、嵌合部として図１に示した凸条ではなく、ベ
ルトの周方向（回転方向）に沿った溝を設け、これを前
記駆動ローラ等の駆動部材の周面に周方向に沿って形成
した凸条と嵌合させるようにしてもよい。本発明の導電
性エンドレスベルトを用いた本発明の画像形成装置とし
ては、図２に示すタンデム方式のものや図３に示す中間
転写方式のもの、又は、タンデム中間転写方式のものを
例示することができるが、これらには限定されない。
尚、図３の装置の場合、本発明の中間転写部材２０を回
転させる駆動ローラ又は駆動ギアには適宜な電源６１か
ら電圧を印加することができ、この場合の電圧は直流の
みの印加又は直流に交流を重量する印加など、印加条件
は適時選択することができる。Although FIG. 1A shows an example in which one continuous convex strip is provided as the fitting portion, this fitting portion has a large number of convex portions in the circumferential direction (rotational direction) of the belt. May be provided so as to be lined up in a line along with, and two or more fitting portions may be provided (FIG. 1B), or may be provided at the central portion in the width direction of the belt. Further, a groove extending along the circumferential direction (rotational direction) of the belt is provided as the fitting portion instead of the ridge shown in FIG. 1, and the groove is formed on the circumferential surface of the driving member such as the driving roller along the circumferential direction. You may make it fit with the said convex line. The image forming apparatus of the present invention using the conductive endless belt of the present invention is exemplified by the tandem type shown in FIG. 2, the intermediate transfer type shown in FIG. 3, or the tandem intermediate transfer type. However, the present invention is not limited to these.
In the case of the apparatus shown in FIG. 3, a voltage can be applied from a suitable power source 61 to the drive roller or drive gear that rotates the intermediate transfer member 20 of the present invention. The application conditions such as the application of weighting alternating current can be appropriately selected.

【００２５】本発明の導電性エンドレスベルトの製法は
特に制限されるべきものではなく、例えば、二軸混練機
により樹脂成分（熱可塑性樹脂とウイスカとの混合物）
と導電性材料等の機能性成分とを混練し、得られた混練
物を環状ダイスを使って押出し成形することにより製造
することができる。あるいは、静電塗装等の粉体塗装
法、溶液ディップ法又は遠心注型法を好適に採用するこ
とができる。The method for producing the electroconductive endless belt of the present invention is not particularly limited, and for example, a resin component (a mixture of a thermoplastic resin and whiskers) can be obtained by using a biaxial kneader.
And a functional component such as a conductive material are kneaded, and the resulting kneaded product is extruded and molded using a ring die. Alternatively, a powder coating method such as electrostatic coating, a solution dipping method, or a centrifugal casting method can be preferably adopted.

【００２６】[0026]

【実施例】以下に、本発明を実施例に基づき説明する。 実施例１ ポリアミド１２樹脂（ダイセル−デグサ（株）製、ダイ
アミドＬ１９４０）５０重量％と、帯電防止剤（チバガ
イギー（株）製、イルガスタットＰ−１８）２０重量％
と、ケイ酸カルシウム水和物ウイスカ（宇部マテリアル
ズ（株）製、ゾノハイジ（平均繊維長１〜５μｍ、平均
繊維径０．１〜０．５μｍ、アスペクト比１０〜２
０）、Ｃａ₆ ・Ｓｉ₆ Ｏ₁₇・（ＯＨ）₂ ）３０重量％と
を二軸混練機によって溶融混練して、得られた混練物を
押出し成形することにより、内径２４５ｍｍ、厚さ１０
０μｍ、幅２５０ｍｍの寸法を有する導電性エンドレス
ベルトを得た。この導電性エンドレスベルトの表面平滑
性Ｒａを東京精密（株）製の表面粗さ・形状測定器サー
フコム５９０Ａを用いて測定した。この値は、数値が小
さいほど表面が滑らかである。また、この導電性エンド
レスベルトの耐折り曲げ回数を東洋精機（株）製の耐揉
疲労試験機を用いて測定し、引張りクリープ量の測定
を、ＪＩＳ Ｋ７１１５試験法に従い、温度２５℃にて
１２００時間で行った。引張りクリープ量は、数値が小
さいほど、耐クリープ性が優れている。さらに、体積固
有抵抗率の測定を、温度２０℃、相対湿度５０％にて、
測定電圧１００Ｖで、測定装置としてアドバンテスト
（ＡＤＶＡＮＴＥＳＴ）社製の、抵抗計Ｒ８３４０Ａに
サンプルチャンバーＲ１２７０４Ａを接続したものを用
いて行った。EXAMPLES The present invention will be described below based on examples. Example 1 Polyamide 12 resin (manufactured by Daicel-Degussa Co., Ltd., Daiamide L1940) 50% by weight and antistatic agent (Ciba Geigy Co., Ltd., Irgasat P-18) 20% by weight
And calcium silicate hydrate whisker (manufactured by Ube Materials Co., Ltd., Zonoheiji (average fiber length 1 to 5 μm, average fiber diameter 0.1 to 0.5 μm, aspect ratio 10 to 2)
0) and 30% by weight of Ca ₆ · Si ₆ O ₁₇ · (OH) ₂ ) are melt-kneaded by a biaxial kneader, and the resulting kneaded product is extruded to give an inner diameter of 245 mm and a thickness of 10
A conductive endless belt having dimensions of 0 μm and a width of 250 mm was obtained. The surface smoothness Ra of this conductive endless belt was measured using a surface roughness / shape measuring device Surfcom 590A manufactured by Tokyo Seimitsu Co., Ltd. The smaller the value, the smoother the surface. Further, the number of times of bending resistance of this conductive endless belt was measured using a kneading fatigue tester manufactured by Toyo Seiki Co., Ltd., and the amount of tensile creep was measured according to JIS K7115 test method at a temperature of 25 ° C. for 1200 hours. I went there. The smaller the tensile creep amount, the better the creep resistance. Further, the volume resistivity is measured at a temperature of 20 ° C. and a relative humidity of 50%.
The measurement was performed at a measurement voltage of 100 V using a resistance meter R8340A manufactured by ADVANTEST Co., Ltd. and a sample chamber R12704A connected thereto.

【００２７】実施例２ ポリアミド１２樹脂に代えて、アクリロニトリル−ブタ
ジエン−スチレン樹脂（ダイセルポリマー（株）製、セ
ビアンＶ５１０）を用いた以外は実施例１と同様にして
導電性エンドレスベルトを作製し、実施例１と同様にし
てその特性を測定した。Example 2 A conductive endless belt was prepared in the same manner as in Example 1 except that acrylonitrile-butadiene-styrene resin (Sebian V510 manufactured by Daicel Polymer Co., Ltd.) was used in place of the polyamide 12 resin. The characteristics were measured in the same manner as in Example 1.

【００２８】実施例３ ケイ酸カルシウム水和物ウイスカに代えて、塩基性硫酸
マグネシウム水和物ウイスカ（宇部マテリアルズ（株）
製、モスハイジ、ＭｇＳＯ₄ ・５Ｍｇ（ＯＨ） ₂ ・３Ｈ
₂ Ｏ）を用いた以外は実施例１と同様にして導電性エン
ドレスベルトを作製し、実施例１と同様にしてその特性
を測定した。Example 3 Calcium silicate hydrate Whisker instead of basic sulfuric acid
Magnesium hydrate whisker (Ube Materials Co., Ltd.)
Made, Mos Heidi, MgSO_Four・ 5Mg (OH) ₂・ 3H
₂O) was used in the same manner as in Example 1 except that the conductive en
A dress belt was produced and its characteristics were the same as in Example 1.
Was measured.

【００２９】実施例４ ケイ酸カルシウム水和物ウイスカに代えて、チタン酸カ
リウムウイスカ（大塚化学（株）製、ティスモ−Ｄ、Ｋ
₂ Ｏ・８ＴｉＯ₂ ）を用いた以外は実施例１と同様にし
て導電性エンドレスベルトを作製し、実施例１と同様に
してその特性を測定した。Example 4 Instead of calcium silicate hydrate whiskers, potassium titanate whiskers (manufactured by Otsuka Chemical Co., Ltd., Tismo-D, K)
_A conductive endless belt was produced in the same manner as in Example 1 except that ₂ O · 8TiO ₂ ) was used, and its characteristics were measured in the same manner as in Example 1.

【００３０】実施例５ 配合比を、ポリアミド１２樹脂６８重量％、帯電防止剤
２７重量％、ケイ酸カルシウム水和物ウイスカ５重量％
とした以外は実施例１と同様にして導電性エンドレスベ
ルトを作製し、実施例１と同様にしてその特性を測定し
た。Example 5 Polyamide 12 resin 68% by weight, antistatic agent 27% by weight, calcium silicate hydrate whisker 5% by weight
A conductive endless belt was produced in the same manner as in Example 1 except for the above, and the characteristics were measured in the same manner as in Example 1.

【００３１】実施例６ 配合比を、ポリアミド１２樹脂３６重量％、帯電防止剤
１４重量％、ケイ酸カルシウム水和物ウイスカ５０重量
％とした以外は実施例１と同様にして導電性エンドレス
ベルトを作製し、実施例１と同様にしてその特性を測定
した。Example 6 A conductive endless belt was prepared in the same manner as in Example 1 except that the compounding ratio was 36% by weight of polyamide 12 resin, 14% by weight of antistatic agent and 50% by weight of calcium silicate hydrate whisker. It was manufactured and its characteristics were measured in the same manner as in Example 1.

【００３２】比較例１ ケイ酸カルシウム水和物ウイスカに代えて、酸化マグネ
シウム（神島化学（株）製、スターマグＬ、ＭｇＯ）を
用いた以外は実施例１と同様にして導電性エンドレスベ
ルトを作製し、実施例１と同様にしてその特性を測定し
た。Comparative Example 1 A conductive endless belt was produced in the same manner as in Example 1 except that magnesium oxide (Star Mag L, MgO manufactured by Kamijima Chemical Co., Ltd.) was used in place of the calcium silicate hydrate whiskers. Then, the characteristics were measured in the same manner as in Example 1.

【００３３】また、上記実施例及び比較例の導電性エン
ドレスベルトを図２に示した転写搬送ベルトを用いたタ
ンデム方式の画像形成装置に装着し、転写操作を繰り返
してＡ４用紙１０万枚の耐久試験を行った。このとき、
随時形成された画像と導電性エンドレスベルトの表面を
観察して亀裂の有無を確認し、画像性とベルトの表面性
について評価した。画像が良好でベルトに亀裂が無いも
のをＯＫ、画像が悪い及び／又はベルトの表面に亀裂が
有るものをＮＧとした。上記表面平滑性Ｒａ、耐折り曲
げ回数、引張りクリープ量、体積抵抗率及び画像性の結
果を下記表１に示す。尚、表中、耐折り曲げ回数につい
ては実施例を１００以上として指数表示した。Further, the conductive endless belts of the above examples and comparative examples were mounted on the tandem type image forming apparatus using the transfer / conveying belt shown in FIG. 2, and the transfer operation was repeated to endure 100,000 A4 sheets. The test was conducted. At this time,
The images formed at any time and the surface of the conductive endless belt were observed to confirm the presence or absence of cracks, and the image property and the surface property of the belt were evaluated. An image having a good image and no cracks on the belt was OK, and a film having a bad image and / or having a crack on the surface of the belt was NG. The results of the surface smoothness Ra, the number of times of bending resistance, the amount of tensile creep, the volume resistivity and the imageability are shown in Table 1 below. In addition, in the table, the number of times of bending resistance was indexed by setting the example to 100 or more.

【００３４】[0034]

【表１】 [Table 1]

【００３５】以上の測定及び試験の結果より、実施例の
導電性エンドレスベルトは、表面平滑性、屈曲耐久性、
耐クリープ性及び画像性の点で顕著な優位性を有するこ
とが確認された。From the results of the above measurement and test, the electroconductive endless belts of the examples have surface smoothness, bending durability, and
It was confirmed that there are remarkable advantages in terms of creep resistance and image quality.

【００３６】[0036]

【発明の効果】以上説明してきたように、本発明によれ
ば、高い寸法精度を有し、強度、特には屈曲耐久性、耐
クリープ性及び表面平滑性に優れる導電性エンドレスベ
ルトを提供することができる。また、かかる本発明の導
電性エンドレスベルトを用いた本発明の画像形成装置に
よれば、長期間の使用においても不良がなく良好な画像
を得ることができ、ベルトが劣化しにくい。As described above, according to the present invention, it is possible to provide a conductive endless belt having high dimensional accuracy and being excellent in strength, particularly bending durability, creep resistance and surface smoothness. You can Further, according to the image forming apparatus of the present invention using the conductive endless belt of the present invention, it is possible to obtain a good image without defects even after long-term use, and the belt is less likely to deteriorate.

【図面の簡単な説明】[Brief description of drawings]

【図１】 本発明の一実施の形態に係る導電性エンドレ
スベルトの幅方向断面図である。FIG. 1 is a cross-sectional view in the width direction of a conductive endless belt according to an embodiment of the present invention.

【図２】 本発明の画像形成装置の一例としての転写搬
送ベルトを用いたタンデム方式の画像形成装置の一例を
示す概略図である。FIG. 2 is a schematic view showing an example of a tandem type image forming apparatus using a transfer / conveying belt as an example of the image forming apparatus of the present invention.

【図３】 本発明の画像形成装置の他の例としての中間
転写部材を用いた中間転写方式の画像形成装置の一例を
示す概略図である。FIG. 3 is a schematic view showing an example of an intermediate transfer type image forming apparatus using an intermediate transfer member as another example of the image forming apparatus of the present invention.

【符号の説明】 １ 感光体ドラム ２ 帯電ロール ３ 現像ロール ４ 現像ブレード ５ トナー供給ロール ６ クリーニングブレード ７ 帯電ロール ８ 除電ロール ９ 駆動ローラ（駆動部材） １０ 転写搬送ベルト １１ 感光体 １２ 一次帯電器 １３ 画像露光 １４，３５ クリーニング装置 １９ 給紙カセット ２０ 中間転写部材 ２５ 転写ローラ ２６ 記録媒体 ２９，６１ 電源 ３０ 駆動ローラ ４１，４２，４３，４４ 現像器[Explanation of symbols] 1 photoconductor drum 2 charging roll 3 developing roll 4 Development blade 5 Toner supply roll 6 cleaning blade 7 charging roll 8 Antistatic roll 9 Drive roller (drive member) 10 Transfer conveyor belt 11 photoconductor 12 Primary charger 13 Image exposure 14,35 Cleaning device 19 paper cassettes 20 Intermediate transfer member 25 Transfer roller 26 recording media 29,61 power supply 30 drive roller 41, 42, 43, 44 developing device

───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2H030 AA01 AB02 BB02 BB23 BB24 BB42 BB46 BB54 2H200 GA23 GA47 GA57 GB03 GB12 GB25 HA03 HB12 JB07 JB45 JC04 JC15 JC16 JC17 JC18 MA04 MA06 MA17 MA20 MB04 MC03 MC04 NA06    ─────────────────────────────────────────────────── ─── Continued front page    F term (reference) 2H030 AA01 AB02 BB02 BB23 BB24                       BB42 BB46 BB54                 2H200 GA23 GA47 GA57 GB03 GB12                       GB25 HA03 HB12 JB07 JB45                       JC04 JC15 JC16 JC17 JC18                       MA04 MA06 MA17 MA20 MB04                       MC03 MC04 NA06

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 静電吸着により保持した記録媒体を、駆
動部材により循環駆動されて、４種の画像形成体に運送
し、各トナー像を該記録媒体に順次転写するタンデム方
式の転写及び／又は搬送用導電性エンドレスベルトにお
いて、熱可塑性樹脂とウイスカ（アスペクト比１０以上
の繊維状無機化合物及び／又は金属粒子）との混合物を
基材とすることを特徴とする導電性エンドレスベルト。1. A tandem transfer and / or transfer method in which a recording medium held by electrostatic attraction is cyclically driven by a driving member to be transported to four types of image forming bodies and each toner image is sequentially transferred to the recording medium. Alternatively, a conductive endless belt for transportation, characterized in that a mixture of a thermoplastic resin and whiskers (fibrous inorganic compound and / or metal particles having an aspect ratio of 10 or more) is used as a base material. 【請求項２】 画像形成体と記録媒体との間に配設さ
れ、駆動部材により循環駆動されて、前記画像形成体表
面に形成されたトナー像を一旦自己の表面に転写保持
し、これを記録媒体へと転写する中間転写部材用導電性
エンドレスベルトにおいて、熱可塑性樹脂とウイスカ
（アスペクト比１０以上の繊維状無機化合物及び／又は
金属粒子）との混合物を基材とすることを特徴とする導
電性エンドレスベルト。2. A toner image formed on the surface of the image forming body is temporarily transferred and held on the surface of the image forming body, which is disposed between the image forming body and the recording medium and is circularly driven by a driving member. A conductive endless belt for an intermediate transfer member, which transfers to a recording medium, characterized by using a mixture of a thermoplastic resin and whiskers (fibrous inorganic compound and / or metal particles having an aspect ratio of 10 or more) as a base material. Conductive endless belt. 【請求項３】 前記混合物中のウイスカ成分の割合が、
５〜５０重量％であることを特徴とする請求項１又は請
求項２記載の導電性エンドレスベルト。3. The proportion of whisker component in the mixture is
The conductive endless belt according to claim 1 or 2, wherein the content is 5 to 50% by weight. 【請求項４】 前記ウイスカの平均長軸繊維長が０．２
〜４０μｍであることを特徴とする請求項１又は２記載
の導電性エンドレスベルト。4. The whisker has an average major axis fiber length of 0.2.
The conductive endless belt according to claim 1, wherein the conductive endless belt has a thickness of about 40 μm. 【請求項５】 前記ウイスカが、ケイ酸カルシウム水和
物（Ｃａ₆ （Ｓｉ₆０₁₇）（ＯＨ）₂ ）を主成分として
９０重量％以上含有することを特徴とする請求項１又は
２記載の導電性エンドレスベルト。5. The whisker contains 90% by weight or more of calcium silicate hydrate (Ca ₆ (Si _{60 17} ) (OH) ₂ ) as a main component. Conductive endless belt. 【請求項６】 前記熱可塑性樹脂が、ポリアミド１２を
含有することを特徴とする請求項１又は２記載の導電性
エンドレスベルト。6. The conductive endless belt according to claim 1, wherein the thermoplastic resin contains polyamide 12. 【請求項７】 請求項１〜６のいずれか１項に記載の導
電性エンドレスベルトを用いたことを特徴とする画像形
成装置。7. An image forming apparatus using the electroconductive endless belt according to claim 1. Description: