JP2003070358A - Planting block for three-dimensional flower bed - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain a lightweight planting block which has excellent water holding property, water permeability and durability, with which a plant can be raised without using soil and which is suitable for forming a three- dimensional flower bed on the rooftop of a building, a veranda, etc. SOLUTION: This planting block for three-dimensional flower bed is equipped with a plurality of planting boards 1 porous ceramic obtained by firing and forming expandable slag granule made by adding a blowing agent to slag, a supporting block 2 having supporting surfaces of the boards, made into curved surfaces or sloping surfaces fit for flower bed formation. The supporting surfaces are equipped with projecting stripes for preventing displacement of each board between the boards. The contact face of each board of the supporting block is provided with a channel 4 for watering piping and water from watering piping 5 is supplied through the planting board 1 to plants.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】この発明は、ビル屋上や家庭
のベランダで土壌等を使用せずに芝生等を植生するのに
用いられる立体花壇用植栽ブロックに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a three-dimensional flowerbed planting block used for planting a lawn or the like on a rooftop of a building or a porch of a household without using soil or the like.

【０００２】[0002]

【従来の技術】ビル屋上や家庭のベランダで植物を育生
し、環境の緑化への取組みが種々行われている。このよ
うな植物の育生には、自然土壌や人工土壌が従来から使
用されているが、これに代わるものとしてポーラスコン
クリートのブロックの空隙部に人工土壌を含む培養土を
充填し、これらブロックに植物を育生して床面、壁面、
あるいは法面などに設置し、緑化をする方法が多数提案
されている。その代表的なものとして特開平１１−３２
３８８２号公報（公報１）による「ポーラスコンクリー
ト部体」の発明がある。2. Description of the Related Art Various efforts have been made to green the environment by cultivating plants on the rooftops of buildings and balconies at home. Natural soil and artificial soil have been conventionally used for the growth of such plants, but as an alternative to this, the pores of porous concrete blocks are filled with culture soil containing artificial soil, and these blocks are planted. Grow up on the floor, walls,
Alternatively, many methods have been proposed for installing trees on slopes and for greening. As a typical example thereof, Japanese Patent Laid-Open No. 11-32
There is an invention of "porous concrete part" according to Japanese Patent No. 3882 (publication 1).

【０００３】上記公報１の「ポーラスコンクリート部
体」は、ポーラス孔とは別に口径が５〜８０ｍｍの独立
又は連続した空隙穴を形成し、これらをポーラス孔と連
通して形成したものである。このポーラスコンクリート
部体は、代表的な形態としてブロック形状に成形し、こ
れに客土、覆土などで土壌を空隙穴に充填し、植物を根
付かせるように使用される。The "porous concrete part" of the above publication 1 is formed by forming independent or continuous voids having a diameter of 5 to 80 mm separately from the porous holes and communicating these with the porous holes. This porous concrete part is formed into a block shape as a typical form, and the soil is filled with soil such as soil and cover soil, and the porous concrete part is used for rooting plants.

【０００４】土壌材を用いずに植物を植栽することがで
きる基盤材の一例として、特開２０００−９２９７８号
公報（公報２）の「無土壌植栽用セラミックブロック及
びその使用方法」の発明が知られている。このセラミッ
クブロックは、表面に植物を直接植栽することができる
軽量のブロックであり、土壌材を用いずに植栽ができる
とされている。As an example of a base material on which a plant can be planted without using a soil material, the invention of "ceramic block for soilless planting and a method of using the same" in Japanese Patent Laid-Open No. 2000-92978 (publication 2) It has been known. This ceramic block is a lightweight block that can be directly planted on the surface, and is said to be plantable without using soil material.

【０００５】[0005]

【発明が解決しようとする課題】しかし、上記公報１の
ポーラスコンクリート部体は、ポーラス孔と空隙穴が形
成されてはいるが、素材がコンクリート材であるため重
量がなお重く、土壌を充填して植栽するため土壌が流出
し、植物が枯れてしまう。又流出した土壌により排水口
が目詰まりするなどの問題がある。このような問題に対
処するため、公報２のセラミックブロックは、軽量であ
って土壌を使用せず植物を植栽できるとしているが、こ
のセラミックブロックでは次のような問題がある。However, the porous concrete part of the above publication 1 has porous holes and voids, but since the material is a concrete material, the weight is still heavy and soil is filled. The soil flows out to plant and die. There is also a problem that the drainage outlet is clogged with the soil that has run out. In order to deal with such a problem, the ceramic block of Publication 2 is light in weight and can be planted without using soil. However, this ceramic block has the following problems.

【０００６】上記セラミックブロックは、嵩比重が０．
８以下と明示され、軽量であるとされているが、０．８
のものでは必ずしも軽量とは言えず、かつ嵩比重が０．
３以下になると強度が低下するとされ、従って嵩比重の
小さいものは好ましくない。この多孔質セラミックブロ
ックに植物を植栽する際に植物の根が入り込む気孔を
０．２〜２０００μｍの大きさとしているが、この気孔
を発生させるために気孔付与材を添加しなければならな
いとされている。このため、材質が脆く、強度が低下す
る。又、保水性は８０リットル／ｍ³ 以上と規定されて
いるが、厚みが薄いと保水量が充分でなく、頻繁に散水
する必要があると記載されているように保水性が不十分
である。The ceramic block has a bulk specific gravity of 0.
It is clearly lighter than 8 and is lightweight, but 0.8
It cannot be said that it is lightweight, and the bulk specific gravity is 0.
When it is 3 or less, the strength is lowered, and therefore, a material having a low bulk specific gravity is not preferable. The pores into which plant roots enter when planting a plant in this porous ceramic block have a size of 0.2 to 2000 μm, but it is said that a pore-imparting material must be added to generate the pores. ing. Therefore, the material is brittle and the strength is reduced. Further, the water retention is regulated to be 80 liters / m ³ or more, but the water retention is insufficient when the thickness is thin, and the water retention is insufficient as described as requiring frequent water spraying. .

【０００７】この発明は、上記の問題に留意して、軽量
で、保水性、透水性、耐久性に優れ、気孔付与材を用い
ることなく形成でき、土壌を使用せずに植物を育生で
き、ビルの屋上やマンションのベランダ等での使用に適
する立体花壇用植栽ブロックを提供することを課題とす
る。In view of the above problems, the present invention is lightweight, has excellent water retention, water permeability and durability, can be formed without using a pore-imparting material, and can grow plants without using soil. An object of the present invention is to provide a planting block for a three-dimensional flower bed suitable for use on the rooftop of a building or the balcony of an apartment.

【０００８】又、上記の立体花壇用植栽ブロックを組み
合わせて立体花壇を得ることをもう１つの課題とする。Another object is to obtain a three-dimensional flower bed by combining the above-mentioned planting blocks for three-dimensional flower beds.

【０００９】[0009]

【課題を解決するための手段】この発明は、上記の課題
を解決する手段として、スラグに発泡剤を添加した発泡
性スラグの造粒物を焼成し成形した多孔質セラミックス
の植栽ボードの複数枚と、これらボードを載置する面が
花壇を形成するに適合する曲面又は斜面から成る支持面
を有する支持ブロックとを備え、上記支持面には各ボー
ドのずれを防止する突条が各ボード間に設けられ支持ブ
ロックの各ボードとの接合面に灌水配管用溝を設けて成
る立体花壇用植栽ブロックとしたのである。[Means for Solving the Problems] As a means for solving the above problems, the present invention provides a plurality of porous ceramics planting boards obtained by firing and molding granules of expandable slag obtained by adding a foaming agent to slag. And a supporting block having a supporting surface composed of a curved surface or a sloped surface adapted to form a flower bed, and a ridge for preventing displacement of each board is provided on the supporting surface. The planting block for a three-dimensional flower bed is provided with a groove for irrigation piping provided on the joint surface between the boards of the supporting block provided between them.

【００１０】上記もう１つの課題を解決する手段とし
て、上記植栽ブロックの複数組を組合せ、植栽ブロック
同士の溝に灌水配管を設け、灌水配管を多孔質材料から
成るパイプとし、この配管からしみ出る水を配管に接し
て置かれる植栽ボードの多孔質セラミックスの造粒物を
介して載置される植物に給水するようにして形成した立
体花壇としたのである。As a means for solving the above-mentioned another problem, a plurality of sets of the above-mentioned planting blocks are combined, irrigation pipes are provided in the grooves between the planting blocks, and the irrigation pipe is made of a porous material. The three-dimensional flower bed was formed by supplying the exuding water to the plant placed through the granules of the porous ceramics of the planting board placed in contact with the pipe.

【００１１】上記の構成としたこの発明の植栽ブロック
は、土壌を使用することなくビルの屋上やベランダで野
草等の植物を育生して立体花壇を形成することができ
る。野草を育生する場合は、予め外部で野草を植付けし
ておき、ある程度育生された状態で所定場所へ運んで植
栽ブロック上に載置するとよい。所定の植栽エリアに複
数個の植栽ブロックを設置し、支持ブロック上面の溝に
灌水用配管を設け、その上に植栽ボードを複数個載置す
ると組立てが完了する。給水管から水を送ると灌水用配
管から水がにじみ出て、その水は植栽ボードの造粒物と
造粒物を介して野草に給水される。The planting block of the present invention having the above-mentioned structure can form a three-dimensional flowerbed by growing plants such as wild grass on the roof of a building or on a veranda without using soil. When cultivating wild grass, it is advisable to plant the wild grass outside in advance, carry it to a predetermined place in a state where it has been bred to some extent, and place it on a planting block. When a plurality of planting blocks are installed in a predetermined planting area, a watering pipe is provided in a groove on the upper surface of the support block, and a plurality of planting boards are placed on the pipes, the assembly is completed. When water is sent from the water supply pipe, water oozes out from the irrigation pipe, and the water is supplied to the wild grass through the granules of the planting board and the granules.

【００１２】植栽部材の造粒物の内部には微細な連続気
孔が形成されているため、造粒物から造粒物へ連続する
気孔を通じて毛細管現象により水の重力に打ち勝って上
へと上昇し野草へと水は給水され、野草の全面に給水が
なされ、野草が育生される。なお、多孔質セラミックに
は気孔付与材などを含まないため、強度が確保される。Since fine continuous pores are formed inside the granulated material of the planting member, it rises upward by overcoming the gravity of water by the capillary phenomenon through the pores continuous from the granulated material to the granulated material. Water is supplied to the wild grass, and water is supplied to the entire surface of the wild grass to cultivate it. Since the porous ceramic does not contain a pore-forming material, the strength is ensured.

【００１３】[0013]

【発明の実施の形態】以下、この発明の実施の形態につ
いて図面を参照して説明する。図１は立体花壇形成用の
植栽ブロックＡの外観斜視図を示す。図示のように、実
施形態の植栽ブロックＡは、多孔質セラミックスの多数
の造粒物を成形した植栽ボード１の複数枚（図示の例で
は３×６＝１８枚）と、これらのボードを曲面上に載置
して立体花壇を形成するための支持ブロック２とから成
る。支持ブロック２は、これを複数個組み合わせて花壇
が形成される。BEST MODE FOR CARRYING OUT THE INVENTION Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 shows an external perspective view of a planting block A for forming a three-dimensional flower bed. As shown in the figure, the planting block A of the embodiment includes a plurality of planting boards 1 (3 × 6 = 18 in the illustrated example) formed by molding a large number of granulated substances of porous ceramics, and these boards. Is placed on a curved surface to form a three-dimensional flowerbed. A plurality of support blocks 2 are combined to form a flower bed.

【００１４】上記多孔質セラミックスの造粒物は、本出
願人他が先の特許出願である特願２０００−２７２７９
７号で提案した「多孔質セラミックスの製造方法」の発
明により製造された多孔質セラミックスが用いられる。
この多孔質セラミックスは、スラグに発泡剤を添加した
発泡性スラグを焼成して得られるものであるが、その詳
細については後で説明する。The granules of the above-mentioned porous ceramics are Japanese Patent Application No. 2000-27279 filed by the present applicant and others.
The porous ceramics manufactured by the invention of "Method for manufacturing porous ceramics" proposed in No. 7 is used.
This porous ceramic is obtained by firing a foamable slag obtained by adding a foaming agent to slag, the details of which will be described later.

【００１５】支持ブロック２は、軽量化するため発泡ス
チロールが用いられ、図２に示すように、平面視長方形
とされ（（ａ）図）、長手方向の断面で示すように、載
置される植栽ボード１との接合面２ａはゆるやかな曲面
の円弧面を成し、２つの支持ブロック２を隣接して置く
と花壇を形成するような大きな曲率半径の円弧面を２等
分した断面（（ｂ）図）を有する。この支持ブロック２
には、その円弧状の接合面２ａ上に載置される複数枚の
植栽ボード１がずれて落ちるのを防止するため、各ボー
ドとボードの間に沿ってブロックの幅方向に突条３が直
線状に設けられ、かつこの突条３の基部付近に灌水配管
５用の溝４がそれぞれ設けられている。Styrofoam is used for the support block 2 in order to reduce its weight, and as shown in FIG. 2, it is formed into a rectangular shape in plan view (FIG. 2 (a)). The joint surface 2a with the plant board 1 forms a gentle curved arc surface, and when two support blocks 2 are placed adjacent to each other, the arc surface having a large radius of curvature that forms a flower bed is divided into two sections (( b) FIG. This support block 2
In order to prevent the plurality of planting boards 1 placed on the arc-shaped joining surface 2a from slipping off, the ridges 3 are provided between the boards in the width direction of the block. Are linearly provided, and grooves 4 for irrigation pipes 5 are provided near the base of the ridge 3.

【００１６】上記溝４は、これに埋設される灌水用配管
５が載置される植栽ボード１に直接接触して給水ができ
るように各植栽ボード１毎に少なくとも１箇所（断面
で）ずつ設けられている。但し、両端の突条３の基部に
は溝４は設けられていない。なお、（ｂ）図の断面と直
角方向の断面では支持ブロック２はコ字状断面とされ、
点線で示す中央部分は中空断面であり、これにより軽量
化している。溝４に埋設される灌水用配管５は、植栽ボ
ード１を載置する前に埋設されるが、この配管５には図
示の例では一般にポーラスパイプと呼ばれる多孔質材料
で形成されたものが使用され、配管５からにじみ出る水
を植栽ボード１に給水する。The groove 4 has at least one location (in cross section) for each planting board 1 so that water can be supplied by directly contacting the planting board 1 on which the irrigation pipe 5 buried therein is placed. Are provided one by one. However, the groove 4 is not provided at the base of the protrusion 3 at both ends. In addition, the support block 2 has a U-shaped cross section in a cross section perpendicular to the cross section of FIG.
The central portion shown by the dotted line has a hollow cross section, which reduces the weight. The irrigation pipe 5 embedded in the groove 4 is embedded before the planting board 1 is placed, but the pipe 5 is made of a porous material generally called a porous pipe in the illustrated example. The planting board 1 is supplied with water that is used and oozes out from the pipe 5.

【００１７】上述した造粒物の多孔質セラミックスは、
スラグに発泡剤を添加して形成した発泡性スラグを焼成
し成形して図１〜図３に示すように薄い瓦状に作られる
が、その概略は次の通りである。スラグは鋳物用キュー
ポラで発生するキューポラスラグ、高炉で発生する高炉
スラグ、転炉、電気炉などで発生する製鋼スラグなどで
ある。このようなスラグに発泡剤を添加して発泡性スラ
グを形成する場合、発泡剤は０．２〜１．０重量％の範
囲の炭化珪素とし、発泡性スラグは平均粒子径が４〜４
０μｍの範囲とされ、この発泡性スラグを０．２ｍｍ〜
１０ｍｍ範囲内の造粒物として形成した後、その造粒物
を焼成するとよい。The porous ceramics of the above-mentioned granulated product are
A foaming slag formed by adding a foaming agent to slag is fired and molded into a thin roof tile shape as shown in FIGS. 1 to 3. The outline thereof is as follows. The slag is, for example, a cupola slag generated in a casting cupola, a blast furnace slag generated in a blast furnace, a steelmaking slag generated in a converter or an electric furnace. When a foaming agent is added to such a slag to form a foaming slag, the foaming agent is silicon carbide in the range of 0.2 to 1.0% by weight, and the foaming slag has an average particle size of 4 to 4%.
The range is 0 μm, and the foamable slag is
After forming the granulated product within a range of 10 mm, the granulated product may be fired.

【００１８】造粒物の形成方法としては、発泡性スラグ
粉末をパン型、インテンシブミキサ（アイリッヒミキ
サ）などの造粒機により形成してもよく、又はスラグ粉
末と発泡材（Ｓ：Ｃ）とを水と共にボールミル等湿式粉
砕し、平均粒子径７〜８μｍのスラリーを作製した後、
スプレードライヤで乾燥して形成してもよい。なお、造
粒物の粒子径を１ｍｍ以下とする場合は、発泡剤と顆粒
の強度保持のため、無機バインダ（水ガラス）０．５％
などや、有機バインダ（ポリビニールアルコール）０．
３％などを添加するのが好ましい。As a method for forming the granulated product, the expandable slag powder may be formed by a granulating machine such as a pan type or an intensive mixer (Eirich mixer), or the slag powder and the foam material (S: C). And wet-milled with water using a ball mill to prepare a slurry having an average particle size of 7 to 8 μm,
It may be formed by drying with a spray dryer. When the particle size of the granulated product is 1 mm or less, 0.5% of an inorganic binder (water glass) is used to maintain the strength of the foaming agent and the granules.
Etc. Organic binder (polyvinyl alcohol) 0.
It is preferable to add 3% or the like.

【００１９】この造粒物は、発泡性スラグを無機質粒子
（粒子径０．５〜１０ｍｍ）の表面にコーティングして
形成してもよく、これにより発泡量が制限され粒子間隙
間（アグリゲート）が確保されるため、無機質粒子の種
類に応じて保水性、吸水性、通気性、吸音性、吸放湿性
などに優れた多孔質セラミックスを作製できる。無機質
粒子は砕石、ガラス粒、スラグ粒子、砂、黒曜石発泡粒
子、真珠岩発泡粒子、又は調質機能を有する材料で形成
した粒子のいずれかとするのがよい。スラグに発泡剤を
添加して形成した発泡性スラグは、ボールミル等の粉砕
機を用いてスラグを微粉化する際に、発泡剤を添加して
乾式粉砕して形成するか、又はボールミル等粉砕機内に
スラグ及び発泡剤を水と共に混入させ湿式粉砕した後ス
プレードライヤなどで乾燥粉末化して形成する。The granulated product may be formed by coating the surface of the inorganic particles (particle diameter: 0.5 to 10 mm) with expandable slag, whereby the amount of foaming is limited and the interparticle gap (aggregate) is formed. Therefore, it is possible to produce porous ceramics excellent in water retention, water absorption, air permeability, sound absorption, moisture absorption and desorption, etc., depending on the type of inorganic particles. The inorganic particles are preferably crushed stones, glass particles, slag particles, sand, obsidian expanded particles, pearlite expanded particles, or particles formed of a material having a tempering function. The foamable slag formed by adding a foaming agent to the slag is formed by dry-grinding with a foaming agent when the slag is pulverized using a crusher such as a ball mill, or in a crusher such as a ball mill. The slag and the foaming agent are mixed with water, wet-pulverized, and then dried and powdered by a spray dryer or the like.

【００２０】コーティングに際しては、無機質粒子の径
によって表面積が異なり、発泡性スラグのコーティング
量が、粒子間隙間（通気性や吸音性と関係する）や製品
強度に影響を与えるため、発泡性スラグの添加量を調整
する必要がある。又、無機質粒子の径も粒子間隙間に係
わり、通気性、透水性又は吸音性に影響するため調整が
必要である。During coating, the surface area differs depending on the diameter of the inorganic particles, and the coating amount of the expandable slag affects the interparticle clearance (related to air permeability and sound absorption) and product strength. It is necessary to adjust the addition amount. In addition, the diameter of the inorganic particles also affects the air gap, the water permeability, or the sound absorbing property because it is related to the gaps between the particles, and thus needs to be adjusted.

【００２１】個々に独立した多孔質セラミックスを得る
場合は、発泡性スラグにて形成した造粒物、又は無機質
粒子に発泡性スラグをコーティングして形成した造粒物
を乾燥した後、ロータリキルンなどで融着防止剤（例え
ば水酸化アルミニウム水簸カオリン粘土類）と共に温度
１０００〜１１００℃で焼成する。所要形態に形成した
一体成形物の多孔質セラミックスを得る場合は、発泡性
スラグ、発泡性スラグにて形成した造粒物、又は無機質
粒子に発泡性スラグをコーティングして形成した造粒物
を耐熱容器内に充填して、トンネルキルンなどを用いて
温度１０００〜１１００℃で焼成する。In the case of obtaining individual independent porous ceramics, a granulated product formed of expandable slag or a granulated product formed by coating inorganic particles with expandable slag is dried and then rotary kiln or the like. Then, it is fired at a temperature of 1000 to 1100 ° C. together with a fusion preventing agent (for example, aluminum hydroxide elutriation kaolin clays). When obtaining the porous ceramics of an integrally molded product formed in the required form, heat-treat the expandable slag, the granulated product formed by the expandable slag, or the granulated product formed by coating the expandable slag on the inorganic particles. It is filled in a container and fired at a temperature of 1000 to 1100 ° C. using a tunnel kiln or the like.

【００２２】具体的に１例として挙げれば次のようなも
のである。無機質粒子として、スラグ粒（粒径１〜２ｍ
ｍ、粒径２〜３ｍｍ）、黒曜石発泡粒（パーライト；粒
径０．７〜１．２ｍｍ、粒径１．７〜２．４ｍｍ、粒径
４．０〜４．８ｍｍ）をそれぞれ準備し、コンクリート
ミキサー（３０１容量）内において、スラグ粒２ｋｇ
（１８００〜１９００ｍｌ）に対して発泡性スラグ１ｋ
ｇの割合でコーティングする。The following is a specific example. As inorganic particles, slag particles (particle size 1-2 m
m, particle size 2-3 mm), obsidian foamed particles (perlite; particle size 0.7-1.2 mm, particle size 1.7-2.4 mm, particle size 4.0-4.8 mm), respectively, 2 kg of slag particles in a concrete mixer (301 volume)
Foaming slag 1k against (1800-1900ml)
Coating at a rate of g.

【００２３】より具体的には、メチルセルロース１重量
％水溶液（有機質バインダー）をスプレーガンで噴霧し
て無機質粒子の表面を濡らしながら転動させて、造粒物
をその表面にコーティングする。その後、耐熱容器中に
充填し、温度１０００〜１０２０℃で３０分、昇温時間
３．５時間の条件下焼成発泡させ、板状の多孔質セラミ
ックスを作製する。More specifically, a 1% by weight aqueous solution of methyl cellulose (organic binder) is sprayed with a spray gun to roll while wetting the surfaces of the inorganic particles to coat the granules on the surfaces. Then, it is filled in a heat-resistant container and fired and foamed under the conditions of a temperature of 1000 to 1020 ° C. for 30 minutes and a temperature rising time of 3.5 hours to produce a plate-shaped porous ceramic.

【００２４】得られた多孔質セラミックスは、１つ１つ
の粒子の表面層に数ミクロンから１００ミクロン程度の
大きさを持つ無数の連続気孔を有し、無機質粒子の表面
に造粒物をコーティングしているため、発泡量が制限さ
れ平均５００〜６００ミクロン程度の粒子間隙間（アグ
リゲート）が確保され、吸水性および保水性の他、通気
性、透水性に富むものとなった。以下表１に各物性値を
示す。また、黒曜石発泡粒にコーティングしたものは、
優れた吸音特性を有する。The obtained porous ceramics have innumerable continuous pores having a size of several microns to 100 microns in the surface layer of each particle, and the surface of the inorganic particle is coated with the granulated material. As a result, the amount of foaming is limited, and interparticle gaps (aggregates) with an average of about 500 to 600 microns are secured, and in addition to water absorption and water retention, air permeability and water permeability are abundant. The physical property values are shown in Table 1 below. Also, the ones coated with obsidian foam particles are
It has excellent sound absorption characteristics.

【００２５】[0025]

【表１】 [Table 1]

【００２６】なお、上記多孔質セラミックスの造粒物
は、各粒子をそれぞればらばらの状態で作製するとした
が、この実施形態で使用される植栽ボードを形成する場
合は、各粒子を一体成形して作製される。この場合、前
述した製造過程において造粒物を耐熱容器内に充填する
代わりに押出成形機やプレス成形機にて所要形態に成形
する。The granules of the above-mentioned porous ceramics are said to be produced in a state in which the particles are separated. However, when forming the planting board used in this embodiment, the particles are integrally molded. It is made by. In this case, instead of filling the granulated product in the heat-resistant container in the above-described manufacturing process, the granulated product is molded into a desired shape by an extrusion molding machine or a press molding machine.

【００２７】上記の構成とした植栽ブロックＡを複数個
用いて組み合わせて花壇を形成する。これにより形成さ
れた花壇の一例を図４に示す。図示の花壇は、Ａ₁ 〜Ａ
₅ の５つの植栽ブロックをＡ₆ 〜Ａ₁₀の５つの植栽ブロ
ックと互いに背中合わせに組み合わせて山形の花壇を形
成している。花壇の長手方向の両端の平面視半円形部は
花壇の外延部であり、これは装飾用に設けられている。
これについては後で説明する。A plurality of planting blocks A having the above structure are used in combination to form a flower bed. An example of the flower bed formed by this is shown in FIG. The flowerbed shown is A ₁ -A
_{The five} planting blocks 5 are combined back to back with the five planting blocks A _{6 to} A ₁₀ to form a mountain-shaped flower bed. The semicircular portions in plan view at both ends in the longitudinal direction of the flower bed are outer extending portions of the flower bed, which are provided for decoration.
This will be described later.

【００２８】図示の花壇を形成する場合、ビルの屋上等
の床面にベース板１０を設置し、その上に植栽ブロック
Ａを複数個（図示の例では１０個）置いて花壇を形成す
る。各植栽ブロックの支持ブロック２を図示のように設
置エリアに設置した後、予め床面上又は下を通って給水
管１１を布設しておき、これに灌水用配管５を接続して
それぞれの支持ブロック２の溝４内に設置する。この状
態で支持ブロック２上に複数の植栽ボード２を置く。In the case of forming the flower bed shown in the figure, the base plate 10 is installed on the floor surface such as the roof of a building, and a plurality of planting blocks A (10 in the illustrated example) are placed thereon to form the flower bed. . After installing the support block 2 of each planting block in the installation area as shown in the figure, a water supply pipe 11 is laid in advance on or under the floor surface, and the irrigation pipes 5 are connected to the water supply pipe 11. It is installed in the groove 4 of the support block 2. In this state, a plurality of planting boards 2 are placed on the support block 2.

【００２９】以上で花壇の本体は形成されるが、花壇の
外延部には装飾用のブロックＢを接続する。図示の例で
は装飾用ブロックＢは放射角度６０°のものを３つ（Ｂ
₁ 〜Ｂ₃ 、Ｂ₄ 〜Ｂ₆ ）ずつ片端に設置して半円形の外
延部を形成する。この装飾用ブロックＢ₁ 〜Ｂ₆ の断面
は、植栽ブロックの断面と同じで、曲面状の接合面が形
成され、かつ突条３は円形状に設けられている。３つの
ブロックを組み合わせると平面視が半円形状となる。但
し、このブロックには溝４は設けられていない。装飾用
ブロックＢ上には植物を植栽しないからである。上記接
合面には突条３の高さまでばらばらの上記造粒物が成形
しないまま置かれ、花壇両端の美観を整える。Although the main body of the flower bed is formed as described above, the decorative block B is connected to the outer extending portion of the flower bed. In the illustrated example, three decorative blocks B having a radiation angle of 60 ° (B
_{1 to} B ₃ and B _{4 to} B ₆ ) are installed at one end to form a semicircular extension. The cross-sections of the decorative blocks B _{1 to} B ₆ are the same as the cross-section of the planting block, a curved joint surface is formed, and the ridges 3 are provided in a circular shape. When the three blocks are combined, the plan view has a semicircular shape. However, the groove 4 is not provided in this block. This is because no plant is planted on the decorative block B. On the joint surface, the granules, which are separated up to the height of the protrusions 3, are placed without being molded, and the appearance of both ends of the flowerbed is adjusted.

【００３０】以上のようにして形成された花壇の植栽ブ
ロック上には芝生やこれに混合して、あるいは芝生とは
別に１年草や多年草を植栽すれば、植栽ボード上に根を
張った野草が美しい花壇を形成することとなる。この場
合、給水は給水管１１から灌水用配管５により行われ、
常に少しずつ配管５からにじみ出て給水される水が植栽
ボード１に与えられ、植栽ボード１では粒状物の微細組
織内に微細な連続気孔が含まれているため、その連続気
孔内に水が毛細管現象で伝達され、下部から上部へと重
力に逆らって上昇し、植栽ボード１上の植物に給水され
る。On the planting block of the flower bed formed as described above, if a lawn or a mixture with this is planted, or if an annual plant or a perennial plant is planted separately from the lawn, the roots are planted on the planting board. The stretched wild grass forms a beautiful flower bed. In this case, water is supplied from the water supply pipe 11 through the irrigation pipe 5,
The water that constantly oozes out from the pipe 5 is supplied to the planting board 1, and since the planting board 1 contains fine continuous pores in the microstructure of the granular material, the water inside the continuous pores is water. Is transmitted by a capillary phenomenon, rises from the bottom to the top against gravity, and is supplied to the plants on the planting board 1.

【００３１】このため、必要以上の水を与えた場合に発
生し易い各種の病気や根腐れの防止にも役立つ。上記花
壇で植栽される植物の対象は、芝生、苔、一部シダ類、
１年草や多年草のような野草である。Therefore, it is also useful for preventing various diseases and root rot which are likely to occur when more water than necessary is given. The plants to be planted in the above flower beds are lawns, moss, some ferns,
It is a wildflower like annual and perennial plants.

【００３２】なお、上記実施形態の植栽ブロックは、支
持ブロック２、植栽ボード１の上面がゆるやかな上に凸
の曲面をなすとしたが、この曲面は下に凹の曲面として
もよいし、あるいは斜面として形成してもよい。又、図
４の例では花壇の幅方向中央が最も高くなる曲面として
いるが、対向する２列の植栽ブロックとブロックの間に
上記中央高さに一致する平面状の植栽ブロックを置くよ
うにしてもよいし、その他種々の形状のものを採用する
ことができる。In the planting block of the above embodiment, the upper surfaces of the support block 2 and the planting board 1 have a gentle upward convex curved surface, but this curved surface may be a concave curved surface below. Alternatively, it may be formed as a slope. In addition, in the example of FIG. 4, the center of the flower bed in the widthwise direction is the highest curved surface. However, a flat planting block that matches the above center height should be placed between two opposite rows of planting blocks. However, various other shapes can be adopted.

【００３３】[0033]

【発明の効果】以上、詳細に説明したように、この発明
の立体花壇用植栽ブロックは、発泡性スラグを利用した
多孔質セラミックスの造粒物で形成される植栽ボードの
複数枚を曲面又は斜面状の支持面を有する支持ブロック
で支持し、支持面に突条を設けて各ボードのずれを防止
し、各ボードとの接合面に灌水配管用溝を設けたから、
溝内に配設される灌水配管から滲み出る水が植栽ボード
で上昇して載置され植栽された植物に水が供給され、土
壌を使用することなく植物を植栽でき、ビル屋上、ベラ
ンダ等で複数個のこのような植栽ブロックを組合わせれ
ば美しく軽量な花壇を形成できるという利点が得られ
る。As described above in detail, the planting block for a three-dimensional flower bed of the present invention has a plurality of planting boards formed by the granulation of the porous ceramics using the foamable slag. Or, because it is supported by a support block having a sloped support surface, a ridge is provided on the support surface to prevent displacement of each board, and a groove for irrigation piping is provided on the joint surface with each board,
Water exuding from the irrigation pipes arranged in the ditch rises on the planting board and is supplied to the planted plant, which allows planting without using soil. Combining multiple such planting blocks on a veranda etc. has the advantage of forming a beautiful and lightweight flowerbed.

【図面の簡単な説明】[Brief description of drawings]

【図１】実施形態の立体花壇用植栽ブロックの外観斜視
図FIG. 1 is an external perspective view of a three-dimensional flowerbed planting block according to an embodiment.

【図２】同上の支持ブロックの（ａ）平面図、（ｂ）側
面図2 (a) is a plan view and FIG. 2 (b) is a side view of the same supporting block.

【図３】植栽ブロックの部分断面図[Fig. 3] Partial sectional view of planting block

【図４】立体花壇の一例の（ａ）平面図、（ｂ）（ａ）
図の矢視Ｂ−Ｂからの断面図FIG. 4A is a plan view of an example of a three-dimensional flowerbed, and FIGS.
Sectional view from the arrow BB of the figure

【符号の説明】[Explanation of symbols]

１ 植栽ボード ２ 支持ブロック ３ 突条 ４ 溝 ５ 灌水用配管 1 planting board 2 support blocks 3 ridges 4 grooves 5 Piping for irrigation

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 スラグに発泡剤を添加した発泡性スラグ
の造粒物を焼成し成形した多孔質セラミックスの植栽ボ
ードの複数枚と、これらボードを載置する面が花壇を形
成するに適合する曲面又は斜面から成る支持面を有する
支持ブロックとを備え、上記支持面には各ボードのずれ
を防止する突条が各ボード間に設けられ、支持ブロック
の各ボードとの接合面に灌水配管用溝を設けて成る立体
花壇用植栽ブロック。1. A plurality of planting boards of porous ceramics obtained by firing and molding granules of expandable slag obtained by adding a foaming agent to slag, and the surface on which these boards are placed is suitable for forming a flower bed. A supporting block having a supporting surface composed of a curved surface or an inclined surface, and the supporting surface is provided with ridges for preventing displacement of the boards between the boards, and the joint surface of the supporting block with the boards is provided with an irrigation pipe. A planting block for a three-dimensional flowerbed that has a groove for use. 【請求項２】 前記突条を直線状に形成し、各突条の基
部に沿って溝を設けたことを特徴とする請求項１に記載
の立体花壇用植栽ブロック。2. The three-dimensional flowerbed planting block according to claim 1, wherein the ridges are formed in a straight line, and grooves are provided along the bases of the ridges. 【請求項３】 前記請求項１又は２に記載の植栽ブロッ
クの複数組を組合せ、植栽ブロック同士の溝に灌水配管
を設け、灌水配管を多孔質材料から成るパイプとし、こ
の配管からしみ出る水を配管に接して置かれる植栽ボー
ドの多孔質セラミックスの造粒物を介して載置される植
物に給水するようにして形成した立体花壇。3. A plurality of sets of the planting blocks according to claim 1 or 2 are combined, irrigation pipes are provided in the grooves between the planting blocks, and the irrigation pipes are pipes made of a porous material. A three-dimensional flower bed formed by supplying the water that comes out to the plant that is placed through the granules of porous ceramics on the planting board that is placed in contact with the piping. 【請求項４】 前記立体花壇に装飾用ブロックを付設し
たことを特徴とする請求項３に記載の立体花壇。4. The three-dimensional flower bed according to claim 3, wherein a decorative block is attached to the three-dimensional flower bed.