JP2003027097A - Cleaning liquid composition - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain a cleaning liquid composition which is a cleaning liquid for cleaning industrial parts with an adhesive, wax or pitch adhering thereto, the above cleaning liquid having a reduced environmental influence and reduced controls from a handling standpoint, simultaneously, sufficient detergency and no properties of attacking on the materials as such constituting the industrial parts. SOLUTION: This cleaning liquid composition is to clean the adhesive, the pitch or the wax attached to the parts and comprises 40-90 wt.% 9-18C aromatic hydrocarbon and 10-60 wt.% 5-11C dicarboxylic acid ester.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、工業部品に付着し
た接着剤、ピッチ、ワックスなどを洗浄除去する洗浄液
組成物に関し、特には、レンズ、プリズムなどの光学部
品に付着している張り合わせ剤などのＵＶ硬化性接着剤
やシアノ系瞬間接着剤、ピッチ、ワックスによる汚損な
どを除去する洗浄液組成物に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cleaning liquid composition for cleaning and removing adhesives, pitches, waxes and the like adhered to industrial parts, and more particularly to a laminating agent adhered to optical parts such as lenses and prisms. Of the present invention relates to a cleaning liquid composition for removing stains due to UV curable adhesives, cyano instant adhesives, pitches, waxes and the like.

【０００２】[0002]

【従来の技術】工業製品は、それを構成する部品を様々
な方法、手段を用いて接合し、組み立てられているが、
その製造においては、加工途中の部品の保護や固定など
のためにワックス・ピッチが用いられている。また、そ
の加工の際に、接着剤を用いて接合される場合がある。
そのため、製造工程においては、工業部品を張り合わせ
て接着剤を用いて接合したとき、接着剤がはみ出した
り、必要のない場所に付着して汚損することが避けられ
ない。このような場合、次工程の邪魔にならないよう
に、または付着物などによって製品性能や商品価値を損
ねないために、はみ出た接着剤あるいは目的外の部分に
付着した接着剤を除去する必要がある。また、部品の保
護や固定のために使用したワックス・ピッチを部品表面
から除去するために、その洗浄工程が必要となる。2. Description of the Related Art Industrial products are assembled by joining the constituent parts thereof by various methods and means.
In its manufacture, wax pitch is used to protect and fix parts during processing. Moreover, in the case of the process, it may be joined using an adhesive agent.
Therefore, in the manufacturing process, when the industrial parts are stuck together and joined using an adhesive, it is unavoidable that the adhesive sticks out or adheres to an unnecessary place to be soiled. In such a case, it is necessary to remove the adhesive that sticks out or the adhesive that has adhered to an unintended portion so as not to interfere with the next process or to impair product performance and commercial value due to adhered substances. . Also, a cleaning step is required to remove the wax pitch used for protection and fixing of the parts from the surface of the parts.

【０００３】従来、このような洗浄には、フロン系溶
剤、あるいはトリクロロエタンなどの塩素系溶剤が洗浄
剤として使用されている。しかし、これらの洗浄液は、
オゾン層の破壊、大気温の上昇や地下水などの水質汚染
などの環境問題を有しており、使用が厳しく制限されて
きている。このような背景から、洗浄液の選択に際して
は、汚れを確実に溶解除去できること、環境上の問題が
なく、臭気や毒性がなく取り扱いが安全で容易であるこ
と、洗浄対象物自体に悪影響を与えないこと、更には入
手しやすいなどの条件を満たすものが求められている。
特に、レンズ、プリズム、ミラーなどの光学部品のよう
に、それ自体が化学物質の影響を受けやすい被洗浄物の
場合、更にそれに付着した汚染が接着剤のような極めて
洗浄、除去しにくい場合、これら全ての条件を満たす洗
浄液は提案されていない。Conventionally, for such cleaning, a fluorocarbon solvent or a chlorine solvent such as trichloroethane has been used as a cleaning agent. However, these cleaning solutions
Due to environmental problems such as destruction of the ozone layer, rise in atmospheric temperature, and water pollution such as groundwater, its use has been severely restricted. Against this background, when selecting a cleaning solution, dirt can be reliably dissolved and removed, there is no environmental problem, there is no odor or toxicity, and handling is safe and easy, and it does not adversely affect the object to be cleaned itself. In addition, there is a demand for products that satisfy the conditions such as easy availability.
In particular, if the object to be cleaned is itself susceptible to chemical substances, such as optical parts such as lenses, prisms, mirrors, etc., and if the contamination attached to it is extremely difficult to clean or remove, such as an adhesive, No cleaning solution that meets all of these requirements has been proposed.

【０００４】[0004]

【発明が解決しようとする課題】本発明は、このような
課題を解決するもので、接着剤、ワックス・ピッチが付
着した工業部品を洗浄する洗浄液であって、環境に与え
る影響が少なく、取り扱い上の規制も少なく、かつ、十
分な洗浄性を有し、加えて、工業部品を構成する材料自
体に対する攻撃性のない洗浄液組成物を提供するもので
ある。SUMMARY OF THE INVENTION The present invention has been made to solve the above problems and is a cleaning liquid for cleaning industrial parts to which adhesives, waxes and pitches are adhered. It is intended to provide a cleaning liquid composition which has few restrictions as described above, has sufficient detergency, and, in addition, has no aggression to the material itself constituting an industrial part.

【０００５】[0005]

【課題を解決するための手段】本発明の洗浄液組成物
は、工業部品に付着した接着剤、ピッチまたはワックス
を洗浄するための洗浄液組成物であり、炭素数９〜１８
の芳香族炭化水素を４０〜９０重量％、炭素数５〜１１
のジカルボン酸エステルを１０〜６０重量％含有する。The cleaning liquid composition of the present invention is a cleaning liquid composition for cleaning an adhesive, pitch or wax adhering to an industrial part and has 9 to 18 carbon atoms.
Aromatic hydrocarbon of 40 to 90% by weight, carbon number of 5 to 11
10 to 60% by weight of the dicarboxylic acid ester of.

【０００６】本発明の洗浄液組成物は、上記のように、
環境保全性、安全性を有し、かつ毒性が少ない化合物を
主成分として用いながら、工業部品に付着した接着剤な
どの溶解除去しにくい物質で汚染された被洗浄物に対し
て良好な洗浄効果を有するものであり、特には化学的に
悪影響を受けやすい光学部品の洗浄に好適に使用するこ
とができる。The cleaning liquid composition of the present invention, as described above,
Good cleaning effect for the objects to be cleaned that are contaminated with substances that are difficult to dissolve and remove, such as adhesives adhering to industrial parts, while using as the main components compounds that have environmental protection and safety and low toxicity In particular, it can be suitably used for cleaning an optical component which is easily chemically adversely affected.

【０００７】本発明の洗浄液組成物は、炭素数９〜１８
の、特には９〜１６の芳香族炭化水素を４０重量％以上
含有する。この芳香族炭化水素は、単環または２環芳香
族炭化水素、及びこれらのアルキル置換体を含む化合物
であり、アルキルベンゼン、インダン、アルキルインダ
ン、テトラリン、ナフタレン、アルキルナフタレンが挙
げられる。なかでも、アルキルベンゼン、ナフタレン及
び／又はアルキルナフタレンが好ましい。The cleaning liquid composition of the present invention has 9 to 18 carbon atoms.
, Particularly 9 to 16 aromatic hydrocarbons in an amount of 40% by weight or more. The aromatic hydrocarbon is a compound containing a monocyclic or bicyclic aromatic hydrocarbon and an alkyl-substituted product thereof, and examples thereof include alkylbenzene, indane, alkylindane, tetralin, naphthalene, and alkylnaphthalene. Of these, alkylbenzene, naphthalene and / or alkylnaphthalene are preferable.

【０００８】具体的には、炭素数９のアルキルベンゼン
として、i−プロピルベンゼン、n−プロピルベンゼン、
１−エチル−２−メチルベンゼン、１−エチル−３−メ
チルベンゼン、１−エチル−４−メチルベンゼン、１，
２，３−トリメチルベンゼン、１，２，４−トリメチル
ベンゼン、インダンなどが、炭素数１０のアルキルベン
ゼンとして、i−ブチルベンゼン、ｓｅｃ−ブチルベン
ゼン、１，３−ジエチルベンゼン、１−メチル−３−n
−プロピルベンゼン、１，４−ジエチルベンゼン、１，
３−ジメチル−５−エチルベンゼン、１，２−ジエチル
ベンゼン、１−メチル−２−n−プロピルベンゼン、
１，４−ジメチル−２−エチルベンゼン、１，３−ジメ
チル−２−エチルベンゼン、１，２−ジメチル−４−エ
チルベンゼン、１，２−ジメチル−３−エチルベンゼ
ン、１，２，４，５−テトラメチルベンゼン、１，２，
３，５−テトラメチルベンゼン、メチルインダン、テト
ラリンなどが、炭素数１１のアルキルベンゼンとして、
ペンチルベンゼン、トリメチルエチルベンゼン、ジエチ
ルメチルベンゼン、ジメチルインダン、エチルインダン
などが、炭素数１２のアルキルベンゼンとして、ヘキシ
ルベンゼン、トリエチルベンゼンなどが、そして、炭素
数１１〜１６のアルキルナフタレンとして、メチルナフ
タレン、ジメチルナフタレン、ジメチル−i−プロピル
ナフタレン、メチル−ｎ−プロピルナフタレン、ジメチ
ルプロピルナフタレン、ジ−i−プロピルナフタレンな
どが挙げられる。これらを単独で用いても、必要に応じ
て２種以上を混合して用いても差し支えない。また、こ
れら芳香族炭化水素を含有する石油留分などを用いるこ
ともできる。Specifically, as alkylbenzene having 9 carbon atoms, i-propylbenzene, n-propylbenzene,
1-ethyl-2-methylbenzene, 1-ethyl-3-methylbenzene, 1-ethyl-4-methylbenzene, 1,
2,3-trimethylbenzene, 1,2,4-trimethylbenzene, indane and the like are alkylbenzenes having 10 carbon atoms, i-butylbenzene, sec-butylbenzene, 1,3-diethylbenzene, 1-methyl-3-n.
-Propylbenzene, 1,4-diethylbenzene, 1,
3-dimethyl-5-ethylbenzene, 1,2-diethylbenzene, 1-methyl-2-n-propylbenzene,
1,4-dimethyl-2-ethylbenzene, 1,3-dimethyl-2-ethylbenzene, 1,2-dimethyl-4-ethylbenzene, 1,2-dimethyl-3-ethylbenzene, 1,2,4,5-tetramethyl Benzene, 1, 2,
3,5-tetramethylbenzene, methylindane, tetralin, etc., are alkylbenzenes having 11 carbon atoms,
Pentylbenzene, trimethylethylbenzene, diethylmethylbenzene, dimethylindane, ethylindane and the like are alkylbenzenes having 12 carbon atoms, such as hexylbenzene and triethylbenzene, and alkylnaphthalene having 11 to 16 carbon atoms, such as methylnaphthalene and dimethylnaphthalene. , Dimethyl-i-propylnaphthalene, methyl-n-propylnaphthalene, dimethylpropylnaphthalene, di-i-propylnaphthalene and the like. These may be used alone or as a mixture of two or more, if necessary. Further, a petroleum fraction containing these aromatic hydrocarbons can also be used.

【０００９】本発明の洗浄液組成物に用いる炭素数５〜
１１のジカルボン酸エステルとしては、マロン酸ジメチ
ル、マロン酸ジエチル、コハク酸ジメチル、コハク酸ジ
エチル、グルタル酸ジメチル、グルタル酸ジエチル、ア
ジピン酸ジメチル、アジピン酸ジエチル、ピメリン酸ジ
メチル、ピメリン酸ジエチルなどの炭素数３〜７のジカ
ルボン酸と炭素数１〜２のアルコールのジエステルが挙
げられる。特に、炭素数３〜７のジカルボン酸とメタノ
ールとのジエステルが好ましい。これらを単独で用いて
も、必要に応じて２種以上を混合して用いても差し支え
ない。The cleaning liquid composition of the present invention has 5 to 5 carbon atoms.
Examples of the dicarboxylic acid ester of 11 include carbon such as dimethyl malonate, diethyl malonate, dimethyl succinate, diethyl succinate, dimethyl glutarate, diethyl glutarate, dimethyl adipate, diethyl adipate, dimethyl pimelate, diethyl pimelate. Examples thereof include diesters of dicarboxylic acids having 3 to 7 and alcohols having 1 to 2 carbon atoms. Particularly, a diester of a dicarboxylic acid having 3 to 7 carbon atoms and methanol is preferable. These may be used alone or as a mixture of two or more, if necessary.

【００１０】本発明による洗浄液組成物は、炭素数９〜
１８の芳香族炭化水素を主成分とする芳香族成分を４０
〜９０重量％、好ましくは４５〜８０重量％と炭素数５
〜１１のジカルボン酸エステル成分を１０〜６０重量
％、好ましくは２０〜５５重量％含有する。炭素数５〜
１１のジカルボン酸エステルの含有量が１０重量％未
満、または、６０重量％を越ると除去洗浄性の効果がな
くなる。また、炭素数５〜１１のジカルボン酸エステル
成分の含有率のが、この範囲を超えると、洗浄対象の工
業部品を構成する材料自体が影響を受ける場合がある。The cleaning liquid composition according to the present invention has 9 to 10 carbon atoms.
40 aromatic compounds containing 18 aromatic hydrocarbons as main components
~ 90 wt%, preferably 45-80 wt% and carbon number 5
It contains 10 to 60% by weight, preferably 20 to 55% by weight of the dicarboxylic acid ester component of 11 to 11. Carbon number 5
When the content of the dicarboxylic acid ester of 11 is less than 10% by weight or exceeds 60% by weight, the effect of removing and detergency is lost. If the content of the dicarboxylic acid ester component having 5 to 11 carbon atoms exceeds this range, the material itself constituting the industrial part to be cleaned may be affected.

【００１１】本発明の洗浄液組成物による洗浄方法は、
特に限定されることなく、液体洗浄剤による周知の方法
で行うことができる。例えば、洗浄液組成物を含浸した
スポンジなどによって拭き取る方法、スプレーなどで噴
霧した後に拭き取ったり、洗浄液組成物中に浸漬する方
法などが挙げられる。浸漬による洗浄においては、洗浄
効果を高めるために、同時に攪拌、揺動、超音波又はエ
アバブリングなどを組み合わせることが更に好ましい。
この場合、超音波の使用条件は、例えば発振周波数２０
〜１００ｋＨｚ、発振出力１０〜２００Ｗ／ｌが好まし
い。エアバブリングの場合、微細な気泡を洗浄液の底部
からバブリングし、洗浄液組成物に不溶な微細な汚れを
気泡と絡ませて共に上昇させ、不溶性の汚れをも分離、
除去することができる。スプレーによる洗浄において、
その圧力は、例えば０．５〜１０ｋｇ／ｃｍ^２Ｇが好ま
しい。いずれの場合も洗浄時間は、好ましくは１５秒間
〜２時間、特に好ましくは２０秒間〜２０分間である。
上記範囲未満では洗浄が不十分で、汚れを十分に除去し
得ず、一方、上記範囲を超えても洗浄効果は格別向上し
ない。洗浄温度は、好ましくは２０〜１２０℃である。
高い温度で処理することにより洗浄効果を著しく向上す
ることができる。上記範囲未満では、洗浄が不十分とな
りやすい。The cleaning method using the cleaning liquid composition of the present invention comprises:
The method is not particularly limited, and a known method using a liquid detergent can be used. For example, a method of wiping with a sponge impregnated with the cleaning liquid composition, a method of wiping after spraying with a spray, or a method of immersing in a cleaning liquid composition can be mentioned. In the cleaning by immersion, it is more preferable to combine stirring, shaking, ultrasonic waves, air bubbling and the like at the same time in order to enhance the cleaning effect.
In this case, the usage conditions of ultrasonic waves are, for example, an oscillation frequency of 20
˜100 kHz and oscillation output of 10 to 200 W / l are preferable. In the case of air bubbling, fine bubbles are bubbled from the bottom of the cleaning liquid, fine contaminants insoluble in the cleaning liquid composition are entangled with the bubbles and raised together, and insoluble contaminants are also separated,
Can be removed. In cleaning by spray,
The pressure is preferably 0.5 to ¹⁰ kg / cm ² G, for example. In any case, the washing time is preferably 15 seconds to 2 hours, particularly preferably 20 seconds to 20 minutes.
If the amount is less than the above range, the cleaning is insufficient and the stain cannot be sufficiently removed. The washing temperature is preferably 20 to 120 ° C.
By treating at a high temperature, the cleaning effect can be remarkably improved. If it is less than the above range, the cleaning tends to be insufficient.

【００１２】本発明の洗浄液組成物は、本発明の目的を
損なわない範囲で、界面活性剤、酸化防止剤、紫外線吸
収剤、防錆剤などの慣用の添加剤を含めることができ
る。通常、本発明の目的を損なわないためには、炭化水
素化合物とジカルボン酸エステル以外の成分は、５重量
％以下、特には、１重量％以下が好ましい。界面活性剤
は、油類、ポリマー、スケールの除去、分散に有効であ
り、非イオン性界面活性剤が好ましく使用できる。該非
イオン性界面活性剤としては、高級アルコールエチレン
オキサイド付加物、アルキルフェノールエチレンオキサ
イド付加物、脂肪酸エチレンオキサイド付加物、高級ア
ルキルアミンエチレンオキサイド付加物、ソルビトール
及びソルビタンの脂肪酸エステル、ショ糖脂肪酸エステ
ル、シリコン系界面活性剤、フッ素系界面活性剤などが
挙げられる。The cleaning liquid composition of the present invention may contain conventional additives such as a surfactant, an antioxidant, an ultraviolet absorber and an anticorrosive agent as long as the object of the present invention is not impaired. Usually, in order not to impair the object of the present invention, the components other than the hydrocarbon compound and the dicarboxylic acid ester are preferably 5% by weight or less, particularly preferably 1% by weight or less. The surfactant is effective for removing and dispersing oils, polymers and scale, and a nonionic surfactant can be preferably used. Examples of the nonionic surfactant include higher alcohol ethylene oxide adducts, alkylphenol ethylene oxide adducts, fatty acid ethylene oxide adducts, higher alkylamine ethylene oxide adducts, fatty acid esters of sorbitol and sorbitan, sucrose fatty acid esters, silicon-based compounds. Examples thereof include surfactants and fluorochemical surfactants.

【００１３】また、酸化防止剤及び紫外線吸収剤は、洗
浄液の保存安定性の向上に役立ち、紫外線吸収剤として
は、ベンゾトリアゾール系、ベンゾフェノン系、ヒンダ
ードアミン系などの紫外線吸収剤を使用でき、酸化防止
剤としては、フェノール系、アミン系、硫黄系、リン系
などの、本発明の洗浄液組成物に溶解するものはいずれ
も使用できる。添加剤及びその添加量は所望の効果を発
揮する添加剤かつその適当量を適宜選定して用いればよ
い。これらの添加剤は１００〜１０００ｐｐｍ程度添加
することが好ましい。Further, the antioxidant and the ultraviolet absorber serve to improve the storage stability of the cleaning liquid, and as the ultraviolet absorber, a benzotriazole-based, benzophenone-based, hindered amine-based ultraviolet absorber or the like can be used. As the agent, any one that is soluble in the cleaning liquid composition of the present invention, such as a phenol-based agent, an amine-based agent, a sulfur-based agent, or a phosphorus-based agent, can be used. Regarding the additive and its addition amount, an additive exhibiting a desired effect and an appropriate amount thereof may be appropriately selected and used. It is preferable to add about 100 to 1000 ppm of these additives.

【００１４】本発明の洗浄液組成物は、機械部品、電気
・電子部品、光学部品などの工業部品に付着した接着剤
による汚れ、例えば接着を必要としない箇所に付着した
接着剤、接着剤で張り合わせた部分からはみ出した不要
な、邪魔になる接着剤や、製造工程で部品表面の保護、
固定などの目的で使用するワックス・ピッチを効果的に
洗浄、除去することができる。The cleaning liquid composition of the present invention is soiled by an adhesive attached to industrial parts such as mechanical parts, electric / electronic parts, and optical parts, for example, an adhesive adhered to a part which does not require adhesion, and is bonded with an adhesive. Unnecessary adhesive that sticks out from the exposed part and protects the surface of parts during the manufacturing process.
It is possible to effectively wash and remove the wax pitch used for the purpose of fixing.

【００１５】このような工業部品としては、電子・電気
部品、光学部品、精密機械部品などがあげられる。対象
となる電気・電子部品としては、リードフレームなどの
半導体パッケージ、リレー、コネクターなどの接点部
材、液晶・プラズマディスプレイなどの表示部品、ハー
ドディスク記憶媒体・磁気ヘッドなどの磁気記憶部品、
水晶振動子などの圧電部品、モータ、ソレノイドなどの
駆動部品、センサー部品があげられる。光学部品として
は、めがね、顕微鏡、望遠鏡、カメラまたは電子機器の
光学ピックアップ用などのレンズ、ミラー、プリズム、
その筐体などがあげられる。精密機械部品としては、Ｖ
ＴＲなどに用いられる精密ベアリングなどの部品があげ
られる。Examples of such industrial parts include electronic / electrical parts, optical parts, precision machine parts and the like. The target electric and electronic parts are semiconductor packages such as lead frames, contact members such as relays and connectors, display parts such as liquid crystal and plasma displays, magnetic storage parts such as hard disk storage media and magnetic heads,
Examples include piezoelectric components such as crystal oscillators, drive components such as motors and solenoids, and sensor components. Optical parts include glasses, microscopes, telescopes, lenses for optical pickups of cameras or electronic devices, mirrors, prisms,
The case etc. are mentioned. As a precision machine part, V
Parts such as precision bearings used for TR etc. can be mentioned.

【００１６】汚染物となるワックス・ピッチを具体的に
例示すれば、研磨用あるいは張付用ピッチとしてのスト
レートアスファルト系、ブローンアスファルト系、ウッ
ド系などのピッチが挙げられる。また、ワックスは金
属、ガラスなどの仮止め接着剤として使用されている天
然樹脂、石油アスファルト、天然ワックス、石油系ワッ
クスなどがあげられる。Specific examples of the wax pitch that becomes a contaminant include straight asphalt-based, blown asphalt-based, and wood-based pitches as polishing or sticking pitches. Examples of the wax include natural resins used as temporary adhesives for metals and glass, petroleum asphalt, natural wax, petroleum wax and the like.

【００１７】汚染物となる接着剤を例示すれば、シアノ
系接着剤、紫外線硬化樹脂系接着剤を挙げることができ
る。シアノ系接着剤は、アルキルシアノアクリレートな
どのシアノ系化合物を主成分とする接着剤であり、メチ
ル−α−シアノアクリレート、エチル−α−シアノアク
リレートなどに代表されるアルキルシアノアクリレート
をモノマーとする接着剤であり、空気中または被着体表
面に存在する水分によって速やかに重合する性質を有し
ている。As an example of an adhesive that becomes a contaminant, a cyano adhesive and an ultraviolet curable resin adhesive can be mentioned. A cyano-based adhesive is an adhesive containing a cyano-based compound such as an alkyl cyanoacrylate as a main component, and an adhesive containing an alkyl cyanoacrylate represented by methyl-α-cyanoacrylate or ethyl-α-cyanoacrylate as a monomer. It is an agent and has the property of being rapidly polymerized by water present in the air or on the surface of an adherend.

【００１８】紫外線硬化樹脂系接着剤、すなわち、ＵＶ
硬化型接着剤は、紫外線を照射された部分のみが硬化
し、接着強度を有することとなる接着剤であり、例え
ば、エポキシアクリレート、ウレタンアクリレート、ポ
リエステルアクリレートと単官能、多官能アクリレート
モノマーとの組み合わせ（ラジカル重合型）、分子末端
にアリール基やアクリロイル基を有するオリゴマーとポ
リチオールの組み合わせ（チオール・エン付加型）、あ
るいは、紫外線カチオン開始剤を光分解して例えば生成
するルイス酸をカチオン反応の触媒として作用させて、
エポキシ、ビニルエーテルを有する樹脂を重合、硬化す
るもの（カチオン重合型）などが挙げられる。UV curable resin adhesive, that is, UV
The curable adhesive is an adhesive that cures only a portion irradiated with ultraviolet rays and has adhesive strength. For example, a combination of epoxy acrylate, urethane acrylate, polyester acrylate with a monofunctional or polyfunctional acrylate monomer. (Radical polymerization type), a combination of an oligomer having an aryl group or an acryloyl group at the molecular end and a polythiol (thiol / ene addition type), or a Lewis acid produced by photolytic decomposition of an ultraviolet cation initiator, for example, as a catalyst for cation reaction To act as
Examples thereof include those that polymerize and cure a resin having an epoxy or vinyl ether (cationic polymerization type).

【００１９】[0019]

【実施例】以下、本発明の洗浄液組成物を実施例に基づ
いてより詳細に説明するが、本発明はこれら実施例によ
り限定されるものではない。EXAMPLES The cleaning liquid composition of the present invention will be described below in more detail based on examples, but the present invention is not limited to these examples.

【００２０】〔洗浄液の調製〕 表1、２の配合量によ
り、洗浄液１〜９を調製した。洗浄液１〜９の構成成分
として、次の芳香族成分１〜３、エステル成分１、２を
用いた。芳香族成分１は、メチルナフタレンを６１重量
％、ジメチルナフタレンを１７重量％、エチルナフタレ
ンを１５重量％含有する。芳香族成分２は、ジメチルナ
フタレンを３４重量％、炭素数１３のアルキルナフタレ
ンを４７重量％、炭素数１４のアルキルナフタレンを４
重量％含有する。芳香族成分３は、ジイソプロピルナフ
タレンを９８重量％含有する。エステル成分１はグルタ
ル酸ジメチルエステルを９８重量％含有する。エステル
成分２はコハク酸ジメチルエステルを１６重量％、グル
タル酸ジメチルエステルを６２重量％、アジピン酸ジメ
チルエステルを２２重量％含有する。[Preparation of Cleaning Liquid] Cleaning liquids 1 to 9 were prepared according to the blending amounts shown in Tables 1 and 2. The following aromatic components 1 to 3 and ester components 1 and 2 were used as the constituents of the cleaning liquids 1 to 9. The aromatic component 1 contains 61% by weight of methylnaphthalene, 17% by weight of dimethylnaphthalene, and 15% by weight of ethylnaphthalene. The aromatic component 2 comprises 34% by weight of dimethylnaphthalene, 47% by weight of alkylnaphthalene having 13 carbon atoms, and 4% of alkylnaphthalene having 14 carbon atoms.
Contains by weight%. The aromatic component 3 contains 98% by weight of diisopropylnaphthalene. Ester component 1 contains 98% by weight of dimethyl glutarate. Ester component 2 contains 16% by weight of dimethyl succinate, 62% by weight of dimethyl glutarate and 22% by weight of dimethyl adipic acid.

【００２１】エステル成分１とウンデカンを配合して洗
浄液を調製しようとしたが、エステル成分１が１６重量
％〜８３重量％、ウンデカンが８４重量％〜１７重量％
の範囲では、相分離するため、洗浄液を調製できなかっ
た。An attempt was made to prepare a cleaning liquid by mixing the ester component 1 and undecane, but the ester component 1 was 16% by weight to 83% by weight and the undecane was 84% by weight to 17% by weight.
In the range of 1, the cleaning liquid could not be prepared because of phase separation.

【００２２】[0022]

【表１】 [Table 1]

【００２３】[0023]

【表２】 [Table 2]

【００２４】〔接着剤洗浄評価〕 接着剤の洗浄性評価
では、張り合わせガラスを次の方法で作成し、その張り
合わせガラスを洗浄物として用いた。この洗浄対象物を
洗浄液が充填された洗浄槽において液温３０℃で超音波
照射下に３０分間洗浄を行った。張り合わせガラスが完
全に分離した場合を○、分離しなかった場合を×として
評価し、表１、２に併せて示した。[Evaluation of Adhesive Cleaning] In the evaluation of the cleaning performance of the adhesive, laminated glass was prepared by the following method, and the laminated glass was used as a cleaning product. The object to be cleaned was cleaned in a cleaning tank filled with a cleaning liquid at a liquid temperature of 30 ° C. under ultrasonic irradiation for 30 minutes. The case where the laminated glass was completely separated was evaluated as ◯, and the case where the laminated glass was not separated was evaluated as ×, and the results are shown in Tables 1 and 2 together.

【００２５】用いた張り合わせガラスは、スライドガラ
ス（７６×２６×１ｍｍ）にシアノ系接着剤、ロックタ
イト４１７（日本ロックタイト製）を１滴たらし、その
上からカバーガラス（２２×２２×０．１５ｍｍ）を置
き、指圧で圧着した。接着剤による汚れを作るためにカ
バーガラスの表面中央にも１滴たらした。室温で放置
後、１分後にガラス同士は接着していたが、そのまま１
０分以上放置してから試験に使用した。The laminated glass used was one drop of cyano-based adhesive, Loctite 417 (manufactured by Nippon Loctite) on a slide glass (76 × 26 × 1 mm), and a cover glass (22 × 22 × 0.15 mm) was placed on it. ) Was placed and crimped by finger pressure. A drop was also placed on the center of the surface of the cover glass to create a stain due to the adhesive. After leaving at room temperature for 1 minute, the glass pieces were adhered to each other.
It was left for 0 minutes or more and then used for the test.

【００２６】〔ピッチ洗浄評価〕 ピッチ洗浄性の評価
では、ピッチ（九重電気（株）製、Ｋ級３号）を溶解し
た３０％濃度トルエン溶液に光学ガラスを浸し、室温で
乾燥することで、均一なピッチを付着させたものを洗浄
対象物として用いた。この洗浄対象物を洗浄液が充填さ
れた洗浄槽において液温３０℃で超音波照射下に２分間
洗浄を行った。洗浄槽から取りだした洗浄対象物を、１
０分間立てて静置後、温風乾燥機で洗浄液を蒸散除去し
乾燥した。洗浄後に、肉眼によりピッチの痕跡が全く認
められないものを〇、微かに痕跡のあるものを△、明ら
かな痕跡のあるものを×として評価し、表１、２に併せ
て示した。[Pitch Cleaning Evaluation] In the evaluation of pitch cleaning property, optical glass was dipped in a 30% concentration toluene solution in which pitch (K grade No. 3 manufactured by Kuju Denki Co., Ltd.) was dissolved and dried at room temperature. The thing to which the uniform pitch was adhered was used as the cleaning object. The object to be cleaned was cleaned in a cleaning tank filled with a cleaning liquid at a liquid temperature of 30 ° C. under ultrasonic irradiation for 2 minutes. 1 object to be cleaned taken out from the cleaning tank
After standing for 0 minutes and standing still, the washing liquid was removed by evaporation with a warm air drier and dried. After the cleaning, evaluation was made as ◯ when no trace of pitch was visually observed, Δ when slightly traced, and x when there was a clear trace, and the results are also shown in Tables 1 and 2.

【００２７】〔ワックス洗浄評価〕 ワックス洗浄性の
評価では、天然樹脂、石油アスファルト、天然ワックス
を成分とするリセスワックス（九重電気（株）製、Ｎ
ｏ．６）０．３ｇを光学ガラス上に置き、８０℃に加熱
し、１５分放置して溶融塗布し、その後室温まで放冷し
たものものを洗浄対象物として用いた。この洗浄対象物
を洗浄液が充填された洗浄槽において液温３０℃で超音
波照射下に２分間洗浄を行った。洗浄槽から取りだした
洗浄対象物を、１０分間立てて静置後、温風乾燥機で洗
浄液を蒸散除去し乾燥した。洗浄後に、ワックスの痕跡
が全く認められないものを〇、微かな痕跡のあるものを
△、明らかに痕跡のあるものを×として評価し、表１、
２に併せて示した。[Wax Cleaning Evaluation] In the evaluation of the wax cleaning property, natural resin, petroleum asphalt, and recessed wax containing natural wax (Kuju Electric Co., Ltd., N
o. 6) 0.3 g was placed on an optical glass, heated to 80 ° C., left standing for 15 minutes for melt coating, and then allowed to cool to room temperature, which was used as a cleaning object. The object to be cleaned was cleaned in a cleaning tank filled with a cleaning liquid at a liquid temperature of 30 ° C. under ultrasonic irradiation for 2 minutes. The object to be cleaned taken out from the cleaning tank was stood for 10 minutes and allowed to stand still, and then the cleaning liquid was removed by evaporation with a warm air dryer and dried. After cleaning, the case where no trace of wax was observed was evaluated as ◯, the case where there was a slight trace was evaluated as Δ, and the case where there was a clear trace was evaluated as x.
It is also shown in 2.

【００２８】[0028]

【発明の効果】本発明の洗浄液を用いることにより、接
着剤およびワックス、ピッチが付着した工業部品を、環
境規制上使用が制限されている化合物を用いることな
く、十分に洗浄することが可能となった。本発明の洗浄
液は、引火性が高いことなどにより使用・取り扱いが比
較的容易であり、かつ、ワックス・ピッチ、接着剤に対
して十分な洗浄性を有し、加えて、光学部品などの工業
部品を構成する材料自体に対する攻撃性のない洗浄が可
能となる。EFFECT OF THE INVENTION By using the cleaning liquid of the present invention, it is possible to sufficiently clean industrial parts to which adhesives, waxes, and pitches adhere without using compounds whose use is restricted by environmental regulations. became. INDUSTRIAL APPLICABILITY The cleaning liquid of the present invention is relatively easy to use and handle due to its high flammability and the like, and has sufficient cleaning properties for wax, pitch and adhesives. This makes it possible to perform cleaning without attacking the material itself that constitutes the part.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.⁷ 識別記号 ＦＩ テーマコート゛(参考） Ｃ２３Ｇ 5/032 Ｃ２３Ｇ 5/032 Ｆターム(参考） 3B201 AA46 BB01 BB21 BB82 BB83 BB94 BB95 4H003 BA12 DA16 DB03 EB09 ED03 ED32 4K053 PA01 QA04 QA07 RA08 RA48 RA57 SA03 SA04 SA06 SA18 YA03 ZA04 ─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. ⁷ Identification code FI theme code (reference) C23G 5/032 C23G 5/032 F term (reference) 3B201 AA46 BB01 BB21 BB82 BB83 BB94 BB95 4H003 BA12 DA16 DB03 EB09 ED03 ED32 4K053 PA01 QA04 QA07 RA08 RA48 RA57 SA03 SA04 SA06 SA18 YA03 ZA04

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 炭素数９〜１８の芳香族炭化水素を４０
〜９０重量％、炭素数５〜１１のジカルボン酸エステル
を１０〜６０重量％含有し、工業部品に付着した接着
剤、ピッチまたはワックスを洗浄する洗浄液組成物。1. An aromatic hydrocarbon having 9 to 18 carbon atoms is 40
A cleaning liquid composition containing 90% by weight to 10% to 60% by weight of a dicarboxylic acid ester having 5 to 11 carbon atoms to wash an adhesive, pitch or wax attached to an industrial part. 【請求項２】 接着剤が、シアノ系接着剤または紫外線
硬化樹脂系接着剤である請求項１に記載の洗浄液組成
物。2. The cleaning liquid composition according to claim 1, wherein the adhesive is a cyano adhesive or an ultraviolet curable resin adhesive. 【請求項３】 工業部品が、光学部品である請求項１に
記載の洗浄方法組成物。3. The cleaning method composition according to claim 1, wherein the industrial part is an optical part. 【請求項４】 接着剤、ピッチまたはワックスが付着し
た工業部品を、炭素数９〜１８の芳香族炭化水素を４０
〜９０重量％、炭素数５〜１１のジカルボン酸エステル
を１０〜６０重量％含有する洗浄液と接触させる洗浄方
法。4. An industrial part to which an adhesive, pitch or wax is attached is used as an aromatic hydrocarbon having 9 to 18 carbon atoms.
~ 90 wt%, a cleaning method of contacting with a cleaning liquid containing 10 to 60 wt% dicarboxylic acid ester having 5 to 11 carbon atoms.