JP2002363513A - Pressure-sensitive adhesive sheet, wrapping material, and wrapped product - Google Patents
Pressure-sensitive adhesive sheet, wrapping material, and wrapped productInfo
- Publication number
- JP2002363513A JP2002363513A JP2001174140A JP2001174140A JP2002363513A JP 2002363513 A JP2002363513 A JP 2002363513A JP 2001174140 A JP2001174140 A JP 2001174140A JP 2001174140 A JP2001174140 A JP 2001174140A JP 2002363513 A JP2002363513 A JP 2002363513A
- Authority
- JP
- Japan
- Prior art keywords
- pressure
- sensitive adhesive
- adhesive sheet
- plasticizer
- wet tissue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は粘着シート、並びに
これを用いた包装材及び包装製品に関する。更に詳しく
は、近年、医療用や衛生用などに使用されるウェットテ
ィシュの取り出し部蓋用ラベルとして使用される粘着シ
ート、並びにこれを用いた包装材及び包装製品に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a pressure-sensitive adhesive sheet, and a packaging material and a product using the same. More specifically, the present invention relates to a pressure-sensitive adhesive sheet used as a label for a lid of a take-out portion of a wet tissue used for medical or hygiene purposes, and a packaging material and a packaged product using the same.
【０００２】[0002]
【従来の技術】ウェットティッシュは、不織布類に化粧
水や洗浄剤の如き任意の薬剤をしみ込ませたもので、近
年、医療用や衛生用などに広く使用されている。このウ
ェットティッシュの包装形態としては、例えばプラスチ
ック製容器に内包されたり、あるいはフィルム包材に個
別包装した、いわゆる詰め替え用や持ち運び用ポケット
タイプのものがあるが、その持ち運び容易性からフィル
ム包材に個別包装されたものがよく使用されている。2. Description of the Related Art A wet tissue is a nonwoven fabric impregnated with an arbitrary agent such as a lotion or a cleaning agent, and has been widely used in medical and sanitary applications in recent years. As a packaging form of the wet tissue, for example, there is a so-called refillable or portable pocket type that is included in a plastic container or individually wrapped in a film packaging material. Individually packaged ones are often used.
【０００３】この個別包装のためのフィルム包材は、片
面にアルミ蒸着処理を施したポリエチレンフィルムとポ
リエチレンテレフタレート（ＰＥＴ）フイルムとを、ド
ライラミネート法などにより積層フィルム化した袋状の
本体を用いるのが一般的である。そして、この袋状本体
の一部には、ウエットティッシュ取出し口として開口が
設けられるが、内部の気密を保つため、その開口を覆う
ようにして粘着ラベルが蓋として貼り付けられる。[0003] As a film packaging material for this individual packaging, a bag-shaped main body is used in which a polyethylene film and a polyethylene terephthalate (PET) film on one side of which are laminated are formed into a laminated film by a dry laminating method or the like. Is common. An opening is provided in a part of the bag-shaped body as a wet tissue outlet, and an adhesive label is attached as a lid so as to cover the opening to keep the inside airtight.
【０００４】この粘着ラベルからなる蓋は、ウェットテ
ィシュを使用する際には、取出し口から一旦引剥がし、
所望枚数のウェットティシュを引き抜いた後に、再度貼
り付けて使用するようになっている。したがって、蓋の
役目をはたす粘着ラベルには、袋状本体からの良好な剥
離性が求められる。すなわち、糊残りがなく剥離抵抗が
小さい良好な剥離感が求められている。また、包装材本
体に対する再貼付性が必要なのはもちろんである。ま
た、何よりも重要なのはウェットティシュ保管時に内部
の気密性を維持することである。これが不十分であると
経時的にウェットティシュの揮発性成分が漏れだした
り、あるいは蒸発してしまい使用できなくなってしまう
からである。なお、特開平１１−７１５５７号公報、特
開平１０−３３０７０７号公報、特開平１０−１５２６
５９号公報において可塑剤が例示されているが、耐溶剤
性および剥離性（特にジッピング適性）を共に解決する
ことまでは至っていない。[0004] When using a wet tissue, the lid made of the adhesive label is once peeled off from the outlet, and
After a desired number of wet tissues are pulled out, they are pasted again and used. Therefore, the adhesive label serving as the lid is required to have good releasability from the bag-shaped main body. That is, there is a demand for a good peeling feeling with no adhesive residue and a small peeling resistance. Needless to say, re-adhesiveness to the packaging material body is necessary. The most important thing is to keep the inside airtight when storing the wet tissue. If this is insufficient, the volatile components of the wet tissue will leak out over time or will evaporate, making it unusable. It should be noted that JP-A-11-71557, JP-A-10-330707, and JP-A-10-1526.
No. 59 discloses a plasticizer, but does not solve both solvent resistance and releasability (particularly, suitability for zipping).
【０００５】[0005]
【発明が解決しようとする課題】ところが、ウェットテ
ィシュの一種として、例えば台所周りの油汚れ落し用
や、あるいは屋外での虫除け用等として、不織布類にし
み込ませる薬剤にエタノール成分を多く含有したものが
ある。このようなウエットティッシュでは、ウェットテ
ィシュ保存中（特に高温環境下）に経時的にウェットテ
ィシュの蓋である粘着ラベルの粘着剤がエタノール類に
より膨潤し、接着力や凝集力が低下する傾向がある。こ
のため、内部の気密性を維持できず、結果としてウェッ
トティシュの薬液成分が漏れだしたり、あるいは蒸発す
るという問題が生じていた。However, as a kind of wet tissue, for example, for removing oil stains around the kitchen, or for repelling insects outdoors, etc., a chemical containing a large amount of ethanol in a non-woven fabric soaked in nonwoven fabrics. There is. In such a wet tissue, the adhesive of the adhesive label, which is the lid of the wet tissue, tends to swell with ethanol over time during storage of the wet tissue (particularly in a high-temperature environment), and the adhesive strength and cohesive strength tend to decrease. . For this reason, the inside airtightness cannot be maintained, and as a result, there has been a problem that the chemical component of the wet tissue leaks out or evaporates.
【０００６】この問題を解決するために粘着剤の初期粘
着力をかなり強くすることで気密性を高めることなどが
考えられる。しかし、この場合ラベルの再剥離時に粘着
剤が包材に残ってしまったり、あるいは剥離抵抗が大き
すぎて包材やラベル自体が破れてしまうおそれがある。
そのため、かえって気密性維持の要請に反することにな
る。[0006] In order to solve this problem, it is conceivable to improve the airtightness by considerably increasing the initial adhesive strength of the adhesive. However, in this case, the adhesive may remain on the packaging material when the label is peeled off again, or the packaging material or the label itself may be broken due to too large peeling resistance.
Therefore, it is contrary to the demand for maintaining airtightness.
【０００７】また、ラベル用粘着剤の分子量や架橋密度
を高めることで耐エタノール性を向上することもでき
る。しかし、一般に分子量や架橋密度を高めると初期の
粘着力が低下してしまうために、結果として粘着剤がエ
タノールに侵される以前にラベル浮きが生じてしまい、
内部の気密性が維持できないという問題があった。この
ように、従来エタノールを含有するウェットティシュの
包装材蓋用として満足できる粘着ラベルはなく、その改
善が強く要望されていた。[0007] Ethanol resistance can also be improved by increasing the molecular weight and crosslink density of the pressure-sensitive adhesive for labels. However, in general, increasing the molecular weight or crosslink density decreases the initial adhesive strength, resulting in the label floating before the adhesive is attacked by ethanol,
There was a problem that the internal airtightness could not be maintained. As described above, there is no pressure-sensitive adhesive label which is satisfactory as a lid for a packaging material of a wet tissue containing ethanol, and improvement thereof has been strongly demanded.
【０００８】本発明は、このような現状を鑑み、袋状本
体からの良好な再剥離性と再貼り付け性を備えると共
に、エタノールを含む薬液に触れても、経時的に粘着剤
が膨潤することなく、長期間気密性を維持できるような
粘着シートを提供することを課題とする。また、エタノ
ールを含有する薬液を用いたウェットティッシュを容易
に取り出せると共に、長期間安定して収納できる包装材
を提供することを課題とする。さらに、容易に取り出せ
ると共に、長期間安定して保管できるエタノール含有薬
液を用いたウェットティッシュの包装製品を提供するこ
とを課題とする。In view of the above situation, the present invention has good removability and re-adhesion properties from the bag-shaped main body, and the adhesive swells with time even when it comes into contact with a chemical solution containing ethanol. It is an object of the present invention to provide a pressure-sensitive adhesive sheet that can maintain airtightness for a long time without any problem. It is another object of the present invention to provide a packaging material that can easily take out a wet tissue using a chemical solution containing ethanol and can stably store the wet tissue for a long period of time. It is another object of the present invention to provide a wet tissue packaged product using an ethanol-containing chemical solution that can be easily taken out and can be stably stored for a long period of time.
【０００９】[0009]
【課題を解決するための手段】本発明者は、粘着ラベル
に使用する再剥離型粘着剤について鋭意研究を行った。
その結果、粘着剤の耐エタノール性は、粘着剤に含まれ
る可塑剤の種類に大きく影響されること、さらに粘着剤
層の粘着力、保持力を特定範囲に規定することにより、
良好な再剥離性と耐エタノール性を両立できることを見
出し、本発明を完成した。Means for Solving the Problems The present inventor has conducted intensive studies on a removable adhesive used for an adhesive label.
As a result, the ethanol resistance of the pressure-sensitive adhesive is greatly affected by the type of plasticizer contained in the pressure-sensitive adhesive, and furthermore, by regulating the pressure-sensitive adhesive layer of the pressure-sensitive adhesive layer to a specific range,
The present inventors have found that good removability and ethanol resistance can be achieved at the same time, and completed the present invention.
【００１０】すなわち、一般に可塑剤としては、フタル
酸ジメチル、フタル酸ジエチル、フタル酸ジブチル、フ
タル酸ジオクチル、フタル酸ジ−ｎ−オクチル、フタル
酸ジシクロヘキシルなどのフタル酸エステル系、アジピ
ン酸オクチル、アゼライン酸オクチル、セバチン酸ジブ
チルなどの脂肪族二塩基酸系、リン酸トリクレジル、リ
ン酸トリオクチル、リン酸トリフェニルなどのリン酸エ
ステル系、トリメリット酸トリオクチル、トリメリット
酸トリイソノニル、トリメリット酸トリイソデシルなど
のトリメリット酸エステル系、アジピン酸系ポリエステ
ル、セバチン酸系ポリエステル、フタル酸系ポリエステ
ルなどのポリエステル系やエポキシ化アマニ油、エポキ
シ化ステアリン酸ブチルなどのエポキシ系などが挙げら
れる。That is, as the plasticizer, phthalate esters such as dimethyl phthalate, diethyl phthalate, dibutyl phthalate, dioctyl phthalate, di-n-octyl phthalate, dicyclohexyl phthalate and the like, octyl adipate, azelaine are generally used. Aliphatic dibasic acids such as octyl acid and dibutyl sebacate, phosphates such as tricresyl phosphate, trioctyl phosphate, and triphenyl phosphate; trioctyl trimellitate, triisononyl trimellitate, and triisodecyl trimellitate Examples include polyesters such as trimellitic acid ester, adipic acid polyester, sebacic acid polyester, and phthalic acid polyester, and epoxidized linseed oil and epoxidized butyl stearate.
【００１１】本発明者は、これら各種可塑剤を粘着剤に
混合し耐エタノール性を検討した。その結果、例えば可
塑剤の内で広く使用されているフタル酸エステル系を使
用した場合、粘着剤自体の耐エタノール性が低くなって
しまうが、ポリエステル系可塑剤を使用すると粘着剤の
耐エタノール性が向上することを見いだした。また、ト
リメリット酸エステル系可塑剤を使用した場合にも、粘
着剤の耐エタノール性が、かなりの程度向上することを
見いだした。この理由について詳細は不明であるが、フ
タル酸エステル系可塑剤の場合は一般に耐移行性や耐溶
剤性に劣り、特に高温環境化では粘着剤表面に可塑剤が
移行しエタノールへ溶解するために、結果として粘着剤
自体の耐エタノール性が低くなってしまうものと考えら
れる。一方、ポリエステル系可塑剤およびトリメリット
酸エステル系可塑剤は、フタル酸エステル系可塑剤より
も高分子量のため、移行性が低く耐溶剤性にも優れるた
めではないかと推測される。The present inventors have studied the ethanol resistance by mixing these various plasticizers with an adhesive. As a result, for example, when a phthalate ester widely used as a plasticizer is used, the ethanol resistance of the adhesive itself becomes low, but when a polyester plasticizer is used, the ethanol resistance of the adhesive is reduced. Was found to improve. In addition, it was also found that the use of a trimellitate plasticizer significantly improved the ethanol resistance of the pressure-sensitive adhesive. The reason for this is unknown, but phthalate plasticizers generally have poor migration resistance and solvent resistance, especially in high temperature environments where the plasticizer migrates to the adhesive surface and dissolves in ethanol. As a result, it is considered that the ethanol resistance of the pressure-sensitive adhesive itself is lowered. On the other hand, it is presumed that the polyester-based plasticizer and the trimellitate-based plasticizer have a higher molecular weight than the phthalate-based plasticizer, and therefore have low migration and excellent solvent resistance.
【００１２】次に、本発明者は、これらポリエステル系
可塑剤とトリメリット酸エステル系可塑剤を粘着剤に混
合し、再剥離性を検討した。その結果、トリメリット酸
エステル系可塑剤を単独で使用した場合には良好な再剥
離性が得られたが、ポリエステル系可塑剤を単独で使用
した場合には剥離抵抗が大きく、再剥離性に問題があっ
た。ところが、ポリエステル系可塑剤とトリメリット酸
エステル系可塑剤の双方を使用したところ、良好な再剥
離性と耐エタノール性を両立できることが見出された。Next, the inventor of the present invention mixed these polyester-based plasticizer and trimellitate-based plasticizer into an adhesive and examined removability. As a result, when the trimellitate-based plasticizer was used alone, good re-peelability was obtained, but when the polyester-based plasticizer was used alone, the peel resistance was large and the re-peelability was poor. There was a problem. However, it was found that when both a polyester plasticizer and a trimellitate plasticizer were used, both good removability and ethanol resistance could be achieved.
【００１３】以上の検討結果に従い、本発明は、シート
状基材の片面に粘着剤層を積層してなる粘着シートにお
いて、前記粘着剤層が可塑剤としてトリメリット酸エス
テル系可塑剤及びポリエステル系可塑剤を含む粘着剤か
らなることを特徴とする粘着シートを提供する。これに
より、耐エタノール性と良好な再剥離性を兼ね備えた粘
着シートとすることができる。According to the above study results, the present invention relates to a pressure-sensitive adhesive sheet comprising a sheet-like base material and a pressure-sensitive adhesive layer laminated on one surface, wherein the pressure-sensitive adhesive layer comprises a trimellitate-based plasticizer and a polyester-based plasticizer as a plasticizer. A pressure-sensitive adhesive sheet comprising a pressure-sensitive adhesive containing a plasticizer is provided. Thereby, an adhesive sheet having both ethanol resistance and good removability can be obtained.
【００１４】本発明において、前記粘着剤層のポリエチ
レンフィルムに対するＪＩＳ Ｚ０２３７に準拠する１
８０度粘着力は、２００〜６００ｇｆ／２５ｍｍである
ことが望ましい。この粘着力が２００ｇｆ／２５ｍｍよ
り小さいと、ラベルの浮きを生じやすく、６００ｇｆ／
２５ｍｍを越えると、再剥離時の抵抗が大きく粘着ラベ
ルやウェットティシュ包材が破れてしまうおそれがある
からである。In the present invention, the pressure-sensitive adhesive layer according to JIS Z0237 for polyethylene film
The 80-degree adhesive strength is desirably 200 to 600 gf / 25 mm. If the adhesive strength is less than 200 gf / 25 mm, the label is likely to float, and 600 gf / 25 mm.
If the thickness exceeds 25 mm, the resistance at the time of re-peeling is large, and the adhesive label or the wet tissue packaging material may be broken.
【００１５】本発明において、前記粘着剤層のＪＩＳ
Ｚ０２３７に準拠する６０℃保持力が８時間以上である
ことが望ましい。６０℃保持力が８時間よりも短いと、
トリメリット酸エステル系可塑剤およびポリエステル系
可塑剤を使用していても耐アルコール性が低下して、再
剥離時に包材に糊残りを生じる等の問題を生じ得るから
である。これは、粘着剤は、低分子量成分に富むと、全
体として耐溶剤性に劣り、架橋度を高める等して高分子
化すると、凝集力が高まり、耐溶剤性が向上するためで
あると考えられる。このことから、粘着剤の望ましい分
子量を規定することも考えられるが、実際上、粘着剤の
分子量を測定することは困難である。そこで本発明は、
分子量と密接な関係があり、しかも客観的な評価が容易
な６０℃保持力をもって、粘着剤の適切な分子量状態を
規定するものである。In the present invention, the pressure-sensitive adhesive layer has a JIS
It is desirable that the 60 ° C. holding power based on Z0237 is 8 hours or more. If the holding power at 60 ° C. is shorter than 8 hours,
This is because even if a trimellitate-based plasticizer and a polyester-based plasticizer are used, the alcohol resistance is reduced, which may cause a problem such as the generation of adhesive residue on the packaging material at the time of re-peeling. This is thought to be due to the fact that, when the pressure-sensitive adhesive is rich in low molecular weight components, it has poor solvent resistance as a whole, and when the pressure-sensitive adhesive is polymerized by increasing the degree of cross-linking, etc., the cohesive force is increased and the solvent resistance is improved. Can be From this fact, it is conceivable to define a desirable molecular weight of the pressure-sensitive adhesive, but it is actually difficult to measure the molecular weight of the pressure-sensitive adhesive. Therefore, the present invention
It has a close relationship with the molecular weight, and has a holding power of 60 ° C. at which the objective evaluation is easy, thereby defining an appropriate molecular weight state of the pressure-sensitive adhesive.
【００１６】本発明の粘着シートは、前記シート状基材
の片面に、前記粘着剤層および剥離シートを順次積層し
たことを特徴とすることができる。この場合、剥離シー
トにより粘着剤層が保護されるので、包装材の蓋として
使用される前の粘着シートを、保管、運搬等することが
容易となる。The pressure-sensitive adhesive sheet of the present invention can be characterized in that the pressure-sensitive adhesive layer and the release sheet are sequentially laminated on one surface of the sheet-like base material. In this case, the pressure-sensitive adhesive layer is protected by the release sheet, so that the pressure-sensitive adhesive sheet before being used as a lid of the packaging material can be easily stored and transported.
【００１７】また、本発明は、一部に開口を有する袋状
本体と、前記開口を覆う蓋体とを備える包装材であっ
て、前記蓋体の少なくとも一部が、上記本発明に係る粘
着シートからなることを特徴とする包装材を提供する。
本発明によれば、エタノールを含有する薬液を用いたウ
ェットティッシュを容易に取り出せると共に、長期間安
定して収納できる包装材とすることができる。Further, the present invention is a packaging material comprising a bag-shaped main body having an opening in a part thereof and a lid covering the opening, wherein at least a part of the lid is an adhesive according to the present invention. A packaging material characterized by comprising a sheet is provided.
ADVANTAGE OF THE INVENTION According to this invention, while being able to take out the wet tissue using the chemical | medical solution containing ethanol easily, it can be set as the packaging material which can be stably accommodated for a long period of time.
【００１８】また、本発明は、前記本発明に係る包装材
と、該包装材の内部に収納されたウェットティッシュと
からなり、前記ウェットティッシュは、吸収基材にエタ
ノールを含む薬液を含浸させてなることを特徴とするウ
ェットティッシュの包装製品を提供する。本発明によれ
ば、容易に取り出せると共に、長期間安定して収納でき
るエタノールを含有する薬液を用いたウェットティッシ
ュの包装製品とすることができる。Further, the present invention comprises the packaging material according to the present invention and a wet tissue stored inside the packaging material, wherein the wet tissue is obtained by impregnating an absorbent substrate with a chemical solution containing ethanol. The present invention provides a packaged product of wet tissue. ADVANTAGE OF THE INVENTION According to this invention, while being easily taken out, the packaged product of the wet tissue using the chemical solution containing ethanol which can be stably stored for a long period of time can be obtained.
【００１９】[0019]
【発明の実施の形態】以下に本発明の実施形態について
図面を参照して説明するが、本発明は以下の実施形態に
限定されるものではない。図１は本発明の第１実施形態
に係る粘着シートの断面図である。図１の粘着シート１
０は、シート状の基材１の片面に粘着剤層２を積層して
構成されている。Embodiments of the present invention will be described below with reference to the drawings, but the present invention is not limited to the following embodiments. FIG. 1 is a sectional view of the pressure-sensitive adhesive sheet according to the first embodiment of the present invention. Adhesive sheet 1 of FIG.
No. 0 is constituted by laminating the pressure-sensitive adhesive layer 2 on one surface of a sheet-like substrate 1.
【００２０】基材１には、ウェットティシュに含まれる
水分やエタノール等を保持するため、耐水性、耐溶剤性
やガスバリヤー性が求められる。そのため、基材１とし
ては、例えば、ポリエチレン、ポリプロピレン、ポリカ
ーボネート、ＰＥＴの如きポリオレフィン系のプラスチ
ックフィルムや、これに有機／無機顔料を内添し中空構
造とした発泡ＰＥＴやユポの如き合成紙、軟質塩ビフィ
ルム、ポリエチレンラミネート紙、金属箔が用いられ
る。これらの市販品としては、例えば、（株）ユポ・コ
ーポレーション製のユポフィルム「ＳＧＳ」、「ＦＰ
Ｇ」、「ＶＥＳ」や、東洋紡績（株）製の発泡ＰＥＴフ
ィルム「クリスパー」、東レ（株）製のＰＥＴフィルム
「ルミラー」等が挙げられる。基材１の厚さは特に限定
されないが、薄すぎると隠蔽性が劣ったり、再剥離時の
ラベル折れシワが発生し易くなる。また厚すぎると基材
の腰が強くなり、粘着ラベルがウェットティシュ製品の
凹凸に十分追従できずにラベル浮きが生じ易くなる。そ
のため、一般的には１０〜１５０μｍ程度のものが好ま
しい。The substrate 1 is required to have water resistance, solvent resistance and gas barrier properties in order to retain moisture, ethanol and the like contained in the wet tissue. Therefore, as the base material 1, for example, a polyolefin-based plastic film such as polyethylene, polypropylene, polycarbonate, or PET, a synthetic paper such as foamed PET or Yupo having a hollow structure by internally adding an organic / inorganic pigment, or a soft paper A PVC film, polyethylene laminated paper, or metal foil is used. These commercially available products include, for example, Yupo Film “SGS” and “FP” manufactured by Yupo Corporation.
G "," VES ", foamed PET film" Crisper "manufactured by Toyobo Co., Ltd., and PET film" Lumirror "manufactured by Toray Industries, Inc. Although the thickness of the substrate 1 is not particularly limited, if it is too thin, the concealing property is poor, and the label is wrinkled easily at the time of re-peeling. On the other hand, if the thickness is too thick, the stiffness of the base material becomes strong, and the adhesive label cannot follow the unevenness of the wet tissue product sufficiently, so that the label easily floats. Therefore, in general, those having a thickness of about 10 to 150 μm are preferable.
【００２１】粘着剤層２は、アクリル系、合成ゴム系、
天然ゴム系等各種組成のものが所望とする品質に応じて
任意に選択使用できるが、その中でも２−エチルヘキシ
ルアクリレート、ブチルアクリレート、エチルアクリレ
ート、メタクリル酸メチルなどのアクリル系モノマーの
共重合体を主成分とするアクリル系粘着剤の使用が好ま
しい。アクリル系粘着剤は、大きく溶剤型とエマルジョ
ン型に分けられるが、一般にエマルジョン型は耐水性、
耐湿性に劣るため、溶剤型の適用が好ましい。The pressure-sensitive adhesive layer 2 is made of acrylic, synthetic rubber,
Various compositions such as natural rubbers can be arbitrarily selected and used according to desired quality. Among them, copolymers of acrylic monomers such as 2-ethylhexyl acrylate, butyl acrylate, ethyl acrylate and methyl methacrylate are mainly used. It is preferable to use an acrylic pressure-sensitive adhesive as a component. Acrylic adhesives are roughly divided into solvent type and emulsion type.
The solvent type is preferred because of its poor moisture resistance.
【００２２】粘着剤層２は、再剥離性が必要であるが、
袋状本体から糊残りなく再剥離させるためには高い凝集
力が必須である。よって溶剤型アクリル系粘着剤の中で
も架橋型粘着剤の使用が好ましい。架橋型粘着剤とは、
架橋前は低分子量ポリマーからなる低凝集力の粘着剤ベ
ースが、粘着剤中アクリルポリマーに存在するカルボキ
シル基、水酸基、エポキシ基の如き官能基と、塗工の際
に添加される架橋剤が反応することで高分子量化し優れ
た凝集力を発現するものである。The pressure-sensitive adhesive layer 2 must have removability,
A high cohesive force is indispensable for re-peeling from the bag-shaped body without leaving any adhesive. Therefore, among solvent-based acrylic pressure-sensitive adhesives, the use of a crosslinked pressure-sensitive adhesive is preferred. What is a cross-linked adhesive?
Before cross-linking, the low-cohesive pressure-sensitive adhesive base composed of a low-molecular-weight polymer reacts with functional groups such as carboxyl groups, hydroxyl groups, and epoxy groups present in the acrylic polymer in the pressure-sensitive adhesive, and the cross-linking agent added during coating. By doing so, the polymer has a high molecular weight and exhibits excellent cohesion.
【００２３】架橋剤としては、公知の架橋剤が使用でき
る。例えば脂肪族イソシアネート化合物、芳香族イソシ
アネート化合物、エポキシ化合物、金属キレート化合物
等が使用できる。具体的には、ヘキサメチレンジイソシ
アネート（ＨＭＤＩ）等やその誘導体の如き脂肪族イソ
シアネート化合物、アルミニウム−イソプロピレート、
アルミニウム−ｓｅｃブチレート、アルミニウムアセチ
ルアセトナート等のアルミニウムキレート化合物や、テ
トライソプロピルチタネート、テトラキス（２−エチル
ヘキソキシ）チタネート等のチタンキレート化合物等の
金属キレート化合物が例示できるが、もちろんこの例示
に限るものではない。なお、２種以上併用することも可
能である。架橋材の使用量としては、粘着力および保持
力の数値範囲を満足するように、架橋材を適宜選択的に
添加するものである。さらに、粘着剤の種類によって一
概には言えないが、一例として、粘着主剤がブチルアク
リレート／アクリル酸系粘着剤の場合、粘着主剤のポリ
マー成分１００部に対する架橋剤の好ましい使用量は、
１．５〜７．５部である。この中でも、２〜６．５部が
好ましく、さらに好ましくは３〜６部である。１．５部
より少ないと粘着力が大きくなりすぎると共に、充分な
保持力が得られない。７．５部より多すぎると、粘着力
が小さくなりすぎ、浮き剥がれ等の問題が生じるおそれ
がある。Known crosslinking agents can be used as the crosslinking agent. For example, aliphatic isocyanate compounds, aromatic isocyanate compounds, epoxy compounds, metal chelate compounds and the like can be used. Specifically, aliphatic isocyanate compounds such as hexamethylene diisocyanate (HMDI) and derivatives thereof, aluminum-isopropylate,
Examples thereof include aluminum chelate compounds such as aluminum-sec butyrate and aluminum acetylacetonate, and metal chelate compounds such as titanium chelate compounds such as tetraisopropyl titanate and tetrakis (2-ethylhexoxy) titanate, but are not limited thereto. . In addition, it is also possible to use 2 or more types together. The amount of the cross-linking agent used is such that the cross-linking agent is appropriately and selectively added so as to satisfy the numerical ranges of the adhesive force and the holding power. Furthermore, although it cannot be said unconditionally depending on the type of the adhesive, as an example, when the adhesive main agent is a butyl acrylate / acrylic acid-based adhesive, the preferable usage amount of the crosslinking agent for 100 parts of the polymer component of the adhesive main agent is
1.5 to 7.5 parts. Among these, 2 to 6.5 parts is preferable, and 3 to 6 parts is more preferable. If the amount is less than 1.5 parts, the adhesive strength becomes too large and a sufficient holding force cannot be obtained. If the amount is more than 7.5 parts, the adhesive strength may be too small, and problems such as peeling off may occur.
【００２４】粘着剤層２の粘着剤中には再剥離時の手め
くり感向上などの目的で可塑剤が併用されるが、この
際、優れた再剥離性と耐エタノール性を両立させるため
に、可塑剤としてトリメリット酸エステル系可塑剤およ
びポリエステル系可塑剤を併用する。可塑剤の配合比率
は特に限定されないが、粘着剤ベース樹脂に対して５〜
１５部程度が好ましい。また、トリメリット酸エステル
系可塑剤とポリエステル系可塑剤の混合比についても特
に限定されないが、トリメリット酸エステル系可塑剤／
ポリエステル系可塑剤＝９０／１０〜５０／５０程度で
耐溶剤性と再剥離性のバランス上好ましい結果が得られ
る。A plasticizer is used in the pressure-sensitive adhesive of the pressure-sensitive adhesive layer 2 for the purpose of, for example, improving the feeling of turning during re-peeling. In this case, in order to achieve both excellent re-peelability and ethanol resistance. A trimellitate plasticizer and a polyester plasticizer are used in combination as a plasticizer. The mixing ratio of the plasticizer is not particularly limited, but is 5 to 5 with respect to the pressure-sensitive adhesive base resin.
About 15 parts is preferable. The mixing ratio between the trimellitate plasticizer and the polyester plasticizer is not particularly limited, either.
When the polyester plasticizer is about 90/10 to 50/50, favorable results can be obtained in terms of the balance between solvent resistance and removability.
【００２５】粘着剤には接着性向上のためロジン系、テ
ルペン系等の天然樹脂や、石油系、フェノール系、キシ
レン系等の合成樹脂からなる各種タッキファイヤー、あ
るいは無機／有機填料や紫外線吸収剤などの公知の助剤
も任意に併用することができる。Various tackifiers made of rosin-based or terpene-based natural resins, petroleum-based, phenol-based, xylene-based synthetic resins, or inorganic / organic fillers or ultraviolet absorbers are used for the adhesive to improve adhesiveness. Known auxiliaries such as can be used arbitrarily.
【００２６】粘着剤の塗工方法は、コンマコーター、ダ
イコーター、リップコーター、ロールコーター、ブレー
ドコーター等高粘度物塗工に適する公知の方法を任意に
使用することができる。また粘着剤塗工は、表面基材に
塗工、乾燥した後、剥離シートと積層する方法（いわゆ
る直接法）と、剥離シートの剥離剤層面に塗工、乾燥し
た後、表面基材を積層する方法（いわゆる転写法）のど
ちらでも採用できる。As a method for applying the pressure-sensitive adhesive, any known method suitable for applying a high-viscosity material such as a comma coater, a die coater, a lip coater, a roll coater, a blade coater, or the like can be used. Adhesive coating is applied to the surface base material, dried and then laminated with a release sheet (so-called direct method), or applied to the release layer surface of the release sheet, dried and then laminated to the surface substrate (A transfer method).
【００２７】粘着剤層２の塗工量は任意に調整可能であ
るが、粘着剤層２のＰＥＴフィルムに対するＪＩＳ Ｚ
０２３７に準拠する１８０度粘着力が、２００〜６００
ｇｆ／２５ｍｍの範囲内であり、ＪＩＳ Ｚ０２３７に
準拠する６０℃での保持力が８時間以上となるよう、充
分な量が塗工される。ただし、塗工量が極端に多くなる
と粘着剤のはみだし（ウーズ）の懸念がある。したがっ
て、望ましい塗工量は１０〜５０ｇ／ｍ2程度である。The coating amount of the pressure-sensitive adhesive layer 2 can be arbitrarily adjusted.
180-degree adhesive strength according to 0237 is 200 to 600
gf / 25 mm, and a sufficient amount is applied so that the holding power at 60 ° C. in accordance with JIS Z0237 is 8 hours or more. However, when the coating amount is extremely large, there is a concern that the pressure-sensitive adhesive will protrude (oose). Therefore, a desirable coating amount is about 10 to 50 g / m 2 .
【００２８】本実施形態の粘着シートは、耐エタノール
性と良好な再剥離性を兼ね備えた粘着シートであり、エ
タノールを含むウエットティッシュの蓋体として好適に
使用できる。The pressure-sensitive adhesive sheet of the present embodiment is a pressure-sensitive adhesive sheet having both ethanol resistance and good removability, and can be suitably used as a lid of a wet tissue containing ethanol.
【００２９】図２は本発明の第２実施形態に係る粘着シ
ートの断面図である。図２の粘着シートは、図１の粘着
シート１０における粘着剤層２の基材１と反対側に剥離
シート３を積層して構成されている。なお、図２におい
て、図１と同一の構成要素には同一の符号を付し、詳細
な説明を省略する。FIG. 2 is a sectional view of a pressure-sensitive adhesive sheet according to a second embodiment of the present invention. The pressure-sensitive adhesive sheet of FIG. 2 is configured by laminating a release sheet 3 on the side of the pressure-sensitive adhesive layer 2 opposite to the base material 1 in the pressure-sensitive adhesive sheet 10 of FIG. In FIG. 2, the same components as those in FIG. 1 are denoted by the same reference numerals, and detailed description thereof will be omitted.
【００３０】剥離シート３の基材としては、例えば、Ｐ
ＥＴフィルム、発泡ＰＥＴフィルム、ポリカーボネート
フィルム、ポリプロピレンフィルム、合成紙などのプラ
スチックフィルムや、上質紙、グラシン紙、塗工紙、ポ
リエチレンラミネート紙等公知のものが挙げられ、特に
その種類については限定されない。剥離シート３の基材
上に塗工される剥離剤としては、シリコーン系剥離剤や
長鎖アルキル基含有の非シリコーン系剥離剤などが使用
できる。剥離シート基材への剥離剤の塗工方法として
は、通常の塗工機、例えば、バーコーター、ロールコー
ター、グラビヤコーター等によって塗工することができ
る。剥離剤の塗工量としては、乾燥重量で０．０５〜３
ｇ／ｍ2、好ましくは、０．２〜１．５ｇ／ｍ2が適当で
ある。因みに、０．０５ｇ／ｍ2未満では、剥離性に乏
しく、また、３ｇ／ｍ2を越えることは、経済性の面か
ら必要性に乏しい。The base material of the release sheet 3 is, for example, P
Examples include plastic films such as ET films, foamed PET films, polycarbonate films, polypropylene films, and synthetic papers, and known materials such as high-quality paper, glassine paper, coated paper, and polyethylene laminated paper, and the type thereof is not particularly limited. As the release agent applied on the base material of the release sheet 3, a silicone release agent or a non-silicone release agent containing a long-chain alkyl group can be used. As a method for applying the release agent to the release sheet substrate, the release agent can be applied using a usual coating machine, for example, a bar coater, a roll coater, a gravure coater, or the like. The coating amount of the release agent is 0.05 to 3 by dry weight.
g / m 2, preferably, suitably 0.2 to 1.5 g / m 2. Incidentally, it is less than 0.05 g / m 2, poor releasability, also exceed 3 g / m 2 is poor necessity from the viewpoint of economy.
【００３１】本実施形態の粘着シートは、剥離シート３
により粘着剤層２が保護されるので、包装材の蓋として
使用される前の粘着シート１０を、保管、運搬等するこ
とが容易となる。なお、剥離材を基材１の表面に塗工す
れば、剥離シート３を用いずに、粘着シート１０を、保
管、運搬等することも可能である。The pressure-sensitive adhesive sheet of this embodiment is a release sheet 3
Thus, the pressure-sensitive adhesive layer 2 is protected, so that the pressure-sensitive adhesive sheet 10 before being used as a lid of the packaging material can be easily stored and transported. Note that if a release material is applied to the surface of the substrate 1, the pressure-sensitive adhesive sheet 10 can be stored, transported, and the like without using the release sheet 3.
【００３２】図３は本発明の第３実施形態に係るウエッ
トティッシュ包装製品の斜視図である。図３の包装製品
は、袋状本体２０の内部に収納されたウェットティッシ
ュ３０を、袋状本体２０の上方中央に設けられた開口２
１から取り出せるようになっている。この開口２１は、
常時は、上述の粘着シート１０、つまみ部１１及び固定
部１２とからなる蓋体で覆われるようになっている。FIG. 3 is a perspective view of a wet tissue packaged product according to a third embodiment of the present invention. In the packaged product of FIG. 3, the wet tissue 30 stored inside the bag-shaped main body 20 is inserted into the opening 2 provided at the upper center of the bag-shaped main body 20.
1 can be taken out. This opening 21
Normally, it is covered with a lid including the above-described pressure-sensitive adhesive sheet 10, knob 11 and fixing part 12.
【００３３】蓋体の中央大部分を占める粘着シート１０
は、基材１を表側に、粘着剤層２を袋状本体２０側に
し、開口２１全体を覆うようにして袋状本体２に再剥離
自在に貼着されている。つまみ部１１は、図３に示すよ
うに、粘着シート１０の一端部に突出して設けられてい
る。このつまみ部１１は粘着面を持たず、粘着シート１
０を袋状本体２０に貼着時にも、袋状本体２０から浮き
上がった状態を保ち、開閉時に手でつまみやすいように
なっている。つまみ部１１の具体的な層構成は、たとえ
ば、粘着シート１０の粘着剤層２の表面に、非粘着加工
（いわゆる糊殺し）を施したものとしたり、粘着剤層２
が積層されていない基材１のみを用いたものとしたりす
ることができる。一方、固定部１２は、粘着シート１０
の他端部に設けられている。この固定部１２は、つまみ
部１１を持って粘着シート１０を引き上げた際にも、袋
状本体２０とのつながりを保てるように構成されてい
る。固定部１２の具体的な層構成は、たとえば、粘着シ
ート１０と同一構成とすることができるが、この場合、
粘着シート１０と共に引き上げられて袋状本体２０から
離脱しないようにした抜き加工（いわゆるストッパー加
工）が施される。また、基材１に再剥離不可能な粘着材
層を設けた構成とすることもできる。Adhesive sheet 10 occupying most of the center of the lid
Is attached to the bag-shaped main body 2 so as to be releasable so that the base material 1 is on the front side and the pressure-sensitive adhesive layer 2 is on the bag-shaped main body 20 side. As shown in FIG. 3, the knob 11 protrudes from one end of the adhesive sheet 10. This knob 11 does not have an adhesive surface, and the adhesive sheet 1
Even when the “0” is attached to the bag-shaped main body 20, it is maintained in a state of being lifted from the bag-shaped main body 20, so that it can be easily picked up by hand when opened and closed. The specific layer configuration of the knob portion 11 is, for example, a non-adhesive process (so-called glue killing) applied to the surface of the adhesive layer 2 of the adhesive sheet 10, or the adhesive layer 2.
Or only the base material 1 on which no is laminated. On the other hand, the fixing part 12 is
At the other end. The fixing portion 12 is configured to maintain the connection with the bag-shaped main body 20 even when the adhesive sheet 10 is pulled up with the knob portion 11. The specific layer configuration of the fixing portion 12 can be, for example, the same configuration as the pressure-sensitive adhesive sheet 10, but in this case,
A punching process (a so-called stopper process) is performed to prevent the bag-like main body 20 from being lifted up together with the adhesive sheet 10. Further, a configuration in which a non-removable pressure-sensitive adhesive layer is provided on the base material 1 may be employed.
【００３４】袋状本体２０は、片面にアルミ蒸着処理を
施したポリエチレンフィルムとＰＥＴフィルムを、アル
ミ蒸着層を内側としてドライラミネート法などにより積
層フィルム化し、開口２１を設けてから袋状に形成した
ものである。The bag-shaped main body 20 is formed by laminating a polyethylene film and a PET film having one side subjected to aluminum vapor deposition processing by a dry laminating method or the like with the aluminum vapor-deposited layer inside, forming an opening 21 and then forming the bag-shaped body. Things.
【００３５】ウェットティシュ３０は、エタノールを含
む薬液を不織布類等の吸収基材にしみ込ませたものであ
る。また、薬液には、化粧水、洗浄剤等の各種用途に応
じて、エタノールの他に種々の成分が含まれている。The wet tissue 30 is formed by impregnating a chemical solution containing ethanol into an absorbent substrate such as a nonwoven fabric. In addition, various components other than ethanol are contained in the chemical solution in accordance with various uses such as lotion and cleaning agents.
【００３６】本実施形態のウエットティッシュ包装製品
は、蓋体として、再剥離性に優れた粘着シート１０を用
いたので、収納されたウェットティッシュ３０を、大き
な剥離抵抗を受けることなく容易に取り出すことがてき
る。また、粘着シート１０は耐エタノール性に優れてい
る。そのため、エタノールに侵されることなく、ウェッ
トティッシュ３０を長期間安定して保管することができ
る。In the wet tissue packaged product of this embodiment, since the adhesive sheet 10 having excellent removability is used as the lid, the stored wet tissue 30 can be easily taken out without receiving a large peel resistance. Comes. Further, the pressure-sensitive adhesive sheet 10 has excellent ethanol resistance. Therefore, the wet tissue 30 can be stably stored for a long period of time without being affected by ethanol.
【００３７】[0037]
【実施例】以下に、実験例を挙げて本発明をより具体的
に説明するが、勿論本発明はそれらに限定されるもので
はない。尚、試料の説明中の％、部、重量、割合、塗被
量等は特に断らない限り、全て固形分重量で示すもので
ある。EXAMPLES The present invention will be described below more specifically with reference to experimental examples, but of course, the present invention is not limited thereto. Unless otherwise specified, all percentages, parts, weights, proportions, coating amounts, and the like in the description of the samples are indicated by solid content weight.
【００３８】（試料１）ブチルアクリレート１００部、
アクリル酸７部を酢酸エチル中にて開始剤として過酸化
ベンゾイル１部を用いて溶液重合し、固形分濃度４０
％、分子量９６０００の粘着主剤を得た。この粘着主剤
１００部に対して、トリメリット酸エステル系可塑剤
（商標名：アデカサイザーＣ−８８０、固形分濃度１０
０％、旭電化工業（株）製）５部、ポリエステル系可塑
剤（商標名：アデカサイザーＰＮ−１４３０、固形分濃
度１００％、旭電化工業（株）製）２部、および多官能
性芳香族イソシアネート架橋剤４部を混合した粘着剤塗
料を、市販のポリエチレンラミネート剥離紙上に絶乾塗
工量が３０ｇ／ｍ2となるようにコンマコーターで塗
工、乾燥した後、ニップロールにより、ポリプロピレン
系合成紙（商標：ユポＳＧＳ８０、（株）ユポ・コーポ
レーション製）を貼り合わせた。これを２２℃で７日間
エージングして粘着シートを得た。(Sample 1) 100 parts of butyl acrylate
Acrylic acid (7 parts) was solution-polymerized in ethyl acetate using benzoyl peroxide (1 part) as an initiator to give a solid content of 40 parts.
%, A molecular weight of 96,000 was obtained. A trimellitic acid ester-based plasticizer (trade name: Adecaizer C-880, solid concentration 10
0%, 5 parts of Asahi Denka Kogyo Co., Ltd.), 2 parts of polyester-based plasticizer (trade name: Adecaizer PN-1430, solid content concentration 100%, 2 parts of Asahi Denka Kogyo Co., Ltd.), and polyfunctional fragrance An adhesive coating obtained by mixing 4 parts of an aromatic isocyanate cross-linking agent is coated on a commercially available polyethylene laminate release paper with a comma coater so that the absolute dry coating amount is 30 g / m 2, and then dried. Synthetic paper (trade name: Yupo SGS80, manufactured by Yupo Corporation) was attached. This was aged at 22 ° C. for 7 days to obtain a pressure-sensitive adhesive sheet.
【００３９】（試料２）粘着剤塗料中の可塑剤として、
トリメリット酸エステル系可塑剤（商標名：アデカサイ
ザーＣ−８８０、固形分濃度１００％、旭電化工業
（株）製）３．５部、ポリエステル系可塑剤（商標名：
アデカサイザーＰＮ−１４３０、固形分濃度１００％、
旭電化工業（株）製）３．５部を用いた以外は、試料１
と同様にして粘着シートを得た。(Sample 2) As a plasticizer in the adhesive paint,
3.5 parts of trimellitic acid ester plasticizer (trade name: Adecaizer C-880, solid content concentration 100%, manufactured by Asahi Denka Kogyo Co., Ltd.), polyester plasticizer (trade name:
ADEKA SIZER PN-1430, solid content concentration 100%,
Sample 1 was used except that 3.5 parts of Asahi Denka Kogyo Co., Ltd. was used.
In the same manner as in the above, an adhesive sheet was obtained.
【００４０】（試料３）粘着剤塗料中の可塑剤として、
ポリエステル系可塑剤（商標名：アデカサイザーＰＮ−
１４３０、固形分濃度１００％、旭電化工業（株）製）
７部を用いた以外は、試料１と同様にして粘着シートを
得た。(Sample 3) As a plasticizer in the adhesive paint,
Polyester plasticizer (trade name: ADEKA SIZER PN-)
1430, solid content concentration 100%, manufactured by Asahi Denka Kogyo Co., Ltd.)
An adhesive sheet was obtained in the same manner as in Sample 1, except that 7 parts were used.
【００４１】（試料４）粘着剤塗料中の可塑剤として、
トリメリット酸エステル系可塑剤（商標名：アデカサイ
ザーＣ−８８０、固形分濃度１００％、旭電化工業
（株）製）７部を用いた以外は、試料１と同様にして粘
着シートを得た。(Sample 4) As a plasticizer in the adhesive paint,
An adhesive sheet was obtained in the same manner as in Sample 1, except that 7 parts of a trimellitic acid ester-based plasticizer (trade name: Adecaizer C-880, solid content concentration 100%, manufactured by Asahi Denka Kogyo KK) was used. .
【００４２】（試料５）粘着剤塗料中の可塑剤として、
フタル酸エステル系可塑剤（ＤＯＰ、固形分濃度１００
％）７部を用いた以外は、試料１と同様にして粘着シー
トを得た。(Sample 5) As a plasticizer in the adhesive paint,
Phthalate plasticizer (DOP, solid content 100
%) An adhesive sheet was obtained in the same manner as in Sample 1, except that 7 parts were used.
【００４３】（試料６）粘着剤塗料中から可塑剤を抜い
た以外は、試料１と同様にして粘着シートを得た。(Sample 6) An adhesive sheet was obtained in the same manner as in Sample 1, except that the plasticizer was removed from the adhesive paint.
【００４４】（試料７）粘着剤塗料中の多官能芳香族イ
ソシアネート架橋剤を１部とした以外は、試料１と同様
にして粘着シートを得た。(Sample 7) A pressure-sensitive adhesive sheet was obtained in the same manner as in Sample 1, except that the polyfunctional aromatic isocyanate crosslinking agent in the pressure-sensitive adhesive paint was changed to 1 part.
【００４５】（試料８）粘着剤塗料中の多官能芳香族イ
ソシアネート架橋剤を８部とした以外は、試料１と同様
にして粘着シートを得た。(Sample 8) A pressure-sensitive adhesive sheet was obtained in the same manner as in Sample 1, except that the polyfunctional aromatic isocyanate crosslinking agent in the pressure-sensitive adhesive paint was changed to 8 parts.
【００４６】（試料９）表面基材を市販のキャストコー
ト紙とした以外は、試料１と同様にして粘着シートを得
た。(Sample 9) A pressure-sensitive adhesive sheet was obtained in the same manner as in Sample 1, except that a commercially available cast-coated paper was used as the surface base material.
【００４７】（評価方法） （１）粘着力 ＪＩＳ Ｚ０２３７に準じ、ＰＥＴフィルムに対する１
８０度粘着力を剥離速度０．３ｍ／分で測定した。(Evaluation method) (1) Adhesive force 1 according to JIS Z0237 for PET film
The 80 degree adhesive force was measured at a peeling speed of 0.3 m / min.
【００４８】（２）保持力 試料を２５ｍｍ×２５ｍｍの面積で研磨したＳＵＳ３０
４鋼板に圧着した後、１ｋｇ荷重で６０℃環境下保持
し、試料がＳＵＳ鋼板から落下するまでの時間を測定し
た。(2) Holding force SUS30 obtained by polishing a sample in an area of 25 mm × 25 mm
After being press-bonded to the four steel plates, the temperature was maintained at 60 ° C. under a load of 1 kg, and the time until the sample dropped from the SUS steel plate was measured.
【００４９】（３）再剥離性 試料をＰＥＴフィルムに貼付け６０℃に２週間放置後、
常温に１時間放置し、手めくりでラベルを引剥がした時
の状況を目視検査し、以下の基準で○、△、×の評価を
した。 ○：剥離抵抗が小さく、なめらかに糊残りなく再剥離で
きる。 △：糊残りはないが、ジッピングを起こしてなめらかに
再剥離できない。 ×：剥離抵抗が大きく、糊残りがあり再剥離適性は低
い。(3) Removability After the sample was stuck on a PET film and left at 60 ° C. for 2 weeks,
It was left at room temperature for 1 hour, and the situation when the label was peeled off by hand was visually inspected, and the evaluation of ○, Δ, and × was made according to the following criteria. ：: Peeling resistance is small, and re-peeling can be performed smoothly without adhesive residue. Δ: No adhesive residue, but zipping occurred and smooth re-peeling was not possible. ×: Peeling resistance is large, adhesive residue remains, and removability is low.
【００５０】（４）保存性 片面にアルミ蒸着処理を施した厚さ５０μｍのポリエチ
レンフィルムと厚さ１２μｍのＰＥＴフィルムを、アル
ミ蒸着層を内側として、ドライラミネート法により積層
フィルム化した。この積層フィルム２枚（内１枚は予め
ウェットティシュ取出しのための開口を設けたもの）を
ポリエチレン面を内側にして重ね、ヒートシールにより
その３辺を閉じ、袋状の本体とした。次いで、この袋状
本体の中に、市販の不織布にエチルアルコール／水＝５
０／５０からなる薬液をしみこませたウェットティシュ
８０枚を充填した。その後、残りの一辺もヒートシール
により閉じた。さらに、上記各試料（粘着シート）を、
この袋状本体の開口に貼着することによりウェットティ
シュを密封した。これを６０℃の環境で２週間保存し、
保存前後の内容物量変化（液漏れ、揮発）と保存後のラ
ベル浮き剥がれの有無の目視検査をし、以下の基準で
○、△、×の評価をした。 ○：内容物量変化も、粘着シートの浮き剥がれもなし。 △：内容物量変化、及び／又は粘着シートの浮き剥がれ
が若干見られる。 ×：内容物量変化、及び／又は粘着シートの浮き剥がれ
がある。(4) Preservation A polyethylene film having a thickness of 50 μm and a PET film having a thickness of 12 μm on which one side was subjected to aluminum vapor deposition was formed into a laminated film by a dry lamination method with the aluminum vapor deposited layer as an inner side. Two laminated films (one of which was provided with an opening for taking out a wet tissue in advance) were stacked with the polyethylene surface inside, and three sides were closed by heat sealing to form a bag-shaped body. Then, in this bag-shaped body, a commercially available non-woven fabric was added with ethyl alcohol / water = 5.
80 sheets of wet tissue impregnated with a chemical solution of 0/50 were filled. Thereafter, the other side was closed by heat sealing. Furthermore, each of the above samples (adhesive sheet)
The wet tissue was sealed by sticking to the opening of the bag-shaped body. Store this in a 60 ° C environment for 2 weeks,
Changes in the amount of contents (leakage and volatilization) before and after storage and visual inspection of the presence or absence of peeling-off of the label after storage were evaluated. ：: No change in the amount of the contents and no peeling of the adhesive sheet. Δ: Changes in the amount of contents and / or slight peeling of the pressure-sensitive adhesive sheet are observed. ×: There is a change in the content amount and / or the adhesive sheet is peeled off.
【００５１】（評価結果）評価結果を表１に示す。表１
に示すように、トリメリット酸エステル系可塑剤と、ポ
リエステル系可塑剤の双方を用いた試料１、２では、再
剥離性、保存性の双方について、良好な結果が得られ
た。一方、ポリエステル系可塑剤のみを用いた試料３で
は、保存性は良好であったものの、再剥離性に劣る結果
であった。また、トリメリット酸エステル系可塑剤のみ
を用いた試料４では、再剥離性は良好であったものの、
保存性が、試料１、２と比較して若干劣っていた。ま
た、フタル酸エステル系可塑剤を用いた試料５は、加熱
処理前には優れた再剥離性が得られるものの、６０℃に
２週間の加熱処理後の再剥離性及び保存性は、共に良い
結果が得られなかった。これは、粘着剤がエタノールに
侵されたためと考えられる。また、試料６では、エタノ
ールに侵されやすい可塑剤を全く使用しないので、保存
性は良好であったが、再剥離性に劣っていた。また、ト
リメリット酸エステル系可塑剤と、ポリエステル系可塑
剤の双方を用いていても、試料７のように、粘着力が大
きくなりすぎると共に、充分な保持力が得られないと、
再剥離性や保存性に問題が生じた。また、試料８のよう
に、粘着力が小さくなりすぎると、保存性の評価項目に
問題が生じた。また、試料９のように、耐水性、耐溶剤
性を有しない基材を用いたところ、基材がエタノールに
侵されることにより、保存性に問題が生じた。(Evaluation Results) The evaluation results are shown in Table 1. Table 1
As shown in Table 2, in Samples 1 and 2 using both the trimellitic acid ester-based plasticizer and the polyester-based plasticizer, good results were obtained with respect to both removability and storage stability. On the other hand, Sample 3 using only the polyester-based plasticizer had good storage stability, but poor removability. In sample 4 using only the trimellitate plasticizer, although the removability was good,
The storage stability was slightly inferior to Samples 1 and 2. Sample 5 using a phthalate-based plasticizer had excellent removability before heat treatment, but both removability and storage stability after heat treatment at 60 ° C. for two weeks were good. No results were obtained. This is probably because the adhesive was attacked by ethanol. Further, in Sample 6, since no plasticizer which is easily attacked by ethanol was used at all, the preservability was good, but the removability was poor. Further, even when both of the trimellitate-based plasticizer and the polyester-based plasticizer are used, as in the case of Sample 7, the adhesive strength becomes too large and sufficient holding power cannot be obtained.
Problems occurred in removability and storage stability. Further, when the adhesive strength was too small as in Sample 8, a problem occurred in the evaluation items of the storage stability. In addition, when a substrate having no water resistance and no solvent resistance was used as in Sample 9, there was a problem in storage stability due to the substrate being attacked by ethanol.
【００５２】[0052]
【表１】 [Table 1]
【００５３】[0053]
【発明の効果】以上説明したとおり、本発明の粘着シー
トは、ウェットティシュの蓋用として使用すると、袋状
本体からの良好な再剥離性と再貼り付け性を備えると共
に、エタノールを含む薬液に触れても、経時的に粘着剤
が膨潤することなく、長期間気密性を維持できる。ま
た、本発明の包装材及び包装製品によれば、エタノール
を含有する薬液を用いたウェットティッシュを容易に取
り出せると共に、長期間安定して収納保存できる。As described above, when the pressure-sensitive adhesive sheet of the present invention is used for a lid of a wet tissue, the pressure-sensitive adhesive sheet has good removability and re-adhesiveness from a bag-shaped main body, and can be used for a chemical solution containing ethanol. Even if touched, the pressure-sensitive adhesive does not swell with time and can maintain airtightness for a long time. Further, according to the packaging material and the packaging product of the present invention, a wet tissue using a chemical solution containing ethanol can be easily taken out, and can be stably stored and stored for a long period of time.
【図面の簡単な説明】[Brief description of the drawings]
【図１】 本発明の第１実施形態に係る粘着シートの
断面図である。FIG. 1 is a sectional view of a pressure-sensitive adhesive sheet according to a first embodiment of the present invention.
【図２】 本発明の第２実施形態に係る粘着シートの
断面図である。FIG. 2 is a sectional view of a pressure-sensitive adhesive sheet according to a second embodiment of the present invention.
【図３】 本発明の第３実施形態に係るウエットティ
ッシュ包装製品の斜視図である。FIG. 3 is a perspective view of a wet tissue packaged product according to a third embodiment of the present invention.
１…基材、２…粘着剤層、３…剥離シート、１０…粘着
シート、２０…袋状本体、３０…ウェットティッシュDESCRIPTION OF SYMBOLS 1 ... Base material 2 ... Adhesive layer 3 ... Release sheet 10 ... Adhesive sheet 20 ... Bag-shaped main body 30 ... Wet tissue
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０９Ｊ 9/00 Ｃ０９Ｊ 9/00 201/00 201/00 Ｆターム(参考） 3E014 LB08 3E067 AA12 AB77 AC01 AC14 BA12A BB12A BB14A BB15A BB25A EA23 EA32 EB17 FA01 FC01 GD10 3E086 AD24 BA04 BA15 BA40 BB90 CA40 4J004 AA04 AA05 AA10 AA17 AB01 CA04 CA05 CA06 CA07 CA08 CB01 CB02 CC02 CC03 DA01 DA04 DB01 DB02 FA06 4J040 CA001 CA011 DF011 DF031 DF041 GA05 GA07 GA11 HB34 HD30 JA09 KA16 KA31 LA07 NA02 NA06 PA23 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (reference) C09J 9/00 C09J 9/00 201/00 201/00 F term (reference) 3E014 LB08 3E067 AA12 AB77 AC01 AC14 BA12A BB12A BB14A BB15A BB25A EA23 EA32 EB17 FA01 FC01 GD10 3E086 AD24 BA04 BA15 BA40 BB90 CA40 4J004 AA04 AA05 AA10 AA17 AB01 CA04 CA05 CA06 CA07 CA08 CB01 CB02 CC02 CC03 DA01 DA04 DB01 DB01 FA04 KA31 LA07 NA02 NA06 PA23
Claims (6)
てなる粘着シートにおいて、前記粘着剤層が可塑剤とし
てトリメリット酸エステル系可塑剤及びポリエステル系
可塑剤を含む粘着剤からなることを特徴とする粘着シー
ト。1. A pressure-sensitive adhesive sheet in which a pressure-sensitive adhesive layer is laminated on one surface of a sheet-like base material, wherein the pressure-sensitive adhesive layer comprises a pressure-sensitive adhesive containing a trimellitate-based plasticizer and a polyester-based plasticizer as a plasticizer. An adhesive sheet characterized by the above-mentioned.
対するＪＩＳ Ｚ０２３７に準拠する１８０度粘着力が
２００〜６００ｇｆ／２５ｍｍであることを特徴とする
請求項１に記載の粘着シート。2. The pressure-sensitive adhesive sheet according to claim 1, wherein the pressure-sensitive adhesive layer has a 180-degree pressure of 200 to 600 gf / 25 mm based on JIS Z0237 with respect to the polyethylene film.
拠する６０℃保持力が８時間以上であることを特徴とす
る請求項１又は請求項２に記載の粘着シート。3. The pressure-sensitive adhesive sheet according to claim 1, wherein the pressure-sensitive adhesive layer has a holding power at 60 ° C. in accordance with JIS Z0237 of 8 hours or more.
層および剥離シートを順次積層したことを特徴とする請
求項１から請求項３の何れかに記載の粘着シート。4. The pressure-sensitive adhesive sheet according to claim 1, wherein the pressure-sensitive adhesive layer and the release sheet are sequentially laminated on one surface of the sheet-like base material.
口を覆う蓋体とを備える包装材であって、前記蓋体の少
なくとも一部が、請求項１から請求項３の何れかに記載
の粘着シートからなることを特徴とする包装材。5. A packaging material comprising a bag-shaped main body having an opening in a part thereof and a lid covering the opening, wherein at least a part of the lid is any one of claims 1 to 3. A packaging material, comprising the pressure-sensitive adhesive sheet according to item 1.
内部に収納されたウェットティッシュとからなり、前記
ウェットティッシュは、吸収基材にエタノールを含む薬
液を含浸させてなることを特徴とするウェットティッシ
ュの包装製品。6. The packaging material according to claim 5, comprising a wet tissue stored inside the packaging material, wherein the wet tissue is formed by impregnating an absorbent substrate with a chemical solution containing ethanol. Characterized wet tissue packaging products.