JP2002301694A - Metal foil compound sheet for boring and drill boring method - Google Patents
Metal foil compound sheet for boring and drill boring methodInfo
- Publication number
- JP2002301694A JP2002301694A JP2001107063A JP2001107063A JP2002301694A JP 2002301694 A JP2002301694 A JP 2002301694A JP 2001107063 A JP2001107063 A JP 2001107063A JP 2001107063 A JP2001107063 A JP 2001107063A JP 2002301694 A JP2002301694 A JP 2002301694A
- Authority
- JP
- Japan
- Prior art keywords
- metal foil
- composite sheet
- water
- boring
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、プリント配線材料
分野で使用される孔明け用金属箔複合シートに関するも
のであり、高品質の孔明けを可能とする孔明け加工法に
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a metal foil composite sheet for perforation used in the field of printed wiring materials, and to a perforation processing method capable of perforating high quality.
【０００２】[0002]
【従来の技術】プリント配線材料に、表裏導通用のドリ
ル孔明けを行う際、該プリント配線材料の片面或いは両
面に水溶性滑剤、具体的にはジエチレングリコールやジ
プロピレングリコールなどのグルコール類と脂肪酸など
の剛性ワックス、非イオン系界面活性剤との混合物を、
紙などに含浸したシートを配置して行う方法が、ＵＳＰ
-4781495、4929370に開示されているが、これらの方法
は、ドリル発熱防止効果が不十分であったり、多孔質シ
ートへのこれら混合物の含浸性が劣ったり、さらにベタ
つく等の欠点があった。2. Description of the Related Art When a printed wiring material is drilled for conduction from front to back, a water-soluble lubricant, specifically, a glycol such as diethylene glycol or dipropylene glycol, and a fatty acid are provided on one or both surfaces of the printed wiring material. A mixture of rigid wax, nonionic surfactant and
USP is a method of arranging sheets impregnated in paper etc.
Although these methods are disclosed in US Pat. No. 4,478,495 and 4,929,370, these methods have drawbacks such as insufficient drill heat prevention effect, poor impregnation of the porous sheet with these mixtures, and stickiness.
【０００３】これらの解決手法として、特開平6-344297
に、ポリエーテルエステルと水溶性滑剤からなるシート
を使用した孔明け加工法が提案されているが、該加工法
では、ドリル孔の品質向上やベタつきの改善は認められ
るものの、使用するドリルビット径が小さくなるに従
い、孔位置精度が低下する傾向が見られ、極小径ドリル
用途への適用には改善が必要であった。As a solution to these problems, Japanese Patent Application Laid-Open No. Hei 6-344297
A drilling method using a sheet made of a polyetherester and a water-soluble lubricant has been proposed. In this processing method, although improvement in drill hole quality and improvement in stickiness are recognized, the drill bit diameter to be used is improved. As the diameter became smaller, the hole position accuracy tended to decrease, and improvement was required for application to ultra-small diameter drills.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、孔形状に優
れ、かつ０.３ｍｍφ以下のドリルビットの孔明け加工
においても、孔位置精度が良好な孔明け用金属箔複合シ
ート、並びに該孔明け用金属箔複合シートを使用する、
高品質のドリル孔明け法を提供するものである。DISCLOSURE OF THE INVENTION The present invention relates to a metal foil composite sheet for drilling which is excellent in hole shape and has good hole positioning accuracy even in drilling a drill bit having a diameter of 0.3 mm or less. Using a metal foil composite sheet for dawn,
It provides a high quality drilling method.
【０００５】[0005]
【課題を解決するための手段】本発明者らは、水溶性ポ
リマー層と特定のアルミニウム純度のアルミニウム箔か
らなる孔明け用金属箔複合シートを使用することによ
り、良好な孔形状と優れた孔位置精度が得られることを
見出し、本発明を完成するに至った。Means for Solving the Problems The present inventors use a metal foil composite sheet for piercing comprising a water-soluble polymer layer and an aluminum foil having a specific aluminum purity to obtain a good hole shape and an excellent hole. The inventors have found that positional accuracy can be obtained, and have completed the present invention.
【０００６】即ち、本発明は、金属箔の片面に、有機物
層を形成した孔明け用金属箔複合シートにおいて、該有
機物層が、水溶性ポリマーからなる厚さ０.０２〜１.０
ｍｍの層であり、該金属箔が、アルミニウム純度が９
９.５％以上のアルミニウム箔であることを特徴とする
プリント配線材料用の孔明け用金属箔複合シートであ
り、該孔明け用金属箔複合シートの金属箔面側を、プリ
ント配線材料に接して配置し、シート面側からドリル孔
明けをすることを特徴とするプリント配線材料の孔明け
加工法である。That is, the present invention relates to a metal foil composite sheet for punching having an organic material layer formed on one surface of a metal foil, wherein the organic material layer has a thickness of 0.02 to 1.0 made of a water-soluble polymer.
mm, and the metal foil has an aluminum purity of 9
What is claimed is: 1. A metal foil composite sheet for punching for printed wiring material, comprising at least 9.5% of aluminum foil, wherein the metal foil side of the metal foil composite sheet for punching is in contact with the printed wiring material. This is a method for drilling a printed wiring material, wherein the drilling is performed from the sheet surface side.
【０００７】[0007]
【発明の実施の形態】本発明において使用される水溶性
ポリマーとは、常温、常圧において、水１００ｇに対
し、１ｇ以上溶解する高分子化合物であれば、特に限定
されるものではない。代表的なものとしては、ポリエチ
レンオキサイド系、ポリプロピレンオキサイド系、ポリ
ビニールアルコール系、ポリアクリル酸系、ポリアクリ
ルアミド系、ポリビニルピロリドン系、カルボキシメチ
ルセルロース系、ポリテトラメチレングリコール系、脂
肪酸エステル系などが例示され、１種もしくは２種以上
を適宜混合して使用することも可能である。水溶性ポリ
マーの融点または軟化点は、３０〜２００℃ の範囲の
ものが選択され、好ましくは４０〜１５０℃の範囲のも
のが使用される。BEST MODE FOR CARRYING OUT THE INVENTION The water-soluble polymer used in the present invention is not particularly limited as long as it is a polymer compound which dissolves at least 1 g in 100 g of water at normal temperature and normal pressure. Representative examples include polyethylene oxide, polypropylene oxide, polyvinyl alcohol, polyacrylic acid, polyacrylamide, polyvinylpyrrolidone, carboxymethylcellulose, polytetramethylene glycol, and fatty acid ester. It is also possible to use one kind or two or more kinds as appropriate. The melting point or softening point of the water-soluble polymer is selected in the range of 30 to 200 ° C, preferably in the range of 40 to 150 ° C.
【０００８】本発明の好ましい態様であるポリエーテル
エステル（Ａ）とは、ポリアルキレンオキシドのエステ
ル化物であれば、特に限定されるものではない。 代表
的な例としては、ポリエチレングリコール、ポリエチレ
ンオキサイド、ポリプロピレングリコール、ポリテトラ
メチレングリコール、ポリプロピレンオキサイドやこれ
らの共重合物で例示されるグリコール類、またはエチレ
ンオキサイド類の重合物と、フタル酸、イソフタル酸、
テレフタル酸、セバシン酸等、及びそれらのジメチルエ
ステル、ジエチルエステル等、ピロメリット酸無水物等
で例示される多価カルボン酸、その無水物、またはその
エステルとを反応させて得られる樹脂などが挙げられ、
１種もしくは２種以上を適宜混合して使用することも可
能である。また、ポリエーテルエステル（Ａ）に、数平
均分子量１００００以上のポリエチレンオキサイドを混
合して使用することも可能である。The polyetherester (A), which is a preferred embodiment of the present invention, is not particularly limited as long as it is a polyalkylene oxide esterified product. Representative examples include polyethylene glycol, polyethylene oxide, polypropylene glycol, polytetramethylene glycol, glycols exemplified by polypropylene oxide and their copolymers, or polymers of ethylene oxides, and phthalic acid, isophthalic acid ,
Terephthalic acid, sebacic acid and the like, and their dimethyl esters, diethyl esters and the like, polycarboxylic acids exemplified by pyromellitic anhydride, etc., their anhydrides, and resins obtained by reacting with esters thereof, and the like. And
It is also possible to use one kind or two or more kinds by appropriately mixing. It is also possible to use a mixture of polyetherester (A) and polyethylene oxide having a number average molecular weight of 10,000 or more.
【０００９】ポリエーテルエステル（Ａ）の配合量は、
ポリエーテルエステル（Ａ）と後述の水溶性滑剤
（Ｂ）の配合量の合計１００重量部に対し、２０〜９０
重量部の範囲であり、２０重量部未満では、シートの強
度が不足し、９０重量部を超えると湿潤性が不十分で、
本発明の目的に適しない。The amount of the polyetherester (A) is
Polyetherester (A) and water-soluble lubricant described below
20 to 90 with respect to a total of 100 parts by weight of the compounding amount of (B).
If the amount is less than 20 parts by weight, the strength of the sheet is insufficient, and if it exceeds 90 parts by weight, the wettability is insufficient.
Not suitable for the purpose of the present invention.
【００１０】本発明の好適な態様である水溶性滑剤
（Ｂ）とは、具体的には、数平均分子量１０００〜９０
００のポリエチレングリコール；ポリオキシエチレンオ
レイルエーテル、ポリオキシエチレンセチルエーテル、
ポリオキシエチレンステアリルエーテル、ポリオキシエ
チレンラウリルエーテル、ポリオキシエチレンノニルフ
ェニルエーテル、ポリオキシエチレンオクチルフェニル
エーテルなどで例示されるポリオキシエチレンのモノエ
ーテル類；ポリオキシエチレンモノステアレート、ポリ
オキシエチレンソルビタンモノステアレート；ヘキサグ
リセリンモノステアレート、デカヘキサグリセリンモノ
ステアレートなどで例示されるポリグリセリンモノステ
アレート類；ポリオキシエチレンプロピレンブロックポ
リマーが挙げられ、１種もしくは２種以上を適宜混合し
て使用することも可能である。水溶性滑剤（Ｂ）の配合
量は、ポリエーテルエステル（Ａ）と水溶性滑剤
（Ｂ）の配合量の合計１００重量部に対し、１０〜８０
重量部の範囲であり、１０重量部未満では粘度が高くな
りすぎ、８０重量部を超えるとシートが脆くなり、好ま
しくない。A water-soluble lubricant according to a preferred embodiment of the present invention.
(B) is, specifically, a number average molecular weight of 1,000 to 90.
00 polyethylene glycol; polyoxyethylene oleyl ether, polyoxyethylene cetyl ether,
Polyoxyethylene monoethers exemplified by polyoxyethylene stearyl ether, polyoxyethylene lauryl ether, polyoxyethylene nonylphenyl ether, polyoxyethylene octyl phenyl ether; polyoxyethylene monostearate, polyoxyethylene sorbitan mono Stearates; polyglycerin monostearates exemplified by hexaglycerin monostearate, decahexaglycerin monostearate, and the like; polyoxyethylene propylene block polymers, and one or more kinds are appropriately mixed and used. It is also possible. The compounding amount of the water-soluble lubricant (B) is the amount of the polyetherester (A) and the water-soluble lubricant.
10 to 80 with respect to 100 parts by weight of the total amount of (B)
If it is less than 10 parts by weight, the viscosity becomes too high, and if it exceeds 80 parts by weight, the sheet becomes brittle, which is not preferable.
【００１１】本発明において使用される金属箔は、アル
ミニウム純度が９９.５％以上のアルミニウム箔であれ
ば、特に制約はないが、純度が９９.７％以上のアルミ
ニウム箔が、より好適である。高純度のアルミニウム箔
を使うことで、ドリルビットの衝撃の緩和や食いつき性
が向上し、水溶性ポリマーによるドリルビットの摩擦熱
による発熱の軽減効果と相俟って、ドリル孔明け時の位
置精度と孔品質の大幅向上が可能となった。アルミニウ
ム箔の具体的な種類としては、ＪＩＳ Ｈ−４１６０に
規定される、１０５０，１０７０、１０８５などが例示
され、特に１０７０、１０８５などがより好ましい。ア
ルミニウム箔の厚さとしては、５０〜５００μｍの範囲
であり、５０μｍ未満では基板のバリが発生し易く、５
００μｍを超えると、発生する切り粉の排出が困難にな
り、好ましくない。The metal foil used in the present invention is not particularly limited as long as it has an aluminum purity of 99.5% or more, but an aluminum foil having a purity of 99.7% or more is more preferable. . The use of high-purity aluminum foil reduces the impact and biting of the drill bit, and the water-soluble polymer reduces the heat generated by the frictional heat of the drill bit, resulting in positional accuracy when drilling. And the hole quality can be greatly improved. Specific types of aluminum foil include, for example, 1050, 1070, 1085 and the like defined in JIS H-4160, and particularly preferably 1070, 1085 and the like. The thickness of the aluminum foil is in the range of 50 to 500 μm.
If it exceeds 00 μm, it becomes difficult to discharge the generated cutting powder, which is not preferable.
【００１２】孔明け用金属箔複合シートの製造方法とし
ては、工業的に使用される公知の方法であれば、特に制
約はされない。具体的には、水溶性ポリマーをロールや
ニーダー、またはその他の混錬手段を使用し、適宜加温
或いは加熱して、好適には粘度５万〜２０万センチポイ
ズ（１５０℃）程度の均一な混合物とし、ロール法やカ
ーテンコート法などで、金属箔上に塗布層を形成する方
法；該混合物をプレスやロール、またはＴ−ダイ押出機
等を使用し、予め所望の厚さのシートに成形し、これを
アルミニウム箔に重ね、プレスやロール等で加熱・加圧
し、必要に応じて接着剤等により、接着する方法が例示
される。The method for producing the metal foil composite sheet for perforation is not particularly limited as long as it is a known method used industrially. Specifically, a water-soluble polymer is heated or heated appropriately using a roll, a kneader, or other kneading means, and is preferably a uniform mixture having a viscosity of about 50,000 to 200,000 centipoise (150 ° C.). And forming a coating layer on a metal foil by a roll method or a curtain coating method; forming the mixture into a sheet having a desired thickness in advance by using a press, a roll, or a T-die extruder. A method of stacking this on an aluminum foil, heating and pressing with a press or a roll, and bonding with an adhesive or the like as necessary is exemplified.
【００１３】孔明け用金属箔複合シートの、シートの厚
さは、０.０２〜１.０ｍｍの範囲であり、０.０２ｍｍ
未満では、得られる孔品質が低下し、１.０ｍｍを超え
るとドリルビットへの巻き付きが起こり、好ましくないThe sheet thickness of the metal foil composite sheet for piercing is in the range of 0.02 to 1.0 mm, and is 0.02 mm.
If it is less than 1, the quality of the obtained hole is reduced, and if it exceeds 1.0 mm, winding around the drill bit occurs, which is not preferable
【００１４】本発明の孔明け加工法は、該孔明け用金属
箔複合シートをプリント配線材料、例えば銅張積層板、
多層板などの最上面に、該孔明け用金属箔複合シートの
金属箔面側が、プリント配線材料に接するように配置
し、該孔明け用金属箔複合シートのシート面側から、ド
リル孔明けを行うものである。[0014] In the perforation processing method of the present invention, the perforated metal foil composite sheet is printed with a printed wiring material such as a copper-clad laminate,
On the uppermost surface of a multilayer board or the like, the metal foil surface side of the metal foil composite sheet for perforation is disposed so as to be in contact with a printed wiring material, and drilling is performed from the sheet surface side of the metal foil composite sheet for perforation. Is what you do.
【００１５】[0015]
【実施例】実施例１ ポリエチレングリコール・ジメチルテレフタレート重縮
合物（商品名：パオゲンＰＰ−１５、第一工業製薬製）
５０重量部、ポリオキシエチレンモノステアレート（商
品名：ノニオンＳ−４０、日本油脂製）５０重量部を、
ニーダーを使用し、温度１５０℃の窒素雰囲気中で混錬
した後、押出機にて、厚さ０.１ｍｍの水溶性ポリマー
シートを作成した。この水溶性ポリマーシートを、厚さ
１００μｍのアルミニウム箔（材質：１０７０、アルミ
ニウム純度：９９.７％）の片面に重ね、加熱ロールを
使用して接着させ、孔明け用アルミニウム箔複合シート
を得た。得られた孔明け用アルミニウム箔複合シート
を、厚さ０.１ｍｍのガラスエポキシ板を３枚重ねた上
面に配置し、下面に当て板（紙フェノール積層板）を配
置し、ドリルビット：０.１ｍｍφ、回転数：１５００
００ｒｐｍ、送り速度：２.５μ／ｒｅｖ．の条件で２
０００ヒットのドリル孔明け加工を行い、孔評価を行っ
た結果を表１に示した。Example 1 Polycondensate of polyethylene glycol / dimethyl terephthalate (trade name: Paogen PP-15, manufactured by Daiichi Kogyo Seiyaku)
50 parts by weight of polyoxyethylene monostearate (trade name: Nonion S-40, manufactured by NOF Corporation)
After kneading in a nitrogen atmosphere at a temperature of 150 ° C. using a kneader, a water-soluble polymer sheet having a thickness of 0.1 mm was prepared with an extruder. This water-soluble polymer sheet was overlaid on one side of a 100 μm-thick aluminum foil (material: 1070, aluminum purity: 99.7%) and bonded using a heating roll to obtain an aluminum foil composite sheet for punching. . The obtained aluminum foil composite sheet for piercing is placed on the upper surface of three stacked glass epoxy plates having a thickness of 0.1 mm, and a backing plate (paper phenol laminate) is placed on the lower surface. 1mmφ, number of rotations: 1500
00 rpm, feed rate: 2.5 μ / rev. 2 under the condition
Table 1 shows the results of drilling for 000 hits and evaluating the holes.
【００１６】実施例２ ポリエチレングリコール・ジメチルテレフタレート重縮
合物（商品名：パオゲンＰＰ−１５）７０重量部、数平
均分子量８０００のポリエチレングリコール３０重量部
を使用し、実施例１と同様にして、厚さ０.１ｍｍの水
溶性ポリマーシートを作成した。この水溶性ポリマーシ
ートを、厚さ１００μmのアルミニウム箔（材質：１０
８５、アルミニウム純度：９９.８５％）の片面に重
ね、加熱ロールを使用して接着させ、孔明け用アルミニ
ウム箔複合シートを得た。得られた孔明け用アルミニウ
ム箔複合シートを実施例１と同様にして、孔評価を行っ
た結果を表１に示した。Example 2 A polycondensate of polyethylene glycol / dimethyl terephthalate (trade name: Paogen PP-15) (70 parts by weight) and 30 parts by weight of polyethylene glycol having a number average molecular weight of 8000 were used. A water-soluble polymer sheet having a thickness of 0.1 mm was prepared. This water-soluble polymer sheet is coated with a 100 μm-thick aluminum foil (material: 10
(85, aluminum purity: 99.85%) and bonded using a heating roll to obtain an aluminum foil composite sheet for punching. The obtained aluminum foil composite sheet for perforation was subjected to hole evaluation in the same manner as in Example 1, and the results are shown in Table 1.
【００１７】実施例３ ポリエチレングリコール・ジメチルテレフタレート重縮
合物（商品名：パオゲンＰＰ−１５）２０重量部、ポリ
エチレンオキサイド（商品名：アルコックスＲ−１５
０、明成化学製）１０重量部、ポリオキシエチレンプロ
ピレンブロックポリマー（商品名：プロノン２０８、日
本油脂製） ７０重量部を使用し、実施例１と同様にし
て、孔明け用アルミニウム箔複合シートを得た。得られ
た孔明け用アルミニウム箔複合シートを実施例１と同様
にして、孔評価を行った結果を表１に示した。Example 3 Polyethylene glycol dimethyl terephthalate polycondensate (trade name: Paogen PP-15) 20 parts by weight, polyethylene oxide (trade name: Alcox R-15)
0, 10 parts by weight of Meisei Chemical Co., Ltd.) and 70 parts by weight of polyoxyethylene propylene block polymer (trade name: PRONON 208, manufactured by NOF CORPORATION). Obtained. The obtained aluminum foil composite sheet for perforation was subjected to hole evaluation in the same manner as in Example 1, and the results are shown in Table 1.
【００１８】比較例１ 実施例１で得られた水溶性ポリマーシートを、厚さ１０
０μｍのアルミニウム箔（材質：ＩＮ３０、アルミニウ
ム純度：９９.３％）の片面に重ね、加熱ロールを使用
して接着させ、孔明け用アルミニウム箔複合シートを得
た。得られた孔明け用アルミニウム箔複合シートを実施
例１と同様にして、孔評価を行った結果を表１に示し
た。Comparative Example 1 The water-soluble polymer sheet obtained in Example 1
One side of a 0 μm aluminum foil (material: IN30, aluminum purity: 99.3%) was overlaid and bonded using a heating roll to obtain an aluminum foil composite sheet for punching. The obtained aluminum foil composite sheet for perforation was subjected to hole evaluation in the same manner as in Example 1, and the results are shown in Table 1.
【００１９】比較例２ 孔明け用アルミニウム箔複合シートの替わりに、厚さ１
５０μｍのアルミニウム箔（材質：ＩＮ３０）を使用
し、他は実施例１と同様のドリル孔明け条件で、孔明け
加工を行った結果、途中で、ドリルビットの折れが発
生、再度試みたが、同様であった。Comparative Example 2 Instead of the aluminum foil composite sheet for perforation, a thickness of 1
Using a 50 μm aluminum foil (material: IN30) and performing drilling under the same drilling conditions as in Example 1, the drill bit was broken on the way. It was similar.
【００２０】[0020]
【表１】 [Table 1]
【００２１】（試験方法） ・孔壁粗さ ：サンプルをメッキ処理後、顕微鏡で断面
観察を行い、孔壁の粗さを測定した値の平均値と最大値
（２０００ヒット後、２０孔）。 ・孔位置精度：２０００ヒットについて、孔位置基準値
と、孔加工後の下板の孔位置とのずれ量を座標測定機で
測定した値の平均値と最大値。(Test method)-Hole wall roughness: After plating the sample, the cross section was observed with a microscope, and the average and maximum values of the measured values of the hole wall roughness (20 holes after 2000 hits). Hole position accuracy: For 2000 hits, the average value and the maximum value of values obtained by measuring the amount of deviation between the hole position reference value and the hole position of the lower plate after hole processing with a coordinate measuring machine.
【００２２】[0022]
【発明の効果】本発明の孔明け用金属箔複合シートを用
いた孔明け加工法は、水溶性ポリマーによる孔明け時の
ドリルビット摩擦熱の軽減効果と、高純度のアルミニウ
ム箔による孔明け時の衝撃緩和やドリルビットの食いつ
き性の向上によって、孔形状や孔位置精度に優れる高品
質の孔明け加工が可能となり、工業的な実用性は極めて
高いものである。The drilling method using the metal foil composite sheet for drilling of the present invention is effective in reducing the frictional heat of a drill bit when drilling with a water-soluble polymer, and reducing the frictional heat when drilling with a high-purity aluminum foil. By reducing the impact of the drill and improving the bitability of the drill bit, high-quality drilling with excellent hole shape and hole position accuracy becomes possible, and industrial practicality is extremely high.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｈ０５Ｋ 3/00 Ｈ０５Ｋ 3/00 Ｋ (72)発明者 永井 憲 東京都葛飾区新宿６丁目１番１号 三菱瓦 斯化学株式会社東京工場内 Ｆターム(参考） 3C060 AA11 BA05 BG01 BH01 4F100 AB01A AB10A AB33A AG00 AK01B AK41B AK53 AK54B AL01B AL05B BA02 CA19 EC03 EC032 EH17 EH172 EJ42 EJ422 GB43 JA07B JB09B JL01 YY00A YY00B 4J002 CH01X CH02W CH02X CH02Y FD17X GQ01 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) H05K 3/00 H05K 3/00 K (72) Inventor Ken Nagai 6-1-1-1 Shinjuku, Katsushika-ku, Tokyo F-term in the Tokyo Plant of Mitsubishi Gas Chemical Co., Ltd. (reference) 3C060 AA11 BA05 BG01 BH01 4F100 AB01A AB10A AB33A AG00 AK01B AK41B AK53 AK54B AL01B AL05B BA02 CA19 EC03 EC032 EH17 EH172 EJ42 EJ422 GB43 GQ01
Claims (5)
明け用金属箔複合シートにおいて、該有機物層が、水溶
性ポリマーからなる厚さ０.０２〜１.０ｍｍの層であ
り、該金属箔が、アルミニウム純度が９９.５％以上の
アルミニウム箔であることを特徴とするプリント配線材
料用の孔明け用金属箔複合シート。1. A metal foil composite sheet for punching having an organic material layer formed on one surface of a metal foil, wherein the organic material layer is a layer of a water-soluble polymer having a thickness of 0.02 to 1.0 mm. A metal foil composite sheet for punching printed wiring materials, wherein the metal foil is an aluminum foil having an aluminum purity of 99.5% or more.
テル（Ａ）２０〜９０重量部と、水溶性滑剤（Ｂ）１０
〜８０重量部を必須成分とする組成物であることを特徴
とする請求項１記載の孔明け用金属箔複合シート。2. The water-soluble polymer comprises 20 to 90 parts by weight of a polyetherester (A) and 10 parts by weight of a water-soluble lubricant (B).
The metal foil composite sheet for perforation according to claim 1, which is a composition containing -80 parts by weight as an essential component.
均分子量１００００以上のポリエチレンオキサイドを混
合することを特徴とする請求項２記載の孔明け用金属箔
複合シート。3. The metal foil composite sheet according to claim 2, wherein polyethylene oxide having a number average molecular weight of 10,000 or more is mixed with the polyetherester (A).
０００〜９０００のポリエチレングリコール、ポリオキ
シエチレンのモノエーテル、ポリオキシエチレンのエス
テル、ポリオキシエチレンソルビタンモノステアレー
ト、ポリグリセリンモノステアレート、ポリオキシエチ
レンプロピレンブロックポリマーからなる群から選択さ
れた1種もしくは２種以上であることを特徴とする請求
項２記載の孔明け用金属箔複合シート。4. The water-soluble lubricant (B) has a number average molecular weight of 1
000-9000 polyethylene glycol, polyoxyethylene monoether, polyoxyethylene ester, polyoxyethylene sorbitan monostearate, polyglycerin monostearate, one selected from the group consisting of polyoxyethylene propylene block polymer or The metal foil composite sheet for perforation according to claim 2, wherein the composite sheet is two or more types.
用金属箔複合シートの金属箔面側を、プリント配線材料
に接して配置し、シート面側からドリル孔明けをするこ
とを特徴とするプリント配線材料の孔明け加工法。5. The method according to claim 1, wherein the metal foil surface side of the metal foil composite sheet for punching according to claim 1 is arranged in contact with a printed wiring material, and drilling is performed from the sheet surface side. Drilling method for printed wiring materials.