JP2002293010A - Ink jet recording sheet and manufacturing method therefor - Google Patents
Ink jet recording sheet and manufacturing method thereforInfo
- Publication number
- JP2002293010A JP2002293010A JP2001095902A JP2001095902A JP2002293010A JP 2002293010 A JP2002293010 A JP 2002293010A JP 2001095902 A JP2001095902 A JP 2001095902A JP 2001095902 A JP2001095902 A JP 2001095902A JP 2002293010 A JP2002293010 A JP 2002293010A
- Authority
- JP
- Japan
- Prior art keywords
- parts
- ink
- coating
- pigment
- jet recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は基材の表裏面の少な
くとも一方の面にインク受容層が形成されたインクジェ
ット記録用シートおよびその製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording sheet having an ink receiving layer formed on at least one of the front and back surfaces of a substrate, and a method for producing the same.
【０００２】[0002]
【従来の技術】インクジェット記録装置は、種々の作動
原理によりインクの微小液滴を記録用シートに直接噴射
して、画像、文字、各種図形などを記録する装置であ
る。このインクジェット記録装置は、精細な記録が可能
であり、銀塩写真に匹敵するカラー記録も可能であるこ
とから、近年、広く普及している。このインクジェット
記録装置に好適に用いられるシートとして、上質紙、合
成紙、合成樹脂フィルムなど平滑度の高い基材の表裏面
の少なくとも一方の面に、顔料、バインダーおよびイン
ク定着剤等を含む塗工液を塗工してインク受容層を設け
た、いわゆる塗工紙タイプのインクジェット記録用シー
トが知られている。この種のインクジェット記録用シー
トは、インクが均一に吸収されて着肉むらおよびにじみ
が生じないように、インク受容層の厚みが均一で、か
つ、塗工むらや塗工欠点がないことが特に重要となる。2. Description of the Related Art An ink jet recording apparatus is an apparatus for recording images, characters, various figures, and the like by directly ejecting minute droplets of ink onto a recording sheet according to various operating principles. This ink jet printing apparatus has been widely used in recent years because it can perform fine printing and can perform color printing comparable to silver halide photography. As a sheet suitably used in the ink jet recording apparatus, a coating containing a pigment, a binder, an ink fixing agent and the like on at least one of the front and back surfaces of a substrate having high smoothness such as a high quality paper, a synthetic paper, a synthetic resin film, etc. A so-called coated paper type ink jet recording sheet provided with an ink receiving layer by applying a liquid is known. This type of ink jet recording sheet has a uniform thickness of the ink receiving layer, and has no coating unevenness or coating defects, so that the ink is uniformly absorbed and unevenness in the coating and blurring do not occur. It becomes important.
【０００３】一方、基材等に塗工液を塗工するのに用い
られる塗工機として、ブレードコーター、エアナイフコ
ーター、カーテンコーターなどが知られている。ブレー
ドコーターは、比較的、平滑な表面形状を有する塗工層
を得ることができるが、パルプ、特に古紙パルプ含有の
パルプ、や合成繊維を抄造して作製された紙等表面の平
滑性の低い基材を用いると、基材の表面形状に対応した
塗工量むらを生じる。また、エアナイフコーターは、エ
アナイフ特有のパターンが塗工層に発生することが不可
避で、均一な塗工量の塗工層を得ることが難しい。上記
塗工機のなかでは、カーテンコーターが、基材の地合の
影響を受けずに、均一な厚さの塗工層を形成するのに適
している。このカーテンコーターは、基材上にスリット
状のコーターリップから塗工液を膜状に垂らして塗工す
るもので、塗工液の成膜性や基材へのぬれ性を改善して
塗工むらや塗工欠点を防止するために、塗工液中に表面
張力低下能力の高い界面活性剤を含有させる必要があ
る。表面張力低下能力が低い界面活性剤では、成膜性の
改善が不充分となりカーテン膜の膜割れが生じやすくな
り、また、基材へのぬれ性も悪く未塗工部が発生し、さ
らにはカーテンコーターのコーターリップ幅よりも塗工
幅が狭くなる現象いわゆるネックインが大きくなる。前
記表面張力低下能力の高い界面活性剤としては、スルホ
琥珀酸ジアルキルエーテルなどアニオン系界面活性剤で
あることが知られており、カーテンコーターの塗工にお
いてもこのアニオン系界面活性剤を用いるのが一般的で
ある。On the other hand, as a coating machine used for applying a coating liquid to a substrate or the like, a blade coater, an air knife coater, a curtain coater and the like are known. The blade coater can obtain a coating layer having a relatively smooth surface shape, but the surface of the pulp, particularly pulp containing waste paper pulp, or paper made of synthetic fibers, has low smoothness. When a substrate is used, uneven coating amount corresponding to the surface shape of the substrate occurs. Further, in the air knife coater, it is inevitable that a pattern peculiar to the air knife is generated in the coating layer, and it is difficult to obtain a coating layer having a uniform coating amount. Among the above coating machines, the curtain coater is suitable for forming a coating layer having a uniform thickness without being affected by the formation of the base material. This curtain coater coats a substrate by applying a coating liquid from a slit-shaped coater lip in a film form, improving the film forming property of the coating liquid and the wettability to the substrate. In order to prevent unevenness and coating defects, it is necessary to include a surfactant having a high surface tension lowering ability in the coating liquid. In the case of a surfactant having a low surface tension lowering ability, the improvement of the film-forming property is insufficient, the film of the curtain film is easily cracked, and the wettability to the base material is poor, and an uncoated portion is generated. The phenomenon in which the coating width is narrower than the coater lip width of the curtain coater, the so-called neck-in, increases. It is known that the surfactant having a high surface tension lowering ability is an anionic surfactant such as sulfosuccinic acid dialkyl ether, and it is preferable to use this anionic surfactant also in coating of a curtain coater. General.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、インク
ジェット記録方式に採用される水性インクのほとんどは
アニオン系であるため、インク受容層を形成するための
塗工液に含有されるインク定着剤はカチオン系のもので
ある。しかるに、従来どおりにカーテンコーターを用い
てインクジェット記録用のインク受容層を形成しようと
しても、表面張力を低下させるために必要となるアニオ
ン系界面活性剤とインク定着性を向上させるためのカチ
オン系インク定着剤とが反応して凝集または過剰に粘度
が増大するため、塗工を行うことはできない。したがっ
て、カーテンコーターを用いてインクジェット記録用の
インク受容層を形成するには、アニオン系以外の界面活
性剤を用いるしかないのだが、一般的なアニオン系以外
の界面活性剤は、表面張力低下能力が低く、カーテンコ
ーターにおける通常の界面活性剤の使用量ではネックイ
ンや膜割れが完全に改善されなかった。しかも、前記一
般的なアニオン系以外の界面活性剤は、発泡性が高く、
使用量を増やすと塗工液を発泡させるうえに、印字性も
悪化させるので、使用量を増やして表面張力を低下させ
る手法をとることもできなかった。However, since most of the aqueous inks used in the ink jet recording system are anionic, the ink fixing agent contained in the coating liquid for forming the ink receiving layer is cationic. belongs to. However, even if it is attempted to form an ink receiving layer for inkjet recording using a curtain coater as in the past, an anionic surfactant required to reduce surface tension and a cationic ink to improve ink fixability are required. Coating cannot be performed because of the reaction with the fixing agent and aggregation or excessive increase in viscosity. Therefore, the only way to form an ink receiving layer for ink jet recording using a curtain coater is to use a surfactant other than anionic surfactants. The neck-in and film cracking were not completely improved by the usual amount of surfactant used in the curtain coater. Moreover, the general non-anionic surfactant has a high foaming property,
Increasing the amount used causes foaming of the coating liquid and deteriorating the printability. Therefore, it was impossible to take a method of increasing the amount used to lower the surface tension.
【０００５】そこで、本発明者らが研究を重ねた結果、
アニオン系以外の界面活性剤でも特にアミンアセテート
系界面活性剤が、アニオン系界面活性剤と同等の表面張
力低下性を有することを知見した。さらに、このアミン
アセテート系界面活性剤は、大きくはカチオン系に属す
るため、塗工液中でインク定着剤と反応することもな
く、また塗工液を発泡させることもないため、カーテン
コーターを用いて好適に塗工でき、均一な厚さのインク
受容層を形成することが可能であることを知見し、本発
明を完成するに至った。Thus, as a result of repeated studies by the present inventors,
It has been found that, among surfactants other than anionic surfactants, particularly, amine acetate surfactants have the same surface tension lowering properties as anionic surfactants. Furthermore, since this amine acetate surfactant is largely of a cationic type, it does not react with the ink fixing agent in the coating liquid and does not foam the coating liquid. The present inventors have found that it is possible to form an ink-receiving layer having a uniform thickness by applying the ink well, and to complete the present invention.
【０００６】[0006]
【課題を解決するための手段】すなわち、本発明請求項
１記載の発明は、基材の表裏面の少なくとも一方の面
に、インク受容層が形成されたインクジェット記録用シ
ートであって、前記インク受容層が、アミンアセテート
系界面活性剤とカチオン系インク定着剤と顔料とを含む
塗工液を、カーテンコーターによって塗工して形成され
たものであることを特徴とするインクジェット記録用シ
ートである。That is, the invention according to claim 1 of the present invention is an ink jet recording sheet having an ink receiving layer formed on at least one of the front and back surfaces of a substrate, An ink jet recording sheet, wherein the receiving layer is formed by applying a coating solution containing an amine acetate surfactant, a cationic ink fixing agent, and a pigment with a curtain coater. .
【０００７】請求項２記載の発明は、基材の表裏面の少
なくとも一方の面に、インク受容層が形成されたインク
ジェット記録用シートの製造方法であって、前記インク
受容層を、アミンアセテート系界面活性剤とカチオン系
インク定着剤と顔料とを含む塗工液をカーテンコーター
によって塗工して形成することを特徴とするインクジェ
ット記録用シートの製造方法である。According to a second aspect of the present invention, there is provided a method of manufacturing an ink jet recording sheet having an ink receiving layer formed on at least one of the front and back surfaces of a substrate, wherein the ink receiving layer is formed of an amine acetate-based material. This is a method for producing an ink jet recording sheet, which is formed by applying a coating liquid containing a surfactant, a cationic ink fixing agent and a pigment using a curtain coater.
【０００８】本発明は、表面張力低下剤としてアミンア
セテート系界面活性剤を使用し、カーテンコーターによ
ってインク受容層を形成するようにしたので、平滑度の
高い基材はもちろんのこと、比較的平滑度の低い基材で
あっても、均一なインク受容層が形成される。In the present invention, an amine acetate surfactant is used as a surface tension lowering agent, and an ink receiving layer is formed by a curtain coater. Therefore, not only a substrate having high smoothness but also a relatively smooth surface is used. Even with a low-grade substrate, a uniform ink-receiving layer is formed.
【０００９】[0009]
【発明の実施の形態】本発明の実施の形態を以下に詳述
する。本発明のインクジェット記録用シートは、基材の
表裏面の少なくとも一方の面に、カーテンコーターによ
って塗工液を塗工して形成されるインク受容層を備えた
ものである。Embodiments of the present invention will be described in detail below. The ink jet recording sheet of the present invention has an ink receiving layer formed by applying a coating liquid with a curtain coater on at least one of the front and back surfaces of the substrate.
【００１０】本発明においては、塗工液の表面張力を調
整するため、前記塗工液中にアミンアセテート系界面活
性剤を含有させる。このアミンアセテート系界面活性剤
としては、例えば、アセタミン２４（花王株式会社製）
やアセタミン８６（花王株式会社製）等が挙げられる。
かかる界面活性剤は、塗工液の顔料１００重量部に対し
て０．１〜２０重量部とするのが好適である。０．１重
量部以下であると、表面張力が充分に低下しない。ま
た、２０重量部以上であると、タンク内での発泡が多く
なるので好ましくない。In the present invention, in order to adjust the surface tension of the coating solution, the coating solution contains an amine acetate surfactant. As the amine acetate surfactant, for example, Acetamine 24 (manufactured by Kao Corporation)
And acetamine 86 (manufactured by Kao Corporation).
The surfactant is preferably used in an amount of 0.1 to 20 parts by weight based on 100 parts by weight of the pigment of the coating liquid. When the amount is less than 0.1 part by weight, the surface tension does not sufficiently decrease. On the other hand, if it is more than 20 parts by weight, foaming in the tank increases, which is not preferable.
【００１１】一方、本発明にかかる塗工液には、インク
の定着性を促進させるために塗工液中にカチオン系イン
ク定着剤を用いる。本発明におけるカチオン性インク定
着剤としては、水に溶解したとき離解してカチオン性を
呈する１級〜３級アミン又は４級アンモニウム塩のモノ
マー、オリゴマー、ポリマーの少なくとも１ 種以上を
使用するのが好ましい。特に好ましくは、オリゴマー又
はポリマーである。On the other hand, in the coating liquid according to the present invention, a cationic ink fixing agent is used in the coating liquid in order to promote the fixing property of the ink. As the cationic ink fixing agent in the present invention, it is preferable to use at least one or more monomers, oligomers and polymers of primary to tertiary amines or quaternary ammonium salts which dissociate when dissolved in water to exhibit cationicity. preferable. Particularly preferred are oligomers and polymers.
【００１２】他方、本発明にかかる塗工液には、従来既
知のバインダーを問題なく用いることができるが、水溶
性インクの溶媒を定着させる必要性から水溶性インクの
溶媒との親和性の点で水溶性バインダーであるのが望ま
しい。かかるバインダーとしては、例えば、ポリビニル
アルコール、酢酸ビニル、酸化澱粉、エステル化澱粉、
エーテル化澱粉、カルボキシメチルセルロース、ヒドロ
キシエチルセルロース等のセルロース誘導体、カゼイ
ン、ゼラチン、大豆蛋白などが挙げられる。On the other hand, a conventionally known binder can be used for the coating liquid according to the present invention without any problem. However, it is necessary to fix the solvent of the water-soluble ink, so that it has an affinity with the solvent of the water-soluble ink. And a water-soluble binder. Such binders include, for example, polyvinyl alcohol, vinyl acetate, oxidized starch, esterified starch,
Examples include etherified starch, cellulose derivatives such as carboxymethylcellulose and hydroxyethylcellulose, casein, gelatin, and soybean protein.
【００１３】他方、本発明にかかる塗工液には、従来既
知の顔料を問題なく用いることができる。前記顔料とし
ては、例えば、軽質炭酸カルシウム、重質炭酸カルシウ
ム、カオリン、タルク、硫酸カルシウム、硫酸バリウ
ム、二酸化チタン、酸化亜鉛、硫化亜鉛、炭酸亜鉛、サ
チンホワイト、珪酸アルミニウム、ケイソウ土、珪酸カ
ルシウム、珪酸マグネシウム、合成非晶質シリカ、コロ
イダルシリカ、コロイダルアルミナ、擬ベーマイト、水
酸化アルミニウム、アルミナ、リトポン、ゼオライト、
加水ハロイサイト、炭酸マグネシウム、水酸化マグネシ
ウム、多孔性合成非晶質シリカ、多孔性炭酸マグネシウ
ム、多孔性アルミナ等の白色無機顔料、スチレン系プラ
スチックピグメント、アクリル系プラスチックピグメン
ト、ポリエチレン、マイクロカプセル、尿素樹脂、メラ
ミン樹脂等の有機顔料等が挙げられる。なかでも、多孔
性の無機顔料である、多孔性合成非晶質シリカ、多孔性
炭酸マグネシウム、多孔性アルミナ等が好適である。ま
た、それらのなかでも細孔容積の大きい多孔性合成非晶
質シリカが特に好適である。On the other hand, conventionally known pigments can be used in the coating liquid according to the present invention without any problem. Examples of the pigment include light calcium carbonate, heavy calcium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth, calcium silicate, Magnesium silicate, synthetic amorphous silica, colloidal silica, colloidal alumina, pseudoboehmite, aluminum hydroxide, alumina, lithopone, zeolite,
White inorganic pigments such as hydrohaloysite, magnesium carbonate, magnesium hydroxide, porous synthetic amorphous silica, porous magnesium carbonate, porous alumina, styrene plastic pigment, acrylic plastic pigment, polyethylene, microcapsules, urea resin, Organic pigments such as melamine resin and the like can be mentioned. Of these, porous inorganic pigments such as porous synthetic amorphous silica, porous magnesium carbonate, and porous alumina are preferred. Among them, porous synthetic amorphous silica having a large pore volume is particularly preferable.
【００１４】ここで、本発明の塗工液におけるアミンア
セテート系界面活性剤以外の含有物の配合割合、すなわ
ち、顔料、カチオン系インク定着剤、バインダー、その
他の添加剤などの配合割合は、従来既知のインクジェッ
ト記録用のインク受容層を形成するための塗工液と同様
でよく、それら従来既知の塗工液を参考に適宜変更すれ
ばよい。当業者であればこれらの変更は容易にできるで
あろう。Here, the mixing ratio of the components other than the amine acetate-based surfactant in the coating liquid of the present invention, that is, the mixing ratio of the pigment, the cationic ink fixing agent, the binder, and other additives is conventionally known. The coating liquid may be the same as a known coating liquid for forming an ink receiving layer for inkjet recording, and may be appropriately changed with reference to these conventionally known coating liquids. Those skilled in the art will readily make these changes.
【００１５】一方、本発明に用いられる基材としては、
カーテンコーターで塗工可能な、パルプを原料とする
紙、熱可塑性樹脂フィルム、合成紙、写真用基材のよう
な合成樹脂ラミネート紙、木材繊維や合成繊維を主体と
した不織布の如き様々なシート状物質を問題なく用いる
ことができる。環境保護にも貢献できることから、古紙
パルプを７０％以上含むパルプ、特には、古紙パルプ１
００％からなるパルプを原料パルプとする紙を用いるの
が望ましい。一般に、古紙パルプを７０％以上含むパル
プを原料とする紙は平滑度が低く、従来方法によってイ
ンク受容層を形成すると塗工量むらが生じ、インク着肉
むらが発生しやすくなるが、本発明に従ってカーテンコ
ーターを用いてインク受容層を設けると、古紙パルプ１
００％からなる紙を基材としても、塗工量むらのないイ
ンク受容層が形成され、インク着肉むらの発生しないイ
ンクジェット記録用紙が得られる。On the other hand, the substrate used in the present invention includes:
Various sheets that can be coated with a curtain coater, such as pulp-based paper, thermoplastic resin film, synthetic paper, synthetic resin-laminated paper such as photographic base materials, and nonwoven fabrics mainly composed of wood fibers and synthetic fibers Substances can be used without any problems. Pulp containing 70% or more waste paper pulp, especially waste paper pulp 1
It is desirable to use paper made from pulp consisting of 00% as a raw material pulp. In general, paper made from pulp containing 70% or more of waste paper pulp has low smoothness, and when an ink receiving layer is formed by a conventional method, unevenness in the amount of coating occurs and unevenness in ink adhesion tends to occur. When an ink receiving layer is provided using a curtain coater according to
Even when the base paper is made of 00%, an ink receiving layer having no unevenness in the coating amount is formed, and an ink jet recording paper free from uneven ink deposition is obtained.
【００１６】また、本発明にかかる基材には、内添サイ
ズ剤、中性サイズ剤、ポリマーサイズ剤、酸性サイズ剤
等のサイズ剤、填料、サイズプレスが含有されていても
よい。白色顔料として、例えば、軽質炭酸カルシウム、
重質炭酸カルシウム、カオリン、クレー、タルク、硫酸
カルシウム、硫酸バリウム、二酸化チタン、酸化亜鉛、
硫化亜鉛、炭酸亜鉛、サチンホワイト、珪酸アルミニウ
ム、ケイソウ土、珪酸カルシウム、珪酸マグネシウム、
合成シリカ、水酸化アルミニウム、アルミナ、リトポ
ン、ゼオライト、炭酸マグネシウム、水酸化マグネシウ
ムのような白色無機顔料、スチレン系プラスチックピグ
メント、アクリル系プラスチックピグメント、ポリエチ
レン、マイクロカプセル、尿素樹脂、メラミン樹脂のよ
うな有機顔料等が１種あるいは２種以上含有されていて
もよい。The base material according to the present invention may contain a sizing agent such as an internal sizing agent, a neutral sizing agent, a polymer sizing agent, an acidic sizing agent, a filler, and a size press. As a white pigment, for example, light calcium carbonate,
Heavy calcium carbonate, kaolin, clay, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide,
Zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth, calcium silicate, magnesium silicate,
White inorganic pigments such as synthetic silica, aluminum hydroxide, alumina, lithopone, zeolite, magnesium carbonate, and magnesium hydroxide, styrene plastic pigments, acrylic plastic pigments, polyethylene, microcapsules, organic materials such as urea resins and melamine resins One or more pigments may be contained.
【００１７】本発明における基材には、その他の添加剤
として、顔料分散剤、増粘剤、流動性改良剤、消泡剤、
抑泡剤、離型剤、発泡剤、浸透剤、着色染料、着色顔
料、蛍光増白剤、紫外線吸収剤、酸化防止剤、防腐剤、
防バイ剤、耐水化剤、湿潤紙力増強剤、乾燥紙力増強剤
等が配合されていてもよい。In the substrate of the present invention, other additives such as a pigment dispersant, a thickener, a flow improver, an antifoaming agent,
Foam inhibitors, release agents, foaming agents, penetrants, coloring dyes, coloring pigments, optical brighteners, ultraviolet absorbers, antioxidants, preservatives,
An anti-binder, a water-proofing agent, a wet paper strength enhancer, a dry paper strength enhancer, and the like may be blended.
【００１８】一方、本発明のインクジェット記録用シー
トに記録するのに好適なアニオン系水性インクは、下記
の着色剤、液媒体、その他の添加剤からなる記録用液体
である。着色剤としては、直接染料、酸性染料、塩基性
染料、反応性染料或は食品用色素等の水溶性染料が挙げ
られる。前記水性インクの溶媒としては、水及び水溶性
の各種有機溶剤、例えば、メチルアルコール、エチルア
ルコール、ｎ−プロピルアルコール、イソプロピルアル
コール、ｎ−ブチルアルコール、 ｓｅｃ−ブチルアル
コール、ｔｅｒｔ−ブチルアルコール、イソブチルアル
コール等の炭素数１ 〜４ のアルキルアルコール類；ジ
メチルホルムアミド、ジメチルアセトアミド等のアミド
類；アセトン、ジアセトンアルコール等のケトン又はケ
トンアルコール類；テトラヒドロフラン、ジオキサン等
のエーテル類；ポリエチレングリコール、ポリプロピレ
ングリコール等のポリアルキレングリコール類；エチレ
ングリコール、プロピレングリコール、ブチレングリコ
ール、トリエチレングリコール、1，2，6−ヘキサント
リオール、チオジグリコール、ヘキシレングリコール、
ジエチレングリコール等のアルキレン基が２〜６個のア
ルキレングリコール類；グリセリン、エチレングリコー
ルメチルエーテル、ジエチレングリコールメチル（又は
エチル）エーテル、トリエチレングリコールモノメチル
エーテル等の多価アルコールの低級アルキルエーテル類
等が挙げられる。これらの多くの水溶性有機溶剤の中で
も、ジエチレングリコール等の多価アルコール、トリエ
チレングリコールモノメチルエーテル、トリエチレング
リコールモノエチルエーテル等の多価アルコールの低級
アルキルエーテルが好ましい。On the other hand, an anionic aqueous ink suitable for recording on the ink jet recording sheet of the present invention is a recording liquid comprising the following colorant, liquid medium, and other additives. Examples of the coloring agent include a direct dye, an acid dye, a basic dye, a reactive dye, and a water-soluble dye such as a food colorant. Examples of the solvent for the aqueous ink include water and various water-soluble organic solvents such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, and isobutyl alcohol. Alkyl alcohols having 1 to 4 carbon atoms such as amides such as dimethylformamide and dimethylacetamide; ketones or ketone alcohols such as acetone and diacetone alcohol; ethers such as tetrahydrofuran and dioxane; polyethylene glycol and polypropylene glycol and the like. Polyalkylene glycols; ethylene glycol, propylene glycol, butylene glycol, triethylene glycol, 1,2,6-hexanetriol, thiodiglycol, Xylene glycol,
Alkylene glycols having 2 to 6 alkylene groups such as diethylene glycol; and lower alkyl ethers of polyhydric alcohols such as glycerin, ethylene glycol methyl ether, diethylene glycol methyl (or ethyl) ether, and triethylene glycol monomethyl ether. Among these many water-soluble organic solvents, polyhydric alcohols such as diethylene glycol, and lower alkyl ethers of polyhydric alcohols such as triethylene glycol monomethyl ether and triethylene glycol monoethyl ether are preferable.
【００１９】また、前記溶媒中には、その他の添加剤と
して、例えば、ＰＨ調節剤、金属封鎖剤、防カビ剤、粘
度調整剤、湿潤剤、界面活性剤、及び防錆剤等が含有さ
れていてもよい。The solvent contains other additives such as a pH adjuster, a metal sequestering agent, a fungicide, a viscosity adjuster, a wetting agent, a surfactant, and a rust inhibitor. It may be.
【００２０】他方、本発明に用いるカーテンコーターの
機種については、特に限定されない。また、本発明にお
いてはカーテンコーターの運転条件、すなわち、吐出量
や塗工速度等も特に限定されない。それら運転条件は、
塗工幅および塗工量を参考にして、従来技術に基づき適
宜変更すればよい。上記に詳述した本発明にかかる塗工
液の表面張力は、２７〜３５ｄｙｎ／ｃｍとなるため、
従来既知のカーテンコーターを用いて好適に基材に塗工
できる。On the other hand, the type of curtain coater used in the present invention is not particularly limited. In the present invention, the operating conditions of the curtain coater, that is, the discharge amount and the coating speed are not particularly limited. These operating conditions are:
What is necessary is just to change suitably based on a prior art, referring to a coating width and a coating amount. Since the surface tension of the coating liquid according to the present invention described above is 27 to 35 dyn / cm,
The substrate can be suitably coated using a conventionally known curtain coater.
【００２１】ここで、本発明におけるインクジェット記
録用シートは、インクジェット記録装置の使用のみに限
定されるもではない。アニオン系水性インクを用いる記
録方式において好適に用いられる。Here, the ink jet recording sheet of the present invention is not limited only to the use of an ink jet recording apparatus. It is suitably used in a recording method using an anionic aqueous ink.
【００２２】（装置例）次いで、カーテンコーターの装
置例を図１に示す。図示されるカーテンコーターを用い
て基材に塗工液を塗工すれば、本発明のインクジェット
記録用シートを得ることができる。なお、本発明は、図
示されるカーテンコーターの使用に限定されるものでは
ない。(Example of Apparatus) FIG. 1 shows an example of an apparatus of a curtain coater. If the coating liquid is applied to the substrate using the illustrated curtain coater, the ink jet recording sheet of the present invention can be obtained. Note that the present invention is not limited to the use of the illustrated curtain coater.
【００２３】図１に示されるカーテンコーター１におい
ては、予め調製されたインク受容層塗工液ｉは、塗工液
貯蔵タンクより給液ポンプ等によってコーターヘッド２
へ送られる。前記コーターヘッド２の内部は、マニホー
ルド２ａおよびスリット２ｂからなり、それぞれ高精度
の仕上げが施されている。供給された塗工液は、前記マ
ニホールド２ａに満たされ、更にスリット２ｂに送られ
るときに通過する狭い間隙において、給液ポンプの送液
による動圧の影響が軽減され、幅方向における圧力分布
が均一化され、リップ３より流出し、垂直なカーテン膜
Ｍを形成する。In the curtain coater 1 shown in FIG. 1, an ink receiving layer coating liquid i prepared in advance is supplied from a coating liquid storage tank to a coater head 2 by a liquid supply pump or the like.
Sent to The inside of the coater head 2 includes a manifold 2a and a slit 2b, each of which is finished with high precision. The supplied coating liquid is filled in the manifold 2a, and in a narrow gap that passes when being sent to the slit 2b, the influence of the dynamic pressure due to the liquid supply of the liquid supply pump is reduced, and the pressure distribution in the width direction is reduced. It is made uniform and flows out of the lip 3 to form a vertical curtain film M.
【００２４】幅方向でプロファイルが均一となった垂直
カーテン膜Ｍは、連続走行している基材Ｓと接触し、基
材Ｓに塗工される。ここでエッジガイド４、４はコータ
ーヘッド２の幅を超えず、更に基材Ｓの幅を超えて設け
られ、垂直カーテン膜は基材Ｓの幅を超えて形成され
る。垂直カーテン膜Ｍが基材Ｓの幅を超えて形成されて
いるのは、垂直カーテン膜Ｍの両端部における塗工層の
厚塗りを防止するためである。基材Ｓの幅を超えて流下
する塗工液は、受液槽５に回収され、塗工液貯蔵タンク
に戻された後再び塗工される。また、基材Ｓが切断され
塗工が中断された場合も、塗工液は受液槽５に回収され
る。The vertical curtain film M having a uniform profile in the width direction comes into contact with the continuously running substrate S and is applied to the substrate S. Here, the edge guides 4 are provided not exceeding the width of the coater head 2 and further exceeding the width of the substrate S, and the vertical curtain film is formed exceeding the width of the substrate S. The vertical curtain film M is formed so as to exceed the width of the base material S in order to prevent thick coating of the coating layer at both ends of the vertical curtain film M. The coating liquid flowing down beyond the width of the base material S is collected in the liquid receiving tank 5, returned to the coating liquid storage tank, and coated again. Also, when the substrate S is cut and the coating is interrupted, the coating liquid is collected in the liquid receiving tank 5.
【００２５】連続走行している基材Ｓと垂直カーテン膜
Ｍとの接触部（以後、「塗工部」という。）には基材Ｓ
に同伴する空気流を遮蔽し、カーテン周辺の空気の回流
などで垂直カーテン膜Ｍが乱れることなく基材Ｓに達す
るようにするため遮風板６が設けられている。また、基
材Ｓの搬送方向は、塗工部の直前でロール７により方向
転換することにより、基材Ｓに同伴する空気の塗工部へ
の影響を最小限にとどめるように構成されている。The contact portion between the continuously running substrate S and the vertical curtain film M (hereinafter, referred to as a "coating portion") is provided at the contact portion.
A wind shield plate 6 is provided in order to shield the air flow accompanying the air flow and to allow the vertical curtain film M to reach the base material S without being disturbed by the circulation of air around the curtain. Further, the transport direction of the substrate S is changed by the roll 7 immediately before the coating section, so that the influence of the air accompanying the substrate S on the coating section is minimized. .
【００２６】形成させた垂直カーテン膜Ｍを安定した状
態で塗工するためには、基材Ｓからコーターヘッド１下
部の流出部までの高さがある程度必要とされるが、垂直
カーテン膜Ｍの安定に適した高さは６０〜３００ｍｍ、
好ましくは１００〜２５０ｍｍ、更に好ましくは１２０
〜１８０ｍｍである。In order to apply the formed vertical curtain film M in a stable state, a certain height from the base material S to the outflow portion below the coater head 1 is required. Height suitable for stabilization is 60 to 300 mm,
Preferably 100-250 mm, more preferably 120
１８０180 mm.
【００２７】＜実験例＞次いで、本発明の実施例および
比較例を示し、本発明をさらに詳述する。なお、本発明
は、下記実施例に限定されるものではない。また、本実
験例において部とは重量部を表す。<Experimental Example> Next, the present invention will be described in more detail by showing Examples and Comparative Examples of the present invention. Note that the present invention is not limited to the following examples. In this experimental example, “parts” means “parts by weight”.
【００２８】［実施例1］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、本発明
にかかるアミンアセテート系界面活性剤としてアセタミ
ン２４（花王株式会社製）０．１部を含む塗工液を、カ
ーテンコーター（石川島播磨重工製）を用いて、吐出量
１０リットル／分、塗工速度１８０ｍ／分、コーター幅
１０００ｍｍの条件で、上質紙に塗工した。Example 1 100 parts of silica as a pigment and 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, 10 parts of a quaternary ammonium salt as a cationic ink fixing agent, Using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries), a coating solution containing 0.1 part of acetamine 24 (manufactured by Kao Corporation) as an amine acetate-based surfactant according to the present invention is applied at a discharge rate of 10 liter / min. The coating was performed on high quality paper under the conditions of a speed of 180 m / min and a coater width of 1000 mm.
【００２９】［実施例２］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、本発明
にかかるアミンアセテート系界面活性剤としてアセタミ
ン２４（花王株式会社製）２０部を含む塗工液を、カー
テンコーター（石川島播磨重工製）を用いて、吐出量１
０リットル／分、塗工速度１８０ｍ／分、コーター幅１
０００ｍｍの条件で、上質紙に塗工した。Example 2 100 parts of silica as a pigment and 100 parts of the pigment: 25 parts of PVA and 25 parts of vinyl acetate as a binder, 10 parts of a quaternary ammonium salt as a cationic ink fixing agent, A coating liquid containing 20 parts of acetamine 24 (manufactured by Kao Corporation) as an amine acetate-based surfactant according to the present invention was discharged using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries) with a discharge amount of 1 part.
0 liter / min, coating speed 180m / min, coater width 1
Under a condition of 000 mm, it was applied to high quality paper.
【００３０】［実施例３］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、本発明
にかかるアミンアセテート系界面活性剤としてアセタミ
ン８６（花王株式会社製）０．１部を含む塗工液を、カ
ーテンコーター（石川島播磨重工製）を用いて、吐出量
１０リットル／分、塗工速度１８０ｍ／分、コーター幅
１０００ｍｍの条件で、上質紙に塗工した。Example 3 100 parts of silica was contained as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent. Using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries), a coating solution containing 0.1 part of acetamine 86 (manufactured by Kao Corporation) as an amine acetate-based surfactant according to the present invention is applied at a discharge rate of 10 liter / min. The coating was performed on high quality paper under the conditions of a speed of 180 m / min and a coater width of 1000 mm.
【００３１】［実施例４］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、本発明
にかかるアミンアセテート系界面活性剤としてアセタミ
ン８６（花王株式会社製）２０部を含む塗工液を、カー
テンコーター（石川島播磨重工製）を用いて、吐出量１
０リットル／分、塗工速度１８０ｍ／分、コーター幅１
０００ｍｍの条件で、上質紙に塗工した。Example 4 100 parts of silica was contained as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent. A coating liquid containing 20 parts of acetamine 86 (manufactured by Kao Corporation) as an amine acetate-based surfactant according to the present invention was discharged using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries).
0 liter / min, coating speed 180m / min, coater width 1
Under a condition of 000 mm, it was applied to high quality paper.
【００３２】［実施例５］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、本発明
にかかるアミンアセテート系界面活性剤としてアセタミ
ン２４（花王株式会社製）０．１部を含む塗工液を、カ
ーテンコーター（石川島播磨重工製）を用いて、吐出量
１０リットル／分、塗工速度１８０ｍ／分、コーター幅
１０００ｍｍの条件で、古紙パルプ１００％を原料とし
た印刷用紙に塗工した。Example 5 100 parts of silica was contained as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent. Using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries), a coating solution containing 0.1 part of acetamine 24 (manufactured by Kao Corporation) as an amine acetate surfactant is applied at a discharge rate of 10 liter / min. The coating was performed on printing paper made from 100% waste paper pulp under the conditions of a speed of 180 m / min and a coater width of 1000 mm.
【００３３】［実施例６］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、本発明
にかかるアミンアセテート系界面活性剤としてアセタミ
ン８６（花王株式会社製）０．１部を含む塗工液を、カ
ーテンコーター（石川島播磨重工製）を用いて、吐出量
１０リットル／分、塗工速度１８０ｍ／分、コーター幅
１０００ｍｍの条件で、古紙パルプ１００％を原料とし
た印刷用紙に塗工した。Example 6 100 parts of silica was contained as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent. Using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries), a coating solution containing 0.1 part of acetamine 86 (manufactured by Kao Corporation) as an amine acetate-based surfactant according to the present invention is applied at a discharge rate of 10 liter / min. The coating was performed on printing paper made from 100% waste paper pulp under the conditions of a speed of 180 m / min and a coater width of 1000 mm.
【００３４】［比較例１］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して、バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部を含み、
界面活性剤を含有しない塗工液を、カーテンコーター
（石川島播磨重工社製）を用いて、吐出量１０リットル
／分、塗工速度１８０ｍ／分、コーター幅１０００ｍｍ
の条件で上質紙に塗工した。[Comparative Example 1] 100 parts of silica as a pigment, 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent, based on 100 parts of the pigment. ,
Using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries Co., Ltd.), a coating liquid containing no surfactant was discharged at a rate of 10 liter / min, a coating speed of 180 m / min, and a coater width of 1000 mm.
Coated on high quality paper under the following conditions.
【００３５】［比較例２］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、従来の
カチオン系界面活性剤であるＳＦ−７５ＰＡ（三洋化成
株式会社製）０．１部を含む塗工液を、カーテンコータ
ー（石川島播磨重工製）を用いて、吐出量１０リットル
／分、塗工速度１８０ｍ／分、コーター幅１０００ｍｍ
の条件で、上質紙に塗工した。[Comparative Example 2] 100 parts of silica was contained as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent. Coating solution containing 0.1 part of SF-75PA (manufactured by Sanyo Chemical Co., Ltd.), which is a cationic surfactant, was applied at a discharge rate of 10 liter / min using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries). Speed 180m / min, coater width 1000mm
Under the conditions described above.
【００３６】［比較例３］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、従来の
カチオン系界面活性剤であるＳＦ−７５ＰＡ（三洋化成
株式会社製）２０部を含む塗工液を、カーテンコーター
（石川島播磨重工製）を用いて、吐出量１０リットル／
分、塗工速度１８０ｍ／分、コーター幅１０００ｍｍの
条件で、上質紙に塗工した。[Comparative Example 3] 100 parts of silica as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, 10 parts of a quaternary ammonium salt as a cationic ink fixing agent, Using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries), a coating liquid containing 20 parts of SF-75PA (manufactured by Sanyo Kasei Co., Ltd.), which is a cationic surfactant, was discharged at a rate of 10 liters / liter.
Min, the coating speed was 180 m / min, and the coater width was 1000 mm.
【００３７】［比較例４］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、従来の
カチオン界面活性剤であるレボンＴＭ１８（三洋化成株
式会社製）０．１部を含む塗工液を、カーテンコーター
（石川島播磨重工製）を用いて、吐出量１０リットル／
分、塗工速度１８０ｍ／分、コーター幅１０００ｍｍの
条件で、上質紙に塗工した。COMPARATIVE EXAMPLE 4 100 parts of silica was contained as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent. A coating liquid containing 0.1 part of Levon TM18 (manufactured by Sanyo Chemical Co., Ltd.), which is a cationic surfactant, was discharged using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries) at a discharge rate of 10 liters / liter.
Min, the coating speed was 180 m / min, and the coater width was 1000 mm.
【００３８】［比較例５］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、従来の
カチオン界面活性剤であるレボンＴＭ１８（三洋化成株
式会社製）２０部を含む塗工液を、カーテンコーター
（石川島播磨重工製）を用いて、吐出量１０リットル／
分、塗工速度１８０ｍ／分、コーター幅１０００ｍｍの
条件で、上質紙に塗工した。[Comparative Example 5] 100 parts of silica as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, 10 parts of a quaternary ammonium salt as a cationic ink fixing agent, conventionally A coating liquid containing 20 parts of Levon TM18 (manufactured by Sanyo Chemical Co., Ltd.), which is a cationic surfactant, was discharged using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries) at a discharge rate of 10 liter / liter.
Min, the coating speed was 180 m / min, and the coater width was 1000 mm.
【００３９】［比較例６］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、従来の
アニオン系界面活性剤であるネオコールＳＷＣ（第一工
業製薬製）０．１部を含む塗工液を、カーテンコーター
（石川島播磨重工製）を用いて、吐出量１０リットル／
分、塗工速度１８０ｍ／分、コーター幅１０００ｍｍの
条件で、上質紙に塗工した。[Comparative Example 6] 100 parts of silica was contained as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, and 10 parts of a quaternary ammonium salt as a cationic ink fixing agent. A coating liquid containing 0.1 part of Neocol SWC (manufactured by Daiichi Kogyo Seiyaku), which is an anionic surfactant, was discharged using a curtain coater (manufactured by Ishikawajima-Harima Heavy Industries) at a discharge rate of 10 liters /
Min, the coating speed was 180 m / min, and the coater width was 1000 mm.
【００４０】［比較例７］顔料としてシリカ１００部を
含み、かつ、前記顔料１００部に対して；バインダーと
してＰＶＡ２５部および酢酸ビニル２５部、カチオン系
インク定着剤として４級アンモニウム塩１０部、アミン
アセテート系界面活性剤としてアセタミン８６（花王株
式会社製）２０部を含む塗工液を、ブレードコーター
（石川島播磨重工製）を用いて、吐出量１０リットル／
分、塗工速度１８０ｍ／分、コーター幅１０００ｍｍの
条件で、古紙パルプ７０％を原料とした印刷用紙に塗工
した。[Comparative Example 7] 100 parts of silica as a pigment and based on 100 parts of the pigment; 25 parts of PVA and 25 parts of vinyl acetate as a binder, 10 parts of a quaternary ammonium salt as a cationic ink fixing agent, amine Using a blade coater (manufactured by Ishikawajima-Harima Heavy Industries), a coating liquid containing 20 parts of acetamine 86 (manufactured by Kao Corporation) as an acetate-based surfactant was discharged at a rate of 10 liters / liter.
The coating was performed on printing paper made from 70% waste paper pulp under the conditions of a coating speed of 180 m / min and a coater width of 1000 mm.
【００４１】上記の実施例および比較例について、表面
張力を測定するとともに、塗工性、印字性、着肉むら、
発泡性およびネックインの評価を行ったので、結果を表
１に示す。With respect to the above Examples and Comparative Examples, the surface tension was measured, and the coating property, printing property,
Table 1 shows the results of the evaluation of foamability and neck-in.
【００４２】[0042]
【表１】 [Table 1]
【００４３】評価方法は、下記のとおりである。 ［表面張力の測定］デュヌーイ氏表面張力計（大平理化
工業株式会社製）を用いて、２４℃で測定した。 ［塗工性］塗工時に膜割れが生じるか否かを目視にて確
認した。塗工時に膜割れが生じなかったものを○、膜割
れが生じたものを×と評価した。 ［印字性］インクジェットプリンタ（PM−８００C：エ
プソン社製）を用いて、温度２３℃、湿度５０％の条件
下で、シアン、マゼンタ、イエローの各色インクの重ね
色で構成される赤、緑、紫を、それぞれベタ印字（大き
さ３.０cm×３.０ｃｍ）し、印字３０分経過後のにじみ
度合いを目視にて確認した。にじみが全くないものを
○、にじみが若干見られるものを△、にじみがはっきり
と見られるものを×と評価した。なお、使用したインク
は、アニオン系のものである。 ［発泡性］界面活性剤を含有することに起因してサービ
スタンク内で塗工液が発泡し塗工性能に影響を及ぼすこ
とがあるので、塗工時にサービスタンク内にて、塗工液
が発泡するか否かを目視にて確認した。発泡が生じなか
ったものを○、発泡が生じたものを×と評価した。 ［着肉むら］上記の印字性と同様にベタ印字し、インク
の着肉むらが見られるか否かを目視にて確認した。着肉
むらが見られないものを○、着肉むらがみられたものを
×と評価した。 ［ネックイン］塗工時のリップコーターから吐出される
塗工液の形状を、目視にて確認した。ネックインが確認
されなかったものを○、ネックインが確認されたものを
×とした。The evaluation method is as follows. [Measurement of Surface Tension] The measurement was performed at 24 ° C. using a Mr. Dunoi's surface tensiometer (manufactured by Ohira Rika Kogyo Co., Ltd.). [Coating property] Whether or not a film crack occurred during coating was visually checked. When no film cracking occurred during coating, it was evaluated as ○, and when film cracking occurred, it was evaluated as x. [Printability] Using an ink jet printer (PM-800C: manufactured by Epson Corporation), at a temperature of 23 ° C. and a humidity of 50%, red, green, and superimposed colors of cyan, magenta, and yellow inks are used. Purple was solid-printed (size 3.0 cm × 3.0 cm), and the degree of bleeding after 30 minutes of printing was visually confirmed. Those without any bleeding were evaluated as ○, those with slight bleeding as △, and those with clear bleeding as ×. The ink used was of an anionic type. [Foamability] The coating liquid may foam in the service tank due to the presence of the surfactant, which may affect the coating performance. It was visually confirmed whether or not foaming occurred. When no foaming occurred, it was evaluated as ○, and when foaming occurred, it was evaluated as x. [Non-colored unevenness] Solid printing was performed in the same manner as in the above-described printability, and it was visually confirmed whether or not non-uniformly colored ink was found. A sample with no unevenness was evaluated as ○, and a sample with unevenness was evaluated as x. [Neck-in] The shape of the coating liquid discharged from the lip coater during coating was visually checked.も の indicates that no neck-in was confirmed, and X indicates that the neck-in was confirmed.
【００４４】表１を見てみると、本発明の実施例１〜３
はいずれも、塗工性、印字性、発泡性、ネックインのす
べての評価において良好な結果であることが読み取ら
れ、所望の効果が得られることが確認された。対して、
比較例１〜７は、いくつかの項目において不適当な評価
があることが読み取られ、所望の効果が得られないこと
が確認された。Referring to Table 1, Examples 1 to 3 of the present invention are shown.
Were read as good results in all evaluations of coating properties, printing properties, foaming properties, and neck-in, and it was confirmed that desired effects were obtained. for,
In Comparative Examples 1 to 7, it was read that some items had inappropriate evaluations, and it was confirmed that the desired effects could not be obtained.
【００４５】[0045]
【発明の効果】以上詳説のとおり本発明によれば、イン
ク定着性に優れた均一なインク受容層が形成されたイン
クジェット記録用シートが提供される。As described in detail above, according to the present invention, there is provided an ink jet recording sheet having a uniform ink receiving layer having excellent ink fixability.
【図１】本発明にかかるカーテンコーターの装置例を示
す概略図である。FIG. 1 is a schematic view showing an example of a curtain coater device according to the present invention.
１…カーテンコーター、２…コーターヘッド、３…コー
ターリップ、４…エッジガイド、５…受液層、６…遮風
板、７…ロール。DESCRIPTION OF SYMBOLS 1 ... Curtain coater, 2 ... Coater head, 3 ... Coater lip, 4 ... Edge guide, 5 ... Liquid receiving layer, 6 ... Wind shield plate, 7 ... Roll.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2C056 FC06 2H086 BA01 BA15 BA31 BA35 BA37 4D075 AC14 CA35 CA48 DA04 DB18 DB20 DB31 DC27 EA07 EB07 EB19 EC03 EC07 EC11 EC33 EC35 ──────────────────────────────────────────────────続 き Continued on front page F term (reference) 2C056 FC06 2H086 BA01 BA15 BA31 BA35 BA37 4D075 AC14 CA35 CA48 DA04 DB18 DB20 DB31 DC27 EA07 EB07 EB19 EC03 EC07 EC11 EC33 EC35
Claims (2)
ンク受容層が形成されたインクジェット記録用シートで
あって、 前記インク受容層が、アミンアセテート系界面活性剤と
カチオン系インク定着剤と顔料とを含む塗工液を、カー
テンコーターによって塗工して形成されたものであるこ
とを特徴とするインクジェット記録用シート。1. An ink jet recording sheet having an ink receiving layer formed on at least one of the front and back surfaces of a substrate, wherein the ink receiving layer comprises an amine acetate surfactant and a cationic ink fixing agent. An ink jet recording sheet formed by applying a coating liquid containing a pigment and a pigment by a curtain coater.
ンク受容層が形成されたインクジェット記録用シートの
製造方法であって、 前記インク受容層を、アミンアセテート系界面活性剤と
カチオン系インク定着剤と顔料とを含む塗工液をカーテ
ンコーターによって塗工して形成することを特徴とする
インクジェット記録用シートの製造方法。2. A method for producing an ink jet recording sheet having an ink receiving layer formed on at least one of the front and back surfaces of a substrate, wherein the ink receiving layer comprises an amine acetate surfactant and a cationic surfactant. A method for producing an ink jet recording sheet, comprising forming a coating liquid containing an ink fixing agent and a pigment by coating with a curtain coater.