JP2002251921A - Dc power cable - Google Patents
Dc power cableInfo
- Publication number
- JP2002251921A JP2002251921A JP2001047814A JP2001047814A JP2002251921A JP 2002251921 A JP2002251921 A JP 2002251921A JP 2001047814 A JP2001047814 A JP 2001047814A JP 2001047814 A JP2001047814 A JP 2001047814A JP 2002251921 A JP2002251921 A JP 2002251921A
- Authority
- JP
- Japan
- Prior art keywords
- insulator
- power cable
- maleic anhydride
- conductor
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明が属する技術分野】この発明は、直流電力ケーブ
ルに関し、無水マレイン酸グラフトポリエチレンからな
る絶縁体を用いることにより、鉛被などの水の浸入を防
ぐ遮水層を不要にし、これによりケーブルを軽量とし、
仕上がり外径を細径化し、熱放散性を良好にしたもので
ある。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a DC power cable, which uses an insulator made of maleic anhydride-grafted polyethylene, thereby eliminating the need for a water-proof layer for preventing water from entering, such as lead coating, and thereby reducing the cable. Lightweight and
The finished outer diameter is reduced to improve heat dissipation.
【０００２】[0002]
【従来の技術】直流電力ケーブルは、交流電力ケーブル
に比べて、誘電損失がなく、充電電流に対する無効分を
補償するための設備が不要であるなどの長所を持つ。ま
た、一般に、絶縁物の絶縁耐圧は、交流より直流のほう
が大きく、安定度を考慮する必要がないことから、送電
距離が長く、かつ大容量送電になればなるほど直流電力
ケーブルのメリットがでてくることが知られている。2. Description of the Related Art A DC power cable has advantages over an AC power cable in that it has no dielectric loss and does not require a facility for compensating for an ineffective component with respect to a charging current. Also, in general, the insulation withstand voltage of insulators is larger in DC than in AC, and there is no need to consider stability.Therefore, the longer the transmission distance and the larger the capacity of transmission, the more the merit of a DC power cable appears. Is known to come.
【０００３】また、直流電力ケーブルは、海底ケーブル
として用いられることが多い。このため、現在実用化さ
れているＯＦケーブルやソリッドケーブルなどの油浸絶
縁ケーブルでは、油圧の維持や油漏れを防ぐためなどに
鉛被などの金属被からなる厚肉の遮水層が施されてい
る。また、現在開発されているプラスチック絶縁直流ケ
ーブルにおいても、架橋ポリエチレンや変性架橋ポリエ
チレンなどから個体状の絶縁体を使用するにもかかわら
ず、浸水防止の目的でやはり鉛被などの金属からなる厚
肉の遮水層が施されている。[0003] DC power cables are often used as submarine cables. For this reason, oil-immersed insulated cables such as OF cables and solid cables that are currently in practical use are provided with a thick water-impervious layer made of metal such as lead coating to maintain oil pressure and prevent oil leakage. ing. In addition, despite the use of solid insulators made of cross-linked polyethylene or modified cross-linked polyethylene, plastic-insulated DC cables currently being developed are still made of thick metal, such as lead sheath, for the purpose of preventing inundation. The impermeable layer is provided.
【０００４】図２は、このようなプラスチック絶縁直流
電力ケーブルを示すもので、図中符号１は導体を示す。
この導体１上には内部半導電層２、絶縁体３、外部半導
電層４、クッション層５、鉛被（遮水層）６および外装
７が順次設けられている。絶縁体３は、架橋低密度ポリ
エチレンからなり、その厚みが１５〜２５ｍｍ程度とな
っている。また、クッション層５は、発泡ゴムなどから
なる厚み２〜３ｍｍのものである。さらに、遮水層とし
ての鉛被６は、その厚みが３〜５ｍｍとなっている。FIG. 2 shows such a plastic insulated DC power cable, wherein reference numeral 1 denotes a conductor.
On the conductor 1, an inner semiconductive layer 2, an insulator 3, an outer semiconductive layer 4, a cushion layer 5, a lead coating (water shielding layer) 6, and an exterior 7 are sequentially provided. The insulator 3 is made of a crosslinked low-density polyethylene, and has a thickness of about 15 to 25 mm. The cushion layer 5 is made of foam rubber or the like and has a thickness of 2 to 3 mm. Further, the thickness of the lead sheath 6 as a water-blocking layer is 3 to 5 mm.
【０００５】このようなプラスチック絶縁直流電力ケー
ブルでは、架橋低密度ポリエチレンの熱膨張率が比較的
大きいため、絶縁体３の半径方向の熱膨張を吸収する必
要があるため、クッション層５が設けられている。とこ
ろが、クッション層５は、発泡体からなるため断熱性が
良好で、導体１からの発熱の放散が妨げられると言う欠
点がある。また、クッション層５は、発泡体からなるた
め、水を吸い込みやすく、このため厚い鉛被６を施して
遮水性を高めておく必要がある。さらに、クッション層
５を設けることでケーブルの仕上がり外径が太くなる欠
点もある。In such a plastic insulated DC power cable, since the thermal expansion coefficient of the crosslinked low-density polyethylene is relatively large, it is necessary to absorb the thermal expansion of the insulator 3 in the radial direction. ing. However, since the cushion layer 5 is made of a foam, it has good heat insulation properties, and has a drawback that heat dissipation from the conductor 1 is prevented. In addition, since the cushion layer 5 is made of a foam, it is easy to absorb water, and therefore, it is necessary to apply a thick lead cover 6 to increase the water shielding. Further, the provision of the cushion layer 5 has a disadvantage that the finished outer diameter of the cable is increased.
【０００６】このように、架橋低密度ポリエチレンから
なる絶縁体３を有するプラスチック絶縁直流電力ケーブ
ルでは、重量が重く、仕上がり外径が太く、コストが嵩
み、熱放散性にも劣るという問題があった。As described above, the plastic insulated DC power cable having the insulator 3 made of cross-linked low-density polyethylene has problems that the weight is heavy, the finished outer diameter is large, the cost is high, and the heat dissipation is poor. Was.
【０００７】[0007]
【発明が解決しようとする課題】よって、本発明におけ
る課題は、軽量で、仕上がり外径を小さくでき、コスト
を抑えることが可能で、しかも熱放散性が良好なプラス
チック絶縁直流電力ケーブルを得ることにある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a plastic insulated DC power cable which is lightweight, can have a small finished outer diameter, can reduce costs, and has good heat dissipation. It is in.
【０００８】[0008]
【課題を解決するための手段】かかる課題は、絶縁体と
して無水マレイン酸グラフトポリエチレンからなるもの
を用いることにより解決される。また、その密度を０．
９２５ｇ／ｃｍ3以上であることが好ましく、無水マレ
イン酸のグラフト量は０．０１〜５ｗｔ％が好ましい。
さらに、導体には水密構造のものが好ましい。This problem is solved by using a maleic anhydride-grafted polyethylene as the insulator. Further, the density is set to 0.
It is preferably 925 g / cm 3 or more, and the grafting amount of maleic anhydride is preferably 0.01 to 5 wt%.
Further, the conductor preferably has a watertight structure.
【０００９】[0009]
【作用】無水マレイン酸グラフトポリエチレンは、直流
電圧下では海水、真水等に浸水した状態でも、電気的特
性の低下がほとんどないことが明らかになった。すなわ
ち、直流下での水トリーの発生がほとんどなく、直流破
壊電圧や直流絶縁抵抗はむしろやや向上する傾向を示す
ことが、本発明者によって確認された。[Action] It has been clarified that the maleic anhydride-grafted polyethylene hardly deteriorates in electrical characteristics even in a state of being immersed in seawater, fresh water or the like under a DC voltage. That is, it has been confirmed by the present inventors that there is almost no occurrence of water trees under DC, and the DC breakdown voltage and DC insulation resistance tend to be rather improved.
【００１０】その理由は、無水マレイン酸グラフトポリ
エチレンのベースとなるポリエチレン部分は疎水性であ
り、水分をほとんど吸収しないが、グラフトされた無水
マレイン酸基が加水開環してカルボキシル基となり、こ
のカルボキシル基に直流高圧印可中の注入電荷やイオン
性キャリヤがトラップ（捕獲）され、これにより、絶縁
抵抗や破壊電圧が向上するものと考えられる。The reason is that the polyethylene portion serving as the base of the maleic anhydride-grafted polyethylene is hydrophobic and hardly absorbs water. It is considered that the injected charge and the ionic carrier during the application of the DC high voltage are trapped (trapped) on the basis thereof, thereby improving the insulation resistance and the breakdown voltage.
【００１１】このような観点から、絶縁体として無水マ
レイン酸グラフトポリエチレンを用いることで、絶縁体
に水分が浸入しても絶縁体の電気的特性が低下すること
がなく、ケーブル内に水分の浸入を防止する遮水層をあ
えて設ける必要はなくなる。また、密度が、０．９２５
ｇ／ｃｍ3以上の無水マレイン酸グラフトポリエチレン
を用いると、絶縁体の半径方向の熱膨張が小さくなり、
絶縁体の熱膨張の吸収のためのクッション層も不要とな
る。From such a viewpoint, by using maleic anhydride-grafted polyethylene as the insulator, even if moisture enters the insulator, the electrical characteristics of the insulator do not deteriorate, and moisture enters the cable. There is no need to dare to provide a water barrier layer for preventing water leakage. The density is 0.925
g / cm 3 or more of maleic anhydride-grafted polyethylene reduces the thermal expansion of the insulator in the radial direction,
A cushion layer for absorbing thermal expansion of the insulator is not required.
【００１２】さらに、無水マレイン酸のグラフト量を
０．０１〜５ｗｔ％とすることで直流絶縁特性も向上す
る。また、導体として、水密構造のものを用いることに
より、万一ケーブル内に浸水すると遮水層がないため、
水が導体にまで浸入する可能性があるが、導体が水密構
造であると、水が導体内を走ることがなく、浸水による
被害を狭い範囲に食い止めることができる。Further, by setting the grafting amount of maleic anhydride to 0.01 to 5% by weight, the DC insulation characteristics are also improved. Also, by using a water-tight structure as the conductor, if there is no water impervious layer in the event of inundation in the cable,
Although there is a possibility that water may penetrate into the conductor, if the conductor has a watertight structure, water does not run in the conductor, and damage due to flooding can be suppressed to a narrow range.
【００１３】[0013]
【発明の実施の形態】以下、本発明を詳しく説明する。
図１は、本発明の直流電力ケーブルの一例を示すもの
で、海底ケーブル用の仕様のものである。図１中符号１
１は導体を示す。この導体１１上には、内部半導電層１
２、絶縁体１３、外部半導電層１４、遮蔽層１５、防食
層１６および外装１７が順次設けられている。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail.
FIG. 1 shows an example of a DC power cable of the present invention, which is a specification for a submarine cable. 1 in FIG.
1 indicates a conductor. On this conductor 11, the inner semiconductive layer 1
2, an insulator 13, an outer semiconductive layer 14, a shielding layer 15, an anticorrosion layer 16, and an exterior 17 are sequentially provided.
【００１４】上記導体１１は、素線として多数本の平角
導体を用い、これを整列状態で撚り合わせたセグメンタ
ル導体であり、導体占積率が高く、素線間の空隙がほと
んどないものである。内部半導電層１２および外部半導
電層１４は、エチレンー酢酸ビニル共重合体、エチレン
ーエチルアクリレート共重合体などにカーボンブラック
を配合した半導電性樹脂組成物からなるものである。The conductor 11 is a segmental conductor obtained by using a number of rectangular conductors as strands and twisting them in an aligned state. The conductor 11 has a high conductor space factor and has almost no gap between the strands. is there. The inner semiconductive layer 12 and the outer semiconductive layer 14 are made of a semiconductive resin composition obtained by blending carbon black with an ethylene-vinyl acetate copolymer, an ethylene-ethyl acrylate copolymer, or the like.
【００１５】絶縁体１３は、密度０．９２５ｇ／ｃｍ3
以上、好ましくは密度０．９４０ｇ／ｃｍ3以上の無水
マレイン酸グラフト高密度ポリエチレンからなってい
る。一般に、ポリエチレンは、その密度が大きくなると
結晶化度が高くなり、その熱膨張率が小さくなる特性を
有している。例えば、密度０．９５ｇ／ｃｍ3の高密度
ポリエチレンの熱膨張は、密度０．９２ｇ／ｃｍ3の低
密度ポリエチレンの熱膨張に比較して、室温から８０℃
の間で、３０〜４０％程度となる。このため、密度０．
９２５ｇ／ｃｍ3以上の無水マレイン酸グラフトポリエ
チレンでもその熱膨張は小さいものとなる。The insulator 13 has a density of 0.925 g / cm 3.
As described above, it is preferably made of maleic anhydride-grafted high-density polyethylene having a density of 0.940 g / cm 3 or more. In general, polyethylene has such a characteristic that as its density increases, the degree of crystallinity increases and its coefficient of thermal expansion decreases. For example, the thermal expansion of high-density polyethylene with a density of 0.95 g / cm 3 is from room temperature to 80 ° C. as compared to the thermal expansion of low-density polyethylene with a density of 0.92 g / cm 3.
Between about 30 to 40%. For this reason, density 0.
Even maleic anhydride-grafted polyethylene of 925 g / cm 3 or more has a small thermal expansion.
【００１６】また、密度０．９２５ｇ／ｃｍ3以上の無
水マレイン酸グラフトポリエチレンは、荷電時の空間電
荷の蓄積が少なく、直流絶縁性能が極めて優れているこ
とが知られている（特公平６ー１６３６６号公報参
照）。これは、無水マレイン酸グラフトポリエチレンの
分子内に存在するカルボニル基が、電子親和性あるいは
電子共鳴性に富み、このカルボニル基が適量存在するこ
とで、注入される空間電荷のトラップを低減させるため
である。したがって、この絶縁体１３は、熱膨張が小さ
く、しかも優れた直流絶縁特性を有するものとなる。It is known that maleic anhydride-grafted polyethylene having a density of 0.925 g / cm 3 or more has a small accumulation of space charge at the time of charging, and has extremely excellent DC insulation performance (Japanese Patent Publication No. 6-1994). No. 16366). This is because the carbonyl group present in the molecule of the maleic anhydride-grafted polyethylene is rich in electron affinity or electron resonance, and the presence of an appropriate amount of this carbonyl group reduces trapping of injected space charges. is there. Therefore, the insulator 13 has a small thermal expansion and excellent DC insulation characteristics.
【００１７】この絶縁体１３をなす無水マレイン酸グラ
フトポリエチレンにおける無水マレイン酸のグラフト量
は、０．０１〜５重量％、好ましくは０．２〜１重量％
がよく、０．０１重量％未満では直流絶縁特性の向上が
なく、５重量％を越えると結晶化度の低下を招いて、絶
縁破壊強度の低下を引き起こす。また、メルトフローレ
イトは、ケーブルへの押出加工性を考慮すると、０．０
５〜１０ｇ／分とすることが好ましい。この無水マレイ
ン酸グラフトポリエチレンの製造は、低密度ポリエチレ
ン、直鎖状低密度ポリエチレン、高密度ポリエチレンな
どのポリエチレンに無水マレイン酸と触媒としての有機
過酸化物などのラジカル発生剤を添加し、加熱、混練し
てグラフト重合する方法で行われる。The grafted amount of maleic anhydride in the maleic anhydride-grafted polyethylene constituting the insulator 13 is 0.01 to 5% by weight, preferably 0.2 to 1% by weight.
When the content is less than 0.01% by weight, the DC insulation characteristics are not improved. When the content is more than 5% by weight, the degree of crystallinity is reduced, and the dielectric breakdown strength is reduced. In addition, the melt flow rate is 0.0
It is preferably 5 to 10 g / min. This maleic anhydride grafted polyethylene is produced by adding a maleic anhydride and a radical generator such as an organic peroxide as a catalyst to polyethylene such as low-density polyethylene, linear low-density polyethylene, or high-density polyethylene, heating, Kneading and graft polymerization are performed.
【００１８】遮蔽層１５は、耐食性の優れた金属テー
プ、例えば厚み０．０５〜０．５ｍｍのステンレス鋼テ
ープ、スズメッキ銅テープなどを、外部半導電層１４の
上に横巻きに重ねて巻き回してなるものである。The shielding layer 15 is formed by winding a metal tape having excellent corrosion resistance, for example, a stainless steel tape having a thickness of 0.05 to 0.5 mm, a tin-plated copper tape or the like on the outer semiconductive layer 14 in a horizontal direction. It is.
【００１９】防食層１６は、この遮水層１５の上に低密
度ポリエチレン、高密度ポリエチレンなどの耐食性の優
れた熱可塑性樹脂を押出被覆して形成したものである。
また、外装１７は、防食層１６上に亜鉛メッキ鋼線を密
に巻き回し、これにタールエポキシ樹脂系などの防食塗
料を塗布したもので、敷設の際の外傷などからケーブル
を保護するためのものある。The anticorrosion layer 16 is formed by extrusion-coating a thermoplastic resin having excellent corrosion resistance such as low-density polyethylene and high-density polyethylene on the water-blocking layer 15.
Further, the exterior 17 is formed by densely winding a galvanized steel wire on the anticorrosion layer 16 and applying an anticorrosion paint such as a tar epoxy resin to the cable to protect the cable from external damage at the time of laying. There is something.
【００２０】このような構造の直流ケーブルにあって
は、遮水層およびクッション層を欠くものであるので、
軽量で、仕上がり外径が細く、熱放散性が良好なものに
なる。すなわち、鉛被などの厚い金属製の遮水層が無
く、万一ケーブル内に浸水しても上述のように絶縁体の
直流電気的特性の低下がないため、実用上の不都合は何
ら生じない。The DC cable having such a structure lacks the water-impervious layer and the cushion layer.
It is lightweight, has a small finished outer diameter, and has good heat dissipation. In other words, there is no thick metal waterproof layer such as lead coating, and even if the cable is immersed in the cable, the DC electrical characteristics of the insulator do not decrease as described above, so that there is no practical inconvenience. .
【００２１】また、通電による絶縁体の熱膨張が小さい
ために、クッション層が不要となり、熱障壁がなくなっ
て、絶縁体の熱の外部への放散が良好になる。さらに、
クッション層が不要になれば、ここに水が貯まる恐れも
なく、これによっても遮水層が不要となる。また、水密
構造のセグメンタル導体を使用しているので、万一導体
にまで水が浸入しても、セグメンタル導体の各素線間に
空隙がほとんどないため、水が導体内を走ることがな
く、浸水による被害を局部的に抑えることができる。Further, since the thermal expansion of the insulator due to energization is small, the cushion layer becomes unnecessary, and the heat barrier is eliminated, so that the heat of the insulator can be radiated to the outside. further,
If the cushion layer is no longer needed, there is no danger that water will accumulate here. In addition, since a watertight segmental conductor is used, even if water enters the conductor, there is almost no gap between each of the segmental conductor wires, so water may run inside the conductor. Therefore, damage due to inundation can be locally suppressed.
【００２２】なお、本発明の直流電力ケーブルでは、導
体としてセグメンタル導体以外に、素線として通常の丸
線を撚り合わせたものでもよい。また、無水マレイン酸
グラフトポリエチレンの密度およびグラフト量は、上記
範囲に限定されるされるものでないが、上記範囲とする
ことが現実的ではある。In the DC power cable of the present invention, in addition to the segmental conductor, a normal round wire may be twisted as a strand. In addition, the density and the graft amount of the maleic anhydride-grafted polyethylene are not limited to the above ranges, but it is realistic to set the above ranges.
【００２３】以下、具体例を示す。導体断面積１０００
ｍｍ2のセグメンタル導体上に、内部半導電層、密度
０．９５ｇ／ｃｍ3の無水マレイン酸グラフト高密度ポ
リエチレン（無水マレイン酸グラフト量約０．２重量
％）からなる厚み１２ｍｍの絶縁体、外部半導電層を３
層同時押出被覆してケーブルコアとした。Hereinafter, specific examples will be described. Conductor cross-sectional area 1000
on segmental conductor mm 2, the inner semiconducting layer, an insulator of a density 0.95 g / cm thickness 12mm made of 3 maleic anhydride-grafted high density polyethylene (about 0.2 wt% grafted maleic anhydride content), 3 external semiconductive layers
The layers were co-extruded into a cable core.
【００２４】このケーブルコアの上に、厚み０．１ｍｍ
のステンレス鋼テープを巻き回して遮蔽層を設け、この
上にポリエチレンの防食層を押出被覆し、さらにこの上
に亜鉛メッキ鋼線を巻き回しタールエポキシ系防食塗料
を塗布して外装を設けて海底用ケーブルとした。On this cable core, a thickness of 0.1 mm
A stainless steel tape is wound around to provide a shielding layer, a polyethylene anticorrosive layer is extrusion-coated on this, and a galvanized steel wire is further wound around this, and a tar epoxy-based anticorrosive paint is applied to provide an exterior, and the seabed is provided. Cable.
【００２５】このケーブルに対し、海水浸漬下、以下の
条件で直流長期課通電試験を行った。すなわち、導体温
度が室温〜９０℃、８時間ＯＮ、１６時間ＯＦＦのヒー
トサイクル下で、 ＋ＤＣ ５４０ｋＶ １０サイクル、 −ＤＣ ５４０ｋＶ １０サイクル、 ±ＤＣ極性反転 ４８０ｋＶ １０サイクルを行っ
た。This cable was subjected to a long-term direct current application test under seawater immersion under the following conditions. That is, 10 cycles of + DC 540 kV, 10 cycles of −DC 540 kV, and 10 cycles of ± DC polarity inversion 480 kV were performed under a heat cycle in which the conductor temperature was from room temperature to 90 ° C., ON for 8 hours, and OFF for 16 hours.
【００２６】上記課通電試験後、９０℃での残存破壊電
圧を測定した結果、ＤＣ→１４０ｋＶ／ｍｍ、インパル
ス→１３０ｋＶ／ｍｍであり、初期特性（課通電試験
前）と同等であった。また、絶縁体として、密度０．９
３０ｇ／ｃｍ3の無水マレイン酸グラフト低密度ポリエ
チレン（無水マレイン酸グラフト量０．０３重量％）を
用いて同様のケーブルを作製し、同様の直流課通電試験
を実施し、９０℃での残存破壊電圧を測定した結果、Ｄ
Ｃ→１２０ｋＶ／ｍｍ、インパルス→１１０ｋＶ／ｍｍ
であり、初期特性（課通電試験前）と同等であった。こ
の結果から、遮水層を有しないケーブルでも、優れた直
流電気特性を発揮することが判明した。After the application test, the residual breakdown voltage at 90 ° C. was measured. As a result, DC → 140 kV / mm and impulse → 130 kV / mm, which were equivalent to the initial characteristics (before the application test). Further, as an insulator, a density of 0.9
A similar cable was produced using maleic anhydride-grafted low-density polyethylene (maleic anhydride graft amount: 0.03% by weight) of 30 g / cm 3 , a similar direct current application test was carried out, and residual breakdown at 90 ° C. As a result of measuring the voltage, D
C → 120 kV / mm, impulse → 110 kV / mm
And was equivalent to the initial characteristics (before the current application test). From this result, it was found that even a cable without a water barrier layer exhibited excellent DC electric characteristics.
【００２７】[0027]
【発明の効果】以上説明したように、本発明の直流電力
ケーブルは、無水マレイン酸グラフト高密度ポリエチレ
ンからなる絶縁体を有し、遮水層を有しないものであ
る。このため、軽量で仕上がり外径が細く、安価なケー
ブルとなる。また、無水マレイン酸グラフトポリエチレ
ンの密度が０．９２５ｇ／ｃｍ3以上のものを用いれば
クッション層も不要になり一層軽量、細径化が可能とな
る。さらに、無水マレイン酸のグラフト量が０．０１〜
５ｗｔ％のものを用いれば、直流電気的特性が更に向上
する。また、水密構造の導体を使用すれば、走水を防
ぎ、浸水被害を最小限に抑えることができる。As described above, the DC power cable of the present invention has an insulator made of maleic anhydride-grafted high-density polyethylene and does not have a water barrier layer. Therefore, the cable is lightweight, has a small finished outer diameter, and is inexpensive. If a maleic anhydride-grafted polyethylene having a density of 0.925 g / cm 3 or more is used, a cushion layer is not required, and the weight and diameter can be further reduced. Further, the graft amount of maleic anhydride is 0.01 to
If 5 wt% is used, the DC electrical characteristics are further improved. In addition, if a conductor having a watertight structure is used, it is possible to prevent water running and to minimize damage caused by inundation.
【図１】本発明の直流電力ケーブルの一例を示す概略断
面図である。FIG. 1 is a schematic sectional view showing an example of a DC power cable of the present invention.
【図２】従来の直流電力ケーブルを示す概略断面図であ
る。FIG. 2 is a schematic sectional view showing a conventional DC power cable.
１３・・・絶縁体。 13 ... an insulator.
Claims (4)
レンからなる絶縁体が設けられたケーブルであって、 ケーブル内への水の浸入を防ぐ遮水層を有しないことを
特徴とする直流電力ケーブル。1. A DC power cable comprising a conductor and an insulator made of maleic anhydride-grafted polyethylene provided on a conductor, wherein the DC power cable does not have a water barrier layer for preventing water from entering the cable.
度が０．９２５ｇ／ｃｍ3以上であることを特徴とする
請求項１記載の直流電力ケーブル。2. The DC power cable according to claim 1, wherein the density of the maleic anhydride-grafted polyethylene is 0.925 g / cm 3 or more.
水マレイン酸グラフト量が０．０１〜５ｗｔ％であるこ
とを特徴とする請求項１記載の直流電力ケーブル。3. The DC power cable according to claim 1, wherein the maleic anhydride-grafted polyethylene has a grafted amount of maleic anhydride of 0.01 to 5 wt%.
求項１記載の直流電力ケーブル。4. The DC power cable according to claim 1, wherein the conductor has a watertight structure.