JP2002228829A - Optical filter - Google Patents
Optical filterInfo
- Publication number
- JP2002228829A JP2002228829A JP2001027450A JP2001027450A JP2002228829A JP 2002228829 A JP2002228829 A JP 2002228829A JP 2001027450 A JP2001027450 A JP 2001027450A JP 2001027450 A JP2001027450 A JP 2001027450A JP 2002228829 A JP2002228829 A JP 2002228829A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- optical filter
- refractive index
- group
- filter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、光学フィルターに
関し、詳しくは、特定のスクアリリウム色素を含有する
ことで、画像表示装置、特に、プラズマディスプレイパ
ネル（ＰＤＰ）用のフィルターとして好適な光学フィル
ターに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical filter, and more particularly to an optical filter which contains a specific squarylium dye and is suitable as a filter for an image display device, particularly, a plasma display panel (PDP). It is.
【０００２】[0002]
【従来の技術及び発明が解決しようとする課題】近年、
多種の画像表示装置（ディスプレイ）、例えば、液晶表
示装置（ＬＣＤ）、プラズマディスプレイパネル（ＰＤ
Ｐ）、エレクトロルミネッセンスディスプレイ（ＥＬ
Ｄ）、陰極管表示装置（ＣＲＴ）、蛍光表示管、電界放
射型ディスプレイの開発とこれらを組み込んだ機器が実
用化されている。これらの各種画像表示装置の中でも、
ハイビジョン用大型壁掛けテレビ、マルチメディア用大
画面ディスプレイとしてカラープラズマディスプレイ
（ＰＤＰ）が注目を浴びている。2. Description of the Related Art In recent years,
Various types of image display devices (displays), for example, a liquid crystal display (LCD), a plasma display panel (PD)
P), electroluminescent display (EL)
D), a cathode ray tube display (CRT), a fluorescent display tube, and a field emission type display, and a device incorporating these have been put to practical use. Among these various image display devices,
A color plasma display (PDP) has attracted attention as a large wall-mounted television for high-definition television and a large-screen display for multimedia.
【０００３】これらの画像表示装置は、原則として、
赤、青、緑の三原色の光の組合せでカラー画像を表示す
る。しかし、表示のための光を理想的な三原色にするこ
とは、実質的には不可能である。例えば、プラズマディ
スプレイパネル（ＰＤＰ）は、波長が５００〜６２０ｎ
ｍの範囲に三原色蛍光体からの発光に余分な光が含まれ
ていることが知られている。そこで、色補正を行うため
の特定の波長の光を吸収するフィルターを用いて、色補
正を行うことが提案されている。フィルターによる色補
正は、例えば、特開昭５８−１５３９０４号公報、特開
昭６１−１８８５０１号公報、特開平３−２３１９８８
号公報、特開平５−２０５６４３号公報、特開平９−１
４５９１８号公報、特開平９−３０６３６６号公報、特
開平１０−２６７０９号公報、特開２０００−１９３８
２０号公報、特開２０００−２４１６２０号公報、特開
２０００−２５０４２０号公報、特開２０００−２６６
９３０号公報等に記載されている。[0003] These image display devices are, in principle,
A color image is displayed using a combination of the three primary colors of red, blue, and green. However, it is practically impossible to make light for display ideal three primary colors. For example, a plasma display panel (PDP) has a wavelength of 500 to 620 n.
It is known that light emitted from the three primary color phosphors contains extra light in the range of m. Therefore, it has been proposed to perform color correction using a filter that absorbs light of a specific wavelength for performing color correction. Color correction using a filter is described in, for example, JP-A-58-153904, JP-A-61-188501, and JP-A-3-231988.
JP, JP-A-5-205643, JP-A-9-19-1
JP-A-45918, JP-A-9-306366, JP-A-10-26709, JP-A-2000-1938
No. 20, JP-A-2000-241620, JP-A-2000-250420, JP-A-2000-266
No. 930, for example.
【０００４】フィルターによる色補正には特定の波長に
吸収を有する色素が用いられ、具体的には、スクアリリ
ウム系、アゾメチン系、シアニン系、オキソノール系、
キサンテン系、アゾ系等の色素が挙げられる。しかしな
がら、これまで使用されてきた色素では、その吸収が不
十分であったり、特定波長以外の領域まで吸収したり、
満足できるものは得られていない。For color correction by a filter, a dye having absorption at a specific wavelength is used. Specifically, squarylium, azomethine, cyanine, oxonol,
Xanthene-based and azo-based dyes are exemplified. However, the dyes that have been used up to now have insufficient absorption or absorb to regions other than specific wavelengths,
No satisfactory has been obtained.
【０００５】従って、本発明の目的は、特定波長におい
てシャープな吸収（λｍａｘ５６０〜６２０ｎｍ、半値
巾５０ｎｍ以下）を有する画像表示装置用の光学フィル
ターを提供することである。Accordingly, it is an object of the present invention to provide an optical filter for an image display device having sharp absorption (λ max 560 to 620 nm, half width at 50 nm or less) at a specific wavelength.
【０００６】[0006]
【課題を解決するための手段】本発明者等は、検討を重
ねた結果、特定のスクアリリウム化合物を使用してなる
光学フィルターが、特定の波長にシャープな吸収を有す
ることで画像表示装置の画像特性を著しく改善し得るこ
とを見出し、本発明に到達した。As a result of repeated studies, the present inventors have found that an optical filter using a specific squarylium compound has sharp absorption at a specific wavelength, so that an image of an image display device can be obtained. The inventors have found that the characteristics can be significantly improved, and arrived at the present invention.
【０００７】本発明は、上記知見に基づいてなされたも
ので、下記一般式（Ｉ）で表される化合物を含有するこ
とを特徴とする光学フィルターを提供するものである。The present invention has been made based on the above findings, and provides an optical filter containing a compound represented by the following general formula (I).
【化２】 Embedded image
【０００８】[0008]
【発明の実施の形態】以下、上記要旨をもってなる本発
明の光学フィルターについてさらに詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the optical filter of the present invention having the above gist will be described in more detail.
【０００９】上記一般式（Ｉ）において、Ｒ1 で表され
る有機基としては、メチル、エチル、プロピル、イソプ
ロピル、ブチル、第二ブチル、第三ブチル、イソブチ
ル、アミル、イソアミル、第三アミル、ヘキシル、シク
ロヘキシル、シクロヘキシルメチル、２−シクロヘキシ
ルエチル、ヘプチル、イソヘプチル、第三ヘプチル、ｎ
−オクチル、イソオクチル、第三オクチル、２−エチル
ヘキシル、ノニル、イソノニル、デシル、ドデシル、ト
リデシル、テトラデシル、ペンタデシル、ヘキサデシ
ル、ペプタデシル、オクタデシル等のアルキル基、ビニ
ル、１−メチルエテニル、２−メチルエテニル、プロペ
ニル、ブテニル、イソブテニル、ペンテニル、ヘキセニ
ル、ヘプテニル、オクテニル、デセニル、ぺンタデセニ
ル、１−フェニルプロペン−３−イル等のアルケニル
基、フェニル、ナフチル、２−メチルフェニル、３−メ
チルフェニル、４−メチルフェニル、４−ビニルフェニ
ル、３−イソプロピルフェニル、４−イソプロピルフェ
ニル、４−ブチルフェニル、４−イソブチルフェニル、
４−第三ブチルフェニル、４−ヘキシルフェニル、４−
シクロヘキシルフェニル、４−オクチルフェニル、４−
（２−エチルヘキシル）フェニル、４−ステアリルフェ
ニル、２，３−ジメチルフェニル、２，４−ジメチルフ
ェニル、２，５−ジメチルフェニル、２，６−ジメチル
フェニル、３，４−ジメチルフェニル、３，５−ジメチ
ルフェニル、２，４−ジ第三ブチルフェニル、シクロヘ
キシルフェニル等のアルキルアリール基、ベンジル、フ
ェネチル、２−フェニルプロパン−２−イル、ジフェニ
ルメチル、トリフェニルメチル、スチリル、シンナミル
等のアリールアルキル基等、それがエーテル結合、チオ
エーテル結合で中断されたもの、例えば、２−メトキシ
エチル、３−メトキシプロピル、４−メトキシブチル、
２−ブトキシエチル、メトキシエトキシエチル、メトキ
シエトキシエトキシエチル、３−メトキシブチル、２−
フェノキシエチル、３−フェノキシプロピル、２−メチ
ルチオエチル、２−フェニルチオエチルが挙げられ、更
にこれらの基は、アルコキシ基、アルケニル基、ニトロ
基、シアノ基、ハロゲン原子等で置換されていてもよ
い。In the general formula (I), examples of the organic group represented by R 1 include methyl, ethyl, propyl, isopropyl, butyl, sec-butyl, tert-butyl, isobutyl, amyl, isoamyl, tert-amyl, Hexyl, cyclohexyl, cyclohexylmethyl, 2-cyclohexylethyl, heptyl, isoheptyl, tertiary heptyl, n
-Alkyl groups such as octyl, isooctyl, tertiary octyl, 2-ethylhexyl, nonyl, isononyl, decyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, peptadecyl, octadecyl, vinyl, 1-methylethenyl, 2-methylethenyl, propenyl, butenyl Alkenyl groups such as isobutenyl, pentenyl, hexenyl, heptenyl, octenyl, decenyl, pentadecenyl, 1-phenylpropen-3-yl, phenyl, naphthyl, 2-methylphenyl, 3-methylphenyl, 4-methylphenyl, 4- Vinylphenyl, 3-isopropylphenyl, 4-isopropylphenyl, 4-butylphenyl, 4-isobutylphenyl,
4-tert-butylphenyl, 4-hexylphenyl, 4-
Cyclohexylphenyl, 4-octylphenyl, 4-
(2-ethylhexyl) phenyl, 4-stearylphenyl, 2,3-dimethylphenyl, 2,4-dimethylphenyl, 2,5-dimethylphenyl, 2,6-dimethylphenyl, 3,4-dimethylphenyl, 3,5 -Alkylaryl groups such as -dimethylphenyl, 2,4-ditert-butylphenyl and cyclohexylphenyl, and arylalkyl groups such as benzyl, phenethyl, 2-phenylpropan-2-yl, diphenylmethyl, triphenylmethyl, styryl and cinnamyl And the like, in which it is interrupted by an ether bond, a thioether bond, for example, 2-methoxyethyl, 3-methoxypropyl, 4-methoxybutyl,
2-butoxyethyl, methoxyethoxyethyl, methoxyethoxyethoxyethyl, 3-methoxybutyl,
Phenoxyethyl, 3-phenoxypropyl, 2-methylthioethyl, 2-phenylthioethyl, and these groups may be further substituted with an alkoxy group, an alkenyl group, a nitro group, a cyano group, a halogen atom, or the like. .
【００１０】Ｒ2 及びＲ3 で表されるアルキル基として
は、例えば、メチル、エチル、プロピル、イソプロピ
ル、ブチル、イソブチル、第二ブチル、第三ブチル、ア
ミル、イソアミル、第三アミル、ヘキシル、ヘプチル、
オクチル、ノニル、デシル等の飽和基、あるいは、ビニ
ル、アリル等の不飽和基が挙げられ、また、これらのア
ルキル基はハロゲン原子、アルコキシ基、アシル基等に
よって置換されたものでもよく、アリール基としては、
例えば、フェニル、トリル、キシリル、エチルフェニ
ル、プロピルフェニル、ブチルフェニル、第三ブチルフ
ェニル、ノニルフェニル、ナフチル等の基が挙げられ
る。The alkyl group represented by R 2 and R 3 includes, for example, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, tert-butyl, amyl, isoamyl, tert-amyl, hexyl, heptyl ,
Saturated groups such as octyl, nonyl, and decyl; and unsaturated groups such as vinyl and allyl may be mentioned.Alkyl groups may be substituted with a halogen atom, an alkoxy group, an acyl group, or the like. as,
For example, groups such as phenyl, tolyl, xylyl, ethylphenyl, propylphenyl, butylphenyl, tertiary butylphenyl, nonylphenyl, naphthyl and the like can be mentioned.
【０００９Ｂ】Ｒ3 で表されるアルコキシ基としては、
例えば、メトキシ、エトキシ、プロポキシ、ブトキシ等
が挙げられる。The alkoxy group represented by R 3 includes:
For example, methoxy, ethoxy, propoxy, butoxy and the like can be mentioned.
【００１１】Ｒ3 で表されるハロゲン原子としては、例
えば、フッ素、塩素、臭素、ヨウ素等が挙げられる。Examples of the halogen atom represented by R 3 include fluorine, chlorine, bromine and iodine.
【００１２】本発明に係る上記一般式（Ｉ）で表される
スクアリリウム化合物の具体的な例を下記に示すが、こ
れによって本発明は制限されるものではない。Specific examples of the squarylium compound represented by the general formula (I) according to the present invention are shown below, but the present invention is not limited thereto.
【００１３】[0013]
【化３】 Embedded image
【００１４】[0014]
【化４】 Embedded image
【００１５】[0015]
【化５】 Embedded image
【００１６】[0016]
【化６】 Embedded image
【００１７】[0017]
【化７】 Embedded image
【００１８】[0018]
【化８】 Embedded image
【００１９】[0019]
【化９】 Embedded image
【００２０】[0020]
【化１０】 Embedded image
【００２１】[0021]
【化１１】 Embedded image
【００２２】[0022]
【化１２】 Embedded image
【００２３】[0023]
【化１３】 Embedded image
【００２４】[0024]
【化１４】 Embedded image
【００２５】[0025]
【化１５】 Embedded image
【００２６】[0026]
【化１６】 Embedded image
【００２７】[0027]
【化１７】 Embedded image
【００２８】[0028]
【化１８】 Embedded image
【００２９】本発明に係る上記一般式（Ｉ）で表される
化合物は、その製造法によって制限を受けることなく、
従来周知の方法に準じて製造することができ、例えば、
以下のルートで合成される。The compound represented by the above general formula (I) according to the present invention is not limited by its production method,
It can be manufactured according to a conventionally known method, for example,
It is synthesized by the following route.
【００３０】[0030]
【化１９】 Embedded image
【００３１】上記スクアリリウム化合物の使用量は、光
学フィルターの単位面積当たり１〜１０００ｍｇ／
ｍ2 、好ましくは５〜１００ｍｇ／ｍ2 であり、１ｍｇ
／ｍ2 未満の使用量では、色補正効果を十分に発揮する
ことができず、１０００ｍｇ／ｍ 2 を超えて使用した場
合には、フィルターの青みが強くなりすぎてグレーに補
正する必要が出てくるおそれがあり、色素の配合量が増
えることで明度が低下するおそれもあるため好ましくな
い。The amount of the squarylium compound used is
1-1000mg / unit area of the chemical filter
mTwo, Preferably 5 to 100 mg / mTwoAnd 1 mg
/ MTwoWith less than the amount used, the color correction effect is fully exhibited
1000mg / m TwoPlaces used beyond
If the filter becomes too bluish and becomes gray
May need to be corrected.
It is not preferable because the brightness may decrease
No.
【００３２】本発明の光学フィルターには、上記特定の
スクアリリウム化合物（色素）の他に、補助的に他の光
吸収性の色素を使用することもでき、これら他の光吸収
性色素としては、例えば、シアニン色素、上記以外のス
クアリリウム色素、アゾメチン色素、オキソノール色
素、アゾ色素、ベンジリデン色素、キサンテン色素等が
挙げられる。In the optical filter of the present invention, other light absorbing dyes may be used in addition to the above-mentioned specific squarylium compound (dye). Examples thereof include cyanine dyes, squarylium dyes other than those described above, azomethine dyes, oxonol dyes, azo dyes, benzylidene dyes, and xanthene dyes.
【００３３】これらの色素の光あるいは熱に対する安定
化を図る目的で各種安定化剤を使用することができる。
安定化剤としては、例えば、ハイドロキノン誘導体（米
国特許３９３５０１６号公報、米国特許３９８２９４４
号公報）、ハイドロキノンジエーテル誘導体（米国特許
４２５４２１６号公報）、フェノール誘導体（特開昭５
４−２１００４号公報）、スピロインダン又はメチレン
ジオキシベンゼンの誘導体（英国特許公開２０７７４５
５号公報、英国特許２０６２８８８号公報）、クロマ
ン、スピロクロマン又はクマランの誘導体（米国特許３
４３２３００号公報、米国特許３５７３０５０号公報、
米国特許３５７４６２７号公報、米国特許３７６４３３
７号公報、特開昭５２−１５２２２５号公報、特開昭５
３−２０３２７号公報、特開昭５３−１７７２９号公
報、特開昭６１−９０１５６号公報）、ハイドロキノン
モノエーテル又はパラアミノフェノールの誘導体（英国
特許１３４７５５６号、英国特許２０６６９７５号公
報、特公昭５４−１２３３７号公報、特開昭５５−６３
２１号公報）、ビスフェノール誘導体（米国特許３７０
０４５５号公報、特公昭４８−３１６２５号公報）、金
属錯体（米国特許４２４５０１８号公報、特開昭６０−
９７３５３号公報）、ニトロソ化合物（特開平２−３０
０２８８号公報）、ジインモニウム化合物（米国特許４
６５６１２号公報）、ニッケル錯体（特開平４−１４６
１８９号公報）、酸化防止剤（欧州特許８２００５７号
公報）等が挙げられる。Various stabilizers can be used for the purpose of stabilizing these dyes against light or heat.
Examples of the stabilizer include hydroquinone derivatives (US Pat. No. 3,935,016, US Pat. No. 3,982,944).
), Hydroquinone diether derivatives (US Pat. No. 4,254,216), and phenol derivatives (JP-A-5
No. 4-22004), spiroindane or a derivative of methylenedioxybenzene (UK Patent Publication No. 207745).
No. 5, British Patent No. 2062888), chroman, spirochroman or a derivative of coumaran (US Pat.
432300, US Pat. No. 3,573,050,
U.S. Pat. No. 3,574,627, U.S. Pat.
No. 7, JP-A-52-152225, JP-A-5-152225
JP-A-3-20327, JP-A-53-17729, JP-A-61-90156), hydroquinone monoether or paraaminophenol derivatives (British Patent No. 1347556, British Patent No. 2066975, Japanese Patent Publication No. 54-12337) No., JP-A-55-63
No. 21), bisphenol derivatives (US Pat. No. 370)
0455, JP-B-48-31625), metal complexes (U.S. Pat.
97353), a nitroso compound (JP-A-2-30)
0288), diimmonium compounds (US Pat.
No. 65612), a nickel complex (JP-A-4-146).
189), antioxidants (European Patent No. 820057) and the like.
【００３４】本発明の光学フィルターは、少なくとも上
記スクアリリウム化合物を含む層を有する光学フィルタ
ーであり、その形状に関しては特に制限されるものでは
ないが、通常、透明支持体に必要に応じて下塗り層、反
射防止層、ハードコート層、潤滑層等各層を設けてなる
ものであり、上記スクアリリウム色素を用いて光学フィ
ルターを製造する方法は、特に限定されるものではな
く、例えば、透明支持体又は任意の各層に含有させる方
法、透明支持体又は任意の各層にコーティングする方
法、各層間のバインダー（接着剤）に混入させる方法あ
るいは別にフィルター層を設ける方法等が挙げられる。The optical filter of the present invention is an optical filter having at least a layer containing the squarylium compound. The shape of the optical filter is not particularly limited. An antireflection layer, a hard coat layer, a layer provided with a lubricating layer, etc., the method of producing an optical filter using the squarylium dye is not particularly limited, for example, a transparent support or any Examples of the method include a method in which each layer is incorporated, a method in which a transparent support or any arbitrary layer is coated, a method in which it is mixed with a binder (adhesive) between the layers, and a method in which a filter layer is separately provided.
【００３５】別にフィルター層を設ける場合には、上記
スクアリリウム化合物をそのまま使用することもできる
が、通常はバインダーを使用する。これらバインダーと
しては、例えば、ゼラチン、カゼイン、澱粉、セルロー
ス誘導体、アルギン酸等の天然高分子材料、あるいはポ
リメチルメタクリレート、ポリビニルブチラール、ポリ
ビニルピロリドン、ポリビニルアルコール、ポリ塩化ビ
ニル、スチレン−ブタジエンコポリマー、ポリスチレ
ン、ポリカーボネート、ポリアミド等の合成高分子材料
が用いられる。When a separate filter layer is provided, the above squarylium compound can be used as it is, but usually a binder is used. As these binders, for example, gelatin, casein, starch, cellulose derivatives, natural polymer materials such as alginic acid, or polymethyl methacrylate, polyvinyl butyral, polyvinyl pyrrolidone, polyvinyl alcohol, polyvinyl chloride, styrene-butadiene copolymer, polystyrene, polycarbonate And a synthetic polymer material such as polyamide.
【００３６】上記透明支持体の材料としては、例えば、
ガラス等の無機材料；あるいは、例えば、ジアセチルセ
ルロース、トリアセチルセルロース（ＴＡＣ）、プロピ
オニルセルロース、ブチリルセルロース、アセチルプロ
ピオニルセルロース、ニトロセルロース等のセルロース
エステル；ポリアミド；ポリカーボネート；ポリエチレ
ンテレフタレート、ポリエチレンナフタレート、ポリブ
チレンテレフタレート、ポリ−１，４−シクロヘキサン
ジメチレンテレフタレート、ポリエチレン−１，２−ジ
フェノキシエタン−４，４' −ジカルボキシレート、ポ
リブチレンテレフタレート等のポリエステル；ポリスチ
レン；ポリエチレン、ポリプロピレン、ポリメチルペン
テン等のポリオレフィン；ポリメチルメタクリレート等
のアクリル系樹脂；ポリカーボネート；ポリスルホン；
ポリエーテルスルホン；ポリエーテルケトン；ポリエー
テルイミド；ポリオキシエチレン等の高分子材料が挙げ
られる。As the material of the transparent support, for example,
Inorganic materials such as glass; or cellulose esters such as diacetylcellulose, triacetylcellulose (TAC), propionylcellulose, butyrylcellulose, acetylpropionylcellulose, and nitrocellulose; polyamides; polycarbonates; Polyesters such as butylene terephthalate, poly-1,4-cyclohexane dimethylene terephthalate, polyethylene-1,2-diphenoxyethane-4,4'-dicarboxylate and polybutylene terephthalate; polystyrene; polyethylene, polypropylene, polymethylpentene, etc. Polyolefin; acrylic resin such as polymethyl methacrylate; polycarbonate; polysulfone;
Polymer materials such as polyether sulfone; polyether ketone; polyether imide; and polyoxyethylene.
【００３７】透明支持体の透過率は８０％以上であるこ
とが好ましく、８６％以上であることがさらに好まし
い。ヘイズは２％以下であることが好ましく、１％以下
であることがさらに好ましい。また、屈折率は１．４５
〜１．７０であることが好ましい。The transmittance of the transparent support is preferably at least 80%, more preferably at least 86%. The haze is preferably at most 2%, more preferably at most 1%. The refractive index is 1.45.
It is preferably from 1.70 to 1.70.
【００３８】これらの透明支持体中には、赤外線吸収
剤、紫外線吸収剤、無機微粒子を添加したり、各種の表
面処理を施すことができる。These transparent supports may be added with an infrared absorber, an ultraviolet absorber and inorganic fine particles, or may be subjected to various surface treatments.
【００３９】上記無機微粒子としては、例えば、二酸化
珪素、二酸化チタン、硫酸バリウム、炭酸カルシウム、
タルク、カオリン等の無機微粒子が挙げられる。Examples of the inorganic fine particles include silicon dioxide, titanium dioxide, barium sulfate, calcium carbonate,
Examples include inorganic fine particles such as talc and kaolin.
【００４０】上記各種表面処理としては、例えば、薬品
処理、機械的処理、コロナ放電処理、火焔処理、紫外線
照射処理、高周波処理、グロー放電処理、活性プラズマ
処理、レーザー処理、混酸処理、オゾン酸化処理等が挙
げられる。Examples of the various surface treatments include chemical treatment, mechanical treatment, corona discharge treatment, flame treatment, ultraviolet irradiation treatment, high frequency treatment, glow discharge treatment, active plasma treatment, laser treatment, mixed acid treatment, and ozone oxidation treatment. And the like.
【００４１】別にフィルター層を設ける場合には、透明
支持体とフィルター層との間に、下塗り層を設けること
が好ましい。下塗り層は、ガラス転移温度が−６０〜６
０℃のポリマーを含む層、フィルター層側の表面が粗面
である層又はフィルター層のポリマーと親和性を有する
ポリマーを含む層として形成する。なお、フィルター層
が設けられていない透明支持体の面に下塗り層を設け
て、透明支持体とその上に設けられる層（例えば、反射
防止層、ハードコート層）との接着力を改善してもよ
い。また、下塗り層は、光学フィルターと画像形成装置
とを接着するための接着剤と光学フィルターとの親和性
を改善するために設けてもよい。下塗り層の厚みは２ｎ
ｍ〜２０μｍが好ましく、５ｎｍ〜５μｍがより好まし
く、２０ｎｍ〜２μｍがさらに好ましく、５０ｎｍ〜１
μｍがさらにまた好ましく、８０ｎｍ〜３００ｎｍが最
も好ましい。When a filter layer is separately provided, an undercoat layer is preferably provided between the transparent support and the filter layer. The undercoat layer has a glass transition temperature of -60 to 6
It is formed as a layer containing a polymer at 0 ° C., a layer having a rough surface on the filter layer side, or a layer containing a polymer having an affinity for the polymer of the filter layer. An undercoat layer is provided on the surface of the transparent support on which the filter layer is not provided to improve the adhesion between the transparent support and a layer provided thereon (for example, an antireflection layer or a hard coat layer). Is also good. The undercoat layer may be provided to improve the affinity between the optical filter and an adhesive for bonding the optical filter and the image forming apparatus. The thickness of the undercoat layer is 2n
m to 20 μm, preferably 5 nm to 5 μm, more preferably 20 nm to 2 μm, and 50 nm to 1 μm.
μm is still more preferred, and 80 nm to 300 nm is most preferred.
【００４２】ガラス転移温度が−６０〜６０℃のポリマ
ーを含む下塗り層は、ポリマーの粘着性で、透明支持体
とフィルター層とを接着する。ガラス転移温度が−６０
〜６０℃のポリマーは、塩化ビニル、塩化ビニリデン、
酢酸ビニル、ブタジエン、ネオプレン、スチレン、クロ
ロプレン、アクリル酸エステル、メタクリル酸エステ
ル、アクリロニトリル又はメチルビニルエーテルの重合
又は共重合により得ることができる。ガラス転移温度は
５０℃以下であることが好ましく、４０℃以下であるこ
とがより好ましく、３０℃以下であることがさらに好ま
しく、２５℃以下であることがさらにまた好ましく、２
０℃以下であることが最も好ましい。下塗り層の２５℃
における弾性率は１〜１０００ＭＰａであることが好ま
しく、５〜８００ＭＰａであることがさらに好ましく、
１０〜５００ＭＰａであることが最も好ましい。表面が
粗面である下塗り層は、粗面の上にフィルター層を形成
することで、透明支持体とフィルター層とを接着する。
表面が粗面である下塗り層は、ポリマーラテックスの塗
布により容易に形成することができる。ラテックスの平
均粒径は０．０２〜３μｍであることが好ましく、０．
０５〜１μｍであることがさらに好ましい。フィルター
層のバインダーポリマーと親和性を有するポリマーの例
には、アクリル樹脂、セルロース誘導体、ゼラチン、カ
ゼイン、澱粉、ポリビニルアルコール、可溶性ナイロン
及び高分子ラテックスが含まれる。二以上の下塗り層を
設けてもよい。下塗り層には、透明支持体を膨潤させる
溶剤、マット剤、界面活性剤、帯電防止剤、塗布助剤や
硬膜剤を添加してもよい。An undercoat layer containing a polymer having a glass transition temperature of -60 to 60 ° C. adheres the transparent support and the filter layer due to the tackiness of the polymer. Glass transition temperature of -60
-60 ° C polymers are vinyl chloride, vinylidene chloride,
It can be obtained by polymerization or copolymerization of vinyl acetate, butadiene, neoprene, styrene, chloroprene, acrylate, methacrylate, acrylonitrile or methyl vinyl ether. The glass transition temperature is preferably 50 ° C. or lower, more preferably 40 ° C. or lower, still more preferably 30 ° C. or lower, still more preferably 25 ° C. or lower.
Most preferably, it is 0 ° C. or lower. 25 ° C for undercoat layer
Is preferably from 1 to 1000 MPa, more preferably from 5 to 800 MPa,
Most preferably, it is 10 to 500 MPa. The undercoat layer having a rough surface adheres the transparent support and the filter layer by forming a filter layer on the rough surface.
The undercoat layer having a rough surface can be easily formed by applying a polymer latex. The average particle size of the latex is preferably 0.02 to 3 μm,
More preferably, the thickness is in the range of 0.5 to 1 μm. Examples of the polymer having an affinity for the binder polymer of the filter layer include acrylic resin, cellulose derivative, gelatin, casein, starch, polyvinyl alcohol, soluble nylon, and polymer latex. Two or more undercoat layers may be provided. The undercoat layer may contain a solvent for swelling the transparent support, a matting agent, a surfactant, an antistatic agent, a coating aid and a hardener.
【００４３】反射防止層としては、低屈折率層が必須で
ある。低屈折率層の屈折率は、上記透明支持体の屈折率
よりも低い。低屈折率層の屈折率は１．２０〜１．５５
であることが好ましく、１．３０〜１．５０であること
がさらに好ましい。低屈折率層の厚さは５０〜４００ｎ
ｍであることが好ましく、５０〜２００ｎｍであること
がさらに好ましい。低屈折率層は、屈折率の低い含フッ
素ポリマーからなる層（特開昭５７−３４５２６号公
報、特開平３−１３０１０３号公報、特開平６−１１５
０２３号公報、特開平８−３１３７０２号公報、特開平
７−１６８００４号公報）、ゾルゲル法により得られる
層（特開平５−２０８８１１号公報、特開平６−２９９
０９１号公報、特開平７−１６８００３号公報）、ある
いは微粒子含む層（特公昭６０−５９２５０号公報、特
開平５−１３０２１号公報、特開平６−５６４７８号公
報、特開平７−９２３０６号公報、特開平９−２８８２
０１号公報）として形成することができる。微粒子を含
む層では、微粒子間又は微粒子内のミクロボイドとし
て、低屈折率層に空隙を形成することができる。微粒子
を含む層は３〜５０体積％の空隙率を有することが好ま
しく、５〜３５体積％の空隙率を有することがさらに好
ましい。As the antireflection layer, a low refractive index layer is essential. The refractive index of the low refractive index layer is lower than the refractive index of the transparent support. The refractive index of the low refractive index layer is 1.20 to 1.55
And more preferably 1.30 to 1.50. The thickness of the low refractive index layer is 50-400n
m, more preferably 50 to 200 nm. The low refractive index layer is a layer made of a fluoropolymer having a low refractive index (JP-A-57-34526, JP-A-3-130103, JP-A-6-115).
023, JP-A-8-313702, JP-A-7-168004), layers obtained by a sol-gel method (JP-A-5-208811, JP-A-6-299)
091, JP-A-7-168003), or a layer containing fine particles (JP-B-60-59250, JP-A-5-13021, JP-A-6-56478, JP-A-7-92306), JP-A-9-2882
No. 01 publication). In the layer containing fine particles, voids can be formed in the low refractive index layer as microvoids between or within the fine particles. The layer containing fine particles preferably has a porosity of 3 to 50% by volume, more preferably 5 to 35% by volume.
【００４４】広い波長領域の反射を防止するためには、
低屈折率層に加えて、屈折率の高い層（中・高屈折率
層）を積層することが好ましい。高屈折率層の屈折率は
１．６５〜２．４０であることが好ましく、１．７０〜
２．２０であることがさらに好ましい。中屈折率層の屈
折率は、低屈折率層の屈折率と高屈折率層の屈折率との
中間の値となるように調整する。中屈折率層の屈折率は
１．５０〜１．９０であることが好ましく、１．５５〜
１．７０であることがさらに好ましい。中・高屈折率層
の厚さは５ｎｍ〜１００μｍであることが好ましく、１
０ｎｍ〜１０μｍであることがさらに好ましく、３０ｎ
ｍ〜１μｍであることが最も好ましい。中・高屈折率層
のヘイズは５％以下であることが好ましく、３％以下で
あることがさらに好ましく、１％以下であることが最も
好ましい。中・高屈折率層は、比較的高い屈折率を有す
るポリマーバインダーを用いて形成することができる。
屈折率が高いポリマーの例には、ポリスチレン、スチレ
ン共重合体、ポリカーボネート、メラミン樹脂、フェノ
ール樹脂、エポキシ樹脂及び環状（脂環式又は芳香族）
イソシアネートとポリオールとの反応で得られるポリウ
レタンが含まれる。その他の環状（芳香族、複素環式、
脂環式）基を有するポリマーや、フッ素以外のハロゲン
原子を置換基として有するポリマーも、屈折率が高い。
二重結合を導入してラジカル硬化を可能にしたモノマー
の重合反応によりポリマーを形成してもよい。In order to prevent reflection in a wide wavelength range,
It is preferable to laminate a layer having a high refractive index (middle / high refractive index layer) in addition to the low refractive index layer. The refractive index of the high refractive index layer is preferably from 1.65 to 2.40, and more preferably from 1.70 to 2.70.
More preferably, it is 2.20. The refractive index of the middle refractive index layer is adjusted to be an intermediate value between the refractive index of the low refractive index layer and the refractive index of the high refractive index layer. The refractive index of the middle refractive index layer is preferably 1.50 to 1.90, and
More preferably, it is 1.70. The thickness of the middle / high refractive index layer is preferably from 5 nm to 100 μm,
0 nm to 10 μm, more preferably 30 nm
Most preferably, it is from m to 1 μm. The haze of the middle / high refractive index layer is preferably 5% or less, more preferably 3% or less, and most preferably 1% or less. The middle / high refractive index layer can be formed using a polymer binder having a relatively high refractive index.
Examples of polymers having a high refractive index include polystyrene, styrene copolymer, polycarbonate, melamine resin, phenol resin, epoxy resin, and cyclic (alicyclic or aromatic).
Polyurethanes obtained by reacting isocyanates with polyols are included. Other cyclic (aromatic, heterocyclic,
Polymers having an (alicyclic) group and polymers having a halogen atom other than fluorine as a substituent also have a high refractive index.
A polymer may be formed by a polymerization reaction of a monomer capable of radical curing by introducing a double bond.
【００４５】さらに高い屈折率を得るため、ポリマーバ
インダー中に無機微粒子を分散してもよい。無機微粒子
の屈折率は１．８０〜２．８０であることが好ましい。
無機微粒子は、金属の酸化物又は硫化物から形成するこ
とが好ましい。金属の酸化物又は硫化物の例には、二酸
化チタン（例、ルチル、ルチル／アナターゼの混晶、ア
ナターゼ、アモルファス構造）、酸化錫、酸化インジウ
ム、酸化亜鉛、酸化ジルコニウム及び硫化亜鉛が含まれ
る。酸化チタン、酸化錫及び酸化インジウムが特に好ま
しい。無機微粒子は、これらの金属の酸化物又は硫化物
を主成分とし、さらに他の元素を含むことができる。主
成分とは、粒子を構成する成分の中で最も含有量（重量
％）が多い成分を意味する。他の元素の例には、Ｔｉ、
Ｚｒ、Ｓｎ、Ｓｂ、Ｃｕ、Ｆｅ、Ｍｎ、Ｐｂ、Ｃｄ、Ａ
ｓ、Ｃｒ、Ｈｇ、Ｚｎ、Ａｌ、Ｍｇ、Ｓｉ、Ｐ及びＳが
含まれる。被膜形成性で溶剤に分散し得るか、それ自身
が液状である無機材料、例えば、各種元素のアルコキシ
ド、有機酸の塩、配位性化合物と結合した配位化合物
（例、キレート化合物）、活性無機ポリマーを用いて、
中・高屈折率層を形成することもできる。In order to obtain a higher refractive index, inorganic fine particles may be dispersed in a polymer binder. The refractive index of the inorganic fine particles is preferably from 1.80 to 2.80.
The inorganic fine particles are preferably formed from a metal oxide or sulfide. Examples of metal oxides or sulfides include titanium dioxide (eg, rutile, rutile / anatase mixed crystal, anatase, amorphous structure), tin oxide, indium oxide, zinc oxide, zirconium oxide, and zinc sulfide. Titanium oxide, tin oxide and indium oxide are particularly preferred. The inorganic fine particles contain oxides or sulfides of these metals as main components and may further contain other elements. The main component means a component having the largest content (% by weight) of the components constituting the particles. Examples of other elements include Ti,
Zr, Sn, Sb, Cu, Fe, Mn, Pb, Cd, A
s, Cr, Hg, Zn, Al, Mg, Si, P and S are included. Inorganic materials that are film-forming and can be dispersed in solvents or are themselves liquid, such as alkoxides of various elements, salts of organic acids, coordination compounds (eg, chelate compounds) combined with coordination compounds, activity Using inorganic polymer,
A medium / high refractive index layer can also be formed.
【００４６】反射防止層は、表面をアンチグレア機能
（入射光を表面で散乱させて、膜周囲の景色が膜表面に
移るのを防止する機能）を付与することができる。例え
ば、透明フィルムの表面に微細な凹凸を形成し、そして
その表面に反射防止層を形成するか、あるいは反射防止
層を形成後、エンボスロールにより表面に凹凸を形成す
ることにより、アンチグレア機能を得ることができる。
アンチグレア機能を有する反射防止層は、一般に３〜３
０％のヘイズを有する。The anti-reflection layer can provide the surface with an anti-glare function (a function of scattering incident light on the surface and preventing a scene around the film from shifting to the film surface). For example, by forming fine irregularities on the surface of a transparent film, and forming an antireflection layer on the surface, or after forming the antireflection layer, by forming irregularities on the surface with an embossing roll, an anti-glare function is obtained. be able to.
The antireflection layer having an antiglare function is generally 3 to 3
Has a haze of 0%.
【００４７】ハードコート層は、透明支持体の硬度より
も高い硬度を有する。ハードコート層は、架橋している
ポリマーを含むことが好ましい。ハードコート層は、ア
クリル系、ウレタン系、エポキシ系のポリマー、オリゴ
マー又はモノマー（例、紫外線硬化型樹脂）を用いて形
成することができる。シリカ系材料からハードコート層
を形成することもできる。The hard coat layer has a hardness higher than the hardness of the transparent support. The hard coat layer preferably contains a cross-linked polymer. The hard coat layer can be formed using an acrylic, urethane, or epoxy polymer, oligomer, or monomer (eg, an ultraviolet-curable resin). The hard coat layer can also be formed from a silica-based material.
【００４８】反射防止層（低屈折率層）の表面に潤滑層
を形成してもよい。潤滑層は、低屈折率層表面に滑り性
を付与し、耐傷性を改善する機能を有する。潤滑層は、
ポリオルガノシロキサン（例、シリコンオイル）、天然
ワックス、石油ワックス、高級脂肪酸金属塩、フッ素系
潤滑剤又はその誘導体を用いて形成することができる。
潤滑層の厚さは２〜２０ｎｍであることが好ましい。A lubricating layer may be formed on the surface of the antireflection layer (low refractive index layer). The lubricating layer has a function of imparting lubricity to the surface of the low refractive index layer and improving scratch resistance. The lubrication layer is
It can be formed using polyorganosiloxane (eg, silicone oil), natural wax, petroleum wax, higher fatty acid metal salt, fluorine-based lubricant or a derivative thereof.
The thickness of the lubricating layer is preferably 2 to 20 nm.
【００４９】フィルター層、下塗り層、反射防止層、ハ
ードコート層、潤滑層、その他の層は、一般的な塗布方
法により形成することができる。塗布方法の例には、デ
ィップコート法、エアーナイフコート法、カーテンコー
ト法、ローラーコート法、ワイヤーバーコート法、グラ
ビアコート法及びホッパーを使用するエクストルージョ
ンコート法（米国特許２６８１２９４号明細書）が含ま
れる。二以上の層を同時塗布により形成してもよい。同
時塗布法については、米国特許２７６１７９１号、米国
特許２９４１８９８号、米国特許３５０８９４７号、米
国特許３５２６５２８号の各明細書及び原崎勇次著「コ
ーティング工学」２５３頁（１９７３年朝倉書店発行）
に記載されている。The filter layer, undercoat layer, antireflection layer, hard coat layer, lubricating layer and other layers can be formed by a general coating method. Examples of the coating method include a dip coating method, an air knife coating method, a curtain coating method, a roller coating method, a wire bar coating method, a gravure coating method, and an extrusion coating method using a hopper (US Pat. No. 2,681,294). included. Two or more layers may be formed by simultaneous coating. The simultaneous coating method is described in U.S. Pat. No. 2,761,791; U.S. Pat. No. 2,918,898; U.S. Pat. No. 3,508,947; U.S. Pat. No. 3,526,528;
It is described in.
【００５０】本発明の光学フィルターは、液晶表示装置
（ＬＣＤ）、プラズマディスプレイパネル（ＰＤＰ）、
エレクトロルミネッセンスディスプレイ（ＥＬＤ）や陰
極管表示装置（ＣＲＴ）のような画像表示装置に適用す
る。低屈折率層を設ける場合は、低屈折率層が設けられ
ていない側の面が画像表示装置の画像表示面と対向する
ように配置する。本発明の光学フィルターは、プラズマ
ディスプレイパネル（ＰＤＰ）のフィルターとして使用
すると、特に顕著な効果が得られる。プラズマディスプ
レイパネル（ＰＤＰ）は、ガス、ガラス基板、電極、電
極リード材料、厚膜印刷材料及び蛍光体により構成され
る。ガラス基板は、前面ガラス基板と後面ガラス基板の
二枚である。二枚のガラス基板には電極と絶縁層を形成
する。後面ガラス基板には、さらに蛍光体層を形成す
る。二枚のガラス基板を組み立てて、その間にガスを封
入する。プラズマディスプレイパネル（ＰＤＰ）は、既
に市販されている。プラズマディスプレイパネルについ
ては、特開平５−２０５６４３号公報及び特開平９−３
０６３６６号公報に記載されている。プラズマディスプ
レイパネルのような画像表示装置では、光学フィルター
をディスプレイの前面に配置する。光学フィルターをデ
ィスプレイの表面に直接貼り付けることができる。ま
た、ディスプレイの前に前面板が設けられている場合
は、前面板の表側（外側）又は裏側（ディスプレイ側）
に光学フィルターを貼り付けることもできる。The optical filter of the present invention includes a liquid crystal display (LCD), a plasma display panel (PDP),
The present invention is applied to an image display device such as an electroluminescence display (ELD) and a cathode ray tube display (CRT). When the low refractive index layer is provided, the low refractive index layer is disposed such that the surface on which the low refractive index layer is not provided faces the image display surface of the image display device. When the optical filter of the present invention is used as a filter of a plasma display panel (PDP), a particularly remarkable effect is obtained. A plasma display panel (PDP) includes a gas, a glass substrate, an electrode, an electrode lead material, a thick film printing material, and a phosphor. There are two glass substrates, a front glass substrate and a rear glass substrate. An electrode and an insulating layer are formed on two glass substrates. A phosphor layer is further formed on the rear glass substrate. Two glass substrates are assembled, and gas is sealed between them. Plasma display panels (PDPs) are already commercially available. Regarding the plasma display panel, Japanese Patent Application Laid-Open Nos.
No. 06366. In an image display device such as a plasma display panel, an optical filter is disposed in front of a display. An optical filter can be attached directly to the surface of the display. When a front panel is provided in front of the display, the front side (outside) or the rear side (display side) of the front panel.
An optical filter can be attached to the device.
【００５１】[0051]
【実施例】以下、製造例及び実施例をもって本発明を更
に詳細に説明する。しかしながら、本発明は以下の実施
例によって何ら制限を受けるものではない。The present invention will be described below in more detail with reference to Production Examples and Examples. However, the present invention is not limited at all by the following examples.
【００５２】［製造例］ （製造例１） ＜スクアリリウム化合物Ｎｏ．１の合成＞１００ｍｌ四
つ口フラスコにＮ−ｎ−ブチル−２−メチルインドール
９．９８ｇ、スクアリリウム酸２．９７ｇ、トルエン１
７．６６ｇ、ブタノール３５．３１ｇを仕込み、分水器
を付し、１０３℃で３時間反応させた。冷却後析出した
結晶をろ過してトルエン−ブタノール混合溶液で洗浄
後、さらにヘキサンで洗浄し、減圧乾燥して、緑色結晶
８．９７ｇを得た。 ＜分析＞ 構造解析： 1Ｈ−ＮＭＲ測定 （ケミカルシフトｐｐｍ；多重度；プロトン数） （０．９５〜１．０２；ｔ；６）（１．４３〜１．５
１；ｍ；４）（１．７８〜１．８５；ｍ；４）（３．２
６〜３．２８；ｔ；４）（４．１５〜４．１８；ｔ；
４）（７．１６〜７．３６；ｍ；６）（９．２１〜９．
２３；ｄ；２） 光学的特性：クロロホルム溶媒でのＵＶスペクトル測
定 λｍａｘ；５８１ｎｍ、ε；１．５１×１０5 [Production Example] (Production Example 1) <Squarylium Compound No. Synthesis of 1> 9.98 g of Nn-butyl-2-methylindole, 2.97 g of squarylic acid, toluene 1 in a 100 ml four-necked flask
7.66 g and 35.31 g of butanol were charged, a water separator was attached, and the mixture was reacted at 103 ° C. for 3 hours. After cooling, the precipitated crystals were filtered, washed with a mixed solution of toluene and butanol, further washed with hexane, and dried under reduced pressure to obtain 8.97 g of green crystals. <Analysis> Structural analysis: 1 H-NMR measurement (chemical shift ppm; multiplicity; number of protons) (0.95 to 1.02; t; 6) (1.43 to 1.5)
1; m; 4) (1.78 to 1.85; m; 4) (3.2)
6-3.28; t; 4) (4.15-4.18; t;
4) (7.16 to 7.36; m; 6) (9.21 to 9.
23; d; 2) Optical properties: UV spectrum measurement with chloroform solvent λmax; 581 nm, ε; 1.51 × 10 5
【００５３】（製造例２） ＜スクアリリウム化合物Ｎｏ．２の合成＞１００ｍｌ四
つ口フラスコにＮ−イソアミル−２−メチルインドール
１０．７８ｇ、スクアリリウム酸２．９７ｇ、トルエン
１７．６６ｇ、ブタノール３５．３１ｇを仕込み、分水
器を付し、１０３℃で３時間反応させた。冷却後析出し
た結晶をろ過してトルエン−ブタノール混合溶液で洗浄
後、さらにヘキサンで洗浄し、減圧乾燥して、緑色結晶
９．２１ｇを得た。 ＜分析＞ 構造解析： 1Ｈ−ＮＭＲ測定 （ケミカルシフトｐｐｍ；多重度；プロトン数） （１．０４〜１．０９；ｔ；１２）（１．６５〜１．６
９；ｍ；４）（１．７１〜１．８２；ｍ；２）（３．３
１；ｓ；６）（４．１２〜４．１６；ｔ；４）（７．２
３〜７．３６；ｍ；６）（９．２０〜９．２２；ｄ；
２） 光学的特性：クロロホルム溶媒でのＵＶスペクトル測
定 λｍａｘ；５８１ｎｍ、ε；１．６３×１０5 (Production Example 2) <Squarylium Compound No. Synthesis of 2> A 100 ml four-necked flask was charged with 10.78 g of N-isoamyl-2-methylindole, 2.97 g of squarylic acid, 17.66 g of toluene, and 35.31 g of butanol, and a water separator was attached. The reaction was performed for 3 hours. After cooling, the precipitated crystals were filtered, washed with a mixed solution of toluene and butanol, further washed with hexane, and dried under reduced pressure to obtain 9.21 g of green crystals. <Analysis> Structural analysis: 1 H-NMR measurement (chemical shift ppm; multiplicity; number of protons) (1.04 to 1.09; t; 12) (1.65 to 1.6)
9; m; 4) (1.71 to 1.82; m; 2) (3.3
1; s; 6) (4.12 to 4.16; t; 4) (7.2
3-7.36; m; 6) (9.20-9.22; d;
2) Optical properties: UV spectrum measurement with chloroform solvent λmax; 581 nm, ε; 1.63 × 10 5
【００５４】〔実施例１〕下記の配合にてＵＶワニスを
作成し、これを易密着処理した１８８μｍ厚のポリエチ
レンテレフタレートフィルムにバーコーター＃９を塗布
し、８０℃、３０秒乾燥した。その後、赤外線カットフ
ィルムフィルター付き高圧水銀灯にて紫外線を１００ｍ
Ｊ照射し、硬化膜厚約５μｍのフィルムを得た。Example 1 A UV varnish was prepared according to the following formulation, and a bar coater # 9 was applied to a polyethylene terephthalate film having a thickness of 188 μm, which was subjected to easy adhesion treatment, and dried at 80 ° C. for 30 seconds. After that, UV rays were irradiated for 100m with a high pressure mercury lamp equipped with an infrared cut film filter.
J irradiation was performed to obtain a film having a cured film thickness of about 5 μm.
【００５５】これを（株）日立製作所製スペクトロフォ
トメーターＵ−３０１０で測定したところ、λｍａｘが
５８０ｎｍ、半値巾が３４ｎｍであり、光学フィルター
として好適である。When this was measured with a spectrophotometer U-3010 manufactured by Hitachi, Ltd., the λmax was 580 nm and the half width was 34 nm, which is suitable as an optical filter.
【００５６】 （配合） アデカオプトマーＫＲＸ−５７１−６５ １００ｇ （旭電化工業（株）製ＵＶ硬化樹脂、樹脂分８０重量％） スクアリリウム化合物Ｎｏ．１ ０．５ｇ メチルエチルケトン ６０ｇ(Blending) 100 g of Adeka Optomer KRX-571-65 (UV curable resin manufactured by Asahi Denka Kogyo Co., Ltd., resin content: 80% by weight) 1 0.5g methyl ethyl ketone 60g
【００５７】〔実施例２〕下記の配合をプラストミルで
２６０℃、５分間溶融紺練した。混練後直径６ｍｍのノ
ズルから押出し水冷却ペレタイザーで色素含有ペレット
を得た。このペレットを電気プレスを用いて２５０℃で
０．２５ｍｍ厚の薄板に成形した。Example 2 The following components were melted and kneaded in a plastmill at 260 ° C. for 5 minutes. After kneading, the mixture was extruded from a nozzle having a diameter of 6 mm and a dye-containing pellet was obtained with a water-cooled pelletizer. The pellet was formed into a thin plate having a thickness of 0.25 mm at 250 ° C. using an electric press.
【００５８】これを上記Ｕ−３０１０で測定したとこ
ろ、λｍａｘが５８２ｍ、半値巾が３８ｎｍであり、光
学フィルターとして好適である。When this was measured with the above U-3010, the λmax was 582 m and the half width was 38 nm, which is suitable as an optical filter.
【００５９】 （配合） ユーピロンＳ−３０００ １００ｇ （三菱瓦斯化学（株）製；ポリカーボネート樹脂） スクアリリウム化合物Ｎｏ．２ ０．０１ｇ(Blending) 100 g of Iupilon S-3000 (manufactured by Mitsubishi Gas Chemical Co., Ltd .; polycarbonate resin) 2 0.01g
【００６０】〔実施例３〕下記の配合にてバインダー組
成物を作成し、これを易密着処理した１８８μｍ厚のポ
リエチレンテレフタレート（ＰＥＴ）フィルムにバーコ
ーター＃９を塗布し、８０℃、３０秒乾燥した。その
後、このフィルムを０．９ｍｍ厚アルカリガラス板に１
００℃で熱圧着し、ガラス板とＰＥＴフィルムの間のバ
インダー層に光吸収性色素を含有するＰＥＴ保護ガラス
板を作成した。Example 3 A bar coater # 9 was applied to a 188 μm-thick polyethylene terephthalate (PET) film, which was prepared by preparing a binder composition having the following composition, and easily dried, and dried at 80 ° C. for 30 seconds. did. Then, this film was placed on a 0.9 mm thick alkaline glass plate for 1 hour.
Thermocompression bonding was performed at 00 ° C. to prepare a PET protective glass plate containing a light-absorbing dye in a binder layer between the glass plate and the PET film.
【００６１】これを上記Ｕ−３０１０で測定したとこ
ろ、λｍａｘが５９４ｎｍ、半値巾が３６ｎｍであり、
光学フィルターとして好適である。When this was measured with the above U-3010, the λmax was 594 nm, the half width was 36 nm, and
It is suitable as an optical filter.
【００６２】 （配合） アデカアークルズＲ−１０３ １００ｇ （旭電化工業（株）製アクリル樹脂系バインダー、樹脂分５０重量％） スクアリリウム化合物Ｎｏ．５ ０．５ｇ(Blending) 100 g of Adeka Aquel's R-103 (Acrylic resin binder manufactured by Asahi Denka Kogyo Co., Ltd., resin content 50% by weight) 5 0.5g
【００６３】[0063]
【発明の効果】本発明は、特定波長においてシャープな
吸収（λｍａｘ５６０〜６２０ｎｍ、半値巾５０ｎｍ以
下）を有することから、特にプラズマディスプレイ（Ｐ
ＤＰ）用途に好適な光学フィルターを提供するものであ
る。The present invention has a sharp absorption (.lambda.max of 560 to 620 nm and a half width of 50 nm or less) at a specific wavelength.
DP) provides an optical filter suitable for use.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 矢野 亨 東京都荒川区東尾久７丁目２番35号 旭電 化工業株式会社内 Ｆターム(参考） 2H048 BA47 CA04 CA14 CA19 CA24 4H056 EA15 EA16 FA01 FA05 5G435 AA01 AA04 BB06 CC12 FF02 GG11 HH03 KK07 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Toru Yano 7-35 Higashiogu, Arakawa-ku, Tokyo Asahi Denka Kogyo Co., Ltd. F-term (reference) 2H048 BA47 CA04 CA14 CA19 CA24 4H056 EA15 EA16 FA01 FA05 5G435 AA01 AA04 BB06 CC12 FF02 GG11 HH03 KK07
Claims (5)
有することを特徴とする光学フィルター。 【化１】 1. An optical filter comprising a compound represented by the following general formula (I). Embedded image
基であることを特徴とする請求項１記載の光学フィルタ
ー。2. The optical filter according to claim 1 , wherein in the general formula (I), R 1 is an alkyl group.
又はフェニル基であることを特徴とする請求項１又は２
記載の光学フィルター。3. The compound according to claim 1, wherein R 2 is a methyl group or a phenyl group in the general formula (I).
The optical filter as described.
することを特徴とする請求項１、２又は３記載の光学フ
ィルター。4. The optical filter according to claim 1, wherein the optical filter is used as a filter for an image display device.
イパネルである請求項４記載の光学フィルター。5. The optical filter according to claim 4, wherein said image display device is a plasma display panel.