JP2002212469A - Ink, color filter and its production method, liquid crystal panel, computer, and image display device - Google Patents
Ink, color filter and its production method, liquid crystal panel, computer, and image display deviceInfo
- Publication number
- JP2002212469A JP2002212469A JP2001008120A JP2001008120A JP2002212469A JP 2002212469 A JP2002212469 A JP 2002212469A JP 2001008120 A JP2001008120 A JP 2001008120A JP 2001008120 A JP2001008120 A JP 2001008120A JP 2002212469 A JP2002212469 A JP 2002212469A
- Authority
- JP
- Japan
- Prior art keywords
- ink
- color filter
- dye
- liquid crystal
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明はカラーフィルタの形
成に好適に用いうるインク、カラーテレビ、パーソナル
コンピュータ等に使用されるカラー液晶ディスプレイの
カラーフィルタ、カラーフィルタの製造方法及びこのよ
うなカラーフィルタを用いた液晶パネル、画像表示デバ
イス及びコンピュータに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink which can be suitably used for forming a color filter, a color filter for a color liquid crystal display used for a color television, a personal computer, etc. The present invention relates to a liquid crystal panel, an image display device, and a computer used.
【0002】[0002]
【従来の技術】近年、パーソナルコンピュータの発達、
特に携帯用パーソナルコンピュータの発達に伴い、液晶
ディスプレイ、特にカラー液晶ディスプレイの需要が増
加する傾向にある。しかしながら、さらなる普及のため
にはコストダウンが必要であり、特にコスト的に比重の
重いカラーフィルタのコストダウンに対する要求が高ま
っている。2. Description of the Related Art In recent years, the development of personal computers,
In particular, with the development of portable personal computers, the demand for liquid crystal displays, especially color liquid crystal displays, tends to increase. However, cost reduction is necessary for further popularization, and in particular, there is an increasing demand for cost reduction of color filters having a high specific gravity.
【0003】カラーフィルタの低コスト化の方法として
は各種提案されているが、その中でも有望な方法の一つ
として、特開昭59−75205号公報、特開昭63−
235901号公報、特開平1−217302号公報等
に提案されている着色透光部の形成にインクジェット方
式を採用する方法が注目されている。Various methods have been proposed for reducing the cost of color filters. Among them, one of the promising methods is disclosed in JP-A-59-75205 and JP-A-63-75205.
Attention has been paid to a method of employing an ink-jet method for forming a colored light-transmitting portion as proposed in JP-A-235901, JP-A-1-217302 and the like.
【0004】インクジェット方式は、インク吐出口から
インクを液滴として吐出させ、これを着色部位に付着さ
せて着色するもので、精細な多数の画素の精細な配列を
精度良く、且つ高速で形成できるという利点を有してい
る。また赤、緑、青の各着色層の形成を一度に行うこと
ができ、更にインクを画素形成部分にのみ付着させれば
よく、インクの無駄が生じないため、大幅な生産性の向
上とコストの低減を図ることができる。In the ink jet system, ink is ejected as ink droplets from an ink ejection port, and the ink is adhered to a colored portion to be colored, and a fine array of a large number of fine pixels can be formed with high accuracy and at high speed. It has the advantage that. Further, the formation of each of the red, green, and blue colored layers can be performed at a time, and the ink only needs to be adhered to the pixel forming portion. Can be reduced.
【0005】一方、カラーフィルタの青色画素部は通
常、透過率が最大となる波長が三波長管の青色輝線と一
致するように作られており、該青色画素を形成する色材
には、単一の色材でそのような色調を有する青色画素を
形成するのは困難であるため、一般的にシアン染料と、
バイオレット染料とを組み合わせて用いられている。On the other hand, the blue pixel portion of the color filter is usually formed so that the wavelength at which the transmittance becomes maximum coincides with the blue emission line of the three-wavelength tube. Since it is difficult to form a blue pixel having such a color tone with one color material, a cyan dye is generally used,
It is used in combination with a violet dye.
【0006】[0006]
【発明が解決しようとする課題】インクジェット方式に
よって例えば、高色再現範囲の色度を有するカラーフィ
ルタを作成する場合、画素に含まれる色材量を増加させ
ることが好ましい。その為には画素に打ち込むインク量
を増加させるか或いは、インク中の染料濃度を増加させ
る方法が最も適切であると考えられる。しかしながらイ
ンクジェット方式によって画素に打ち込むインク量を増
加させると、隣接画素間の混色等の問題を引き起こす可
能性がある。従って、画素に打ち込むインクの染料濃度
を増加させる方法を用いることが適当であると考えられ
る。しかし、染料の溶媒への溶解度や、インクジェット
適性等を考慮すると、染料濃度の増加にはある程度の限
界があり、その為染料によってはインク中の濃度を上限
まで高めても目標とする色度が得られない場合があるこ
とを本発明者らは見出した。For example, when a color filter having a chromaticity in a high color reproduction range is produced by an ink jet method, it is preferable to increase the amount of color material contained in a pixel. For that purpose, it is considered that the most appropriate method is to increase the amount of ink to be applied to the pixel or to increase the dye concentration in the ink. However, increasing the amount of ink to be applied to a pixel by the inkjet method may cause a problem such as color mixing between adjacent pixels. Therefore, it is considered appropriate to use a method of increasing the dye concentration of the ink to be applied to the pixel. However, considering the solubility of the dye in the solvent and the suitability for ink-jet, there is a certain limit to the increase in the dye concentration. The present inventors have found that it may not be obtained.
【0007】そこで本発明の一つの目的は、色特性に優
れて且つ、カラーフィルタの製造に従来から使用されて
いるインクと比べ、色度を同一にした場合、より染料濃
度が低くなるような青インク、いいかえれば、従来のイ
ンクよりも低い色材濃度で、従来のインクと同等以上の
色度を達成できるような青インクを提供することにあ
る。Therefore, one object of the present invention is to provide an ink composition which has excellent color characteristics and has a lower dye concentration when the chromaticity is the same as that of the ink conventionally used in the production of color filters. It is an object of the present invention to provide a blue ink, in other words, a blue ink capable of achieving a chromaticity equal to or higher than that of the conventional ink with a lower colorant density than the conventional ink.
【0008】また本発明は、色特性に優れ、かつインク
ジェット法を用いることによっても安定して製造するこ
とのできるカラーフィルタを提供することを他の目的と
する。Another object of the present invention is to provide a color filter which is excellent in color characteristics and can be stably manufactured even by using an ink jet method.
【0009】又本発明は、色特性に優れた、高品位の液
晶パネルを提供することを他の目的とする。It is another object of the present invention to provide a high-quality liquid crystal panel having excellent color characteristics.
【0010】また本発明は、高品位な表示装置を備えて
いるコンピュータを提供することを他の目的とする。It is another object of the present invention to provide a computer having a high-quality display device.
【0011】更に本発明は、色再現性に優れた画像表示
デバイスを提供することを他の目的とする。Another object of the present invention is to provide an image display device having excellent color reproducibility.
【0012】更にまた本発明は、高い透明性を有し、色
特性にも優れているカラーフィルタを安定して得ること
のできるカラーフィルタの製造方法を提供することを他
の目的とする。Still another object of the present invention is to provide a method of manufacturing a color filter which can stably obtain a color filter having high transparency and excellent color characteristics.
【0013】[0013]
【課題を解決するための手段】上記目的を達成すること
のできる本発明の一態様にかかるインクは、シアン染料
及び下記一般式(I)で示されるバイオレット染料とを
含むことを特徴とする:According to one aspect of the present invention, there is provided an ink comprising a cyan dye and a violet dye represented by the following general formula (I):
【0014】[0014]
【外3】 〔上記式(I)中、R1、R1’、R2及びR2’は、各々
独立に、水素原子、炭素数1〜5の直鎖状もしくは分岐
鎖状のアルキル基、または置換もしくは未置換のアリー
ル基を表し、R3は置換フェニル基を表わす〕。[Outside 3] [In the above formula (I), R 1 , R 1 ′, R 2 and R 2 ′ each independently represent a hydrogen atom, a linear or branched alkyl group having 1 to 5 carbon atoms, Represents an unsubstituted aryl group, and R 3 represents a substituted phenyl group].
【0015】また上記目的を達成することのできる本発
明の一態様にかかるカラーフィルタは、光透過性基板、
及び該基板上の所定の位置に青の着色画素を備えている
カラーフィルタにおいて、該着色画素が、シアン染料と
上記式(I)で示されるバイオレット染料とを含むこと
を特徴とするものである。A color filter according to one embodiment of the present invention, which can achieve the above object, includes a light-transmitting substrate,
And a color filter having a blue colored pixel at a predetermined position on the substrate, wherein the colored pixel contains a cyan dye and a violet dye represented by the above formula (I). .
【0016】また上記目的を達成することのできる本発
明の一態様にかかる液晶パネルは、上記のカラーフィル
タ及び該カラーフィルタに対向配置されているパネル基
板を有し、該カラーフィルタと該パネル基板との間に液
晶化合物が封入されていることを特徴とするものであ
る。According to another embodiment of the present invention, there is provided a liquid crystal panel having the above color filter and a panel substrate disposed opposite to the color filter, wherein the color filter and the panel substrate are provided. And a liquid crystal compound is sealed between them.
【0017】また上記目的を達成することのできる本発
明の一態様にかかるコンピュータは、上記の液晶パネル
を画像表示部として供えていることを特徴とするもので
ある。A computer according to one embodiment of the present invention which can achieve the above object is characterized in that the above-mentioned liquid crystal panel is provided as an image display unit.
【0018】また上記の目的を達成することの出来る画
像表示デバイスは、上記のカラーフィルタを備えている
ことを特徴とするものである。An image display device capable of achieving the above object is characterized by including the above color filter.
【0019】また上記目的を達成することのできるカラ
ーフィルタの製造方法の一態様は、シアン染料および上
記一般式(I)で示されるバイオレット染料を含むイン
クジェット用のインクの滴を光透過基板表面の所定の位
置にインクジェット法で付着させて着色画素を形成する
工程を有することを特徴とするものである。One embodiment of a method of manufacturing a color filter which can achieve the above object is to form a droplet of an ink jet ink containing a cyan dye and a violet dye represented by the above general formula (I) on a light transmitting substrate surface. The method further comprises a step of forming a colored pixel by attaching the pixel to a predetermined position by an inkjet method.
【0020】更に上記目的を達成することのできるカラ
ーフィルタの製造方法の一態様は、シアン染料、上記一
般式(I)で示されるバイオレット染料および硬化性樹
脂を含むインクジェット用のインクの滴を光透過性基板
表面の所定の位置にインクジェット法で付着させて着色
画素を形成する工程を有することを特徴とするものであ
る。Further, one embodiment of a method of manufacturing a color filter which can achieve the above object is to form a droplet of an ink jet ink containing a cyan dye, a violet dye represented by the above general formula (I) and a curable resin. The method further includes a step of forming a colored pixel by attaching the pixel to a predetermined position on the surface of the transparent substrate by an inkjet method.
【0021】本発明者らは鋭意研究を進めた結果、シア
ン染料及びバイオレット染料とを含むインクジェット用
インクにおいて、バイオレット染料にキサンテン骨格を
有する上記一般式(I)で示される染料を用いることに
より、インク中の染料濃度を低減し且つ、青インクとし
て優れた色特性を示すことを見出した。これは該バイオ
レット染料が従来青インクに好適に用いられていたバイ
オレット染料に比べ、吸光度のピーク波長が長波長側に
存在するためで、それによってバイオレット染料の添加
量は増加するが、元々添加量の多かったシアン染料を低
減することができるので、結果として、インク中の全染
料濃度を低減することができるのである。The inventors of the present invention have made intensive studies and have found that, in an ink-jet ink containing a cyan dye and a violet dye, a dye represented by the above general formula (I) having a xanthene skeleton is used as a violet dye. It has been found that the dye concentration in the ink is reduced and the ink exhibits excellent color characteristics as a blue ink. This is because the violet dye has a longer peak wavelength of absorbance than the violet dye that has been conventionally used favorably in blue ink, thereby increasing the amount of the violet dye added. Can be reduced, and as a result, the total dye concentration in the ink can be reduced.
【0022】[0022]
【発明の実施の形態】本発明の一実施態様にかかるイン
クジェット記録用のインクは、シアン染料とバイオレッ
ト染料とを含んでいる。そしてこのインクは、例えば課
アラーフィルタの青色画像をインクジェット法で形成す
るのに好適に用いられる。DESCRIPTION OF THE PREFERRED EMBODIMENTS An ink for inkjet recording according to one embodiment of the present invention contains a cyan dye and a violet dye. This ink is suitably used, for example, for forming a blue image of a sectional error filter by an inkjet method.
【0023】(バイオレット染料)バイオレット染料と
は、例えば下記式(II)で表されるキサンテン構造を
分子内に含む染料であり、具体的には例えば下記一般式
(I)で示される染料が好適に用いられる。(Violet dye) The violet dye is a dye containing, for example, a xanthene structure represented by the following formula (II) in the molecule, and specifically, for example, a dye represented by the following general formula (I) is preferable. Used for
【0024】[0024]
【外4】 [Outside 4]
【0025】[0025]
【外5】 上記式(I)において、R1、R1’、R2及びR2’は、
各々独立に、水素原子、炭素数1〜5の直鎖状もしくは
分岐鎖状のアルキル基、または置換もしくは未置換のア
リール基を表わす。ここでアリール基の例としては、例
えば下記の構造式で示される基が挙げられる:[Outside 5] In the above formula (I), R 1 , R 1 ′, R 2 and R 2 ′ are
Each independently represents a hydrogen atom, a linear or branched alkyl group having 1 to 5 carbon atoms, or a substituted or unsubstituted aryl group. Here, examples of the aryl group include a group represented by the following structural formula:
【0026】[0026]
【外6】 またアリール基中の少なくとも1つの水素原子は、カル
ボキシル基やスルホキシル基等で置換されていても良
い。[Outside 6] At least one hydrogen atom in the aryl group may be substituted with a carboxyl group, a sulfoxyl group, or the like.
【0027】また上記式(I)中、R3は、置換フェニル
基を表わし,具体的には例えば下記式(III)で示さ
れるような基を挙げることができる。In the above formula (I), R 3 represents a substituted phenyl group, and specific examples include a group represented by the following formula (III).
【0028】(III)(III)
【外7】 [Outside 7]
【0029】上記式(III)中、Mは水素原子、アルカリ
金属(Li,Na、Kなど)アルカリ土類金属(Mg、Caなど)を表
わし、Xはアミノ基や炭素数1〜5程度のアルコキシ基
を表わす。そして上記式(I)で示されるバイオレット
染料の具体例としては、例えば下記No.1〜5のもの
を挙げることができる。In the above formula (III), M represents a hydrogen atom, an alkali metal (Li, Na, K, etc.) or an alkaline earth metal (Mg, Ca, etc.), and X represents an amino group or an alkyl group having about 1 to 5 carbon atoms. Represents an alkoxy group. Specific examples of the violet dye represented by the above formula (I) include, for example, 1 to 5 can be mentioned.
【0030】No.1No. 1
【外8】 [Outside 8]
【0031】No.2No. 2
【外9】 [Outside 9]
【0032】No.3No. 3
【外10】 [Outside 10]
【0033】No.4No. 4
【外11】 [Outside 11]
【0034】No.5No. 5
【外12】 [Outside 12]
【0035】(シアン染料)シアン染料としては、例え
ばフタロシアニン染料を用いることができる。具体的に
は例えば、C.I.Direct Blue 86、
C.I.DirectBlue 87、C.I.Dir
ect Blue 199、C.I.Acid Blu
e 83、C.I.Acid Blue 90等があげ
られる。(Cyan Dye) As the cyan dye, for example, a phthalocyanine dye can be used. Specifically, for example, C.I. I. Direct Blue 86,
C. I. DirectBlue 87, C.I. I. Dir
ect Blue 199, C.I. I. Acid Blu
e83, C.I. I. Acid Blue 90 and the like.
【0036】本発明にかかるインク中におけるシアン染
料とバイオレット染料との重量比は50:1〜1:2、
特には20:1〜1:1、更には10:1〜2:1とし
た場合、光学的な特性に優れた青色画素を得られるため
好ましい。The weight ratio of the cyan dye to the violet dye in the ink according to the present invention is 50: 1 to 1: 2,
In particular, a ratio of 20: 1 to 1: 1, more preferably 10: 1 to 2: 1 is preferable because a blue pixel having excellent optical characteristics can be obtained.
【0037】また、インク中におけるシアン染料とバイ
オレット染料の総重量、即ちインク中の色材の総重量と
しては、インク全重量を基準として0.1〜20wt
%、特には1〜15wt%、更には3〜12wt%の範
囲では、画素に満足しうる光学特性を担持させられると
共にインク特性がインクジェット記録法によって正確に
吐出させることのできる範囲を逸脱するような変化を生
じることもなく好ましいものである。The total weight of the cyan dye and the violet dye in the ink, that is, the total weight of the coloring material in the ink is 0.1 to 20 wt.
%, Especially 1 to 15 wt%, and more preferably 3 to 12 wt%, so that the pixel can have satisfactory optical characteristics and the ink characteristics deviate from the range in which the ink can be ejected accurately by the inkjet recording method. It is preferable that no significant change occurs.
【0038】上記した色材を溶解状態、分散状態あるい
は溶解及び分散状態で保持し、インクを構成する媒体と
しては例えば水を含む水性媒体等を用いることができ、
水性媒体の構成成分としての水の割合は、インク全重量
を基準として10〜90wt%、特には20〜80wt
%とすることが好ましい。The above-mentioned coloring material is held in a dissolved state, a dispersed state or a dissolved and dispersed state, and as a medium constituting the ink, for example, an aqueous medium containing water can be used.
The proportion of water as a component of the aqueous medium is 10 to 90 wt%, especially 20 to 80 wt% based on the total weight of the ink.
% Is preferable.
【0039】インク中に含まれる有機溶剤としては、例
えばメチルアルコール、エチルアルコール、n−プロピ
ルアルコール、イソプロピルアルコール、n−ブチルア
ルコール、sec−ブチルアルコール、tert−ブチ
ルアルコール等の炭素数1〜4のアルキルアルコール
類;ジメチルホルムアミド、ジメチルアセトアミド等の
アミド類アセトン、ジアセトンアルコール等のケトンマ
タハケトアルコール類;テトラヒドロフラン、ジオキサ
ン等のエーテル類;ポリエチレングリコール、ポリプロ
ピレングリコール等のポリアルキレングリコール類;エ
チレングリコール、プロピレングリコール、ブチレング
リコール、トリエチレングリコール、1、2、6−ヘキ
サントリオール、チオジグリコール、ヘキシレングリコ
ール、ジエチレングリコール等のアルキレン基が2〜6
個の炭素原子を含むアルキレングリコール類;グリセリ
ン;エチレングリコールモノメチル(またはエチル)エ
ーテル、ジエチレングリコールメチル(またはエチル)
エーテル、トリエチレングリコールモノメチル(または
エチル)エーテル、等の多価アルコールの低級アルキル
エーテル類;N−メチル−2−ピロリドン、2−ピロリ
ドン、1、3−ジメチル−2−イミダゾリジノン等が挙
げられる。Examples of the organic solvent contained in the ink include those having 1 to 4 carbon atoms such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol and tert-butyl alcohol. Alkyl alcohols; amides such as dimethylformamide and dimethylacetamide; ketone mathataketo alcohols such as acetone and diacetone alcohol; ethers such as tetrahydrofuran and dioxane; polyalkylene glycols such as polyethylene glycol and polypropylene glycol; ethylene glycol and propylene Glycol, butylene glycol, triethylene glycol, 1,2,6-hexanetriol, thiodiglycol, hexylene glycol, diethylene glycol Alkylene group such as a call 2-6
Glycerin; ethylene glycol monomethyl (or ethyl) ether, diethylene glycol methyl (or ethyl)
Lower alkyl ethers of polyhydric alcohols such as ether and triethylene glycol monomethyl (or ethyl) ether; N-methyl-2-pyrrolidone, 2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone and the like; .
【0040】また、インクは非イオン系、アニオン系、
カチオン系等の界面活性剤を用いても良く、他にもpH
調整剤、防カビ剤等の添加剤を必要に応じて添加しても
良い。The ink may be a nonionic type, an anionic type,
A surfactant such as a cationic surfactant may be used.
Additives such as a regulator and a fungicide may be added as necessary.
【0041】ところでこの様なインクは、インクジェッ
ト方式、例えばエネルギー発生素子として電気熱変換体
を用いたバブルジェットタイプ、あるいは圧電素子を用
いたピエゾジェットタイプ等によって記録ヘッドから吐
出させ、カラーフィルタ基板上に付着させて青色の画素
を形成するのに極めて好適に用いられるものである。ま
たこのインクの特性として、インク調合時点において、
インク温度25℃のときに表面張力が30〜60mN/m
(dyne/cm)、粘度を15cP以下、特には10
cP以下、更には5cP以下にすることで、インクの吐
出特性は優れたものとなる。そして本実施態様におい
て、かかる特性を達成することのできる具体的なインク
組成としては例えば後述する実施例に記載したインクを
挙げることができる。By the way, such an ink is ejected from a recording head by an ink jet system, for example, a bubble jet type using an electrothermal converter as an energy generating element, or a piezo jet type using a piezoelectric element, and the like. To form a blue pixel. As a characteristic of this ink, at the time of ink preparation,
Surface tension is 30-60mN / m when ink temperature is 25 ℃
(Dyne / cm) and a viscosity of 15 cP or less, especially 10
By setting the pressure to cP or less, and further to 5 cP or less, the ink ejection characteristics become excellent. In this embodiment, specific ink compositions that can achieve such characteristics include, for example, the inks described in Examples described later.
【0042】(カラーフィルタの製造方法)図1(a)
は、パターン状に遮光部(以降「ブラックマトリク
ス」)2が形成された光透過性の基板1(例えばガラス
基板等)を示したものである。ブラックマトリクス2の
形成方法としては、基板上に直接設ける場合は例えば、
スパッタもしくは蒸着により金属(例えばクロム、酸化
クロム等)の薄膜を形成し、フォトリソ工程によりパタ
ーニングする方法が挙げられ、また樹脂組成物上に設け
る場合は、一般的なフォトリソ工程によるパターニング
の方法が挙げられる。又7は光透過部である。(Method of Manufacturing Color Filter) FIG. 1 (a)
Shows a light-transmitting substrate 1 (for example, a glass substrate or the like) on which a light-shielding portion (hereinafter referred to as a “black matrix”) 2 is formed in a pattern. When the black matrix 2 is formed directly on the substrate, for example,
A method of forming a thin film of a metal (for example, chromium, chromium oxide, or the like) by sputtering or vapor deposition and patterning by a photolithography process is used. In the case of providing a thin film on a resin composition, a patterning method by a general photolithography process is used. Can be Reference numeral 7 denotes a light transmitting portion.
【0043】まず、ブラックマトリクス2の形成された
基板1上に硬化可能な樹脂組成物を含む層を形成し、基
板1上にインク受容層3を形成する(図1(b))。な
お基板としては一般にガラスが用いられるが、液晶用カ
ラーフィルタとしての一般に求められる光透過性や機械
的強度等の特性を満足し得るものであればガラスに限定
されず、例えば透明アクリル樹脂基板等を用いることも
できる。First, a layer containing a curable resin composition is formed on the substrate 1 on which the black matrix 2 is formed, and an ink receiving layer 3 is formed on the substrate 1 (FIG. 1B). In general, glass is used as the substrate, but is not limited to glass as long as it can satisfy characteristics such as light transmittance and mechanical strength generally required as a color filter for liquid crystal. Can also be used.
【0044】インク受容層3を形成する材料としては公
知のものが使用できるが、例えば耐熱性等を考慮する
と、アクリル系樹脂、エポキシ系樹脂、イミド系樹脂が
好適であり、更に水性インクの吸収性を考慮すると、ヒ
ドロキシプロピルセルロース、ヒドロキシエチルセルロ
ース、メチルセルロース、カルボキシメチルセルロース
等のセルロース系水溶性ポリマーを含むものが好まし
い。その他にも例えばポリビニルピロリドン、ポリビニ
ルアルコール、ポリビニルアセタール、ポリウレタン、
ポリエステル等や、アルブミン、ゼラチン、カゼイン、
でんぷん、カチオン化でんぷん、アラビアゴム、アルギ
ン酸ソーダ等の天然樹脂を挙げることができる。特に耐
熱性、インク吸収性に加えて前述した着色部の透明性、
にじみ、染料の耐光性等を考慮すると、ヒドロキシプロ
ピルセルロースとメチロール化メラミンとの混合物、或
は以下の構造単位(IV)からなる単量体の単独及び/
又は他のビニル系単量体との共重合体を少なくとも含む
化合物を用いることが好ましい。As the material for forming the ink receiving layer 3, known materials can be used. For example, in consideration of heat resistance and the like, acrylic resins, epoxy resins, and imide resins are preferable. Considering the properties, those containing a cellulose-based water-soluble polymer such as hydroxypropylcellulose, hydroxyethylcellulose, methylcellulose and carboxymethylcellulose are preferable. In addition, for example, polyvinylpyrrolidone, polyvinyl alcohol, polyvinyl acetal, polyurethane,
Polyester, etc., albumin, gelatin, casein,
Natural resins such as starch, cationized starch, acacia, sodium alginate and the like can be mentioned. In particular, the heat resistance, the transparency of the colored portion described above in addition to the ink absorbency,
In view of the bleeding and light resistance of the dye, etc., a mixture of hydroxypropylcellulose and methylolated melamine, or a monomer having the following structural unit (IV) alone and / or
Alternatively, it is preferable to use a compound containing at least a copolymer with another vinyl monomer.
【0045】式(IV)Formula (IV)
【外13】 [Outside 13]
【0046】なお、上記一般式(IV)中、R12はHま
たはCH3 等、R13はHまたは未置換もしくは炭素数1
〜5の直鎖状もしくは分岐鎖状のアルキル基等で置換さ
れていてもよいアルキル基を表す。上記式(IV)で表
される構造単位に相当する単量体としては、例えばN−
メチロールアクリルアミド、N−メトキシメチルアクリ
ルアミド、N−エトキシメチルアクリルアミド、N−イ
ソプロポキシメチルアクリルアミド、N−メチロールメ
タクリルアミド、N−メトキシメチルメタクリルアミ
ド,N−エトキシメチルメタクリルアミド等を挙げられ
る。また他のビニル系単量体としては、アクリル酸、メ
タクリル酸、アクリル酸エステル(アクリル酸メチル、
アクリル酸エチル等)、メタクリル酸エステル(メタク
リル酸メチル、メタクリル酸エチル等)、水酸基を含有
したビニル系単量体(ヒドロキシメチルメタクリレー
ト、ヒドロキシエチルメタクリレート、ヒドロキシメチ
ルアクリレート、ヒドロキシエチルアクリレート等)、
スチレン、α−メチルスチレン、アクリルアミド、メタ
クリルアミド、アクリロニトリル、アリルアミン、ビニ
ルアミン、酢酸ビニル、プロピオン酸ビニル等を挙げる
ことができる。上記一般式(IV)の構造単位に相当す
る単量体と他のビニル系単量体との共重合比はモル比で
95:5〜5:95の範囲が望ましい。In the above general formula (IV), R12 is H or CH3, etc., and R13 is H or unsubstituted or C1.
Represents an alkyl group which may be substituted with a linear or branched alkyl group, etc. Examples of the monomer corresponding to the structural unit represented by the above formula (IV) include N-
Methylol acrylamide, N-methoxymethyl acrylamide, N-ethoxymethyl acrylamide, N-isopropoxymethyl acrylamide, N-methylol methacrylamide, N-methoxymethyl methacrylamide, N-ethoxymethyl methacrylamide and the like. Other vinyl monomers include acrylic acid, methacrylic acid, acrylic acid esters (methyl acrylate,
Ethyl acrylate, etc.), methacrylates (methyl methacrylate, ethyl methacrylate, etc.), vinyl monomers containing hydroxyl groups (hydroxymethyl methacrylate, hydroxyethyl methacrylate, hydroxymethyl acrylate, hydroxyethyl acrylate, etc.),
Styrene, α-methylstyrene, acrylamide, methacrylamide, acrylonitrile, allylamine, vinylamine, vinyl acetate, vinyl propionate and the like can be mentioned. The copolymerization ratio of the monomer corresponding to the structural unit of the general formula (IV) to another vinyl monomer is desirably in the range of 95: 5 to 5:95 in molar ratio.
【0047】また、上記受容層3には必要に応じて各種
添加剤を含んでもよい。添加剤の具体的な一例としては
各種界面活性剤、染料固着剤(耐水化剤)、消泡剤、酸
化防止剤、蛍光増白剤、紫外線吸収剤、分散剤、粘度調
整剤、pH調整剤、防カビ剤、可塑剤が挙げられる。こ
れらの添加剤については従来公知の化合物から目的に応
じて任意に選択すればよい。The receiving layer 3 may contain various additives as necessary. Specific examples of additives include various surfactants, dye fixatives (waterproofing agents), defoamers, antioxidants, fluorescent brighteners, ultraviolet absorbers, dispersants, viscosity adjusters, and pH adjusters. , A fungicide and a plasticizer. These additives may be arbitrarily selected from conventionally known compounds according to the purpose.
【0048】インク受容層3の形成方法としては、スピ
ンコート、ロールコート、バーコート、スプレーコー
ト、ディップコート等の方法を用いることができる。ま
た必要に応じてプリベークを行なっても良い。As a method for forming the ink receiving layer 3, methods such as spin coating, roll coating, bar coating, spray coating, and dip coating can be used. Prebaking may be performed as needed.
【0049】次いでインクジェット方式により前記した
本発明にかかるインクをインク受容層3の画素形成部位
に付着させ、該インク受容層3の所定の部位を着色せし
める(図1(c))。インクジェット方式としては、エ
ネルギー発生素子として電気熱変換体を用いたバブルジ
ェット(登録商標)タイプ、あるいは圧電素子を用いた
ピエゾジェットタイプ等が使用可能であり、着色面積お
よび着色パターンは任意に設定することができる。ここ
で図2を用いてインクジェット法にてインクを噴射し画
素を形成するための好ましい方法について述べると、図
2はインクジェット法にてカラーフィルタの着色部を描
画する装置の構成を示すブロック図である。図2におい
てCPU21はヘッド駆動回路22を介してインクジェ
ット記録ヘッド4と接続されている。更にCPU21に
はプログラムメモリ23内の制御プログラム情報が入力
される様に構成されている。そしてCPU21はインク
ジェット記録ヘッド4を基板1上の所定の位置まで移動
させ(不図示)、基板1上の所望の画素位置をインクジ
ェットヘッドの下方にもたらし、その位置に所望の色の
インク24を吐出して着色する。これを基板1上の所望
の画素位置に対して行うことによりカラーフィルタを製
造することができるものである。Next, the ink according to the present invention described above is attached to the pixel forming portion of the ink receiving layer 3 by an ink jet method, and a predetermined portion of the ink receiving layer 3 is colored (FIG. 1C). As the ink jet method, a bubble jet (registered trademark) type using an electrothermal converter or a piezo jet type using a piezoelectric element as an energy generating element can be used, and the coloring area and the coloring pattern are arbitrarily set. be able to. Here, a preferred method for forming pixels by ejecting ink by an ink-jet method will be described with reference to FIG. 2. FIG. 2 is a block diagram showing a configuration of an apparatus for drawing a colored portion of a color filter by an ink-jet method. is there. In FIG. 2, the CPU 21 is connected to the ink jet recording head 4 via a head driving circuit 22. Further, the CPU 21 is configured so that control program information in the program memory 23 is input. Then, the CPU 21 moves the ink jet recording head 4 to a predetermined position on the substrate 1 (not shown), brings a desired pixel position on the substrate 1 below the ink jet head, and discharges a desired color ink 24 to the position. And color. By performing this for a desired pixel position on the substrate 1, a color filter can be manufactured.
【0050】ところで作成しようとするカラーフィルタ
がR(レッド)、G(グリーン)及びB(ブルー)の画
素を有するものとする場合、グリーン及びブルーの画素
の形成に用いるインクとしては適宜公知のインクを用い
て本発明にかかる赤のインクと同時に、或いは1色毎に
インク受容層3の所定の部位を染色してRGB各々の画
素を形成すればよい。When the color filter to be formed has R (red), G (green) and B (blue) pixels, a known ink may be used as an ink for forming the green and blue pixels. A predetermined portion of the ink receiving layer 3 may be dyed simultaneously with the red ink according to the present invention or for each color to form RGB pixels.
【0051】次にインク受容層3を硬化させる(図1
(d)。硬化方法としてはインク受容層に用いた硬化性
樹脂に適した方法を用いれば良く例えば加熱、光照射あ
るいは加熱及び光照射を行なって硬化させ、各色の着色
画素11を形成する。ここでインク吸収層に照射する光
としては特に限定されるものではない。また光照射条件
としては1〜3000mJ/cm2 程度が好適である。
また熱処理としては例えばオーブン、ホットプレート等
の手段によるものが挙げられ、温度条件150〜250
℃で1〜120分行えばよい。Next, the ink receiving layer 3 is cured (FIG. 1)
(D). As a curing method, a method suitable for the curable resin used for the ink receiving layer may be used. For example, heating, light irradiation, or heating and light irradiation are performed to cure, thereby forming colored pixels 11 of each color. Here, the light applied to the ink absorbing layer is not particularly limited. Light irradiation conditions are preferably about 1 to 3000 mJ / cm 2 .
Examples of the heat treatment include those using means such as an oven and a hot plate.
C. for 1 to 120 minutes.
【0052】この後、必要に応じて硬化せしめたインク
受容層3上に保護層を形成する(図1(e))。保護層
6は、例えば光照射または熱処理により硬化可能な樹脂
材料を塗布し、それに引き続いて硬化せしめることによ
って、或いは無機膜を蒸着又はスパッタリングにより形
成することで設けることができる。保護層に用い得る材
料としては、保護層としたときにカラーフィルターに必
要な透明性を損なわず、またその後に必要に応じて行わ
れるITO形成プロセスや配向膜形成プロセス等に耐え
うるものが好適に用いられ、具体的には例えば有機材料
としてはエポキシアクリレート、ウレタンアクリレート
等のアクリル系樹脂等が、無機材料としてはSiO2 等
を挙げることができる。この様にして本実施態様にかか
るカラーフィルタ9を得ることができる。Thereafter, a protective layer is formed on the cured ink receiving layer 3 as required (FIG. 1 (e)). The protective layer 6 can be provided by applying a resin material curable by, for example, light irradiation or heat treatment, and subsequently curing the resin material, or by forming an inorganic film by vapor deposition or sputtering. As a material that can be used for the protective layer, a material that does not impair the transparency required for the color filter when the protective layer is used and that can withstand an ITO forming process or an alignment film forming process that is performed as necessary thereafter is preferable. Specifically, for example, an organic material includes an acrylic resin such as epoxy acrylate and urethane acrylate, and an inorganic material includes SiO 2 . Thus, the color filter 9 according to the present embodiment can be obtained.
【0053】(第2の実施態様)次に本発明にかかるカ
ラーフィルタの第2の実施態様について説明する。本実
施態様は、インク受容層3に対してインクを付与するに
先立って、インク受容層3のブラックマトリックス2に
対応する部位を硬化させ、インク吸収性を予め低下させ
る点において第1の実施態様とは異なっている。本実施
態様を図3を用いてその製造プロセスに沿って説明する
と、まず第1の実施態様にて説明したのと同様の方法で
作成した、表面にブラックマトリックス2を形成した基
板1を用意し、ブラックマトリックス2を被覆する様に
インク受容層3を形成する(図3(a)及び(b))。
ここでインク受容層3は光照射によってその表面がイン
クの吸収性が低下する様な材料を用いることが好まし
い。(Second Embodiment) Next, a second embodiment of the color filter according to the present invention will be described. The first embodiment is characterized in that before ink is applied to the ink receiving layer 3, a portion of the ink receiving layer 3 corresponding to the black matrix 2 is cured to reduce the ink absorbency in advance. Is different from This embodiment will be described with reference to FIG. 3 along the manufacturing process. First, a substrate 1 having a black matrix 2 formed on the surface, prepared by the same method as described in the first embodiment, is prepared. Then, an ink receiving layer 3 is formed so as to cover the black matrix 2 (FIGS. 3A and 3B).
Here, it is preferable that the ink receiving layer 3 be made of a material whose surface has reduced ink absorbability by light irradiation.
【0054】この実施態様においてインク受容層3を構
成する材料としては、上記した第1の実施態様において
用いられるインク受容層3の構成材料に、更に光重合開
始剤を含有させたものが好適に用いられる。ここで用い
られる光重合開始剤の例としては、例えばオニウム塩、
ハロゲン化トリアジン化合物が好ましく用いられる。具
体的にはオニウム塩としては、トリフェニルスルホニウ
ムヘキサフルオロアンチモネート、トリフェニルスルホ
ニウムテトラフルオロボレート、トリフェニルスルホニ
ウムヘキサフルオロホスフェート、トリフェニルスルホ
ニウムトリフルオロメチルスルホネートまたこれらの誘
導体、さらにジフェニルヨードニウムヘキサフルオロア
ンチモネート、ジフェニルヨードニウムテトラフルオロ
ボレート、ジフェニルヨードニウムヘキサフルオロホス
フェート、ジフェニルヨードニウムトリフルオロメチル
スルホネートまたはこれらの誘導体等が挙げられる。そ
の中でもハロゲン化トリアジン化合物が好適に用いられ
る。さらにそれら化合物の誘導体等も挙げられる。上記
光重合開始剤の配合量は、前記インク受容層材料に対し
て重量基準で0.01〜20%、好ましくは0.1〜1
0%である。また増感剤としてペリレン、アントラセン
等の化合物を加えてもよい。The material constituting the ink receiving layer 3 in this embodiment is preferably a material obtained by further adding a photopolymerization initiator to the material of the ink receiving layer 3 used in the first embodiment. Used. Examples of the photopolymerization initiator used here, for example, onium salt,
Halogenated triazine compounds are preferably used. Specifically, as onium salts, triphenylsulfonium hexafluoroantimonate, triphenylsulfonium tetrafluoroborate, triphenylsulfonium hexafluorophosphate, triphenylsulfonium trifluoromethylsulfonate and derivatives thereof, and further diphenyliodonium hexafluoroantimonate , Diphenyliodonium tetrafluoroborate, diphenyliodonium hexafluorophosphate, diphenyliodonium trifluoromethylsulfonate or derivatives thereof. Among them, halogenated triazine compounds are preferably used. Further, derivatives of these compounds are also included. The compounding amount of the photopolymerization initiator is 0.01 to 20% by weight, preferably 0.1 to 1%, based on the weight of the ink receiving layer material.
0%. Further, a compound such as perylene or anthracene may be added as a sensitizer.
【0055】次いでインク受容層3のブラックマトリク
スに対応する部分を、例えばフォトマスク41等を用い
て選択的に露光し、インク受容層3のブラックマトリッ
クス2に対応する部分を硬化させる(図3(c))。そ
の結果インク受容層3に選択的にインク吸収性の低い部
分(非着色用部分)42が形成される。ここでパターン
露光に用いるフォトマスク42としては、例えばブラッ
クマトリクス2に対応するインク受容層部分に選択的に
露光可能な開口部43を備えたものを使用する。ここで
開口部43の幅(Y)はブラックマトリクス2の幅
(X)よりも狭くすることが好ましい。即ちこの方法で
カラーフィルタを形成したときに、各画素とブラックマ
トリクス2の境界部分において色ヌケが生じることは好
ましくなく、それを防止するためにはインク受容層の各
画素が形成されるべき領域に多めのインクを吐出するこ
とが好ましい。このことを考慮するとインク受容層3の
非着色用部分の幅をブラックマトリックス2の幅(X)
よりも狭くすることが好ましく、このような非着色用部
分は、上記した開口部43の幅(Y)はブラックマトリ
クス2の幅(X)よりも狭くしたフォトマスク42を用
いることによって形成することができる。なお非着色用
部分43を形成する際にインク吸収層に照射する光とし
ては特に限定されるものではない。また光照射条件とし
ては1〜3000mJ/cm2 程度が好適である。また
熱処理は例えばオーブン、ホットプレート等の手段によ
るものが挙げられ、温度条件150−250℃で1−1
20分行なえばよい。Next, the portion corresponding to the black matrix of the ink receiving layer 3 is selectively exposed using, for example, a photomask 41 or the like, and the portion corresponding to the black matrix 2 of the ink receiving layer 3 is cured (FIG. c)). As a result, a portion (non-coloring portion) 42 having a low ink absorbency is selectively formed on the ink receiving layer 3. Here, as the photomask 42 used for pattern exposure, for example, a photomask having an opening 43 that can be selectively exposed to an ink receiving layer portion corresponding to the black matrix 2 is used. Here, the width (Y) of the opening 43 is preferably smaller than the width (X) of the black matrix 2. That is, when a color filter is formed by this method, it is not preferable that a color drop occurs at a boundary portion between each pixel and the black matrix 2. It is preferable to discharge more ink. In consideration of this, the width of the non-colored portion of the ink receiving layer 3 is set to the width (X) of the black matrix 2.
Such a non-colored portion is preferably formed by using a photomask 42 in which the width (Y) of the opening 43 is smaller than the width (X) of the black matrix 2. Can be. The light to be applied to the ink absorbing layer when forming the non-colored portion 43 is not particularly limited. Light irradiation conditions are preferably about 1 to 3000 mJ / cm 2 . The heat treatment may be performed by, for example, an oven, a hot plate, or the like.
All you have to do for 20 minutes.
【0056】それ以降の工程(図3(d)〜(f))
は、図1(c)〜(e)に記載した様に各画素が形成さ
れるべき位置にインクジェット法によってインクを付与
し、インク受容層3の硬化を行うことにより、カラーフ
ィルタを作製することができる。Subsequent steps (FIGS. 3D to 3F)
Is to form a color filter by applying ink to a position where each pixel is to be formed by an inkjet method and curing the ink receiving layer 3 as described in FIGS. 1C to 1E. Can be.
【0057】この実施態様によれば、インクジェット法
にてR,G,B各画を形成する際に発生しやすい各画素
間、特に隣接する画素間等での混色、色ムラ等によるト
ラブルを防止することができ、低コストかつ高画質のカ
ラーフィルタの製造が可能となる。According to this embodiment, troubles due to color mixing, color unevenness, etc., between pixels, particularly between adjacent pixels, which are likely to occur when forming R, G, B images by the ink jet method, are prevented. Thus, a low-cost and high-quality color filter can be manufactured.
【0058】(第3の実施態様)次にインク受容層3を
設けることなしにカラーフィルタを製造する点に一つの
特徴を有する、本発明の第3の実施態様にかかるカラー
フィルタについて図4を用いてその製造工程に沿って説
明する。(Third Embodiment) Next, FIG. 4 shows a color filter according to a third embodiment of the present invention, which has one feature in that a color filter is manufactured without providing the ink receiving layer 3. The method will be described along with the manufacturing process.
【0059】まず第1の実施態様にて記載したのと同様
の方法で表面にブラックマトリクス2を形成した基板を
用意する(図4(a))。なお本態様においては、各画
素間に所定の厚さ(例えば0.5μm以上の壁を作って
おくことが好ましく、その為に黒色の樹脂レジストをパ
ターニングしてブラックマトリックス2を形成すること
が好ましい。First, a substrate having a black matrix 2 formed on the surface by the same method as described in the first embodiment is prepared (FIG. 4A). In this embodiment, it is preferable that a wall having a predetermined thickness (for example, 0.5 μm or more) is formed between each pixel, and for this purpose, it is preferable to form a black matrix 2 by patterning a black resin resist. .
【0060】次に、図4(b)に示すように、インクジ
ェット方式を利用して、前記した本発明にかかる赤イン
ク51、及び公知の種々のGインク52及びBインク5
3を、ブラックマトリクス2の間の光透過部55を埋め
るようにして付与する。このときブラックマトリクス2
上で各色インクが重ならない様に付与することが好まし
い。Next, as shown in FIG. 4 (b), the above-described red ink 51 according to the present invention and various known G inks 52 and B inks 5 are formed by using an ink jet method.
3 is applied so as to fill the light transmitting portion 55 between the black matrices 2. At this time, black matrix 2
It is preferable to apply the inks so that the color inks do not overlap.
【0061】(インク組成)ここで本態様に用いる赤の
画素を与えるインクとしては、前記の含金アゾピラゾロ
ン染料とキサンテン骨格を備えた染料とを含むインクを
用いることができるが、該インクに光、熱あるいは光及
び熱などのエネルギーの付与により硬化可能な樹脂を含
有させたものを特に好適に用いることができる。またG
インク及びBインクにも該樹脂を含有させたものを用い
ることが好ましい。(Ink Composition) As the ink for giving a red pixel used in the present embodiment, an ink containing the above-described gold-containing azopyrazolone dye and a dye having a xanthene skeleton can be used. Those containing a resin curable by application of energy such as light, heat, or light and heat can be particularly preferably used. G
It is preferable to use the ink and the B ink containing the resin.
【0062】(インク中硬化性樹脂成分の説明/含有
量)ここで上記樹脂としては、様々な市販の樹脂、硬化
剤を用いることができるが、インク中で固着等の問題を
起こさないものが好ましい。このような材料としては例
えばアクリル系樹脂、エポキシ系樹脂、メラミン樹脂等
が挙げられる。また、インク中に含まれる光硬化可能な
成分あるいは熱硬化可能である成分あるいは光及び熱の
双方により硬化可能な成分の量としては、インク全重量
を基準として例えば0.1〜20%程度が好ましい。(Explanation / Content of Curable Resin Component in Ink) As the above resin, various commercially available resins and curing agents can be used, but those which do not cause a problem such as fixation in the ink can be used. preferable. Examples of such a material include an acrylic resin, an epoxy resin, and a melamine resin. The amount of the photo-curable component or the thermo-curable component or the component curable by both light and heat contained in the ink is, for example, about 0.1 to 20% based on the total weight of the ink. preferable.
【0063】次いで、図4(c)に示すように光照射、
加熱あるいは光照射と加熱の両方を行って基板1上の開
口部55に付与したインクを部分硬化させ、次いで図4
(d)に示すようにブラックマトリクス2及び各色のイ
ンクによって形成された着色部位54を被覆する様に硬
化性樹脂組成物を塗布し、光照射及び/又は熱処理によ
り着色部位54を完全に硬化させて着色画素11を完成
させると共に硬化性樹脂組成物を硬化させて保護層6を
形成し、カラーフィルタを得る。なお保護層6として
は、光照射または熱処理、あるいはこれらの両方により
硬化可能な樹脂材料を硬化させて形成する他に、無機膜
を蒸着またはスパッタによって形成して保護膜6として
もよい。また保護膜6の形成に用い得る材料としては、
カラーフィルタとした場合の透明性を有し、その後のI
TO形成プロセス、配光膜形成プロセス等に耐えうるも
のが好適に使用できる。Next, as shown in FIG.
The ink applied to the openings 55 on the substrate 1 is partially cured by heating or both light irradiation and heating, and then FIG.
As shown in (d), the curable resin composition is applied so as to cover the colored portion 54 formed by the black matrix 2 and the ink of each color, and the colored portion 54 is completely cured by light irradiation and / or heat treatment. Thus, the colored pixel 11 is completed, and the curable resin composition is cured to form the protective layer 6, thereby obtaining a color filter. The protective layer 6 may be formed by curing a resin material that can be cured by light irradiation or heat treatment, or both, or may be formed by depositing or sputtering an inorganic film to form the protective film 6. Materials that can be used for forming the protective film 6 include:
It has the transparency of a color filter, and
What can withstand a TO formation process, a light distribution film formation process, etc. can be used suitably.
【0064】(液晶パネル)ところで上記した各実施態
様によって形成されるカラーフィルタ9は、例えば図5
に示した様にカラーフィルタ9と基板61とを対向配置
し、その間に液晶組成物62を封入することによって液
晶パネルを形成することができる。図5に本発明のカラ
ーフィルタを組み込んだTFTカラー液晶パネルの断面
図を示す。即ちカラー液晶パネルは、カラーフィルタ9
と対向する基板61を合わせ込み、その間に液晶組成物
62を封入することにより形成される。液晶パネルの一
方の基板の内側にTFT(不図示)と透明な画素電極6
3がマトリクス状に形成されている。またカラーフィル
タ9の保護層6の表面には透明な対向(共通)電極64
が一面に形成されている。更に該対向基板61の内側表
面には該画素電極63を被覆する様に配向膜65が形成
され、また該対向電極64の内側表面にも配向膜66が
形成されている。そしてこれらの配向膜をラビング処理
することにより液晶分子を一定方向に配列させることが
できる。こうして作成された液晶パネルは、カラーフィ
ルタの基板1及び対向基板61の外側に偏光板67を接
着し、一般的には蛍光灯と散乱板を組合わせたバックラ
イトを用いて、液晶化合物をバックライトの光68の透
過率を変化させる光シャッターとして機能させることに
より表示を行なわせることができる。なおブラックマト
リクス及び着色部は、図5に示した様に、通常カラーフ
ィルター基板側に形成されるが、ブラックマトリクス
(BM)オンアレイタイプの液晶パネルにおいては図6
に示す様にBMは対向するTFT基板側に形成され、ま
たカラーフィルタ(CF)オンアレイタイプの場合はC
F部が図7に示す様にTFT基板側に形成される。(Liquid Crystal Panel) By the way, the color filter 9 formed by each of the above-described embodiments is, for example, shown in FIG.
The liquid crystal panel can be formed by disposing the color filter 9 and the substrate 61 to face each other and sealing the liquid crystal composition 62 therebetween as shown in FIG. FIG. 5 is a sectional view of a TFT color liquid crystal panel incorporating the color filter of the present invention. That is, the color liquid crystal panel is
Are formed by combining a substrate 61 facing the substrate and sealing a liquid crystal composition 62 therebetween. A TFT (not shown) and a transparent pixel electrode 6 are provided inside one substrate of the liquid crystal panel.
3 are formed in a matrix. A transparent opposing (common) electrode 64 is provided on the surface of the protective layer 6 of the color filter 9.
Is formed on one side. Further, an alignment film 65 is formed on the inner surface of the counter substrate 61 so as to cover the pixel electrode 63, and an alignment film 66 is formed on the inner surface of the counter electrode 64. By subjecting these alignment films to a rubbing treatment, liquid crystal molecules can be arranged in a certain direction. In the liquid crystal panel thus manufactured, a polarizing plate 67 is adhered to the outside of the color filter substrate 1 and the counter substrate 61, and the liquid crystal compound is generally backed using a backlight in which a fluorescent lamp and a scattering plate are combined. Display can be performed by functioning as an optical shutter that changes the transmittance of the light 68 of the light. The black matrix and the colored portion are usually formed on the color filter substrate side as shown in FIG. 5, but in a black matrix (BM) on-array type liquid crystal panel, FIG.
As shown in the figure, the BM is formed on the opposite TFT substrate side, and in the case of a color filter (CF) on-array type, C
An F portion is formed on the TFT substrate side as shown in FIG.
【0065】そしてこの様にして作成された液晶パネル
は例えば図8に示すようなコンピュータ91等の画像表
示装置92として用いられる。The liquid crystal panel thus prepared is used as an image display device 92 such as a computer 91 as shown in FIG.
【0066】[0066]
【実施例】〔実施例1〕60×150μmの大きさの開
口部を有するクロムからなるブラックマトリクスを備え
たガラス基板上に、インク受容層としてN−メチロール
アクリルアミドとヒドロキシエチルメタクリレートの2
元重合体(重合比40:60)を膜厚1.2μmとなる
ようにスピンコートし、120℃、20分のプリベーク
を行いインク受容層とした。Example 1 A glass substrate provided with a black matrix made of chromium having openings of 60 × 150 μm was provided on a glass substrate with N-methylolacrylamide and hydroxyethyl methacrylate as ink receiving layers.
The base polymer (polymerization ratio 40:60) was spin-coated so as to have a film thickness of 1.2 μm, and prebaked at 120 ° C. for 20 minutes to form an ink receiving layer.
【0067】一方青インクとして、シアン染料にはDi
rect Blue 199を、バイオレット染料には表
1に示す化合物を用い、それぞれ各青インクの色度を合
わせる為に、色度座標でy=0.13のときx=0.1
5になるように、シアン染料とバイオレット染料の比率
を約5:1に設定し、水性有機溶媒(エチレングリコー
ル)を30wt%含んでいる水に、インクに対する全色
材濃度が、インク全量に対して、約3.5wt%重量%
となるように溶解した。On the other hand, as a blue ink, a cyan dye
Rect Blue 199 and the compounds shown in Table 1 as violet dyes. In order to adjust the chromaticity of each blue ink, x = 0.1 when y = 0.13 in chromaticity coordinates.
The ratio of the cyan dye to the violet dye was set to about 5: 1 so that the total colorant concentration of the ink in water containing 30% by weight of an aqueous organic solvent (ethylene glycol) was adjusted with respect to the total amount of the ink. About 3.5wt% weight%
It dissolved so that it might become.
【0068】[0068]
【表1】表1 [Table 1] Table 1
【0069】また赤インクについてはC.I.Acid
Red 158を染料として用い、また緑インクにつ
いてはC.I.Acid Green 9を染料として
用い、同様に水及び水性有機溶媒に溶解した。For the red ink, C.I. I. Acid
Red 158 is used as a dye, and green ink is C.I. I. Acid Green 9 was used as a dye and similarly dissolved in water and aqueous organic solvents.
【0070】これらのインクを、予め吐出観察によって
常にほぼ一定の吐出量であることが確認されているイン
クジェット記録装置を用いて、吐出量20ng、吐出ピ
ッチ20μmでインク受容層に付与し、マトリクスパタ
ーンを形成した。次いで230℃、50分のベーキング
を行うことにより硬化反応を進行させ、乾燥後、更にそ
の上に2液型のアクリル系熱硬化方樹脂材料(商品名S
S-7625 日本合成ゴム社製)を膜厚1μmになる
ようにスピンコートし、240℃、20分の熱処理を行
って硬化させ、本実施例のカラーフィルタを作成した。
得られたカラーフィルタを以下の項目について評価し
た。その結果を表3に示す。These inks are applied to the ink receiving layer at an ejection amount of 20 ng and an ejection pitch of 20 μm by using an ink jet recording apparatus which has been confirmed in advance by an ejection observation that the ejection amount is always substantially constant. Was formed. Next, a baking is performed at 230 ° C. for 50 minutes to advance a curing reaction, and after drying, a two-component acrylic thermosetting resin material (trade name S)
S-7625 (manufactured by Nippon Synthetic Rubber Co., Ltd.) was spin-coated so as to have a film thickness of 1 μm, and cured by heat treatment at 240 ° C. for 20 minutes to produce a color filter of this example.
The obtained color filters were evaluated for the following items. Table 3 shows the results.
【0071】評価1 :着色部の透明性 得られたカラーフィルタの青色画素部の透明性を目視に
て3段階にグループ分けすることにより評価した。 A :透明性良好。 B :やや透明性が劣る。 C :A、Bのものと比較してよりくすんでいる。Evaluation 1: Transparency of the Colored Part The transparency of the blue pixel part of the obtained color filter was visually evaluated by being divided into three groups. A: Good transparency. B: Transparency is somewhat poor. C: It is more dull than those of A and B.
【0072】評価2 :染料濃度 y=0.13、x=0.15の色度を示す青色画素を得る為に必
要なインクの染料濃度を、本実施例にかかる色材の組合
せと、当該組合せのうちのバイオレット染料を、従来の
青色画素形成用のインクに用いられているバイオレット
染料に代えた組合せとの間で、下記の様にして比較し
た。即ち、まず本実施例において用いたバイオレット染
料に代えて、従来青インクに好適に用いられているC.
I.アシッドレッド52を用いた以外は、同様にしてイ
ンクを調製し、同様にしてカラーフィルタ基板上に青色
画素部を形成した。これを対照例とする。本実施例およ
び対照例のカラーフィルタ基板の各々の青色画素部を分
光光度計(商品名:OSP200、オリンパス社製)で
測定し、得られた透過率スペクトルから、色度座標でy
=0.13の青色画素を得る為に必要なインクの染料濃
度をそれぞれシミュレーションによって算出した。そし
て対照例の色材の組合せにおいて必要なインクの色材濃
度を基準として、本発明の色材の組合せにおいて必要な
インクの色材濃度を算出した。その結果を表2に示す。Evaluation 2: Dye concentration The dye concentration of the ink required to obtain a blue pixel having a chromaticity of y = 0.13 and x = 0.15 is determined by the combination of the color materials according to the present embodiment and the combination of the color materials. The violet dye was compared as follows with a combination replacing the violet dye used in the conventional ink for forming a blue pixel. That is, first, in place of the violet dye used in this example, C.I.
An ink was prepared in the same manner except that I. Acid Red 52 was used, and a blue pixel portion was formed on a color filter substrate in the same manner. This is used as a control. The blue pixel portions of each of the color filter substrates of the present example and the comparative example were measured with a spectrophotometer (trade name: OSP200, manufactured by Olympus Corporation), and y in chromaticity coordinates was obtained from the obtained transmittance spectrum.
The dye concentration of the ink required to obtain a blue pixel of = 0.13 was calculated by simulation. Then, the color material density of the ink required in the combination of the color materials of the present invention was calculated based on the color material density of the ink required in the color material combination of the control example. Table 2 shows the results.
【0073】〔比較例1〕バイオレット染料にC.
I. Acid Red 94を用いる以外は、実施例1
と同様にしてカラーフィルタを作成し、上記と同様にし
て評価した。その結果を表2に示す。[Comparative Example 1] C.I.
I. Example 1 except that Acid Red 94 was used.
A color filter was prepared in the same manner as described above, and evaluated in the same manner as above. Table 2 shows the results.
【0074】[0074]
【表2】表2 [Table 2] Table 2
【0075】〔実施例2〕ガラス基板上に黒色顔料を含
む感光性樹脂(商品名:黒色顔料レジストCK−S17
1B;富士ハント(株)社製)をスピンコート法により
塗布し、パターン露光、現像、熱処理により厚さ1.0
μmのブラックマトリクスを形成した。Example 2 A photosensitive resin containing a black pigment on a glass substrate (trade name: Black Pigment Resist CK-S17)
1B; manufactured by Fuji Hunt Co., Ltd.) by spin coating and pattern exposure, development and heat treatment to a thickness of 1.0
A black matrix of μm was formed.
【0076】一方青インクとして、シアン染料にはDi
rect Blue 199を、バイオレット染料には表
1に示す化合物を用い、それぞれ各青インクの色度を合
わせる為に、色度座標でy=0.13のときx=0.1
5になるようシアン染料とバイオレット染料の比率を、
シアン染料:バイオレット染料=5:1に設定し、N−
メチロールアクリルアミド20部、N,N−ジメチルア
ミノエチルメタクリレート10部、メタクリル酸メチル
30部、2-ヒドロキシエチルメタクリレート40部か
らなる高分子化合物を5.0wt%の割合で水に溶解し
た樹脂溶液に、全色材濃度がインク全量に対して3.5
wt%となるように溶解した。On the other hand, as a blue ink, a cyan dye
Rect Blue 199 and the compounds shown in Table 1 as violet dyes. In order to adjust the chromaticity of each blue ink, x = 0.1 when y = 0.13 in chromaticity coordinates.
The ratio of the cyan dye to the violet dye is set to be 5,
Cyan dye: violet dye = 5: 1, N-
A polymer solution comprising 20 parts of methylolacrylamide, 10 parts of N, N-dimethylaminoethyl methacrylate, 30 parts of methyl methacrylate, and 40 parts of 2-hydroxyethyl methacrylate was dissolved in water at a ratio of 5.0 wt% to a resin solution. All color material density is 3.5 with respect to the total amount of ink
It melt | dissolved so that it might become wt%.
【0077】また赤インクについてはC. I. Aci
d Red 158を染料として用い、また緑インクにつ
いてはC. I. Acid Green 9を染料として
用い、同様に樹脂溶媒に溶解した。For the red ink, C.I. I. Aci
d Red 158 is used as a dye, and green ink is C.I. I. Acid Green 9 was used as a dye and similarly dissolved in a resin solvent.
【0078】これらのインクを実施例1で用いたインク
ジェット記録装置により開口部に60ng吐出し、次い
で230℃、30分の熱処理により該インクを硬化させ
本実施例のカラーフィルタを作成した。[0078] These inks were ejected into the openings by 60 ng by the ink jet recording apparatus used in Example 1, and then cured by heat treatment at 230 ° C for 30 minutes to produce a color filter of this example.
【0079】評価1 :着色部の透明性 得られたカラーフィルタを実施例1と同様にして評価し
た。その結果を表3に示す。Evaluation 1: Transparency of colored part The obtained color filter was evaluated in the same manner as in Example 1. Table 3 shows the results.
【0080】評価2 :染料濃度 y=0.13、x=0.15の色度を有する青色画素を得る為に
必要なインクの染料濃度を、本実施例にかかる色材の組
合せと、当該組合せのうちのバイオレット染料を、従来
の青色が素の形成用インクに用いられているC.I.アシ
ッドレッド289に代えた組合せとの間で、比較した。
具体的な方法は、実施例1の評価2に記載の方法に準じ
て行った。その結果を表3に示す。Evaluation 2: Dye Concentration The dye concentration of the ink required to obtain a blue pixel having chromaticity of y = 0.13 and x = 0.15 is determined by the combination of the color materials according to the present embodiment and the combination of the color materials. The violet dye was compared with a combination replacing CI Acid Red 289, which is used in conventional blue based inks.
The specific method was performed according to the method described in Evaluation 2 of Example 1. Table 3 shows the results.
【0081】〔比較例2〕バイオレット染料にC.
I. Acid Red 51を用いる以外は実施例2と
同様にしてカラーフィルタを作成し、上記と同様にして
評価した。その結果を表3に示す。y=[Comparative Example 2] C.I.
I. A color filter was prepared in the same manner as in Example 2 except that Acid Red 51 was used, and evaluated in the same manner as above. Table 3 shows the results. y =
【0082】[0082]
【表3】表3 [Table 3] Table 3
【0083】[0083]
【発明の効果】以上説明したように、本発明によれば、
色特性に優れて且つ、従来カラーフィルタに一般的に使
用されていたインクと比べ、色度を同一にした場合、よ
り染料濃度が低くなるような青インクを提供することが
できる。また本発明によれば、透明度の高い青色画素を
具備している高品位なカラーフィルタを得ることができ
る。また、かかるカラーフィルタを用いることで、高品
位な液晶パネルを得ることができる。更に、このような
カラーフィルタを用いることにより、高品位な画像表示
部を有しているコンピュータや画像表示デバイスを得る
ことができる。As described above, according to the present invention,
It is possible to provide a blue ink that has excellent color characteristics and has a lower dye concentration when the chromaticity is the same as that of the ink generally used in the conventional color filters. Further, according to the present invention, a high-quality color filter having blue pixels with high transparency can be obtained. Further, by using such a color filter, a high-quality liquid crystal panel can be obtained. Further, by using such a color filter, a computer or an image display device having a high-quality image display portion can be obtained.
【図1】本発明の一実施態様にかかるカラーフィルタの
製造方法の工程図である。FIG. 1 is a process chart of a method for manufacturing a color filter according to an embodiment of the present invention.
【図2】インクジェット法を用いたカラーフィルタの画
素を形成する方法の概略説明図である。FIG. 2 is a schematic explanatory view of a method of forming a pixel of a color filter using an inkjet method.
【図3】本発明の他の実施態様にかかるカラーフィルタ
の製造方法の工程図である。FIG. 3 is a process chart of a method for manufacturing a color filter according to another embodiment of the present invention.
【図4】本発明の更に他の実施態様にかかるカラーフィ
ルタの製造方法の工程図である。FIG. 4 is a process chart of a method of manufacturing a color filter according to still another embodiment of the present invention.
【図5】本発明の一実施態様にかかる液晶パネルの概略
断面図である。FIG. 5 is a schematic sectional view of a liquid crystal panel according to one embodiment of the present invention.
【図6】本発明の他の実施態様にかかる液晶パネルの概
略断面図である。FIG. 6 is a schematic sectional view of a liquid crystal panel according to another embodiment of the present invention.
【図7】本発明の更に他の実施態様にかかる液晶パネル
の概略断面図である。FIG. 7 is a schematic sectional view of a liquid crystal panel according to still another embodiment of the present invention.
【図8】本発明の一実施態様にかかるコンピュータの概
略斜視図である。FIG. 8 is a schematic perspective view of a computer according to an embodiment of the present invention.
1 光透過性基板 2 ブラックマトリックス 3 インク受容層 4 インクジェット記録ヘッド 6 保護層 9 カラーフィルタ 11 着色画素 21 CPU 22 ヘッド駆動回路 23 プログラムメモリ 24 インク 41 フォトマスク 42 インク吸収性の低い部分 43 開口部 51、52、53 インク 54 インク受容層の着色部 55 光透過部 61 対向基板 62 液晶組成物 63 画素電極 64 共通電極 65、66 配向膜 67 偏光板 68 バックライトの光 91 コンピュータ 92 画像表示部 REFERENCE SIGNS LIST 1 light-transmitting substrate 2 black matrix 3 ink receiving layer 4 ink jet recording head 6 protective layer 9 color filter 11 colored pixel 21 CPU 22 head drive circuit 23 program memory 24 ink 41 photomask 42 low ink absorption portion 43 opening 51 , 52, 53 Ink 54 Colored portion of ink receiving layer 55 Light transmitting portion 61 Counter substrate 62 Liquid crystal composition 63 Pixel electrode 64 Common electrode 65, 66 Alignment film 67 Polarizing plate 68 Backlight 91 Computer 92 Image display
───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 2C056 FB01 2H048 BA57 BA64 BB02 BB44 2H086 BA53 BA56 2H091 FA02Y FB02 FB12 FD24 LA15 4J039 AD09 AE03 AE05 BC07 BC08 BC09 BC10 BC13 BC16 BC31 BC33 BC36 BC50 BC51 BC54 BC60 BC68 BC79 BE02 BE12 EA03 EA05 EA16 EA21 FA04 GA24 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 2C056 FB01 2H048 BA57 BA64 BB02 BB44 2H086 BA53 BA56 2H091 FA02Y FB02 FB12 FD24 LA15 4J039 AD09 AE03 AE05 BC07 BC08 BC09 BC10 BC13 BC16 BC31 BC33 BC36 BC12 BC68 EA05 EA16 EA21 FA04 GA24
Claims (25)
れるバイオレット染料を含むことを特徴とするインク: 【外1】 〔上記式(I)中、R1、R1’、R2及びR2’は、各々
独立に、水素原子、炭素数1〜5の直鎖状もしくは分岐
鎖状のアルキル基、または置換もしくは未置換のアリー
ル基を表し、R3は置換フェニル基を表わす〕。1. An ink comprising a cyan dye and a violet dye represented by the following general formula (I): [In the above formula (I), R 1 , R 1 ′, R 2 and R 2 ′ are each independently a hydrogen atom, a linear or branched alkyl group having 1 to 5 carbon atoms, Represents an unsubstituted aryl group, and R 3 represents a substituted phenyl group].
20:1〜2:1の割合で含む請求項1記載のインク。2. The ink according to claim 1, comprising the cyan dye and the violet dye in a ratio of 20: 1 to 2: 1.
0.1〜20重量%である請求項1記載のインク。3. The ink according to claim 1, wherein the dye concentration is 0.1 to 20% by weight based on the total weight of the ink.
重量%含む請求項1記載のインク。4. A solvent having a boiling point of 150 to 250 ° C.
2. The ink according to claim 1, wherein the ink comprises about 10% by weight.
ンク。5. The ink according to claim 1, further comprising a curable resin.
方の印加によって硬化する樹脂である請求項5記載のイ
ンク。6. The ink according to claim 5, wherein said curable resin is a resin which is cured by application of at least one of light and heat.
ある請求項1〜6のいずれかに記載のインク。7. The ink according to claim 1, wherein the cyan dye is a phthalocyanine dye.
に用いられるインクである請求項1〜4のいずれかに記
載のインク。8. The ink according to claim 1, wherein the ink is used for discharging by an ink-jet method.
に用いられるものである請求項5または6に記載のイン
ク。9. The ink according to claim 5, wherein the ink is used for discharging by an inkjet method.
位置に青の着色画素を備えているカラーフィルタにおい
て、該着色画素が、シアン染料と下記式(I)で示され
るバイオレット染料とを含むことを特徴とするカラーフ
ィルタ: 【外2】 (上記式(I)において、R1、R1’、R2及びR2’
は、は各々独立に、水素原子、炭素数1〜5の直鎖状も
しくは分岐鎖状のアルキル基、または置換もしくは未置
換のアリール基を表し、R3は置換フェニル基を表わ
す)。10. A light-transmitting substrate, and a color filter having a blue colored pixel at a predetermined position on the substrate, wherein the colored pixel comprises a cyan dye and a violet dye represented by the following formula (I). Color filter characterized by containing: (In the above formula (I), R 1 , R 1 ′, R 2 and R 2 ′
Each independently represents a hydrogen atom, a linear or branched alkyl group having 1 to 5 carbon atoms, or a substituted or unsubstituted aryl group, and R 3 represents a substituted phenyl group).
脂層の一部が該着色画素を構成する請求項10記載のカ
ラーフィルタ。11. The color filter according to claim 10, wherein the substrate has a resin layer on a surface, and a part of the resin layer constitutes the colored pixel.
素は互いに離間しており、且つ各々の着色画素の間に遮
光層を有する請求項10記載のカラーフィルタ。12. The color filter according to claim 10, comprising a plurality of the colored pixels, each of the colored pixels being separated from each other, and having a light shielding layer between each of the colored pixels.
項10記載のカラーフィルタ。13. The color filter according to claim 10, wherein a surface of said light shielding layer is non-colored.
ラーフィルタ及び該カラーフィルタに対向配置されてい
るパネル基板を有し、該カラーフィルタと該パネル基板
との間に液晶化合物が封入されていることを特徴とする
液晶パネル。14. A color filter according to claim 10, further comprising a panel substrate facing the color filter, wherein a liquid crystal compound is sealed between the color filter and the panel substrate. A liquid crystal panel characterized by the following.
電極を、該カラーフィルタの光透過性基板の、該着色画
素を有する側とは反対側の面に有する請求項14記載の
液晶パネル。15. The liquid crystal panel according to claim 14, wherein an electrode for controlling the alignment of the liquid crystal compound is provided on a surface of the light transmitting substrate of the color filter opposite to a side having the colored pixels.
ルを画像表示部として備えていることを特徴とするコン
ピュータ。16. A computer comprising the liquid crystal panel according to claim 13 as an image display unit.
基板表面の所定の位置にインクジェット法で付着させて
着色画素を形成する工程を有することを特徴とするカラ
ーフィルタの製造方法。17. A method for manufacturing a color filter, comprising the step of forming a colored pixel by applying the ink droplet according to claim 8 to a predetermined position on the surface of a light transmitting substrate by an ink-jet method.
いる請求項17記載のカラーフィルタの製造方法。18. The method according to claim 17, wherein the light transmitting substrate has a resin layer on the surface.
水溶性アクリルモノマー単位を含むポリマーである請求
項17記載のカラーフィルタの製造方法。19. The method according to claim 17, wherein the material forming the resin layer is a polymer containing at least a water-soluble acrylic monomer unit.
セルロース系水溶性ポリマーを含む請求項18または1
9に記載のカラーフィルタの製造方法。20. The material according to claim 18, wherein the material forming the resin layer contains at least a cellulose-based water-soluble polymer.
10. The method for producing a color filter according to item 9.
基板表面の所定の位置にインクジェット法で付着させる
工程、及び該光透過基板上の該インク滴中の硬化性樹脂
を硬化せしめて着色画素を形成する工程、を有すること
を特徴とするカラーフィルタの製造方法。21. A step of attaching the ink droplet according to claim 9 to a predetermined position on the surface of the light transmitting substrate by an ink-jet method, and curing the curable resin in the ink droplet on the light transmitting substrate. Forming a colored pixel.
る複数の画素を互いに隔てる遮光層を有する基板を用い
る請求項21記載のカラーフィルタの製造方法。22. The method for manufacturing a color filter according to claim 21, wherein a substrate having a light-shielding layer that separates a plurality of pixels formed on the surface from each other is used as the light transmitting substrate.
脂層を形成し、該硬化性樹脂層を硬化せしめる工程を更
に有する請求項22記載のカラーフィルタの製造方法。23. The method for manufacturing a color filter according to claim 22, further comprising a step of forming a curable resin layer so as to cover the colored pixels, and curing the curable resin layer.
エネルギーの少なくとも一方のエネルギーの印加によっ
て硬化するものである請求項23記載のカラーフィルタ
の製造方法。24. The method according to claim 23, wherein the curable resin layer is cured by application of at least one of light energy and heat energy.
載のカラーフィルタを備えていることを特徴とする画像
表示デバイス。25. An image display device comprising the color filter according to claim 10. Description: