JP2002180073A - Fuel composition - Google Patents
Fuel compositionInfo
- Publication number
- JP2002180073A JP2002180073A JP2000379287A JP2000379287A JP2002180073A JP 2002180073 A JP2002180073 A JP 2002180073A JP 2000379287 A JP2000379287 A JP 2000379287A JP 2000379287 A JP2000379287 A JP 2000379287A JP 2002180073 A JP2002180073 A JP 2002180073A
- Authority
- JP
- Japan
- Prior art keywords
- frp
- cement
- fuel composition
- fuel
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、繊維強化プラスチ
ック（以下、ＦＲＰともいう。）破砕物をセメント製造
等の燃料として用いるための新規な燃料組成物に関す
る。詳しくは、ＦＲＰ破砕物をセメント製造設備や高炉
等の燃焼設備に供給する際、取扱い時の粉塵の発生が抑
えられ、良好なハンドリング性を有し、更に、安定した
燃焼性を示す燃料組成物である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a novel fuel composition for using a crushed fiber reinforced plastic (hereinafter, also referred to as FRP) as a fuel for producing cement or the like. More specifically, when supplying crushed FRP to a combustion facility such as a cement manufacturing facility or a blast furnace, the generation of dust during handling is suppressed, the fuel composition has good handling properties, and furthermore, shows stable combustion properties. It is.
【０００２】[0002]
【従来の技術】廃ＦＲＰは、樹脂成形品の原料として再
利用したとき、多量に含有される繊維が成形品の外観を
悪化させて商品価値を低下させること、また、ＦＲＰに
使用されている樹脂が熱硬化性樹脂である場合には熱成
形ができず、他の製品に成形加工して再利用することが
極めて困難であること、などの理由から、主として、埋
立により最終処分されている。2. Description of the Related Art When waste FRP is reused as a raw material for a resin molded product, a large amount of fibers deteriorates the appearance of the molded product, lowering the commercial value, and is used for FRP. If the resin is a thermosetting resin, thermoforming is not possible, and it is extremely difficult to mold and recycle it into other products, mainly because it is finally disposed of by landfill. .
【０００３】しかし、埋立処分場の埋立可能量は年々減
少し、また、新たな埋立処分場の確保は今後更に困難に
なっていくため、ＦＲＰの埋立処理を半永久的に継続す
ることはできない。However, the amount of landfills that can be landfilled at landfills decreases year by year, and it becomes more difficult to secure new landfills in the future. Therefore, landfilling of FRP cannot be continued semipermanently.
【０００４】その一方では、各種耐久性用品はその高強
度化、高耐久性、軽量化を追求し、ＦＲＰの使用量が増
加する傾向にあり、その結果、廃ＦＲＰの処理量も今後
増加すると予想される。On the other hand, in the case of various durable products, the use of FRP tends to increase in pursuit of higher strength, higher durability, and lighter weight. As a result, the amount of waste FRP to be processed will increase in the future. is expected.
【０００５】そこで、ＦＲＰを燃料として使用して処理
する方法が、今後期待される再利用方法として検討され
始めている。Therefore, a method of processing using FRP as a fuel has begun to be studied as a recycling method expected in the future.
【０００６】ところが、ＦＲＰを燃料として使用する場
合、破砕後の取り扱い時の粉塵の発生が問題となる。即
ち、ＦＲＰの破砕物の移送時、燃料としての供給時に破
砕によって分離した微細な繊維が飛散し、作業環境、周
辺の環境を悪化させるという問題が生じる。However, when FRP is used as a fuel, the generation of dust during handling after crushing becomes a problem. That is, when transferring the crushed material of the FRP, the fine fibers separated by the crushing during the supply as the fuel are scattered, which causes a problem that the working environment and the surrounding environment are deteriorated.
【０００７】上記問題は、燃料として使用できる程度ま
で破砕処理されたＦＲＰ破砕物においては避けられない
問題であり、早急な解決が望まれるところである。[0007] The above problem is an unavoidable problem in the case of FRP crushed material that has been crushed to such an extent that it can be used as fuel, and an immediate solution is desired.
【０００８】上記問題を解決するために、破砕時に散水
し、前記した微細な繊維の飛散を防止する事も考えられ
るが、散水された水は、比較的短時間のうちに乾燥し、
長期の飛散防止効果が望めない。また、ＦＲＰ破砕物に
対して水は親和性が悪いため、水と均一に混合し難く、
ハンドリング性が悪いばかりでなく、燃焼において水の
付着量に差が生じ、安定した燃焼を行うことができない
という問題もある。To solve the above problem, it is conceivable to sprinkle water at the time of crushing to prevent the fine fibers from scattering, but the sprinkled water dries in a relatively short time,
Long-term scattering prevention effect cannot be expected. In addition, since water has poor affinity for the FRP crushed material, it is difficult to uniformly mix with water,
Not only is the handling property poor, but there is also a problem that a difference occurs in the amount of water adhered in combustion, and stable combustion cannot be performed.
【０００９】[0009]
【発明が解決しようとする課題】従って、本発明の目的
は、ＦＲＰの破砕物を燃料として使用する際、取扱い時
の粉塵の発生問題を解決し、良好なハンドリングで燃焼
設備に供給可能で、且つ安定した燃焼性を有する燃料組
成物を提供することにある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to solve the problem of dust generation during handling when using a crushed FRP as fuel, and to supply it to combustion equipment with good handling. Another object of the present invention is to provide a fuel composition having stable combustibility.
【００１０】[0010]
【課題を解決するための手段】本発明者らは、上記目的
を達成すべく鋭意研究を重ねた。その結果、ＦＲＰ破砕
物を特定の可燃性液体と混合することにより、上記課題
を解決し得ることを見い出し、本発明を完成するに至っ
た。Means for Solving the Problems The present inventors have intensively studied to achieve the above object. As a result, it has been found that the above problem can be solved by mixing the crushed FRP with a specific flammable liquid, and the present invention has been completed.
【００１１】即ち、本発明は、繊維強化プラスチック破
砕物及び２０℃における蒸気圧が２．３ｋPa以下で粘度
５０００ｍPa・ｓ以下である可燃性液体によりなること
を特徴とする燃料組成物である。That is, the present invention is a fuel composition comprising a crushed fiber-reinforced plastic and a combustible liquid having a vapor pressure at 20 ° C. of 2.3 kPa or less and a viscosity of 5000 mPa · s or less.
【００１２】[0012]
【発明の実施の形態】本発明において、ＦＲＰは公知の
ものが特に制限なく使用される。即ち、ＦＲＰは、ガラ
ス繊維、炭素繊維等の繊維状充填材と熱硬化性樹脂や熱
可塑性樹脂の樹脂とより基本的に構成される複合体であ
り、本発明ではこれらのＦＲＰが好適に使用される。DETAILED DESCRIPTION OF THE INVENTION In the present invention, known FRPs are used without any particular limitation. That is, FRP is a composite basically composed of a fibrous filler such as glass fiber or carbon fiber and a resin of a thermosetting resin or a thermoplastic resin, and these FRPs are preferably used in the present invention. Is done.
【００１３】具体的には、上記熱硬化性樹脂として、不
飽和ポリエステル樹脂、エポキシ樹脂、フェノール樹脂
等が例示される。また、熱可塑性樹脂として、ポリプロ
ピレン、飽和ポリエステル樹脂、ポリアミド樹脂等が例
示される。Specifically, examples of the thermosetting resin include an unsaturated polyester resin, an epoxy resin, and a phenol resin. Examples of the thermoplastic resin include polypropylene, saturated polyester resin, and polyamide resin.
【００１４】また、上記組成には、必要に応じて、炭酸
カルシウム、タルク、水酸化アルミニウム等の無機充填
材やその他、酸化防止剤、紫外線吸収剤等の安定剤、チ
タン系、鉄系等の無機顔料や溶性宇アゾ系、不溶性アゾ
系、フタロシアン系等の有機顔料の着色剤などの添加剤
が含有される場合もある。The above composition may contain, if necessary, an inorganic filler such as calcium carbonate, talc or aluminum hydroxide, or a stabilizer such as an antioxidant or an ultraviolet absorber, or a titanium or iron based material. In some cases, additives such as coloring agents for inorganic pigments and organic pigments such as soluble azo-based, insoluble azo-based, and phthalocyanine-based pigments are contained.
【００１５】上記含有される繊維状充填材の含有量は、
一般に、樹脂１００重量部に対して繊維は１０〜１００
重量部であり、また、無機充填材は樹脂１００重量部に
対して２００重量部以下である。The content of the above-mentioned fibrous filler is as follows:
Generally, the fiber is 10 to 100 per 100 parts by weight of the resin.
Parts by weight, and the inorganic filler is 200 parts by weight or less based on 100 parts by weight of the resin.
【００１６】これらＦＲＰを使用した成形体は、一般
に、家庭用品、浴槽、自動車部品、船舶用部品等の用途
に使用される場合が多い。In general, molded articles using these FRPs are often used for applications such as household articles, bathtubs, automobile parts, and marine parts.
【００１７】本発明において、ＦＲＰ破砕物は、上記用
途に代表されるＦＲＰ成形体の廃棄物より、必要に応じ
て、ＦＲＰを分別し、これを破砕したものが好適に使用
される。In the present invention, as the FRP crushed product, a product obtained by separating and crushing FRP, if necessary, from waste of an FRP molded product represented by the above-mentioned application is suitably used.
【００１８】本発明において、ＦＲＰ破砕物は、燃料と
しての燃焼性、供給の容易性などを考慮すれば、平均長
径２００ｍｍ以下が適当であり、後記可燃性液体との混
合、輸送時の作業性を考慮すれば、１００ｍｍ以下、特
に、３〜５０ｍｍの大きさに破砕されたものが好まし
い。In the present invention, the average length of the FRP crushed material is preferably 200 mm or less in consideration of the flammability as a fuel, the ease of supply, and the like. In consideration of the above, those crushed to a size of 100 mm or less, particularly 3 to 50 mm are preferable.
【００１９】本発明の燃料組成物の特徴は、上記ＦＲＰ
破砕物と２０℃における蒸気圧が、２．３ｋPa、好まし
くは、２．３ｋPa以下、更に好ましくは、１．３ｋＰa
以下で、粘度５０００ｍＰa・ｓ以下、好ましくは、１
００ｍＰa・ｓ以下、さらに好ましくは、５０ｍPa・ｓ
以下である可燃性液体を混合して成ることにある。The fuel composition of the present invention is characterized by the above-mentioned FRP.
The crushed material and the vapor pressure at 20 ° C. are 2.3 kPa, preferably 2.3 kPa or less, more preferably 1.3 kPa.
Or less, and a viscosity of 5000 mPa · s or less, preferably 1
00 mPa · s or less, more preferably 50 mPa · s
The following flammable liquids are mixed.
【００２０】前述したように、通常、粉塵が起こり易い
物質を貯蔵する場合に散水することは行われているが、
これをＦＲＰ破砕物よりなる燃料に適用した場合、繊
維、樹脂との親和性の低さにより、水の付着量が少な
く、しかも、水の蒸発のし易さが伴い、長期間にわたる
粉塵発生の防止効果は殆どない。そのため、貯蔵時に限
らず、取扱中における水の乾燥も早く、燃料として燃焼
設備に供給する際には多量の粉塵が発生するようにな
る。As described above, watering is usually performed when storing a substance that easily generates dust.
When this is applied to a fuel made of FRP crushed material, the amount of water attached is small due to the low affinity for fibers and resin, and the water is easily evaporated, so that dust generation over a long period of time is prevented. There is almost no prevention effect. Therefore, not only during storage, but also during the handling, water dries quickly, and a large amount of dust is generated when the fuel is supplied to the combustion equipment.
【００２１】また、上記ＦＲＰ破砕物と水との親和性の
悪さから均一な混合が困難であり、仮に均一に混合した
場合でも、均一性を持続できず、貯蔵されたＦＲＰ破砕
物の取出位置により含水率が異なり、燃料として使用し
た場合の燃焼性が不安定となる。In addition, uniform mixing is difficult due to poor affinity between the above-mentioned FRP crushed product and water, and even if mixed uniformly, uniformity cannot be maintained, and the stored FRP crushed product removal position Therefore, the moisture content differs, and the flammability when used as a fuel becomes unstable.
【００２２】これに対して、本発明の組成物において
は、前記特定の粘度に調整された可燃性液体が親和性良
くＦＲＰ破砕物表面に付着した均一な組成物として得ら
れ、燃料として使用する際、安定した燃焼を行うことが
できる。また、特定の粘度の可燃性液体を使用すること
により、ＦＲＰ破砕物の部分的な凝集の問題もなく、極
めてハンドリング性が良好な組成物となる。更に、可燃
性液体の低い蒸気圧により、ＦＲＰ破砕物表面に均一に
付着した可燃性燃料の蒸発を抑え、長期間にわたって安
定した粉塵防止性を発揮することができる。On the other hand, in the composition of the present invention, the flammable liquid adjusted to the above specific viscosity is obtained as a uniform composition adhered to the surface of the FRP crushed material with good affinity and used as fuel. In this case, stable combustion can be performed. In addition, by using a flammable liquid having a specific viscosity, a composition having extremely good handling properties can be obtained without the problem of partial aggregation of the FRP crushed product. Further, due to the low vapor pressure of the flammable liquid, evaporation of the flammable fuel uniformly adhered to the surface of the crushed FRP can be suppressed, and stable dust prevention can be exhibited over a long period of time.
【００２３】更にまた、多く含まれる繊維により低下し
た発熱量が回復され、後述するセメント製造のための燃
料として使用する場合、燃料代替率を高く設定すること
も可能である。Furthermore, the reduced calorific value is recovered by the fibers contained in a large amount, and when used as a fuel for cement production described later, it is possible to set a high fuel substitution rate.
【００２４】従って、本発明において、上記可燃性液体
の２０℃における蒸気圧が２．３ｋPaを超えた場合、或
いは可燃性液体の２０℃における粘度が５０００ｍＰa
・ｓを超えた場合は、上述した効果を発揮することが困
難となる。Accordingly, in the present invention, when the vapor pressure of the flammable liquid at 20 ° C. exceeds 2.3 kPa, or when the viscosity of the flammable liquid at 20 ° C. is 5000 mPa
-If it exceeds s, it will be difficult to exhibit the above-described effects.
【００２５】本発明において、可燃性液体は上記特性を
満足するものであれば特に制限されず、公知の可燃性液
体としては、、粘度５０００ｍＰa・ｓ以下、常温で液
体である性質を持つものであれば公知のものが特に制限
無く使用される。上記可燃性液体は、本発明においては
ＦＲＰが燃料として使用できれば良く、爆発性が低いも
のであれば、使用することができる。例えば、２０℃に
おける蒸気圧が１．３３ｋＰa、粘度０．８３ｍＰa・ｓ
（２０℃）のＯ−キシレン等が好ましい。しかし、ＦＲ
Ｐ破砕物は廃棄物であり、その処理における経済性を考
慮した場合、かかる可燃性液体も廃棄物を利用すること
が好ましい。In the present invention, the flammable liquid is not particularly limited as long as it satisfies the above characteristics. Known flammable liquids have a viscosity of 5,000 mPa · s or less and are liquid at room temperature. If so, known ones are used without any particular limitation. In the present invention, the above flammable liquid may be used as long as FRP can be used as fuel, and as long as it has low explosiveness. For example, the vapor pressure at 20 ° C. is 1.33 kPa and the viscosity is 0.83 mPa · s.
(20 ° C.) O-xylene and the like are preferred. But FR
P crushed material is waste, and it is preferable to use waste as the flammable liquid in consideration of economical efficiency in the treatment.
【００２６】例えば、本発明に好適に用いられる可燃性
液体としては、各種工場等より廃棄される油類が好適に
使用される。より具体的には、食品製造工場、その他の
化学工場等から発生する油類や有機化合物等が例示され
る。For example, as the flammable liquid suitably used in the present invention, oils discarded from various factories and the like are preferably used. More specifically, oils and organic compounds generated from food manufacturing factories and other chemical factories are exemplified.
【００２７】また、上記可燃性液体は、ＦＲＰ破砕物の
繊維状充填材による発熱量の低下を補い、燃料の代替率
を向上するため、発熱量が４０００Ｋcal／ｋｇ以上の
ものを選択することが好ましい。The flammable liquid may be selected to have a calorific value of 4000 Kcal / kg or more in order to compensate for the decrease in calorific value due to the fibrous filler of the crushed FRP and to improve the fuel substitution rate. preferable.
【００２８】また、本発明の燃料組成物において、可燃
性液体の割合は特に制限されないが、繊維強化プラスチ
ック破砕物１００重量部に対して１〜２００重量部、好
ましくは、４０〜１９０重量部が適当である。即ち、上
記可燃性液体の割合が１重量部未満の場合、ＦＲＰ破砕
物の粉塵防止効果に乏しく、一方、該可燃性液体の占め
る割合が２００重量部を超える場合、燃料組成物として
のＦＲＰの使用量が激減したり、多量の可燃性液体を必
要とするため、省エネルギーの面からも好ましくない。
また、燃焼した可燃性液体により排出ガス量が増加し、
例えば、セメント製造の燃料として供給した場合には、
運転状態を変化させるため好ましくない。In the fuel composition of the present invention, the proportion of the flammable liquid is not particularly limited, but is preferably 1 to 200 parts by weight, more preferably 40 to 190 parts by weight, per 100 parts by weight of the crushed fiber reinforced plastic. Appropriate. That is, when the proportion of the flammable liquid is less than 1 part by weight, the dust prevention effect of the crushed FRP is poor. On the other hand, when the proportion of the flammable liquid exceeds 200 parts by weight, Since the amount of use is drastically reduced or a large amount of flammable liquid is required, it is not preferable from the viewpoint of energy saving.
In addition, the amount of exhaust gas increases due to the combustible liquid burned,
For example, when supplied as fuel for cement production,
It is not preferable because it changes the operating state.
【００２９】本発明の燃料組成物の製造方法は特に制限
されないが、好適な方法を例示すれば、前記特定の可燃
性液体の存在下に、ＦＲＰ成形体を破砕する方法であ
る。即ち、上記のように、破砕時に該可燃性液体を存在
させることにより、ＦＲＰ成形体の破砕時に発生する繊
維状充填材、樹脂等の粉塵の飛散を防止することがで
き、極めて好都合である。The method for producing the fuel composition of the present invention is not particularly limited, but a preferred method is, for example, a method of crushing an FRP molded article in the presence of the above-mentioned specific flammable liquid. That is, as described above, the presence of the flammable liquid at the time of crushing can prevent scattering of dust such as fibrous filler and resin generated at the time of crushing of the FRP molded article, which is extremely advantageous.
【００３０】上記破砕において使用する破砕機として
は、特に制限されないが、一軸方式の破砕機、二軸方式
の破砕機、ハンマークラッシャーなどの破砕機、破砕機
等の公知のものが使用可能である。The crusher used in the crushing is not particularly limited, but known crushers such as a single-shaft crusher, a twin-shaft crusher, a crusher such as a hammer crusher, and a crusher can be used. .
【００３１】上記破砕時において、可燃性液体の蒸気に
よる爆発を防止するため、破砕機の空間部を、例えば窒
素等の不活性ガス雰囲気に保つことが好ましい。At the time of the crushing, in order to prevent explosion due to the vapor of the flammable liquid, the space of the crusher is preferably kept in an inert gas atmosphere such as nitrogen.
【００３２】また、上記破砕において、ＦＲＰ成形体と
共に存在させる可燃性液体の量は、最終組成に相当する
量であっても良いし、その一部であっても良い。In the above-mentioned crushing, the amount of the flammable liquid to be present together with the FRP molded body may be an amount corresponding to the final composition or a part thereof.
【００３３】本発明の燃料組成物を得る方法は、ＦＲＰ
破砕物を得た後、必要に応じて、可燃性液体を添加する
ことができる。この場合の混合機は、スクリュー式の混
合機、攪拌式の混合機等がしよう可能であり、そのうち
輸送と同時に液体燃流を添加混合可能なクリューコンベ
ア等が好適に使用される。The method for obtaining the fuel composition of the present invention comprises the steps of:
After obtaining the crushed material, a flammable liquid can be added if necessary. In this case, the mixer may be a screw-type mixer, a stirring-type mixer, or the like. Among them, a screw conveyor or the like capable of adding and mixing a liquid fuel stream at the same time as transportation is suitably used.
【００３４】本発明の燃料組成物は、種々の燃焼設備、
例えば、セメントの製造設備、高炉等の燃焼設備におい
て、燃料として使用される。特に、ＦＲＰに含まれる繊
維状充填材が無機充填材の場合は、燃焼後に発生する残
渣を有効に処理するためには、セメント製造設備に使用
する燃料としての用途が最も適している。The fuel composition of the present invention can be used in various combustion facilities,
For example, it is used as fuel in a cement production facility, a combustion facility such as a blast furnace, or the like. In particular, when the fibrous filler contained in the FRP is an inorganic filler, in order to effectively treat the residue generated after combustion, the use as a fuel used in cement manufacturing equipment is most suitable.
【００３５】即ち、セメント製造設備においては、燃料
組成物を燃焼することによって生成する残渣は、製造さ
れるセメントの成分として有効に活用することができ、
廃棄すべき固形分を殆ど無くすることが可能である。That is, in the cement production facility, the residue generated by burning the fuel composition can be effectively used as a component of the produced cement,
It is possible to almost eliminate the solid matter to be discarded.
【００３６】本発明の燃料組成物の貯蔵方法は、特に制
限されないが、密閉型サイロ等による貯蔵方法が好まし
い。The method for storing the fuel composition of the present invention is not particularly limited, but a storage method using a closed silo or the like is preferable.
【００３７】上記セメント製造設備は、図１に示すよう
に、セメント原料を予熱、更には仮焼するためのセメン
ト原料予熱装置２と、かかる予熱されたセメント原料を
焼成を行うためのセメント原料焼成用キルン３とよりな
る。As shown in FIG. 1, the cement manufacturing equipment includes a cement raw material preheating apparatus 2 for preheating and further calcining a cement raw material, and a cement raw material firing for firing the preheated cement raw material. It consists of a kiln 3.
【００３８】上記セメント原料予熱装置２は、複数のサ
イクロン４をダクト５により連接し、その上部より供給
されたセメント原料１が、順次予熱されながら、下方に
移動し、最下段サイクロンの原料シュート９より焼成用
キルン３に供給されるように構成される。また、セメン
ト原料予熱装置の下部には仮焼室６が設けられ、キルン
排ガスの熱と共に、予熱或いは仮焼に必要な熱をバーナ
ーによって補充して該予熱装置に供給するよう構成され
る。In the cement raw material preheating apparatus 2, a plurality of cyclones 4 are connected by a duct 5, and the cement raw material 1 supplied from above moves downward while being preheated sequentially, and the raw material chute 9 of the lowermost cyclone is moved. It is configured to be supplied to the kiln 3 for firing. In addition, a calcining chamber 6 is provided below the cement raw material preheating device, and is configured so that heat necessary for preheating or calcining is replenished by a burner together with heat of the kiln exhaust gas and supplied to the preheating device.
【００３９】一方、セメント原料焼成用キルン３には主
バーナー７が取り付けられており、セメント原料は、そ
の発生熱により焼成されてクリンカーとしてグレートク
ーラー８に取り出され、冷却された後、石膏等の添加成
分の配合、破砕処理等を経てセメントとなる。On the other hand, a main burner 7 is attached to the cement raw material firing kiln 3. The cement raw material is fired by the generated heat, taken out as a clinker to a great cooler 8, cooled, and then cooled with gypsum or the like. Cement is obtained through mixing of additional components, crushing treatment, and the like.
【００４０】本発明の燃料組成物を上記セメントの製造
設備に投入する場所は特に制限ないが、ＦＲＰ破砕物１
００重量部に対する可燃性液体の割合が６０重量部以
上、特に、１５０重量部以上の場合、燃焼熱を有効に利
用するため、図中Ａで示すように、セメント原料予熱装
置の最下段サイクロンから焼成用キルンの窯尻に原料を
投入する原料シュート９における位置が最適である。The place where the fuel composition of the present invention is introduced into the cement production facility is not particularly limited.
In the case where the ratio of the flammable liquid to 00 parts by weight is 60 parts by weight or more, particularly 150 parts by weight or more, as shown in A in the figure, from the lowest cyclone of the cement raw material preheating apparatus, in order to effectively use the combustion heat. The position of the raw material chute 9 for charging the raw material to the kiln bottom of the firing kiln is optimal.
【００４１】また、ＦＲＰ破砕物１００重量部に対する
可燃性液体の割合が１５０重量部未満、特に、６０重量
部未満の場合、その発熱量が少ないため、燃料としての
用途と共にセメント原料としての機能をも有するため、
セメント原料予熱装置の上部、即ち、図中Ｂで示すよう
に、原料１と共にセメント原料予熱装置に供給すること
が好ましい。上記燃料組成物を原料と共にセメント原料
予熱装置に供給する場合、ＦＲＰの平均長径は１０ｍｍ
以下であることが好ましい。即ち、平均長径が１０ｍｍ
を超えるＦＲＰ破砕物を使用した場合、予熱装置でのセ
メント原料の流れを阻害するおそれがあり、好ましくな
い。Further, when the proportion of the flammable liquid is less than 150 parts by weight, especially less than 60 parts by weight, based on 100 parts by weight of the FRP crushed material, the calorific value is small, so that the function as a cement raw material can be obtained as well as the use as a fuel. Also have
It is preferable to supply the raw material 1 together with the raw material 1 to the cement raw material preheating apparatus as shown in the upper part of the cement raw material preheating apparatus. When the fuel composition is supplied to a cement raw material preheating apparatus together with a raw material, the average major axis of FRP is 10 mm.
The following is preferred. That is, the average major axis is 10 mm
When the FRP crushed material exceeding the above is used, the flow of the cement raw material in the preheating device may be obstructed, which is not preferable.
【００４２】セメントの製造において、燃料組成物の供
給量は、予熱装置、焼成用キルンの運転状況に影響を及
ぼさない範囲で供給することが好ましい。その上限は、
ＦＲＰ破砕物湖の組成や可燃性液体の発熱量等によって
左右され、一概に限定することはできないが、例えば、
セメントの中間製品であるクリンカー１ｔの製造に対し
て、燃料組成物が４０ｋｇ以下の割合となるように供給
することが好ましい。In the production of cement, it is preferable to supply the fuel composition within a range that does not affect the operating conditions of the preheating device and the kiln for firing. The upper limit is
It depends on the composition of the FRP crushed material lake, the calorific value of the flammable liquid, etc., and cannot be limited unconditionally.
It is preferable to supply the fuel composition so as to have a ratio of 40 kg or less for the production of clinker 1t which is an intermediate product of cement.
【００４３】尚、ＦＲＰ破砕物をセメント原料予熱装置
のまで燃料組成物を運搬する方法は特に制限されない
が、ベルトコンベアー、スクリューコンベアー、空気輸
送が好ましく用いられる。The method for transporting the fuel composition from the FRP crushed product to the cement raw material preheating apparatus is not particularly limited, but a belt conveyor, a screw conveyor, and pneumatic transportation are preferably used.
【００４４】[0044]
【発明の効果】以上の説明より理解されるように、本発
明の燃料組成物は、ＦＲＰ破砕物中の粉塵の発生を極め
て効果的に防止することができ、また、良好なハンドリ
ング性を有すると共に、安定した燃焼性を発揮するとい
う、優れた特性を有する。As will be understood from the above description, the fuel composition of the present invention can very effectively prevent the generation of dust in the FRP crushed material and has good handling properties. In addition, it has excellent characteristics of exhibiting stable flammability.
【００４５】そして、本発明の可燃性液体は、各種燃焼
設備の燃料として、工業的に極めて有効に使用すること
ができる。The flammable liquid of the present invention can be industrially used very effectively as a fuel for various combustion facilities.
【００４６】特に、セメントの製造設備に燃料として使
用し、セメントを製造する場合には、埋立場の問題、焼
却に伴う排ガスの問題など環境への負荷を少なくし、焼
却時の熱をセメント製造用のエネルギーとして有効に利
用できる一方、焼却残渣はセメントの原料として使用す
ることができ、よって、資源の有効利用を図ることがで
きる。In particular, when cement is used as a fuel in a cement manufacturing facility, the burden on the environment such as the problem of landfills and the problem of exhaust gas from incineration is reduced, and the heat generated during incineration is reduced. While the incineration residue can be used effectively as a cement raw material, the resources can be effectively used.
【００４７】[0047]
【実施例】以下実施例を挙げて本発明を詳細に説明す
る。The present invention will be described in detail with reference to examples.
【００４８】尚、実施例及び比較例において、燃料組成
物の各種試験は下記の方法により行った。In the examples and comparative examples, various tests of the fuel composition were performed by the following methods.
【００４９】１．ハンドリング性 上記供給時における燃料組成物の輸送機、供給設備での
運搬時のハンドリング性を下記の基準によって評価し
た。1. Handling Property The handling property of the fuel composition at the time of the supply at the time of transportation by the transport machine and the supply equipment was evaluated according to the following criteria.
【００５０】○ ：装置壁面への付着も無く、何ら問題
なく運搬できた。：: There was no adhesion to the wall of the device, and the device could be transported without any problem.
【００５１】△ ：壁面への付着で運搬、供給に多少の
支障が生じた。△: Some trouble occurred in transportation and supply due to adhesion to the wall surface.
【００５２】× ：壁面に著しく付着し、運搬、供給が
不可能となった。X: markedly adhered to the wall surface, making transport and supply impossible.
【００５３】２．粉塵の発生度合い燃料組成物を密閉型
サイロに１ヶ月貯蔵後、受入ホッパー投入作業時におけ
る繊維等の粉塵の再飛散程度を下記の基準によって評価
した。2. Dust Generation Degree After the fuel composition was stored in a closed silo for one month, the degree of re-dispersion of dust such as fibers during the loading operation of the receiving hopper was evaluated according to the following criteria.
【００５４】○ ：繊維の再飛散は全く発生しなかっ
た。○: No re-scattering of fibers occurred.
【００５５】△ ：繊維の再飛散が若干発生した。△: Some re-scattering of the fiber occurred.
【００５６】× ：多量の繊維が再飛散して作業環境が
著しく悪化し、実施が困難であった。X: A large amount of fibers were re-scattered and the working environment was remarkably deteriorated, making it difficult to carry out.
【００５７】３．燃焼安定性 燃料組成物を投入後のセメント原料焼成用キルンの入口
温度（図のＡよりキルン側）を測定し、その変化の度合
いを下記の基準により評価した。3. Combustion stability The inlet temperature of the kiln for sintering cement raw material after charging the fuel composition (on the kiln side from A in the figure) was measured, and the degree of the change was evaluated according to the following criteria.
【００５８】○ ：殆ど変化が無く、極めて安定してセ
メントを製造することができた。○: There was almost no change, and the cement could be produced extremely stably.
【００５９】△ ：キルンの入り口温度に僅かな変動が
あった。Δ: The inlet temperature of the kiln fluctuated slightly.
【００６０】× ：キルンの入り口温度に大きな変動が
生じ、キルンの運転を中止した。X: The kiln operation was stopped due to a large fluctuation in the kiln entrance temperature.
【００６１】実施例１〜６、比較例１〜３ 表１に示すＦＲＰ成形体と表２に示す性状の可燃性液体
とを、表３に示す組成となるように混合した後、ハンマ
ークラッシャーにより破砕し、表３に示す燃料組成物を
それぞれ得た。Examples 1 to 6 and Comparative Examples 1 to 3 After mixing the FRP molded product shown in Table 1 and the flammable liquid having the properties shown in Table 2 so as to have the composition shown in Table 3, the mixture was mixed with a hammer crusher. The mixture was crushed to obtain the fuel compositions shown in Table 3.
【００６２】これらの燃料組成物を、セメント原料予熱
装置の所定の場所に供給してセメントの製造を行った。
セメント原料予熱装置への供給場所は、可燃性液体の少
ない燃料組成物は、セメント原料と共に（Ｂ）、可燃性
液体の多い燃料組成物は原料シュートに（Ａ）供給し
た。These fuel compositions were supplied to a predetermined place of a cement raw material preheating apparatus to produce cement.
The fuel composition containing less flammable liquid was supplied to the cement raw material preheating apparatus together with the cement raw material (B), and the fuel composition containing more flammable liquid was supplied to the raw material chute (A).
【００６３】また、燃料組成物の供給量は、何れもクリ
ンカー１ｔの製造量に対し３０ｋｇの割合となるように
調整した。Further, the supply amount of the fuel composition was adjusted so that the ratio was 30 kg with respect to the production amount of clinker 1t.
【００６４】[0064]
【表１】 [Table 1]
【００６５】[0065]
【表２】 [Table 2]
【００６６】[0066]
【表３】 [Table 3]
【００６７】上記実施例の燃料組成物を使用して得られ
たセメントの品質には特に問題なく、通常のセメントと
同様の特性を有するものが得られた。The quality of the cement obtained using the fuel composition of the above example was not particularly problematic, and a cement having the same properties as ordinary cement was obtained.
【図１】 セメント製造設備の代表的な態様を示す概略
図FIG. 1 is a schematic diagram showing a typical embodiment of a cement production facility.
１ セメント原料 ２ 予熱装置 ３ 焼成用キルン ４ サイクロン ５ ダクト ６ 仮焼室 ７ 主バーナー ８ グレートクーラー ９ 原料シュート DESCRIPTION OF SYMBOLS 1 Cement raw material 2 Preheating device 3 Firing kiln 4 Cyclone 5 Duct 6 Calcination room 7 Main burner 8 Great cooler 9 Raw material chute
Claims (4)
における蒸気圧が２．３ｋPa以下で且つ粘度５０００ｍ
Pa・ｓ以下である可燃性液体よりなることを特徴とする
燃料組成物。1. A crushed fiber reinforced plastic and 20 ° C.
Is less than 2.3kPa and viscosity 5000m
A fuel composition comprising a flammable liquid having a pressure of Pa · s or less.
部に対して可燃性液体１〜２００重量部よりなる請求項
１記載の燃料組成物。2. The fuel composition according to claim 1, comprising 1 to 200 parts by weight of a flammable liquid per 100 parts by weight of the crushed fiber-reinforced plastic.
が１０ｍｍ以下である請求項１又は２記載の燃料組成
物。3. The fuel composition according to claim 1, wherein the average length of the crushed fiber-reinforced plastic is 10 mm or less.
焼成用キルンを備えたセメント製造設備を用いたセメン
トの製造方法において、請求項１〜３のいずれかに記載
の燃料組成物を該予熱装置に供給して該セメント製造設
備内で燃焼させることを特徴とするセメントの製造方
法。4. A method for producing a cement using a cement raw material preheating apparatus and a cement production equipment provided with a cement raw material firing kiln, wherein the fuel composition according to claim 1 is supplied to the preheat apparatus. And burning in said cement production facility.