JP2002103313A - Method for forming concrete segment - Google Patents
Method for forming concrete segmentInfo
- Publication number
- JP2002103313A JP2002103313A JP2000306226A JP2000306226A JP2002103313A JP 2002103313 A JP2002103313 A JP 2002103313A JP 2000306226 A JP2000306226 A JP 2000306226A JP 2000306226 A JP2000306226 A JP 2000306226A JP 2002103313 A JP2002103313 A JP 2002103313A
- Authority
- JP
- Japan
- Prior art keywords
- concrete
- water
- segment
- molded product
- soluble polysaccharide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、外観及び強度の優
れたコンクリートセグメントを製造する成形方法に関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a molding method for producing a concrete segment having excellent appearance and strength.
【０００２】[0002]
【従来の技術】コンクリートセグメントの製造する方法
としては上蓋付きの配筋済みの型枠に硬練りコンクリー
トを詰め、振動締固めで成形した後蒸気養生する方法が
一般的であり、他に上型枠を使用して加圧による締固め
を併用する所謂加圧成形法や高流動コンクリートを使用
して振動締固めを不要とする方法などが知られている。2. Description of the Related Art As a method of manufacturing a concrete segment, there is a general method in which stiff concrete is packed in a form-fitted formwork with an upper lid, compacted by vibration compaction, and then steam-cured. There are known a so-called pressure molding method in which compaction by pressure is used together with a frame, and a method in which vibration compaction is not required by using high-fluid concrete.
【０００３】[0003]
【発明が解決しようとする課題】通常の硬練りコンクリ
ートの振動締固めによる成形法では、コンクリートセグ
メントの外観を良好にするとともに、強度欠陥部のない
製品とするため、振動締固め直後のコンクリートセグメ
ントの上面を荒仕上げし、さらに、コンクリートのブリ
ージングが完了した後、もう一度上面を本仕上げする整
形方法が採用されている。この荒仕上げ、本仕上げは共
に手作業であり、特に本仕上げは長時間を要するので、
この上面の整形作業に多大の労力を要していた。In the molding method of ordinary hardened concrete by vibration compaction, in order to improve the appearance of the concrete segment and to obtain a product having no strength defect, the concrete segment immediately after compaction by vibration is compacted. After finishing the breathing of the concrete, the shaping method of finishing the upper surface once again is adopted. Both the rough finishing and the final finishing are manual work, especially since the final finishing takes a long time,
A great deal of labor was required for shaping the upper surface.
【０００４】さらに、本仕上げを施しても、過度の本仕
上げにより浮き水が発生してレイタンス層を形成する傾
向が大きく、このレイタンス層の形成は製品上面の乾燥
収縮の増大、微細ば収縮クラックの発生に繋がり、製品
上面の外観を損ずるのみでなく、強度欠陥部を生むこと
になる。Further, even if the final finishing is performed, floating water is generated due to excessive final finishing, and the latence layer is more likely to be formed. Not only impairs the appearance of the top surface of the product, but also produces a strength defect.
【０００５】[0005]
【課題を解決するための手段】本発明は、セグメントの
上面の整形作業の中、長時間を要していたブリージング
完了後の整形作業を不要とすることによって、上記のセ
グメント上面の整形の手間を軽減するともに、外観を良
くし強度欠陥部の発生を防止することを目的とする。SUMMARY OF THE INVENTION The present invention eliminates the need for the shaping work after the completion of breathing, which takes a long time during the shaping work for the upper surface of the segment. It is an object of the present invention to improve the appearance and to prevent the occurrence of a strength defect portion while reducing the occurrence of a defect.
【０００６】即ち、本発明は、（Ａ）テーブルバイブレ
ータ上に載置した準備済の型枠の上に、開口部を有する
円弧状に湾曲した打設蓋を載置し、開口部よりスランプ
値３．０cm±１．５cmの硬練りコンクリートを打設しな
がら、テーブルバイブレータを作動して、打設したコン
クリートを締固める工程、（Ｂ）型枠より打設蓋を取り
外し、締固められたコンクリート成形品の上面を整形す
る工程、（Ｃ）整形後のコンクリート成形品の上面に不
織布、織物、円弧状に湾曲した穴開き整形板の順に載置
固定して、コンクリート成形品を蒸気養生する工程、よ
りなるコンクリートセグメントの成形方法、である。That is, according to the present invention, (A) an arc-shaped curved casting lid having an opening is placed on a prepared mold placed on a table vibrator, and a slump value is set from the opening. A step of operating the table vibrator and compacting the poured concrete while placing 3.0 cm ± 1.5 cm of hardened concrete. (B) Removing the casting cover from the formwork and compacting the concrete. A step of shaping the upper surface of the molded article, and (C) a step of placing and fixing a nonwoven fabric, a woven fabric, an arc-shaped curved perforated shaping plate on the upper surface of the shaped concrete article in this order, and steam curing the concrete molded article. And a method for forming a concrete segment.
【０００７】本発明の要点は、荒仕上げ完了後のセグメ
ント上面に不織布、織物、円弧状に湾曲した穴開き整形
板の順に載置固定し、ブリージングや硬化中のセグメン
ト上面のたれや変形を防止しながら、コンクリートの硬
化を完了する点である。The gist of the present invention is to place and fix a nonwoven fabric, a woven fabric, and an arc-shaped curved perforated plate on the upper surface of the segment after the rough finish in order to prevent sagging and deformation of the upper surface of the segment during breathing and curing. The point is to complete the hardening of the concrete.
【０００８】本発明で使用される不織布としては、セ
グメント上面に直接接触してその表面状態がセグメント
上面に転写されること、ブリージング水やコンクリー
ト中の空気を速やかに通過させて型枠外に逃すこと、
コンクリート中の固形分は通過させてはならないこと、
などが性能として要求されるので、比較的小さい径の疎
水性繊維（ポリエステル繊維、ポリエチレン繊維、ポリ
プロピレン繊維など）を使用して比較的密に製造した表
面が平滑なものが使用される。[0008] The nonwoven fabric used in the present invention is such that the surface condition is transferred to the segment upper surface by directly contacting the upper surface of the segment, and that breathing water or air in concrete is quickly passed to escape from the formwork. ,
Solids in concrete must not be allowed to pass,
Since a high performance is required as the performance, a relatively dense surface manufactured using hydrophobic fibers having relatively small diameters (eg, polyester fibers, polyethylene fibers, and polypropylene fibers) is used.
【０００９】本発明で使用される織物は、不織布を通過
したブリージング水やコンクリート中の空気を速やかに
通過させて型枠外に逃すともに、下層の不織布と上層の
穴開き整形板の中間に介在して、両者を均一に密着させ
る機能を有するものであり、疎水性繊維（ガラス繊維、
ポリエステル繊維、ポリエチレン繊維、ポリプロピレン
繊維など）の通常の織物である。この織物層は１枚の織
物であってもよく、織物の厚さ、設置面積などの状況に
よっては２枚以上の織物であってもよい。[0009] The woven fabric used in the present invention allows the breathing water or the air in the concrete that has passed through the nonwoven fabric to quickly pass therethrough and escape from the formwork, and also intervenes between the lower nonwoven fabric and the upper perforated shaping plate. And has a function of uniformly adhering them to each other.
Polyester fiber, polyethylene fiber, polypropylene fiber, etc.). The woven fabric layer may be a single woven fabric, or may be two or more woven fabrics depending on conditions such as the thickness of the woven fabric and the installation area.
【００１０】穴開き整形板は載置後、型枠に固定され、
織物層を通過したブリージング水や空気の排出を妨げる
ことなく、硬化したセグメントの上面を所定通りに綺麗
な均一な曲面とする働きをする。従って、小さい穴が多
数開いている整形板が好ましい。After placing the perforated shaping plate, it is fixed to the formwork.
It serves to make the upper surface of the hardened segment a clean and uniform curved surface as prescribed, without obstructing the discharge of breathing water and air passing through the fabric layer. Therefore, a shaping plate having many small holes is preferable.
【００１１】本発明により、蒸気養生の工程中にコンク
リートセグメントの上面は静的に整形され、平滑で綺麗
な上面の製品が得られる。従って、従来の手作業による
本仕上げは全く不要となり、外観が良く強度欠陥部のな
い製品が得られる。According to the present invention, the upper surface of the concrete segment is statically shaped during the process of steam curing, and a product having a smooth and clean upper surface is obtained. Therefore, the conventional manual finishing is completely unnecessary, and a product having a good appearance and no strength defect can be obtained.
【００１２】本発明における原料のコンクリートとして
は、従来のものと同様のスランプ値３．０cm±１．５cm
の硬練りコンクリートが使用される。この硬練りコンク
リートとしては、硬練りであるベースコンクリートをそ
のまま使用してもよいことは勿論であるが、スランプ値
が４．５cmより大きい中練りコンクリートをベースコン
クリートとし、混和後のコンクリートのスランプ値が
３．０cm±１．５cmとなるように、ベースコンクリート
に混和剤として水溶性多糖類を少量混和したコンクリー
トを使用するのが好ましい。厳密さを欠くかも知れない
が、本発明では、ベースコンクリートに水溶性多糖類を
少量混和した場合を含めて「スランプ値３．０cm±１．
５cmの硬練りコンクリート」と表現する。As the raw material concrete in the present invention, a slump value of 3.0 cm ± 1.5 cm similar to the conventional one is used.
Stiff concrete is used. As the hardened concrete, it is a matter of course that the hardened base concrete may be used as it is, but the medium-hardened concrete having a slump value of more than 4.5 cm is used as the base concrete, and the slump value of the mixed concrete is used. It is preferable to use a concrete in which a small amount of a water-soluble polysaccharide is mixed as an admixture with a base concrete so that the average particle size is 3.0 cm ± 1.5 cm. Although strictness may be lacking, in the present invention, "a slump value of 3.0 cm ± 1.0.cm" includes a case where a small amount of a water-soluble polysaccharide is mixed in a base concrete.
5cm hardened concrete ".
【００１３】この水溶性多糖類は高流動コンクリートの
増粘剤の１つとして注目されているものであり、本発明
では通常の水溶性多糖類が使用される。具体例としては
可溶性でんぷん、デキストリン、マンナン、ウエランガ
ム、キサンタンガム、ガッチガム、アラビアガムなどが
挙げられる。This water-soluble polysaccharide is attracting attention as one of the thickeners for high-fluidity concrete. In the present invention, ordinary water-soluble polysaccharide is used. Specific examples include soluble starch, dextrin, mannan, welan gum, xanthan gum, gatch gum, gum arabic and the like.
【００１４】未だ固まらないコンクリートの流動性は、
振動締め固めに対する流動性、硬化過程での垂れ下がり
変形に対する流動性、の両者ともスランプ値が小さいほ
ど小さい。ところでベースコンクリートに少量の水溶性
多糖類を混合したコンクリートについてみると、振動締
め固めに対する流動性はもとのベースコンクリートの流
動性を受け継ぎ、垂れ下がり変形に対する流動性は混合
後の新たなコンクリートの流動性を示すものである。The fluidity of concrete that has not yet set is
Both the fluidity for vibration compaction and the fluidity for sagging deformation during the hardening process are smaller as the slump value is smaller. By the way, regarding concrete mixed with a small amount of water-soluble polysaccharide in base concrete, the fluidity for compaction by vibration inherits the fluidity of the original base concrete, and the fluidity for sagging deformation is the flow of new concrete after mixing. It shows the nature.
【００１５】この現象を利用して、振動締め固めに対す
る流動性が比較的高い、スランプ値が４．５cmより大き
い中練りコンクリートをベースコンクリートとし．これ
に少量の水溶性多糖類を混合してスランプ値を３．０cm
±１．５cmとしたコンクリートを原料とすれば、硬練り
のベースコンクリートをそのまま使用した場合に比較し
て振動締め固めは容易であり、硬化過程における垂れ下
がり変形は硬練りコンクリートの場合とほぼ同等である
ことになる。かかる水溶性多糖類配合の効果を利用した
点が本発明のもう１つの要点である。By taking advantage of this phenomenon, a medium concrete having a relatively high flowability against vibration compaction and a slump value of more than 4.5 cm is used as a base concrete. A small amount of a water-soluble polysaccharide was mixed with the mixture to obtain a slump of 3.0 cm.
Using concrete with ± 1.5 cm as the raw material, vibration compaction is easier than when using hardened base concrete as it is, and sag deformation in the hardening process is almost the same as that of hardened concrete. There will be. Another point of the present invention is to utilize the effect of such a water-soluble polysaccharide combination.
【００１６】上記の水溶性多糖類配合の効果は、硬練り
に近い中練りのベースコンクリートに少量の水溶性多糖
類を混合した場合にのみ見られる現象であり、遙かにス
ランプ値の大きいベースコンクリートに多量の水溶性多
糖類を配合した場合には、かかる挙動は生じない。その
ため、本発明ではスランプ値４．５〜１５cmのベースコ
ンクリートが使用され、水溶性多糖類の配合量は３０〜
７０g/m3程度である。（この配合量は水溶性多糖類を0.
02〜0.05％溶解した水を混練水とする量に略相当す
る。）The effect of the above-mentioned water-soluble polysaccharide blending is a phenomenon that can be seen only when a small amount of a water-soluble polysaccharide is mixed into a medium-kneaded base concrete close to stiffness, and a base material having a much larger slump value. Such behavior does not occur when a large amount of water-soluble polysaccharide is mixed with concrete. Therefore, in the present invention, a base concrete having a slump value of 4.5 to 15 cm is used, and the compounding amount of the water-soluble polysaccharide is 30 to
It is about 70 g / m 3 . (The amount of water-soluble polysaccharide is 0.
This corresponds approximately to the amount of water kneaded with 02 to 0.05% dissolved water. )
【００１７】[0017]
【発明の実施の形態】以下図面を参照しながら、本発明
の成形工程を説明する。図１は本発明の成形工程を工程
順に示した斜視図である。 （１）型枠１（通常の通り、底型枠、側型枠、端型枠か
ら構成され、内部に鉄筋、インサート、中子などを所定
の位置に配設してある。）をテーブルバイブレータ２の
上に載置し、型枠１の上方に円弧状に湾曲した打設蓋３
をセットし固定する。（図１(a) ） （２）打設蓋３の中央の開口部４から硬練りコンクリー
ト５を投入する。この投入に合わせてテーブルバイブレ
ータ２の運転を開始する。（図１(b) ） （３）型枠１内への硬練りコンクリート５の充填及び振
動締固めが終了すると、テーブルバイブレータ２の運転
を停止し、打設蓋３を取り外す。表れたコンクリート成
形品の上面６を均一な円弧状の平滑面となるよう手作業
で整形する。（図１(c) ）DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The molding process of the present invention will be described below with reference to the drawings. FIG. 1 is a perspective view showing a molding step of the present invention in the order of steps. (1) Form vibrator 1 (consisting of a bottom form, a side form, and an end form as usual, and reinforcing bars, inserts, cores, etc. are disposed at predetermined positions inside). 2, and a casting cover 3 which is placed in an arc shape above the form 1.
Set and fix. (FIG. 1 (a)) (2) Pour hardened concrete 5 from the central opening 4 of the casting lid 3. The operation of the table vibrator 2 is started in accordance with the input. (FIG. 1 (b)) (3) When the filling of the stiff concrete 5 in the form 1 and the compaction by vibration are completed, the operation of the table vibrator 2 is stopped and the casting cover 3 is removed. The upper surface 6 of the exposed concrete molded product is manually shaped so as to have a uniform arc-shaped smooth surface. (Fig. 1 (c))
【００１８】（４）整形されたコンクリート成形品上面
６の上に不織布７、２枚の織物８、円弧状に湾曲した穴
開き整形板９の順に載置し、穴開き整形板９を型枠１の
上部に固定する。（図１(d) ） （５）この状態で蒸気養生槽に入れ、所定時間の蒸気養
生を行なった後、穴開き整形板９、２枚の織物８、不織
布７を取り外し、型枠１を開いて、コンクリートセグメ
ントを脱型する。 取り外した不織布７、織物８、穴開き整形板９は必要に
応じて洗浄しながら、循環再使用する。(4) The nonwoven fabric 7, two woven fabrics 8, and a perforated shaping plate 9 curved in an arc shape are placed on the shaped concrete molded product upper surface 6 in this order, and the perforated shaping plate 9 is mounted on a mold. Secure to the top of 1. (FIG. 1 (d)) (5) In this state, after putting into a steam curing tank and performing steam curing for a predetermined time, the perforated shaping plate 9, the two woven fabrics 8 and the nonwoven fabric 7 are removed, and the mold 1 is removed. Open and remove the concrete segment. The removed nonwoven fabric 7, woven fabric 8, and perforated shaping plate 9 are circulated and reused while washing as necessary.
【００１９】[0019]
【実施例】コンクリートセグメントのコンクリートの設
計基準強度＝４２０kgf/cm2 コンクリートセグメントのコンクリートの脱型基準強度
＝１５０kgf/cm2 蒸気養生時間＝６．５時間 により、コンクリートセグメントを成形した。EXAMPLES design strength of the concrete of the concrete segments = 420kgf / cm 2 demolding reference intensity of the concrete of the concrete segments = 150 kgf / cm 2 steam curing time = by 6.5 hours, and molded concrete segments.
【００２０】[0020]
【表１】 [Table 1]
【００２１】表１に見られるように、通常の硬練りコン
クリートを原料とした場合（実施例１）及びスランプ値
１０．６cmのベースコンクリートにウエランガムを少量
混合したコンクリートを原料とした場合（実施例２）は
共にコンクリートセグメントの上面は平滑で均一であ
り、強度欠陥部はなく、設計基準強度、脱型基準強度を
十分満足するものであった。さらに、実施例２の場合が
実施例１の場合に比較して、早期に強度が発現し、成形
時間を短縮し得る可能性の大きいことを示す。As can be seen from Table 1, a case where ordinary hardened concrete was used as a raw material (Example 1) and a case where a small amount of welan gum was mixed with base concrete having a slump value of 10.6 cm (Example 1) In both cases, the upper surface of the concrete segment was smooth and uniform, and there was no strength defect, and the design standard strength and the demolding standard strength were sufficiently satisfied. Furthermore, it is shown that the strength of the case of Example 2 is developed earlier than the case of Example 1 and the molding time is more likely to be reduced.
【００２２】スランプ値１０．６cmのベースコンクリー
トのみを原料とした場合（比較例）はコンクリートセグ
メントの上面は平滑で均一であり、強度欠陥部はない
が、設計基準強度、脱型基準強度を満足することはでき
なかった。When only the base concrete having a slump value of 10.6 cm was used as a raw material (comparative example), the upper surface of the concrete segment was smooth and uniform, and there was no strength defect, but the design standard strength and the demolding standard strength were satisfied. I couldn't.
【００２３】[0023]
【発明の効果】本発明は上記のように構成されており、
次の効果を奏する。 セグメント上面の整形作業の中、長時間を要していた
ブリージング完了後の整形作業が不要となり、整形の手
間が軽減するのみならず、外観良好で強度欠陥部のない
コンクリートセグメントが得られる。 中練りコンクリートであるベースコンクリートに少量
の水溶性多糖類を混合してスランプ値を３．０cm±１．
５cmとしたコンクリートを原料とすれば、スランプ値が
これと同等である通常の硬練りのベースコンクリートを
使用した場合に比較して強度発現時間が短縮されるの
で、成形時間を短縮することができる。The present invention is configured as described above,
The following effects are obtained. In the shaping work on the upper surface of the segment, the shaping work after the completion of the breathing, which took a long time, becomes unnecessary, and not only the labor for shaping is reduced, but also a concrete segment having a good appearance and no strength defect is obtained. A small amount of a water-soluble polysaccharide is mixed with a base concrete, which is a medium-mixed concrete, to give a slump value of 3.0 cm ± 1.
When the concrete having a size of 5 cm is used as a raw material, the time required for developing the strength is shortened as compared with the case of using a normal hardened base concrete having a slump value equivalent to this, so that the molding time can be shortened. .
【００２４】以上を綜合して高強度で外観の優れたコン
クリート製品を少ない労力で能率よく生産することが可
能となる。In summary, it is possible to efficiently produce concrete products having high strength and excellent appearance with little labor.
【図１】本発明の成形工程を工程順に示した斜視図であ
る。FIG. 1 is a perspective view showing a molding step of the present invention in the order of steps.
１……型枠、２……テーブルバイブレータ、３……打設
蓋、４……開口部、５……硬練りコンクリート、６……
コンクリート成形品の上面、７……不織布、８……織
物、９……穴開き整形板。1 ... formwork, 2 ... table vibrator, 3 ... casting lid, 4 ... opening, 5 ... hardened concrete, 6 ...
Upper surface of concrete molded product, 7: Non-woven fabric, 8: Fabric, 9: Perforated shaping plate.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 久保田 敏治 東京都港区芝４丁目２番３号 ジオスター 株式会社内 (72)発明者 早田 亜由美 東京都港区芝４丁目２番３号 ジオスター 株式会社内 (72)発明者 石井 公雄 埼玉県東松山市大字大谷4453 石田工業株 式会社内 Ｆターム(参考） 2D055 BA01 EB10 KA08 4G012 PB39 PC01 PC08 PC12 PE02 PE05 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Toshiharu Kubota 2-3-2 Shiba, Minato-ku, Tokyo Inside Geostar Co., Ltd. (72) Inventor Ayumi Hayata 4-2-2 Shiba, Minato-ku, Tokyo Geostar Co., Ltd. (72) Inventor Kimio Ishii 4453 Otani, Higashimatsuyama-shi, Saitama F-term within Ishida Kogyo Co., Ltd. 2D055 BA01 EB10 KA08 4G012 PB39 PC01 PC08 PC12 PE02 PE05
Claims (3)
た準備済の型枠の上に、開口部を有する円弧状に湾曲し
た打設蓋を載置し、開口部よりスランプ値３．０cm±
１．５cmの硬練りコンクリートを打設しながら、テーブ
ルバイブレータを作動して、打設したコンクリートを締
固める工程、（Ｂ）型枠より打設蓋を取り外し、締固め
られたコンクリート成形品の上面を整形する工程、
（Ｃ）整形後のコンクリート成形品の上面に不織布、織
物、円弧状に湾曲した穴開き整形板の順に載置固定し
て、コンクリート成形品を蒸気養生する工程、よりなる
コンクリートセグメントの成形方法。1. (A) An arc-shaped curved casting lid having an opening is placed on a prepared formwork placed on a table vibrator, and a slump value of 3.0 cm ± from the opening.
A step of operating a table vibrator while compacting 1.5 cm of hardened concrete to compact the cast concrete. (B) Removing the casting lid from the formwork, and the top surface of the compacted concrete molded product The process of shaping the
(C) A method of forming a concrete segment, comprising the steps of placing and fixing a nonwoven fabric, a woven fabric, and a perforated shaping plate curved in an arc shape on the upper surface of a shaped concrete molded product in order, and steam curing the concrete molded product.
ンクリートを打設することを特徴とする請求項１記載の
コンクリートセグメントの成形方法。2. The method for forming a concrete segment according to claim 1, wherein concrete using a water-soluble polysaccharide as an admixture is cast.
項２記載のコンクリートセグメントの成形方法。3. The method according to claim 2, wherein the water-soluble polysaccharide is welan gum.