JP2002094286A - Radio wave absorber - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a radio wave absorber that has extremely excellent absorption efficiency (excellent slant incidence characteristics) even if a radio wave enters the side of a radio wave absorption layer slantwise, and, furthermore, can easily create an optimum electromagnetic absorption surface according to the degree of the arrival of an electromagnetic wave in an execution site. SOLUTION: This radio wave absorber comprises at least two radio wave absorption layers, and a heat transfer conversion layer. In this case, a hologram layer should be provided at the side of each radio wave absorption layer.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は室内ＬＡＮ対応、レ
ーダ偽像防止、無線障害防止、およびＥｌｅｃｔｒｏ
Ｍａｇｎｅｔｉｃ Ｉｎｔｅｒｆｅｒｅｎｃｅ（ＥＭ
Ｉ）対策分野で使用される電波吸収体に関するものであ
る。特に斜めからの電波の入射でも極めて吸収効率が良
い（斜入射特性の良い）、ミリ波を含む高周波電波吸収
体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an indoor LAN, radar false image prevention, radio interference prevention, and Electro.
Magnetic Interference (EM
I) A radio wave absorber used in the field of countermeasures. In particular, the present invention relates to a high-frequency radio wave absorber including millimeter waves having extremely high absorption efficiency (good oblique incidence characteristics) even when oblique radio waves are incident.

【０００２】[0002]

【従来の技術】近年、各種電子機器の発達により種々な
電子機器が事務所、工場、研究所、店舗、一般家庭等の
あらゆる場所に導入されて使用される様に成って来た
が、これら電子機器に起因する電波障害の問題が多く発
生し、その防止策として電磁波シールド材を壁材として
用いたり、シールドルームを設けたりしている。2. Description of the Related Art In recent years, with the development of various electronic devices, various electronic devices have been introduced and used in various places such as offices, factories, laboratories, stores, and general homes. There are many problems of radio interference caused by electronic devices, and as a preventive measure, an electromagnetic wave shielding material is used as a wall material or a shield room is provided.

【０００３】この様な電磁波シールド材に就いては種々
提案されており、また、電波吸収材と電波反射材との複
合材に就いても種々提案されている。斯様な電磁シール
ド材の一例として、例えば特開昭６４−８６５９５号公
報記載のものを列挙することが出来る。Various proposals have been made for such an electromagnetic wave shielding material, and various proposals have been made for a composite material of a radio wave absorbing material and a radio wave reflecting material. As an example of such an electromagnetic shielding material, for example, those described in JP-A-64-86595 can be listed.

【０００４】併し乍ら、シールドルームの設置には多額
の費用が掛かる等の問題が有り、また、電磁波シールド
材を壁材として使用するものでは、室内を金属材料でシ
ールドしたシールド・ビルが知られているが、この様な
シールド・ビルに用いられる金属系のシールド材は電波
をほゞ１００％反射することによって機能するために、
反射された電波が更に他に悪影響を及ぼす等の問題や、
無線ＬＡＮ等のＯＡ化に対しても十分でない等の問題が
見られる。即ち、電磁波シールドの場合、基本的には入
射される不要電磁波に対して反射作用を利用して、電子
機器筐体内に電磁波が侵入されるのを防ぐ事となる。そ
のためこの場合には、利用空間内に対して電磁波は何ら
かの意味で存在していることになり、２次的ノイズのも
とになってしまう。[0004] However, there is a problem that the installation of the shield room requires a large amount of cost and the like. In the case of using an electromagnetic wave shielding material as a wall material, a shield building in which the room is shielded with a metal material is known. However, the metallic shielding material used in such shielded buildings works by reflecting almost 100% of radio waves.
Problems such as the reflected radio waves having other adverse effects,
There are problems such as insufficient OA for a wireless LAN or the like. That is, in the case of the electromagnetic wave shield, basically, the electromagnetic wave is prevented from entering the electronic device housing by utilizing the reflection function for the incident unnecessary electromagnetic wave. Therefore, in this case, the electromagnetic wave exists in the use space in some sense, and causes a secondary noise.

【０００５】一方、従来の電磁波吸収体の場合は、設計
段階から完全反射体である金属板からの反射レベルに対
して、幾何学的に同面積の電波吸収体層からの反射レベ
ルがどの程度低下するか、つまりは入射電磁波に対して
どの程度吸収されるかを考慮して製造される。そのため
この場合には、利用空間内に対して入射された電磁波は
存在しなくなる。そのため不要電磁波に対する根本的な
解決となり両者はその作用・構成等において明確に区別
される。On the other hand, in the case of a conventional electromagnetic wave absorber, from the design stage, the reflection level from a radio wave absorber layer having the same geometrical area as the reflection level from a metal plate which is a perfect reflector is determined. It is manufactured in consideration of the degree of reduction, that is, how much the incident electromagnetic wave is absorbed. Therefore, in this case, there is no electromagnetic wave incident on the use space. Therefore, this is a fundamental solution to unnecessary electromagnetic waves, and both are clearly distinguished in their operation and configuration.

【０００６】この電磁波吸収体としては、最も基本的な
ものとして構造的に単純な金属で裏打ちした１層型電波
吸収体がある。一般にはゴム材料に炭素粒子を混入した
１層型ゴムシート電波吸収体が多い。さらには、表面層
と吸収層を有する２層型電波吸収体がある。これは、グ
ラファイト含有発泡スチロールや炭化ケイ素ＦＲＰを用
いた電波吸収体が多い。The most basic type of the electromagnetic wave absorber is a one-layer type electromagnetic wave absorber lined with a structurally simple metal. Generally, there are many one-layer rubber sheet radio wave absorbers in which carbon particles are mixed in a rubber material. Further, there is a two-layer type radio wave absorber having a surface layer and an absorption layer. This is often a radio wave absorber using graphite-containing styrofoam or silicon carbide FRP.

【０００７】さらには、電波暗室に使用する電波吸収体
のように広帯域性を必要とする多層型電波吸収体があ
る。これは構造形態より、ピラミッド形のものやウエッ
ジ形のものに区分される。薄膜多層構造電磁波吸収体と
しては、例えば日本エネシス株式会社の「フレクステ
ル」（商品名）がある。これは、１５種類を超える素材
を施工状況から組み合わせを決定し製造する。さらに各
層は特殊な熱可塑性接着剤で強固に結合させるものであ
り、施工後の修正あるいはその場での修正は不可能であ
る。また、周波数に応じた形態にならざるをえず、構成
材料を別にそれぞれ用意しておく必要が生じる。[0007] Further, there is a multilayer type radio wave absorber which requires a wide band, such as a radio wave absorber used in an anechoic chamber. This is classified into a pyramid type and a wedge type according to the structural form. As a thin film multilayer electromagnetic wave absorber, there is, for example, "Flextel" (trade name) of Nippon Enesis Co., Ltd. In this method, a combination of more than 15 kinds of materials is determined from the construction conditions and manufactured. Furthermore, each layer is firmly bonded with a special thermoplastic adhesive, and it is impossible to correct it after construction or correct it on the spot. In addition, it is inevitable to be in a form corresponding to the frequency, and it is necessary to separately prepare constituent materials.

【０００８】また、最近は携帯電話を中心としたミリ波
帯を意識した電波の需要が急速に進み、それに伴ないミ
リ波帯（特に６０ＧＨｚ、９０ＧＨｚ）における電波吸
収体の研究開発も盛んに行なわれている。この場合一般
には、抵抗皮膜型電波吸収体が多くある。しかしなが
ら、電波吸収体の電波吸収層面に対して、斜めからの電
波の入射でも極めて吸収効率が良い（斜入射特性の良
い）電波吸収体は、今までには無かった。In recent years, the demand for radio waves conscious of the millimeter wave band centering on mobile phones has been rapidly increasing, and accompanying this, research and development of radio wave absorbers in the millimeter wave band (especially 60 GHz and 90 GHz) have been actively conducted. Have been. In this case, generally, there are many resistance film type radio wave absorbers. However, there has been no radio wave absorber with extremely high absorption efficiency (having good oblique incidence characteristics) even when a radio wave is obliquely incident on the radio wave absorption layer surface of the radio wave absorber.

【０００９】[0009]

【発明が解決しようとする課題】本発明が解決しようと
する課題は、高周波（１ＧＨｚ〜７０ＧＨｚ）対応の電
波吸収体において、斜入射特性を改善し、なるべく薄
く、軽量・安価で、高効率、広帯域の電波吸収能を持つ
とともに、必要に応じて、施工の容易さをも実現するこ
とである。The problem to be solved by the present invention is to improve the oblique incidence characteristics of a radio wave absorber corresponding to a high frequency (1 GHz to 70 GHz), to be as thin as possible, light and inexpensive, to have high efficiency, Along with having a broadband radio wave absorption capability, it is also necessary to realize ease of construction as required.

【００１０】[0010]

【課題を解決するための手段】上記課題を解決するため
に、本発明の「電波吸収体」は、 （１）２層以上の電波吸収層と、熱伝達変換層とから構
成された電波吸収体であって、前記各電波吸収層側にホ
ログラム層（回折格子層）を設けたことを特徴とする電
波吸収体。 （２）前記電波吸収体の各層間に易接着層を設けたこと
を特徴とする（１）に記載の電波吸収体。 （３）熱伝達変換層が有機繊維や無機繊維を用いた高熱
伝導性樹脂シートであることを特徴とする（１）又は
（２）に記載の電波吸収体。 としたのである。例えば、ホログラム層が表面に形成さ
れた電波及び／または電磁波を吸収するための電波吸収
層を２層以上持ち、これと各電波吸収層で吸収された電
波や電磁波を熱エネルギーに変換する役目をする熱伝達
変換層を積層した構成とした。本発明で製造した電波吸
収特性の異なる各種電波吸収層は複層で用いる。易接着
層を介して複数積層させて用いても良い。吸収効率と電
磁波周波数に応じて、各層に機能分離するほうがより有
利であり、これにより帯域も広がり高周波全域を無駄無
く吸収することが可能となる。Means for Solving the Problems To solve the above problems, the "radio wave absorber" of the present invention comprises: (1) a radio wave absorber composed of two or more radio wave absorbing layers and a heat transfer conversion layer. A radio wave absorber, wherein a hologram layer (diffraction grating layer) is provided on each radio wave absorption layer side. (2) The radio wave absorber according to (1), wherein an easy adhesion layer is provided between each layer of the radio wave absorber. (3) The radio wave absorber according to (1) or (2), wherein the heat transfer conversion layer is a high heat conductive resin sheet using organic fibers or inorganic fibers. It was. For example, the hologram layer has two or more radio wave absorbing layers for absorbing radio waves and / or electromagnetic waves formed on the surface, and plays a role of converting the radio waves and electromagnetic waves absorbed by each radio wave absorbing layer into thermal energy. And a heat transfer conversion layer. Various radio wave absorption layers having different radio wave absorption characteristics manufactured in the present invention are used as a multilayer. A plurality of such layers may be laminated via an easy-adhesion layer. It is more advantageous to separate the functions into layers according to the absorption efficiency and the electromagnetic wave frequency, whereby the band is widened and the entire high frequency range can be absorbed without waste.

【００１１】また、本発明の「電波吸収体」は、上記構
成において更に、熱伝達変換層が有機繊維を用いた高熱
伝導性樹脂シートから成る構成とした。熱伝達変換層
は、一般にはアルミニウムや銅などの金属板、金属ネッ
トを複合加工して製品としているが、本発明では軽量か
つ放熱性および熱伝導率の点から炭素繊維等の有機繊維
等を用いた高熱伝導性樹脂シートを用いた。Further, the "radio wave absorber" of the present invention has a constitution in which the heat transfer conversion layer further comprises a high heat conductive resin sheet using organic fibers. The heat transfer conversion layer is generally a product obtained by compounding a metal plate such as aluminum or copper, or a metal net, but in the present invention, organic fibers such as carbon fibers are used from the viewpoint of light weight and heat dissipation and thermal conductivity. The used high thermal conductive resin sheet was used.

【００１２】[0012]

【発明の実施の形態】以下、本発明の電波吸収体につい
て、実施の形態を説明する。Embodiments of the radio wave absorber of the present invention will be described below.

【００１３】先ず本発明の電波吸収体の典型的な構造を
図１及び図２を引用して説明する。図１は本発明の電波
吸収体の一実施例の断面図である。図１の電波吸収体７
は、ホログラム層付き電波吸収層Ａ（図示の符号１）と
ホログラム層付き電波吸収層Ｂ（図示の符号３）とホロ
グラム層付き電波吸収層Ｃ（図示の符号４）と熱伝達変
換層５とをそれぞれ易接着層２を介して積層された構成
である。また、図２は本発明の電波吸収体（図１）の一
実施例の分解した構成を示す斜視図である。図２の電波
吸収体は、ホログラム層付き電波吸収層Ａ（図示の符号
１）とホログラム層付き電波吸収層Ｂ（図示の符号３）
とホログラム層付き電波吸収層Ｃ（図示の符号４）と熱
伝達変換層５とをそれぞれ易接着層２を介して積層され
た構成である。ホログラム層付き電波吸収層Ａ（図示の
符号１）とホログラム層付き電波吸収層Ｂ（図示の符号
３）とホログラム層付き電波吸収層Ｃ（図示の符号４）
はいずれも、角部を切断され、剥離用切り込み６が形成
されている。First, a typical structure of the radio wave absorber of the present invention will be described with reference to FIGS. FIG. 1 is a sectional view of one embodiment of the radio wave absorber of the present invention. Radio wave absorber 7 of FIG.
Are a radio wave absorbing layer A with a hologram layer (1 in the figure), a radio wave absorbing layer B with a hologram layer (3 in the figure), a radio wave absorbing layer C with a hologram layer (4 in the figure), and a heat transfer conversion layer 5. Are laminated with the easy-adhesion layer 2 interposed therebetween. FIG. 2 is a perspective view showing an exploded configuration of one embodiment of the radio wave absorber (FIG. 1) of the present invention. The radio wave absorber of FIG. 2 includes a radio wave absorption layer A with a hologram layer (reference numeral 1 in the drawing) and a radio wave absorption layer B with a hologram layer (reference numeral 3 in the drawing).
A hologram layer-equipped radio wave absorbing layer C (reference numeral 4 in the figure) and a heat transfer conversion layer 5 are laminated with an easy-adhesion layer 2 interposed therebetween. Radio wave absorption layer A with hologram layer (reference number 1 in the figure), radio wave absorption layer B with hologram layer (reference number 3 in the figure), and radio wave absorption layer C with hologram layer (reference number 4 in the figure)
In each case, the corners are cut, and the cuts 6 for peeling are formed.

【００１４】以下、これら各層について更に詳述する。Hereinafter, each of these layers will be described in more detail.

【００１５】（電波吸収層）電波及び／または電磁波を
吸収するための電波吸収層は、軽量化を意識した材料を
用いるのが好ましい。すなわち、一般にはフェライトを
中心とした磁性金属類が用いられるが、ここではさらな
る軽量化を実現するために、カーボン粉体（カーボンブ
ラック）あるいは希土類粉体または磁性スピンを有する
Ｃｏ、Ｆｅなどを中心金属とした有機金属錯体類などを
用いる。これらを固定させ電波吸収層を作製する方法に
は、主に圧延ロール法とホットプレス法がある。ここで
は、実験室レベルで簡便で、異方性の生じにくいホット
プレス法によった。(Radio Wave Absorbing Layer) The radio wave absorbing layer for absorbing radio waves and / or electromagnetic waves is preferably made of a material that is conscious of weight reduction. That is, generally, magnetic metals such as ferrite are mainly used. However, in order to further reduce the weight, carbon powder (carbon black), rare earth powder, or Co or Fe having magnetic spin is mainly used. Organometallic complexes used as metals are used. There are mainly roll-rolling methods and hot-pressing methods for fixing these to form a radio wave absorbing layer. Here, a hot press method which is simple at the laboratory level and hardly causes anisotropy is used.

【００１６】ホットプレス法は、ゴムなどの結着用材料
に対するカーボンブラックの混合比を変化させ混入し、
これをペイントロールで混合した後、スペーサで厚みを
各種調整してホットプレスすることにより製作する。も
ちろんカーボンブラックの代わりに希土類粉体または磁
性スピンを有するＣｏ、Ｆｅなどを中心金属とした有機
金属錯体類などを結着用材料に分散、練り込んでも良
い。また分散、混合する代わりにカーボンブラックある
いは希土類粉体または磁性スピンを有するＣｏ、Ｆｅな
どを中心金属とした有機金属錯体類を結着用材料で含浸
させ硬化結着させる方法や含浸させ硬化結着させなが
ら、スペーサで厚みを各種調整してホットプレスや圧延
ロールにより製作することもある。In the hot pressing method, the mixing ratio of carbon black to a binding material such as rubber is changed and mixed.
After mixing with a paint roll, the thickness is variously adjusted with a spacer and hot-pressed. Of course, instead of carbon black, a rare earth powder or an organic metal complex having a magnetic spin of Co, Fe or the like as a central metal may be dispersed and kneaded in the binding material. Instead of dispersing and mixing, a method of impregnating a carbon black or a rare earth powder or an organometallic complex having a magnetic spin with Co, Fe, or the like as a central metal with a binding material and curing and binding is used. In some cases, the thickness is adjusted in various ways with a spacer, and the product is manufactured by a hot press or a rolling roll.

【００１７】結着用材料としては、エポキシ変性ウレタ
ンゴム等の各種ゴム類、シリコーン、各種の合成樹脂が
用いられる。例えばポリエチレン樹脂、ポリプロピレン
樹脂、ポリメチルペンテン樹脂、ポリブテン樹脂、エチ
レン−プロピレン共重合樹脂、オレフィン系熱可塑性エ
ラストマー等のオレフィン系樹脂、ポリ塩化ビニル樹
脂、ポリ塩化ビニリデン樹脂、ポリビニルアルコール樹
脂、塩化ビニル−酢酸ビニル共重合樹脂、エチレン−酢
酸ビニル共重合樹脂、エチレン−ビニルアルコール共重
合樹脂等のビニル系樹脂、ポリエチレンテレフタレート
樹脂、ポリブチレンテレフタレート樹脂、ポリエチレン
ナフタレート、エチレン−テレフタレート−イソフタレ
ート共重合樹脂、ポリエステル系熱可塑性エラストマー
等のポリエステル系樹脂、ポリ（メタ）アクリル酸メチ
ル樹脂、ポリ（メタ）アクリル酸エチル樹脂、ポリ（メ
タ）アクリル酸ブチル樹脂、（メタ）アクリル酸メチル
−（メタ）アクリル酸ブチル共重合樹脂等のアクリル樹
脂、ナイロン６又はナイロン６６等で代表されるポリア
ミド樹脂、三酢酸セルロース樹脂、セロファン、ポリス
チレン樹脂、ポリカーボネート樹脂、ポリアリレート樹
脂、ポリイミド樹脂、エポキシフェノール樹脂、エポキ
シ樹脂、エポキシウレタン変性樹脂、又はフェノール樹
脂等である。上記の内、エポキシ変性ウレタンゴム、シ
リコーン、エポキシフェノール樹脂、エポキシウレタン
変性樹脂、フェノール樹脂、アクリル樹脂などを用いる
のが好ましい。As the binding material, various rubbers such as epoxy-modified urethane rubber, silicone, and various synthetic resins are used. For example, polyethylene resins, polypropylene resins, polymethylpentene resins, polybutene resins, ethylene-propylene copolymer resins, olefinic resins such as olefinic thermoplastic elastomers, polyvinyl chloride resins, polyvinylidene chloride resins, polyvinyl alcohol resins, polyvinyl chloride resins Vinyl acetate copolymer resin, ethylene-vinyl acetate copolymer resin, vinyl resin such as ethylene-vinyl alcohol copolymer resin, polyethylene terephthalate resin, polybutylene terephthalate resin, polyethylene naphthalate, ethylene-terephthalate-isophthalate copolymer resin, Polyester resins such as polyester-based thermoplastic elastomers, poly (meth) methyl acrylate resin, poly (meth) ethyl acrylate resin, poly (meth) butyl acrylate resin, ) Acrylic resin such as methyl acrylate-butyl (meth) acrylate copolymer resin, polyamide resin represented by nylon 6 or nylon 66, cellulose triacetate resin, cellophane, polystyrene resin, polycarbonate resin, polyarylate resin, polyimide Resin, epoxy phenol resin, epoxy resin, epoxy urethane modified resin, phenol resin and the like. Of the above, it is preferable to use epoxy-modified urethane rubber, silicone, epoxy phenol resin, epoxy urethane-modified resin, phenol resin, acrylic resin, and the like.

【００１８】混合、分散するための分散機は、前記した
ペイントロール以外にもペイントシェーカ、ビーズミ
ル、アトライターなどを用いても良い。スペーサで設計
厚みに調整してホットプレスによって作製する際、例え
ば、設計数値等に関しては橋本修等の論文を参考に分散
調合を決定していった。（橋本修等：電子情報通信学会
論文誌 Ｂ Ｖｏｌ．Ｊ８２−Ｂ Ｎｏ．３ ｐｐ．４
６９−４７５ １９９９年３月）As a disperser for mixing and dispersing, a paint shaker, a bead mill, an attritor, or the like may be used in addition to the above-described paint roll. When adjusting to the design thickness with a spacer and manufacturing by hot pressing, for example, regarding the design numerical values and the like, the dispersion formulation was determined with reference to a paper by Osamu Hashimoto and the like. (Osamu Hashimoto et al .: Transactions of the Institute of Electronics, Information and Communication Engineers, B Vol. J82-B No. 3 pp. 4
69-475 Mar 1999)

【００１９】カーボンブラックあるいは希土類粉体また
は磁性スピンを有するＣｏ、Ｆｅなどを中心金属とした
有機金属錯体類などの種類や混合比や電波吸収層の厚み
によって、電波吸収特性の異なる各種電波吸収層を作製
できる。Various radio wave absorption layers having different radio wave absorption characteristics depending on the type, mixing ratio, and thickness of the radio wave absorption layer, such as carbon black, rare earth powder, or organometallic complexes having a central metal such as Co or Fe having magnetic spin. Can be produced.

【００２０】さらにこのようにして製造したものの表面
に後記のホログラム層が形成された、電波吸収特性の異
なる各種電波吸収層は、易接着層２を介して複数積層さ
せて用いても良い（図１、２）。吸収効率と電磁波周波
数に応じて、各層に機能分離するほうが有利であり、こ
れにより帯域も広がり高周波全域を無駄無く吸収するこ
とが可能となる。Further, a plurality of various radio wave absorption layers having different radio wave absorption characteristics, in which a hologram layer described later is formed on the surface of the thus-produced product, may be used by laminating a plurality of layers via the easy adhesion layer 2 (FIG. 1, 2). It is more advantageous to separate the functions into the respective layers according to the absorption efficiency and the electromagnetic wave frequency, whereby the band is widened and the entire high frequency range can be absorbed without waste.

【００２１】（熱伝達変換層）熱伝達変換層５は、一般
にはアルミニウムや銅などの金属板、金属ネットを複合
加工して製品としている。ここでは、軽量かつ放熱性お
よび熱伝導率の点から有機繊維または無機繊維を用いた
高熱伝導性樹脂シートを用いた。(Heat Transfer Conversion Layer) In general, the heat transfer conversion layer 5 is a product obtained by compounding a metal plate such as aluminum or copper or a metal net. Here, a high heat conductive resin sheet using organic fibers or inorganic fibers was used from the viewpoint of light weight, heat dissipation and heat conductivity.

【００２２】これは炭素繊維、アラミド繊維、ガラス繊
維等の特殊な繊維の繊維方向を制御して高濃度で整列さ
せエポキシ樹脂やポリイミド樹脂等の熱硬化性樹脂で硬
化させることによって得られる。例えば、日機装株式会
社の商品名 ＭＡＴＥＬＩＧＨＴ（炭素繊維強化プラス
チック、アラミド繊維強化プラスチック、ガラス繊維強
化プラスチック）やポリマテック株式会社の繊維配向複
合材などを使用するのがよい。この炭素繊維は、レーヨ
ン系、ポリアクリロニトリル（ＰＡＮ）系、フェノール
樹脂系、石炭ピッチ系、石油ピッチ系など、各種の炭素
繊維が使用でき、そして、通常、繊維直径が２〜３０μ
ｍ程度、平均繊維長さが０．１〜１０ｍｍ程度のものを
使用するのが好ましい。This can be obtained by controlling the fiber direction of special fibers such as carbon fibers, aramid fibers, and glass fibers, aligning them at a high concentration, and curing them with a thermosetting resin such as an epoxy resin or a polyimide resin. For example, it is preferable to use MATELIGHT (carbon fiber reinforced plastic, aramid fiber reinforced plastic, glass fiber reinforced plastic) (trade name of Nikkiso Co., Ltd.) or a fiber oriented composite material of Polymertec Corporation. Various carbon fibers such as rayon-based, polyacrylonitrile (PAN) -based, phenolic resin-based, coal pitch-based, and petroleum pitch-based carbon fibers can be used as the carbon fiber.
m and an average fiber length of about 0.1 to 10 mm are preferably used.

【００２３】ここで炭素繊維、アラミド繊維（芳香族ポ
リアミド繊維）、ガラス繊維等の特殊な繊維の繊維方向
を制御しないでエポキシ樹脂やポリイミド樹脂等の熱硬
化性樹脂で硬化させても良い。熱硬化性樹脂は、例え
ば、エポキシ樹脂、ＢＭＩ系樹脂（フェノール樹脂、不
飽和ポリエステル樹脂、フラン樹脂など）、ポリイミド
樹脂等の一般の熱硬化性樹脂であり、特に限定されるも
のではない。なお、熱硬化性樹脂には、必要に応じて、
硬化剤等の配合剤を配合することができる。また、エポ
キシ樹脂やポリイミド樹脂等の熱硬化性樹脂の代わり
に、ポリエーテルエーテルケトン、ポリフェニレンサル
ファイド等の熱可塑性樹脂を使用しても良い。Here, without controlling the fiber direction of special fibers such as carbon fibers, aramid fibers (aromatic polyamide fibers), and glass fibers, the fibers may be cured with a thermosetting resin such as an epoxy resin or a polyimide resin. The thermosetting resin is, for example, a general thermosetting resin such as an epoxy resin, a BMI-based resin (a phenol resin, an unsaturated polyester resin, a furan resin, etc.), a polyimide resin and the like, and is not particularly limited. In addition, the thermosetting resin, if necessary,
A compounding agent such as a curing agent can be compounded. Instead of a thermosetting resin such as an epoxy resin or a polyimide resin, a thermoplastic resin such as polyetheretherketone or polyphenylene sulfide may be used.

【００２４】特殊な繊維としては綿、麻、竹、木等の植
物原料から得た繊維（セルロースパルプを含む）等の天
然有機繊維、または炭化珪素繊維、金属繊維、セピオラ
イト、石綿等の天然乃至は人造無機繊維や、ポリエステ
ル、ポリアクリロニトリル、ポリビニールアルコール、
ポリプロピレン、ポリアミド繊維等の人造有機繊維も使
用できる。The special fibers include natural organic fibers such as fibers (including cellulose pulp) obtained from plant materials such as cotton, hemp, bamboo, and wood; and natural or natural fibers such as silicon carbide fibers, metal fibers, sepiolite, and asbestos. Are artificial inorganic fibers, polyester, polyacrylonitrile, polyvinyl alcohol,
Artificial organic fibers such as polypropylene and polyamide fibers can also be used.

【００２５】（ホログラム層）前記電波吸収層の上に
は、ホログラム層、即ち、ホログラムまたは回折格子を
形成した層を設けておく。ホログラムまたは回折格子自
体は、平面ホログラム、体積ホログラムともに使用で
き、具体例としては、レリーフホログラム、リップマン
ホログラム、フルネルホログラム、フラウンホーファホ
ログラム、レンズレスフーリエ変換ホログラム、レーザ
ー再生ホログラム（イメージホログラムなど）、白色光
再生ホログラム（レインボーホログラムなど）、カラー
ホログラム、コンピュータホログラム、ホログラムディ
スプレイ、マルチプレックスホログラム、ホログラフィ
ックステレオグラム、ホログラフィック回折格子などが
挙げられる。(Hologram layer) A hologram layer, that is, a layer on which a hologram or diffraction grating is formed, is provided on the radio wave absorption layer. The hologram or diffraction grating itself can be used for both planar holograms and volume holograms. Specific examples include relief holograms, Lippmann holograms, Fresnel holograms, Fraunhofer holograms, lensless Fourier transform holograms, laser reproduction holograms (image holograms, etc.), white Light reproduction holograms (rainbow holograms, etc.), color holograms, computer holograms, hologram displays, multiplex holograms, holographic stereograms, holographic diffraction gratings and the like can be mentioned.

【００２６】これらのホログラム層を形成する層の材料
には、ポリ塩化ビニル、アクリル樹脂（例、ＰＭＭ
Ａ）、ポリスチレン、ポリカーボネートなどの熱可塑性
樹脂、不飽和ポリエステル、メラミン、エポキシ、ポリ
エステル（メタ）アクリレート、ウレタン（メタ）アク
リレート、エポキシ（メタ）アクリレート、ポリエーテ
ル（メタ）アクリレート、ポリオール（メタ）アクリレ
ート、メラミン（メタ）アクリレート、トリアジン系ア
クリレートなどの熱硬化性樹脂をそれぞれ単独、或いは
上記熱可塑性樹脂と熱硬化性樹脂とを混合して使用する
ことができ、更には、ラジカル重合性不飽和基を有する
熱成形性物質、或いは、これらにラジカル重合性不飽和
単量体を加え電離放射線硬化性としたものなどを使用す
ることができる。このほか、銀塩、重クロム酸ゼラチ
ン、サーモプラスチック、ジアゾ系感光材料、フォトレ
ジスト、強誘電体、フォトクロミックス材料、サーモク
ロミックス材料、カルコゲンガラスなどの感光材料など
も使用できる。The materials for the layers forming these hologram layers include polyvinyl chloride and acrylic resin (eg, PMM).
A), thermoplastic resins such as polystyrene and polycarbonate, unsaturated polyester, melamine, epoxy, polyester (meth) acrylate, urethane (meth) acrylate, epoxy (meth) acrylate, polyether (meth) acrylate, polyol (meth) acrylate , A thermosetting resin such as melamine (meth) acrylate or triazine acrylate can be used alone, or a mixture of the above-mentioned thermoplastic resin and thermosetting resin can be used. Or a material obtained by adding a radical polymerizable unsaturated monomer to these materials to make them ionizing radiation-curable. In addition, photosensitive materials such as silver salts, dichromated gelatin, thermoplastics, diazo photosensitive materials, photoresists, ferroelectrics, photochromic materials, thermochromic materials, and chalcogen glass can be used.

【００２７】上記の材料を用いてホログラム層を形成す
る方法は、従来既知の方法によって形成することがで
き、例えば、回折格子やホログラムの干渉縞を表面凹凸
のレリーフとして記録する場合には、回折格子や干渉縞
が凹凸の形で記録された原版をプレス型として用い、前
記熱伝達変換層上に電波吸収層を積層した電波吸収体の
電波吸収層の上に、前記ホログラム層形成用樹脂の塗布
液をグラビアコート法、ロールコート法、バーコート法
などの手段で塗布して、塗膜を形成し、その上に前記原
版を重ねて加熱ロールなどの適宜手段により、両者を加
熱圧着することにより、原版の凹凸模様を複製すること
ができる。また、フォトポリマーを用いる場合は、前記
電波吸収体の電波吸収層の上に、フォトポリマーを同様
にコーティングした後、前記原版を重ねてレーザー光を
照射することにより複製することができる。このよう
に、表面凹凸のレリーフとして回析格子やホログラムの
干渉縞をホログラム層の表面に記録する方法は、量産性
があり、コストも低くできる点で特に好ましい。このよ
うなホログラム層の膜厚は０．１〜６μｍの範囲が好ま
しく、０．１〜４μｍの範囲が更に好ましい。さらに
は、ホログラム面における入射特性をさらに良好とする
ためブレーズドアングルで形状を微細加工したり、回折
格子のピッチ配列をチャーピングによる焦点調整をおこ
なってもよい。また、これらのホログラム記録に関して
は、光学露光方式として、レーザの２光束干渉法や間接
的に設けたマスターマスクからのレーザ露光によってホ
ログラム感材へ記録し作製する。The method of forming the hologram layer using the above materials can be formed by a conventionally known method. For example, when recording a diffraction grating or an interference fringe of a hologram as a relief of surface unevenness, a diffraction method is used. Using an original plate in which lattices and interference fringes are recorded in the form of concavities and convexities as a press mold, on the radio wave absorption layer of a radio wave absorber having a radio wave absorption layer laminated on the heat transfer conversion layer, the hologram layer forming resin The coating solution is applied by means of a gravure coating method, a roll coating method, a bar coating method or the like to form a coating film, and the original is superimposed thereon, and both are heated and pressed by appropriate means such as a heating roll. As a result, the concave and convex pattern of the original plate can be duplicated. In the case where a photopolymer is used, a photopolymer can be similarly coated on the radio wave absorbing layer of the radio wave absorber, and then the original can be overlaid and duplicated by irradiating a laser beam. As described above, the method of recording the diffraction grating or the interference pattern of the hologram on the surface of the hologram layer as the relief of the surface unevenness is particularly preferable because it has mass productivity and can reduce the cost. The thickness of such a hologram layer is preferably in the range of 0.1 to 6 μm, more preferably in the range of 0.1 to 4 μm. Furthermore, in order to further improve the incident characteristics on the hologram surface, the shape may be finely processed by a blazed angle, or the focus adjustment may be performed by chirping the pitch arrangement of the diffraction grating. These hologram recordings are recorded and produced on a hologram photosensitive material by an optical exposure method, such as laser two-beam interferometry or laser exposure from a master mask provided indirectly.

【００２８】また、本発明の「電波吸収体」は、図１と
図２におけるように、ホログラム層付きの電波吸収層Ａ
〜Ｃと熱伝達変換層５の各層間に易接着層２をもたせた
もので、これにより施工場所における電磁波到達度合い
に応じて最適な電磁波吸収面を、剥離用切り込み６を指
標に剥離することで容易に作り出すことが可能となる。The "radio wave absorber" of the present invention comprises a radio wave absorbing layer A having a hologram layer as shown in FIGS.
C and the heat transfer conversion layer 5 with the easy-adhesion layer 2 between them, thereby separating the optimum electromagnetic wave absorbing surface in accordance with the degree of arrival of the electromagnetic wave at the construction site by using the cut 6 for separation as an index. And can be easily produced.

【００２９】易接着層２の一例としては、信越化学株式
会社製のアクリルシリコーンエマルジョン溶液を溶媒
（トルエンとアセトンの１：１混合溶媒）で５％に希釈
したものをメイヤーバーや各種コーティング法によって
１〜２５μｍの厚さに塗布して形成する。また、易接着
層２の材料としての樹脂（バインダー）には、ポリビニ
ルアルコール単独あるいはその部分ケン化品（商品名
ポバール）、塩化ビニル−酢酸ビニル共重合体、エチレ
ン−酢酸ビニル共重合体を使用でき、接着力の強弱を調
整するためシリコーン油等のシリコーン類を数％含有す
ればよい。さらには、シリコーン油のみならず、シラン
カップリング剤単独あるいはその加水分解物を数％含有
させても良い。（東芝シリコン株式会社製）ただし、ホ
ログラム材料と易接着材料の屈折率差は少ないものを選
択し使用することが好ましい。すなわち、ホログラム材
料には、感材をデュポン社製やアグファ社製８Ｅ７５Ｈ
Ｄを記録材料として使用することが好ましい。これらの
屈折率が１．５１−１．５５程度であるので易接着層の
これと同等にし、表面反射等による入射特性を損なわな
いよう調整することが好ましい。各層を積層して貼り合
わせ電波吸収体７を構成させる。さらに施工現場におい
て、ホログラム層付きの電波吸収層Ａ（図示の符号１）
を剥離用切り込み６に従って剥離したが、容易に剥離で
き、ホログラム層付きの電波吸収層Ｂ（図示の符号３）
を最表面に持ってくることもできた。As an example of the easy-adhesion layer 2, an acrylic silicone emulsion solution manufactured by Shin-Etsu Chemical Co., Ltd. diluted to 5% with a solvent (1: 1 mixed solvent of toluene and acetone) is prepared by a Meyer bar or various coating methods. It is formed by coating to a thickness of 1 to 25 μm. The resin (binder) as the material of the easy-adhesion layer 2 includes polyvinyl alcohol alone or a partially saponified product thereof (trade name).
Poval), vinyl chloride-vinyl acetate copolymer, ethylene-vinyl acetate copolymer can be used, and it is only necessary to contain a few percent of silicones such as silicone oil in order to adjust the strength of adhesion. Furthermore, not only silicone oil, but also a silane coupling agent alone or a hydrolyzate thereof may be contained in several percent. (Manufactured by Toshiba Silicon Corporation) However, it is preferable to select and use a material having a small difference in the refractive index between the hologram material and the easily adhesive material. That is, in the hologram material, the photosensitive material is 8E75H manufactured by DuPont or Agfa.
It is preferable to use D as a recording material. Since these refractive indices are about 1.51 to 1.55, it is preferable to make them equal to those of the easy-adhesion layer and adjust so as not to impair the incident characteristics due to surface reflection or the like. The respective layers are laminated to form a laminated electromagnetic wave absorber 7. Further, at the construction site, a radio wave absorbing layer A with a hologram layer (reference numeral 1 in the drawing)
Was peeled off according to the peeling cut 6, but could be easily peeled off, and the radio wave absorbing layer B with the hologram layer (reference numeral 3 in the figure)
Could be brought to the outermost surface.

【００３０】[0030]

【実施例】以下、本発明について、実施例により更に説
明する。EXAMPLES The present invention will be further described below with reference to examples.

【００３１】（実施例１）図１及び図２の如き構成の電
波吸収体７を次の様にして作製した。エポキシフェノー
ル樹脂１００ｇ当たりにカーボンブラック３．０９ｇ添
加してペイントロールで混合した後、スペーサで厚みを
１．９１ｍｍに調整してホットプレスによって作製した
もの（電波吸収層）の上に、下記（２）組成のホログラ
ム層形成用塗布液をグラビアリバーズコート法により、
乾燥時の厚さが２μｍとなるように塗布し、１００℃、
１分間の条件で乾燥させて光回折構造を形成するための
樹脂層を形成した。Example 1 A radio wave absorber 7 having the structure shown in FIGS. 1 and 2 was produced as follows. After adding 3.09 g of carbon black per 100 g of the epoxy phenol resin and mixing with a paint roll, the thickness was adjusted to 1.91 mm with a spacer and prepared by hot pressing (a radio wave absorbing layer). ) The hologram layer forming coating liquid having the composition is applied by a gravure rivers coating method.
Apply so that the thickness at the time of drying becomes 2 μm,
Drying was performed for one minute to form a resin layer for forming an optical diffraction structure.

【００３２】 （２）ホログラム層形成用塗布液の組成 アクリル樹脂 ４０重量部 メラミン樹脂 １０重量部 溶剤 シクロヘキサノン ５０重量部 溶剤 メチルエチルケトン ２５重量部(2) Composition of hologram layer forming coating solution Acrylic resin 40 parts by weight Melamine resin 10 parts by weight Solvent Cyclohexanone 50 parts by weight Solvent Methyl ethyl ketone 25 parts by weight

【００３３】前記ホログラム層形成用樹脂層の上に、ホ
ログラム原版を載置し、１５０℃、５０ｋｇ／ｃｍ2 、
１分間の条件で加熱圧着してホログラムレリーフを型付
けした後、ホログラム原版を剥離してホログラムレリー
フを備えたホログラム層８を形成した。これをホログラ
ム層８付き電波吸収層Ａ（図示の符号１）とした 。A hologram master is placed on the hologram layer forming resin layer, and the hologram master is placed at 150 ° C., 50 kg / cm 2,
After forming the hologram relief by heating and pressing under the condition of 1 minute, the hologram master was peeled off to form the hologram layer 8 having the hologram relief. This was designated as a radio wave absorption layer A with a hologram layer 8 (reference numeral 1 in the drawing).

【００３４】エポキシフェノール樹脂１００ｇ当たりに
カーボンブラック２．０８ｇ添加してペイントロールで
混合した後、スペーサで厚みを３．３１ｍｍに調整して
ホットプレスによって作製したもの（電波吸収層）の上
に、上記（２）組成のホログラム層形成用塗布液をグラ
ビアリバーズコート法により、乾燥時の厚さが２μｍと
なるように塗布し、１００℃、１分間の条件で乾燥させ
てホログラム層を形成するための樹脂層を形成した。After adding 2.08 g of carbon black per 100 g of the epoxy phenol resin and mixing with a paint roll, the thickness was adjusted to 3.31 mm with a spacer, and a hot-pressed (wave-absorbing layer) was prepared. In order to form a hologram layer by applying a coating liquid for forming a hologram layer having the above composition (2) by a gravure rivers coating method so as to have a dry thickness of 2 μm and drying at 100 ° C. for 1 minute. Was formed.

【００３５】前記ホログラム層形成用樹脂層の上に、ホ
ログラム原版を載置し、１５０℃、５０ｋｇ／ｃｍ2 、
１分間の条件で加熱圧着してホログラムレリーフを型付
けした後、ホログラム原版を剥離してホログラムレリー
フを備えたホログラム層９を形成した。これをホログラ
ム層９付き電波吸収層Ｂ（図示の符号３）とした 。The hologram master is placed on the hologram layer forming resin layer, and the hologram master is placed at 150 ° C., 50 kg / cm 2,
After forming the hologram relief by heating and pressing under the condition of 1 minute, the hologram master was peeled off to form the hologram layer 9 having the hologram relief. This was designated as a radio wave absorbing layer B with a hologram layer 9 (reference numeral 3 in the drawing).

【００３６】エポキシフェノール樹脂１００ｇ当たりに
カーボンブラック２．６８ｇ添加してペイントロールで
混合した後、スペーサで厚みを２．０１ｍｍに調整して
ホットプレスによって作製したもの（電波吸収層）の上
に、上記（２）組成のホログラム層形成用塗布液をグラ
ビアリバーズコート法により、乾燥時の厚さが２μｍと
なるように塗布し、１００℃、１分間の条件で乾燥させ
てホログラム層を形成するための樹脂層を形成した。After adding 2.68 g of carbon black per 100 g of the epoxy phenol resin and mixing with a paint roll, the thickness was adjusted to 2.01 mm with a spacer, and the product was prepared by hot pressing (a radio wave absorbing layer). In order to form a hologram layer by applying a coating liquid for forming a hologram layer having the above composition (2) by a gravure rivers coating method so as to have a dry thickness of 2 μm and drying at 100 ° C. for 1 minute. Was formed.

【００３７】前記ホログラム層形成用樹脂層の上に、ホ
ログラム原版を載置し、１５０℃、５０ｋｇ／ｃｍ2 、
１分間の条件で加熱圧着してホログラムレリーフを型付
けした後、ホログラム原版を剥離してホログラムレリー
フを備えたホログラム層１０を形成した。これをホログ
ラム層１０付き電波吸収層Ｃ（図示の符号４）とした
。ホログラム層付き電波吸収層Ａ〜Ｃの角部を斜めに
切断して剥離用切り込み６を設けた。A hologram master is placed on the hologram layer forming resin layer, and the hologram master is placed at 150 ° C., 50 kg / cm 2,
The hologram relief was molded by applying heat and pressure under the condition of 1 minute, and then the hologram master was peeled off to form the hologram layer 10 having the hologram relief. This was designated as a radio wave absorbing layer C with a hologram layer 10 (reference numeral 4 in the drawing). Corners of the hologram layer-attached radio wave absorbing layers A to C were cut obliquely to provide peeling cuts 6.

【００３８】熱伝達変換層５は、日機装株式会社の商品
名 ＭＡＴＥＬＩＧＨＴ ＣＯＭＰＯＳＩＴＥ（炭素繊
維強化プラスチック）０．３ｍｍ厚さをそのまま用い
た。ホログラム層付き電波吸収層Ａ〜Ｃと熱伝達変換層
５の各層間には易接着層２を設けた。As the heat transfer conversion layer 5, a 0.3 mm thick MATELIGHT COMPOSITE (carbon fiber reinforced plastic) manufactured by Nikkiso Co., Ltd. was used. The easy-adhesion layer 2 was provided between each layer of the radio wave absorption layers A to C with hologram layers and the heat transfer conversion layer 5.

【００３９】易接着層２は、信越化学株式会社製のアク
リルシリコーンエマルジョン溶液を溶媒（トルエンとア
セトンの１：１混合溶媒）で５％に希釈したものをメイ
ヤーバーによって５μｍの厚さに塗布して形成した。The easy-adhesion layer 2 was prepared by diluting an acrylic silicone emulsion solution manufactured by Shin-Etsu Chemical Co., Ltd. to 5% with a solvent (a mixed solvent of 1: 1 toluene and acetone) to a thickness of 5 μm using a Meyer bar. Formed.

【００４０】各層を積層して貼り合わせ電波吸収体７を
構成させた。さらにホログラム層付き電波吸収層Ａ（図
示の符号１）を剥離用切り込み６に従って剥離したが、
容易に剥離でき、ホログラム層付き電波吸収層Ｂ（図示
の符号３）上のホログラム層を最表面に持ってくること
ができた。The respective layers were laminated to form a laminated electromagnetic wave absorber 7. Further, the hologram layer-attached radio wave absorbing layer A (reference numeral 1 in the drawing) was peeled off according to the peeling cut 6,
The hologram layer was easily peeled off, and the hologram layer on the hologram layer-attached radio wave absorption layer B (reference numeral 3 in the drawing) could be brought to the outermost surface.

【００４１】電波吸収特性はアドバンテスト法によって
行なった。電波吸収層Ａ、Ｂ、Ｃで構成の場合には１Ｇ
Ｈｚ〜２０ＧＨｚ（測定限界のため）においてほぼフラ
ットに−２０ｄＢの吸収損失を確認した。さらに、電波
吸収層Ｂ、Ｃの場合には５ＧＨｚ〜２０ＧＨｚ（測定限
界のため）においてほぼフラットに−２５ｄＢの吸収損
失を確認した。さらに、電波吸収層Ｃの場合には１５Ｇ
Ｈｚ〜２０ＧＨｚ（測定限界のため）において鋭い吸収
ピークが見られ、−３５ｄＢの吸収損失を確認した。The radio wave absorption characteristics were measured by the Advantest method. 1G in the case of the structure composed of the radio wave absorption layers A, B and C
An absorption loss of −20 dB was confirmed almost flat at a frequency of 20 Hz to 20 GHz (for a measurement limit). Furthermore, in the case of the radio wave absorbing layers B and C, an absorption loss of -25 dB was confirmed to be almost flat at 5 GHz to 20 GHz (due to the measurement limit). Further, in the case of the radio wave absorption layer C, 15 G
A sharp absorption peak was observed at Hz to 20 GHz (due to the measurement limit), and an absorption loss of -35 dB was confirmed.

【００４２】[0042]

【発明の効果】以上説明したように、この発明によれ
ば各電波吸収層にホログラム層を設けたことにより、斜
めからの電波の入射でも極めて吸収効率が良い（斜入射
特性の良い）新規な構成となる電磁波吸収体を提供でき
る。さらには、同一ロットで製造ができ、安価な電波吸
収体を提供することが容易になる。同一ロットで構成さ
れているので製造工程を一括管理できる。 施工場所における電磁波到達度合いに応じて最適な電
磁波吸収面を容易に作り出すことが可能となる。例えば
屋内壁面への施工の場合には、窓面からの入射と天井面
では電磁波の散乱・反射度合いが異なる。その様な状況
に対しても周波数等の電波測定後に最適な電波吸収面ま
で剥離してその場で施工すればよい。また、施工面積に
もよるが、壁面の様な場合には予め大きさは規格化され
ているので、不要の電波吸収層は巻き取り回収すること
で再利用が可能となる。As described above, according to the present invention, a hologram layer is provided on each radio wave absorbing layer, so that a novel absorption efficiency (having good oblique incidence characteristics) is obtained even with oblique radio wave incidence. An electromagnetic wave absorber having a configuration can be provided. Furthermore, it can be manufactured in the same lot, and it becomes easy to provide an inexpensive radio wave absorber. Since they are composed of the same lot, the manufacturing process can be managed collectively. It is possible to easily create an optimal electromagnetic wave absorbing surface according to the degree of arrival of electromagnetic waves at the construction site. For example, in the case of construction on an indoor wall surface, the degree of scattering / reflection of electromagnetic waves differs between the incidence from the window surface and the ceiling surface. Even in such a situation, after measuring the radio waves such as the frequency, it is sufficient to peel off to the optimum radio wave absorbing surface and to perform the work on the spot. In addition, although it depends on the construction area, in the case of a wall surface, the size is standardized in advance, so that unnecessary radio wave absorbing layers can be reused by winding and collecting them.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明の電波吸収体の一実施例の断面図であ
る。FIG. 1 is a sectional view of one embodiment of a radio wave absorber of the present invention.

【図２】本発明の電波吸収体の一実施例（図１）の構成
を示す斜視図である。FIG. 2 is a perspective view showing a configuration of an embodiment (FIG. 1) of the radio wave absorber of the present invention.

【符号の説明】[Explanation of symbols]

１ ホログラム層付き電波吸収層Ａ ２ 易接着層 ３ ホログラム層付き電波吸収層Ｂ ４ ホログラム層付き電波吸収層Ｃ ５ 熱伝達変換層 ６ 剥離用切り込み ７ 電波吸収体 ８ ホログラム層 ９ ホログラム層 １０ ホログラム層 REFERENCE SIGNS LIST 1 radio wave absorbing layer with hologram layer A 2 easy adhesion layer 3 radio wave absorbing layer with hologram layer B 4 radio wave absorbing layer with hologram layer 5 heat transfer conversion layer 6 notch for peeling 7 radio wave absorber 8 hologram layer 9 hologram layer 10 hologram layer

───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2E001 DH01 FA03 GA03 GA24 GA42 HA20 HD11 HD13 HE01 JA00 JA22 JA24 JA29 JB01 JB02 JC00 JC01 JC02 JC03 JC06 JC07 JD02 JD04 JD05 4F100 AA01C AA37 AD11 AK01C AK25 AK33 AK36 BA03 BA10A BA10C CB00 DG01C DH02C HB08A HB08B JD14A JD14B JJ01C JL11 JL16 5E321 AA41 BB02 BB23 BB24 BB25 GG11 GH03  ──────────────────────────────────────────────────続 き Continued on the front page F-term (reference) 2E001 DH01 FA03 GA03 GA24 GA42 HA20 HD11 HD13 HE01 JA00 JA22 JA24 JA29 JB01 JB02 JC00 JC01 JC02 JC03 JC06 JC07 JD02 JD04 JD05 4F100 AA01C AA37 AD11 AK01 BAK AK25 BA33 CB01 BAK DH02C HB08A HB08B JD14A JD14B JJ01C JL11 JL16 5E321 AA41 BB02 BB23 BB24 BB25 GG11 GH03

Claims (3)

【特許請求の範囲】[Claims] 【請求項１】 ２層以上の電波吸収層と、熱伝達変換層
とから構成された電波吸収体であって、前記各電波吸収
層側にホログラム層を設けたことを特徴とする電波吸収
体。1. A radio wave absorber comprising at least two radio wave absorption layers and a heat transfer conversion layer, wherein a hologram layer is provided on each of the radio wave absorption layers. . 【請求項２】 前記電波吸収体の各層間に易接着層を設
けたことを特徴とする請求項１記載の電波吸収体。2. The radio wave absorber according to claim 1, wherein an easy adhesion layer is provided between each layer of the radio wave absorber. 【請求項３】 熱伝達変換層が有機繊維や無機繊維を用
いた高熱伝導性樹脂シートであることを特徴とする請求
項１又は２に記載の電波吸収体。3. The radio wave absorber according to claim 1, wherein the heat transfer conversion layer is a high heat conductive resin sheet using organic fibers or inorganic fibers.