JP2002079747A - Polyester film easily bondable with ink image accepting layer - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a polyester film easily bondable with an ink image accepting layer, which is excellent in opacifying properties, water resistant adhesion to the water-based ink image accepting layer of an ink jet printer or the like, a conveyability, antistatic properties and useful for an image accepting paper. SOLUTION: On one side of a polyester film, on the other side of which an antistatic coating film is provided, a coating film easily bondable with the ink image accepting layer is provided for forming a laminating film or the polyester film easily bondable with the ink image accepting layer. The coating film easily bondable with the ink image accepting layer is mainly made of a composition consisting of 30 to 80 wt.% of a copolyester (A) having a secondary transition point of 20 to 90 deg.C, 15 to 45 wt.% of a polyvinyl alcohol (B) having a saponification degree of 80 to 90 mol%, 3 to 25 wt.% of particles (C) having an average particle diameter of 20 to 80 nm and 5 to 20 wt.% of a compound (D) represented by formula (I) under the condition that the surface energy of 50 to 90 mN/m. In the formula (I), R represents formulae (II), (III) and (IV).

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明はインク受像層易接着
ポリエステルフィルムに関し、更に詳しくは隠蔽性に優
れ、インクジェットプリンター等の水性インク受像層に
対する耐水接着性に優れ、かつ搬送性、帯電防止性に優
れた、受像紙用に有用なインク受像層易接着ポリエステ
ルフィルムに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyester film having a good adhesion to an ink image-receiving layer, and more particularly to an excellent concealing property, excellent water-resistant adhesion to an aqueous ink image-receiving layer of an ink jet printer or the like, and excellent transportability and antistatic property. The present invention relates to an excellent ink-receiving layer adhesive polyester film useful for an image-receiving paper.

【０００２】[0002]

【従来の技術】ポリエチレンテレフタレートフイルムに
代表されるポリエステルフィルムは、受像紙用フィルム
のベースフイルムとして従来より広く使用されている。
近年、カラープリンターの需要に伴い、インクジェット
方式等の新しい印字方式が発展してきた。このような印
字方式用の受像紙用フィルムでは、特開昭６４―３６４
７９号公報、特開平１―９５０９１号公報で提案されて
いるように、フィルム上にインク受像層の形成が必要と
なる。このインク受像層には多孔質でインクの吸収性が
良好なものが使用されるが、このインク受像層はベース
フイルムとして用いるポリエステルフィルムに対する接
着性が乏しい。2. Description of the Related Art A polyester film represented by a polyethylene terephthalate film has been widely used as a base film of a film for an image receiving paper.
In recent years, with the demand for color printers, new printing methods such as an ink jet method have been developed. Such a film for an image receiving paper for a printing system is disclosed in JP-A-64-364.
No. 79 and Japanese Patent Application Laid-Open No. 1-95091, it is necessary to form an ink image receiving layer on a film. The ink image receiving layer is porous and has good ink absorbency, but the ink image receiving layer has poor adhesion to a polyester film used as a base film.

【０００３】[0003]

【発明が解決しようとする課題】本発明の目的は、イン
ク受像層との接着性、隠蔽性に優れ、かつ搬送性、帯電
防止性を兼備した、インクジェットプリンター用受像紙
などに有用なインク受像層易接着ポリエステルフィルム
を提供することにある。SUMMARY OF THE INVENTION It is an object of the present invention to provide an ink receiving layer which is excellent in adhesiveness and concealing property with an ink receiving layer, and has both transportability and antistatic property and is useful for an image receiving paper for an ink jet printer. It is an object of the present invention to provide a layer-adhesive polyester film.

【０００４】[0004]

【課題を解決するための手段】本発明のかかる目的は、
本発明によれば、ポリエステルフィルムの片面にインク
受像層易接着塗膜を設け、もう一方の面に帯電防止性塗
膜を設けた積層フィルムであって、インク受像層易接着
塗膜は二次転移点が２０〜９０℃であるコポリエステル
（Ａ）３０〜８０重量％、ケン化度８０〜９０ｍｏｌ％
のポリビニルアルコール（Ｂ）１５〜４５重量％、平均
粒径が２０〜８０ｎｍの微粒子（Ｃ）３〜２５重量％及
び下記式（Ｉ）で示される化合物（Ｄ）５〜２０重量％
からなる組成物を主成分とし、該インク受像層易接着塗
膜の表面エネルギーが５０〜７０ｍＮ／ｍであることを
特徴とするインク受像層易接着ポリエステルフィルムに
より達成できる。SUMMARY OF THE INVENTION The object of the present invention is as follows.
According to the present invention, a polyester film is provided with an ink-receiving layer easy-adhesion coating film on one surface and a laminated film provided with an antistatic coating film on the other surface. Copolyester (A) having a transition point of 20 to 90 ° C, 30 to 80% by weight, saponification degree 80 to 90 mol%
15 to 45% by weight of polyvinyl alcohol (B), 3 to 25% by weight of fine particles (C) having an average particle diameter of 20 to 80 nm, and 5 to 20% by weight of a compound (D) represented by the following formula (I).
And a surface energy of the ink image-receiving layer easy-adhesion coating film is 50 to 70 mN / m.

【０００５】[0005]

【化３】 Embedded image

【０００６】[0006]

【発明の実施の形態】以下、本発明を詳細に説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail.

【０００７】［ポリエステルフィルム］本発明において
ポリエステルフィルムを構成するポリエステルは、ジカ
ルボン酸成分とグリコール成分からなるポリエステルで
あり、例えばテレフタル酸、イソフタル酸、２，６−ナ
フタレンジカルボン酸、４，４′−ジフェニルジカルボ
ン酸等の芳香族ジカルボン酸成分と、例えばエチレング
リコール、１，４−ブタンジオール、１，４−シクロヘ
キサンジメタノール、１，６−ヘキサンジオール等のグ
リコール成分とから構成されるポリエステルが好まし
く、特にポリエチレンテレフタレート、ポリエチレン−
２，６−ナフタレンジカルボキシレートが好ましい。ま
た、上記成分等の共重合ポリエステルであっても良い。[Polyester Film] In the present invention, the polyester constituting the polyester film is a polyester comprising a dicarboxylic acid component and a glycol component, such as terephthalic acid, isophthalic acid, 2,6-naphthalenedicarboxylic acid, and 4,4'-polyester. Polyester composed of an aromatic dicarboxylic acid component such as diphenyldicarboxylic acid and a glycol component such as ethylene glycol, 1,4-butanediol, 1,4-cyclohexanedimethanol, and 1,6-hexanediol is preferable. Especially polyethylene terephthalate, polyethylene
2,6-Naphthalenedicarboxylate is preferred. Further, a copolymerized polyester such as the above components may be used.

【０００８】ポリエステルにはフィルムを製造する際の
巻取性や、インク受像層等を塗設する際のフィルムの搬
送性等を良くするため、必要に応じて滑剤としての有機
又は無機の微粒子を含有させることが好ましい。かかる
微粒子としては、炭酸カルシウム、酸化カルシウム、酸
化アルミニウム、カオリン、酸化珪素、酸化亜鉛、架橋
アクリル樹脂粒子、架橋ポリスチレン樹脂粒子、尿素樹
脂粒子、メラミン樹脂粒子、架橋シリコーン樹脂粒子等
が例示される。また、微粒子以外にも着色剤、帯電防止
剤、酸化防止剤、潤滑剤、触媒、ポリエチレン、ポリプ
ロピレン、エチレン―プロピレン―ポリマー、オレフィ
ン系アイオノマーのような他の樹脂等も透明性を損なわ
ない範囲で任意に含有させることができる。If necessary, organic or inorganic fine particles as a lubricant may be added to the polyester to improve the winding property in producing the film and the transport property of the film in coating the ink image receiving layer. It is preferable to include them. Examples of such fine particles include calcium carbonate, calcium oxide, aluminum oxide, kaolin, silicon oxide, zinc oxide, crosslinked acrylic resin particles, crosslinked polystyrene resin particles, urea resin particles, melamine resin particles, crosslinked silicone resin particles, and the like. Also, besides fine particles, colorants, antistatic agents, antioxidants, lubricants, catalysts, polyethylene, polypropylene, ethylene-propylene-polymer, other resins such as olefinic ionomers, etc., as long as the transparency is not impaired. It can be arbitrarily contained.

【０００９】また、本発明におけるポリエステルフィル
ムには、帯電防止性塗膜として、ポリカチオンポリマー
からなる帯電防止剤（Ｅ）５〜５０重量％と、ポリエス
テル樹脂（Ｆ−１）、アクリル樹脂（Ｆ−２）からなる
群から選ばれた少なくとも一種のバインダー樹脂（Ｆ）
４０〜８５重量％を含む塗膜を設け、光沢度が６０度以
上、光線透過率が２０％以下でありかつ白色であるポリ
エステルフィルム（白色ポリエステルフィルム）を用い
ることが好ましい。この白色ポリエステルフィルムは、
ポリエステルに白色顔料、例えば酸化チタン及び／また
は硫酸バリウムを例えば５〜２０重量％含有させること
により得ることができる。また、白色ポリエステルフィ
ルムは、受像紙として用いるときの印字物の鮮映性より
光沢度が５０以上で、印字物の意匠性から、その光線透
過率が２０％以下であることが好ましい。In the polyester film of the present invention, as an antistatic coating film, 5 to 50% by weight of an antistatic agent (E) comprising a polycationic polymer, a polyester resin (F-1) and an acrylic resin (F -2) at least one binder resin (F) selected from the group consisting of:
It is preferable to provide a coating film containing 40 to 85% by weight, and use a white polyester film (white polyester film) having a gloss of 60 ° or more and a light transmittance of 20% or less and white. This white polyester film
The polyester can be obtained by adding a white pigment, for example, titanium oxide and / or barium sulfate, for example, in an amount of 5 to 20% by weight. In addition, the white polyester film preferably has a gloss of 50 or more from the sharpness of the printed matter when used as an image receiving paper, and preferably has a light transmittance of 20% or less from the design of the printed matter.

【００１０】本発明におけるポリエステルフィルムは、
１５０℃で３０分間保持したときの熱収縮率が１％以下
の二軸延伸フィルムであることが、ポリエステルフィル
ムを受像紙に用いた際に寸法安定性が良好であり、印字
のずれ等を抑制できるため好ましい。このような熱収縮
率を有する二軸延伸フィルムは、例えば、二軸延伸後に
熱固定やポリエステルのＴｇ以上の温度での熱処理によ
りフィルムの密度を例えば１．３９０ｇ／ｃｍ³以上と
することにより得ることができる。[0010] The polyester film in the present invention comprises:
A biaxially stretched film having a heat shrinkage of 1% or less when held at 150 ° C. for 30 minutes has good dimensional stability when a polyester film is used as an image receiving paper, and suppresses printing misalignment and the like. It is preferable because it is possible. A biaxially stretched film having such a heat shrinkage is obtained by, for example, setting the density of the film to 1.390 g / cm ³ or more by heat setting or heat treatment at a temperature equal to or higher than Tg of the polyester after biaxial stretching. be able to.

【００１１】［インク受像層易接着塗膜］本発明におい
ては、ポリエステルフィルムにインク受像層易接着塗膜
としてコポリエステル（Ａ）、ポリビニルアルコール
（Ｂ）、微粒子（Ｃ）及び下記式（Ｉ）で示される化合
物（Ｄ）を主成分とする塗膜を積層する。In the present invention, a copolyester (A), a polyvinyl alcohol (B), a fine particle (C) and a compound represented by the following formula (I) are used as the ink-receiving layer easily adhesive coating on a polyester film. Is laminated with a compound (D) as a main component.

【００１２】[0012]

【化４】 Embedded image

【００１３】このインク受像層塗膜を形成する成分に用
いるコポリエステル（Ａ）は、ポリカルボン酸成分とヒ
ドロキシ化合物成分からなる共重合ポリエステルであ
り、テレフタル酸、イソフタル酸、２，６−ナフタレン
ジカルボン酸、ヘキサヒドロテレフタル酸、４，４′−
ジフェニルジカルボン酸、フェニルインダンジカルボン
酸、アジピン酸、セバシン酸、５−スルホイソフタル
酸、トリメリット酸、ジメチロールプロピオン酸等のポ
リカルボン酸成分及び５−Ｎａスルホイソフタル酸、５
−Ｋスルホイソフタル酸、５−Ｋスルホテレフタル酸等
のスルホン酸塩基を有するジカルボン酸成分と、エチレ
ングリコール、ジエチレングリコール、ネオペンチレン
グコール、１，４−ブタンジオール、１，６−ヘキサン
ジオール、１，４−シクロヘキサンジメタノール、グリ
セリン、トリメチロールプロパン、ビスフェノール−Ａ
のアルキレンオキシド付加物等のヒドロキシ化合物成分
とから構成されるポリエステルであって、水溶液、水分
散液又は乳化液として使用される。The copolyester (A) used as the component for forming the ink image-receiving layer coating film is a copolymerized polyester comprising a polycarboxylic acid component and a hydroxy compound component, and is terephthalic acid, isophthalic acid, 2,6-naphthalenedicarboxylic acid. Acid, hexahydroterephthalic acid, 4,4'-
Polycarboxylic acid components such as diphenyldicarboxylic acid, phenylindanedicarboxylic acid, adipic acid, sebacic acid, 5-sulfoisophthalic acid, trimellitic acid, dimethylolpropionic acid, and 5-Na sulfoisophthalic acid;
-K sulfoisophthalic acid, a dicarboxylic acid component having a sulfonic acid group such as 5-K sulfoterephthalic acid, ethylene glycol, diethylene glycol, neopentylene glycol, 1,4-butanediol, 1,6-hexanediol, 4-cyclohexanedimethanol, glycerin, trimethylolpropane, bisphenol-A
And a hydroxy compound such as an alkylene oxide adduct of the formula (I), which is used as an aqueous solution, aqueous dispersion or emulsion.

【００１４】コポリエステル（Ａ）の二次転移点（Ｔ
ｇ）は２０〜９０℃、好ましくは２５〜８０℃である。
Ｔｇが２０℃未満ではフィルムがブロッキングしやす
く、一方９０℃を超えるとフィルムの削れ性や接着性が
低下するので好ましくない。The secondary transition point (T) of the copolyester (A)
g) is from 20 to 90C, preferably from 25 to 80C.
If the Tg is less than 20 ° C., the film is likely to be blocked, while if it exceeds 90 ° C., the abrasion and adhesion of the film are undesirably reduced.

【００１５】また、コポリエステル（Ａ）は、親水性を
付与するためのスルホン酸塩基を有するジカルボン酸成
分が、分子内の全カルボン酸成分に対し１〜１６モル％
のものであり、好ましくは１．５〜１４モル％のもので
ある。スルホン酸塩基を有するジカルボン酸成分が１モ
ル％未満ではコポリエステル（Ａ）の親水性が不足し、
一方１６モル％を超えると塗膜の耐湿性が低下するので
好ましくない。In the copolyester (A), the dicarboxylic acid component having a sulfonic acid group for imparting hydrophilicity is present in an amount of 1 to 16 mol% based on all carboxylic acid components in the molecule.
And preferably 1.5 to 14 mol%. When the dicarboxylic acid component having a sulfonic acid group is less than 1 mol%, the hydrophilicity of the copolyester (A) is insufficient,
On the other hand, if it exceeds 16 mol%, the moisture resistance of the coating film is undesirably reduced.

【００１６】上記インク受像層易接着塗膜を形成する成
分として用いるポリビニルアルコール（Ｂ）は、ケン化
度が８０〜９０ｍｏｌ％である必要がある。このケン化
度が８０ｍｏｌ％未満では塗膜の耐湿性が低下し、一方
９０ｍｏｌ％を超えるとインク受像層に対する接着性が
低下するので好ましくない。The polyvinyl alcohol (B) used as a component for forming the above-mentioned ink-receiving layer easily adhesive coating film must have a saponification degree of 80 to 90 mol%. If the degree of saponification is less than 80 mol%, the moisture resistance of the coating film is reduced. On the other hand, if it exceeds 90 mol%, the adhesion to the ink receiving layer is undesirably reduced.

【００１７】上記インク受像層易接着塗膜を形成する成
分として用いる微粒子（Ｃ）は有機又は無機の微粒子で
あり、粒径が２０〜８０ｎｍのものである。かかる微粒
子としては、炭酸カルシウム、酸化カルシウム、酸化ア
ルミニウム、カオリン、酸化珪素、酸化亜鉛、架橋アク
リル樹脂粒子、架橋ポリスチレン樹脂粒子、メラミン樹
脂粒子、架橋シリコーン樹脂粒子等が例示される。該微
粒子の粒径が２０ｎｍ未満ではフィルムがブロッキング
しやすく、一方８０ｎｍを超えると削れ性が低下するの
で好ましくない。The fine particles (C) used as a component for forming the above-mentioned ink image-receiving layer easily adhesive coating film are organic or inorganic fine particles having a particle diameter of 20 to 80 nm. Examples of such fine particles include calcium carbonate, calcium oxide, aluminum oxide, kaolin, silicon oxide, zinc oxide, crosslinked acrylic resin particles, crosslinked polystyrene resin particles, melamine resin particles, crosslinked silicone resin particles, and the like. If the particle size of the fine particles is less than 20 nm, the film is likely to be blocked, while if it exceeds 80 nm, the shaving property is undesirably reduced.

【００１８】さらに、上記インク受像層易接着塗膜を形
成する成分として用いる化合物（Ｄ）は前記式（Ｉ）で
示される化合物であり、これ以外のエポキシ系化合物で
は、インク受像層との接着性が不十分となる。Further, the compound (D) used as a component for forming the above-mentioned ink image-receiving layer easy-adhesion coating film is a compound represented by the above formula (I). Performance becomes insufficient.

【００１９】本発明において、インク受像層易接着塗膜
を構成する各成分、コポリエステル（Ａ）、ポリビニル
アルコール（Ｂ）、微粒子（Ｃ）、及び化合物（Ｄ）の
配合割合は、コポリエステル（Ａ）３０〜８０重量％、
ポリビニルアルコール（Ｂ）１５〜４５重量％、微粒子
（Ｃ）３〜３５重量％、化合物（Ｄ）５〜２０重量％で
ある。成分（Ａ）の割合が３０重量％未満ではポリエス
テルフィルムとの接着性が不足し、一方８０重量％を超
えるとインク受像層との接着性が低下するので好ましく
ない。成分（Ｂ）の割合が１５重量％未満ではインク受
像層との接着性が不足し、一方４５重量％を超えるとフ
ィルムの耐ブロッキング性が低下するので好ましくな
い。また、成分（Ｃ）の割合が３重量％未満ではフィル
ムの滑性（搬送性）が不足し、一方２５重量％をこえる
と削れ性が低下するので好ましくない。成分（Ｄ）の割
合が５重量％未満ではインクジェットプリンターでの印
刷後のインク受像層との接着性が不足し、一方２０重量
％を超えると耐ブロッキング性の低下、ポリエステルフ
ィルムとの接着性が低下するため好ましくない。In the present invention, the components constituting the ink-receiving layer easy-adhesion coating film, the copolyester (A), the polyvinyl alcohol (B), the fine particles (C), and the compound (D) are compounded in the copolyester ( A) 30-80% by weight,
The content is 15 to 45% by weight of polyvinyl alcohol (B), 3 to 35% by weight of fine particles (C), and 5 to 20% by weight of compound (D). If the proportion of the component (A) is less than 30% by weight, the adhesion to the polyester film is insufficient, while if it exceeds 80% by weight, the adhesion to the ink image receiving layer is undesirably reduced. If the proportion of the component (B) is less than 15% by weight, the adhesion to the ink image-receiving layer is insufficient, while if it exceeds 45% by weight, the blocking resistance of the film is undesirably reduced. On the other hand, if the proportion of the component (C) is less than 3% by weight, the lubricity (transportability) of the film is insufficient, while if it exceeds 25% by weight, the shaving property is undesirably reduced. When the proportion of the component (D) is less than 5% by weight, the adhesion to the ink image-receiving layer after printing with an ink jet printer is insufficient. On the other hand, when the proportion exceeds 20% by weight, the blocking resistance is reduced and the adhesion to the polyester film is poor. It is not preferable because it decreases.

【００２０】また、本発明におけるインク受像層易接着
塗膜は、その表面エネルギーが５０〜７０ｍＮ／ｍであ
ることが必要であり、特に５２〜６５ｍＮ／ｍであるこ
とが好ましい。この表面エネルギーが５０ｍＮ／ｍ未満
であると、水性インク受像層の塗工性及び接着性が不良
となり、７０ｍＮ／ｍを超えると基体であるポリエステ
ルフィルムとの密着性が不足し、塗膜の耐湿性が不足す
ることがあるため好ましくない。Further, the surface energy of the ink-receiving layer easy-adhesion coating film in the present invention needs to be 50 to 70 mN / m, and particularly preferably 52 to 65 mN / m. If the surface energy is less than 50 mN / m, the coating properties and adhesiveness of the aqueous ink image-receiving layer will be poor, and if it exceeds 70 mN / m, the adhesion to the polyester film as the substrate will be insufficient, and the moisture resistance of the coating film will be insufficient. It is not preferable because the property may be insufficient.

【００２１】表面エネルギーが５０〜７０ｍＮ／ｍのイ
ンク受像層易接着塗膜は、コポリエステル（Ａ）、ポリ
ビニルアルコール（Ｂ）、微粒子（Ｃ）及び化合物
（Ｄ）が本発明の範囲であるインク受像層易接着塗膜
を、例えば０．０２〜１μｍの厚さで積層することによ
り得ることができる。The ink-receiving layer easily adhesive coating film having a surface energy of 50 to 70 mN / m is an ink in which the copolyester (A), polyvinyl alcohol (B), fine particles (C) and compound (D) are within the scope of the present invention. It can be obtained by laminating the image-receiving layer easily adhesive coating film, for example, with a thickness of 0.02 to 1 μm.

【００２２】［帯電防止性塗膜］帯電防止性塗膜（制電
性塗膜）として、塗膜中に低分子型、または高分子型の
帯電防止剤を含有する塗膜が知られている。低分子型の
帯電防止剤としては、スルホン酸塩基を有する長鎖アル
キル化合物（特開平４−２８７２８号）等のような界面
活性剤型のアニオン系帯電防止剤が知られており、また
高分子型の帯電防止剤としては、主鎖にイオン化された
窒素元素を有するポリマー（特開平３−２５５１３９
号、特開平４−２８８１２７号、特開平６−３２０３９０
号）や、スルホン酸塩基変性ポリスチレン（特開平５−
３２０３９４号）等が知られている。[Antistatic coating film] As an antistatic coating film (antistatic coating film), a coating film containing a low-molecular type or high-molecular type antistatic agent in the coating film is known. . As the low molecular weight antistatic agent, a surfactant type anionic antistatic agent such as a long chain alkyl compound having a sulfonate group (JP-A-4-28728) is known. Examples of the antistatic agent of the type include polymers having an ionized nitrogen element in the main chain thereof (JP-A-3-255139).
JP-A-4-288127, JP-A-6-320390
No.) and sulfonic acid group-modified polystyrene (Japanese Unexamined Patent Publication No.
No. 320394) is known.

【００２３】しかしながら、低分子型の帯電防止剤を用
いた帯電防止性塗膜では、帯電防止剤の一部が塗膜中を
移動して界面に集積しフィルムの反対面等に移行する問
題や、帯電防止性が経時的に低下するという問題があ
る。一方、高分子型の帯電防止剤を用いた帯電防止性塗
膜では、良好な帯電防止性を得るために多量の帯電防止
剤の配合が必要であり、膜厚の厚い帯電防止性塗膜を形
成させることが必要であるため経済的でない。また、製
品にならなかった屑フィルム（例えば、製造工程で切断
除去したフィルム端部等）を回収し、フィルム製造用の
再生材料として使用すると、溶融製膜の際に該再生材料
中に含まれる塗膜成分が熱劣化し、得られたフィルムが
著しく着色し実用性に欠ける（回収性が劣る）ものとな
る等の問題が生じる。However, in the case of an antistatic coating film using a low-molecular type antistatic agent, there is a problem that a part of the antistatic agent moves in the coating film, accumulates at the interface, and migrates to the opposite surface of the film. In addition, there is a problem that the antistatic property decreases with time. On the other hand, in the case of an antistatic coating film using a polymer type antistatic agent, a large amount of an antistatic agent is required to obtain good antistatic properties, and a thick antistatic coating film is required. It is not economical because it needs to be formed. In addition, when a scrap film that has not become a product (for example, a film end portion cut and removed in a manufacturing process) is collected and used as a reclaimed material for film production, it is included in the reclaimed material during melt film formation. There are problems such as the coating film components being thermally degraded and the resulting film being markedly colored and lacking practicality (recoverability is poor).

【００２４】更に、フィルム同士が剥離し難い（ブロッ
キングする）、塗膜が削れ易い等の欠点が生じ、その解
決が望まれている。これらの問題より、本発明で使用さ
れる帯電防止剤（Ｅ）は、ポリカチオンポリマーが好ま
しい。ポリカチオンポリマーとしては、例えば、下記式
（II）で示される構造の繰り返し単位を主成分とする化
合物が挙げられる。Further, disadvantages such as difficulty in peeling (blocking) between the films and easiness of shaving of the coating film occur, and it is desired to solve them. From these problems, the antistatic agent (E) used in the present invention is preferably a polycationic polymer. Examples of the polycation polymer include a compound having a repeating unit having a structure represented by the following formula (II) as a main component.

【００２５】[0025]

【化５】 Embedded image

【００２６】ただし、式中のＲ¹、Ｒ²はそれぞれＨ又は
ＣＨ₃、Ｒ³は炭素数が２〜１０のアルキレン基、Ｒ⁴、
Ｒ⁶はそれぞれ炭素数が１〜５の飽和炭化水素基、Ｒ⁶は
炭素数が２〜１０のアルキレン基、ｐは１〜２０の数、
ｑは１〜４０の数、Ｙ^-はハロゲンイオン、モノもしく
はポリハロゲン化アルキルイオン、ナイトレートイオ
ン、サルフェートイオン、アルキルサルフェートイオ
ン、スルホネートイオン又はアルキルスルホネートイオ
ンである。Wherein R ¹ and R ² are each H or CH ₃ , R ³ is an alkylene group having 2 to 10 carbon atoms, R ⁴ ,
R ⁶ is a saturated hydrocarbon group having 1 to 5 carbon atoms, R ⁶ is an alkylene group having 2 to 10 carbon atoms, p is a number of 1 to 20,
q is a number of 1 to 40; Y ^- is a halogen ion, mono- or polyhalogenated alkyl ion, nitrate ion, sulfate ion, alkyl sulfate ion, sulfonate ion or alkyl sulfonate ion.

【００２７】前記帯電防止剤のうち、前記式（II）中の
Ｙ^-がＲ⁷ＳＯ₃ ^-で示されるアルキルスルホネートイオン
（ただし、Ｒ⁷は炭素数が１〜５の飽和炭化水素基）で
あり、−（ＯＲ³）ｐ−のＲ³がエチレン基であり、ｐが
１〜２０の数、−（Ｒ⁶Ｏ）ｑ−のＲ⁶がエチレン基であ
り、ｑが１〜４０の数であるものは、塗膜とポリエステ
ルフイルムとの接着性、塗膜の耐熱性が良好であり、特
に制電性に優れるので好ましい。[0027] Among the anti-static agent, wherein in formula (II) Y ^- alkyl sulfonate ion represented by (wherein, saturated hydrocarbon group of R ⁷ has a carbon number 1 to 5) ^- is R ⁷ SO ₃ Yes, - (OR ³⁾ p- of R ³ is an ethylene group, the number of p is ^{1~20, - (R 6 O)} R 6 in q- is an ethylene group, the number of q is from 1 to 40 Is preferred because the adhesiveness between the coating film and the polyester film and the heat resistance of the coating film are good, and particularly, the antistatic property is excellent.

【００２８】前記帯電防止剤は、例えば下記の方法で好
ましく製造することができる。すなわち、アクリル酸エ
ステルモノマーを、乳化重合により、重量平均分子量２
０００〜１０００００のポリアクリル酸エステルとし、
次いでＮ，Ｎ−ジアルキルアミノアルキルアミン（例え
ば、Ｎ，Ｎ−ジメチルアミノプロピルアミン、Ｎ，Ｎ−
ジエチルアミノプロピルアミン等）と反応させてアミド
化し、最後に４級ヒドロキシアルキル化反応を行わせて
４級カチオン対を導入することで製造できる。The antistatic agent can be preferably produced, for example, by the following method. That is, the acrylate monomer is subjected to emulsion polymerization to obtain a weight average molecular weight of 2
000 to 100,000 polyacrylate and
Then, N, N-dialkylaminoalkylamine (for example, N, N-dimethylaminopropylamine, N, N-
Amidation by reaction with diethylaminopropylamine or the like) and finally a quaternary hydroxyalkylation reaction to introduce a quaternary cation pair.

【００２９】帯電防止剤の平均分子量（数平均分子量）
は任意であるが、３０００〜３０００００、更に５００
０〜１０００００であることが好ましい。この平均分子
量が３０００未満であると、帯電防止剤の背面転写性が
悪化する傾向があり、一方平均分子量が３０００００を
超えると、水性塗液の粘度が高くなりすぎフィルムに均
一に塗布し難くなるため好ましくない。Average molecular weight of antistatic agent (number average molecular weight)
Is optional, but 3000 to 300,000, and further 500
It is preferably from 0 to 100,000. When the average molecular weight is less than 3,000, the back transferability of the antistatic agent tends to deteriorate, while when the average molecular weight exceeds 300,000, the viscosity of the aqueous coating solution becomes too high, making it difficult to uniformly coat the film. Therefore, it is not preferable.

【００３０】上記の制電性被膜に用いる帯電防止剤は、
前記式（II）中のＹ^-が、ＣＨ₃ＳＯ₃ ^-、Ｃ₂Ｈ₅ＳＯ₃ ^-、ま
たはＣ₃Ｈ₇ＳＯ₃ ^-であり、−(ＯＲ³)ｑ−が−（ＯＣ
₂Ｈ₄）ｐ−であり、かつｐが１〜５であることが好まし
い。また、−（Ｒ⁶Ｏ）ｑ−が−（Ｃ₂Ｈ₄Ｏ）ｑ−であ
り、かつｑが１〜１０であることが好ましい。The antistatic agent used for the antistatic film is as follows:
Formula (II) Y in ^{- _{is, CH 3 SO 3 -, C}} 2 H 5 SO 3 -, or C ₃ H ₇ SO ₃ ^- a and, - (OR ³⁾ q- is - (OC
₂ H ₄ ) p−, and p is preferably 1 to 5. Also, - (R ⁶ O) q- is - (C ₂ H ₄ O) a q-, and it is preferable q is 1-10.

【００３１】また、本発明で用いることができる帯電防
止剤としては、この他に下記式（II−１）のごとき繰り
返し単位を有するポリマーが挙げられる。Further, examples of the antistatic agent that can be used in the present invention include a polymer having a repeating unit represented by the following formula (II-1).

【００３２】[0032]

【化６】 Embedded image

【００３３】上記式（II−１）において、Ｒ¹¹、Ｒ¹²は
各々炭素数１〜１０の１価の有機基、例えばアルキル
基、シクロアルキル基、アリール基、アラキラル基等で
ある。この他に先に記した特開平１−１４６９３１号公
報に記載されている下記式（II−２）に示す化合物も挙
げられる。これらの中で炭素数１〜６のアルキル基が好
ましい。In the above formula (II-1), R ¹¹ and R ¹² are each a monovalent organic group having 1 to 10 carbon atoms, for example, an alkyl group, a cycloalkyl group, an aryl group, an arachiral group and the like. In addition, the compound represented by the following formula (II-2) described in the above-mentioned JP-A No. 1-146931 may also be used. Among them, an alkyl group having 1 to 6 carbon atoms is preferable.

【００３４】[0034]

【化７】 Embedded image

【００３５】上記式（II−２）において、Ｒ¹³〜Ｒ¹⁵は
各々炭素数１〜１０の１価の有機基、例えばアルキル
基、シクロアルキル基、アリール基、アラキラル基等で
あり、Ｒ¹⁷、Ｒ¹⁸は各々炭素数２〜１０の２価の有機
基、例えばアルキレン基、シクロアルキレン基、アリー
レン基、アレルキレン基、ヘテロ原子（Ｏ、Ｎ等）含有
の２価の脂肪族基等が挙げられる。この脂肪族基として
は、−ＣＨ（ＯＨ）ＣＨ₂−、−ＣＨ₂ＣＨ（ＯＨ）ＣＨ
₂−、−ＣＨ₂ＣＨ₂ＣＨ₂ＮＨＣＯＣＨ₂ＣＨ₂ＣＨ₂−等
が例示される。この他に先の特開平３−２５５１３９号
公報、特開平４−２８８２１７号公報等に記載されてい
る化合物も挙げられるが、これらに限定されるものでは
ない。[0035] In the above formula ^{(II-2), R 13} ~R 15 each a monovalent organic group having 1 to 10 carbon atoms, for example alkyl, cycloalkyl, aryl, Arakiraru group, R ¹⁷ And R ¹⁸ each represent a divalent organic group having 2 to 10 carbon atoms, such as an alkylene group, a cycloalkylene group, an arylene group, an allylene group, a divalent aliphatic group containing a hetero atom (O, N, etc.), and the like. Can be Examples of the aliphatic _{group, -CH (OH) CH 2 -} , - CH 2 CH (OH) CH
_{2 -, - CH 2 CH 2} CH 2 NHCOCH 2 CH 2 CH 2 - and the like. Other examples include compounds described in the above-mentioned JP-A-3-255139, JP-A-4-288217, and the like, but are not limited thereto.

【００３６】これらはホモポリマーでも、他の不飽和モ
ノマーと共重合として用いることもできる。他の不飽和
モノマーと共重合して用いる場合、上記の繰り返し単位
は５０ｍｏｌ％以上で構成されていることが好ましい。
５０ｍｏｌ％未満では帯電防止性が不足する。他の不飽
和モノマーとしては、アクリル酸メチル、アクリル酸エ
チル、アクリル酸ブチル、２−ヒドロキシエチルアクリ
レート、メタクリル酸メチル、メタクリル酸エチル、メ
タクリル酸ブチル、２−ヒドロキシエチルメタクリレー
ト、クロトン酸メチル、グリシジルメタクリレート、ア
クリルメタクリレート、アクリルアミド、メタクリルア
ミド、Ｎ−メチロールアクリルアミド、エチレン、スチ
レン、酢酸ビニル、アクリルニトリル、メタクリルニト
リル、塩化ビニル、塩化ビニリデン、ジビニルベンゼ
ン、アクリル酸、メタクリル酸、マレイン酸、フマル酸
等を挙げることができる。These can be used as homopolymers or as copolymers with other unsaturated monomers. When used by copolymerizing with another unsaturated monomer, the above repeating unit is preferably constituted by 50 mol% or more.
If it is less than 50 mol%, the antistatic property is insufficient. Other unsaturated monomers include methyl acrylate, ethyl acrylate, butyl acrylate, 2-hydroxyethyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, 2-hydroxyethyl methacrylate, methyl crotonate, glycidyl methacrylate , Acrylic methacrylate, acrylamide, methacrylamide, N-methylolacrylamide, ethylene, styrene, vinyl acetate, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, divinylbenzene, acrylic acid, methacrylic acid, maleic acid, fumaric acid, and the like. be able to.

【００３７】この帯電防止性塗膜に添加するバインダー
樹脂（Ｆ）はポリエステル樹脂（Ｆ−１）及びアクリル
樹脂（Ｆ−２）から選ばれる少なくとも１種のバインダ
ー樹脂であることが好ましい。The binder resin (F) to be added to the antistatic coating film is preferably at least one binder resin selected from a polyester resin (F-1) and an acrylic resin (F-2).

【００３８】このポリエステル樹脂（Ｆ−１）を構成す
る酸成分としては、テレフタル酸、イソフタル酸、フタ
ル酸、２，６−ナフタレンジカルボン酸、１，４−シク
ロヘキサンジカルボン酸、アジピン酸、セバシン酸、フ
ェニルインダンジカルボン酸、ダイマー酸等を例示する
ことができる。これら成分は二種以上を用いることがで
きる。更に、これら成分とともにマレイン酸、フマル
酸、イタコン酸等の如き不飽和多塩基酸やｐ−ヒドロキ
シ安息香酸、ｐ−（β−ヒドロキシエトキシ）安息香酸
等の如きヒドロキシカルボン酸を少割合用いることがで
きる。不飽和多塩基酸成分やヒドロキシカルボン酸成分
の割合は高々１０モル％、好ましくは５モル％以下であ
る。The acid components constituting the polyester resin (F-1) include terephthalic acid, isophthalic acid, phthalic acid, 2,6-naphthalenedicarboxylic acid, 1,4-cyclohexanedicarboxylic acid, adipic acid, sebacic acid, Examples thereof include phenylindanedicarboxylic acid and dimer acid. Two or more of these components can be used. Further, it is also possible to use a small proportion of unsaturated polybasic acids such as maleic acid, fumaric acid, itaconic acid and the like and hydroxycarboxylic acids such as p-hydroxybenzoic acid and p- (β-hydroxyethoxy) benzoic acid together with these components. it can. The proportion of the unsaturated polybasic acid component or hydroxycarboxylic acid component is at most 10 mol%, preferably 5 mol% or less.

【００３９】また、ポリオール成分としては、エチレン
グリコール、１，４−ブタンジオール、ネオペンチルグ
リコール、ジエチレングリコール、ジプロピレングリコ
ール、１，６−ヘキサンジオール、１，４−シクロヘキ
サンジメタノール、キシリレングリコール、ジメチロー
ルプロピオン酸、グリセリン、トリメチロールプロパ
ン、ポリ（エチレンオキシ）グリコール、ポリ（テトラ
メチレンオキシ）グリコール、更に下記式で示されるビ
スフェノールＡのエチレンオキサイド付加物やプロピレ
ンオキサイド付加物等を例示することができる。これら
は二種以上を用いることができる。As the polyol component, ethylene glycol, 1,4-butanediol, neopentyl glycol, diethylene glycol, dipropylene glycol, 1,6-hexanediol, 1,4-cyclohexanedimethanol, xylylene glycol, Examples thereof include methylolpropionic acid, glycerin, trimethylolpropane, poly (ethyleneoxy) glycol, poly (tetramethyleneoxy) glycol, and ethylene oxide adducts and propylene oxide adducts of bisphenol A represented by the following formula. . Two or more of these can be used.

【００４０】[0040]

【化８】 Embedded image

【００４１】[0041]

【化９】 Embedded image

【００４２】かかるポリオール成分の中でもエチレング
リコール、ビスフェノールＡのエチレンオキサイド付加
物やプロピレンオキサイド付加物、１，４−ブタンジオ
ールが好ましく、更にエチレングリコールが好ましい。Among such polyol components, ethylene glycol, ethylene oxide adduct of bisphenol A, propylene oxide adduct, and 1,4-butanediol are preferable, and ethylene glycol is more preferable.

【００４３】また、前記ポリエステル樹脂（Ｆ−１）に
は、水性液化を容易にするために若干量の、スルホン酸
塩基を有する化合物やカルボン酸塩基を有する化合物を
共重合させることが可能であり、その方が好ましい。The polyester resin (F-1) can be copolymerized with a small amount of a compound having a sulfonic acid group or a compound having a carboxylic acid group to facilitate aqueous liquefaction. , Which is preferred.

【００４４】このスルホン酸塩基を有する化合物として
は、例えば５−Ｎａスルホイソフタル酸、５−アンモニ
ウムスルホイソフタル酸、４−Ｎａスルホイソフタル
酸、４−メチルアンモニウムスルホイソフタル酸、２−
Ｎａスルホイソフタル酸、５−Ｋスルホイソフタル酸、
４−Ｋスルホイソフタル酸、２−Ｋスルホイソフタル
酸、Ｎａスルホコハク酸等のスルホン酸アルカリ金属塩
系またはスルホン酸アミン塩系化合物等が好ましく挙げ
られる。また、このカルボン酸塩基を有する化合物とし
ては、例えば無水トリメリット酸、トリメリット酸、無
水ピロメリット酸、ピロメリット酸、トリメシン酸、シ
クロブタンテトラカルボン酸、ジメチロールプロピオン
酸等、あるいはこれらのモノアルカリ金属塩等が挙げら
れる。なお、遊離カルボキシル基は共重合後にアルカリ
金属化合物やアミン化合物を作用させてカルボン酸塩基
とする。Examples of the compound having a sulfonate group include 5-Na sulfoisophthalic acid, 5-ammonium sulfoisophthalic acid, 4-Na sulfoisophthalic acid, 4-methylammonium sulfoisophthalic acid,
Na sulfoisophthalic acid, 5-K sulfoisophthalic acid,
Preferable examples include alkali metal sulfonic acid salts such as 4-K sulfoisophthalic acid, 2-K sulfoisophthalic acid, and sodium sulfosuccinic acid, and amine sulfonic acid salts. Examples of the compound having a carboxylic acid group include, for example, trimellitic anhydride, trimellitic acid, pyromellitic anhydride, pyromellitic acid, trimesic acid, cyclobutanetetracarboxylic acid, dimethylolpropionic acid, etc. Metal salts and the like. The free carboxyl group is converted to a carboxylate group by the action of an alkali metal compound or an amine compound after copolymerization.

【００４５】前記ポリエステル樹脂（Ｆ−１）は、変性
ポリエステル共重合体、たとえば前記ポリエステル共重
合体をアクリル、ポリウレタン、シリコーン、エポキ
シ、フェノール樹脂等で変性したブロック重合体、ある
いはグラフト重合体として用いることもできる。The polyester resin (F-1) is used as a modified polyester copolymer, for example, a block polymer or a graft polymer obtained by modifying the polyester copolymer with an acryl, polyurethane, silicone, epoxy, phenol resin or the like. You can also.

【００４６】かかるポリエステル樹脂（Ｆ−１）は、従
来から知られまたは用いられているポリエステルの製造
技術によって製造することができる。例えば、２，６−
ナフタレンジカルボン酸またはそのエステル形成性誘導
体（特にジメチルエステル）、イソフタル酸またはその
エステル形成性誘導体（特にジメチルエステル）及び無
水トリメリット酸をエチレングリコール及びビスフェノ
ールＡのプロピレンオキサイド付加物と反応せしめてモ
ノマーもしくはオリゴマーを形成し、その後真空下で重
縮合反応せしめることによって所定の固有粘度（ｏ−ク
ロロフェノールを用いて３５℃で測定した固有粘度が
０．２〜０．８ｄｌ／ｇが好ましい。）の共重合ポリエ
ステルとし、さらに遊離のカルボキシ基をアルカリ化合
物またはアミン化合物と反応させて塩とする方法で製造
することができる。その際、反応を促進する触媒、例え
ばエステル化もしくはエステル交換触媒、重縮合触媒等
を用いることが好ましく、また種々の添加剤、例えば安
定剤等を添加することもできる。The polyester resin (F-1) can be produced by a conventionally known or used polyester production technique. For example, 2,6-
Naphthalenedicarboxylic acid or its ester-forming derivative (particularly dimethyl ester), isophthalic acid or its ester-forming derivative (particularly dimethyl ester) and trimellitic anhydride are reacted with ethylene glycol and a propylene oxide adduct of bisphenol A to give a monomer or An oligomer is formed and then subjected to a polycondensation reaction under vacuum to obtain a copolymer having a predetermined intrinsic viscosity (the intrinsic viscosity measured at 35 ° C. using o-chlorophenol is preferably 0.2 to 0.8 dl / g). It can be produced by a method of forming a polymerized polyester and further reacting a free carboxy group with an alkali compound or an amine compound to form a salt. At that time, it is preferable to use a catalyst for accelerating the reaction, for example, an esterification or transesterification catalyst, a polycondensation catalyst, and the like, and various additives such as a stabilizer can be added.

【００４７】本発明において帯電防止性塗膜に添加する
バインダー樹脂（Ｆ）として用いるアクリル樹脂（Ｆ−
２）の構成成分としては、アクリル酸、アクリル酸メチ
ル、アクリル酸エチル、アクリル酸ブチル、アクリル酸
ソーダ、アクリル酸アンモニウム、２−ヒドロキシエチ
ルアクリレート、メタクリル酸、メタクリル酸メチル、
メタクリル酸エチル、メタクリル酸ブチル、メタクリル
酸ソーダ、メタクリル酸アンモニウム、２−ヒドロキシ
エチルメタクリレート、グリシジルメタクリレート、ア
クリルメタクリレート、ビニルスルホン酸ナトリウム、
メタリルスルホン酸ナトリウム、スチレンスルホン酸ナ
トリウム、アクリルアミド、メタクリルアミド，Ｎ−メ
チロールメタクリルアミド等を例示することができる。
これらのモノマーは、例えばスチレン、酢酸ビニル、ア
クリルニトリル、メタクリルニトリル、塩化ビニル、塩
化ビニリデン、ジビニルベンゼン等の他の不飽和単量体
と併用することもできる。In the present invention, the acrylic resin (F-) used as the binder resin (F) to be added to the antistatic coating film is used.
The constituent components of 2) include acrylic acid, methyl acrylate, ethyl acrylate, butyl acrylate, sodium acrylate, ammonium acrylate, 2-hydroxyethyl acrylate, methacrylic acid, methyl methacrylate,
Ethyl methacrylate, butyl methacrylate, sodium methacrylate, ammonium methacrylate, 2-hydroxyethyl methacrylate, glycidyl methacrylate, acrylic methacrylate, sodium vinyl sulfonate,
Examples thereof include sodium methallylsulfonate, sodium styrenesulfonate, acrylamide, methacrylamide, and N-methylol methacrylamide.
These monomers can be used in combination with other unsaturated monomers such as styrene, vinyl acetate, acrylonitrile, methacrylonitrile, vinyl chloride, vinylidene chloride, and divinylbenzene.

【００４８】また前記アクリル樹脂（Ｆ−２）として、
変性アクリル共重合体、例えば前記アクリル共重合体を
ポリエステル、ポリウレタン、シリコーン、エポキシ、
フェノール樹脂等で変性したブロック重合体、あるいは
グラフト重合体として用いることもできる。Also, as the acrylic resin (F-2),
Modified acrylic copolymer, for example, the acrylic copolymer polyester, polyurethane, silicone, epoxy,
It can also be used as a block polymer modified with a phenol resin or the like, or as a graft polymer.

【００４９】本発明において、帯電防止性塗膜は、ポリ
カチオンポリマーからなる帯電防止剤（Ｅ）と、ポリエ
ステル樹脂（Ｆ−１）、アクリル樹脂（Ｆ−２）からな
る群から選ばれた少なくとも一種のバインダー樹脂
（Ｆ）からなる組成に当り、前記帯電防止剤（Ｅ）の割
合は５〜５０ｗｔ％、好ましくは１０〜４０ｗｔ％であ
る。この割合が５ｗｔ％未満では帯電防止性が不足し、
他方５０ｗｔ％を超えるとプライマー層のポリエステル
フィルムへの密着力が不足するので好ましくない。該バ
インダー樹脂（Ｆ）の割合は４０〜８５ｗｔ％、好まし
くは５０〜８０ｗｔ％である。この割合が４０ｗｔ％未
満では、被膜(プライマー層)のポリエステルフィルムへ
の密着力が不足し、好ましくない。他方８５wt％を超え
ると、塗布フィルムのブロッキング性が悪化するので好
ましくない。In the present invention, the antistatic coating film comprises at least an antistatic agent (E) composed of a polycationic polymer and at least one selected from the group consisting of a polyester resin (F-1) and an acrylic resin (F-2). The proportion of the antistatic agent (E) in the composition comprising one kind of binder resin (F) is 5 to 50 wt%, preferably 10 to 40 wt%. If this ratio is less than 5 wt%, the antistatic property is insufficient,
On the other hand, if it exceeds 50 wt%, the adhesion of the primer layer to the polyester film becomes insufficient, which is not preferable. The ratio of the binder resin (F) is 40 to 85% by weight, preferably 50 to 80% by weight. If the proportion is less than 40 wt%, the adhesion of the coating (primer layer) to the polyester film is insufficient, which is not preferable. On the other hand, when the content exceeds 85% by weight, the blocking property of the coated film deteriorates, which is not preferable.

【００５０】［水性塗液］本発明において帯電防止性塗
膜を形成する前記成分の組成物は、水性塗液（水を媒体
とするもの）として塗布することが好ましいが、有機溶
剤を溶剤として塗布することも可能である。この有機溶
剤としては、メチルエチルケトン、アセトン、酢酸エチ
ル、テトラヒドロフラン、ジオキサン、シクロヘキサノ
ン、ｎ−ヘキサン、トルエン、キシレン、メタノール、
エタノール、ｎ−プロパノール、イソプロパノール等を
例示することができる。これらは単独で、もしくは複数
を組み合わせて用いることができる。[Aqueous coating liquid] The composition of the above-mentioned components for forming an antistatic coating film in the present invention is preferably applied as an aqueous coating liquid (using water as a medium). It is also possible to apply. Examples of the organic solvent include methyl ethyl ketone, acetone, ethyl acetate, tetrahydrofuran, dioxane, cyclohexanone, n-hexane, toluene, xylene, methanol,
Ethanol, n-propanol, isopropanol and the like can be exemplified. These can be used alone or in combination of two or more.

【００５１】本発明においては、好ましくは前記組成を
含む水性塗液を用いて被膜を塗設するが、この水性塗液
には被膜表面の滑り性を良好なものとし、かつフィルム
の耐ブロッキング性を良好なものとするため、接着性等
の特性を損なわない範囲で滑剤を添加することが好まし
い。この滑剤としては、例えばポリスチレン樹脂、アク
リル樹脂、メラミン樹脂、シリコーン樹脂、フッ素樹
脂、尿素樹脂、ベンゾグアナミン樹脂、ポリアミド樹
脂、ポリエステル樹脂等の微粒子を好ましく挙げること
ができる。これらの樹脂の微粒子は、被膜中に微粒子で
含まれるものであれば熱可塑性であっても熱硬化性のも
のであってもよい。この微粒子の平均粒径は２０〜８０
ｎｍであり、含有量が５〜２０ｗｔ％であることが好ま
しい。In the present invention, the coating is preferably applied by using an aqueous coating liquid containing the above-mentioned composition. This aqueous coating liquid has good slipperiness on the surface of the coating and has good blocking resistance. It is preferable to add a lubricant within a range that does not impair properties such as adhesiveness, in order to improve the surface roughness. Preferred examples of the lubricant include fine particles such as polystyrene resin, acrylic resin, melamine resin, silicone resin, fluorine resin, urea resin, benzoguanamine resin, polyamide resin, and polyester resin. The fine particles of these resins may be thermoplastic or thermosetting as long as the fine particles are contained in the coating. The average particle size of the fine particles is 20 to 80.
nm, and the content is preferably 5 to 20 wt%.

【００５２】さらに本発明の目的を損なわない範囲にお
いて、他の界面活性剤、紫外線吸収剤、顔料、潤滑剤、
ブロッキング防止剤、メラミン、エポキシ、アジリジン
等の架橋剤や他の帯電防止剤等の添加剤を配合すること
ができる。Further, as long as the object of the present invention is not impaired, other surfactants, ultraviolet absorbers, pigments, lubricants,
Additives such as a blocking inhibitor, a crosslinking agent such as melamine, epoxy and aziridine, and other antistatic agents can be added.

【００５３】本発明においては帯電防止性塗膜を形成す
る成分として、上記の成分以外にオキサゾリン樹脂、エ
ポキシ樹脂、メラミン樹脂等の他の樹脂、他の帯電防止
剤、着色剤、界面活性剤、紫外線吸収剤等を使用するこ
とができる。In the present invention, in addition to the above components, other resins such as oxazoline resin, epoxy resin and melamine resin, other antistatic agents, coloring agents, surfactants, etc. An ultraviolet absorber or the like can be used.

【００５４】［塗膜の積層］本発明においては、ポリエ
ステルフィルムの片面にインク受像層易接着塗膜を、も
う一方の面に帯電防止性塗膜（以下併せて単に『塗膜』
と略記することがある）を積層するが、例えば延伸可能
なポリエステルフィルムに塗膜を形成する成分を含む水
性塗液を塗布した後、乾燥、延伸し、必要に応じて熱処
理することにより積層することや、または延伸後のポリ
エステルフィルムに塗膜を形成する成分を含む水性塗液
を塗布した後、乾燥することで積層することができる。
この水性塗液の固形分濃度は、通常３０重量％以下であ
り、１０重量％以下がさらに好ましい。[Lamination of Coating Film] In the present invention, a polyester film is coated with an ink-receiving layer easy-adhesion coating film on one surface and an antistatic coating film (hereinafter simply referred to as “coating film”) on the other surface.
May be abbreviated), for example, after applying an aqueous coating solution containing a component forming a coating film on a stretchable polyester film, drying, stretching, and heat-treating as necessary. Or after applying an aqueous coating solution containing a component for forming a coating film on the stretched polyester film, followed by drying.
The solid content concentration of this aqueous coating liquid is usually 30% by weight or less, and more preferably 10% by weight or less.

【００５５】上記の延伸可能なポリエステルフィルムと
は、未延伸ポリエステルフィルム、一軸延伸ポリエステ
ルフィルム又は二軸延伸ポリエステルフィルムである。
このうちフィルムの押出し方向（縦方向）に一軸延伸し
た縦延伸ポリエステルフィルムが特に好ましい。The above-mentioned stretchable polyester film is an unstretched polyester film, a uniaxially stretched polyester film or a biaxially stretched polyester film.
Of these, a longitudinally stretched polyester film uniaxially stretched in the film extrusion direction (longitudinal direction) is particularly preferred.

【００５６】ポリエステルフィルムへ水性塗液を塗布す
る場合は、通常の塗工工程、即ち二軸延伸熱固定したポ
リエステルフィルムに該フイルムの製造工程と切り離し
た工程で行うと、芥、塵埃等を巻き込み易く好ましくな
い。かかる観点よりクリーンな雰囲気での塗布、即ちフ
ィルム製造工程での塗布が好ましい。そして、この塗布
によれば、塗膜のポリエステルフィルムへの密着性がさ
らに向上する。When the aqueous coating liquid is applied to the polyester film, the coating is carried out in a normal coating step, that is, in a step separated from the film manufacturing step in the biaxially stretched and heat-set polyester film. Easier and not preferred. From such a viewpoint, application in a clean atmosphere, that is, application in a film manufacturing process is preferable. According to this coating, the adhesion of the coating film to the polyester film is further improved.

【００５７】塗布方法としては、公知の任意の塗布法が
適用できる。例えばロールコート法、グラビアコート
法、ロールブラッシュ法、スプレーコート法、エアーナ
イフコート法、含浸法及びカーテンコート法などを単独
または組み合わせて用いることができる。塗布量は走行
しているフィルム１ｍ²当り０．５〜２０ｇ、更に１〜
１０ｇが好ましい。水性塗液は水分散液又は乳化液とし
て用いるのが好ましい。As a coating method, any known coating method can be applied. For example, a roll coating method, a gravure coating method, a roll brushing method, a spray coating method, an air knife coating method, an impregnation method, a curtain coating method and the like can be used alone or in combination. The coating amount is 0.5 to ²⁰ g per 1 m ² of the running film, and 1 to ²
10 g is preferred. The aqueous coating liquid is preferably used as an aqueous dispersion or an emulsion.

【００５８】水性塗液を塗布した延伸可能なポリエステ
ルフィルムは、乾燥、延伸処理工程に導かれるが、かか
る処理は、従来から当業界に蓄積された条件で行うこと
ができる。好ましい条件としては、例えば乾燥条件は９
０〜１３０℃×２〜１０秒であり、延伸温度は９０〜１
３０℃、延伸倍率は縦方向３〜５倍、横方向３〜５倍、
必要ならば再縦方向１〜３倍であり、熱固定する場合は
１８０〜２４０℃×２〜２０秒である。The stretchable polyester film coated with the aqueous coating solution is guided to a drying and stretching step, which can be performed under conditions conventionally accumulated in the art. As preferable conditions, for example, the drying condition is 9
0 to 130 ° C. × 2 to 10 seconds, and the stretching temperature is 90 to 1
30 ° C., stretching ratio 3-5 times in the vertical direction, 3-5 times in the horizontal direction,
If necessary, the length is 1 to 3 times in the vertical direction, and if heat-fixed, the temperature is 180 to 240 ° C. × 2 to 20 seconds.

【００５９】かかる処理後のポリエステルフィルムの厚
さは５０〜１５０μｍであること、また塗膜の厚さは
０．０２〜３μｍであることが好ましい。The thickness of the polyester film after such treatment is preferably 50 to 150 μm, and the thickness of the coating film is preferably 0.02 to 3 μm.

【００６０】[0060]

【実施例】以下実施例により、本発明を更に説明する。
なお、各特性値は以下の方法で測定した。The present invention will be further described with reference to the following examples.
In addition, each characteristic value was measured by the following method.

【００６１】１．印刷前接着性 ポリエステルフィルムの塗膜面に、球状シリカ（平均粒
径１８μ、平均細孔径２００オングストローム、平均細
孔容積１．５ｃｃ／ｇ）７０重量％、ポリビニルアルコ
ール（クラレ製ＰＶＡ１１７）３０重量％を混合した水
性スラリーを乾燥厚さで２０μｍ塗設し、その上に幅１
２．７ｍｍ、長さ１５０ｍｍのスコッチテープ（スリー
エム社製・Ｎｏ．６００）を気泡が入らないよう粘着
し、この上をＪＩＳ・Ｃ２７０１（１９７５）記載の手
動式荷重ロールでならして密着させた後、テープ幅に切
り出す。このようにして作成したサンプルからスコッチ
テープを剥離する際の、インク受像層のポリエステルフ
ィルムからの剥離状態を観察して接着性を下記の通り評
価した。 Ａ：剥離が全く認められず、密着性が良好である。 Ｂ：異物部分で僅かに剥離が認められる。 Ｃ：剥離が顕著に認められる。1. Adhesion before printing On the coating surface of the polyester film, 70% by weight of spherical silica (average particle diameter 18μ, average pore diameter 200 angstrom, average pore volume 1.5cc / g), 30% by weight of polyvinyl alcohol (Kuraray PVA117) Is applied in a dry thickness of 20 μm, and a width 1
A 2.7 mm, 150 mm long scotch tape (No. 600, manufactured by 3M Co.) was adhered so as to prevent air bubbles from entering, and the top of the scotch tape was adhered by a manual load roll described in JIS C2701 (1975). Later, cut out to tape width. When the scotch tape was peeled from the sample thus prepared, the state of peeling of the ink image receiving layer from the polyester film was observed, and the adhesion was evaluated as follows. A: No peeling was observed, and the adhesion was good. B: Slight peeling is observed in the foreign matter portion. C: Peeling is remarkably observed.

【００６２】２．印刷後接着性 ポリエステルフィルムの塗膜面に、球状シリカ（平均粒
径１８μ、平均細孔径２００オングストローム、平均細
孔容積１．５ｃｃ／ｇ）７０重量％、ポリビニルアルコ
ール（クラレ製ＰＶＡ１１７）３０重量％を混合した水
性スラリーを乾燥厚さで２０μｍ塗設し、その上に、イ
ンクジェットプリンター（ＥＰＳＯＮ製ＰＭ−７５０
Ｃ）にてデジタルカメラ等で撮影した画像をパソコンに
取り込み、印刷し、印刷の上に幅１２．７ｍｍ、長さ１
５０ｍｍのスコッチテープ（スリーエム社製・Ｎｏ．６
００）を気泡が入らないよう粘着し、この上をＪＩＳ・
Ｃ２７０１（１９７５）記載の手動式荷重ロールでなら
して密着させた後、テープ幅に切り出す。このようにし
て作成したサンプルからスコッチテープを剥離する際
の、インク受像層のポリエステルフィルムからの剥離状
態を観察して接着性を下記の通り評価した。 Ａ：剥離が全く認められず、密着性が良好である。 Ｂ：異物部分で僅かに剥離が認められる。 Ｃ：剥離が顕著に認められる。[0062] 2. Adhesion after printing 70% by weight of spherical silica (average particle diameter 18μ, average pore diameter 200 angstrom, average pore volume 1.5cc / g) 70% by weight, polyvinyl alcohol (Kuraray PVA117) 30% by weight on the coating surface of the polyester film Is applied in a dry thickness of 20 μm, and an ink jet printer (PM-750 manufactured by EPSON) is applied thereon.
The image captured by a digital camera or the like in step C) is taken into a personal computer and printed, and the printed image has a width of 12.7 mm and a length of 1 mm.
50mm scotch tape (No. 6 manufactured by 3M)
00) to prevent air bubbles from entering.
After being leveled and adhered with a manual load roll described in C2701 (1975), it is cut out to a tape width. When the scotch tape was peeled from the sample thus prepared, the state of peeling of the ink image receiving layer from the polyester film was observed, and the adhesion was evaluated as follows. A: No peeling was observed, and the adhesion was good. B: Slight peeling is observed in the foreign matter portion. C: Peeling is remarkably observed.

【００６３】３．耐水接着性 上記接着性を評価した物について、インク受像層の上か
ら、ガーゼに水を染み込ませ、ラビングし、何回ラビン
グしたらインク受像層が脱落するかを下記の通り評価し
た。 Ａ：５０回以上・・・耐水接着性が極めて良好。 Ｂ：３０〜５０回・・耐水接着性が良好。 Ｃ：３０回未満 ・・耐水接着性不良。3. Water-Resistant Adhesion The grease was impregnated with water from above the ink image-receiving layer, rubbed, and the number of rubbings before the ink-image-receiving layer was dropped was evaluated as described below. A: 50 times or more: Extremely good water resistance adhesiveness. B: 30 to 50 times: good water-resistant adhesion. C: Less than 30 times ··· Poor water resistance.

【００６４】４．表面固有抵抗（帯電防止性） サンプルフィルムの表面固有抵抗を、タケダ理研社製・
固有抵抗測定器を使用し、測定温度２３℃、測定湿度６０
％の条件で、印加電圧５００Ｖで１分後の表面固有抵抗
値（Ω／□）を測定する。尚、表面固有抵抗値は３×１０
¹²［Ω／□］以下が好ましく、３×１０¹¹以下が更に好
ましい。4. Surface resistivity (antistatic property) The surface resistivity of the sample film was measured by Takeda Riken Co., Ltd.
Using a specific resistance measuring instrument, measured temperature 23 ° C, measured humidity 60
%, The surface specific resistance (Ω / □) after one minute at an applied voltage of 500 V is measured. The surface specific resistance is 3 × 10
^It is preferably ¹² [Ω / □] or less, more preferably 3 × 10 ¹¹ or less.

【００６５】５．摩擦係数 ＡＳＴＭ・Ｄ１８９４―６３に準じ、東洋テスター社製
のスリッパ―測定器を使用し、フィルムの表面と裏面を
合わせ、荷重１ｋｇを加えて静摩擦係数を測定した。摩
擦係数が０．６を超えるとフィルム搬送性に支障をきた
す。5. Coefficient of friction According to ASTM D 1894-63, the surface and back of the film were combined using a slipper measuring device manufactured by Toyo Tester, and a static friction coefficient was measured by applying a load of 1 kg. If the coefficient of friction exceeds 0.6, the film transportability is impaired.

【００６６】６．ブロッキング性 ５０ｍｍ幅に切断したフィルムを２枚重ね、５０ｋｇ／
ｃｍ²の荷重下４０℃×５０％ＲＨ×１７時間処理した
後、引張り試験機にて荷重を加えた箇所の剥離強度（ｇ
／５０ｍｍ）を測定した。剥離強度の値により下記の通
り評価した。 剥離強度≦１０ｇ／５０ｍｍ…ブロッキング性良好。 １０ｇ／５０ｍｍ＜剥離強度≦３０ｇ／５０ｍｍ…ブロッキング性やや良好。 ３０ｇ／５０ｍｍ＜剥離強度 …ブロッキング性不良。6. Blocking property Two films cut to a width of 50 mm are stacked, and 50 kg /
After treatment at 40 ° C. × 50% RH × 17 hours under a load of cm ² , the peel strength (g
/ 50 mm). Evaluation was made as follows by the value of the peel strength. Peel strength ≦ 10 g / 50 mm Good blocking property. 10 g / 50 mm <peel strength ≦ 30 g / 50 mm ... Slightly good blocking property. 30 g / 50 mm <peel strength: poor blocking property.

【００６７】７．表面エネルギー Ｗ．Ａ．Ｚｉｓｍａｎ：“Ｃｏｎｔａｃｔ Ａｕｇｌ
ｅ， Ｗｅｔｔａｂｉｌｉｔｙ ａｎｄ Ａｄｈｅｓｉ
ｏｎ ”，Ａｍ． Ｃｈｅｍ．Ｓｏｃ．， （１９６
４）に従い、測定した臨界表面張力γｃをもって、表面
エネルギーとした。7. Surface energy W. A. Zisman: "Contact Augl
e, Wetability and Adhesi
on ", Am. Chem. Soc., (196
According to 4), the measured critical surface tension γc was used as the surface energy.

【００６８】８．二次転移点 デュポン製 Ｔｈｅｒｍａｌ Ａｎａｌｙｓｔ ２００
０型 示差熱量計にて、２０℃／分の昇温速度にて測定
した。8. Secondary transition point Thermal Analyst 200 manufactured by DuPont
It was measured at a heating rate of 20 ° C./min with a type 0 differential calorimeter.

【００６９】９．固有粘度 オルソクロロフェノール溶媒による溶液の粘度を３５℃
にて測定し求めた。9. Intrinsic viscosity The viscosity of the solution with orthochlorophenol solvent is 35 ℃
Was measured and determined.

【００７０】１０．光沢度Ｇｓ（６０°） （株）村上色彩技術研究所製光沢計ＧＭ−３Ｄ型を使用
し、ＪＩＳ Ｚ ８７４１−１９６２に準じて測定する。
測定角は６０°とし、測定数はｎ＝５とし、その平均値
を光沢度Ｇｓ（６０°）の値とする。10. Gloss Gs (60 °) Gloss is measured according to JIS Z 8741-1962 using a gloss meter GM-3D manufactured by Murakami Color Research Laboratory.
The measurement angle is 60 °, the number of measurements is n = 5, and the average value is the value of the gloss Gs (60 °).

【００７１】１１．光線透過率 村上色彩技術研究所製 ＨＲ―１００型 ヘーズメータ
ーにより、ＡＳＴＭ・Ｄ１００３に準じて測定した。11. Light transmittance The light transmittance was measured using a HR-100 haze meter manufactured by Murakami Color Research Laboratory in accordance with ASTM D1003.

【００７２】１２．熱収縮率 ポリエステルフィルムを１５０℃×３０分熱処理した後
の収縮率を標点間距離３０ｃｍで測定した。12. Heat shrinkage The shrinkage after heat treatment of the polyester film at 150 ° C. for 30 minutes was measured at a distance between the gauge points of 30 cm.

【００７３】１３．鮮映性 インク受像層を塗布したポリエステルフィルムについ
て、インクジェットプリンター（ＥＰＳＯＮ製 ＰＭ−
７５０Ｃ）にてデジタルカメラ等で撮影した画像をパソ
コンに取り込み、印刷し、印刷物の鮮明性を目視で観察
し、下記の通り評価した。 Ａ：印刷が極めて鮮明性で良好 ・・・・鮮映性が極めて良好。 Ｂ：印刷が鮮明性で良好 ・・・・鮮映性が極めて良好。 Ｃ：印刷が不鮮明で鮮明性が不良・・・・鮮映性が不良。13. Sharpness The polyester film coated with the ink image-receiving layer was printed on an inkjet printer (PM-
The image taken with a digital camera or the like at 750C) was taken into a personal computer, printed, and the sharpness of the printed matter was visually observed, and evaluated as follows. A: Printing is extremely clear and excellent.... B: Printing is excellent in sharpness. C: The printing is unclear and the sharpness is poor. The sharpness is poor.

【００７４】１４．搬送性 インク受像層を塗布したポリエステルフィルムについ
て、インクジェットプリンター（ＥＰＳＯＮ製 ＰＭ−
７５０Ｃ）にてデジタルカメラ等で撮影した画像をパソ
コンに取り込み、５０枚を連続印刷し、フィルムが連続
的に印刷できるかについて、下記の通り評価した。 Ａ：５０枚連続給紙しても詰まりが無く、印刷できた・・搬送性が極めて良好。 Ｂ：４５枚連続給紙しても詰まりが無く、印刷できた・・搬送性がやや不良。 Ｃ：４５枚以下で、連続的に給紙できず、印刷ができない・・搬送性が不良。14. Conveyance The polyester film coated with the ink image-receiving layer is printed on an inkjet printer (PM-
At 750C), images taken by a digital camera or the like were taken into a personal computer, and 50 sheets were continuously printed, and whether or not films could be continuously printed was evaluated as follows. A: There was no clogging even when 50 sheets were continuously fed, and printing was possible. B: There was no clogging even when 45 sheets were continuously fed, and printing was possible. The transportability was slightly poor. C: 45 sheets or less, continuous paper cannot be fed and printing cannot be performed. Poor transportability.

【００７５】［実施例１］テレフタル酸成分及びエチレ
ングリコール成分からなるポリエステル（固有粘度が
０．６２）を２０℃に維持した回転冷却ドラム上に溶融
押し出しして未延伸フィルムとし、次に該未延伸フィル
ムを機械軸方向に３．６倍延伸した後、片面にインク受
像層易接着層用水性塗液、水性バインダーとして、共重
合ポリエステル、酸成分がテレフタル酸［６０モル
％］、イソフタル酸［３６モル％］および５―Ｎａスル
ホイソフタル酸［４モル％］、グリコール成分がエチレ
ングリコール［６０モル％］およびネオペンチルグリコ
ール［４０モル％］よりなる共重合ポリエステル（Ｔｇ
＝３０℃、以下、単に［Ｈ］という）５１重量％、ケン
化度８６〜８９モル％のポリビニルアルコール２０重量
％、平均粒径４０ｎｍの架橋アクリル樹脂粒子１０重量
％、下記式（Ｉ−１）で示される化合物（Ｏ）１０重量
％並びにポリオキシエチレンラウリルエーテル９重量％
からなる組成の、固形分濃度４重量％の水性塗液をロー
ルコーターにて塗布した。Example 1 A polyester (intrinsic viscosity: 0.62) comprising a terephthalic acid component and an ethylene glycol component was melt-extruded onto a rotating cooling drum maintained at 20 ° C. to form an unstretched film. After the stretched film is stretched 3.6 times in the machine axis direction, the aqueous coating solution for the ink-receiving layer easy-adhesion layer on one side, a copolymerized polyester as the aqueous binder, terephthalic acid [60 mol%] as an acid component, isophthalic acid [ 36 mol%] and 5-Na sulfoisophthalic acid [4 mol%], and a glycol component composed of ethylene glycol [60 mol%] and neopentyl glycol [40 mol%] (Tg
= 30 ° C, hereinafter simply referred to as [H]) 51% by weight, polyvinyl alcohol 20% by weight having a saponification degree of 86 to 89% by mole, 10% by weight of crosslinked acrylic resin particles having an average particle diameter of 40 nm, the following formula (I-1) 10% by weight of compound (O) and 9% by weight of polyoxyethylene lauryl ether
An aqueous coating solution having a solid content concentration of 4% by weight was applied by a roll coater.

【００７６】[0076]

【化１０】 Embedded image

【００７７】同時にもう片面に、帯電防止性塗膜層用水
性塗液としてテレフタル酸（２２ｍｏｌ％）、イソフタ
ル酸（１ｍｏｌ％）、２，６−ナフタレンジカルボン酸
（６５ｍｏｌ％）、４，４´−ジフェニルジカルボン酸
（１２ｍｏｌ％）、エチレングリコール（７５ｍｏｌ
％）、１，４−シクロヘキサンジメタノール（１０ｍｏ
ｌ％）、ネオペンチルグリコール（１５ｍｏｌ％）から
つくられた共重合ポリエステル（Ｔｇ＝８０℃、平均分
子量＝２１，５００）（Ｆ−１）７５ｗｔ％、下記式
（II−３）で示される高分子帯電防止剤（Ｅ）２０ｗｔ
％およびポリオキシエチレンラウリルエーテル５ｗｔ％
からなる固形分組成の１０ｗｔ％水性塗液を４ｇ／ｍ²
（ｗｅｔ）の塗布量でロールコーターにて塗布した。次
いで、水性塗液を塗布した縦延伸フィルムを乾燥しつつ
横方向に４倍延伸し、更に２３０℃で熱固定して厚さ１
００μｍの二軸延伸フィルムを得た。At the same time, on the other side, terephthalic acid (22 mol%), isophthalic acid (1 mol%), 2,6-naphthalenedicarboxylic acid (65 mol%), 4,4′- Diphenyl dicarboxylic acid (12 mol%), ethylene glycol (75 mol%)
%), 1,4-cyclohexanedimethanol (10 mol
1%), a copolyester made from neopentyl glycol (15 mol%) (Tg = 80 ° C., average molecular weight = 21,500) (F-1) 75 wt%, a high polymer represented by the following formula (II-3) Molecular antistatic agent (E) 20wt
% And polyoxyethylene lauryl ether 5wt%
4 g / m ^{2 of} a 10 wt% aqueous coating liquid having a solid content composition of
(Wet) with a roll coater. Next, the vertically stretched film coated with the aqueous coating solution was stretched 4 times in the transverse direction while drying, and further heat-set at 230 ° C. to a thickness of 1
A 00 μm biaxially stretched film was obtained.

【００７８】[0078]

【化１１】 Embedded image

【００７９】このフィルムでのインク受像層易接着層の
塗膜厚さは０．０５μｍ、表面エネルギーは５９ｍＮ／
ｍ、熱収縮率は縦方向で０．９％、横方向で０．２％で
あった。また、帯電防止性塗膜の塗膜層の塗膜厚さは
０．１μｍであった。このフィルムの特性を表１に示
す。The film thickness of the ink image-receiving layer easy-adhesion layer in this film was 0.05 μm, and the surface energy was 59 mN /
m, the heat shrinkage was 0.9% in the vertical direction and 0.2% in the horizontal direction. The coating thickness of the coating layer of the antistatic coating was 0.1 μm. Table 1 shows the properties of this film.

【００８０】［比較例１］水性塗液を塗布しない以外
は、実施例１と同様にして得た二軸延伸ポリエステルフ
ィルムの特性を表１に示す。Comparative Example 1 Table 1 shows the properties of the biaxially stretched polyester film obtained in the same manner as in Example 1 except that the aqueous coating solution was not applied.

【００８１】［比較例２］片面のインク受像層易接着層
用の水性塗液を塗布しない以外は、実施例１と同様にし
て得た二軸延伸ポリエステルフィルムの特性を表１に示
す。Comparative Example 2 Table 1 shows the properties of the biaxially stretched polyester film obtained in the same manner as in Example 1 except that the aqueous coating solution for the ink-receiving layer on the one surface was easily applied.

【００８２】［比較例３］片面の帯電防止性塗膜用の水
性塗液を塗布しない以外は、実施例１と同様にして得た
二軸延伸ポリエステルフィルムの特性を表１に示す。Comparative Example 3 Table 1 shows the properties of the biaxially stretched polyester film obtained in the same manner as in Example 1 except that the aqueous coating solution for a single-sided antistatic coating film was not applied.

【００８３】［実施例２〜７］インク受像層易接着用塗
布剤の種類と比率を表１に示すように変える以外は、実
施例１と同様にして二軸延伸ポリエステルフィルムを得
た。このフィルムの特性を表１に示す。[Examples 2 to 7] A biaxially stretched polyester film was obtained in the same manner as in Example 1 except that the kind and ratio of the ink image-receiving layer coating for easy adhesion were changed as shown in Table 1. Table 1 shows the properties of this film.

【００８４】[0084]

【表１】 [Table 1]

【００８５】表１に示す結果から明らかなように、本発
明のインク受像層易接着ポリエステルフィルムは接着
性、帯電防止性、および搬送性に優れる。As is clear from the results shown in Table 1, the ink-receiving layer easily adhesive polyester film of the present invention is excellent in adhesiveness, antistatic property and transportability.

【００８６】尚、表１においてコポリエステル（Ａ）の
種類ＨおよびＪ（注１）は、下記の化合物であることを
示す。 Ｈ：テレフタル酸［６０モル％］・イソフタル酸［３６
モル％］・５―Ｎａスルホイソフタル酸［４モル％］／
エチレングリコール［６０モル％］・ネオペンチルグリ
コール［４０モル％］の共重合体（Ｔｇ＝３０℃） Ｊ：２，６―ナフタリンジカルボン酸［２０モル％］・
イソフタル酸［７６モル％］・５―Ｋスルホテレフタル
酸［４モル％］／エチレングリコール［５０モル％］・
ネオペンチルグリコール［５０モル％］共重合体（Ｔｇ
＝４２℃）In Table 1, types H and J (Note 1) of copolyester (A) indicate the following compounds. H: terephthalic acid [60 mol%] / isophthalic acid [36
Mol%] · 5-Na sulfoisophthalic acid [4 mol%] /
Copolymer of ethylene glycol [60 mol%] / neopentyl glycol [40 mol%] (Tg = 30 ° C.) J: 2,6-naphthalene dicarboxylic acid [20 mol%]
Isophthalic acid [76 mol%] 5-K sulfoterephthalic acid [4 mol%] / ethylene glycol [50 mol%]
Neopentyl glycol [50 mol%] copolymer (Tg
= 42 ° C)

【００８７】また、表１において水溶性高分子（Ｂ）の
種類Ｐ、ＱおよびＲ（注２）は、下記の化合物であるこ
とを示す。 Ｐ：ケン化度８６〜８９ｍｏｌ％のポリビニルアルコー
ル Ｑ：ケン化度７４〜７８ｍｏｌ％のポリビニルアルコー
ル Ｒ：ケン化度９２〜９５ｍｏｌ％のポリビニルアルコー
ルIn Table 1, types P, Q and R (Note 2) of the water-soluble polymer (B) indicate the following compounds. P: polyvinyl alcohol having a saponification degree of 86 to 89 mol% Q: polyvinyl alcohol having a saponification degree of 74 to 78 mol% R: polyvinyl alcohol having a saponification degree of 92 to 95 mol%

【００８８】表１において微粒子（Ｃ）の種類Ｍおよび
Ｎ（注３）は、下記の化合物であることを示す。 Ｍ：平均粒径 ４０ｎｍの架橋アクリル粒子 Ｎ：平均粒径 ８０ｎｍのコロイダルシリカ粒子In Table 1, the types M and N (Note 3) of the fine particles (C) indicate the following compounds. M: Crosslinked acrylic particles having an average particle size of 40 nm N: Colloidal silica particles having an average particle size of 80 nm

【００８９】表１において化合物（Ｄ）の種類Ｏおよび
Ｓ（注４）は下記式（Ｉ−１）及び式（Ｉ−２）で示し
た化合物であることを示す。In Table 1, types O and S (Note 4) of compound (D) indicate that they are compounds represented by the following formulas (I-1) and (I-2).

【００９０】[0090]

【化１２】 Embedded image

【００９１】[0091]

【化１３】 Embedded image

【００９２】［実施例８〜１１及び比較例４、５］イン
ク受像層易接着層用塗布剤の水性塗液の（Ａ）コポリエ
ステルの種類を表２、表３に示す様に変えて、Ｔｇの異
なるコポリエステルを用いた以外は実施例１と同様にし
て二軸延伸ポリエステルフィルムを得た。得られたフィ
ルムの特性を表２に示す。[Examples 8 to 11 and Comparative Examples 4 and 5] The type of the copolyester (A) of the aqueous coating solution of the coating for the ink-receiving layer was easily changed as shown in Tables 2 and 3. A biaxially stretched polyester film was obtained in the same manner as in Example 1 except that copolyesters having different Tg were used. Table 2 shows the properties of the obtained film.

【００９３】[0093]

【表２】 [Table 2]

【００９４】[0094]

【表３】 [Table 3]

【００９５】表２に示す結果から明らかなように、本発
明のインク受像層易接着ポリエステルフィルムは耐ブロ
ッキング性、接着性、帯電防止性および搬送性に優れ
る。As is clear from the results shown in Table 2, the ink-receiving layer easily adhesive polyester film of the present invention is excellent in blocking resistance, adhesiveness, antistatic property and transportability.

【００９６】［実施例１２〜１６及び比較例６〜１３］
インク受像層易接着層用塗布剤の水性塗液のコポリエス
テル（Ａ）、水溶性高分子（Ｂ）、微粒子（Ｃ）および
化合物（Ｄ）の種類および比率を表４に示すように変え
た以外は実施例１と同様にして二軸延伸ポリエステルフ
ィルムを得た。得られたフィルムの特性を表４に示す。[Examples 12 to 16 and Comparative Examples 6 to 13]
The types and ratios of the copolyester (A), the water-soluble polymer (B), the fine particles (C) and the compound (D) in the aqueous coating liquid of the coating agent for the ink-receiving layer were easily changed as shown in Table 4. Except for the above, a biaxially stretched polyester film was obtained in the same manner as in Example 1. Table 4 shows the properties of the obtained film.

【００９７】[0097]

【表４】 [Table 4]

【００９８】表４に示す結果から明らかなように、本発
明のインク受像層易接着ポリエステルフィルムは接着
性、帯電防止性、搬送性に優れる。As is clear from the results shown in Table 4, the ink-receiving layer easily adhesive polyester film of the present invention is excellent in adhesiveness, antistatic property and transportability.

【００９９】［実施例１７、１８及び比較例１４、１
５］インク受像層易接着層用塗布剤の水性塗液中の微粒
子（Ｃ）の粒径を表５に示すように変えた以外は実施例
１と同様にして二軸延伸ポリエステルフィルムを得た。
得られたフィルムの特性を表５に示す。[Examples 17 and 18 and Comparative Examples 14 and 1
5] A biaxially stretched polyester film was obtained in the same manner as in Example 1, except that the particle size of the fine particles (C) in the aqueous coating solution of the coating composition for the ink image receiving layer and the adhesive layer was changed as shown in Table 5. .
Table 5 shows the properties of the obtained film.

【０１００】[0100]

【表５】 [Table 5]

【０１０１】表５に示す結果から明らかなように、本発
明のインク受像層易接着ポリエステルフィルムは耐ブロ
ッキング性に優れる。As apparent from the results shown in Table 5, the ink-receiving layer easily adhesive polyester film of the present invention has excellent blocking resistance.

【０１０２】［実施例１９、２０及び比較例１６、１
７］インク受像層易接着層用塗布剤の水性塗液のコポリ
エステル（Ａ）、水溶性高分子（Ｂ）、微粒子（Ｃ）お
よび化合物（Ｄ）の比率を表６に示すように変えた以外
は実施例１と同様にして二軸延伸ポリエステルフィルム
を得た。得られたフィルムの特性を表６に示す。[Examples 19 and 20 and Comparative Examples 16 and 1
7] The ratios of the copolyester (A), the water-soluble polymer (B), the fine particles (C) and the compound (D) in the aqueous coating solution of the coating agent for the ink image-receiving layer and the adhesive layer were changed as shown in Table 6. Except for the above, a biaxially stretched polyester film was obtained in the same manner as in Example 1. Table 6 shows the properties of the obtained film.

【０１０３】[0103]

【表６】 [Table 6]

【０１０４】表６に示す結果から明らかなように、本発
明のインク受像層易接着ポリエステルフィルムは接着
性、帯電防止性及び搬送性に優れる。As is clear from the results shown in Table 6, the ink-receiving layer easily adhesive polyester film of the present invention is excellent in adhesiveness, antistatic property and transportability.

【０１０５】［実施例２１］実施例１の帯電防止性塗膜
用水性塗液の共重合ポリエステル（Ｆ−１）をメタクリ
ル酸メチル（３０ｍｏｌ％）、アクリル酸エチル（５５
ｍｏｌ％）、アクリロニトリル（１０ｍｏｌ％）及びＮ
−メチロールメタクリルアミド（５ｍｏｌ％）から作成
されたアクリル共重合体（数平均分子量：２５８００
０）（Ｆ−２）に変更する以外は、実施例１と全く同様
にして二軸延伸ポリエステルフィルムを得た。得られた
フィルムの特性を表７にまとめて示す。Example 21 The copolymerized polyester (F-1) of the aqueous coating solution for an antistatic coating film of Example 1 was prepared by adding methyl methacrylate (30 mol%) and ethyl acrylate (55
mol%), acrylonitrile (10 mol%) and N
-Acrylic copolymer prepared from methylol methacrylamide (5 mol%) (number average molecular weight: 25800)
0) Except changing to (F-2), a biaxially stretched polyester film was obtained in exactly the same manner as in Example 1. Table 7 summarizes the properties of the obtained film.

【０１０６】［実施例２２］実施例２１の帯電防止性塗
膜用水性塗液の帯電防止剤（Ｅ）を主鎖に下記構造のピ
ロリジウム環を複数有するポリカチオンポリマー（数平
均分子量：２９０００、下記式（II−４）で示したポリ
マー）に変更する以外は、実施例１と全く同様にして二
軸延伸ポリエステルフィルムを得た。得られたフィルム
の特性を表７にまとめて示す。[Example 22] A polycationic polymer having the antistatic agent (E) of the aqueous coating solution for an antistatic coating film of Example 21 and a plurality of pyrrolidium rings having the following structure in the main chain (number average molecular weight: 29000; A biaxially stretched polyester film was obtained in exactly the same manner as in Example 1, except that the polymer was changed to the polymer represented by the following formula (II-4). Table 7 summarizes the properties of the obtained film.

【０１０７】[0107]

【化１４】 Embedded image

【０１０８】［実施例２３］実施例２１の帯電防止性塗
膜用水性塗液の帯電防止剤（Ｅ）を下記構造のポリカチ
オンポリマー（数平均分子量：６０００、下記式（II−
５）で示したポリマー）に変更する以外は、実施例１と
全く同様にして二軸延伸ポリエステルフィルムを得た。
得られたフィルムの特性を表７にまとめて示す。Example 23 The antistatic agent (E) of the aqueous coating solution for an antistatic coating film of Example 21 was replaced with a polycation polymer having the following structure (number-average molecular weight: 6000;
A biaxially stretched polyester film was obtained in exactly the same manner as in Example 1, except that the polymer was changed to the polymer shown in 5).
Table 7 summarizes the properties of the obtained film.

【０１０９】[0109]

【化１５】 Embedded image

【０１１０】［実施例２４］テレフタル酸成分及びエチ
レングリコール成分からなるポリエステル（固有粘度が
０．６２）を２０℃に維持した回転冷却ドラム上に溶融
押し出しして未延伸フィルムとし、次に該未延伸フィル
ムを機械軸方向に３．６倍延伸した後、片面にインク受
像層易接着層用水性塗液、水性バインダーとして、共重
合ポリエステル、酸成分がテレフタル酸［６０モル
％］、イソフタル酸［３６モル％］および５―Ｎａスル
ホイソフタル酸［４モル％］、グリコール成分がエチレ
ングリコール［６０モル％］およびネオペンチルグリコ
ール［４０モル％］よりなる共重合ポリエステル（Ｔｇ
＝３０℃：［Ｈ］）５１重量％、ケン化度８６〜８９モ
ル％のポリビニルアルコール２０重量％、平均粒径４０
ｎｍの架橋アクリル樹脂粒子１０重量％、前記式（Ｉ−
１）で示される化合物（Ｏ）１０重量％並びにポリオキ
シエチレンラウリルエーテル９重量％からなる組成の、
固形分濃度４重量％の水性液をロールコーターにて塗布
した。Example 24 A polyester (intrinsic viscosity: 0.62) comprising a terephthalic acid component and an ethylene glycol component was melt-extruded onto a rotating cooling drum maintained at 20 ° C. to form an unstretched film. After the stretched film is stretched 3.6 times in the machine axis direction, the aqueous coating solution for the ink-receiving layer easy-adhesion layer on one side, a copolymerized polyester as the aqueous binder, terephthalic acid [60 mol%] as an acid component, isophthalic acid [ 36 mol%] and 5-Na sulfoisophthalic acid [4 mol%], and a glycol component composed of ethylene glycol [60 mol%] and neopentyl glycol [40 mol%] (Tg
= 30 ° C: [H]) 51% by weight, 20% by weight of polyvinyl alcohol having a degree of saponification of 86 to 89% by mole, average particle size 40
10% by weight of crosslinked acrylic resin particles of
A composition comprising 10% by weight of the compound (O) represented by 1) and 9% by weight of polyoxyethylene lauryl ether,
An aqueous liquid having a solid concentration of 4% by weight was applied using a roll coater.

【０１１１】次いで、水性塗液を塗布した縦延伸フィル
ムを乾燥しつつ横方向に４倍延伸し、更に２３０℃で熱
固定して厚さ１００μｍの二軸延伸フィルムを得た。こ
のフィルムでのインク受像層易接着層の塗膜厚さは０．
０５μｍ、表面エネルギーは５９ｍＮ／ｍ、熱収縮率は
縦方向で０．９％、横方向で０．２％であった。得られ
たサンプルのインク受像層易接着層の反対面に、帯電防
止性塗膜として、テレフタル酸（２２ｍｏｌ％）、イソ
フタル酸（１ｍｏｌ％）、２，６−ナフタレンジカルボ
ン酸（６５ｍｏｌ％）、４，４´−ジフェニルジカルボ
ン酸（１２ｍｏｌ％）、エチレングリコール（７５ｍｏ
ｌ％）、１，４−シクロヘキサンジメタノール（１０ｍ
ｏｌ％）、ネオペンチルグリコール（１５ｍｏｌ％）か
らつくられた共重合ポリエステル（Ｔｇ＝８０℃、平均
分子量＝２１，５００）（Ｆ−１）７５ｗｔ％、前記式
（II−３）で示される高分子帯電防止剤（Ｅ）２０ｗｔ
％およびポリオキシエチレンラウリルエーテル５ｗｔ％
からなり、溶剤としてイソプロパノールを１５％添加
し、固形分組成の１０ｗｔ％の塗液を６ｇ／ｍ²（ｗｅ
ｔ）の塗布量でグラビアコーターにて塗布した後、乾燥
炉を用い、炉内フィルム張力３００ｇ／ｍ²、温度１７
０℃、２０秒間乾燥させ、厚さ０．５μｍの帯電防止性
塗膜を塗布した二軸延伸ポリエステルフィルムを得た。
このフィルムの特性を表７にまとめて示す。Next, the vertically stretched film coated with the aqueous coating solution was stretched 4 times in the transverse direction while drying, and further heat-set at 230 ° C. to obtain a 100 μm thick biaxially stretched film. In this film, the coating thickness of the ink image-receiving layer easy-adhesion layer is 0.1.
The surface energy was 59 mN / m, the heat shrinkage was 0.9% in the vertical direction, and 0.2% in the horizontal direction. On the opposite side of the ink image receiving layer easy adhesion layer of the obtained sample, as antistatic coating film, terephthalic acid (22 mol%), isophthalic acid (1 mol%), 2,6-naphthalenedicarboxylic acid (65 mol%), 4 , 4'-diphenyldicarboxylic acid (12mol%), ethylene glycol (75mo
1%), 1,4-cyclohexanedimethanol (10 m
ol%), a copolyester made from neopentyl glycol (15 mol%) (Tg = 80 ° C., average molecular weight = 21,500) (F-1) 75 wt%, a high polymer represented by the formula (II-3) Molecular antistatic agent (E) 20wt
% And polyoxyethylene lauryl ether 5wt%
15% of isopropanol as a solvent was added, and a coating solution having a solid content of 10% by weight was coated at 6 g / m ² (we
After coating with a gravure coater with the coating amount of t), using a drying furnace, the film tension in the furnace is 300 g / m ² , and the temperature is 17
It was dried at 0 ° C. for 20 seconds to obtain a biaxially stretched polyester film coated with a 0.5 μm-thick antistatic coating film.
Table 7 summarizes the properties of this film.

【０１１２】［実施例２５］実施例２４の帯電防止性塗
膜の帯電防止剤をポリスチレンスルホン酸ナトリウムに
変更する以外は、実施例２４と全く同様にして二軸延伸
ポリエステルフィルムを得た。このフィルムの特性を表
７にまとめて示す。Example 25 A biaxially stretched polyester film was obtained in the same manner as in Example 24 except that the antistatic agent of the antistatic coating film of Example 24 was changed to sodium polystyrene sulfonate. Table 7 summarizes the properties of this film.

【０１１３】［実施例２６］テレフタル酸成分及びエチ
レングリコール成分からなるポリエステル（固有粘度が
０．６２）９０重量％と酸化チタン１０重量％からなる
組成物を２０℃に維持した回転冷却ドラム上に溶融押し
出しして未延伸フィルムとし、次に該未延伸フィルムを
機械軸方向に３．６倍延伸した一軸延伸フィルムの片面
に、水性バインダーとして、共重合ポリエステル（酸成
分がテレフタル酸［６０モル％］、イソフタル酸［３６
モル％］および５―Ｎａスルホイソフタル酸［４モル
％］、グリコール成分がエチレングリコール［６０モル
％］およびネオペンチルグリコール［４０モル％］より
なる共重合ポリエステル：Ｔｇ＝３０℃、［Ｈ］）５１
重量％、ケン化度８６〜８９モル％のポリビニルアルコ
ール２０重量％、平均粒径４０ｎｍの架橋アクリル樹脂
粒子１０重量％、前記式（Ｉ−１）で示される化合物
（Ｏ）１０重量％並びにポリオキシエチレンラウリルエ
ーテル９重量％からなる組成の、固形分濃度４重量％の
水性塗液をロールコーターにて塗布した。Example 26 A composition comprising 90% by weight of a polyester (having an intrinsic viscosity of 0.62) comprising a terephthalic acid component and an ethylene glycol component and 10% by weight of titanium oxide was placed on a rotary cooling drum maintained at 20 ° C. A non-stretched film is melt-extruded, and then the unstretched film is stretched 3.6 times in the machine axis direction on one surface of a uniaxially stretched film. As an aqueous binder, a copolymerized polyester (acid component containing terephthalic acid [60 mol% ], Isophthalic acid [36
Mol%], 5-Nasulfoisophthalic acid [4 mol%], and a glycol component composed of ethylene glycol [60 mol%] and neopentylglycol [40 mol%]: Tg = 30 ° C., [H]) 51
20% by weight of polyvinyl alcohol having a saponification degree of 86 to 89% by mole, 10% by weight of crosslinked acrylic resin particles having an average particle diameter of 40 nm, 10% by weight of the compound (O) represented by the formula (I-1), and An aqueous coating solution having a composition of 9% by weight of oxyethylene lauryl ether and having a solid content of 4% by weight was applied by a roll coater.

【０１１４】同時に一軸延伸フィルムのもう片面に、帯
電防止性塗膜層用水性塗液としてテレフタル酸（２２ｍ
ｏｌ％）、イソフタル酸（１ｍｏｌ％）、２，６−ナフ
タレンジカルボン酸（６５ｍｏｌ％）、４，４´−ジフ
ェニルジカルボン酸（１２ｍｏｌ％）、エチレングリコ
ール（７５ｍｏｌ％）、１，４−シクロヘキサンジメタ
ノール（１０ｍｏｌ％）、ネオペンチルグリコール（１
５ｍｏｌ％）からつくられた共重合ポリエステル（Ｔｇ
＝８０℃、平均分子量＝２１，５００）（Ｆ−１）７５
ｗｔ％、前記式（II−３）で示される高分子帯電防止剤
（Ｅ）２０ｗｔ％およびポリオキシエチレンラウリルエ
ーテル５ｗｔ％からなる固形分組成の１０ｗｔ％水性塗
液を４ｇ／ｍ²（ｗｅｔ）の塗布量でロールコーターに
て塗布した。水性塗液を塗布した一軸延伸フィルムを乾
燥しつつ横方向に４倍延伸し、更に２３０℃で熱固定し
て厚さ１００μｍの二軸延伸フィルムを得た。このフィ
ルムでの塗膜厚さは０．０５μｍ、表面エネルギーは５
９ｄｙｎｅ／ｃｍ、光沢度が６０、光線透過率は３％で
鮮映性、接着性、帯電防止性、および搬送性は良好であ
った。At the same time, on the other side of the uniaxially stretched film, terephthalic acid (22 m
ol%), isophthalic acid (1 mol%), 2,6-naphthalenedicarboxylic acid (65 mol%), 4,4'-diphenyldicarboxylic acid (12 mol%), ethylene glycol (75 mol%), 1,4-cyclohexanedimethanol (10 mol%), neopentyl glycol (1
5mol%) (Tg
= 80 ° C, average molecular weight = 21,500) (F-1) 75
4 g / m ² (wet) of a 10 wt% aqueous coating liquid having a solid content composition comprising 20 wt% of a polymer antistatic agent (E) represented by the above formula (II-3) and 5 wt% of polyoxyethylene lauryl ether represented by the above formula (II-3). With a roll coater. The uniaxially stretched film coated with the aqueous coating solution was stretched 4 times in the transverse direction while drying, and further heat-set at 230 ° C. to obtain a biaxially stretched film having a thickness of 100 μm. The film thickness of this film is 0.05 μm and the surface energy is 5
9 dyne / cm, glossiness was 60, light transmittance was 3%, and clearness, adhesion, antistatic properties, and transportability were good.

【０１１５】[0115]

【表７】 [Table 7]

【０１１６】[0116]

【発明の効果】本発明はインク受像層易接着ポリエステ
ルフィルムに関し、更に詳しくは隠蔽性に優れ、インク
ジェットプリンター等の水性インク受像層に対する耐水
接着性に優れ、かつ搬送性、帯電防止性に優れた、受像
紙用に有用なインク受像層易接着ポリエステルフィルム
に関する。Industrial Applicability The present invention relates to a polyester film having an ink-receiving layer which is easy to adhere to, and more particularly to an excellent concealing property, excellent water-resistant adhesion to an aqueous ink-receiving layer of an ink jet printer or the like, and excellent transportability and antistatic property. And an ink-receiving layer which is useful for an image-receiving paper.

───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2H086 BA12 BA15 BA19 BA24 BA31 BA35 BA36 BA41 BA45 4F006 AA35 AB12 AB20 AB34 AB35 AB43 BA01 BA07 CA01 DA04 4F100 AH02B AH02H AK21B AK25C AK41A AK41B AK41C AK53B AK53H AL01B AL05B BA03 BA07 BA10B BA10C BA15 CA18C CA22C CC00B CC00C DE01B DE01H EJ38A GB90 HB00 JA03A JA05B JA20B JG03C JL10 JL11B JN02 JN21 YY00 YY00A YY00B YY00C 4J038 CE022 CG002 DB152 DD001 KA09 KA20 MA13 NA20 PC08 ──────────────────────────────────────────────────続 き Continued on the front page F-term (reference) 2H086 BA12 BA15 BA19 BA24 BA31 BA35 BA36 BA41 BA45 4F006 AA35 AB12 AB20 AB34 AB35 AB43 BA01 BA07 CA01 DA04 4F100 AH02B AH02H AK21B AK25C AK41B CA18C CA22C CC00B CC00C DE01B DE01H EJ38A GB90 HB00 JA03A JA05B JA20B JG03C JL10 JL11B JN02 JN21 YY00 YY00A YY00B YY00C 4J038 CE022 CG002 DB152 DD001 KA09 KA20 MA13 NA20 PC08

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 ポリエステルフィルムの片面にインク受
像層易接着塗膜を設け、もう一方の面に帯電防止性塗膜
を設けた積層フィルムであって、インク受像層易接着塗
膜は二次転移点が２０〜９０℃であるコポリエステル
（Ａ）３０〜８０重量％、ケン化度８０〜９０ｍｏｌ％
のポリビニルアルコール（Ｂ）１５〜４５重量％、平均
粒径が２０〜８０ｎｍの微粒子（Ｃ）３〜２５重量％及
び下記式（Ｉ）で示される化合物（Ｄ）５〜２０重量％
からなる組成物を主成分とし、該インク受像層易接着塗
膜の表面エネルギーが５０〜７０ｍＮ／ｍであることを
特徴とするインク受像層易接着ポリエステルフィルム。 【化１】 1. A laminated film in which an ink-receiving layer easy-adhesion coating film is provided on one surface of a polyester film and an antistatic coating film is provided on the other surface, wherein the ink-image receiving layer easy-adhesion coating film is secondarily transferred. Copolyester (A) having a point of 20 to 90 ° C, 30 to 80% by weight, saponification degree 80 to 90 mol%
15 to 45% by weight of polyvinyl alcohol (B), 3 to 25% by weight of fine particles (C) having an average particle diameter of 20 to 80 nm, and 5 to 20% by weight of a compound (D) represented by the following formula (I).
And a surface energy of the ink-receiving layer easy-adhesion coating film is 50 to 70 mN / m. Embedded image 【請求項２】 帯電防止性塗膜が、ポリカチオンポリマ
ーからなる帯電防止剤（Ｅ）５〜５０重量％と、ポリエ
ステル樹脂（Ｆ−１）、アクリル樹脂（Ｆ−２）からな
る群から選ばれた少なくとも一種のバインダー樹脂
（Ｆ）４０〜８５重量％とを含む塗膜である請求項１に
記載のインク受像層易接着ポリエステルフィルム。2. The antistatic coating film is selected from the group consisting of 5 to 50% by weight of an antistatic agent (E) composed of a polycation polymer, a polyester resin (F-1) and an acrylic resin (F-2). The ink-receiving layer easily adhesive polyester film according to claim 1, which is a coating film containing 40 to 85% by weight of at least one binder resin (F). 【請求項３】 帯電防止性塗膜が、ポリエステル樹脂
（Ｆ−１）及びアクリル樹脂（Ｆ−２）から選ばれる少
なくとも１種のバインダー樹脂（Ｆ）４０〜８５重量
％、下記式（II）で示される構造の繰り返し単位を主成
分とする帯電防止剤（Ｅ）５〜５０重量％及び界面活性
剤（Ｇ）５〜１５重量％を含む塗膜である請求項２に記
載のインク受像層易接着ポリエステルフィルム。 【化２】 （ただし、式中のＲ¹、Ｒ²はそれぞれＨ又はＣＨ₃、Ｒ³は
炭素数が２〜１０のアルキレン基、Ｒ⁴、Ｒ⁵はそれぞれ
炭素数が１〜５の飽和炭化水素基、Ｒ⁶は炭素数が２〜１
０のアルキレン基、ｐは１〜２０の数、ｑは１〜４０の
数、Ｙ^-はハロゲンイオン、モノもしくはポリハロゲン化
アルキルイオン、ナイトレートイオン、サルフェートイオ
ン、アルキルサルフェートイオン、スルホネートイオン又
はアルキルスルホネートイオンである。）3. An antistatic coating film comprising 40 to 85% by weight of at least one binder resin (F) selected from a polyester resin (F-1) and an acrylic resin (F-2); The ink image-receiving layer according to claim 2, wherein the coating film contains 5 to 50% by weight of an antistatic agent (E) and 5 to 15% by weight of a surfactant (G) having a repeating unit represented by the following formula as a main component. Easy adhesion polyester film. Embedded image (However, R ¹ and R ² in the formula are each H or CH ₃ , R ³ is an alkylene group having 2 to 10 carbon atoms, R ⁴ and R ⁵ are each a saturated hydrocarbon group having 1 to 5 carbon atoms, R ⁶ has 2 to 1 carbon atoms
0 is an alkylene group, p is a number from 1 to 20, q is a number from 1 to 40, Y ^- is a halogen ion, mono- or polyhalogenated alkyl ion, nitrate ion, sulfate ion, alkyl sulfate ion, sulfonate ion or alkyl. It is a sulfonate ion. ) 【請求項４】 ポリエステルフィルムの光沢度が５０以
上、光線透過率が２０％以下であり、かつ白色である請
求項１に記載のインク受像層易接着ポリエステルフィル
ム。4. The polyester film according to claim 1, wherein the polyester film has a glossiness of 50 or more, a light transmittance of 20% or less, and is white. 【請求項５】 ポリエステルフィルムが、１５０℃で３
０分間保持したときの熱収縮率が１％以下の二軸延伸フ
ィルムである請求項１に記載のインク受像層易接着ポリ
エステルフィルム。5. A polyester film having a viscosity of 3 ° C. at 150 ° C.
The polyester film according to claim 1, which is a biaxially stretched film having a heat shrinkage of 1% or less when held for 0 minutes. 【請求項６】 ポリエステルフィルムの光線透過率が２
０％以下、かつ白色であり、インク受像層易接着塗膜の
上に更に水性インク受像層を設けて用いる請求項４に記
載のインク受像層易接着ポリエステルフィルム。6. The polyester film having a light transmittance of 2
5. The polyester film according to claim 4, wherein the polyester film is 0% or less, is white, and is further provided with an aqueous ink image-receiving layer on the ink-image-receiving layer easily adhesive coating film. 【請求項７】 インクジェットプリンター用受像紙に用
いる請求項６に記載のインク受像層易接着ポリエステル
フィルム。7. The polyester film according to claim 6, which is used for an image receiving paper for an ink jet printer.