JP2002002099A - Ink jet recording sheet - Google Patents
Ink jet recording sheetInfo
- Publication number
- JP2002002099A JP2002002099A JP2000186832A JP2000186832A JP2002002099A JP 2002002099 A JP2002002099 A JP 2002002099A JP 2000186832 A JP2000186832 A JP 2000186832A JP 2000186832 A JP2000186832 A JP 2000186832A JP 2002002099 A JP2002002099 A JP 2002002099A
- Authority
- JP
- Japan
- Prior art keywords
- recording sheet
- receiving layer
- ink
- ink jet
- jet recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、インクの吸収性お
よび発色性などの画像特性に優れ、かつ表裏の識別が容
易であるインクジェット記録用シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording sheet which is excellent in image characteristics such as ink absorbency and color forming property, and can be easily distinguished between front and back.
【０００２】[0002]
【従来の技術】近年、デジタルカメラの普及、およびコ
ンピュータの普及とともに、それらの画像を紙面などに
記録するためのハードコピー技術が急速に発達した。こ
れらハードコピーの究極の目標は銀塩写真であり、とく
に、色再現性、画像密度、光沢性および耐候性などをい
かに銀塩写真に近づけるかが、開発の課題となってい
る。ハードコピーの記録方式には、銀塩写真によって画
像を表示したディスプレーを直接撮影するもののほか、
昇華型熱転写方式、インクジェット方式、静電転写方式
など多種多様である。2. Description of the Related Art In recent years, with the spread of digital cameras and computers, hard copy technology for recording such images on paper or the like has rapidly developed. The ultimate goal of these hard copies is silver halide photography. In particular, how to bring color reproduction, image density, glossiness, weather resistance, etc. close to that of silver halide photography has been an issue for development. Hard copy recording methods include direct shooting of displays displaying images using silver halide photography,
There are various types such as a sublimation type thermal transfer method, an ink jet method, and an electrostatic transfer method.
【０００３】このうちインクジェット方式は、装置が比
較的小型であり、ランニングコストも低いなどの利点を
有し、昇華型熱転写方式などとともにハードコピー方式
の主流と見られている。インクジェット方式は、ノズル
から記録媒体に向けて色剤と多量の溶媒よりなるインク
液滴を高速で射出するものである。インクジェット方式
によるプリンターは、フルカラー化や高速化が容易なこ
とや、印字騒音が低いことなどから、近年急速に普及し
つつある。Among them, the ink jet system has advantages such as a relatively small apparatus and low running cost, and is considered to be the mainstream of the hard copy system together with the sublimation type thermal transfer system and the like. In the ink jet method, ink droplets composed of a colorant and a large amount of a solvent are ejected from a nozzle toward a recording medium at a high speed. 2. Description of the Related Art Inkjet printers have been rapidly spreading in recent years due to the fact that full color printing and high speed printing are easy and printing noise is low.
【０００４】記録シートとしては、通常、白色度の高い
支持体に、白色度の高い不透明性のインク受容層を塗布
したり、あるいは、透明性の高いインク受容層を塗布す
ることで、銀塩写真印画紙に近い風合いを持たせてい
る。しかしながら、これらのインクジェト記録シート
は、インク受容層が白色か透明であるため、支持体と同
じ色相を有するために表裏の識別が難しい。このため、
誤ってインク受容性の劣る裏面に印刷をすることがあ
り、その場合記録シートがインクを吸収しないため、溢
れたインクがプリンター内部を汚染することがある。[0004] A recording sheet is usually prepared by applying an opaque ink-receiving layer having a high whiteness to a support having a high whiteness, or by applying an ink-receiving layer having a high transparency to a silver salt. It has a texture close to that of photographic paper. However, since these ink jet recording sheets have the same hue as the support because the ink receiving layer is white or transparent, it is difficult to distinguish between the front and back. For this reason,
In some cases, printing is performed on the back surface having poor ink receptivity, in which case the recording sheet does not absorb the ink, and the overflowed ink may contaminate the inside of the printer.
【０００５】カール現象を防止するために、表面のイン
ク受容層とほぼ同じ物性を有する裏面塗工層を形成した
インクジェット記録シートも提案されているが、多くの
場合、裏面塗工層も支持体と同じ白色を有するために表
裏の識別が容易ではない。[0005] In order to prevent the curl phenomenon, an ink jet recording sheet having a back coating layer having substantially the same physical properties as the ink receiving layer on the front surface has been proposed. It is not easy to identify the front and back because it has the same white color.
【０００６】その解決策として、裏面にグラビア印刷な
どによりロゴ印刷を施し、表裏の識別性を付与すること
が知られている。しかしながら、裏面に印刷する場合
は、支持体に事前に印刷をするか、またはインク受容層
塗工後に印刷をすることとなり、工程が増えコスト的に
不利である。さらに塗工後に印刷する場合、インク受容
層の光沢度の高い用紙は、光沢面が印刷機の搬送ローラ
ーで擦られて、折角の光沢面が擦傷により性状が劣化す
ることがある。[0006] As a solution, it is known to print a logo on the back surface by gravure printing or the like to impart distinction between the front and back surfaces. However, in the case of printing on the back surface, printing is performed in advance on the support or after the ink receiving layer is applied, which is disadvantageous in terms of the number of steps and the cost. Further, when printing is performed after coating, the glossy surface of the paper having a high glossiness of the ink receiving layer may be rubbed by the conveying roller of the printing machine, and the glossy surface at the corner may be deteriorated due to abrasion.
【０００７】[0007]
【発明が解決しようとする課題】本発明の目的は、大き
なコストの上昇を伴うことなく、表裏の識別が容易にか
つ確実にでき、インクの吸収性および発色性、審美性な
どの本来の画像特性や商品価値を損なうことのない、イ
ンクジェット記録用シートを提供することを目的とす
る。SUMMARY OF THE INVENTION An object of the present invention is to make it possible to easily and reliably identify the front and back sides without a large increase in cost, and to improve the original image quality such as ink absorbency, color development and aesthetics. An object of the present invention is to provide an inkjet recording sheet that does not impair characteristics or commercial value.
【０００８】[0008]
【課題を解決するための手段】本発明のインクジェット
記録用シートは、支持体の一面にインク受容層、その反
対面に裏面塗工層を設けたインクジェット記録シートに
おいて、前記裏面塗工層が着色物質を含有し、かつ前記
インク受容層面と前記裏面塗工層面との、ＪＩＳ Ｚ８
７３０によるL*a*b*表色系における色差 ΔE*ab＝〔(Δ
L*)2＋(Δa*)2＋(Δb*)2〕1/2が、５〜４０であること
を特徴とする。According to the present invention, there is provided an ink jet recording sheet comprising an ink receiving layer on one side of a support and a back side coating layer on the opposite side, wherein the back side coating layer is colored. JIS Z8, which contains a substance, and the surface of the ink receiving layer and the surface of the back coating layer
730, the color difference ΔE * ab = [((Δ
L *) 2 + (Δa *) 2 + (Δb *) 2 ] 1/2 is from 5 to 40.
【０００９】本発明によれば、インクジェット記録シー
トにおける表裏の識別が容易にかつ確実にできるが、本
発明において、裏面塗工層に着色物質を添加すること、
およびその場合において、インク受容層との色相の差が
所定の範囲になるようにすることが、上記本発明の目的
の達成のために必要であることが判明した。According to the present invention, the front and back sides of the ink jet recording sheet can be easily and reliably identified.
In that case, it has been found that it is necessary to make the difference in hue from the ink receiving layer within a predetermined range in order to achieve the object of the present invention.
【００１０】すなわち、着色物質をインク受容層に含有
させた場合には、カラー画像の場合はもちろん、モノ黒
のときも得られる画像の色相が変わってしまうので好ま
しくない。一方で、裏面途工層に着色物質を含有させる
場合も、インク受容層との色差大きすぎる場合には、表
面に得られる画像に影響するので好ましくない。That is, when a coloring substance is contained in the ink receiving layer, the hue of the obtained image is changed not only in the case of a color image but also in the case of a monochrome image, which is not preferable. On the other hand, when the coloring material is contained in the back surface processing layer, if the color difference from the ink receiving layer is too large, the image obtained on the surface is unfavorably affected.
【００１１】本発明によれば、裏面途工層に着色物質を
含有させて得られる色相と、表面のインク受容層の色相
との、上記ＪＩＳ Ｚ８７３０によるL*a*b*表色系によ
る色差 ΔE*ab＝〔(ΔL*)2＋(Δa*)2＋(Δb*)2〕
1/2が、上記所定範囲の場合には、表面の画像の特性に
影響せず、また色相も極めて淡いものであるのでインク
ジェット記録シートとしての審美性が損なわれることが
なく、上記目的を達成できることを見出した。また、か
かる着色物質を添加する本発明は、裏面塗工層の形成と
同時にできるので記録シートの製造におけるコストの上
昇を招くこともない。以下に、本発明のインクジェット
記録シートについて更に詳しく説明する。According to the present invention, the color difference between the hue obtained by including the coloring material in the back surface working layer and the hue of the ink receiving layer on the front surface by the L * a * b * color system according to JIS Z8730. ΔE * ab = [(ΔL *) 2 + (Δa *) 2 + (Δb *) 2 ]
In the case where 1/2 is within the above-mentioned predetermined range, the above-mentioned object is achieved without affecting the properties of the image on the surface, and the hues as the ink jet recording sheet are not impaired because the hue is also extremely light. I found what I could do. Further, since the present invention in which such a coloring substance is added can be formed at the same time as the formation of the backside coating layer, there is no increase in cost in the production of the recording sheet. Hereinafter, the inkjet recording sheet of the present invention will be described in more detail.
【００１２】[0012]
【発明の実施の形態】本発明の記録シートにおける支持
体としては、特定のものに制限されるものではないが、
色相は白色、淡色または透明色が好ましく、本発明では
効果的である。その材料は、特に限定されるものではな
く、一般に塗工紙分野で使用される酸性紙、中性紙、コ
ーテッド紙、フィルム、合成紙などの紙化処理したフィ
ルムなどが使用できる。フィルムとしては、ポリエチレ
ンテレフタレート、ポリブチレンナフタレート、ポリエ
ステルジアセテートなどのポリエステル樹脂フィルム、
ポリカーボネート樹脂フィルム、ＥＴＦＥなどのフッ素
系樹脂シートなどを挙げることができる。これらの支持
体の厚みは、好ましくは、４０ 〜３００μｍであり、
その表面には、接着性を改善するために適宜コロナ処理
や放電処理を施したり、アンダーコートなどを設けるこ
とができる。DESCRIPTION OF THE PREFERRED EMBODIMENTS The support in the recording sheet of the present invention is not limited to a specific one,
The hue is preferably white, light color or transparent color, and is effective in the present invention. The material is not particularly limited, and a paper-treated film such as an acidic paper, a neutral paper, a coated paper, a film, and a synthetic paper generally used in the coated paper field can be used. As the film, polyethylene terephthalate, polybutylene naphthalate, polyester resin film such as polyester diacetate,
Examples thereof include a polycarbonate resin film and a fluorine-based resin sheet such as ETFE. The thickness of these supports is preferably 40 to 300 μm,
The surface may be appropriately subjected to a corona treatment or a discharge treatment to improve the adhesiveness, or may be provided with an undercoat or the like.
【００１３】本発明におけるインク受容層は、顔料の微
粒子間の空隙にインクを受容させる、いわゆる空隙型受
容層であっても、水溶性樹脂にインクを膨潤定着させ
る、いわゆる膨潤型受容層であってもよい。The ink-receiving layer in the present invention is a so-called swelling-type receiving layer, which is a so-called void-type receiving layer in which the ink is received in the spaces between the pigment fine particles, and which swells and fixes the ink in the water-soluble resin. You may.
【００１４】上記空隙型のインク受容層は、主に顔料と
結着剤からなり、顔料としては、コロイダルシリカ、ア
ルミナゾル、ベーマイトゾル、合成微粒子シリカ、合成
微粒子アルミナシリケート、気相法合成シリカ、ゼオラ
イト、モンモリロナイト群鉱物、バイデライト群鉱物、
サポナイト群鉱物、ヘクトライト群鉱物、スチーブンサ
イト群鉱物、ハイドロタルサイト群鉱物、スメクタイト
群鉱物、ベントナイト群鉱物、炭酸カルシウム、炭酸マ
グネシウム、硫酸カルシウム、硫酸バリウム、ニ酸化チ
タン、チタンゾル、酸化亜鉛、炭酸亜鉛、珪酸アルミニ
ウム、珪酸カルシウム、珪酸マグネシウム、カオリン、
タルク、酸化アルミニウム、水酸化アルミニウム、ポリ
水酸化アルミニウム化合物、アルミナ水和物、プラスチ
ックピグメント、尿素樹脂顔料、セルロース粒子、澱粉
粒子、クレー、サチンホワイトなどが挙げられ、なかで
も、コロイダルシリカ、アルミナゾル、ベーマイトゾ
ル、合成微粒子シリカが好ましい。The void-type ink receiving layer is mainly composed of a pigment and a binder, and examples of the pigment include colloidal silica, alumina sol, boehmite sol, synthetic fine particle silica, synthetic fine particle alumina silicate, vapor-phase synthetic silica, and zeolite. , Montmorillonite group minerals, beidellite group minerals,
Saponite mineral, hectorite mineral, stevensite mineral, hydrotalcite mineral, smectite mineral, bentonite mineral, calcium carbonate, magnesium carbonate, calcium sulfate, barium sulfate, titanium dioxide, titanium sol, zinc oxide, carbonate Zinc, aluminum silicate, calcium silicate, magnesium silicate, kaolin,
Talc, aluminum oxide, aluminum hydroxide, polyaluminum hydroxide compound, alumina hydrate, plastic pigment, urea resin pigment, cellulose particles, starch particles, clay, satin white, etc., among others, colloidal silica, alumina sol, Boehmite sol and synthetic particulate silica are preferred.
【００１５】上記結着剤としては、でんぷんまたはその
変性物、ポリビニルアルコールまたはその変性物，スチ
レン・ブタジエンゴム（ＳＢＲ）ラテックス，ニトリル
・ブタジエンゴムラテックス、メチルセルロース、ヒド
ロキシセルロース、ヒドロキシメチルセルロース、カル
ボキシメチルセルロース、ゼラチン、ポリビニルピロリ
ドン、ポリアクリル酸、ポリアクリルアミドなどの水溶
性重合体、アルコール可溶性の重合体若しくはこれらの
重合体の混合物などを用いることができる。なかでも、
本発明では、インク吸収性や耐水性が良好であることか
ら、ポリビニルアルコールまたはその変性物の使用が好
ましい。結着剤は，インク受容層における上記顔料１０
０質量部に対して、好ましくは、１〜３０質量部、特に
は、３〜１５質量部含まれるのが適切である。Examples of the binder include starch or a modified product thereof, polyvinyl alcohol or a modified product thereof, styrene-butadiene rubber (SBR) latex, nitrile-butadiene rubber latex, methylcellulose, hydroxycellulose, hydroxymethylcellulose, carboxymethylcellulose, gelatin And water-soluble polymers such as polyvinylpyrrolidone, polyacrylic acid and polyacrylamide, alcohol-soluble polymers, and mixtures of these polymers. Above all,
In the present invention, use of polyvinyl alcohol or a modified product thereof is preferred because of good ink absorption and water resistance. The binder is the pigment 10 in the ink receiving layer.
It is suitable that the amount is preferably 1 to 30 parts by mass, particularly preferably 3 to 15 parts by mass with respect to 0 parts by mass.
【００１６】上記膨潤型のインク受容層としては、主に
水溶性樹脂からなり、該水溶性樹脂とは、完全鹸化ない
しは部分鹸化のポリビニルアルコール、変性ポリビニル
アルコール、エチレンビニルアルコール、ポリビニルピ
ロリドン、ポリアルキレンオキサイドなどの合成高分子
水溶性樹脂、ゼラチン、変性ゼラチン、デンプン、変性
デンプン、カゼイン、大豆カゼイン、変性大豆カゼイ
ン、セルロース誘導体（メチルセルロース、エチルセル
ロース、カルボキシメチルセルロース、ヒドロキシエチ
ルセルロース、ヒドロキシプロピルセルロース、ヒドロ
キシプロピルメチルセルロース、ニトロセルロースな
ど）などの天然高分子水溶性樹脂が挙げられる。これら
２種以上を適宜選択して使用することも可能である。The swellable ink-receiving layer is mainly composed of a water-soluble resin, which is completely or partially saponified polyvinyl alcohol, modified polyvinyl alcohol, ethylene vinyl alcohol, polyvinyl pyrrolidone, polyalkylene. Synthetic polymer water-soluble resin such as oxide, gelatin, modified gelatin, starch, modified starch, casein, soy casein, modified soy casein, cellulose derivatives (methyl cellulose, ethyl cellulose, carboxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxypropyl methyl cellulose, And natural polymer water-soluble resins such as nitrocellulose. These two or more types can be appropriately selected and used.
【００１７】本発明において、支持体上に設けられるイ
ンク受容層の厚みは、インク吸収性、塗工層の強度、用
途などに応じても選択されるが、乾燥後の厚みとして、
好ましくは、５〜１００μｍが採用される。この厚みが
５μｍに満たない場合はインク受容層としての効果が発
現し難く、一方，１００μｍを超える場合は、透明性や
強度が低下するおそれがあるので好ましくない。なかで
も、インク受容層の厚みは、５〜５０μｍであるのが適
切である。In the present invention, the thickness of the ink receiving layer provided on the support is selected depending on the ink absorption, the strength of the coating layer, the application, and the like.
Preferably, 5 to 100 μm is employed. When the thickness is less than 5 μm, the effect as an ink receiving layer is hardly exhibited, while when the thickness is more than 100 μm, transparency and strength may be reduced, which is not preferable. In particular, the thickness of the ink receiving layer is suitably from 5 to 50 μm.
【００１８】支持体面にインク受容層を設ける手段は、
例えば、顔料に結着剤を加えてスラリー状とし、ロール
コーター、エアナイフコーター、ブレードコーター、ロ
ッドコーター、バーコーター、コンマコーター、グラビ
アコーター、ダイコーター、カーテンコーター、スプレ
ーコーター、スライドダイコーターなどを用いて塗工
し、乾燥する方法を採用することができる。Means for providing an ink receiving layer on the support surface includes:
For example, by adding a binder to a pigment to form a slurry, using a roll coater, an air knife coater, a blade coater, a rod coater, a bar coater, a comma coater, a gravure coater, a die coater, a curtain coater, a spray coater, a slide die coater, or the like. Coating and drying.
【００１９】このようにして形成されたインク受容層の
表面を、更に、スーパーカレンダー、グロスカレンダー
などの装置を使用し、温度が好ましくは、０〜１６０
℃、特には、３０〜１００℃、圧力が好ましくは、５０
〜４００ｋN／m、特には、１００〜２５０ｋN／mにてロ
ール間を通過させることで、カレンダー処理により光沢
を付与してもよい。かかる光沢の付与は、インク受容層
を形成する際、その表面を平滑な成形面と接した状態で
乾燥、離型する、いわゆるキャスト被覆によって行って
もよい。The surface of the ink receiving layer thus formed is further subjected to a temperature of preferably 0 to 160 using an apparatus such as a super calender or a gloss calender.
° C, especially 30 to 100 ° C, pressure is preferably 50
Gloss may be imparted by calendering by passing between rolls at a pressure of 400 to 400 kN / m, particularly 100 to 250 kN / m. When forming the ink receiving layer, the gloss may be imparted by so-called cast coating in which the surface of the ink receiving layer is dried and released in contact with a smooth molding surface.
【００２０】本発明の記録シートにおける裏面塗工層を
形成する材料としては、着色物質以外に、上記したイン
ク受容層について記載した顔料および結着剤を含むこと
が好ましい。なかでも、裏面塗工層の材料としては、カ
オリン、クレー、タルク、サチンホワイト、ニ酸化チタ
ン、水酸化アルミニウムなどが、水に分散しやすい、塗
工液にしたときの粘性が適当で製造しやすい、化学的に
不活性である、適当な粒径分布のものが入手しやすい、
さらに価額などの点で好ましい。裏面塗工層における結
着剤の使用量、および裏面塗工層の厚みについても、上
記したインク受容層について記載した範囲から選ばれ
る。The material for forming the back coating layer in the recording sheet of the present invention preferably contains, in addition to the coloring substance, the pigment and the binder described for the ink receiving layer. Among them, kaolin, clay, talc, satin white, titanium dioxide, aluminum hydroxide, etc. are easily dispersed in water, and the viscosity of the coating liquid is appropriate. Easy, chemically inert, suitable particle size distribution is readily available,
Further, it is preferable in terms of price and the like. The amount of the binder used in the backside coating layer and the thickness of the backside coating layer are also selected from the ranges described above for the ink receiving layer.
【００２１】そして、本発明では、かかる裏面塗工層に
対して、着色物質が添加され、添加された裏面塗工層と
表面のインク受容層との色相の差である色差が所定の範
囲になるようにされる。すなわち、この場合の色差は、
ＪＩＳ Ｚ８７３０によるL*a*b*表色系による色差。す
なわち、ΔE*ab＝〔(ΔL*)2＋(Δa*)2＋(Δb*)2〕1/2で
表され、かかる色差が５〜４０になるようにされる。か
かる色差が、５より小さい場合には、表裏の識別が困難
である。なかでも、上記色差が７以上が好ましいことが
判明した。In the present invention, a coloring substance is added to the back coating layer, and the color difference, which is the difference in hue between the added back coating layer and the ink receiving layer on the surface, falls within a predetermined range. To be. That is, the color difference in this case is
Color difference by L * a * b * color system according to JIS Z8730. That is, ΔE * ab = [(ΔL *) 2 + (Δa *) 2 + (Δb *) 2 ] 1/2 , and the color difference is set to 5 to 40. If the color difference is smaller than 5, it is difficult to distinguish between the front and back sides. Among them, it was found that the color difference was preferably 7 or more.
【００２２】インク受容層または裏面塗工層との色差
ば、表裏の識別のためには、大きい方が好ましいが、大
き過ぎる場合には、着色物質の添加量が大きくなり、表
面のインク受容層の形成される画像に悪影響するとも
に、コスト的にも不利になるので４０以下である。本発
明では、３０ 以下、特には、１５ 以下であるのが好ま
しいことが見出された。なお、裏面塗工層における色相
は、面全体にわたって均一であるのが好ましい。The color difference between the ink receiving layer and the back coating layer is preferably large for discrimination between the front and back sides. However, if the color difference is too large, the amount of the coloring substance added becomes large, and the ink receiving layer on the front surface becomes large. Is not more than 40 because it adversely affects the image formed and has a disadvantage in cost. In the present invention, it has been found that it is preferably 30 or less, particularly preferably 15 or less. In addition, it is preferable that the hue in the back coating layer is uniform over the entire surface.
【００２３】裏面塗工層に添加される着色物質として
は、染料または着色顔料が使用できる。染料としては、
カチオン性直接染料、アニオン性直接染料、両性染料、
塩基性染料、蛍光染料などが使用できる。また、着色顔
料としては、非イオン性水分散顔料、アニオン性水分散
顔料、カチオン性水分散顔料などの水分散顔料が好まし
く使用できる。As the coloring substance added to the back coating layer, a dye or a coloring pigment can be used. As a dye,
Cationic direct dye, anionic direct dye, amphoteric dye,
Basic dyes, fluorescent dyes and the like can be used. As the color pigment, a water-dispersible pigment such as a nonionic water-dispersed pigment, an anionic water-dispersed pigment, or a cationic water-dispersed pigment can be preferably used.
【００２４】支持体に対して、裏面塗工層を設ける手段
は、上記したインク受容層について記載した手段か選ば
れた適宜のものが使用できる。As the means for providing the back surface coating layer on the support, any of the means described for the ink receiving layer described above and any suitable means can be used.
【００２５】[0025]
【実施例】以下に、実施例を挙げて本発明をより具体的
に説明する。例１、４、５は、本発明の実施例であり、
例２、３は、比較例である。また、本発明は勿論これら
に限定されて解釈されるものではない。また、例中の部
は特に断らない限り、質量部を示す。The present invention will be described below more specifically with reference to examples. Examples 1, 4, and 5 are examples of the present invention,
Examples 2 and 3 are comparative examples. The present invention is, of course, not construed as being limited to these. Parts in the examples are parts by mass unless otherwise specified.
【００２６】［例１］坪量１５７ｇ／ｍ2を有する上質
紙の片側の表面に、下記のインク受容層処方１を、バー
コーターを用いて乾燥後の塗工厚が１５μmとなるよう
に塗工し、１２０℃ にて乾燥し、インク受容層を有す
るシートを得た。 インク受容層処方１ アルミナゾル（触媒化成社製、商品名：カタロイドＡＳ
−３）：１００部、ポリビニルアルコール（クラレ社
製、商品名：ＰＶＡ−１２４）：１０部。 上記インク受容層を片面に有するシートの裏面に、下記
の裏面塗工層処方１を、バーコーターを用いて乾燥後の
塗工厚が１０μｍとなるように塗工し、１２０℃にて乾
燥し、インクジェット記録シートを得た。[Example 1] The following ink receiving layer formulation 1 was coated on one surface of a high-quality paper having a basis weight of 157 g / m 2 using a bar coater so that the coating thickness after drying was 15 μm. After drying at 120 ° C., a sheet having an ink receiving layer was obtained. Ink receiving layer formulation 1 Alumina sol (catalyst AS
-3): 100 parts, polyvinyl alcohol (Kuraray Co., trade name: PVA-124): 10 parts. On the back surface of the sheet having the ink receiving layer on one side, the following back coating layer formulation 1 was applied using a bar coater so that the coating thickness after drying was 10 μm, and dried at 120 ° C. Thus, an ink jet recording sheet was obtained.
【００２７】裏面塗工層処方１ カオリン（エンゲルハルト社製、商品名：ULTRA WHITE
90）、１００部、 SBRラテックス（住友A＆L社製、商品
名：SN307）：２０部、着色顔料（大日精化工業社製、
商品名：TB-110 yellow 2G） ：０．０２部、着色顔料
（大日精化工業社製、商品名：ＴB-510 black TR）：
０．００５部。 かくして得られるインクジェット記録シートは、インク
受容層の色相が L*／a*／b*＝９７．０５／０．６５／
２．２３であり、裏面塗塗工層の色相が L*／a*／b*
＝９４．１６／０．０１／８．０２であるので、両者の
色差は６．５であった。Backside coating layer formulation 1 Kaolin (Engelhard Co., trade name: ULTRA WHITE
90), 100 parts, SBR latex (manufactured by Sumitomo A & L Co., trade name: SN307): 20 parts, coloring pigment (manufactured by Dainichi Seika Kogyo Co., Ltd.)
Product name: TB-110 yellow 2G): 0.02 parts, coloring pigment (manufactured by Dainichi Seika Kogyo Co., Ltd., product name: TB-510 black TR):
0.005 parts. The ink jet recording sheet thus obtained has a hue of the ink receiving layer of L * / a * / b * = 97.05 / 0.65 /
2.23, and the hue of the back coating layer is L * / a * / b *
= 94.16 / 0.01 / 8.02, so the color difference between the two was 6.5.
【００２８】［例２］例１において、裏面塗工層１の代
わりに、下記の裏面塗工層処方２を用いて製造したほか
は、上記例１と同様にしてンクジェット記録シートを得
た。 裏面塗工層処方２ カオリン（エンゲルハルト社製、商品名：ULTRA WHITE
90）： １００部、 SBRラテックス（住友A＆L社製、商
品名：SN307）、２０部、着色顔料（大日精化工業社
製、商品名：TB-110 yellow 2G）０．０１部、着色顔料
（大日精化工業社製、商品名：TB-510 black TR）：
０．００５部。 かくして得られるインクジェット記録シートは、インク
受容層の色相が L*／a*／b*＝９７．１２／０．６６
／２．１１であり、裏面塗塗工層の色相がL*／a*／b*＝
９４．２１／０．０２／５．４８であるので、両者の色
差は４．５であった。Example 2 An ink jet recording sheet was obtained in the same manner as in Example 1 except that in Example 1, the following back coating layer formulation 2 was used in place of the back coating layer 1. . Back coating layer formulation 2 Kaolin (Engelhardt, product name: ULTRA WHITE
90): 100 parts, SBR latex (manufactured by Sumitomo A & L Co., trade name: SN307), 20 parts, coloring pigment (manufactured by Dainichi Seika Industries, trade name: TB-110 yellow 2G) 0.01 part, coloring pigment ( Dainichi Seika Industry Co., Ltd., trade name: TB-510 black TR):
0.005 parts. The thus obtained ink jet recording sheet has a hue of the ink receiving layer of L * / a * / b * = 97.12 / 0.66.
/2.11, and the hue of the back coating layer is L * / a * / b * =
Since the ratio was 94.21 / 0.02 / 5.58, the color difference between the two was 4.5.
【００２９】［例３］例１において、裏面塗工層１の代
わりに、下記の裏面塗工層処方３を用いて製造したほか
は、上記例１と同様にしてンクジェット記録シートを得
た。 裏面塗工層処方３ カオリン（エンゲルハルト社製、商品名：ULTRA WHITE
90）：１００部、 SBRラテックス（住友A＆L社製、商
品名：SN307）：２０部。 かくして得られるインクジェット記録シートは、インク
受容層の色相が L*／a*／b*＝９７．２０／０．６８
／２．０２であり、裏面塗塗工層の色相が L*／a*／b*
＝９６．２１／０．０２／３．７５であるので、両者の
色差は２．１であった。[Example 3] An ink jet recording sheet was obtained in the same manner as in Example 1 except that the following backside coating layer 1 was used in place of backside coating layer 1 and preparation was carried out. . Back coating layer formulation 3 Kaolin (Engelhardt, product name: ULTRA WHITE
90): 100 parts, SBR latex (Sumitomo A & L, product name: SN307): 20 parts. In the ink jet recording sheet thus obtained, the hue of the ink receiving layer is L * / a * / b * = 97.20 / 0.68.
/2.02, and the hue of the back coating layer is L * / a * / b *
= 96.21 / 0.02 / 3.75, so the color difference between the two was 2.1.
【００３０】［例４］例１において、裏面塗工層１の代
わりに、下記の裏面塗工層処方４を用いて製造したほか
は、上記例１と同様にしてインクジェット記録シートを
得た。 裏面塗工層処方４ 炭酸カルシウム（白石カルシウム社製、商品名：ブリリ
アントＳ１５）：１００部、 SBRラテックス（住友A＆
L社製、商品名：SN307）：２０部、着色顔料（ＴＢ−１
１０ Ｙｅｌｌｏｗ Ｓ２Ｇ１：０．０２部、着色顔料
（ＴＢ―５１０Ｂｌａｃｋ ＴＲ）０．００５部。 かくして得られるインクジェット記録シートは、インク
受容層の色相が L*／a*／b*＝９７．０８／０．５１
／２．１４であり、裏面塗塗工層の色相が L*／a*／b*
＝９４．５８／０．１３／７．２５であるので、両者の
色差は５．７であった。[Example 4] An ink jet recording sheet was obtained in the same manner as in Example 1 except that the back coating layer 1 was replaced with the following back coating layer formulation 4 in Example 1. Backside coating layer formula 4 Calcium carbonate (Shiraishi Calcium Co., trade name: Brilliant S15): 100 parts, SBR latex (Sumitomo A &
Company L, trade name: SN307): 20 parts, coloring pigment (TB-1)
10 Yellow S2G1: 0.02 part, coloring pigment (TB-510Black TR) 0.005 part. In the ink jet recording sheet thus obtained, the hue of the ink receiving layer was L * / a * / b * = 97.08 / 0.51.
/2.14, and the hue of the back coating layer is L * / a * / b *
= 94.58 / 0.13 / 7.25, so the color difference between the two was 5.7.
【００３１】［例５］例１において、インク受容層１の
代わりに、下記のインク受容層処方２を用いて、乾燥後
の厚みを１０μｍに塗工したほかは、上記例１と同様に
してインクジェット記録シートを製造した。 インク受容層処方３ 合成微粒子シリカ（水沢化学社製、商品名：Ｐ７８
Ａ）：１００部、 ポリビニルアルコール（クラレ社
製、商品名：Ｒ−１１３０）：４０部。 かくして得られるインクジェット記録シートは、インク
受容層の色相が L*／a*／b*＝９５．２１／１．８６
／０．１３であり、裏面塗塗工層の色相が L*／a*／b*
＝９３．９２／３．６５／７．８２であるので、両者の
色差は８．０であった。Example 5 The procedure of Example 1 was repeated, except that the ink-receiving layer 1 was replaced with the following ink-receiving layer formulation 2 to a thickness of 10 μm after drying. An ink jet recording sheet was manufactured. Ink receiving layer formulation 3 Synthetic fine particle silica (trade name: P78, manufactured by Mizusawa Chemical Co., Ltd.)
A): 100 parts, polyvinyl alcohol (manufactured by Kuraray Co., trade name: R-1130): 40 parts. In the ink jet recording sheet thus obtained, the hue of the ink receiving layer is L * / a * / b * = 95.21 / 1.86.
/0.13, and the hue of the back coating layer is L * / a * / b *
= 93.92 / 3.65 / 7.82, so the color difference between the two was 8.0.
【００３２】上記の例１〜例５で得られたインクジェッ
ト記録シートについて、以下のようにして、インク受容
層と裏面塗工層の色相を測定し、［色差］および［表裏
識別性］を調べ、その結果を表１に示した。また、例１
〜例５の記録シートについて、下記に述べるようにし
て、［印刷性評価］および「環境カール性」を調べた。With respect to the ink jet recording sheets obtained in Examples 1 to 5, the hues of the ink receiving layer and the back coating layer were measured as follows, and [color difference] and [front / back discrimination] were examined. The results are shown in Table 1. Example 1
[Printability evaluation] and "Environmental curl" of the recording sheets of Examples to 5 were examined as described below.
【００３３】［色差］インク受容層面と裏面の色相（L*
a*b*）を、測色計（GRETAG社製、商品名： SPM100II）
を用いて測定し、色差ΔE*ab＝〔(ΔL*)2＋(Δa*)2＋
(Δb*)2〕1/2を算出した。[Color difference] Hue (L *) of the ink receiving layer surface and the back surface
a * b *) with a colorimeter (GRETAG, trade name: SPM100II)
And the color difference ΔE * ab = [(ΔL *) 2 + (Δa *) 2 +
(Δb *) 2 ] 1/2 was calculated.
【００３４】［表裏識別性］目視で表裏の識別性を調べ
た。 〇：容易に表裏が識別出来る ×：表裏識別が困難である。 表１に評価結果を示す。[Front / back discrimination] The front / back discrimination was visually inspected. 〇: The front and back can be easily identified ×: The front and back identification is difficult. Table 1 shows the evaluation results.
【００３５】[0035]
【表１】 表１に示されるように、本発明のインクジェット記録用
シートは、特に表裏識別が容易なインクジェット記録シ
ートであることがわかる。[Table 1] As shown in Table 1, it is understood that the ink jet recording sheet of the present invention is an ink jet recording sheet in which front and back sides can be easily distinguished.
【００３６】［印刷性評価］例１〜例５の記録シートの
インク受容層の面に対してインクジェットプリンター
（セイコーエプソン社製、商品名：ＰＭ８００Ｃ）を使
用して、イエロー、マゼンタ、シアンおよびブラックの
階調パターンに印刷した。いずれの記録物も十分なイン
ク吸収性と発色性を示した。[Evaluation of printability] Yellow, magenta, cyan and black were applied to the surfaces of the ink receiving layers of the recording sheets of Examples 1 to 5 using an ink jet printer (trade name: PM800C, manufactured by Seiko Epson Corporation). Was printed in the gradation pattern of. All of the recorded materials showed sufficient ink absorbency and coloring.
【００３７】「環境カール性」下記の３つの環境条件に
おいて、例１〜例５の記録シートをそのインク受容層が
上向きになるように24時間静置した。静置後における各
記録シートの４隅の水平面からの高さを測定し、その平
均値をカール値（単位：ｍｍ）とした。"Environmental curl" Under the following three environmental conditions, the recording sheets of Examples 1 to 5 were allowed to stand for 24 hours so that their ink receiving layers faced upward. The heights of the four corners of each recording sheet after standing were measured from the horizontal plane, and the average value was defined as a curl value (unit: mm).
【００３８】また、下記の３つの環境条件Ａ〜Ｃにおけ
る記録シートの上記カール値の最大値と最小値の差をカ
ール変動幅として、それらの結果を上記のカール値とと
もに、表２に示した。なお、カール値は、インク受容層
側にカールしているものを、＋（プラス）カールとし、
反対側にカールしているものを、−（マイナス）カール
とした。 環境条件 Ａ： 温度 ２０℃ 湿度 ２０％（相対湿度） 環境条件 Ｂ： 温度 ２０℃ 湿度 ６５％（相対湿度） 環境条件 Ｃ： 温度 ３０℃ 湿度 ８０％ＲＨFurther, the difference between the maximum value and the minimum value of the curl values of the recording sheet under the following three environmental conditions A to C is defined as a curl fluctuation width, and the results are shown in Table 2 together with the curl values. . The curl value is defined as a curl on the ink receiving layer side as + (plus) curl,
The curl on the opposite side was defined as-(minus) curl. Environmental conditions A: Temperature 20 ° C Humidity 20% (relative humidity) Environmental conditions B: Temperature 20 ° C Humidity 65% (relative humidity) Environmental conditions C: Temperature 30 ° C Humidity 80% RH
【００３９】[0039]
【表２】 [Table 2]
【００４０】[0040]
【発明の効果】本発明によれば、表裏の識別が容易にか
つ確実にできることはもちろん、そのために大きなコス
トの上昇を伴うことなく、さらには、インクの吸収性お
よび発色性、審美性、環境カール防止性などの本来の画
像特性や商品価値を損なうことのない、インクジェット
記録用シートが提供される。According to the present invention, the front and back sides can be easily and reliably distinguished, and therefore, there is no increase in cost, and further, the ink absorbency and color development, aesthetics, and environment are improved. Provided is an inkjet recording sheet which does not impair the original image characteristics such as curl prevention and the commercial value.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2H086 BA01 BA15 BA24 BA32 BA33 BA41 4L055 AG04 AG12 AG17 AG27 AG32 AG63 AG64 AG76 AG88 AH02 AH03 AH37 AJ01 AJ04 BE08 EA19 FA11 GA09 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 2H086 BA01 BA15 BA24 BA32 BA33 BA41 4L055 AG04 AG12 AG17 AG27 AG32 AG63 AG64 AG76 AG88 AH02 AH03 AH37 AJ01 AJ04 BE08 EA19 FA11 GA09
Claims (5)
に裏面塗工層を設けたインクジェット記録シートにおい
て、前記裏面塗工層が着色物質を含有し、かつ前記イン
ク受容層面と前記裏面塗工層面との、ＪＩＳ Ｚ８７３
０によるL*a*b*表色系における色差 ΔE*ab＝〔(ΔL*)2
＋(Δa*)2＋(Δb*)2〕1/2が、５〜４０であることを特
徴とするインクジェット記録用シート。1. An ink jet recording sheet comprising an ink receiving layer on one side of a support and a backside coating layer on the opposite side, wherein the backside coating layer contains a coloring substance, and the ink receiving layer side and the backside face each other. JIS Z873 with coating layer surface
Color difference in L * a * b * color system due to 0 ΔE * ab = [(ΔL *) 2
+ (Δa *) 2 + (Δb *) 2 ] 1/2 is from 5 to 40, wherein the sheet is an inkjet recording sheet.
は白色である請求項１に記載のインクジェット記録用シ
ート。2. The ink jet recording sheet according to claim 1, wherein the ink receiving layer is substantially colorless and transparent or white.
る請求項１または２に記載のインクジェット記録用シー
ト。3. The ink jet recording sheet according to claim 1, wherein the coloring substance is a dye or a coloring pigment.
む請求項１〜３のいずれか一つに記載のインクジェット
記録用シート。4. The ink jet recording sheet according to claim 1, wherein the ink receiving layer contains alumina hydrate.
１〜４のいずれか一つに記載のインクジェット記録用シ
ート。5. The ink jet recording sheet according to claim 1, wherein the back coating layer contains kaolin.