JP2001316530A - Polyolefin-based resin composition and resin film using the same - Google Patents
Polyolefin-based resin composition and resin film using the sameInfo
- Publication number
- JP2001316530A JP2001316530A JP2000133332A JP2000133332A JP2001316530A JP 2001316530 A JP2001316530 A JP 2001316530A JP 2000133332 A JP2000133332 A JP 2000133332A JP 2000133332 A JP2000133332 A JP 2000133332A JP 2001316530 A JP2001316530 A JP 2001316530A
- Authority
- JP
- Japan
- Prior art keywords
- ion
- inorganic powder
- resin film
- polyolefin
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、優れた保温性と優
れた透明性とをバランスよく有する樹脂フィルム、それ
を与えるポリオレフィン系樹脂組成物、および前記樹脂
フィルムの用途に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a resin film having a good balance between excellent heat retention and excellent transparency, a polyolefin resin composition providing the same, and uses of the resin film.
【０００２】[0002]
【従来の技術】近年、自動車資材、建築資材、農業用資
材等、屋外で用いられる樹脂の需要量は飛躍的に増加し
ている。例えば、農業用資材としては、施設園芸におけ
るハウス、トンネル等の施設の被覆に用いられる農業用
フィルムが挙げられる。農業用フィルムとしては、従
来、ポリ塩化ビニルフィルムや、ポリオレフィン系樹脂
フィルム（例えば、ポリエチレンフィルム、エチレン／
酢酸ビニル共重合体フィルム）等が汎用的に使用されて
いる。中でも、最近では、汚れにくく、軽量で、焼却時
に有毒ガスが発生し難いポリオレフィン系樹脂フィルム
が施設園芸用に広く普及している。良好な作物生育性を
発現するため、これら農業用フィルムに要求される性能
としては、太陽光が良好に透過するための透明性や、特
に夜間の温度低下を防ぎハウスなど施設内の温度を高く
保つ保温性等が挙げられる。2. Description of the Related Art In recent years, the demand for resins used outdoors, such as automotive materials, building materials, agricultural materials, etc., has increased dramatically. For example, agricultural materials include agricultural films used for covering facilities such as houses and tunnels in greenhouse horticulture. Conventional agricultural films include polyvinyl chloride films and polyolefin resin films (eg, polyethylene film, ethylene /
Vinyl acetate copolymer film) and the like are widely used. Among them, recently, polyolefin-based resin films, which are hardly soiled, lightweight, and hardly generate toxic gas during incineration, have been widely used for greenhouse horticulture. In order to express good crop growth, the performance required for these agricultural films includes transparency for good penetration of sunlight and high temperatures inside facilities such as houses to prevent temperature drop at night, especially at night. Keeping heat retention and the like can be mentioned.
【０００３】例えば特開昭５６―８４９５６号公報、特
開昭５５―１５１０４３号公報、特開昭６３−２８６３
４３号公報および特開昭５６―４１２５４号等の各公報
に記載されているような、酸化珪素、アルミニウムシリ
ケート、ハイドロタルサイト類、アルミナ、ゼオライト
等の無機化合物やアセタール樹脂等の有機化合物を添加
して保温性を改良した樹脂フィルムが知られている。For example, JP-A-56-84956, JP-A-55-151043, and JP-A-63-2863
Addition of inorganic compounds such as silicon oxide, aluminum silicate, hydrotalcites, alumina and zeolite and organic compounds such as acetal resin as described in JP-A-43-43 and JP-A-56-41254. There is known a resin film having improved heat retention.
【０００４】しかしながら、従来の技術では、目的とす
る保温性を得るためにこれらの化合物を多量に添加しな
ければならず、そのために、フィルムの透明性が損われ
るという問題があった。[0004] However, in the prior art, a large amount of these compounds must be added in order to obtain a desired heat retaining property, which causes a problem that the transparency of the film is impaired.
【０００５】[0005]
【発明が解決しようとする課題】本発明の目的は、優れ
た保温性と優れた透明性とをバランスよく有する樹脂フ
ィルム、およびそれを与えるポリオレフィン系樹脂組成
物を提供することにある。SUMMARY OF THE INVENTION An object of the present invention is to provide a resin film having a good balance between excellent heat retention and excellent transparency, and a polyolefin resin composition for providing the same.
【０００６】[0006]
【課題を解決するための手段】本発明者らは、上記目的
を達成すべく鋭意検討した結果、ポリオレフィン系樹脂
に特定の無機粉末を特定量配合してなるポリオレフィン
系樹脂組成物からなる層を有してなる樹脂フィルムが上
記目的に適うことを見出し、本発明を完成した。Means for Solving the Problems The present inventors have conducted intensive studies to achieve the above object, and as a result, have found that a layer made of a polyolefin resin composition obtained by mixing a specific amount of a specific inorganic powder with a polyolefin resin. The present inventors have found that the resin film provided has the above-mentioned object, and have completed the present invention.
【０００７】本発明の一の態様は、ポリオレフィン系樹
脂１００重量部に対して、下記式（Ｉ）で表される無機
粉末を１〜２５０重量部含有することを特徴とするポリ
オレフィン系樹脂組成物である。 M2+ 1-xAl3+ x（OH-）2・［（An-）(x-a)/n・（Bm-）a/m］・ｂH2O (I) 但し、Ｍ2+はＭｇ、Ｃａ及びＺｎから選ばれる１種以上
の２価金属イオン、Ａn-は２個以上のＳｉを含む１種以
上のｎ価の珪酸イオン、Ｂm-はＳｉを含まない１種以上
のｍ価のアニオンであり、ｘ、ａ、ｂは下記の条件式を
満足する。 ０＜ｘ＜０．５、０＜ａ＜ｘ、０≦ｂ≦２ 該樹脂組成物は、ヒンダードアミン系化合物、紫外線吸
収剤、防曇剤、および防霧剤の少なくとも１種を更に含
有することができる。本発明の他の態様は、上記樹脂組
成物からなる層を少なくとも一層有する樹脂フィルムで
ある。該フィルムは、ヒンダードアミン系化合物、紫外
線吸収剤、防曇剤および防霧剤から選ばれる少なくとも
１種を更に含有することができる。また、本発明の樹脂
フィルムは、防曇性被膜層を有することができる。本発
明の更に他の態様は、上記樹脂フィルムを用いてなる園
芸施設内で行なうことを特徴とする作物の栽培方法であ
る。[0007] One embodiment of the present invention is a polyolefin resin composition comprising 1 to 250 parts by weight of an inorganic powder represented by the following formula (I) based on 100 parts by weight of a polyolefin resin. It is. M 2+ 1-x Al 3+ x (OH -) 2 · [(A n-) (xa) / n · (B m-) a / m] · bH 2 O (I) where, M 2+ is mg, one or more divalent metal ion selected from Ca and Zn, a n-1 or more n-valent silicate ions containing two or more Si, B m-is one or more that do not contain Si It is a m-valent anion, and x, a, and b satisfy the following conditional expressions. 0 <x <0.5, 0 <a <x, 0 ≦ b ≦ 2 The resin composition further contains at least one of a hindered amine compound, an ultraviolet absorber, an anti-fog agent, and an anti-fog agent. Can be. Another embodiment of the present invention is a resin film having at least one layer made of the above resin composition. The film may further contain at least one selected from a hindered amine compound, an ultraviolet absorber, an anti-fogging agent and an anti-fog agent. Further, the resin film of the present invention can have an antifogging coating layer. Still another embodiment of the present invention is a method for cultivating a crop, wherein the method is performed in a horticultural facility using the resin film.
【０００８】[0008]
【発明の実施の形態】本発明に係る樹脂フィルムは、ポ
リオレフィン系樹脂１００重量部に対して、下記式
（Ｉ）で表される無機粉末を１〜２５０重量部含有する
ポリオレフィン系樹脂組成物からなる層を少なくとも１
層有することを特徴とする。 M2+ 1-xAl3+ x（OH-）2・［（An-）(x-a)/n・（Bm-）a/m］・ｂH2O (I) 但し、Ｍ2+はＭｇ、Ｃａ及びＺｎから選ばれる１種以上
の２価金属イオン、Ａn-は２個以上のＳｉを含む１種以
上のｎ価の珪酸イオン、Ｂm-はＳｉを含まない１種以上
のｍ価のアニオンであり、ｘ、ａ、ｂは下記の条件式を
満足する。０＜ｘ＜０．５、０＜ａ＜ｘ、０≦ｂ≦２BEST MODE FOR CARRYING OUT THE INVENTION A resin film according to the present invention comprises a polyolefin resin composition containing 1 to 250 parts by weight of an inorganic powder represented by the following formula (I) per 100 parts by weight of a polyolefin resin. At least one layer
It is characterized by having a layer. M 2+ 1-x Al 3+ x (OH -) 2 · [(A n-) (xa) / n · (B m-) a / m] · bH 2 O (I) where, M 2+ is mg, one or more divalent metal ion selected from Ca and Zn, a n-1 or more n-valent silicate ions containing two or more Si, B m-is one or more that do not contain Si It is a m-valent anion, and x, a, and b satisfy the following conditional expressions. 0 <x <0.5, 0 <a <x, 0 ≦ b ≦ 2
【０００９】上記樹脂フィルムにおける式（Ｉ）の無機
粉末中のＡn-は、Ｓｉを２個以上含む１種以上の珪酸イ
オンであり、（ＳｉoＯp）n-で示される。ここで、ｏは
２以上の整数、ｐは（２ｏ＋１）以上の整数である。Ｂ
m-は、Ｓｉを含まないｍ価のアニオンであれば特に限定
されないが、炭酸イオン、硫酸イオン、硝酸イオン、ハ
ロゲンイオン、塩素のオキシ酸のイオン、硼素のオキシ
酸のイオンおよび燐のオキシ酸のイオンからなる群より
選ばれるアニオンが好ましい。更にＢm-は、炭酸イオン
および硫酸イオン、または、炭酸イオンおよび硼素のオ
キシ酸のイオン、または、炭酸イオンおよび燐のオキシ
酸のイオンであることがより好ましい。上記無機粉末の
好ましい例としては、協和化学工業製のマグクリスタ
（商品名）が挙げられる。無機粉末の平均粒子径は、通
常５μｍ以下であり、好ましくは０．０３〜２μｍであ
る。[0009] A n- is an inorganic powder of the formula (I) in the resin film is one or more silicate ions containing two or more Si, represented by n- (Si o O p). Here, o is an integer of 2 or more, and p is an integer of (2o + 1) or more. B
m- is not particularly limited as long as it is a m-valent anion that does not contain Si. However, carbonate ion, sulfate ion, nitrate ion, halogen ion, oxyacid ion of chlorine, oxyacid ion of boron and oxyacid of phosphorus Anions selected from the group consisting of the following ions are preferred. Further, B m- is more preferably a carbonate ion and a sulfate ion, or a carbonate ion and a boron oxyacid ion, or a carbonate ion and a phosphorus oxyacid ion. Preferred examples of the inorganic powder include Magcrysta (trade name) manufactured by Kyowa Chemical Industry. The average particle diameter of the inorganic powder is usually 5 μm or less, preferably 0.03 to 2 μm.
【００１０】式（Ｉ）の無機粉末の見掛密度は、ＪＩＳ
Ｋ６７２１記載の方法で測定された値で０．１３ｇ／
cm3以上が好ましく、０．１８ｇ／cm3以上がより好まし
い。無機粉末の見掛密度が０．１３ｇ／cm3以上である
と、フィルムは透明性に特に優れたものとなる。The apparent density of the inorganic powder of the formula (I) is determined according to JIS
0.13 g / value measured by the method described in K6721.
cm 3 or more is preferable, and 0.18 g / cm 3 or more is more preferable. When the apparent density of the inorganic powder is 0.13 g / cm 3 or more, the film becomes particularly excellent in transparency.
【００１１】式（Ｉ）の無機粉末の屈折率は、ＪＩＳ
Ｋ００６２記載の方法で測定された値で１．４８〜１．
５２の範囲にあることが好ましく、１．４９〜１．５１
の範囲にあることがより好ましい。The refractive index of the inorganic powder of the formula (I) is determined according to JIS
The values measured by the method described in K0062 are 1.48 to 1.
52, preferably 1.49 to 1.51.
Is more preferably within the range.
【００１２】上記無機粉末は、ポリオレフィン系樹脂組
成物中での分散性を更に向上させるために、分散剤で表
面処理を施されていてもよい。分散剤としては、ステア
リン酸、パルミチン酸、ラウリン酸等の高級脂肪酸、高
級脂肪酸のカルシウム塩、亜鉛塩、マグネシウム塩、バ
リウム塩、ナトリウム塩等の金属石鹸、リン酸エステ
ル、シラン系カップリング剤、アルミニウム系カップリ
ング剤、ジルコニウム系カップリング剤、ワックス等が
例示できる。表面処理の方法は、分散剤が無機粉末表面
に均一に付着する方法であればよい。The inorganic powder may be subjected to a surface treatment with a dispersant in order to further improve the dispersibility in the polyolefin resin composition. As dispersants, stearic acid, palmitic acid, higher fatty acids such as lauric acid, calcium salts of higher fatty acids, zinc salts, magnesium salts, barium salts, metal soaps such as sodium salts, phosphate esters, silane coupling agents, Examples thereof include an aluminum-based coupling agent, a zirconium-based coupling agent, and a wax. The surface treatment method may be any method as long as the dispersant adheres uniformly to the surface of the inorganic powder.
【００１３】上記ポリオレフィン系樹脂組成物の式
（Ｉ）の無機粉末の含有量は、ポリオレフィン系樹脂１
００重量部に対して１〜２５０重量部である。かかる量
で式（Ｉ）の無機粉末を含有するポリオレフィン系樹脂
組成物からなる層を有することにより、本発明の樹脂フ
ィルムは、優れた保温性と優れた透明性とをバランスよ
く有するものとなる。The content of the inorganic powder of the formula (I) in the polyolefin resin composition is as follows.
It is 1 to 250 parts by weight with respect to 00 parts by weight. By having a layer comprising the polyolefin-based resin composition containing the inorganic powder of the formula (I) in such an amount, the resin film of the present invention has a good balance between excellent heat retention and excellent transparency. .
【００１４】フィルムの透明性および強度の観点から、
本発明の樹脂フィルムの式（Ｉ）の無機粉末の含有量
は、フィルム全体の１〜３０重量％の範囲にあることが
好ましく、２〜２０重量％の範囲がより好ましく、３〜
１５重量％の範囲が更に好ましい。１重量％未満ではフ
ィルムの保温性が不充分になる傾向があり、また３０重
量％を超えるとフィルムの透明性や強度が低下する傾向
がある。From the viewpoint of the transparency and strength of the film,
The content of the inorganic powder of the formula (I) in the resin film of the present invention is preferably in the range of 1 to 30% by weight, more preferably 2 to 20% by weight, and more preferably 3 to 3% by weight.
A range of 15% by weight is more preferred. If it is less than 1% by weight, the heat retention of the film tends to be insufficient, and if it exceeds 30% by weight, the transparency and strength of the film tend to decrease.
【００１５】上記ポリオレフィン系樹脂組成物における
ポリオレフィン系樹脂としては、例えば、ポリエチレ
ン、ポリプロピレン等のα−オレフィンの単独重合体；
エチレン／プロピレン共重合体、エチレン／ブテン−１
共重合体、エチレン／４−メチル−１−ペンテン共重合
体、エチレン／ヘキセン−１共重合体、エチレン／オク
テン−１共重合体などのエチレン／α−オレフィン共重
合体；エチレン／酢酸ビニル共重合体、エチレン／アク
リル酸共重合体、エチレン／メタクリル酸メチル共重合
体、エチレン／酢酸ビニル／メタクリル酸メチル共重合
体、アイオノマー樹脂などのα−オレフィンを主成分と
する異種単量体との共重合体が挙げられる。本発明の樹
脂フィルムが農業用フィルムである場合には、透明性、
耐候性、経済性等の観点から、ポリエチレン、エチレン
／α−オレフィン共重合体、酢酸ビニル単位の含有量が
３０重量％以下のエチレン／酢酸ビニル共重合体が好ま
しい。Examples of the polyolefin resin in the polyolefin resin composition include homopolymers of α-olefin such as polyethylene and polypropylene;
Ethylene / propylene copolymer, ethylene / butene-1
Ethylene / α-olefin copolymer such as copolymer, ethylene / 4-methyl-1-pentene copolymer, ethylene / hexene-1 copolymer, ethylene / octene-1 copolymer; ethylene / vinyl acetate copolymer Polymers, ethylene / acrylic acid copolymers, ethylene / methyl methacrylate copolymers, ethylene / vinyl acetate / methyl methacrylate copolymers, ionomer resins and other hetero-monomers as main components And copolymers. When the resin film of the present invention is an agricultural film, transparency,
From the viewpoints of weather resistance, economy and the like, polyethylene, ethylene / α-olefin copolymer, and ethylene / vinyl acetate copolymer having a vinyl acetate unit content of 30% by weight or less are preferred.
【００１６】エチレンと炭素数３〜１８のα−オレフィ
ンとをパラジウム、ニッケルなどの遷移金属錯体触媒や
メタロセン系触媒などのいわゆるシングルサイト触媒を
使用して、溶媒の存在下又は不存在下に、気相−固相、
液相−固相又は均一液相下で重合して得られるエチレン
／α−オレフィン共重合体は、上記ポリオレフィン系樹
脂として好ましい。通常、かかるエチレン／α−オレフ
ィン共重合体の製造における重合温度は約３０℃〜約３
００℃であり、重合圧力は大気圧〜約３０００ｋｇ／ｃ
ｍ2である。例えば、特開平６−９７２４号公報、特開
平６−１３６１９５号公報、特開平６−１３６１９６号
公報、特開平６−２０７０５７号公報等に記載されてい
るメタロセン触媒成分を含む、いわゆるメタロセン系オ
レフィン重合用触媒の存在下に、エチレンと炭素原子数
３〜１８のα−オレフィンとを共重合させて得られるエ
チレン／α−オレフィン共重合体は、本発明において好
ましく用いることができる。[0016] Ethylene and an α-olefin having 3 to 18 carbon atoms are converted to a so-called single-site catalyst such as a transition metal complex catalyst such as palladium or nickel or a metallocene catalyst, in the presence or absence of a solvent. Gas phase-solid phase,
The ethylene / α-olefin copolymer obtained by polymerization under a liquid phase-solid phase or a uniform liquid phase is preferable as the polyolefin-based resin. Usually, the polymerization temperature in the production of such an ethylene / α-olefin copolymer is from about 30 ° C to about 3 ° C.
And the polymerization pressure is from atmospheric pressure to about 3000 kg / c.
m 2 . For example, a so-called metallocene-based olefin polymerization containing a metallocene catalyst component described in JP-A-6-9724, JP-A-6-136195, JP-A-6-136196, JP-A-6-207057, etc. An ethylene / α-olefin copolymer obtained by copolymerizing ethylene with an α-olefin having 3 to 18 carbon atoms in the presence of a catalyst for use can be preferably used in the present invention.
【００１７】本発明の樹脂フィルムは、ヒンダードアミ
ン系化合物、紫外線吸収剤、防曇剤および防霧剤から選
ばれる少なくとも１種を含有することができる。The resin film of the present invention may contain at least one selected from a hindered amine compound, an ultraviolet absorber, an anti-fogging agent and an anti-fog agent.
【００１８】本発明の樹脂フィルムに用いるヒンダード
アミン系化合物は、例えば、特開平７−２８６０５２号
公報に記載の構造式を有するものでよく、具体例として
は、チヌビン６２２−ＬＤ、キマソーブ９４４−ＬＤ、
ホスタビンＮ３０、ＶＰ Ｓａｎｄｕｖｏｒ ＰＲ−３
１、チヌビン１２３（商品名）がある。また、特開昭６
３−２８６４４８号記載のヒンダードアミン系化合物含
有安定化剤である、チバスペシャルティ・ケミカルズ社
製のチヌビン４９２、チヌビン４９４（商品名）等を使
用することもできる。また、「プラスチックスエージ」
２０００年４月号 １１０頁〜１１６頁に記載されてい
るＮ−Ｏ−Ｒ型ヒンダードアミン系化合物を使用するこ
ともできる。ヒンダードアミン系化合物は単独で用いて
も２種類以上を併用してもよい。耐候性付与効果とブル
ーミングの観点から、本発明の樹脂フィルム中のヒンダ
ードアミン系化合物の含有量は、フィルム全体の０．０
１〜５重量％が好ましく、０．１〜２重量％がより好ま
しい。The hindered amine compound used in the resin film of the present invention may have, for example, the structural formula described in JP-A-7-286052. Specific examples include tinuvin 622-LD, chimassorb 944-LD,
Hostabin N30, VP Sanduvor PR-3
1, Tinuvin 123 (trade name). In addition, Japanese Unexamined Patent Publication
It is also possible to use Tinuvin 492, Tinuvin 494 (trade name) manufactured by Ciba Specialty Chemicals, which is a hindered amine compound-containing stabilizer described in 3-286448. Also, "Plastic Swage"
The NOR-type hindered amine compounds described in April 2000, pages 110 to 116 can also be used. The hindered amine compounds may be used alone or in combination of two or more. From the viewpoint of the weather resistance imparting effect and blooming, the content of the hindered amine compound in the resin film of the present invention is 0.0% of the entire film.
It is preferably from 1 to 5% by weight, more preferably from 0.1 to 2% by weight.
【００１９】本発明の樹脂フィルムに用いられる紫外線
吸収剤としては、ベンゾフェノン系紫外線吸収剤、ベン
ゾトリアゾール系紫外線吸収剤、ベンゾエート系紫外線
吸収剤、シアノアクリレート系紫外線吸収剤等が挙げら
れる。また、紫外線吸収剤は単独で用いても２種類以上
を併用してもよい。耐候性付与効果とブルーミング抑制
の観点から、本発明の樹脂フィルム中の紫外線吸収剤の
含有量は、フィルム全体の０．０１〜３重量％が好まし
く、０．０３〜２重量％がより好ましい。The ultraviolet absorber used in the resin film of the present invention includes a benzophenone ultraviolet absorber, a benzotriazole ultraviolet absorber, a benzoate ultraviolet absorber, a cyanoacrylate ultraviolet absorber and the like. The ultraviolet absorber may be used alone or in combination of two or more. In light of the effect of imparting weather resistance and suppressing blooming, the content of the ultraviolet absorber in the resin film of the present invention is preferably 0.01% to 3% by weight, and more preferably 0.03% to 2% by weight of the entire film.
【００２０】本発明の樹脂フィルムに用いられる防霧剤
としては、例えば、パ−フルオロアルキル基、ω−ヒド
ロフルオロアルキル基等を有するフッ素化合物（特にフ
ッ素系界面活性剤）、またアルキルシロキサン基を有す
るシリコン系化合物（特にシリコン系界面活性剤）等が
挙げられる。フッ素系界面活性剤の具体例としては、ダ
イキン工業(株)製のユニダインＤＳ−４０３、ＤＳ−４
０６、ＤＳ−４０１（商品名）、セイミケミカル(株)製
のサーフロンＫＣ−４０（商品名）等が挙げられ、シリ
コン系界面活性剤としては、東レダウコーニングシリコ
ン（株）社製のＳＨ−３７４６（商品名）が挙げられ
る。本発明の樹脂フィルム中の防霧剤の含有量は、フィ
ルム全体の０．０１〜３重量％が好ましく、０．０２〜
２重量％がより好ましく、０．０５〜１．５重量％が特
に好ましい。As the antifog agent used in the resin film of the present invention, for example, a fluorine compound having a perfluoroalkyl group, an ω-hydrofluoroalkyl group or the like (particularly a fluorine-based surfactant), or an alkylsiloxane group Silicon-based compounds (especially silicon-based surfactants). Specific examples of the fluorine-based surfactant include Unidyne DS-403 and DS-4 manufactured by Daikin Industries, Ltd.
06, DS-401 (trade name), Surflon KC-40 (trade name) manufactured by Seimi Chemical Co., Ltd., and as the silicon-based surfactant, SH- manufactured by Toray Dow Corning Silicon Co., Ltd. is used. 3746 (trade name). The content of the antifog agent in the resin film of the present invention is preferably 0.01 to 3% by weight of the whole film,
2 wt% is more preferable, and 0.05 to 1.5 wt% is particularly preferable.
【００２１】本発明の樹脂フィルムに用いられる防曇剤
は、界面活性剤であれば特に限定されないが、樹脂との
相溶性および熱安定性の観点から、非イオン界面活性剤
が好ましく用いられる。具体的には、ソルビタンモノパ
ルミテート、ソルビタンモノステアレート、ソルビタン
モノパルミテート、ソルビタンモノモンタネート、ソル
ビタンモノオレエート、ソルビタンジオレエート等のソ
ルビタン脂肪酸エステル及びそのアルキレンオキサイド
付加物等のソルビタン系界面活性剤、グリセリンモノパ
ルミテート、グリセリンモノステアレート、ジグリセリ
ンジステアレート、トリグリセリンモノステアレート、
テトラグリセリンジモンタネート、グリセリンモノオレ
エート、ジグリセリンモノオレエート、ジグリセリンセ
スキオレエート、テトラグリセリンモノオレエート、ヘ
キサグリセリンモノオレエート、ヘキサグリセリントリ
オレエート、テトラグリセリントリオレエート、テトラ
グリセリンモノラウレート、ヘキサグリセリンモノラウ
レート等のグリセリン脂肪酸エステル及びそのアルキレ
ンオキサイド付加物等のグリセリン系界面活性剤、ポリ
エチレングリコールモノパルミテート、ポリエチレング
リコールモノステアレート等のポリエチレングリコール
系界面活性剤、アルキルフェノールのアルキレンオキシ
ド付加物、ソルビタン／グリセリン縮合物と有機酸との
エステル、ポリオキシエチレン（２モル）ステアリルア
ミン、ポリオキシエチレン（４モル）ステアリルアミ
ン、ポリオキシエチレン（２モル）ステアリルアミンモ
ノステアレート、ポリオキシエチレン（４モル）ラウリ
ルアミンモノステアレート等のポリオキシエチレンアル
キルアミン及びその脂肪酸エステル等が挙げられる。本
発明の樹脂フィルム中の防曇剤の含有量は、フィルム全
体の０．１〜４重量％が好ましく、０．５〜３重量％が
より好ましく、１〜２．５重量％が特に好ましい。The antifogging agent used in the resin film of the present invention is not particularly limited as long as it is a surfactant, but a nonionic surfactant is preferably used from the viewpoint of compatibility with the resin and thermal stability. Specifically, sorbitan monopalmitate, sorbitan monostearate, sorbitan monopalmitate, sorbitan monomontanate, sorbitan monooleate, sorbitan fatty acid esters such as sorbitan dioleate and sorbitan-based interfaces such as alkylene oxide adducts thereof Activator, glycerin monopalmitate, glycerin monostearate, diglycerin distearate, triglycerin monostearate,
Tetraglycerin dimontanate, glycerin monooleate, diglycerin monooleate, diglycerin sesquioleate, tetraglycerin monooleate, hexaglycerin monooleate, hexaglycerin trioleate, tetraglycerin trioleate, tetraglycerin monolaurate Glycerin surfactants such as glycerin fatty acid esters such as hexaglycerin monolaurate and alkylene oxide adducts thereof; polyethylene glycol surfactants such as polyethylene glycol monopalmitate and polyethylene glycol monostearate; alkylene oxide addition of alkylphenol , Sorbitan / glycerin condensate and ester of organic acid, polyoxyethylene (2 mol) stearylamine, polyoxy Styrene (4 mol) stearylamine, polyoxyethylene (2 mol) stearylamine monostearate, polyoxyethylene (4 mol) Polyoxyethylene alkyl amines such as laurylamine monostearate and fatty acid esters. The content of the antifogging agent in the resin film of the present invention is preferably 0.1 to 4% by weight, more preferably 0.5 to 3% by weight, and particularly preferably 1 to 2.5% by weight of the whole film.
【００２２】本発明の樹脂フィルムは、本発明の効果が
著しく損なわれない限り、ワックス、酸化防止剤、帯電
防止剤、ヒンダ−ドアミン系以外の光安定剤、滑剤、顔
料、防藻剤、前記式（Ｉ）の無機粉末以外の無機粉末等
の各種の添加剤を含有することもできる。これらの添加
剤は、単独で用いても２種類以上を併用してもかまわな
い。The resin film of the present invention may be a wax, an antioxidant, an antistatic agent, a light stabilizer other than a hindered amine type, a lubricant, a pigment, an antialgal agent, as long as the effects of the present invention are not significantly impaired. Various additives such as an inorganic powder other than the inorganic powder of the formula (I) can be contained. These additives may be used alone or in combination of two or more.
【００２３】式（Ｉ）の無機粉末以外の無機粉末として
は、リチウムアルミニウム複合水酸化物類化合物及びそ
の類似化合物（例えば、特開平５−１７９０５２号公
報、ＷＯ９７／００８２８公報、特開平８−３１１２８
４号公報に開示）などの複合水酸化物、酸化マグネシウ
ム、酸化カルシウム、酸化アルミニウム、酸化珪素、酸
化チタンなどの金属の酸化物、水酸化リチウム、水酸化
マグネシウム、水酸化カルシウム、水酸化アルミニウム
などの水酸化物、炭酸マグネシウム、炭酸カルシウム、
特開平９−２７９１３１号公報記載の塩基性炭酸アルミ
ニウム塩などの炭酸塩類、硫酸カリウム、硫酸マグネシ
ウム、硫酸カルシウム、硫酸亜鉛、硫酸アルミニウムな
どの硫酸塩類、燐酸リチウム、燐酸ナトリウム、燐酸カ
リウム、燐酸カルシウム、燐酸ジルコニウム（例えば、
特開平８−６７７７４号公報に開示されたＨ型燐酸ジル
コニウム）などの燐酸塩類、珪酸マグネシウム、珪酸カ
ルシウム、珪酸アルミニウム、珪酸チタンなどの珪酸塩
類、アルミン酸ナトリウム、アルミン酸カリウム、アル
ミン酸カルシウムなどのアルミン酸塩類、アルミノ珪酸
ナトリウム、アルミノ珪酸カリウム、アルミノ珪酸カル
シウムなどのアルミノ珪酸塩類、カオリン、クレー、タ
ルクなどの粘土鉱物、その他複合酸化物などが挙げられ
る。Examples of the inorganic powder other than the inorganic powder of the formula (I) include lithium-aluminum composite hydroxides and similar compounds (for example, JP-A-5-179052, WO97 / 00828, JP-A-8-31128).
No. 4), oxides of metals such as magnesium oxide, calcium oxide, aluminum oxide, silicon oxide, titanium oxide, lithium hydroxide, magnesium hydroxide, calcium hydroxide, aluminum hydroxide, etc. Hydroxide, magnesium carbonate, calcium carbonate,
Carbonates such as basic aluminum carbonate described in JP-A-9-279131, sulfates such as potassium sulfate, magnesium sulfate, calcium sulfate, zinc sulfate and aluminum sulfate, lithium phosphate, sodium phosphate, potassium phosphate, calcium phosphate; Zirconium phosphate (for example,
Phosphates such as H-type zirconium phosphate disclosed in JP-A-8-67774, silicates such as magnesium silicate, calcium silicate, aluminum silicate and titanium silicate, sodium aluminate, potassium aluminate, calcium aluminate and the like. Aluminosilicates, aluminosilicates such as sodium aluminosilicate, potassium aluminosilicate, calcium aluminosilicate, clay minerals such as kaolin, clay and talc, and other composite oxides are exemplified.
【００２４】本発明の樹脂フィルムは、その少なくとも
片側の表面に防曇性被膜を有してもよい。防曇性被膜を
有する樹脂フィルムは、その防曇性を長期間持続するこ
とができる。かかる防曇性被膜としては、例えば、特公
昭４９−３２６６８号公報、特公昭５０−１１３４８号
公報などに記載されている、コロイダルシリカやアルミ
ナゾルに代表される無機酸化物ゾルのコーティング膜、
特開昭５５−５６１７７号公報、特開昭５７−９８５７
８号公報、特開昭５７−１１９９７４号公報、特開平３
−２０７６４３号公報等に記載された無機酸化物ゾルと
有機化合物（界面活性剤や樹脂など）などのコーティン
グ膜、界面活性剤を主成分とする液のコーティング膜、
親水性樹脂（例えば、ポリビニルアルコール、多糖類、
ポリアクリル酸などが挙げられる。）を主成分とする膜
などが挙げられる。これら防曇性被膜の形成方法は、コ
ーティングでもよいし、防曇性被膜を形成後、該被膜を
積層フィルムに積層してもよい。また、防曇性被膜は単
層でも２層以上でもよい。The resin film of the present invention may have an antifogging film on at least one surface. A resin film having an anti-fogging film can maintain its anti-fogging property for a long period of time. Examples of the anti-fog coating include, for example, coating films of inorganic oxide sols represented by colloidal silica and alumina sol described in JP-B-49-32668 and JP-B-50-11348.
JP-A-55-56177, JP-A-57-9857
No. 8, JP-A-57-119974, JP-A-5-119974
A coating film of an inorganic oxide sol and an organic compound (such as a surfactant or a resin) described in JP-A-207643, a coating film of a liquid containing a surfactant as a main component,
Hydrophilic resin (for example, polyvinyl alcohol, polysaccharide,
And polyacrylic acid. ) As a main component. The method of forming these antifogging films may be coating, or after forming the antifogging film, the film may be laminated on a laminated film. The antifogging film may be a single layer or two or more layers.
【００２５】本発明の樹脂フィルムは、ポリオレフィン
系樹脂と式（Ｉ）で表わされる無機粉末とからなる前記
のポリオレフィン系樹脂組成物からなる単一の層からな
っていてもよいし、該樹脂組成物からなる二以上の層か
らなる多層フィルムでもよい。また、本発明の効果が著
しく損なわれない限り、上記ポリオレフィン系樹脂組成
物からなる一以上の層と、該樹脂組成物以外の樹脂材料
からなる一以上の層からなる多層フィルムであってもよ
い。多層フィルムの層構成は特に限定はされず、例え
ば、２種２層、２種３層、３種３層、５種５層などが可
能である。The resin film of the present invention may be composed of a single layer of the above-mentioned polyolefin-based resin composition comprising a polyolefin-based resin and an inorganic powder represented by the formula (I). It may be a multilayer film composed of two or more layers made of an object. Further, as long as the effects of the present invention are not significantly impaired, a multilayer film composed of one or more layers made of the polyolefin-based resin composition and one or more layers made of a resin material other than the resin composition may be used. . The layer constitution of the multilayer film is not particularly limited, and for example, two kinds, two layers, two kinds, three layers, three kinds, three layers, five kinds, five layers and the like are possible.
【００２６】本発明の樹脂フィルムは、前記ポリオレフ
ィン系樹脂組成物を用いて、カレンダー法、押出Ｔダイ
成形法、インフレーション成形法などの慣用的なフィル
ム形成方法により製造することができる。また、本発明
の樹脂フィルムが多層フィルムである場合には、共押出
成形法、溶融コーティング法、押出ラミネーション法、
ドライラミネーション法等の多層フィルム形成方法によ
り製造することができる。The resin film of the present invention can be produced from the polyolefin resin composition by a conventional film forming method such as a calendering method, an extrusion T-die molding method and an inflation molding method. Further, when the resin film of the present invention is a multilayer film, co-extrusion molding method, melt coating method, extrusion lamination method,
It can be manufactured by a multilayer film forming method such as a dry lamination method.
【００２７】本発明の樹脂フィルムは、厚みの点では、
一般にフィルムと称されるものと一般にシートと称され
るものの両方を包含するものであり、通常は５μｍ〜１
ｍｍ程度の厚みのものであり、フィルム厚みは、フィル
ムの用途に応じて適宜選択することができる。フィルム
強度の観点から、０．０１ｍｍ以上であることが好まし
い。また、フィルムの中継ぎ加工性や、農業用フィルム
としての使用時の被覆作業性などの観点からは、０．３
ｍｍ以下が好ましく、０．０３〜０．２５ｍｍがより好
ましい。The resin film of the present invention has a thickness
It includes both what is commonly referred to as a film and what is generally referred to as a sheet.
mm, and the film thickness can be appropriately selected according to the use of the film. From the viewpoint of film strength, the thickness is preferably 0.01 mm or more. Further, from the viewpoint of the splicing workability of the film and the workability of coating when used as an agricultural film, 0.3
mm or less, more preferably 0.03 to 0.25 mm.
【００２８】本発明の樹脂フィルムは、優れた透明性と
優れた保温性をバランスよく有するために、施設園芸用
資材、特に農業用ハウスやトンネル等の農業用施設の被
覆フィルムとして好適に用いることができる。本発明の
樹脂フィルムを被覆フィルムとして用いてなる園芸施設
（農業用ハウスやトンネル）は、日中に太陽光を効率的
に取り入れることができると共に、夜間に施設内をよく
保温することができる。従って、このような条件下での
栽培が好まれる作物は、本発明の樹脂フィルムを用いて
なる園芸施設内で好適に栽培可能である。Since the resin film of the present invention has a good balance between excellent transparency and excellent heat retaining property, it is preferably used as a material for facility horticulture, particularly as a covering film for an agricultural facility such as an agricultural house or a tunnel. Can be. A horticultural facility (agricultural house or tunnel) using the resin film of the present invention as a covering film can efficiently take in sunlight during the day and keep the inside of the facility well warm at night. Therefore, crops that are preferred to be cultivated under such conditions can be suitably cultivated in a horticulture facility using the resin film of the present invention.
【００２９】上記本発明の樹脂フィルムは、保温性と透
明性とのバランスに優れているが、該フィルムのこの優
れた性能は、式（Ｉ）の無機粉末を含有する前記ポリオ
レフィン系樹脂組成物からなる層が保温性と透明性のバ
ランスに優れていることに基づいている。このポリオレ
フィン系樹脂組成物、すなわち、ポリオレフィン系樹脂
１００重量部に対して、下記式（Ｉ）で表される無機粉
末を１〜２５０重量部含有することを特徴とするポリオ
レフィン系樹脂組成物は新規な組成物であり、本発明の
一つの態様である。 M2+ 1-xAl3+ x（OH-）2・［（An-）(x-a)/n・（Bm-）a/m］・ｂH2O (I) 但し、Ｍ2+はＭｇ、Ｃａ及びＺｎから選ばれる１種以上
の２価金属イオン、Ａn-は２個以上のＳｉを含む１種以
上のｎ価の珪酸イオン、Ｂm-はＳｉを含まない１種以上
のｍ価のアニオンであり、ｘ、ａ、ｂは下記の条件式を
満足する。 ０＜ｘ＜０．５、０＜ａ＜ｘ、０≦ｂ≦２The resin film of the present invention has an excellent balance between heat insulation and transparency, and the excellent performance of the film is based on the polyolefin resin composition containing an inorganic powder of the formula (I). Is based on the fact that the layer consisting of has an excellent balance between heat retention and transparency. This polyolefin-based resin composition, that is, a polyolefin-based resin composition characterized by containing 1 to 250 parts by weight of an inorganic powder represented by the following formula (I) based on 100 parts by weight of a polyolefin-based resin, is novel. And is an embodiment of the present invention. M 2+ 1-x Al 3+ x (OH -) 2 · [(A n-) (xa) / n · (B m-) a / m] · bH 2 O (I) where, M 2+ is mg, one or more divalent metal ion selected from Ca and Zn, a n-1 or more n-valent silicate ions containing two or more Si, B m-is one or more that do not contain Si It is a m-valent anion, and x, a, and b satisfy the following conditional expressions. 0 <x <0.5, 0 <a <x, 0 ≦ b ≦ 2
【００３０】本発明のポリオレフィン系樹脂組成物は、
ヒンダードアミン系化合物、紫外線吸収剤、防曇剤およ
び防霧剤から選ばれる少なくとも１種を含有することが
でき、かかる成分を含有する組成物は、前記樹脂フィル
ムに好適に使用することができる。本発明のポリオレフ
ィン系樹脂組成物は、ワックス、酸化防止剤、帯電防止
剤、ヒンダ−ドアミン系以外の光安定剤、滑剤、顔料、
防藻剤、前記式（Ｉ）の無機粉末以外の無機粉末等の各
種の添加剤を含有することもできる。これらの添加剤
は、単独で用いても２種類以上を併用してもかまわな
い。The polyolefin resin composition of the present invention comprises:
It can contain at least one selected from a hindered amine compound, an ultraviolet absorber, an anti-fogging agent and an anti-fog agent, and a composition containing such components can be suitably used for the resin film. The polyolefin-based resin composition of the present invention is a wax, an antioxidant, an antistatic agent, a light stabilizer other than a hindered amine type, a lubricant, a pigment,
Various additives such as an anti-algal agent and an inorganic powder other than the inorganic powder of the formula (I) can also be contained. These additives may be used alone or in combination of two or more.
【００３１】上記ポリオレフィン系樹脂組成物は、前述
の通り、本発明の樹脂フィルムの材料として有用である
が、該組成物の上記特性を活かして、フィルム以外の種
々の形状の成形体に加工することもでき、農業用資材、
家電製品、自動車資材、建築資材などの分野に適用する
ことができる。As described above, the above-mentioned polyolefin resin composition is useful as a material for the resin film of the present invention. By utilizing the above-mentioned properties of the composition, it is processed into molded articles of various shapes other than the film. Can also be used for agricultural materials,
It can be applied to fields such as home appliances, automobile materials, and building materials.
【００３２】本発明のポリオレフィン系樹脂組成物は、
例えば、以下の方法によって製造することができる。ポ
リオレフィン系樹脂に所定量の無機粉末、および必要に
応じて添加剤を、混合機を用いて混合する。混合機とし
ては、例えば、リボンブレンダー、スーパーミキサー、
バンバリーミキサー、１軸押出機、２軸押出機などの慣
用的な装置を用いることができる。得られた樹脂組成物
は、押出成形、射出成形、ブロー成形等で種々の形状の
成形品に加工することができる。The polyolefin resin composition of the present invention comprises:
For example, it can be manufactured by the following method. A predetermined amount of inorganic powder and, if necessary, an additive are mixed with the polyolefin resin using a mixer. As a mixing machine, for example, a ribbon blender, a super mixer,
Conventional devices such as a Banbury mixer, a single screw extruder, and a twin screw extruder can be used. The obtained resin composition can be processed into molded articles of various shapes by extrusion molding, injection molding, blow molding or the like.
【００３３】[0033]
【発明の効果】本発明の樹脂フィルムは、それに含まれ
る特定のポリオレフィン系樹脂組成物からなる層の保温
性と透明性との優れたバランスに基いて、優れた保温性
と優れた透明性とをバランスよく有する。従って、当該
フィルムは、農業用のハウスやトンネルなどの施設の被
覆フィルムやマルチングフィルムとして好適に用いるこ
とができる。換言すれば、本発明のポリオレフィン系樹
脂組成物は、優れた保温性と優れた透明性とをバランス
よく有する樹脂フィルムを与えることができることか
ら、工業的に有用である。The resin film of the present invention has excellent heat retention and excellent transparency based on the excellent balance between the heat retention and transparency of the layer comprising the specific polyolefin resin composition contained therein. Have a good balance. Therefore, the film can be suitably used as a covering film or a mulching film for facilities such as an agricultural house or a tunnel. In other words, the polyolefin-based resin composition of the present invention is industrially useful because it can provide a resin film having excellent balance between excellent heat retention and excellent transparency.
【００３４】[0034]
【実施例】以下に、本発明の実施例を示すが、本発明は
これらに限定されるものではない。なお実施例及び比較
例中の試験方法は次の通りであり、いずれも多層フィル
ムでの評価である。EXAMPLES Examples of the present invention will be described below, but the present invention is not limited to these examples. In addition, the test method in an Example and a comparative example is as follows, and all are evaluations with a multilayer film.
【００３５】［保温性評価］赤外分光光度計（パーキン
エルマー社製 １６４０型ＦＴＩＲ）を用いて、以下の
方法により、輻射線透過指数を求め、保温性の尺度とし
た。波数４４００〜３５０ｃｍ-1の範囲でフィルムの赤
外線吸収スペクトルを温度２３℃にて測定し、波数νで
の透過率Ｔ（ν）％の値を得た。一方、プランクの法則
から得られる下記式（１）に従い、２３℃における波数
νでの黒体輻射スペクトル強度ｅ（ν）を計算した。こ
こで黒体輻射スペクトル強度ｅ(ν)に透過率Ｔ(ν)をか
けたものが輻射線透過強度ｆ(ν)となる［式（２）を参
照］。 ｅ（ν）＝（Ａ／λ5）／｛ｅｘｐ[Ｂ／（λ×Ｔ）]−１｝ （１） 但し、 Ａ＝２πｈｃ2＝３．７４２×１０-12（Ｗ／ｃｍ2） Ｂ＝ｈｃ／ｋ ＝１．４３８ （ｃｍ・Ｋ） ここで、Ｔは絶対温度（Ｋ）、λは波長（ｃｍ）（＝１
／ν）、ｈはプランク定数、ｃは光速度、ｋはボルツマ
ン定数である。 ｆ（ν）＝ｅ（ν）×Ｔ（ν）／１００ （２） 輻射線透過強度ｆ（ν）を波数４４００〜３５０ｃｍ-1
の範囲で積分したものを輻射線透過エネルギーＦ、黒体
輻射スペクトルｅ（ν）を波数４４００〜３５０ｃｍ-1
の範囲で積分したものを輻射線透過エネルギーＥとし
て、輻射線透過指数Ｇ＝Ｆ／Ｅ×１００と定義する。実
際の積分は、波数間隔２ｃｍ-1ごとに区切り、台形近似
にて積算した。この輻射線透過指数が小さいほど、フィ
ルムの保温性は優れる。[Evaluation of Heat Insulation] Using an infrared spectrophotometer (1640 type FTIR manufactured by Perkin Elmer), a radiation transmission index was determined by the following method and used as a measure of heat insulation. An infrared absorption spectrum of the film was measured at a temperature of 23 ° C. in a wave number range of 4400 to 350 cm −1 , and a value of transmittance T (ν)% at a wave number ν was obtained. On the other hand, according to the following equation (1) obtained from Planck's law, the blackbody radiation spectrum intensity e (ν) at 23 ° C. at a wavenumber ν was calculated. Here, the value obtained by multiplying the blackbody radiation spectrum intensity e (ν) by the transmittance T (ν) becomes the radiation transmission intensity f (ν) [see equation (2)]. e (ν) = (A / λ 5 ) / {exp [B / (λ × T)] − 1} (1) where A = 2πhc 2 = 3.742 × 10 −12 (W / cm 2 ) B = Hc / k = 1.438 (cm · K) where T is the absolute temperature (K), λ is the wavelength (cm) (= 1
/ Ν), h is Planck's constant, c is light speed, and k is Boltzmann's constant. f (ν) = e (ν) × T (ν) / 100 (2) Change the radiation transmission intensity f (ν) to a wave number of 4400 to 350 cm −1.
Is the radiation transmission energy F, and the black body radiation spectrum e (ν) is the wave number of 4400 to 350 cm −1.
Is defined as a radiation transmission energy E, which is a radiation transmission index G = F / E × 100. The actual integration was performed by trapezoidal approximation by dividing at every wave number interval of 2 cm -1 . The smaller the radiation transmission index, the better the heat retention of the film.
【００３６】［透明性測定］ＪＩＳＫ７１０５に準拠
し、直読式ヘーズコンピューターＨＧＭ−２ＤＰ（スガ
試験機製）を用いて、フィルムの全光線透過率およびＨ
ＡＺＥを測定した。ＨＡＺＥの値が小さいほど、フィル
ムは透明性に優れる。[Measurement of Transparency] According to JIS K7105, using a direct-read type haze computer HGM-2DP (manufactured by Suga Test Instruments), the total light transmittance and H of the film were measured.
AZE was measured. The smaller the value of HAZE, the better the transparency of the film.
【００３７】［見掛密度測定］無機粉末の見掛密度は、
ＪＩＳ Ｋ６７２１に準拠して測定した。[Apparent Density Measurement] The apparent density of the inorganic powder is as follows:
It was measured in accordance with JIS K6721.
【００３８】（実施例１）エチレン／酢酸ビニル共重合
体（商品名：エバテートＨ２０３１； 住友化学工業
製）８３．９重量部に、見掛密度０．１８ｇ／ｃｍ3の
無機粉末Ｍを１０重量部、ヒンダードアミン系化合物Ａ
（商品名：チヌビン６２２； チバ・スペシャルティ・
ケミカルズ製）０．３重量部、ヒンダードアミン系化合
物Ｂ（商品名：キマソーブ９４４； チバ・スペシャル
ティ・ケミカルズ製）０．３重量部、紫外線吸収剤（商
品名：スミソーブ１３０； 住友化学工業製）０．１重
量部、酸化防止剤（商品名：イルガノックス１０１０；
チバ・スペシャルティ・ケミカルズ製）０．１重量
部、防曇剤としてソルビタンモノステアレート１．０重
量部、ジグリセリンジステアレート０．６重量部および
ジグリセリンモノオレート１．０重量部、防霧剤として
フッ素系界面活性剤（商品名：ＤＳ−４０３； ダイキ
ン工業製）０．１重量部を加え、バンバリーミキサーを
用いて１５０℃、５分間混練した後、造粒機により造粒
し、樹脂組成物のペレットを得た。この樹脂組成物を樹
脂組成物(1)とする。次に、エチレン／酢酸ビニル共重
合体（商品名：エバテートＤ２０１１； 住友化学工業
製）９６．９重量部に、ヒンダードアミン系化合物Ａ
０．６重量部、紫外線吸収剤０．１重量部、酸化防止剤
０．１重量部、ソルビタンモノステアレート１．４重量
部、ジグリセリンジステアレート０．６重量部、ステア
リン酸アミド０．２重量部、フッ素系界面活性剤０．１
重量部を加え、バンバリーミキサーを用いて１５０℃、
５分間混練した後、造粒機により造粒し、樹脂組成物の
ペレットを得た。この樹脂組成物を樹脂組成物(2)とす
る。上記二種類のペレットを用いてインフレーションフ
ィルム成形機により、樹脂組成物(1)からなる中間層、
およびその両側に積層された樹脂組成物(2)からなる内
層および外層からなる厚み０．１ｍｍの積層フィルム
（中間層０．０６ｍｍ、内外層各０．０２ｍｍ）を作製
した。表１に示すとおり、このフィルムは優れた保温性
と優れた透明性とをバランスよく有していた。Example 1 10 parts by weight of an inorganic powder M having an apparent density of 0.18 g / cm 3 was added to 83.9 parts by weight of an ethylene / vinyl acetate copolymer (trade name: Evatate H2031; manufactured by Sumitomo Chemical Co., Ltd.). Part, hindered amine compound A
(Product name: Tinuvin 622; Ciba Specialty
Chemicals) 0.3 parts by weight, hindered amine compound B (trade name: Chimasorb 944; Ciba Specialty Chemicals) 0.3 parts by weight, ultraviolet absorber (trade name: Sumisorb 130; Sumitomo Chemical Co., Ltd.) 1 part by weight, an antioxidant (trade name: Irganox 1010;
0.1 part by weight, Ciba Specialty Chemicals), 1.0 part by weight of sorbitan monostearate, 0.6 part by weight of diglycerin distearate and 1.0 part by weight of diglycerin monooleate as an antifogging agent, fog proof 0.1 parts by weight of a fluorine-based surfactant (trade name: DS-403; manufactured by Daikin Industries, Ltd.) was added as an agent, and the mixture was kneaded at 150 ° C. for 5 minutes using a Banbury mixer. A pellet of the composition was obtained. This resin composition is referred to as a resin composition (1). Next, the hindered amine compound A was added to 96.9 parts by weight of an ethylene / vinyl acetate copolymer (trade name: Evatate D2011; manufactured by Sumitomo Chemical Co., Ltd.).
0.6 parts by weight, 0.1 part by weight of ultraviolet absorber, 0.1 part by weight of antioxidant, 1.4 parts by weight of sorbitan monostearate, 0.6 part by weight of diglycerin distearate, 0.1 part by weight of stearamide. 2 parts by weight, fluorine surfactant 0.1
Parts by weight, using a Banbury mixer at 150 ° C,
After kneading for 5 minutes, the mixture was granulated by a granulator to obtain pellets of the resin composition. This resin composition is referred to as a resin composition (2). An inflation film molding machine using the above two types of pellets, an intermediate layer composed of the resin composition (1),
Further, a 0.1 mm-thick laminated film (intermediate layer 0.06 mm, inner and outer layers 0.02 mm each) composed of an inner layer and an outer layer composed of the resin composition (2) laminated on both sides thereof was prepared. As shown in Table 1, this film had a good balance between excellent heat retention and excellent transparency.
【００３９】（比較例１）実施例１で用いた無機粉末Ｍ
のかわりに、ハイドロタルサイト化合物（表１において
無機粉末Ｈで表示する）を用いた以外は実施例と全く同
様にしてフィルムを作製した。表１に示すとおり、この
フィルムは、保温性および透明性に関して実施例１のフ
ィルムよりも劣っていた。Comparative Example 1 Inorganic powder M used in Example 1
Instead of using a hydrotalcite compound (indicated by inorganic powder H in Table 1), a film was produced in exactly the same manner as in the example. As shown in Table 1, this film was inferior to the film of Example 1 in heat retention and transparency.
【００４０】（比較例２）実施例１で用いた無機粉末Ｍ
のかわりに、酸化珪素を用いた以外は実施例と全く同様
にしてフィルムを作製した。表１に示すとおり、このフ
ィルムは、保温性および透明性に関して実施例１のフィ
ルムよりも劣っていた。Comparative Example 2 Inorganic Powder M Used in Example 1
Instead, a film was produced in exactly the same manner as in the example except that silicon oxide was used. As shown in Table 1, this film was inferior to the film of Example 1 in heat retention and transparency.
【００４１】（実施例２）エチレン／酢酸ビニル共重合
体（商品名：エバテートＨ２０３１； 住友化学工業
製）８７．１重量部に、見掛密度０．１８ｇ／ｃｍ3の
無機粉末Ｍを１２重量部、ヒンダードアミン系化合物Ａ
０．３０重量部、ヒンダード系化合物Ｂ０．３重量部、
酸化防止剤０．１重量部、滑剤としてステアリン酸アミ
ド０．２重量部を加え、バンバリーミキサーを用いて１
５０℃、５分間混練した後、造粒機により造粒し、樹脂
組成物のペレットを得た。この樹脂組成物を樹脂組成物
(3)とする。次にエチレン／ヘキセン−１共重合体（商
品名：スミカセンＥ ＦＶ２０１；住友化学工業製）６
０重量部、低密度ポリエチレン（商品名：スミカセン
Ｆ２０８−１； 住友化学工業製）３９重量部、ヒンダ
ードアミン系化合物Ａ０．６重量部、紫外線吸収剤０．
１重量部、酸化防止剤０．１重量部、ステアリン酸アミ
ド０．２重量部を加え、バンバリーミキサーを用いて１
５０℃、５分間混練した後、造粒機により造粒し、樹脂
組成物のペレットを得た。この樹脂組成物を樹脂組成物
(4)とする。上記二種類のペレットを用いてインフレー
ションフィルム成形機により、樹脂組成物(3)からなる
中間層、およびその両側に積層された樹脂組成物(4)か
らなる内層および外層からなる厚み０．０７５ｍｍの積
層フィルム（中間層０．０４５ｍｍ、内外層各０．０１
５ｍｍ）を作製した。その後、内層表面にコロナ処理を
行い、その上にアルミナゾル（商品名：アルミナゾル５
２０； 日産化学製； 固形分：２０％）、コロイダル
シリカ（商品名：スノーテックス２０； 日産化学製；
固形分：２０％）、ドデシルベンゼンスルホン酸ナト
リウム（商品名：ネオペレックスＦ２５； 花王製）、
デカン酸ナトリウム（ナカライテスク製）をそれぞれ固
形分濃度１．６／０．４／０．０８／０．０８となるよ
うに水で希釈して調製されたコーティング液を、固形分
厚み約０．１ｇ／ｍ2となるように塗布し、室温で乾燥
し、防曇性被膜を有する積層フィルムを得た。表２に示
すとおり、このフィルムは優れた保温性と優れた透明性
とをバランスよく有していた。Example 2 128.1 parts by weight of an inorganic powder M having an apparent density of 0.18 g / cm 3 was added to 87.1 parts by weight of an ethylene / vinyl acetate copolymer (trade name: Evatate H2031; manufactured by Sumitomo Chemical Co., Ltd.). Part, hindered amine compound A
0.30 parts by weight, hindered compound B 0.3 parts by weight,
0.1 parts by weight of an antioxidant and 0.2 parts by weight of stearamide as a lubricant were added, and 1 part was added using a Banbury mixer.
After kneading at 50 ° C. for 5 minutes, the mixture was granulated by a granulator to obtain pellets of the resin composition. This resin composition is
(3). Next, an ethylene / hexene-1 copolymer (trade name: Sumikacene EFV201; manufactured by Sumitomo Chemical Co., Ltd.) 6
0 parts by weight, low density polyethylene (trade name: Sumikasen
F208-1; manufactured by Sumitomo Chemical Co., Ltd.) 39 parts by weight, hindered amine compound A 0.6 parts by weight, ultraviolet absorber 0.
1 part by weight, 0.1 part by weight of an antioxidant, and 0.2 part by weight of stearamide were added, and 1 part by weight was added using a Banbury mixer.
After kneading at 50 ° C. for 5 minutes, the mixture was granulated by a granulator to obtain pellets of the resin composition. This resin composition is
(4). Inflation film molding machine using the above two types of pellets, an intermediate layer composed of the resin composition (3), and a thickness of 0.075 mm composed of an inner layer and an outer layer composed of the resin composition (4) laminated on both sides thereof. Laminated film (intermediate layer 0.045 mm, inner and outer layers 0.01
5 mm). Thereafter, the inner layer surface is subjected to corona treatment, and alumina sol (trade name: alumina sol 5)
20; manufactured by Nissan Chemical; solid content: 20%), colloidal silica (trade name: Snowtex 20; manufactured by Nissan Chemical;
Solid content: 20%), sodium dodecylbenzenesulfonate (trade name: Neoperex F25; manufactured by Kao),
A coating solution prepared by diluting sodium decanoate (manufactured by Nacalai Tesque) with water so as to have a solid concentration of 1.6 / 0.4 / 0.08 / 0.08, respectively, was coated with a solid having a solid content of about 0.1%. The coating was applied at 1 g / m 2 and dried at room temperature to obtain a laminated film having an antifogging film. As shown in Table 2, this film had a good balance between excellent heat retention and excellent transparency.
【００４２】（比較例３）実施例２で用いた無機粉末Ｍ
のかわりに、ハイドロタルサイト類化合物（表２におい
て無機粉末Ｈで表示する）を用いた以外は実施例と全く
同様にしてフィルムを作製した。表２に示すとおり、こ
のフィルムは、保温性および透明性に関して実施例２の
フィルムよりも劣っていた。Comparative Example 3 Inorganic Powder M Used in Example 2
Instead of using a hydrotalcite compound (indicated by inorganic powder H in Table 2), a film was produced in exactly the same manner as in the example. As shown in Table 2, this film was inferior to the film of Example 2 in heat retention and transparency.
【００４３】（比較例４）実施例２で用いた無機粉末Ｍ
のかわりに、リチウムアルミニウム複合水酸化物（表２
において無機粉末Ｌで表示する）を用いた以外は実施例
と全く同様にしてフィルムを作製した。表２に示すとお
り、このフィルムは、保温性および透明性に関して実施
例２のフィルムよりも劣っていた。Comparative Example 4 Inorganic Powder M Used in Example 2
Instead of lithium aluminum composite hydroxide (Table 2
In this example, a film was produced in exactly the same manner as in Example except that inorganic powder L was used. As shown in Table 2, this film was inferior to the film of Example 2 in heat retention and transparency.
【００４４】[0044]
【表１】 無機粉末Ｍ： Mg2+ 0.67Al3+ 0.33(OH-)2・(Si4O9 2-)0.065(SO4 2-)0.070.
07(CO3 2-)0.03・0.58H2O 無機粉末Ｈ：ハイドロタルサイト Mg2+ 0.69Al3+ 0.31(OH-)2・(CO3 2-)0.155・0.54H2O[Table 1] Inorganic powder M: Mg 2+ 0.67 Al 3+ 0.33 (OH − ) 2. (Si 4 O 9 2- ) 0.065 (SO 4 2- ) 0.07 0.
07 (CO 3 2-) 0.03 · 0.58H 2 O inorganic powder H: hydrotalcite Mg 2+ 0.69 Al 3+ 0.31 (OH -) 2 · (CO 3 2-) 0.155 · 0.54H 2 O
【００４５】[0045]
【表２】 無機粉末Ｍ： Mg2+ 0.67Al3+ 0.33(OH-)2・(Si4O9 2-)0.065(SO4 2-)0.070.
07(CO3 2-)0.03・0.58H2O 無機粉末Ｈ：ハイドロタルサイト Mg2+ 0.69Al3+ 0.31(OH-)2・(CO3 2-)0.155・0.54H2O 無機粉末Ｌ：リチウムアルミニウム複合水酸化物 Li+ 2Al3+ 4(OH-)12・(CO3 2-)・3H2O[Table 2] Inorganic powder M: Mg 2+ 0.67 Al 3+ 0.33 (OH − ) 2. (Si 4 O 9 2- ) 0.065 (SO 4 2- ) 0.07 0.
07 (CO 3 2-) 0.03 · 0.58H 2 O inorganic powder H: hydrotalcite Mg 2+ 0.69 Al 3+ 0.31 (OH -) 2 · (CO 3 2-) 0.155 · 0.54H 2 O inorganic powder L: lithium aluminum complex hydroxide Li + 2 Al 3+ 4 (OH -) 12 · (CO 3 2-) · 3H 2 O
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０８Ｋ 3/38 Ｃ０８Ｋ 3/38 5/17 5/17 Ｆターム(参考） 2B024 DB01 EA01 2B029 EC02 EC09 EC14 EC16 EC17 EC19 EC20 4F071 AA15X AA28X AA76X AC10 AC12 AE05 AE10 AE22 AF03 AF30 AF56 BA01 BB06 BB09 BC01 4J002 BB031 BB051 BB061 BB071 BB081 BB121 BB151 BB231 DJ006 DK006 EH037 EN007 ET007 EU177 FA086 FD047 FD057 FD207 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C08K 3/38 C08K 3/38 5/17 5/17 F term (Reference) 2B024 DB01 EA01 2B029 EC02 EC09 EC14 EC16 EC17 EC19 EC20 4F071 AA15X AA28X AA76X AC10 AC12 AE05 AE10 AE22 AF03 AF30 AF56 BA01 BB06 BB09 BC01 4J002 BB031 BB051 BB061 BB071 BB081 BB121 BB151 BB231 DJ006 DK006 EH037 FD57 EU007 FE070 007
Claims (15)
て、下記式（Ｉ）で表される無機粉末を１〜２５０重量
部含有することを特徴とするポリオレフィン系樹脂組成
物。 M2+ 1-xAl3+ x（OH-）2・［（An-）(x-a)/n・（Bm-）a/m］・ｂH2O (I) 但し、Ｍ2+はＭｇ、Ｃａ及びＺｎから選ばれる１種以上
の２価金属イオン、Ａn-は２個以上のＳｉを含む１種以
上のｎ価の珪酸イオン、Ｂm-はＳｉを含まない１種以上
のｍ価のアニオンであり、ｘ、ａ、ｂは下記の条件式を
満足する。 ０＜ｘ＜０．５、０＜ａ＜ｘ、０≦ｂ≦２1. A polyolefin-based resin composition comprising 1 to 250 parts by weight of an inorganic powder represented by the following formula (I) based on 100 parts by weight of a polyolefin-based resin. M 2+ 1-x Al 3+ x (OH -) 2 · [(A n-) (xa) / n · (B m-) a / m] · bH 2 O (I) where, M 2+ is mg, one or more divalent metal ion selected from Ca and Zn, a n-1 or more n-valent silicate ions containing two or more Si, B m-is one or more that do not contain Si It is a m-valent anion, and x, a, and b satisfy the following conditional expressions. 0 <x <0.5, 0 <a <x, 0 ≦ b ≦ 2
ン、硝酸イオン、ハロゲンイオン、塩素のオキシ酸のイ
オン、硼素のオキシ酸のイオンおよび燐のオキシ酸のイ
オンからなる群より選ばれるアニオンであることを特徴
とする請求項１記載のポリオレフィン系樹脂組成物。Wherein the inorganic powder B m-is, carbonate ion, selected from the group consisting of ions of sulfate ion, nitrate ion, halogen ions, ions of oxyacids of chlorine ion and oxy acids of phosphorus oxyacid of boron The polyolefin resin composition according to claim 1, wherein the composition is an anion.
イオン、または、炭酸イオンおよび硼素のオキシ酸のイ
オン、または、炭酸イオンおよび燐のオキシ酸のイオン
であることを特徴とする請求項１記載のポリオレフィン
系樹脂組成物。3. The inorganic powder according to claim 2, wherein B m- is a carbonate ion and a sulfate ion, a carbonate ion and a boron oxyacid ion, or a carbonate ion and a phosphorus oxyacid ion. Item 7. The polyolefin resin composition according to Item 1.
以上であることを特徴とする請求項１〜３のいずれか一
項に記載のポリオレフィン系樹脂組成物。4. An inorganic powder having an apparent density of 0.13 g / cm 3.
The polyolefin-based resin composition according to any one of claims 1 to 3, characterized in that:
範囲にあることを特徴とする請求項１〜４のいずれか一
項に記載のポリオレフィン系樹脂組成物。5. The polyolefin resin composition according to claim 1, wherein the refractive index of the inorganic powder is in the range of 1.48 to 1.52.
防曇剤および防霧剤から選ばれる少なくとも１種を含有
することを特徴とする請求項１〜５のいずれか一項に記
載のポリオレフィン系樹脂組成物。6. A hindered amine compound, an ultraviolet absorber,
The polyolefin resin composition according to any one of claims 1 to 5, comprising at least one selected from an antifogging agent and an antifog agent.
て、下記式（Ｉ）で表される無機粉末を１〜２５０重量
部含有するポリオレフィン系樹脂組成物からなる層を少
なくとも１層有することを特徴とする樹脂フィルム。 M2+ 1-xAl3+ x（OH-）2・［（An-）(x-a)/n・（Bm-）a/m］・ｂH2O (I) 但し、Ｍ2+はＭｇ、Ｃａ及びＺｎから選ばれる１種以上
の２価金属イオン、Ａn-は２個以上のＳｉを含む１種以
上のｎ価の珪酸イオン、Ｂm-はＳｉを含まない１種以上
のｍ価のアニオンであり、ｘ、ａ、ｂは下記の条件式を
満足する。 ０＜ｘ＜０．５、０＜ａ＜ｘ、０≦ｂ≦２7. A layer comprising a polyolefin resin composition containing 1 to 250 parts by weight of an inorganic powder represented by the following formula (I) per 100 parts by weight of a polyolefin resin. Resin film. M 2+ 1-x Al 3+ x (OH -) 2 · [(A n-) (xa) / n · (B m-) a / m] · bH 2 O (I) where, M 2+ is mg, one or more divalent metal ion selected from Ca and Zn, a n-1 or more n-valent silicate ions containing two or more Si, B m-is one or more that do not contain Si It is a m-valent anion, and x, a, and b satisfy the following conditional expressions. 0 <x <0.5, 0 <a <x, 0 ≦ b ≦ 2
ン、硝酸イオン、ハロゲンイオン、塩素のオキシ酸のイ
オン、硼素のオキシ酸のイオンおよび燐のオキシ酸のイ
オンからなる群より選ばれるアニオンであることを特徴
とする請求項７記載の樹脂フィルム。8. The inorganic powder wherein B m− is selected from the group consisting of carbonate ion, sulfate ion, nitrate ion, halogen ion, chlorine oxyacid ion, boron oxyacid ion and phosphorus oxyacid ion. The resin film according to claim 7, wherein the resin film is an anion.
イオン、または、炭酸イオンおよび硼素のオキシ酸のイ
オン、または、炭酸イオンおよび燐のオキシ酸のイオン
であることを特徴とする請求項７記載の樹脂フィルム。9. Bm- in the inorganic powder is a carbonate ion and a sulfate ion, a carbonate ion and a boron oxyacid ion, or a carbonate ion and a phosphorus oxyacid ion. Item 7. The resin film according to Item 7.
3以上であることを特徴とする請求項７〜９のいずれか
一項に記載の樹脂フィルム。10. The inorganic powder has an apparent density of 0.13 g / cm.
The resin film according to any one of claims 7 to 9, wherein the number is 3 or more.
の範囲にあることを特徴とする請求項７〜１０のいずれ
か一項に記載の樹脂フィルム。11. The inorganic powder has a refractive index of 1.48 to 1.52.
The resin film according to any one of claims 7 to 10, wherein
０重量％であることを特徴とする請求項７〜１１のいず
れか一項に記載の樹脂フィルム。12. The content of the inorganic powder in the film is from 1 to 3.
The resin film according to any one of claims 7 to 11, wherein the content is 0% by weight.
剤、防曇剤および防霧剤から選ばれる少なくとも１種を
含有することを特徴とする請求項７〜１２のいずれか一
項に記載の樹脂フィルム。13. The resin film according to claim 7, further comprising at least one selected from the group consisting of a hindered amine compound, an ultraviolet absorber, an anti-fogging agent and an anti-fog agent.
ことを特徴とする請求項７〜１３のいずれか一項に記載
の樹脂フィルム。14. The resin film according to claim 7, which has an antifogging coating layer on at least one side.
樹脂フィルムを用いてなる園芸施設内で行なうことを特
徴とする作物の栽培方法。15. A method for cultivating a crop, wherein the method is carried out in a horticultural facility using the resin film according to any one of claims 6 to 14.