JP2001215747A - Electrophotographic ohp image accepting sheet - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain an electrophotographic OHP image accepting sheet on which a sharp image having excellent reproducibility of the tone can be obtained, and to find out an image accepting sheet which does not produce a grayish color in an projected image by an OHP by an easy measuring method. SOLUTION: The electrophotographic OHP image accepting sheet shows <=40% haze when the transmission density of a yellow image formed by an electrophotographic process ranges from 0 to 1.0. Or, the haze is <=30% when the transmission density ranges 0 to 0.6. Or, the haze is in the range expressed by formula (1): Y<=32-17/(7X+0.6), wherein X is the transmission density and Y is the haze, when the transmission density ranges from 0 to 0.6. Thus, the sheet on which a sharp image with excellent reproducibility in the tone can be obtained and which does not produce a grayish color in a projected image by an OHP can be obtained by an easy method based on the measurement of the haze and transmission density of an image formed by using an actual printer.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、電子写真方式によ
って形成される画像を記録する受像シートに関して、特
にカラー画像をＯＨＰにて投影した場合に、投影画像の
グレー化を抑えることができる電子写真用ＯＨＰ受像シ
ートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an image receiving sheet for recording an image formed by an electrophotographic method, and more particularly to an electrophotographic method capable of suppressing graying of a projected image when a color image is projected by an OHP. OHP image receiving sheet for use.

【０００２】[0002]

【従来の技術】最近、電子写真方式を使用して、イエロ
ー、マゼンタ、シアンの３色または上記の３色にブラッ
クを加えた４色のトナーの混色によりフルカラー画像の
形成方法が実用化されている。この電子写真方式で用い
られる受像シートは、文字や画像などの記録情報を、確
実に記録保持するため、一般的に、基材上に、受像層を
形成した構成をとっている。この受像シートは、例え
ば、講演会、学校、企業、その他の説明会や展示会など
で使用されている情報伝達手段として、ＯＨＰ（オーバ
ーヘッドプロジェクター）用で用いられている。2. Description of the Related Art Recently, a method of forming a full-color image has been put to practical use by using an electrophotographic system and mixing three colors of yellow, magenta, and cyan, or a mixture of four colors of toner obtained by adding black to the above three colors. I have. The image receiving sheet used in the electrophotographic method generally has a configuration in which an image receiving layer is formed on a base material in order to reliably record and hold recorded information such as characters and images. The image receiving sheet is used for an OHP (overhead projector) as an information transmission means used in, for example, lectures, schools, companies, other briefings and exhibitions.

【０００３】電子写真方式により形成されたカラー画像
をＯＨＰにて投影した時に、投影画像がグレー化（グレ
ーの色調を示す）し、色調再現の範囲が狭まるという現
象が生じる。これは、受像シートの平滑な受像表面の上
に付着したトナーが、定着時の加熱によって、充分に受
像層に埋め込み、平滑化されずに、粒状に盛り上がって
しまい、ＯＨＰの投影時に入射光が散乱され、スクリー
ン上に影を形成するからである。When a color image formed by an electrophotographic method is projected by an OHP, a phenomenon occurs that the projected image is grayed (indicating a gray color tone), and a range of color tone reproduction is narrowed. This is because the toner adhering to the smooth image receiving surface of the image receiving sheet is sufficiently embedded in the image receiving layer due to heating during fixing and is not smoothed, but rises in a granular form, and the incident light during the OHP projection is reduced. This is because they are scattered and form shadows on the screen.

【０００４】このグレー化の問題の解決方法として、例
えば特開平５−８８４００や特開平５−１９７１８４で
は、受像シートの受像面とトナーの定着温度におけるト
ナーとの溶融トナー傾斜角を規定している。しかし、こ
の溶融トナー傾斜角の測定方法は、実際の記録するプリ
ンターにおける定着条件とは異なり、試料としてトナー
のディスクを成形し、ホットプレート上に受像シートと
該ディスクを置いて、指定された測定器で溶融トナー傾
斜角を測定するものであり、成形用部材やホットプレー
ト等の特殊の機器が必要であり、また、上記の測定には
注意力が必要であり、測定値がばらつく等、実用できる
利便性を有しているものではない。As a method for solving the problem of graying, for example, Japanese Patent Application Laid-Open No. 5-88400 and Japanese Patent Application Laid-Open No. 5-197184 specify the inclination angle of the molten toner between the image receiving surface of the image receiving sheet and the toner at the fixing temperature of the toner. . However, this method of measuring the inclination angle of the molten toner differs from the fixing conditions in an actual recording printer, in which a toner disk is molded as a sample, the image receiving sheet and the disk are placed on a hot plate, and the specified measurement is performed. It measures the inclination angle of the molten toner with a container, and requires special equipment such as a molding member and a hot plate.In addition, the above-mentioned measurement requires attention, and the measured value may vary. It does not have the convenience that can be achieved.

【０００５】[0005]

【発明が解決しようとする課題】したがって、本発明で
は、上記の問題を解決するために、色調再現性に優れ、
鮮明な画像が得られる電子写真用ＯＨＰ受像シートで、
ＯＨＰの投影画像において、簡便な測定方法にてグレー
化を生じないものを見出すことができることを目的とし
ている。Therefore, in order to solve the above problems, the present invention has excellent color tone reproducibility,
An OHP image receiving sheet for electrophotography that gives clear images,
An object of the present invention is to be able to find an image that does not cause graying by a simple measuring method in an OHP projection image.

【０００６】[0006]

【課題を解決するための手段】上記目的を達成するため
に、本発明の電子写真用ＯＨＰ受像シートは、電子写真
方式で形成されたイエロー画像の透過濃度が０〜１．０
の範囲で、曇価が４０％以下であることを特徴とする。
また、電子写真用ＯＨＰ受像シートにおいて、電子写真
方式で形成されたイエロー画像の曇価が、透過濃度０〜
０．６において、３０％以下であることを特徴とする。In order to achieve the above object, an electrophotographic OHP image-receiving sheet according to the present invention has a yellow image formed by an electrophotographic system having a transmission density of 0 to 1.0.
, The haze value is 40% or less.
Further, in the electrophotographic OHP image receiving sheet, the cloudiness of the yellow image formed by the electrophotographic method is set to a transmission density of 0 to 0.
0.6, 30% or less.

【０００７】電子写真用ＯＨＰ受像シートにおいて、電
子写真方式で形成されたイエロー画像の曇価が、透過濃
度が０〜０．６の範囲では、次式（１）の範囲となるこ
とを特徴とする。 Ｙ≦３２−１７／（７Ｘ＋０．６） ……（１） ［Ｘ：透過濃度、Ｙ：曇価であり、但し０≦Ｘ≦０．
６］ また、上記の電子写真用ＯＨＰ受像シートにおいて、基
材フィルムの少なくとも一方の面に、受像層を設けたこ
とを特徴とすることが好ましい。以上の電子写真用ＯＨ
Ｐ受像シートにより、上記の課題を解決することができ
た。The electrophotographic OHP image receiving sheet is characterized in that the cloudiness of a yellow image formed by the electrophotographic method is in the range of the following equation (1) when the transmission density is in the range of 0 to 0.6. I do. Y ≦ 32−17 / (7X + 0.6) (1) [X: transmission density, Y: haze value, provided that 0 ≦ X ≦ 0.
6] In the electrophotographic OHP image receiving sheet, it is preferable that an image receiving layer is provided on at least one surface of the base film. OH for electrophotography
The above problem was solved by the P image receiving sheet.

【０００８】本発明の電子写真用ＯＨＰ受像シートは、
電子写真方式で形成されたイエロー画像の透過濃度が０
〜１．０の範囲で、曇価が４０％以下である。または、
上記の曇価が、透過濃度０〜０．６において、３０％以
下である。または、上記の曇価が、透過濃度が０〜０．
６の範囲では、上式（１）で示される範囲にある。これ
により、実際のプリンターを用いて、画像形成したもの
について曇価の測定（ＪＩＳ Ｋ ７１０５に準じた日
本電色工業（株）製ヘーズメータ）と透過濃度測定（Ｍ
ａｃｂｅｔｈ ＴＲ−９２４、フィルター；ｓｔａｔｕ
ｓ Ａ ｂｌｕｅ（ＩＳＯ ５−３））とを行い、簡便
な方法により、色調再現性に優れ、鮮明な画像が得ら
れ、ＯＨＰの投影画像において、グレー化を生じないも
のが得られる。The OHP image-receiving sheet for electrophotography according to the present invention comprises:
The transmission density of a yellow image formed by electrophotography is 0
Within the range of 1.0 to 1.0, the haze value is 40% or less. Or
The haze value is 30% or less at a transmission density of 0 to 0.6. Alternatively, when the haze value is from 0 to 0.
The range of 6 is in the range represented by the above equation (1). Thus, the haze value of the image formed using an actual printer (Haze meter manufactured by Nippon Denshoku Industries Co., Ltd. according to JIS K 7105) and the transmission density measurement (M
acbeth TR-924, filter; statu
s A blue (ISO 5-3)), a clear image with excellent color tone reproducibility is obtained by a simple method, and an OHP projection image that does not cause graying is obtained.

【０００９】[0009]

【発明の実施の形態】次に、電子写真用ＯＨＰ受像シー
トの具体例を挙げて、本発明をさらに詳細に説明する。
尚、本発明に関わる受像シートは、静電潜像をトナー現
像して形成した可視像を転写記録するための受像シート
全般を包含しており、電子写真記録用受像シートだけに
限定されるものではない。図面を基に、本発明の実施の
形態について説明する。図３は本発明の受像シートの一
つの実施の形態を表す縦断面図であり、基材フィルム１
の一方の面に、受像層２を設けた受像シートである。Next, the present invention will be described in more detail by giving specific examples of OHP image receiving sheets for electrophotography.
The image receiving sheet according to the present invention includes all image receiving sheets for transferring and recording a visible image formed by developing an electrostatic latent image with toner, and is limited to only an image receiving sheet for electrophotographic recording. Not something. An embodiment of the present invention will be described with reference to the drawings. FIG. 3 is a longitudinal sectional view showing one embodiment of the image receiving sheet of the present invention.
Is an image receiving sheet provided with an image receiving layer 2 on one surface.

【００１０】また、図４、５は、本発明の受像シートの
他の実施の形態を表す縦断面図であり、図４は基材フィ
ルム１の一方の面に、受像層２を設け、その受像層２の
上に抵抗制御層３を設けている。図５は、基材フィルム
１の一方の面に、受像層２を設け、その受像層２の上に
抵抗制御層３を設け、さらに基材フィルム１の他方の面
に抵抗制御層４を設けた構成である。また、本発明の受
像シートは、基材フィルムの一方の面に受像層を設け、
必要に応じて、抵抗制御層を受像面及び／または裏面の
最外層に、また受像層と基材フィルムの間にプライマー
層を設けることができ、また基材フィルムの他方の面に
裏面層を設けることが可能である。FIGS. 4 and 5 are longitudinal sectional views showing another embodiment of the image receiving sheet of the present invention. FIG. 4 shows an image receiving layer 2 provided on one surface of a base film 1. A resistance control layer 3 is provided on the image receiving layer 2. FIG. 5 shows an image receiving layer 2 provided on one surface of a base film 1, a resistance control layer 3 provided on the image receiving layer 2, and a resistance control layer 4 provided on the other surface of the base film 1. Configuration. Further, the image receiving sheet of the present invention is provided with an image receiving layer on one surface of the base film,
If necessary, a resistance control layer can be provided on the outermost layer on the image receiving surface and / or the back surface, a primer layer can be provided between the image receiving layer and the base film, and a back surface layer can be provided on the other surface of the base film. It is possible to provide.

【００１１】以下、本発明の電子写真用ＯＨＰ受像シー
トの各部の構成について順次説明する。 （基材フィルム）本発明の受像シートで用いられる基材
フィルム１としては、受像シートがＯＨＰシート用等で
透過光により記録画像を観察する用途であり、透明性、
耐熱性、寸法安定性、剛性を備えた熱可塑性樹脂により
形成されたものが好ましい。具体的には、ポリエチレン
テレフタレート樹脂、ポリカーボネート樹脂、アクリル
樹脂、ポリ塩化ビニル樹脂、ポリプロピレン樹脂、ポリ
スチレン樹脂、ポリエチレン樹脂、二酢酸セルロース樹
脂、三酢酸セルロース樹脂等の、厚さ１０〜２５０μｍ
程度、好ましくは５０〜１５０μｍ程度のフィルム、又
はシートが挙げられる。中でも、ポリエチレンテレフタ
レート樹脂、ポリ塩化ビニル樹脂、ポリプロピレン樹
脂、三酢酸セルロース樹脂が上記の性能の点でより好ま
しい。Hereinafter, the structure of each part of the electrophotographic OHP image receiving sheet of the present invention will be sequentially described. (Base Film) The base film 1 used in the image receiving sheet of the present invention is used for observing a recorded image with transmitted light when the image receiving sheet is for an OHP sheet or the like.
Those formed of a thermoplastic resin having heat resistance, dimensional stability, and rigidity are preferable. Specifically, a polyethylene terephthalate resin, a polycarbonate resin, an acrylic resin, a polyvinyl chloride resin, a polypropylene resin, a polystyrene resin, a polyethylene resin, a cellulose diacetate resin, a cellulose triacetate resin, etc., have a thickness of 10 to 250 μm.
Film or sheet having a thickness of about 50 to 150 μm. Among them, a polyethylene terephthalate resin, a polyvinyl chloride resin, a polypropylene resin, and a cellulose triacetate resin are more preferable in view of the above performance.

【００１２】尚、本発明の受像シートはＯＨＰシート用
等で透過光により記録画像を観察する用途のものであ
り、基材フィルムと受像層、必要に応じて、抵抗制御
層、プライマー層、裏面層等を加えた受像シート全体の
構成で、平行線透過率が７０％以上にすることが望まし
い。それによって、優れた透過画像を得ることができ
る。尚、基材フィルム上に形成される層との密着性を向
上させる目的で、基材フィルムの表面にプライマー処理
やコロナ放電処理等の公知の易接着処理を施しても良
い。The image receiving sheet of the present invention is used for observing a recorded image by transmitted light, for example, for an OHP sheet, and includes a substrate film and an image receiving layer, if necessary, a resistance control layer, a primer layer, and a back surface. In the configuration of the entire image receiving sheet including the layers and the like, it is desirable that the parallel line transmittance be 70% or more. Thereby, an excellent transmission image can be obtained. For the purpose of improving the adhesion to the layer formed on the substrate film, the surface of the substrate film may be subjected to a known easy adhesion treatment such as a primer treatment or a corona discharge treatment.

【００１３】（受像層）基材の少なくとも一方の面に設
ける受像層２は、トナー定着性を有し、カラートナーの
濡れ性に優れた樹脂が用いられる。本発明の電子写真用
ＯＨＰ受像シートは、基材フィルム自体の上、または基
材フィルムの上に設けられた受像層上に、電子写真画像
を形成するもので、電子写真方式で形成されたイエロー
画像の透過濃度が０〜１．０の範囲で、曇価が４０％以
下である。または、上記の曇価が、透過濃度０〜０．６
において、３０％以下である。または、上記の曇価が、
透過濃度が０〜０．６の範囲では、下記式（１）で示さ
れる範囲にあることで、色調再現性に優れ、鮮明な画像
が得られ、ＯＨＰの投影画像において、グレー化を生じ
ないものが得られる。(Image-Receiving Layer) The image-receiving layer 2 provided on at least one surface of the base material is made of a resin having a toner fixing property and an excellent wettability of a color toner. The electrophotographic OHP image-receiving sheet of the present invention forms an electrophotographic image on the base film itself or on an image receiving layer provided on the base film, and is formed by an electrophotographic method. When the transmission density of the image is in the range of 0 to 1.0, the haze value is 40% or less. Or, when the haze value is 0 to 0.6
, Is 30% or less. Or, if the haze is
When the transmission density is in the range of 0 to 0.6, by being in the range represented by the following formula (1), excellent color tone reproducibility and a clear image can be obtained, and graying does not occur in the OHP projected image. Things are obtained.

【００１４】 Ｙ≦３２−１７／（７Ｘ＋０．６） ……（１） ［Ｘ：透過濃度、Ｙ：曇価であり、但し０≦Ｘ≦０．
６］Y ≦ 32−17 / (7X + 0.6) (1) [X: transmission density, Y: haze value, provided that 0 ≦ X ≦ 0.
6]

【００１５】Ｘを横軸、Ｙを縦軸として、Ｙ＝３２−１
７／（７Ｘ＋０．６）をグラフで示すと、図１の実線の
曲線であり、したがって、上記の式（１）で示される範
囲は、図１の実線部及びその実線よりも下の領域であ
る。X = horizontal axis, Y = vertical axis, Y = 32-1
7 / (7X + 0.6) is a curve indicated by the solid line in FIG. 1. Therefore, the range indicated by the above equation (1) is the solid line in FIG. 1 and the area below the solid line. is there.

【００１６】本発明の受像シートで基材フィルム上に受
像層を形成した場合は、その受像層上に電子写真方式で
イエロー画像を形成した条件で、曇価と透過濃度を測定
し、上記条件を満足するかをチェックするだけで、簡便
な方法により、ＯＨＰの投影画像において、グレー化を
生じるかどうかが判別できる。つまり、ＯＨＰ投影機が
なくても、最終用途であるＯＨＰの投影画像で、上記の
曇価を測定するだけでグレー化を生じるかどうかが判別
できる。但し、本発明で曇価の測定値は、ＪＩＳ Ｋ
７１０５で規定した方法に準じて、日本電色工業（株）
製ヘーズメータにより、また透過濃度の測定値は、Ｍａ
ｃｂｅｔｈ ＴＲ−９２４、ｓｔａｔｕｓ Ａ ｂｌｕ
ｅ フィルター（ＩＳＯ５−３）で計られたものであ
る。When an image receiving layer is formed on a base film using the image receiving sheet of the present invention, the haze value and the transmission density are measured under the condition that a yellow image is formed on the image receiving layer by electrophotography. Is satisfied, it is possible to determine by a simple method whether or not the OHP projection image is grayed. That is, even if there is no OHP projector, it is possible to determine whether or not graying occurs only by measuring the above-mentioned haze value in the projected image of the OHP which is the final use. However, in the present invention, the measured value of the haze value is based on JIS K
Nippon Denshoku Industries Co., Ltd. according to the method specified in 7105
The measured value of the transmission density by a haze meter manufactured by
cbeth TR-924, status A blue
e Measured with a filter (ISO5-3).

【００１７】電子写真方式で形成されたイエロー画像の
透過濃度が０〜１．０の範囲で、曇価が４０％を越える
と、色調再現性に劣り、画像の鮮明性がなくなり、ＯＨ
Ｐの投影画像に、グレー化が生じてくる。また、電子写
真方式で形成されたイエロー画像の曇価が、透過濃度０
〜０．６において、３０％を越えても、上記と同様に色
調再現性に劣り、画像の鮮明性がなくなり、ＯＨＰの投
影画像に、グレー化が生じてくる。また、電子写真方式
で形成されたイエロー画像の曇価が、透過濃度が０〜
０．６の範囲で、下記式（２）で示される範囲にある
と、色調再現性に劣り、画像の鮮明性がなくなり、ＯＨ
Ｐの投影画像に、グレー化が生じてくる。If the transmission density of an electrophotographic yellow image is in the range of 0 to 1.0 and the haze exceeds 40%, the color tone reproducibility is poor, the image is not sharp, and the OH
Graying occurs in the projected image of P. Further, the haze value of the yellow image formed by the electrophotographic method has a transmission density of 0.
If it exceeds 30% in the range of 0.6 to 0.6, the color tone reproducibility is inferior, the image sharpness is lost, and the OHP projection image is grayed as described above. In addition, the cloudiness of a yellow image formed by the electrophotographic method is such that the transmission density is 0 to 0.
In the range of 0.6 and the range represented by the following formula (2), the color tone reproducibility is poor, the image sharpness is lost, and the OH
Graying occurs in the projected image of P.

【００１８】 Ｙ＞３２−１７／（７Ｘ＋０．６） ……（２） ［Ｘ：透過濃度、Ｙ：曇価であり、但し０≦Ｘ≦０．
６］Y> 32-17 / (7X + 0.6) (2) [X: transmission density, Y: haze value, provided that 0 ≦ X ≦ 0.
6]

【００１９】電子写真方式で形成されたイエロー画像の
曇価が特許請求の範囲に記載したようにするには、受像
層を形成する樹脂としては、例えばポリエチレン、ポリ
プロピレン等のポリオレフィン樹脂、ポリ塩化ビニル、
ポリ塩化ビニリデン、ポリ酢酸ビニル、塩化ビニル−酢
酸ビニル共重合体、ポリアクリル酸エステル、ポリスチ
レン等のビニル樹脂、ビスフェノール骨格やアルキレン
骨格を有するジオールと、２価のカルボン酸あるいは３
価のカルボン酸が縮重合してなるポリエステル樹脂やそ
の変性物、ポリアミド系樹脂、エチレンやプロピレン等
のポリオレフィンと他のビニルモノマーとの共重合体、
アイオノマー、エチルセルロース、酢酸セルロース等の
セルロース系樹脂、ポリカーボネート樹脂、エポキシ樹
脂、フェノキシ樹脂等が挙げられる。In order for the haze value of the yellow image formed by the electrophotographic system to be as described in the claims, the resin forming the image receiving layer may be, for example, a polyolefin resin such as polyethylene or polypropylene, or a polyvinyl chloride. ,
Vinyl resins such as polyvinylidene chloride, polyvinyl acetate, vinyl chloride-vinyl acetate copolymer, polyacrylate, and polystyrene; a diol having a bisphenol skeleton or an alkylene skeleton; and a divalent carboxylic acid or 3
Polyester resin and its modified product obtained by condensation polymerization of polyvalent carboxylic acid, polyamide resin, copolymer of polyolefin such as ethylene and propylene and other vinyl monomers,
Examples thereof include ionomers, cellulose resins such as ethyl cellulose and cellulose acetate, polycarbonate resins, epoxy resins, and phenoxy resins.

【００２０】これらの受像層のバインダー樹脂は、軟化
点が３０℃以上２００℃以下のものが用いられる。軟化
点が３０℃未満のものは、保存性の点で好ましくなく、
受像シートを積み重ねた時に受像層が接触面と接着す
る、いわゆるブロッキングが生じやすい。また、軟化点
が２００℃を越えると、画像形成（定着）時に多量のエ
ネルギーを必要とするため好ましくない。トナーの結着
樹脂には、一般的にビスフェノールＡ骨格を有するポリ
エステル樹脂が多用されるために、その相溶性、定着性
等の点で、特にポリエステル樹脂及びその変性物を受像
層のバインダーに用いることが好ましい。As the binder resin for these image receiving layers, those having a softening point of 30 ° C. or more and 200 ° C. or less are used. Those having a softening point of less than 30 ° C are not preferred in terms of storage stability,
When the image receiving sheets are stacked, the image receiving layer is easily adhered to the contact surface, that is, so-called blocking tends to occur. On the other hand, if the softening point exceeds 200 ° C., a large amount of energy is required during image formation (fixing), which is not preferable. Generally, a polyester resin having a bisphenol A skeleton is frequently used as a binder resin of the toner. Therefore, in terms of compatibility, fixability, and the like, particularly, a polyester resin and a modified product thereof are used as a binder for an image receiving layer. Is preferred.

【００２１】受像層のバインダー樹脂に用いるポリエス
テル樹脂は、２価アルコール成分として、エチレングリ
コールやプロピレングリコールで変性したビスフェノー
ルＡのジオール成分や、エチレングリコール、ネオペン
チルグリコール、プロピレングリコール、トリメチレン
グリコール等の２価アルコール成分と、ジカルボン酸成
分として、テレフタール酸、イソフタール酸やフタール
酸等の芳香族ジカルボン酸、またアジピン酸、シュウ
酸、コハク酸、フマル酸、マレイン酸、セバシン酸、マ
ロン酸等の脂肪族ジカルボン酸等挙げられる。これらの
２価アルコール成分とジカルボン酸との縮重合して、ポ
リエステル樹脂が得られる。The polyester resin used as the binder resin in the image receiving layer includes a dihydric alcohol component such as a diol component of bisphenol A modified with ethylene glycol or propylene glycol, or ethylene glycol, neopentyl glycol, propylene glycol or trimethylene glycol. Dihydric alcohol component and dicarboxylic acid component such as terephthalic acid, isophthalic acid, phthalic acid and other aromatic dicarboxylic acids, and adipic acid, oxalic acid, succinic acid, fumaric acid, maleic acid, sebacic acid, malonic acid and other fats Group dicarboxylic acids and the like. Polycondensation of these dihydric alcohol components and dicarboxylic acids gives polyester resins.

【００２２】上記に挙げたポリエステル樹脂は、その構
成成分の種類に関わらず、その数平均分子量が１，５０
０〜７，０００の範囲であることが好ましく、その分子
量が小さすぎると、樹脂が柔らかすぎるため、受像シー
トを積み重ねた時に受容層が接触面と接着し、ブロッキ
ングが生じやすい。一方、その分子量が大きすぎると受
像層バインダー樹脂としては硬すぎるため、トナーとの
相溶性が低下し、受像表面上に付着したトナーが、定着
時の加熱によって、充分に受容層に埋め込まれずに、粒
状に盛り上がってしまい、ＯＨＰの投影時に入射光が散
乱され、スクリーン上に影を形成する、いわゆる投影画
像のグレー化が特にハイライト部で生じやすくなる。The above-mentioned polyester resins have a number average molecular weight of 1,50, irrespective of the type of the constituent components.
The molecular weight is preferably in the range of 0 to 7,000. If the molecular weight is too small, the resin is too soft, so that the receiving layer adheres to the contact surface when the image receiving sheets are stacked, and blocking tends to occur. On the other hand, if the molecular weight is too large, the compatibility with the toner is lowered because the binder resin is too hard for the image receiving layer, and the toner attached on the image receiving surface is not sufficiently embedded in the receiving layer by heating during fixing. When the OHP is projected, the incident light is scattered and a shadow is formed on a screen, that is, graying of a projected image is likely to occur particularly in a highlight portion.

【００２３】以上のような受像層バインダー樹脂は、電
子写真記録に用いるトナーのバインダー樹脂との相溶性
が良く、トナー定着性及びトナー濡れ性が良いものであ
り、優れた画像再現性を発揮し、かつ電子写真方式で形
成されたイエロー画像の透過濃度が０〜１．０の範囲
で、曇価を４０％以下とすることができ、また、同曇価
が、透過濃度０〜０．６において、３０％以下とでき、
また、同曇価が、透過濃度が０〜０．６の範囲では、前
記式（１）で示される範囲にすることが可能となる。The binder resin of the image receiving layer as described above has good compatibility with the binder resin of the toner used for electrophotographic recording, and has good toner fixability and toner wettability, and exhibits excellent image reproducibility. When the transmission density of the yellow image formed by the electrophotographic method is in the range of 0 to 1.0, the haze value can be set to 40% or less. , It can be 30% or less,
Further, when the transmission density is in the range of 0 to 0.6, the haze value can be in the range represented by the above formula (1).

【００２４】また、受像層には有機フィラーや無機フィ
ラーのいずれか一方、または両方を受像層の曇価を上昇
させる影響があまりない程度に含有させることができ、
搬送適性を向上させる。有機フィラーとしては、四フッ
化エチレン樹脂、エチレン−四フッ化エチレン共重合体
等のフッ素系樹脂、ポリエチレン樹脂、ポリスチレン樹
脂、アクリル樹脂、ポリアミド樹脂、ベンゾグアナミン
樹脂等の有機樹脂からなる微粒子が挙げられる。一方、
無機フィラーとしては、シリカ、コロイダルシリカ、ア
ルミナ、カオリン、クレー、炭酸カルシウム、タルク、
二酸化チタン、炭酸カルシウム等が挙げられる。The image receiving layer may contain one or both of an organic filler and an inorganic filler to such an extent that the effect of increasing the haze of the image receiving layer is not so much affected.
Improves transport suitability. Examples of the organic filler include fine particles made of an organic resin such as a tetrafluoroethylene resin, a fluorine-based resin such as an ethylene-tetrafluoroethylene copolymer, a polyethylene resin, a polystyrene resin, an acrylic resin, a polyamide resin, and a benzoguanamine resin. . on the other hand,
As the inorganic filler, silica, colloidal silica, alumina, kaolin, clay, calcium carbonate, talc,
Examples include titanium dioxide and calcium carbonate.

【００２５】また、含有させるフィラーの平均粒径は
０．１〜３０μｍ程度、好ましくは３〜２０μｍ程度で
ある。平均粒径が０．１μｍ未満であると、所望の効果
が充分に得られず、また３０μｍを越えても画像ヌケを
起こしたり、ＯＨＰに使用する時の透明感が低下するの
で好ましくない。また、フィラーの含有量は受像層バイ
ンダー樹脂に対して０．１〜１０質量％の範囲が好まし
い。含有量が多すぎると透明性が低下し、また、含有量
が少なすぎると、所望の搬送適性の向上効果が得られな
い。また、受像層には上記フィラーの他、各種界面活性
剤、ワックス、オイル等の添加剤を本発明の効果を妨げ
ない範囲で混合使用しても良い。受像層の形成は、上記
樹脂成分、フィラー、その他必要に応じて各種添加剤な
どを有する塗液を、グラビア印刷、シルクスクリーン印
刷等の公知の印刷手段、あるいは、グラビアコート等の
公知の塗工手段により形成し、厚さは乾燥時で１〜１０
μｍ程度とする。The average particle size of the filler to be contained is about 0.1 to 30 μm, preferably about 3 to 20 μm. If the average particle size is less than 0.1 μm, the desired effects cannot be sufficiently obtained, and even if it exceeds 30 μm, it is not preferable because image dropping occurs and transparency when used for OHP is reduced. The content of the filler is preferably in the range of 0.1 to 10% by mass based on the binder resin of the image receiving layer. If the content is too large, the transparency is lowered, and if the content is too small, a desired effect of improving transportability cannot be obtained. Further, in the image receiving layer, in addition to the above filler, additives such as various surfactants, waxes and oils may be mixed and used as long as the effects of the present invention are not impaired. The image-receiving layer is formed by applying a coating liquid containing the above resin component, filler, and other various additives as necessary, using a known printing method such as gravure printing or silk screen printing, or a known coating method such as gravure coating. The thickness is 1-10 when dry.
It is about μm.

【００２６】（裏面層）本発明の受像シートは、必要に
応じて前記基材フィルムの他方の面に、フィラーあるい
はＳｉ基を含有した裏面層６を設けることができる。本
発明の受像シートは、搬送適性をより向上させ、基材フ
ィルム表面側の受像層に対して、カール防止性をもたせ
るため、基材フィルムの受像層の設けられていない側
に、裏面層を形成できる。さらに、裏面層は、基材フィ
ルム表面の受像層と同様の画像受容性をもたせれば、受
像シートの表、裏に関わらず、また受像シートの両面に
画像を形成することができる。(Back Layer) In the image receiving sheet of the present invention, a back layer 6 containing a filler or a Si group can be provided on the other surface of the base film, if necessary. The image-receiving sheet of the present invention further improves transportability and, for the image-receiving layer on the front surface side of the base film, has a curl preventing property. Can be formed. Further, if the backside layer has the same image receptivity as the image receiving layer on the surface of the base film, an image can be formed on both sides of the image receiving sheet irrespective of the front and back sides of the image receiving sheet.

【００２７】裏面層は、アクリル系樹脂、ポリエステル
系樹脂、ウレタン系樹脂等や、シリコーン基が付加され
た熱可塑性樹脂として、シリコーン変性アクリル系樹
脂、シリコーン変性ウレタン系樹脂、シリコーン変性ポ
リエステル系樹脂等が使用できる。さらに、アクリル
系、ビニル系、ポリエステル系、ポリウレタン系、ポリ
アミド系又はセルロース系樹脂のバインダー樹脂の主鎖
に、ポリシロキサンセグメント、フッ化炭素セグメント
及び長鎖アルキルセグメントの中の少なくとも１種の離
型性セグメントを有するグラフトコポリマーも、熱可塑
性樹脂として、使用できる。The back layer is made of an acrylic resin, a polyester resin, a urethane resin, or a thermoplastic resin to which a silicone group is added, such as a silicone-modified acrylic resin, a silicone-modified urethane resin, or a silicone-modified polyester resin. Can be used. Further, at least one of a polysiloxane segment, a fluorocarbon segment and a long-chain alkyl segment is released from the main chain of an acrylic, vinyl, polyester, polyurethane, polyamide or cellulose resin binder resin. A graft copolymer having a functional segment can also be used as a thermoplastic resin.

【００２８】裏面層の形成は、上記の樹脂と有機フィラ
ーまたは無機フィラーと、その他添加剤を必要に応じて
加えて、受像層と同様に公知の塗工手段により、行わ
れ、裏面層の厚さは、乾燥時で０．０１〜１．０μｍ程
度あれば十分な効果が得られるが、表面電気抵抗率を制
御する場合には、それに応じた厚みが必要になり、０．
１〜２．０μｍ程度が好ましい。裏面層のフィラーは、
有機フィラーとしては、四フッ化エチレン樹脂、エチレ
ン−四フッ化エチレン共重合体等のフッ素系樹脂、ポリ
エチレン樹脂、ポリスチレン樹脂、アクリル樹脂、ポリ
アミド樹脂、ベンゾグアナミン樹脂等の有機樹脂からな
るフィラーが挙げられる。一方、無機フィラーとして
は、シリカ、コロイダルシリカ、アルミナ、カオリン、
クレー、炭酸カルシウム、タルク、二酸化チタン、炭酸
カルシウム等が使用できる。The back layer is formed by a known coating method similarly to the image receiving layer by adding the above-mentioned resin, an organic filler or an inorganic filler, and other additives as necessary. A sufficient effect can be obtained if the dryness is about 0.01 to 1.0 μm. However, when the surface electrical resistivity is controlled, a thickness corresponding to the thickness is required.
About 1 to 2.0 μm is preferable. The filler in the back layer is
Examples of the organic filler include a filler made of an organic resin such as a tetrafluoroethylene resin, a fluororesin such as an ethylene-tetrafluoroethylene copolymer, a polyethylene resin, a polystyrene resin, an acrylic resin, a polyamide resin, and a benzoguanamine resin. . On the other hand, as the inorganic filler, silica, colloidal silica, alumina, kaolin,
Clay, calcium carbonate, talc, titanium dioxide, calcium carbonate and the like can be used.

【００２９】（抵抗制御層）抵抗制御層を受像面及び／
または裏面の最外層に、または受像層と基材フィルムの
間及び／または裏面層と基材フィルムの間に、設けるこ
とで、帯電防止性やトナー定着性を良好に保持させるこ
とができる。抵抗制御層で使用する抵抗制御材料とし
て、イオン伝導性材料、金属微粒子、π電子共役二重結
合を有する導電性ポリマーが挙げられる。イオン伝導性
材料としては、陽イオン、陰イオン、両性イオン系のも
のがあり、例えば、第４級アンモニウム塩、ポリアミン
誘導体等のカチオン系帯電防止剤、アルキルホスフェー
ト等のアニオン系帯電防止剤、脂肪酸エステル等のノニ
オン系帯電防止剤が挙げられる。(Resistance Control Layer) The resistance control layer is formed on the image receiving surface and / or
Alternatively, by providing the outermost layer on the back surface or between the image receiving layer and the base film and / or between the back surface layer and the base film, the antistatic property and the toner fixing property can be kept good. Examples of the resistance control material used in the resistance control layer include an ion conductive material, metal fine particles, and a conductive polymer having a π electron conjugated double bond. Examples of the ion conductive material include cations, anions, and zwitterionics. Examples thereof include quaternary ammonium salts, cationic antistatic agents such as polyamine derivatives, anionic antistatic agents such as alkyl phosphates, and fatty acids. Nonionic antistatic agents such as esters are exemplified.

【００３０】金属微粒子としては、例えば、酸化スズ
（ＳｎＯ₂）、酸化亜鉛（ＺｎＯ）、酸化インジウム
（Ｉｎ₂Ｏ₃）、酸化チタン（ＴｉＯ₂）等が挙げること
ができ、これらの１種あるいは２種以上の組合せを使用
することができる。このような金属微粒子は、平均粒径
が０．０１〜１．０μｍの範囲にあるものが好ましい。
また上記のような金属微粒子は、必要に応じてドーパン
トを添加しても良く、ドーパントは、例えば、ＳｎＯ₂
の場合はＳｂ（アンチモン）、ＺｎＯの場合はＡｌ（ア
ルミニウム）、またＩｎ₂Ｏ₃の場合はＳｎが一般的に使
用される。尚、上記の金属酸化物は、１種類でも、他の
種類と組み合わせて使用してもよい。さらに、上記金属
酸化物は、ＳｎＯ₂または、ＳｂでドープされたＳｎＯ₂
で被覆されていても良い。Examples of the metal fine particles include tin oxide (SnO ₂ ), zinc oxide (ZnO), indium oxide (In ₂ O ₃ ), and titanium oxide (TiO ₂ ). Two or more combinations can be used. Such metal fine particles preferably have an average particle diameter in the range of 0.01 to 1.0 μm.
The fine metal particles as described above, may be optionally added a dopant, the dopant, for example, SnO ₂
In general, Sb (antimony) is used for ZnO, Al (aluminum) for ZnO, and Sn for In ₂ O ₃ . The above metal oxides may be used alone or in combination with other types. Furthermore, the metal oxide, SnO _2, or, SnO ₂ doped with Sb
It may be coated with.

【００３１】さらに上記のような金属微粒子は針状粒子
であっても良く、この場合、長軸が０．１〜２μｍの範
囲内にあり、アスペクト比が１０〜５０の範囲内にある
針状粒子が好ましい。このような針状の金属微粒子を使
用することにより、球状の金属微粒子よりも少ない量で
抵抗率制御が可能になるため、その金属微粒子を含有す
る層の透明性が向上し、受像シートをＯＨＰのような透
過光により記録画像を観察するような用途に使用する場
合に、透過画像の品質を高めることができる。本発明の
受像シートでは、金属微粒子として塗工適性、表面電気
抵抗率の安定性と金属電気伝導性、価格等の点から、Ｓ
ｎＯ₂あるいは、ＳｎＯ₂で被覆された金属酸化物や、特
にアンチモンでドープした酸化スズが好ましく用いられ
る。Further, the metal fine particles as described above may be acicular particles, and in this case, the major axis is in the range of 0.1 to 2 μm and the aspect ratio is in the range of 10 to 50. Particles are preferred. By using such needle-shaped metal fine particles, the resistivity can be controlled with a smaller amount than that of the spherical metal fine particles. Therefore, the transparency of the layer containing the metal fine particles can be improved, and the image receiving sheet can be made of OHP. When used for applications such as observing recorded images with transmitted light, the quality of transmitted images can be improved. In the image receiving sheet of the present invention, from the viewpoints of coating suitability, stability of surface electric resistivity, metal electric conductivity, and price as metal fine particles,
Metal oxide coated with nO ₂ or SnO ₂ , or tin oxide doped with antimony is particularly preferably used.

【００３２】上記の金属微粒子を含有した層の塗工液の
配合として、金属微粒子の質量／熱可塑性樹脂（バイン
ダー）の質量＝０．２〜２．０が好ましい。金属微粒子
の質量／熱可塑性樹脂の質量比が０．２未満では、金属
微粒子の量が少ないため、形成される層の表面電気抵抗
率が安定しない。また、金属微粒子の質量／熱可塑性樹
脂の質量比が２．０を越えると、特にアンチモンでドー
プされた酸化スズの場合、その金属微粒子の特有の色が
目立ち、好ましくない。（アンチモンでドープされた酸
化スズの場合、青味の色が表面に目立って出てくる。）
上記の金属微粒子は、その微粒子表面を親水性処理を施
したり、界面活性剤、エチレングリコール等の既知の分
散剤を添加して、バインダー樹脂水溶液中に分散させる
ことが好ましく行われる。The composition of the coating liquid for the layer containing the fine metal particles is preferably 0.2 to 2.0 = (weight of fine metal particles) / (weight of thermoplastic resin (binder)). If the mass ratio of the metal fine particles / the thermoplastic resin is less than 0.2, the amount of the metal fine particles is small, so that the surface electric resistivity of the formed layer is not stable. On the other hand, if the mass ratio of the metal fine particles / the thermoplastic resin exceeds 2.0, the tin oxide doped with antimony has a distinctive color, which is not preferable. (In the case of tin oxide doped with antimony, a bluish color appears prominently on the surface.)
The metal fine particles are preferably dispersed in an aqueous binder resin solution by subjecting the surface of the fine particles to hydrophilic treatment or adding a known dispersant such as a surfactant or ethylene glycol.

【００３３】次に、π電子共役二重結合を有する導電性
ポリマーとしては、例えば、ポリチオフェン、ポリアニ
リン、スルホン化ポリアニリン、化学的にドーピングし
たポリアセチレン、ポリパラフェニレン、ポリフェニレ
ンビニレン、ポリパラフェニレンスルフィド、化学的に
重合とドーピングしたポリピロール、熱処理により生成
したフェノール樹脂の熱処理物、ポリアミドの熱処理
物、ペリレン酸無水物の熱処理物等が挙げられる。上記
のπ電子共役系構造を有する導電性ポリマーとして、特
にスルホン基でドープしたポリアニリンやポリチオフェ
ンが有用である。Next, examples of the conductive polymer having a π electron conjugated double bond include polythiophene, polyaniline, sulfonated polyaniline, chemically doped polyacetylene, polyparaphenylene, polyphenylenevinylene, polyparaphenylene sulfide, and polyparaphenylene sulfide. Polypyrrole, which is thermally polymerized and doped, a heat-treated product of a phenol resin produced by heat treatment, a heat-treated product of polyamide, a heat-treated product of perylene anhydride, and the like. As the conductive polymer having the π-electron conjugated structure, polyaniline and polythiophene doped with a sulfone group are particularly useful.

【００３４】また、上記のポリチオフェンは透明性が高
いので、ＯＨＰ用の受像シートを作成するのにも利用で
きる。本発明に係る受像シートに、特に透明性が求めら
れる場合には、その光線の透過率を７０％以上にするこ
とができる。さらに、かかるポリチオフェンはポリマー
であり、従来の低分子帯電制御剤とは異なり、含有層か
らブリードアウトしにくいので、受像シートのべタツキ
や、保存中における帯電制御能力の低下や、ブリードア
ウトした帯電制御剤によるトナー受像層の汚染（裏移
り）をほとんど起こさない。Since the above-mentioned polythiophene has high transparency, it can be used for preparing an image receiving sheet for OHP. When the image receiving sheet according to the present invention is particularly required to have transparency, the light transmittance of the image receiving sheet can be 70% or more. Further, such polythiophene is a polymer and unlike conventional low-molecular charge control agents, it is difficult to bleed out from the containing layer, so that the image receiving sheet is sticky, the charge control ability is reduced during storage, and the bleed-out charge is reduced. Almost no contamination (set-off) of the toner image receiving layer by the control agent occurs.

【００３５】上記のポリチオフェンは、水、又は、水と
水混和性有機溶剤（例えば、メタノール、エタノール、
アセトン等）の混合溶剤中に、ポリ陰イオンの共存下で
部分的に正の電荷を帯びて溶解又は分散する。従って、
かかるポリチオフェンを含有する帯電制御層用塗工液又
は受像層用塗工液などの塗工液を調整して受像シートの
基材上に塗布することにより、ポリチオフェンを含有す
る層を容易に形成することができる。ポリ陰イオンの供
給源としては、例えば、ポリスチレンスルホン酸のよう
な高分子スルホン酸、ポリアクリル酸のような高分子カ
ルボン酸、ポリりん酸、或いはそれらのアルカリ塩、と
りわけ分子量が２，０００〜５００，０００のものを用
いることができる。好ましいポリ陰イオンはポリスチレ
ンスルホン酸である。分散体を調製する場合には、かか
る分散体中のポリチオフェンの平均粒径を１０μｍ以下
とするのが好ましい。ポリチオフェンの溶液又は分散体
は、市販品を入手することも可能であり、例えば、バイ
エル社から「バイトロン Ｐ（Ｂａｙｔｒｏｎ Ｐ）」
の表品名で入手できる。The above polythiophene can be prepared from water or a water-miscible organic solvent (for example, methanol, ethanol,
In a mixed solvent of acetone or the like) in the presence of a polyanion and partially dissolved or dispersed with a positive charge. Therefore,
A polythiophene-containing layer is easily formed by preparing a coating liquid such as a coating liquid for a charge control layer or a coating liquid for an image receiving layer containing the polythiophene, and applying the prepared coating liquid on a substrate of an image receiving sheet. be able to. As the source of the polyanion, for example, a high molecular sulfonic acid such as polystyrene sulfonic acid, a high molecular carboxylic acid such as polyacrylic acid, polyphosphoric acid, or an alkali salt thereof, particularly, having a molecular weight of 2,000 to 500,000 can be used. A preferred polyanion is polystyrene sulfonic acid. When preparing a dispersion, the average particle size of the polythiophene in such a dispersion is preferably 10 μm or less. As the solution or dispersion of polythiophene, a commercially available product can be obtained. For example, “Baytron P” from Bayer is available.
It can be obtained under the table name.

【００３６】また、他のπ電子共役系構造を有する導電
性高分子材料として、スルホン化ポリアニリンも有用で
ある。スルホン化ポリアニリンは、スルホン基でドープ
したポリアニリンである。スルホン化ポリアニリンは、
例えば、日東化学工業（株）からａｑｕａ Ｐａｓｓ−
０１Ｚの商品名で、かつ水溶液や水と有機溶剤との混合
溶媒の溶液として入手して本発明で使用することができ
る。これらの溶液は黄色を帯びた溶液であるが、濃度が
低い場合には殆ど無色の溶液であり、ＯＨＰシート用等
で透過光により記録画像を観察する用途では、受像シー
トに透明性が要求されるが、問題なく使用することがで
きる。Sulfonated polyaniline is also useful as another conductive polymer material having a π-electron conjugated structure. Sulfonated polyaniline is polyaniline doped with sulfone groups. Sulfonated polyaniline is
For example, from Nitto Chemical Industry Co., Ltd., Aqua Pass-
It can be used in the present invention under the trade name of 01Z and obtained as an aqueous solution or a mixed solvent solution of water and an organic solvent. These solutions are yellowish solutions, but are almost colorless when the concentration is low, and the transparency of the image receiving sheet is required for applications such as OHP sheets for observing recorded images with transmitted light. But can be used without any problems.

【００３７】抵抗制御層の形成は、バインダー樹脂と抵
抗制御材料を主体とした塗工液を受像シートの最表面
（受像面、裏面）または受像層の下、あるいは裏面層の
下に、例えば、グラビアコーター、ロールコーター、ワ
イヤーバー等の慣用の塗工方式で塗工及び乾燥して行わ
れる。その塗工量は、乾燥後の塗工厚みとして約０．０
０１〜５μｍ程度であり、塗工量が上記範囲より少ない
と、帯電制御の性能が不十分であり、一方、塗工量が上
記範囲より多くても、その厚みに比例して、上記性能が
向上する訳ではないので、経済的に不利であるばかりで
なく、電子写真複写機、プリンターによる画像の濃度が
低下するので好ましくない。The resistance control layer is formed by applying a coating liquid mainly composed of a binder resin and a resistance control material to the outermost surface (image receiving surface, back surface) of the image receiving sheet or under the image receiving layer or under the back surface layer, for example, Coating and drying are performed by a conventional coating method such as a gravure coater, a roll coater, and a wire bar. The coating amount is about 0.0 as coating thickness after drying.
When the coating amount is less than the above range, the charge control performance is insufficient. On the other hand, even when the coating amount is larger than the above range, the above-described performance is proportional to the thickness. Since it does not mean that the density is not improved, it is not only economically disadvantageous but also unfavorably because the density of an image by an electrophotographic copying machine or a printer is reduced.

【００３８】上記の抵抗制御層を、受像シートの受像面
及び／または裏面の最外層に、または受像層と基材フィ
ルムの間及び／または裏面層と基材フィルムの間に、設
け、その抵抗制御層の抵抗制御剤の含有量、塗工量を制
御することで、受像シートの抵抗制御層を表面にした状
態で、表面抵抗率を、温度２３±２℃、相対湿度５０±
１０％の環境で、１×１０⁸〜１×１０¹⁴Ω／□の範囲
に収めることが好ましい。その表面抵抗率が１×１０⁸
Ω／□より低いと、転写効率が低下し、記録濃度が低下
しやすく、逆に１×１０¹⁴Ω／□を越えると、トナー転
写後に感光体から受像シートを剥離する時に放電が発生
し、トナーが飛散する等文字、画像が乱れるため、画
質、鮮明性が低下し、また静電気発生や滑性不足により
電子写真複写機、プリンターにおける搬送不良や埃の付
着が起こりやすい。The above-mentioned resistance control layer is provided on the outermost layer on the image receiving surface and / or the back surface of the image receiving sheet, or between the image receiving layer and the base film and / or between the back surface layer and the base film. By controlling the content of the resistance control agent in the control layer and the amount of coating, the surface resistivity is adjusted to a temperature of 23 ± 2 ° C. and a relative humidity of 50 ± with the resistance control layer of the image receiving sheet on the surface.
In an environment of 10%, it is preferable that the density be within a range of 1 × 10 ⁸ to 1 × 10 ¹⁴ Ω / □. Its surface resistivity is 1 × 10 ⁸
If it is lower than Ω / □, the transfer efficiency is lowered and the recording density is apt to be lowered. Conversely, if it exceeds 1 × 10 ¹⁴ Ω / □, discharge occurs when the image receiving sheet is peeled off from the photoreceptor after toner transfer. Characters and images are disturbed, such as toner being scattered, so that the image quality and clarity are deteriorated. In addition, due to the generation of static electricity and insufficient lubrication, poor conveyance and dust adhesion in electrophotographic copying machines and printers are likely to occur.

【００３９】（プライマー層）本発明の受像シートは、
受像層と基材フィルムの間に、プライマー層を設けるこ
とができ、基材フィルムと受像層との接着性が向上し、
受像層の基材フィルムからの剥離がなくなり、受像層の
定着ローラーへのオフセット等を防止できる。プライマ
ー層に用いる樹脂として、例えばアルキッド樹脂、ポリ
エステル樹脂、ポリ酢酸ビニル樹脂、塩ビ酢ビ共重合樹
脂、ＮＢＲ樹脂、ＳＢＲ樹脂、ポリウレタン樹脂、アク
リル系樹脂、ポリアミド等が単独もしくは混合物、共重
合物、あるいは変性物として用いられる。変性物とは、
例えば、水酸基やカルボン酸、４級アンモニウム塩含有
モノマーを共重合もしくはグラフトさせて、接着性、親
水性を上げたもの等である。(Primer Layer) The image-receiving sheet of the present invention comprises:
A primer layer can be provided between the image receiving layer and the base film, and the adhesion between the base film and the image receiving layer is improved,
Peeling of the image receiving layer from the base film is eliminated, and offset of the image receiving layer to the fixing roller can be prevented. As the resin used for the primer layer, for example, an alkyd resin, a polyester resin, a polyvinyl acetate resin, a vinyl chloride-vinyl acetate copolymer resin, an NBR resin, an SBR resin, a polyurethane resin, an acrylic resin, a polyamide or the like alone or as a mixture, a copolymer, Alternatively, it is used as a denatured product. A denatured product is
For example, those obtained by copolymerizing or grafting a monomer containing a hydroxyl group, a carboxylic acid, or a quaternary ammonium salt to increase the adhesiveness and hydrophilicity, and the like.

【００４０】また、プライマー層の接着性、塗膜強度を
向上させるために、上記の樹脂を各種硬化剤、例えばエ
ポキシ樹脂、メラミン樹脂、イソシアネート等により架
橋させてもよい。上述したプライマー層の形成方法は、
前述の受像層の形成方法と同様な方法が選べる。プライ
マー層の厚みは、乾燥時で、０．０１〜１０μｍ、好ま
しくは０．０５〜１．０μｍとするのが良い。この厚み
が、少なすぎると、接着性で充分な性能が発揮せず、一
方で、厚みが多すぎると、受像シートを裁断時に端面が
ベタついたり、製造コストが高くついたり、好ましくな
い。In order to improve the adhesion of the primer layer and the strength of the coating film, the above resin may be crosslinked with various curing agents, for example, epoxy resin, melamine resin, isocyanate and the like. The method for forming the above-mentioned primer layer,
A method similar to the above-described method for forming the image receiving layer can be selected. The thickness of the primer layer when dried is preferably 0.01 to 10 μm, and more preferably 0.05 to 1.0 μm. If the thickness is too small, sufficient performance cannot be exhibited in adhesiveness, while if the thickness is too large, the end face becomes sticky when the image receiving sheet is cut, and the production cost is high, which is not preferable.

【００４１】[0041]

【実施例】次に実施例をあげて、本発明を具体的に説明
する。尚、文中、部または％とあるのは、特に断りのな
い限り質量基準である。 （実施例１）下記に示す基材フィルムの一方の面に、下
記組成の受像層塗工液１を用いて、受像層を形成し、そ
の受像層の上に、下記の抵抗制御層塗工液を用いて、抵
抗制御層を形成し、実施例１の受像シートを作製した。
また、受像層の厚み（乾燥時）は２μｍ、抵抗制御層の
厚みは受像シートの表面電気抵抗率が１×１０¹⁰Ω／□
になるように調整した。Next, the present invention will be described in detail with reference to examples. In the following description, “parts” or “%” is based on mass unless otherwise specified. Example 1 An image receiving layer was formed on one surface of a base film shown below using an image receiving layer coating solution 1 having the following composition, and the following resistance control layer was coated on the image receiving layer. A resistance control layer was formed using the liquid, and an image receiving sheet of Example 1 was produced.
The thickness of the image receiving layer (when dried) is 2 μm, and the thickness of the resistance control layer is such that the surface electric resistivity of the image receiving sheet is 1 × 10 ¹⁰ Ω / □.
It was adjusted to become.

【００４２】基材フィルム 厚さ１００μｍのポリエチレンテレフタレートフィルム（東レ（株）製、１０ ０−Ｔ６０）受像層塗工液１ ポリエステル樹脂 ３０部 （油化シェルエポキシ社製、エピコート１００４、数平均分子量１，６００、軟 化点９７℃、Ｔｇ５５℃） シリカフィラー（平均粒径５μｍ） ０．５部 メチルエチルケトン ３５部 トルエン ３５部 Base film 100 μm thick polyethylene terephthalate film (100-T60, manufactured by Toray Industries, Inc.) Image receiving layer coating liquid 1 polyester resin 30 parts (Yuka Kasper Epoxy, Epicoat 1004, number average molecular weight 1) , 600, softening point 97 ° C, Tg 55 ° C) Silica filler (average particle size 5 μm) 0.5 part Methyl ethyl ketone 35 parts Toluene 35 parts

【００４３】抵抗制御層塗工液 カチオン変性４級アンモニウム塩 １部 イソプロピルアルコール １００部 Coating solution for resistance control layer Cation-modified quaternary ammonium salt 1 part Isopropyl alcohol 100 parts

【００４４】（実施例２）実施例１で使用した基材フィ
ルムの一方の面に、下記の受像層塗工液２を用いて、受
像層を形成し、その受像層の上に、実施例１で使用した
抵抗制御層塗工液を用いて、抵抗制御層を形成し、実施
例２の受像シートを作製した。また、受像層の厚み（乾
燥時）は２μｍ、抵抗制御層の厚みは受像シートの表面
電気抵抗率が１×１０¹⁰Ω／□になるように調整した。(Example 2) An image receiving layer was formed on one surface of the base film used in Example 1 by using the following image receiving layer coating liquid 2, and an example was formed on the image receiving layer. A resistance control layer was formed using the resistance control layer coating solution used in Example 1, and an image receiving sheet of Example 2 was produced. The thickness (when dried) of the image receiving layer was adjusted to 2 μm, and the thickness of the resistance control layer was adjusted so that the surface electrical resistivity of the image receiving sheet was 1 × 10 ¹⁰ Ω / □.

【００４５】受像層塗工液２ ポリエステル樹脂 ３０部 （東洋紡績（株）製、ＲＶ２２０、数平均分子量４，０００、Ｔｇ５３℃） シリカフィラー（平均粒径５μｍ） ０．５部 メチルエチルケトン ３５部 トルエン ３５部Image receiving layer coating liquid 2 Polyester resin 30 parts (Toyobo Co., Ltd., RV220, number average molecular weight 4,000, Tg 53 ° C.) Silica filler (average particle size 5 μm) 0.5 part Methyl ethyl ketone 35 parts Toluene 35 Department

【００４６】（実施例３）実施例１で使用した基材フィ
ルムの一方の面に、下記の受像層塗工液３を用いて、受
像層を形成し、その受像層の上に、実施例１で使用した
抵抗制御層塗工液を用いて、抵抗制御層を形成し、実施
例３の受像シートを作製した。また、受像層の厚み（乾
燥時）は２μｍ、抵抗制御層の厚みは受像シートの表面
電気抵抗率が１×１０¹⁰Ω／□になるように調整した。Example 3 An image-receiving layer was formed on one surface of the base film used in Example 1 by using the following image-receiving layer coating liquid 3, and an example was formed on the image-receiving layer. A resistance control layer was formed using the resistance control layer coating solution used in Example 1, and an image receiving sheet of Example 3 was produced. The thickness (when dried) of the image receiving layer was adjusted to 2 μm, and the thickness of the resistance control layer was adjusted so that the surface electrical resistivity of the image receiving sheet was 1 × 10 ¹⁰ Ω / □.

【００４７】受像層塗工液３ ポリエステル樹脂 ３０部 （日本合成化学（株）製、ＨＰ３２０、数平均分子量３，３００、Ｔｇ６３℃） シリカフィラー（平均粒径５μｍ） ０．５部 メチルエチルケトン ３５部 トルエン ３５部Image receiving layer coating liquid 3 Polyester resin 30 parts (Nippon Synthetic Chemical Co., Ltd., HP320, number average molecular weight 3,300, Tg 63 ° C.) Silica filler (average particle size 5 μm) 0.5 part Methyl ethyl ketone 35 parts Toluene 35 parts

【００４８】（比較例１）実施例１で使用した基材フィ
ルムの一方の面に、下記の受像層塗工液４を用いて、受
像層を形成し、その受像層の上に、実施例１で使用した
抵抗制御層塗工液を用いて、抵抗制御層を形成し、比較
例１の受像シートを作製した。また、受像層の厚み（乾
燥時）は２μｍ、抵抗制御層の厚みは受像シートの表面
電気抵抗率が１×１０¹⁰Ω／□になるように調整した。(Comparative Example 1) An image receiving layer was formed on one surface of the base film used in Example 1 by using the following image receiving layer coating liquid 4, and an example was formed on the image receiving layer. A resistance control layer was formed using the resistance control layer coating solution used in Example 1, and an image receiving sheet of Comparative Example 1 was produced. The thickness (when dried) of the image receiving layer was adjusted to 2 μm, and the thickness of the resistance control layer was adjusted so that the surface electrical resistivity of the image receiving sheet was 1 × 10 ¹⁰ Ω / □.

【００４９】受像層塗工液４ ポリエステル樹脂 ３０部 （日本合成化学（株）製、ＨＰ３１３、数平均分子量８，０００、Ｔｇ６４℃） シリカフィラー（平均粒径５μｍ） ０．５部 メチルエチルケトン ３５部 トルエン ３５部Image receiving layer coating liquid 4 Polyester resin 30 parts (HP313, Nippon Synthetic Chemical Co., Ltd., number average molecular weight 8,000, Tg 64 ° C.) Silica filler (average particle size 5 μm) 0.5 part Methyl ethyl ketone 35 parts Toluene 35 parts

【００５０】（比較例２）実施例１で使用した基材フィ
ルムの一方の面に、下記の受像層塗工液５を用いて、受
像層を形成し、その受像層の上に、実施例１で使用した
抵抗制御層塗工液を用いて、抵抗制御層を形成し、比較
例２の受像シートを作製した。また、受像層の厚み（乾
燥時）は２μｍ、抵抗制御層の厚みは受像シートの表面
電気抵抗率が１×１０¹⁰Ω／□になるように調整した。Comparative Example 2 An image receiving layer was formed on one surface of the base film used in Example 1 by using the following image receiving layer coating liquid 5, and an example was formed on the image receiving layer. A resistance control layer was formed using the resistance control layer coating solution used in Example 1, and an image receiving sheet of Comparative Example 2 was produced. The thickness (when dried) of the image receiving layer was adjusted to 2 μm, and the thickness of the resistance control layer was adjusted so that the surface electrical resistivity of the image receiving sheet was 1 × 10 ¹⁰ Ω / □.

【００５１】受像層塗工液５ ポリエステル樹脂 ３０部 （東洋紡績（株）製、ＲＶ２００、数平均分子量１７，０００、軟化点１６３℃ 、Ｔｇ５３℃） シリカフィラー（平均粒径５μｍ） ０．５部 メチルエチルケトン ３５部 トルエン ３５部Image receiving layer coating liquid 5 Polyester resin 30 parts (Toyobo Co., Ltd., RV200, number average molecular weight 17,000, softening point 163 ° C., Tg 53 ° C.) Silica filler (average particle size 5 μm) 0.5 part 35 parts of methyl ethyl ketone 35 parts of toluene

【００５２】上記の実施例及び比較例の受像シートを用
いて、下記の方法にて、電子写真方式で形成されたイエ
ロー画像の曇価、透過濃度を測定し、また画像品質の評
価を実施した。尚、実施例及び比較例の受像シートの受
像シートの表面電気抵抗率は、各受像シートの表面に、
２３℃５０％ＲＨの環境下で、５００Ｖの電圧を印加
し、印加開始から１０秒後の表面電気抵抗率を、表面抵
抗測定機（Ｈｉｅｓｔａ、三菱油化株式会社製）を用い
て測定した。Using the image receiving sheets of the above Examples and Comparative Examples, the haze value and transmission density of the yellow image formed by the electrophotographic method were measured by the following method, and the image quality was evaluated. . Incidentally, the surface electrical resistivity of the image receiving sheets of the image receiving sheets of the examples and comparative examples, the surface of each image receiving sheet,
Under an environment of 23 ° C. and 50% RH, a voltage of 500 V was applied, and the surface electrical resistivity 10 seconds after the start of application was measured using a surface resistance measuring device (Hiesta, manufactured by Mitsubishi Yuka Corporation).

【００５３】（曇価、透過濃度）各実施例及び比較例の
受像シートの受像面に、自作の電子写真方式のプリンタ
（使用するトナーのバインダーの軟化点が１００℃、定
着ロールの表面温度が１８０℃）を用いて、下記条件の
イエロー画像のみを記録し、その記録された印字物を、
ＪＩＳ Ｋ ７１０５で規定する方法に準じて、日本電
色工業（株）製ヘーズメータにより、曇価を測定し、ま
たＭａｃｂｅｔｈ社の透過濃度計ＴＲ−９２４にて、Ｉ
ＳＯ ５−３に規定されているｓｔａｔｕｓ Ａ ｂｌ
ｕｅ フィルターを使用して透過濃度を測定した。(Haze Value, Transmission Density) A self-made electrophotographic printer (the softening point of the toner binder used was 100 ° C., and the surface temperature of the fixing roll was 100 ° C.) 180 ° C.), only the yellow image under the following conditions was recorded, and the recorded printed matter was
The haze value was measured with a haze meter manufactured by Nippon Denshoku Industries Co., Ltd. in accordance with the method specified in JIS K 7105, and I was measured with a Macbeth transmission density meter TR-924.
Status A bl specified in SO 5-3
The transmission density was measured using a ue filter.

【００５４】イエロー画像条件；電子写真学会テストチ
ャートＮｏ．５−１にあるイエロー階調パターンと同等
条件、または２５６階調にてＲ＝２２５、Ｇ＝２２５、
Ｂ＝Ｘ（０≦Ｘ≦２５５）のデータにて作成された画像
を使用する。上記の曇価、透過濃度の測定結果を下記の
表１に示す。また、各測定データを横軸に透過濃度、縦
軸に曇価として、プロットしたグラフを図２に示す。そ
の表及びグラフに示されているように、実施例１〜３
は、電子写真のイエロー画像の透過濃度０〜１．０の範
囲で、曇価が４０％以下であり、また実施例１、２はイ
エロー画像の透過濃度０〜０．６において、曇価が３０
％以下である。さらに、実施例１、２では、イエロー画
像の透過濃度０〜０．６において、透過濃度をＸ、曇価
をＹとして、Ｙ≦３２−１７／（７Ｘ＋０．６）の関係
を満足している。但し、図２の実線で示された曲線が、
Ｙ＝３２−１７／（７Ｘ＋０．６）である。Yellow image conditions; Test chart No. R = 225, G = 225, and the same conditions as the yellow gradation pattern in 5-1 or 256 gradations
An image created with data of B = X (0 ≦ X ≦ 255) is used. Table 1 below shows the measurement results of the above haze value and transmission density. FIG. 2 is a graph in which each measurement data is plotted as the transmission density on the horizontal axis and the haze value on the vertical axis. As shown in the table and the graph, Examples 1 to 3
Indicates that the transmission density of the electrophotographic yellow image is in the range of 0 to 1.0, and the haze value is 40% or less. 30
% Or less. Further, in Examples 1 and 2, when the transmission density of the yellow image is 0 to 0.6, the transmission density is X and the haze value is Y, and the relationship of Y ≦ 32−17 / (7X + 0.6) is satisfied. . However, the curve shown by the solid line in FIG.
Y = 32−17 / (7X + 0.6).

【００５５】[0055]

【表１】 [Table 1]

【００５６】画像品質 上記の自作の電子写真方式のプリンタにより、イエロ
ー、マゼンタ、シアン、ブラックの各トナーを用いて、
各受像シートにカラーチャートの画像を形成し、その受
像シートをＯＨＰにて投影した時の投影画像について、
グレー化の有無、色調再現性を目視にて評価した。 Image Quality Using the self-made electrophotographic printer described above, using yellow, magenta, cyan, and black toners,
An image of a color chart is formed on each image receiving sheet, and the projected image when the image receiving sheet is projected by OHP is:
The presence or absence of graying and color tone reproducibility were visually evaluated.

【００５７】実施例１及び実施例２の画像形成したＯＨ
Ｐ受像シートは、ハイライト部からシャドー部の全体に
わたって、グレー化が無く、色調再現性が良好であり、
鮮明な投影画像である。実施例３のＯＨＰ受像シート
は、中間濃度において、グレー化が少し認められるが、
色調再現性はほぼ良好であり、画像鮮明性もほぼ良好で
ある。それに対し、比較例１及び比較例２のＯＨＰ受像
シートは、ハイライト部からシャドー部の全体にわたっ
て、グレー化が明瞭に認められ、色調再現性が悪く、不
鮮明な画像である。Image-formed OH of Examples 1 and 2
The P image receiving sheet has no graying and good color tone reproducibility from the highlight portion to the entire shadow portion,
It is a clear projected image. In the OHP image receiving sheet of Example 3, graying was slightly recognized at the intermediate density.
The color tone reproducibility is almost good, and the image clarity is also almost good. On the other hand, in the OHP image receiving sheets of Comparative Examples 1 and 2, graying was clearly recognized from the highlight portion to the entire shadow portion, the color tone reproducibility was poor, and the image was unclear.

【００５８】[0058]

【発明の効果】本発明の電子写真用ＯＨＰ受像シート
は、電子写真方式で形成されたイエロー画像の透過濃度
が０〜１．０の範囲で、曇価が、４０％以下である。ま
たは上記の曇価が、透過濃度０〜０．６において、３０
％以下である。または、上記の曇価が、透過濃度が０〜
０．６の範囲では、上式（１）で示される範囲にある。
これにより、実際のプリンターを用いて、画像形成した
ものを、曇価の測定（ＪＩＳ Ｋ ７１０５に準じた日
本電色工業（株）製ヘーズメータ）と透過濃度測定（Ｍ
ａｃｂｅｔｈ ＴＲ−９２４、フィルター；ｓｔａｔｕ
ｓ Ａ ｂｌｕｅ（ＩＳＯ ５−３））とを行い、簡便
な方法により、色調再現性に優れ、鮮明な画像が得ら
れ、ＯＨＰの投影画像において、グレー化を生じないも
のが得られる。According to the OHP image-receiving sheet for electrophotography of the present invention, the transmission density of a yellow image formed by electrophotography is in the range of 0 to 1.0, and the haze value is 40% or less. Alternatively, when the haze value is 30
% Or less. Or, when the haze value is 0 to 0
In the range of 0.6, it is in the range represented by the above equation (1).
Thus, the image formed using an actual printer was measured for the haze value (Haze meter manufactured by Nippon Denshoku Industries Co., Ltd. according to JIS K 7105) and the transmission density was measured (M
acbeth TR-924, filter; statu
s A blue (ISO 5-3)), a clear image with excellent color tone reproducibility is obtained by a simple method, and an OHP projection image that does not cause graying is obtained.

【図面の簡単な説明】[Brief description of the drawings]

【図１】電子写真方式で形成されたイエロー画像の曇価
が、透過濃度が０〜０．６の範囲で、透過濃度をＸ、曇
価をＹとして、Ｙ≦３２−１７／（７Ｘ＋０．６）の関
係式をグラフ化したものである。FIG. 1 is a graph showing the cloudiness of a yellow image formed by an electrophotographic method, where the transmission density is in the range of 0 to 0.6 and the transmission density is X and the cloudiness is Y, and Y ≦ 32−17 / (7X + 0. 6 is a graph of the relational expression of 6).

【図２】実施例と比較例の各透過濃度、曇価のデータ
を、プロットしたグラフである。FIG. 2 is a graph in which data of transmission density and haze of an example and a comparative example are plotted.

【図３】本発明の受像シートの一つの実施の形態を表す
縦断面図である。FIG. 3 is a longitudinal sectional view illustrating an embodiment of the image receiving sheet of the present invention.

【図４】本発明の受像シートの他の実施の形態を表す縦
断面図である。FIG. 4 is a longitudinal sectional view showing another embodiment of the image receiving sheet of the present invention.

【図５】本発明の受像シートの他の実施の形態を表す縦
断面図である。FIG. 5 is a longitudinal sectional view illustrating another embodiment of the image receiving sheet of the present invention.

【符号の説明】[Explanation of symbols]

１ 基材フィルム ２ 受像層 ３，４ 抵抗制御層 DESCRIPTION OF SYMBOLS 1 Base film 2 Image receiving layer 3, 4 Resistance control layer

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 電子写真方式で形成されたイエロー画像
の透過濃度が０〜１．０の範囲で、曇価が４０％以下で
あることを特徴とする電子写真用ＯＨＰ受像シート。1. An OHP image receiving sheet for electrophotography, wherein the transmission density of a yellow image formed by an electrophotographic method is in the range of 0 to 1.0 and the haze value is 40% or less. 【請求項２】 電子写真方式で形成されたイエロー画像
の曇価が、透過濃度０〜０．６において、３０％以下で
あることを特徴とする電子写真用ＯＨＰ受像シート。2. An OHP image receiving sheet for electrophotography, wherein the haze value of a yellow image formed by an electrophotographic method is 30% or less at a transmission density of 0 to 0.6. 【請求項３】 電子写真方式で形成されたイエロー画像
の曇価が、透過濃度が０〜０．６の範囲では、次式
（１）の範囲となることを特徴とする電子写真用ＯＨＰ
受像シート。 Ｙ≦３２−１７／（７Ｘ＋０．６） ……（１） ［Ｘ：透過濃度、Ｙ：曇価であり、但し０≦Ｘ≦０．
６］3. An OHP for electrophotography, wherein the haze of a yellow image formed by electrophotography is in the range of the following formula (1) when the transmission density is in the range of 0 to 0.6.
Image receiving sheet. Y ≦ 32−17 / (7X + 0.6) (1) [X: transmission density, Y: haze value, provided that 0 ≦ X ≦ 0.
6] 【請求項４】 基材フィルムの少なくとも一方の面に、
受像層を設けたことを特徴とする上記の請求項１〜３の
いずれか一つに記載する電子写真用ＯＨＰ受像シート。4. At least one surface of the base film,
The OHP image receiving sheet for electrophotography according to any one of claims 1 to 3, further comprising an image receiving layer.