JP2001205928A - Material to be recorded for ink jetting with nonaqueous ink - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a fixability-excellent material to be recorded for ink jetting with a nonaqueous ink, which has a favorable absorbability of nonaqueous ink, prevents bleeding of an ink solvent from the periphery of a printed portion with the elapse of time (bleeding properties) from developing in the material to be recorded for ink jetting with the nonaqueous ink used in a printer or a plotter which utilizes an ink jet recording system with the nonaqueous ink. SOLUTION: In the material to be recorded for ink jetting with the nonaqueous ink, which is formed by providing an at least pigment-containing ink absorbing layer on a support and coating or impregnating with a polymer dissolved or swollen by a petroleum high boiling solvent in the ink absorbing layer, a barium sulfate is employed as the pigment in the material.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、非水系インクを用
いたインクジェット記録方式を利用したプリンターやプ
ロッターに使用される非水系インク用インクジェット被
記録材料に関するものである。特に、石油系高沸点溶剤
を含む非水系インクの定着性及びインク吸収性に優れた
非水系インク用インクジェット被記録材料に関するもの
である。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a non-aqueous ink-jet recording material for a non-aqueous ink used in a printer or a plotter utilizing an ink-jet recording system using a non-aqueous ink. In particular, the present invention relates to a non-aqueous ink jet recording material for a non-aqueous ink having excellent fixability and ink absorbability of a non-aqueous ink containing a petroleum-based high boiling point solvent.

【０００２】[0002]

【従来の技術】従来、インクジェット記録では、水性イ
ンク、すなわち水あるいは水と親水性溶剤の混合溶媒
に、染料・顔料などの着色剤を分散あるいは溶解したイ
ンクが多く用いられてきた。2. Description of the Related Art Conventionally, in ink jet recording, an aqueous ink, that is, an ink in which a colorant such as a dye or a pigment is dispersed or dissolved in water or a mixed solvent of water and a hydrophilic solvent has been often used.

【０００３】しかし、水性インクを用いたインクジェッ
ト記録には、被記録材料の印字部分が、インク中の溶媒
を吸収して伸長することによって発生する種々の問題が
ある。かかる被記録材料の伸長は、支持体の機械的強度
を維持している繊維間の水素結合が、水性インクの溶
媒、特に水によって切断されることにより生じ、被記録
材料のプリンター内での搬送に悪影響を及ぼすばかりで
なく、被記録材料とプリントヘッドの相対的な位置関係
の精度を悪化させて、得られる図面の寸法精度が低下し
たり、画像にムラが生じるなどの好ましくない現象を引
き起こしている。[0003] However, ink jet recording using an aqueous ink has various problems that occur when a printed portion of a recording material absorbs and expands a solvent in the ink. Such elongation of the recording material occurs when hydrogen bonds between the fibers that maintain the mechanical strength of the support are cut by the solvent of the aqueous ink, particularly water, and the recording material is transported in the printer. Not only adversely affects the print quality, but also degrades the accuracy of the relative positional relationship between the recording material and the print head, causing undesired phenomena such as a decrease in the dimensional accuracy of the resulting drawing and an uneven image. ing.

【０００４】このような問題に対して、特開昭５７−１
０６６０号公報、同５７−１０６６１号公報、特開平５
−２０２３２４号公報、同５−３３１３９７号公報等で
は、イソパラフィン系炭化水素などの非水系溶剤中に着
色剤を溶解または分散させたインクを用いることが開示
されている。これらの発明によれば、被記録材の伸長を
まったく伴わず、寸法精度が高く、また画像にムラが生
じないインクジェット記録を行うことが可能である。さ
らに、非水系溶剤の特徴である低粘度・低表面張力によ
って、水性インクを用いたインクジェット記録と比較し
て、プリントヘッドの駆動周波数を高くすることが可能
になり、非常に高速なインクジェット記録を行うことが
できる。To solve such a problem, Japanese Patent Laid-Open Publication No.
No. 0660, 57-10661,
JP-A-202324 and JP-A-5-331397 disclose the use of an ink in which a coloring agent is dissolved or dispersed in a non-aqueous solvent such as an isoparaffin hydrocarbon. According to these inventions, it is possible to perform ink jet recording with high dimensional accuracy and no unevenness of the image without any extension of the recording material. In addition, the low viscosity and low surface tension of non-aqueous solvents make it possible to increase the drive frequency of the print head compared to inkjet recording using aqueous inks. It can be carried out.

【０００５】かかる非水系インクを用いたインクジェッ
ト記録に用いる被記録材料として、特開昭６４−２４７
８５号公報等では吸油性無機顔料、有機顔料および水系
接着剤からなる記録材料が開示されており、また特開平
１−２５５５８０号公報等では、シリカおよび接着剤か
らなる記録材料が記載されている。これらの記録材料
は、記録面がつや消し状の外観を有する、いわゆるマッ
トコートタイプの記録材料であった。As a recording material used for ink jet recording using such a non-aqueous ink, Japanese Patent Application Laid-Open No. 64-247 has been disclosed.
No. 85 discloses a recording material comprising an oil-absorbing inorganic pigment, an organic pigment and an aqueous adhesive, and Japanese Patent Application Laid-Open No. 1-255580 discloses a recording material comprising silica and an adhesive. . These recording materials were so-called mat coat type recording materials in which the recording surface had a matte appearance.

【０００６】一方、近年のインクジェットプリンターの
進歩に伴い、銀塩写真に匹敵する高精細の画像を得るこ
とが可能になってきている。これに伴い、銀塩写真のプ
リントに類似した質感、すなわち表面に光沢をもつイン
クジェット用被記録材料が望まれるようになってきてい
る。当然のことながら、このような記録材料には、光沢
を有すると同時に、記録画像の濃度が高いこと、記録画
像の精細性が高い、すなわち各ドットの周囲がなめらか
であり、且つ輪郭が鮮明で、且つインクのはじきや流れ
がないこと、また画像の保存性に優れる、特に着色剤の
定着性が高いことなどが要求される。On the other hand, with the recent development of ink jet printers, it has become possible to obtain high-definition images comparable to silver halide photographs. Accordingly, an ink jet recording material having a texture similar to that of a silver halide photograph print, that is, a glossy surface has been desired. Naturally, such a recording material has glossiness, high density of a recorded image and high definition of a recorded image, that is, the periphery of each dot is smooth, and the outline is clear. In addition, it is required that the ink does not repel or flow and that the image has excellent storability, especially high fixability of the colorant.

【０００７】このような要求に対し、水性インクを使用
したインクジェット記録に対しては、特開昭６３−２６
５６８０号公報、特開平５−５９６９４号公報等で、キ
ャストコート法によって塗工層を設けたインクジェット
用被記録材料が開示されている。また、特開平６−１５
５８９２号公報等では同様の記録材料上にポリビニルア
ルコール等の水溶性ポリマーからなる皮膜を形成した記
録材料が公開されている。さらに、特開平６−１９９０
３５号公報等では、支持体上に擬ベーマイトからなるイ
ンク吸収層を設けた記録材料が記載されている。これら
の発明によれば、高い光沢を有し、水性インクに対して
高い吸収性を有するインクジェット記録材料が得られ
る。しかしながら、これらの記録材料に対し非水系イン
クで記録を行おうとしても、記録材料を形成している素
材とインクに含まれる溶剤あるいは着色剤との間に親和
性がないため、記録材料中での着色剤の分布が不均一に
なって低い画像濃度しか得られなかったり、記録材料の
表面でインクがはじかれてムラが生じたり、着色剤がわ
ずかな摩擦で容易に脱落してしまうなどの欠点があっ
た。従って、これらの記録材料を非水系インクで記録し
ても、濃度・精細性が高く、また保存定着性に優れた記
録画像を得ることは全く不可能であった。[0007] In response to such a demand, an ink jet recording using an aqueous ink is disclosed in
JP-A-5680 and JP-A-5-59694 disclose an inkjet recording material provided with a coating layer by a cast coating method. Also, Japanese Patent Application Laid-Open No.
No. 5892 discloses a recording material in which a film made of a water-soluble polymer such as polyvinyl alcohol is formed on the same recording material. Further, JP-A-6-1990
No. 35 describes a recording material in which an ink absorbing layer made of pseudo-boehmite is provided on a support. According to these inventions, it is possible to obtain an ink jet recording material having high gloss and high absorptivity for aqueous ink. However, even if recording is performed on these recording materials with a non-aqueous ink, there is no affinity between the material forming the recording material and the solvent or colorant contained in the ink. The distribution of the colorant becomes uneven and only a low image density can be obtained, the ink is repelled on the surface of the recording material to cause unevenness, and the colorant easily falls off with a slight friction. There were drawbacks. Therefore, even when these recording materials are recorded with a non-aqueous ink, it was impossible at all to obtain a recorded image having high density and fineness and excellent storage fixability.

【０００８】このような問題を解決した非水系インクを
用いたインクジェット記録に用いる記録材料として、特
開平１０−２５０２１８号公報には、塗工層上にイソパ
ラフィン系炭化水素に可溶なポリマーを含ませること
で、高い記録画像の精細性、着色剤の定着性を併せ持つ
記録材料が開示されている。塗工層上に含まれるイソパ
ラフィン系炭化水素に可溶なポリマーは、印字後インク
中の溶媒によって一旦溶解して着色剤をその内部に捕捉
する。次いで溶媒が乾燥して流動性を失い、着色剤をそ
の内部に固定させることにより、記録材料内部の着色剤
分布を均一化することが可能であり、濃度・精細性を向
上させ、また着色剤の記録材料への定着性を向上させる
効果を有している。しかしながら、印字に使用されるイ
ンクの種類、例えばライトシアン、ライトマゼンタとい
った低濃度インクを使用した場合にはインク溶剤の吸収
性が劣ったり、インク溶剤の保持力が劣るため、経時で
印字部分の周囲からインク溶剤が滲み出してくるおそれ
があった。As a recording material used for ink-jet recording using a non-aqueous ink which has solved such a problem, Japanese Patent Application Laid-Open No. Hei 10-250218 includes a polymer which is soluble in an isoparaffinic hydrocarbon on a coating layer. A recording material having both high definition of a recorded image and high fixability of a coloring agent is disclosed. The polymer soluble in the isoparaffinic hydrocarbon contained in the coating layer is once dissolved by the solvent in the ink after printing, and captures the colorant therein. Then, the solvent is dried and loses fluidity, and the colorant is fixed inside the colorant, whereby the colorant distribution inside the recording material can be made uniform, and the density and definition can be improved. Has the effect of improving the fixability to the recording material. However, when low-concentration inks such as light cyan and light magenta are used for printing, for example, the ink solvent absorbs poorly or the ink solvent retains poorly. Solvent may ooze out of the ink.

【０００９】[0009]

【発明が解決しようとする課題】本発明の課題は、非水
系インクを用いたインクジェット記録方式を利用したプ
リンターやプロッターに使用される非水系インク用イン
クジェット被記録材料において、非水系インクのインク
吸収性および定着性に優れ、インクの裏抜けや経時によ
る印字部分の周囲からインク溶剤の滲み出し（ブリード
性）が防止された非水系インク用インクジェット被記録
材料を提供することである。SUMMARY OF THE INVENTION It is an object of the present invention to provide an ink-jet recording material for a non-aqueous ink used in a printer or a plotter utilizing an ink-jet recording method using a non-aqueous ink. An object of the present invention is to provide an ink jet recording material for a non-aqueous ink, which is excellent in the properties and fixability, and prevents the bleeding (bleeding property) of the ink solvent from around the printed portion due to strikethrough or aging of the ink.

【００１０】[0010]

【課題を解決するための手段】本発明の課題は以下に述
べる手段によって解決される。The object of the present invention is solved by the following means.

【００１１】すなわち、支持体上に少なくとも顔料を含
有するインク吸収層を設け、該インク吸収層上に石油系
高沸点溶剤により溶解又は膨潤するポリマーを塗工また
は含浸させてなる非水系インク用インクジェット被記録
材料において、該顔料が硫酸バリウムであることによっ
て非水系インクのインク溶剤の吸収性および定着性に優
れた非水系インク用インクジェット被記録材料を提供す
ることができる。That is, an ink-jet ink for a non-aqueous ink comprising an ink-absorbing layer containing at least a pigment provided on a support, and a polymer that dissolves or swells with a petroleum-based high boiling point solvent is coated or impregnated on the ink-absorbing layer. In the recording material, when the pigment is barium sulfate, it is possible to provide an ink jet recording material for a non-aqueous ink which is excellent in absorptivity and fixability of an ink solvent of the non-aqueous ink.

【００１２】また、該インク吸収層がカレンダー処理法
にて表面平滑化処理して、７５度鏡面光沢度が２０％以
上としたものであることで、光沢感を有する非水系イン
ク用インクジェット被記録材料を提供することができ
る。In addition, since the surface of the ink absorbing layer is smoothed by a calendering method so that the 75 ° specular glossiness is 20% or more, the inkjet recording for non-aqueous ink having a glossy feeling. Material can be provided.

【００１３】また、該インク吸収層がキャスト処理法に
て表面平滑化処理したものであることにより、より光沢
感の高い非水系インク用インクジェット被記録材料を提
供することができる。Further, since the surface of the ink absorbing layer is subjected to a surface smoothing treatment by a casting treatment method, an ink jet recording material for a non-aqueous ink having a higher glossiness can be provided.

【００１４】更に、インク吸収層をキャスト処理法にて
表面平滑化処理する際には、一般紙、コーテッド紙、不
織布、布帛等のごとく透気性がある支持体を用いること
で、光沢感の高い非水系インク用インクジェット被記録
材料を提供することができる。Further, when the ink absorbing layer is subjected to a surface smoothing treatment by a casting treatment method, a high glossiness can be obtained by using an air-permeable support such as a general paper, a coated paper, a nonwoven fabric, and a cloth. An inkjet recording material for a non-aqueous ink can be provided.

【００１５】[0015]

【発明の実施の形態】以下に好ましい実施の形態を挙
げ、本発明を更に詳細に説明する。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in more detail with reference to preferred embodiments.

【００１６】本発明の非水系インク用インクジェット被
記録材料は、支持体上に少なくとも顔料を含有するイン
ク吸収層を設け、該インク吸収層上に石油系高沸点溶剤
により溶解又は膨潤するポリマー（以下、溶剤可溶性ポ
リマーと記述）を塗工または含浸させてなる非水系イン
ク用インクジェット被記録材料において、該顔料が硫酸
バリウムであることを特徴とする。The ink-jet recording material for a non-aqueous ink of the present invention is provided with an ink-absorbing layer containing at least a pigment on a support, and a polymer which dissolves or swells with a petroleum-based high-boiling solvent on the ink-absorbing layer. , A solvent-soluble polymer) coated or impregnated with a non-aqueous ink, characterized in that the pigment is barium sulfate.

【００１７】硫酸バリウムを顔料として使用することに
より、インク吸収性に優れ、経時による印字部分の周囲
からインク溶剤が滲み出してくることを防止することが
できる。By using barium sulfate as a pigment, the ink absorbability is excellent, and it is possible to prevent the ink solvent from seeping out from the periphery of the printed portion with the passage of time.

【００１８】硫酸バリウムがなぜ非水系インクのインク
溶剤の滲み出し（ブリード性）を防止するのかは定かで
はないが、硫酸バリウムが非水系インクの溶媒に対し極
めて親和力が強く、浸透してきたこれら溶媒を顔料表面
に吸着、保持する能力が通常の水性インクジェット被記
録材料に使用されている顔料であるシリカ等より優れて
いるのではないかと考えられる。It is not clear why barium sulfate prevents the bleeding of the ink solvent of the non-aqueous ink, but barium sulfate has a very strong affinity for the solvent of the non-aqueous ink, It is considered that the ability of adsorbing and holding the pigment on the surface of the pigment is superior to silica or the like which is a pigment used in a general aqueous ink jet recording material.

【００１９】かかる顔料のうち、硫酸バリウムは種々の
製造方法により得られるが、一例としては、中性結晶硫
酸ナトリウム５〜２０％水溶液と中性結晶塩化バリウム
５〜２０％水溶液で片方の液を攪拌しながらもう一方の
液を加え、反応させることにより硫酸バリウムを生成さ
せる方法がある。この方法で得られた硫酸バリウムの硫
化物の含有量は０．０１ｐｐｍ以下である。この硫酸バ
リウムは硫化物の不純物が少ない為、変色が少なく、且
つ耐候性に優れた硫酸バリウムである。Among these pigments, barium sulfate can be obtained by various production methods. For example, one solution is prepared by using a 5 to 20% aqueous solution of neutral crystalline sodium sulfate and a 5 to 20% aqueous solution of neutral crystalline barium chloride. There is a method in which the other liquid is added with stirring and reacted to generate barium sulfate. The sulfide content of barium sulfate obtained by this method is 0.01 ppm or less. This barium sulfate is a barium sulfate which has less discoloration and less discoloration and has excellent weather resistance.

【００２０】また、硫酸バリウムの平均粒子径が０．３
〜３μｍの範囲、より好ましくは０．４〜１．５μｍの
範囲のものが好ましい。この様な範囲の粒子径を有する
硫酸バリウムを使用することで、インク溶剤の吸収性を
満足することができる。平均粒子径が０．３μｍより小
さいと、塗工液の粘度が上昇したり、基材との接着性が
悪くなるため好ましくない。また、平均粒子径が３μｍ
より大きいと表面の平滑性が劣りインクの吸収性にムラ
が生じたり、光沢が低下するため好ましくない。The average particle diameter of barium sulfate is 0.3
It is preferably in the range of 3 to 3 m, more preferably in the range of 0.4 to 1.5 m. By using barium sulfate having a particle size in such a range, the ink solvent absorbency can be satisfied. If the average particle size is smaller than 0.3 μm, the viscosity of the coating liquid increases and the adhesiveness to the base material deteriorates, which is not preferable. The average particle diameter is 3 μm
If it is larger, the surface smoothness is inferior, the ink absorbency becomes uneven, and the gloss decreases, which is not preferable.

【００２１】硫酸バリウムを結着させるバインダーとし
ては、例えば、でんぷんおよびその変性物、ゼラチンお
よびそれらの変性物、カゼイン、プルラン、アラビアゴ
ム、カラヤゴム、アルブミン等の天然高分子樹脂または
これらの誘導体、ポリビニルアルコールまたはそのカチ
オン変性物やシラノール変性物、ＳＢＲラテックス、Ｎ
ＢＲラテックス、メチルメタクリレート−ブタジエン共
重合体やエチレン−酢酸ビニル共重合体等のラテックス
類、ポリアクリルアミド、ポリビニルピロリドン等のビ
ニルポリマー、ポリエチレンイミン、ポリプロピレング
リコール、ポリエチレングリコール、無水マレイン酸の
重合体またはその共重合体等を挙げることができるが、
これらを単独または二種以上を組み合わせて使用しても
良い。Examples of the binder for binding barium sulfate include starch and modified products thereof, gelatin and modified products thereof, natural polymer resins such as casein, pullulan, gum arabic, gum karaya, albumin, and derivatives thereof, and polyvinyl resins. Alcohol or its cation modification or silanol modification, SBR latex, N
Latexes such as BR latex, methyl methacrylate-butadiene copolymer and ethylene-vinyl acetate copolymer, polyacrylamide, vinyl polymers such as polyvinylpyrrolidone, polyethyleneimine, polypropylene glycol, polyethylene glycol, and maleic anhydride polymer or the like. Copolymers and the like can be mentioned,
These may be used alone or in combination of two or more.

【００２２】インク吸収層を形成するための塗工液に
は、顔料およびバインダーに加え、必要に応じて、界面
活性剤、着色染料、着色顔料、カチオン性のインク染料
定着剤、紫外線吸収剤、酸化防止剤、顔料の分散剤、消
泡剤、レベリング剤、防腐剤、蛍光増白剤、粘度安定
剤、ｐＨ調節剤等の公知の各種添加剤を添加することも
できる。In the coating liquid for forming the ink absorbing layer, a surfactant, a coloring dye, a coloring pigment, a cationic ink dye fixing agent, an ultraviolet absorbing agent, Known various additives such as an antioxidant, a pigment dispersant, an antifoaming agent, a leveling agent, a preservative, an optical brightener, a viscosity stabilizer, and a pH adjuster can also be added.

【００２３】インク吸収層の支持体への塗工量として
は、インクの溶剤吸収性および表面の平滑性を付与する
ために５〜５０ｇ／ｍ²、より好ましくは１０〜３０ｇ
／ｍ²の範囲が好ましい。The amount of the ink-absorbing layer applied to the support is preferably 5 to 50 g / m ² , more preferably 10 to 30 g, in order to impart the solvent absorbency and the smoothness of the surface of the ink.
/ M ² is preferred.

【００２４】インク吸収層は塗工装置を用いて塗布、乾
燥することにより形成される。塗工液の塗工方法として
は、例えば、スライドホッパー方式、カーテン方式、エ
クストルージョン方式、エアナイフ方式、ロールコーテ
ィング方式、ロッドバーコーティング方式等の通常用い
られている塗工方法が用いられる。The ink absorbing layer is formed by applying and drying using a coating apparatus. As a method for applying the coating liquid, for example, a commonly used coating method such as a slide hopper method, a curtain method, an extrusion method, an air knife method, a roll coating method, and a rod bar coating method is used.

【００２５】本発明におけるインク吸収層は、スーパー
カレンダー等の加工装置を用い圧力をかけたロール間を
通すことで、表面平滑化処理することができる。７５度
鏡面光沢度を２０％以上とすることにより、写真調ある
いはアート紙、コート紙様の光沢感となるため特に好ま
しい。The ink absorbing layer in the present invention can be subjected to a surface smoothing treatment by passing between ink rolls using a processing device such as a super calender. It is particularly preferable to set the 75-degree specular glossiness to 20% or more because the glossiness becomes like a photographic or art paper or a coated paper.

【００２６】本発明におけるインク吸収層は、塗工層が
湿潤状態にある間、もしくは一旦乾燥後再湿潤してか
ら、鏡面を有する加熱ロール面に圧着し、その後乾燥、
離型することによりその鏡面を写し取ることによって得
られる、いわゆるキャスト処理法により表面平滑化処理
することも好ましい。The ink-absorbing layer in the present invention is pressed against a mirror-finished heating roll surface while the coating layer is in a wet state, or after the coating layer is once dried and re-wet, and then dried.
It is also preferable to carry out a surface smoothing treatment by a so-called cast treatment method, which is obtained by copying the mirror surface by releasing the mold.

【００２７】本発明における溶剤可溶性ポリマーは、印
字後インク中の溶媒によって一旦溶解して着色剤をその
内部に捕捉し、次いで溶媒が消失して流動性を失って着
色剤をその内部に固定することにより、着色剤の記録媒
体への定着性を向上させる効果を有している。The solvent-soluble polymer in the present invention is once dissolved by the solvent in the ink after printing to capture the colorant therein, and then the solvent disappears and loses fluidity to fix the colorant therein. This has the effect of improving the fixability of the colorant to the recording medium.

【００２８】このような溶剤可溶性ポリマーとは、室温
下、石油系高沸点溶剤と任意の割合で溶解もしくは膨潤
するものをいい、この条件に当てはまるさまざまのポリ
マーを用いることができる。一例をあげると、ポリブタ
ジエン・ポリイソプレンなどのポリ(１，３−ジエン)、
ポリアルキル(Ｃ４以上)ビニルエーテル、ポリアルキル
(Ｃ４以上)カルボン酸ビニル、ポリアルキル(Ｃ４以上)
(メタ)アクリレート、ポリアルキル(Ｃ６以上)(メタ)ア
クリルアミド、ポリオキシアルキレン(Ｃ４以上)、ポリ
ジメチルシロキサン、石油樹脂(Ｃ５系、Ｃ９系)、ノボ
ラック樹脂、グッタペルカなどのポリマー、およびこれ
らのポリマーを構成するモノマーから構成されるコポリ
マーを、本発明における溶剤可溶性ポリマーとして使用
することができる。Such a solvent-soluble polymer is one that dissolves or swells at an arbitrary ratio with a petroleum-based high-boiling solvent at room temperature, and various polymers satisfying these conditions can be used. For example, poly (1,3-diene) such as polybutadiene / polyisoprene,
Polyalkyl (C4 or more) vinyl ether, polyalkyl
(C4 or more) vinyl carboxylate, polyalkyl (C4 or more)
(Meth) acrylate, polyalkyl (C6 or more) (meth) acrylamide, polyoxyalkylene (C4 or more), polydimethylsiloxane, petroleum resin (C5 type, C9 type), novolak resin, polymer such as gutta percha, and polymers thereof Can be used as the solvent-soluble polymer in the present invention.

【００２９】これらの溶剤可溶性ポリマーには、石油系
高沸点溶剤に対する溶解性が失われない範囲で各種の変
性を施しても良い。一例をあげると、低級アルキルビニ
ルエーテル、低級アルキルカルボン酸ビニル、低級アル
キル(メタ)アクリレート、(メタ)アクリル酸、テトラヒ
ドロフルフリル(メタ)アクリレート、アルキルオキシエ
チル(メタ)アクリレート、ジアルキルアミノエチル(メ
タ)アクリレート、低級アルキル(メタ)アクリルアミ
ド、(メタ)アクリルアミド、低級(ジ)アルキル(メタ)ア
クリルアミド、ジアセトン(メタ)アクリルアミド、２−
(メタ)アクリルアミド−２−メチルプロパンスルホン
酸、ジアルキルアミノプロピル(メタ)アクリルアミド、
スチレンなどのモノマーを、上記のポリマーを構成する
モノマーと共重合することにより、本発明の石油系高沸
点溶剤に可溶なポリマーを変性することができる。These solvent-soluble polymers may be subjected to various modifications as long as the solubility in petroleum-based high-boiling solvents is not lost. For example, lower alkyl vinyl ether, lower alkyl vinyl carboxylate, lower alkyl (meth) acrylate, (meth) acrylic acid, tetrahydrofurfuryl (meth) acrylate, alkyloxyethyl (meth) acrylate, dialkylaminoethyl (meth) Acrylate, lower alkyl (meth) acrylamide, (meth) acrylamide, lower (di) alkyl (meth) acrylamide, diacetone (meth) acrylamide, 2-
(Meth) acrylamide-2-methylpropanesulfonic acid, dialkylaminopropyl (meth) acrylamide,
By copolymerizing a monomer such as styrene with the monomer constituting the polymer, the polymer soluble in the petroleum-based high boiling point solvent of the present invention can be modified.

【００３０】溶剤可溶性ポリマーをインク吸収層上に含
有せしめる方法としては、適切な有機溶剤に溶解して塗
工することにより含有させることが好ましい。これは、
該溶剤可溶性ポリマーを、記録材料の表面部分に集中的
に存在させて、該溶剤可溶性ポリマーを含有せしめた効
果をより好ましく発揮させることができるからである。As a method for incorporating the solvent-soluble polymer into the ink absorbing layer, it is preferable to dissolve the polymer in an appropriate organic solvent and apply it. this is,
This is because the solvent-soluble polymer can be concentrated on the surface portion of the recording material to more preferably exert the effect of including the solvent-soluble polymer.

【００３１】インク吸収層上に含有せしめる溶剤可溶性
ポリマーの塗工量は、０．３〜１５ｇ／ｍ²とすること
が好ましく、３〜１０ｇ／ｍ²とすることが特に好まし
い。塗工量がこの範囲より少ない場合には着色剤を強く
固定することができず、着色剤の定着性が悪くなり、該
塗工量がこの範囲よりも多い場合には、インクの吸収速
度が不十分になって、ムラが画像に生じるようになり好
ましくない。The coating amount of the solvent-soluble polymer allowed to contain on the ink absorbing layer is preferably in a 0.3~15g / m ^2, and particularly preferably to 3 to 10 g / m ^2. If the coating amount is less than this range, the colorant cannot be firmly fixed, and the fixability of the colorant will be poor.If the coating amount is larger than this range, the ink absorption speed will decrease. Insufficiently, unevenness occurs in the image, which is not preferable.

【００３２】この溶剤可溶性ポリマーの塗工方法として
は、ロールコーター、エアナイフコーター、ブレードコ
ーター、ロッドコーター、バーコーター、グラビアコー
ター、カーテンコーターなどの通常用いられている塗工
方式が挙げられるが、本発明ではこれらに限定されるも
のではない。Examples of the method of applying the solvent-soluble polymer include commonly used coating methods such as a roll coater, an air knife coater, a blade coater, a rod coater, a bar coater, a gravure coater, and a curtain coater. The invention is not limited to these.

【００３３】本発明で使用される支持体としては、透
明、不透明のいずれの基材も使用できる。例えば、ポリ
エステル、ポリスルホン、ポリ塩化ビニル、ポリカーボ
ネート、ポリスチレン、ポリメチルメタクリレート、酢
酸セルロース、ポリエチレン、ポリプロピレンなどの透
明フィルム、あるいは、これらに白色顔料を充填した
り、あるいは微細な発泡により白色化したフィルムや合
成紙、更に一般紙、コーテッド紙、バライタ紙、樹脂被
覆紙等が主に用いられる。更にガラス、アルミニウム
箔、蒸着紙、蒸着フィルム、布帛などインク吸収層を設
けることができる支持体であれば特に限定されるもので
はないが、一般紙、コーテッド紙、布帛等の透気性のあ
るものが好ましい。As the support used in the present invention, any of transparent and opaque substrates can be used. For example, polyester, polysulfone, polyvinyl chloride, polycarbonate, polystyrene, polymethyl methacrylate, cellulose acetate, polyethylene, transparent films such as polypropylene, or filled with a white pigment, or a film whitened by fine foaming or Synthetic paper, general paper, coated paper, baryta paper, resin-coated paper and the like are mainly used. Further, the support is not particularly limited as long as it can be provided with an ink-absorbing layer such as glass, aluminum foil, vapor-deposited paper, vapor-deposited film, and cloth, but is generally air-permeable such as general paper, coated paper, and cloth. Is preferred.

【００３４】特に、キャスト処理法にて表面平滑化処理
する場合には、湿潤状態にある塗工面をキャストドラム
に密着させて乾燥させる為、水分を支持体のウラ面から
蒸散させる必要がある。透気性のない支持体を用いた場
合、水分がウラ面へ蒸散できずに塗工面とキャストドラ
ム面との間で気泡が発生し、その部分は鏡面が形成され
ない状態で斑点となってしまう為、支持体は通気性のあ
るものが好ましい。In particular, when the surface is smoothed by a casting method, it is necessary to evaporate moisture from the back surface of the support in order to dry the coated surface in a wet state by bringing it into close contact with the cast drum. If a non-permeable support is used, water cannot evaporate to the back surface and air bubbles are generated between the coating surface and the cast drum surface, and that portion becomes spots without a mirror surface formed The support is preferably air-permeable.

【００３５】支持体の透気性の尺度として用いる指標に
透気度があるが、キャスト処理法にて表面平滑化処理す
る際には、「ＪＩＳ Ｐ ８１１７」による透気度の値
が１０００秒以下であることが好ましい。より好ましく
５００秒以下である。透気度が１０００秒より大きい場
合には、塗工面とキャストドラム面との間に気泡が発生
しやすくなるため好ましくない。An index used as a measure of the air permeability of the support is air permeability. When the surface is smoothed by a casting method, the air permeability value according to "JIS P 8117" is 1000 seconds or less. It is preferred that It is more preferably 500 seconds or less. If the air permeability is more than 1000 seconds, air bubbles are easily generated between the coating surface and the cast drum surface, which is not preferable.

【００３６】本発明における支持体には、接着性向上等
の目的でアンカー層を設けてもよい。アンカー層にはゼ
ラチン等の親水性バインダー、ポリビニルブチラール等
の溶剤可溶性バインダー、ラテックス、硬化剤、顔料、
界面活性剤等を適宜組み合わせて含有させることができ
る。The support in the present invention may be provided with an anchor layer for the purpose of improving adhesiveness and the like. The anchor layer is a hydrophilic binder such as gelatin, a solvent-soluble binder such as polyvinyl butyral, a latex, a curing agent, a pigment,
Surfactants and the like can be appropriately combined and contained.

【００３７】本発明における支持体には、帯電防止性、
搬送性、カール防止性、筆記性、糊付け性等のために、
各種のバックコート層を塗設することができる。バック
コート層には、無機帯電防止剤、有機帯電防止剤、親水
性バインダー、ラテックス、硬化剤、顔料、滑剤、界面
活性剤等を適宜組み合わせて含有させることができる。The support in the present invention has an antistatic property,
For transportability, curl prevention, writing, gluing, etc.
Various back coat layers can be applied. In the back coat layer, an inorganic antistatic agent, an organic antistatic agent, a hydrophilic binder, a latex, a curing agent, a pigment, a lubricant, a surfactant and the like can be appropriately combined and contained.

【００３８】本発明における非水系インクには、非水系
溶剤中に着色剤を溶解または分散させたインクが用いら
れる。As the non-aqueous ink in the present invention, an ink in which a coloring agent is dissolved or dispersed in a non-aqueous solvent is used.

【００３９】この非水系溶剤としては、インクジェット
記録装置のインク吐出ヘッドの特性に適合するように、
あるいは安全性の観点から種々な溶剤が選択され、場合
によっては複数種の溶剤を混合して用いる場合もある。The non-aqueous solvent may be selected so as to conform to the characteristics of the ink ejection head of the ink jet recording apparatus.
Alternatively, various solvents are selected from the viewpoint of safety, and in some cases, a mixture of plural kinds of solvents may be used.

【００４０】このような溶剤の代表的な例を以下に挙げ
れば、例えば、ペガゾール（モービル石油株式会社
製）、シェルＳＢＲ、シェルゾール（シェル石油化学株
式会社製）などの石油ナフサ系溶剤類、ハイソゾール
（日本石油株式会社製）などの芳香族系石油溶剤、ソル
トール（フィリップス石油株式会社製）、エクソゾー
ル、アイソパー（エクソン化学株式会社製）、ＩＰソル
ベント（出光石油化学株式会社製）などの脂肪族系石油
溶剤、インクソルベント（三菱石油株式会社製）などの
ナフテン系石油溶剤などを挙げることができる。Representative examples of such solvents include the following: petroleum naphtha-based solvents such as pegazole (manufactured by Mobil Petroleum Co., Ltd.), Shell SBR, and Shell Sol (manufactured by Shell Petrochemical Co., Ltd.); Aromatic petroleum solvents such as Hizosol (Nippon Oil Co., Ltd.), aliphatics such as Solutol (Philips Oil Co., Ltd.), Exoxol, Isopar (Exxon Chemical Co., Ltd.), IP Solvent (Idemitsu Petrochemical Co., Ltd.) And a naphthenic petroleum solvent such as an ink solvent (manufactured by Mitsubishi Petroleum Corporation).

【００４１】非水系インクに用いられる着色剤として、
例えば、ナフトール染料、アゾ染料、金属錯塩染料、ア
ントラキノン染料、キノイミン染料、インジゴ染料、シ
アニン染料、キノリン染料、ニトロ染料、ニトロソ染
料、ベンゾキノン染料、カーボニウム染料、ナフトキノ
ン染料、ナフタルイミド染料、フタロシアニン染料、ペ
リニン染料などの油溶性染料を溶解または分散したもの
や、ファーネストブラック、ランプブラック、アセチレ
ンブラック、チャンネルブラック等のカーボンブラック
類、またはオルトニトロアニリンブラック等の有機顔
料、トルイジンレッド、パーマネントカーミンＦＢ、フ
ァーストイエロＡＡＡ、ジスアゾオレンジＰＭＰ、レー
キレッドＣ、ブリリアントカーミン６Ｂ、フタロシアニ
ンブルー、キナクリドンレッド、ジオキサンバイオレッ
ト、ピクトリアピュアブルー、アルカリブルートナー、
ファーストイエロー１０Ｇ、オルトニトロアニリンオレ
ンジ、トルイジンレッド、バリウムレッド２Ｂ、カルシ
ウムレッド２Ｂ、ピグメントスカーレッド３Ｂレーキ、
アンソシン３Ｂレーキ、ローダミン６Ｇレーキ、メチル
バイオレッドレーキ、ベーシックブルー５Ｂレーキ、フ
ァーストスカイブルー、アルカリブルーＲトナー、紺
青、群青、レフレックスブルー２Ｇ、ブリリアントグリ
ーンレーキ、フタロシアニングリーンＧ、酸化鉄粉、亜
鉛華、炭酸カルシウム、クレー、硫酸バリウム、アルミ
ナホワイト、アルミニウム粉、昼光けい光顔料、パール
顔料などが挙げられ、その他これらを表面処理した加工
顔料等が使用できるが、これらに限定されるものではな
い。As a coloring agent used in the non-aqueous ink,
For example, naphthol dye, azo dye, metal complex dye, anthraquinone dye, quinoimine dye, indigo dye, cyanine dye, quinoline dye, nitro dye, nitroso dye, benzoquinone dye, carbonium dye, naphthoquinone dye, naphthalimide dye, phthalocyanine dye, perinine Dissolving or dispersing oil-soluble dyes such as dyes, carbon blacks such as furnace black, lamp black, acetylene black, channel black, or organic pigments such as ortho nitroaniline black, toluidine red, permanent carmine FB, first Yellow AAA, Disazo Orange PMP, Lake Red C, Brilliant Carmine 6B, Phthalocyanine Blue, Quinacridone Red, Dioxane Violet, Pictoria Pure Lou, alkali blue toner,
Fast Yellow 10G, orthonitroaniline orange, toluidine red, barium red 2B, calcium red 2B, pigment scar red 3B lake,
Ansosine 3B Lake, Rhodamine 6G Lake, Methyl Bio Red Lake, Basic Blue 5B Lake, Fast Sky Blue, Alkaline Blue R Toner, Navy Blue, Ultramarine, Reflex Blue 2G, Brilliant Green Lake, Phthalocyanine Green G, Iron Oxide Powder, Zinc Flower , Calcium carbonate, clay, barium sulfate, alumina white, aluminum powder, daylight fluorescent pigments, pearl pigments and the like, and other processed pigments which have been surface-treated can be used, but are not limited thereto. .

【００４２】また、非水系インクには、その保存安定性
や印字後の耐擦過性などを向上させる目的で、例えば、
ポリアクリル酸エステル、アマニ油変性アルキッド樹
脂、ポリスチレン、ロジン系樹脂、テルペンフェノール
系樹脂、アルキルフェノール変性キシレン樹脂などの極
性樹脂を添加したり、金属封鎖剤、表面張力調整剤、界
面活性剤、粘度調整剤、消泡剤、抑泡剤、離型剤、発泡
剤、浸透剤、蛍光増白剤、紫外線吸収剤、防腐剤、耐水
化剤、レオロジーモデファイヤーおよび酸化防止剤など
の添加剤を適宜組み合わせ含有することもできる。For the purpose of improving the storage stability and scratch resistance after printing, non-aqueous inks include, for example,
Add polar resins such as polyacrylic acid ester, linseed oil-modified alkyd resin, polystyrene, rosin-based resin, terpene phenol-based resin, alkylphenol-modified xylene resin, sequestering agent, surface tension regulator, surfactant, and viscosity control Agents, defoamers, defoamers, mold release agents, foaming agents, penetrants, optical brighteners, ultraviolet absorbers, preservatives, water-resistant agents, rheology modifiers and antioxidants It can also be contained.

【００４３】[0043]

【実施例】以下、実施例により本発明を詳しく説明する
が、本発明の内容は実施例に限定されるものではない。
尚、実施例において示す「部」は、特に明記しない限り
重量部を示す。EXAMPLES The present invention will be described below in detail with reference to examples, but the contents of the present invention are not limited to the examples.
In the examples, "parts" indicates parts by weight unless otherwise specified.

【００４４】（支持体の作製）濾水度４５０ｍｌＣＳＦ
のＬＢＫＰ１００部からなる木材パルプに、軽質炭酸カ
ルシウム／重質炭酸カルシウム／タルクの比率が３０／
３５／３５の顔料５部、市販アルキルケテンダイマー
０．１部、市販カチオン性ポリアクリルアミド０．０３
部、市販カチオン化澱粉１．０部、硫酸バンド０．５部
を調製後、長網抄紙機をもちいて坪量９０ｇ／ｍ²で抄
造して支持体を得た。得られた支持体の透気度は２０秒
であった。(Preparation of support) Freeness 450 ml CSF
Wood pulp consisting of 100 parts of LBKP, the ratio of light calcium carbonate / heavy calcium carbonate / talc is 30 /
5 parts of 35/35 pigment, 0.1 part of commercially available alkyl ketene dimer, 0.03 of commercially available cationic polyacrylamide
After preparing 1.0 part of a commercially available cationized starch and 0.5 part of a sulfuric acid band, the support was obtained using a Fourdrinier paper machine with a basis weight of 90 g / m ² . The air permeability of the obtained support was 20 seconds.

【００４５】実施例１ （インク吸収層Ａの作製）平均粒径０．８μｍの硫酸バ
リウム１００重量部、ゼラチン８重量部、硫酸クロム
０．２４重量部を順次配合し、塗工液を調製した。この
塗工液を上で作製した支持体上にエアナイフコーターで
２０ｇ／ｍ²塗布し、「インク吸収層Ａ」を作製した。Example 1 (Preparation of Ink Absorbing Layer A) 100 parts by weight of barium sulfate having an average particle diameter of 0.8 μm, 8 parts by weight of gelatin, and 0.24 parts by weight of chromium sulfate were sequentially mixed to prepare a coating liquid. . This coating liquid was applied onto the support prepared above with an air knife coater at a rate of 20 g / m ² to prepare “ink absorbing layer A”.

【００４６】（溶剤可溶性ポリマー塗工液の調製及び塗
工）攪拌装置を備えた４つ口フラスコに、溶媒としてキ
シレン１００部を仕込み、窒素を通じながら水浴中で７
０℃まで加熱した。ここに、重合開始剤として２，２′
−アゾビス（２−メチルブチロニトリル）５部を添加
し、４時間かけてメタクリル酸ラウリル５０部＋メタク
リル酸イソボルニル５０部の混合物を滴下し、滴下終了
後さらに７０℃に４時間維持した。この後９０℃まで加
温し、この温度で２時間維持してポリマー溶液を得た。
このポリマー溶液をガラス板上に薄く広げて、８０℃で
乾燥させた後に、この乾燥皮膜をはがして４倍重量のア
イソパーＧ中で攪拌し溶解させた。また、このポリマー
溶液を、 ロータリーエバポレーターを用いていったん
乾固させた後、アイソパーＧに溶解して２０％濃度に調
製して、「溶剤可溶性ポリマー塗工液」を調製した。こ
の塗工液を、「インク吸収層Ａ」上にワイヤーバーを用
いて乾燥塗工量が５ｇ／ｍ²になるように塗工し、実施
例１の非水系インク用インクジェット被記録材料を得
た。(Preparation and Coating of Solvent-Soluble Polymer Coating Liquid) In a four-necked flask equipped with a stirrer, 100 parts of xylene was charged as a solvent, and the mixture was placed in a water bath while passing nitrogen.
Heated to 0 ° C. Here, 2,2 'is used as a polymerization initiator.
5 parts of -azobis (2-methylbutyronitrile) was added, and a mixture of 50 parts of lauryl methacrylate + 50 parts of isobornyl methacrylate was added dropwise over 4 hours. After the completion of the addition, the mixture was maintained at 70 ° C for 4 hours. Thereafter, the mixture was heated to 90 ° C. and maintained at this temperature for 2 hours to obtain a polymer solution.
The polymer solution was spread thinly on a glass plate and dried at 80 ° C., and then the dried film was peeled off and stirred and dissolved in 4-fold weight Isopar G. Further, the polymer solution was evaporated to dryness using a rotary evaporator, and then dissolved in Isopar G to adjust the concentration to 20% to prepare a “solvent-soluble polymer coating solution”. This coating liquid was applied on the “ink-absorbing layer A” using a wire bar so that the dry coating amount was 5 g / m ² , to obtain an ink jet recording material for a non-aqueous ink of Example 1. Was.

【００４７】実施例２ （インク吸収層Ｂの作製）上で作製された「インク吸収
層Ａ」を、線圧１８６２Ｎ／ｃｍでスーパーカレンダー
処理を行い、「インク吸収層Ｂ」を作製した。Example 2 (Preparation of Ink Absorbing Layer B) The above-prepared "Ink Absorbing Layer A" was subjected to a super calendering treatment at a linear pressure of 1862 N / cm to prepare "Ink Absorbing Layer B".

【００４８】実施例１の「インク吸収層Ａ」の代わり
に、「インク吸収層Ｂ」を使用した以外は、実施例１と
同様にして、実施例２の非水系インク用インクジェット
被記録材料を得た。The ink-jet recording material for a non-aqueous ink of Example 2 was prepared in the same manner as in Example 1 except that “ink absorbing layer B” was used instead of “ink absorbing layer A” of Example 1. Obtained.

【００４９】実施例３ （インク吸収層Ｃの作製）平均粒径０．８μｍの硫酸バ
リウム１００重量部、ゼラチン８重量部、硫酸クロム
０．２４重量部を順次配合し、塗工液を調製した。この
塗工液を上で作製した支持体上にエアナイフコーターで
２０ｇ／ｍ²塗布し、表面温度９０℃の鏡面ロールに圧
接して乾燥して、「インク吸収層Ｃ」を作製した。Example 3 (Preparation of Ink Absorbing Layer C) 100 parts by weight of barium sulfate having an average particle diameter of 0.8 μm, 8 parts by weight of gelatin, and 0.24 parts by weight of chromium sulfate were sequentially mixed to prepare a coating liquid. . This coating liquid was applied onto the support prepared above with an air knife coater at a rate of 20 g / m ² , and was pressed against a mirror-like roll having a surface temperature of 90 ° C. and dried to prepare “ink absorbing layer C”.

【００５０】実施例１の「インク吸収層Ａ」の代わり
に、「インク吸収層Ｃ」を使用した以外は、実施例１と
同様にして、実施例３の非水系インク用インクジェット
被記録材料を得た。The ink-jet recording material for non-aqueous ink of Example 3 was prepared in the same manner as in Example 1 except that “ink absorbing layer C” was used instead of “ink absorbing layer A” in Example 1. Obtained.

【００５１】比較例１ （インク吸収層Ｄの作製）実施例１の硫酸バリウムの代
わりに、平均粒径３．３μｍの合成非晶質シリカを使用
した以外は実施例１と同様にして、「インク吸収層Ｄ」
を作製した。Comparative Example 1 (Preparation of Ink Absorbing Layer D) The procedure of Example 1 was repeated, except that barium sulfate of Example 1 was replaced with synthetic amorphous silica having an average particle size of 3.3 μm. Ink absorption layer D "
Was prepared.

【００５２】実施例１の「インク吸収層Ａ」の代わり
に、「インク吸収層Ｄ」を使用した以外は、実施例１と
同様にして、比較例１の非水系インク用インクジェット
被記録材料を得た。A non-aqueous ink-jet recording material for a non-aqueous ink of Comparative Example 1 was prepared in the same manner as in Example 1 except that “ink absorbing layer D” was used instead of “ink absorbing layer A” of Example 1. Obtained.

【００５３】比較例２ 「インク吸収層Ａ」をそのまま用い、比較例２の非水系
インク用インクジェット被記録材料を得た。Comparative Example 2 An ink-jet recording material for a non-aqueous ink of Comparative Example 2 was obtained using “ink absorbing layer A” as it was.

【００５４】比較例３ 「インク吸収層Ｂ」をそのまま用い、比較例３の非水系
インク用インクジェット被記録材料を得た。Comparative Example 3 An ink-jet recording material for a non-aqueous ink of Comparative Example 3 was obtained using “ink absorbing layer B” as it was.

【００５５】比較例４ 「インク吸収層Ｃ」をそのまま用い、比較例４の非水系
インク用インクジェット被記録材料を得た。Comparative Example 4 An ink-jet recording material for a non-aqueous ink of Comparative Example 4 was obtained using “ink absorbing layer C” as it was.

【００５６】比較例５ 「インク吸収層Ｄ」をそのまま用い、比較例５の非水系
インク用インクジェット被記録材料を得た。Comparative Example 5 An ink-jet recording material for a non-aqueous ink of Comparative Example 5 was obtained using “ink absorbing layer D” as it was.

【００５７】以上のようにして作製した実施例１〜３、
比較例１〜５の非水系インク用インクジェット被記録材
料について、インクジェットプリンタ（ＰＪ３６００：
オリンパス光学工業式会社製）を用いて、単色（シア
ン、マゼンタ、イエロー、ブラック）、２色重色（シア
ン＋マゼンタ、マゼンタ＋イエロー、シアン＋イエロ
ー）、３色重色（シアン＋マゼンタ＋イエロー）の正方
形のベタ印字パターンの印字を行い、以下に示すような
方法にて評価を行い、結果を表１に示す。Examples 1 to 3 produced as described above,
With respect to the inkjet recording materials for non-aqueous inks of Comparative Examples 1 to 5, an inkjet printer (PJ3600:
Single color (cyan, magenta, yellow, black), double color (cyan + magenta, magenta + yellow, cyan + yellow), multicolor (cyan + magenta + yellow) ), A square solid print pattern was printed and evaluated by the following methods. The results are shown in Table 1.

【００５８】（評価方法） （光沢度）「光沢度」の評価は、光沢度計（ＧＭ−２６
Ｄ型 株式会社村上色彩技術研究所製）を使用し、未印
字部の７５度鏡面光沢（Ｇs）をＪＩＳ−Ｚ−８７４１
の方法で測定した光沢度を表す。(Evaluation Method) (Glossiness) "Glossiness" was evaluated using a glossmeter (GM-26).
D type, manufactured by Murakami Color Research Laboratory Co., Ltd.), and the 75-degree specular gloss (Gs) of the unprinted portion is JIS-Z-8741.
Represents the glossiness measured by the method described above.

【００５９】（定着性）「定着性」の評価は、ブラック
インクのベタ印字部分の表面を人差し指で片方向に１回
こすり、着色剤が周囲の白紙（未印字）部分に拡がらな
かったもの（定着性良好）を「○」、実用上問題はない
がわずかに着色剤が拡がったものを「△」、着色剤が表
面から脱落したもの（定着性不良）を「×」とした。(Fixing property) The evaluation of "fixing property" was made by rubbing the surface of the solid printed portion of the black ink once with an index finger in one direction, and the colorant did not spread to the surrounding white paper (unprinted) portion. (Good fixability) was evaluated as “○”, practically no problem but slightly spread of the colorant was evaluated as “Δ”, and colorant dropped off from the surface (defective fixability) was evaluated as “x”.

【００６０】（インク吸収性）「インク吸収性」の評価
は、単色、２色重色および３色重色したベタ印字部分の
印字直後のインク乾燥状態を目視で観察、評価を行い、
全くインクが溢れずに印字できたものを「○」、実用上
問題ないが多少インクが溢れ印字ムラが生じたものを
「△」、溢れが生じたものを「×」とした。(Ink Absorption) The ink absorption was evaluated by visually observing and evaluating the ink drying state immediately after printing of the solid printing portion of a single color, two colors and three colors, and three colors.
A sample that could be printed without any overflow of ink was rated as “A”, a sample that caused some ink overflow but caused printing unevenness was rated as “Δ”, and a sample that did overflow did not have “X”.

【００６１】（インク裏抜け）「インク裏抜け」の評価
は、３色重色したベタ印字部分を印字面の裏側から観察
し、インクの原紙側への裏抜け具合を目視で観察、評価
を行い、全くインクの裏抜けが見られなかったものを
「○」、多少インクが裏抜けしたものを「△」、裏抜け
がひどかったものを「×」とした。「○」以上が実用上
良好である。(Ink strikethrough) Evaluation of “ink strikethrough” was performed by observing a solid printed portion of three colors and superimposed colors from the back side of the printing surface, and visually observing the degree of strikethrough of the ink to the base paper side. When no ink strikethrough was observed at all, “○” was assigned to the ink, strikethrough was slightly observed for the ink, and “x” was assigned for severe strikethrough. "O" or more is practically good.

【００６２】（ブリード性）「ブリード性」の評価は、
３色重色したベタ印字部分の２４時間後の印字部分周囲
からのインク溶剤の滲み出しを目視で観察、評価を行
い、全く滲み出しが無いものを「○」、実用上問題ない
がわずかに滲み出しが生じたものを「△」、滲み出しが
はっきりと生じたものを「×」とした。(Bleedability) The evaluation of “bleedability” is as follows.
The bleeding of the ink solvent from around the printed portion 24 hours after the three-color superimposed solid printing portion was visually observed and evaluated. If no bleeding was observed, “も の” indicates that no bleeding was observed. The case where oozing occurred was indicated by “Δ”, and the case where oozing occurred clearly was indicated by “×”.

【００６３】[0063]

【表１】 [Table 1]

【００６４】支持体上に少なくとも顔料を含有するイン
ク吸収層を設け、該インク吸収層上に石油系高沸点溶剤
により溶解又は膨潤するポリマーを塗工または含浸させ
てなる非水系インク用インクジェット被記録材料におい
て、該顔料が硫酸バリウムである実施例１〜３は、イン
ク溶剤の吸収性が良く、経時による印字部分の周囲から
インク溶剤が滲み出し（ブリード性）が防止された、定
着性に優れた非水系インク用インクジェット被記録材料
であった。比較例１、５は硫酸バリウムに換えてシリカ
のインク吸収層であり、インク裏抜けとブリード性が不
良であった。インク吸収層が硫酸バリウムである比較例
２、３、４は溶剤可溶性ポリマー層が無いため、インク
定着性が劣るものであった。Ink-jet recording for non-aqueous inks by providing an ink absorbing layer containing at least a pigment on a support, and coating or impregnating a polymer that dissolves or swells with a petroleum-based high boiling point solvent on the ink absorbing layer. In the materials, Examples 1 to 3 in which the pigment is barium sulfate have good ink solvent absorbency, prevent ink solvent bleeding (bleeding property) from the periphery of a printed portion over time, and have excellent fixability. Was a non-aqueous ink jet recording material. Comparative Examples 1 and 5 were ink absorption layers made of silica instead of barium sulfate, and had poor ink strike-through and bleeding properties. Comparative Examples 2, 3, and 4, in which the ink absorbing layer was barium sulfate, had no ink-soluble polymer layer, and thus had poor ink fixability.

【００６５】[0065]

【発明の効果】本発明により、非水系インクでのブリー
ド性に優れ、且つ定着性、インク吸収性、インク裏抜け
にも優れた非水系インク用インクジェット被記録材料を
提供することができる。According to the present invention, it is possible to provide an ink jet recording material for a non-aqueous ink which is excellent in bleeding property with a non-aqueous ink, and excellent in fixability, ink absorption and ink strike-through.

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 支持体上に少なくとも顔料を含有するイ
ンク吸収層を設け、該インク吸収層上に石油系高沸点溶
剤により溶解又は膨潤するポリマーを塗工または含浸さ
せてなる非水系インク用インクジェット被記録材料にお
いて、該顔料が硫酸バリウムであることを特徴とする非
水系インク用インクジェット被記録材料。1. An ink jet for non-aqueous ink, comprising: providing an ink absorbing layer containing at least a pigment on a support; and coating or impregnating a polymer that dissolves or swells with a petroleum-based high boiling point solvent on the ink absorbing layer. An ink-jet recording material for a non-aqueous ink, wherein the pigment is barium sulfate. 【請求項２】 該インク吸収層がカレンダー処理法にて
表面平滑化処理して、７５度鏡面光沢度が２０％以上と
したものであることを特徴とする請求項１記載の非水系
インク用インクジェット被記録材料。2. The non-aqueous ink according to claim 1, wherein the surface of the ink absorbing layer is subjected to a surface smoothing treatment by a calendering method so that the 75 ° specular glossiness is 20% or more. Ink jet recording material. 【請求項３】 該インク吸収層がキャスト処理法にて表
面平滑化処理したものであることを特徴とする請求項１
記載の非水系インク用インクジェット被記録材料。3. The ink absorbing layer according to claim 1, wherein the surface is smoothed by a casting method.
The inkjet recording material for a non-aqueous ink according to the above. 【請求項４】 該支持体が透気性のある支持体であるこ
とを特徴とする請求項１〜３のいずれか一項記載の非水
系インク用インクジェット被記録材料。4. The non-aqueous ink jet recording material according to claim 1, wherein the support is a gas permeable support.