JP2001159026A - Polypropylene-containing fiber and fiber sheet - Google Patents
Polypropylene-containing fiber and fiber sheetInfo
- Publication number
- JP2001159026A JP2001159026A JP33943299A JP33943299A JP2001159026A JP 2001159026 A JP2001159026 A JP 2001159026A JP 33943299 A JP33943299 A JP 33943299A JP 33943299 A JP33943299 A JP 33943299A JP 2001159026 A JP2001159026 A JP 2001159026A
- Authority
- JP
- Japan
- Prior art keywords
- polypropylene
- fiber
- strength
- mass
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明はポリプロピレン含有
繊維及びこのポリプロピレン含有繊維を含む繊維シート
に関する。より具体的には、電池用セパレータ（繊維シ
ート）を構成する繊維として好適に使用することのでき
るポリプロピレン含有繊維、及び電池用セパレータとし
て好適に使用することのできる、ポリプロピレン含有繊
維を含む繊維シートに関する。The present invention relates to a polypropylene-containing fiber and a fiber sheet containing the polypropylene-containing fiber. More specifically, the present invention relates to a polypropylene-containing fiber that can be suitably used as a fiber constituting a battery separator (fiber sheet) and a fiber sheet containing a polypropylene-containing fiber that can be suitably used as a battery separator. .
【0002】[0002]
【従来の技術】ポリプロピレン繊維は比重が小さくしか
も耐薬品性に優れているため、軽量化や耐薬品性を必要
とする用途に好適に使用することができる。しかしなが
ら、従来のポリプロピレン繊維の引張り強さは高々６．
７ｃＮ／ｄｔｅｘ程度であったため、強度を必要とする
用途に適用するには困難な場合があった。そのため、特
開平５−９８０５号公報には、「Ｑ値（Ｑ：重量平均分
子量／数平均分子量の比）が５未満、沸騰ｎ−ヘプタン
不溶分（ＨＩ；重量％）が９７＜ＨＩ＜１００、アイソ
タクチックペンタッド分率（ＩＰＦ；モル％）が９４＜
ＩＰＦ＜１００である高結晶性ポリプロピレンの延伸糸
であって、破断強度が８ｇ／デニール（＝７．１ｃＮ／
ｄｔｅｘ）を超える強度を有するポリプロピレン繊
維。」が提案されている。このポリプロピレン繊維は確
かに強度の優れるものであったが、実施例に記載されて
いるように、実際に紡糸できるポリプロピレン繊維は繊
度が２．２ｄｔｅｘ（＝２デニール）以上の太いものし
か得ることができなかった。このようにポリプロピレン
繊維が太いと、例えばこのポリプロピレン繊維を使用し
て不織布を製造した場合、少量で均一に分散させること
が困難であるため、強度的にムラのある不織布しか製造
できない、という問題が発生する場合があった。また、
このポリプロピレン繊維を含む不織布を電池用セパレー
タとして使用した場合、ポリプロピレン繊維が太いため
電解液の保持性が悪くなる、という問題を発生する場合
があった。2. Description of the Related Art Polypropylene fibers have a small specific gravity and are excellent in chemical resistance, so that they can be suitably used for applications requiring weight reduction and chemical resistance. However, the tensile strength of conventional polypropylene fibers is at most 6.
Since it was about 7 cN / dtex, it was sometimes difficult to apply to applications requiring strength. For this reason, JP-A-5-9805 discloses that "Q value (Q: ratio of weight average molecular weight / number average molecular weight) is less than 5 and boiling n-heptane insoluble matter (HI; weight%) is 97 <HI <100. , Isotactic pentad fraction (IPF; mol%) is 94 <
A drawn yarn of a highly crystalline polypropylene having an IPF <100, which has a breaking strength of 8 g / denier (= 7.1 cN /
polypropylene fiber having a strength exceeding dtex). Has been proposed. Although this polypropylene fiber certainly had excellent strength, as described in the Examples, the only polypropylene fiber that can be actually spun has a fineness of 2.2 dtex (= 2 denier) or more. could not. As described above, when the polypropylene fiber is thick, for example, when a nonwoven fabric is manufactured using the polypropylene fiber, it is difficult to uniformly disperse the nonwoven fabric in a small amount, so that only a nonwoven fabric having unevenness in strength can be manufactured. Occurred in some cases. Also,
When a nonwoven fabric containing this polypropylene fiber is used as a battery separator, there is a case where a problem arises in that the polypropylene fiber is too thick and the retention of the electrolyte is deteriorated.
【0003】[0003]
【発明が解決しようとする課題】本発明は上記の問題を
解決するためになされたものであり、強度的に優れしか
も細いポリプロピレン含有繊維を提供すること、及びこ
のポリプロピレン含有繊維を含む繊維シートを提供する
ことを目的とする。DISCLOSURE OF THE INVENTION The present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a polypropylene-containing fiber excellent in strength and thin, and a fiber sheet containing the polypropylene-containing fiber. The purpose is to provide.
【0004】[0004]
【課題を解決するための手段】本発明のポリプロピレン
含有繊維は、Ｑ値（Ｑ：重量平均分子量を数平均分子量
で除した値）が５未満で、アイソタクチックペンタッド
分率が９３％以上のポリプロピレン中に、メルトインデ
ックスが１００〜１，５００のポリプロピレンが１〜１
０ｍａｓｓ％（全体の質量に対して）の割合で混在した
ポリプロピレン成分を備えたものである。本発明の発明
者らは鋭意研究の結果、従来と同様にＱ値が５未満で、
アイソタクチックペンタッド分率が９３％以上の高強度
化可能なポリプロピレンに、メルトインデックスが１０
０〜１，５００のポリプロピレンを１〜１０ｍａｓｓ％
（全体の質量に対して）の割合で混在させ、紡糸し、延
伸することによって、優れた強度の発現性を維持又は向
上させると同時に、紡糸性及び延伸性を改良することに
よって、より細いポリプロピレン含有繊維を得ることが
できることを見い出したのである。アイソタクチックペ
ンタッド分率が９３％以上のポリプロピレンは、延伸に
よる結晶配向を助長できる立体規則性に優れるものであ
るが、このようなポリプロピレンに対して、立体規則性
を損なう可能性のあるメルトインデックスが１００〜
１，５００のポリプロピレンを混在させることによっ
て、強度の発現性を維持又は向上させると同時に、より
細いポリプロピレン含有繊維を得ることができたのは驚
くべきことである。本発明のポリプロピレン含有繊維は
前述のポリプロピレン成分のみを備えたものであること
もできるし、前述のポリプロピレン成分とポリオレフィ
ン系樹脂成分とを備えたものであることもできる。本発
明のポリプロピレン含有繊維は引張り強さが７．１ｃＮ
／ｄｔｅｘ以上、かつ繊度が２．２ｄｔｅｘ未満の、強
度的に優れしかも細い繊維であるのが好ましい。The polypropylene-containing fiber of the present invention has a Q value (Q: a value obtained by dividing the weight average molecular weight by the number average molecular weight) of less than 5, and has an isotactic pentad fraction of 93% or more. Of polypropylene having a melt index of 100 to 1,500
It is provided with a polypropylene component mixed at a ratio of 0 mass% (based on the total mass). As a result of intensive studies, the inventors of the present invention have a Q value of less than 5 as in the past,
Polypropylene having an isotactic pentad fraction of 93% or more and capable of increasing strength has a melt index of 10
0 to 1,500 polypropylene of 1 to 10 mass%
By mixing, spinning and stretching at a ratio of (based on the total mass), the expression of excellent strength is maintained or improved, and at the same time, the spinnability and stretchability are improved, resulting in thinner polypropylene. They have found that it is possible to obtain contained fibers. Polypropylene having an isotactic pentad fraction of 93% or more is excellent in stereoregularity that can promote crystal orientation by stretching. However, a melt having a possibility of impairing stereoregularity with respect to such polypropylene is considered. Index is 100 ~
It is surprising that by mixing 1,500 polypropylene, it was possible to maintain or improve the strength development and at the same time obtain finer polypropylene-containing fibers. The polypropylene-containing fiber of the present invention may include only the above-described polypropylene component, or may include the above-described polypropylene component and a polyolefin-based resin component. The polypropylene-containing fiber of the present invention has a tensile strength of 7.1 cN.
It is preferable that the fibers are not less than / dtex and have a fineness of less than 2.2 dtex and are excellent in strength and thin.
【0005】本発明の繊維シートは前述のようなポリプロピ
レン含有繊維を含んでいるため、少量で均一に分散した
強度的にムラのない繊維シートである。また、この繊維
シートを電池用セパレータとして用いた場合には、電解
液の保持性に優れ、しかも電極群製造時に繊維シートが
破断したり、極板のバリが繊維シートを貫通することが
ない。[0005] Since the fiber sheet of the present invention contains the above-mentioned polypropylene-containing fiber, it is a fiber sheet which is uniformly dispersed in a small amount and has no unevenness in strength. In addition, when this fiber sheet is used as a battery separator, the fiber sheet is excellent in retaining the electrolytic solution, and the fiber sheet is not broken at the time of manufacturing the electrode group, and the burr of the electrode plate does not penetrate the fiber sheet.
【0006】[0006]
【発明の実施の形態】本発明のポリプロピレン含有繊維
は強度的に優れるように、Ｑ値（Ｑ：重量平均分子量を
数平均分子量で除した値）が５未満で、アイソタクチッ
クペンタッド分率が９３％以上のポリプロピレン（以
下、「高強度化可能ポリプロピレン」という）を含んで
いる。このＱ値が５未満であると、延伸倍率を高くする
ことができるため高度に結晶配向させることができ、結
果として強度的に優れるポリプロピレン含有繊維とする
ことができる。より好ましいＱ値は４以下である。な
お、「重量平均分子量」及び「数平均分子量」は、溶媒
に１，２，４−トリクロロベンゼンを用い、温度１８０
℃でＧＰＣ法（ゲルパーミエーションクロマトグラフィ
ー）により、ポリスチレン換算分子量として測定した値
をいう。この高強度化可能ポリプロピレンのアイソタク
チックペンタッド分率が９３％以上であると立体規則性
に優れているため、延伸によって結晶配向が助長され、
結果として強度的に優れるポリプロピレン含有繊維とす
ることができる。より好ましいアイソタクチックペンタ
ッド分率は９５％以上である。このアイソタクチックペ
ンタッド分率は、５ｇの高強度化可能ポリプロピレンを
５００ｍｌの沸騰キシレン中に全溶解させ、これらを５
リットルのメタノール中に投入して析出させたものを回
収して乾燥した後、沸騰ｎ−ヘプタンで６時間、ソック
スレー抽出した抽出残部について「マクロモレキュラー
ズ」（Macromolecules，6925(1973)及び8687(1975)）に
準じて測定した値をいう。このようなＱ値及びアイソタ
クチックペンタッド分率を満足する高強度化可能ポリプ
ロピレンは市販されているため容易に入手することがで
きる。BEST MODE FOR CARRYING OUT THE INVENTION The polypropylene-containing fiber of the present invention has a Q value (Q: a value obtained by dividing a weight average molecular weight by a number average molecular weight) of less than 5 and an isotactic pentad fraction so as to be excellent in strength. Contains 93% or more of polypropylene (hereinafter referred to as “high-strength polypropylene”). When the Q value is less than 5, the draw ratio can be increased, so that a high degree of crystal orientation can be achieved. As a result, a polypropylene-containing fiber having excellent strength can be obtained. A more preferable Q value is 4 or less. The “weight average molecular weight” and “number average molecular weight” were determined using 1,2,4-trichlorobenzene as a solvent and a temperature of 180.
It means a value measured as a polystyrene-equivalent molecular weight by a GPC method (gel permeation chromatography) at ° C. When the isotactic pentad fraction of the high-strength polypropylene is 93% or more, it has excellent stereoregularity.
As a result, a polypropylene-containing fiber having excellent strength can be obtained. A more preferred isotactic pentad fraction is 95% or more. The isotactic pentad fraction was obtained by completely dissolving 5 g of the high-strength polypropylene in 500 ml of boiling xylene,
After pouring the precipitate in liter of methanol and collecting and drying the precipitate, it was dried for 6 hours with boiling n-heptane. Soxhlet extraction was carried out for "Macromoleculars" (Macromolecules, 6925 (1973) and 8687 (1975)). The value measured according to)). A polypropylene having a high strength that satisfies such a Q value and an isotactic pentad fraction can be easily obtained because it is commercially available.
【0007】本発明のポリプロピレン含有繊維は、前述のよ
うな高強度化可能ポリプロピレンに対して、メルトイン
デックスが１００〜１，５００のポリプロピレン（以
下、「混在ポリプロピレン」という）が１〜１０ｍａｓ
ｓ％（全体の質量に対して）の割合で混在したものであ
る。このような混在ポリプロピレンが混在していること
によって、強度の発現性を維持又は向上させると同時
に、紡糸性及び延伸性を改良することができ、結果とし
て、強度的に優れる細いポリプロピレン含有繊維とする
ことができる。この混在ポリプロピレンのメルトインデ
ックスが１００未満であると、延伸による強度向上効果
が低くて強度が低下しやすい傾向があり、メルトインデ
ックスが１，５００を越えると、強度が低下しすぎる傾
向があるためで、より好ましくは１５０〜１３００であ
り、更に好ましくは２００〜１０００である。なお、メ
ルトインデックスはＪＩＳ Ｋ ７２１０に規定されて
いる方法に準じて測定した値をいう。また、この混在ポ
リプロピレンの混在量は混在後のポリプロピレン成分全
体の質量に対して１〜１０ｍａｓｓ％である必要があ
る。この混在量が１ｍａｓｓ％未満では紡糸性及び延伸
性の改良が不十分で、細いポリプロピレン含有繊維とす
ることが困難であり、混在量が１０ｍａｓｓ％を越える
と、前述の高強度化可能ポリプロピレンの立体規則性が
阻害されるためか、強度的に低いポリプロピレン含有繊
維しか得ることしかできないためで、より好ましい混在
量は２〜８ｍａｓｓ％である。なお、メルトインデック
スが前記範囲内にあり、総混在量が前記範囲内にある限
り、混在ポリプロピレンは１種類である必要はなく、２
種類以上の混在ポリプロピレンが混在していても良い。[0007] The polypropylene-containing fiber of the present invention has a polypropylene having a melt index of 100 to 1,500 (hereinafter, referred to as "mixed polypropylene") in an amount of 1 to 10mass in comparison with the above-mentioned polypropylene having a high strength.
s% (based on the total mass). By mixing such a mixed polypropylene, the spinnability and stretchability can be improved while maintaining or improving the strength expression, and as a result, a thin polypropylene-containing fiber excellent in strength is obtained. be able to. When the melt index of the mixed polypropylene is less than 100, the strength improving effect by stretching tends to be low, and the strength tends to decrease. When the melt index exceeds 1,500, the strength tends to decrease too much. , More preferably 150 to 1300, still more preferably 200 to 1000. The melt index refers to a value measured according to a method defined in JIS K7210. Further, the mixed amount of the mixed polypropylene needs to be 1 to 10 mass% with respect to the total weight of the mixed polypropylene components. If the content is less than 1 mass%, the spinnability and stretchability are not sufficiently improved, and it is difficult to obtain fine polypropylene-containing fibers. If the content is more than 10 mass%, the above-mentioned solidified polypropylene having high strength can be obtained. A more preferable mixed amount is 2 to 8 mass% because the regularity is impaired or only a polypropylene-containing fiber having a low strength can be obtained. In addition, as long as the melt index is within the above range and the total mixed amount is within the above range, the mixed polypropylene need not be one kind,
More than one type of mixed polypropylene may be mixed.
【0008】本発明のポリプロピレン含有繊維は前述のよう
な高強度化可能ポリプロピレン中に混在ポリプロピレン
が混在したポリプロピレン成分を備えたものであるが、
本発明のポリプロピレン含有繊維はポリプロピレン成分
のみから構成されていても良いし、ポリプロピレン成分
以外にポリオレフィン系樹脂成分を含んでいても良い。
このポリオレフィン系樹脂成分としては、例えば、ポリ
エチレン系樹脂(例えば、低密度ポリエチレン、直鎖状
低密度ポリエチレン、中密度ポリエチレン、高密度ポリ
エチレンなど)、エチレン系共重合体（例えば、エチレ
ン−ビニルアルコール共重合体、エチレン−酢酸ビニル
共重合体、エチレン−アクリル酸共重合体、エチレン−
アクリル酸エステル共重合体、エチレン−メタクリル酸
共重合体、エチレン−メタクリル酸エステル共重合体な
ど）、ポリ４−メチルペンテン−１樹脂、エチレンとプ
ロピレンとブテン−１などのα−オレフィン共重合体な
どを使用できる。このようにポリオレフィン系樹脂成分
も備えている場合、繊維断面形状は、例えば、芯鞘型
（偏芯型を含む）、サイドバイサイド型、海島型、オレ
ンジ型、多重バイメタル型などであることができる。ポ
リプロピレン含有繊維がポリプロピレン成分とポリオレ
フィン系樹脂成分とを備えている場合、その質量比率は
特に限定するものではないが、ポリプロピレン成分の強
度を活かすため、（ポリプロピレン成分）：（ポリオレ
フィン系樹脂成分）＝４０：６０〜９０：１０であるの
が好ましく、（ポリプロピレン成分）：（ポリオレフィ
ン系樹脂成分）＝４５：５５〜８０：２０であるのがよ
り好ましい。[0008] The polypropylene-containing fiber of the present invention is provided with a polypropylene component in which mixed polypropylene is mixed in the above-mentioned high strength polypropylene.
The polypropylene-containing fiber of the present invention may be composed of only a polypropylene component, or may contain a polyolefin-based resin component in addition to the polypropylene component.
Examples of the polyolefin resin component include polyethylene resins (for example, low-density polyethylene, linear low-density polyethylene, medium-density polyethylene, and high-density polyethylene), and ethylene-based copolymers (for example, ethylene-vinyl alcohol copolymer). Polymer, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, ethylene-
Acrylic acid ester copolymer, ethylene-methacrylic acid copolymer, ethylene-methacrylic acid ester copolymer, etc.), poly-4-methylpentene-1 resin, α-olefin copolymer such as ethylene, propylene and butene-1 Etc. can be used. When the polyolefin resin component is also provided, the fiber cross-sectional shape can be, for example, a core-sheath type (including an eccentric type), a side-by-side type, a sea-island type, an orange type, a multiple bimetal type, and the like. When the polypropylene-containing fiber has a polypropylene component and a polyolefin resin component, the mass ratio is not particularly limited. However, in order to utilize the strength of the polypropylene component, (polypropylene component) :( polyolefin resin component) = The ratio is preferably from 40:60 to 90:10, and more preferably (polypropylene component) :( polyolefin resin component) = 45: 55 to 80:20.
【0009】本発明のポリプロピレン含有繊維はポリオレフ
ィン系樹脂成分を含んでいるかいないかにかかわらず、
引張り強さが７．１ｃＮ／ｄｔｅｘ以上、かつ繊度が
２．２ｄｔｅｘ未満の、強く細い繊維であるのが好まし
い。より好ましくは引張り強さが７．１ｃＮ／ｄｔｅｘ
以上、かつ繊度が１．７ｄｔｅｘ以下である。この「引
張り強さ」はＪＩＳ Ｌ １０１５（化学繊維ステープ
ル試験法）に規定された方法により測定した値を意味す
る。また、「繊度」はＪＩＳ Ｌ １０１５（化学繊維
ステープル試験法）の見掛繊度（参考法（振動法））に
規定された方法により測定した値を意味する。[0009] Regardless of whether the polypropylene-containing fiber of the present invention contains a polyolefin resin component,
It is preferable that the fiber is a strong and thin fiber having a tensile strength of 7.1 cN / dtex or more and a fineness of less than 2.2 dtex. More preferably, the tensile strength is 7.1 cN / dtex.
As described above, the fineness is 1.7 dtex or less. This “tensile strength” means a value measured by a method specified in JIS L 1015 (test method for chemical fiber staples). The “fineness” means a value measured by a method specified in the apparent fineness (reference method (vibration method)) of JIS L 1015 (chemical fiber staple test method).
【0010】本発明のポリプロピレン含有繊維はポリオレフ
ィン系樹脂成分を含んでいるかいないかにかかわらず、
その繊維断面形状は円形であっても、非円形（例えば、
楕円状、長円状、Ｔ状、Ｙ状、＋状、中空状、多角形状
など）であっても良い。また、ポリプロピレン含有繊維
はフィラメントであっても良いし、１〜１６０ｍｍ長程
度に切断されたステープルであっても良い。なお、ポリ
プロピレン含有繊維のポリプロピレン成分中に、或いは
ポリオレフィン系樹脂成分も含む場合にはポリプロピレ
ン成分及び／又はポリオレフィン系樹脂成分中に、例え
ば、酸化防止剤、蛍光増白剤、紫外線吸収剤、吸湿剤、
艶消し剤、顔料、難燃剤、安定剤、帯電防止剤、着色
剤、染色剤、導電剤、耐熱剤、親水化剤、脱臭剤、或い
は抗菌剤などの機能性物質を混合し、各種機能を付加し
ても良い。[0010] Regardless of whether the polypropylene-containing fiber of the present invention contains a polyolefin resin component,
Even though the fiber cross section is circular, it is non-circular (for example,
Oval, elliptical, T-shaped, Y-shaped, + -shaped, hollow, polygonal, etc.). The polypropylene-containing fiber may be a filament or a staple cut to a length of about 1 to 160 mm. In addition, when the polypropylene component of the polypropylene-containing fiber or the polyolefin-based resin component is also contained, in the polypropylene component and / or the polyolefin-based resin component, for example, an antioxidant, a fluorescent whitening agent, an ultraviolet absorber, a moisture absorbent ,
Mixing functional materials such as matting agents, pigments, flame retardants, stabilizers, antistatic agents, coloring agents, dyeing agents, conductive agents, heat-resistant agents, hydrophilic agents, deodorants, or antibacterial agents to achieve various functions May be added.
【0011】このような本発明のポリプロピレン含有繊維は
常法の溶融紡糸装置を利用することにより紡糸すること
ができる。例えば、紡糸温度を２３０〜２８０℃程度に
設定して紡糸することができる。このように紡糸した未
延伸糸は１３０〜１６０℃程度の温度で３〜１２倍延伸
して、ポリプロピレン含有繊維を製造することができ
る。なお、このポリプロピレン含有繊維を乾式不織布の
原料として、又は紡績糸として使用する場合には、機械
的に又は熱的に５〜５０個／インチ程度の巻縮を付与す
るのが好ましい。[0011] Such a polypropylene-containing fiber of the present invention can be spun by using a conventional melt spinning apparatus. For example, spinning can be performed at a spinning temperature of about 230 to 280 ° C. The undrawn yarn spun in this way can be drawn 3 to 12 times at a temperature of about 130 to 160 ° C. to produce a polypropylene-containing fiber. When the polypropylene-containing fiber is used as a raw material of a dry nonwoven fabric or as a spun yarn, it is preferable to mechanically or thermally apply a crimp of about 5 to 50 pieces / inch.
【0012】本発明のポリプロピレン含有繊維は強度的に優
れしかも細いものであるため、強度を必要とする用途、
例えば、セメント補強用繊維などとして使用することが
できる。[0012] Since the polypropylene-containing fiber of the present invention is excellent in strength and thin, it can be used for applications requiring strength.
For example, it can be used as a fiber for reinforcing cement.
【0013】本発明の繊維シートは前述のようなポリプロピ
レン含有繊維を含んでいるため、少量でも均一に分散し
た強度的にムラのないものである。また、本発明の繊維
シートを電池用セパレータとして使用した場合には、電
池を製造する際に、極板のバリが繊維シートを突き抜け
たり、繊維シートが切断されにくいため、短絡を生じに
くいものである。この繊維シートとしては、例えば、織
物、編物、不織布、或いはこれらの複合体などがある。
なお、この繊維シートを電池用セパレータとして使用す
る場合には、電解液の保持性に優れるように、不織布を
含んでいるのが好ましい。本発明のポリプロピレン含有
繊維の繊維シート中における質量比率は、繊維シートの
強度向上に寄与できるように、１０ｍａｓｓ％以上含ま
れているのが好ましく、２０ｍａｓｓ％以上含まれてい
るのがより好ましく、３０ｍａｓｓ％以上含まれている
のが更に好ましい。このポリプロピレン含有繊維以外の
繊維としては通常の繊維を使用することができ、例え
ば、ガラス繊維や炭素繊維などの無機繊維、絹、羊毛、
綿、麻などの天然繊維、レーヨン繊維などの再生繊維、
アセテート繊維などの半合成繊維、ポリアミド繊維、ポ
リビニルアルコール繊維、アクリル繊維、ポリエステル
繊維、ポリ塩化ビニル系繊維、ポリ塩化ビニリデン繊
維、ポリウレタン繊維、ポリエチレン繊維、ポリプロピ
レン繊維、ポリメチルペンテン繊維、芳香族ポリアミド
繊維、又は２種類以上の樹脂成分からなり、巻縮発現
性、熱接着性、或いは分割性を有する複合繊維などの合
成繊維を使用できる。[0013] Since the fiber sheet of the present invention contains the above-mentioned polypropylene-containing fiber, it is evenly dispersed even in a small amount and has no unevenness in strength. Further, when the fiber sheet of the present invention is used as a battery separator, when a battery is manufactured, the burr of the electrode plate penetrates the fiber sheet or the fiber sheet is hard to be cut, so that a short circuit is unlikely to occur. is there. Examples of the fiber sheet include a woven fabric, a knitted fabric, a nonwoven fabric, and a composite thereof.
When this fiber sheet is used as a battery separator, it is preferable that the fiber sheet contains a nonwoven fabric so as to have excellent electrolyte solution retention. The mass ratio of the polypropylene-containing fiber of the present invention in the fiber sheet is preferably at least 10 mass%, more preferably at least 20 mass%, and more preferably at least 30 mass%, so as to contribute to the improvement of the strength of the fiber sheet. % Is more preferable. As the fibers other than the polypropylene-containing fibers, ordinary fibers can be used, for example, inorganic fibers such as glass fibers and carbon fibers, silk, wool,
Regenerated fibers such as natural fibers such as cotton and hemp, rayon fibers,
Semi-synthetic fiber such as acetate fiber, polyamide fiber, polyvinyl alcohol fiber, acrylic fiber, polyester fiber, polyvinyl chloride fiber, polyvinylidene chloride fiber, polyurethane fiber, polyethylene fiber, polypropylene fiber, polymethylpentene fiber, aromatic polyamide fiber Alternatively, a synthetic fiber such as a conjugate fiber composed of two or more resin components and having crimping property, heat bonding property, or splitting property can be used.
【0014】本発明の繊維シートを電池用セパレータ用途に
使用する場合には、繊維径が６μｍ以下（より好ましく
は５μｍ以下、更に好ましくは４μｍ以下）の極細繊維
を含んでいるのが好ましい。このような極細繊維を含ん
でいることによって、電解液の保持性を向上させること
ができたり、デンドライト防止性を向上させることがで
きる。なお、極細繊維の断面形状が非円形である場合に
は、断面積が同じ円の直径をその極細繊維の繊維径とみ
なす。このような極細繊維は、例えば、メルトブロー法
や分割可能な分割繊維を分割することによって得ること
ができる。この分割繊維は水流などの流体流、ニードル
或いはカレンダーなどの物理的作用により分割可能であ
るのが好ましく、これらの中でも、流体流で分割可能で
あるのが好ましい。この分割繊維の断面形状としては、
例えば、オレンジ状、多重バイメタル状などがある。こ
の極細繊維を構成する樹脂成分は耐電解液性に優れるよ
うに、ポリオレフィン系樹脂から構成されているのが好
ましく、より具体的には、ポリエチレン（例えば、低密
度ポリエチレン、直鎖状低密度ポリエチレン、中密度ポ
リエチレン、高密度ポリエチレンなど)、エチレン系共
重合体（例えば、エチレン−ビニルアルコール共重合
体、エチレン−酢酸ビニル共重合体、エチレン−アクリ
ル酸共重合体、エチレン−アクリル酸エステル共重合
体、エチレン−メタクリル酸共重合体、エチレン−メタ
クリル酸エステル共重合体など）、ポリ４−メチルペン
テン−１樹脂、エチレンとプロピレンとブテン−１など
のα−オレフィン共重合体、ポリプロピレン、プロピレ
ン系共重合体、ポリブテン、ブテン系共重合体など１種
類以上から構成されているのが好ましい。この極細繊維
は樹脂組成の点において１種類である必要はなく、２種
類以上混在していても良い。また、本発明のポリプロピ
レン含有繊維がポリオレフィン系樹脂成分も備えてお
り、分割可能である場合（例えば、繊維断面形状がオレ
ンジ状、多重バイメタル状の場合）には、本発明のポリ
オレフィン含有繊維に由来する極細繊維を含んでいても
良い。このような極細繊維は電解液の保持性に優れるよ
うに、またデンドライト防止性に優れるように、繊維シ
ート中、５ｍａｓｓ％以上含まれているのが好ましい。When the fiber sheet of the present invention is used for a battery separator, it preferably contains ultrafine fibers having a fiber diameter of 6 μm or less (more preferably 5 μm or less, and still more preferably 4 μm or less). By containing such ultrafine fibers, the retention of the electrolyte can be improved, and the anti-dendritic properties can be improved. When the cross-sectional shape of the microfiber is non-circular, the diameter of a circle having the same cross-sectional area is regarded as the fiber diameter of the microfiber. Such ultrafine fibers can be obtained, for example, by a melt blow method or by splitting splittable split fibers. It is preferable that the split fibers can be split by a fluid flow such as a water flow or a physical action such as a needle or a calender. Among them, it is preferable that the split fibers can be split by a fluid flow. As the cross-sectional shape of this split fiber,
For example, there are an orange shape, a multiple bimetal shape, and the like. The resin component constituting the ultrafine fibers is preferably composed of a polyolefin-based resin so as to have excellent resistance to an electrolytic solution. More specifically, polyethylene (for example, low-density polyethylene, linear low-density polyethylene) , Medium-density polyethylene, high-density polyethylene, etc.), ethylene copolymers (eg, ethylene-vinyl alcohol copolymer, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, ethylene-acrylate copolymer) Copolymer, ethylene-methacrylic acid copolymer, ethylene-methacrylic acid ester copolymer), poly-4-methylpentene-1 resin, α-olefin copolymers such as ethylene, propylene and butene-1, polypropylene, propylene-based Composed of one or more copolymers, polybutenes, butene-based copolymers, etc. It is preferable to that. The ultrafine fibers need not be one kind in terms of resin composition, and two or more kinds may be mixed. In addition, when the polypropylene-containing fiber of the present invention also includes a polyolefin-based resin component and is dividable (for example, when the fiber cross-sectional shape is orange or multiple bimetallic), the fiber originates from the polyolefin-containing fiber of the present invention. May be contained. It is preferable that such ultra-fine fibers are contained in the fiber sheet in an amount of 5 mass% or more so as to have excellent retention of the electrolytic solution and excellent anti-dendritic properties.
【0015】更に、本発明の繊維シートを電池用セパレータ
として使用する場合には、融着繊維を含んでいるのが好
ましい。融着繊維を含んでいることによって、引張強さ
や剛軟度を向上させることができる。この融着繊維は融
着繊維以外の繊維（例えば、極細繊維やポリプロピレン
含有繊維）を溶融させないように、融着繊維以外の繊維
を構成するいずれの樹脂成分の融点よりも低い融点を有
する樹脂成分（以下、「低融点成分」という）を、少な
くとも繊維表面に有するのが好ましい。融着繊維を構成
する低融点成分の融点は融着繊維以外の繊維を構成する
最も融点の低い樹脂成分の融点よりも、１０℃以上低い
のが好ましく、１５℃以上低いのがより好ましい。な
お、「融点」は示差熱量計を用い、昇温温度１０℃／分
で室温から昇温して得られる融解吸熱曲線の極大値を与
える温度をいう。この融着繊維も耐電解液性に優れるよ
うに、前述の極細繊維を構成する樹脂成分と同様の樹脂
成分１種類以上から構成されているのが好ましい。な
お、融着繊維は単一成分から構成されていても良いし、
２種類以上の樹脂成分から構成されていても良いが、２
種類以上の樹脂成分から構成されていると、繊維シート
の引張強さをより向上させることができるため好適であ
る。この２種類以上の樹脂成分からなる融着繊維の断面
形状としては、例えば、芯鞘型、偏芯型、サイドバイサ
イド型のものを使用でき、芯鞘型であると均一に融着で
きるため好適である。この融着繊維は樹脂組成の点にお
いて１種類である必要はなく、２種類以上混在していて
も良い。また、本発明のポリプロピレン含有繊維がポリ
オレフィン系樹脂成分も備えており、このポリオレフィ
ン系樹脂成分が低融点成分として作用できる場合には、
本発明のポリオレフィン含有繊維を融着繊維として使用
することもできる。更に、前述の極細繊維が融着繊維と
して作用できる場合には、極細繊維を融着繊維として使
用しても良い。このような融着繊維は引張強さや剛軟度
が向上するように、繊維シート中、１０ｍａｓｓ％以上
含まれているのが好ましい。[0015] Further, when the fiber sheet of the present invention is used as a battery separator, the fiber sheet preferably contains fused fibers. By including the fused fibers, the tensile strength and the softness can be improved. The fused fiber is a resin component having a melting point lower than the melting point of any resin component constituting the fiber other than the fused fiber so as not to melt fibers other than the fused fiber (for example, ultrafine fibers or polypropylene-containing fibers). (Hereinafter, referred to as “low melting point component”) at least on the fiber surface. The melting point of the low melting point component constituting the fused fiber is preferably lower than the melting point of the resin component having the lowest melting point constituting the fiber other than the fused fiber by 10 ° C. or more, more preferably 15 ° C. or more. The “melting point” refers to a temperature at which a maximum value of a melting endothermic curve obtained by raising the temperature from room temperature at a temperature rise rate of 10 ° C./min using a differential calorimeter is given. It is preferable that the fusion fiber is also composed of at least one resin component similar to the resin component constituting the above-mentioned ultrafine fiber so as to have excellent electrolytic solution resistance. In addition, the fused fiber may be composed of a single component,
Although it may be composed of two or more resin components,
It is preferable that the fiber sheet is composed of more than two kinds of resin components because the tensile strength of the fiber sheet can be further improved. As the cross-sectional shape of the fused fiber composed of two or more types of resin components, for example, a core-sheath type, an eccentric type, and a side-by-side type can be used. is there. The fused fibers need not be one kind in terms of the resin composition, and two or more kinds may be mixed. Further, when the polypropylene-containing fiber of the present invention also includes a polyolefin-based resin component, and the polyolefin-based resin component can act as a low melting point component,
The polyolefin-containing fiber of the present invention can be used as a fusion fiber. Further, when the above-mentioned ultrafine fibers can function as fusion fibers, the ultrafine fibers may be used as fusion fibers. Such a fused fiber is preferably contained in the fiber sheet in an amount of 10 mass% or more so that the tensile strength and the softness are improved.
【0016】本発明の繊維シートは常法により製造すること
ができる。例えば、本発明のポリプロピレン含有繊維を
含む不織布は次のようにして製造することができる。ま
ず、前述のようなポリプロピレン含有繊維を含む繊維ウ
エブを形成する。この繊維ウエブの形成方法としては、
例えば、カード法、エアレイ法、スパンボンド法、メル
トブロー法などの乾式法や、湿式法などがある。なお、
繊維ウエブの形成方法によって繊維長が異なり、前者の
乾式法により形成する場合（スパンボンド法、メルトブ
ロー法を除く）には、２０〜１６０ｍｍ長程度の繊維を
使用し、後者の湿式法により形成する場合には、１〜３
０ｍｍ長程度の繊維を使用する。また、これら繊維ウエ
ブを形成した後、製法の異なる繊維ウエブを積層した
り、繊維配合の異なる繊維ウエブを積層するなど、種類
の異なる繊維ウエブを積層しても良い。なお、電池用セ
パレータに使用する繊維シートを製造する場合には、繊
維の分散性に優れる湿式法により形成した繊維ウエブを
含んでいるのが好ましい。なお、乾式法により形成した
繊維ウエブと湿式法により形成した繊維ウエブとを積層
した積層繊維ウエブは強度と均一分散性の両方を兼ね備
えた好適なものである。次いで、ニードルや流体流（特
に水流）により絡合したり、繊維ウエブ中に含まれてい
る融着繊維を部分的又は全面的に融着したり、バインダ
ーにより部分的又は全面的に接着したり、或いはこれら
を併用して不織布を製造することができる。この不織布
を電池用セパレータとして使用する場合には、強度的に
優れるように、また物理的作用により分割可能な分割繊
維を繊維ウエブ中に含んでいる場合には分割繊維を分割
できるように、流体流を作用させるのが好ましい。ま
た、前述のような融着繊維を含んでいる場合には、融着
繊維を融着させるのが好ましい。このようにして製造で
きる本発明の不織布の面密度は１０〜１５０ｇ／ｍ2程
度であるのが適当である。例えば、電池用セパレータと
して使用する場合には、２０〜１００ｇ／ｍ2であるの
が好ましく、３０〜８０ｇ／ｍ2であるのがより好まし
い。[0016] The fiber sheet of the present invention can be produced by a conventional method. For example, the nonwoven fabric containing the polypropylene-containing fiber of the present invention can be manufactured as follows. First, a fiber web containing the above-mentioned polypropylene-containing fiber is formed. As a method of forming this fiber web,
For example, there are a dry method such as a card method, an air lay method, a spun bond method, and a melt blow method, and a wet method. In addition,
The fiber length varies depending on the method of forming the fiber web. When the fiber web is formed by the dry method (excluding the spun bond method and the melt blow method), a fiber having a length of about 20 to 160 mm is used, and the fiber is formed by the wet method. In case, 1-3
A fiber having a length of about 0 mm is used. Further, after forming these fiber webs, different types of fiber webs may be laminated, such as laminating fiber webs having different production methods or laminating fiber webs having different fiber compositions. In the case where a fiber sheet used for a battery separator is manufactured, it is preferable to include a fiber web formed by a wet method having excellent fiber dispersibility. A laminated fiber web obtained by laminating a fiber web formed by a dry method and a fiber web formed by a wet method is a suitable one having both strength and uniform dispersibility. Next, the fibers are entangled by a needle or a fluid stream (especially a water stream), the fused fibers contained in the fiber web are partially or completely fused, or partially or completely adhered by a binder. Alternatively, a nonwoven fabric can be produced by using these in combination. When this non-woven fabric is used as a battery separator, the fluid should be excellent in strength, and if the fiber web contains split fibers that can be split by physical action, the split fibers can be split. It is preferred to act on the flow. In the case where the above-mentioned fused fibers are contained, it is preferable to fuse the fused fibers. Suitably, the areal density of the nonwoven fabric of the present invention that can be produced in this way is about 10 to 150 g / m 2 . For example, when used as a battery separator is preferably from 20 to 100 g / m 2, and more preferably 30 to 80 g / m 2.
【0017】本発明の繊維シートは前述のようなポリプロピ
レン含有繊維を含んでいるため、強度的に優れしかも強
度ムラのないものである。そのため、強度を必要とする
用途、例えば、電池用セパレータ、濾過布などの各種用
途に使用することができる。特に本発明の繊維シートを
電池用セパレータとして使用すると、極板群形成時に繊
維シートを極板のバリが突き抜けたり、極板のエッジに
よって繊維シートが引き裂かれることがないため、高収
率で電池を製造することができる。なお、各種用途に適
合するように、染色加工、バフィング処理、バインダー
による顔料着色加工、揉み加工、エレクトレット加工、
親水化処理などの後加工を実施することができる。例え
ば、電池用セパレータとして使用する場合には、電解液
の保持性に優れるように、例えば、スルホン化処理、フ
ッ素ガス処理、ビニルモノマーのグラフト重合処理、界
面活性剤処理、放電処理、或は親水性樹脂付与処理など
の親水化処理を実施するのが好ましい。[0017] Since the fiber sheet of the present invention contains the above-mentioned polypropylene-containing fiber, the fiber sheet is excellent in strength and free from unevenness in strength. Therefore, it can be used for applications requiring strength, for example, various applications such as battery separators and filter cloths. In particular, when the fiber sheet of the present invention is used as a battery separator, the burr of the electrode plate does not penetrate the fiber sheet during formation of the electrode plate group, and the fiber sheet is not torn by the edge of the electrode plate. Can be manufactured. In addition, dyeing processing, buffing processing, pigment coloring processing with a binder, kneading processing, electret processing,
Post-processing such as a hydrophilic treatment can be performed. For example, when used as a battery separator, for example, a sulfonation treatment, a fluorine gas treatment, a graft polymerization treatment of a vinyl monomer, a surfactant treatment, a discharge treatment, or a hydrophilic treatment so as to have excellent electrolyte retention. It is preferable to perform a hydrophilic treatment such as a treatment for imparting a hydrophilic resin.
【0018】以下に、本発明の実施例を記載するが、本発明
は以下の実施例に限定されるものではない。Hereinafter, embodiments of the present invention will be described, but the present invention is not limited to the following embodiments.
【0019】[0019]
【実施例】（実施例１）常法の溶融紡糸装置により、Ｑ
値が３、アイソタクチックペンタッド分率が９５％の高
強度化可能ポリプロピレン９７ｍａｓｓ％と、メルトイ
ンデックスが６８０の混在ポリプロピレン３ｍａｓｓ％
とを混合したペレットを、紡糸温度２６０℃、吐出量を
１ホールあたり０．１２５ｇ／ｍｉｎで溶融紡糸を実施
した。紡出された糸を冷却しながら引き取り、繊度６．
７ｄｔｅｘの未延伸ポリプロピレン繊維を得た。この溶
融紡糸時においては紡糸性に優れていた。次いで、この
未延伸ポリプロピレン繊維を集束し、延伸温度１２０℃
で４．１倍延伸して、延伸ポリプロピレン繊維を得た。
次いで、切断して、繊度１．８ｄｔｅｘ、繊維長１０ｍ
ｍの延伸ポリプロピレン繊維（引張り強さ：７．３ｃＮ
／ｄｔｅｘ、断面形状：円形）を得た。Example 1 Example 1
97 mass% of high strength polypropylene with a value of 3, isotactic pentad fraction of 95%, and 3 mass% of a mixed polypropylene with a melt index of 680
The pellets were melt-spun at a spinning temperature of 260 ° C. and a discharge rate of 0.125 g / min per hole. 5. The spun yarn is taken off while cooling, and the fineness is 6.
An undrawn polypropylene fiber of 7 dtex was obtained. At the time of this melt spinning, the spinnability was excellent. Next, the undrawn polypropylene fibers are bundled, and drawn at a temperature of 120 ° C.
To 4.1 times to obtain a drawn polypropylene fiber.
Next, it is cut and has a fineness of 1.8 dtex and a fiber length of 10 m.
m drawn polypropylene fiber (tensile strength: 7.3 cN)
/ Dtex, cross-sectional shape: circular).
【0020】（実施例２）Ｑ値が３、アイソタクチックペン
タッド分率が９５％の高強度化可能ポリプロピレン９５
ｍａｓｓ％と、メルトインデックスが６８０の混在ポリ
プロピレン５ｍａｓｓ％とを混合したペレットを使用し
たこと、及び延伸倍率を４．４倍としたこと以外は実施
例１と同じ操作を繰り返して、繊度１．６７ｄｔｅｘ、
繊維長１０ｍｍの延伸ポリプロピレン繊維（引張り強
さ：７．６ｃＮ／ｄｔｅｘ、断面形状：円形）を得た。
なお、溶融紡糸時においては紡糸性に優れていた。(Example 2) High-strength polypropylene 95 having a Q value of 3 and an isotactic pentad fraction of 95%
The same operation as in Example 1 was repeated, except that a pellet obtained by mixing 5% by mass of a mixed polypropylene having a melt index of 680 and 5% by mass of a mixed polypropylene was used, and the fineness was 1.67 dtex. ,
A drawn polypropylene fiber having a fiber length of 10 mm (tensile strength: 7.6 cN / dtex, sectional shape: circular) was obtained.
In addition, during the melt spinning, the spinning property was excellent.
【0021】（実施例３）Ｑ値が３、アイソタクチックペン
タッド分率が９５％の高強度化可能ポリプロピレン９２
ｍａｓｓ％と、メルトインデックスが６８０の混在ポリ
プロピレン８ｍａｓｓ％とを混合したペレットを使用し
たこと、及び延伸倍率を４．７倍としたこと以外は実施
例１と同じ操作を繰り返して、繊度１．５８ｄｔｅｘ、
繊維長１０ｍｍの延伸ポリプロピレン繊維（引張り強
さ：７．４ｃＮ／ｄｔｅｘ、断面形状：円形）を得た。
なお、溶融紡糸時においては紡糸性に優れていた。(Example 3) Polypropylene 92 having a Q value of 3 and an isotactic pentad fraction of 95% capable of increasing strength.
The same operation as in Example 1 was repeated, except that a pellet obtained by mixing a mass% and a mixed polypropylene of 8 mass% having a melt index of 680 was used, and the stretching ratio was set to 4.7 times, to obtain a fineness of 1.58 dtex. ,
A drawn polypropylene fiber having a fiber length of 10 mm (tensile strength: 7.4 cN / dtex, sectional shape: circular) was obtained.
In addition, during the melt spinning, the spinning property was excellent.
【0022】（実施例４）Ｑ値が３、アイソタクチックペン
タッド分率が９５％の高強度化可能ポリプロピレン９５
ｍａｓｓ％と、メルトインデックスが１２００の混在ポ
リプロピレン５ｍａｓｓ％とを混合したペレットを使用
したこと、及び延伸倍率を５．１倍としたこと以外は実
施例１と同じ操作を繰り返して、繊度１．５ｄｔｅｘ、
繊維長１０ｍｍの延伸ポリプロピレン繊維（引張り強
さ：７．７ｃＮ／ｄｔｅｘ、断面形状：円形）を得た。
なお、溶融紡糸時においては紡糸性に優れていた。(Example 4) High strength polypropylene 95 having a Q value of 3 and an isotactic pentad fraction of 95%
The same operation as in Example 1 was repeated except that a pellet obtained by mixing 5% by mass of a mixed polypropylene having a melt index of 1200 and 5 mass% of a mixed polypropylene having a melt index of 1200 was used, and a fineness of 1.5 dtex was obtained. ,
A drawn polypropylene fiber having a fiber length of 10 mm (tensile strength: 7.7 cN / dtex, cross-sectional shape: circular) was obtained.
In addition, during the melt spinning, the spinning property was excellent.
【0023】（比較例１）Ｑ値が３、アイソタクチックペン
タッド分率が９５％の高強度化可能ポリプロピレンのペ
レットを１００％使用したこと、及び延伸倍率を３．９
倍としたこと以外は実施例１と同じ操作を繰り返して、
繊度２．２ｄｔｅｘ、繊維長１０ｍｍの延伸ポリプロピ
レン繊維（引張り強さ：６．１ｃＮ／ｄｔｅｘ、断面形
状：円形）を得た。なお、溶融紡糸時においては単糸切
れが起こり、紡糸性の劣るものであった。(Comparative Example 1) A high strength polypropylene pellet having a Q value of 3 and an isotactic pentad fraction of 95% was used 100%, and the stretching ratio was 3.9.
The same operation as in Example 1 was repeated, except that
A drawn polypropylene fiber having a fineness of 2.2 dtex and a fiber length of 10 mm (tensile strength: 6.1 cN / dtex, cross-sectional shape: circular) was obtained. At the time of melt spinning, single yarn breakage occurred, resulting in poor spinnability.
【0024】（比較例２）Ｑ値が３、アイソタクチックペン
タッド分率が９５％の高強度化可能ポリプロピレン８８
ｍａｓｓ％と、メルトインデックスが６８０の混在ポリ
プロピレン１２ｍａｓｓ％とを混合したペレットを使用
したこと、及び延伸倍率を５倍としたこと以外は実施例
１と同じ操作を繰り返して、繊度１．５ｄｔｅｘ、繊維
長１０ｍｍの延伸ポリプロピレン繊維（引張り強さ：
６．９ｃＮ／ｄｔｅｘ、断面形状：円形）を得た。な
お、溶融紡糸時においては紡糸性に優れていた。(Comparative Example 2) High-strength polypropylene 88 having a Q value of 3 and an isotactic pentad fraction of 95%
The same operation as in Example 1 was repeated except that a pellet obtained by mixing a mass% and a 12% by mass mixed polypropylene having a melt index of 680 and the stretching ratio was set to 5 times was repeated to obtain a fineness of 1.5 dtex and a fiber of 1.5%. 10 mm drawn polypropylene fiber (tensile strength:
6.9 cN / dtex, cross-sectional shape: circular). In addition, during the melt spinning, the spinning property was excellent.
【0025】（比較例３）Ｑ値が３、アイソタクチックペン
タッド分率が９５％の高強度化可能ポリプロピレン９５
ｍａｓｓ％と、メルトインデックスが６５の混在ポリプ
ロピレン５ｍａｓｓ％とを混合したペレットを使用した
こと、及び延伸倍率を４倍としたこと以外は実施例１と
同じ操作を繰り返して、繊度１．８７ｄｔｅｘ、繊維長
１０ｍｍの延伸ポリプロピレン繊維（引張り強さ：６．
４ｃＮ／ｄｔｅｘ、断面形状：円形）を得た。なお、溶
融紡糸時においては単糸切れが起こり、紡糸性の劣るも
のであった。(Comparative Example 3) A high-strength polypropylene 95 having a Q value of 3 and an isotactic pentad fraction of 95%
The same operation as in Example 1 was repeated except that a pellet obtained by mixing 5% by mass of a mixed polypropylene having a melt index of 65 with a melt index of 65 was used, and the fineness was 1.87 dtex and the fiber was 10 mm long drawn polypropylene fiber (tensile strength: 6.
4 cN / dtex, sectional shape: circular). At the time of melt spinning, single yarn breakage occurred, resulting in poor spinnability.
【0026】以上の実施例及び比較例から次のことがわかっ
た。 （１）実施例１〜４及び比較例１〜２より、混在ポリプ
ロピレンの混在量が１〜１０ｍａｓｓ％程度である場合
に、強度的に優れかつ細いポリプロピレン含有繊維を得
ることができる。 （２）実施例２、４及び比較例３より、混在ポリプロピ
レンのメルトインデックスが１００〜１，５００程度で
ある場合に、強度的に優れかつ細いポリプロピレン含有
繊維を得ることができる。From the above examples and comparative examples, the following has been found. (1) From Examples 1 to 4 and Comparative Examples 1 and 2, when the content of the mixed polypropylene is about 1 to 10 mass%, a polypropylene-containing fiber excellent in strength and thin can be obtained. (2) From Examples 2 and 4 and Comparative Example 3, when the melt index of the mixed polypropylene is about 100 to 1,500, a polypropylene-containing fiber excellent in strength and thin can be obtained.
【0027】[0027]
【発明の効果】本発明のポリプロピレン含有繊維は強度
的に優れかつ細い繊維である。そのため、本発明のポリ
プロピレン含有繊維を含む繊維シートは少量でも均一に
分散した強度ムラのないものである。また、この繊維シ
ートを電池用セパレータとして用いた場合には、電解液
の保持性に優れ、しかも電極群製造時に繊維シートが破
断したり、極板のバリが繊維シートを貫通することがな
い。The polypropylene-containing fibers of the present invention are excellent in strength and thin. Therefore, the fiber sheet containing the polypropylene-containing fiber of the present invention is uniformly dispersed even in a small amount and has no strength unevenness. In addition, when this fiber sheet is used as a battery separator, the fiber sheet is excellent in retaining the electrolytic solution, and the fiber sheet is not broken at the time of manufacturing the electrode group, and the burr of the electrode plate does not penetrate the fiber sheet.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｄ０４Ｈ 1/42 Ｄ０４Ｈ 1/42 Ｘ Ｈ０１Ｍ 2/16 Ｈ０１Ｍ 2/16 Ｐ Ｆターム(参考） 4J002 BB033 BB063 BB073 BB083 BB103 BB121 BB122 BB153 BB173 BE033 BF033 GK01 4L035 BB31 BB89 BB91 EE01 EE08 FF05 FF06 4L047 AA14 AB02 AB10 BA03 BA04 BA09 BB02 CB01 CB07 CC14 5H021 CC02 EE04 HH00 HH01 HH06 HH07 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI theme coat ゛ (Reference) D04H 1/42 D04H 1/42 X H01M 2/16 H01M 2/16 PF term (Reference) 4J002 BB033 BB063 BB073 BB083 BB103 BB121 BB122 BB153 BB173 BE033 BF033 GK01 4L035 BB31 BB89 BB91 EE01 EE08 FF05 FF06 4L047 AA14 AB02 AB10 BA03 BA04 BA09 BB02 CB01 CB07 CC14 5H021 CC02 EE04 HH06 HH01
Claims (6)
量で除した値）が５未満で、アイソタクチックペンタッ
ド分率が９３％以上のポリプロピレン中に、メルトイン
デックスが１００〜１，５００のポリプロピレンが１〜
１０ｍａｓｓ％（全体の質量に対して）の割合で混在し
たポリプロピレン成分を備えていることを特徴とするポ
リプロピレン含有繊維。1. A polypropylene having a Q value (Q: a value obtained by dividing a weight average molecular weight by a number average molecular weight) of less than 5 and having an isotactic pentad fraction of 93% or more has a melt index of 100 to 1, 500 polypropylenes
A polypropylene-containing fiber comprising a polypropylene component mixed at a ratio of 10 mass% (based on the total mass).
量で除した値）が５未満で、アイソタクチックペンタッ
ド分率が９３％以上のポリプロピレン中に、メルトイン
デックスが１００〜１，５００のポリプロピレンが１〜
１０ｍａｓｓ％（全体の質量に対して）の割合で混在し
たポリプロピレン成分のみからなることを特徴とするポ
リプロピレン含有繊維。2. A polypropylene having a Q value (Q: a value obtained by dividing a weight average molecular weight by a number average molecular weight) of less than 5 and having an isotactic pentad fraction of 93% or more has a melt index of 100 to 1, 500 polypropylenes
A polypropylene-containing fiber comprising only a polypropylene component mixed at a ratio of 10 mass% (based on the total mass).
量で除した値）が５未満で、アイソタクチックペンタッ
ド分率が９３％以上のポリプロピレン中に、メルトイン
デックスが１００〜１，５００のポリプロピレンが１〜
１０ｍａｓｓ％（全体の質量に対して）の割合で混在し
たポリプロピレン成分と、ポリオレフィン系樹脂成分と
を備えていることを特徴とする、ポリプロピレン含有繊
維。A polypropylene having a Q value (Q: a value obtained by dividing a weight average molecular weight by a number average molecular weight) of less than 5 and having an isotactic pentad fraction of 93% or more has a melt index of 100 to 1, 500 polypropylenes
A polypropylene-containing fiber, comprising: a polypropylene component mixed at a ratio of 10 mass% (based on the total mass); and a polyolefin-based resin component.
ンチニュートン／デシテックス）以上、かつ繊度が２．
２ｄｔｅｘ（デシテックス）未満であることを特徴とす
る、請求項１〜請求項３のいずれかに記載のポリプロピ
レン含有繊維。4. A tensile strength of 7.1 cN / dtex (centinewton / decitex) or more and a fineness of 2.
The polypropylene-containing fiber according to any one of claims 1 to 3, wherein the fiber content is less than 2 dtex (decitex).
ポリプロピレン含有繊維を含んでいることを特徴とする
繊維シート。A fiber sheet comprising the polypropylene-containing fiber according to any one of claims 1 to 4.
徴とする、請求項５に記載の繊維シート。6. The fiber sheet according to claim 5, wherein the fiber sheet is used as a battery separator.