JP2001151615A - Paving stone for preventing weed growth and method for producing the same - Google Patents
Paving stone for preventing weed growth and method for producing the sameInfo
- Publication number
- JP2001151615A JP2001151615A JP33883299A JP33883299A JP2001151615A JP 2001151615 A JP2001151615 A JP 2001151615A JP 33883299 A JP33883299 A JP 33883299A JP 33883299 A JP33883299 A JP 33883299A JP 2001151615 A JP2001151615 A JP 2001151615A
- Authority
- JP
- Japan
- Prior art keywords
- calcium
- igneous rock
- powder
- stone
- propagation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は道路や公園等に敷き
詰めて、雑草が繁殖するのを防止する敷石とその製造方
法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a paving stone which is laid on a road, a park, or the like to prevent the propagation of weeds and a method of manufacturing the same.
【０００２】[0002]
【従来の技術】カルシウムが、除草効果を示すことは知
られている（特開昭４９−８６５４２号公報）。さら
に、地面に、たとえば数ｃｍの厚さに砂利等の細骨材を
敷き詰めて、雑草が繁殖するのを防止することができる
技術も知られている。地面に敷き詰められた細骨材は、
乾燥状態となるために、この上に雑草の種子が落下して
も、種子には水分が供給されず、発芽しない。しかしな
がら、細骨材を敷き積める構造は、数年もすると雑草が
繁殖するようになる。それは、土砂が風で運ばれて来
て、種子を発芽させる環境となるからである。2. Description of the Related Art It is known that calcium has a herbicidal effect (JP-A-49-86542). Further, there is also known a technique in which fine aggregate such as gravel is spread on the ground to a thickness of, for example, several cm to prevent weeds from growing. Fine aggregate spread on the ground,
Since the seeds of the weeds fall on the dry state, no water is supplied to the seeds and the seeds do not germinate. However, the structure in which fine aggregates are laid allows weeds to grow in a few years. This is because earth and sand are brought by the wind and provide an environment for germinating seeds.
【０００３】[0003]
【発明が解決しようとする課題】地面に敷き詰める骨材
に、カルシウム含有量の多い石が使用できるなら、雑草
の繁殖を効果的に防止できる。骨材に含まれるカルシウ
ムが、表面のｐＨを強アルカリ性として種子の発芽を阻
止するからである。しかしながら、実際には天然石を破
砕したもので、骨材の表面ｐＨを、雑草の発芽を効果的
に阻止できる強アルカリとすることができない。このた
め、カルシウムを含む天然石を破砕した骨材を地面に敷
き詰めても、２年もすると雑草が繁殖する欠点がある。If a stone having a high calcium content can be used as the aggregate to be spread on the ground, the propagation of weeds can be effectively prevented. This is because calcium contained in the aggregate makes the surface pH highly alkaline and inhibits seed germination. However, actually, natural stone is crushed, and the surface pH of the aggregate cannot be set to a strong alkali that can effectively prevent the germination of weeds. For this reason, even if the aggregate which crushed the natural stone containing calcium is laid on the ground, there is a fault that weeds propagate in two years.
【０００４】本発明は、この欠点を解決するために種々
の実験を繰り返した結果、カルシウムを含む石を焼成す
ることにより、内部に含有されるカルシウムを表面に移
行させて、極めて長期間にわたって効果的に雑草の繁殖
を阻止することに成功した。したがって、本発明の大切
な目的は、安価に多量生産して、雑草の繁殖を効果的に
阻止できる敷石とこの敷石の製造方法を提供することに
ある。According to the present invention, as a result of repeating various experiments in order to solve this drawback, as a result of calcining a stone containing calcium, the calcium contained therein is transferred to the surface, which is effective for a very long time. We succeeded in stopping weed propagation. Therefore, an important object of the present invention is to provide a cobblestone that can be mass-produced at low cost and that can effectively prevent the propagation of weeds, and a method of manufacturing the cobblestone.
【０００５】[0005]
【課題を解決するための手段】本発明の雑草の繁殖を防
止する敷石は、カルシウムを含有している火成岩を焼成
して、内部に含まれるカルシウムを表面移行させてい
る。表面のカルシウムは、雨水が付着するときに付着水
のｐＨを強アルカリとして、雑草の繁殖を阻止する。The paving stones of the present invention for preventing the propagation of weeds are obtained by firing igneous rocks containing calcium and transferring the calcium contained therein to the surface. Calcium on the surface prevents the growth of weeds by making the pH of the attached water a strong alkali when rainwater is attached.
【０００６】本発明の敷石は、好ましくは、酸化カルシ
ウムの含有量を０．５重量％以上とする火成岩を８５０
〜１３００℃で焼成したものである。この温度で焼成さ
れた敷石は、含有されるカルシウムをもっとも効果的に
表面に移行できる。８５０℃よりも低温で焼成すると、
含有されるカルシウムを効率よく移行できない。また、
１３００℃よりも高温で焼成すると、含有されるカルシ
ウムが消失して少なくなる。The paving stone of the present invention is preferably made of 850 igneous rocks having a calcium oxide content of 0.5% by weight or more.
It is fired at １1300 ° C. Paving stones fired at this temperature can transfer the contained calcium to the surface most effectively. When firing at a temperature lower than 850 ° C,
The contained calcium cannot be transferred efficiently. Also,
When calcined at a temperature higher than 1300 ° C., the contained calcium disappears and decreases.
【０００７】さらに、本発明の敷石は、平均粒径を１〜
２０ｍｍとする砕石に破砕された火成岩を焼成したもの
である。この粒径に破砕して焼成すると、敷石の表面積
が大きくなって、含有カルシウムを効率よく表面に移行
できる。Further, the paving stone of the present invention has an average particle size of 1 to 1.
It is obtained by firing igneous rock crushed into crushed stone having a size of 20 mm. When crushed to this particle size and fired, the surface area of the paving stones increases, and the contained calcium can be efficiently transferred to the surface.
【０００８】また、敷石は、火成岩の一種である噴出岩
を破砕して製作される。[0008] Paving stones are produced by crushing erupted rocks, a type of igneous rock.
【０００９】本発明の雑草の繁殖を防止する敷石の製造
方法は、カルシウムを含有する火成岩を破砕する工程で
発生する火成岩粉末と、コンクリートの骨材に使用され
る砕石を人工的に製造する工程で発生する粉末残渣とを
混合して粒状に成形し、成形された原料粒を焼成してカ
ルシウムを表面に移行させる。The method of the present invention for producing a cobblestone for preventing the propagation of weeds comprises a step of artificially producing igneous rock powder generated in the step of crushing igneous rock containing calcium and crushed stone used for concrete aggregate. Is mixed with the powder residue generated in step (1) to form granules, and the formed raw material particles are calcined to transfer calcium to the surface.
【００１０】以上の方法で製造される敷石は、たとえ
ば、火成岩粉末の混合量を１０〜７０重量％とする。火
成岩粉末の添加量が少なくなると、カルシウム含有量が
少なくなって、雑草の除草効果が低下する。火成岩粉末
の添加量を多くすると、粉末残渣の添加量が少なくなっ
て、多量の粉末残渣を有効に再利用するのが難しくな
る。In the paving stones manufactured by the above method, for example, the mixing amount of igneous rock powder is 10 to 70% by weight. When the amount of the igneous rock powder is reduced, the calcium content is reduced, and the herbicidal effect of the weeds is reduced. When the addition amount of igneous rock powder is increased, the addition amount of powder residue becomes small, and it becomes difficult to effectively reuse a large amount of powder residue.
【００１１】火成岩粉末と粉末残渣の混合体は、好まし
くは多孔質な状態に成形して焼成する。The mixture of igneous rock powder and powder residue is preferably formed into a porous state and fired.
【００１２】[0012]
【発明の実施の形態】以下、本発明の実施例を図面に基
づいて説明する。ただし、以下に示す実施例は、本発明
の技術思想を具体化するための雑草の繁殖を防止する敷
石とその製造方法を例示するものであって、本発明は雑
草の繁殖を防止する敷石とその製造方法を下記のものに
特定しない。Embodiments of the present invention will be described below with reference to the drawings. However, the following examples illustrate the paving stones for preventing the propagation of weeds and the method for producing the same to embody the technical concept of the present invention, and the present invention relates to paving stones for preventing the propagation of weeds. The manufacturing method is not specified as follows.
【００１３】雑草の繁殖を防止する敷石１は、図１の断
面図に示すように、地面２の上に所定の厚さ（ｄ）に敷
設される。敷設厚さ（ｄ）は、たとえば２〜２０ｃｍ、
好ましくは３〜１５ｃｍ、さらに好ましくは３〜１０ｃ
ｍ、最適には約５ｃｍとする。敷設厚さを厚くすると、
より長い年月にわたって雑草の繁殖を有効に防止でき
る。敷設厚さが薄過ぎると、種子が発芽しやすくなる。The paving stones 1 for preventing the propagation of weeds are laid on the ground 2 at a predetermined thickness (d) as shown in the sectional view of FIG. The laying thickness (d) is, for example, 2 to 20 cm,
Preferably 3 to 15 cm, more preferably 3 to 10 c
m, optimally about 5 cm. If you increase the laying thickness,
Weed propagation can be effectively prevented over a longer period of time. If the laying thickness is too thin, the seeds are likely to germinate.
【００１４】敷石１は、たとえば、平均粒径を１〜２０
ｍｍ、好ましくは２〜２０ｍｍ、さらに好ましくは２．
５〜２０ｍｍとする。この平均粒径の敷石は、地面に敷
いて外観を美しくできる。また、表面を簡単に平面状に
できる特長もある。ただ、平均粒径を１ｍｍより小さ
く、あるいは、２０ｍｍより大きくすることもできる。
さらに、平均粒径が異なる複数種のものを混合すること
もできる。The paving stone 1 has, for example, an average particle size of 1 to 20.
mm, preferably 2 to 20 mm, more preferably 2.
5 to 20 mm. Paving stones of this average particle size can be laid on the ground to make the appearance beautiful. Another feature is that the surface can be easily made flat. However, the average particle size may be smaller than 1 mm or larger than 20 mm.
Further, a plurality of kinds having different average particle diameters may be mixed.
【００１５】地面に敷設される敷石１は、雨水や散水に
よって表面に水が付着する。本発明の敷石は、表面に付
着する水を強アルカリ性として、雑草の種子が発芽する
のを阻止する。表面付着水は、焼成して敷石の表面に移
行させたカルシウムによって強アルカリとなる。カルシ
ウムは、焼成する前には内部に含有されているが、焼成
するときに、表面移行する。敷石は、焼成前と、焼成後
では、表面付着水のｐＨが著しく異なる。カルシウムを
含有している天然石は、焼成しない状態では、表面付着
水のｐＨを強アルカリとすることができない。Water is attached to the surface of the paving stones 1 laid on the ground by rainwater or water spray. The paving stones of the present invention make the water adhering to the surface highly alkaline and prevent the seeds of weeds from germinating. The water adhering to the surface becomes a strong alkali by the calcium transferred to the surface of the cobblestone by firing. Calcium is contained inside before firing, but migrates to the surface when firing. Paving stones have a markedly different pH of water adhering to the surface before and after firing. Uncalcined natural stones containing calcium cannot make the pH of the water adhering to the surface strongly alkaline.
【００１６】焼成して表面付着水を強アルカリとする天
然石は、たとえば、酸化カルシウムの含有量を、たとえ
ば０．５重量％以上、好ましくは１．５重量％、さらに
好ましくは２重量％、最適には２．２重量％とする火成
岩である。酸化カルシウムの含有量が多い天然石を焼成
した敷石は、カルシウムの表面移行量が多く、表面付着
水をより強いアルカリとして雑草の繁殖をより効果的
に、しかも長期間にわたって保持する。Natural stones which are calcined to make the surface-adhered water a strong alkali have a calcium oxide content of, for example, 0.5% by weight or more, preferably 1.5% by weight, more preferably 2% by weight, Is an igneous rock with 2.2% by weight. Paving stones obtained by calcining natural stones having a high content of calcium oxide have a large amount of calcium transferred to the surface, and use the surface-adhering water as a stronger alkali to more effectively maintain the propagation of weeds over a long period of time.
【００１７】敷石は、天然石である火成岩を、前述の粒
径に破砕したものを焼成して製造され、あるいは、粉末
を成形し焼成して製造する方法とがある。粉末を成形し
て焼成する方法は、カルシウムを含有する火成岩を破砕
する工程で発生する火成岩粉末と、コンクリートの骨材
に使用される砕石を人工的に製造する工程で、天然石を
破砕して砕石を分離したときに発生する粉末残渣とを混
合して粒状に成形する。このようにして成形された原料
粒が焼成されて、火成岩粉末に含有されるカルシウムを
表面移行させる。いずれの方法で製造された敷石も、焼
成工程で含有カルシウムを表面移行させる。Paving stones are produced by firing igneous rock, which is a natural stone, crushed to the above-mentioned particle size, or by molding and firing powder. The method of molding and firing the powder is a process of artificially producing igneous rock powder generated in the step of crushing igneous rock containing calcium and crushed stone used for concrete aggregate, crushing natural stone Is mixed with a powder residue generated when the powder is separated and formed into granules. The raw material particles thus formed are fired to transfer calcium contained in the igneous rock powder to the surface. The paving stones manufactured by any of the methods transfer the contained calcium to the surface in the firing step.
【００１８】火成岩粉末と粉末残渣とを混合して粒状に
成形して焼成する方法は、火成岩を所定の形状に加工す
るときに廃棄物として発生する火成岩粉末と、コンクリ
ートの骨材を製造する工程で発生する膨大な量の粉末残
渣とを有効に再利用して、雑草の繁殖を防止できる。こ
の方法は、粉末残渣の添加量を多くして、原料コストを
低減できる。ただ、粉末残渣が多すぎると含有されるカ
ルシウム量が少なくなって、雑草の繁殖を阻止する効力
が低下する。したがって、好ましくは、火成岩粉末の混
合量を全体の１０〜７０重量％とする。ただし、火成岩
粉末に、含有カルシウム量の多いものを使用すると、火
成岩粉末の混合量を少なく、いいかえると、多量の粉末
残渣を混合して、表面移行したカルシウム量を多くして
いる敷石を製造できる。The method of mixing igneous rock powder and powder residue, forming the mixture into granules, and firing the mixture comprises the steps of producing igneous rock powder, which is generated as waste when processing igneous rock into a predetermined shape, and a concrete aggregate. The enormous amount of powder residue generated in the above can be effectively reused to prevent the propagation of weeds. This method can reduce the raw material cost by increasing the amount of powder residue added. However, if the amount of the powder residue is too large, the amount of calcium contained becomes small, and the effect of inhibiting the propagation of weeds decreases. Therefore, the mixing amount of the igneous rock powder is preferably set to 10 to 70% by weight of the whole. However, if the igneous rock powder contains a large amount of calcium, the mixing amount of the igneous rock powder is small, in other words, a large amount of powder residue can be mixed to produce a cobblestone with a large amount of calcium transferred to the surface. .
【００１９】さらに、火成岩粉末と粉末残渣とを混合し
て成形し、この成形品を焼成して製造される敷石は、多
孔質な状態として焼成することもできる。多孔質な敷石
は、焼成工程における割れを少なくできる。それは、多
孔質な空隙が、焼成時に発生する熱膨張歪を吸収する緩
衝作用をするからである。天然の火成岩も、ミクロに観
察すると微細な空隙がある多孔質な天然石である。この
ため、火成岩は、所定の粒度に破砕して焼成するとき、
熱歪で割れが発生しない特長がある。Further, the igneous rock powder and the powder residue are mixed and molded, and the paving stones produced by firing the molded article can be fired in a porous state. Porous paving stones can reduce cracks in the firing process. This is because the porous voids have a buffering function of absorbing thermal expansion strain generated during firing. Natural igneous rock is also a porous natural stone with microscopic voids when observed microscopically. For this reason, when igneous rock is crushed to a predetermined particle size and fired,
There is a feature that cracks do not occur due to thermal strain.
【００２０】焼成して製造される敷石は、酸化鉄を含有
する天然石を使用し、あるいは、酸化鉄を含有する粉末
を成形して焼成し、焼成後の表面を、極めて美しい赤色
ないし茶色にできる。この敷石は、地面に敷設して極め
て美しくできる。とくに、雨水や散水で濡れたときに、
より鮮やかな赤色から褐色になる特長がある。焼成して
赤色から茶色になる敷石は、酸化鉄の含有量を１〜１０
重量％とする。For the paving stones produced by firing, natural stones containing iron oxide are used, or powder containing iron oxide is molded and fired, and the surface after firing can be made very beautiful red or brown. . This paving stone can be laid down on the ground to make it very beautiful. Especially when it gets wet with rainwater or watering,
It has the feature of becoming more vivid red to brown. Paving stones that turn from red to brown when fired have an iron oxide content of 1 to 10
% By weight.
【００２１】敷石は焼成温度によって、表面移行するカ
ルシウム量が変化する。焼成温度が低すぎると、含有さ
れるカルシウムを効率よく表面移行することが難しい。
反対に焼成温度が高すぎると、カルシウムが消失して表
面のカルシウム量が少なくなる。最適な焼成温度は、約
１０００℃である。ただし、好ましくは、８５０〜１３
００℃、より好ましくは８９０〜１２００℃の範囲で焼
成して、含有カルシウムを効率よく表面移行できる。The amount of calcium transferred to the surface of the paving stone varies depending on the firing temperature. If the firing temperature is too low, it is difficult to efficiently transfer the contained calcium to the surface.
Conversely, if the firing temperature is too high, calcium disappears and the amount of calcium on the surface decreases. The optimal firing temperature is about 1000 ° C. However, preferably, 850 to 13
By firing at 00 ° C, more preferably in the range of 890 to 1200 ° C, the contained calcium can be efficiently transferred to the surface.
【００２２】[0022]
【実施例】［実施例１］以下の方法で、雑草の繁殖を防
止する敷石を製造する。 以下の成分を含有する火成岩である噴出岩を、平均
粒径が約３〜５ｍｍとなるように破砕する。 ＳｉＯ２…………７０重量％ Ａｌ２Ｏ３……… １６重量％ Ｆｅ２Ｏ３………… ２重量％ ＣａＯ……… ２．５重量％[Example 1] A pavement for preventing weed propagation is manufactured by the following method. Erupted rocks, which are igneous rocks containing the following components, are crushed to have an average particle size of about 3 to 5 mm. SiO 2 70% by weight Al 2 O 3 16% by weight Fe 2 O 3 2% by weight CaO 2.5% by weight
【００２３】 破砕した火成岩を焼成炉に搬入し、１
０００℃で３時間焼成して、含有するカルシウムを表面
移行して敷石とする。The crushed igneous rock is carried into a firing furnace, and
Calcination is carried out at 000 ° C. for 3 hours to transfer the contained calcium to the surface to form a cobblestone.
【００２４】［実施例２］焼成後に破砕する以外、実施
例１と同様にして敷石を製造する。Example 2 A pavement is manufactured in the same manner as in Example 1 except that the stone is crushed after firing.
【００２５】［実施例３］焼成温度を１１００℃とする
以外、実施例１と同様にして敷石を製造する。Example 3 A cobblestone is manufactured in the same manner as in Example 1 except that the firing temperature is 1100 ° C.
【００２６】［実施例４］焼成温度を９００℃とする以
外、実施例１と同様にして敷石を製造する。Example 4 A cobblestone is manufactured in the same manner as in Example 1 except that the firing temperature is 900 ° C.
【００２７】［実施例５］以下の方法で、雑草の繁殖を
防止する敷石を製造する。 実施例１の製造方法に使用した火成岩を粉末にした
火成岩粉末と、コンクリートの骨材に使用される砕石を
人工的に製造する工程で、天然石を破砕して砕石を分離
したときに発生する粉末残渣とを混合して粒状に成形す
る。火成岩粉末と粉末残渣の混合量は、同重量、すなわ
ち、火成岩粉末の添加量を５０重量％とする。混合した
粉末に水を添加して、これを平均粒径を約５ｍｍとする
球形に成形する。成形は、水を添加した粉末を金型に入
れてプレス成形し、あるいは、粉末を回転するトロンメ
ルに供給し、トロンメルに散水しながら転動させて雪ダ
ルマのように大きく成長させて所定の球形にする。トロ
ンメルで球形に成形する方法は、焼成した状態でより多
孔質な状態にできる。それは、粉末が隙間ができる状態
で結合して成形されるからである。粉末を成形するとき
に、焼成して消失される有機質のバインダー、たとえ
ば、ＰＶＣ等を添加して成形することもできる。バイン
ダーを使用する方法は、乾燥した後、焼成炉に搬入する
までの型崩れを防止できる。また、バインダーが消失し
て、より多孔質な状態に焼結できる。Example 5 A cobblestone for preventing weed propagation is manufactured by the following method. In the process of artificially producing igneous rock powder obtained by powdering igneous rock used in the production method of Example 1 and crushed stone used for concrete aggregate, powder generated when crushed natural stone is separated by crushing natural stone The residue is mixed and formed into granules. The mixing amount of the igneous rock powder and the powder residue is the same weight, that is, the addition amount of the igneous rock powder is 50% by weight. Water is added to the mixed powder to form a spherical shape having an average particle size of about 5 mm. For molding, the powder with water added is put into a mold and press-molded, or the powder is supplied to a rotating trommel, rolled while sprinkling water on the trommel, and grown to a large spherical shape like a snow darma to form a predetermined spherical shape. To The method of forming a spherical shape by trommel can make the fired state more porous. This is because the powders are combined and formed in a state where a gap is formed. When molding the powder, an organic binder which is eliminated by firing, for example, PVC or the like may be added to the powder for molding. The method of using the binder can prevent the shape from being lost after being dried and carried into the firing furnace. In addition, the binder disappears and sintering to a more porous state is possible.
【００２８】 成形された原料粒を乾燥させた後、焼
成炉に搬入して、９００℃で３時間焼成する。この焼成
工程で、含有カルシウムは表面に移行され、さらに、成
形品がを硬い粒状に焼結されて敷石となる。After the formed raw material particles are dried, they are carried into a firing furnace and fired at 900 ° C. for 3 hours. In this firing step, the contained calcium is transferred to the surface, and the molded article is sintered into hard granules to form paving stones.
【００２９】［実施例６］３０重量部の火成岩粉末と、
７０重量部の粉末残渣とを混合して成形し、焼成温度を
１０００℃とする以外、実施例５と同様にして敷石を製
造する。Example 6 30 parts by weight of igneous rock powder,
A pavement is manufactured in the same manner as in Example 5, except that 70 parts by weight of the powder residue is mixed and molded, and the firing temperature is set to 1000 ° C.
【００３０】［実施例７］２０重量部の火成岩粉末と、
８０重量部の粉末残渣とを混合して成形し、焼成温度を
１２００℃とする以外、実施例５と同様にして、敷石を
製造する。Example 7 20 parts by weight of igneous rock powder,
A cobblestone is manufactured in the same manner as in Example 5 except that 80 parts by weight of the powder residue is mixed and molded, and the firing temperature is set to 1200 ° C.
【００３１】［実施例８］８０重量部の火成岩粉末と、
２０重量部の粉末残渣とを混合して成形し、焼成温度を
１０００℃とする以外、実施例５と同様にして、敷石を
製造する。Example 8 80 parts by weight of igneous rock powder,
A pavement is manufactured in the same manner as in Example 5, except that 20 parts by weight of the powder residue is mixed and molded, and the firing temperature is set to 1000 ° C.
【００３２】実施例１〜８で製造した敷石１００ｇを、
１０００ｃｃの水に２０分間浸漬して、水のｐＨを測定
すると以下のように強アルカリとなった。参考に、比較
例として、実施例１で使用した火成岩と同じものであっ
て焼成しないものも水に浸漬して、水のｐＨを測定し
た。敷石を浸漬する前の水ｐＨは７．７とほぼ中性であ
った。100 g of the paving stones produced in Examples 1 to 8 were
When immersed in 1000 cc of water for 20 minutes and the pH of the water was measured, it became strongly alkaline as follows. For reference, as a comparative example, the same igneous rock as that used in Example 1 but not fired was immersed in water, and the pH of the water was measured. The water pH before immersion of the paving stones was almost neutral at 7.7.
【００３３】 実施例１…………９．８ 実施例２…………９．７ 実施例３…………９．６ 実施例４…………９．７ 実施例５…………９．３ 実施例６…………９．２ 実施例７…………９．２ 実施例８…………９．５ 比較例……………７．６Example 1 9.8 Example 2 9.7 Example 3 9.6 Example 4 9.7 Example 5 Example 5 9.3 Example 6 ... 9.2 Example 7 ... 9.2 Example 8 ... 9.5 Comparative example ... 7.6
【００３４】以上のように、実施例で試作した敷石は、
浸漬した水のｐＨが極めて強いアルカリ性を示した。こ
れに対して、焼成しない火成岩は、ｐＨが７．６とほぼ
中性となり、表面に付着する水をアルカリ性にできない
ことが明かとなった。As described above, the paving stones prototyped in the examples are:
The pH of the immersed water showed extremely strong alkalinity. In contrast, igneous rocks that were not fired had a pH of about 7.6 and were almost neutral, indicating that water adhering to the surface could not be made alkaline.
【００３５】さらに、実施例１〜８で試作した敷石と、
比較例の敷石を、実際に地面に敷設して、雑草が繁殖す
る状態を観察すると、実施例１〜８の敷石は、３年経過
後も雑草は全く繁殖しなかった。これに対して、比較例
の敷石は、３年経過後に多量の雑草が繁殖した。ただ
し、実験は、敷設場所を、風雨に晒されて、かつ太陽が
よくあたり、さらに、付近に雑草が繁殖した山間部とし
た。Further, paving stones prototyped in Examples 1 to 8
When the paving stones of the comparative examples were actually laid on the ground and the state where weeds propagated was observed, the paving stones of Examples 1 to 8 showed no weed propagation even after 3 years. On the other hand, in the paving stones of the comparative example, a large amount of weeds propagated after three years. However, in the experiment, the laying site was set in a mountain area where the area was exposed to the wind and rain, the sun hit well, and weeds proliferated nearby.
【００３６】[0036]
【発明の効果】本発明の雑草の繁殖を防止する敷石は、
安価に多量生産して、雑草の繁殖を効果的に阻止できる
特長がある。それは、本発明の敷石が、焼成して含有カ
ルシウムを表面移行させ、このカルシウムで表面に付着
する水のｐＨを強アルカリにして、雑草の種子の発芽を
阻止するからである。The paving stones of the present invention for preventing weed propagation are:
It has the feature that it can be mass-produced at low cost and can effectively prevent the propagation of weeds. This is because the paving stones of the present invention are calcined to transfer the contained calcium to the surface and make the pH of water adhering to the surface with the calcium strong alkali, thereby preventing germination of weed seeds.
【００３７】さらに、本発明の請求項５の雑草の繁殖を
防止する敷石の製造方法は、天然石を破砕するときに発
生する膨大な粉末残渣を有効に再利用して、雑草の繁殖
を有効に防止できる特長がある。Further, the method for producing a cobblestone for preventing the propagation of weeds according to the fifth aspect of the present invention effectively recycles an enormous amount of powder residue generated when crushing natural stones to effectively promote the propagation of weeds. There is a feature that can be prevented.
【図１】本発明の雑草の繁殖を防止する敷石の使用状態
を示す断面図FIG. 1 is a sectional view showing a use state of a cobblestone for preventing the propagation of weeds of the present invention.
１…敷石 ２…地面 1 ... paving stone 2 ... ground
Claims (8)
カルシウムを表面移行させ、表面のカルシウムでもっ
て、表面付着水のｐＨをアルカリとすることを特徴とす
る雑草の繁殖を防止する敷石。1. A paving stone for preventing the propagation of weeds, characterized in that calcium-containing igneous rock is calcined to transfer calcium to the surface, and that the surface of the water attached to the surface is made alkaline with calcium on the surface.
以上とする火成岩を８５０〜１３００℃で焼成してなる
請求項１に記載される雑草の繁殖を防止する敷石。2. The content of calcium oxide is 0.5% by weight.
The paving stone according to claim 1, wherein the igneous rock is fired at 850 to 1300 ° C.
砕された火成岩を焼成してなる請求項１に記載される雑
草の繁殖を防止する敷石。3. The paving stone for preventing weed propagation according to claim 1, wherein the igneous rock crushed into crushed stone having an average particle size of 1 to 20 mm is fired.
項１に記載される雑草の繁殖を防止する敷石。4. The paving stone for preventing weed propagation according to claim 1, wherein igneous rock, which is a gushing rock, is fired.
工程で発生する火成岩粉末と、コンクリートの骨材に使
用される砕石を人工的に製造する工程で、天然石を破砕
して砕石を分離したときに発生する粉末残渣とを混合し
て粒状に成形し、成形された原料粒を焼成してカルシウ
ムを表面に移行させることを特徴とする雑草の繁殖を防
止する敷石の製造方法。5. A process for artificially producing igneous rock powder generated in the step of crushing igneous rock containing calcium and crushed stone used for aggregate of concrete, wherein natural stone is crushed to separate crushed stone. A method for producing a cobblestone for preventing the propagation of weeds, characterized by mixing the resulting powder residue and forming the mixture into granules, and calcining the formed raw material particles to transfer calcium to the surface.
０〜１３００℃で焼成する請求項５に記載される雑草の
繁殖を防止する敷石の製造方法。6. A molded product of igneous rock powder and powder residue,
The method for producing a cobblestone for preventing weed propagation according to claim 5, wherein the method is calcined at 0 to 1300 ° C.
である請求項５に記載される雑草の繁殖を防止する敷石
の製造方法。7. The mixture of the igneous rock powder is 10 to 70% by weight.
The method for producing a cobblestone for preventing the propagation of weeds according to claim 5.
に成形して焼成する請求項５に記載される雑草の繁殖を
防止する敷石の製造方法。8. The method according to claim 5, wherein the igneous rock powder and the powder residue are formed into a porous state and fired.