JP2001120668A - Clean cotton for medical treatment - Google Patents
Clean cotton for medical treatmentInfo
- Publication number
- JP2001120668A JP2001120668A JP30918899A JP30918899A JP2001120668A JP 2001120668 A JP2001120668 A JP 2001120668A JP 30918899 A JP30918899 A JP 30918899A JP 30918899 A JP30918899 A JP 30918899A JP 2001120668 A JP2001120668 A JP 2001120668A
- Authority
- JP
- Japan
- Prior art keywords
- cotton
- fibers
- liquid flow
- clean
- pressure liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、医療時に皮膚を払
拭清浄化するために用いられる清浄綿に関するものであ
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a cleaning cotton used for wiping and cleaning the skin during medical treatment.
【0002】[0002]
【従来の技術】従来、医療分野において皮膚を払拭清浄
化する際、例えば、注射等を行う前に皮膚を払拭清浄化
するのに、消毒液等の薬液が含浸された脱脂綿を用いて
いる。脱脂綿は、吸水性が高く薬液をよく吸収・保持す
ること、また、肌触りが柔らかいこと、さらに天然繊維
である綿(コットン)からなるので人体に優しい等の理
由で使用されている。そして、脱脂綿を構成する繊維と
しては、日本薬局法の脱脂綿試験法で定められた純度試
験に合格した綿繊維を使用しなければならないという規
定がある。2. Description of the Related Art Conventionally, when wiping and cleaning skin in the medical field, for example, absorbent cotton impregnated with a chemical such as a disinfectant is used for wiping and cleaning the skin before performing injection or the like. Absorbent cotton is used because it has a high water absorbency, absorbs and retains a chemical solution well, has a soft touch, and is made of natural fiber cotton (cotton) and is therefore gentle on the human body. In addition, there is a rule that as a fiber constituting the absorbent cotton, a cotton fiber that has passed a purity test defined by an absorbent cotton test method of the Japanese Pharmacopoeia Law must be used.
【0003】しかし、脱脂綿は綿繊維を単に集積してな
るものであるので、皮膚の清浄化のために払拭する際、
脱脂綿より綿繊維が脱落しやすく、皮膚に綿繊維が残存
するということがあった。また、ピンセット等で脱脂綿
を摘まむ際、隣接する脱脂綿同士が表面の毛羽によって
絡まりやすいため、他の脱脂綿もまた一緒にくっついて
来たりし、作業性に劣るという問題があった。[0003] However, since absorbent cotton is simply a collection of cotton fibers, when wiping for cleansing the skin,
Cotton fibers are more likely to fall off than absorbent cotton, and cotton fibers sometimes remain on the skin. In addition, when picking cotton wool with tweezers or the like, there is a problem that since the adjacent cotton wool is easily entangled by the fluff on the surface, other cotton wool may also be stuck together, resulting in poor workability.
【0004】近年、この脱脂綿の使いやすさを向上させ
る目的で、シート状の脱脂綿を数枚重ね合わせ、エンボ
ス装置(表面凹凸を有するエンボスロールと表面平滑な
フラットロールからなる)に通し、圧縮により押さえつ
けて一体化させた清浄綿が用いられている。しかし、こ
の清浄綿は、エンボスロールの凸部にて押さえつけられ
てはいるが、払拭の際の皮膚との摩擦によって脱落繊維
が生じるものであり、また、凸部にて押さえつけられた
部分以外については、毛羽があり、隣接する清浄綿同士
はその表面毛羽により絡まりやすく、くっつきやすいも
のであった。In recent years, in order to improve the ease of use of this absorbent cotton, several sheets of absorbent cotton are stacked, passed through an embossing device (consisting of an embossing roll having surface irregularities and a flat roll having a smooth surface), and compressed. Clean cotton that is pressed down and integrated is used. However, although this clean cotton is pressed down by the protruding portion of the embossing roll, fibers that fall off due to friction with the skin at the time of wiping are generated, and the portion other than the portion pressed down by the protruding portion is generated. Had fluff, and the adjacent clean cotton was easily entangled with the surface fluff, and was easily sticked.
【0005】[0005]
【発明が解決しようとする課題】本発明は、吸水性が良
好で、表面の毛羽立ちや繊維脱落がなく、皮膚への肌触
りが柔らかい清浄綿を提供することを課題とするもので
ある。SUMMARY OF THE INVENTION It is an object of the present invention to provide a clean cotton which has good water absorption, has no fluff on the surface and does not lose fibers, and has a soft touch to the skin.
【0006】[0006]
【課題を解決するための手段】本発明者らは、前記課題
を達成すべく鋭利検討の結果、本発明に到達した。すな
わち、本発明は、主として脱脂綿からなる清浄綿であっ
て、清浄綿の構成繊維同士は高圧液体流の作用により交
絡一体化し、かつ清浄用薬液を含浸していることを特徴
とする医療清浄綿を要旨とするものである。Means for Solving the Problems The present inventors have reached the present invention as a result of sharp studies to achieve the above object. That is, the present invention is a cleaning cotton mainly composed of absorbent cotton, wherein the constituent fibers of the cleaning cotton are entangled and integrated by the action of a high-pressure liquid flow, and are impregnated with a cleaning chemical. It is the gist.
【0007】[0007]
【発明の実施の形態】次に、本発明を詳細に説明する。
本発明は、主として脱脂綿からなる清浄綿である。脱脂
綿は、脱脂処理された綿繊維である。本発明において
は、目的を達する範囲であれば、綿繊維以外の他の繊維
を混綿してもよい。Next, the present invention will be described in detail.
The present invention is a clean cotton mainly composed of absorbent cotton. The absorbent cotton is a cotton fiber that has been subjected to a debinding treatment. In the present invention, fibers other than cotton fibers may be mixed as long as the purpose is achieved.
【0008】また、本発明の清浄綿を構成する繊維とし
て、脱脂処理された綿繊維以外に、コットンリンターを
好ましく用いることができる。コットンリンターは、綿
実に残った短い繊維であって、平均繊維長が5mm以下
のものを好ましく用いることができる。 コットンリン
ターの平均繊維長が5mmを超えると、高圧液体流の作
用による移動性に劣る傾向となり、また、抄造シートを
製造するにあたり抄造時に繊維同士の絡みが生じ、繊維
が分散されず地合の均一なシートが得られない。[0008] In addition to the defatted cotton fiber, a cotton linter can be preferably used as the fiber constituting the clean cotton of the present invention. As the cotton linter, short fibers remaining in cottonseed and having an average fiber length of 5 mm or less can be preferably used. If the average fiber length of the cotton linter exceeds 5 mm, the mobility due to the action of the high-pressure liquid flow tends to be inferior, and the fibers become entangled at the time of papermaking when producing a papermaking sheet, and the fibers are not dispersed and the A uniform sheet cannot be obtained.
【0009】コットンリンターは、綿繊維のような短繊
維(通常15〜25mm程度)と比較して繊維長が非常
に短いために、高圧液体流の作用における移動性がはる
かに優れている。従って、高圧液体流処理を施した際、
低い液体流のエネルギーによっても十分に移動して、繊
維に絡みつくことができる。したがって、目付の高い清
浄綿(0.1kg/m2を超えるもの)であっても、移
動性と交絡性に優れたコットンリンターが存在している
ので、繊維同士が十分に交絡することができるため、実
用的な機械的強力を備えたものを得ることができる。さ
らに、その際の高圧液体流の圧力においても、比較的低
い水圧エネルギーで、十分に交絡させることができるの
で、コストの点からも有利である。[0009] Cotton linters have a much shorter fiber length than short fibers (usually of the order of 15 to 25 mm) such as cotton fibers, and therefore have much better mobility in the action of high pressure liquid flow. Therefore, when high-pressure liquid flow treatment is performed,
Even the energy of the low liquid flow can move well enough to get entangled in the fibers. Therefore, even with clean cotton having a high basis weight (more than 0.1 kg / m 2 ), there is a cotton linter excellent in mobility and entanglement, so that the fibers can be sufficiently entangled with each other. Therefore, a product having practical mechanical strength can be obtained. Further, even at the pressure of the high-pressure liquid flow at that time, the entanglement can be sufficiently performed with relatively low hydraulic energy, which is advantageous in terms of cost.
【0010】また、コットンリンターは、いわゆる直線
状ではなく、クリンプを有し、半円状の弧を描いた形態
を有しているため、繊維長は短いがリンター同士は絡み
やすい。また、清浄綿に嵩高性を付与することができ、
繊維間空隙が大きく保液性の高い清浄綿を得ることがで
きる。[0010] Further, since the cotton linter has a crimp and a semicircular arc shape instead of a so-called linear shape, the linters are easily entangled with each other although the fiber length is short. Also, bulkiness can be imparted to the clean cotton,
It is possible to obtain clean cotton having a large inter-fiber space and a high liquid retaining property.
【0011】本発明の清浄綿は、構成繊維同士が高圧液
体流の作用により交絡して一体化している。構成繊維同
士が絡み合うことで互いに押さえ込んでいるので、清浄
綿表面に毛羽が発生しにくい。また、皮膚を払拭した際
に受ける摩擦に対しても、表面に毛羽が発生しにくく、
また、繊維が脱落し皮膚に残存することはない。また、
繊維同士が交絡することにより一体化しているので、柔
軟性が高い。In the clean cotton of the present invention, the constituent fibers are entangled and integrated by the action of the high-pressure liquid flow. Since the constituent fibers are entangled with each other and pressed against each other, fluff is not easily generated on the surface of the clean cotton. Also, against the friction received when wiping the skin, fuzz is less likely to occur on the surface,
Also, the fibers do not fall off and remain on the skin. Also,
Since the fibers are integrated by entanglement, the flexibility is high.
【0012】本発明の清浄綿は、表裏層および内層にお
ける構成繊維同士が一様に交絡して一体化してなるもの
であってもよい。清浄綿全体が一様に交絡してなるもの
は、全体において一様な機械的強度を有するものであ
る。また、表裏層に存在する構成繊維同士の交絡が特に
緻密であり、内層に存在する繊維同士の交絡が、表裏層
に存在する繊維同士の交絡度合より低いものであっても
よい。構成繊維同士の交絡が緻密になる程、繊維間の空
隙が小さくなり、また、繊維同士が絡み合い押さえ合う
ので、毛羽立ちが少なく、摩擦に対するリントフリー性
(繊維が脱落する度合)が良好となる。内層に存在する
繊維同士の交絡度合を下げることにより、繊維間の空隙
を大きく保ち、清浄綿に含浸させた薬液の保液量を多く
することができる。The cleaning cotton of the present invention may be one in which the constituent fibers in the front and back layers and the inner layer are uniformly entangled and integrated. Those in which the entire clean cotton is uniformly entangled have uniform mechanical strength as a whole. Further, the entanglement of the constituent fibers present in the front and back layers may be particularly dense, and the entanglement of the fibers present in the inner layer may be lower than the entanglement degree of the fibers present in the front and back layers. As the entanglement of the constituent fibers becomes denser, the gap between the fibers becomes smaller, and the fibers become entangled and pressed, so that the fluff is less and the lint-free property against friction (the degree to which the fibers fall off) becomes better. By reducing the degree of entanglement between the fibers present in the inner layer, the gap between the fibers can be kept large, and the amount of the chemical solution impregnated in the clean cotton can be increased.
【0013】高圧液体流による作用とは、水を噴射孔か
ら高圧力で噴射させて得られる水流(高圧液体流)を衝
突させることをいう。具体的には、孔径0.05〜2.
0mmの噴射孔が、噴射孔間隔0.05〜10mmで一
列ないし複数列に配置した装置を用い、噴射孔から液体
を1.9〜19.6Mpaの圧力で噴射して、支持板に
載置した脱脂綿に衝突させる。支持板としては、脱脂綿
と支持板とを高圧液体流が貫通する構成のものであれば
よく、メッシュユスクリーンや有孔板を用いるとよい。
メッシュスクリーンの組織やメッシュの大きさ等を適宜
選択することによって、清浄綿の表面形態を平滑とする
他、模様等を付与することができる。また、脱脂綿内を
高圧液体流が通過するため、脱脂綿内に異物が存在した
場合、脱脂綿内を貫通する高圧液体流が異物も一緒に流
し落とすので、異物のない衛生的な清浄綿を得ることが
できる。The action by the high-pressure liquid flow means that a water flow (high-pressure liquid flow) obtained by injecting water from an injection hole at a high pressure impinges. Specifically, the pore size is 0.05-2.
Using a device in which the injection holes of 0 mm are arranged in one or a plurality of rows with an injection hole interval of 0.05 to 10 mm, the liquid is injected from the injection holes at a pressure of 1.9 to 19.6 Mpa and placed on the support plate. Collision with the absorbent cotton. As the support plate, any structure may be used as long as the high-pressure liquid flow passes through the absorbent cotton and the support plate, and a mesh screen or a perforated plate may be used.
By appropriately selecting the structure of the mesh screen, the size of the mesh, and the like, the surface morphology of the clean cotton can be smooth, and a pattern or the like can be provided. In addition, since the high-pressure liquid flow passes through the absorbent cotton, if there is a foreign substance in the absorbent cotton, the high-pressure liquid flow penetrating through the absorbent cotton also drops off the foreign substance, so that a sanitary clean cotton free of foreign substances can be obtained. Can be.
【0014】上述した表裏層の繊維同士は緻密に交絡
し、内層の繊維同士の交絡度合が低い清浄綿は、例えば
以下のようにして得ることができる。脱脂綿の片面より
高圧液体流を作用させた後、脱脂綿を反転させて、もう
一方の面より高圧液体流を作用させることにより得る。The above-described fibers of the front and back layers are densely entangled with each other, and the clean cotton having a low entanglement degree of the fibers of the inner layer can be obtained, for example, as follows. After the high-pressure liquid flow is applied from one side of the absorbent cotton, the absorbent cotton is turned over, and the high-pressure liquid flow is applied from the other side to obtain the liquid.
【0015】高圧液体流を作用させる脱脂綿は、ばらば
らの繊維が単に集積されたものである。このばらばらの
繊維に高圧の液体流を衝突させた際、液体流のエネルギ
ーは繊維の運動エネルギーに転換されて繊維が移動し、
互いに交絡して一体化する。本発明に用いる脱脂綿のよ
うな高目付(0.1kg/m2以上)のものに高圧液体
流を衝突させた場合、液体流のエネルギーは表層の繊維
が運動するために費やされ、液体流が内層に達する時に
は繊維が積極的に運動し緻密に交絡できるだけの十分な
液体流エネルギーは残っていない。さらに、液体流を衝
突させると、脱脂綿の表層面の繊維は互いに交絡して緻
密な構造が形成されるので、この緻密表層面がバリヤと
なって水流を跳ね返し液体流エネルギーを消耗し、内層
に液体流が達する時には、繊維を積極的に運動させる程
の高いエネルギーが残存していないため、内層の繊維同
士の交絡は表層ほど緻密なものとならない。引き続き、
片方の表層が緻密に交絡してなる脱脂綿を反転させて、
もう一方の面より高圧液体流を作用させることによっ
て、同様に表層面のみ緻密に交絡させて、内層の繊維同
士は交絡度合の低いものを得ることができる。Absorbent cotton subjected to a high pressure liquid stream is simply a collection of discrete fibers. When a high-pressure liquid flow collides with the discrete fibers, the energy of the liquid flow is converted into the kinetic energy of the fibers and the fibers move,
Entangled and integrated. When a high-pressure liquid stream is made to impinge on a high-weight (0.1 kg / m 2 or more) such as absorbent cotton used in the present invention, the energy of the liquid stream is consumed by the movement of the surface fibers, and When the fibers reach the inner layer, there is not enough liquid flow energy left to allow the fibers to actively move and densely entangle. Furthermore, when the liquid flow collides, the fibers on the surface layer of the absorbent cotton are entangled with each other to form a dense structure.The dense surface layer acts as a barrier and repels the water flow, consuming the liquid flow energy and depleting the liquid flow energy. When the liquid flow reaches, there is no remaining energy high enough to actively move the fibers, so that the entanglement of the fibers in the inner layer is not as dense as the surface layer. Continued
Invert the absorbent cotton that one surface layer is densely entangled with,
By applying the high-pressure liquid flow from the other surface, only the surface layer is densely entangled in the same manner, and the fibers of the inner layer can have a low entanglement degree.
【0016】本発明の清浄綿において、コットンリンタ
ーを含有させる場合は、高圧液体流を作用させる際に、
コットンリンターからなる抄造シートを用いることが好
ましい。コットンリンターからなる抄造シートは、コッ
トンリンターを主原料として、従来公知の湿式抄造法に
より得られ、コットンリンターが絡み合った状態で固定
されてなる紙様のシートであり、ある程度の形態安定性
を有するものであるので取り扱いやすく、また、地合が
良好である。When the cotton linter is contained in the clean cotton of the present invention, when the high-pressure liquid stream is applied,
It is preferable to use a sheet made of cotton linter. The papermaking sheet made of cotton linter is a paper-like sheet obtained by a conventionally known wet papermaking method using cotton linter as a main raw material, and fixed with cotton linter entangled, and has a certain degree of form stability. It is easy to handle and good in texture.
【0017】高圧液体流を作用させる際には、脱脂綿と
コットンリンターからなる抄造シートとを積層した積層
体を抄造シート側より高圧液体流を噴射させるとよい。
コットンリンターは繊維長が短いために、支持板が有す
る孔より高圧液体流とともに下方へ脱落しやすいためで
ある。高圧液体流が作用されると、コットンリンターか
らなる抄造シートは、水を吸収して膨潤するとともに、
高圧液体流の衝撃でコットンリンター相互間の絡み合い
が解け、各コットンリンターが自由に運動する。一方、
脱脂綿を構成している綿繊維もまた、自由に運動し、こ
れらの繊維同士(コットンリンター同士、綿繊維同士、
コットンリンターと綿繊維)が絡み合って全体として一
体化したものとなる。When applying the high-pressure liquid flow, it is preferable to spray a high-pressure liquid flow from the papermaking sheet side of a laminate obtained by laminating a sheet made of absorbent cotton and cotton linter.
This is because the cotton linter has a short fiber length and easily falls down with the high-pressure liquid flow from the holes of the support plate. When the high-pressure liquid flow is applied, the sheet made of cotton linter absorbs water and swells,
The entanglement between the cotton linters is released by the impact of the high-pressure liquid flow, and each cotton linter moves freely. on the other hand,
The cotton fibers that make up absorbent cotton also move freely, and these fibers (cotton linters, cotton fibers,
(Cotton linter and cotton fiber) are entangled and integrated as a whole.
【0018】また、高圧液体流を作用させる積層体とし
ては、コットンリンターからなる抄造シートの両側に脱
脂綿を積層してなる3層構造のものでもよい。The laminate to which the high-pressure liquid flow is applied may have a three-layer structure in which absorbent cotton is laminated on both sides of a sheet made of cotton linter.
【0019】コットンリンターからなる抄造シートは、
その目付が0.03〜0.1kg/m2であるのが好ま
しい。目付が0.03kg/m2未満であると、抄造シ
ートを製造するにあたり地合の均一なシートが得られな
い。一方、目付が0.1kg/m2を超えると、このコ
ットンリンターからなる抄造シートに脱脂綿を積層して
高圧液体流処理を施すに際して、コットンリンターから
なる抄造シートと脱脂綿の構成繊維とが三次元的に十分
交絡せず、このため全体としての一体化がなされにくく
なる。したがって、本発明の清浄綿に用いるコットンリ
ンターの目付は0.03〜0.1kg/m2の範囲であ
るのが好ましく、より好ましくは0.05〜0.08k
g/m2の範囲である。The sheet made of cotton linter is
It is preferable that the basis weight is 0.03 to 0.1 kg / m 2 . If the basis weight is less than 0.03 kg / m 2 , a sheet having a uniform formation cannot be obtained in producing a sheet-like sheet. On the other hand, if the basis weight exceeds 0.1 kg / m 2 , when the absorbent sheet is laminated on the paper-made sheet made of the cotton linter and subjected to high-pressure liquid flow treatment, the paper-made sheet made of the cotton linter and the constituent fibers of the absorbent cotton are three-dimensionally formed. Entanglement is not sufficient, and it is difficult for the whole to be integrated. Therefore, the basis weight of the cotton linter used for the clean cotton of the present invention is preferably in the range of 0.03 to 0.1 kg / m 2 , more preferably 0.05 to 0.08 k / m 2.
g / m 2 .
【0020】清浄綿がコットンリンターを含有する場
合、コットンリンターと脱脂綿との混合比率は、コット
ンリンター:脱脂綿=0:100〜70:30(重量
%)の範囲であるのが好ましい。コットンリンターの混
合比率が70重量%を超えると、得られる清浄綿の機械
的強力が劣る傾向となる。高圧液体処理の際に、コット
ンリンターが脱落し易く、歩留まりが悪くなり生産性に
劣る結果となる。When the clean cotton contains cotton linter, the mixing ratio of cotton linter and absorbent cotton is preferably in the range of cotton linter: absorbent cotton = 0: 100 to 70:30 (% by weight). When the mixing ratio of the cotton linter exceeds 70% by weight, the mechanical strength of the obtained clean cotton tends to be inferior. During the high-pressure liquid treatment, the cotton linter is apt to fall off, resulting in a poor yield and poor productivity.
【0021】本発明の清浄綿(薬液を含まない状態)の
目付は、0.1kg/m2以上が好ましく、より好まし
くは0.15〜0.2kg/m2である。0.1kg/
m2未満であると、清浄綿の厚みが薄いために、薬液を
保液する量が減少する傾向となる。The basis weight of the clean cotton present invention (a state free of liquid medicine) is preferably from 0.1 kg / m 2 or more, more preferably 0.15~0.2kg / m 2. 0.1kg /
If it is less than m 2 , the cleaning cotton has a small thickness, and the amount of the liquid medicine retained tends to decrease.
【0022】本発明の清浄綿の嵩密度は、130kg/
m3以下であることが好ましい。嵩密度が130kg/
m3を超えると、繊維間の空隙が少なく、薬液を保液す
る量が減少する傾向となる。The bulk density of the clean cotton of the present invention is 130 kg /
It is preferably at most m 3 . The bulk density is 130kg /
If it exceeds m 3 , the space between the fibers will be small, and the amount of holding the chemical solution tends to decrease.
【0023】本発明の清浄綿の引張強力は、50N/5
cm幅以上であることが好ましい。50N/5cm幅未
満であると、皮膚を払拭する際の摩擦力によって、形態
を維持することが困難となり使い勝手に劣り、また、脱
落繊維が発生して皮膚に残存することとなる。The tensile strength of the clean cotton of the present invention is 50 N / 5.
It is preferably at least a cm width. If the width is less than 50 N / 5 cm, it is difficult to maintain the shape due to the frictional force when wiping the skin, and it is inconvenient to use. In addition, dropped fibers are generated and remain on the skin.
【0024】本発明の清浄綿は、上述した脱脂綿の構成
繊維同士が交絡してなると共に清浄用薬液を含浸してい
る。清浄用薬液は、特に限定されるものではなく、通
常、医療分野において皮膚清浄の際に用いられているも
のを採用すればよい。The cleaning cotton of the present invention is obtained by entanglement of the constituent fibers of the above-described absorbent cotton and is impregnated with a cleaning chemical. The cleaning chemical is not particularly limited, and may be one that is usually used for cleaning the skin in the medical field.
【0025】[0025]
【実施例】次に実施例に基づき、本発明を具体的に説明
するが、本発明はこれらの実施例のみに限定されるもの
ではない。 (1)目付(kg/m2):標準状態の試料から縦10
cm×横10cmの試料片計10点を作成し、平衡水分
に至らしめた後、各試料片の重量(kg)を秤量し、得
られた値の平均値を単位面積(m2)当たりに換算して
目付(kg/m2)とした。Next, the present invention will be specifically described based on examples, but the present invention is not limited to these examples. (1) Weight (kg / m 2 ): 10 samples from standard condition
After making a total of 10 sample pieces of 10 cm × 10 cm width to reach equilibrium moisture, the weight (kg) of each sample piece was weighed, and the average value of the obtained values was measured per unit area (m 2 ). It was converted to the basis weight (kg / m 2 ).
【0026】(2)嵩密度(kg/m3):試料幅10
cm、試料長10cmの試料片を5個作成し、厚み測定
器(大栄科学精機製作所(株)製)にて0.03N/c
m2の荷重の印加により個々の試料の厚み(mm)を測
定して平均値を厚み(mm)とし、下式により得られる
値を清浄綿の嵩密度とした。 嵩密度(g/cc)=[目付(kg/m2)/厚み(m
m)]/1000(2) Bulk density (kg / m 3 ): sample width 10
cm, a sample length of 10 cm, 5 pieces were prepared, and 0.03 N / c was measured with a thickness measuring instrument (manufactured by Daiei Kagaku Seiki Seisakusho Co., Ltd.).
The thickness (mm) of each sample was measured by applying a load of m 2 , the average value was defined as the thickness (mm), and the value obtained by the following equation was defined as the bulk density of the clean cotton. Bulk density (g / cc) = [basis weight (kg / m 2 ) / thickness (m
m)] / 1000
【0027】(3)引張強力(N/5cm幅):JIS
-L-1096Aに記載の方法に準じて測定した。すなわ
ち、試料長15cm、試料幅5cmの試料片を清浄綿の
機械方向(MD)に10点作成し、各試料片毎に、清浄
綿のMD方向について、定速伸長型引張試験機(オリエ
ンテック社製テンシロンUTM−100)を用い、試料
の掴み間隔10cmとし、引張速度10cm/分で伸長
した。そして、得られた切断時荷重値(N/5cm幅)
の平均値を引張強力(N/5cm幅)とした。また、試
料は、乾燥状態(保水していない状態)と、保水率20
0重量%に保持した状態について、それぞれ用意して測
定した。(3) Tensile strength (N / 5 cm width): JIS
-Measured according to the method described in L-1096A. That is, ten test pieces having a sample length of 15 cm and a sample width of 5 cm were prepared in the machine direction (MD) of the clean cotton, and for each sample piece, a constant-speed elongation type tensile tester (Orientec) in the MD direction of the clean cotton. The sample was stretched at a pulling speed of 10 cm / min by using Tensilon UTM-100 (manufactured by TOSHIBA CORPORATION) at a gripping interval of 10 cm between samples. And the obtained cutting load value (N / 5 cm width)
Was defined as the tensile strength (N / 5 cm width). In addition, the sample was in a dry state (a state where no water was retained) and a water retention rate of 20%.
The state maintained at 0% by weight was prepared and measured.
【0028】(4)リントフリー性:清浄度クラス10
0、換気量1.9m3/分のクリーンボックス(井内盛
英堂 ラウンドクリーンブースRCB−100)内に、
測定粒径0.3μm以上、吸入空気量2.8L/分のダ
ストカウンター(ダン科学 82−3200N)を用い
て行った。幅10cm、長さ10cmの試料片を4つ折
にしたものを4枚重ねて1セットとし、これを3セット
用意した。これの試料を上述のクリーンボックスの中
で、1分間揉んだ後、さらに間をおいて1分間揉み、ダ
ストカウンターにカウントされた総数を測定し、3セッ
トの平均値を求め、下記のように評価した。 ○: 総数が40個未満であった。 × : 総数が40個を超えた。(4) Lint-free property: cleanliness class 10
0, in a clean box (Inside Seideido Round Clean Booth RCB-100) with a ventilation volume of 1.9 m 3 / min.
The measurement was performed using a dust counter (Dan Kagaku 82-3200N) having a measured particle size of 0.3 μm or more and an intake air amount of 2.8 L / min. Four sets of four specimens each having a width of 10 cm and a length of 10 cm were stacked to form one set, and three sets were prepared. After rubbing this sample in the above-mentioned clean box for 1 minute, further rub it for 1 minute, measure the total number counted in the dust counter, calculate the average value of 3 sets, and evaluated. :: The total number was less than 40. ×: The total number exceeded 40.
【0029】(5)吸水性(mm/10分):JIS−
L−1096に記載のバイレック法に準じて測定した。(5) Water absorption (mm / 10 minutes): JIS-
It was measured according to the Bilek method described in L-1096.
【0030】(6)保水率(重量%):幅2.5cm、
試料長20cmの試料片を5個作成し、あらかじめ試料
の重量を測定し、その後、蒸留水中に10分間浸漬す
る。その後、試料を取り出し、10分間吊り干した後の
重量を測定した。測定値を下記式にあてはめて保水率を
算出した。 保水率(重量%)=(Y−X)×100/X 上式において、Xは試料の重量、Yは蒸留水中に浸漬
後、吊り干した後の重量とする。(6) Water retention (weight%): width 2.5 cm,
Five sample pieces each having a sample length of 20 cm are prepared, the weight of the sample is measured in advance, and then immersed in distilled water for 10 minutes. Thereafter, the sample was taken out and weighed after hanging for 10 minutes. The measured value was applied to the following equation to calculate the water retention. Water retention (% by weight) = (Y−X) × 100 / X In the above formula, X is the weight of the sample, and Y is the weight after immersion in distilled water and hanging down.
【0031】(7)圧縮剛軟度(N):試料長が10c
m、試料幅が5cmの試料片計5点を作成し、各試料片
毎に横方向に曲げて高さが5cmの円筒状物とし、各々
その端部を接合したものを圧縮剛軟度測定試料とした。
尚、試料は保水率200重量%に保持したものを使用し
た。次いで、測定試料毎に各々その軸方向について、定
速伸長型引張試験機(オリエンテク社製テンシロンUT
M-4-1-100)を用い、圧縮速度5cm/分で圧縮
し、得られた最大荷重値(N)の平均を不織布の圧縮剛
軟度とした。この圧縮剛軟度は、値が小さいほど柔軟性
が優れることを意味する。(7) Compression bristles (N): sample length is 10c
m, a sample width of 5 cm, a total of 5 sample pieces are created, and each sample piece is bent in the lateral direction to form a 5 cm high cylindrical object, and the end of each is joined to measure the compression bending resistance. A sample was used.
The sample used was kept at a water retention of 200% by weight. Next, a constant-speed elongation type tensile tester (Tensilon UT manufactured by Orientec Co., Ltd.)
M-4-1-100), and compression was performed at a compression rate of 5 cm / min, and the average of the obtained maximum load values (N) was defined as the compression stiffness of the nonwoven fabric. The smaller the compression bending resistance, the higher the flexibility.
【0032】(8)耐摩耗性(級):学振型摩擦試験機
を用い、 JIS-L-1096の6.17.3[C法)テー
バ形法]に準じて測定した結果を目視観察し、不織布表
面の摩耗がなく毛羽立ちが認められないものを5級、不
織布表面の摩耗が激しく毛羽立ったものを1級、その間
のものを4〜2級に区分し、計5段階で評価した。な
お、往復摩擦回数を100回とした。試料は、保水率2
00重量%に保持したものを使用した。(8) Abrasion resistance (grade): Using a Gakushin type friction tester, visually observe the results measured according to JIS-L-1096 6.17.3 [Method C] Taber type method]. The nonwoven fabric surface was not abraded and no fluff was observed, and the nonwoven fabric surface was classified into Class 5, the nonwoven fabric surface with severely worn fluff was classified into Class 1, and the intermediate one was classified into Class 4 or 2, and evaluated in a total of 5 grades. The number of reciprocating friction was set to 100 times. The sample has a water retention of 2
What was kept at 00% by weight was used.
【0033】実施例1 平均繊維長25mmのコットンの晒し綿を用い、目付
0.15kg/m2のランダムカードウエブを作成し
た。このウエブを移動する100メッシュの金属製ネッ
ト上に載置し、孔径0.6mmで一列に配されたオリフ
ィスヘッドを用い、このウエブの上方50mmの位置よ
り噴射圧4Mpaの高圧液体流を噴射し予備交絡を行っ
た。引き続き、噴射圧12Mpaの高圧液体流を噴射し
交絡処理を施した。その後、反転させて、反対側より噴
射圧12Mpaの高圧液体流を噴射し、反対面も交絡処
理を施した。交絡処理後、余剰の水分を公知の水分除去
装置であるマングルにより除去し、引き続きサクション
バンド方式の乾燥機を用い90℃で乾燥処理を行った。Example 1 A random card web having a basis weight of 0.15 kg / m 2 was prepared using bleached cotton having an average fiber length of 25 mm. The web is placed on a moving 100-mesh metal net, and a high-pressure liquid flow of 4 Mpa is injected from a position 50 mm above the web using orifice heads arranged in a row with a hole diameter of 0.6 mm. Preconfounding was performed. Subsequently, a high-pressure liquid flow having an injection pressure of 12 Mpa was injected to perform a confounding process. Thereafter, the liquid was turned over, and a high-pressure liquid flow having an injection pressure of 12 Mpa was injected from the opposite side, and the opposite side was also subjected to the entanglement treatment. After the confounding treatment, excess water was removed by a mangle, which is a known water removing device, and then dried at 90 ° C. using a suction band type dryer.
【0034】実施例2 コットンリンターからなる抄造シートとして、平均繊維
長3mmからなるコットンリンターを用い、目付0.0
5kg/m2の抄造シートを製造した。一方、平均繊維
長25mmのコットンの晒し綿を用い、目付0.1g/
m2のランダムカードウエブを作成した。Example 2 As a sheet made of cotton linter, a cotton linter having an average fiber length of 3 mm was used.
A sheet of 5 kg / m 2 was produced. On the other hand, using bleached cotton having an average fiber length of 25 mm, a basis weight of 0.1 g /
you create a random card web of the m 2.
【0035】カードウエブの上に抄造シートを積層した
積層体を得、抄造シート側が上になるように積層体を移
動する100メッシュの金属製ネット上に載置し、積層
体の上方50mmの位置より噴射圧4Mpaの高圧液体
流を噴射し予備交絡を行った。引き続き、噴射圧7Mp
aの高圧液体流を噴射し交絡処理を施した。その後、反
転させて、反対側より噴射圧7Mpaの高圧液体流を噴
射し、反対面も交絡処理を施した。交絡処理後、余剰の
水分を公知の水分除去装置であるマングルにより除去
し、引き続きサクションバンド方式の乾燥機を用い90
℃で乾燥処理を行った。A laminate in which a sheet of paper is laminated on a card web is obtained, and the laminate is placed on a 100-mesh metal net which moves the laminate so that the side of the sheet of paper is facing upward, at a position 50 mm above the laminate. A high-pressure liquid flow having an injection pressure of 4 Mpa was injected to perform pre-entanglement. Subsequently, the injection pressure 7Mp
The high-pressure liquid flow of a was injected to perform the confounding treatment. Thereafter, the liquid was turned over, a high-pressure liquid flow having an injection pressure of 7 Mpa was jetted from the opposite side, and the opposite side was also subjected to entanglement processing. After the confounding treatment, excess water is removed by a mangle, which is a known water removal device, and then a suction band dryer is used to remove excess water.
A drying treatment was performed at ℃.
【0036】実施例3 実施例1において、予備交絡後の噴射水圧10Mpaと
したこと以外は、実施例1と同様に行った。Example 3 Example 3 was carried out in the same manner as in Example 1, except that the injection water pressure after the pre-entanglement was changed to 10 Mpa.
【0037】比較例 実施例1において、目付0.1kg/m2のランダムカ
ードウエブをフラットロールとエンボスロールとからな
るエンボス装置に通し、ロール温度150℃、圧着面積
率14.9%、圧着点密度21.9個/cm2、線圧4
90N/cmの条件にて部分的に熱圧着し、清浄綿を得
た。COMPARATIVE EXAMPLE In Example 1, a random card web having a basis weight of 0.1 kg / m 2 was passed through an embossing device composed of a flat roll and an embossing roll, at a roll temperature of 150 ° C., a compression area ratio of 14.9%, and a compression point. Density 21.9 / cm 2 , linear pressure 4
Partially thermocompression-bonded under the condition of 90 N / cm to obtain clean cotton.
【0038】得られた実施例1〜3、および比較例の清
浄綿(液含浸していない状態)の各物性、および保水し
た状態での各物性を測定し、表1に示した。The physical properties of the obtained clean cotton (in a state not impregnated with the liquid) and the physical properties in a state of retaining water obtained in Examples 1 to 3 and Comparative Example are shown in Table 1.
【0039】[0039]
【表1】 [Table 1]
【0040】表1からも明らかなように、実施例1〜3
のものは、いずれも構成繊維同士は高圧液体流の作用に
より交絡一体化しているため、構成繊維同士が絡み合う
ことで互いに押さえ込んでいるので、清浄綿表面に毛羽
がほとんどなく、機械的強力が高く、耐摩耗性およびリ
ントフリー性に優れたものであった。特に実施例3の清
浄綿は、内層の構成繊維同士の交絡よりも、表裏面に存
在する繊維同士がより緻密に交絡したものであり表面の
毛羽が少ないものであった。As is clear from Table 1, Examples 1 to 3 were used.
In all of the above, the constituent fibers are entangled and integrated by the action of the high-pressure liquid flow, and the constituent fibers are held together by entanglement.Therefore, there is almost no fluff on the surface of the clean cotton, and the mechanical strength is high. , Abrasion resistance and lint-free properties. In particular, the clean cotton of Example 3 was one in which the fibers present on the front and back surfaces were more closely entangled and had less fuzz on the surface than the entanglement of the constituent fibers of the inner layer.
【0041】一方、比較例のものは、圧力をかけて部分
的に圧縮したものであるので、構成繊維同士は、単に配
列しているものであるので、表面の毛羽が多く、機械的
強力が低く、耐摩耗性およびリントフリー性に劣るもの
であった。On the other hand, in the case of the comparative example, which is partially compressed by applying pressure, the constituent fibers are simply arranged, so that the surface has many fluffs and the mechanical strength is low. It was inferior in wear resistance and lint-free property.
【0042】[0042]
【発明の効果】本発明は、主として脱脂綿からなる清浄
綿であって、清浄綿の構成繊維同士は高圧液体流の作用
により交絡し、一体化していると共に清浄用薬液を含浸
しているものであるので、清浄綿の構成繊維同士が絡み
合うことで互いに押さえ込んでいるので、清浄綿表面に
毛羽が発生しにくい。したがって、清浄綿を使用する際
に、ピンセット等により摘まんだ時に隣り合う清浄綿が
くっついて来たりすることなく、作業性が良好となる。
また、皮膚を払拭した際に受ける摩擦に対しても、表面
に毛羽が発生しにくく、また、繊維が脱落し皮膚に残存
することはない。繊維同士が交絡することにより一体化
しているので、柔軟性が高く、人体に優しいものであ
る。According to the present invention, the cleaning cotton is mainly made of absorbent cotton, and the constituent fibers of the cleaning cotton are entangled and integrated by the action of a high-pressure liquid flow and are impregnated with a cleaning chemical. Since the constituent fibers of the clean cotton are entangled with each other and pressed against each other, fluff is unlikely to be generated on the clean cotton surface. Therefore, when using the clean cotton, the adjacent clean cotton does not stick together when pinched with tweezers or the like, and the workability is improved.
Also, against the friction received when the skin is wiped, fluff is unlikely to be generated on the surface, and the fibers do not fall off and remain on the skin. Since the fibers are integrated by being entangled with each other, the fibers have high flexibility and are friendly to the human body.
【0043】また、交絡手段として高圧液体流を採用し
ているため、交絡処理の際に、脱脂綿内を高圧液体流が
通過するため、脱脂綿内に異物が存在した場合であって
も、脱脂綿内を貫通する高圧液体流が異物も一緒に流し
落とすので、異物のない衛生的な清浄綿を得ることがで
きる。Further, since the high-pressure liquid flow is employed as the entanglement means, the high-pressure liquid flow passes through the cotton wool at the time of the confounding treatment. The high-pressure liquid flow penetrating through also removes foreign substances together, so that sanitary clean cotton free of foreign substances can be obtained.
フロントページの続き (72)発明者 万代 典昭 大阪府大阪市中央区久太郎町四丁目1番3 号 ユニチカ株式会社内 Fターム(参考) 2D034 CC00 4L047 AA08 AB02 BA04 CA19 CB07 CC03 DA00 Continuation of front page (72) Inventor Noriaki Bandai 4-3-1 Kutaro-cho, Chuo-ku, Osaka City, Osaka Prefecture Unitika Corporation F-term (reference) 2D034 CC00 4L047 AA08 AB02 BA04 CA19 CB07 CC03 DA00
Claims (3)
て、清浄綿の構成繊維同士は高圧液体流の作用により交
絡一体化し、かつ清浄用薬液を含浸していることを特徴
とする医療清浄綿。1. A medical cleaning cotton, which is a cleaning cotton mainly made of absorbent cotton, wherein the constituent fibers of the cleaning cotton are entangled and integrated by the action of a high-pressure liquid flow and impregnated with a cleaning chemical.
密に交絡し、内層に存在する繊維同士の交絡は、表裏層
に存在する繊維同士の交絡度合より低いことを特徴とす
る請求項1記載の医療清浄綿。2. The method according to claim 1, wherein the fibers present in the front and back layers of the clean cotton are densely entangled, and the entanglement of the fibers present in the inner layer is lower than the degree of entanglement of the fibers present in the front and back layers. Medical clean cotton according to 1.
のコットンリンターを含むことを特徴とする請求項1ま
たは2記載の医療清浄綿。3. The medical cleaning cotton according to claim 1, wherein the constituent fibers of the cleaning cotton include a cotton linter having a fiber length of 5 mm or less.