JP2001092128A - Photosensitive composition for columnar spacer and color filter for liquid crystal display device using same - Google Patents
Photosensitive composition for columnar spacer and color filter for liquid crystal display device using sameInfo
- Publication number
- JP2001092128A JP2001092128A JP26685999A JP26685999A JP2001092128A JP 2001092128 A JP2001092128 A JP 2001092128A JP 26685999 A JP26685999 A JP 26685999A JP 26685999 A JP26685999 A JP 26685999A JP 2001092128 A JP2001092128 A JP 2001092128A
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- crystal display
- display device
- photosensitive composition
- columnar spacer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、液晶表示装置に用
いるカラーフィルタに関するものであり、特に、スペー
サー機能を有する液晶表示装置用カラーフィルタの製造
に用いる柱状スペーサー用感光性組成物及びそれを用い
た液晶表示装置用カラーフィルタに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a color filter used for a liquid crystal display device, and more particularly to a photosensitive composition for a columnar spacer used for producing a color filter for a liquid crystal display device having a spacer function, and a photosensitive composition for the same. To a color filter for a liquid crystal display device.
【０００２】[0002]
【従来の技術】従来の液晶表示装置の技術に於いては、
基板間にギャップを形成するために、スペーサーと呼ば
れるガラス又は合成樹脂の透明球状体粒子（ビーズ）を
散布している。このスペーサーは透明な粒子であること
から、画素内に液晶と一諸にスペーサーが入っている
と、黒色表示時にスペーサーを介して光が漏れてしま
い、また液晶材料が封入されている基板間にスペーサー
が存在することによって、スペーサー近傍の液晶分子の
配列が乱され、この部分で光漏れを生じ、コントラスト
が低下し表示品質に悪影響を及ぼす、などの問題を有し
ている。2. Description of the Related Art In the technology of a conventional liquid crystal display device,
In order to form a gap between the substrates, transparent spherical particles (beads) of glass or synthetic resin called spacers are dispersed. Since these spacers are transparent particles, if there are any spacers in the pixel with the liquid crystal, light will leak through the spacers when displaying black, and between the substrates in which the liquid crystal material is sealed. The presence of the spacer disturbs the alignment of liquid crystal molecules near the spacer, causing light leakage at this portion, lowering contrast and adversely affecting display quality.
【０００３】このような問題を解決する技術として、例
えば、画素間上にスペーサー機能を有する突起部を形成
する方法が提案されている。図１は、このような例を示
す液晶表示装置用カラーフィルタの部分断面図である。
図１において、液晶表示装置用カラーフィルタ（１０）
は、透明基板（１１）上に、遮光層（１２）、画素状カ
ラーフィルタ層（１３）、透明導電膜（１４）が形成さ
れ、この画素状カラーフィルタ層（１３）間の透明導電
膜（１４）上にスペーサー機能を有する突起部としての
柱状スペーサー（１５）が形成されているものである。As a technique for solving such a problem, for example, a method of forming a protrusion having a spacer function between pixels has been proposed. FIG. 1 is a partial cross-sectional view of a color filter for a liquid crystal display device showing such an example.
In FIG. 1, a color filter for a liquid crystal display device (10)
A light-shielding layer (12), a pixel-like color filter layer (13), and a transparent conductive film (14) are formed on a transparent substrate (11), and a transparent conductive film (14) between the pixel-like color filter layers (13) is formed. 14) A columnar spacer (15) as a projection having a spacer function is formed thereon.
【０００４】図２は、このような液晶表示装置用カラー
フィルタ（１０）を液晶表示装置に使用した例を示す液
晶表示装置の部分断面図である。図２において、液晶表
示装置（３０）は、液晶表示装置用カラーフィルタ（１
０）と、例えば、透明基板（２１）上に透明導電膜（２
４）が形成された対向基板（２０）が貼り合わされて構
成されているものである。このような液晶表示装置（３
０）においては、上記コントラストの改善がみられるこ
とに加え、液晶表示装置としての耐衝撃性が向上するも
のとなる。FIG. 2 is a partial sectional view of a liquid crystal display device showing an example in which such a color filter (10) for a liquid crystal display device is used in a liquid crystal display device. In FIG. 2, the liquid crystal display device (30) includes a color filter (1) for a liquid crystal display device.
0) and, for example, a transparent conductive film (2) on a transparent substrate (21).
The counter substrate (20) on which 4) is formed is bonded to each other. Such a liquid crystal display device (3
In 0), in addition to the improvement of the contrast, the impact resistance of the liquid crystal display device is improved.
【０００５】液晶表示装置のカラーフィルタ（１０）と
対向基板（２０）を貼り合わせる際には、液晶表示装置
の周辺部にシール部（図示せず）を設け、カラーフィル
タ（１０）と対向基板（２０）のギャップができるだけ
平行になるようにして、上下定盤間に力を加えシール部
及び柱状スペーサーを圧着し貼り合わせるが、この柱状
スペーサー（１５）の強度が弱いとギャップが均一にな
らず、液晶表示装置としては表示品質が悪化し、例え
ば、色ムラが顕著なものとなってしまう。[0005] When the color filter (10) of the liquid crystal display device and the opposing substrate (20) are bonded together, a seal portion (not shown) is provided around the liquid crystal display device, and the color filter (10) and the opposing substrate are attached. The seal of (20) is made as parallel as possible, and a force is applied between the upper and lower platens to press and adhere the seal portion and the columnar spacer. If the strength of the columnar spacer (15) is weak, the gap becomes uniform. However, the display quality of the liquid crystal display device is deteriorated, and, for example, the color unevenness becomes remarkable.
【０００６】図３、及び図４は、このような柱状スペー
サーの強度に関連する柱状スペーサーの形状を説明する
模式図である。図３は、柱状スペーサーの平面図であ
り、図４は、図３における柱状スペーサーのＸ−Ｘ’断
面図である。図３、及び図４に示すように、柱状スペー
サの強度は、上面面積（Ｓ2 ）と下面面積（Ｓ1 ）との
比（Ｓ2 ／Ｓ1 ）が大きなものほど大きくなるものであ
る。FIG. 3 and FIG. 4 are schematic diagrams for explaining the shape of the columnar spacer in relation to the strength of such a columnar spacer. FIG. 3 is a plan view of the columnar spacer, and FIG. 4 is a cross-sectional view of the columnar spacer taken along line XX ′ in FIG. As shown in FIGS. 3 and 4, the strength of the columnar spacer increases as the ratio (S 2 / S 1 ) between the upper surface area (S 2 ) and the lower surface area (S 1 ) increases.
【０００７】[0007]
【発明が解決しようとする課題】本発明は、柱状スペー
サを設けた液晶表示装置用カラーフィルタを液晶表示装
置に使用した際に、液晶表示装置用カラーフィルタと対
向基板との貼り合わせにて、ギャップが不均一になるこ
とを防ぐために、柱状スペーサの剛性を表すヤング率を
大きくし、且つ柱状スペーサの上面面積（Ｓ2 ）と下面
面積（Ｓ1 ）との比（Ｓ2 ／Ｓ1 ）を大きくする柱状ス
ペーサの製造を可能とする柱状スペーサー用感光性組成
物を提供することを課題とするものである。また、その
柱状スペーサー用感光性組成物を用いて柱状スペーサを
設けた液晶表示装置用カラーフィルタを提供することを
課題とするものである。SUMMARY OF THE INVENTION According to the present invention, when a color filter for a liquid crystal display device provided with a columnar spacer is used for a liquid crystal display device, the color filter for the liquid crystal display device and the counter substrate are bonded together. to prevent the gap becomes uneven, the ratio of increasing the Young's modulus representing the stiffness of the columnar spacers, and the upper surface area of the columnar spacers (S 2) and the lower surface area (S 1) (S 2 / S 1) It is an object of the present invention to provide a photosensitive composition for a columnar spacer that enables the production of a columnar spacer capable of increasing the particle size. Another object of the present invention is to provide a color filter for a liquid crystal display device provided with a columnar spacer using the photosensitive composition for a columnar spacer.
【０００８】[0008]
【課題を解決するための手段】本発明は、樹脂、モノマ
ー、光重合開始剤、溶剤を主成分とする感光性組成物に
おいて、該樹脂がスチレン系樹脂であることを特徴とす
る柱状スペーサー用感光性組成物である。According to the present invention, there is provided a photosensitive composition comprising a resin, a monomer, a photopolymerization initiator and a solvent as main components, wherein the resin is a styrene resin. It is a photosensitive composition.
【０００９】また、本発明は、上記発明による柱状スペ
ーサー用感光性組成物において、前記スチレン系樹脂
が、スチレン系樹脂１００重量％に対しスチレン１０〜
８０重量％含有することを特徴とする柱状スペーサー用
感光性組成物である。The present invention also provides a photosensitive composition for a columnar spacer according to the present invention, wherein the styrene resin is 100% by weight of styrene resin and 10% of styrene.
A photosensitive composition for columnar spacers, characterized in that it contains 80% by weight.
【００１０】また、本発明は、上記発明による柱状スペ
ーサー用感光性組成物を用いて柱状スペーサーを設けた
ことを特徴とする液晶表示装置用カラーフィルタであ
る。[0010] The present invention is also a color filter for a liquid crystal display device, wherein a columnar spacer is provided using the photosensitive composition for a columnar spacer according to the above invention.
【００１１】[0011]
【発明の実施の形態】以下に本発明による柱状スペーサ
ー用感光性組成物を、その実施形態に基づいて説明す
る。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the photosensitive composition for a columnar spacer according to the present invention will be described based on its embodiments.
【００１２】本発明による柱状スペーサー用感光性組成
物は、樹脂、モノマー、光重合開始剤、溶剤を主成分と
するものであり、この樹脂がスチレン系樹脂であること
を特徴とするものである。スチレン系樹脂を含有するこ
とにより、この柱状スペーサー用感光性組成物を用いて
形成した柱状スペーサーは、そのヤング率が向上し、且
つその上面面積（Ｓ2 ）と下面面積（Ｓ1 ）との比（Ｓ
2 ／Ｓ1 ）が向上したものとなる。The photosensitive composition for a columnar spacer according to the present invention comprises a resin, a monomer, a photopolymerization initiator and a solvent as main components, and is characterized in that the resin is a styrene resin. . By containing the styrene-based resin, the columnar spacer formed by using the photosensitive composition for a columnar spacer has an improved Young's modulus and a lower surface area (S 2 ) and lower surface area (S 1 ). Ratio (S
2 / S 1 ) is improved.
【００１３】従って、本発明による柱状スペーサー用感
光性組成物を用いて形成した柱状スペーサーを有する液
晶表示装置用カラーフィルタを使用した液晶表示装置に
おいては、色ムラなどの表示品質が改善されたものとな
り、また、耐衝撃性が向上したものとなる。また、この
ような強度のある柱状スペーサーを有する液晶表示装置
用カラーフィルタは、強誘電性液晶、或いは反強誘電性
液晶を用いた液晶表示装置のようにギャップの狭い液晶
表示装置において、その効果が特に発揮されたものとな
る。Therefore, a liquid crystal display device using a color filter for a liquid crystal display device having a columnar spacer formed using the photosensitive composition for a columnar spacer according to the present invention has improved display quality such as color unevenness. And the impact resistance is improved. Further, the color filter for a liquid crystal display device having such a strong columnar spacer is effective in a liquid crystal display device having a narrow gap such as a liquid crystal display device using a ferroelectric liquid crystal or an antiferroelectric liquid crystal. Is particularly exhibited.
【００１４】スチレン系樹脂としては、例えば、スチレ
ンと，メタクリル酸（ＭＡＡ）、２−ヒドロキシエチル
メタクリレート（ＨＥＭＡ）、ブチルメタクリレート
（ＢＭＡ）、シクロヘキシルメタクリレート（ＣＨＭ
Ａ）、メタクリロイルオキシエチルイソシアネート（Ｍ
ＯＩ）を付加した２−ヒドロキシエチルメタクリレート
（ＭＯＩ−ＨＥＭＡ）などのアクリル系モノマーとの共
重合物があげられる。この共重合物であるスチレン系樹
脂に含有するスチレンは、スチレン系樹脂１００重量％
に対しスチレン１０〜８０重量％含有することが好まし
い。スチレンがこの範囲に含有することにより、得られ
る柱状スペーサーのヤング率は十分に向上したものとな
り、また、上面面積（Ｓ2 ）と下面面積（Ｓ1 ）との比
（Ｓ 2 ／Ｓ1 ）が十分に向上したものとなる。スチレン
が１０重量％以下の含有量であると、ヤング率及び上面
面積（Ｓ2 ）と下面面積（Ｓ1 ）との比（Ｓ2 ／Ｓ1 ）
が十分に向上せず、また、スチレンが８０重量％以上の
含有量であると、柱状スペーサー用感光性組成物の塗布
性が悪くなる。Examples of the styrene resin include styrene
And methacrylic acid (MAA), 2-hydroxyethyl
Methacrylate (HEMA), butyl methacrylate
(BMA), cyclohexyl methacrylate (CHM)
A), methacryloyloxyethyl isocyanate (M
OI) -added 2-hydroxyethyl methacrylate
(MOI-HEMA) and other acrylic monomers
And polymers. Styrene tree which is this copolymer
Styrene contained in fat is 100% by weight of styrene resin
Preferably contains 10 to 80% by weight of styrene
No. It can be obtained by containing styrene in this range.
The Young's modulus of the columnar spacers has been sufficiently improved.
And the top surface area (STwo) And lower surface area (S1) And ratio
(S Two/ S1) Is sufficiently improved. styrene
Is less than 10% by weight, the Young's modulus and the upper surface
Area (STwo) And lower surface area (S1) And the ratio (STwo/ S1)
Is not sufficiently improved, and the content of styrene is 80% by weight or more.
Content, the application of the photosensitive composition for columnar spacers
Worse.
【００１５】柱状スペーサー用感光性組成物を構成する
スチレン系樹脂は、柱状スペーサー用感光性組成物１０
０重量％に対し１５〜３０重量％、モノマーは、柱状ス
ペーサー用感光性組成物１００重量％に対し５〜２０重
量％、光重合開始剤は、柱状スペーサー用感光性組成物
１００重量％に対し０．０５〜５．０重量％、溶剤は、
柱状スペーサー用感光性組成物１００重量％に対し６０
〜７５重量％であることが好ましい。また、柱状スペー
サー用感光性組成物の固形分は、１０〜４０％であるこ
とが好ましい。The styrenic resin constituting the photosensitive composition for columnar spacers is composed of the photosensitive composition 10 for columnar spacers.
15 to 30% by weight based on 0% by weight, monomer is 5 to 20% by weight based on 100% by weight of the photosensitive composition for a columnar spacer, and photopolymerization initiator is based on 100% by weight of the photosensitive composition for a columnar spacer. 0.05-5.0% by weight, the solvent is
60 per 100% by weight of the photosensitive composition for columnar spacers
Preferably it is ~ 75% by weight. The solid content of the photosensitive composition for a columnar spacer is preferably 10 to 40%.
【００１６】[0016]
【実施例】＜実施例１＞ （柱状スペーサー用感光性組成物の調製）以下の組成に
て柱状スペーサー用感光性組成物を調製した。 ・スチレン系樹脂 （スチレン系樹脂、大阪有機化学（株）製、ＰＬＡ１１８） ・・・・・１７重量％ ・スチレン ・・・３６重量％ ・メタクリル酸（ＭＡＡ） ・・・１５重量％ ・２−ヒドロキシエチルメタクリレート（ＨＥＭＡ） ・・・１２重量％ ・メタクリロイルオキシエチルイソシアネート付加２−ヒドロキシエチル メタクリレート（ＭＯＩ−ＨＥＭＡ） ・・・３７重量％ ・モノマー ３官能モノマー （大阪有機化学（株）製、ＰＥＴ３Ａ）・・・・・ ４重量％ ６官能モノマー （大阪有機化学（株）製、ＵＡ−ＤＰＨ）・・・・ ４重量％ ・光重合開始剤 （アセトフェノン系、チバガイギー社製、ＩＲＧ３６９） ・・・・・ ２重量％ ・溶剤 プロピレングリコールモノメチルエーテルアセテート ・・・・・７３重量％ 尚、得られた柱状スペーサー用感光性組成物の固形分は
１５％であった。EXAMPLES <Example 1> (Preparation of photosensitive composition for columnar spacer) A photosensitive composition for columnar spacer was prepared with the following composition. Styrene resin (Styrene resin, PLA118, manufactured by Osaka Organic Chemical Co., Ltd.) 17% by weight Styrene 36% by weight Methacrylic acid (MAA) 15% by weight 2- Hydroxyethyl methacrylate (HEMA) ... 12% by weight-Methacryloyloxyethyl isocyanate-added 2-hydroxyethyl methacrylate (MOI-HEMA) ... 37% by weight-Monomer trifunctional monomer (PET3A, manufactured by Osaka Organic Chemical Co., Ltd.) 4% by weight 6-functional monomer (UA-DPH, manufactured by Osaka Organic Chemical Co., Ltd.) 4% by weight Photopolymerization initiator (acetophenone, IRG369, manufactured by Ciba Geigy) 2% by weight Solvent propylene glycol monomethyl ether acetate 73% by weight Solids of the columnar spacers photosensitive composition was 15%.
【００１７】（柱状スペーサーの作製）上記柱状スペー
サー用感光性組成物を用いて、下面面積（Ｓ1 ）が１６
μｍ×２２μｍ、厚みが０．４５μｍの柱状スペーサー
を形成し反強誘電性液晶表示装置用カラーフィルタとし
た。形成した柱状スペーサーは、ヤング率が約１．７×
１０5 （Ｎ／ｃｍ2 ）、上面面積（Ｓ2 ）と下面面積
（Ｓ1 ）との比（Ｓ2 ／Ｓ 1 ）が約８４．６％のもので
あった。結果を表１に示す。(Production of Columnar Spacer)
The lower surface area (S1) Is 16
μm × 22μm, 0.45μm thick columnar spacer
To form a color filter for antiferroelectric liquid crystal display
Was. The formed columnar spacer has a Young's modulus of about 1.7 ×.
10Five(N / cmTwo), Top surface area (STwo) And bottom surface area
(S1) And the ratio (STwo/ S 1) Is about 84.6%
there were. Table 1 shows the results.
【００１８】[0018]
【表１】 [Table 1]
【００１９】＜比較例１＞ （柱状スペーサー用感光性組成物の調製）以下の組成に
て柱状スペーサー用感光性組成物を調製した。比較例１
においては、樹脂として従来から用いられてきたアクリ
ル系樹脂を、また、モノマーとして従来から用いられて
きたジペンタエリスリトールヘキサアクリレート（ＤＰ
ＨＡ）を用いた。 ・アクリル系樹脂 ・・・・・１７重量％ ・メタクリル酸（ＭＡＡ） ・・・２０重量％ ・２−ヒドロキシエチルメタクリレート（ＨＥＭＡ） ・・・１２重量％ ・ブチルメタクリレート（ＢＭＡ） ・・・２０重量％ ・シクロヘキシルメタクリレート（ＣＨＭＡ） ・・・１１重量％ ・メタクリロイルオキシエチルイソシアネート付加２−ヒドロキシエチル メタクリレート（ＭＯＩ−ＨＥＭＡ） ・・・３７重量％ ・モノマー （ジペンタエリスリトールヘキサアクリレート（ＤＰＨＡ）、 東亜合成（株）製、Ｍ−４００） ・・・・・ ８重量％ ・光重合開始剤 （アセトフェノン系、チバガイギー社製、ＩＲＧ３６９） ・・・・・ ２重量％ ・溶剤 プロピレングリコールモノメチルエーテルアセテート ・・・・・７３重量％ 尚、得られた柱状スペーサー用感光性組成物の固形分は
１５％であった。<Comparative Example 1> (Preparation of photosensitive composition for columnar spacer) A photosensitive composition for columnar spacer was prepared with the following composition. Comparative Example 1
In the above, an acrylic resin conventionally used as a resin and a dipentaerythritol hexaacrylate (DP) conventionally used as a monomer are used.
HA) was used. · Acrylic resin · · · · · 17% by weight · Methacrylic acid (MAA) · · · 20% by weight · 2-hydroxyethyl methacrylate (HEMA) · · · 12% by weight · Butyl methacrylate (BMA) · · · 20% by weight %-Cyclohexyl methacrylate (CHMA) ... 11% by weight-Methacryloyloxyethyl isocyanate-added 2-hydroxyethyl methacrylate (MOI-HEMA) ... 37% by weight-Monomer (dipentaerythritol hexaacrylate (DPHA), Toa Gosei ( 8% by weight-Photopolymerization initiator (acetophenone, IRG369, Ciba-Geigy)-2% by weight-Solvent Propylene glycol monomethyl ether acetate ...・ 73% by weight The obtained columnar shape The solid content of the photosensitive composition for a spacer was 15%.
【００２０】（柱状スペーサーの作製）上記柱状スペー
サー用感光性組成物を用いて、下面面積（Ｓ1 ）が１６
μｍ×２２μｍ、厚みが０．４５μｍの柱状スペーサー
を形成し反強誘電性液晶表示装置用カラーフィルタとし
た。形成した柱状スペーサーは、上面面積（Ｓ2 ）と下
面面積（Ｓ1 ）との比（Ｓ2 ／Ｓ1 ）が約３８％、ヤン
グ率が約１．５×１０5（Ｎ／ｃｍ2 ）のものであっ
た。結果を表１に示す。(Preparation of Columnar Spacer) Using the above photosensitive composition for columnar spacer, the lower surface area (S 1 ) was 16
A columnar spacer having a size of μm × 22 μm and a thickness of 0.45 μm was formed to obtain a color filter for an antiferroelectric liquid crystal display device. The ratio of the upper surface area (S 2 ) to the lower surface area (S 1 ) (S 2 / S 1 ) is about 38%, and the Young's modulus is about 1.5 × 10 5 (N / cm 2 ). It was. Table 1 shows the results.
【００２１】[0021]
【発明の効果】本発明は、樹脂、モノマー、光重合開始
剤、溶剤を主成分とする感光性組成物において、樹脂が
スチレン系樹脂であるので、この柱状スペーサー用感光
性組成物を用いて液晶表示装置用カラーフィルタに形成
した柱状スペーサは、ヤング率が大きく、且つ上面面積
（Ｓ2 ）と下面面積（Ｓ1 ）との比（Ｓ2 ／Ｓ1 ）が大
きな柱状スペーサとなる。また、このような柱状スペー
サを有する液晶表示装置用カラーフィルタを用いた液晶
表示装置は、柱状スペーサーの強度が強いのでギャップ
が不均一にならず、色ムラなどの発生で表示品質が悪化
することはない。According to the present invention, in a photosensitive composition containing a resin, a monomer, a photopolymerization initiator and a solvent as main components, the resin is a styrene-based resin. columnar spacers formed on the color filter for a liquid crystal display device has a large Young's modulus, and the ratio of the top surface area and (S 2) and the lower surface area (S 1) (S 2 / S 1) is a major columnar spacers. Further, in a liquid crystal display device using a color filter for a liquid crystal display device having such columnar spacers, the strength of the columnar spacers is high, so that the gap does not become non-uniform, and the display quality deteriorates due to the occurrence of color unevenness. There is no.
【図１】液晶表示装置用カラーフィルタの部分断面図で
ある。FIG. 1 is a partial sectional view of a color filter for a liquid crystal display device.
【図２】液晶表示装置用カラーフィルタを液晶表示装置
に使用した例を示す液晶表示装置の部分断面図である。FIG. 2 is a partial cross-sectional view of a liquid crystal display device showing an example in which a color filter for a liquid crystal display device is used in a liquid crystal display device.
【図３】柱状スペーサーの平面図である。FIG. 3 is a plan view of a columnar spacer.
【図４】柱状スペーサーのＸ−Ｘ’断面図である。FIG. 4 is a cross-sectional view of the columnar spacer taken along line X-X '.
１０…液晶表示装置用カラーフィルタ １１、２１…透明基板 １２…遮光層 １３…画素状カラーフィルタ層 １４、２４…透明導電膜 １５…柱状スペーサー ２０…対向基板 ３０…液晶表示装置 Ｓ1 …柱状スペーサの下面面積 Ｓ2 …柱状スペーサの上面面積10 ... liquid crystal display device for color filters 11, 21 ... transparent substrate 12 ... shielding layer 13 ... pixelated color filter layer 14, 24 ... transparent conductive film 15 ... columnar spacers 20 ... counter substrate 30 ... liquid crystal display device S 1 ... columnar spacers Lower surface area of S 2 ... Upper surface area of columnar spacer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｇ０３Ｆ 7/023 ５１１ Ｇ０３Ｆ 7/023 ５１１ Ｆターム(参考） 2H025 AA00 AB13 AC01 AD01 BC34 BC43 BJ07 CB16 2H048 BA45 BA48 BB08 BB14 2H089 LA09 MA07X NA14 NA17 QA14 RA14 TA12 2H091 FA02Y GA08 LA15 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) G03F 7/023 511 G03F 7/023 511 F-term (Reference) 2H025 AA00 AB13 AC01 AD01 BC34 BC43 BJ07 CB16 2H048 BA45 BA48 BB08 BB14 2H089 LA09 MA07X NA14 NA17 QA14 RA14 TA12 2H091 FA02Y GA08 LA15
Claims (3)
成分とする感光性組成物において、該樹脂がスチレン系
樹脂であることを特徴とする柱状スペーサー用感光性組
成物。1. A photosensitive composition for a columnar spacer, wherein the photosensitive composition mainly comprises a resin, a monomer, a photopolymerization initiator and a solvent, wherein the resin is a styrene resin.
００重量％に対しスチレン１０〜８０重量％含有するこ
とを特徴とする請求項１記載の柱状スペーサー用感光性
組成物。2. The method according to claim 1, wherein the styrene resin is a styrene resin.
2. The photosensitive composition for a columnar spacer according to claim 1, wherein styrene is contained in an amount of 10 to 80% by weight based on 00% by weight.
サー用感光性組成物を用いて柱状スペーサーを設けたこ
とを特徴とする液晶表示装置用カラーフィルタ。3. A color filter for a liquid crystal display device, wherein a columnar spacer is provided using the photosensitive composition for a columnar spacer according to claim 1.