JP2001047734A - Image recording medium - Google Patents

Image recording medium

Info

Publication number
JP2001047734A
JP2001047734A JP11223918A JP22391899A JP2001047734A JP 2001047734 A JP2001047734 A JP 2001047734A JP 11223918 A JP11223918 A JP 11223918A JP 22391899 A JP22391899 A JP 22391899A JP 2001047734 A JP2001047734 A JP 2001047734A
Authority
JP
Japan
Prior art keywords
ink
recording medium
receiving layer
support layer
image recording
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP11223918A
Other languages
Japanese (ja)
Inventor
Yasuyuki Takeda
康之 武田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Innovative Properties Co
Original Assignee
3M Innovative Properties Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Co filed Critical 3M Innovative Properties Co
Priority to JP11223918A priority Critical patent/JP2001047734A/en
Priority to KR1020027001621A priority patent/KR20020019966A/en
Priority to AU67601/00A priority patent/AU6760100A/en
Priority to BR0012911-9A priority patent/BR0012911A/en
Priority to CA002378358A priority patent/CA2378358A1/en
Priority to PCT/US2000/021507 priority patent/WO2001010650A1/en
Priority to CN00811289A priority patent/CN1368917A/en
Priority to EP00955387A priority patent/EP1216155A1/en
Publication of JP2001047734A publication Critical patent/JP2001047734A/en
Priority to US10/476,334 priority patent/US20050025912A1/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To provide an ink image recording medium capable of accelerating quick-drying by realizing excellent color developability, and effectively preventing transfer of a coloring component in an ink to fine holes of the medium. SOLUTION: In the image recording medium comprising a support layer containing gas permeable micropores, and an ink image receiving layer disposed on a surface of the support layer and containing aqueous soluble salt or the like as a coagulant, the receiving layer further contains an organic polymer, and the surface of the support layer and the micropores are hydrophilized by a surfactant.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、画像記録媒体に関
し、さらに詳しく述べると、インクジェット記録法等の
印刷方法により、インク像を記録するために用いられる
画像記録媒体に関する。本発明は、特に、高いインク乾
燥性（速乾性）と、高い耐水性とを有する画像を形成あ
るいは記録することが可能なインク像記録媒体に関す
る。The present invention relates to an image recording medium, and more particularly, to an image recording medium used for recording an ink image by a printing method such as an ink jet recording method. The present invention particularly relates to an ink image recording medium capable of forming or recording an image having high ink drying properties (quick drying properties) and high water resistance.

【０００２】[0002]

【従来の技術】これまで、インクジェット記録紙等のイ
ンク像記録媒体として、複数個の通気性微細孔を含む、
すなわち、多孔質の支持体層を有するものが、有用であ
ることは知られている。たとえば、国際公開公報第ＷＯ
９９／０３６８５号には、多孔質フィルムを含む支持体
層の微細孔内に、界面活性剤と多価金属塩とを含有する
インク像記録媒体が開示されている。多価金属塩は、支
持体層の微細孔の内壁（内面）を界面活性剤により親水
化処理した後、多価金属塩を含む液体を塗布することに
より、微細孔内に固定される。インクは、この支持体層
の表面に定着する様に印刷（記録）される。しかしなが
ら、このインク像記録媒体の場合、インクに含まれる顔
料の一部が、記録媒体の表面に留まらずに微細孔内にま
で移行するので、発色性や速乾性の改善が困難である。2. Description of the Related Art Hitherto, as an ink image recording medium such as an ink jet recording paper, a plurality of air permeable fine holes have been used.
That is, those having a porous support layer are known to be useful. For example, International Publication No. WO
No. 99/03685 discloses an ink image recording medium containing a surfactant and a polyvalent metal salt in micropores of a support layer containing a porous film. The polyvalent metal salt is fixed in the micropores by applying a liquid containing a polyvalent metal salt after the inner wall (inner surface) of the micropores of the support layer is hydrophilized with a surfactant. The ink is printed (recorded) so as to be fixed on the surface of the support layer. However, in the case of this ink image recording medium, a part of the pigment contained in the ink migrates to the inside of the micropores without remaining on the surface of the recording medium, so that it is difficult to improve the coloring property and the quick drying property.

【０００３】また、米国特許第５，６０５，７５０号明
細書には、非水溶性の充填粒子（たとえば、シリカ）が
分散されて含まれる多孔質支持体層を用い、その多孔質
支持体層の表面に、多孔質の擬似ベーマイトからなる画
像形成層（インク受容層）を配置したインク像記録媒体
が開示されている。支持体層の具体例としては、ＰＰＧ
インダストリー社製の多孔性延伸樹脂フィルム、「Tesl
in」（商標）が挙げられている。この記録媒体では、支
持体層の上に上記の様な画像形成層を設けたので、発色
性の高い画像の形成および記録が容易に実現可能であ
る。しかしながら、速乾性においては、改善の余地が残
されている。Further, US Pat. No. 5,605,750 discloses a porous support layer containing a water-insoluble filler particle (eg, silica) dispersed therein. Discloses an ink image recording medium in which an image forming layer (ink receiving layer) made of porous pseudo-boehmite is disposed on the surface of the ink image recording medium. Specific examples of the support layer include PPG
Industry's porous stretched resin film, "Tesl
in "(trademark). In this recording medium, since the image forming layer as described above is provided on the support layer, it is possible to easily form and record an image having high color developing properties. However, quick drying leaves room for improvement.

【０００４】上記したインク像記録媒体において、支持
体層の上に配置されるインク受容層は、ポリマーを含有
する層でも良い。たとえば、この場合のインク受容層
は、ポリマーと、無機質ピグメントとを含有する層であ
る。無機質ピグメントは、インク受容層に対して多孔性
を付与するためのもので、通常、多孔質合成シリカ、ア
ルミナヒドロゾル等の非水溶性粒子が用いられる。ま
た、ポリマーは、たとえば、水溶性ポリマー、カチオン
変性ポリマー（ポリウレタン等）などである。特に、カ
チオン変性ポリマーは、インクセット性を高めるのに有
利であり、発色性の高い画像の実現が容易である。しか
しながら、この様なインク受容層でも、やはり、速乾性
においては改善の余地が残されている。In the ink image recording medium described above, the ink receiving layer disposed on the support layer may be a layer containing a polymer. For example, the ink receiving layer in this case is a layer containing a polymer and an inorganic pigment. The inorganic pigment is for imparting porosity to the ink receiving layer, and usually uses water-insoluble particles such as porous synthetic silica and alumina hydrosol. Further, the polymer is, for example, a water-soluble polymer, a cation-modified polymer (eg, polyurethane). In particular, a cation-modified polymer is advantageous for enhancing the ink setting property, and it is easy to realize an image having high color development. However, such an ink receiving layer still has room for improvement in quick drying.

【０００５】[0005]

【発明が解決しようとする課題】前述の様に、インク像
記録媒体において発色性や画質を高めるためには、多孔
質の支持体層に加えて、インク受容層を設けるのが有利
である。また、インク乾燥性（速乾性）を高めるには、
インク受容層の通気性、すなわち、多孔性を損なわない
様にするのが有利である。しかしながら、インク受容層
の多孔性を改善しても、実際には、インク中の着色成
分、特に顔料がインク受容層、またはインク受容層およ
び支持体層の内部の微細孔まで移行し、印刷後の乾燥性
が低下する傾向が見られた。As described above, it is advantageous to provide an ink receiving layer in addition to the porous support layer in order to improve the color developability and image quality of the ink image recording medium. Also, to improve the ink drying property (quick drying property),
It is advantageous not to impair the air permeability, ie the porosity, of the ink receiving layer. However, even if the porosity of the ink receiving layer is improved, in practice, the coloring components, particularly the pigment, in the ink migrate to the ink receiving layer or the micropores inside the ink receiving layer and the support layer, and after printing, There was a tendency that the drying property of the powder decreased.

【０００６】したがって、本発明の目的は、優れた発色
性を実現するとともに、インク中の着色成分（顔料等）
が、媒体内部の微細孔まで移行することを効果的に防止
し、速乾性を高めることが可能な、新規なインク像記録
媒体を提供することにある。Accordingly, it is an object of the present invention to realize excellent color developing properties and to provide coloring components (such as pigments) in ink.
However, an object of the present invention is to provide a novel ink image recording medium capable of effectively preventing migration to micropores inside the medium and improving quick drying.

【０００７】[0007]

【課題を解決するための手段】本発明によれば、上記課
題を解決する手段として、（ｉ）通気性微細孔を含む支
持体層と、（ii）その支持体層の表面に配置され、凝集
剤として水溶性塩類を含むインク像受容層とを有してな
る画像記録媒体において、前記インク像受容層が有機ポ
リマーをさらに含有し、かつ前記支持体層の表面および
前記微細孔が、界面活性剤により親水化処理されている
ことを特徴とする、画像記録媒体が提供される。According to the present invention, as means for solving the above-mentioned problems, there are provided (i) a support layer containing air-permeable fine pores, and (ii) a support layer disposed on the surface of the support layer, In an image recording medium having an ink image receiving layer containing a water-soluble salt as a coagulant, the ink image receiving layer further contains an organic polymer, and the surface of the support layer and the micropores are formed at an interface. An image recording medium characterized by being subjected to a hydrophilic treatment with an activator is provided.

【０００８】[0008]

【作用】本発明の画像記録媒体は、親水化処理された通
気性微細孔を含む支持体層の上に、インク像受容層とし
て、有機ポリマーと、凝集剤としての水溶性の塩類（有
機酸または無機酸の塩類）とを含む層を配置したことを
特徴とする。上記の様な凝集剤は、記録媒体の表面にイ
ンクが印刷等により適用された時、顔料等の着色成分を
すばやくインク像受容層の表面で凝集させる作用を有し
ている。したがって、顔料等が、記録媒体内部の微細孔
内まで移行することを効果的に防止し、速乾性を高める
ことができる。また、本発明のインク像受容層は、凝集
剤に加えて有機ポリマーを含有する。有機ポリマーは、
凝集剤をインク像受容層内に効果的に固定するバインダ
として機能し、その結果、上記の様な凝集作用と、ポリ
マーの結着作用との相乗効果により、インク像受容層の
表面に定着されたインク像の耐水性をさらに効果的に高
めることができる。このようなバインダ作用をいっそう
効果的に高めるためには、カチオン変性ポリウレタン等
の水分散性のカチオン変性ポリマーが好適である。The image recording medium of the present invention comprises an organic polymer as an ink image receiving layer and a water-soluble salt (organic acid) as a coagulant, on a support layer containing air-permeable micropores subjected to hydrophilic treatment. Or a salt containing an inorganic acid). The aggregating agent as described above has an action of rapidly aggregating coloring components such as pigments on the surface of the ink image receiving layer when the ink is applied to the surface of the recording medium by printing or the like. Therefore, it is possible to effectively prevent the pigment and the like from migrating into the fine pores inside the recording medium, and to improve the quick drying property. Further, the ink image receiving layer of the present invention contains an organic polymer in addition to the coagulant. Organic polymers are
It functions as a binder to effectively fix the flocculant in the ink image receiving layer. As a result, the flocculant is fixed to the surface of the ink image receiving layer by the synergistic effect of the above flocculating action and the binding action of the polymer. The water resistance of the resulting ink image can be more effectively increased. In order to more effectively enhance such a binder effect, a water-dispersible cation-modified polymer such as a cation-modified polyurethane is suitable.

【０００９】支持体層の通気性は、ガレー透気度を用い
てそれを規定すれば、通常１０〜３，０００秒／１００
ml、好適には５０〜２，５００秒／１００ml、特に好適
には１００〜２，０００秒／１００mlの範囲である。な
お、ここで言う「ガレー透気度」は、ＪＩＳ Ｐ−８１
１７−１９８０に準拠し、ガレー透気度試験機を用いて
測定した値であり、通常１００mlの体積の空気が通過す
るのに要する時間で表わされる。The air permeability of the support layer is usually from 10 to 3,000 seconds / 100, if it is defined by using the galley air permeability.
ml, preferably 50 to 2,500 seconds / 100 ml, particularly preferably 100 to 2,000 seconds / 100 ml. The “galley air permeability” mentioned here is based on JIS P-81.
This is a value measured using a galley air permeability tester according to 17-1980, and is usually expressed by the time required for passing a volume of 100 ml of air.

【００１０】上記した水溶性の塩類の凝集作用は、それ
らの塩類がイオン化されることにより効果的に高めるこ
とができる。したがって、画像記録媒体（インク像受容
層）の表面に適用されるインクは、水を含有するイン
ク、すなわち、水性インクであるのが好適である。ま
た、塩類が「水溶性」（水に可溶な性質を有すること）
であるということは、水と反応して、イオン化学種を発
生可能であることを意味する。なお、溶解度を、２０℃
の水１００ｇに溶解する量で表せば、通常０．００１〜
１００ｇ、好適には０．０１〜９０ｇ、特に好適には
０．１〜８０ｇである。この様な塩類としては、無機酸
の多価金属塩が好適である。これらの塩類は、凝集作用
が比較的高く、速乾性と、定着インク像の耐水性とを同
時に高める効果にすぐれている。The aggregating action of the above-mentioned water-soluble salts can be effectively enhanced by ionizing those salts. Therefore, the ink applied to the surface of the image recording medium (ink image receiving layer) is preferably an ink containing water, that is, an aqueous ink. In addition, salts are "water-soluble" (have the property of being soluble in water)
Means that it can react with water to generate ionic species. In addition, the solubility was 20 ° C.
In terms of the amount dissolved in 100 g of water,
100 g, preferably 0.01 to 90 g, particularly preferably 0.1 to 80 g. As such salts, polyvalent metal salts of inorganic acids are suitable. These salts have a relatively high aggregating effect, and are excellent in the effect of simultaneously increasing the quick drying property and the water resistance of the fixed ink image.

【００１１】インク像受容層の厚さは広い範囲にわたっ
て変更することができるが、インク像のにじみを容易に
防止するには比較的厚い方が好適である。この様な観点
から、インク像受容層の厚さは、通常５〜２００μｍ、
好適には１０〜１００μｍである。なお、厚さの上限は
インク像の特性には影響しないものの、画像記録媒体の
厚みを不要に厚くするおそれがあるので、上記の様な値
が好適である。Although the thickness of the ink image receiving layer can be changed over a wide range, it is preferable that the thickness is relatively large in order to easily prevent the bleeding of the ink image. From such a viewpoint, the thickness of the ink image receiving layer is usually 5 to 200 μm,
Preferably, it is 10 to 100 μm. The upper limit of the thickness does not affect the characteristics of the ink image, but may unnecessarily increase the thickness of the image recording medium. Therefore, the above value is preferable.

【００１２】また、支持体層の表面およびその内部の微
細孔は、界面活性剤により親水化処理される。インク像
の速乾性をさらに効果的に高めるためである。親水化処
理は、インク像受容層を形成するための塗布液に界面活
性剤を添加し、その塗布液を支持体層の表面に塗布し、
インク像受容層の形成と同時に行うこともできる。しか
しながら、インク像受容層の形成前に親水化処理を行う
のが好適である。すなわち、まず、支持体層の表面に界
面活性剤を含む液体を塗布し、または支持体層をその液
体に含浸し、親水化処理を行った後、親水化処理された
支持体層の表面に、ポリマーと凝集剤とを含む塗布液を
塗布すること等により、インク像受容層を形成するのが
良い。この様にすれば、ポリマーを含む塗布液を支持体
層上に塗布する際に、支持体層の微細孔の空気を効果的
に追い出し、気泡欠陥のないインク像受容層を形成する
のが容易であり、速乾性の高い画像記録媒体を、いっそ
う容易に製造できる。Further, the surface of the support layer and the fine pores inside the support layer are subjected to a hydrophilic treatment with a surfactant. This is because the quick drying property of the ink image is more effectively improved. Hydrophilic treatment, a surfactant is added to a coating solution for forming an ink image receiving layer, the coating solution is applied to the surface of the support layer,
It can be carried out simultaneously with the formation of the ink image receiving layer. However, it is preferable to perform a hydrophilic treatment before forming the ink image receiving layer. That is, first, a liquid containing a surfactant is applied to the surface of the support layer, or the support layer is impregnated with the liquid, and subjected to a hydrophilization treatment, and then applied to the surface of the hydrophilized support layer. The ink image receiving layer is preferably formed by applying a coating solution containing a polymer and a coagulant. In this way, when a coating solution containing a polymer is applied onto the support layer, the air in the micropores of the support layer is effectively expelled, and it is easy to form an ink image receiving layer without bubble defects. Therefore, an image recording medium having high quick-drying property can be manufactured more easily.

【００１３】[0013]

【発明の実施の形態】以下、本発明の好ましい実施の形
態を、特に本発明の画像記録媒体の構成要素のそれぞれ
および使用方法を参照して説明する。支持体層 支持体層は、複数個の通気性微細孔を含むフィルムまた
はシート（以下、「多孔質フィルム」と総称する。）を
含んでなる。これにより、記録媒体に適用されるインク
中の水等の溶媒（分散媒）をいち早く吸収し、速乾性を
高めることができる。多孔質フィルムは、上記の様な効
果を奏するものであれば特に限定されず、従来からイン
ク像記録媒体において基材として使用されているものが
使用できる。たとえば、前述のＰＰＧインダストリー社
製の多孔性延伸樹脂フィルム、「Teslin」（商標）など
を含む各種の延伸樹脂フィルムが好適である。BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, preferred embodiments of the present invention will be described with particular reference to each of the components of the image recording medium of the present invention and how to use them. Support Layer The support layer comprises a film or sheet containing a plurality of air-permeable micropores (hereinafter, collectively referred to as “porous film”). As a result, a solvent (dispersion medium) such as water in the ink applied to the recording medium can be quickly absorbed and the quick drying property can be improved. The porous film is not particularly limited as long as it has the above-mentioned effects, and those conventionally used as a substrate in an ink image recording medium can be used. For example, various stretched resin films including the aforementioned porous stretched resin films manufactured by PPG Industries and “Teslin” (trademark) are suitable.

【００１４】樹脂フィルムの材料の具体例としては、ポ
リエチレン、ポリプロピレン、ポリメチルペンテン−１
等のポリオレフィン、ポリ塩化ビニル、ポリ塩化ビニリ
デン、ポリスチレン、スチレン−ブタジエン−アクリル
ニトリル共重合体、ナイロン６、ナイロン６６等のポリ
アミド、共重合ポリアミド、ポリカーボネート、ポリメ
チルメタクリレート、ポリスルホン、ポリエチレンテレ
フタレート、ポリブチレンフタレート等のポリエステ
ル、共重合ポリエステル、ポリエーテルエステル、ポリ
エーテルアミドおよびポリエステルアミドなどが挙げら
れる。これらの材料は、単独で使用してもよく、あるい
は２種以上を混合して使用してもよい。これらの材料の
中でも、耐水性、コストの面からは汎用樹脂、たとえ
ば、ポリプロピレン、高密度ポリエチレン等のポリオレ
フィン樹脂が好適である。Specific examples of the material of the resin film include polyethylene, polypropylene, polymethylpentene-1
Such as polyolefin, polyvinyl chloride, polyvinylidene chloride, polystyrene, styrene-butadiene-acrylonitrile copolymer, polyamide such as nylon 6, nylon 66, copolymerized polyamide, polycarbonate, polymethyl methacrylate, polysulfone, polyethylene terephthalate, polybutylene Examples include polyester such as phthalate, copolymerized polyester, polyetherester, polyetheramide, and polyesteramide. These materials may be used alone or in combination of two or more. Among these materials, general-purpose resins, for example, polyolefin resins such as polypropylene and high-density polyethylene are preferable in terms of water resistance and cost.

【００１５】樹脂フィルムは、必要に応じて無機の微細
粉末を含有してもよい。無機の微細粉末としては、たと
えば、炭酸カルシウム、アルミナ、焼成クレイ、シリカ
（アモルファスシリカを含む）、珪藻土、タルク、酸化
チタン、硫酸バリウム等が使用できる。微細粉末の粒径
は、通常０．３〜１０μｍ、好適には０．８〜５μｍで
ある。また、その他の添加剤、たとえば、熱安定剤、紫
外線吸収剤、分散剤、帯電防止剤、酸化防止剤、オイル
（鉱油等）などを配合することもできる。The resin film may contain an inorganic fine powder if necessary. As the inorganic fine powder, for example, calcium carbonate, alumina, calcined clay, silica (including amorphous silica), diatomaceous earth, talc, titanium oxide, barium sulfate and the like can be used. The particle size of the fine powder is usually 0.3 to 10 μm, preferably 0.8 to 5 μm. Further, other additives, for example, a heat stabilizer, an ultraviolet absorber, a dispersant, an antistatic agent, an antioxidant, an oil (such as mineral oil), and the like can also be blended.

【００１６】上記した樹脂フィルム（必要に応じて無機
の微細粉末や添加剤を加えたものも含む）の延伸に用い
られる延伸装置の具体例としては、インフレーションフ
ィルム成形装置、内部マンドレルを備えたインフレーシ
ョンフィルム成形装置、テンターまたは縦延伸ロール群
とテンターを備えたＴ−ダイフィルム成形装置を挙げる
ことができる。延伸方向は、一軸方向でも二軸方向でも
よい。延伸倍率は、少なくとも１．３倍以上で、縦、横
方向とも１〜１０倍が好ましく、より好ましくは１．３
〜９倍である。延伸温度は、樹脂がプロピレンの単独重
合体（融点１６４〜１６７℃）のときは１４０〜１５５
℃、高密度ポリエチレン（融点１２１〜１３４℃）のと
きは１１０〜１２０℃である。また、延伸速度は、通常
１０〜３５０ｍ／分である。Specific examples of the stretching apparatus used for stretching the above-mentioned resin film (including those to which inorganic fine powder and additives are added as necessary) include an inflation film forming apparatus and an inflation film having an internal mandrel. Examples include a film forming apparatus, a tenter or a T-die film forming apparatus equipped with a longitudinal stretching roll group and a tenter. The stretching direction may be uniaxial or biaxial. The stretching ratio is at least 1.3 times or more, preferably 1 to 10 times in both the vertical and horizontal directions, and more preferably 1.3.
~ 9 times. The stretching temperature is 140 to 155 when the resin is a propylene homopolymer (melting point: 164 to 167 ° C).
° C and 110-120 ° C for high density polyethylene (melting point 121-134 ° C). The stretching speed is usually from 10 to 350 m / min.

【００１７】多孔質フィルムの空隙率（フィルム全体の
体積に占める空隙の体積）は、通常１０〜９０体積％、
好適には２０〜８０体積％である。多孔質フィルムの空
隙率が小さすぎると、インクの乾燥性が低下するおそれ
があり、反対に大きすぎると、支持体層の腰（機械的強
度）が低下し、記録媒体の供給、排出が滑らかに行えな
いおそれがある。The porosity of the porous film (the volume of the voids relative to the total volume of the film) is usually 10 to 90% by volume,
Preferably, it is 20 to 80% by volume. If the porosity of the porous film is too small, the drying properties of the ink may be reduced. Conversely, if it is too large, the stiffness (mechanical strength) of the support layer is reduced, and the supply and discharge of the recording medium are smooth. May not be possible.

【００１８】多孔質フィルムの空隙の孔径は、そのフィ
ルムを厚さ断面方向に垂直（多孔質フィルムの水平方
向）に切断して測定した時、通常０．０１〜３μｍ、好
適には０．０２〜２μｍ、特に好適には０．０３〜１μ
ｍである。空隙の孔径が小さすぎると、インクの乾燥性
が低下するおそれがあり、反対に大きすぎると、インク
適用後の発色性（色濃度）の低下や、その上に塗布して
形成されるインク像受容層の均一性を低下させるおそれ
がある。The pore diameter of the voids in the porous film is usually 0.01 to 3 μm, preferably 0.02 μm, when the film is cut perpendicularly to the thickness cross-sectional direction (horizontal direction of the porous film). ２2 μm, particularly preferably 0.03 to 1 μm
m. If the pore size of the voids is too small, the drying property of the ink may be reduced. Conversely, if the pore size is too large, the color developability (color density) after application of the ink may decrease, or an ink image formed by coating on the ink. The uniformity of the receiving layer may be reduced.

【００１９】支持体層の全体の厚さは、３０〜５００μ
ｍ、好ましくは５０〜３００μｍである。支持体層が薄
すぎると、インク乾燥性が低下するおそれがあり、反対
に厚すぎると、記録媒体の取り扱いに不便を生じるおそ
れがある。本発明の画像記録媒体は、好適には、いろい
ろなタイプのインクジェットプリンタ等の印刷装置で使
用できるものである。記録媒体が厚すぎると、使用でき
ないタイプのプリンタが出てくるおそれがある。また、
本発明の画像記録媒体は、支持体層のインク像受容層の
配置面とは反対側の面に、接着剤層を配置し、壁等の被
着体に貼り付けて使用できるのが好適である。記録媒体
が厚すぎると、被着体の表面の湾曲や凹凸に記録媒体が
追従できず、貼り付けが困難になるおそれがある。The total thickness of the support layer is 30 to 500 μm.
m, preferably 50 to 300 μm. If the support layer is too thin, the ink drying property may decrease. On the other hand, if the support layer is too thick, the handling of the recording medium may be inconvenient. The image recording medium of the present invention is preferably one that can be used in printing devices such as various types of ink jet printers. If the recording medium is too thick, some types of printers may not be usable. Also,
The image recording medium of the present invention is preferably arranged such that an adhesive layer is disposed on the surface of the support layer opposite to the surface on which the ink image receiving layer is disposed, and can be used by being attached to an adherend such as a wall. is there. If the recording medium is too thick, the recording medium cannot follow the curvature or unevenness of the surface of the adherend, and it may be difficult to attach the recording medium.

【００２０】本発明の好適な実施形態では、支持体層の
表面および支持体層内の微細孔は、界面活性剤により親
水化処理される。界面活性剤は、アニオン性、カチオン
性、両性およびノニオン性のいずれのものも使用でき
る。アニオン性のものとしては、たとえば、カルボン酸
塩系、スルホン酸塩系、燐酸エステル塩系等が使用で
き、カチオン性のものとしては、たとえば、アミン塩
系、第四級アンモニウム塩系等が使用でき、両性のもの
としては、たとえば、ベタイン系、スルホベタイン系等
が使用でき、ノニオン性のものとしては、たとえば、ポ
リエチレングリコール等のポリオキシアルキレン系、ソ
ルビタン系、ソリビトール系等が使用できる。In a preferred embodiment of the present invention, the surface of the support layer and the micropores in the support layer are subjected to a hydrophilic treatment with a surfactant. As the surfactant, any of anionic, cationic, amphoteric and nonionic surfactants can be used. Examples of the anionic type include carboxylate type, sulfonate type, and phosphate type, and examples of the cationic type include amine salt type and quaternary ammonium salt type. As the amphoteric one, for example, a betaine type, a sulfobetaine type or the like can be used, and as the nonionic type, for example, a polyoxyalkylene type such as polyethylene glycol, a sorbitan type, a sorivitol type or the like can be used.

【００２１】親水化処理を、界面活性剤を含む液体を塗
布し、乾燥して行う場合、溶媒として、水や、エタノー
ル等のアルコールを用いるのが好適である。界面活性剤
を含む液体中の界面活性剤の濃度は、通常１〜３０重量
％、好適には５〜２５重量％である。また、塗布装置に
は、通常のコータ、たとえば、バーコータ、ナフコー
タ、ロールコータ、ダイコータ等が使用できる。インク像受容層 本発明の画像記録媒体のインク像受容層は、有機ポリマ
ーと、水溶性の塩類を含む凝集剤とを含んでなる。When the hydrophilic treatment is performed by applying a liquid containing a surfactant and drying the liquid, it is preferable to use water or an alcohol such as ethanol as a solvent. The concentration of the surfactant in the liquid containing the surfactant is usually 1 to 30% by weight, preferably 5 to 25% by weight. Further, a usual coater, for example, a bar coater, a naph coater, a roll coater, a die coater or the like can be used for the coating apparatus. Ink image receiving layer The ink image receiving layer of the image recording medium of the present invention comprises an organic polymer and a coagulant containing a water-soluble salt.

【００２２】有機ポリマーとしては、前述の、たとえば
カチオン変性ポリウレタン等の水分散性のカチオン変性
ポリマーの他、ポリオレフィン、ポリ塩化ビニル、ポリ
塩化ビニリデン、ポリスチレン、スチレン・ブタジエン
・アクリルニトリル共重合体、ポリアミド、アクリル系
ポリマー、ポリエステル、通常の未変性のポリウレタン
等も使用できる。Examples of the organic polymer include the above-mentioned water-dispersible cation-modified polymers such as cation-modified polyurethane, polyolefin, polyvinyl chloride, polyvinylidene chloride, polystyrene, styrene-butadiene-acrylonitrile copolymer, polyamide , An acrylic polymer, a polyester, and an ordinary unmodified polyurethane.

【００２３】凝集剤は、記録媒体表面にインクが適用
（印刷等）された時、顔料等の着色成分をすばやくイン
ク像受容層の表面で凝集させることができるものであれ
ば、特に限定されないが、水溶性の塩類を必須成分とす
る。前述の様に、塩類は、無機酸の多価金属塩が好適で
ある。多価金属イオン、および酸の対イオンは、インク
を適用し、乾燥した後、インク像受容層表面にインク成
分を凝集させ、効果的に固定することができる。The coagulant is not particularly limited as long as it can coagulate coloring components such as pigments quickly on the surface of the ink image receiving layer when the ink is applied (printed or the like) to the recording medium surface. And water-soluble salts as essential components. As described above, the salts are preferably polyvalent metal salts of inorganic acids. The polyvalent metal ion and the counter ion of the acid can coagulate and effectively fix the ink component on the surface of the ink image receiving layer after the ink is applied and dried.

【００２４】多価金属イオンとしては、アルミニウム、
ガリウム、チタン、ジルコニウム、ハフニウム、亜鉛、
マグネシウム、カルシウム、ニオブ、タンタル、鉄、
銅、スズ、コバルト等のうちの、１または２以上を組み
合わせて使用することができる。金属イオンとして、好
適には、アルミニウムイオン（３価）が挙げられる。ア
ルミニウムイオンは、シラノール基に強く結合し、顔料
等の着色成分の凝集が、アルミニウムイオンによって効
果的に引き起こされるからである。The polyvalent metal ions include aluminum,
Gallium, titanium, zirconium, hafnium, zinc,
Magnesium, calcium, niobium, tantalum, iron,
One, two or more of copper, tin, cobalt and the like can be used in combination. The metal ion is preferably an aluminum ion (trivalent). This is because aluminum ions strongly bind to silanol groups, and aggregation of coloring components such as pigments is effectively caused by aluminum ions.

【００２５】無機酸の例として、好適には、硫酸、硝
酸、または塩酸が挙げられる。有機ポリマーが、カチオ
ン変性ポリウレタン等のカチオン変性ポリマーの場合、
有機酸塩よりも無機酸塩が好適である。無機酸塩は、カ
チオン変性ポリマーと共同して速乾性と耐水性とを効果
的に高めることができるからである。無機酸塩として、
好適には、硫酸アルミニウム、硫酸マグネシウム、硝酸
アルミニウム等が挙げられる。その理由の詳細について
は明らかではないが、ポリマーのカチオン部分と、
（Ａ）硫酸イオンと、塩のカチオン部分（アルミニウム
またはマグネシウムイオン）との３者の相互作用、また
は（Ｂ）塩のアニオン部分と、アルミニウムイオンとの
３者の相互作用により、インク定着力が効果的に高めら
れ、速乾性と耐水性に反映していると考えられる。Suitable examples of inorganic acids include sulfuric acid, nitric acid, or hydrochloric acid. When the organic polymer is a cation-modified polymer such as a cation-modified polyurethane,
Inorganic acid salts are preferred over organic acid salts. This is because the inorganic acid salt can effectively enhance quick drying and water resistance in cooperation with the cation-modified polymer. As an inorganic acid salt,
Preferably, aluminum sulfate, magnesium sulfate, aluminum nitrate and the like are mentioned. Although the details of the reason are not clear, the cationic portion of the polymer,
(A) interaction between sulfate ions and a cation portion (aluminum or magnesium ion) of a salt, or (B) interaction between an anion portion of a salt and an aluminum ion to increase ink fixing power. It is thought that it is effectively enhanced and reflects quick drying and water resistance.

【００２６】インク像受容層に含まれる凝集剤の量は、
有機ポリマー１００重量部に対して、通常１〜７０重量
部、好適には３〜５０重量部、特に好適には５〜３０重
量部である。凝集剤の量が少なすぎるとインク定着力が
低下し、耐水性や発色性が低下するおそれがあり、反対
に多すぎるとインク像のにじみが生じるおそれがある。The amount of the coagulant contained in the ink image receiving layer is
The amount is usually 1 to 70 parts by weight, preferably 3 to 50 parts by weight, particularly preferably 5 to 30 parts by weight, based on 100 parts by weight of the organic polymer. If the amount of the coagulant is too small, the ink fixing power may be reduced, and water resistance and color development may be reduced. Conversely, if the amount is too large, bleeding of the ink image may occur.

【００２７】インク像受容層には、受容層の多孔性を高
めるために、必要に応じて無機の微細粉末を含ませるこ
ともできる。無機の微細粉末としては、炭酸カルシウ
ム、アルミナ、焼成クレイ、シリカ（アモルファスシリ
カを含む）、珪藻土、タルク、酸化チタン、硫酸バリウ
ム等が使用できる。このような微細粉末の粒径は、通常
０．３〜１０μｍ、好適には０．８〜５μｍである。ま
た、その他の添加剤、たとえば、熱安定剤、紫外線吸収
剤、分散剤、帯電防止剤、酸化防止剤、などを配合する
こともできる。The ink image receiving layer may contain an inorganic fine powder, if necessary, in order to increase the porosity of the receiving layer. As the inorganic fine powder, calcium carbonate, alumina, calcined clay, silica (including amorphous silica), diatomaceous earth, talc, titanium oxide, barium sulfate and the like can be used. The particle size of such a fine powder is usually 0.3 to 10 μm, preferably 0.8 to 5 μm. Further, other additives, for example, a heat stabilizer, an ultraviolet absorber, a dispersant, an antistatic agent, an antioxidant, and the like can be added.

【００２８】インク像受容層は、たとえば、凝集剤およ
び有機ポリマーを含む塗布液を塗布し、乾燥して形成す
ることができる。この場合の溶媒として、水やアルコー
ルを用いるのが好適である。また、塗布装置には、通常
のコータ、たとえば、バーコータ、ナイフコータ、ロー
ルコータ、ダイコータ等が使用できる。画像記録媒体の使用方法 本発明の画像記録媒体は、インクジェットプリンタ等の
印刷装置により、インク像を記録するために用いられ
る。ここで画像形成のために使用するインクは、通常、
顔料、染料等の着色剤と、水、アルコール等の溶媒とを
含んでなる。本発明の記録媒体は、水性インク（溶媒は
水を含む）を用いたインクジェットプリンタによる記録
において特に効果を発揮し、速乾性と、耐水性とがとも
に効果的に高められる。なお、プリント条件は、通常の
記録紙の場合と同様であることができ、この様に、特に
特殊な条件での印刷を必要としない点でも、本発明の記
録媒体はすぐれている。The ink image receiving layer can be formed, for example, by applying a coating solution containing a coagulant and an organic polymer and drying the coating solution. In this case, it is preferable to use water or alcohol as the solvent. Further, a usual coater, for example, a bar coater, a knife coater, a roll coater, a die coater or the like can be used for the coating apparatus. Method of Using Image Recording Medium The image recording medium of the present invention is used for recording an ink image by a printing device such as an inkjet printer. Here, the ink used for image formation is usually
It comprises a colorant such as a pigment or a dye, and a solvent such as water or alcohol. The recording medium of the present invention is particularly effective in recording by an ink jet printer using an aqueous ink (the solvent contains water), and both the quick drying property and the water resistance are effectively enhanced. The printing conditions can be the same as those for ordinary recording paper. Thus, the recording medium of the present invention is excellent also in that printing under special conditions is not required.

【００２９】本発明の画像記録媒体は、装飾用接着シー
トの構成材料として用いることもできる。たとえば、支
持体層のインク像受容層を有する表面とは反対側の面
に、粘着剤、接着剤等を含む接着剤層を配置し、その上
にさらに、接着剤層の接着面を保護するライナーを配置
し、よって、画像記録媒体、接着剤層およびライナーか
らなる積層体を形成する。この積層体を、記録媒体単体
の場合と同様にしてプリンタにかけ、記録媒体（インク
像受容層）の表面のインク受容／定着面に装飾用の印刷
を施し、装飾用接着シートを作製する。本発明による接
着シートは、通常の装飾用接着シートと同様にして、
壁、車両ボディ、ガラス窓等の被着体表面に接着し、被
着体を装飾することができる。もちろん、この接着シー
トは、必要に応じて、上記した装飾目的以外にも使用す
ることができる。その他の使途の一例としては、たとえ
ば、広告目的、表示目的などを挙げることができる。The image recording medium of the present invention can also be used as a constituent material of a decorative adhesive sheet. For example, on the surface of the support layer opposite to the surface having the ink image receiving layer, an adhesive layer containing a pressure-sensitive adhesive, an adhesive or the like is arranged, and further thereon, the adhesive surface of the adhesive layer is protected. The liner is placed, thus forming a laminate comprising the image recording medium, the adhesive layer and the liner. The laminate is applied to a printer in the same manner as in the case of the recording medium alone, and decorative printing is performed on the ink receiving / fixing surface of the recording medium (ink image receiving layer) to produce a decorative adhesive sheet. The adhesive sheet according to the present invention is similar to a normal decorative adhesive sheet,
It can be attached to the surface of an adherend such as a wall, a vehicle body, or a glass window to decorate the adherend. Of course, this adhesive sheet can be used for any purpose other than the above-mentioned decoration, if necessary. Examples of other uses include, for example, advertising purposes, display purposes, and the like.

【００３０】[0030]

【実施例】引き続いて、下記の実施例を参照して本発明
を詳細に説明する。なお、本発明は、下記の実施例によ
って限定されるものではないことを理解されたい。例１ ＰＰＧ社製のアモルファスシリカ含有多孔質フィルム、
「Teslin」（商標）を支持体層として用意した。この多
孔質フィルムは、厚さが１８０μｍ、空隙率が６５体積
％、そして空隙の孔径が０．０１〜１μｍであった。ま
た、この支持体層の一方の表面に、ライナー付きアクリ
ル系粘着剤層（層厚＝３０μｍ）を積層した。The present invention will be described in detail with reference to the following examples. It should be understood that the present invention is not limited by the following examples. Example 1 A porous film containing amorphous silica manufactured by PPG,
“Teslin” ™ was provided as a support layer. This porous film had a thickness of 180 µm, a porosity of 65% by volume, and a pore size of the voids of 0.01 to 1 µm. An acrylic pressure-sensitive adhesive layer with a liner (layer thickness = 30 μm) was laminated on one surface of the support layer.

【００３１】得られた接着剤層付き支持体層の、接着剤
層を有しない表面に、次の組成の親水化処理液をバーコ
ータにて塗布し、乾燥した。 〔親水化処理液の組成〕 界面活性剤（花王製、（商標）ペレックス（品番）ＴＲ） １３重量部 脱イオン水 ６１重量部 エタノール ２６重量部 親水化処理の完了後、支持体層の親水化処理面の上に、
次の組成のインク像受容層形成用塗布液１をバーコータ
にて塗布した。 〔インク像受容層形成用塗布液１の組成〕 コーティング剤（下記参照） ９５重量部 硫酸アルミニウム・１４〜１８水和物の水溶液 ５重量部 ここで、コーティング剤は、水分散性のカチオン変性ポ
リウレタンと無機の微粉末とを含有するコーティング剤
として、大日本インキ化学工業社から（商標）パテラコ
ール（品番）ＩＪ−１７０として入手したものである。A hydrophilic treatment liquid having the following composition was applied to a surface of the obtained support layer having an adhesive layer having no adhesive layer by using a bar coater and dried. [Composition of hydrophilization treatment liquid] Surfactant (manufactured by Kao, (trademark) Perex (product number) TR) 13 parts by weight Deionized water 61 parts by weight Ethanol 26 parts by weight After completion of the hydrophilization treatment, the support layer is made hydrophilic. On the processing surface,
A coating solution 1 for forming an ink image receiving layer having the following composition was applied using a bar coater. [Composition of the coating solution 1 for forming an ink image receiving layer] Coating agent (see below) 95 parts by weight Aqueous solution of aluminum sulfate 14 to 18 hydrate 5 parts by weight Here, the coating agent is a water-dispersible cation-modified polyurethane. And a coating agent containing inorganic fine powder and obtained from Dainippon Ink and Chemicals, Inc. as (trademark) Pateracol (product number) IJ-170.

【００３２】塗布液１の塗膜を１００℃で３分間にわた
って乾燥したところ、厚さ２０μｍのインク像受容層が
完成し、本例の画像記録媒体（装飾用接着シートの構成
材料となり得る形態）が得られた。 〔印刷試験１〕本例の画像記録媒体のインク像受容層の
表面（インク受容／定着面）に、Ｅｎｃａｄ社製のイン
クジェットプリンタ、（商標）Ｎａｖａｊｅｔ、（品
番）III、を使用してフルカラー印刷を行い、印刷特性
を評価した。なお、適用した印刷条件は、下記の通りで
ある。When the coating film of the coating liquid 1 was dried at 100 ° C. for 3 minutes, an ink image receiving layer having a thickness of 20 μm was completed, and the image recording medium of the present example (a form which can be a constituent material of the decorative adhesive sheet) was gotten. [Printing Test 1] Full-color printing on the surface (ink receiving / fixing surface) of the ink image receiving layer of the image recording medium of the present example using an inkjet printer manufactured by Encad, Navajet (trade name) III, Was performed to evaluate the printing characteristics. The printing conditions applied are as follows.

【００３３】 印刷方向 単方向 インク噴射レート ５０００Hz 使用インク ３Ｍ社製の顔料インク（品番）８５５０シリーズ： シアン＃８５５１、マゼンダ＃８５５３、 イエロー＃８５５２および黒＃８５５４印刷特性（評価項目） （１）乾燥時間 シアン、マゼンダ、イエローおよび黒の４色が全部混ざ
った部分（インク量：４００％部）の乾燥時間（目視で
観察できる光沢を失うまでの時間）を測定し、評価し
た。乾燥時間は７５秒であり、インクの乾燥性が十分に
高く、速乾性であることが立証された。 （２）境界にじみ シアン、マゼンダおよびイエローの３色が混ざった部分
（インク量：３００％部）と、それと隣接する他の色の
部分との境界の色のにじみを、目視で観察して評価し
た。色のにじみは、ほとんど観察されなかった。 （３）発色性（色濃度） シアン、マゼンダ、イエローおよび黒の４色について、
各色単独の部分および混色部のそれぞれの発色性を目視
により観察した。いずれの部分の発色性も非常に高いこ
とが確認された。 〔印刷試験２〕印刷試験１と同様にフルカラー印刷を行
い、印刷特性を評価した。しかし、この印刷試験では、
Ｅｎｃａｄ社製のインクジェットプリンタに代えて、キ
ャノン社製のインクジェットプリンタ、（品番）ＢＪＣ
−６００Ｊ、と専用のシアン、マゼンダ、イエローおよ
び黒の４色の染料インクを使用した。Printing direction Unidirectional Ink jetting rate 5000 Hz Ink used 3M pigment ink (product number) 8550 series: Cyan # 8551, Magenta # 8553, Yellow # 8552, and Black # 8554 Printing characteristics (evaluation items) (1) Drying Time Drying time (time until loss of gloss that can be visually observed) of a portion where all four colors of cyan, magenta, yellow and black are mixed (ink amount: 400% portion) was measured and evaluated. The drying time was 75 seconds, which proved that the ink was sufficiently dry and quick-drying. (2) Boundary Bleed Bleeding of the color of the boundary between the portion where the three colors of cyan, magenta and yellow are mixed (ink amount: 300% portion) and the portion of the other color adjacent thereto is visually observed and evaluated. did. Little color bleeding was observed. (3) Color development (color density) For four colors of cyan, magenta, yellow and black,
The color developability of each color alone portion and each color mixture portion was visually observed. It was confirmed that the coloring properties of all parts were very high. [Printing test 2] Full-color printing was performed in the same manner as in printing test 1, and the printing characteristics were evaluated. However, in this printing test,
An inkjet printer manufactured by Canon Inc. instead of an inkjet printer manufactured by Encad, (product number) BJC
−600 J, and dedicated dye inks of four colors of cyan, magenta, yellow and black were used.

【００３４】この印刷試験の場合、４００％部のインク
の乾燥性は優れて良好であり、印刷後の用紙がプリンタ
から出てくるまでに乾燥が完了していた。また、３００
％部の境界にじみはほとんど観察されなかった。さら
に、発色性も非常に高かった。 例２（比較例） 前記例１に記載の手法を繰り返したが、本例の場合、比
較のため、インク像受容層形成用塗布液に硫酸アルミニ
ウムを添加しなかった。Ｅｎｃａｄ社製のインクジェッ
トプリンタを用いて印刷試験１を行った結果は、下記の
通りであった。In the case of this printing test, 400% of the ink
The drying properties of the paper are excellent and the paper after printing is
Drying had been completed by the time it came out. Also, 300
The border bleeding in the% part was hardly observed. Further
In addition, the coloring was also very high. Example 2 (comparative example) The method described in Example 1 was repeated.
For comparison, aluminum sulfate was added to the coating solution for forming the ink image receiving layer.
Was not added. Encad Inkjet
The results of printing test 1 using a printer were as follows:
It was right.

【００３５】乾燥時間が８０秒であり、十分な速乾性が
あったものの、３００％部の境界にじみが非常に顕著で
あった。これは、インク定着力の低下に起因しているも
のと思われる。また、発色性も、例１に比べて鈍かっ
た。例３（比較例） 前記例１に記載の手法を繰り返したが、本例の場合、比
較のため、支持体層の表面に対する親水化処理工程を省
略した。Ｅｎｃａｄ社製のインクジェットプリンタを用
いて印刷試験１を行った結果は、下記の通りであった。The drying time was 80 seconds, and although there was sufficient quick-drying, the bleeding at the boundary of 300% was very remarkable. This is considered to be due to a decrease in ink fixing power. Further, the coloring property was also lower than that of Example 1. Example 3 (Comparative Example) The procedure described in Example 1 was repeated. However, in the case of this example, the hydrophilizing treatment step on the surface of the support layer was omitted for comparison. The result of the printing test 1 using an inkjet printer manufactured by Encad was as follows.

【００３６】乾燥時間は４０分であり、インクの乾燥が
遅いと評価された。なお、３００％部の境界にじみはほ
とんど観察されず、発色性も例１と同等であった。例４ 前記例１に記載の手法を繰り返したが、本例の場合、硫
酸アルミニウム・１４〜１８水和物の水溶液に代えて同
量の硫酸マグネシウム７水和物（ＭｇＳＯ4 ・７Ｈ
2 Ｏ）の水溶液をインク像受容層形成用塗布液に添加し
た。Ｅｎｃａｄ社製のインクジェットプリンタを用いて
印刷試験１を行った結果は、下記の通りであった。The drying time was 40 minutes, and the drying of the ink was evaluated as slow. In addition, almost no border bleeding of the 300% portion was observed, and the coloring properties were the same as in Example 1. Example 4 The procedure described in Example 1 was repeated, except that in this case, the same amount of magnesium sulfate heptahydrate (MgSO 4 .7H) was used instead of the aqueous solution of aluminum sulfate 14-18 hydrate.
An aqueous solution of 2 O) was added to the ink image receiving layer coating liquid. The result of the printing test 1 using an inkjet printer manufactured by Encad was as follows.

【００３７】乾燥時間は約７５秒であり、速乾性は十分
であると評価された。また、境界にじみはほとんど観察
されず、発色性も例１と同等であった。例５ 前記例１に記載の手法を繰り返したが、本例の場合、硫
酸アルミニウム・１４〜１８水和物の水溶液に代えて同
量の硝酸アルミニウム９水和物（ＡｌＮＯ3 ・９Ｈ
2 Ｏ）をインク像受容層形成用塗布液に添加した。Ｅｎ
ｃａｄ社製のインクジェットプリンタを用いて印刷試験
１を行った結果は、下記の通りであった。The drying time was about 75 seconds, and the quick drying property was evaluated to be sufficient. In addition, almost no border bleeding was observed, and the coloring properties were the same as in Example 1. Example Although 5 was repeated procedure of Example 1, in this example, aluminum sulfate 14-18 instead of an aqueous solution of a hydrate same amount of aluminum nitrate nonahydrate (AlNO 3-9H
The 2 O) was added to the ink image receiving layer coating liquid. En
The results of print test 1 performed using an inkjet printer manufactured by cad were as follows.

【００３８】乾燥時間は約７５秒であり、境界にじみは
ほとんど観察されず、発色性も例１と同等であった。The drying time was about 75 seconds, almost no border bleeding was observed, and the coloring was the same as in Example 1.

【００３９】[0039]

【発明の効果】以上に説明したように、本発明による
と、優れた発色性を実現するとともに、インク中の着色
成分（顔料等）が、媒体内部の微細孔まで移行すること
を効果的に防止し、速乾性を高めることが可能な、従来
において得られたことがない優れた画像記録媒体を提供
することができる。As described above, according to the present invention, excellent color developability is realized, and at the same time, the coloring component (eg, pigment) in the ink is effectively transferred to the fine pores inside the medium. It is possible to provide an excellent image recording medium which has been obtained in the related art and which can prevent the problem and improve the quick drying property.

【００４０】特に、本発明の画像記録媒体を使用する
と、インクの乾燥性が極めて高く、換言すると、インク
像が速乾性であるので、印刷時間を大幅に短縮すること
ができると同時に、印刷後の作業性および生産性も大幅
に改善することができる。また、速乾性であることを生
かして、高速プリンタにも対応可能である。また、本発
明の画像記録媒体では、顔料、染料等の着色成分がイン
ク像受容層に含まれる多価金属塩によっていち早く凝集
し、より大きな固まりとなってインク像受容層の表面に
定着可能であるので、非常に高い色濃度、換言すると、
優れた発色性を有し、しかも色にじみのない高品位なイ
ンク像を得ることができ、よって、画像記録媒体を広範
囲な使途において有利に使用することができる。In particular, when the image recording medium of the present invention is used, the drying property of the ink is extremely high. In other words, since the ink image is quick-drying, the printing time can be greatly reduced, and at the same time, the post-printing time can be reduced. Workability and productivity can be greatly improved. In addition, it can be used for a high-speed printer by taking advantage of its quick drying property. Further, in the image recording medium of the present invention, the coloring components such as pigments and dyes are quickly aggregated by the polyvalent metal salt contained in the ink image receiving layer, and can be fixed to the surface of the ink image receiving layer as a larger mass. There is a very high color density, in other words,
It is possible to obtain a high-quality ink image having excellent color developability and without color bleeding, so that the image recording medium can be advantageously used in a wide range of uses.

【００４１】さらに、本発明の画像記録媒体では、イン
ク像の速乾性に加えて、耐水性も良好であるので、屋外
の風雨にさらされるような環境下においても十分に満足
し得る結果を期待できる。さらに加えて、従来の画像記
録媒体ではそれぞれの記録媒体ごとに使用するプリンタ
やインクの種類が限定されていたけれども、本発明の画
像記録媒体では、その優れたインク受容性などのため、
そのような限定が取り除かれ、各種のプリンタおよびイ
ンクについて同等の良好な印刷特性を得ることができ
る。Further, since the image recording medium of the present invention has good water resistance in addition to the quick drying of the ink image, a satisfactory result can be expected even in an environment exposed to the wind and rain outdoors. it can. In addition, in the conventional image recording medium, the type of printer and ink used for each recording medium was limited, but in the image recording medium of the present invention, due to its excellent ink receptivity and the like,
Such limitations have been removed, and equivalent good printing characteristics can be obtained for various printers and inks.

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 （ｉ）通気性微細孔を含む支持体層と、 （ii）その支持体層の表面に配置され、凝集剤として水
溶性塩類を含むインク像受容層とを有してなる画像記録
媒体において、 前記インク像受容層が有機ポリマーをさらに含有し、か
つ前記支持体層の表面および前記微細孔が、界面活性剤
により親水化処理されていることを特徴とする、画像記
録媒体。1. An ink image receiving layer comprising: (i) a support layer containing air-permeable micropores; and (ii) an ink image receiving layer disposed on the surface of the support layer and containing a water-soluble salt as a coagulant. An image recording medium, wherein the ink image receiving layer further contains an organic polymer, and the surface of the support layer and the micropores are subjected to a hydrophilic treatment with a surfactant. . 【請求項２】 前記インク像受容層は、前記支持体層の
表面および前記微細孔が親水化処理された後、配置され
た層である、請求項１に記載の画像記録媒体。2. The image recording medium according to claim 1, wherein the ink image receiving layer is a layer disposed after the surface of the support layer and the micropores are subjected to a hydrophilic treatment. 【請求項３】 前記有機ポリマーが水分散性のカチオン
変性ポリマーを含んでなる、請求項１または２に記載の
画像記録媒体。3. The image recording medium according to claim 1, wherein said organic polymer comprises a water-dispersible cation-modified polymer. 【請求項４】 前記支持体層のインク像受容層を有する
表面とは反対側の面に、さらに接着剤層を有している、
請求項１に記載の画像記録媒体。4. An adhesive layer is further provided on the surface of the support layer opposite to the surface having the ink image receiving layer.
The image recording medium according to claim 1.
JP11223918A 1999-08-06 1999-08-06 Image recording medium Pending JP2001047734A (en)