JP2001026073A - Waterproof sealing medium - Google Patents
Waterproof sealing mediumInfo
- Publication number
- JP2001026073A JP2001026073A JP11199184A JP19918499A JP2001026073A JP 2001026073 A JP2001026073 A JP 2001026073A JP 11199184 A JP11199184 A JP 11199184A JP 19918499 A JP19918499 A JP 19918499A JP 2001026073 A JP2001026073 A JP 2001026073A
- Authority
- JP
- Japan
- Prior art keywords
- silicone gel
- waterproof sealing
- gel layer
- porous sheet
- sealing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、防水封止材に関
する。The present invention relates to a waterproof sealing material.
【０００２】[0002]
【従来の技術】ケーブル類のジョイント部のコネクター
等においては、外部からの水分の侵入による腐食や導通
不良を防ぐため、防水封止材を用いる防水封止処理が行
われている。2. Description of the Related Art Waterproof sealing using a waterproof sealing material is performed on connectors at joints of cables and the like in order to prevent corrosion and poor conduction due to intrusion of moisture from the outside.
【０００３】従来の防水封止材としては、合成ゴム等の
エラストマー（弾性体）からなるものが多用され、その
防水封止材をジョイント部等にはめたり、コネクター等
の筐体内に詰め込むこｔによって防水封止処理を行って
いる。As a conventional waterproof sealing material, a material made of an elastomer (elastic body) such as synthetic rubber is widely used. The waterproof sealing material is fitted to a joint or the like or packed in a housing such as a connector. Waterproof sealing process.
【０００４】[0004]
【発明が解決しようとする課題】しかしながら、エラス
トマー製防水封止材は、硬度が高く、しかもコネクター
の形状やケーブルの断面形状等に応じて成形されたＯ
（オー）リングやパッキンが用いられるため、コネクタ
ーの形状やケーブルの断面形状が異なると対応できず、
新たに専用の防水封止材を成形する必要があり、経済的
ではなかった。しかも、エラストマー製防水封止材の硬
度を低くすると、ケーブルやコネクター等に対する封止
性が損なわれ易く、特に長期に渡って使用すると反発弾
性が低下して良好な封止性が得られなくなる。However, the waterproof sealing material made of an elastomer has a high hardness and is formed according to the shape of the connector or the sectional shape of the cable.
(O) Since a ring or packing is used, it cannot be handled if the shape of the connector or the sectional shape of the cable is different,
A special waterproof sealing material must be newly formed, which is not economical. In addition, if the hardness of the waterproof sealing material made of elastomer is lowered, the sealing property for cables, connectors and the like is liable to be impaired. Especially when used for a long time, the rebound resilience is reduced and good sealing property cannot be obtained.
【０００５】さらに、従来のエラストマー製防水封止材
は硬度が高いため、高低差のあるような立体的な部分に
は充分に追随できず、封止不良を生じ易い。また、エラ
ストマー製防水封止材をコネクター内面及びケーブルの
ジョイント部周囲に密着させてコネクターを閉じるの
に、防水封止材をコネクターの筐体で強く押圧しなけれ
ばならず、その押圧力に耐えられる強度がコネクターの
筐体に求められるようになる。その要求強度を満たすた
めには、コネクターの壁面を厚くしたり、コネクターの
材質を強度の高いものにしたり、さらには構造を工夫し
なければならず、コストアップにつながるという問題が
ある。Further, the conventional elastomer waterproof sealing material has a high hardness, so that it cannot sufficiently follow a three-dimensional portion having a difference in elevation, and is likely to cause poor sealing. In addition, to close the connector with an elastomer waterproof sealant in close contact with the inner surface of the connector and around the joints of the cable, the waterproof sealant must be strongly pressed by the connector housing, and cannot withstand the pressing force. The required strength is required for the connector housing. In order to satisfy the required strength, the wall of the connector must be thickened, the material of the connector must be high in strength, and furthermore, the structure must be devised, leading to an increase in cost.
【０００６】なお、ブチルゴム層に板状発泡体の層を埋
設した防水材も提案されている（特開平９−１８５９６
７）が、ブチルゴム層に埋設された板状発泡体によっ
て、防水材の変形性が損なわれ、、ケーブル外面やコネ
クター内面に対して密着不良を生じ易く、防水封止を充
分に行えないおそれがある。しかも、ブチルゴム層も硬
度が高いため、コネクターを閉じる際に大なる力で防水
材を圧縮しなければならず、前記と同様にコネクターの
筐体に高い強度が必要となる。[0006] A waterproofing material in which a layer of a plate-like foam is embedded in a butyl rubber layer has also been proposed (Japanese Patent Application Laid-Open No. Hei 9-18596).
7) However, the deformability of the waterproof material is impaired by the plate-like foam embedded in the butyl rubber layer, poor adhesion to the outer surface of the cable or the inner surface of the connector is likely to occur, and the waterproof sealing may not be sufficiently performed. is there. Moreover, since the butyl rubber layer also has a high hardness, the waterproof material must be compressed with a large force when closing the connector, and a high strength is required for the housing of the connector as described above.
【０００７】また、ケーブルのジョイント部等は、自動
車のボンネット内のような、夏期等に非常に高温となる
場所に位置することが多いため、前記防水封止材として
は、高温時にも優れた防水封止性を発揮するものが望ま
れる。[0007] Further, since the joint portion of the cable and the like is often located in a place where the temperature becomes extremely high in the summer or the like, such as in the hood of an automobile, the waterproof sealing material is excellent even at a high temperature. What exhibits a waterproof sealing property is desired.
【０００８】この発明は、前記の点に鑑みなされたもの
で、形状の異なる種々のケーブルやコネクターに対して
も適応でき、しかもケーブルやコネクター等への装着が
容易で、長期に渡って、また高温時においても優れた防
水封止性を発揮する防水封止材を提供する。The present invention has been made in view of the above points, and can be applied to various cables and connectors having different shapes, and can be easily attached to cables and connectors. Provided is a waterproof sealing material that exhibits excellent waterproof sealing properties even at high temperatures.
【０００９】[0009]
【課題を解決するための手段】前記問題を解決する請求
項１の発明は、多孔シートの片面にシリコーンゲル層を
積層した防水封止材に係る。Means for Solving the Problems The invention according to claim 1 which solves the above problems relates to a waterproof sealing material in which a silicone gel layer is laminated on one surface of a porous sheet.
【００１０】前記請求項１の発明におけるシリコーンゲ
ル層は、粘着性（自己接着性）及び他物体に対する密着
性を有し、しかも柔軟に変形するものである。そのた
め、請求項１の発明に係る防水封止材を、シリコーンゲ
ル層がケーブルのジョイント部等を向くようにして用い
れば、シリコーンゲル層の表面がジョイント部等に密着
し、その密着部を確実に防水封止することができる。さ
らに、シリコーンゲル層が自己粘着性を有するため、１
つの防水封止材をシリコーンゲル層が内側となるように
折り重ねてシリコーンゲル層でジョイント部等を挟むこ
とにより、あるいは２つの防水封止材をシリコーンゲル
層が内側となるように重ねてシリコーンゲル層間でジョ
イント部等を挟むことにより、ジョイント部等の周囲を
シリコーンゲル層で簡単に密封することができる。The silicone gel layer according to the first aspect of the present invention has adhesiveness (self-adhesiveness) and adhesion to other objects, and is deformable flexibly. Therefore, when the waterproof sealing material according to the first aspect of the present invention is used such that the silicone gel layer faces the joint portion of the cable, the surface of the silicone gel layer adheres to the joint portion and the like, and the adhered portion is securely formed. Waterproof sealing. Furthermore, since the silicone gel layer has self-adhesiveness,
One waterproof sealant is folded so that the silicone gel layer is on the inside, and the joint is sandwiched between the silicone gel layers, or two waterproof sealants are stacked so that the silicone gel layer is on the inner side. By sandwiching the joint and the like between the gel layers, the periphery of the joint and the like can be easily sealed with the silicone gel layer.
【００１１】また、シリコーンゲルは多孔シートによっ
て形状が保持されるため、ジョイント部等の外面やコネ
クター内への装着が容易である。しかも、多孔シートの
孔によって、多孔シートとシリコーンゲル層との一体性
が強くなっているため、シリコーンゲル層が多孔シート
から剥離し難い。Since the shape of the silicone gel is maintained by the porous sheet, the silicone gel can be easily mounted on the outer surface of a joint or the like or in a connector. In addition, since the hole between the porous sheet and the silicone gel layer enhances the integration between the porous sheet and the silicone gel layer, the silicone gel layer hardly peels off from the porous sheet.
【００１２】請求項２の発明は、多孔シートに対してシ
リコーンゲル層が一体成形されてなることを特徴とす
る。この請求項２の発明によれば、多孔シートとシリコ
ーンゲル層とが強固に一体化し、ジョイント部等への装
着等の際にシリコーンゲル層が多孔シートから剥離する
おそれがない。A second aspect of the present invention is characterized in that the silicone gel layer is formed integrally with the porous sheet. According to the second aspect of the present invention, the porous sheet and the silicone gel layer are firmly integrated, and there is no possibility that the silicone gel layer is peeled off from the porous sheet at the time of attachment to a joint or the like.
【００１３】請求項３の発明は、シリコーンゲル層が、
無機充填剤を添加した１液タイプのシリコーンゲルから
なることを特徴とする。According to a third aspect of the present invention, the silicone gel layer comprises:
It is made of a one-pack type silicone gel to which an inorganic filler is added.
【００１４】前記請求項３の発明によれば、無機充填剤
を添加することによって、シリコーンゲル層に対して強
度増大や物性改良、さらには適度な自己接着性（タック
性）及び良好な密着性を得ることができる。According to the third aspect of the present invention, by adding an inorganic filler, the strength and physical properties of the silicone gel layer can be increased and the physical properties can be improved. Can be obtained.
【００１５】請求項４の発明は、シリコーンゲル層が、
主剤１００重量部に無機充填剤を２〜５０重量部、硬化
剤を５０〜２００重量部添加した２液タイプのシリコー
ンゲルからなることを特徴とする。According to a fourth aspect of the present invention, the silicone gel layer comprises:
It is characterized by comprising a two-part type silicone gel in which 2 to 50 parts by weight of an inorganic filler and 50 to 200 parts by weight of a curing agent are added to 100 parts by weight of a main agent.
【００１６】前記請求項４の発明によれば、無機充填剤
を２〜５０重量部添加することによって、シリコーンゲ
ル層に対して強度増大や物性改良、さらには適度な自己
接着性（タック性）及び良好な密着性を得ることができ
る。また、硬化剤を５０〜２００重量部添加することに
よって、シリコーンゲル層に高温時に流れない適度な柔
軟性と、長期に渡って良好な密着性、すなわち良好な応
力緩和性を付与することができ、より確実にジョイント
部等を防水封止することができる。なお、応力緩和性が
低いと、コネクター等によりジョイント部等を防水封止
材で長期にわたり押圧してシリコーンゲル層をジョイン
ト部に密着し続けた場合、シリコーンゲル層の反発弾性
力が低下して、コネクター内面等と防水封止材との間に
隙間が発生し、防水封止性が低下するおそれがある。According to the fourth aspect of the present invention, by adding 2 to 50 parts by weight of an inorganic filler, the strength and physical properties of the silicone gel layer are improved and the self-adhesiveness (tackiness) is improved. And good adhesion can be obtained. Also, by adding 50 to 200 parts by weight of a curing agent, it is possible to impart appropriate flexibility that does not flow at high temperatures to the silicone gel layer and good adhesion over a long period, that is, good stress relaxation. Thus, the joints and the like can be more securely waterproof-sealed. If the stress relaxation property is low, when the silicone gel layer is kept in close contact with the joint part by pressing the joint part with a waterproof sealing material for a long time by a connector or the like, the resilience of the silicone gel layer is reduced. In addition, a gap may be generated between the inner surface of the connector and the like and the waterproof sealing material, and the waterproof sealing property may be reduced.
【００１７】請求項５の発明は、無機充填剤が煙霧質シ
リカであることを特徴とする。煙霧質シリカは、シリコ
ーンゲル原料との相溶性、混練性が良好なため、充填効
果が良好で、物理的強度増大や適度な密着性付与効果に
優れる。The invention according to claim 5 is characterized in that the inorganic filler is fumed silica. The fumed silica has a good compatibility with the raw material of the silicone gel and a good kneading property, so that the filling effect is good, and the effect of increasing the physical strength and imparting an appropriate adhesion is excellent.
【００１８】請求項６の発明は、シリコーンゲルに反応
性シリコーンオイルを添加したことを特徴とする。この
反応性シリコーンオイルの添加によって、シリコーンゲ
ル層が硬くなりすぎるのを防止し、良好な密着性を得る
ことができ、防水封止性を高めることができる。A sixth aspect of the present invention is characterized in that a reactive silicone oil is added to the silicone gel. By adding the reactive silicone oil, the silicone gel layer is prevented from becoming too hard, good adhesiveness can be obtained, and waterproof sealing property can be enhanced.
【００１９】[0019]
【発明の実施の形態】図１はこの発明の一実施例に係る
防水封止材の断面図、図２はこの発明の防水封止材に対
する使用状態の一例を示す断面図、図３は他の使用例を
示す断面図、図４はさらに他の使用例を示す断面図であ
る。FIG. 1 is a cross-sectional view of a waterproof sealing material according to an embodiment of the present invention, FIG. 2 is a cross-sectional view showing an example of use of the waterproof sealing material of the present invention, and FIG. FIG. 4 is a sectional view showing still another example of use.
【００２０】図１に示す防水封止材１０は、多孔シート
１１の片面にシリコーンゲル層２１を積層したものから
なり、ケーブルのジョイント部等の防水封止に用いられ
る。この防水封止材１０を用いる防水封止は、図２に示
すように２つの防水封止材１０，１０のシリコーンゲル
層２１，２１間でジョイント部等の対象部分３１を挟む
ことにより、あるいは図３に示すように、１つの防水封
止材１０をシリコーンゲル層２１が内側となるようにし
て折り重ね、それによって対象部分３１をシリコーンゲ
ル層２１で挟むことにより、または、図４に示すよう
に、防水封止材１０をコネクターの筐体３５内に収容し
てジョイント部等の対象部分３１をシリコーンゲル層２
１で挟むことにより行われる。A waterproof sealing material 10 shown in FIG. 1 is formed by laminating a silicone gel layer 21 on one surface of a porous sheet 11 and is used for waterproof sealing of a joint portion of a cable or the like. The waterproof sealing using the waterproof sealing material 10 is performed by sandwiching a target portion 31 such as a joint portion between the silicone gel layers 21 and 21 of the two waterproof sealing materials 10 and 10, as shown in FIG. As shown in FIG. 3, one waterproof sealing material 10 is folded so that the silicone gel layer 21 is on the inside, whereby the target portion 31 is sandwiched between the silicone gel layers 21, or as shown in FIG. As described above, the waterproof sealing material 10 is housed in the housing 35 of the connector, and the target portion 31 such as the joint portion is formed on the silicone gel layer 2.
This is performed by sandwiching them with 1.
【００２１】多孔シート１１は、この防水封止材１０の
使用時におけるシリコーンゲル層２１の形状保持及び補
強、さらにはシリコーンゲル層２１表面をジョイント部
等の封止対象部分に良好に密着し易くするためのもので
ある。The porous sheet 11 easily retains and reinforces the shape of the silicone gel layer 21 when the waterproof sealing material 10 is used, and easily adheres the surface of the silicone gel layer 21 to a portion to be sealed such as a joint. It is for doing.
【００２２】多孔シート１１としては、表面と裏面間を
貫通する孔が全面に多数形成されたものであればよく、
繊維間が孔を構成する織布、不織布、あるいは多数の小
孔が形成されたプラスチックフィルムを問わず使用でき
る。それらの中でも、適度な柔軟性、厚み、強度等の点
から織物が特に好ましい。この織物の組織には平織り、
平編み、からみ織り、綾織り等がある。それらのなかで
も、厚みが薄く、しかも適度な柔軟性を有するという点
から平織りが特に好ましい。The porous sheet 11 may be any sheet as long as a large number of holes penetrating between the front and back surfaces are formed on the entire surface.
It can be used irrespective of a woven fabric, a nonwoven fabric, or a plastic film in which many small holes are formed between fibers. Among them, a woven fabric is particularly preferable in terms of appropriate flexibility, thickness, strength, and the like. The weave of this fabric has a plain weave,
There are flat knitting, leno weaving and twill weaving. Among them, plain weave is particularly preferable in that it has a small thickness and has appropriate flexibility.
【００２３】織物の繊維の材質は、ポリエステル繊維等
の化学繊維が好適であるが、それに限られるものではな
い。繊維の種類は、モノフィラメントあるいはマルチフ
ィラメントのいずれでもよいが、マルチフィラメントの
方が、シリコーンゲルとの密着性において好ましい。化
学繊維のモノフィラメントからなる平織りの織物を用い
る場合には、１インチ当たりのメッシュ数が１４〜７
０，厚みが２４０〜９００μｍの網状シートが好適であ
る。それに対し、マルチフィラメントからなる平織りの
織物を用いる場合には、１インチ当たりのメッシュ数が
９．０〜２００、開口面積が１０〜６１％、線径が４３
〜６７０μｍの網状シートが好適である。中でも、７０
〜１１０メッシュ、４２ｄ（デニール）−２４ｆ（フィ
ラメント）のポリエステルマルチフィラメントからなる
ものが好ましい。The fiber material of the woven fabric is preferably a chemical fiber such as a polyester fiber, but is not limited thereto. The type of fiber may be either a monofilament or a multifilament, but a multifilament is more preferable in terms of adhesion to the silicone gel. When a plain woven fabric composed of monofilaments of chemical fibers is used, the number of meshes per inch is 14 to 7
0, a mesh sheet having a thickness of 240 to 900 μm is preferable. On the other hand, when a plain weave fabric made of multifilaments is used, the number of meshes per inch is 9.0 to 200, the opening area is 10 to 61%, and the wire diameter is 43%.
A mesh sheet of 670 μm is preferred. Among them, 70
What consists of polyester multifilament of -110 mesh and 42d (denier)-24f (filament) is preferred.
【００２４】シリコーンゲル層２１を構成するシリコー
ンゲルは、液状シリコーンゴムの架橋密度を通常よりも
低くして硬化させた寒天状のものである。このシリコー
ンゲルは、オルガノシロキサンポリマーを主成分とし、
１液タイプ、２液タイプを問わず、また加熱加硫タイプ
のものであって低温架橋（ＬＴＶ）型や室温硬化（ＲＴ
Ｖ）型いずれでも使用できる。このシリコーンゲルの具
体例を挙げると、ポリジメチルシロキサンゲル、ポリメ
チルトリフルオロプロピルシロキサンゲル、ポリフェニ
ルメチルシロキサンゲル等を示すことができる。The silicone gel constituting the silicone gel layer 21 is an agar-like one obtained by setting the crosslink density of liquid silicone rubber lower than usual and hardening it. This silicone gel is based on an organosiloxane polymer,
Regardless of the one-pack type or the two-pack type, it is also a heat vulcanization type, and is a low temperature crosslinking (LTV) type or a room temperature curing (RT
V) Any type can be used. Specific examples of the silicone gel include polydimethylsiloxane gel, polymethyltrifluoropropylsiloxane gel, and polyphenylmethylsiloxane gel.
【００２５】前記シリコーンゲルが１液タイプの場合、
シリコーンゲルには無機充填剤を添加するのが好まし
い。無機充填剤を添加することによって物理的強度を高
め、表面のべた付き性（タック性）が適度に押さえられ
て、封止対象部分に対する密着性が適度なものになる。
無機充填剤の添加量はシリコーンゲル原料１００重量部
に対して２〜５０重量部が好ましい。添加量が２重量部
よりも少ないと、べた付き性（自己接着性）が高くなり
すぎると共に硬度が低くなり、しかも高温環境下では流
動し易くなって封止性が低下するようになる。それに対
し、添加量が５０重量部よりも多いと硬くなりすぎ、ジ
ョイント部等の封止対象部へのシリコーンゲル層２１の
密着性が低下したり、コネクターの筐体等内への防水封
止材１０配置が難しくなったり、筐体等を閉じにくくな
る。When the silicone gel is a one-pack type,
It is preferable to add an inorganic filler to the silicone gel. By adding the inorganic filler, the physical strength is increased, the stickiness (tackiness) of the surface is appropriately suppressed, and the adhesion to the portion to be sealed becomes appropriate.
The addition amount of the inorganic filler is preferably 2 to 50 parts by weight based on 100 parts by weight of the silicone gel raw material. If the addition amount is less than 2 parts by weight, the stickiness (self-adhesiveness) becomes too high and the hardness becomes low, and further, under a high temperature environment, it becomes easy to flow and the sealing property is lowered. On the other hand, if the addition amount is more than 50 parts by weight, the silicone gel layer 21 becomes too hard, the adhesion of the silicone gel layer 21 to a portion to be sealed such as a joint portion is reduced, or the sealing of the connector into a casing or the like is performed. It becomes difficult to dispose the member 10 or to close the housing or the like.
【００２６】無機充填剤としては、炭酸カルシウム、マ
イカ、水酸化アルミニウム、煙霧質シリカ、硫酸バリウ
ム等を使用することができる。それらのなかでも、煙霧
質シリカが、シリコーンゲルとの相溶性、混練性等に優
れ、良好な製品が得られる。As the inorganic filler, calcium carbonate, mica, aluminum hydroxide, fumed silica, barium sulfate and the like can be used. Among them, the fumed silica is excellent in compatibility with the silicone gel, kneading property and the like, and a good product can be obtained.
【００２７】また、前記シリコーンゲルが２液タイプの
場合、シリコーンゲル原料は、主剤と硬化剤からなる。
主剤は、直鎖状のジオルガノポリシロキサンからなり、
その両端末にアルケニル基が結合している。通常、分子
端末に位置するアルケニル基はビニル基である。When the silicone gel is of a two-pack type, the silicone gel raw material comprises a main agent and a curing agent.
The main agent is composed of a linear diorganopolysiloxane,
An alkenyl group is bonded to both terminals. Usually, the alkenyl group located at the molecular end is a vinyl group.
【００２８】硬化剤は、架橋剤として機能するものであ
って、有機珪素化合物が用いられる。この硬化剤は、珪
素原子に直接結合した活性水素である官能基が、前記主
剤のアルケニル基と反応することによって架橋する。分
子構造としては、直鎖状、側鎖を有する鎖状、環状等適
宜選択される。具体的には、トリオルガノシロキサン基
が末端にあるオルガノハイドロジエンポリシロキサン、
ジオルガノシロキサンとオルガノハイドロジエンシロキ
サンとの共重合体、テトラオルガノテトラハイドロジエ
ンシクロテトラシロキサン等が挙げられる。The curing agent functions as a crosslinking agent, and an organic silicon compound is used. This curing agent is cross-linked by reacting a functional group, which is an active hydrogen directly bonded to a silicon atom, with an alkenyl group of the main agent. The molecular structure is appropriately selected from a linear structure, a chain having a side chain, and a cyclic structure. Specifically, an organohydrogenpolysiloxane terminated with a triorganosiloxane group,
Copolymers of diorganosiloxane and organohydrodienesiloxane, tetraorganotetrahydrodienecyclotetrasiloxane and the like can be mentioned.
【００２９】前記硬化剤の量は、従来のシリコーンゲル
においては主剤１００重量部に対して同量とされるが、
この発明では、主剤１００重量部に対して５０〜２００
重量部とされる。硬化剤が５０重量部よりも少ないと、
シリコーンゲル層表面のべた付き性が高くなると共に硬
度が低くなり、高温環境下では前記シリコーンゲル層２
１が流動し易くなって、良好な防水封止性が得られなく
なる。しかも、応力緩和性が低下するため、長期に渡っ
てケーブルのジョイント部等に良好に密着させられなく
なる。また、硬化剤の量が２００重量部より多いと、シ
リコーンゲル層２１が硬くなりすぎて、防水封止性が低
下したり、コネクターの筐体等内への防水封止材１０配
置が難くなったり、筐体等を閉じにくくなる。In the conventional silicone gel, the amount of the curing agent is equal to 100 parts by weight of the main agent.
According to the present invention, 50 to 200 parts by weight of the main ingredient is used.
Parts by weight. If the curing agent is less than 50 parts by weight,
The stickiness of the surface of the silicone gel layer is increased and the hardness is reduced.
1 easily flows, and good waterproof sealing property cannot be obtained. In addition, since the stress relaxation property is reduced, the cable cannot be brought into good contact with the joint portion of the cable for a long period of time. On the other hand, when the amount of the curing agent is more than 200 parts by weight, the silicone gel layer 21 becomes too hard, and the waterproof sealing property is reduced, and it is difficult to dispose the waterproof sealing material 10 in a connector housing or the like. Or it becomes difficult to close the housing or the like.
【００３０】また、前記主剤には無機充填剤が添加され
る。この無機充填剤は、前記１液タイプと同様のものが
用いられ、特には煙霧質シリカが好ましい。無機充填剤
の添加量は、主剤１００重量部に対して２〜５０重量部
が好ましい。添加量が前記範囲を外れると、前記１液タ
イプの場合と同様の問題を生じ易くなる。Further, an inorganic filler is added to the base material. As the inorganic filler, the same one as the one-pack type is used, and fumed silica is particularly preferable. The addition amount of the inorganic filler is preferably 2 to 50 parts by weight based on 100 parts by weight of the main agent. If the addition amount is out of the above range, the same problem as in the case of the one-liquid type is likely to occur.
【００３１】さらに、２液タイプにあっては、通常触媒
が混合される。触媒としては、白金系触媒が一般的であ
り、塩化白金酸、酸化白金、オレフィン白金錯塩等があ
る。Further, in the case of the two-liquid type, a catalyst is usually mixed. As the catalyst, a platinum-based catalyst is generally used, and examples thereof include chloroplatinic acid, platinum oxide, and olefin platinum complex.
【００３２】また、１液タイプ、２液タイプのいずれに
あっても、前記シリコーンゲル原料には反応性シリコー
ンオイルを添加するのが好ましい。反応性シリコーンオ
イルとは、水酸基価を有するシリコーンオリゴマーをい
う。具体的には、１官能物と２官能物があって、官能基
として下記の（１）〜（５）構造のものが挙げられる。It is preferable to add a reactive silicone oil to the silicone gel raw material in either one-pack type or two-pack type. The reactive silicone oil refers to a silicone oligomer having a hydroxyl value. Specifically, there are a monofunctional substance and a bifunctional substance, and the functional groups include those having the following structures (1) to (5).
【００３３】[0033]
【化１】 Embedded image
【００３４】前記反応性シリコーンオイルを添加混合す
ることによって、シリコーンゲル層２１が硬くなりすぎ
るのを防止でき、良好な密着性を得ることができる。１
液タイプにあっては、シリコーンゲル原料１００重量部
に対して１０〜１００重量部が好ましく、２液タイプに
あっては主剤１００重量部に対して１０〜５００重量部
が好ましい。By adding and mixing the reactive silicone oil, the silicone gel layer 21 can be prevented from becoming too hard, and good adhesion can be obtained. 1
In the case of the liquid type, the amount is preferably 10 to 100 parts by weight based on 100 parts by weight of the silicone gel raw material, and in the case of the two-liquid type, the amount is preferably 10 to 500 parts by weight based on 100 parts by weight of the main agent.
【００３５】なお、この発明において、使用可能な市販
シリコーンゲル原料として、東芝シリコーン社製のＴＯ
ＳＩＬシリーズ：ＴＳＥ３０７０、ＹＥ５８１８、ロー
ヌプラーン社製のＲＴＶ：Ｊ５３０、ワッカー社製のＲ
ＴＶ：Ｍ４４４０等を挙げることができる。In the present invention, TOSHIBA Silicone's TO
SIL series: TSE3070, YE5818, RTV: R530 manufactured by Rhone Pran, R: manufactured by Wacker
TV: M4440 and the like.
【００３６】前記シリコーンゲル層２１は多孔シート１
１の片面で一体に形成されたものが好ましい。その一体
化により、多孔シート１１とシリコーンゲル層２１とが
強固に一体化し、ジョイント部等への装着等の際にシリ
コーンゲル層２１が多孔シート１１から剥離し難くな
る。なお、前記一体化は、多孔シート１１の片面にシリ
コーンゲル原料を充填し、硬化させることによって、容
易に行うことができる。The silicone gel layer 21 is formed of the porous sheet 1
One formed integrally on one side is preferred. By the integration, the porous sheet 11 and the silicone gel layer 21 are firmly integrated, and it is difficult for the silicone gel layer 21 to peel off from the porous sheet 11 at the time of attachment to a joint or the like. The integration can be easily performed by filling one side of the porous sheet 11 with a silicone gel raw material and curing the raw material.
【００３７】[0037]
【実施例】・実施例１，２ ２液タイプのＲＴＶ樹脂（商品名：ＣＹ５２−２７６、
東レ・ダウコーニングシリコーン社製）を、主剤：硬化
剤＝１００：１１５、白金触媒（商品名：ＸＣ９１−Ａ
６２５９、東芝シリコーン社製）０．１重量部添加して
撹拌した後、真空脱泡し、シリコーンゲル原料を調製し
た。前記シリコーンゲル原料を、あらかじめ多孔シート
を敷いた注入型キャビティ内に所定量注入し、キャビテ
ィ面を９０℃に保って硬化させた後、シリコーンゲル層
が多孔シートの片面に一体成形された、厚み５ｍｍの平
板状積層品を脱型した。多孔シートは、実施例１ではポ
リエステルからなる不織布を用い、実施例２ではポリア
ミド樹脂繊維のマルチフィラメントからなる平織りであ
って、２００メッシュ、線径３０ｄのものを用いた。そ
の後、積層品をトムソン刃で打ち抜いて所要サイズの防
水封止材を得た。なお、前記トムソン刃は、注入型キャ
ビティのサイズや、求められる製品サイズ等に応じて適
宜行われる。EXAMPLES Examples 1 and 2 RTV resin of two liquid type (trade name: CY52-276,
Toray Dow Corning Silicone Co., Ltd.), a base agent: curing agent = 100: 115, a platinum catalyst (trade name: XC91-A)
6259, manufactured by Toshiba Silicone Co., Ltd.), stirred and then degassed in vacuo to prepare a silicone gel raw material. A predetermined amount of the silicone gel raw material is injected into an injection mold cavity previously laid with a porous sheet, and the cavity surface is cured at 90 ° C., and then a silicone gel layer is integrally formed on one surface of the porous sheet. The 5 mm plate-shaped laminate was demolded. The porous sheet used in Example 1 was a nonwoven fabric made of polyester, and Example 2 used a plain weave made of polyamide resin fiber multifilaments having a mesh of 200 mesh and a wire diameter of 30d. Thereafter, the laminated product was punched out with a Thomson blade to obtain a waterproof sealing material of a required size. The Thomson blade is appropriately formed according to the size of the injection mold cavity, the required product size, and the like.
【００３８】・実施例３，４ 実施例２において、主剤と硬化剤及び触媒の混合後、煙
霧質シリカ（商品名：＃２００、日本アエロジル社製）
を主剤１００重量部に対して１０重量部添加し、さらに
撹拌した後に真空脱泡してシリコーンゲル原料を調製し
た。その他は実施例１，２と同様にして、防水封止材を
得た。Examples 3 and 4 In Example 2, after mixing the main agent, the curing agent and the catalyst, the fumed silica (trade name: # 200, manufactured by Nippon Aerosil Co., Ltd.)
Was added to 100 parts by weight of the base material, and the mixture was further stirred and then degassed in vacuo to prepare a silicone gel raw material. Otherwise, in the same manner as in Examples 1 and 2, a waterproof sealing material was obtained.
【００３９】・実施例５．６ 実施例３．４において、煙霧質シリカを添加混合する際
に、主剤１００重量部に対して反応性シリコーンオイル
（商品名：ＳＨ１１０７、東レ・ダウコーニングシリコ
ーン社製）１５０重量部を添加混合した他は、実施例
３、４と同様にして防水封止材を得た。Example 5.6 In Example 3.4, when adding and mixing fumed silica, reactive silicone oil (trade name: SH1107, manufactured by Dow Corning Toray Silicone Co., Ltd.) was used with respect to 100 parts by weight of the main agent. ) A waterproof sealing material was obtained in the same manner as in Examples 3 and 4, except that 150 parts by weight were added and mixed.
【００４０】・実施例６，７ １液タイプのＲＴＶ樹脂（商品名：ＳＥ１８８０ＧＥ
Ｌ、東レ・ダウコーニングシリコーン社製）１００重量
部に対して、煙霧質シリカ（商品名：＃２００、日本ア
エロジル社製）１０重量部と、反応性シリコーンオイル
（商品名：ＳＨ１１０７、東レ・ダウコーニングシリコ
ーン社製）５０重量部を添加混合し、真空脱泡してシリ
コーンゲル原料を調製した。前記シリコーンゲル原料
を、あらかじめ多孔シートを敷いた注入型キャビティ内
に所定量注入し、硬化させた後、シリコーンゲル層が多
孔シートの片面に一体成形された、厚み５ｍｍの平板状
積層品を脱型した。Examples 6 and 7 One-component RTV resin (trade name: SE1880GE)
L, 100 parts by weight of Dow Corning Toray Silicone Co., Ltd.), 10 parts by weight of fumed silica (trade name: # 200, manufactured by Nippon Aerosil Co., Ltd.) and reactive silicone oil (trade name: SH1107, Dow Corning Toray) 50 parts by weight of Corning Silicone Co., Ltd.) were added and mixed, followed by vacuum degassing to prepare a silicone gel raw material. After injecting a predetermined amount of the silicone gel raw material into an injection mold cavity in which a porous sheet is preliminarily laid, and curing, a 5 mm-thick plate-shaped laminate in which a silicone gel layer is integrally formed on one surface of the porous sheet is removed. Typed.
【００４１】・比較例 ２液タイプのシリコーンゲル（商品名：ＴＳＥ３０７
０、東芝シリコーン社製）を、その主剤：硬化剤を１０
０：１５０にし、白金触媒（商品名：ＸＣ９１−Ａ６５
２９、東芝シリコーン社製）０．１重量部添加して混合
して撹拌した後、真空脱泡し、シリコーンゲル原料を調
製した。前記シリコーンゲル原料を注入型キャビティ内
に所定量注入し、キャビティ面を９０℃に保って硬化さ
せた後、厚み５ｍｍの平板状シリコーンゲル製品を脱型
した。Comparative Example Two-pack type silicone gel (trade name: TSE307)
0, manufactured by Toshiba Silicone Co., Ltd.)
0: 150 and a platinum catalyst (trade name: XC91-A65)
29, manufactured by Toshiba Silicone Co., Ltd.), mixed and stirred, and then degassed under vacuum to prepare a silicone gel raw material. A predetermined amount of the silicone gel raw material was injected into the injection mold cavity, the cavity surface was cured at 90 ° C., and the flat silicone gel product having a thickness of 5 mm was demolded.
【００４２】前記実施例及び比較例に対して、応力緩和
性（長期にわたる封止性）を評価した。評価方法は、Ｊ
ＩＳ Ｋ ６４０１に準拠するＣＬＤ（圧縮加重）測定
法にしたがい、ＣＬＤ（圧縮量）４０％の値を初期値と
し、２５℃で２２時間そのまま放置したときの値を初期
値で割って百分率を計算し、その百分率の値が大なる
程、応力緩和性が高いもの、すなわち、長期にわたる封
止性が高いものとした。また、高温下でシリコーンゲル
層に液だれが見られるか否かを調べた。その方法は、６
０℃の雰囲気下、試験片を４５度の斜面に静置した状態
で２２時間放置し、シリコーンゲル層に液だれを生じる
か否かを目視で判断した。それらの結果を表１に示す。With respect to the above Examples and Comparative Examples, stress relaxation properties (long-term sealing properties) were evaluated. Evaluation method is J
According to the CLD (compression weight) measurement method based on IS K6401, a value of 40% of CLD (compression amount) is set as an initial value, and a value calculated by dividing the value when left at 25 ° C. for 22 hours by the initial value by the initial value is calculated. The larger the value of the percentage, the higher the stress relaxation property, that is, the higher the long-term sealing property. Further, it was examined whether dripping was observed in the silicone gel layer at a high temperature. The method is 6
In a 0 ° C. atmosphere, the test piece was allowed to stand for 22 hours while being left on a 45 ° slope, and it was visually determined whether or not the silicone gel layer was dripped. Table 1 shows the results.
【００４３】[0043]
【表１】 [Table 1]
【００４４】[0044]
【発明の効果】以上説明したように、請求項１の発明に
係る防水封止材によれば、シリコーンゲル層が適度な柔
軟性を有し、しかも自己接着性を有するものであるた
め、シリコーンゲル層の表面がジョイント部等に密着
し、その密着部を確実に防水封止することができる。As described above, according to the waterproof sealing material according to the first aspect of the present invention, since the silicone gel layer has appropriate flexibility and self-adhesiveness, The surface of the gel layer closely adheres to the joint and the like, and the tightly adhered part can be reliably sealed with water.
【００４５】また、シリコーンゲル層は多孔シートの存
在によって形状が保持されるため、ジョイント部等の外
面やコネクター内への装着が容易である。しかも、多孔
シートの孔によって、多孔シートとシリコーンゲル層と
の一体性が強くなって、防水封止作業が容易になる。Further, since the shape of the silicone gel layer is maintained by the presence of the porous sheet, the silicone gel layer can be easily mounted on the outer surface of the joint or the like or in the connector. In addition, due to the holes in the porous sheet, the integrity of the porous sheet and the silicone gel layer is strengthened, and the waterproof sealing operation is facilitated.
【００４６】請求項２の発明によれば、多孔シートとシ
リコーンゲル層とが強固に一体化し、ジョイント部等へ
の装着等の際にシリコーンゲル層が多孔シートから剥離
するおそれがない。According to the second aspect of the present invention, the porous sheet and the silicone gel layer are firmly integrated, and there is no possibility that the silicone gel layer is peeled off from the porous sheet when it is attached to a joint or the like.
【００４７】請求項３の発明によれば、無機充填剤を添
加することによって、シリコーンゲル層の強度増大や物
性改良効果が得られ、さらにはべた付き性の少ない適度
な自己接着性及び密着性を得ることができ、防水封止性
を高めることができる。According to the third aspect of the invention, by adding an inorganic filler, an effect of increasing the strength of the silicone gel layer and improving the physical properties can be obtained, and furthermore, a suitable self-adhesiveness and adhesiveness with less stickiness. Can be obtained, and the waterproof sealing property can be improved.
【００４８】請求項４の発明によれば、無機充填剤及び
効果剤を所定範囲とすることによって、シリコーンゲル
層の強度増大や物性改良効果や、適度な自己接着性、密
着性及び柔軟性を付与することができ、より確実にジョ
イント部等に密着させることができる。According to the fourth aspect of the present invention, by setting the inorganic filler and the effecting agent in a predetermined range, the effect of increasing the strength of the silicone gel layer and improving the physical properties, and the appropriate self-adhesiveness, adhesion and flexibility can be obtained. And can be more securely brought into close contact with a joint portion or the like.
【００４９】請求項５の発明によれば、無機充填剤とし
て用いる煙霧質シリカが、シリコーンゲル原料との相溶
性、混練性の良好なものであるため、充填効果が良好
で、物理的強度増大や適度な密着性付与効果に優れる。According to the fifth aspect of the present invention, since the fumed silica used as the inorganic filler has good compatibility with the silicone gel raw material and good kneading properties, the filling effect is good and the physical strength is increased. Excellent moderate adhesion effect.
【００５０】請求項６の発明によれば、反応性シリコー
ンオイルの添加によって、シリコーンゲル層が硬くなり
すぎるのを防止でき、良好な密着性を得ることができ
る。According to the sixth aspect of the present invention, the addition of the reactive silicone oil can prevent the silicone gel layer from becoming too hard, and can obtain good adhesion.
【図１】この発明の一実施例に係る防水封止材の断面図
である。FIG. 1 is a sectional view of a waterproof sealing material according to an embodiment of the present invention.
【図２】この発明の防水封止材に対する使用状態の一例
を示す断面図である。FIG. 2 is a cross-sectional view showing an example of a use state of the waterproof sealing material of the present invention.
【図３】他の使用例を示す断面図である。FIG. 3 is a cross-sectional view showing another example of use.
【図４】さらに他の使用例を示す断面図である。FIG. 4 is a cross-sectional view showing still another usage example.
１０ 防水封止材 １１ 多孔シート ２１ シリコーンゲル層 Reference Signs List 10 waterproof sealing material 11 porous sheet 21 silicone gel layer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｃ０８Ｌ 83/04 Ｃ０８Ｌ 83/04 Ｈ０１Ｒ 13/52 ３０１ Ｈ０１Ｒ 13/52 ３０１Ｚ //(Ｃ０８Ｌ 83/04 83:05） Ｆターム(参考） 4F100 AA20H AH06H AK41 AK46 AK52B AS00A BA02 CA23 DG01 DG15 EH31 EH312 GB33 JD05 4J002 CP031 CP042 CP063 CP121 DE146 DE236 DG046 DJ016 DJ056 EX037 FD016 FD142 FD147 GF00 GQ00 5E087 LL03 LL12 QQ04 RR12 RR25──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C08L 83/04 C08L 83/04 H01R 13/52 301 H01R 13/52 301Z // (C08L 83/04 83: 05) F-term (reference) 4F100 AA20H AH06H AK41 AK46 AK52B AS00A BA02 CA23 DG01 DG15 EH31 EH312 GB33 JD05 4J002 CP031 CP042 CP063 CP121 DE146 DE236 DG046 DJ016 DJ056 EX037 FD016 FD142 FD147 GF12 G04Q03
Claims (6)
積層した防水封止材。1. A waterproof sealing material in which a silicone gel layer is laminated on one surface of a porous sheet.
一体成形されてなる請求項１記載の防水封止材。2. The waterproof sealing material according to claim 1, wherein a silicone gel layer is formed integrally with the porous sheet.
した１液タイプのシリコーンゲルからなる請求項１また
は２記載の防水封止材。3. The waterproof sealing material according to claim 1, wherein the silicone gel layer is formed of a one-pack type silicone gel to which an inorganic filler is added.
に無機充填剤を２〜５０重量部、硬化剤を５０〜２００
重量部添加した２液タイプのシリコーンゲルからなる請
求項１または２記載の防水封止材。4. The silicone gel layer comprises 2 to 50 parts by weight of an inorganic filler and 100 to 200 parts by weight of a curing agent per 100 parts by weight of a base material.
3. The waterproof sealing material according to claim 1, comprising a two-part type silicone gel to which parts by weight are added.
３または４記載の防水封止材。5. The waterproof sealing material according to claim 3, wherein the inorganic filler is fumed silica.
ルを添加した請求項１ないし５のいずれかに記載の防水
封止材。6. The waterproof sealing material according to claim 1, wherein a reactive silicone oil is added to the silicone gel.