JP2000275437A - Optical film, optical member and optical element - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a practical optical film excellent in scattering anisotropy with respect to linearly polarized light, being easy to be manufactured, and being excellent in thermal stability, and an optical element using the same. SOLUTION: An optical film 1 comprises a resin film containing microareas (e) in a dispersed fashion, which microareas consist of a polymer liquid crystal with a polymerization degree of 8 or more, and differences Δn1, Δn2 in refractive index between the microareas and other portions are 0.03 or more (Δn1) in a direction perpendicular to an axial direction in which the maximum transmission of linear polarization is shown, and are 50% or less (Δn2) of Δn1 in the axial direction of the maximum transmission. An optical element comprises at least either one of a polarizing plate or a phase difference plate and a laminate having one or two or more layers of the optical films. Thus, a heat- resistant liquid-crystal display device can be obtained which provides linearly polarized light that shows scattering anisotropy such that it is scattered in the direction of Δn1 and transmitted in the direction of Δn2, and which absorbs little light so that it is excellent in brightness and visibility as well as in thermal stability of optical functions, so that it can be put to practical use.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の技術分野】本発明は、直線偏光の散乱異方性や
熱的安定性に優れて液晶表示装置等の視認性や輝度や耐
久性等の向上に好適な光学フィルム及び光学素子に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical film and an optical element having excellent scattering anisotropy and thermal stability of linearly polarized light and suitable for improving visibility, luminance, durability and the like of a liquid crystal display device.

【０００２】[0002]

【発明の背景】従来、母材中に屈折率異方性の領域を分
散含有させて直線偏光に対し散乱異方性を示す光学フィ
ルムとしては、熱可塑性樹脂と低分子液晶との組合せか
らなるもの、低分子液晶と光架橋性低分子液晶との組合
せからなるもの、ポリエステルとアクリル系樹脂又はポ
リスチレンとの組合せからなるもの、ポリビニルアルコ
ールと低分子液晶との組合せからなるものが知られてい
た（ＵＳＰ２１２３９０号、ＷＯ８７／０１８２２号公
報、ＥＰ０５０６１７号、ＷＯ９７／３２２２４号公
報、ＷＯ９７／４１４８４号公報、特開平９−２７４１
０８号公報）。BACKGROUND OF THE INVENTION Conventionally, an optical film exhibiting scattering anisotropy with respect to linearly polarized light by dispersing a region having a refractive index anisotropy in a base material is composed of a combination of a thermoplastic resin and a low-molecular liquid crystal. Those comprising a combination of a low-molecular liquid crystal and a photocrosslinkable low-molecular liquid crystal, those comprising a combination of a polyester and an acrylic resin or polystyrene, and those comprising a combination of a polyvinyl alcohol and a low-molecular liquid crystal were known. (USP 212390, WO 87/01822, EP 050617, WO 97/32224, WO 97/41484, Japanese Patent Application Laid-Open No. 9-2741.
08 publication).

【０００３】前記の光学フィルムには、その直線偏光に
対する散乱異方性に基づく偏光分離機能や光拡散機能に
より、液晶表示装置等の視認性や輝度等を向上させるこ
となどが期待されている。しかしながら、従来の光学フ
ィルムではその製造が煩雑であり、耐熱性等の実用的安
定性に乏しい問題点があった。[0003] The above optical film is expected to improve the visibility and luminance of a liquid crystal display device and the like by a polarization separation function and a light diffusion function based on scattering anisotropy with respect to linearly polarized light. However, the conventional optical film has a problem that its production is complicated and has poor practical stability such as heat resistance.

【０００４】[0004]

【発明の技術的課題】本発明は、直線偏光に対する散乱
異方性に優れると共に、容易に製造できて熱的安定性に
優れる実用的な光学フィルム、及びそれを用いた光学素
子の開発を課題とする。SUMMARY OF THE INVENTION An object of the present invention is to develop a practical optical film which has excellent scattering anisotropy with respect to linearly polarized light, can be easily manufactured and has excellent thermal stability, and an optical element using the same. And

【０００５】[0005]

【課題の解決手段】本発明は、重合度が８以上の高分子
液晶からなる微小領域を分散含有する樹脂フィルムより
なり、その微小領域と他の部分との屈折率差△ｎ１、△
ｎ２が直線偏光の最大透過率を示す軸方向に直交する方
向において０．０３以上（△ｎ１）、かつ最大透過率の
軸方向において前記△ｎ１の５０％以下（△ｎ２）であ
ることを特徴とする光学フィルム、及び偏光板又は位相
差板の少なくとも一方と、前記光学フィルムの１層又は
２層以上を有する積層体からなることを特徴とする光学
素子を提供するものである。According to the present invention, there is provided a resin film in which a minute region composed of a polymer liquid crystal having a degree of polymerization of 8 or more is dispersed and contained, and a refractive index difference between the minute region and another portion is {n1,}.
n2 is 0.03 or more (△ n1) in a direction orthogonal to the axial direction showing the maximum transmittance of linearly polarized light, and 50% or less of the △ n1 (△ n2) in the axial direction of the maximum transmittance. And an optical element comprising a laminate having at least one of a polarizing plate and a retardation plate, and one or more layers of the optical film.

【０００６】[0006]

【発明の効果】本発明による光学フィルムは、直線偏光
の最大透過率を示す軸方向（△ｎ２方向）では直線偏光
がその偏光状態を良好に維持して透過し、前記△ｎ２方
向と直交する方向（△ｎ１方向）では樹脂フィルムと微
小領域との屈折率差△ｎ１に基づいて直線偏光が散乱さ
れその偏光状態が緩和ないし解消して、優れた散乱異方
性を示す。According to the optical film of the present invention, in the axial direction (Δn2 direction) showing the maximum transmittance of linearly polarized light, linearly polarized light is transmitted while maintaining its polarization state in a good condition, and is orthogonal to the Δn2 direction. In the direction (Δn1 direction), linearly polarized light is scattered based on the refractive index difference Δn1 between the resin film and the minute region, and the polarization state is relaxed or eliminated, and excellent scattering anisotropy is exhibited.

【０００７】また重合度が８以上の高分子系微小領域を
分散含有する樹脂フィルムよりなり、その取扱性に優れ
て光学フィルムの製造が容易であると共に均一性に優れ
る微小領域を安定性よく形成でき、得られた光学フィル
ムが優れた熱的安定性を示して光学機能の安定性に優れ
実用性に優れている。ちなみに８０℃以上の高温にても
外観や散乱性等の光学特性に変化を生じないものの形成
も可能である。Further, the resin film is made of a resin film containing a polymer-based microregion having a degree of polymerization of 8 or more in a dispersed state. The microfilm has excellent handleability, is easy to manufacture an optical film, and has excellent uniformity. The obtained optical film shows excellent thermal stability, and has excellent stability of optical functions and excellent practicality. By the way, it is possible to form a material having no change in optical characteristics such as appearance and scattering even at a high temperature of 80 ° C. or higher.

【０００８】前記の結果、その散乱異方性による偏光特
性等に基づいて光の吸収による損失や発熱を防止でき、
また良好な耐熱性にも基づいて輝度や視認性に優れると
共に、光学機能の熱的安定性に優れて実用足りうる耐熱
性を有する液晶表示装置を得ることができる。As a result, loss and heat generation due to light absorption can be prevented based on the polarization characteristics and the like due to the scattering anisotropy.
In addition, a liquid crystal display device which is excellent in luminance and visibility based on good heat resistance, has excellent thermal stability of optical functions, and has sufficient heat resistance for practical use can be obtained.

【０００９】[0009]

【発明の実施形態】本発明による光学フィルムは、重合
度が８以上の高分子液晶からなる微小領域を分散含有す
る樹脂フィルムよりなり、その微小領域と他の部分との
屈折率差△ｎ１、△ｎ２が直線偏光の最大透過率を示す
軸方向に直交する方向において０．０３以上（△ｎ
１）、かつ最大透過率の軸方向において前記△ｎ１の５
０％以下（△ｎ２）であるものからなる。その例を図１
に示した。１が光学フィルムで、ｅがその微小領域であ
る。なお、２は被着体に接着するための粘着層からなる
接着層、２１は粘着層を仮着カバーするセパレータであ
る。DETAILED DESCRIPTION OF THE INVENTION The optical film according to the present invention is composed of a resin film in which minute regions composed of high-molecular liquid crystal having a degree of polymerization of 8 or more are dispersed and contained, and the refractive index difference Δn1, between the minute regions and other parts, Δn2 is 0.03 or more (Δn) in the direction orthogonal to the axial direction showing the maximum transmittance of linearly polarized light.
1) and in the axial direction of the maximum transmittance,
0% or less (△ n2). Figure 1 shows an example
It was shown to. 1 is an optical film, and e is its minute area. Reference numeral 2 denotes an adhesive layer formed of an adhesive layer for adhering to the adherend, and reference numeral 21 denotes a separator for temporarily covering the adhesive layer.

【００１０】光学フィルムの形成は、例えば樹脂フィル
ムを形成するための樹脂の１種又は２種以上と、微小領
域を形成するための高分子液晶の１種又は２種以上を混
合し、高分子液晶を微小領域の状態で分散含有する樹脂
フィルムを形成して適宜な方式で配向処理し、複屈折特
性が相違する領域を形成する方法などにて行うことがで
きる。The optical film is formed, for example, by mixing one or more of a resin for forming a resin film and one or more of a liquid crystal polymer for forming a fine region, It can be carried out by a method of forming a resin film containing liquid crystal dispersedly in a fine region, orienting it by an appropriate method, and forming regions having different birefringence characteristics.

【００１１】前記の樹脂フィルムを形成する樹脂として
は、光透過性、就中、光透過率に優れる適宜な樹脂を用
いることができ、特に限定はない。従って耐熱性なども
適宜に設定することができる。ちなみに前記樹脂の例と
しては、ポリエチレンテレフタレートやポリエチレンナ
フタレートの如きポリエステル系樹脂、ポリスチレンや
アクリロニトリル・スチレン共重合体の如きスチレン系
樹脂、ポリエチレンやポリプロピレン、シクロ系ないし
ノルボルネン構造を有するポリオレフィンやエチレン・
プロピレン共重合体の如きオレフィン系樹脂があげられ
る。As the resin forming the resin film, any suitable resin having excellent light transmittance, particularly, excellent light transmittance can be used, and there is no particular limitation. Accordingly, heat resistance and the like can be set as appropriate. Incidentally, examples of the resin include polyester resins such as polyethylene terephthalate and polyethylene naphthalate, styrene resins such as polystyrene and acrylonitrile-styrene copolymer, polyethylene and polypropylene, and polyolefin and ethylene having a cyclo or norbornene structure.
An olefin resin such as a propylene copolymer can be used.

【００１２】またポリメチルメタクリレートの如きアク
リル系樹脂、二酢酸セルロースや三酢酸セルロースの如
きセルロース系樹脂、ナイロンや芳香族ポリアミドの如
きアミド系樹脂、カーボネート系樹脂や塩化ビニル系樹
脂、イミド系樹脂やスルホン系樹脂、ポリエーテルスル
ホン系樹脂やポリエーテルエーテルケトン系樹脂、ポリ
フェニレンスルフィド系樹脂やビニルアルコール系樹
脂、塩化ビニリデン系樹脂やビニルブチラール系樹脂、
アリレート系樹脂やポリオキシメチレン系樹脂、それら
のブレンド物なども前記した樹脂の例としてあげられ
る。Acrylic resins such as polymethyl methacrylate, cellulose resins such as cellulose diacetate and cellulose triacetate, amide resins such as nylon and aromatic polyamide, carbonate resins, vinyl chloride resins, imide resins, and the like. Sulfone resins, polyethersulfone resins and polyetheretherketone resins, polyphenylene sulfide resins and vinyl alcohol resins, vinylidene chloride resins and vinyl butyral resins,
Allylate-based resins, polyoxymethylene-based resins, and blends thereof are also examples of the above-mentioned resins.

【００１３】耐熱性などの点より好ましく用いうる樹脂
は、加重たわみ温度が８０℃以上で、かつガラス転移温
度が１１０℃以上、就中１１５℃以上、特に１２０℃以
上のものである。また液晶表示装置等に用いる場合には
可視光領域での光透過率に優れる樹脂が好ましく用いう
る。なお前記の加重たわみ温度は、ＪＩＳ Ｋ ７２０
７に準じ、１８．５kgf／cm^２の曲げ応力を加熱浴中の
高さ１０mmの試験片に加えながら２℃／分で伝熱媒体を
昇温させ、試験片のたわみ量が０．３２mmに達したとき
の伝熱媒体の温度にて定義される。The resin which can be preferably used from the viewpoint of heat resistance and the like has a weight deflection temperature of 80 ° C. or more and a glass transition temperature of 110 ° C. or more, especially 115 ° C. or more, particularly 120 ° C. or more. When used in a liquid crystal display device or the like, a resin having excellent light transmittance in a visible light region can be preferably used. The weight deflection temperature described above is JIS K 720
While applying a bending stress of 18.5 kgf / cm ² to a test piece having a height of 10 mm in a heating bath, the heat transfer medium was heated at a rate of 2 ° C./min according to the method described in No. 7, and the deflection of the test piece was reduced to 0.32 mm. It is defined by the temperature of the heat transfer medium when it is reached.

【００１４】一方、微小領域を形成する高分子液晶とし
ても、重合度が８以上の主鎖型や側鎖型等の適宜な液晶
ポリマーを用いることができ、その種類について特に限
定はない。重合度が８未満の液晶では、フィルム形成用
の樹脂と混合した場合に形成される微小領域のバラツキ
が大きくて粒径分布が広範囲となり、光学特性の均質性
に乏しくなる。On the other hand, as the high-molecular liquid crystal forming the minute region, an appropriate liquid crystal polymer such as a main chain type or a side chain type having a degree of polymerization of 8 or more can be used, and the type thereof is not particularly limited. In a liquid crystal having a degree of polymerization of less than 8, when mixed with a resin for forming a film, a minute region formed has a large variation, and the particle size distribution becomes wide, resulting in poor uniformity of optical characteristics.

【００１５】前記微小領域の均一な粒径分布の形成性や
熱的安定性、フィルムへの成形性や配向処理の容易性な
どの点より好ましく用いうる高分子液晶の重合度は、１
０以上、就中１２〜１万、特に１５〜２０００のもので
ある。The degree of polymerization of the high-molecular liquid crystal which can be preferably used from the viewpoints of the formability of a uniform particle size distribution of the fine regions, the thermal stability, the moldability into a film, and the ease of alignment treatment is as follows.
0 or more, especially 120,000 to 10000, especially 15 to 2000.

【００１６】配向処理による上記した屈折率差△ｎ^１、
△ｎ^２の制御性などの点よりは、ガラス転移温度が５０
℃以上で、併用の樹脂フィルムを形成する樹脂のガラス
転移温度よりも低い温度域でネマチック液晶相を呈する
ものが好ましく用いうる。ちなみにその具体例として
は、下記の一般式で表されるモノマー単位を有する側鎖
型の液晶ポリマーなどがあげられる。The refractive index difference Δn ¹ ,
△ n from the viewpoint of the ^second controllability has a glass transition temperature of 50
Those exhibiting a nematic liquid crystal phase in a temperature range lower than the glass transition temperature of the resin forming the combined resin film at a temperature of at least ° C can be preferably used. Incidentally, specific examples thereof include a side chain type liquid crystal polymer having a monomer unit represented by the following general formula.

【００１７】一般式： General formula:

【００１８】前記一般式においてＸは、液晶ポリマーの
主鎖を形成する骨格基であり、線状や分岐状や環状等の
適宜な連結鎖にて形成されていてよい。ちなみにその例
としては、ポリアクリレート類やポリメタクリレート
類、ポリ−α−ハロアクリレート類やポリ−α−シアノ
アクリレート類、ポリアクリルアミド類やポリアクリロ
ニトリル類、ポリメタクリロニトリル類やポリアミド
類、ポリエステル類やポリウレタン類、ポリエーテル類
やポリイミド類、ポリシロキサン類などがあげられる。In the above general formula, X is a skeletal group forming the main chain of the liquid crystal polymer, and may be formed by an appropriate connecting chain such as linear, branched or cyclic. Incidentally, examples thereof include polyacrylates and polymethacrylates, poly-α-haloacrylates and poly-α-cyanoacrylates, polyacrylamides and polyacrylonitriles, polymethacrylonitriles and polyamides, polyesters and Examples include polyurethanes, polyethers, polyimides, and polysiloxanes.

【００１９】またＹは、主鎖より分岐するスペーサ基で
あり、屈折率制御等の光学フィルムの形成性などの点よ
り好ましいスペーサ基Ｙは、例えばエチレンやプロピレ
ン、ブチレンやペンチレン、ヘキシレンなどであり、就
中エチレンが好ましい。Y is a spacer group branched from the main chain, and a preferable spacer group Y from the viewpoint of forming an optical film such as controlling the refractive index is, for example, ethylene, propylene, butylene, pentylene, hexylene and the like. , Especially ethylene.

【００２０】一方、Ｚはネマチック配向性を付与するメ
ソゲン基であり、下記の化合物などがあげられる。 On the other hand, Z is a mesogenic group for imparting nematic orientation, and examples thereof include the following compounds.

【００２１】前記化合物における末端置換基Ａは、例え
ばシアノ基やアルキル基、アルケニル基やアルコキシ
基、オキサアルキル基や水素の１個以上がフッ素又は塩
素にて置換されたハロアルキル基やハロアルコキシ基や
ハロアルケニル基などの適宜なものであってよい。The terminal substituent A in the compound may be, for example, a cyano group, an alkyl group, an alkenyl group, an alkoxy group, an oxaalkyl group, a haloalkyl group in which at least one of hydrogen is substituted by fluorine or chlorine, a haloalkoxy group, It may be an appropriate one such as a haloalkenyl group.

【００２２】前記において、スペーサ基Ｙとメソゲン基
Ｚはエーテル結合、すなわち−Ｏ−を介して結合してい
てもよい。またメソゲン基Ｚにおけるフェニル基は、そ
の１個又は２個の水素がハロゲンで置換されていてもよ
く、その場合、ハロゲンとしては塩素又はフッ素が好ま
しい。In the above, the spacer group Y and the mesogen group Z may be bonded via an ether bond, that is, via —O—. In the phenyl group in the mesogen group Z, one or two hydrogens may be substituted with a halogen. In this case, the halogen is preferably chlorine or fluorine.

【００２３】上記したネマチック配向性の側鎖型液晶ポ
リマーは、前記一般式で表されるモノマー単位を有する
ホモポリマーやコポリマー等の適宜な熱可塑性樹脂であ
ればよく、就中モノドメイン配向性に優れるものが好ま
しい。The nematic alignment side chain type liquid crystal polymer may be any suitable thermoplastic resin such as a homopolymer or a copolymer having a monomer unit represented by the above general formula. Excellent ones are preferred.

【００２４】上記したネマチック配向性の高分子液晶を
用いた光学フィルムの形成は、例えば樹脂フィルムを形
成するための樹脂と、その樹脂のガラス転移温度よりも
低い温度域でネマチック液晶相を呈するガラス転移温度
が５０℃以上、就中６０℃以上、特に７０℃以上の高分
子液晶を混合して、高分子液晶を微小領域の状態で分散
含有する樹脂フィルムを形成した後、その微小領域を形
成する高分子液晶を加熱処理してネマチック液晶相に配
向させ、その配向状態を冷却固定する方法などにて行う
ことができる。In the formation of the optical film using the nematic-oriented polymer liquid crystal, for example, a resin for forming a resin film and a glass exhibiting a nematic liquid crystal phase in a temperature range lower than the glass transition temperature of the resin are used. A polymer liquid crystal having a transition temperature of 50 ° C. or higher, particularly 60 ° C. or higher, particularly 70 ° C. or higher is mixed to form a resin film containing the polymer liquid crystal dispersed in a fine region, and then the fine region is formed. The polymer liquid crystal to be formed can be subjected to a heat treatment to align the liquid crystal in a nematic liquid crystal phase, and the alignment state can be fixed by cooling.

【００２５】上記において用いる樹脂フィルム形成用の
樹脂と高分子液晶の組合せとしては、得られる光学フィ
ルムにおける微小領域の分散分布性などの点より、材料
同士が完全相溶性でない組合せ、就中、相分離する組合
せで用いることが好ましい。その組合せによる相溶性に
より分散分布性を制御することができる。相分離は、例
えば非相溶性の材料を溶媒にて溶液化する方式や加熱溶
融下に混合する方式などの適宜な方式にて行うことがで
きる。The combination of the resin for forming the resin film and the polymer liquid crystal used in the above is a combination in which the materials are not completely compatible with each other in view of the dispersion distribution of the minute regions in the obtained optical film. It is preferable to use a combination for separation. The dispersion distribution can be controlled by the compatibility of the combination. The phase separation can be performed by an appropriate method such as a method in which an incompatible material is made into a solution with a solvent or a method in which the materials are mixed while heating and melting.

【００２６】高分子液晶を微小領域の状態で分散含有す
る樹脂フィルム、すなわち配向処理対象のフィルムの形
成は、例えばキャスティング法や押出成形法、射出成形
法やロール成形法、流延成形法などの適宜な方式にて得
ることができ、モノマー状態で展開しそれを加熱処理や
紫外線等の放射線処理などにより重合してフィルム状に
製膜する方式などにても行うことができる。The formation of a resin film containing a polymer liquid crystal dispersed in a minute area, ie, a film to be subjected to an alignment treatment, is performed by, for example, a casting method, an extrusion molding method, an injection molding method, a roll molding method, a casting method, or the like. It can be obtained by an appropriate method, and can also be applied to a method of developing in a monomer state, polymerizing it by a heat treatment or a radiation treatment such as ultraviolet rays, and forming a film.

【００２７】微小領域の均等分布性に優れる光学フィル
ムを得る点などよりは、溶媒を介した形成材の混合液を
キャスティング法や流延成形法等にて製膜する方式が好
ましい。その場合、溶媒の種類や混合液の粘度、混合液
展開層の乾燥速度などにより微小領域の大きさや分布性
などを制御することができる。ちなみに微小領域の小面
積化には混合液の低粘度化や混合液展開層の乾燥速度の
急速化などが有利である。From the viewpoint of obtaining an optical film having excellent uniform distribution of minute regions, a method of forming a mixed solution of a forming material through a solvent by a casting method, a casting method, or the like is preferable. In this case, the size and distribution of the minute region can be controlled by the type of the solvent, the viscosity of the mixed solution, the drying speed of the mixed solution developing layer, and the like. Incidentally, in order to reduce the area of the minute region, it is advantageous to lower the viscosity of the mixed liquid and to increase the drying rate of the mixed liquid developing layer.

【００２８】配向処理対象のフィルムの厚さは、適宜に
決定しうるが、一般には配向処理性などの点より１μm
〜３mm、就中５μm〜１mm、特に１０〜５００μmとされ
る。なおフィルムの形成に際しては、例えば分散剤や界
面活性剤、紫外線吸収剤や色調調節剤、難燃剤や離型
剤、酸化防止剤などの適宜な添加剤を配合することがで
きる。The thickness of the film to be subjected to the orientation treatment can be determined as appropriate, but is generally 1 μm
３3 mm, especially 5 μm to 1 mm, especially 10 to 500 μm. In forming the film, for example, appropriate additives such as a dispersant, a surfactant, an ultraviolet absorber, a color tone adjuster, a flame retardant, a release agent, and an antioxidant can be blended.

【００２９】配向処理は、例えば樹脂フィルム中に微小
領域として分散分布する高分子液晶がネマチック相等の
目的とする液晶相を呈する温度に加熱して溶融させ、そ
れを配向規制力の作用化に配向させて急冷し、配向状態
を固定化する方式などにて行うことができる。その配向
状態は、可及的にモノドメイン状態にあることが光学特
性のバラツキ防止などの点より好ましい。In the alignment treatment, for example, the polymer liquid crystal dispersed and distributed as fine regions in the resin film is heated and melted to a temperature at which a desired liquid crystal phase such as a nematic phase is exhibited. Then, rapid cooling is performed to fix the alignment state. The orientation state is preferably in a mono-domain state as much as possible from the viewpoint of preventing variations in optical characteristics.

【００３０】なお前記の配向規制力としては、例えば樹
脂フィルムを適宜な倍率で延伸処理する方式による延伸
力やフィルム形成時のシェアリング力、電界や磁界など
の、高分子液晶を配向させうる適宜な規制力を適用で
き、その１種又は２種以上の規制力を作用させて高分子
液晶の配向処理を行うことができる。The above-mentioned alignment regulating force may be, for example, a stretching force by a method of stretching a resin film at an appropriate magnification, a sharing force at the time of film formation, an electric field or a magnetic field, etc. It is possible to apply the one or more kinds of restricting force to perform the alignment treatment of the polymer liquid crystal.

【００３１】従って光学フィルムにおける高分子液晶か
らなる微小領域以外の部分は、複屈折性を示すものであ
ってもよいし、等方性のものであってもよい。光学フィ
ルムの全体が複屈折性を示すものは、フィルム形成用の
樹脂に配向複屈折性のものを用いて上記した製膜過程に
おける分子配向などにより得ることができ、必要に応じ
例えば延伸処理等の公知の配向手段を加えて複屈折性を
付与ないし制御することができる。また微小領域以外の
部分が等方性の光学フィルムは、例えばフィルム形成用
の樹脂に等方性のものを用いて、そのフィルムを当該樹
脂のガラス転移温度以下の温度領域で延伸処理する方式
などにより得ることができる。Therefore, the portion of the optical film other than the microscopic region composed of the liquid crystal polymer may exhibit birefringence or may be isotropic. The entire optical film having birefringence can be obtained by the molecular orientation or the like in the film forming process described above by using an orientation birefringent resin for the film forming resin, and if necessary, for example, a stretching treatment or the like. The birefringence can be imparted or controlled by adding known orientation means. In addition, an optical film having an isotropic portion other than the minute region is, for example, a method of using an isotropic resin for forming a film and stretching the film in a temperature region equal to or lower than the glass transition temperature of the resin. Can be obtained by

【００３２】本発明による光学フィルムは、高分子液晶
からなる微小領域とそれ以外の部分、すなわち樹脂フィ
ルムからなる部分との屈折率差△ｎ１、△ｎ２が直線偏
光の最大透過率を示す軸方向に直交する方向において
０．０３以上（△ｎ１）であり、かつその最大透過率の
軸方向において前記△ｎ１の５０％以下（△ｎ２）に制
御したものである。かかる屈折率差とすることにより、
△ｎ１方向での散乱性に優れ、△ｎ２方向での偏光状態
の維持性及び直進透過性に優れるものとすることができ
る。In the optical film according to the present invention, the refractive index differences Δn1 and Δn2 between the minute region composed of the polymer liquid crystal and the other region, that is, the region composed of the resin film, indicate the maximum transmittance of linearly polarized light in the axial direction. Is controlled to be 0.03 or more (△ n1) in the direction perpendicular to the direction and to 50% or less (△ n2) of the Δn1 in the axial direction of the maximum transmittance. By setting such a refractive index difference,
It can be excellent in scattering in the Δn1 direction and excellent in maintaining the polarization state in the Δn2 direction and in straight transmissivity.

【００３３】散乱性などの点より△ｎ１方向における屈
折率差△ｎ１は、適度に大きいことが好ましく、０．０
４〜１、就中０．０４５〜０．５の屈折率差△ｎ１であ
ることが好ましい。一方、偏光状態の維持性などの点よ
り△ｎ２方向における屈折率差△ｎ２は、小さいほど好
ましく、０．０３以下、就中０．０２以下、特に０．０
１以下の屈折率差△ｎ２であることが好ましい。It is preferable that the refractive index difference Δn1 in the Δn1 direction is appropriately large from the viewpoint of scattering properties and the like.
It is preferable that the refractive index difference Δn1 is 4 to 1, especially 0.045 to 0.5. On the other hand, the refractive index difference Δn2 in the Δn2 direction is preferably as small as possible from the viewpoint of maintaining the polarization state, and is preferably 0.03 or less, particularly 0.02 or less, and particularly preferably 0.02 or less.
It is preferable that the refractive index difference Δn2 is 1 or less.

【００３４】よって上記した微小領域の配向処理は、微
小領域を形成する高分子液晶を可及的に一定方向に配向
させて当該△ｎ１方向の屈折率差を大きくする操作、又
は当該△ｎ２方向の屈折率差を小さくする操作、あるい
はそれらの両方を達成する操作として位置付けることも
できる。Therefore, the above-mentioned alignment treatment of the minute region is performed by aligning the polymer liquid crystal forming the minute region in a certain direction as much as possible to increase the refractive index difference in the Δn1 direction or in the Δn2 direction. Can be positioned as an operation to reduce the refractive index difference of the two or an operation to achieve both of them.

【００３５】従って前記の屈折率差特性を達成する点よ
り、樹脂フィルムを形成する樹脂の屈折率が、微小領域
を形成する高分子液晶の常光線屈折率と可及的に一致
し、異常光線屈折率と大きく相違するような関係の樹脂
と高分子液晶の組合せで用いて光学フィルムを形成する
ことが有利である。Therefore, from the viewpoint of achieving the above-mentioned refractive index difference characteristic, the refractive index of the resin forming the resin film matches as much as possible the ordinary light refractive index of the polymer liquid crystal forming the minute area, It is advantageous to form an optical film using a combination of a resin and a polymer liquid crystal having a relationship that is significantly different from the refractive index.

【００３６】光学フィルムにおける微小領域は、前記散
乱効果等の均質性などの点より可及的に均等に分散分布
していることが好ましい。微小領域の大きさ、特に散乱
方向である△ｎ１方向の長さは、後方散乱（反射）や波
長依存性に関係する。光利用効率の向上や波長依存性に
よる着色の防止、微小領域の視覚による視認阻害の防止
ないし鮮明な表示の阻害防止、さらには製膜性やフィル
ム強度などの点より微小領域の好ましい大きさ、特に△
ｎ１方向の好ましい長さは、０．０５〜５００μm、就
中０．１〜２５０μm、特に１〜１００μmである。なお
微小領域は、通例ドメインの状態で光学フィルム中に存
在するが、その△ｎ２方向の長さについては特に限定は
ない。It is preferable that the minute regions in the optical film are dispersed and distributed as uniformly as possible from the viewpoint of homogeneity such as the scattering effect. The size of the minute region, particularly the length in the △ n1 direction, which is the scattering direction, is related to backscattering (reflection) and wavelength dependency. Improvement of light use efficiency and prevention of coloring due to wavelength dependence, prevention of visual obstruction of fine regions or prevention of clear display, and more preferable size of micro regions from the viewpoint of film forming property and film strength, Especially △
The preferred length in the n1 direction is 0.05-500 μm, especially 0.1-250 μm, especially 1-100 μm. The minute region is usually present in the optical film in the state of a domain, but the length in the Δn2 direction is not particularly limited.

【００３７】光学フィルム中に占める微小領域の割合
は、△ｎ１方向の散乱性などの点より適宜に決定しうる
が、一般にはフィルム強度なども踏まえて０．１〜７０
重量％、就中０．５〜５０重量％、特に１〜３０重量％
とされる。The proportion of the minute area occupying in the optical film can be appropriately determined in view of the scattering property in the Δn1 direction and the like, but is generally 0.1 to 70 in consideration of the film strength and the like.
% By weight, especially 0.5 to 50% by weight, especially 1 to 30% by weight
It is said.

【００３８】本発明による光学フィルムは、図１に例示
の如く単層１で用いることもできるし、その２層以上を
重畳した光学部材として用いることもできる。その光学
部材の例を図２に示した。１１，１３，１５，１７が光
学フィルムであり、１２，１４，１６は接着層である。The optical film according to the present invention can be used as a single layer 1 as illustrated in FIG. 1, or can be used as an optical member in which two or more layers are overlapped. FIG. 2 shows an example of the optical member. 11, 13, 15, and 17 are optical films, and 12, 14, and 16 are adhesive layers.

【００３９】かかる光学フィルムの重畳化により、厚さ
増加以上の相乗的な散乱効果を発揮させることができ
る。光学部材は、△ｎ１方向又は△ｎ２方向の任意な配
置角度で光学フィルムを積層したものであってよいが、
散乱効果の拡大などの点よりは△ｎ１方向が上下の層で
平行関係となるように重畳したものが好ましい。光学フ
ィルムの重畳数は、２層以上の適宜な数とすることがで
きる。By superposing such optical films, a synergistic scattering effect more than an increase in thickness can be exhibited. The optical member may be formed by laminating optical films at an arbitrary arrangement angle in the △ n1 direction or the △ n2 direction,
It is preferable that the Δn1 direction is superposed so that the upper and lower layers are in a parallel relationship from each other, for example, from the viewpoint of expansion of the scattering effect. The number of superimposed optical films can be an appropriate number of two or more layers.

【００４０】重畳する光学フィルムは、△ｎ１又は△ｎ
２が同じものであってもよいし、異なるものであっても
よい。なお△ｎ１方向等における上下の層での平行関係
は、可及的に平行であることが好ましいが、作業誤差に
よるズレなどは許容される。また△ｎ１方向等にバラツ
キがある場合には、その平均方向に基づく。The optical film to be superimposed is Δn1 or Δn
2 may be the same or different. The parallel relationship between the upper and lower layers in the Δn1 direction and the like is preferably as parallel as possible, but deviation due to a work error is allowed. If there is variation in the △ n1 direction or the like, it is based on the average direction.

【００４１】光学部材における光学フィルムは、単に重
ね置いた状態にあってもよいが、△ｎ１方向等のズレ防
止や各界面への異物等の侵入防止などの点よりは接着層
等を介して接着されていることが好ましい。その接着に
は、例えばホットメルト系や粘着系などの適宜な接着剤
を用いうる。反射損を抑制する点よりは、光学フィルム
との屈折率差が可及的に小さい接着層が好ましく、光学
フィルムを形成する樹脂にて接着することもできる。The optical films of the optical members may be simply placed on top of each other. However, the optical films may be provided through an adhesive layer or the like in order to prevent displacement in the Δn1 direction or the like and to prevent foreign substances from entering each interface. Preferably, they are adhered. For the bonding, for example, a suitable adhesive such as a hot melt type or an adhesive type can be used. From the viewpoint of suppressing the reflection loss, an adhesive layer having a refractive index difference as small as possible from the optical film is preferable, and it is also possible to adhere with a resin forming the optical film.

【００４２】本発明による光学フィルムや光学部材は、
その直線偏光の透過性と散乱性を示す特性に基づいて例
えば偏光板等の偏光の形成や制御などを目的とした各種
の用途に用いることができる。ちなみに偏光板として用
いた場合には、前記の如く偏光形成原理が二色性吸収型
偏光板などとは相違して、光を吸収しにくいため発熱や
劣化を伴いにくい利点を有する。また散乱光を他の光学
部品等により偏光に変換して再利用することにより光の
利用効率を向上させうる可能性なども有している。The optical film and the optical member according to the present invention include:
Based on the characteristics showing the transmission and scattering properties of the linearly polarized light, it can be used for various purposes such as forming and controlling polarized light such as a polarizing plate. Incidentally, when used as a polarizing plate, unlike the dichroic absorption polarizing plate, the principle of forming a polarized light is unlikely to absorb light, as described above. Further, there is a possibility that the efficiency of light utilization can be improved by converting the scattered light into polarized light by another optical component or the like and reusing it.

【００４３】従って本発明による光学フィルムや光学部
材の実用に際しては、その１層又は２層以上を例えば偏
光板又は／及び位相差板等の適宜な光学部品の片面や両
面に配置した積層体からなる光学素子として用いること
もできる。その例を図３に示した。３が光学部品であ
る。かかる積層体は、単に重ね置いたものであってもよ
いし、接着層等を介して接着したものであってもよい。
その接着層としては、上記した光学フィルムの重畳の場
合に準じうる。Therefore, when the optical film or optical member according to the present invention is put to practical use, one or two or more layers are formed from a laminate in which one or both of suitable optical components such as a polarizing plate and / or a retardation plate are disposed. It can also be used as an optical element. An example is shown in FIG. 3 is an optical component. Such a laminate may be simply stacked, or may be bonded via an adhesive layer or the like.
The adhesive layer can conform to the case of the above-mentioned superposition of the optical films.

【００４４】前記積層対象の光学部品については特に限
定はなく、例えば偏光板や位相差板、導光板等のバック
ライトや反射板、多層膜等からなる偏光分離板や液晶セ
ルなどの適宜なものであってよい。また偏光板や位相差
板等の光学部品は、各種のタイプのものであってよい。The optical components to be laminated are not particularly limited, and may be, for example, a suitable one such as a backlight such as a polarizing plate, a retardation plate, or a light guide plate, a reflecting plate, a polarized light separating plate composed of a multilayer film, a liquid crystal cell, or the like. It may be. Optical components such as a polarizing plate and a retardation plate may be of various types.

【００４５】すなわち偏光板では吸収型タイプや反射型
タイプや散乱型タイプ、位相差板では１／４波長板や１
／２波長板、一軸や二軸等による延伸フィルムタイプや
さらに厚さ方向にも分子配向させた傾斜配向フィルムタ
イプ、液晶ポリマータイプ、視野角や複屈折による位相
差を補償するタイプ、それらを積層したタイプのものな
どの各種のものがあるが、本発明においてはそのいずれ
のタイプも用いうる。That is, for a polarizing plate, an absorption type, a reflection type, or a scattering type, and for a retardation plate, a 板 wavelength plate or 1
/ 2 wavelength plate, stretched film type with uniaxial or biaxial orientation, tilted film type with molecular orientation in the thickness direction, liquid crystal polymer type, type that compensates for phase difference due to viewing angle or birefringence, laminated There are various types such as the type described above, and any of these types can be used in the present invention.

【００４６】ちなみに前記した偏光板の具体例として
は、ポリビニルアルコール系フィルムや部分ホルマール
化ポリビニルアルコール系フィルム、エチレン・酢酸ビ
ニル共重合体系部分ケン化フィルムの如き親水性高分子
フィルムに、ヨウ素や二色性染料等の二色性物質を吸着
させて延伸した吸収型偏光フィルム、ポリビニルアルコ
ールの脱水処理物やポリ塩化ビニルの脱塩酸処理物の如
きポリエン配向フィルムなどがあげられる。Incidentally, specific examples of the above-mentioned polarizing plate include iodine and diols on a hydrophilic polymer film such as a polyvinyl alcohol-based film, a partially formalized polyvinyl alcohol-based film, and an ethylene / vinyl acetate copolymer-based partially saponified film. Absorption type polarizing films which are drawn by adsorbing a dichroic substance such as a coloring dye, and polyene oriented films such as dehydrated polyvinyl alcohol and dehydrochlorinated polyvinyl chloride are exemplified.

【００４７】また前記偏光フィルムの片面又は両面に耐
水性等の保護目的で、プラスチックの塗布層やフィルム
のラミネート層等からなる透明保護層を設けた偏光板な
どもあげられる。さらにその透明保護層に、例えば平均
粒径が０．５〜２０μmのシリカやアルミナ、チタニア
やジルコニア、酸化錫や酸化インジウム、酸化カドミウ
ムや酸化アンチモン等の導電性のこともある無機系微粒
子、架橋又は未架橋ポリマー等の有機系微粒子等の透明
微粒子を含有させて表面に微細凹凸構造を付与したもの
などもあげられる。Further, a polarizing plate having a transparent protective layer formed of a plastic coating layer or a film laminating layer on one or both sides of the polarizing film for the purpose of protecting water resistance or the like can also be mentioned. Further, in the transparent protective layer, for example, inorganic fine particles that may be conductive such as silica or alumina, titania or zirconia, tin oxide or indium oxide, cadmium oxide or antimony oxide having an average particle size of 0.5 to 20 μm, Alternatively, a transparent fine particle such as an organic fine particle such as an uncrosslinked polymer may be contained to impart a fine uneven structure to the surface.

【００４８】一方、位相差板の具体例としては、上記の
光学フィルムで例示した樹脂からなる延伸フィルムや液
晶ポリマー、就中、捩じれ配向の液晶ポリマーなどから
なるものがあげられる。On the other hand, specific examples of the retardation plate include a stretched film made of the resin exemplified in the above optical film and a liquid crystal polymer, especially a liquid crystal polymer having a twisted orientation.

【００４９】さらに導光板の具体例としては、透明な樹
脂板の側面に（冷，熱）陰極管等の線状光源や発光ダイ
オード、ＥＬ等の光源を配置し、その樹脂板に板内を伝
送される光を拡散や反射、回折や干渉等により板の片面
側に出射するようにしたものなどがあげられる。Further, as a specific example of the light guide plate, a linear light source such as a (cold or hot) cathode tube or a light source such as a light emitting diode or EL is disposed on a side surface of a transparent resin plate. Light transmitted to one side of the plate by diffusion, reflection, diffraction, interference, or the like may be used.

【００５０】導光板を含む光学素子の形成に際しては、
光の出射方向を制御するためのプリズムシート等からな
るプリズムアレイ層、均一な発光を得るための拡散板、
線状光源からの出射光を導光板の側面に導くための光源
ホルダなどの補助手段を導光板の上下面や側面などの所
定位置に必要に応じ１層又は２層以上を配置して適宜な
組合せ体とすることができる。In forming an optical element including a light guide plate,
A prism array layer composed of a prism sheet or the like for controlling the light emission direction, a diffusion plate for obtaining uniform light emission,
Auxiliary means such as a light source holder for guiding the light emitted from the linear light source to the side surface of the light guide plate may be provided by appropriately arranging one or more layers at predetermined positions such as the upper and lower surfaces and side surfaces of the light guide plate. It can be a combination.

【００５１】本発明による光学素子を形成する積層体
は、１種の光学部品を用いたものであってもよいし、２
種以上の光学部品を用いたものであってもよい。また例
えば位相差板等の同種の光学部品を２層以上積層したも
のであってもよく、その場合、光学部品の位相差板等の
特性は同じであってもよいし、相違していてもよい。光
学素子における光学フィルムや光学部材は、積層体の片
外面や両外面、積層体を形成する光学部品の片面や両面
などの積層体の外部や内部の適宜な位置に１層又は２層
以上が配置されていてよい。The laminate for forming the optical element according to the present invention may be one using one kind of optical component.
It may use one or more kinds of optical components. Further, for example, two or more layers of the same type of optical component such as a phase difference plate may be laminated, and in this case, the characteristics of the phase difference plate or the like of the optical component may be the same or different. Good. The optical film or the optical member in the optical element has one or two or more layers at appropriate positions inside or outside the laminate such as one or both outer surfaces of the laminate and one or both sides of the optical component forming the laminate. May be arranged.

【００５２】光学素子が偏光板を含むものである場合、
光学フィルムの透過・散乱特性を有効に活用する点など
より光学フィルム又は光学部材は、その△ｎ１方向又は
△ｎ２方向が偏光板の透過軸と平行関係となるように配
置されていることが好ましい。その平行関係は、上記し
た光学フィルムを重畳する場合に準じうる。When the optical element includes a polarizing plate,
The optical film or the optical member is preferably arranged such that the Δn1 direction or the Δn2 direction is parallel to the transmission axis of the polarizing plate from the viewpoint of effectively utilizing the transmission / scattering characteristics of the optical film. . The parallel relationship can be based on the case where the optical films described above are superimposed.

【００５３】光学フィルム等の△ｎ１方向と偏光板の透
過軸を平行関係とした配置の光学素子は、偏光板を透過
した直線偏光を光学フィルム等の△ｎ１方向を介して散
乱させることができる。従って、例えば光学素子をその
偏光板が液晶セル側となるように視認側に配置して液晶
表示装置等における視野角の拡大などに有効である。An optical element such as an optical film, which is arranged so that the Δn1 direction and the transmission axis of the polarizing plate are in a parallel relationship, can scatter linearly polarized light transmitted through the polarizing plate through the Δn1 direction of the optical film or the like. . Therefore, for example, the optical element is arranged on the viewing side such that the polarizing plate is on the liquid crystal cell side, which is effective for expanding the viewing angle in a liquid crystal display device or the like.

【００５４】一方、光学フィルム等の△ｎ２方向と偏光
板の透過軸を平行関係とした配置の光学素子は、偏光板
吸収性の直線偏光を光学フィルム等の△ｎ１方向を介し
て散乱させることができる。従って例えば光が光学フィ
ルム等を介して偏光板に入射するように光学素子を配置
して偏光板を透過する光量の増大などに有効である。On the other hand, an optical element such as an optical film having a parallel relationship between the Δn2 direction and the transmission axis of the polarizing plate is capable of scattering linearly absorptive linearly polarized light through the Δn1 direction of the optical film or the like. Can be. Therefore, for example, it is effective to increase the amount of light transmitted through the polarizing plate by disposing the optical element so that light enters the polarizing plate via an optical film or the like.

【００５５】[0055]

【実施例】実施例１ 加重たわみ温度１６５℃、ガラス転移温度１８５℃のノ
ルボルネン系樹脂（ＪＳＲ社製、アートン）９５０部
（重量部、以下同じ）を含有する２０重量％ジクロロメ
タン溶液に、下式で表される重合度が２９（ポリスチレ
ン換算の重量平均分子量１２０００、ガラス転移温度８
０℃、ネマチック液晶化温度１００〜２９０℃）の高分
子液晶５０部を溶解させてキャスト法により厚さ１００
μmの樹脂フィルムを得た。 EXAMPLE 1 A 20% by weight dichloromethane solution containing 950 parts (parts by weight, hereinafter the same) of a norbornene resin (ARTON, manufactured by JSR) having a weighted deflection temperature of 165 ° C. and a glass transition temperature of 185 ° C. Is 29 (weight average molecular weight in terms of polystyrene is 12000, glass transition temperature is 8)
(0 ° C., nematic liquid crystal forming temperature: 100 to 290 ° C.) 50 parts of a polymer liquid crystal is dissolved and cast to a thickness of 100 ° C.
A μm resin film was obtained.

【００５６】前記の樹脂フィルムは、ノルボルネン系樹
脂からなるフィルム中に高分子液晶がドメイン状に分散
したものであり、そのドメインの径をフィルム断面の走
査型電子顕微鏡観察にて測定した結果、０．２〜１．５
μmであった。次にその樹脂フィルムを１８０℃で３倍
に延伸処理したのち急冷して、複屈折性の樹脂フィルム
中に高分子液晶からなる微小領域が分散分布してなり、
屈折率差△ｎ１が０．２３０で、△ｎ２が０．０２９の
光学フィルムを得た。The above resin film is obtained by dispersing polymer liquid crystals in a domain form in a film made of a norbornene-based resin. The diameter of the domain was measured by observing a cross section of the film with a scanning electron microscope. .2 to 1.5
μm. Next, the resin film is stretched three times at 180 ° C. and then quenched, so that microscopic regions composed of high-molecular liquid crystal are dispersed and distributed in the birefringent resin film.
An optical film having a refractive index difference Δn1 of 0.230 and Δn2 of 0.029 was obtained.

【００５７】実施例２ 実施例１で得た光学フィルムと市販の全光線透過率が４
１％で透過光の偏光度が９９％の偏光板を△ｎ１方向と
透過軸が一致するように厚さ２０μmのアクリル系粘着
層を介し接着して光学素子を得た。Example 2 The optical film obtained in Example 1 and a commercially available total light transmittance of 4
An optical element was obtained by bonding a polarizing plate of 1% and having a degree of polarization of transmitted light of 99% via an acrylic adhesive layer having a thickness of 20 μm such that the transmission axis coincides with the Δn1 direction.

【００５８】比較例１ 高分子液晶として重合度が５（ポリスチレン換算の重量
平均分子量２０００）のものを用いたほかは実施例１に
準じて樹脂フィルムを得、それを延伸処理して屈折率差
△ｎ１が０．２３０で、△ｎ２が０．０２９の光学フィ
ルムを得た。なお前記樹脂フィルム中における高分子液
晶からなるドメインの径は、０．０５〜３μmの範囲で
あり、粒径分布の広がりの大きいものであった。Comparative Example 1 A resin film was obtained in the same manner as in Example 1 except that a polymer liquid crystal having a degree of polymerization of 5 (weight average molecular weight in terms of polystyrene of 2,000) was used, and the resulting resin film was stretched to obtain a refractive index difference. An optical film having Δn1 of 0.230 and Δn2 of 0.029 was obtained. The diameter of the domain composed of the polymer liquid crystal in the resin film was in the range of 0.05 to 3 μm, and the particle size distribution was large.

【００５９】比較例２ 比較例１で得た光学フィルムと市販の全光線透過率が４
１％で透過光の偏光度が９９％の偏光板を△ｎ２方向と
透過軸が一致するように厚さ２０μmのアクリル系粘着
層を介し接着して光学素子を得た。Comparative Example 2 The optical film obtained in Comparative Example 1 and a commercially available total light transmittance of 4
An optical element was obtained by bonding a polarizing plate of 1% and having a degree of polarization of transmitted light of 99% via an acrylic adhesive layer having a thickness of 20 μm so that the transmission axis coincides with the Δn2 direction.

【００６０】評価試験１ 実施例１、比較例１で得た光学フィルムに室温又は９０
℃の雰囲気下において延伸方向と平行又は垂直な偏光を
入射させてその散乱状態を目視観察した。また室温にお
いて延伸方向と平行又は垂直な偏光を入射させてそのヘ
イズをＡＳＴＭＤ１００３−６１に準拠してポイック積
分球式ヘイズメータにて測定した。その結果を次表に示
した。なお９０℃の雰囲気下における散乱状態を（ ）
内に示した。Evaluation Test 1 The optical films obtained in Example 1 and Comparative Example 1
Polarized light parallel or perpendicular to the stretching direction was made incident in an atmosphere of ° C., and the scattering state was visually observed. Further, at room temperature, polarized light parallel or perpendicular to the stretching direction was applied, and the haze was measured with a Poick integrating sphere haze meter according to ASTM D1003-61. The results are shown in the following table. Note that the scattering state in an atmosphere at 90 ° C.
Shown within.

【００６１】 散 乱 状 態 ヘ イ ズ 平行方向 垂直方向 平行方向 垂直方向 実施例１ 散乱（散乱） 透過（透過） ９２ ９ 比較例１ 散乱（透過） 透過（透過） ８５ ９[0061] scattering state f size b parallel vertical parallel vertical Example 1 scattering (scattered) transmission (transmission) 92 9 Comparative Example 1 Scattering (transmission) transmission (transmission) 85 9

【００６２】表より、いずれの場合も室温では偏光の方
向により散乱特性が相違する異方性を示し、実施例１で
はその特性を高温においても良好に維持するものの、比
較例１では高温においてその異方性を消失して熱安定性
に劣ることがわかる。また比較例１では平行方向のヘイ
ズが低く、同じ組成でも高分子液晶の重合度の大小で微
小領域の形成状態に変化が生じて光学特性に影響するこ
とがわかる。As can be seen from the table, in each case, at room temperature, anisotropy in which the scattering characteristics are different depending on the polarization direction is exhibited. In Example 1, the characteristics are favorably maintained even at a high temperature. It can be seen that the anisotropy disappears and the thermal stability is poor. Further, in Comparative Example 1, the haze in the parallel direction was low, and it was found that, even with the same composition, the degree of polymerization of the polymer liquid crystal was large and small, and the formation state of the minute region was changed, thereby affecting the optical characteristics.

【００６３】評価試験２ 実施例２、比較例２で得た光学素子をその光学フィルム
側を介し、また市販のヨウ素系偏光板をプロジェクタ用
ランプ（メタルハライドランプ２５０Ｗ）の出光レンズ
に隣接配置して３００時間の累積照射後の変化を目視観
察した。その結果、市販の偏光板は著しく赤変して使用
に耐えないレベルに劣化しており、また比較例２の光学
素子も変色して著しく変形していたが、実施例２の光学
素子には殆ど変化が認められなかった。Evaluation Test 2 The optical elements obtained in Example 2 and Comparative Example 2 were disposed through the optical film side, and a commercially available iodine-based polarizing plate was disposed adjacent to the light-emitting lens of a projector lamp (metal halide lamp 250W). The change after 300 hours of cumulative irradiation was visually observed. As a result, the commercially available polarizing plate was remarkably reddened and deteriorated to a level unusable for use, and the optical element of Comparative Example 2 was also discolored and significantly deformed. Little change was observed.

【００６４】上記の結果より、本発明による光学フィル
ム及び光学素子では、入射直線偏光の偏光方向により強
い散乱異方性を示すと共に、熱的安定性に優れているこ
とがわかり、液晶表示装置等に用いて視認性や輝度や耐
久性等の向上を期待することができる。From the above results, it can be seen that the optical film and the optical element according to the present invention exhibit strong scattering anisotropy in the polarization direction of the incident linearly polarized light and have excellent thermal stability. It can be expected to improve visibility, brightness, durability and the like.

【図面の簡単な説明】[Brief description of the drawings]

【図１】光学フィルム例の断面図FIG. 1 is a cross-sectional view of an example of an optical film.

【図２】他の光学フィルム例の断面図FIG. 2 is a cross-sectional view of another example of an optical film.

【図３】光学素子例の断面図FIG. 3 is a cross-sectional view of an example of an optical element.

【符号の説明】[Explanation of symbols]

１，１１，１３，１５，１７：光学フィルム ｅ：微小領域 ２：接着層 ３：光学部品 1, 11, 13, 15, 17: optical film e: minute area 2: adhesive layer 3: optical component

───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2H049 BA02 BA06 BA24 BA25 BA42 BB03 BB16 BB43 BB44 BB45 BB46 BB47 BB48 BB49 BB51 BB62 2H091 FA08X FA08Z FA11X FA11Z FA21Z FA23Z FA50X FA50Z FB02 FC01 FC22 FC23 FD06 FD14 GA17 JA01 KA01 LA04 ──────────────────────────────────────────────────続 き Continued on the front page F-term (reference) 2H049 BA02 BA06 BA24 BA25 BA42 BB03 BB16 BB43 BB44 BB45 BB46 BB47 BB48 BB49 BB51 BB62 2H091 FA08X FA08Z FA11X FA11Z FA21Z FA23Z FA50X FA50Z FB02 FC01 FC01 FC23 FC23

Claims (9)

【特許請求の範囲】[Claims] 【請求項１】 重合度が８以上の高分子液晶からなる微
小領域を分散含有する樹脂フィルムよりなり、その微小
領域と他の部分との屈折率差△ｎ１、△ｎ２が直線偏光
の最大透過率を示す軸方向に直交する方向において０．
０３以上（△ｎ１）、かつ最大透過率の軸方向において
前記△ｎ１の５０％以下（△ｎ２）であることを特徴と
する光学フィルム。1. A resin film in which minute regions composed of a polymer liquid crystal having a degree of polymerization of 8 or more are dispersed and contained, and the refractive index differences Δn1 and Δn2 between the minute regions and other portions are the maximum transmission of linearly polarized light. 0 in the direction orthogonal to the axial direction indicating the rate.
An optical film characterized by being at least 03 (Δn1) and at most 50% (Δn2) of the Δn1 in the axial direction of the maximum transmittance. 【請求項２】 請求項１において、微小領域を相分離に
より分散含有するものである光学フィルム。2. The optical film according to claim 1, wherein the fine region is dispersed and contained by phase separation. 【請求項３】 請求項１又は２において、微小領域の△
ｎ１方向の長さが０．０５〜５００μmである光学フィ
ルム。3. The method according to claim 1, wherein the 領域
An optical film having a length in the n1 direction of 0.05 to 500 µm. 【請求項４】 請求項１又は２において、微小領域の△
ｎ１方向の長さが１〜１００μmである光学フィルム。4. The method according to claim 1 or 2, wherein
An optical film having a length in the n1 direction of 1 to 100 μm. 【請求項５】 請求項１〜４において、微小領域を形成
する高分子液晶がガラス転移温度５０℃以上で、かつ樹
脂フィルムを形成する樹脂のガラス転移温度よりも低い
温度域にてネマチック液晶相を呈するものである光学フ
ィルム。5. The nematic liquid crystal phase according to claim 1, wherein the polymer liquid crystal forming the minute region has a glass transition temperature of 50 ° C. or higher and a temperature lower than the glass transition temperature of the resin forming the resin film. An optical film that exhibits 【請求項６】 請求項１〜５において、樹脂フィルムを
形成する樹脂が８０℃以上の加重たわみ温度を有するガ
ラス転移温度１１０℃以上のものである光学フィルム。6. The optical film according to claim 1, wherein the resin forming the resin film has a glass transition temperature of 110 ° C. or more having a weight deflection temperature of 80 ° C. or more. 【請求項７】 請求項１〜６に記載の光学フィルムの２
層以上を当該△ｎ１方向が上下の層で平行関係となるよ
うに重畳してなることを特徴とする光学部材。7. The optical film according to claim 1, wherein
An optical member comprising a plurality of layers overlapped so that the Δn1 direction is in a parallel relationship between upper and lower layers. 【請求項８】 偏光板又は位相差板の少なくとも一方
と、請求項１〜６に記載の光学フィルムの１層又は２層
以上を有する積層体からなることを特徴とする光学素
子。8. An optical element comprising a laminate having at least one of a polarizing plate and a retardation plate and one or more layers of the optical film according to claim 1. Description: 【請求項９】 請求項８において、偏光板を有してその
偏光板の透過軸と光学フィルムの当該△ｎ１方向又は当
該△ｎ２方向が平行関係にある光学素子。9. The optical element according to claim 8, comprising a polarizing plate, wherein the transmission axis of the polarizing plate and the Δn1 direction or the Δn2 direction of the optical film are in a parallel relationship.