JP2000037742A - Manufacture of thermosetting resin molded body - Google Patents
Manufacture of thermosetting resin molded bodyInfo
- Publication number
- JP2000037742A JP2000037742A JP10209531A JP20953198A JP2000037742A JP 2000037742 A JP2000037742 A JP 2000037742A JP 10209531 A JP10209531 A JP 10209531A JP 20953198 A JP20953198 A JP 20953198A JP 2000037742 A JP2000037742 A JP 2000037742A
- Authority
- JP
- Japan
- Prior art keywords
- thermosetting resin
- molding material
- mold
- molding
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、抗菌性に優れる熱
硬化性樹脂成形体の製造方法に関する。TECHNICAL FIELD The present invention relates to a method for producing a thermosetting resin molded article having excellent antibacterial properties.
【０００２】[0002]
【従来の技術】不飽和ポリエステル樹脂のような熱硬化
性樹脂に充填剤、硬化剤、離型剤、顔料、増粘剤等を加
えた樹脂組成物をガラス繊維等の強化用繊維物質に含浸
し、シート状あるいはバルク状に形成した不飽和ポリエ
ステル樹脂成形材料は、シートモールディングコンパウ
ンド（ＳＭＣ）やシックモールディングコンパウンド
（ＴＭＣ）或いはバルクモールディングコンパウンド
（ＢＭＣ）等と呼称され、主として圧縮成形により成形
体となされ、住宅設備、工業部品、自動車部品等として
広く用いられている。2. Description of the Related Art A resin composition obtained by adding a filler, a curing agent, a release agent, a pigment, a thickener, and the like to a thermosetting resin such as an unsaturated polyester resin is impregnated into a reinforcing fiber material such as glass fiber. The unsaturated polyester resin molding material formed in a sheet or bulk is called a sheet molding compound (SMC), a thick molding compound (TMC), a bulk molding compound (BMC), or the like. It is widely used as housing equipment, industrial parts, automobile parts and the like.
【０００３】一方、近年の清潔・健康意識の高揚に伴
い、抗菌・防黴性を付与した樹脂成形体が注目されてお
り、成形用の樹脂組成物中に各種抗菌剤を含有させるこ
とが行われている。上記各種抗菌剤のなかでも、成形時
の熱安定性、効果の持続性、安全性等の観点から銀系無
機抗菌剤が好ましく用いられている。[0003] On the other hand, as the awareness of cleanliness and health has risen in recent years, resin molded articles provided with antibacterial and antifungal properties have attracted attention, and various antibacterial agents have been included in resin compositions for molding. Have been done. Among the above various antibacterial agents, silver-based inorganic antibacterial agents are preferably used from the viewpoints of heat stability at the time of molding, continuity of effects, safety and the like.
【０００４】抗菌剤の機能については、一般に、成形体
の表面層に存在する抗菌剤のみが抗菌効果を発揮するも
のと考えられ、成形体内部に存在する抗菌剤は長期的に
も殆ど抗菌効果を発揮しないものと考えられている。従
って、上記ＳＭＣやＴＭＣ或いはＢＭＣ等の成形材料に
抗菌剤を含有させる場合、成形体の表面層にのみ抗菌剤
が存在するように出来れば、低コストで効果的に抗菌性
を付与することが可能となると言える。[0004] Regarding the function of the antibacterial agent, it is generally considered that only the antibacterial agent present in the surface layer of the molded article exerts the antibacterial effect, and the antibacterial agent present inside the molded article has almost no antibacterial effect for a long term. Is not considered to be effective. Therefore, when the antibacterial agent is contained in the molding material such as the SMC, TMC or BMC, if the antibacterial agent can be present only in the surface layer of the molded article, the antibacterial property can be effectively provided at low cost. It is possible.
【０００５】このような観点から種々の試みが行われて
おり、例えば、特開平９−１６４５３８号公報では、
「抗菌剤を分散させた離型剤を成形型に塗布した後、該
成形型に合成樹脂、及び、充填剤等が配合されて成る合
成樹脂組成物を導入し、該合成樹脂組成物を硬化させて
成形することを特徴とする人工大理石（成形体）の製造
方法」が提案されている。Various attempts have been made from such a viewpoint. For example, in Japanese Patent Application Laid-Open No. 9-164538,
"After applying a mold release agent in which an antimicrobial agent is dispersed to a mold, a synthetic resin, and a synthetic resin composition including a filler and the like are introduced into the mold, and the synthetic resin composition is cured. And a method for producing artificial marble (molded body) characterized by being molded.
【０００６】しかし、上記提案にあるような製造方法の
場合、確かに成形体表面に抗菌剤を付着させることは出
来るものの、成形体の使用時に抗菌剤が剥落し易いた
め、抗菌効果の持続性が乏しいという問題点や、抗菌剤
の付着量が離型剤の塗布量によって左右されるため、抗
菌効果の部分的な変動が大きくなりがちであり、均一で
安定した抗菌性を有する成形体を得るのが難しいという
問題点等がある。[0006] However, in the case of the manufacturing method as proposed above, although the antibacterial agent can be adhered to the surface of the molded article, the antibacterial agent is easily peeled off when the molded article is used. And the amount of antibacterial agent adhered depends on the amount of release agent applied, so that the antibacterial effect tends to partially fluctuate. There is a problem that it is difficult to obtain.
【０００７】[0007]
【発明が解決しようとする課題】本発明は、上記従来の
問題点を解決するため、成形体の表面層に抗菌剤をより
多く安定的に存在させることにより、優れた抗菌性と抗
菌効果の持続性を有する成形体を安価に得ることの出来
る熱硬化性樹脂成形体の製造方法を提供することを課題
とする。SUMMARY OF THE INVENTION In order to solve the above-mentioned conventional problems, the present invention provides an excellent antibacterial property and an antibacterial effect by providing a more stable antibacterial agent in the surface layer of a molded article. It is an object of the present invention to provide a method for producing a thermosetting resin molded article that can obtain a molded article having durability at low cost.
【０００８】[0008]
【課題を解決するための手段】本発明による熱硬化性樹
脂成形体の製造方法は、熱硬化性樹脂、銀系無機抗菌剤
及び硬化剤が含有されてなる熱硬化性樹脂成形材料を、
金型内に投入し、加熱下、金型に振動を加えながら圧縮
成形して賦形し、成形体となすことを特徴とする。According to the present invention, there is provided a method for producing a thermosetting resin molded article, comprising the steps of: preparing a thermosetting resin molding material containing a thermosetting resin, a silver-based inorganic antibacterial agent and a curing agent;
It is characterized by being put into a mold, compression-molding and shaping under heating while applying vibration to the mold to form a molded body.
【０００９】本発明で用いられる熱硬化性樹脂成形材料
に主成分として含有される熱硬化性樹脂としては、特に
限定されるものではないが、例えば、不飽和ポリエステ
ル樹脂、ビニルエステル樹脂、エポキシ樹脂、フェノー
ル樹脂等が挙げられ、いずれも好適に用いられるが、な
かでも不飽和ポリエステル樹脂やビニルエステル樹脂が
より好適に用いられ、そのなかでも増粘性や成形性が良
好であり、比較的安価でもある不飽和ポリエステル樹脂
が特に好適に用いられる。The thermosetting resin contained as a main component in the thermosetting resin molding material used in the present invention is not particularly limited, but examples thereof include unsaturated polyester resins, vinyl ester resins, and epoxy resins. , Phenol resin and the like, all of which are preferably used, among which unsaturated polyester resins and vinyl ester resins are more preferably used, and among them, good viscosity and moldability are preferable, and even relatively inexpensive. Certain unsaturated polyester resins are particularly preferably used.
【００１０】上記不飽和ポリエステル樹脂とは、不飽和
二塩基酸とグリコール及び必要に応じて飽和二塩基酸と
を重縮合させて得られる不飽和ポリエステルと、重合性
単量体及び必要に応じて含有させる低収縮化剤としての
熱可塑性樹脂等からなる混合物である。The above-mentioned unsaturated polyester resin includes an unsaturated polyester obtained by polycondensing an unsaturated dibasic acid with glycol and, if necessary, a saturated dibasic acid, a polymerizable monomer and optionally It is a mixture comprising a thermoplastic resin or the like as a low shrinkage agent to be contained.
【００１１】不飽和二塩基酸としては、特に限定される
ものではないが、例えば、無水マレイン酸、フマル酸、
イタコン酸、シトラコン酸等が挙げられ、好適に用いら
れる。The unsaturated dibasic acid is not particularly restricted but includes, for example, maleic anhydride, fumaric acid,
Itaconic acid, citraconic acid and the like can be mentioned, and are preferably used.
【００１２】上記不飽和二塩基酸は、単独で用いられて
も良いし、２種類以上が併用されても良い。The above unsaturated dibasic acids may be used alone or in combination of two or more.
【００１３】グリコールとしては、特に限定されるもの
ではないが、例えば、エチレングリコール、ジエチレン
グリコール、トリエチレングリコール、プロピレングリ
コール、１，３−ブタンジオール、１，４−ブタンジオ
ール、１，６−ヘキサンジオール、ビスフェノールＡ、
水素添加ビスフェノールＡ、ビスフェノールＡのエチレ
ンオキサイド付加物、ネオペンチルグリコール等が挙げ
られ、好適に用いられる。The glycol is not particularly limited. For example, ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, 1,3-butanediol, 1,4-butanediol, 1,6-hexanediol , Bisphenol A,
Hydrogenated bisphenol A, an ethylene oxide adduct of bisphenol A, neopentyl glycol, and the like are mentioned, and are preferably used.
【００１４】上記グリコールは、単独で用いられても良
いし、２種類以上が併用されても良い。The above glycols may be used alone or in combination of two or more.
【００１５】必要に応じて用いられる飽和二塩基酸とし
ては、特に限定されるものではないが、例えば、無水フ
タル酸、オルソフタル酸、イソフタル酸、テレフタル
酸、アジピン酸、琥珀酸、テトラクロロフタル酸、ヘッ
ト酸等が挙げられ、好適に用いられる。The saturated dibasic acid optionally used is not particularly restricted but includes, for example, phthalic anhydride, orthophthalic acid, isophthalic acid, terephthalic acid, adipic acid, succinic acid, tetrachlorophthalic acid And het acid are preferably used.
【００１６】上記飽和二塩基酸は、単独で用いられても
良いし、２種類以上が併用されても良い。The above-mentioned saturated dibasic acids may be used alone or in combination of two or more.
【００１７】又、重合性単量体としては、特に限定され
るものではないが、例えば、スチレン、ジクロロスチレ
ン、ビニルトルエン、酢酸ビニル、アクリル酸、アクリ
ル酸エステル、メタクリル酸、メタクリル酸エステル、
フタル酸ジアリル等が挙げられ、好適に用いられるが、
なかでも性能とコストのバランスが良好なスチレンがよ
り好適に用いられる。The polymerizable monomer is not particularly restricted but includes, for example, styrene, dichlorostyrene, vinyltoluene, vinyl acetate, acrylic acid, acrylic acid ester, methacrylic acid, methacrylic acid ester,
Examples include diallyl phthalate, which is preferably used,
Among them, styrene having a good balance between performance and cost is more preferably used.
【００１８】上記重合性単量体は、単独で用いられても
良いし、２種類以上が併用されても良い。The above polymerizable monomers may be used alone or in combination of two or more.
【００１９】又、不飽和ポリエステル樹脂中における上
記重合性単量体の含有量は、特に限定されるものではな
いが、２０〜６０重量％であることが好ましい。The content of the polymerizable monomer in the unsaturated polyester resin is not particularly limited, but is preferably 20 to 60% by weight.
【００２０】さらに、必要に応じて含有させる低収縮化
剤としての熱可塑性樹脂としては、特に限定されるもの
ではないが、例えば、ポリスチレン、ポリ酢酸ビニル、
ポリメチルメタクリレート、ポリエチレン、ポリε−カ
プロラクトン、飽和ポリエステル、ポリ塩化ビニル、ポ
リブタジエン、スチレン−アクリル酸共重合体、スチレ
ン−酢酸ビニル共重合体、エチレン−酢酸ビニル共重合
体、塩化ビニル−酢酸ビニル共重合体、アクリロニトリ
ル−スチレン共重合体等が挙げられ、好適に用いられ
る。Further, the thermoplastic resin as a low-shrinking agent to be contained as required is not particularly limited, and examples thereof include polystyrene, polyvinyl acetate, and the like.
Polymethyl methacrylate, polyethylene, poly ε-caprolactone, saturated polyester, polyvinyl chloride, polybutadiene, styrene-acrylic acid copolymer, styrene-vinyl acetate copolymer, ethylene-vinyl acetate copolymer, vinyl chloride-vinyl acetate copolymer Polymers, acrylonitrile-styrene copolymers and the like are mentioned, and they are preferably used.
【００２１】上記低収縮化剤としての熱可塑性樹脂は、
単独で用いられても良いし、２種類以上が併用されても
良い。The thermoplastic resin as the above-mentioned low-shrinking agent is:
They may be used alone or in combination of two or more.
【００２２】又、ビニルエステル樹脂とは、エステル連
鎖もしくはエーテル連鎖の末端にビニル基を有する樹脂
であり、エポキシアクリレート樹脂がその代表例として
挙げられる。The vinyl ester resin is a resin having a vinyl group at an end of an ester or ether chain, and an epoxy acrylate resin is a typical example.
【００２３】上記エポキシアクリレート樹脂とは、ビス
フェノール型やノボラック型等のエポキシ樹脂とアクリ
ル酸やメタクリル酸等の不飽和一塩基酸とを反応させて
得られるエポキシアクリレートと、重合性単量体及び必
要に応じて含有させる低収縮化剤としての熱可塑性樹脂
等からなる混合物である。The above-mentioned epoxy acrylate resin refers to an epoxy acrylate obtained by reacting an epoxy resin of bisphenol type or novolak type with an unsaturated monobasic acid such as acrylic acid or methacrylic acid, a polymerizable monomer, Is a mixture composed of a thermoplastic resin or the like as a low-shrinking agent to be contained in accordance with the present invention.
【００２４】上記重合性単量体及び必要に応じて含有さ
せる低収縮化剤としての熱可塑性樹脂としては、特に限
定されるものではないが、例えば、前記不飽和ポリエス
テル樹脂の場合に用いられるものと同様のものが挙げら
れ、好適に用いられる。The above-mentioned polymerizable monomer and, if necessary, the thermoplastic resin as a low-shrinking agent are not particularly limited. For example, those used in the case of the unsaturated polyester resin are used. The same ones as mentioned above can be mentioned, and are preferably used.
【００２５】上記重合性単量体及び低収縮化剤としての
熱可塑性樹脂は、それぞれ単独で用いられても良いし、
それぞれ２種類以上が併用されても良い。The polymerizable monomer and the thermoplastic resin as a low-shrinking agent may be used alone,
Two or more types may be used in combination.
【００２６】本発明で用いられる熱硬化性樹脂成形材料
に抗菌性付与剤として含有される銀系無機抗菌剤として
は、特に限定されるものではないが、例えば、ガラス、
ゼオライト、セラミックス、シリカゲル、リン酸ジルコ
ニウム等を担持体とする銀−ガラス系無機抗菌剤、銀−
ゼオライト系無機抗菌剤、銀−セラミックス系無機抗菌
剤、銀−シリカゲル系無機抗菌剤、銀−リン酸ジルコニ
ウム系無機抗菌剤等が挙げられ、好適に用いられる。The silver-based inorganic antibacterial agent contained as an antibacterial agent in the thermosetting resin molding material used in the present invention is not particularly limited.
Silver-glass inorganic antibacterial agent with zeolite, ceramics, silica gel, zirconium phosphate, etc. as carrier, silver-
Zeolite-based inorganic antibacterial agents, silver-ceramics-based inorganic antibacterial agents, silver-silica gel-based inorganic antibacterial agents, silver-zirconium phosphate-based inorganic antibacterial agents, and the like are mentioned, and are preferably used.
【００２７】上記銀系無機抗菌剤は、銀を主抗菌成分と
するが、銅、亜鉛、錫等の銀以外の金属の１種もしくは
２種以上が銀と併用されていても良い。The silver-based inorganic antibacterial agent contains silver as a main antibacterial component, but one or more metals other than silver, such as copper, zinc and tin, may be used in combination with silver.
【００２８】又、上記銀系無機抗菌剤は、単独で用いら
れても良いし、２種類以上が併用されても良い。The silver-based inorganic antibacterial agents may be used alone or in combination of two or more.
【００２９】さらに、熱硬化性樹脂成形材料中における
上記銀系無機抗菌剤の含有量は、特に限定されるもので
はないが、前記熱硬化性樹脂１００重量部に対し、銀系
無機抗菌剤０．００５〜２重量部であることが好まし
い。Further, the content of the silver-based inorganic antibacterial agent in the thermosetting resin molding material is not particularly limited, but the silver-based inorganic antibacterial agent is added to 100 parts by weight of the thermosetting resin. It is preferably 0.005 to 2 parts by weight.
【００３０】熱硬化性樹脂１００重量部に対する銀系無
機抗菌剤の含有量が０．００５重量部未満であると、得
られる成形体の抗菌性が不十分となることがあり、逆に
２重量部を超えると、もはや抗菌性はそれ以上向上しな
いにもかかわらず、コスト高となることがある。If the content of the silver-based inorganic antibacterial agent is less than 0.005 parts by weight based on 100 parts by weight of the thermosetting resin, the obtained molded article may have insufficient antibacterial properties, and on the contrary, 2 parts by weight. If the amount exceeds the limit, the antibacterial property may no longer be improved, but the cost may be increased.
【００３１】本発明で用いられる熱硬化性樹脂成形材料
に含有される硬化剤としては、特に限定されるものでは
ないが、例えば、ターシャリーブチルパーオキシイソブ
チレート、ターシャリーブチルパーオキシ２−エチルヘ
キサノエート、ターシャリーアミルパーオキシ２−エチ
ルヘキサノエート、２，４，４−トリメチルペンチルパ
ーオキシ２−エチルヘキサノエート、ターシャリーブチ
ルパーオキシピバレート、ターシャリーブチルパーオキ
シベンゾエート、ターシャリーブチルパーオキシイソプ
ロピルカーボネート、ターシャリーブチルパーオキシ
３，５，５−トリメチルヘキサノエート、１，１−ビス
（ターシャリーブチルパーオキシ）３，３，５−トリメ
チルシクロヘキサン、ベンゾイルパーオキサイド、メチ
ルエチルケトンパーオキサイド、クメンハイドロパーオ
キサイド等の有機過酸化物が挙げられ、好適に用いられ
る。The curing agent contained in the thermosetting resin molding material used in the present invention is not particularly limited. For example, tertiary butyl peroxyisobutyrate, tertiary butyl peroxy 2-butyrate, etc. Ethyl hexanoate, tertiary amyl peroxy 2-ethylhexanoate, 2,4,4-trimethylpentylperoxy 2-ethylhexanoate, tertiary butyl peroxypivalate, tertiary butyl peroxybenzoate, tertiary T-butylperoxyisopropyl carbonate, tert-butylperoxy 3,5,5-trimethylhexanoate, 1,1-bis (tert-butylperoxy) 3,3,5-trimethylcyclohexane, benzoyl peroxide, methyl ethyl ketone per Kisaido, organic peroxides such as cumene hydroperoxide and the like, is preferably used.
【００３２】上記硬化剤は、単独で用いられても良い
し、２種類以上が併用されても良い。The above curing agents may be used alone or in combination of two or more.
【００３３】本発明で用いられる熱硬化性樹脂成形材料
中には、必須成分である熱硬化性樹脂、銀系無機抗菌剤
及び硬化剤以外に、本発明の課題達成を阻害しない範囲
で必要に応じて、強化繊維、無機充填剤、滑剤、増粘
剤、離型剤、重合禁止剤、安定剤、酸化防止剤、紫外線
吸収剤、空気（酸素）遮断剤、着色剤等の各種添加剤の
１種もしくは２種以上が含有されていても良い。In the thermosetting resin molding material used in the present invention, in addition to the essential components of the thermosetting resin, the silver-based inorganic antibacterial agent and the hardening agent, it is necessary that the thermosetting resin does not impair the achievement of the object of the present invention. Accordingly, various additives such as reinforcing fibers, inorganic fillers, lubricants, thickeners, release agents, polymerization inhibitors, stabilizers, antioxidants, ultraviolet absorbers, air (oxygen) blocking agents, coloring agents, etc. One or more kinds may be contained.
【００３４】強化繊維としては、特に限定されるもので
はないが、例えば、ガラス繊維、炭素繊維、石綿繊維、
ホイスカー、有機合成繊維、天然繊維等が挙げられ、好
適に用いられるが、なかでも物性とコストのバランスが
良好なガラス繊維がより好適に用いられる。これらの強
化繊維は、単独で用いられても良いし、２種類以上が併
用されても良い。The reinforcing fibers are not particularly limited, but include, for example, glass fibers, carbon fibers, asbestos fibers,
Whiskers, organic synthetic fibers, natural fibers, and the like are mentioned, and are preferably used. Among them, glass fibers having a good balance between physical properties and cost are more preferably used. These reinforcing fibers may be used alone or in combination of two or more.
【００３５】上記強化繊維は、一定長さ又は連続した繊
維をそのまま使用しても良いし、マット状やクロス状の
ものを使用しても良い。例えばガラス繊維の場合、スト
ランドを一定長さに切断したチョップドストランド、チ
ョップドストランドをバインダーで接着しマット状にし
たチョップドストランドマット等が好適に使用される。
一定長さの繊維の繊維長は、特に限定されるものではな
いが、１〜８０ｍｍであることが好ましい。繊維長が１
ｍｍ未満であると、十分な補強効果を得られないことが
あり、逆に８０ｍｍを超えると、得られる熱硬化性樹脂
成形材料の粘度が高くなり過ぎて、成形性が悪くなるこ
とがある。又、熱硬化性樹脂成形材料中の強化繊維の方
向性は、特に限定されるものではなく、ランダム状に並
べたもの、一定方向に並べたもの、Ｘ字状に並べたもの
等のいずれであっても良い。As the reinforcing fiber, a fiber having a fixed length or a continuous length may be used as it is, or a mat-like or cloth-like fiber may be used. For example, in the case of glass fiber, a chopped strand obtained by cutting a strand into a predetermined length, a chopped strand mat formed by bonding a chopped strand with a binder and forming a mat, and the like are preferably used.
The fiber length of the fiber having a fixed length is not particularly limited, but is preferably 1 to 80 mm. Fiber length is 1
If it is less than 80 mm, a sufficient reinforcing effect may not be obtained. On the contrary, if it exceeds 80 mm, the viscosity of the obtained thermosetting resin molding material becomes too high, and the moldability may be deteriorated. The directionality of the reinforcing fibers in the thermosetting resin molding material is not particularly limited, and may be any of those arranged in a random shape, those arranged in a fixed direction, those arranged in an X shape, and the like. There may be.
【００３６】さらに、熱硬化性樹脂成形材料中の上記強
化繊維の含有量は、特に限定されるものではないが、成
形材料全体に対して強化繊維１〜４０重量％であること
が好ましく、３〜３５重量％であることがより好まし
い。Further, the content of the reinforcing fibers in the thermosetting resin molding material is not particularly limited, but is preferably 1 to 40% by weight of the reinforcing fibers with respect to the whole molding material. More preferably, it is about 35% by weight.
【００３７】成形材料全体に対する強化繊維の含有量が
１重量％未満であると、十分な補強効果を得られないこ
とがあり、逆に４０重量％を超えると、成形材料の粘度
が上昇して成形時の流動性が乏しくなることがある。If the content of the reinforcing fibers with respect to the whole molding material is less than 1% by weight, a sufficient reinforcing effect may not be obtained. Conversely, if it exceeds 40% by weight, the viscosity of the molding material increases. The fluidity during molding may be poor.
【００３８】無機充填剤としては、特に限定されるもの
ではないが、例えば、炭酸カルシウム、水酸化アルミニ
ウム、硫酸カルシウム、ガラス粉末、タルク、マイカ等
が挙げられ、好適に用いられる。これらの無機充填剤
は、単独で用いられても良いし、２種類以上が併用され
ても良い。The inorganic filler is not particularly restricted but includes, for example, calcium carbonate, aluminum hydroxide, calcium sulfate, glass powder, talc, mica and the like, and are preferably used. These inorganic fillers may be used alone or in combination of two or more.
【００３９】上記無機充填剤の平均粒子径は、特に限定
されるものではないが、０．１〜１００μｍであること
が好ましく、０．５〜６０μｍであることがより好まし
い。無機充填剤の平均粒子径が０．１μｍ未満である
と、成形材料の粘度が高くなり過ぎて、強化繊維に十分
含浸しないため、成形材料内部にエアーを混入し易くな
って、得られる成形体に巣やピンホールが発生し易くな
ることがあり、逆に無機充填剤の平均粒子径が１００μ
ｍを超えると、成形時の成形材料の流動性が低下するこ
とがある。The average particle diameter of the inorganic filler is not particularly limited, but is preferably 0.1 to 100 μm, more preferably 0.5 to 60 μm. When the average particle size of the inorganic filler is less than 0.1 μm, the viscosity of the molding material becomes too high, and the reinforcing fibers are not sufficiently impregnated. In some cases, nests and pinholes are easily generated, and conversely, the average particle diameter of the inorganic filler is 100 μm.
If it exceeds m, the fluidity of the molding material during molding may decrease.
【００４０】又、無機充填剤の含有量は、特に限定され
るものではないが、主成分である前記熱硬化性樹脂１０
０重量部に対し、無機充填剤８０〜３５０重量部である
ことが好ましく、１００〜３００重量部であることがよ
り好ましい。Although the content of the inorganic filler is not particularly limited, the content of the thermosetting resin 10
The amount of the inorganic filler is preferably 80 to 350 parts by weight, more preferably 100 to 300 parts by weight, based on 0 parts by weight.
【００４１】熱硬化性樹脂１００重量部に対する無機充
填剤の含有量が８０重量部未満であると、成形前の成形
材料の取扱い性が低下することがあり、逆に３５０重量
部を超えると、成形材料の粘度が大幅に上昇し、成形時
の成形材料の流動性が低下したり、強化繊維に対する含
浸性が低下して成形材料内部にエアーを混入し易くな
り、得られる成形体に巣やピンホールが発生し易くなる
ことがある。If the content of the inorganic filler relative to 100 parts by weight of the thermosetting resin is less than 80 parts by weight, the handleability of the molding material before molding may be deteriorated. The viscosity of the molding material is greatly increased, the fluidity of the molding material at the time of molding is reduced, or the impregnating property with respect to the reinforcing fibers is reduced, so that air is easily mixed into the molding material, and nests and Pinholes may easily occur.
【００４２】滑剤としては、特に限定されるものではな
いが、例えば、ポリエチレンワックスや流動パラフィン
等のような炭化水素系滑剤、ステアリン酸等のような高
級脂肪酸系滑剤、脂肪酸アミドやアルキレンビス脂肪酸
アミド等のような脂肪酸アミド系滑剤、脂肪酸の一価ア
ルコールエステル、脂肪酸の多価アルコールエステル、
脂肪酸のポリグリコールエステル等のようなエステル系
滑剤、脂肪族アルコール、多価アルコール、ポリグリコ
ール、ポリグリセロール等のようなアルコール系滑剤、
金属石鹸系滑剤等が挙げられ、好適に用いられるが、な
かでも一価の脂肪族アルコール、ソルビタン脂肪酸エス
テル、グリセリン脂肪酸エステル、ネオペンチル系ポリ
オール脂肪酸エステル、高級アルコール脂肪酸エステ
ル、脂肪酸アミド等がより好適に用いられる。これらの
滑剤は、単独で用いられても良いし、２種類以上が併用
されても良い。The lubricant is not particularly restricted but includes, for example, hydrocarbon lubricants such as polyethylene wax and liquid paraffin, higher fatty acid lubricants such as stearic acid, fatty acid amides and alkylene bis fatty acid amides. Fatty acid amide lubricants such as, monohydric alcohol esters of fatty acids, polyhydric alcohol esters of fatty acids,
Ester lubricants such as polyglycol esters of fatty acids, aliphatic alcohols, polyhydric alcohols, polyglycols, alcohol lubricants such as polyglycerol,
Examples include metal soap-based lubricants, which are preferably used, among which monohydric aliphatic alcohols, sorbitan fatty acid esters, glycerin fatty acid esters, neopentyl polyol fatty acid esters, higher alcohol fatty acid esters, fatty acid amides and the like are more preferable. Used. These lubricants may be used alone or in combination of two or more.
【００４３】上記滑剤の融点は、特に限定されるもので
はないが、４０〜１５０℃であることが好ましく、４０
〜１２０℃であることがより好ましい。The melting point of the lubricant is not particularly limited, but is preferably 40 to 150 ° C.,
It is more preferable that the temperature is 120 ° C.
【００４４】滑剤の融点が４０℃未満であると、成形前
の成形材料の取扱い性が低下することがあり、逆に１５
０℃を超えると、成形時の成形材料の流動性を向上させ
るために成形温度を高める必要が生じることがある。If the melting point of the lubricant is less than 40 ° C., the handleability of the molding material before molding may be reduced.
If the temperature exceeds 0 ° C., it may be necessary to increase the molding temperature in order to improve the fluidity of the molding material during molding.
【００４５】又、滑剤の含有量は、特に限定されるもの
ではないが、主成分である前記熱硬化性樹脂１００重量
部に対し、滑剤０．１〜２０重量部であることが好まし
く、０．５〜１０重量部であることがより好ましい。The content of the lubricant is not particularly limited, but is preferably 0.1 to 20 parts by weight of the lubricant with respect to 100 parts by weight of the thermosetting resin as the main component. More preferably, it is 0.5 to 10 parts by weight.
【００４６】熱硬化性樹脂１００重量部に対する滑剤の
含有量が０．１重量部未満であると、成形時の成形材料
の流動性向上効果を十分に得られないことがあり、逆に
２０重量部を超えると、得られる成形体の機械的強度が
低下することがある。If the content of the lubricant is less than 0.1 part by weight with respect to 100 parts by weight of the thermosetting resin, the effect of improving the fluidity of the molding material at the time of molding may not be sufficiently obtained. When the amount exceeds the part, the mechanical strength of the obtained molded body may be reduced.
【００４７】増粘剤としては、特に限定されるものでは
ないが、例えば、酸化マグネシウム、水酸化マグネシウ
ム、酸化カルシウム、水酸化カルシウム、酸化亜鉛等が
挙げられ、好適に用いられる。これらの増粘剤は、単独
で用いられても良いし、２種類以上が併用されても良
い。The thickener is not particularly restricted but includes, for example, magnesium oxide, magnesium hydroxide, calcium oxide, calcium hydroxide, zinc oxide and the like, and is preferably used. These thickeners may be used alone or in combination of two or more.
【００４８】離型剤としては、特に限定されるものでは
ないが、例えば、ステアリン酸亜鉛、ステアリン酸カル
シウム等が挙げられ、好適に用いられる。これらの離型
剤は、単独で用いられても良いし、２種類以上が併用さ
れても良い。The release agent is not particularly restricted but includes, for example, zinc stearate and calcium stearate, and is preferably used. These release agents may be used alone or in combination of two or more.
【００４９】重合禁止剤としては、特に限定されるもの
ではないが、例えば、ハイドロキノンやパラベンゾキノ
ン等のキノン類が挙げられ、好適に用いられる。これら
の重合禁止剤は、単独で用いられても良いし、２種類以
上が併用されても良い。The polymerization inhibitor is not particularly restricted but includes, for example, quinones such as hydroquinone and parabenzoquinone, and are preferably used. These polymerization inhibitors may be used alone or in combination of two or more.
【００５０】本発明で用いられる熱硬化性樹脂成形材料
は、シート状に形成された成形材料であっても良いし、
バルク状に形成された成形材料であっても良い。The thermosetting resin molding material used in the present invention may be a sheet-shaped molding material,
It may be a molding material formed in a bulk.
【００５１】シート状成形材料は、シートモールディン
グコンパウンド（ＳＭＣ）又はシックモールディングコ
ンパウンド（ＴＭＣ）と呼称され、公知の機械を用いて
形成される。シート状成形材料の形成方法は、特に限定
されるものではなく、例えば、ドクターブレード等の塗
工機を用いて、ポリエチレンフィルム等のような離型シ
ートの上に強化繊維を除く熱硬化性樹脂組成物を塗工厚
みが均一となるように塗工し、その塗工面に強化繊維を
散布した後、同様にして塗工した離型シート上の熱硬化
性樹脂組成物で強化繊維をサンドイッチ状に積層し、ロ
ールを用いて、強化繊維中に熱硬化性樹脂組成物を含浸
させながらシート状に形成することにより、所望のシー
ト状成形材料を得ることが出来る。The sheet-shaped molding material is called a sheet molding compound (SMC) or a thick molding compound (TMC), and is formed using a known machine. The method of forming the sheet-shaped molding material is not particularly limited. For example, using a coating machine such as a doctor blade, a thermosetting resin excluding reinforcing fibers on a release sheet such as a polyethylene film or the like. The composition is coated so that the coating thickness is uniform, and the reinforcing fibers are sprayed on the coated surface, and then the reinforcing fibers are sandwiched with the thermosetting resin composition on the release sheet similarly coated. And forming the sheet into a sheet using a roll while impregnating the thermosetting resin composition in the reinforcing fiber, whereby a desired sheet-like molding material can be obtained.
【００５２】又、バルク状成形材料は、バルクモールデ
ィングコンパウンド（ＢＭＣ）と呼称され、その形成方
法は、特に限定されるものではなく、例えば、ニーダー
等の混練機を用いて、熱硬化性樹脂組成物に含有させる
各成分の所定量を均一に攪拌混練することにより、所望
のバルク状成形材料を得ることが出来る。The bulk molding material is called a bulk molding compound (BMC), and its forming method is not particularly limited. For example, a thermosetting resin composition is prepared by using a kneading machine such as a kneader. A desired bulk molding material can be obtained by uniformly stirring and kneading a predetermined amount of each component contained in the product.
【００５３】上記で得られたシート状もしくはバルク状
の熱硬化性樹脂成形材料は、通常、３０〜５０℃の雰囲
気下で半日〜２日間熟成され、増粘し、半固形状となっ
た状態で使用に供される。The sheet-like or bulk-like thermosetting resin molding material obtained above is usually aged in an atmosphere of 30 to 50 ° C. for half a day to two days, and is thickened to a semi-solid state. Served for use.
【００５４】又、上記シート状もしくはバルク状の熱硬
化性樹脂成形材料は、通常、６０〜１６０℃に加熱され
た金型内に必要量が投入され、２〜１５０ｋｇ／ｃｍ2
の成形圧力で圧縮成形されて賦形され、成形体となされ
る。The sheet or bulk thermosetting resin molding material is usually charged in a required amount into a mold heated to 60 to 160 ° C., and then a required amount is set to 2 to 150 kg / cm 2.
Compression molding at a molding pressure of, and shaping to form a molded body.
【００５５】本発明による熱硬化性樹脂成形体の製造方
法は、上述の如くして得られたシート状もしくはバルク
状熱硬化性樹脂成形材料の必要量を、加熱された金型内
に投入し、加熱下、金型に振動を加えながら圧縮成形し
て賦形し、成形体となすことを特徴とする。In the method for producing a thermosetting resin molded article according to the present invention, a required amount of the sheet-shaped or bulk-shaped thermosetting resin molding material obtained as described above is charged into a heated mold. The compression molding is performed while applying vibrations to the mold under heating to form a molded body.
【００５６】上記金型の加熱温度（成形温度）は、特に
限定されるものではないが、６０〜１６０℃であること
が好ましく、８０〜１５０℃であることがより好まし
い。The heating temperature (molding temperature) of the mold is not particularly limited, but is preferably from 60 to 160 ° C., more preferably from 80 to 150 ° C.
【００５７】金型の加熱温度（成形温度）が６０℃未満
であると、成形材料の流動性が不十分となって、所望の
成形体を得られ難いことがあり、逆に１６０℃を超える
と、高コストの金型を使用する必要性が生じることがあ
る。If the heating temperature (molding temperature) of the mold is less than 60 ° C., the fluidity of the molding material becomes insufficient, and it may be difficult to obtain a desired molded body. In some cases, it is necessary to use a high-cost mold.
【００５８】又、圧縮成形時の成形圧力は、特に限定さ
れるものではないが、２〜１５０ｋｇ／ｃｍ2 であるこ
とが好ましく、１０〜１００ｋｇ／ｃｍ2 であることが
より好ましい。[0058] In addition, the molding pressure at the time of compression molding is not particularly limited, is preferably 2~150kg / cm 2, and more preferably 10 to 100 kg / cm 2.
【００５９】圧縮成形時の成形圧力が２ｋｇ／ｃｍ2 未
満であると、成形材料の流動性が不十分となって、所望
の成形体を得られ難いことがあり、逆に１５０ｋｇ／ｃ
ｍ2を超えると、高コストの金型を使用する必要性が生
じることがある。If the molding pressure at the time of compression molding is less than 2 kg / cm 2 , the fluidity of the molding material becomes insufficient, and it may be difficult to obtain a desired molded body.
Above m 2 , it may be necessary to use expensive molds.
【００６０】本発明の製造方法においては、前記熱硬化
性樹脂成形材料は、振動が加えられている状態にある加
熱された金型内で流動し、賦形される。In the production method of the present invention, the thermosetting resin molding material flows and is shaped in a heated mold in a state where vibration is applied.
【００６１】金型に振動を加える時の時間帯は、特に限
定されるものではないが、例えば、成形材料を下型もし
くは上型のどちらか一方の金型内に投入した後、他方の
金型が成形材料に接触した時点から成形材料の流動性が
失われる迄の時間帯、換言すれば、成形材料の硬化が十
分に進行する迄の時間帯、であることが好ましい。The time period during which vibration is applied to the mold is not particularly limited. For example, after the molding material is charged into one of the lower mold and the upper mold, the other mold is used. The time period from the point when the mold comes into contact with the molding material to the time when the fluidity of the molding material is lost, in other words, the time period until the curing of the molding material sufficiently proceeds is preferable.
【００６２】又、金型に振動を加える時の振動特性は、
特に限定されるものではないが、例えば、振動周波数２
０〜５０００Ｈｚ、振動振幅２〜６０μｍであることが
好ましく、なかでも、振動を加えることによって得られ
る効果と金型の耐久性とのバランスを考慮すると、振動
周波数５００〜３０００Ｈｚ、振動振幅５〜３０μｍで
あることがより好ましい。The vibration characteristics when applying vibration to the mold are as follows:
Although not particularly limited, for example, the vibration frequency 2
Preferably, the vibration frequency is 0 to 5000 Hz and the vibration amplitude is 2 to 60 μm. In particular, considering the balance between the effect obtained by applying vibration and the durability of the mold, the vibration frequency is 500 to 3000 Hz and the vibration amplitude is 5 to 30 μm. Is more preferable.
【００６３】さらに、上記振動の方向は、特に限定され
るものではなく、鉛直方向、水平方向、三次元方向のい
ずれの方向であっても良い。Further, the direction of the vibration is not particularly limited, and may be any of a vertical direction, a horizontal direction, and a three-dimensional direction.
【００６４】さらに又、上記振動の発生方式としては、
特に限定されるものではないが、例えば、カム・クラン
ク式やアンバランスウェイト式等の機械的方式、動電型
加振機のような電磁型の電気的方式、電気油圧方式等が
挙げられ、いずれの方式も好適に採用される。Further, as a method of generating the vibration,
Although not particularly limited, for example, a mechanical system such as a cam-crank system or an unbalanced weight system, an electromagnetic electric system such as an electrodynamic shaker, an electrohydraulic system, and the like, Either method is suitably adopted.
【００６５】[0065]
【作用】本発明の製造方法によれば、熱硬化性樹脂、銀
系無機抗菌剤及び硬化剤が含有されてなる熱硬化性樹脂
成形材料を、加熱下、圧縮成形して賦形する際に、金型
に振動を加えるので、熱硬化性樹脂と銀系無機抗菌剤と
の比重差を利用して、銀系無機抗菌剤の濃度を成形体の
厚み方向に分布させることが出来る。しかも銀系無機抗
菌剤の濃度分布は、振動を加えるタイミング、振動を加
える時間帯、振動周波数、振動振幅等を適宜調整するこ
とにより自在に制御出来る。従って、銀系無機抗菌剤を
成形体の表面層を含む厚み方向の所望の位置に選択的に
分布させることが可能であり、その結果、銀系無機抗菌
剤の使用量が比較的少量であっても、得られる熱硬化性
樹脂成形体の抗菌性及び抗菌効果の持続性は優れたもの
となる。According to the production method of the present invention, when a thermosetting resin molding material containing a thermosetting resin, a silver-based inorganic antibacterial agent and a curing agent is subjected to compression molding under heating to shape it, Since the vibration is applied to the mold, the concentration of the silver-based inorganic antibacterial agent can be distributed in the thickness direction of the molded body by utilizing the difference in specific gravity between the thermosetting resin and the silver-based inorganic antibacterial agent. Moreover, the concentration distribution of the silver-based inorganic antibacterial agent can be freely controlled by appropriately adjusting the timing of applying the vibration, the time period during which the vibration is applied, the vibration frequency, the vibration amplitude, and the like. Accordingly, it is possible to selectively distribute the silver-based inorganic antibacterial agent at a desired position in the thickness direction including the surface layer of the molded article, and as a result, the amount of the silver-based inorganic antibacterial agent used is relatively small. However, the obtained thermosetting resin molded article has excellent antibacterial properties and sustainability of the antibacterial effect.
【００６６】[0066]
【発明の実施の形態】本発明における好ましい実施の形
態を以下に述べる。DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the present invention will be described below.
【００６７】熱硬化性樹脂として不飽和ポリエステル樹
脂を用い、不飽和ポリエステル樹脂１００重量部に対
し、銀系無機抗菌剤０．０１〜１重量部、無機充填剤と
して、炭酸カルシウム（平均粒子径０．５〜２０μｍ）
１００〜３００重量部、もしくは、水酸化アルミニウム
（平均粒子径０．５〜３０μｍ）１００〜３００重量
部、又は、ガラス粉末（平均粒子径０．５〜２０μｍ）
１００〜３００重量部を添加混合する。尚、上記無機充
填剤を２種類以上併用する場合には、その合計量１００
〜３００重量部を添加混合する。次いで、上記混合物
に、硬化剤として有機過酸化物０．２〜２重量部、離型
剤としてステアリン酸亜鉛２〜１０重量部及び増粘剤と
して酸化マグネシウム０．２〜３重量部を添加し、均一
に攪拌混合して熱硬化性樹脂組成物を得る。An unsaturated polyester resin is used as a thermosetting resin, and 0.01 to 1 part by weight of a silver-based inorganic antibacterial agent is used with respect to 100 parts by weight of the unsaturated polyester resin. 0.5 to 20 μm)
100 to 300 parts by weight, or 100 to 300 parts by weight of aluminum hydroxide (average particle diameter 0.5 to 30 μm) or glass powder (average particle diameter 0.5 to 20 μm)
100 to 300 parts by weight are added and mixed. When two or more of the above-mentioned inorganic fillers are used in combination, the total amount thereof is 100
３００300 parts by weight are added and mixed. Next, 0.2 to 2 parts by weight of an organic peroxide as a curing agent, 2 to 10 parts by weight of zinc stearate as a release agent, and 0.2 to 3 parts by weight of magnesium oxide as a thickener are added to the mixture. The mixture is uniformly stirred and mixed to obtain a thermosetting resin composition.
【００６８】ＳＭＣやＴＭＣ又はＢＭＣ製造装置を用い
て、上記で得られた熱硬化性樹脂組成物に対し、熱硬化
性樹脂組成物と強化繊維との合計量の３〜３５重量％に
相当する強化繊維を添加し、ＳＭＣやＴＭＣ又はＢＭＣ
を形成した後、３０〜５０℃で半日〜２日間熟成して、
熱硬化性樹脂成形材料を作製する。Using an SMC, TMC or BMC production equipment, the amount of the thermosetting resin composition corresponds to 3 to 35% by weight of the total amount of the thermosetting resin composition and the reinforcing fibers. Add reinforced fiber, SMC, TMC or BMC
After aging at 30 to 50 ° C. for half a day to 2 days,
A thermosetting resin molding material is produced.
【００６９】次いで、上記で得られた熱硬化性樹脂成形
材料を８０〜１５０℃に加熱された一方の金型内に投入
し、８０〜１５０℃に加熱された他方の金型を閉じ、成
形材料が両金型に接触した時点から、金型に対し振動周
波数５００〜３０００Ｈｚ、振動振幅５〜３０μｍの振
動を５秒〜５分間加えつつ、成形圧力１０〜１００ｋｇ
／ｃｍ2 で圧縮成形を行って成形材料を賦形し、所望の
熱硬化性樹脂成形体を得る。Next, the thermosetting resin molding material obtained above is put into one mold heated to 80 to 150 ° C., the other mold heated to 80 to 150 ° C. is closed, and the molding is performed. After the material comes into contact with both molds, a molding pressure of 10 to 100 kg is applied to the molds while applying a vibration frequency of 500 to 3000 Hz and a vibration amplitude of 5 to 30 μm for 5 seconds to 5 minutes.
/ Cm 2 to form a molding material by compression molding to obtain a desired thermosetting resin molded body.
【００７０】本発明をさらに詳しく説明するため以下に
実施例を挙げるが、本発明はこれら実施例のみに限定さ
れるものではない。The present invention will be described in more detail with reference to the following examples, but the present invention is not limited to these examples.
【００７１】（実施例）(Example)
【００７２】（１）熱硬化性樹脂組成物及び成形材料の
作製 フマル酸、イソフタル酸及びプロピレングリコールから
なる不飽和ポリエステルとポリスチレンとをスチレン単
量体に溶解して得られた不飽和ポリエステル樹脂１００
重量部に対し、銀系無機抗菌剤として銀−ガラス系無機
抗菌剤０．１重量部、無機充填剤として水酸化アルミニ
ウム（平均粒子径８μｍ）１８０重量部、硬化剤として
ターシャリーブチルパーオキシベンゾエート１重量部、
増粘剤として酸化マグネシウム１重量部、重合禁止剤と
してパラベンゾキノン０．０３重量部、離型剤としてス
テアリン酸亜鉛５重量部及び強化繊維としてチョップド
ストランドガラス繊維（繊維長３ｍｍ）を添加し、均一
に攪拌混練した後、４０℃の雰囲気下で１日間熟成し
て、バルク状成形材料（ＢＭＣ）を得た。得られたＢＭ
Ｃ中の強化繊維の含有量は１０重量％であった。(1) Preparation of Thermosetting Resin Composition and Molding Material Unsaturated polyester resin 100 obtained by dissolving polystyrene and an unsaturated polyester comprising fumaric acid, isophthalic acid and propylene glycol in a styrene monomer.
0.1 part by weight of a silver-glass inorganic antibacterial agent as a silver-based inorganic antibacterial agent, 180 parts by weight of aluminum hydroxide (average particle size 8 μm) as an inorganic filler, and tertiary butyl peroxybenzoate as a curing agent 1 part by weight,
Add 1 part by weight of magnesium oxide as a thickener, 0.03 part by weight of parabenzoquinone as a polymerization inhibitor, 5 parts by weight of zinc stearate as a release agent, and chopped strand glass fiber (fiber length 3 mm) as a reinforcing fiber. Then, the mixture was aged in a 40 ° C. atmosphere for 1 day to obtain a bulk molding material (BMC). BM obtained
The content of the reinforcing fibers in C was 10% by weight.
【００７３】（２）成形体の成形 上記で得られたＢＭＣを用い、振動プレス機（型式「Ｓ
Ａ−５０」、能力５０トン、アサヒエンジニアリング社
製）を使用して、下記成形条件で圧縮成形を行ってＢＭ
Ｃを賦形し、平板状の成形体を得た。 〔成形条件〕 金型：平板金型（２７０ｍｍ×１５０ｍｍ×４ｍｍ） 金型温度：下型（成形体の製品面側）１５０℃、上型１
３５℃ 振動時間帯：ＢＭＣが上下金型に接触した時点から開始
し、２分間 成形圧力：５０ｋｇ／ｃｍ2 加圧時間：４分間(2) Molding of molded article Using the BMC obtained above, a vibration press (model “S
A-50 ”, capacity 50 tons, manufactured by Asahi Engineering Co., Ltd.) and compression molding under the following molding conditions
C was shaped to obtain a flat molded product. [Molding conditions] Mold: Flat mold (270 mm x 150 mm x 4 mm) Mold temperature: Lower mold (product side of molded body) 150 ° C, Upper mold 1
35 ° C. Vibration time zone: starting from the point when the BMC contacts the upper and lower molds, 2 minutes Molding pressure: 50 kg / cm 2 Pressing time: 4 minutes
【００７４】（３）抗菌性評価 上記で得られた成形体を供試片とし、その抗菌性を、銀
等無機抗菌剤研究会により１９９５年に制定された「抗
菌加工製品の抗菌力試験法Ｉ」のフィルム密着法に準拠
して、以下の試験方法で評価した。その結果は表１に示
すとおりであった。 〔試験方法〕大腸菌（ＩＦＯ−３９７２）を菌株として
用い、供試片の表面に１／５００ブイヨン加菌液を滴下
し、フィルムで密着させ、３５℃の雰囲気下に２４時間
放置した後の生菌数を測定した。その結果、減菌率９
９．０％以上を抗菌性有り、減菌率９９．０％未満を抗
菌性無しと判定した。(3) Evaluation of antibacterial activity The molded article obtained above was used as a test piece, and its antibacterial activity was evaluated by the “Testing method of antibacterial activity of antibacterial processed products” established in 1995 by the Research Group for Inorganic Antibacterial Agents such as Silver. Based on the film adhesion method of "I", evaluation was made by the following test methods. The results were as shown in Table 1. [Test Method] Using Escherichia coli (IFO-3972) as a bacterial strain, a 1/500 broth-added solution was dropped on the surface of a test piece, adhered with a film, and allowed to stand in a 35 ° C atmosphere for 24 hours. The number of bacteria was measured. As a result, the sterilization rate was 9
9.0% or more was determined to have antimicrobial activity, and the sterilization rate was determined to be less than 99.0% to have no antimicrobial activity.
【００７５】（比較例）実施例で作製したＢＭＣを用
い、成形体の成形において金型に振動を加えなかったこ
と以外は実施例と同様にして、成形体を得た。(Comparative Example) A molded article was obtained in the same manner as in the example except that no vibration was applied to the mold in molding the molded article using the BMC produced in the example.
【００７６】比較例で得られた成形体の抗菌性を実施例
の場合と同様にして評価した。その結果は表１に示すと
おりであった。The antibacterial properties of the molded articles obtained in the comparative examples were evaluated in the same manner as in the examples. The results were as shown in Table 1.
【００７７】[0077]
【表１】 [Table 1]
【００７８】表１から明らかなように、本発明の製造方
法により得られた実施例の熱硬化性樹脂成形体は、優れ
た抗菌性を発揮した。As is clear from Table 1, the thermosetting resin molded articles of the examples obtained by the production method of the present invention exhibited excellent antibacterial properties.
【００７９】これに対し、圧縮成形時に金型を振動させ
なかった比較例の熱硬化性樹脂成形体は、抗菌性が悪か
った。On the other hand, the thermosetting resin molded article of the comparative example in which the mold was not vibrated during the compression molding had poor antibacterial properties.
【００８０】[0080]
【発明の効果】以上述べたように、本発明の製造方法に
よれば、抗菌性及びその持続性に優れる熱硬化性樹脂成
形体を安価且つ簡便に得ることが出来る。As described above, according to the production method of the present invention, a thermosetting resin molded article having excellent antibacterial properties and its sustainability can be obtained inexpensively and easily.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） // Ａ０１Ｎ 59/16 Ａ０１Ｎ 59/16 Ａ Ｆターム(参考） 4F204 AA36 AB01 AB03 AB16 AD16 AH17 AH46 FA01 FB01 FB11 FG01 FN15 FN25 4H011 AA02 BA01 BB18 BC19 4J002 CC031 CD001 CD201 CF211 DA076 DH046 DJ006 DL006 DM006 EK007 FB076 FD010 FD147 FD160 FD170 FD186 FD200 GL00 GN00 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) // A01N 59/16 A01N 59/16 A F term (Reference) 4F204 AA36 AB01 AB03 AB16 AD16 AH17 AH46 FA01 FB01 FB11 FG01 FN15 FN25 4H011 AA02 BA01 BB18 BC19 4J002 CC031 CD001 CD201 CF211 DA076 DH046 DJ006 DL006 DM006 EK007 FB076 FD010 FD147 FD160 FD160 FD170 FD186 FD200 GL00 GN00
Claims (1)
剤が含有されてなる熱硬化性樹脂成形材料を、金型内に
投入し、加熱下、金型に振動を加えながら圧縮成形して
賦形し、成形体となすことを特徴とする熱硬化性樹脂成
形体の製造方法。1. A thermosetting resin molding material containing a thermosetting resin, a silver-based inorganic antibacterial agent and a curing agent is charged into a mold, and compression molding is performed while heating and applying vibration to the mold. A method for producing a thermosetting resin molded article, wherein the molded article is formed into a molded article.