JP2000037486A - Golf club shaft made from fiber reinforced plastic - Google Patents
Golf club shaft made from fiber reinforced plasticInfo
- Publication number
- JP2000037486A JP2000037486A JP10209961A JP20996198A JP2000037486A JP 2000037486 A JP2000037486 A JP 2000037486A JP 10209961 A JP10209961 A JP 10209961A JP 20996198 A JP20996198 A JP 20996198A JP 2000037486 A JP2000037486 A JP 2000037486A
- Authority
- JP
- Japan
- Prior art keywords
- golf club
- club shaft
- layer
- reinforced plastic
- diameter end
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、繊維強化プラスチ
ック製ゴルフクラブシャフトに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a golf club shaft made of fiber-reinforced plastic.
【０００２】[0002]
【従来の技術】強化繊維で補強した繊維強化プラスチッ
ク製ゴルフクラブシャフトは、一方向に引き揃えた引き
揃え糸からなるシート状の繊維に樹脂を含浸させたいわ
ゆる一方向プリプレグをテーパー付きの芯金に巻き付け
て積層し、これを硬化させて成形したものが、ゴルフク
ラブシャフトの比剛性及び比強度が高く、しかもその設
計度の自由さ等において優れていることから、広く用い
られている。2. Description of the Related Art A golf club shaft made of fiber-reinforced plastic reinforced with reinforcing fibers is a so-called one-way prepreg obtained by impregnating a resin with sheet-like fibers made of aligned yarns aligned in one direction. The golf club shaft is widely used because it has a high specific rigidity and a high specific strength and is excellent in freedom of design and the like.
【０００３】繊維強化プラスチック製ゴルフクラブシャ
フトは、太径端部側から細径端部側に向かってその外径
が徐々に小さくなっており、その曲げ剛性は多くの場合
その外径が小さくなるに従って徐々に小さくなってい
る。The outer diameter of a fiber reinforced plastic golf club shaft is gradually reduced from the large-diameter end to the small-diameter end, and the bending rigidity of the outer diameter is reduced in many cases. Gradually become smaller.
【０００４】このような形状の従来のゴルフクラブシャ
フトにあっては、手元部（グリップ部）と細径部との曲
げ剛性のバランスが適格でないと、スイング時及び打撃
時のタイミングをつかむことが非常に難しく、打球の方
向性や飛距離にバラツキを生じ易い。In a conventional golf club shaft having such a shape, if the balance between the bending rigidity of the hand portion (grip portion) and the small diameter portion is not appropriate, the timing at the time of swinging and hitting can be grasped. It is very difficult and tends to cause variation in the directionality and flight distance of the hit ball.
【０００５】つまり、細径部の曲げ剛性が低すぎると打
撃時にヘッドが上を向き易く、ボールの打ち出し角度が
大きくなるために飛距離が落ちる。又手元部（グリップ
部）の曲げ剛性が低すぎると、バックスイング時からス
イングに移る際の“タメ”をつくることが難しくなり、
安定したスイングを行ない難く、打球の弾道が不安定に
なる。That is, if the bending stiffness of the small-diameter portion is too low, the head tends to face upward at the time of hitting, and the launch angle of the ball becomes large, so that the flight distance decreases. Also, if the flexural rigidity of the hand (grip) is too low, it will be difficult to create “tame” when moving from the backswing to the swing,
It is difficult to perform a stable swing, and the trajectory of the hit ball becomes unstable.
【０００６】なお特開昭５７−２９３７４号公報には、
ヘッド側がしなり易く、良好なフィーリングが得られる
ゴルフクラブシャフトとして、中間部において外径が急
激に変化するテーパー状段部を設けた炭素繊維強化プラ
スチック製ゴルフクラブシャフトが説明されている。JP-A-57-29374 discloses that
A golf club shaft made of a carbon fiber reinforced plastic provided with a tapered step portion in which an outer diameter changes abruptly in an intermediate portion is described as a golf club shaft that easily bends on the head side and obtains a good feeling.
【０００７】しかしながら上記のゴルフクラブシャフト
は、中間部に形成されている段部から細径部側にかけて
の曲げ剛性が急激に低下してしまうために、スイング時
のヘッドの挙動を抑えきれず、このためにボールの打ち
出し角度の高い弾道を生じ易く、飛距離が落ちるという
欠点を有する。However, in the golf club shaft described above, the bending rigidity from the step formed in the intermediate portion to the small-diameter portion rapidly decreases, so that the behavior of the head at the time of swing cannot be suppressed. For this reason, there is a disadvantage that a trajectory having a high launch angle of the ball is easily generated, and a flight distance is reduced.
【０００８】[0008]
【発明が解決しようとする課題】従って本発明の課題
は、“鞭”のような振り抜き易さを有し、かつ球の吹き
上がりを抑え得る繊維強化プラスチック製ゴルフクラブ
シャフトを提供することにある。SUMMARY OF THE INVENTION Accordingly, an object of the present invention is to provide a fiber reinforced plastic golf club shaft which can be easily swung like a "whip" and can suppress the blowing of a ball. is there.
【０００９】[0009]
【課題を解決するための手段】上記の課題は、下記の通
りの構成を具備してなる本発明の繊維強化プラスチック
製ゴルフクラブシャフトによって解決することができ
る。すなわち本発明は、少なくともアングル層とストレ
ート層との２層以上の繊維強化プラスチック層を積層さ
せてなるゴルフクラブシャフトであって、該ゴルフクラ
ブシャフトをその細径端部側から太径端部側に向かって
順次、全長の１５〜４０％の範囲をなす長さの細径部
（ＡＬ）と、同じく全長の３０〜６０％の範囲をなす長
さの中央部（ＢＬ）と、同じく全長の２５〜４０％の範
囲をなす長さの太径部（ＣＬ）との３つのブロックにし
たときに、曲げ剛性値がこれらの３つのブロック内にお
いてそれぞれ１個の極大値を有している繊維強化プラス
チック製ゴルフクラブシャフトからなる。The above objects can be attained by a fiber reinforced plastic golf club shaft of the present invention having the following structure. That is, the present invention relates to a golf club shaft obtained by laminating at least two fiber-reinforced plastic layers of an angle layer and a straight layer, wherein the golf club shaft is moved from the small-diameter end to the large-diameter end. , A small-diameter portion (AL) having a length in the range of 15 to 40% of the total length, a central portion (BL) having a length in the range of 30 to 60% of the total length, and a A fiber having a bending rigidity value of one maximum value in each of these three blocks when formed into three blocks with a large diameter portion (CL) having a length ranging from 25 to 40%. It consists of a golf club shaft made of reinforced plastic.
【００１０】上記の構成を備えてなる本発明の繊維強化
プラスチック製ゴルフクラブシャフトにおいては、細径
部（ＡＬ）における曲げ剛性値の極大値（Ａｍａｘ）が
１２〜２８Ｎ・ｍ2 であり、中央部（ＢＬ）における曲
げ剛性値の極大値（Ｂｍａｘ）が２５〜５０Ｎ・ｍ2 で
あり、太径部（ＣＬ）における曲げ剛性値の極大値（Ｃ
ｍａｘ）が３５〜７０Ｎ・ｍ2 であることが好ましい。In the fiber reinforced plastic golf club shaft of the present invention having the above structure, the maximum value (Amax) of the bending rigidity value in the small diameter portion (AL) is 12 to 28 N · m 2 , The maximum value (Bmax) of the bending stiffness value in the portion (BL) is 25 to 50 N · m 2 , and the maximum value (C) of the bending stiffness value in the large diameter portion (CL).
max) is preferably from 35 to 70 N · m 2 .
【００１１】又、上記の構成を備えてなる本発明の繊維
強化プラスチック製ゴルフクラブシャフトにおいては、
重量が４０〜７０ｇであり、全長が８５０〜１２７０ｍ
ｍであり、細径端部の外径が７〜１０ｍｍであり、太径
端部の外径が１４〜３０ｍｍであることが好ましい。[0011] In the fiber reinforced plastic golf club shaft of the present invention having the above structure,
Weight is 40-70g and total length is 850-1270m
m, the outer diameter of the small diameter end is preferably 7 to 10 mm, and the outer diameter of the large diameter end is preferably 14 to 30 mm.
【００１２】なお、繊維強化プラスチック製ゴルフクラ
ブシャフトにおける上記の曲げ剛性値の極大値の有、
無、及び該極大値の数値は、後述する曲げ剛性分布の測
定結果に基づいて行なう。The golf club shaft made of fiber reinforced plastic has a maximum bending stiffness value.
None and the value of the maximum value are determined based on the measurement result of the bending rigidity distribution described later.
【００１３】[0013]
【発明の実施の形態】以下に、本発明の繊維強化プラス
チック製ゴルフクラブシャフトの望ましい実施の形態を
説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS Preferred embodiments of the fiber reinforced plastic golf club shaft of the present invention will be described below.
【００１４】本発明の繊維強化プラスチック製ゴルフク
ラブシャフトは、少なくともアングル層とストレート層
との２層以上の繊維強化プラスチック層を具備するもの
であって、これらの各繊維強化プラスチック層は、強化
繊維とマトリックス樹脂とからなる。The fiber reinforced plastic golf club shaft of the present invention has at least two or more fiber reinforced plastic layers of an angle layer and a straight layer. And a matrix resin.
【００１５】上記のアングル層をなす繊維強化プラスチ
ック層は、該プラスチック層中の強化繊維がシャフトの
長手方向に対して±（３０〜７０°）に配向しているプ
ラスチック層であり、又ストレート層をなす繊維強化プ
ラスチック層は、該プラスチック層中の強化繊維がシャ
フトの長手方向に対して−２０〜２０°に配向している
プラスチック層である。なお、シャフトの長手方向に対
する強化繊維の配向角度を、強化繊維の配向角という。
つまりアングル層は、強化繊維の配向角が±（３０〜７
０°）のプラスチック層であり、又ストレート層は、強
化繊維の配向角が−２０〜２０°のプラスチック層であ
る。The fiber reinforced plastic layer forming the angle layer is a plastic layer in which the reinforcing fibers in the plastic layer are oriented at ± (30 to 70 °) with respect to the longitudinal direction of the shaft. Is a plastic layer in which the reinforcing fibers in the plastic layer are oriented at -20 to 20 with respect to the longitudinal direction of the shaft. Note that the orientation angle of the reinforcing fibers with respect to the longitudinal direction of the shaft is referred to as the orientation angle of the reinforcing fibers.
That is, in the angle layer, the orientation angle of the reinforcing fiber is ± (30 to 7).
0 °), and the straight layer is a plastic layer in which the orientation angle of the reinforcing fibers is −20 to 20 °.
【００１６】繊維強化プラスチック層中の強化繊維とし
ては、従来の繊維強化プラスチック製ゴルフクラブシャ
フトに使用されている繊維、例えばパラ系芳香族ポリア
ミドや高強度ポリエチレン等の有機系繊維、炭素繊維、
ガラス繊維、ボロン繊維、炭化ケイ素繊維、アルミナ繊
維、チラノ繊維等の無機繊維、及び金属繊維を使用し得
る。なお強化繊維は、単一種類のものを使用しても、或
いは２種類以上のものを併用してもよい。As the reinforcing fibers in the fiber-reinforced plastic layer, fibers used in conventional golf club shafts made of fiber-reinforced plastics, for example, organic fibers such as para-aromatic polyamide and high-strength polyethylene, carbon fibers,
Inorganic fibers such as glass fibers, boron fibers, silicon carbide fibers, alumina fibers, and Tyranno fibers, and metal fibers can be used. In addition, a single type of reinforcing fiber may be used, or two or more types may be used in combination.
【００１７】又マトリックス樹脂も特に限定されること
なく、従来の繊維強化プラスチック製ゴルフクラブシャ
フトに使用されている樹脂、例えばエポキシ樹脂、不飽
和ポリエステル樹脂、ビニルエステル樹脂、ポリイミド
樹脂、ポリビスマレイミド樹脂等の熱硬化性樹脂や、そ
の他の熱可塑性樹脂を使用することができる。The matrix resin is not particularly limited, and resins used in conventional golf club shafts made of fiber-reinforced plastics, for example, epoxy resins, unsaturated polyester resins, vinyl ester resins, polyimide resins, polybismaleimide resins And the like, and other thermoplastic resins.
【００１８】本発明の繊維強化プラスチック製ゴルフク
ラブシャフトは、上記のように強化繊維がゴルフクラブ
シャフトの長手方向に対して±（３０〜７０°）に配向
したアングル層と、強化繊維がシャフトの長手方向に対
して−２０〜２０°に配向したストレート層とを具備
し、しかも該ゴルフクラブシャフトをその細径端部側か
ら太径端部側に向かって順次、全長の１５〜４０％の範
囲をなす長さの細径部（ＡＬ）と、同じく全長の３０〜
６０％の範囲をなす長さの中央部（ＢＬ）と、同じく全
長の２５〜４０％の範囲をなす長さの太径部（ＣＬ）と
の３つのブロックにしたときに、曲げ剛性値がこれらの
３つのブロック内においてそれぞれ１個の極大値を有し
ているものであればよく、その製造方法に制限を受ける
ものではない。The golf club shaft made of fiber-reinforced plastic according to the present invention comprises, as described above, an angle layer in which the reinforcing fibers are oriented at ± (30 to 70 °) with respect to the longitudinal direction of the golf club shaft; A straight layer oriented at −20 ° to 20 ° with respect to the longitudinal direction, and the golf club shaft is successively 15 to 40% of the total length from the small-diameter end to the large-diameter end. The narrow diameter part (AL) of the length that makes up the range
The bending stiffness value of the three blocks of a central part (BL) having a length of 60% and a large diameter part (CL) having a length of 25 to 40% of the total length is also obtained. What is necessary is just to have one maximum value in each of these three blocks, and there is no limitation on the manufacturing method.
【００１９】しかしながら樹脂含有率を抑えることによ
ってゴルフクラブシャフトの軽量化を図るためには、繊
維を引き揃えてなるシート状の強化繊維にマトリックス
樹脂を含浸させたプリプレグをマンドレルに数回巻き付
けた後、これを加熱、成形するシートラッピング法を使
用するのが好適である。However, in order to reduce the weight of the golf club shaft by suppressing the resin content, a prepreg obtained by impregnating a matrix resin into a sheet-like reinforcing fiber obtained by aligning fibers is wound several times around a mandrel. It is preferable to use a sheet wrapping method for heating and forming the sheet.
【００２０】このシートラッピング法で使用するプリプ
レグの厚み、繊維目付、樹脂含有率等は特に限定される
ものではなく、各層に必要な厚みや巻き径等に基づいて
適宜選択すればよい。The thickness, fiber weight, resin content and the like of the prepreg used in the sheet wrapping method are not particularly limited, and may be appropriately selected based on the thickness and winding diameter required for each layer.
【００２１】上記の特性を具備する本発明の繊維強化プ
ラスチック製ゴルフクラブシャフトは、該ゴルフクラブ
シャフトの全長に亙って、厚さ方向においてその内側か
ら外側に向かって積層されているアングル層とストレー
ト層とを主体構造とし、これに更に細径部、中央部、及
び太径部のそれぞれの曲げ剛性を調整するための繊維強
化プラスチック層からなる補強層を、所定の領域に積層
させることによって得られる。The golf club shaft made of fiber-reinforced plastic of the present invention having the above characteristics has an angle layer laminated from the inside to the outside in the thickness direction over the entire length of the golf club shaft. A straight layer and a main structure, and a reinforcing layer made of a fiber reinforced plastic layer for adjusting the bending rigidity of each of the small diameter portion, the central portion, and the large diameter portion is further laminated on a predetermined region. can get.
【００２２】上記の補強層を形成するためのプリプレグ
として、強化繊維の配向角がゴルフクラブシャフトの長
手方向に対して−４５〜＋４５°、より好ましくは−２
０〜＋２０゜であり、かつ厚さが０．０２〜０．１５ｍ
ｍものを使用することにより、本発明のゴルフクラブシ
ャフトに必要な曲げ剛性に係る特性値のバランスを具備
させ易くなる。As a prepreg for forming the above-mentioned reinforcing layer, the orientation angle of the reinforcing fibers is -45 to + 45 °, more preferably -2 with respect to the longitudinal direction of the golf club shaft.
0 to + 20 ° and thickness of 0.02 to 0.15 m
By using m, the golf club shaft of the present invention can be easily provided with a balance of characteristic values related to bending rigidity.
【００２３】本発明の繊維強化プラスチック製ゴルフク
ラブシャフトにあっては、上記の細径部、中央部、及び
太径部のそれぞれの曲げ剛性を調整するための繊維強化
プラスチック層からなる補強層の外にも、必要に応じて
先端部の補強のためや径合わせ等のために、他の繊維強
化プラスチック層を積層してもよいことは勿論である。In the fiber reinforced plastic golf club shaft of the present invention, the reinforcing layer comprising a fiber reinforced plastic layer for adjusting the bending rigidity of each of the small diameter portion, the central portion, and the large diameter portion. Needless to say, another fiber reinforced plastic layer may be laminated as needed for reinforcing the tip portion or adjusting the diameter.
【００２４】本発明の繊維強化プラスチック製ゴルフク
ラブシャフトにおいては、アングル層の厚さは特に規定
されるものではなく、従来の繊維強化プラスチック製ゴ
ルフクラブシャフトにおけるアングル層の厚さと同様で
よいが、成形の際の芯金を抜き取る工程での縦割れの発
生を防ぐために、該アングル層は０．１０〜０．２５ｍ
ｍの厚さを有していることが好ましい。In the fiber reinforced plastic golf club shaft of the present invention, the thickness of the angle layer is not particularly limited, and may be the same as that of the conventional fiber reinforced plastic golf club shaft. In order to prevent the occurrence of vertical cracks in the step of removing the core metal during molding, the angle layer is 0.10 to 0.25 m.
Preferably, it has a thickness of m.
【００２５】上記のアングル層は、上記の通りゴルフク
ラブシャフトの全長に亙って形成されているが、全体が
均一の厚みである必要はなく、本発明のゴルフクラブシ
ャフトに必要な曲げ剛性に係る特性値、重量、その他の
強力等を犠牲にしない範囲内で、他の特性の向上を目的
として自由に設計することが可能である。Although the angle layer is formed over the entire length of the golf club shaft as described above, the angle layer does not need to have a uniform thickness as a whole, and has the required bending rigidity for the golf club shaft of the present invention. It is possible to design freely for the purpose of improving other characteristics within a range not sacrificing such characteristic values, weight, and other strengths.
【００２６】ゴルフクラブシャフトの全長に亙って形成
されるストレート層は、該ゴルフクラブシャフトに適度
な曲げ剛性、及び曲げ強力を付与する点から、厚さの合
計が０．２〜０．４ｍｍであることが好ましい。The straight layer formed over the entire length of the golf club shaft has a total thickness of 0.2 to 0.4 mm from the viewpoint of imparting appropriate bending rigidity and bending strength to the golf club shaft. It is preferred that
【００２７】ゴルフクラブシャフトをその細径端部側か
ら太径端部側に向かって順次、全長の１５〜４０％の範
囲をなす長さの細径部（ＡＬ）と、同じく全長の３０〜
６０％の範囲をなす長さの中央部（ＢＬ）と、同じく全
長の２５〜４０％の範囲をなす長さの太径部（ＣＬ）と
の３つのブロックにしたときに、細径部（ＡＬ）におけ
る曲げ剛性値の極大値（Ａｍａｘ）が１２Ｎ・ｍ2 未満
になると、該細径部（ＡＬ）の曲げ剛性の不足により、
シャフト細径部（ＡＬ）の強度が低下する。又該細径部
（ＡＬ）における曲げ剛性値の極大値（Ａｍａｘ）が２
８Ｎ・ｍ2 を超えるようになると、細径部（ＡＬ）の曲
げ剛性値が高くなり過ぎてしまい、打撃時にシャフト細
径部（ＡＬ）のしなりが不足するようになるために、打
感が鈍くなると共に、弾道が低くなる傾向が出る。The golf club shaft has a small-diameter portion (AL) having a length in the range of 15 to 40% of the entire length, sequentially from the small-diameter end to the large-diameter end, and 30 to 30% of the total length.
When formed into three blocks, a central portion (BL) having a length of 60% and a large-diameter portion (CL) having a length of 25 to 40% of the entire length, a small-diameter portion (BL) is formed. When the maximum value (Amax) of the bending rigidity value in (AL) is less than 12 N · m 2 , the bending rigidity of the small diameter portion (AL) is insufficient.
The strength of the small diameter portion (AL) of the shaft decreases. Further, the maximum value (Amax) of the bending rigidity value in the small diameter portion (AL) is 2
If it exceeds 8 N · m 2 , the bending rigidity value of the small diameter portion (AL) becomes too high, and the bending of the shaft small diameter portion (AL) becomes insufficient at the time of impact. And the trajectory tends to decrease.
【００２８】これによって、上記の細径部（ＡＬ）にお
ける曲げ剛性値の極大値（Ａｍａｘ）は、１２〜２８Ｎ
・ｍ2 であることが好ましく、又、細径部（ＡＬ）にお
ける曲げ剛性値のこの極大値（Ａｍａｘ）とバランスし
て、中央部（ＢＬ）における曲げ剛性値の極大値（Ｂｍ
ａｘ）は２５〜５０Ｎ・ｍ2 であることが好ましく、
又、太径部（ＣＬ）における曲げ剛性値の極大値（Ｃｍ
ａｘ）は３５〜７０Ｎ・ｍ2 であることが好ましい。Thus, the maximum value (Amax) of the bending stiffness value in the small diameter portion (AL) is 12 to 28 N
M 2 , and the maximum value (Bm) of the bending stiffness value at the central portion (BL) is balanced with the maximum value (Amax) of the bending stiffness value at the small diameter portion (AL).
ax) is preferably 25 to 50 N · m 2 ,
In addition, the maximum value (Cm) of the bending rigidity value in the large diameter portion (CL)
ax) is preferably 35 to 70 N · m 2 .
【００２９】更に、上記の本発明の繊維強化プラスチッ
ク製ゴルフクラブシャフトは、スイングスピードを上げ
て飛距離を伸ばすための軽量化に対応し得るように、重
量が４０〜７０ｇであることが好ましく、又、折損に耐
え得る強度と適度なしなりとが得られるように、細径端
部の外径が７〜１０ｍｍであることが望ましい。Further, the fiber reinforced plastic golf club shaft of the present invention preferably has a weight of 40 to 70 g so as to cope with a reduction in weight for increasing a swing speed and extending a flight distance. Further, it is desirable that the outer diameter of the small-diameter end portion is 7 to 10 mm so that strength enough to withstand breakage and moderate bending can be obtained.
【００３０】[0030]
【実施例】以下、本発明の繊維強化プラスチック製ゴル
フクラブシャフトの具体的な構成を実施例に基づいてよ
り詳しく説明し、併せて該実施例品のゴルフクラブシャ
フトの諸物性を、比較例品のゴルフクラブシャフトの諸
物性と比較して説明する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The specific structure of the fiber reinforced plastic golf club shaft of the present invention will be described in more detail below with reference to examples, and various physical properties of the golf club shaft of the example product will be compared with those of a comparative example product. This will be described in comparison with various physical properties of the golf club shaft.
【００３１】なお、実施例及び比較例で使用したプリプ
レグ、すなわち炭素繊維を一方向に引き揃えてなる炭素
繊維シートに樹脂を含浸させたプリプレグの種類とその
厚さは、下記の表１〜表２に示す通りである。The types and thicknesses of the prepregs used in the examples and comparative examples, that is, the prepregs obtained by impregnating a resin into a carbon fiber sheet formed by aligning carbon fibers in one direction are shown in Tables 1 to 3 below. As shown in FIG.
【００３２】[0032]
【表１】 [Table 1]
【００３３】[0033]
【表２】 [Table 2]
【００３４】実施例１ 表１〜表２の所定欄に示す三菱レイヨン株式会社製の市
販のプリプレグＡ〜Ｅをそれぞれ裁断し、細径端部外径
５．７４ｍｍ、太径端部外径１３．６５ｍｍ、長さ１１
６５ｍｍを有しており、かつ太径端部〜該太径端部から
３００ｍｍの部分迄が外径１３．６５ｍｍの平行部をな
しており、太径端部から３００ｍｍの位置〜細径端部に
至る８６５ｍｍに亙る長さ部分がテーパー度９．１４／
１０００のテーパー部をなしている芯金の上に、下記の
（１）〜（３）に説明する手順により、強化繊維の配向
角が９０°の補強層用の巻き付け層、アングル層用の巻
き付け層、及びストレート層用の巻き付け層を形成し
た。Example 1 Commercially available prepregs A to E manufactured by Mitsubishi Rayon Co., Ltd. shown in predetermined columns of Tables 1 and 2 were cut, and the small-diameter end outer diameter 5.74 mm and the large-diameter end outer diameter 13 were cut. .65 mm, length 11
65 mm, and a portion from the large diameter end to the portion 300 mm from the large diameter end forms a parallel portion having an outer diameter of 13.65 mm, and a position 300 mm from the large diameter end to a small diameter end. The length of 865 mm leading to is 9.14 / taper.
A winding layer for a reinforcing layer and a winding for an angle layer in which the orientation angle of the reinforcing fiber is 90 ° are formed on the core metal having a tapered portion of 1000 by the procedure described in the following (1) to (3). A layer and a winding layer for a straight layer were formed.
【００３５】（１）プリプレグ（Ａ）を、繊維方向が芯
金の径方向中心線に対して９０°となるようにして芯金
に巻き付けたときに、細径端部〜太径端部の全長に亙っ
て１層となって巻き付かるような略台形に裁断し、これ
を芯金に巻き付け、強化繊維の配向角が９０°の補強層
用の巻き付けを行なった。(1) When the prepreg (A) is wound around the core metal so that the fiber direction is at 90 ° to the center line in the radial direction of the core metal, the prepreg (A) has a small diameter end to a large diameter end. It was cut into a substantially trapezoidal shape that could be wound as a single layer over the entire length, wound around a cored bar, and wound for a reinforcing layer having a reinforcing fiber orientation angle of 90 °.
【００３６】（２）プリプレグ（Ｂ）を、繊維方向が芯
金の径方向中心線に対して＋４５°となるようにして、
（１）にて形成した補強層用の巻き付け層の上に巻き付
けたときに、細径端部において３層、その後はなだらか
に減少して太径端部において２層になって巻き付かるよ
うな略台形に裁断し、又同じくプリプレグ（Ｂ）を、繊
維方向が芯金の径方向中心線に対して−４５°となるよ
うに巻き付けたときに、細径端部において３層、その後
はなだらかに減少して太径端部において２層になって巻
き付かるような略台形に裁断し、これらの２枚のプリプ
レグを繊維方向が互いに直交するように貼り合わせた
後、この貼り合わせプリプレグを、（１）にて形成した
補強層用の巻き付け層の上に巻き付け、アングル層用の
巻き付けを行なった。(2) The prepreg (B) is oriented such that the fiber direction is + 45 ° with respect to the radial center line of the cored bar.
When wound on the reinforcing layer winding layer formed in (1), three layers are formed at the small-diameter end, and then gradually reduced to two layers at the large-diameter end. When the prepreg (B) is wound in such a manner that the fiber direction is -45 ° with respect to the radial center line of the core metal, three layers are formed at the narrow end, and thereafter, The tape is cut into a substantially trapezoidal shape that gradually decreases and is wound in two layers at the large-diameter end, and the two prepregs are bonded so that the fiber directions are orthogonal to each other. Was wound on the winding layer for the reinforcing layer formed in (1), and was wound for the angle layer.
【００３７】（３）プリプレグ（Ｃ）を、繊維方向が芯
金の径方向中心線に対して０°となるようにして、
（２）にて形成したアングル層用の巻き付け層の上に巻
き付けたときに、細径端部から太径端部に亙る全長にて
３層となって巻き付かるような形状に裁断し、（２）に
て形成したアングル層用の巻き付け層の上に巻き付け、
ストレート層用の巻き付けを行なった。(3) The prepreg (C) is oriented such that the fiber direction is at 0 ° to the radial centerline of the cored bar.
When wound on the winding layer for the angle layer formed in (2), it is cut into a shape such that it is wound in three layers over the entire length from the small-diameter end to the large-diameter end, Winding on the angle layer winding layer formed in (2),
Winding for a straight layer was performed.
【００３８】続いて、同じく下記の（４）〜（７）に説
明する手順によって、それぞれ所定の領域に、細径部補
強層、中央部補強層、太径部補強層、及び細径端部径調
整層用の巻き付け層を形成した。Subsequently, the small-diameter portion reinforcing layer, the central-portion reinforcing layer, the large-diameter portion reinforcing layer, and the small-diameter end portion are respectively provided in predetermined regions by the procedures described in the following (4) to (7). A winding layer for a diameter adjusting layer was formed.
【００３９】（４）プリプレグ（Ｄ）を、繊維方向が芯
金の径方向中心線に対して０°となるようにして、
（３）にて形成したストレート層用の巻き付け層の上
に、細径端部において２層、その後は徐々に巻き付けが
増えて細径端部から１７０ｍｍの位置にて３層に巻き付
かり、その後は徐々に巻き付けが減少して細径端部から
３００ｍｍの位置にて巻き付けが無くなる形状に裁断
し、（３）にて形成したストレート層用の巻き付け層の
上に巻き付け、細径部補強層用の巻き付けを行なった。(4) The prepreg (D) is oriented such that the fiber direction is at 0 ° to the radial center line of the cored bar.
On the winding layer for the straight layer formed in (3), two layers are formed at the small-diameter end, and thereafter, the number of windings is gradually increased, and three layers are wound at a position 170 mm from the small-diameter end, Thereafter, the winding is gradually reduced and cut into a shape where the winding is eliminated at a position 300 mm from the small-diameter end portion, and is wound on the winding layer for the straight layer formed in (3) to form the small-diameter portion reinforcing layer. Was wound.
【００４０】（５）プリプレグ（Ｅ）を、繊維方向が芯
金の径方向中心線に対して０°となるようにして、
（３）にて形成したストレート層用の巻き付け層の上
に、細径端部〜該細径端部から３００ｍｍ迄の長さ範囲
においては巻き付けが無く、細径端部から３００ｍｍの
位置から巻き付けが徐々に始まり、細径端部から６５０
ｍｍの位置で３層、その後は巻き付けが徐々に無くなっ
て細径端部から８００ｍｍの位置で巻き付けががなくな
るような三角形状に裁断し、（３）にて形成したストレ
ート層用の巻き付け層の上に巻き付け、中央部補強層用
の巻き付けを行なった。(5) The prepreg (E) is oriented such that the fiber direction is at 0 ° to the radial center line of the cored bar.
On the winding layer for the straight layer formed in (3), there is no winding in the length range from the small-diameter end to 300 mm from the small-diameter end, and winding is performed from a position 300 mm from the small-diameter end. Gradually starts, and 650 from the narrow end
3 mm, and then cut into a triangular shape such that winding is gradually eliminated and winding is stopped at a position 800 mm from the small-diameter end, and the winding layer for a straight layer formed in (3) is cut. The upper part was wound, and the center part of the reinforcing layer was wound.
【００４１】（６）プリプレグ（Ｄ）を、繊維方向が芯
金の径方向中心線に対して０°となるようにして、
（３）にて形成したストレート層用の巻き付け層の上
に、太径端部にて１層、その後は巻き付けが徐々に増加
して太径端部から２００ｍｍの位置にて２層に巻き付か
り、続いて巻き付けが徐々に減少して太径端部から３０
０ｍｍの位置で巻き付けが無くなる形状に裁断し、
（３）にて形成したストレート層用の巻き付け層の上に
巻き付け、太径部補強層用の巻き付けを行なった。(6) The prepreg (D) is set so that the fiber direction is at 0 ° to the radial center line of the cored bar.
On the winding layer for the straight layer formed in (3), one layer is formed at the large-diameter end, and thereafter the winding is gradually increased to form two layers at a position 200 mm from the large-diameter end. Then, the winding gradually decreases from the end of the large diameter to 30
Cut to a shape where winding is lost at the position of 0 mm,
Winding was performed on the winding layer for the straight layer formed in (3), and winding for the large diameter portion reinforcing layer was performed.
【００４２】（７）プリプレグ（Ｃ）を、繊維方向が直
角を挟む２辺のうちの１辺と同方向であって、かつ該直
角を挟む辺の長さが１００ｍｍ×１００ｍｍの直角３角
形に裁断し、これを繊維方向が芯金の径方向中心線に対
して０°となるようにして、細径端部において最も多重
に巻き付け、その後は徐々に巻き付けが無くなるように
して、（４）にて形成した細径部補強層用の巻き付け層
の上に巻き付け、細径端部径調整層用の巻き付けを行な
った。(7) The prepreg (C) is formed into a right-angled triangle having a fiber direction in the same direction as one of the two sides sandwiching the right angle and having a length of 100 mm × 100 mm across the right angle. (4) The fiber was cut so that the direction of the fiber was 0 ° with respect to the center line in the radial direction of the core metal, and the winding was wrapped most multiplely at the small diameter end, and thereafter the winding was gradually eliminated. Was wound on the winding layer for the small-diameter portion reinforcing layer formed in the above, and was wound for the small-diameter end portion diameter adjusting layer.
【００４３】続いてその最外層に、幅２０ｍｍ、厚さ３
０μｍのポリプロピレンテープを２ｍｍピッチで巻き付
けた後、１４５℃の硬化炉で２４０分間の加熱硬化を行
ない、更に芯金の除去、ラッピングテープの除去、外周
面の研磨を順次行なった後、細径端部及び太径端部のそ
れぞれから１０ｍｍをトリミングカットし、重量５０
ｇ、長さ１１４５ｍｍ、細径端部の外径８．５ｍｍ、太
径端部の外径１５．２ｍｍのゴルフクラブシャフトを得
た。Subsequently, the outermost layer has a width of 20 mm and a thickness of 3 mm.
After winding a 0 μm polypropylene tape at a pitch of 2 mm, heat-curing is performed in a curing oven at 145 ° C. for 240 minutes, and the core metal is removed, the wrapping tape is removed, and the outer peripheral surface is polished sequentially. 10mm is trimmed from each part and the large diameter end, and the weight is 50mm.
g, a golf club shaft having a length of 1145 mm, an outer diameter of 8.5 mm at the small diameter end, and an outer diameter of 15.2 mm at the large diameter end.
【００４４】上記のゴルフクラブシャフトは、シャフト
全体の曲げ剛性が１８０ｍｍであり、ねじり剛性が４．
７ｄｅｇであり、その曲げ剛性分布は図１に示す通りで
ある。The golf club shaft described above has a flexural rigidity of the entire shaft of 180 mm and a torsional rigidity of 4.
7 deg, and the bending stiffness distribution is as shown in FIG.
【００４５】なお、ゴルフクラブシャフトのシャフト全
体の曲げ剛性（ｍｍ）、ねじり剛性（ｄｅｇ）、及び曲
げ剛性分布は、それぞれ下記の通りにして測定した。 （１） シャフト全体の曲げ剛性（ｍｍ） シャフトの太径部を固定し、シャフトの細径端部から１
０ｍｍの位置に３ｋｇの荷重を掛け、そのときのたわみ
量（ｍｍ）を測定し、これをシャフト全体の曲げ剛性と
した。The flexural rigidity (mm), torsional rigidity (deg), and flexural rigidity distribution of the entire golf club shaft were measured as follows. (1) Flexural rigidity of the entire shaft (mm) Fix the large diameter part of the shaft, and
A load of 3 kg was applied to the position of 0 mm, the amount of deflection (mm) at that time was measured, and this was defined as the bending rigidity of the entire shaft.
【００４６】（２） ねじり剛性（ｄｅｇ） シャフトの太径部を固定し、シャフトの細径端部から５
０ｍｍの位置にアームを取り付け、更にこのアームのシ
ャフト軸中央から３００ｍｍの位置に４５４ｇの錘を釣
り下げ、そのときのアームの変化量を角度（ｄｅｇ）で
表示し、これをねじり剛性とした。(2) Torsional rigidity (deg) The large diameter portion of the shaft is fixed, and 5 mm from the small diameter end of the shaft.
An arm was attached at a position of 0 mm, and a weight of 454 g was further suspended at a position of 300 mm from the center of the shaft axis of the arm. The amount of change of the arm at that time was indicated by an angle (deg), which was defined as torsional rigidity.
【００４７】（３） 曲げ剛性分布 下記の通りの三点曲げ試験を、シャフトの細径端部から
太径端部に亙って５０ｍｍピッチで行なったときの各点
での曲げ剛性値を、シャフトの細径端部からの距離に対
してプロットし、これを曲げ剛性分布とした。上記の三
点曲げ試験は、Ｌ＝０．２（ｍ）、Ｐ＝２００（Ｎ）で
行ない、シャフトの細径端部から２０ｍｍの位置に片方
の支持具を配置する状態、つまりシャフトの細径端部か
ら１２０ｍｍの位置での試験から始めた。 三点曲げ試験 シャフトを、Ｌ（ｍ）離して設置した２つの支持具（１
２．５ｍｍＲ）の上に配置し、該支持具間の中央部上方
から圧子（１５．５ｍｍＲ）によりＰ（Ｎ）の荷重を加
えたときのシャフトの歪み量σ（ｍ）を測定し、曲げ剛
性値を下記の計算式により算出した。 曲げ剛性値＝（Ｌ3 ／４８）・（Ｐ／σ）［Ｎ・ｍ2 ］ Ｌ・・・・支持具間の距離（ｍ） Ｐ・・・・シャフトに加えた荷重（Ｎ） σ・・・・荷重を加えたときのシャフトの歪み量（ｍ）(3) Bending rigidity distribution The bending rigidity value at each point when the following three-point bending test was performed at a pitch of 50 mm from the small diameter end to the large diameter end of the shaft, The plot was plotted against the distance from the small-diameter end of the shaft, and this was used as the bending rigidity distribution. The above three-point bending test is performed at L = 0.2 (m) and P = 200 (N), and one support is arranged at a position 20 mm from the small-diameter end of the shaft, that is, the fineness of the shaft is reduced. The test was started at a position 120 mm from the diameter end. Three-point bending test Two supports (1) with the shaft installed L (m) apart
2.5 mmR), and measure the amount of strain σ (m) of the shaft when a load of P (N) is applied from above the central part between the supports by an indenter (15.5 mmR). The rigidity value was calculated by the following formula. Flexural rigidity = (L 3/48) · (P / σ) [N · m 2] L ···· distance between support (m) applied load to P · · · · shaft (N) σ · ... Shaft distortion when a load is applied (m)
【００４８】比較例１ 実施例１の（１）〜（３）工程と同様にして、強化繊維
の配向角が９０°の補強層用の巻き付け層、アングル層
用の巻き付け層、及びストレート層用の巻き付け層を形
成した。Comparative Example 1 In the same manner as in the steps (1) to (3) of Example 1, the winding layer for the reinforcing layer, the winding layer for the angle layer, and the straight layer Was formed.
【００４９】（４）続いてプリプレグＣを、繊維方向が
芯金の径方向中心線に対して０°となるようにして、
（３）にて形成したストレート層用の巻き付け層の上
に、細径端部〜該細径端部から１７０ｍｍの位置迄が１
層、その後は徐々に巻き付けが減少して細径端部から３
００ｍｍの位置にて巻き付けが無くなる形状に裁断し、
（３）にて形成したストレート層用の巻き付け層の上に
巻き付け、細径部補強層用の巻き付けを行なった。(4) Subsequently, the prepreg C is set so that the fiber direction is at 0 ° to the radial center line of the cored bar.
On the winding layer for the straight layer formed in (3), 1 mm from the small diameter end to a position 170 mm from the small diameter end.
Layer, then the wrapping gradually decreases from the narrow end to 3
Cut to a shape where winding is lost at the position of 00 mm,
Winding was performed on the winding layer for the straight layer formed in (3), and winding for the small diameter portion reinforcing layer was performed.
【００５０】（５）プリプレグ（Ｅ）によって、実施例
１の（５）工程と同様にして中央部補強層用の巻き付け
を行なった。(5) The prepreg (E) was used to wind the central reinforcing layer in the same manner as in the step (5) of Example 1.
【００５１】（６）プリプレグＤを、繊維方向がが芯金
の径方向中心線に対して０°となるようにして、（３）
にて形成したストレート層用の巻き付け層の上に、太径
端部〜該太径端部から２００ｍｍ迄に亙って１層、その
後はなだらかに巻き付けが減少してゆき、太径端部から
３００ｍｍの位置で巻き付けが無くなる形状に裁断し、
（３）にて形成したストレート層用の巻き付け層の上に
巻き付け、太径部補強層用の巻き付けを行なった。(6) The prepreg D is set so that the fiber direction is at 0 ° with respect to the radial centerline of the cored bar.
On the winding layer for the straight layer formed by the above, one layer from the large-diameter end to the 200 mm from the large-diameter end, and thereafter, the winding gradually decreases, and from the large-diameter end, Cut into a shape where winding is lost at the position of 300 mm,
Winding was performed on the winding layer for the straight layer formed in (3), and winding for the large diameter portion reinforcing layer was performed.
【００５２】（７）実施例１の（７）と同じ工程によっ
て、細径端部径調整層用の巻き付けを行なった。(7) Winding for the small diameter end portion diameter adjusting layer was performed by the same process as (7) in Example 1.
【００５３】続いてその最外層に、幅２０ｍｍ、厚さ３
０μｍのポリプロピレンテープを２ｍｍピッチで巻き付
けた後、１４５℃の硬化炉で２４０分間の加熱硬化を行
ない、更に芯金の除去、ラッピングテープの除去、外周
面の研磨を順次行ない、続いて細径端部及び太径端部の
それぞれから１０ｍｍをトリミングカットし、重量４９
ｇ、長さ１１４５ｍｍ、細径端部の外径８．５ｍｍ、太
径端部の外径１５．２ｍｍのゴルフクラブシャフトを得
た。Subsequently, the outermost layer has a width of 20 mm and a thickness of 3 mm.
After winding a 0 μm polypropylene tape at a pitch of 2 mm, it is heated and cured in a curing oven at 145 ° C. for 240 minutes, and further, the core metal is removed, the wrapping tape is removed, and the outer peripheral surface is sequentially polished. 10mm was trimmed from each of the end and the large diameter end.
g, a golf club shaft having a length of 1145 mm, an outer diameter of 8.5 mm at the small diameter end, and an outer diameter of 15.2 mm at the large diameter end.
【００５４】上記のゴルフクラブシャフトは、シャフト
全体の曲げ剛性が１８０ｍｍであり、ねじり剛性が４．
７ｄｅｇである。又その曲げ剛性分布は図１に示す通り
であり、細径部（ＡＬ）の領域での曲げ剛性値ではその
極大値の存在が不明確であり、又太径部（ＣＬ）の領域
の曲げ剛性値には、極大値が存在していない。The golf club shaft described above has a flexural rigidity of the entire shaft of 180 mm and a torsional rigidity of 4.
7 deg. The distribution of bending stiffness is as shown in FIG. 1. The presence of the maximum value is not clear in the bending stiffness value in the area of the small diameter part (AL). There is no maximum value for the stiffness value.
【００５５】［実験］上記の各ゴルフクラブシャフトに
グリップとヘッドとを装着し、# １ウッドのゴルフクラ
ブを作製した。続いて初級、中級、及び上級の各ゴルフ
ァー１０ずつによって上記のゴルフクラブの試打を行な
ったところ、クラブ振動数の好みはそれぞれ相違するも
のの、実施例品によるゴルフクラブによる方がより力強
いスイングを行なうことができ、これによって高弾道の
飛距離の延びた打球が得られた。[Experiment] A grip and a head were attached to each of the above golf club shafts to produce a # 1 wood golf club. Subsequently, the above golf clubs were hit by each of the beginner, intermediate, and advanced golfers 10, and although the club frequencies were different in preference, the golf club according to the example product performed a stronger swing. As a result, a hit ball with a high trajectory and a long flight distance was obtained.
【００５６】[0056]
【発明の効果】本発明の繊維強化プラスチック製ゴルフ
クラブシャフトは、該ゴルフクラブシャフトをその細径
端部側から太径端部側に向かって順次、全長の１５〜４
０％の範囲をなす長さの細径部（ＡＬ）と、同じく全長
の３０〜６０％の範囲をなす長さの中央部（ＢＬ）と、
同じく全長の２５〜４０％の範囲をなす長さの太径部
（ＣＬ）との３つのブロックにしたときに、曲げ剛性値
がこれらの３つのブロック内においてそれぞれ１個の極
大値を有しているものである。According to the golf club shaft made of fiber-reinforced plastic of the present invention, the total length of the golf club shaft is 15 to 4 in the order from the small-diameter end to the large-diameter end.
A small diameter portion (AL) having a length of 0%, a central portion (BL) having a length of 30-60% of the total length,
Similarly, when three blocks with a large-diameter portion (CL) having a length in the range of 25 to 40% of the total length are formed, the bending stiffness value has one maximum value in each of these three blocks. Is what it is.
【００５７】これによって、本発明の繊維強化プラスチ
ック製ゴルフクラブシャフトを使用してなるゴルフクラ
ブは、該ゴルフクラブシャフトの調子（キックポイン
ト）が明確になり、“鞭”のような振り抜き易さを有
し、しかも打撃時の球の吹き上がりを抑えることがで
き、且つ俗に言われる“手元部がしっかり”したゴルフ
クラブになる。As a result, the golf club using the fiber reinforced plastic golf club shaft of the present invention has a clear condition (kick point) of the golf club shaft, and is easy to swing like a "whip". A golf club having the ball, which can suppress the blow-up of the ball at the time of hitting, and which is commonly referred to as having "a firm hand".
【００５８】従って、本発明の繊維強化プラスチック製
ゴルフクラブシャフトを使用してなるゴルフクラブにお
いては、初級ゴルファーから上級ゴルファーに至る迄、
“鞭”のような振り抜き易さと安定した力強いスイング
を行なうことが可能になり、飛距離の延びが得られる。Accordingly, in a golf club using the fiber-reinforced plastic golf club shaft of the present invention, from a beginner golfer to a senior golfer,
This makes it easy to swing out like a "whip" and makes it possible to perform a stable and powerful swing, thereby extending the flight distance.
【図１】実施例で作成したゴルフクラブ用シャフトの曲
げ剛性分布（細径端部からの距離に対してその位置での
曲げ剛性）をプロットしたグラフである。FIG. 1 is a graph plotting a bending rigidity distribution (bending rigidity at a position with respect to a distance from a small diameter end) of a golf club shaft prepared in an example.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 滝口 郁朗 愛知県豊橋市牛川通四丁目１番地の２ 三 菱レイヨン株式会社豊橋事業所内 Ｆターム(参考） 2C002 AA05 MM02 4F100 AD11 AK53 BA02 BA03 BA04 BA05 BA06 BA07 BA08 BA10A BA10B BA13 BA22 DA16 DG04 DH01A DH01B EJ82 GB87 JK01 JK04 JL05 YY00 ────────────────────────────────────────────────── ─── Continued on the front page (72) Inventor Ikuro Takiguchi 4-1-1 Ushikawa-dori, Toyohashi-shi, Aichi F-term (reference) 2C002 AA05 MM02 4F100 AD11 AK53 BA02 BA03 BA04 BA05 BA06 BA07 BA08 BA10A BA10B BA13 BA22 DA16 DG04 DH01A DH01B EJ82 GB87 JK01 JK04 JL05 YY00
Claims (3)
の２層以上の繊維強化プラスチック層を積層させてなる
ゴルフクラブシャフトであって、該ゴルフクラブシャフ
トをその細径端部側から太径端部側に向かって順次、全
長の１５〜４０％の範囲をなす長さの細径部（ＡＬ）
と、同じく全長の３０〜６０％の範囲をなす長さの中央
部（ＢＬ）と、同じく全長の２５〜４０％の範囲をなす
長さの太径部（ＣＬ）との３つのブロックにしたとき
に、曲げ剛性値がこれらの３つのブロック内においてそ
れぞれ１個の極大値を有していることを特徴とする繊維
強化プラスチック製ゴルフクラブシャフト。1. A golf club shaft comprising at least two fiber-reinforced plastic layers, an angle layer and a straight layer, laminated on each other, wherein the golf club shaft is moved from a small-diameter end to a large-diameter end. The narrow diameter part (AL) of which length is in the range of 15 to 40% of the total length in order
And a central portion (BL) having a length of 30 to 60% of the entire length and a large diameter portion (CL) having a length of 25 to 40% of the entire length. A golf club shaft made of a fiber-reinforced plastic, wherein the flexural rigidity sometimes has one maximum value in each of these three blocks.
大値（Ａｍａｘ）が１２〜２８Ｎ・ｍ2 であり、中央部
（ＢＬ）における曲げ剛性値の極大値（Ｂｍａｘ）が２
５〜５０Ｎ・ｍ2 であり、太径部（ＣＬ）における曲げ
剛性値の極大値（Ｃｍａｘ）が３５〜７０Ｎ・ｍ2 であ
ることを特徴とする請求項１に記載の繊維強化プラスチ
ック製ゴルフクラブシャフト。2. The maximum value (Amax) of the bending rigidity value in the small diameter portion (AL) is 12 to 28 N · m 2 , and the maximum value (Bmax) of the bending rigidity value in the central portion (BL) is 2
A 5~50N · m 2, fiber reinforced plastic golf according to claim 1, the maximum value of flexural rigidity in the large diameter portion (CL) (Cmax) is characterized in that it is a 35~70N · m 2 Club shaft.
０〜１２７０ｍｍであり、細径端部の外径が７〜１０ｍ
ｍであり、太径端部の外径が１４〜３０ｍｍである請求
項１又は請求項２に記載の繊維強化プラスチック製ゴル
フクラブシャフト。3. The weight is 40 to 70 g and the total length is 85.
0 to 1270 mm, and the outer diameter of the small diameter end is 7 to 10 m
3. The golf club shaft made of a fiber-reinforced plastic according to claim 1, wherein the outer diameter of the large-diameter end portion is 14 to 30 mm. 4.