GB995565A - Improvements in or relating to nozzles and other refractories for use in teeming andcasting steel - Google Patents
Improvements in or relating to nozzles and other refractories for use in teeming andcasting steelInfo
- Publication number
- GB995565A GB995565A GB3345962A GB3345962A GB995565A GB 995565 A GB995565 A GB 995565A GB 3345962 A GB3345962 A GB 3345962A GB 3345962 A GB3345962 A GB 3345962A GB 995565 A GB995565 A GB 995565A
- Authority
- GB
- United Kingdom
- Prior art keywords
- andcasting
- teeming
- refractories
- nozzles
- relating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
Shaped refractory articles are formed from a composition containing 2-30% by weight of carbon, e.g. graphite, the balance being selected from 1, a mixture of fireclay and calcined fireclay, e.g. grog or chamotte or 2, a graded mixture of alumino-silicates or fused or calcined alumina with or without plastic clay or 3, a graded mixture of magnesia with or without spinels or spinel forming oxides, e.g. alumina, chromia, magnesium aluminate spinel containing chromium sesqui-oxide and iron oxide and chrome ore. The formed bodies are fired in an inert or reducing atmosphere.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3345962A GB995565A (en) | 1962-08-31 | 1962-08-31 | Improvements in or relating to nozzles and other refractories for use in teeming andcasting steel |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3345962A GB995565A (en) | 1962-08-31 | 1962-08-31 | Improvements in or relating to nozzles and other refractories for use in teeming andcasting steel |
Publications (1)
Publication Number | Publication Date |
---|---|
GB995565A true GB995565A (en) | 1965-06-16 |
Family
ID=10353244
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB3345962A Expired GB995565A (en) | 1962-08-31 | 1962-08-31 | Improvements in or relating to nozzles and other refractories for use in teeming andcasting steel |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB995565A (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2169899A1 (en) * | 1971-12-30 | 1973-09-14 | Maximilianshuette Eisenwerk | |
WO2002034693A1 (en) * | 2000-10-21 | 2002-05-02 | Refractory Intellectual Property Gmbh & Co. Kg | Fire-resistant substance and method for producing a fire-resistant lining |
-
1962
- 1962-08-31 GB GB3345962A patent/GB995565A/en not_active Expired
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2169899A1 (en) * | 1971-12-30 | 1973-09-14 | Maximilianshuette Eisenwerk | |
WO2002034693A1 (en) * | 2000-10-21 | 2002-05-02 | Refractory Intellectual Property Gmbh & Co. Kg | Fire-resistant substance and method for producing a fire-resistant lining |
US6803336B1 (en) | 2000-10-21 | 2004-10-12 | Refractory Intellectual Property Gmbh & Co. Kg | Fire-resistant substance and method for producing a fire-resistant lining |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB995565A (en) | Improvements in or relating to nozzles and other refractories for use in teeming andcasting steel | |
GB1533890A (en) | Alumina-chrome refractory composition | |
GB1334763A (en) | Electric furnace and process for melting refractory material therein | |
GB1472114A (en) | Refractory material or articles | |
GB995712A (en) | Bottom pour ladle nozzle and stopper rod construction | |
US3285761A (en) | Abrasion resistant refractory material | |
GB1213530A (en) | Basic fused refractory material | |
GB892048A (en) | Improvements in or relating to ceramics | |
GB1253974A (en) | Prodcustion of refractory shaped articles | |
GB1256636A (en) | ||
GB1293524A (en) | Production of refractory shaped articles | |
GB985502A (en) | Ramming mix | |
GB1450089A (en) | High alumina refractories | |
GB1148259A (en) | Metallurgical vessel | |
ATE97122T1 (en) | COMPOUND FOR COATING A LINING OF A METALLURGICAL MELTING VESSEL BASED ON REFRACTORY OXIDES. | |
SU637383A1 (en) | Refractory mass for guniting lining of metallurgical plants | |
GB1046661A (en) | Carbon-containing, basic, burnt refractory brick | |
GB1062373A (en) | Basic refractories | |
GB724980A (en) | Improvements in or relating to refractory materials | |
GB694057A (en) | Improvements in the production of repair of refractory articles | |
Davydenkov et al. | Production of refractory bodies in the system magnesite-chromite-alumina for gunning the crown of open-hearth furnaces | |
GB1256915A (en) | ||
FR2340919A1 (en) | Hydration resistant dolomite for refractory bricks - consisting of sintered dolomite aggregates interspersed with refractory additive binder phase | |
GB1486352A (en) | Method for making refractory articles | |
Barthel et al. | USE OF MAGNESIA CHROMITE REFRACTORIES MADE FROM SINTERED CO-CLINKER IN SECONDARY STEELMAKING AND OPEN HEARTH FURNACES |