GB2130941A - A cast bar of an aluminum alloy for wrought products, having improved mechanical properties and workability - Google Patents
A cast bar of an aluminum alloy for wrought products, having improved mechanical properties and workability Download PDFInfo
- Publication number
- GB2130941A GB2130941A GB08234033A GB8234033A GB2130941A GB 2130941 A GB2130941 A GB 2130941A GB 08234033 A GB08234033 A GB 08234033A GB 8234033 A GB8234033 A GB 8234033A GB 2130941 A GB2130941 A GB 2130941A
- Authority
- GB
- United Kingdom
- Prior art keywords
- cast bar
- alloy
- cast
- jam
- aluminum base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The continuously cast bar of aluminum base alloy for wrought product according to the present invention: is of homogeneous structure; is free of defects; exhibits excellent mechanical properties, and; can be subjected, as cast or after a heat, treatment, to a working operation such as forging. The critical value of the secondary dendrite arm spacing (DAS) is 20 mu m; critical value of the size of second phase particles is 15 mu m and the critical value of primary crystal size is 50 mu m for the following composition:- AA 4000 Al-Si-Mg series alloy: 4-12% Si; 0.6-1.3% Mg, and; balance Al. AA 4000 Al-Si-Cu-Mg series alloy: 2-12% Si; 1.5-5.0% Cu; 0.8-1.3% Mg, and balance Al.
Description
SPECIFICATION
A cast bar of an aluminum alloy for wrought products, having improved mechanical properties and workability, as well as process for producing the same
Field of the invention
The present invention relates to an aluminum alloy and a process for producing the same. More particularly, the present invention relates to an aluminum alloy having improved mechanical properties and workability and a process for producing the same.
In the AA (Aluminum Association) standard 2000, 5000 and 4000 series aluminum alloys, which have been commercially used for wrought products, are as follows: the major alloying component of
AA 2000 series is copper, the major alloying component of AA 5000 series is magnesium, and the major alloying component of AA 4000 series is silicon.
As is well-known, because of high specific tenacity, i.e. high strength per unit weight, high impact resistance and high fatigue strength, aluminum base alloys for wrought products according to the above-mentioned standard have been widely used in the production of parts for automobiles and aircraft and various other machinery and apparatus. The above-mentioned series alloys for wrought products can be generally converted into forgings by using either an open die forging process or a die forging process. In the case of the open die forging process to be intended for producing large-sized forgings, it is usual that billets having a diameter of from 150 to 300 mm which are produced by a continuous casting method or a semicontinuous casting method are used.Large diameter billets, which have been conventionally used as a starting material for producing large-sized forgings, exhibit a significantly non-uniform cast structure throughout the cross-sectional area thereof. Particularly, the cast structure of the peripheral portion is substantially different from that of the center portion of the billets. For this reason, the mechanical properties of the billet are variable in different portions of the cross-sectional area of the billets. In addition, there is a possibility that such billets possess defects, such as pinholes, segregation, microshrinkage or microcracking.Accordingly, in order to produce forgings having satisfactory mechanical properties, it is not only necessary to select non-defective billets after being inspected throughly, but it is also necessary to subject the billets to a repeated forging operation to completely eliminate the above-mentioned defects and nonuniform cast structure during the forging process. Accordingly, the production of large-sized forgings from the conventional billets requires a long period of time and much labor.
On the other hand, in the case of the die forging process intended for producing small-sized forgings, it is usual that starting material having a small diameter of from 5 to 70 mm is used. The small diameter starting material is generally obtained by producing billets having a diameter of from 1 50 to 300 mm by a continuous casting method, subjecting the billet to a homogenizing heat treatment at a temperature of from 450 to 6000C over a period of 2 to 20 hours and hot-extruding the heat-treated billet at a temperature of from 350 to 5000 C. In this manner, the conventional process for producing the small diameter starting material requires the extrusion step, which results in an increase in the production cost.
In addition, the conventional processes for producing the aluminum alloys for wrought products have the following disadvantages.
(1) The AA 2000 series alloy and AA 5000 series Al-Mg base alloy generally exhibit a high deformation resistance and a low deformability at the extrusion. This feature makes it difficult to set adequate extrusion conditions such as an extrusion speed. If the extrusion conditions are inadequate, the extruded articles have coarse recrystallization grains at the region near the peripheral surface thereof. Microcracks may be generated at and propagated from the boundaries of the recrystallization grains. In addition the rupture of the extruded articles may eventually be caused due to the recrystallization grains and the intergranular crack.
(2) AA 2000 and 5000 series alloys exhibit a high deformation resistance at the extrusion, as described above. When these alloys are subjected to extrusion, a temperature increase by plastic working occurs because of friction between the die and the workpiece. Accordingly, the working temperature is higher at a later stage of one extrusion pass, which results in a change in the properties of the extruded articles along the longitudinal direction of the extruded articles. As a result, forgings produced from such extruded articles exhibit nonuniformity in properties.
(3) When an alloy material is subjected to extrusion working, the deformation degree in the portion near the peripheral surface is different from that in the central portion of the extruded material.
As a result, the extruded article shows a difference in the work structure between these two portions.
Particularly, in the case of AA standard 2000 and 5000 series alloys, the extruded articles exhibit a prominently fine work-structure at the portion near the peripheral surface thereof because of its high deformation degree, while the central portion thereof exhibits a coarse work-structure because of its low deformation degree. If the extruded articles having such a nonuniform structure are forged, the fiber structure of resultant forgings is broken up into fragments and exhibit poor fatigue and impact strengths.
(4) When billets made of the AA 2000 or 5000 series alloys are subjected to the extrusion k, the crystal grains and precipitates such as intermetallic compounds in the billets are forced to elongate in
the extrusion direction. As a result, the extruded articles have a crystal texture having a particular
directional property and are neither isotropic nor homogeneous. For this reasons, the extruded articles
must be forged in consideration of the extrusion direction of the bidet However, if a product having a
particular shape is to be produced, it is often difficult to apply the forging to the entire parts of the
extruded article so as to provide these parts with the optimal directional property. In such a case, the
resultant forgings may suffer from cracks and a local deterioration in the mechanical properties
including fatigue strength.
As described above, the small diameter material for forgings produced by extrusion possesses
inevitable disadvantages due to the extrusion, particularly, the disadvantages that properties of this
material are anisotropic and nonhomogeneous. For this reasons, forgings produced from such a
material do not always exhibit satisfactory mechanical properties, particularly, high fatigue strength
and high impact strength. The small diameter forging material may also be produced by using a
continuous cast- or semicontinuous cast-bar. However, in this case, the same problems as those
described for the large diameter billet, such as the nonuniform structure or structural defects, arise.
Apart from these problems, it is difficult under the present circumstances to produce a small diameter
bar having a diameter of 100 mm or less by a continuous casting method on an industrial scale.
The AA 2014 and AA 2017 Al-Cu alloys and AA 7075 Al-Zn-Mg alloys which have been
commercially used as a high strength aluminum base alloy for forgings are superior to the AA 4000
series alloy in respect to mechanical strength, while the former alloys are inferior to the latter alloy in
respect to the heat- and wear-resistance. The AA 4000 series alloy exhibits excellent heat- and wear
resistances due to the presence of silicon contained therein.
AA 4032 Al-Si-Cu-Mg-Ni alloy for forgings has particularly excellent heat- and wear-resistances.
This grade of alloy is however, disadvantageous in that its forgeability is remarkably inferior because
nickel is contained in the alloy in an amount of from 0.5 to 1.3% by weight. Also, in the case of AA
4000 series alloy, the forgings are produced by an extrusion followed by forging as is the case with AA
2000 and 5000 series alloys. That is, the forgings are produced by continuously casting a melt of the
aluminum alloys into large diameter billets having a diameter of 10 inches or more, subjecting the
billets to a high temperature heat treatment, a so-called homogenizing heat treatment, at a
temperature of from 450 to 5000C over a period from 2 to 24 hours, and extruding the heat-treated
billets thereby to obtain forgings having a desired diameter. In the die forging operation most widely
practiced, a round extruded bar having a diameter of 100 mm or less is used.However, this extrusion is
highly expensive. In addition, the extruded round bar is not suitable as a forging because the extruded
round bar possesses the following disadvantages:
(a) the alloy structure is nonuniform over the cross section perpendicular to the extrusion
direction, that is, the crystal grains along the peripheral surface of the extruded articles are liable to be
coarsened due to the heat generated by the friction between the surface of the extruded article and the
inner surface of the die;
(b) the alloy structure is nonuniform over the cross section along the extrusion direction, (that is, the crystal) grains at the final extrusion stage are liable to be made more coarse due to the heat generated during the working operation, as compared with the crystal grain coarsening at the initial extrusion stage), and::
(c) the extruded articles have a directional property in the extrusion direction, that is, extruded articles have undergone a high degree of working in the extrusion direction and acquire a directional property due to the flow of the structure.
Under these circumstances, the inventors have made extensive studies to develop a continuously cast bar of aluminum base alloys for wrought products, particularly, AA 2000, 5000 and 4000 series alloys, so that the bar is; homogeneous in structure: free of defects; exhibits excellent mechanical properties, and; can be subjected, as cast or after a heat treatment, to a working operation such as forging. This operation for producing wrought products must be a single operation, that is the bar is not subjected to any preliminary plastic working having an adverse effect on the properties of the cast bar, such as the above mentioned hot extrusion.As a result, the inventors have found that an adequate combination of the composition of the aluminum base alloy to be cast and the cast structure of the aluminum base alloy produces an aluminum alloy cast bar capable of satisfying the above-mentioned requirements and that when a melt of an aluminum base alloy having a particular composition is cast under particular conditions, it is possible to produce an aluminum alloy cast bar having the desired structure.
Summary of the invention
An object of the present invention is to provide a continuously cast bar of aluminum base alloys for wrought products equivalent to the AA standard 2000, 5000 and 4000 series, which bar is of a homogeneous structure; is free of defects; exhibits excellent mechanical properties, and; can be subjected, as cast or after heat treatment, to one of the working operations for producing wrought products such as forging, without applying any preliminary plastic working, such as hot extrusion, having an adverse effect on the properties of the cast bar.
Another object of the present invention is to provide a process for producing a continuously cast bar of aluminum base alloys possessing a satisfactory workability, such as excellent forgeability, by selecting an adequate combination of the composition of AA standard 2000, 5000 and 4000 series alloys with cast structure thereof and by selecting the casting conditions.
Still another object of the present invention is to increase the wòrkability of the continuously cast bar produced by the above-mentioned process by subjecting the bar to a heat treatment.
Still another object of the present invention is to provide an aluminum base alloy in cast state, which exhibits mechanical properties equivalent to, because of no directional properties, or, superior to that possessed by the conventional extrusion of aluminum base alloys.
The basic technical concept of the present invention resides in the discovery that, a critical value of the secondary dendrite arm spacing (hereinafter referred to as DAS) and a critical value of the size of second phase particles and/or the grain diameter, which critical values are substantially lower than the
DAS, the size of the second phase particles and the grain diameter in the conventional aluminum alloy ingot, are responsible for fine cast structure capable of remarkably enhancing the workability and the mechanical properties of the aluminum base alloys for wrought products having the compositions described hereinbelow.
The process for producing an aluminum base alloy bar according to the present invention is based on the technical concept that, when an aluminum base alloy melt is cast into a smaller diameter bar at a higher casting speed than in the case of the conventional continuous casting method industrially practiced, the resultant bar has a cast structure which is microscopically fine, macroscopically fine, isotropic and free from defects.
In accordance with one aspect of the present invention, there is provided a cast bar of an aluminum base alloy for wrought products (AA standard 2000 series for wrought products), exhibiting high tensile strength, impact strength and fatigue strength, which comprises 2.0 to 9.0 wt% of copper, 0.2 to 1.2 wt% of magnesium, 0.2 to 1.2 wt% of silicon, 0.2 to 0.8 wt% of manganese, and the balance consisting of aluminum and unavoidable impurities and occasionally an optional component(s), and wherein the DAS is not greater than 1 5 ,um, the grain diameter is not greater than 80 Mm and the second phase particles comprising intermetallic compounds have a size not greater than 10 ym.
In accordance with another aspect of the present invention, a cast bar of an aluminum base alloy for wrought products of the present invention is characterized by a combination of a particular composition and a particular structure, particularly, relating to a uniform distribution of solute components (solution components) throughout the grain boundaries and the matrix of the crystal grains. More specifically, the present invention provides a cast bar of an aluminum base alloy for wrought products (AA standard 2000 series homogeneous alloy) exhibiting high tensile strength, impact strength and fatigue strength, having the same composition as that of the above-mentioned AA standard 2000 series alloy and wherein the ratio of the concentration (a) of the solute components in the matrix within the crystal grain to the concentration (b) of the solute components in the grain boundaries, i.e.a/b, is not smaller than 0.70.
In accordance with still another aspect of the present invention, there is provided a process for producing a cast bar of an aluminum base alloy for wrought products corresponding to AA standard 2000 series alloy. More specifically, the process comprises preparing a melt of the alloy composition and continuously casting the melt at a solidification speed of not lower than 250C/sec.
In accordance with still more another aspect of the present invention, there is provided a process for producing a cast bar of an aluminum base alloy corresponding to the AA standard 2000 series homogeneous alloy. More specifically, there is provided a process for producing a cast bar of an aluminum base alloy which comprises preparing a melt of the alloy composition, continuously casting the melt at a solidification speed of not lower than 250 C/sec, and subjecting the cast bar to a homogenizing heat treatment at a temperature of from 450 to 5300C over a period of from 0.5 to 20 hours.
In accordance with a further aspect of the present invention, there is provided a cast bar of an aluminum base alloy (AA standard 5000 series alloy) comprising 2.0 to 6.0 wt% of magnesium, 0.03 to 0.3 wt% of chromium, and the balance being aluminum and unavoidable impurities, and, occasionally an optional component(s), and wherein, the grain diameter is not greater than 80 ,um, the DAS is not greater than 13 Hm, and the size of the second phase particles is not greater than 10 Mm.
The above mentioned AA standard 5000 series alloy may further contain at least one of the following optional elements selected from the group consisting of: titanium in an amount of from 0.005 to 0.2 wt%; manganese in an amount not more than 0.5 wt%; zirconium in an amount not more than 0.3 wt%, and tin in an amount not more than 0.5 wt%. The titanium may be partly replaced with boron so that the total amounts of titanium and boron are not more than 0.2 wt%.
In accordance with another aspect of the present invention, a cast bar of an aluminum alloy (AA standard 5000 series homogeneous alloy) has the same composition as that of the above mentioned
AA standard 5000 series alloy and wherein the ratio of the concentration (a) of the solute components in the matrix of the crystal grain to the concentration (b) of the solute components in the grain boundaries, i.e., a/b, is not greater tahn 0.70.
In accordance with another aspect of the present invention, there is provided a process for producing a cast bar of the above-mentioned AA standard 5000 series alloy. More specifically, the process comprises preparing a melt of the above-mentioned alloy composition and continuously casting the melt at a solidification speed of not lower than 1 50 C/sec.
In accordance with another aspect of the present invention there is provided a process for producing a cast bar of an aluminum alloy corresponding to the above-mentioned AA standard 5000 series homogeneous alloy. More particularly, there is provided a process for producing a cast bar of an aluminum alloy which comprises preparing a melt of the alloy composition, continuously casting the melt at a solidification speed of 15 C/sec or higher, and subjecting the cast bar to a homogenizing heat treatment at a temperature of from 450 to 5000C over a period of 1 to 24 hours.
In accordance with a further aspect of the present invention, there is provided a cast bar of an aluminum base alloy for forgings (AAstandard 4000 series Al-Si-Mg alloy) exhibiting excellent workability, wear and heat-resistances, which comprise 4 to 12 wt% of silicon 0.6 to 1.3 wt% of magnesium and the balance consisting essentially of aluminum and unavoidable impurities and occasionally an optional component, and which has a fine cast structure, in which the primary crystals have a size of not greater than 50 ,um, preferably, not greater than 25,um, the intermetallic compounds of second phase particles have a size of not greater than 1 5 ,um and the DAS is not greater than 20 jam. This alloy may further contain as an optional component, at least one member selected from the group consisting of 0.05 to 0.2 wt% of titanium, 0.02, to 0.2 wt% of vanadium, 0.01 to 0.1 wt% of lithium, 0.001 to 0.05 wt% of beryllium, 0.1 to 0.5 wt% of chromium and 0.02 to 0.2 wt% of zirconium, with the proviso that the total of these optional components is not more than 1.2 wt%.
In accordance with another aspect of the present invention, there is provided a cast bar of an aluminum base alloy (AA standard 4000 series Al-Si-Cu-Mg alloy) exhibiting excellent workability, wear- and heat-resistance, which comprises 2 to 12 wt% of silicon, 1.5 to 5.0 wt% of copper and, 0.8 to 1.3 wt% of magnesium.This alloy may further contain as an optional component, at least one member selected from the group consisting of 0.05 to 0.2 wt% of titanium, 0.02 to 0.2 wt% of vanadium, 0.01 to 0.1 wt% of lithium, 0.001 to 0.05 wt% of beryilium, 0.1 to 0.5 wt% of chromium and 0.02 to 0.2 wt% of zirconium, with the proviso that the sum of these optional components is not greater than 1.2 wt%, and the balance consisting essentially of aluminum and unavoidable impurities, and which has a fine cast structure, in which the primary crystals have a size of not greater than 50 jam, preferably, not greater than 25 jam, the intermetallic compounds have a size of not greater than 1 5 jam, and the DAS is not greater than 20 jam.
In accordance with a still another aspect of the present invention, there is provided a process for producing a cast bar of an aluminum base alloy which comprises preparing a melt of the AA standard 4000 series Al-Si-Mg alloy, and continuously casting the melt at a solidification speed of not lower than 250C/sec.
In accordance with a still more another aspect of the present invention, there is provided a process for producing a cast bar of an aluminum base alloy which comprises preparing a melt of the AA standard 4000 series Al-Si-Cu-Mg alloy and continuously casting the melt at a solidification speed of not lower than 250 C/sec.
In accordance with a further aspect of the present invention, the above-mentioned AA standard 4000 series Al-Si-Mg alloy and Al-Si-Cu-Mg alloy are characterized in that the area occupied by the second phase particles comprising the primary crystals and at least one member selected from intermetallic compounds such as Al-Cu, Al-Si, Mg-Si, Al-Mn-Fe, Al-Fe-Si and Al-Cu-Mg compounds, does not exceed 25% at any region of the examined cross section of the cast bar, and the primary crystals have a grain size of not exceeding 25 jam and the intermetallic compounds have a size of not exceeding 15 jam.
The cast structure of the aluminum base alloy cast bars of the present invention is fine, homogeneous and isotropic from the central portion to the peripheral surface throughout the cross sections thereof taken in any direction. In addition, the aluminum alloy cast bars exhibit high tensile strength, impact strength and fatique strength, and, further, even if they may contain a large amount of alloying elements, exhibit an excellent workability. The aluminum alloy cast bars of the present invention can be subjected directly to plastic workings such as forging or mechanical workings such as machining without applying a preliminary working, such as extrusion. This feature makes it possible to produce various aluminum alloy parts at low cost and to eliminate adverse effects on the parts due to a preliminary working such as extrusion working.Forgings or other wrought products, therefore, exhibit excellent properties and are produced at a low cost. Also, in accordance with the process of the present invention, aluminum base alloy for wrought products exhibiting the above-mentioned excellent properties can be simply and easily obtained.
Brief description of the drawings
Fig. 1 is a cross sectional microscope view of a cast bar consisting of one of AA standard 2000 series aluminum alloy and being produced by casting at a solidification speed of 250C/sec; Fig. 2 is the same view as in Fig. 1, except that the solidification speed was 0.5 C/sec; Fig. 3 is a cross sectional microscope view of a cast bar consisting of one of AA standard 5000 series aluminum alloy and being produced by casting at a solidification speed of 1 50 C/sec;
Fig. 4 is the same view as in Fig. 3, except that the solidification speed was 0.1 C/sec; Fig. 5 is a cross sectional microscope view of a cast bar consisting of an AA standard 4000 series alloys and being produced by casting at a solidification speed of 300 C/sec;;
Fig. 6 is the same view as in Fig. 5, except that the solidification speed was 300 C/sec; Fig. 7 is a graph showing a tensile strength and an elongation versus sampling positions of a specimen in Example 1;
Figs. 8A and 8B are perspective views of a wedge specimen and an illustration showing a method for testing, using the wedge specimen, respectively;
Fig. 9 is a graph showing a Imitative working degree versus solidification speed of a wedge specimen from Example 2, the limitative working degree being a working degree at which forging cracks occur;
Fig. 10 is a graph showing a deformation resistance and a deformability versus solidification speed of a specimen in Example 2; Fig. 11 is a graph showing a DAS versus solidification speed of each of alloy ingots A, B and C in
Example 3;;
Fig. 12 is a graph showing a tensile strength and an elongation versus solidification speed of an alloy B in Example 3;
Fig. 13 is a graph showing an impact value and a reduction of area versus solidification speed of an alloy B in Example 3;
Fig. 14 is a graph showing a fatigue strength in terms of test load of a specimen in Example 4; Fig. 1 5 is a graph showing a tensile strength and an elongation versus the sampling positions of a specimen from Example 5;
Fig. 1 6 is a graph showing a limitative working degree versus solidification speed of wedge specimens in Example 6; Fig. 1 7 is a graph showing a deformation resistance and a deformability versus solidification speed of specimens in Example 6; Fig. 1 8 is a graph showing a DAS versus solidification speed of each of alloys D, E and F in
Example 7;; Fig. 19 is a graph showing a tensile strength and an elongation versus solidification speed of the alloy E in Example 7;
Fig. 20 is a graph showing an impact value and a reduction of area versus solidification speed of the E in Example 7;
Fig. 21 is a graph showing an effect of the size of a second phase particles on a limitative working degree of aluminum ingots which were forged at a temperature ranging from 200 and 4500 C; Fig. 22 shows a wear resistance in terms of a specific wear ratio of the present alloy in comparison to that of several conventional alloys;
Fig. 23 shows a tensile strength at a temperature of from ambient temperature to 4000C of the present alloy in comparison to the conventional alloy, and; Figs. 24A, 24B and 24C each are an illustration showing an upsetting test.
Detailed description of the invention
The term "working" as used herein is not always limited to forging, and it is intended to include other plastic workings such as rolling, drawing, wire drawing and extrusion and also machining such as cutting. Accordingly, the aluminum base alloys for wrought products of the present invention can be subjected to various plastic workings and machining. It is to be understood that the term "continuous casting" as used herein is intended to include not only a so-called-completed continuous casting, but also a semi-continuous casting for producing a certain length of cast articles.
The term "secondary dendrite" as used herein is used in an ordinary sense in the field of metallography. The secondary dendrite is distinguished from the dendrite cell meaning a primary dendrite.
The fine structure of AA standard 2000 series alloy for wrought products according to the present invention is explained first. This alloy should have the above-mentioned composition and a fine cast structure, such that the grain diameter is not greater than 80 jam, the DAS is not greater than 1 5 jam and the second phase particles comprising intermetallic compounds have size not exceeding 10 jam.
The intermetallic compounds constituting the second phase particles include Al-Cu, Mg-Si, Al
Mn-Fe, Al-Fe-Si compounds and the like.
When the grain diameter, the DAS and the second phase particle size are outside each of the above defined values, even if the composition of the alloy is within the compositional ranges as described hereinafter, the resultaht cast bar cannot exhibit desired properties, such as high tensile strength, high fatigue strength and high impact strength. In addition, the isotropic macrostructure of the alloy is lost and the macrostructure tends to be inhomogeneous, with the result that the alloy exhibits a poor workability.
The fine structure of AA standard 5000 series alloy for wrought product of the present invention is explained second. This alloy should satisfy conditions such that the.grain diameter is not greater than 80 jam, the DAS is not greater than 13 jam and the second phase particles comprising intermetallic compounds have a size of not greater than 10 jam. Thus, this alloy exhibits excellent workability and high tensile strength, impact strength and fatigue strength.
The fine structure of the AA standard 4000 series alloy for wrought products of the present invention explained third. This alloy has a cast structure, wherein the DAS is not greater than 20 jam and the size of the second phase particles is not greater than 50 jam. Also, desirably, the area a percentage of the second phase particles comprising primary crystals and one or more intermetallic compounds, composed of Al-Cu, Al-Si, Mg-Si, Al-Mn-Fe, Al-Fe-Si, Al-Cu-Mg and the like is 25% or less at any sectional region of the alloy.
If the area percentage occupied by the second phase particles is more than 25%, the resultant alloy exhibits a remarkably poorforgeability. Also, if the size of the second phase particles is more than 50 jam, the resultant alloy is not only liable to crack during the forging but also has a poor machinability.
The conditions of homogenity of the AA standard 2000 series and 5000 series homogeneous alloys of the present invention may be satisfied, in substitution for the above defined fine structures.
Namely, these alloys should have such a structure that the ratio of the concentration (a) of the solute components, such as Cu, Cr, Mg, Si and Mn, in the matrix of the crystal grains to the concentration (b) of the solute components, such as Cu, Mg, Si and Mn, contained in the grain boundaries i.e. a/b, is 0.70 or more. The concentration (b) can be determined by locally applying the X-ray over a specimen across the grain boundaries by emission spectroanalysis or X-ray analysis, and then comparing the detected concentration of the components of the grain boundaries with the detected concentration of the components in the matrix of the crystal grains. In accordance with the present invention, enrichment of -the solute components in the grain boundaries is suppressed so as to avoid a reduction in the ductility of the aluminum base alloys.This suppression of the solute component enrichment is effective for attaining the effects equivalent to those obtained by the limitation of the DAS, the grain diameter and the size of the second phase particles.
It is some times difficult to maintained by the control of the solidification speed the macroscopically isotropic property of the cast bars. In such a case, if the cast bars produced by a solidification speed of at least a critical cooling speed is subjected to a homogenizing heat treatment suitable for adjusting the distribution of the solute components so as to obtain a ratio of a/b of at least 0.70, the homogenized bars exhibit almost same desired properties as those attained by the aluminum base alloys for wrought products, having the fine structure. In order to obtain the concentration a ratio of a/b of at least 0.70, the homogenizing heat treatment is carried out at a temperature of from 450 to 5300C over the period of 0.5 to 20 hours for AA standard 2000 series alloy, and at a temperature of from 450 to 5800C over the period of 1 to 24 hours forAA standard 5000 series alloy.
Ideally, not only the limitation of the grain diameter, the DAS and the second phase particle size to the above-mentioned maximum values but also the limitation of the ratio, a/b, to the value of at least 0.70 should be satisfied in AA standard 2000 series and 5000 series alloys for wrought products. In this case, the workability and the mechanical properties of the cast bar are further enhanced as compared in the alloys satisfying grain diameter, DAS and second phase particle size but not the concentration ratio, a/b.
The aluminum alloy bar satisfying the grain diameter, DAS and the second phase particle size can be produced by a continuous casting process wherein the solidification speed at any site throughout the cross section of the bars is set to at least a critical speed.
The critical solidification speed is 250 C/sec for the AA standard 2000 series alloy, 1 50 C/sec for the AA standard 5000 series alloy and 250 C/sec, preferably, 300C/sec for the AA standard 4000 series alloy.
When the solidification speeds are gradually increased from a level much lower than the critical solidification speeds in the production of the AA standard 2000 series, 5000 series and 4000 series alloys for wrought products, the grain diameter, the DAS and the second phase particles of the alloys become extremely small or very fine in the vicinity of the critical solidification speeds, whereby the above-mentioned structure conditions are satisfied. In other words, solidification of at least the critical solidification speeds permits to provide the cast bars with the desired mechanical properties and workability. For this reason, the solidification speeds should be set to values of at least the critical speeds.
The term "solidification speed" as used herein refers to a temperature dropping speed at the
interface between the solid phase and the liquid phase of an alloy placed in a continuous casting mold.
The temperature dropping speed can be experimentally detected, for example, by inserting a
thermocouple into the liquid phase from above the mold and determining a change in temperature of
the place where the thermocouple comes into a contact with the solid phase.
In the continuous casting production of the aluminum base alloys for wrought products of the
present invention, a conventional float type continuous casting process is difficult to apply for the
production of bars having a diameter of 100 mm or less. As far as the inventors know, a gas pressure
applying type hot top continuous casting process, which has been proposed in USP No. 4,157,728 is
the best process for producing a bar with a small diameter of particuladyfrom 5 to 70 mm. It is
however, to be understood that if any continuous casting process other than the process of USP No.
4,1 57,728 allows to obtain good qualities and solidification speeds greater than the critical solidification speeds, this process can be applied to the processes of the present invention.
The cast bars thus prepared may be subjected directly to plastic working or mechanical working.
Alternately, the cast bars may be subjected to a homogenizing heat treatment before being worked on by various procedures. Furthermore, the cast bar may be subjected to a heat treatment such as T6 treatment before being worked on by various procedures.
The fact that the cast structure of AA standard 2000 series alloy becomes suddenly fine at a solidification speed of about 250C/sec will be illustrated with reference to Figs. 1 and 2. Fig. 1 shows a microscope view of a structure of an aluminum base alloy bar consisting of 4.5 wt% of Cu, 0.6 wt% of Mg, 0.6 wt% of Si, 0.4 wt% of Mn, 0.01 wt% of Ti and the balance being Al and trace of impurities. The aluminum base alloy was continuously cast at a solidification speed of 250 C/sec into the form of the bar which was cut so as to observe the micro structure of the bar cross section.Fig. 2 shows a microscope view of the same aluminum base alloy bar as in Fig. 1 except that the bar was produced by casting with the solidification speed of 0.5 C/sec. As being apparent from Fig. 1 , the granular crystals are uniformly distributed through the structure shown in Fig. 1 ,the DAS is not greater than 1 5 jam and all of the second phase particles comprising intermetallic compounds have a size not greater than 10 jam, with regard to the alloy cast at the high solidification speed. In contrast, as being apparent from
Fig. 2, the DAS is greater than 1 5 jam, the second phase particles comprising intermetallic compounds are significantly coarse with regard to the alloy cast at the low solidification speed.
Fig. 3 shows a microscope view of a structure of an aluminum alloy bar consisting of 3.0 wt% of
Mg, O.15 wt% of Cr, 0.01 wt% of Ti, 0.2 wt% of Mn and the balance consisting being Al and trace of impurities. The aluminum alloy was cast at a solidification speed of 1 SOC/sec into the form of a bar which was cut so as to observe the micro structure of the bar cross section.Fig. 4 shows a microscope view of the same aluminum alloy bar as in Fig. 3 except that the bar was produced by casting with the solidification speed of 0.1 OC/sec. As being apparent from Fig. 3, the granular crystals are uniformly distributed through the structure shown in Fig. 3, the DAS is not greater than 1 3 jam and all of the second phase particles comprising intermetallic compounds have a size not greater than 10 jam, with regard to the alloy cast at the high solidification speed. In constract, as being apparent from Fig. 4, the
DAS is greater than 13 jam, the second phase particles comprising intermetallic compounds are significantly coarse with regard to the alloy cast at the low solidification speed.
Fig. 5 shows a microscope view of a structure of a cast bar consisting of an AA standard 4000 series alloys. The aluminum alloy was cast at a solidification speed of 30 C/sec into the form of a bar which was cut so as to observe the structure of the bar cross section. Fig. 6 shows a microscope view of the same aluminum alloy bar as in Fig. 5 except that the bar was produced by casting with the solidification speed of 30C/sec.As being apparent from Fig. 5, crystals are uniformly distributed through the structure shown in Fig. 5, the DAS is not greater than 20 jam, the second phase particles comprising intermetallic compounds have a size not greater than 1 5 jam, and, the second phase particles comprising primary crystals have a size not greater than 50 jam with regard to the alloy cast at the high solidification speed. In contrast, as being apparent from Fig. 6, the DAS is greater than 20 jam, the second phase particles comprising intermetallic compounds and primary crystals are significantly coarse with regard to the alloy cast at the low solidification speed.
As a result of our investigations of the relationship between the solidification speed and the properties of the resultant alloy ingot, the lower limit of the solidification speed was found to be 250C/sec for AA standard 2000 series and 4000 series alloys and 1 50 C/sec for AA standard 5000 series alloy. It goes without saying that in order to produce an alloy ingot at a high solidification speed, a continuous casting is the most suitable. The most convenient continuous casting process which can be industrially used; today, is a vertical semi-continuous casting process. In order to realize a high solidification speed, for example, 250C/sec or more, in this vertical semi-continuous casting process, casting a melt into a bar having a small diameter is appropriate.The solidification speed 250C/sec or more, preferably 300C/sec or more suitable for the AA standard 4000 series alloy can be realized by determining the diameter of the resultant bar to a small size of from 40 to 100 mm without making any substantial modification in the cooling-water injecting conditions, such as the water temperature, the water-flow rate, and the water-injecting position, usually employed in the operation of the process according to USP No. 4,1 57,728.
The alloy compositions of the present invention will be discussed, below.
First. the reasons for the limitation of the composition of the AA standard 2000 series alloy will be illustrated. If the copper content is less than 2.0 wt%, the resultant bar exhibits an unsatisfactory mechanical strength. If the copper content is more than 9.0 wt%, the copper is not solutionized to a satisfactory extent even by a solution treatment and is precipitated as intermetallic compounds. As a result, the mechanical properties, such as tensile strength, elongation and impact strength, of the cast bar become inferior, which leads to the formation of casting cracks of the resultant bar during a continuous casting operation. However, by establishing a solidification speed of 25"C/sec or higher at any site throughout the solid-liquid interface, it is possible to carry out the continuous casting operation smoothly without causing any casting cracks due to high copper content of up to 9.0 wt%. Since a high cooling speed is maintained uniformly over the bar cross section being cast, the segregation tendency seen in the bar cross section is reduced and the solidification, which is quite similar to an ideal unidirectional solidification, takes place. Such solidification seems to make it possible to increase the maximum copper content, at which no serious copper segregation pccurs, as compared with the prior art.
Also, if the magnesium content is less than 0.2 wt%, the resultant cast bar exhibits a poor tensile strength. If the magnesium content is more than 1.2 wt%, the Mg-Si intermetallic compounds are formed, which causes deterioration of elongation and tensile strength of the resultant cast bar. As a result of the intermetallic compounds, a cast bar exhibiting the desired properties, i.e. high fatigue strength and high impact strength, cannot be obtained. Also, if the silicon content is less than 0.2 wt%, the resultant alloy is not heat-treatable. On the other hand, a silicon content more than 1.2 wt% causes deterioration of a tensile strength and impact strength of resultant cast bar. A manganese content less than 0.2 wt% is ineffective for obtaining high tensile strength and impact strength.If the manganese content is more than 0.8 wt%, coarse grains are formed, with the result that the structure conditions described above cannot be satisfied, which causes the resultant cast bar to exhibit a poor tensile strength. The aluminum alloy of the present invention may contain, if necessary, titanium. Alternately, the aluminum alloy may contain both titanium and boron, in a total amount of from 0.005 to 0.15 wt%.
The titanium or both titanium and boron is effective for further refining the crystal grains and thus, for attaining more excellent mechanical properties.
Secondly, the reasons for the limitation of the composition of the AA standard series 5000 alloy will be illustrated. If the magnesium content is less than 2.0 wt%, the resultant cast bar is unsatisfactory in mechanical properties. Also, a magnesium content more than 6.0 wt% has an adverse effect on the hot workability of the resultant cast bar and has a possibility of causing the stress corrosion cracking. A chromium content less than 0.03 wt% is ineffective for preventing the resultant cast bar from undergoing stress corrosion cracking. Also, a chromium content more than 0.3 wt% results in the formation of macro-sized intermetailic compounds which have an adverse effect on the mechanical properties and the workability of the resultant cast bar.
If necessary, titanium in an amount of from 0.005 to 0.2 wt% may be added to the AA standard 5000 series alloy for the purpose of refining the crystal grains. Titanium may be partly replaced with boron. In this case, a total amount of titanium plus boron must be 0.2 wt% or less. Manganese is effective for preventing stress corrosion cracking. However, the manganese content more than 0.5 wt% results in the formation of macro-sized intermetallic compounds which are detrimental to the mechanical properties and the workability. Zirconium is partially solutionized and contributes to the strengthening of the alloy matrix. The other portion of zirconium reacts with magnesium to form the
Mg2Zr intermetallic compounds which are effective for imparting a free cutting property to the resultant cast bar.The solubility of tin is low and, instead, tin reacts with magnesium to form the
Mg2Sn intermetallic compounds which are effective for enhancing the free cutting of the resultant cast bar.
The composition ranges of the AA standard 4000 series alloy will be illustrated, below.
In the case of the AA standard 4000 series Al-Si-Mg alloy, silicon is not only effective for strengthening the alloy matrix, but also interacts with aluminum to form an Al-Si eutectic which is effective for increasing the wear resistance and the corrosion resistance in an oxidizing atmosphere. If the silicon content is less than 4 wt%, the resultant cast bar is unsatisfactory in wear resistance. A silicon content greater than 12 wt% results in an increase in the silicon primary crystals which are effective for increasing the wear resistance but detrimental to the tensile strength. The silicon content is preferably in the range of from 6 to 10 wt%.
Magnesium is not only solutionized in aluminum to strengthen the alloy matrix, but also reacts with silicon to from the Mg2Si intermetallic compounds which contribute to enhancement of the tensile strength and the wear resistance of the cast bar. However, if the magnesium content is less than 0.6 wt%, the contribution of the intermetallic compounds to the tensile strength and wear resistance is unsatisfactory. Also, if the magnesium content is more than 1.3 wt%, the resultant alloy becomes brittle. Accordingly, it is necessary that the silicon content and the magnesium content be in a range of from 4 to 12 wt% and 0.6 to 1.3 wt%, respectively.
In the above-mentioned AA standard series 4000 Al-Si-Cu-Mg alloy, copper is essential for imparting a heat treatable property and high tensile strength to the resultant cast bar. However, if the copper content less than 1.5 wt%, the resultant cast bar exhibits an unsatisfactory toughness. A copper content exceeding 5.0 wt% results in a deterioration in the workability of the resultant cast bar. Silicon has the same effects as those described for the AA standard series 4000 Al-Si-Mg alloy. In addition, silicon is effective for mitigating the cracking during the forging of the resultant cast bar and the porosity of the cast bar. Further, silicon reacts with magnesium to form the Mg2Si intermetallic compounds which enhances the heat treatable property of the alloy. However, if the silicon content is less than 2.0 wt%, the desired effects cannot be attained.Also, a silicon content exceeding 1 2 wt% is effective for increasing the wear resistance but is detrimental to the forgeability and the machinability of the cast bar. Magnesium enhances the strength of the alloy matrix, and the heat treatable property and the wear resistance of the alloy. However, a magnesium content less than 0.8 wt% is ineffective for attaining the these effects. On the other hand, if the magnesium content is greater than 1.3 wt%, the resultant cast bar becomes brittle and exhibits a poor workability.
In the AA standard 4000 series Al-Si-Cu-Mg alloys with an optional components particularly the heat resistance and machinability are enhanced by the optional element (A).
In summary, the above described compositions and structure conditions, i.e. grain diameter, the
DAS and the second phase particles which are intermetallic compounds composed of, for example Mg
Si, Al-Mn-Fe and Al-Fe-Si and occasionally silicon primary crystals make it possible to produce a cast bar exhibiting high tensile strength, fatigue strength and impact strength as well as fine and isotropic structures. The cast bar, which is subjected to a plastic working e.g. forging, and is usually referred to as an ingot or billet, and the cast bar, which is directly subjected to machining according to one of the features of the present invention, possess excellent workability.
The wrought products produced by using the cast bar of the present invention are free from undesirable effects of the conventional primary working of the conventional cast bars. The cast bars of
AA standard 4000 series alloys according to the present invention are suitable for forgings used as components of a compressor, a vehicle, an air plane and the like.
The present invention will be further ilJustrated by the examples set forth below, which are provided for the purpose of illustration and should not be interpreted as in any way limiting the scope of the present invention.
Example 1
Run Neo. 1 (invention)
An aluminum alloy melt comprising 4.7 wt% of copper, 0.7 wt% of silicon, 0.6 wt% of manganese, 0.5 wt% of magnesium, 0.01 5 wt% of titanium and boron, and the balance consisting essentially of aluminum was prepared and the melt was subjected to a hot top continuous casting process at a solidification speed of 250C/sec, thereby to produce a round bar having a diameter of 53 mm. The gas pressure was applied to the molten metal body being cast as described in USP No.
4,1 57,728.
Run No. 2 (control)
The same procedures as those described in Run No. 1 were repeated, except that a solidification speed of 0.1 50C/sec was used.
Run No. 3 (control)
The same procedures as those described in Run No. 1 were repeated, except that a solidification speed of 3 C/sec was used.
From each of the round bars obtained by Run Nos 1, 2 and 3, specimens were cut out along the longitudinal direction of the bars at varying distances from the outer periphery thereof. Each of the specimens was heated at a temperature of 5050C for 6 hours and, then, cooled in hot water.
Thereafter, the specimens were aged at a temperature of 170"C for 8 hours to produce a so-called Te material. The tensile strength and elongation at normal temperature of the specimens were determined and the results are shown in Fig. 7. In Fig. 7, the cross symbol X denotes a specimen from Run No. 1 (25 OC/sec), the black circle symbol denotes a specimen from Run No. 2 (0.1 50C/sec) and the circle symbol 0 denotes a specimen from Run No. 3 (30C/sec). It is apparent from Fig. 7 that in the case of solidification speeds of 0.1 50 C/sec and 3 OC/sec, a considerable scattering of tensile strength and elongation is noted between the outer periphery portion and the central portion.In the case of the solidification speed of 250C/sec, there is little scattering in both tensile strength and elongation between the outer periphery and the central portions, which suggests almost homogeneous properties of the cast bar from the outer periphery to the central portions. Also, the DAS, the second- phase particle size and the ratio a/b of solute concentration within the matrix of the grain to solute concentration in the grain boundary of the ingot bar obtained by Run Nos. 1, 2 and 3 were determined.
The results are shown in Table 1.
Table 1
Solute con
Solidification Size of secondary centration
speed DAS phase particles ratio a/b C/sec ym jam Run No.2 0.15 40 21 40
Run No.3 3 25 16 55
Run No.1 25 12 8 75
As is apparent from Table 1, in the case of the solidification speed of 25"C/sec, both DAS and second phase particles are fine-sized and the ratio of the solute component concentration (a) to the solute component concentration (b), hereinafter referred to as the solute concentration ratio a/b, is high, while in the case of solidification speeds of 0.1 50C/sec and 30C/sec, both DAS and second phase particles are significantly coarse and the solute concentration ratip a/b, is low.In view of these results and the test results shown in Fig. 7, it is apparent that the structure factors have a great influence on the tensile strength and the elongation of the cast bar.
Example 2
An alloy melt comprising 4.5 wt% of copper, 0.6 wt% of silicon, 0.6 wt% of magnesium, 0.8 wt% of manganese, 0.015 wt% of titanium and the balance consisting essentially of aluminum was prepared, and the melt was cast into a round bar having a diameter of 78 mm by means of a hot top continuous casting process. The gas pressure was applied to the molten metal body being cast as described in USP No. 4,157,728. This casting is hereinafter referred to as the gas-pressure applying type hot top continuous casting. The solidification speed was varied between 5 and 800 C/sec. The bar was homogenized at a temperature of 5050C for 8 hours to produce test specimens.
Wedge specimens as shown in Fig. 8A were cut out from each of the test specimens. The wedge specimens were hot-forged at a temperature of 300, 400 and 4500 C, respectively, thereby to determine a limitative working degree at which forging cracks were generated on the specimens.
The wedge test was carried out according to a testing procedure described in "Metal Plastic
Working", (in Japanese) Kenzo Kato, published by Maruzen Co. Ltd. In this testing procedure, a specimen in the form of a wedge as shown in Fig. 8A is placed on a platen 2 as shown in Fig. 8B. Then, a 1/2 ton hammer 3 was struck on the wedge specimen 4. The working limit is determined on the basis of the crack of the specimen 4 generated after the forging operation. This procedure is very suitable and reliable for evaluating the forgeability of a material.
The test results are shown in Fig. 9. The obliquely line region of Fig. 9 above the polygonal lines indicates the levels of forging temperature and wedge-shaped reduction ratio allowing the forging without cracks. It is apparent from Fig. 9 that the limitative working degree is increased as the forging temperature is increased. Also, when the solidification speed is high the limitative working degree is high and forging cracks are difficult to occur at any forging temperature. Particularly, the limitative working degree is remarkably increased when the solidification speed is increased to about 250C/sec.
This fact corresponds to an abrupt change in structure at the solidification speed of about 250C/sec as described hereinabove. In addition, in order to evaluate workability by general hot working including forging and rolling of the cast bars produced at various solidification speeds, the testing material was subjected to a hot torsion test (cf. for example, "Light Metal", Horiuchi et al, (in Japanese) Vol. 20, No.
5) to determine the deformation resistance and the deformability thereof. The results are shown in Fig.
1 0. As is apparent from Fig.10, the deformation resistance change depending on the solidification speed increase displays an abrupt decrease at about 250C/sec and the deformability change depending on the solidification speed displays an abrupt increase at a solidification speed of about 250C/sec. In view of these results, it is clear that workability of the cast bars according to the present invention is excellent.
Example 3
An alloy melt comprising 2.3 wt% of copper, 0.3 wt% of magnesium, 0.3 wt% of silicon, 0.2 wt% of manganese, 0.02 wt% of titanium and the balance consisting essentially of aluminum (which alloy is referred to as alloy A), alloy melt comprising 4.5 wt% of copper, 0.6 wt% of magnesium, 0.7 wt% of silicon, 0.6 wt% of manganese, 0.01 wt% of titanium and the balance consisting essentially of aluminum (which alloy is referred to as alloy B) and an alloy melt comprising 8.7 wt% of copper 1.0 wt% of magnesium, 1.0 wt% of silicon, 0.7 wt% of manganese, 0.01 5 wt% of total of titanium and boron and the balance consisting essentially of aluminum (which alloy is referred to as alloy C) were separately prepared.Each of these melts was cast into a round bar having a diameter of 62 mm by means of a gas-pressure applying type hot top continuous casting process at a solidification speed varying between about 6 to about 800 C/sec. The master alloy comprising 5 wt% of titanium, 0.7 wt% of boron and the balance consisting essentially of aluminum was added into the melt of the alloy C so as to incorporate titanium and boron.
The DAS of each of the round bars prepared above was is shown in Fig. 11.
As is clearly shown in Fig. 11, the DAS change of each of the alloys A, B and C depending on the solidification speed increase displays a prominent decrease at the solidification speed up to about 25"C/sec, and DAS assumed an almost constant value of about 6 jam at a solidification speed above 250C/sec which is a critical so!idification speed. This clearly indicates that a solidification speed of 250C/sec is significant for the fine structure of the AA standard 2000 series alloy according to the present invention, that is, 25"C/sec is a critical solidification speed at which the structure of such alloy becomes fine.
In addition, as a representative example of the above-mentioned three alloys, the alloy B was cast at various solidification speeds into the bars and the tensile strength and elongation of the bars were measured. The results are shown in Fig. 12. It was confirmed from Fig.12 12 taking into consideration Fig.
11, that both tensile strength and elongation are increased with the increase in the DAS values.
Particularly, an increase in elongation is outstandingly shown. Furthermore, the cast bars produced from the alloy B at various solidification speeds were subjected to an impact test and a drawing test.
The results are shown in Fig. 13. It was also confirmed that the solidification speed of 250C/sec causes a prominent increase of the mechanical properties, i.e., impact value and the reduction of area.
Example 4
Run No. 4 (invention)
An alloy melt comprising 4.0 wt% of copper, 0.2 wt% of silicon, 0.6 wt% of magnesium, 0.6 wt% of manganese, 0.01 wt% of titanium and the balance consisting essentially of aluminum was prepared, and cast into a round bar having a diameter of 35 mm. The casting was carried out by the gas-pressure applying type hot top continuous casting and the solidification speed was 300 C/sec. The bar was forged into a connecting rod by a conventional hot forging. The connecting rod was heat-treated at a temperature of 5050C for 2 hours, and, then, water-cooled, for the purpose of solution treatment.
Thereafter, the connecting rod was aged at room temperature (T4 treatment) for two days. The resultant material in the form of the connecting rod was subjected to a fatigue test.
Run No. 5 (control)
An alloy melt having the same composition as that of Run No. 4 was cast by a conventional direct chill-casting method. The obtained cast bar was extruded at an extrusion ratio of 40, thereby to produce an extruded bar having a diameter of 35 mm. The extruded bar was hot forged, solutionized and was subject to aT4 treatment successively, under the same conditions as those described in Run
No. 4. A fatigue test was carried out on the resultant bar.
The results of the fatigue tests carried out in Run Nos. 4 and 5 are shown in Fig. 14. Since the stress levels in the connecting rod are locally varied within the planes across the connecting rod, the ordinate axis of Fig. 1 4 indicates not the stress but test load. It is clear from Fig. 14 that the forged material produced by Run No. 4 exhibits a remarkably excellent fatigue strength as compared with the forged material produced by Run No. 5. The superiority of the material of Run No. 4 to the material of
Run No. 5 is probably ascribable to the following.The material of Run No. 5 subjected to the forging is an extruded material having a fibrous texture developed during the extrusion, and the fibrous texture is broken up during the forging, with the result that the forged product cannot possess a normal fibrous texture, while the material of Run No. 4 subjected to the forging is a cast bar having a homogeneous internal structure and a macroscopically isotropic property, with the result that a normal fibrous structure is formed at any direction of forging force applied to the production of the connecting rod.
Example 5
Run No. 6 (invention)
An aluminum alloy melt comprising 3.0 wt% of magnesium, 0.25 wt% of chromium, 0.18 wt% of iron, 0.1 5 wt% of silicon, 0.01 wt% of titanium and the balance consisting essentially of aluminum was prepared and the melt was cast into a round bar having a diameter of 62 mm. The casting was carried out by the gas-pressure applying type hot top continuous casting and the solidification speed was 15 C/sec.
Run No. 7 (control)
The same procedures as those described in Run No. 6 were repeated, except that a solidification speed of 0.10 C/sec was used.
Run No. 8 (control)
The same procedures as those described in Run No. 6 were repeated, except that a soliditication speed of 30C/sec was used.
From each of the round bars obtained by Run Nos. 6, 7 and 8, specimens were cut out along the longitudinal direction of the bars at varying distances from the outer periphery. Each of the specimens was homogenized at a temperature of 5250C for 6 hours. Then, the tensile strength and the elongation of the specimens were determined at normal temperature. The results are shown in Fig. 1 5.In Fig. 1 5, the symbol "X" denotes a specimen from Run No. 6 (15 C/sec), the symbol "" denotes a specimen from Run No. 7 (0.1 00 C/sec) and the symbol "0" denotes a specimen from Run No. 8 (3 C/sec). As is apparent from Fig. 15, in the case of solidification speeds of 0.1 00C/sec and 30C/sec, a considerable scattering of tensile strength and elongation is noted between the outer periphery and central portions.
In the case of a solidification speed of 15 C/sec, there is little scattering in both tensile strength and elongation between the outer periphery and central portions. This suggests an almost uniform property of the cast bar from the outer periphery to central portions. Also, the DAS, the second phase particle size and the solute concentration ratio a/b of the case bar obtained by Run Nos. 6, 7 and 8 were determined. The results are shown in Table 2.
Table 2
Solidification Size ofsecondary Solute
speed DAS phase particle concentration OC/sec jam jam ratio a/b %
Run No.7 0.10 35 20 38
Run No.8 3 22 14 52
Run No.6 15 13 7 73
As is apparent from Table 2, in the case of a solidification speed of 1 50 C/sec, both DAS and
second phase particles are fine-sized and the solute concentration ratio a/b is high, while in the case of
solidification speeds of 0.1 00C/sec and 30C/sec, both DAS and second phase particles are significantly
coarse and the solute concentration ratio a/b is low.In view of these results and the test results shown
in Fig.14, it is clear that these structure factors have a great influence on the tensile strength and the
elongation of the bar.
Example 6
An alloy melt comprising 5.8 wt% of magnesium, 0.20 wt% of chromium, 0.20 wt% of
manganese, 0.013 wt% of tatal of titanium and boron and the balance consisting essentially of
aluminum was prepared, and was cast into a round bar having a diameter of 78 mm.
The casting was carried out by the gas-pressure applying type hot top continuous casting and the
solidification speed was varied as shown in Fig. 1 6. The resultant cast bar was homogenized at a
temperature of 5300C for 8 hours to produce test specimens.
A wedge specimen as shown in Fig. 8A was cut out from each test specimen. The wedge
specimen was subjected to a hot-forging operation at a temperature of 300, 400 and 4500 C, respectively, thereby to determine a limitative working degree at which forging cracks were produced
on the specimen. The results are shown in Fig. 1 6. In Fig.16, the obliquely-lined region above the
polygonal lines indicates levels of the working degree, above which forging cracks occur. As is
apparent from Fig. 1 6, the limitative working degree is increased as the forging temperature is
increased. Also, in all levels of the forging temperatures, as the solidification speed is increased, the
limitative working degree is increased and forging cracks are unlikely to occur.Particularly, the limitative working degree change with the increase in the solidification speed displays a prominent increase at a solidification speed of about 1 SOC/sec. This fact corresponds to an abrupt change in the structure of a cast bar at a solidification speed of about 1 SOC/sec as described above.
In addition, in order to evaluate the workability at general hot working including rolling and forging of each test specimen produced at various solidification speeds, the test specimens were subjected to a hot-torsion test according to the same procedures as those used in Example 2 to determine the deformation resistance and the deformability thereof. The results are shown in Fig. 1 7.
As is apparent from Fig. 17, the deformation resistance change with the solidification speed increase displays a remarkable decrease at a solidification speed of about 1 50 C/sec, and the deformability change with the solidification speed increase displays a prominent increase at a solidification speed of about 1 SOC/sec. In view of these results, it is clear that the cast bar according to the present invention exhibits excellent workability.
Example 7
An alloy melt comprising 2.3 wt% of magnesium, 0.15 wt% of chromium, 0.20 wtSo of manganese, 0.015 wt% of titanium and the balance consisting essentially of aluminum (the alloy referred to as alloy D), an melt alloy comprising 3.5 wt% of magnesium, 0.25 wt% of chromium, 0.15 wt% of manganese, 0.012 wt% of titanium and the balance consisting essentially of aluminum (the alloy referred to as alloy E), and an alloy melt comprising 5.8 wt% of magnesium, 0.30 wt% of chromium, 0.01 wt% of manganese, 0.015 wt% of total of titanium and boron and the balance consisting essentially of aluminum (the alloy referred to as alloy F) were separately prepared.Each of these melts were cast into a round bar having a diameter of 53 mm.
The casting was carried out by the gas-pressure applying type hot top continuous casting and the solidification speed was varied as shown in Fig. 18. In preparing the alloy F, the addition of Ti and B to the melt was carried out by using a master alloy comprising 5 wt% of titanium, 0.7 wt% of boron and the balance consisting essentially of aluminum.
The DAS of each of the cast bars prepared above was determined. The results are shown in Fig.
18. As is clearly shown in Fig. 18, the DAS change the alloys D, E and F with the solidification speed increase displays a decrease up to approximately 1 50C/sec of the solidification speed, and the DAS assumes an almost constant value at a solidification speed above 1 SOC/sec which is, therefore, a critical solidification speed. This clearly indicates that a solidification speed of 1 SOC/sec is significant for the fine structure of an AA standard 5000 series alloy, that is,15 C/sec is a critical solidification speed at which the structure of the such alloy becomes fine.
In addition, the melt of alloy E was cast into the bars at various solidification speeds and the tensile strength and elongation of the bars were measured. The results are shown in Fig. 1 9. It was confirmed from Fig. 1 9 taking into consideration Fig. 1 8 that both tensile strength and elongation are increased with the increase in correspondance with the DAS values. Particularly, an increase in elongation is outstandingly shown. Furthermore, the cast bars produced from the alloy E at various solidification speeds were subjected to an impact test and a drawing test. The results are shown in Fig.
20. It was also confirmed that the solidification speed of 1 50C/sec causes a prominent increase of the mechanical properties, i.e. the impact value and the reduction of area.
Example 8
The forgeability of the AA standard 5000 series alloys with the structure and composition of the present invention will be illustrated.
Ten alloy melts of the Al-Si-Mg type and Al-Cu-Si-Mg type alloys according to the present invention were separately prepared. These ten types of alloys are designated as G, H, I, J, K, L, M, N, O and P, respectively. Each of these melts was cast into a small diameter billet having a diameter of 50 mm by a semi-continuous casting process at a solidification speed of from 26 to 300C/sec, the resultant billets had a DAS ranging from 8 to 14 jam and an average DAS of 12 jam. Also, the billets had an average grain diameter of 120 jam.
For comparison purposes with the AA standard 5000 series alloy three melts of AA 2014, 2017 and 4032 alloys, which have widely been used, were subjected to a conventional semi-continuous casting process, thereby to produce billets having a diameter of 8 inches. The billets were homogenized and, then, extruded into bars having a diameter of 30 mm. The extruded bars were used as starting material for forging.
Each of the billets and the extruded bars were machined to manufacture specimens for wedge test as shown in Fig. 8A. The results are shown in Table 3, together with the alloy compositions and the percentage of an area of the second phase particles. The specimens were forged at a temperature of 2000C. The percentage of an area of the second phase particles was determined according to a voltage integration procedure by using an area analyzer.
Table 3 clearly indicates that the cast bars of the present invention exhibit a limitative working degree similar or superior to that of the extruded bars of the control alloys and thus, is excellent in forgeability. Also, Table 3 shows that the forgeability of the cast bars of the present invention is enhanced as the percentage of an area of the second phase particles in decreased.
Table 3
Percentage of area of Limitativ Composition (wt%) secondary working phase par- degree Alloy Si Cu Mg Ti V Mn Be Cr Zr ticles (%) (%) Invention G 2.0 - 1.3 0.015 - - - 0.2 0.2 6.8 85 H 6.0 - 0.9 0.015 - - - - - 12.5 83 i 8.0 - 1.0 0.02 - - - - 0.2 14.5 79 J 11.7 - 1.3 0.02 - - - - - 21.7 70 K 2.0 5.0 0.9 0.015 - - - - - 12.5 84 L 4.0 4.5 1.0 - - - - - - 17.3 83 M 6.0 3.0 1.0 0.015 - - - - - 19.3 72 N 10.0 2.0 0.7 0.015 - - - - 0.2 20.1 76 O 11.5 2.0 0.9 0.015 - - - - - 23.2 70 P 11.5 2.0 0.9 0.015 - - - 0.3 0.2 24.7 68 Control Q 0.6 4.5 0.6 0.01 - - 0.8 - - 5.2 69 R 0.4 4.0 0.5 0.01 - - 0.8 - - 4.7 83 S 12.0 0.9 1.0 0.01 - Ni= 1.0 - - 23.8 32 Note: K: 2014, L: 2017, M: 4032
Example 9
Melts of four types of the AA standard 5000 series alloys of the present invention were cast into four billets having a DAS different from each other by a semi-continuous casting process at various solidification speeds. The limitative working degree of these billets was determined according to the same procedure as that described in Example 1.Melts of six types of control alloys including a hyper eutectic Al-Si-Cu-Mg type were cast into six billets having a DAS different from each other using semicontinuous casting process at various solidification speeds. The limitative working degree of these six billets was determined in the same manner.The solidification speed of the alloys T, U, V and W was 300 C/sec, that of the alloys X and Y was 270C/sec, and that of the alloys Z, AA, AB and AC was in the range of from 8 to 1 00C/sec. As is apparent from Table 4, the forgeability is poor, when the alloy billets have an area percentage of the second phase particles more than 25% or when the alloy billets have
DAS of more than 20 jam. Also, although alloys X and Y having a composition outside the present invention were cast at the solidification speed of the present invention, the resultant billets had an area percentage of the second phase particles higher than 25% and thus, extremely poor forgeability. Table 4
Ares per centage of Limitative Composition (wt%) second phase working Particles DAS degree Alloy Si Cu Mg T@ V Mn Be Cr Zr % m % This T 6.0 - 0.9 0.015 - 0.2 - 0.2 0.2 13.0 12 82 invention U 12.7 - 1.3 0.015 0.4 - - - - 22.0 12 71 V 4.0 4.5 1.2 0.02 - - - 0.2 - 18.0 13 81 W 11.5 4.0 1.0 0.02 - - - 0.2 - 24.0 15 70 Control X 14.0 3.0 1.0 0.02 - - - - - 26.5 12 49 Y 18.0 4.5 0.5 0.02 - 0.1 - - - 34.5 13 35 Z 6.0 - 0.9 0.015 - 0.2 - 0.2 0.2 13.5 22 48 AA 11.7 - 1.3 0.015 0.4 - - - - 22.3 25 31 AB 11.5 4.0 1.0 0.02 - - - 0.2 - 24.5 24 32 AC 18.0 4.5 0.5 0.02 - 0.1 - - - 35.2 21 27 Example 10
Size of second phase particles including primary silicon crystals of the alloy corresponding to the alloy W described in Table 4 was changed by adding phosphorous, as a refining agent, in an amount of from 0.1 to 30 ppm to the alloy and by varying the solidification speed during the casting operation of the alloy. Fig. 21 shows how the forgeability was influenced by such size. The forgeability is indicated in terms of a limitative working degree at a forging temperature varying from 200 to 4500 C. Referring to Fig. 21, it will be understood that, when the size of the second phase particles exceed 50 jam, the forgeability of the alloy ingot is considerably low. The size of the second phase particles has therefore a great influence on the forgeability.
Example 11
In this example, the wear resistance of the alloy of the present invention will be discussed. Before going into the description of the experiment by the present inventors, a general knowledge of a wearresistant aluminum alloy is described. It is known that an aluminum alloy containing a high content of silicon exhibits a high wear resistance but is inferior in workability. One example of such an alloy is an A 390 alloy comprising 18 wt% of silicon, 45 wt% of copper, 0.5 wt% of magnesium, 0.1 wt% of manganese, 0.02 wt% of titanium and the balance consisting essentially of aluminum.
The inferior workability of the wear-resistant aluminum alloy previously known is coincident with the results given in Table 4. Namely, the alloys falling within the composition range A 390 alloys are indicated in Table 4 as alloys Y and AC both exhibiting remarkably inferiorforgeability. This is because, according to opinion of the present inventors, the precipitated amount of the primary silicon crystals is too large to provide the alloy with a satisfactorily low area ratio of the second phase particles.
Now, referring to Table 5, alloys cast by a continuous casting process at a solidification speed of 300C/sec, and then subjected to a wear resistance test are shown. The resultant cast bars had a DAS of 1 3 jam, an area ratio of the second phase particles of 1 8% and an average grain diameter of crystal grains (2-Al) of 120 jam.
Specimens of comparison alloys AC-8A and 99.7% Al were sampled out from the JIS H boatbottom shaped permanent mold and a specimen of a 4032 alloy was sampled out from a billet having a diameter of 1 50 mm. The 99.7% Al specimen was tested as cast, while these the AC-8A specimens were solutionized at a temperature of 5000C for 6 hours and, then, cooled in hot water having a temperature of 600C, and, finally, aged at a temperature of 1 600C for 8 hours thereby to produce T6 materials.
The wear resistance of the above mentioned specimens was determined under no lubricant condition by using an Ogoshi type rapid wear testing machine. The results are shown in Fig. 22.
Referring to Fig.22, it is clear that the alloys of the present invention exhibit a much more excellent wear resistance than the conventional typical wear resistant alloys.
Example 12
In this example, the alloy cast bars having the composition given in Table 5 were subjected to a tensile strength testing machine at a temperature of from normal temperature to 4000C.
Table 5
Composition (wit%) Alloy Si Cu Mg Ni Ti V Mn Be Cr Zr This AD 11.7 - 1.3 - 0.02 - 0.2 - 0.2 0.2 invention AE 11.5 4.0 1.0 - 0.02 - - - - - AF 8.0 5.0 1.0 - 0.02 - - - - - Com- AG 12.0 1.2 1.0 2.0 0.1 - 0.2 0.004 parison AH 12.0 0.9 1.0 1.0 0.01 - - - - Al 99.7%Al Note... AG:AC-8A, (JIS H 5202-1971) AH: 4032
The results of the tensile strength test of the alloys shown in Table 5 are shown in Fig. 23. As can be seen in Fig. 23, the present alloy (AD) exhibits a tensile strength exceeding 45 kg/mm2 at normal temperature and further, it exhibits a much higher tensile strength at elevated temperature than the 4032 alloy which is a typical heat resistant alloy material forforgings. In this manner, the alloy of the present invention is also very excellent in tensile strength.
Example 13
An aluminum alloy melt comprising 4.0 wt% of copper, 0.6 wt% of magnesium 0.3 wt% silicon, 0.6 wt% mangan, 0.02 wt% titanium, and the balance consisting essentially of Al was prepared, and the melt was cast into a round bar having a diameter of 53 mm. The casting was carried out by the gas-pressure applying hot top continuous casting and the solidification speed was 300 C/sec. For comparison purpose, round bar having a diameter of 53 mm was produced according to the same procedures as those described above, except that the gas pressure was not applied to the cast melt body.
The existence and non existence of the gas-pressure application caused a change in the surface of the cast bars. The influence of the surface on the forgeability was investigated by the method illustrated in Figs. 24A, B and C. That is, a billet 11 having diameter of 53 mm and a length of 140 mm was subjected to upsetting by using a hammer 10, then, the free surface was observed to determine whether or not 11 a, cracks were formed. In the case of no application of gas pressure, the resultant cast bar has a lapping surface or a bleb surface and tends to generate cracks on the free surface of the ingot at the first and second steps shown in Figs. 24A and 248. Microscope inspection of the structure of this cast bar indicated that defects such as cracks, pinholes, and blow holes, were sporadically present in the vicinity of the surface of cast bar. These defects are responsible for the notch effect, causing cracks during forging. In contrast, in the cast of application of gas pressure, the resultant cast bar has a smooth surface and tends not to crack in the three steps shown in Figs. 22A through 22C. In this case, forging without surface defects was obtained.
Claims (14)
1. A cast bar of an aluminum base alloy for forgings, exhibiting excellent workability and wearand heat-resistances, which comprises 4.0 to 12.0 wt% of silicon, 0.6 to 1.3 wt% of magnesium, and which has a fine cast structure, in which the primary crystals have a size of not greater than 50 jam, preferably, not greater than 25 jam, the intermetallic compounds of second phase particles have a size of not greater than 1 5 jam and the DAS is not greater than 20 jam.
2. A cast bar according to claim 1, wherein said aluminum base alloy further comprises at least one member selected from the group consisting of 0.05 to 0.2 wt% of titanium, 0.02 to 0.2 wt% of vanadium, 0.01 to 0.1 wt% of lithium, 0.001 to 0.05 wt% of beryllium, 0.1 to 0.5 wt% of chromium and 0.02 to 0.2 wt% of zirconium, with the proviso that the total of these members is not greater than 1.2 wt%.
3. A cast bar of an aluminum base alloy for forgings, exhibiting excellent workability and wearand heat-resistances, which comprises 2 to 1 2 wt% of silicon, 1.5 to 5.0 wt% of copper, and 0.8 to 1.3 wt% of magnesium, and which has a fine cast structure, in which the primary crystals have a size of not greater than 50 jam, preferably, not greater than 25 jam, the intermetallic compounds have a size of not greater than 1 5 jam and the DAS is not greater than 20 jam.
4. A cast bar according to claim 3, wherein said aluminum base alloy further comprises, at least one member selected from the group consisting of 0.05 to 0.2 wt% of titanium, 0.02 to 0.2 wt% of vanadium, 0.01 to 0.1 wt% of lithium, 0.001 to 0.05 wt% of beryllium, 0.1 to 0.5 wt% of chromium and 0.02 to 0.2 wt% of zirconium, with the proviso that the sum of these members is pot greater than 1.2 wt%.
5. A cast bar according to claim 1 or 4, characterized in that, the area occupied by the second phase particles comprising the primary crystals and intermetallic compounds does not exceed 25% at any region of the examined cross section of the cast bar.
6. A process for producing a cast bar of an aluminum base alloy for forgings, which comprises 4.0 to 12.0 wt% of silicon, 0.6 to 1.3 wt% of magnesium, said process comprises preparing a melt of the alloy composition, and continuously casting the melt at a solidification speed of not lower than 250C/sec.
7. A process for producing a cast bar of an aluminum base alloy for forgings, exhibiting excellent workability and wear- and heat-resistances, which comprises 2 to 1 2 wt% of silicon, 1.5 to 5.0 wt% of copper, and 0.8 to 1.3 wt% of magnesium, said process comprises preparing a melt of the alloy composition and continuously casting the melt at a solidification speed of not lower than 250 C/sec.
8. A cast bar of an aluminum base alloy for wrought products exhibiting high tensile strength, impact resistance and fatigue strength, which comprises 2.0 to 9.0 wt% of copper, 0.2 to 1.2 wt% of magnesium, 0.2 to 1.2 wt% of silicon, 0.2 to 0.8 wt% of manganese, and the balance consisting of aluminum and unavoidable impurities, and wherein the DAS, i.e. secondary dendrite arm spacing, is not greater than 1 5 jam, the grain diameter is not greater than 80 jam and the second phase particles comprising intermetallic compounds have a size not greater than 10 jam.
9. A cast bar of an aluminum base alloy for wrought products, exhibiting high tensile strength, impact strength and fatigue strength, which comprises 2.0 to 9.0 wt% of copper, 0.2 to 1.2 wt% of magnesium, 0.2 to 1.2 wt% of silicon, 0.2 to 0.8 wt% of manganese, and the balance consisting of aluminum and unavoidable impurities, and wherein the ratio of the concentration (a) of the solute components in the matrix within the crystal grain to the concentration (b) of the solute components in the grain boundaries, i.e. a/b, is not smaller than 0.70.
10. A cast bar of an aluminum base alloy for wrought products, exhibiting high tensile strength, impact resistance and fatigue strength, comprising 2.0 to 6.0 wt% of magnesium, 0.03 to 0.3 wt% of chromium, and wherein, the grain diameter is not greater than 80 jam, the DAS is not greater than 1 3 jam and the size of the second phase particles is not greater than 10 jam.
11. A cast bar according to claim 10, wherein said aluminum base alloy further comprises at least one member selected from the group consisting of 0.005 to 0.2 wt% of titanium, a total amount of not more than 0.2 wt% of titanium and boron, 0.5 wt% of manganese, not more than 0.3 wt% of zirconium and not more than 0.5 wt% of tin.
12. A cast bar of an aluminum base alloy for wrought products, exhibiting high tensile strength, impact resistance and fatigue strength, comprising 2.0 to 6.0 wt% of magnesium, and 0.03 to 0.3 wt% of chromium, and wherein the ratio of the concentration (a) of the solute components in the matrix within the crystal grain to the concentration (b) of the solute components in the grain boundaries, i.e.
a/b, is not smaller than 0.70.
13. A cast bar according to claim 11 or 12, wherein said alloy further comprises at least one member selected from the group consisting of 0.005 to 0.2 wt% of titanium, not more than 0.5 wt% of manganese, not more than 0.3 wt% of zirconium and not more than 0.5 wt% of tin.
14. A process according to claim 10, substantially as hereinbefore described with reference to the Examples.
14. A cast bar according to claim 13, wherein said titanium is partly replaced with boron so that the total amount of titanium and boron is not more than 0.2%.
1 5. A cast bar according to claim 1, 2,3,4, 8, 9, 10, 11, 12, 1 3 or 14, characterized in that the cast bar is for use as machining in the heat treated- or non-heat treated state.
16. A cast bar according to claim 1, 2, 3, 4, 8, 9, 10, 11, 12, 1 3 or 14, characterized in that the cast bar has a diameter of not greater than 100 mm.
17. A cast bar according to claim 16, characterized in that the cast bar has a diameter of from 5 to 70 mm.
1 8. A process for producing a cast bar of an aluminum base alloy which comprises 2.0 to 9.0 wt% of copper, 0.2 to 1.2 wt% of magnesium, 0.2 to 1.2 wt% of silicon, 0.2 to 0.8 wt% of manganese, said process comprising preparing a melt of the alloy composition and continuously casting the melt at a solidification speed of not lower than 25"C/sec.
19. A process according to claim 1 8, further comprising subjecting the cast bar to a homogenizing heat treatment at a temperature of from 450 to 5300C over a period of from 0.5 to 20 hours.
20. A process for producing a cast bar of an aluminum base alloy for forgings, comprising 2.0 to 6.0 wt% of magnesium, and 0.03 to 0.3 wt% of chromium, said process comprises preparing a melt of the alloy composition and continuously casting the melt at a solidification speed of not lower than 15 C/sec.
21. A process according to claim 20 further comprising subjecting the cast bar to a homogenizing treatment at a temperature of from 450 to 5800C over a period of from 1 to 24 hours.
22. A process for producing the cast bar according to claim 21 , wherein the solidification speed is not lower than 350C/sec.
New claims filed on 17 October 1983.
Superseded claims 1-22 New or amended claims:
1. A cast bar of an aluminum base alloy for forgings, exhibiting excellent workability and wearand heat-resistances, which comprises 4.0 to 12.0 wt% of silicon, 0.6 to 1.3 wt% of magnesium, and which has a fine cast structure in which the second phase particles comprising the primary crystals and the intermetallic compounds have a size not greater than 50 jam and the secondary dendrite arm spacing is not greater than 20 jam.
2. A cast bar according to Claim 1, wherein said aluminum base alloy further comprises at least one member selected from 0.05 to 0.2 wt% of titanium, 0.02 to 0.2 wt% of vanadium, 0.01 to 0.1 wt% of lithium, 0.001 to 0.05 wt% of beryllium, 0.1 to 0.5 wt% of chromium and 0.02 to 0.2 wt% of zirconium, with the proviso that the total of these members is not greater than 1.2 wt%.
3. A cast bar of an aluminum base alloy for forgings, exhibiting excellent workability and wearand heat-resistances, which comprises 2 to 1 2 wt% of silicon, 1.5 to 5.0 wt% of copper, and 0.8 to 1.3 wt% of magnesium, and which has a fine cast structure, in which the second phase particles comprising the primary crystals and the intermetallic compounds have a size no greater than 50 jam and the second dendrite arm spacing is not greater than 2 jam.
4. A cast bar according to claim 3, wherein said aluminum base alloy further comprises, at least one member selected from 0.05 to 0.2 wt% of titanium, 0.02 to 0.2 wt% of vanadium, 0.01 to 0.1 wt% of lithium, 0.001 to 0.05 wt% of beryllium, 0.1 to 0.5 wt% of chromium and 0.02 to 0.2 wt% of zirconium, with the proviso that the sum of these members is not greater than 1.2 wt%.
5. A cast bar according to any preceding claim, wherein the area occupied by the second phase particles and the primary crystals does not exceed 25% at any region of the examined cross section of the cast bar.
6. A cast bar according to any preceding claim, wherein the cast bar is for use as machining in the heat treated- or non-heat treated state.
7. A cast bar according to any one of claims 1 to 5, wherein the cast bar has a diameter of not greater than 100 mm.
8. A cast bar according to any preceding claim, wherein the primary crystals have a size of not greater than 25 jam.
9. A process for producing a cast bar of an aluminum base alloy for forgings, which comprises 4.0 to 12.0 wt% of silicon, 0.6 to 1.3 wt% of magnesium, wherein said process comprises preparing a melt of the alloy composition, and continuously casting the melt at a solidification speed of not lower than 250C/sec.
1 0. A process for producing a cast bar of an aluminum base alloy for forgings, exhibiting excellent workability and wear- and heat-resistances, which comprises 2 to 12 wt% of silicon, 1.5 to 5.0 wt% of copper, and 0.8 to 1.3 wt% of magnesium, wherein said process comprises preparing a melt of the alloy composition and continuously casting the melt at a solidification speed of not lower than 250C/sec.
11. A cast bar according to claim 1, substantially as hereinbefore described with reference to the
Examples.
1 2. A cast bar according to claim 3, substantially as hereinbefore described with reference to the
Examples.
1 3. A process according to claim 9, substantially as hereinbefore described with reference to the
Examples.