GB1518649A - Sintered self-lubricating article - Google Patents
Sintered self-lubricating articleInfo
- Publication number
- GB1518649A GB1518649A GB24790/77A GB2479077A GB1518649A GB 1518649 A GB1518649 A GB 1518649A GB 24790/77 A GB24790/77 A GB 24790/77A GB 2479077 A GB2479077 A GB 2479077A GB 1518649 A GB1518649 A GB 1518649A
- Authority
- GB
- United Kingdom
- Prior art keywords
- sintered self
- graphite
- sintered
- lubricating
- article
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1518649 Sn-Zn-graphite-Cu bearing alloy OILES INDUSTRY CO Ltd 22 Oct 1975 24790/77 Divided out of 1519289 Heading C7A A sintered self lubricating composition containing:- The composition may be prepared by mixing Sn, graphite, Cu, Zn and/or Brass powder, moulding and sintering in a non-oxidizing atmosphere e.g. hydrogen or natural gas at 750-830‹C for 30-60 minutes and may be used in bushes for high temperature bearings where good dimensional stability is required.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB24790/77A GB1518649A (en) | 1975-10-22 | 1975-10-22 | Sintered self-lubricating article |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB24790/77A GB1518649A (en) | 1975-10-22 | 1975-10-22 | Sintered self-lubricating article |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1518649A true GB1518649A (en) | 1978-07-19 |
Family
ID=10217285
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB24790/77A Expired GB1518649A (en) | 1975-10-22 | 1975-10-22 | Sintered self-lubricating article |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB1518649A (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2317899A (en) * | 1996-10-02 | 1998-04-08 | Westaim Technologies Inc | Abradable seal assembly |
CN113430421A (en) * | 2021-07-02 | 2021-09-24 | 中国科学院兰州化学物理研究所 | High-strength nickel-niobium-based wide-temperature-range self-lubricating alloy |
-
1975
- 1975-10-22 GB GB24790/77A patent/GB1518649A/en not_active Expired
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2317899A (en) * | 1996-10-02 | 1998-04-08 | Westaim Technologies Inc | Abradable seal assembly |
US5976695A (en) * | 1996-10-02 | 1999-11-02 | Westaim Technologies, Inc. | Thermally sprayable powder materials having an alloyed metal phase and a solid lubricant ceramic phase and abradable seal assemblies manufactured therefrom |
GB2317899B (en) * | 1996-10-02 | 2000-09-20 | Westaim Technologies Inc | Abradable seal assembly |
CN113430421A (en) * | 2021-07-02 | 2021-09-24 | 中国科学院兰州化学物理研究所 | High-strength nickel-niobium-based wide-temperature-range self-lubricating alloy |
CN113430421B (en) * | 2021-07-02 | 2022-06-10 | 中国科学院兰州化学物理研究所 | High-strength nickel-niobium-based wide-temperature-range self-lubricating alloy |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB1519289A (en) | Sintered self-lubricating article | |
GB1470118A (en) | Self-lubricating sintered compotite materials | |
ES463769A1 (en) | Process for manufacturing iron based powder | |
GB1518649A (en) | Sintered self-lubricating article | |
GB1409921A (en) | Solid lubricant | |
GB1441768A (en) | Method of making bearing bushes | |
JPS5732304A (en) | Production of glass grinding sheet | |
GB797365A (en) | Improvements in or relating to lubricants | |
SE7700125L (en) | PROCEDURE FOR MANUFACTURE OF HIGH COAL HARD ALLOYS | |
GB1223641A (en) | Solid lubricant composites | |
GB936938A (en) | Sintered bearings and methods of making them | |
JPS55134102A (en) | Cu-base sintered bearing of high graphite content and production thereof | |
GB1420813A (en) | Copper alloys | |
JPS54131528A (en) | High-strength, high-oil content, sintered oil-containing bearing | |
JPS5610002A (en) | Lubricating piece for slider of pantograph collector | |
FR2095726A5 (en) | Self-lubricating bearing materials - from compressed and sintered mixtures of metal, lubricant and metallic soaps | |
GB1162573A (en) | Improvements in or relating to Metal Powders | |
ES460045A1 (en) | Method of manufacturing sintered components | |
JPS54148110A (en) | Manufacture of sintered copper alloy product | |
GB704035A (en) | Bearings and the like | |
GB1281164A (en) | Improvements in and relating to ferrous alloys | |
JPS56102534A (en) | Manufacture of sintered lead bronze alloy with high wear resistance | |
GB1000651A (en) | Improvements in or relating to metal powders | |
JPS56156703A (en) | Manufacture of sintered alloy | |
GB1496843A (en) | Self lubricating bearings |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PS | Patent sealed | ||
PCNP | Patent ceased through non-payment of renewal fee |