GB1501445A - Silica-containing porous bodies of controlled pore size - Google Patents
Silica-containing porous bodies of controlled pore sizeInfo
- Publication number
- GB1501445A GB1501445A GB5068/75A GB506875A GB1501445A GB 1501445 A GB1501445 A GB 1501445A GB 5068/75 A GB5068/75 A GB 5068/75A GB 506875 A GB506875 A GB 506875A GB 1501445 A GB1501445 A GB 1501445A
- Authority
- GB
- United Kingdom
- Prior art keywords
- solution
- silicate solution
- sio
- balance
- sodium silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1501445 Porous bodies CORNING GLASS WORKS 6 Feb 1975 [8 Feb 1974] 5068/75 Heading C1A A method of making a porous silica-containing body exhibiting a compressive strength greater than 50 p.s.i., having a pore diameter ranging from 100 Š to 1 micron, and wherein at least 80% of the pores therein fall within Œ30% of the average pore diameter value comprises: (a) providing solutions having apH of from 10 to 15 and containing from 1 to 12 moles SiO 2 /litre in solution from silicate solutions selected from lithium polysilicate, sodium silicate, potassium silicate, quaternary ammonium silicate and colloidal silica; (b) combining the said solutions in one of the indicated proper proportions equivalent to: (A) a weight ratio of from 19:1 to 1:4 potassium silicate solution to colloidal silica solution, wherein the said potassium silicate solution consists essentially of 8À3% K 2 O, 20À8% SiO 2 , balance H 2 O and the said colloidal silica solution consists essentially of 40% SiO 2 , balance H 2 O; (B) a weight ratio of from 1:9 to 1:3 sodium silicate solution to colloidal silica solution, wherein the said sodium silicate solution consists essentially of 6À8% Na 2 O, 25À3% SiO 2 , balance H 2 O and the colloidal silica solution is that defined in (A); (C) a weight ratio of from 9:1 to 1:4 potassium silicate solution and/or sodium silicate solution to quaternary ammonium silicate solution, wherein the said potassium silicate solution is that defined in (A), the said sodium silicate solution is that defined in (B), and the said quaternary ammonium silicate solution consists essentially of 9À9% quaternary ammonium ions, 45% SiO 2 , balance H 2 O; (D) a weight ratio of from 19:1 to 1:4 potassium silicate solution and/or sodium silicate solution to lithium polysilicate solution, wherein the said potassium silicate solution is that defined in (A), the said sodium silicate solution is that defined in (B), and the said lithium polysilicate solution consists essentially of 2À1% Li 2 O, 20% SiO 2 , balance H 2 O; in the absence of other oxide species soluble in the solutions; (c) reacting an organic compound therewith selected from formaldehyde, paraformaldehyde, formamide, glyoxal, methyl formate, ethyl formate, methyl acetate, ethyl acetate, and mixtures thereof, at a temperature of from the freezing point to the boiling point of the solution for a sufficient period of time to polymerize the silica into a coherent, porous gelled body and; (d) leaching the said gelled body with a weakly acid solution. The body may also contain up to 70% by weight of an unreactive particulate material passing a 200 U.S. Standard Sieve selected from Alumina, Titania, Zirconia, Carbon, Silicon Carbide, Silicon Nitride, Iron Oxides and catalytically active transition metal oxides, or carbon-containing materials, preferably colloidal carbon, which are subsequently burnt out in a firing step at 600-800‹ C.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US44069374A | 1974-02-08 | 1974-02-08 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1501445A true GB1501445A (en) | 1978-02-15 |
Family
ID=23749795
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB5068/75A Expired GB1501445A (en) | 1974-02-08 | 1975-02-06 | Silica-containing porous bodies of controlled pore size |
Country Status (6)
Country | Link |
---|---|
JP (1) | JPS50115191A (en) |
CA (1) | CA1059975A (en) |
DE (1) | DE2503332C2 (en) |
FR (1) | FR2260547B1 (en) |
GB (1) | GB1501445A (en) |
NL (1) | NL7501483A (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5098576A (en) * | 1988-11-05 | 1992-03-24 | Merck Patent Gesellschaft Mit Beschrankter Haftung | Adsorbents for chromatography and adsorption processes |
WO2003099431A1 (en) * | 2002-05-24 | 2003-12-04 | Ppg Industries Ohio, Inc. | An attrition resistant silica carrier product |
WO2006013043A1 (en) * | 2004-07-29 | 2006-02-09 | Qiagen Gmbh | Monolithic shaped bodies for purifying and separating biopolymers |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4090887A (en) * | 1975-11-25 | 1978-05-23 | E. I. Du Pont De Nemours And Company | Pigmented microporous silica microspheres produced by a water in oil emulsion |
US4230679A (en) | 1978-12-22 | 1980-10-28 | E. I. Du Pont De Nemours And Company | Poly(silicic acid) |
DE4142902A1 (en) * | 1991-12-23 | 1993-06-24 | Sued Chemie Ag | Producing mouldings for catalytic use from pyrogenic silicic acid - by hydrothermally treating initially moulded body with ammonia contg. solution |
DE4142898A1 (en) * | 1991-12-23 | 1993-06-24 | Sued Chemie Ag | Pyrogenic silica moulding used as catalyst support or catalyst - prepd. from paste in aq. alcoholic ammonia by moulding, drying and calcining |
DE102009046257A1 (en) * | 2009-10-30 | 2011-05-12 | Carcoustics Techconsult Gmbh | Plate-like insulating layer for plate-like wall element of wall, particularly building wall, has plate-like foamed plastic which is open-cell or mixed cell and subset of cell of foamed plastic is filled with gel |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3678144A (en) * | 1970-06-12 | 1972-07-18 | Corning Glass Works | Silicate bodies containing coprecipitated oxides |
-
1974
- 1974-08-14 CA CA206,974A patent/CA1059975A/en not_active Expired
-
1975
- 1975-01-28 DE DE2503332A patent/DE2503332C2/en not_active Expired
- 1975-02-06 JP JP50015840A patent/JPS50115191A/ja active Pending
- 1975-02-06 GB GB5068/75A patent/GB1501445A/en not_active Expired
- 1975-02-07 NL NL7501483A patent/NL7501483A/en not_active Application Discontinuation
- 1975-02-07 FR FR7503875A patent/FR2260547B1/fr not_active Expired
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5098576A (en) * | 1988-11-05 | 1992-03-24 | Merck Patent Gesellschaft Mit Beschrankter Haftung | Adsorbents for chromatography and adsorption processes |
WO2003099431A1 (en) * | 2002-05-24 | 2003-12-04 | Ppg Industries Ohio, Inc. | An attrition resistant silica carrier product |
US7135429B2 (en) | 2002-05-24 | 2006-11-14 | Ppg Industries Ohio, Inc. | Attrition resistant carrier product |
WO2006013043A1 (en) * | 2004-07-29 | 2006-02-09 | Qiagen Gmbh | Monolithic shaped bodies for purifying and separating biopolymers |
EP1629887A1 (en) * | 2004-07-29 | 2006-03-01 | Qiagen GmbH | Monolithic shaped body for purification and separation of biopolymers |
AU2005268888B2 (en) * | 2004-07-29 | 2009-12-24 | Qiagen Gmbh | Monolithic shaped bodies for purifying and separating biopolymers |
US9017557B2 (en) | 2004-07-29 | 2015-04-28 | Qiagen Gmbh | Monolithic-shaped bodies for purifying and separating biopolymers |
Also Published As
Publication number | Publication date |
---|---|
FR2260547A1 (en) | 1975-09-05 |
FR2260547B1 (en) | 1980-03-21 |
DE2503332A1 (en) | 1975-08-14 |
CA1059975A (en) | 1979-08-07 |
JPS50115191A (en) | 1975-09-09 |
DE2503332C2 (en) | 1983-12-01 |
NL7501483A (en) | 1975-08-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR870009702A (en) | Dental prosthesis and its manufacturing method | |
GB1374273A (en) | Catalysis | |
GB989242A (en) | Catalysts for the synthesis of ammonia and methods of producing same | |
GB1501445A (en) | Silica-containing porous bodies of controlled pore size | |
GB1402801A (en) | Production of finely divided acicular magnetic iron oxides | |
GB1502003A (en) | Catalyst carrier method for preparing the catalyst carrier a catalyst containing the carrier and a hydrocarbon hydrodesulphurization process using the catalyst | |
JPS5742547A (en) | Preparation of optical glass part | |
ES462104A1 (en) | Aluminosilicate aquasols and powders | |
US3827893A (en) | Silicate bodies | |
ES8506548A1 (en) | Method of forming a glass or ceramic product. | |
GB1397198A (en) | Porous glass support material | |
GB1393039A (en) | Preparation of reinforcing amorphous silica | |
GB1352972A (en) | Ceramic sintering process | |
GB1287687A (en) | Cellulated glassy bodies and their method of manufacture | |
GB1274112A (en) | Improvements in or relating to the production of refractory material | |
GB1395561A (en) | Process for the production of spherical metal oxide or metal carbide particles | |
Wallace et al. | Metal organic‐derived 20L gel monoliths | |
GB1029057A (en) | Foundry sand compositions | |
GB1468565A (en) | Aqueous solutions of alkali metal polysilicates | |
GB1192237A (en) | Glass Forming Composition and process for preparing same | |
GB1188182A (en) | Hydrophilic Silica Sol | |
GB1137464A (en) | Process for improving soil | |
GB769719A (en) | Improvements in or relating to exothermic mixtures | |
GB1280397A (en) | Silica sols | |
GB1279465A (en) | Production of light-conducting fibres |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PS | Patent sealed | ||
PCNP | Patent ceased through non-payment of renewal fee |