GB1407240A - Refractory shapes - Google Patents

Refractory shapes

Info

Publication number
GB1407240A
GB1407240A GB5714572A GB5714572A GB1407240A GB 1407240 A GB1407240 A GB 1407240A GB 5714572 A GB5714572 A GB 5714572A GB 5714572 A GB5714572 A GB 5714572A GB 1407240 A GB1407240 A GB 1407240A
Authority
GB
United Kingdom
Prior art keywords
refractory
shapes
dec
grains
grain
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB5714572A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
STEETLEY Manufacturing Ltd
Original Assignee
STEETLEY Manufacturing Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by STEETLEY Manufacturing Ltd filed Critical STEETLEY Manufacturing Ltd
Priority to GB5714572A priority Critical patent/GB1407240A/en
Publication of GB1407240A publication Critical patent/GB1407240A/en
Expired legal-status Critical Current

Abstract

1407240 Refractory magnesia shapes STEETLEY (MFG) Ltd 11 Dec 1973 [11 Dec 1972] 57145/72 Addition to 1401282 Heading C1A A process for isostatically pressing a refractory magnesia grain material into a shape and then firing is disclosed, the materials being similar to the compositions of parent Specification 1,401,282, the grains having a particle size such that their surface area is from 0À10 to 0À90 m.<SP>2</SP>/gram. The refractory grain is preferably one which has been calcined or dead-burnt at, e.g. 1300‹ to 2000‹ C. and the material to be pressed will usually also contain some form of binder or lubricant such as methyl cellulose or a wax emulsion. Other refractory grains such as chrome ore zirconia or lime may be present. Typically the shapes are fired at temperatures in the range 1600‹ to 1900‹ C. and may be impregnated with tar or pitch afterwards. The shapes may take the form of bricks, crucibles etc.
GB5714572A 1972-12-11 1972-12-11 Refractory shapes Expired GB1407240A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB5714572A GB1407240A (en) 1972-12-11 1972-12-11 Refractory shapes

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB5714572A GB1407240A (en) 1972-12-11 1972-12-11 Refractory shapes

Publications (1)

Publication Number Publication Date
GB1407240A true GB1407240A (en) 1975-09-24

Family

ID=10478482

Family Applications (1)

Application Number Title Priority Date Filing Date
GB5714572A Expired GB1407240A (en) 1972-12-11 1972-12-11 Refractory shapes

Country Status (1)

Country Link
GB (1) GB1407240A (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0140221A2 (en) * 1983-10-31 1985-05-08 Shin Nihon Chemical Industry Co., Ltd. Magnesia clinker and method of producing the same

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0140221A2 (en) * 1983-10-31 1985-05-08 Shin Nihon Chemical Industry Co., Ltd. Magnesia clinker and method of producing the same
EP0140221A3 (en) * 1983-10-31 1987-01-07 Shin Nihon Chemical Industry Co., Ltd. Magnesia clinker and method of producing the same

Similar Documents

Publication Publication Date Title
GB1415431A (en) Monolithic refractory material
CA972769A (en) Refractory composition comprising coarse particles of clay or bauxite and carbon
GB1433915A (en) Alumina refractory composition
GB1407240A (en) Refractory shapes
SE7709752L (en) PROCEDURE FOR THE PRODUCTION OF BASIC REFRACTORY FEEDING
IE40377L (en) Refractory linings on hot metallurgical ladles.
ES480473A1 (en) Refractory dry ramming mix for lining crucible induction furnaces.
ES413829A1 (en) Fired refractory brick
GB1423596A (en) Silicon carbide-containing refractory bricks
DE658893C (en) Process for the production of refractory products with practically no shrinkage
ES331184A1 (en) A process for the manufacture of refractory bricks, especially not calcinated, of magnesite-chromium and of chrome-magnesium. (Machine-translation by Google Translate, not legally binding)
GB1450089A (en) High alumina refractories
GB1486352A (en) Method for making refractory articles
GB1327749A (en) Process of producing a sintered refractory material
GB1281771A (en) Furnace linings
CH615014A5 (en) Process for burning and sintering lumpy material such as lime, dolomite, magnesite or cement and shaft furnace for carrying out the process
SE311857B (en)
SU419496A1 (en)
GB1510949A (en) Process for the manufacture of fired refractory bricks
GB1137831A (en) Refractory materials
SU771064A1 (en) Refractory mass
GB1300714A (en) Refractories with a non-aqueous bond
SU423776A1 (en) MASS FOR THE MANUFACTURE OF ELECTRO-MELTED COGNI UFOROVI I I ^
GB1386825A (en) Burned basic refractory and batch therefor
Primachenko et al. The grain-size distribution of the chamotte and burn-out additive as a factor in the properties of semidry-molded light-weight refractories

Legal Events

Date Code Title Description
PS Patent sealed
PCNP Patent ceased through non-payment of renewal fee