GB1393116A - Hard metal articles and methods of treatment thereof - Google Patents
Hard metal articles and methods of treatment thereofInfo
- Publication number
- GB1393116A GB1393116A GB2526372A GB2526372A GB1393116A GB 1393116 A GB1393116 A GB 1393116A GB 2526372 A GB2526372 A GB 2526372A GB 2526372 A GB2526372 A GB 2526372A GB 1393116 A GB1393116 A GB 1393116A
- Authority
- GB
- United Kingdom
- Prior art keywords
- carbide
- sintering
- article
- weight ratio
- treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1393116 Sintered carbides bonded with cobalt ruthenium & asmium INTERNATIONAL NICKEL Ltd 26 May 1972 [28 May 1971 27 Aug 1971] 25263/72 and 40324/71 Divided out of 1393115 Headings C7D and C7F A cemented carbide article e.g. a cutting tool or tip in which the binder, at least at the cutting edge consists of Co together with an equal or lesser amount of Ru and/or Os. The cemented carbide consists of 97-80% WC, TiC, TaC or NbC with a weight ratio of Co:Ru of 1.5:1 to 6:1 or a weight ratio of Co:Os of 1:1 to 4:1. The article may be made by compacting and sintering a powder mixture of the carbide, Co, Os & Ru or by coating a green compact of the carbide and Co with a slurry of carbide, Co, Os and/or Ru and then sintering. Alternatively the green or sintered carbide - Co body may be coated with Ru and/or Os e.g. by electrolysis, plasma spraying, vanour deposition or from liquid bright Ru and diffusion at 1250-1400C.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB2526372A GB1393116A (en) | 1971-05-28 | 1971-05-28 | Hard metal articles and methods of treatment thereof |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB2526372A GB1393116A (en) | 1971-05-28 | 1971-05-28 | Hard metal articles and methods of treatment thereof |
GB1799271A GB1393115A (en) | 1971-05-28 | 1971-05-28 | Cutting tools and cutting processes |
GB4032471 | 1971-08-27 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1393116A true GB1393116A (en) | 1975-05-07 |
Family
ID=27257562
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB2526372A Expired GB1393116A (en) | 1971-05-28 | 1971-05-28 | Hard metal articles and methods of treatment thereof |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB1393116A (en) |
Cited By (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4610931A (en) * | 1981-03-27 | 1986-09-09 | Kennametal Inc. | Preferentially binder enriched cemented carbide bodies and method of manufacture |
USRE34180E (en) * | 1981-03-27 | 1993-02-16 | Kennametal Inc. | Preferentially binder enriched cemented carbide bodies and method of manufacture |
US5976707A (en) * | 1996-09-26 | 1999-11-02 | Kennametal Inc. | Cutting insert and method of making the same |
US7235211B2 (en) * | 2000-05-01 | 2007-06-26 | Smith International, Inc. | Rotary cone bit with functionally-engineered composite inserts |
US8440314B2 (en) | 2009-08-25 | 2013-05-14 | TDY Industries, LLC | Coated cutting tools having a platinum group metal concentration gradient and related processes |
US8512882B2 (en) | 2007-02-19 | 2013-08-20 | TDY Industries, LLC | Carbide cutting insert |
CN113444953A (en) * | 2021-06-30 | 2021-09-28 | 株洲硬质合金集团有限公司 | Hard alloy containing titanium and ruthenium and preparation method thereof |
-
1971
- 1971-05-28 GB GB2526372A patent/GB1393116A/en not_active Expired
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4610931A (en) * | 1981-03-27 | 1986-09-09 | Kennametal Inc. | Preferentially binder enriched cemented carbide bodies and method of manufacture |
USRE34180E (en) * | 1981-03-27 | 1993-02-16 | Kennametal Inc. | Preferentially binder enriched cemented carbide bodies and method of manufacture |
US5976707A (en) * | 1996-09-26 | 1999-11-02 | Kennametal Inc. | Cutting insert and method of making the same |
US7235211B2 (en) * | 2000-05-01 | 2007-06-26 | Smith International, Inc. | Rotary cone bit with functionally-engineered composite inserts |
US8397841B1 (en) | 2000-05-01 | 2013-03-19 | Smith International, Inc. | Drill bit with cutting elements having functionally engineered wear surface |
US8512882B2 (en) | 2007-02-19 | 2013-08-20 | TDY Industries, LLC | Carbide cutting insert |
US8440314B2 (en) | 2009-08-25 | 2013-05-14 | TDY Industries, LLC | Coated cutting tools having a platinum group metal concentration gradient and related processes |
CN113444953A (en) * | 2021-06-30 | 2021-09-28 | 株洲硬质合金集团有限公司 | Hard alloy containing titanium and ruthenium and preparation method thereof |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US5649279A (en) | Cemented carbide with binder phase enriched surface zone | |
GB1494544A (en) | Coated laminated carbide cutting tool | |
JPS6464703A (en) | Polycrystalline diamond tool | |
GB1297896A (en) | ||
DE3464063D1 (en) | Sintered alloy based on carbides, and article made from this alloy | |
ES8308589A1 (en) | Cemented carbides with binder enriched surface | |
GB1319913A (en) | Cermet alloy composition | |
EP1155158A1 (en) | Sintered cemented carbide body and use thereof | |
RU95113877A (en) | SINTERED POWDER MIXTURE FOR PRODUCTION OF MATERIAL AS BINDED CARBIDES ON A TUNGSTEN BASIS | |
GB1310381A (en) | Infiltrated cemented carbides | |
GB1393116A (en) | Hard metal articles and methods of treatment thereof | |
JPS6417836A (en) | Diamond sintered body and its production | |
GB1504547A (en) | Process for making alloyed steel sintered parts and sinter powder for use in the process | |
GB1291387A (en) | Improvements in or relating to the production of a coated sintered hard metal body | |
JP2000334608A (en) | Cutting insert and manufacture of same | |
GB1279303A (en) | Production of sintered nickel steels | |
GB1490773A (en) | Encapsulated shaped parts to be subjected to isostatic compression and process for their manufacture | |
GB1404752A (en) | Wear-resistant articles of hard material | |
GB1438728A (en) | Method of preparing metal alloy composite powders | |
GB1332451A (en) | Cemented carbide materials | |
JPS56152960A (en) | Tungsten carbide melt-spraying powder and its manufacture | |
JPS6479340A (en) | Hard alloy | |
GB1321807A (en) | Diamond compacts | |
GB1319144A (en) | Outlet nozzles for hot gases | |
Majagi et al. | Sintering of WC--10 Co Hard Metal Containing Intermetallic Compound |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PS | Patent sealed [section 19, patents act 1949] | ||
PE20 | Patent expired after termination of 20 years |