GB1352921A - Continuous process for preparing extruded alumina bodies - Google Patents
Continuous process for preparing extruded alumina bodiesInfo
- Publication number
- GB1352921A GB1352921A GB1589671*[A GB1352921DA GB1352921A GB 1352921 A GB1352921 A GB 1352921A GB 1352921D A GB1352921D A GB 1352921DA GB 1352921 A GB1352921 A GB 1352921A
- Authority
- GB
- United Kingdom
- Prior art keywords
- alumina
- slurry
- weight
- continuous process
- ammonium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1352921 Alumina catalyst carrier NALCO CHEMICAL CO 19 May 1971 15896/71 Heading C1A An alumina or silica-alumina catalyst carrier containing from 0-20% by weight silica is prepared in a continuous process in which a solution of an aluminate of an alkali metal (e.g. sodium aluminate) or ammonium, an acidic reagent (e.g. aluminium sulphate) and from 0-20% based on the dry weight of Al 2 O 3 produced of a silicate salt of an alkali metal (e.g. sodium silicate) or ammonium are reacted in an aqueous medium at a temperature within the range 70-135 C. and at a pH of from 5-12 while the concentration of alumina in the so formed slurry is maintained within the range 1-25% as Al 2 O 3 , the slurry is then filtered to increase the concentration of recovered solids to 10-20% by weight of Al 2 O 3 the precipitate dried at from 200-1,000 F. and the recovered precipitate in the form of a powder washed either before or after drying, wetted to form a slurry mix which is extruded to form pellets. An aldonate, e.g. gluconic acid may be added to the reaction mixture in an amount from 0À5-6% calculated as gluconic acid based on the dry weight of Al 2 O 3 . The extruded alumina bodies produced by this process may be used as catalyst carriers in fixed bed processes for hydrocracking, desulphurization and hydrogenation processes.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB1589671 | 1971-05-19 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1352921A true GB1352921A (en) | 1974-05-15 |
Family
ID=10067503
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB1589671*[A Expired GB1352921A (en) | 1971-05-19 | 1971-05-19 | Continuous process for preparing extruded alumina bodies |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB1352921A (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0130734A2 (en) * | 1983-06-20 | 1985-01-09 | Engelhard Corporation | Porous mullite production |
GB2146633A (en) * | 1983-08-04 | 1985-04-24 | Nikki Universal Co Ltd | Process of preparing alumina for use as a catalyst carrier |
EP0669162A1 (en) * | 1994-02-24 | 1995-08-30 | Fina Research S.A. | Silica-alumina carriers preparation, hydrogenation catalysts preparation therewith and their use for aromatics hydrogenation |
-
1971
- 1971-05-19 GB GB1589671*[A patent/GB1352921A/en not_active Expired
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0130734A2 (en) * | 1983-06-20 | 1985-01-09 | Engelhard Corporation | Porous mullite production |
EP0130734A3 (en) * | 1983-06-20 | 1986-07-30 | Engelhard Corporation | Porous mullite |
GB2146633A (en) * | 1983-08-04 | 1985-04-24 | Nikki Universal Co Ltd | Process of preparing alumina for use as a catalyst carrier |
EP0669162A1 (en) * | 1994-02-24 | 1995-08-30 | Fina Research S.A. | Silica-alumina carriers preparation, hydrogenation catalysts preparation therewith and their use for aromatics hydrogenation |
US6479004B1 (en) | 1994-02-24 | 2002-11-12 | Fina Research, S.A. | Silica-alumina carriers preparation, hydrogenation catalysts preparation therewith and their use for aromatics hydrogenation |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US1920795A (en) | Production of hydrocyanic acid | |
US2349243A (en) | Catalysis | |
KR960012696B1 (en) | Preparation of promoted silica catalysts | |
GB1284086A (en) | Preparation of silica gels | |
KR930701228A (en) | Hydrogenation Catalytic Catalyst | |
US3416888A (en) | Method for preparing spheroidal alumina | |
US4935574A (en) | Preparation of para-xylene by toluene methylation | |
US3501264A (en) | Glassy alkalized alumina | |
GB1452279A (en) | Fluids purification | |
US4119568A (en) | Solid supported catalysts for catalytic reduction of nitrogen oxides in waste gases | |
GB907910A (en) | Process for manufacturing spheroidal alumina particles | |
US3105053A (en) | Process for preparing alumina hydrosol and gel | |
US2967159A (en) | Hydrodesulfurization catalyst and method of preparing same | |
GB592116A (en) | Stabilized alumina and preparation thereof | |
GB1352921A (en) | Continuous process for preparing extruded alumina bodies | |
KR920003219B1 (en) | Process for the production of zeolite | |
US3042628A (en) | Production of alumina and catalyst containing same | |
US3151939A (en) | Process for preparing alumina hydrate having 1. 2 to 2. 6 moles of water of hydration | |
GB986561A (en) | A process for decomposing zircon sand | |
US2685569A (en) | Silica-magnesia catalyst and method of preparation | |
US4111967A (en) | Silicon containing catalysts | |
US3027233A (en) | Process for the production of alumina from aluminum sulfate | |
US3900425A (en) | Catalyst for oxidation of hydrocarbons and method of making same | |
US3098032A (en) | Hydrodesulfurization process employing cobalt-molybdenum-molecular sieve catalyst | |
US2657184A (en) | Alumina gel-containing catalysts |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PS | Patent sealed [section 19, patents act 1949] | ||
427A | Application made for restoration (sect. 27/1949) | ||
427C | Application for amendment of specification now open to opposition (sect. 27/1949) | ||
427B | Order made restoring the patent (sect. 27/1949) | ||
732 | Registration of transactions, instruments or events in the register (sect. 32/1977) | ||
PCNP | Patent ceased through non-payment of renewal fee |